KR102403888B1 - Composition for discolored cosmetic container dropper - Google Patents
Composition for discolored cosmetic container dropper Download PDFInfo
- Publication number
- KR102403888B1 KR102403888B1 KR1020200091481A KR20200091481A KR102403888B1 KR 102403888 B1 KR102403888 B1 KR 102403888B1 KR 1020200091481 A KR1020200091481 A KR 1020200091481A KR 20200091481 A KR20200091481 A KR 20200091481A KR 102403888 B1 KR102403888 B1 KR 102403888B1
- Authority
- KR
- South Korea
- Prior art keywords
- color
- dropper
- weight
- pigment
- cosmetic container
- Prior art date
Abstract
본 발명은 변색성 화장품용기 스포이트용 조성물에 관한 것으로, 더욱 상세하게는 가역성 광변색안료 및 가역성 감온변색안료가 함유되는 것을 특징으로 한다.
상기와 같이 가역성 광변색안료 및 가역성 감온변색안료가 함유되면 자외선에 노출되는 경우 스포이트가 변색되어 자외선 차단효과를 나타내기 때문에 화장품 성분의 변질을 억제하고, 고온에 노출되는 경우 사용자가 인식할 수 있도록 하여 화장품의 관리를 용이하게 하는 변색성 화장품용기 스포이트가 제공된다.The present invention relates to a composition for a color-changeable cosmetic container dropper, and more particularly, it is characterized in that it contains a reversible photochromic pigment and a reversible thermochromic pigment.
As described above, when the reversible photochromic pigment and the reversible thermochromic pigment are contained, when exposed to ultraviolet light, the dropper is discolored and exhibits a UV-blocking effect. There is provided an eyedropper for a color-changing cosmetic container that facilitates the management of cosmetics.
Description
본 발명은 변색성 화장품용기 스포이트용 조성물에 관한 것으로, 더욱 상세하게는 자외선에 노출되는 경우 스포이트가 변색되어 자외선 차단효과를 나타내기 때문에 화장품 성분의 변질을 억제하고, 고온에 노출되는 경우 사용자가 인식할 수 있도록 하여 화장품의 관리를 용이하게 하는 변색성 화장품용기 스포이트용 조성물에 관한 것이다.The present invention relates to a composition for a color-changeable cosmetic container dropper, and more particularly, when exposed to ultraviolet light, the dropper is discolored and exhibits a UV-blocking effect. It relates to a composition for a color-changeable cosmetic container dropper that facilitates the management of cosmetics by making it possible to do so.
일반적으로 화장품은 내용물, 기능, 화장품의 종류, 용도 등에 따라 매우 다양하며, 화장품 내용물의 타입 별로도 파우더, 액체, 겔(gel) 또는 크림(cream), 고체 등의 여러 가지 형태로 이루어질 수 있다.In general, cosmetics are very diverse depending on the content, function, type of cosmetic, use, etc., and may be made in various forms such as powder, liquid, gel or cream, solid, etc. according to the type of cosmetic content.
또한, 상기의 다양한 화장품 내용물을 담는 용기도 화장품 내용물이나 종류, 기능 등에 따라 다양한 형상으로 형성될 수 있는데, 스킨 및 로션과 같은 액상 화장품의 경우 내부에 내용물을 일정량 수용하도록 하고 입구는 좁은 배출부를 구비하도록 하고 평상시에는 캡에 의하여 막힌 상태가 되도록 형성되는 것이 대부분이었다.In addition, the container containing the above various cosmetic contents may also be formed in various shapes depending on the cosmetic contents, type, function, etc. In the case of liquid cosmetics such as skin and lotion, a certain amount of contents is accommodated therein, and the entrance is provided with a narrow discharge part Most of them were formed so that they were closed by the cap in normal times.
이러한 액상 화장품의 사용시에는 캡을 분리하고 용기를 기울여서 사용하거나 또는 그 상태로 충격을 주어 배출구를 통해 내용물을 손에 묻힌 후 사용하였는데, 이러한 경우 내용물인 화장품을 적정한 양으로 조절하는 것이 힘들고 내용물이 손에 묻어 낭비되는 문제점이 있었다.When using such liquid cosmetics, the cap was removed and the container was tilted, or the contents were immersed in the hands through the outlet by giving a shock in that state. There was a problem of wasting buried in the .
