KR102371764B1 - Eco-friendly snow composition for deicer and manufacturing method thereof - Google Patents
Eco-friendly snow composition for deicer and manufacturing method thereof Download PDFInfo
- Publication number
- KR102371764B1 KR102371764B1 KR1020190024686A KR20190024686A KR102371764B1 KR 102371764 B1 KR102371764 B1 KR 102371764B1 KR 1020190024686 A KR1020190024686 A KR 1020190024686A KR 20190024686 A KR20190024686 A KR 20190024686A KR 102371764 B1 KR102371764 B1 KR 102371764B1
- Authority
- KR
- South Korea
- Prior art keywords
- calcium chloride
- eco
- coating
- liquid additive
- chloride
- Prior art date
Abstract
본 발명은 재결빙 방지 기능이 강화된 친환경 제설제 및 그 제조방법에 관한 것으로, 더욱 상세하게는 염화칼슘, 소금 중 선택되는 1종 이상의 염화물과, 액상 첨가제를 포함하되, 상기 액상 첨가제는 융빙보조제와 부식방지제가 혼합된 것이고, 상기 융빙보조제는 유기산염 수용액이며, 상기 부식방지제는 인산나트륨, 구연산나트륨 또는 이들의 혼합물인 것임을 특징으로 한다. 본 발명에 따른 친환경 제설제 조성물에 의하면, 친환경적이면서도 저온 환경에서의 융빙 성능이 염화칼슘보다 우수하며, 재결빙 현상이 없어 지속성이 우수할 뿐 아니라, 제조비용 역시 낮아 친환경 제설제로서 상용화가 가능하다는 장점이 있다. The present invention relates to an eco-friendly snow remover with enhanced re-freezing prevention function and a method for manufacturing the same, and more particularly, it includes at least one chloride selected from calcium chloride and salt, and a liquid additive, wherein the liquid additive includes an ice melting aid and It is characterized in that the corrosion inhibitor is mixed, the ice melting aid is an organic acid salt aqueous solution, and the corrosion inhibitor is sodium phosphate, sodium citrate, or a mixture thereof. According to the eco-friendly snow remover composition according to the present invention, it is environmentally friendly and has superior ice melting performance in a low temperature environment than calcium chloride, has excellent durability due to no re-freezing phenomenon, and has low manufacturing cost, enabling commercialization as an eco-friendly snow removing agent. There is this.
Description
본 발명은 재결빙 방지 기능이 강화된 친환경 제설제 및 그 제조방법에 관한 것으로, 더욱 상세하게는 제설제용 염화물과 융빙보조제와 부식방지제가 혼합된 액상의 첨가제를 포함하는 재결빙 방지 기능이 강화된 친환경 제설제 및 그 제조방법에 관한 것이다. The present invention relates to an eco-friendly snow remover with enhanced anti-reicing function and a method for manufacturing the same, and more particularly, to an eco-friendly snow remover having a reinforced anti-reicing function and a liquid additive in which a chloride for a snow-removing agent, an ice melting aid, and a corrosion inhibitor are mixed. It relates to an eco-friendly snow removal agent and a manufacturing method thereof.
최근 들어 전 세계의 기상 이변 등으로 인하여 동절기에 폭설이 우리나라는 물론 전 세계적으로 빈번하게 발생하고 있으며, 그에 따라 도로에 사용되는 제설제의 사용량도 급증하고 있다.In recent years, heavy snowfall has occurred not only in Korea but also around the world during winter due to extreme weather conditions around the world, and accordingly, the amount of snow removal agent used on roads is also increasing rapidly.
현재 국내에서 사용하고 있는 제설제는 가격이 저렴한 염화칼슘(CaCl2)이나 염화나트륨(NaCl), 염화마그네슘(MgCl2)가 대표적이다. The deicing agents currently used in Korea are cheap calcium chloride (CaCl 2 ), sodium chloride (NaCl), and magnesium chloride (MgCl 2 ).
상기 염화칼슘, 염화나트륨, 염화마그네슘은 융빙 성능이 우수하면서도 가격이 저렴한 염화물계 제설제로 식품첨가제로 사용되기도 하는 저독성의 물질이다. 하지만, 이들 염화물계 제설제의 지나친 사용은 차량부식 및 도로 포트홀 그리고 식물성장 저해라는 심각한 환경문제를 일으키고 있다. The calcium chloride, sodium chloride, and magnesium chloride are low-toxic substances that are also used as food additives as chloride-based snow removal agents that have excellent ice melting performance and are inexpensive. However, excessive use of these chloride-based snow removal agents causes serious environmental problems such as vehicle corrosion, road potholes, and inhibition of plant growth.
더욱이, 염화칼슘 제설제는 초기 융빙 성능은 아주 우수한 반면에, 살포 후 대략 30분이 지나면 염화칼슘이 눈과 얼음을 급속히 녹이면서 생기는 염화칼슘 수용액의 농도가 점차 묽어짐으로써, 그 수용액이 다시 얼어붙는 재결빙 현상이 일어나서 융빙 성능이 급속히 저하되는 단점이 있다.Moreover, while calcium chloride snow remover has very good initial ice melting performance, approximately 30 minutes after spraying, calcium chloride rapidly melts snow and ice, and the concentration of calcium chloride aqueous solution gradually becomes thinner, and the aqueous solution freezes again. This has a disadvantage in that the ice melting performance is rapidly deteriorated.
