KR102406534B1 - A Luminiscent Paint Composition for Fishing - Google Patents
A Luminiscent Paint Composition for Fishing Download PDFInfo
- Publication number
- KR102406534B1 KR102406534B1 KR1020200090898A KR20200090898A KR102406534B1 KR 102406534 B1 KR102406534 B1 KR 102406534B1 KR 1020200090898 A KR1020200090898 A KR 1020200090898A KR 20200090898 A KR20200090898 A KR 20200090898A KR 102406534 B1 KR102406534 B1 KR 102406534B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- fishing
- pigment
- light
- Prior art date
Abstract
본 발명은 낚시용 축광 도료 조성물에 관한 것으로, 그 구성은, 고휘도장축광안료, 아크릴올리고머, 메타아크릴레이트 및 페닐글리옥실레이트을 포함하여 구성되며, 그 조성은 상기 고휘도장축광안료 60중량부와, 상기 페닐글리옥실레이트 1 내지 5중량부와, 아크릴올리고머 3중량부와, 메타아크릴레이트 10중량부를 포함하여 구성되는 것을 특징으로 한다. The present invention relates to a photoluminescent paint composition for fishing, the composition of which includes a high-brightness long photoluminescent pigment, acrylic oligomer, methacrylate and phenylglyoxylate, the composition comprising: 60 parts by weight of the high-brightness long photoluminescent pigment; 1 to 5 parts by weight of the phenylglyoxylate, 3 parts by weight of acryl oligomer, and 10 parts by weight of methacrylate.
Description
본 발명은 낚시용 축과 동료 조성물에 관한 것으로, 더욱 상세하게는 경화가 빠르고 발광시간이 긴 낚시용 축광 도료 조성물에 관한 것이다. The present invention relates to a fishing shaft and companion composition, and more particularly, to a phosphorescent paint composition for fishing with a fast curing and a long luminescence time.
일반적으로, 전철역이나 터미널, 백화점 또는 상가건물과 같이 불특정 다수인이 사용하는 각종 대형 건축물에서는 그 특성상 내부 공간이 상하로 구획되어 구성되어 있어 정전이나 기타 불의의 재난으로 전력이 끓어지면 실내공간의 조명이 정상적으로 작동되지 않고 이에 의해 비상통로 등과 같은 대피로를 찾을 수 없어 치명적인 안전사고로 이어질 수 있는 위험이 있는 등의 문제점이 있어 이를 해결하기 위한 방안으로, 건물의 내부 뿐 아니라 통상적으로 도로, 항공, 선박, 철도와 같은 교통관련 시설이나 건설 등의 안전산업은 물론 제품에 심미감을 부여하기 위한 목적의 일환으로 의복, 신발, 팬시, 낚시용품, 문구, 장난감 등 많은 산업분야에서 통상 야광 발광의 수단이 사용되고 있는데, 이러한 야광발광 수단은 주로 안전 표지나 광고 등의 목적으로 사용되는데, 자세하게는 축광(발광) 안료를 플라스틱, 도자기, 유리, 섬유 등으로 된 각종 안전제품 등을 생산할 때 첨가물로 첨가하거나 또는 잉크, 페인트 등에 이들 안료를 부가하여 상기 제품의 표면에 도포하여 어둠 속에서도 자체 발광기능에 의해 물체의 형상이나 무늬 등이 인식되도록 하는 기능을 제공한다.In general, in various large buildings used by unspecified people, such as train stations, terminals, department stores, or commercial buildings, the interior space is divided up and down due to the nature of the structure. This is a method to solve the problem that there is a risk that a fatal safety accident may occur because the evacuation route cannot be found, such as an emergency passage, etc. Transportation-related facilities such as ships and railroads, as well as the safety industry such as construction, as well as the safety industry such as construction, are used in many industrial fields such as clothes, shoes, fancy goods, fishing goods, stationery, and toys as part of the purpose of giving aesthetics to products. These luminescent means are mainly used for the purpose of safety signs or advertisements, and in detail, luminescent (luminescent) pigments are added as additives when producing various safety products made of plastics, ceramics, glass, fibers, etc., or These pigments are added to ink, paint, etc. and applied to the surface of the product to provide a function of recognizing the shape or pattern of an object by its self-luminous function even in the dark.
상기한 축광 발광 안료는 태양광, 형광등, 백열등, 수은 등을 포함하는 거의 모든 광원으로부터 나오는 빛을 흡수 및 축적해두었다가 어두운 곳에서 빛을 서서히 방출하여 발광하는 성질을 가지는 것이다.The photoluminescent pigment has a property of absorbing and accumulating light emitted from almost all light sources including sunlight, fluorescent lamps, incandescent lamps, mercury, etc., and then gradually emitting light in a dark place to emit light.