이에 따라, 내용물이 수용되는 용기의 입구에 스포이트(Spuit)를 장착하고, 사용자가 이를 파지하여 내용물을 소량씩 토출하여 사용함으로써 내용물의 낭비를 최소화하는 방법이 이용되고 있다.Accordingly, a method of minimizing wastage of the contents is used by mounting a dropper at the entrance of the container in which the contents are accommodated, and then discharging the contents little by little by the user holding them.
한편, 최근에는 액상화장품이 자외선에 의해 변질되는 것을 방지하고자 액상화장품의 용기를 갈색으로 제조하는 경우가 많은데, 이러한 경우에도 상기의 스포이트는 대부분이 투명한 재질로 이루어진다. 그 이유는 스포이트가 유색으로 제조되는 경우 미관상 좋지 못하며, 사용자가 화장품 용기 내에 스포이트를 화장품이 변질된 것으로 오인할 소지가 있기 때문이다.On the other hand, in recent years, in order to prevent the deterioration of the liquid cosmetics by ultraviolet rays, the container of liquid cosmetics is often manufactured in brown color. Even in this case, most of the droppers are made of a transparent material. The reason is that, when the dropper is manufactured in a colored color, it is not aesthetically good, and there is a possibility that the user may mistake the dropper in the cosmetic container as that the cosmetic is altered.
그러나, 상기와 같이 스포이트가 투명한 재질로 이루어지는 경우에는 화장품 용기에서 내용물을 토출하는 과정에서 자외선에 의해 내용물이 변질되는 현상이 발생할 수 있는 문제점이 있다.However, when the dropper is made of a transparent material as described above, there is a problem in that the contents may be deteriorated by ultraviolet rays in the process of discharging the contents from the cosmetic container.
또한, 액상 화장품은 온도에 민감하기 때문에, 적정온도를 유지해야 하는데, 종래에 화장품 용기는 온도를 감지하는 기능이 없어 보관에 불편함이 따르는 문제점이 있었다.In addition, since liquid cosmetics are sensitive to temperature, it is necessary to maintain an appropriate temperature. Conventionally, cosmetic containers do not have a function of sensing temperature, so there is a problem with storage inconvenience.
본 발명의 목적은 자외선에 노출되는 경우 스포이트가 변색되어 자외선 차단효과를 나타내기 때문에 화장품 성분의 변질을 억제하고, 고온에 노출되는 경우 사용자가 인식할 수 있도록 하여 화장품의 관리를 용이하게 하는 변색성 화장품용기 스포이트용 조성물을 제공하는 것이다.The object of the present invention is to suppress the deterioration of cosmetic ingredients because the dropper is discolored when exposed to ultraviolet rays and exhibits a ultraviolet blocking effect, and discoloration to facilitate the management of cosmetics by allowing the user to recognize when exposed to high temperatures. To provide a composition for a cosmetic container dropper.
본 발명의 목적은 가역성 광변색안료 및 가역성 감온변색안료가 함유되는 것을 특징으로 하는 변색성 화장품용기 스포이트용 조성물을 제공함에 의해 달성된다.An object of the present invention is achieved by providing a composition for a color-changeable cosmetic container dropper, characterized in that it contains a reversible photochromic pigment and a reversible thermochromic pigment.
본 발명의 바람직한 특징에 따르면, 상기 변색성 화장품용기 스포이트용 조성물은 가역성 광변색안료 5 내지 20 중량% 및 가역성 감온변색안료 5 내지 20 중량%가 함유되는 것으로 한다.According to a preferred feature of the present invention, the composition for a color-changeable cosmetic container dropper contains 5 to 20% by weight of a reversible photochromic pigment and 5 to 20% by weight of a reversible thermochromic pigment.
본 발명의 더 바람직한 특징에 따르면, 상기 변색성 화장품용기 스포이트용 조성물은 유리 또는 투명성 합성수지 60 내지 90 중량%, 광변색안료 5 내지 20 중량% 및 가역성 감온변색안료 5 내지 20 중량%로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the composition for a color-changeable cosmetic container dropper is 60 to 90% by weight of glass or transparent synthetic resin, 5 to 20% by weight of a photochromic pigment, and 5 to 20% by weight of a reversible thermochromic pigment. .
