KR102351902B1 - sculpture paste and its manufacturing method - Google Patents

sculpture paste and its manufacturing method Download PDF

Info

Publication number
KR102351902B1
KR102351902B1 KR1020200057242A KR20200057242A KR102351902B1 KR 102351902 B1 KR102351902 B1 KR 102351902B1 KR 1020200057242 A KR1020200057242 A KR 1020200057242A KR 20200057242 A KR20200057242 A KR 20200057242A KR 102351902 B1 KR102351902 B1 KR 102351902B1
Authority
KR
South Korea
Prior art keywords
weight
parts
dough
preparing
mixing
Prior art date
Application number
KR1020200057242A
Other languages
Korean (ko)
Other versions
KR20210139023A (en
Inventor
박수정
Original Assignee
박수정
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박수정 filed Critical 박수정
Priority to KR1020200057242A priority Critical patent/KR102351902B1/en
Publication of KR20210139023A publication Critical patent/KR20210139023A/en
Application granted granted Critical
Publication of KR102351902B1 publication Critical patent/KR102351902B1/en

Abstract

스컬프쳐 페이스트 및 그 제조방법 제공된다. 스컬프쳐 페이스트의 제조방법은, 제1 반죽을 제조하는 단계와, 제2 반죽을 제조하는 단계와, 제1 반죽과 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계와, 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계 및 제4 반죽을 숙성하는 단계를 포함하고, 제1 반죽을 제조하는 단계는, 붕사물을 제조하는 단계와, PVA풀과 정제수를 혼합하여 제1 혼합물을 제조하는 단계와, 제1 혼합물에 소다를 첨가하여 제2 혼합물을 제조하는 단계와, 제2 혼합물에 상기 붕사물을 혼합하는 단계를 포함한다.Sculpture paste and a method for manufacturing the same are provided. The method for manufacturing the sculptural paste includes the steps of preparing a first dough, preparing a second dough, mixing the first dough and a second dough to prepare a third dough, and adding cotton to the third dough Including the steps of preparing a fourth dough by mixing cotton and maturing the fourth dough, the step of preparing the first dough, preparing a borax, and mixing PVA paste and purified water to a first mixture and preparing a second mixture by adding soda to the first mixture, and mixing the borax in the second mixture.

Description

스컬프쳐 페이스트 및 그 제조방법{sculpture paste and its manufacturing method}Sculpture paste and its manufacturing method

본 발명은 스컬프쳐 페이스트 및 그 제조방법에 관한 것으로서, 뛰어난 입체감과 목화솜에 의한 독특한 질감을 표현할 수 있는 스컬프쳐 페이스트 및 그 제조방법에 관한 것이다.The present invention relates to a sculpture paste and a method for manufacturing the same, and to a sculpture paste capable of expressing excellent three-dimensionality and a unique texture by cotton wool and a method for manufacturing the same.

점성을 갖는 재료를 이용하여 꽃과 같은 장식물 또는 조형물을 만드는 공예에 있어서, 점성을 갖는 재료의 점성과 장력을 조절하여 다양한 조형물이 만들어지고 있다. In the craft of making decorations or sculptures such as flowers using viscous materials, various sculptures are being made by adjusting the viscosity and tension of the viscous materials.

최근에는 석고반죽으로 꽃과 같은 장식물 또는 조형물 등을 제작하여 석고공예품이 등장하면서 석고공예가 많은 사람들로부터 큰 인기를 끌고 있다. 이러한 석고공예품의 경우 제작하고자 하는 공예품 모양의 틀을 만들어 묽은 석고반죽을 주입하기도 하고, 굳혀진 석고덩어리를 깎아서 제작하기도 하지만, 진흙처럼 반죽된 석고반죽을 점토공예 하듯이 주물러서 만드는 경우도 있다.In recent years, gypsum crafts are gaining popularity among many people as gypsum crafts have appeared by making decorations or sculptures such as flowers with gypsum dough. In the case of these gypsum crafts, thin gypsum dough is poured into them by making a mold in the shape of the crafts to be produced, and some are made by shaving the hardened gypsum mass.