특히, 야간에 낚시 등을 하는 경우에 축광 발광 안료를 낚시찌 등에 도포하여 물고기를 유인하거나 낚시찌의 동작을 사용자가 쉽게 확인할 수 있도록 한다. In particular, in the case of fishing at night, a luminescent pigment is applied to a fishing rod, etc. to attract fish or to allow a user to easily check the operation of the fishing rod.
그러나, 종래 기술에서는 다음과 같은 문제점이 있었다. However, the prior art has the following problems.
낚시찌에 안료를 도포하면 안료가 고정되는데까지 장시간이 걸리고, 광유지력이 수초에 불과하며 광도도 낮은 문제점이 있었다. When the pigment is applied to the fishing rod, it takes a long time for the pigment to be fixed, the light retention is only a few seconds, and the luminosity is low.
상술한 문제점을 해결하기 위한 것으로, 본 발명의 목적은 도포된 안료가 빠르게 경화하고, 광유지 시간이 긴 낚시용 축광 도료 조성물을 제공하는 것이다. In order to solve the above-mentioned problems, an object of the present invention is to provide a phosphorescent paint composition for fishing in which the applied pigment cures quickly and the light retention time is long.
상술한 목적을 달성하기 위한 것으로, 본 발명인 낚시용 축광 도료 조성물은, 고휘도장축광안료, 아크릴올리고머, 메타아크릴레이트 및 페닐글리옥실레이트을 포함하여 구성될 수 있다. In order to achieve the above object, the phosphorescent paint composition for fishing of the present invention may include a high-brightness long phosphorescent pigment, acryl oligomer, methacrylate and phenylglyoxylate.
상기 고휘도장축광안료 60중량부와, 상기 페닐글리옥실레이트 1 내지 5중량부와, 아크릴올리고머 3중량부와, 메타아크릴레이트 10중량부를 포함하여 구성될 수 있다. 60 parts by weight of the high-brightness long photoluminescent pigment, 1 to 5 parts by weight of the phenylglyoxylate, 3 parts by weight of an acryl oligomer, and 10 parts by weight of methacrylate.
본 발명인 낚시용 축광 도료 조성물은 다음과 같은 효과가 있다. The phosphorescent paint composition for fishing according to the present invention has the following effects.
고휘도장축광안료를 사용하여 발광시간이 길고, 페닐글리옥실레이트을 사용하여 경화시간이 짧아 사용상의 편의가 높아지는 이점이 있다. There is an advantage in that the luminescence time is long by using a high-brightness long phosphorescent pigment, and the curing time is short by using phenylglyoxylate, which increases the convenience of use.
도 1은 본 발명인 낚시용 축광 도료 조성물을 루어에 도포한 모습을 보인 도면.1 is a view showing a state in which a phosphorescent paint composition for fishing according to the present invention is applied to a lure.
이하 본 발명인 낚시용 축광 도료 조성물의 바람직한 실시예가 첨부된 도면을 참고하여 상세하게 설명한다. Hereinafter, a preferred embodiment of the phosphorescent paint composition for fishing according to the present invention will be described in detail with reference to the accompanying drawings.
본 발명인 낚시용 축광 도료 조성물은 고휘도장축광안료, 아크릴올리고머, 메타아크릴레이트 및 페닐글리옥실레이트을 포함하여 구성될 수 있다. The phosphorescent paint composition for fishing according to the present invention may include a high-brightness long-term phosphorescent pigment, acryl oligomer, methacrylate and phenylglyoxylate.
먼저, 본 발명인 낚시용 축광 도료 조성물에는 고휘도장축광안료가 포함되다. First, the phosphorescent paint composition for fishing according to the present invention includes a high-luminance long-term phosphorescent pigment.
일반적으로, 축광 안료는 매우 비중이 크고 입자 사이즈가 19 내지 25mm로 크므로 종래의 통상적인 축광 안료는 저장한 상태에서 단시간에 침전하여 굳어지는 단점이 있다. 그러나, 상기한 바와 같이 본 발명에 따른 안료는 이러한 침전에 따른 단점을 방지하기 위해서 축광 안료에 나노사이즈의 실리카 입자를 부가하므로 이들 입자가 안료의 침전을 방지하는 역할을 하여 장시간 정치하더라도 침전현상이 발생하지 않게 한다.In general, since the photoluminescent pigment has a very large specific gravity and a particle size of 19 to 25 mm, conventional photoluminescent pigments have a disadvantage in that they precipitate and harden in a short time in a stored state. However, as described above, in the pigment according to the present invention, nano-sized silica particles are added to the phosphorescent pigment in order to prevent the disadvantages caused by the precipitation, so these particles serve to prevent the precipitation of the pigment, so that the precipitation phenomenon is prevented even after standing for a long time. make it not happen
또한, 종래의 축광 발광 코팅제는 일반적으로 용제형으로 되어 코팅 시 용제의 휘발에 의한 냄새 등으로 인체에 유해할 뿐 아니라 공해가 심하여 바람직하지 않았으나, 상기 본 발명에 따른 발광 안료는 휘발성 용제를 사용하지 않아 상기한 공해문제를 발생하지 않는다.In addition, the conventional photoluminescent coating agent is generally of a solvent type, and it is not preferable because it is harmful to the human body due to the smell caused by volatilization of the solvent during coating, and the pollution is severe. Therefore, the above-mentioned pollution problem does not occur.