본 발명의 더욱 바람직한 특징에 따르면, 상기 가역성 광변색안료는 자외선이 조사되면 갈색으로 변색되는 것으로 한다.According to a more preferred feature of the present invention, the reversible photochromic pigment is to be discolored to brown when irradiated with ultraviolet rays.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 가역성 광변색안료는 흑색 광변색안료 100 중량부 및 황색 광변색안료 50 내지 150 중량부로 이루어지는 것으로 한다.According to an even more preferred feature of the present invention, the reversible photochromic pigment is composed of 100 parts by weight of a black photochromic pigment and 50 to 150 parts by weight of a yellow photochromic pigment.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 가역성 감온변색안료는 35℃ 이상의 온도에서 갈색으로 변색되는 것으로 한다.According to an even more preferred feature of the present invention, the reversible thermochromic pigment is to be discolored to brown at a temperature of 35° C. or higher.
또한, 본 발명의 목적은 갈색 색상안료가 함유되며, 상기 갈색 색상안료는 산화철 및 산화망간으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 갈색을 나타내는 화장품용기 스포이트용 조성물을 제공함에 의해서도 달성될 수 있다.In addition, the object of the present invention is to be achieved by providing a composition for dropper for cosmetic containers exhibiting brown color, characterized in that the brown color pigment contains at least one selected from the group consisting of iron oxide and manganese oxide. can
본 발명에 따른 변색성 화장품용기 스포이트용 조성물은 자외선에 노출되는 경우 스포이트가 변색되어 자외선 차단효과를 나타내기 때문에 화장품 성분의 변질을 억제하고, 고온에 노출되는 경우 사용자가 인식할 수 있도록 하여 화장품의 관리를 용이하게 하는 변색성 화장품용기 스포이트를 제공하는 탁월한 효과를 나타낸다.The composition for dropper for a color-changeable cosmetic container according to the present invention suppresses deterioration of cosmetic ingredients because the dropper is discolored when exposed to ultraviolet rays and exhibits a UV-blocking effect, and when exposed to high temperature, the user can recognize the cosmetic product. It has an excellent effect of providing a color-changing cosmetic container dropper that facilitates management.
도 1은 본 발명의 실시예 1을 통해 제조된 변색성 화장품용기 스포이트를 실내 및 상온조건에서 촬영하여 나타낸 사진이다.
도 2는 본 발명의 실시예 1을 통해 제조된 변색성 화장품용기 스포이트에 자외선을 조사한 후에 촬영하여 나타낸 사진이다.
도 3은 본 발명의 실시예 1을 통해 제조된 변색성 화장품용기 스포이트를 가열한 후에 촬영하여 나타낸 사진이다.1 is a photograph showing a color-changing cosmetic container dropper prepared in Example 1 of the present invention, taken indoors and at room temperature.
2 is a photograph taken after irradiating ultraviolet rays to the eyedropper for a color-changing cosmetic container prepared in Example 1 of the present invention.
3 is a photograph taken after heating the color-changeable cosmetic container dropper prepared in Example 1 of the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.Hereinafter, a preferred embodiment of the present invention and the physical properties of each component will be described in detail, which is intended to describe in detail enough that a person of ordinary skill in the art to which the present invention pertains can easily carry out the invention, This does not mean that the technical spirit and scope of the present invention is limited.
본 발명에 따른 변색성 화장품용기 스포이트용 조성물은 가역성 광변색안료 및 가역성 감온변색안료가 함유되며, 가역성 광변색안료 5 내지 20 중량% 및 가역성 감온변색안료 5 내지 20 중량%가 함유되는 것이 더욱 바람직하고, 유리 또는 투명성 합성수지 60 내지 90 중량%, 광변색안료 5 내지 20 중량% 및 가역성 감온변색안료 5 내지 20 중량%로 이루어지는 것이 가장 바람직하다.The composition for a color-changeable cosmetic container dropper according to the present invention contains a reversible photochromic pigment and a reversible thermochromic pigment, more preferably 5 to 20% by weight of the reversible photochromic pigment and 5 to 20% by weight of the reversible thermochromic pigment and 60 to 90% by weight of a glass or transparent synthetic resin, 5 to 20% by weight of a photochromic pigment, and 5 to 20% by weight of a reversible thermochromic pigment.