또한, 석고는 물과 쉽게 반응하여 굳어지는 화학적 특성을 가지고 있다. 가열하면 쉽게 수분을 잃게 되어 반수석고(CaSO4·1/2H20)로 되며, 반대로 분말형태로 된 반수석고(CaSO4·1/2H20)에 물을 첨가하면 물과 반응해서 결정수를 거두어들여 안정된 이수석고(CaSO4·2H20)로 되어 단단한 형태로 된다.In addition, gypsum has a chemical property of being hardened by easily reacting with water. When heated, it loses moisture easily and becomes hemihydrate gypsum (CaSO4·1/2H20). Conversely, when water is added to hemihydrate gypsum (CaSO4·1/2H20) in powder form, it reacts with water and collects crystal water and stabilizes dihydrate gypsum. (CaSO4·2H20) and becomes a hard form.

다만, 이와 같은 석고반죽을 이용한 공예의 경우 반죽의 탄성 및 점성의 한계에 따라 입체감을 나타내기 어렵고, 석고반죽을 이용함에 따라 다양한 질감을 표현하는데 한계가 있다.However, in the case of a craft using such a plaster dough, it is difficult to express a three-dimensional effect due to the limitations of elasticity and viscosity of the dough, and there is a limit in expressing various textures according to the use of the plaster dough.

본 발명이 해결하고자 하는 과제는 뛰어난 입체감과 목화솜에 의한 독특한 질감을 표현할 수 있는 스컬프쳐 페이스트 및 그 제조방법을 제공하는 것에 있다.The problem to be solved by the present invention is to provide a sculpture paste capable of expressing an excellent three-dimensional feeling and a unique texture by cotton wool and a method for manufacturing the same.

본 발명의 과제들은 이상에서 언급한 과제로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems of the present invention are not limited to the problems mentioned above, and other technical problems not mentioned will be clearly understood by those skilled in the art from the following description.

상기 과제를 해결하기 위한 일 실시예에 따른 스컬프쳐 페이스트의 제조방법은, 제1 반죽을 제조하는 단계와, 제2 반죽을 제조하는 단계와, 상기 제1 반죽과 상기 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계와, 상기 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계 및 제4 반죽을 숙성하는 단계를 포함하고, 상기 제1 반죽을 제조하는 단계는, 붕사물을 제조하는 단계와, PVA풀과 정제수를 혼합하여 제1 혼합물을 제조하는 단계와, 상기 제1 혼합물에 소다를 첨가하여 제2 혼합물을 제조하는 단계와, 상기 제2 혼합물에 상기 붕사물을 혼합하는 단계를 포함한다.The method of manufacturing a sculpture paste according to an embodiment for solving the above problems includes the steps of preparing a first dough, preparing a second dough, and mixing the first dough and the second dough to make a 3 comprising the steps of preparing a dough, mixing the third dough with cotton wool to prepare a fourth dough, and aging the fourth dough, and the step of preparing the first dough includes borax Preparing a first mixture by mixing the PVA pool and purified water, adding soda to the first mixture to prepare a second mixture, and mixing the borax in the second mixture includes steps.

상기 제1 반죽은 상기 PVA풀 100중량부에 대하여 상기 정제수 30중량부 내지 40중량부, 상기 소다 2중량부 내지 6중량부, 상기 붕사물 20중량부 내지 30중량부 비율로 혼합될 수 있다.The first dough may be mixed in a ratio of 30 parts by weight to 40 parts by weight of the purified water, 2 parts by weight to 6 parts by weight of the soda, and 20 parts by weight to 30 parts by weight of the borax with respect to 100 parts by weight of the PVA paste.

상기 제2 반죽을 제조하는 단계는, 석회가루와 정제수를 혼합하여 제3 혼합물을 제조하는 단계 및 상기 제3 혼합물에 첨가제를 첨가하는 단계를 포함하고, 상기 제3 혼합물은, 상기 석회가루 100중량부에 대하여 상기 정제수 400중량부 내지 800중량부 비율로 혼합되며, 상기 첨가제는, 접착제와, 기포제거제와, 윤활제 및 중화제를 포함하고, 상기 제2 반죽은 상기 제3 혼합물 100중량부에 대하여 상기 접착제 3중량부 내지 6중량부, 상기 기포제거제 1중량부 내지 3중량부, 상기 윤활제 2중량부 내지 4중량부, 상기 중화제 3중량부 내지 6중량부 비율로 혼합될 수 있다.Preparing the second dough includes preparing a third mixture by mixing lime powder and purified water and adding an additive to the third mixture, wherein the third mixture is 100 weight of the lime powder It is mixed in a ratio of 400 parts by weight to 800 parts by weight of the purified water with respect to parts, and the additive includes an adhesive, a defoaming agent, a lubricant and a neutralizer, and the second dough is the third mixture based on 100 parts by weight of the third mixture. 3 to 6 parts by weight of the adhesive, 1 to 3 parts by weight of the bubble remover, 2 to 4 parts by weight of the lubricant, and 3 to 6 parts by weight of the neutralizer may be mixed in a ratio.