한편, 대한민국 환경부에서는 2008년부터 친환경제설제 인증제도(EL.610)를 만들어 지방자치단체의 친환경 제설제 사용을 적극적으로 독려하고 있지만 대부분은 기존 제설제 중에 초기 융빙 성능이 가장 우수한 염화칼슘보다 저조한 융빙 성능을 이유로 친환경 제설제의 사용을 꺼리고 있는 실정이다. Meanwhile, the Ministry of Environment of the Republic of Korea has been actively encouraging local governments to use eco-friendly snow removal agents by creating an eco-friendly snow removal agent certification system (EL.610) since 2008, but most of the existing ice removal agents have lower initial ice melting performance than calcium chloride Due to performance reasons, they are reluctant to use eco-friendly snow removers.
기존 친환경 제설제의 종류로는 구성 성분에 따라 염화물계, 비염화물계, 하이브리드계와 같이 3가지로 분류할 수 있다. 염화물계는 염화물 원료(소금, 염화칼슘, 염화마그네슘)에, 비염화물계는 유무기염 원료(초산염, 탄산염 등)에, 하이브리드계는 염화물과 유무기염의 혼합 원료에 각각 3~5중량%의 부식방지제를 첨가한 형태의 제품들을 말한다. 이 중 가장 많이 사용되는 것은 염화물계 친환경 제설제이다.Existing eco-friendly snow removal agents can be classified into three types: chloride, non-chloride, and hybrid depending on the composition. In the case of chloride, in the raw material of chloride (salt, calcium chloride, magnesium chloride), in the case of non-chloride, in the raw material of organic/inorganic salt (acetate, carbonate, etc.), and in the hybrid system in the mixed raw material of chloride and organic-inorganic salt, 3-5% by weight of each corrosion inhibitor It refers to products in the form of added Among them, the most used is a chloride-based eco-friendly snow removal agent.
상기 염화물계 친환경 제설제는 제조방법에 따라 단순 혼합형과 일체형 그리고 코팅형의 세 가지로 구분된다. 단순 혼합형은 소금(순도 85%이상), 염화칼슘 편상 또는 입상(순도 74%이상), 염화마그네슘 편상(순도 46%이상) 중 전부 또는 일부(95~97%)와 입상형태의 부식방지제(3~5%)를 혼합기(믹서)로 골고루 혼합한 형태이고, 일체형은 소금 분말(순도 85%이상), 염화칼슘 분말(순도 74%이상), 염화마그네슘 분말(순도 46%이상) 중 전부 또는 일부(95~97%)와 분말 형태의 부식방지제(3~5%)를 믹서기로 골고루 혼합 후 펠렛 기계에서 입상(求) 모양으로 성형한 형태이며, 코팅형은 편상의 염화마그네슘과 소금 혼합물에 액상의 부식첨가제를 코팅한 형태이다.The chloride-based eco-friendly snow remover is divided into three types: a simple mixed type, an integrated type, and a coating type according to a manufacturing method. Simple mixed type includes all or part (95-97%) of salt (purity 85% or more), calcium chloride flakes or granules (purity 74% or more), magnesium chloride flakes (purity 46% or more), and granular corrosion inhibitors (3~ 5%) is mixed evenly with a mixer (mixer), and all or part (95) of salt powder (purity 85% or more), calcium chloride powder (purity 74% or more), magnesium chloride powder (purity 46% or more) ~97%) and powder corrosion inhibitor (3~5%) are mixed evenly with a mixer and then molded in a granular shape in a pellet machine. It is a form coated with additives.
이 중 단순 혼합형은 부식방지제의 균질화가 어려우며 혼합공정 중 분진이 많이 생기는 문제점이 있고, 일체형은 부식방지제의 균질화는 쉬우나 제조방법이 복잡하며 성형된 입상이 쉽게 부서져서 분말화 되는 문제점이 있고, 코팅형은 액상의 부식첨가제가 건조되지 않고 제설제 표면에 습식 상태로 남아 있어 융빙 성능이 저하되는 단점이 있다. Among these, the simple mixing type has a problem in that it is difficult to homogenize the corrosion inhibitor and generates a lot of dust during the mixing process. Since the liquid corrosion additive is not dried and remains in a wet state on the surface of the snow removal agent, there is a disadvantage in that the ice melting performance is deteriorated.
따라서, 기존 제조방법의 단점들을 보완한 새로운 형태의 친환경 제설제로서 기존 염화칼슘 제설제보다 우수한 융빙 성능을 지닌 새로운 형태의 친환경 제설제 제조방법이 필요하게 되었다.Therefore, there is a need for a new type of environmentally friendly snow removal method that has better ice melting performance than the existing calcium chloride snow removal agent as a new type of environmentally friendly snow removal agent that compensates for the disadvantages of the existing manufacturing method.
이러한 친환경 제설제의 선행문헌으로는 대한민국 등록특허 제10-1537338호 및 대한민국 등록특허 제10-1514676호가 있다.Prior literature on such an eco-friendly snow removal agent includes Korean Patent Registration No. 10-1537338 and Korean Patent Registration No. 10-1514676.
먼저, 대한민국 등록특허 제10-1537338호는, 친환경 및 저부식성 제설제의 제조에 있어서, 염화칼슘과 복합 금속산화물(산화칼슘, 산화마그네슘, 산화알루미늄)의 혼합물을 프로필렌글리콜로 코팅한 후 탄산칼슘과 규산나트륨을 혼합하여 제조하는 방법을 개시하고 있다. 그러나 고가의 원료인 프로필렌글리콜을 전체 중량의 8~15%만큼 사용하는 기술로 경제성이 전혀 없었다. First, Korean Patent Registration No. 10-1537338 discloses, in the manufacture of an eco-friendly and low-corrosion snow remover, a mixture of calcium chloride and a complex metal oxide (calcium oxide, magnesium oxide, aluminum oxide) is coated with propylene glycol and then calcium carbonate and Disclosed is a method for preparing by mixing sodium silicate. However, the technology using propylene glycol, an expensive raw material, as much as 8 to 15% of the total weight, was not economical at all.