상기 유리 또는 투명 합성수지는 본 발명에 따른 변색성 화장품용기 스포이트용 조성물의 주재료가 되는 성분으로, 유리의 경우 통상의 재료를 사용할 수 있으며, 합성수지의 경우 화장품용기로 적용되어야하기 때문에, 투명성 뿐만 아니라 내화학성이 우수한 합성수지로 이루어지는 것이 바람직하며, 아크릴계 합성수지로 이루어지는 것이 바람직하다.The glass or transparent synthetic resin is a main material of the composition for dropper for color-changing cosmetic containers according to the present invention, and in the case of glass, ordinary materials can be used. It is preferable that it consists of a synthetic resin excellent in chemical property, and it is preferable that it consists of an acrylic synthetic resin.
상기와 같이 유리 또는 투명 합성수지로 이루어지는 주재료에는 상기 가역성 광변색안료나 상기 감온변색안료와의 혼합성을 향상시키기 위해 상기 유리 또는 투명 합성수지 100 중량부 대비 윤활제 0.1 내지 1 중량부 및 결합제 0.1 내지 1 중량부가 사용될 수 있다.As described above, in the main material made of glass or transparent synthetic resin, 0.1 to 1 parts by weight of a lubricant and 0.1 to 1 parts by weight of a binder relative to 100 parts by weight of the glass or transparent synthetic resin to improve the compatibility with the reversible photochromic pigment or the thermochromic pigment Additional may be used.
상기 가역성 광변색안료는 5 내지 20 중량%가 함유되며, 자외선이 조사되면 갈색으로 변색되는데, 흑색 광변색안료 100 중량부 및 황색 광변색안료 50 내지 150 중량부로 이루어지는 것이 바람직하다.The reversible photochromic pigment is contained in an amount of 5 to 20% by weight, and is discolored to brown when irradiated with ultraviolet rays. Preferably, it is composed of 100 parts by weight of a black photochromic pigment and 50 to 150 parts by weight of a yellow photochromic pigment.
상기의 성분으로 이루어지는 가역성 광변색안료는 특정한 파장의 빛 에너지를 흡수하여 분자구조의 변화가 일어나는 물질로, 이 상태에서 외부에 나타내는 색상이 변화하는 화합물이다. 따라서 이 물질에 가해지는 에너지가 중단되면 이전의 분자구조로 가역적으로 돌아가는 특성을 나타낸다.A reversible photochromic pigment composed of the above components is a material in which a change in molecular structure occurs by absorbing light energy of a specific wavelength, and in this state, the color displayed to the outside is changed. Therefore, when the energy applied to this material is stopped, it shows the property of reversibly returning to the previous molecular structure.
더욱 상세하게는 가역성 광변색안료는 자외선의 흡수량이 증가하면 분자 내의 고리 구조가 콘쥬게이션 구조로 되어 반사되는 빛의 파장이 변화하여 색상이 갈색으로 변화하는데, 반대로 자외선의 흡수량이 감소하면 다시 고리 구조가 형성되어 본래의 투명한 상태로 돌아가게 되는 가역적 특성을 나타낸다.More specifically, in the case of a reversible photochromic pigment, when the amount of absorption of ultraviolet light increases, the ring structure in the molecule becomes a conjugated structure, and the wavelength of the reflected light changes and the color changes to brown. is formed and shows the reversible property of returning to the original transparent state.
상기와 같이 자외선이 조사되면 갈색으로 변색되는 광변색안료가 함유되면 본 발명에 따른 변색성 화장품용기 스포이트용 조성물로 제조된 스포이트에 자외선이 조사되는 경우 스포이트가 갈색으로 변색되어 스포이트 내 화장품 성분이 자외선으로 인해 변질되는 것을 억제할 수 있다.As described above, when a photochromic pigment that turns brown when irradiated with ultraviolet rays is contained, when ultraviolet rays are irradiated to the dropper prepared with the composition for a color-changeable cosmetic container dropper according to the present invention, the dropper is discolored to brown and the cosmetic component in the dropper is UV-rayed. deterioration due to this can be suppressed.