상기 제1 반죽과 상기 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계는, 상기 제1 반죽 100중량부에 대하여 제2 반죽 150중량부 내지 300중량부 비율로 혼합되는 단계를 포함할 수 있다.The step of preparing the third dough by mixing the first dough and the second dough may include mixing 150 parts by weight to 300 parts by weight of the second dough with respect to 100 parts by weight of the first dough. .

상기 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계는, 제3 반죽 100중량부에 대하여 목화솜 0.5중량부 내지 2중량부 비율로 혼합하는 단계를 포함할 수 있다.The step of preparing the fourth dough by mixing cotton wool with the third dough may include mixing 0.5 parts by weight to 2 parts by weight of cotton wool with respect to 100 parts by weight of the third dough.

상기 과제를 해결하기 위한 다른 실시예에 따른 스컬프쳐 페이스트의 제조방법은, 제1 반죽에 정제수를 넣어 혼합하는 제1 반죽물질을 제조하는 단계와, 상기 제1 반죽물질에 제2 반죽을 혼합하여 제2 반죽물질을 제조하는 단계와, 상기 제2 반죽물질에 경화지연제를 혼합하여 제3 반죽물질을 제조하는 단계 및 상기 제3 반죽물질에 목화솜을 혼합하는 단계를 포함하고, 상기 제1 반죽은 점토로 이루어지고, 상기 제2 반죽은 수성퍼티 조성물로 이루어진다.The method of manufacturing a sculpture paste according to another embodiment for solving the above problems includes the steps of preparing a first dough material for mixing purified water into a first dough, and mixing a second dough with the first dough material A second kneading material comprising the steps of preparing a third kneading material by mixing a curing retardant with the second kneading material, and mixing cotton wool with the third kneading material, The dough is made of clay, and the second dough is made of an aqueous putty composition.

상기 점토는, 인조점토와, 겔 미디엄 및 실리콘 경화제를 포함하되, 상기 인조점토와 상기 겔 미디엄 및 상기 실리콘 경화제는 1:1:0.2 비율로 배합될 수 있다.The clay may include artificial clay, a gel medium, and a silicone curing agent, wherein the artificial clay, the gel medium, and the silicone curing agent may be mixed in a ratio of 1:1:0.2.

상기 수성퍼티 조성물은, 석회가루와, 정제수와, 접착제와, 기포제거제와, 윤활제 및 중화제를 포함하되, 상기 석회가루 100중량부에 대하여 상기 정제수 20중량부 내지 40중량부, 상기 접착제 1중량부 내지 3중량부, 상기 기포제거제 2중량부 내지 4중량부, 상기 윤활제 0.5중량부 내지 2중량부, 상기 중화제 0.5중량부 내지 1.5중량부 비율로 혼합될 수 있다.The aqueous putty composition includes lime powder, purified water, an adhesive, a bubble remover, a lubricant and a neutralizer, and 20 to 40 parts by weight of the purified water, 1 part by weight of the adhesive with respect to 100 parts by weight of the lime powder to 3 parts by weight, 2 parts by weight to 4 parts by weight of the defoaming agent, 0.5 parts by weight to 2 parts by weight of the lubricant, 0.5 parts by weight to 1.5 parts by weight of the neutralizing agent may be mixed in a ratio.

상기 제1 반죽 100중량부에 대하여 상기 제2 반죽 150중량부 내지 300중량부, 상기 정제수 15중량부 내지 30중량부, 상기 목화솜 0.5중량부 내지 2중량부, 상기 경화지연제 5중량부 내지 9중량부 비율로 혼합될 수 있다.150 parts by weight to 300 parts by weight of the second dough with respect to 100 parts by weight of the first dough, 15 parts by weight to 30 parts by weight of the purified water, 0.5 parts by weight to 2 parts by weight of the cotton wool, 5 parts by weight to the curing retardant It may be mixed in a ratio of 9 parts by weight.