본 발명의 고휘도장축광안료는 Al2O3, SrO3 및 B2O3로 구성될 수 있다. 상기 고휘도장축광안료는 무기물을 주원료로 하여 기존의 방사능 물질에 의해 발광하는 소재에 비하여 안전성이 높아진다. 상기 고휘도장축광안료는 60중량부가 포함될 수 있다. The high luminance long photoluminescent pigment of the present invention may be composed of Al 2 O 3 , SrO 3 and B 2 O 3 . The high-brightness long-term phosphorescent pigment uses an inorganic material as a main raw material and has higher safety than a material that emits light by a conventional radioactive material. The high-brightness long photoluminescent pigment may contain 60 parts by weight.
특히, 상기 고휘도장축광안료는 산화알루미늄(Al2O3) 60중량부, 산화스트론튬(SrO3) 20중량부 및 산화붕소(B2O3) 20중량부의 비율로 구성될 수 있다. In particular, the high-brightness long photoluminescent pigment may be composed of 60 parts by weight of aluminum oxide (Al 2 O 3 ), 20 parts by weight of strontium oxide (SrO 3 ), and 20 parts by weight of boron oxide (B 2 O 3 ).
이는 기존의 ZnS 계에 비하여 암실에서 인식 가능한 잔광시간이 20시간 이상되고 안전표지나 광고물에 사용될 수 있다. 또한, 1500℃의 고온 및 -20℃의 저온에서도 축광성이 보전되며, 파장범위가 400 내지 700nm로 형성된다. Compared to the existing ZnS system, the recognizable afterglow time in the dark room is more than 20 hours, and it can be used for safety signs or advertisements. In addition, the photoluminescence property is preserved even at a high temperature of 1500°C and a low temperature of -20°C, and the wavelength range is 400 to 700 nm.
그리고, 본 발명인 낚시용 축광 도료 조성물에는 아크릴올리고머가 포함된다. 상기 아크릴올리고머는 도료의 베이스 역할을 한다. 상기 아크릴올리고머는 3중량부가 포함될 수 있다. And, the phosphorescent paint composition for fishing according to the present invention contains an acrylic oligomer. The acrylic oligomer serves as a base for the paint. The acrylic oligomer may contain 3 parts by weight.
그리고, 본 발명인 낚시용 축광 도료 조성물에는 메타아크릴레이트가 포함된다. 상기 메타아크릴레이트는 반응성모노머로 개시제 역할을 한다. 상기 메타아크릴레이트는 10중량부가 포함될 수 있다. And methacrylate is contained in the phosphorescent paint composition for fishing which is this invention. The methacrylate is a reactive monomer and serves as an initiator. The methacrylate may be included in 10 parts by weight.
그리고, 본 발명인 낚시용 축광 도료 조성물에는 페닐글리옥실레이트이 포함된다. 상기 페닐글리옥실레이트은 광개시제 역할을 하는 것으로, 본 발명인 낚시용 축광 도료 조성물을 도포한 후 광을 조사하면 광에 의하여 반응이 시작된다. And, the phosphorescent paint composition for fishing of the present invention contains phenylglyoxylate. The phenylglyoxylate acts as a photoinitiator, and when the photoluminescent paint composition for fishing of the present invention is applied and then irradiated with light, a reaction is started by the light.
상기 페닐글리옥실레이트은 1 내지 5중량부가 포함될 수 있다. 상기 페닐글리옥실레이트은 1중량부 미만으로 포함되면 광을 조사하여도 반응이 이루어지지 않거나 광을 과하게 오랫동안 조사해야 되는 문제점이 발생한다. The phenylglyoxylate may be included in 1 to 5 parts by weight. When the phenylglyoxylate is included in an amount of less than 1 part by weight, there is a problem that the reaction does not occur even when irradiated with light or that light must be irradiated for an excessively long time.