이때, 상기 가역성 광변색안료의 성분은 특별히 한정되지 않고 통상의 제품화된 성분이면 어떠한 것이든 사용가능한데, 상기 가역성 광변색안료의 함량이 5 중량% 미만이면 상기의 효과가 미미하며, 상기 가역성 광변색안료의 함량이 20 중량%를 초과하게 되면 변색성 화장품용기의 투명도가 지나치게 낮아지기 때문에 바람직하지 못하다.In this case, the component of the reversible photochromic pigment is not particularly limited and any commercially available component can be used. If the content of the reversible photochromic pigment is less than 5% by weight, the above effect is insignificant, and the reversible photochromic pigment is When the content of the pigment exceeds 20% by weight, it is not preferable because the transparency of the color-changing cosmetic container is too low.
일반적으로 가역성 광변색안료 금속산화물, 알칼리토금속, 수은 화합물, 전이금속 화합물 등의 무기물로 구성되어 있는 무기성과, 벤조피란, 나프토피란, 스피로 피란, 스피로 옥사진, 펄지미드, 디아릴에텐, 아조 화합물 등의 유기성으로 구분되는데, 본 발명에서는 자외선 조사 시 이색성을 나타낼 수 있는 착색 상태로 변화하는 자외선 변색성을 갖고 있는 화합물로서, 공지의 자외선 변색성을 갖는 화합물이라면 제한 없이 사용될 수 있다.In general, reversible photochromic pigments include inorganic substances such as metal oxides, alkaline earth metals, mercury compounds, and transition metal compounds; It is classified into organic properties such as azo compounds. In the present invention, as a compound having ultraviolet color change to a colored state capable of exhibiting dichroism when irradiated with ultraviolet light, any compound having known ultraviolet color change properties may be used without limitation.
상기 가역성 광변색안료의 예로서는 스피로피란(spiropyran)계 화합물, 스피로옥사진(spirooxazine)계 화합물, 디아릴에텐(diarylethene)계 화합물, 풀지드(fulgide)계 화합물 및 나프토피란(naphtopyran)계 화합물로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다.Examples of the reversible photochromic pigment include a spiropyran-based compound, a spirooxazine-based compound, a diarylethene-based compound, a fulgide-based compound, and a naphtopyran-based compound It is preferable that it consists of one or more selected from the group consisting of.
또한, 상기 가역성 광변색안료는 제한되지 않으나, 분자 구조 상 종횡 길이가 다른 장쇄 구조(long chain structure)를 가지는 것이 바람직하며, 벤젠환, 복소환 등의 π 공액(conjugation) 구조가 확장되고, π 공액 구조로 연결되는 각 구성 골격의 입체적(steric) 구조가 변화하지 않는 것이 보다 바람직하다.In addition, the reversible photochromic pigment is not limited, but preferably has a long chain structure having different vertical and horizontal lengths in terms of molecular structure, and π conjugated structures such as benzene rings and heterocycles are extended, and π It is more preferable that the steric structure of each structural skeleton connected by the conjugated structure does not change.
상기 가역성 감온변색안료는 5 내지 20 중량%가 함유되며 특정온도 이상에서 변색되는 특성을 나타내는데, 본 발명에서는 액상화장품이 변질될 수 있는 온도인 35℃ 이상에서 갈색으로 변색되는 것을 사용하는 것이 바람지하다.The reversible thermochromic pigment contains 5 to 20% by weight and exhibits discoloration at a specific temperature or higher. do.