상기 과제를 해결하기 위한 다른 실시예에 따른 스컬프쳐 페이스트는 스컬피쳐 페이스트의 제조방법에 의하여 제조될 수 있다.Sculpture paste according to another embodiment for solving the above problems may be manufactured by a method of manufacturing a skull feature paste.

기타 실시예의 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.Details of other embodiments are included in the detailed description and drawings.

일 실시예에 따른 스컬프쳐 페이스트 및 그 제조방법에 의하면, 뛰어난 입체감과 목화솜에 의한 독특한 질감을 표현할 수 있게 된다.According to the sculpture paste and its manufacturing method according to an embodiment, it is possible to express an excellent three-dimensional feeling and a unique texture by cotton wool.

나아가, 스컬프쳐 페이스트가 굳은 후 높은 강도를 유지함으로써 공예품의 손상 및 변형을 효과적으로 방지할 수 있다.Furthermore, damage and deformation of the craft can be effectively prevented by maintaining high strength after the sculpture paste is hardened.

실시예들에 따른 효과는 이상에서 예시된 내용에 의해 제한되지 않으며, 더욱 다양한 효과들이 본 명세서 내에 포함되어 있다.Effects according to the embodiments are not limited by the contents exemplified above, and more various effects are included in the present specification.

도 1은 일 실시예에 따른 스컬프쳐 페이스트의 제조 공정도이다.
도 2는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이다.
도 3은 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이다.
도 4는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이다.
도 5는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽과 제2 반죽을 혼합하여 제3 반죽을 제조하는 모습을 나타낸 사진이다.
도 6은 일 실시예에 따른 스컬프쳐 페이스트의 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 모습을 나타낸 사진이다.
도 7은 일 실시예에 따른 스컬프쳐 페이스트의 제4 반죽이 숙성되어 스컬프쳐 페이스트가 완성된 모습을 나타낸 사진이다.
1 is a manufacturing process diagram of a sculpture paste according to an embodiment.
2 is a photograph showing a state of manufacturing the first dough of the sculpture paste according to an embodiment.
3 is a photograph showing a state of manufacturing the first dough of the sculpture paste according to an embodiment.
4 is a photograph showing a state of manufacturing the first dough of the sculpture paste according to an embodiment.
5 is a photograph showing a state in which the third dough is prepared by mixing the first dough and the second dough of the sculpture paste according to an embodiment.
6 is a photograph showing a state in which a fourth dough is prepared by mixing cotton wool with the third dough of the sculpture paste according to an embodiment.
7 is a photograph showing a state in which the fourth dough of the sculpture paste is aged to complete the sculpture paste according to an embodiment.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.Advantages and features of the present invention and methods of achieving them will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in a variety of different forms, and only these embodiments allow the disclosure of the present invention to be complete, and common knowledge in the technical field to which the present invention belongs It is provided to fully inform the possessor of the scope of the invention, and the present invention is only defined by the scope of the claims.

이하 첨부된 도면을 참조하여 구체적인 실시예들에 대해 설명한다. Hereinafter, specific embodiments will be described with reference to the accompanying drawings.

도 1은 일 실시예에 따른 스컬프쳐 페이스트의 제조 공정도이고, 도 2는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이며, 도 3은 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이고, 도 4는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽을 제조하는 모습을 나타낸 사진이며, 도 5는 일 실시예에 따른 스컬프쳐 페이스트의 제1 반죽과 제2 반죽을 혼합하여 제3 반죽을 제조하는 모습을 나타낸 사진이고, 도 6은 일 실시예에 따른 스컬프쳐 페이스트의 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 모습을 나타낸 사진이며, 도 7은 일 실시예에 따른 스컬프쳐 페이스트의 제4 반죽이 숙성되어 스컬프쳐 페이스트가 완성된 모습을 나타낸 사진이다.Figure 1 is a manufacturing process diagram of a sculpture paste according to an embodiment, Figure 2 is a photograph showing a state of manufacturing a first dough of the sculpture paste according to an embodiment, Figure 3 is a sculpture according to an embodiment It is a photograph showing a state of preparing the first dough of the paste, Figure 4 is a photograph showing the state of preparing the first dough of the sculptural paste according to an embodiment, Figure 5 is a sculpture of the paste according to an embodiment It is a photograph showing a state of manufacturing the third dough by mixing the first dough and the second dough, and FIG. 6 is a state of preparing the fourth dough by mixing cotton wool with the third dough of the sculpture paste according to an embodiment 7 is a photograph showing a state in which the fourth dough of the sculpture paste according to an embodiment is aged and the sculpture paste is completed.