또한, 대한민국 등록특허 제10-1514676호는 친환경 및 저부식성 제설제의 제조에 있어서, 염화물인 염화마그네슘과 소금의 혼합물에 액상의 첨가제를 코팅하여 제조하는 방법을 개시하고 있다. 그러나 코팅된 제설제가 건식이 아닌 습식 상태로 남아 있어서 기존 염화칼슘 제설제보다 융빙 성능이 떨어지는 단점이 있었다.In addition, Korean Patent Registration No. 10-1514676 discloses a method for manufacturing an eco-friendly and low-corrosion snow removal agent by coating a liquid additive on a mixture of magnesium chloride and salt, which is a chloride. However, there was a disadvantage that the ice-melting performance was inferior to that of the existing calcium chloride deicing agent because the coated deicing agent remained wet rather than dry.
따라서, 본 발명은 상기한 종래의 친환경 제설제가 지닌 재결빙 현상으로 인한 융빙 성능 저하, 수질 및 토양 오염, 생태독성, 콘크리트 부식 및 강재 부식의 문제점을 해소하기 위한 것으로, 친환경적이면서도 저온 환경에서의 융빙 성능이 염화칼슘보다 우수한 친환경의 제설제를 제공하는 데 그 목적이 있다.Accordingly, the present invention is to solve the problems of deterioration of ice melting performance, water and soil pollution, ecotoxicity, concrete corrosion and steel corrosion due to the re-icing phenomenon of the conventional eco-friendly snow removal agent, and is environmentally friendly and ice melting in a low temperature environment The purpose is to provide an eco-friendly snow remover that has better performance than calcium chloride.
또한, 제조비용이 낮고, 저장성 및 취급성이 우수한 친환경 제설제를 제공하는 데 있다. Another object of the present invention is to provide an eco-friendly snow removal agent having a low manufacturing cost and excellent storability and handling properties.
상기한 목적을 달성하기 위한 본 발명에 따른 친환경 제설제는, 염화칼슘, 소금 중 선택되는 1종 이상의 염화물과, 액상 첨가제를 포함하되, 상기 액상 첨가제는 융빙보조제와 부식방지제가 혼합된 것이고, 상기 융빙보조제는 유기산염 수용액이며, 상기 부식방지제는 인산나트륨, 구연산나트륨 또는 이들의 혼합물인 것을 특징으로 한다.The eco-friendly snow removal agent according to the present invention for achieving the above object includes at least one chloride selected from calcium chloride and salt, and a liquid additive, wherein the liquid additive is a mixture of an ice melting aid and a corrosion inhibitor, and the ice melting agent The auxiliary agent is an aqueous organic acid salt solution, and the corrosion inhibitor is sodium phosphate, sodium citrate, or a mixture thereof.
상기 염화물은 입상 또는 편상 형태의 염화칼슘 및 소금이고, 상기 염화물이 상기 액상 첨가제에 의해 1차 코팅된 것으로, 고상인 것을 특징으로 한다.The chloride is calcium chloride and salt in granular or flake form, and the chloride is first coated with the liquid additive, characterized in that it is in a solid state.
상기 1차 코팅된 염화물은 염화칼슘 분말에 의한 2차 코팅층이 추가로 형성된 것임을 특징으로 한다.The first coated chloride is characterized in that the secondary coating layer is additionally formed by calcium chloride powder.
상기 염화물은 염화칼슘이고, 물을 더 포함함으로써 액상인 것을 특징으로 한다.The chloride is calcium chloride, characterized in that the liquid by further including water.
그리고 그 제조방법은, 염화칼슘과 소금에 액상 첨가제를 분사하여 1차 코팅하는 단계와, 상기 1차 코팅된 코팅물을 혼합기에 투입하여 액상 첨가제의 코팅을 균질화하는 단계를 포함하며, 상기 액상 첨가제는 융빙보조제와 부식방지제가 혼합된 것이고, 상기 융빙보조제는 유기산염 수용액이고, 상기 부식방지제는 인산나트륨, 구연산나트륨 또는 이들의 혼합물인 것을 특징으로 한다. And the manufacturing method comprises the steps of spraying a liquid additive on calcium chloride and salt to perform a primary coating, and injecting the primary coated coating material into a mixer to homogenize the coating of the liquid additive, wherein the liquid additive is It is characterized in that the ice melting aid and the corrosion inhibitor are mixed, the ice melting aid is an aqueous organic acid salt solution, and the corrosion inhibitor is sodium phosphate, sodium citrate, or a mixture thereof.
상기 1차 코팅 단계 전, 상기 염화칼슘을 선별하는 단계를 더 포함하되, 편상 또는 입상 형태의 염화칼슘 2수화물을 선별기로 입자 크기가 2mm 이상인 입자를 선별하는 것이고, 상기 균질화하는 단계 후, 상기 균질화된 1차 코팅물에 상기 선별 단계 시 선별되고 남은 입자 크기가 2mm 미만인 염화칼슘 분말을 투입하여 2차 코팅하는 단계를 더 포함하는 것을 특징으로 한다.Before the first coating step, further comprising the step of screening the calcium chloride, to screening the particles having a particle size of 2 mm or more with a separator in a flake or granular form of calcium chloride dihydrate, and after the homogenizing step, the homogenized 1 It is characterized in that it further comprises the step of secondary coating by adding calcium chloride powder having a particle size of less than 2 mm left after being screened during the screening step to the tea coating material.