상기와 같은 역할을 하는 가역성 감온변색안료는 색상을 결정하는 역할을 하는 전자공여성 유기화합물, 농도를 결정해주는 역할을 하는 전자수용성 화합물 및 변색온도를 결정해주는 역할을 하는 알콜류로 구성되는데, 전자공여성 유기화합물은 구체적으로 노란색을 결정하는 3, 6-디메톡시플루오레인, 오렌지색을 결정하는 3-사이클로헥실아미노-6-클로로플루오레인, 오렌지레드색을 결정하는 3-디에틸아미노벤플루오레인, 빨간색을 결정하는 로다민 B 락톤, 파란색을 결정하는 크리스탈 바이올렛 락톤, 녹색을 결정하는 3-디에틸아미노-7-디벤질아미노플루오레인, 검정색을 결정하는 3-디에틸아미노-6-메틸아미노플루오레인 등이 있는데, 본 발명에서는 스포이트가 일반적인 액상화장품 용기에 적용되는 갈색을 나타내도록 노란색을 결정하는 3, 6-디메톡시플루오레인 및 검정색을 결정하는 3-디에틸아미노-6-메틸아미노플루오레인의 혼합물로 이루어지는 것이 바람지하다.The reversible thermochromic pigment that plays the above role is composed of an electron-donating organic compound that determines the color, an electron-accepting compound that determines the concentration, and alcohols that determine the discoloration temperature. Specifically, the compound is 3,6-dimethoxyfluorane, which determines yellow, 3-cyclohexylamino-6-chlorofluorane, which determines orange color, 3-diethylaminobenfluorane, which determines orange-red color, and red color. Rhodamine B lactone to determine blue, crystal violet lactone to determine blue, 3-diethylamino-7-dibenzylaminofluorane to determine green, 3-diethylamino-6-methylaminofluorane to determine black, etc. There is, in the present invention, a mixture of 3,6-dimethoxyfluorane, which determines yellow, and 3-diethylamino-6-methylaminofluorane, which determines black color so that the dropper shows brown applied to general liquid cosmetic containers. It is preferable to make it with
또한, 상기 전자수용성 화합물은, 프로필갈레이트를 사용하는 것이 바람직하며, 상기 알코올류는 선택하고자 하는 변색온도에 따라, N-옥틸알콜(-40℃), N-덱틸알콜(-13℃), N-라우릴알콜(16℃), N-미리스틸알콜(35℃), N-세틸알콜(45℃), N-스테아릴알콜(53℃)등을 사용할 수 있는데, 상기에 나열된 전자공여성 물질과 전자수용성 물질이 알코올류가 존재하는 상태에서 열적 평형에 따라 색상의 변화를 나타내게 되는 것이다.In addition, it is preferable to use propyl gallate as the electron-accepting compound, and the alcohols are N-octyl alcohol (-40° C.), N-dectyl alcohol (-13° C.), depending on the color change temperature to be selected. N-lauryl alcohol (16°C), N-myristyl alcohol (35°C), N-cetyl alcohol (45°C), N-stearyl alcohol (53°C), etc. can be used, and the electron-donating substances listed above And the electron-accepting material will show a change in color according to the thermal equilibrium in the presence of alcohols.
또한, 가역성 감온변색안료는 상기에 나열된 색상의 변화를 부여하기 위한 온도 범위를 5℃ 간격 이상으로 조절할 수 있으며, 본 발명에 따른 가역성 감온변색안료는 상온에서는 무색을 나타내어 육안으로 관찰할 수 없으며, 특정 온도 범위에서 반응하여 육안으로 인식할 수 있는 색상을 띠게 되는 것으로서, 상기에 기재된 내용외에도 통상적으로 공지된 기술로부터 해당내용을 용이하게 파악할 수 있다.In addition, the reversible thermochromic pigment can adjust the temperature range for imparting the color change listed above to an interval of 5° C. or more, and the reversible thermochromic pigment according to the present invention is colorless at room temperature and cannot be observed with the naked eye, It reacts in a specific temperature range to have a color recognizable by the naked eye, and in addition to the above, the content can be easily grasped from commonly known techniques.
상기와 같이 유리 또는 투명성 합성수지 60 내지 90 중량%, 광변색안료 5 내지 20 중량% 및 가역성 감온변색안료 5 내지 20 중량%로 이루어지는 변색성 화장품용기 스포이트용 조성물은 상기의 원료를 호모믹서기와 같은 교반기에 투입하고 합성수지의 성분에 따라 탄화되는 온도미만이 유지될 수 있도록 약 100 내지 200℃ 정도의 온도에서 약 1000 내지 2000rpm의 속도로 1 내지 3시간 동안 교반하는 과정을 통해 제조된다.As described above, the composition for a color-changeable cosmetic container dropper comprising 60 to 90% by weight of glass or transparent synthetic resin, 5 to 20% by weight of a photochromic pigment, and 5 to 20% by weight of a reversible thermochromic pigment is prepared by mixing the above raw materials with a stirrer such as a homomixer. It is prepared through a process of stirring for 1 to 3 hours at a speed of about 1000 to 2000 rpm at a temperature of about 100 to 200 ° C.