도 1 내지 도 7을 참조하면, 일 실시예에 따른 스컬프쳐 페이스트의 제조방법은, 제1 반죽을 제조하는 단계(S10)와, 제2 반죽을 제조하는 단계(S20)와, 제1 반죽과 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계(S30)와, 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계(S40) 및 제4 반죽을 숙성하는 단계(S50)를 포함할 수 있다.1 to 7 , the method for manufacturing a sculpture paste according to an embodiment includes the steps of preparing a first dough (S10), preparing a second dough (S20), a first dough and Including the steps of preparing a third dough by mixing the second dough (S30), mixing the third dough with cotton wool to prepare a fourth dough (S40), and aging the fourth dough (S50) can do.

몇몇 실시예에서 제1 반죽을 제조하는 단계(S10)는, PVA(Poly viny alcohol)가 함유된 풀(이하, PVA풀), 정제수, 소다(Soda) 및 붕사물을 혼합하는 단계일 수 있다. In some embodiments, the step of preparing the first dough (S10) may be a step of mixing poly viny alcohol (PVA)-containing paste (hereinafter, PVA paste), purified water, soda and borax.

몇몇 실시예에서 제1 반죽을 제조하는 단계(S10)는, 붕사물을 제조하는 단계, PVA풀과 정제수를 혼합하여 제1 혼합물을 제조하는 단계, 제1 혼합물에 소다를 첨가하여 제2 혼합물을 제조하는 단계, 제2 혼합물에 붕사물을 혼합하여 제1 반죽을 제조하는 단계를 포함할 수 있다.In some embodiments, the step of preparing the first dough (S10) is a step of preparing a borax, a step of preparing a first mixture by mixing PVA grass and purified water, a second mixture by adding soda to the first mixture It may include the step of preparing the first dough by mixing the borax in the second mixture.

붕사물을 제조하는 단계는, 붕사(Borax)와 정제수를 혼합하는 단계일 수 있다. 정제수는 85℃ 내지 95℃의 온수일 수 있다. 몇몇 실시예에서 정제수 100중량부에 대해서 붕사 5중량부 내지 15중량부 비율로 혼합될 수 있다. 이와 같이, 붕사와 정제수가 혼합되면 붕사이온(Borate)이 형성되며, 붕사이온(Borate)은 PVA 분자간의 결합력을 더욱 견고하게 할 수 있다.The step of preparing the borax may be a step of mixing borax (Borax) and purified water. Purified water may be hot water of 85 ℃ to 95 ℃. In some embodiments, it may be mixed in a ratio of 5 parts by weight to 15 parts by weight of borax with respect to 100 parts by weight of purified water. As such, when borax and purified water are mixed, borate ions are formed, and borate ions can further strengthen the bonding force between PVA molecules.

PVA풀과 정제수를 혼합하여 제1 혼합물을 제조하는 단계는, 도 2와 같이 PVA풀에 정제수를 넣고 섞어주는 단계를 포함할 수 있다. PVA풀에 정제수를 넣고 섞어주는 단계를 거치면서 일정한 점도를 갖는 제1 혼합물이 제조될 수 있게 된다. 몇몇 실시예에서 제1 혼합물은 PVA풀 100중량부에 대해여 정제수 30중량부 내지 40중량부 비율로 혼합될 수 있다. The step of preparing the first mixture by mixing the PVA pool and purified water may include mixing the purified water into the PVA pool as shown in FIG. 2 . The first mixture having a constant viscosity can be prepared through a step of adding purified water to the PVA pool and mixing. In some embodiments, the first mixture may be mixed in a ratio of 30 parts by weight to 40 parts by weight of purified water based on 100 parts by weight of the PVA pool.