본 발명에 따른 친환경 제설제 조성물에 의하면, 친환경적이면서도 저온 환경에서의 융빙 성능이 염화칼슘보다 우수하며, 재결빙 현상이 없어 지속성이 우수할 뿐 아니라, 제조비용 역시 낮아 친환경 제설제로서 상용화가 가능하다는 장점이 있다. According to the eco-friendly snow remover composition according to the present invention, it is environmentally friendly and has superior ice melting performance in a low temperature environment than calcium chloride, has excellent durability due to no re-freezing phenomenon, and has low manufacturing cost, enabling commercialization as an eco-friendly snow removing agent. There is this.
도 1은 본 발명에 의한 친환경 제설제의 제조 공정도.1 is a manufacturing process diagram of an eco-friendly snow removal agent according to the present invention.
이하, 본 발명을 상세히 설명한다. Hereinafter, the present invention will be described in detail.
종래, 친환경 제설제들은 그 제조비용이 높아 상용화가 어렵거나, 융빙 성능이 염화칼슘보다 좋지 못해 상용화가 어려운 단점이 있었다. Conventionally, eco-friendly snow removal agents have disadvantages in that it is difficult to commercialize them due to their high manufacturing cost, or because their ice melting performance is not better than that of calcium chloride.
본 발명은 이러한 종래의 제설제가 갖는 문제를 해소하기 위한 것으로, 가장 특징적으로 염화칼슘과 소금 중 1종 이상을 포함하는 염화물과, 융빙보조제와 부식방지제가 혼합된 액상 첨가제를 포함함으로써, 부식 및 재결빙을 방지하여 친환경성 및 낮은 제조비용을 갖도록 하는 것이다.The present invention is to solve the problem of the conventional deicing agent, and most characteristically, by including a liquid additive in which a chloride containing at least one of calcium chloride and salt, an ice melting aid and a corrosion inhibitor are mixed, corrosion and re-freezing This is to have eco-friendliness and low manufacturing cost.
이러한 본 발명에 따른 친환경 제설제는, 염화칼슘, 소금 중 선택되는 1종 이상의 염화물과, 액상 첨가제를 포함하되, 상기 액상 첨가제는 융빙보조제와 부식방지제가 혼합된 것이고, 상기 융빙보조제는 유기산염 수용액이며, 상기 부식방지제는 인산나트륨, 구연산나트륨 또는 이들의 혼합물인 것을 특징으로 한다.The eco-friendly snow remover according to the present invention includes at least one chloride selected from calcium chloride and salt, and a liquid additive, wherein the liquid additive is a mixture of an ice melting aid and a corrosion inhibitor, and the ice melting aid is an aqueous solution of an organic acid salt. , The corrosion inhibitor is characterized in that sodium phosphate, sodium citrate or a mixture thereof.
먼저, 상기 염화물은 통상 제설제로서 사용되는 것으로, 염화칼슘, 소금 중 1종 이상을 선택하여 사용할 수 있다.First, the chloride is usually used as a snow remover, and one or more of calcium chloride and salt may be selected and used.
상기 염화칼슘(CaCl)은, 공기 중 수분을 흡수하는 조해성이 강한 성질을 갖고 있으며, 공용점이 매우 낮아 물의 어는점을 낮추는 역할을 한다. 그리고 물과의 용해시 발열반응을 하므로 저온에서 눈과 얼음을 잘 녹이는 특징을 가지고 있다. 즉, 눈과 얼음이 덮여있는 노면에 염화칼슘을 뿌리면 염화칼슘은 주위 수분을 흡수하여 녹기 시작하며, 녹는 과정에서 발열하고, 발열로 인해 융빙이 촉진되므로 더 많은 양의 눈과 얼음을 녹이고 용해된다. 그리고 상기 녹은 수용액의 어는 점을 최고 -51℃ 이하로 낮추게 되어 우수한 융빙성능을 발휘하는 것이다. The calcium chloride (CaCl) has a strong property of absorbing moisture in the air, and has a very low common point and serves to lower the freezing point of water. In addition, it has an exothermic reaction when dissolved with water, so it has the characteristic of melting snow and ice well at low temperatures. That is, when calcium chloride is sprayed on the road surface covered with snow and ice, calcium chloride absorbs the surrounding moisture and begins to melt, and generates heat during the melting process, and the heat promotes melting of snow and ice. And the freezing point of the molten aqueous solution is lowered to -51° C. or less at the maximum, thereby exhibiting excellent ice melting performance.
상기 소금(NaCl)은 제설용으로 사용 가능한 천일염을 주로 지칭하는 것으로, 본 발명에서는 산업용 염화나트륨을 사용한다. 더욱 구체적으로는 산업용 염화나트륨으로서 수분함량이 10% 미만인 것을 사용한다. The salt (NaCl) mainly refers to sea salt that can be used for snow removal, and industrial sodium chloride is used in the present invention. More specifically, as industrial sodium chloride, a water content of less than 10% is used.
상기 염화나트륨은 물에 용해되어 어는점을 -21℃까지 강하시킴으로써, 눈을 녹이고 결빙을 방해하는 융빙제의 역할을 장시간 수행한다. 그리고 상기 염화나트륨은 염화칼슘에 비해 포화용해도가 약 15배이기 때문에 염화칼슘보다 더 효율적인바, 본 발명에서는 상기 염화칼슘과 소금을 함께 사용하는 것이다. The sodium chloride dissolves in water and lowers the freezing point to -21° C., thereby dissolving snow and preventing freezing for a long time. And since the sodium chloride has a saturated solubility of about 15 times that of calcium chloride, it is more efficient than calcium chloride. In the present invention, the calcium chloride and salt are used together.