이때, 상기에 언급한 바와 같이 상기 유리 또는 투명 합성수지 100 중량부 대비 윤활제 0.1 내지 1 중량부 및 결합제 0.1 내지 1 중량부가 사용될 수도 있다.In this case, as mentioned above, 0.1 to 1 parts by weight of the lubricant and 0.1 to 1 parts by weight of the binder may be used based on 100 parts by weight of the glass or transparent synthetic resin.
또한, 본 발명에 따른 갈색을 나타내는 화장품용기 스포이트용 조성물은 갈색 색상안료가 함유되며, 상기 갈색 색상안료는 산화철 및 산화망간으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는데, 유리 또는 투명성 합성수지 100 중량부에 산화철 및 산화망간으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 갈색 색상안료 0.01 내지 0.5 중량부가 함유되어 이루어지는 것이 바람직하다.In addition, the composition for dropper for cosmetic containers exhibiting brown color according to the present invention contains a brown color pigment, and the brown color pigment is made of at least one selected from the group consisting of iron oxide and manganese oxide, glass or transparent synthetic resin 100 parts by weight It is preferable that 0.01 to 0.5 parts by weight of a brown color pigment comprising at least one selected from the group consisting of iron oxide and manganese oxide is contained.
상기와 같이 갈색 색상안료가 함유된 화장품용기 스포이트용 조성물은 갈색을 나타내기 때문에, 자외선으로부터 화장품 성분이 변질되는 것을 억제할 수 있다.As described above, since the composition for dropper for cosmetic containers containing a brown color pigment has a brown color, it is possible to suppress deterioration of cosmetic components from UV rays.
또한, 상기의 갈색을 나타내는 화장품용기 스포이트용 조성물에는 상기 변색성 화장품용기 스포이트용 조성물에 사용되는 감온변색안료가 함유되어 갈색으로 인한 자외선 차단 효과 뿐만 아니라, 온도에 따른 색상변화를 인지할 수 있는 스포이트를 제공하게 된다.In addition, the composition for dropper for cosmetic containers exhibiting brown color contains a thermochromic pigment used in the composition for color-changeable cosmetic container dropper, so that not only the UV blocking effect due to brown but also the color change according to temperature can be recognized. will provide
이때, 상기 감온변색안료의 함량, 성분 및 역할은 상기 변색성 화장품용기 스포이트용 조성물에 기재된 내용과 동일하므로, 이에 대한 설명은 생략하기로 한다.At this time, since the content, component and role of the thermochromic pigment are the same as those described in the composition for dropper for color-changeable cosmetic containers, a description thereof will be omitted.
이하에서는, 본 발명에 따른 변색성 화장품용기 스포이트용 조성물의 제조방법 및 그 제조방법을 통해 제조된 변색성 화장품용기 스포이트의 물성을 실시예를 들어 설명하기로 한다.Hereinafter, the method for producing the composition for a color-changeable cosmetic container dropper according to the present invention and the physical properties of the color-changeable cosmetic container dropper manufactured through the manufacturing method will be described with reference to examples.
<제조예 1> 변색성 화장품용기 스포이트용 조성물의 제조<Preparation Example 1> Preparation of composition for color-changeable cosmetic container dropper
폴리메틸메타아크릴레이트 100 중량부, 가역성 광변색안료(흑색 광변색안료 100 중량부 및 황색 광변색안료 100 중량부) 11 중량부, 감온변색안료(3, 6-디메톡시플루오레인, 3-디에틸아미노-6-메틸아미노플루오레인, 프로필갈레이트 및 N-미리스틸알콜) 11 중량부, 윤활제(동원코퍼레이션, TPX1300) 0.5 중량부 및 결합제(롯데케미칼, PH-200)를 호모믹서기에 투입하고 160℃의 온도에서 1500rpm의 속도로 2시간 동안 교반하여 변색성 화장품용기 스포이트용 조성물을 제조하였다.100 parts by weight of polymethyl methacrylate, reversible photochromic pigment (100 parts by weight of black photochromic pigment and 100 parts by weight of yellow photochromic pigment) 11 parts by weight of thermochromic pigment (3,6-dimethoxyfluorane, 3-di 11 parts by weight of ethylamino-6-methylaminofluorane, propyl gallate and N-myristyl alcohol), 0.5 parts by weight of a lubricant (Dongwon Corporation, TPX1300) and a binder (Lotte Chemical, PH-200) were put into a homomixer, A composition for color-changeable cosmetic container dropper was prepared by stirring at a temperature of 160° C. at a speed of 1500 rpm for 2 hours.