그리고, 상기 페닐글리옥실레이트은 5중량부를 초과하여 포함되면 아주 적은 양의 광에도 반응이 이루어져 제품으로서 반응을 조절할 수 없는 문제점이 발생한다. In addition, when the phenylglyoxylate is included in excess of 5 parts by weight, a reaction occurs even in a very small amount of light, thereby causing a problem in that the reaction cannot be controlled as a product.
이하, 상술한 방법으로 제조된 본 발명인 낚시용 축광 도료 조성물을 실험한 결과를 토대로 설명한다. Hereinafter, it will be described based on the experimental results of the present invention, the phosphorescent paint composition for fishing prepared by the above-described method.
[ 실시예 1 ][Example 1]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 0.5중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다. A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 0.5 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to 10 parts by weight. irradiated for seconds.
[ 실시예 2 ][Example 2]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 1중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다. A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 1 part by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2) and then UV light was applied to 10 parts by weight. irradiated for seconds.
[ 실시예 3 ][Example 3]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 2중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다. A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 2 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to 10 parts by weight. irradiated for seconds.
[ 실시예 4 ][Example 4]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 3중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다. A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 3 parts by weight of the phenylglyoxylate, 3 parts by weight of acryl oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to the luer (2). irradiated for seconds.
[ 실시예 5 ][Example 5]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 4중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다. A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 4 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to the luer (2). irradiated for seconds.
[ 실시예 6 ][Example 6]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 5중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다.A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 5 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2) and then UV light was applied to 10 parts by weight. irradiated for seconds.
[ 실시예 7 ][Example 7]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 6중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다.A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 6 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to 10 parts by weight. irradiated for seconds.
[ 실시예 8 ][Example 8]
고휘도장축광안료 60중량부와 상기 페닐글리옥실레이트 7중량부와 아크릴올리고머 3중량부와 메타아크릴레이트 10중량부를 혼합하여 제조된 도료(4)를 루어(2)에 도포한 후 UV광을 10초 동안 조사하였다.A paint (4) prepared by mixing 60 parts by weight of a high-brightness long photoluminescent pigment, 7 parts by weight of the phenylglyoxylate, 3 parts by weight of acrylic oligomer, and 10 parts by weight of methacrylate was applied to the luer (2), and then UV light was applied to 10 parts by weight. irradiated for seconds.
시간light irradiation
hour
발광partial
radiation
표 1에 나타난 바와 같이, 광개시제를 1중량부 미만으로 포함되면 발광을 나타내기 까지 광을 조사해야 하는 시간이 너무 오래 걸려 사용하기가 어렵고, 광개시제를 5중량부를 초과하여 포함하면 도포하여 광을 개시하기도 전에 발광하여 제품으로서 취급하기가 어려운 문제점이 있음을 확인할 수 있다. As shown in Table 1, when the photoinitiator is included in less than 1 part by weight, the time required to irradiate light until light emission is too long and difficult to use, and when the photoinitiator is included in excess of 5 parts by weight, it is applied to initiate light It can be seen that there is a problem that it is difficult to handle as a product because it emits light before it is used.
이와 같이, 상술한 본 발명의 기술적 구성은 본 발명이 속하는 기술분야의 당업자가 본 발명의 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다.As such, those skilled in the art to which the present invention pertains will understand that the above-described technical configuration of the present invention may be implemented in other specific forms without changing the technical spirit or essential characteristics of the present invention.
그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해되어야 하고, 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허등록청구범위에 의하여 나타나며, 특허등록청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.Therefore, the embodiments described above are to be understood as illustrative and not restrictive in all respects, and the scope of the present invention is indicated by the following claims rather than the above detailed description, and the meaning and scope of the claims And all changes or modifications derived from the concept of equivalents should be construed as being included in the scope of the present invention.
2: 루어 4: 도료2: Lure 4: Paint
Claims (2)
상기 안료 60중량부;
상기 페닐글리옥실레이트 1중량부;
아크릴올리고머 3중량부; 및
메타아크릴레이트 10중량부를 포함하며,
상기 안료는 ,
산화알루미늄(Al2O3) 60중량부, 산화스트론튬(SrO3) 20중량부 및 산화붕소(B2O3) 20중량부의 비율로 구성되는 것을 특징으로 하는 낚시용 축광 도료 조성물.Contains pigments, acrylic oligomers, methacrylates and phenylglyoxylates,
60 parts by weight of the pigment;
1 part by weight of the phenylglyoxylate;
3 parts by weight of acrylic oligomer; and
Contains 10 parts by weight of methacrylate,
The pigment is
Aluminum oxide (Al 2 O 3 ) 60 parts by weight, strontium oxide (SrO 3 ) 20 parts by weight and boron oxide (B 2 O 3 ) A phosphorescent paint composition for fishing, characterized in that it consists of 20 parts by weight.