그리고 상기 액상 첨가제는 융빙보조제와 부식방지제가 1:0.5~1.5 중량비로 혼합된 것으로, 부식 및 재결빙을 방지하는 역할을 한다. 이때, 상기 융빙보조제로는 고가의 프로필렌글리콜이나 글리세린을 사용하는 것이 아닌, 산업 부산물인 유기산염 수용액을 사용하는 것이다. 상기 유기산염 수용액으로는 초산염, 프로피오산염 및 젖산염 중 어느 하나의 수용액, 더욱 바람직하게는 초산염, 프로피오산염 및 젖산염의 혼합물 3~20중량%와 물 80~97중량%를 혼합한 것을 사용할 수 있다. 이때, 상기 초산염, 프로피오산염 및 젖산염의 혼합비는 제한하지 않으나, 1:0.5~1.5:0.5~1.5 중량비 정도일 수 있다.In addition, the liquid additive is a mixture of an ice melting aid and a corrosion inhibitor in a weight ratio of 1:0.5 to 1.5, and serves to prevent corrosion and re-freezing. In this case, as the ice melting aid, an aqueous solution of an organic acid salt, an industrial by-product, is used rather than expensive propylene glycol or glycerin. As the aqueous organic acid salt solution, an aqueous solution of any one of acetate, propioate and lactate, more preferably a mixture of 3 to 20% by weight of a mixture of acetate, propioate and lactate and 80 to 97% by weight of water may be used. there is. In this case, the mixing ratio of the acetate, propioate and lactate is not limited, but may be about 1:0.5 to 1.5:0.5 to 1.5 by weight.
그리고 상기 부식방지제로는 인산나트륨, 구연산나트륨 또는 이들의 혼합물을 사용할 수 있다.And as the corrosion inhibitor, sodium phosphate, sodium citrate, or a mixture thereof may be used.
즉, 상기 액상 첨가제는 상기 유기산염 수용액에 부식방지제인 인산나트륨, 구연산나트륨 또는 이들의 혼합물을 용해시켜 제조되는 것으로, 친환경 제설제의 제조비용을 낮춰주는 것은 물론, 우수한 융빙 성능을 발휘할 수 있게 해주는 것이다.That is, the liquid additive is prepared by dissolving sodium phosphate, sodium citrate, or a mixture thereof, which are corrosion inhibitors, in the aqueous solution of the organic acid salt. will be.
그리고 본 발명의 친환경 제설제는 고상 또는 액상의 형태로 제공될 수 있는데, 고상의 친환경 제설제는 상기 염화물에 상기 액상 첨가제가 1차 코팅된 형태임이 바람직하다. 그리고 상기 염화물로는 입상 또는 편상의 염화칼슘과 소금의 2종을 사용함이 바람직하다.And the eco-friendly snow remover of the present invention may be provided in a solid or liquid form, and the solid eco-friendly snow remover is preferably in a form in which the liquid additive is first coated on the chloride. And as the chloride, it is preferable to use two kinds of granular or flaky calcium chloride and salt.
또한, 필요에 따라 염화칼슘 분말로 상기 액상 첨가제가 코팅된 염화물이 2차 코팅된 상태, 즉 2차 코팅층이 염화칼슘 분말에 의해 형성된 것일 수도 있다. 이러한 코팅층의 형성방법은 하기의 제조방법을 통해 더욱 상세히 설명한다. In addition, if necessary, the chloride coated with the liquid additive with calcium chloride powder may be in a secondary coating state, that is, the secondary coating layer may be formed by calcium chloride powder. A method of forming such a coating layer will be described in more detail through the following manufacturing method.
이때, 상기 고상의 친환경 제설제는 상기 입상 또는 편상의 염화칼슘 48.5~70중량%, 소금 29~50중량% 및 액상 첨가제 1~1.5중량%를 포함하여 상기 액상 첨가제가 코팅된 염화물이 구성되고, 이에 다시 염화칼슘 분말이 2차 코팅되는 것인바, 상기 2차 코팅되는 염화칼슘 분말의 사용량은 제한하지 않는다. At this time, the solid eco-friendly snow removal agent comprises 48.5 to 70% by weight of the granular or flaky calcium chloride, 29 to 50% by weight of salt, and 1 to 1.5% by weight of the liquid additive, the chloride coated with the liquid additive, Again, since the calcium chloride powder is to be secondary coated, the amount of calcium chloride powder to be secondary coated is not limited.
그리고 액상의 친환경 제설제는, 염화물 30~40중량%, 상기 액상 첨가제 1~1.5중량% 및 잔량의 물을 포함하되, 상기 염화물로서 염화칼슘을 단독으로 사용함이 바람직하다.And the liquid eco-friendly snow remover includes 30 to 40% by weight of chloride, 1 to 1.5% by weight of the liquid additive, and the remaining amount of water, but it is preferable to use calcium chloride alone as the chloride.
상기 본 발명에 의한 액상의 친환경 제설제는, 물에 염화물 및 액상 첨가제를 배합비에 따라 혼합하여 제조된다.The liquid eco-friendly snow remover according to the present invention is prepared by mixing a chloride and a liquid additive in water according to the mixing ratio.
그리고 본 발명에 의한 고상의 친환경 제설제는, 염화칼슘, 소금 및 이들의 혼합물 중 어느 하나인 염화물에 액상 첨가제를 분사하여 1차 코팅하는 단계와, 상기 1차 코팅된 코팅물을 혼합기에 투입하여 액상 첨가제의 코팅을 균질화하는 단계를 포함하여 제조된다. 여기서, 상기 염화물로는 바람직하게 염화칼슘과 소금을 사용하는 것이다. And the solid eco-friendly snow removal agent according to the present invention comprises the steps of spraying a liquid additive on chloride, which is any one of calcium chloride, salt, and a mixture thereof, for primary coating; and homogenizing the coating of the additive. Here, as the chloride, calcium chloride and salt are preferably used.