<실시예 1><Example 1>
상기 제조예 1을 통해 제조된 변색성 화장품용기 스포이트용 조성물을 사출성형기에 투입하고 사출성형하여 변색성 화장품용기 스포이트를 제조하였다.The composition for a color-changeable cosmetic container dropper prepared in Preparation Example 1 was put into an injection molding machine and injection-molded to prepare a color-changeable cosmetic container dropper.
상기 실시예 1을 통해 제조된 변색성 화장품용기 스포이트의 외관을 상온인 실내에서 촬영하여 아래 도 1에 나타내었다.The appearance of the color-changeable cosmetic container dropper prepared in Example 1 was photographed indoors at room temperature, and is shown in FIG. 1 below.
아래 도 1에 나타낸 것처럼, 본 발명의 실시예 1을 통해 제조된 변색성 화장품용기 스포이트는 자외선이 차단된 조건과 상온조건에서는 투명성이 유지되는 것을 알 수 있다.As shown in FIG. 1 below, it can be seen that the color-changeable cosmetic container dropper prepared in Example 1 of the present invention maintains transparency under UV-blocking conditions and room temperature conditions.
또한, 상기 실시예 1을 통해 제조된 변색성 화장품용기 스포이트에 자외선(315nm)을 1분 동안 조사한 후에 외관을 촬영하여 아래 도 2에 나타내었으며, 상기 실시예 1을 통해 제조된 변색성 화장품용기 스포이트를 38℃의 온도로 가열한 후에 외관을 촬영하여 아래 도 3에 나타내었다.In addition, after irradiating ultraviolet (315nm) for 1 minute to the color-changeable cosmetic container dropper prepared in Example 1, the appearance was photographed and shown in FIG. 2 below, and the color-changeable cosmetic container dropper prepared in Example 1 After heating to a temperature of 38 ℃ was photographed the appearance is shown in Figure 3 below.
아래 도 2 내지 3에 나타낸 것처럼, 본 발명의 실시예 1을 통해 제조된 변색성 화장품용기 스포이트는 자외선에 노출되거나 35℃ 이상의 온도로 가열되면 갈색으로 변색되는 것을 알 수 있다.As shown in FIGS. 2-3 below, it can be seen that the color-changeable cosmetic container dropper prepared in Example 1 of the present invention turns brown when exposed to ultraviolet rays or heated to a temperature of 35° C. or higher.
따라서, 본 발명에 따른 변색성 화장품용기 스포이트용 조성물은 자외선에 노출되는 경우 스포이트가 변색되어 자외선 차단효과를 나타내기 때문에 화장품 성분의 변질을 억제하고, 고온에 노출되는 경우 사용자가 인식할 수 있도록 하여 화장품의 관리를 용이하게 하는 변색성 화장품용기 스포이트를 제공한다.Therefore, the composition for a color-changeable cosmetic container dropper according to the present invention suppresses deterioration of cosmetic ingredients because the dropper is discolored and exhibits a UV-blocking effect when exposed to ultraviolet rays, and when exposed to high temperature, the user can recognize it. Provided is a color-changing cosmetic container dropper that facilitates the management of cosmetics.
Claims (8)
상기 가역성 광변색안료는 흑색 광변색안료 100 중량부 및 황색 광변색안료 50 내지 150 중량부로 이루어지며, 자외선이 조사되면 갈색으로 변색되고,
상기 가역성 감온변색안료는 35℃ 이상의 온도에서 갈색으로 변색되는 것을 특징으로 하는 변색성 화장품용기 스포이트용 조성물.60 to 90% by weight of glass or transparent synthetic resin, 5 to 20% by weight of a reversible photochromic pigment, and 5 to 20% by weight of a reversible thermochromic pigment,
The reversible photochromic pigment consists of 100 parts by weight of a black photochromic pigment and 50 to 150 parts by weight of a yellow photochromic pigment, and is discolored to brown when irradiated with ultraviolet rays,
The reversible thermochromic pigment is a color-changeable cosmetic container dropper composition, characterized in that it is discolored to brown at a temperature of 35° C. or higher.