또한, 상기 1차 코팅 단계 전, 상기 염화물 중 염화칼슘을 선별하는 단계를 더 포함할 수 있다.In addition, before the first coating step, the step of selecting calcium chloride from the chloride may be further included.
또한, 상기 균질화하는 단계 후, 상기 균질화된 1차 코팅물을 2차 코팅하는 단계를 더 포함할 수 있다. In addition, after the homogenizing step, the second coating step of the homogenized primary coating may be further included.
이하, 본 발명에 따른 고상 친환경 제설제의 제조방법에 대하여, 첨부된 도 1을 참조하여 단계별로 상세히 설명한다. Hereinafter, with respect to the manufacturing method of the solid eco-friendly snow removal agent according to the present invention, with reference to the accompanying Figure 1 will be described in detail step by step.
염화칼슘을 선별하는 단계.Selecting calcium chloride.
먼저, 편상 또는 입상 형태의 염화칼슘 2수화물을 준비한다. 그리고 상기 준비된 염화칼슘의 2수화물을 입자 선별기로 입자 크기가 2mm 이상인 입자, 더욱 바람직하게는 2~10mm인 입자를 선별한다. First, calcium chloride dihydrate in flake or granular form is prepared. And the prepared dihydrate of calcium chloride is used to sort particles having a particle size of 2 mm or more, more preferably particles having a particle size of 2 to 10 mm.
본 발명에서 상기 염화칼슘의 입자 크기를 선별하는 이유는 후 단계인 액상 첨가제의 코팅시 입자의 크기가 작을 경우 액상 첨가제로의 코팅이 어려울 뿐 아니라, 취급성 및 저장 안정성 역시 저하되기 때문이나, 이를 반드시 제한하는 것은 아니다.The reason for selecting the particle size of the calcium chloride in the present invention is that, when the particle size is small during coating of the liquid additive, which is a later step, it is difficult to coat with the liquid additive, and handleability and storage stability are also reduced. It is not limiting.
상기 선별된 염화칼슘과 소금에 액상 첨가제를 분사하여 1차 코팅하는 단계.First coating by spraying a liquid additive on the selected calcium chloride and salt.
다음으로, 상기 선별된 염화칼슘과 함께 제설제로서 사용할 소금, 건조된 것을 준비한다.Next, prepare salt to be used as a snow remover together with the selected calcium chloride, and dried.
그리고 상기 선별된 염화칼슘과 상기 소금을 낙하시키면서, 상기 낙하되는 염화칼슘과 소금에 액상 첨가제를 분사하여 1차 코팅한다. And while the selected calcium chloride and the salt are dropped, a liquid additive is sprayed on the falling calcium chloride and the salt to perform a primary coating.
여기서, 상기 액상 첨가제는 앞서 설명된 바와 같이, 융빙보조제와 부식방지제가 1:0.5~1.5 중량비로 혼합된 것으로, 부식 및 재결빙을 방지하는 역할을 한다. Here, as described above, the liquid additive is a mixture of an ice melting aid and a corrosion inhibitor in a weight ratio of 1:0.5 to 1.5, and serves to prevent corrosion and re-freezing.
한편, 상기 선별된 염화칼슘, 소금 및 액상 첨가제의 사용량은, 상기 염화칼슘 48.5~70중량%, 소금 29~50중량% 및 액상 첨가제 1~1.5중량%임이 바람직한바, 이는 융빙 성능 및 친환경성을 고려한 것이다. On the other hand, the amount of the selected calcium chloride, salt and liquid additive used is preferably 48.5 to 70% by weight of calcium chloride, 29 to 50% by weight of salt, and 1 to 1.5% by weight of liquid additive, which is in consideration of ice melting performance and eco-friendliness .
상기 1차 코팅된 코팅물을 혼합기에 투입하여 액상 첨가제의 코팅을 균질화 하는 단계. Homogenizing the coating of the liquid additive by putting the first coated coating material in a mixer.
상기 1차 코팅이 완료되면 그 코팅물을 혼합기, 예시적으로 리본 믹서로 투입하여 혼합과 동시에 이동시키면서 5~30분간 액상 첨가제의 코팅을 균질화한다. When the first coating is completed, the coating material is put into a mixer, for example, a ribbon mixer, and the coating of the liquid additive is homogenized for 5 to 30 minutes while mixing and moving at the same time.
상기 remind 균질화된homogenized 1차 Primary 코팅물을coating 2차 코팅하는 단계. Second coating step.
추가적으로, 상기 균질화된 1차 코팅물을 상기 선별 단계 시 선별되고 남은 입자 크기가 2mm 미만인 염화칼슘 분말로 2차 코팅할 수 있다. 이는 추가 코팅을 통해 제설제의 초기 융빙 성능을 높이는 것은 물론, 상기 액상 첨가제로 코팅된 1차 코팅물이 습식 상태로 남아있는 것을 방지하기 위함이다.Additionally, the homogenized primary coating may be secondarily coated with calcium chloride powder having a particle size of less than 2 mm remaining after being screened during the screening step. This is to increase the initial ice melting performance of the snow remover through additional coating, as well as to prevent the primary coating coated with the liquid additive from remaining in a wet state.
상기 2차 코팅은 상기 혼합기, 즉 리본 믹서 내 상기 염화칼슘 분말을 더 투입하여 혼합함으로써, 상기 액상 첨가제로 코팅된 염화칼슘 및 소금의 표면에 염화칼슘 분말이 코팅될 수 있도록 하는 정도면 족하다. The secondary coating is sufficient to allow the calcium chloride powder to be coated on the surface of the calcium chloride and salt coated with the liquid additive by further adding and mixing the calcium chloride powder in the mixer, that is, the ribbon mixer.
여기서, 상기 추가 투입되는 염화칼슘 분말의 사용량은 제한하지 않는 것으로, 선별 후 남은 양을 사용하면 족하다. Here, the amount of the additionally added calcium chloride powder is not limited, and it is sufficient to use the remaining amount after screening.
본 발명에 의한 친환경 제설제는 앞서 설명된 바와 같이, 액상 또는 고상의 형태로 제공가능하며, 재결빙 현상으로 인한 융빙 성능 저하, 수질 및 토양 오염, 생태독성, 콘크리트 부식 및 강재 부식의 문제점이 없으며, 제조비용이 낮아 상용화가 가능하다는 특징이 있다.As described above, the eco-friendly snow remover according to the present invention can be provided in liquid or solid form, and there is no problem of deterioration of ice melting performance, water and soil pollution, ecotoxicity, concrete corrosion and steel corrosion due to re-freezing phenomenon. , it is characterized by low manufacturing cost and possible commercialization.
이하, 구체적인 실시예를 통해 본 발명을 더욱 상세히 설명한다. Hereinafter, the present invention will be described in more detail through specific examples.
(실시예 1)(Example 1)
염화칼슘 2수화물을 입자 선별기로 선별하여, 입자 크기가 2mm 이상인 입자와 2mm 미만인 입자로 분리하였다. Calcium chloride dihydrate was separated into particles having a particle size of 2 mm or more and particles having a particle size of less than 2 mm by screening with a particle separator.
다음으로, 상기 크기가 2mm 이상인 염화칼슘 2수화물 5kg과 공업용 염화나트륨(함수율이 10% 미만인 것) 4.9kg을 함께 낙하시키면서, 100g의 액상 첨가제를 분무하여 1차 코팅시켰다. 여기서, 상기 액상 첨가제는 초산염, 프로피오산염 및 젖산염을 1:1:1중량비로 혼합한 유기산염 5중량%를 물 95중량%에 혼합하여 유기산염 수용액을 제조하고, 이에 인산나트륨 분말 및 구연산나트륨 분말을 1:1 중량비로 혼합한 부식방지제를 1:1 중량비로 용해시켜 제조하였다. Next, while dropping together 5 kg of calcium chloride dihydrate having a size of 2 mm or more and 4.9 kg of industrial sodium chloride (with a moisture content of less than 10%), 100 g of a liquid additive was sprayed to give a primary coating. Here, the liquid additive is prepared by mixing 5% by weight of an organic acid salt obtained by mixing acetate, propioate and lactate in a 1:1:1 weight ratio with 95% by weight of water to prepare an aqueous organic acid salt solution, and thus sodium phosphate powder and sodium citrate. It was prepared by dissolving the corrosion inhibitor mixed with the powder in a 1:1 weight ratio in a 1:1 weight ratio.
그리고 상기 코팅된 염화칼슘 2수화물과 공업용 염화나트륨을 리본믹서에 투입한 후 10분간 혼합하여 코팅을 균질화시켰다. Then, the coated calcium chloride dihydrate and industrial sodium chloride were put in a ribbon mixer and mixed for 10 minutes to homogenize the coating.
(실시예 2)(Example 2)
실시예 1과 동일하게 실시하되, 상기 균질화시킨 코팅물 10kg을 그대로 리본믹서에 두고, 상기 리본믹서에 선별 시 선별되고 남은 입자 크기가 2mm 미만인 염화칼슘 분말 500g을 투입하여 다시 5분간 혼합함으로써, 2차 코팅시켰다.The same procedure as in Example 1, except that 10 kg of the homogenized coating material is placed in the ribbon mixer as it is, and 500 g of calcium chloride powder having a particle size of less than 2 mm remaining after being screened is added to the ribbon mixer and mixed for another 5 minutes. coated.
(비교예 1)(Comparative Example 1)
염화칼슘 2수화물을 준비하였다.Calcium chloride dihydrate was prepared.
(비교예 2)(Comparative Example 2)
염화마그네슘 6수화물을 준비하였다.Magnesium chloride hexahydrate was prepared.
(비교예 3)(Comparative Example 3)
제설용 염화나트륨을 준비하였다.Sodium chloride for snow removal was prepared.
(시험예 1)(Test Example 1)
유해원소 함량 시험Harmful element content test
상기 실시예 1, 2에서 제조한 제설제에 대한 유해원소 함량 시험을 실시하여 환경친화성 정도를 알아보았다. 시험방법은 ICP분석 시험방법을 이용하여 유해원소 시험을 실시하였다.The degree of environmental friendliness was investigated by conducting a test for the content of harmful elements on the snow removers prepared in Examples 1 and 2 above. As for the test method, a harmful element test was performed using the ICP analysis test method.
그 결과 실시예 1, 2은 모든 항목에서 유해원소가 하기 표 1의 기준치 이하임을 확인하였다.As a result, in Examples 1 and 2, it was confirmed that the harmful elements in all items were below the standard values in Table 1 below.
(시험예 2)(Test Example 2)
융빙성능 시험Ice melting test
영하 3℃, 영하 15℃에서 15분, 30분, 60분 동안의 융빙 성능을 측정하였다. 상기 융빙 성능의 측정은 환경부 친환경 제설제의 시험기준인 EL.610에 따랐다.Ice melting performance was measured for 15 minutes, 30 minutes, and 60 minutes at minus 3°C and minus 15°C. The measurement of the ice melting performance was in accordance with EL.610, a test standard for environment-friendly snow removal agents of the Ministry of Environment.
그리고 그 결과를 하기 표 2에 나타내었다.And the results are shown in Table 2 below.
상기 표 2에서 확인할 수 있는 바와 같이, 상기 실시예 1, 2는 모두 초기 융빙 성능이 우수할 뿐 아니라, 30분 경과 및 60분 경과시에도 초기의 융빙 성능이 그대로 유지됨을 확인할 수 있었다. As can be seen in Table 2, it was confirmed that Examples 1 and 2 both had excellent initial ice melting performance and maintained the initial ice melting performance even after 30 minutes and 60 minutes.
반면, 비교예 1, 2는 모두 초기 융빙 성능은 우수하나, 30분 경과 후에는 급격히 융빙 성능이 저하되는 것을 확인할 수 있었다. 또한, 비교예 3은 융빙성능이 좋지 못함을 확인할 수 있었다.On the other hand, in Comparative Examples 1 and 2, although the initial ice melting performance was excellent, it was confirmed that the ice melting performance rapidly deteriorated after 30 minutes. In addition, it was confirmed that Comparative Example 3 had poor ice melting performance.
(시험예 3)(Test Example 3)
강제부식성 시험Forced Corrosion Test
실시예 1, 2 및 비교예 3의 강제부식성을 평가하였다.The forced corrosion properties of Examples 1 and 2 and Comparative Example 3 were evaluated.
상기 강제부식성의 측정은 환경부 친환경 제설제의 시험기준인 EL.610에 따랐다.The forced corrosion resistance was measured in accordance with EL.610, the test standard for environment-friendly snow removal agents of the Ministry of Environment.
그리고 그 결과를 하기 표 3에 나타내었다.And the results are shown in Table 3 below.
상기 표 3에서 확인할 수 있는 바와 같이, 실시예 1, 2는 모두 부식 손실율이 30% 미만으로 우수함을 확인할 수 있었다. As can be seen in Table 3, in Examples 1 and 2, it was confirmed that the corrosion loss rate was excellent at less than 30%.
본 발명을 바람직한 실시예를 사용하여 상세히 설명하였으나, 본 발명의 범위는 특정 실시예에 한정되는 것은 아니며, 첨부된 특허청구범위에 의하여 해석되어야 할 것이다 또한, 이 기술분야에서 통상의 지식을 습득한 자라면, 본 발명의 범위에서 벗어나지 않으면서도 많은 수정과 변형이 가능함을 이해하여야 할 것이다.Although the present invention has been described in detail using preferred embodiments, the scope of the present invention is not limited to specific embodiments, and should be construed by the appended claims. As it grows, it will be understood that many modifications and variations are possible without departing from the scope of the present invention.
Claims (6)
상기 1차 코팅된 코팅물을 혼합기에 투입하여 액상 첨가제의 코팅을 균질화하는 단계를 포함하며,
상기 액상 첨가제는 융빙보조제와 부식방지제가 1:0.5~1.5 중량비로 혼합된 것이고,
상기 융빙보조제는 유기산염 수용액이며,
상기 부식방지제는 인산나트륨, 구연산나트륨 또는 이들의 혼합물이고,
상기 유기산염 수용액은 초산염, 프로피오산염 및 젖산염의 혼합물 3~20중량%와 물 80~97중량%를 혼합한 것이며,
상기 1차 코팅하는 단계에서, 상기 염화칼슘, 소금 및 액상 첨가제의 사용량은, 염화칼슘 48.5~70중량%, 소금 29~50중량% 및 액상 첨가제 1~1.5중량%인 것을 특징으로 하는 재결빙 방지 기능이 강화된 친환경 제설제의 제조방법.
First coating by spraying liquid additives on calcium chloride and salt;
Including the step of homogenizing the coating of the liquid additive by putting the first coated coating in a mixer,
The liquid additive is a mixture of an ice melting aid and a corrosion inhibitor in a weight ratio of 1:0.5 to 1.5,
The ice melting aid is an aqueous organic acid salt solution,
The corrosion inhibitor is sodium phosphate, sodium citrate or a mixture thereof,
The organic acid salt aqueous solution is a mixture of 3 to 20% by weight of a mixture of acetate, propioate and lactate and 80 to 97% by weight of water,
In the first coating step, the amount of calcium chloride, salt and liquid additive used is 48.5 to 70% by weight of calcium chloride, 29 to 50% by weight of salt and 1 to 1.5% by weight of liquid additive. A method for manufacturing an enhanced eco-friendly snow remover.
상기 1차 코팅 단계 전,
상기 염화칼슘을 선별하는 단계를 더 포함하되,
편상 또는 입상 형태의 염화칼슘 2수화물을 선별기로 입자 크기가 2mm 이상인 입자를 선별하는 것이고,
상기 균질화하는 단계 후,
상기 균질화된 1차 코팅물에 상기 선별 단계 시 선별되고 남은 입자 크기가 2mm 미만인 염화칼슘 분말을 투입하여 2차 코팅하는 단계를 더 포함하는 것을 특징으로 하는 재결빙 방지 기능이 강화된 친환경 제설제의 제조방법.6. The method of claim 5,
Before the first coating step,
Further comprising the step of selecting the calcium chloride,
It is to select particles with a particle size of 2 mm or more by using a flaky or granular form of calcium chloride dihydrate with a separator,
After the homogenizing step,
Manufacture of an eco-friendly snow removal agent with enhanced anti-freezing function, characterized in that it further comprises the step of secondary coating by adding calcium chloride powder having a particle size of less than 2 mm left after being screened during the screening step to the homogenized primary coating material method.