제1 혼합물에 소다를 첨가하여 제2 혼합물을 제조하는 단계는, 도 3과 같이 제1 혼합물에 소다를 참가하여 제1 혼합물을 녹이는 단계를 포함할 수 있다. 소다는 탄산나트륨을 의미하며, 흰색의 결정으로 물에 녹으며 알칼리성을 나타낸다. 몇몇 실시예에서 소다는 베이킹 소다일 수 있다. 즉, 탄산수소나트륨을 사용할 수 있다. 몇몇 실시예에서 제2 혼합물은 제1 혼합물 100중량부에 대하여 소다 2중량부 내지 5중량부 비율로 혼합될 수 있다. The step of preparing the second mixture by adding soda to the first mixture may include dissolving the first mixture by adding soda to the first mixture as shown in FIG. 3 . Soda means sodium carbonate, and it is a white crystal that dissolves in water and shows alkalinity. In some embodiments, the soda may be baking soda. That is, sodium hydrogen carbonate can be used. In some embodiments, the second mixture may be mixed in an amount of 2 parts by weight to 5 parts by weight of soda based on 100 parts by weight of the first mixture.

제2 혼합물에 붕사물을 혼합하여 제1 반죽을 제조하는 단계는, 도 4와 같이 붕사물을 조금씩 혼합하며 제2 혼합물의 굳는 정도를 확인하면서 섞어주는 단계를 포함할 수 있다. 이와 같이, 소다가 포함되어 염기성을 띄는 제1 혼합물에 붕사물이 혼합됨으로써 붕사이온(Borate)과 PVA 분자가 결합되어 탄성을 갖는 제1 반죽이 제조될 수 있다. 몇몇 실시예에서 제1 반죽은 제2 혼합물 100중량부에 대하여 붕사물 10중량부 내지 20중량부 비율로 혼합될 수 있다. The step of preparing the first dough by mixing the borax water with the second mixture may include mixing the borax material little by little as shown in FIG. 4 and mixing while checking the degree of hardening of the second mixture. In this way, the first dough having elasticity by combining borax ions (Borate) and PVA molecules may be prepared by mixing the borax in the first mixture containing soda and having basic properties. In some embodiments, the first dough may be mixed in a ratio of 10 parts by weight to 20 parts by weight of borax with respect to 100 parts by weight of the second mixture.

몇몇 실시예에서 제1 반죽에 포함되는 PVA풀, 정제수, 소다(Soda) 및 붕사물은 PVA풀 100중량부에 대하여 정제수 30중량부 내지 40중량부, 소다 2중량부 내지 6중량부, 붕사물 20중량부 내지 30중량부 비율로 혼합될 수 있다.In some embodiments, PVA paste, purified water, soda and borax contained in the first dough are 30 parts by weight to 40 parts by weight of purified water, 2 parts by weight to 6 parts by weight of soda, borax water based on 100 parts by weight of PVA paste. It may be mixed in a ratio of 20 parts by weight to 30 parts by weight.

몇몇 실시예에서 제1 반죽에는 목화솜이 더 혼합될 수 있다. 이와 같이 목화솜이 혼합되는 경우 제1 반죽에 독특한 질감을 부여할 수 있다. 몇몇 실시예에서 제1 반죽 100중량부에 대하여 묵화솜 2중량부 내지 4중량부 비율로 혼합될 수 있다.In some embodiments, the first dough may be further mixed with cotton wool. In this way, when the cotton wool is mixed, a unique texture can be imparted to the first dough. In some embodiments, it may be mixed in a ratio of 2 parts by weight to 4 parts by weight of the ink cotton with respect to 100 parts by weight of the first dough.

몇몇 실시예에서 제2 반죽을 제조하는 단계(S20)는, 석회가루, 정제수 및 첨가제를 혼합하는 단계일 수 있다.In some embodiments, the step of preparing the second dough (S20) may be a step of mixing lime powder, purified water and additives.

몇몇 실시예에서 제2 반죽을 제조하는 단계(S20)는, 석회가루와 정제수를 혼합하여 제3 혼합물을 제조하는 단계 및 제3 혼합물에 첨가제를 첨가하여 제2 반죽을 제조하는 단계를 포함할 수 있다.In some embodiments, preparing the second dough (S20) may include preparing a third mixture by mixing lime powder and purified water, and adding an additive to the third mixture to prepare a second dough have.

석회가루와 정제수를 혼합하여 제3 혼합물을 제조하는 단계는, 석회가루와 정제수를 넣고 섞어주는 단계이다. 예를 들어, 제3 혼합물은 석회가루 100중량부에 대하여 정제수 400중량부 내지 800중량부 비율로 혼합될 수 있다. 이와 같은 석회가루와 정제수를 혼합과정에서 발열현상이 일어나므로, 60시간 내지 80시간 숙성하는 단계가 추가적으로 필요할 수도 있다. 몇몇 실시예에서 석회가루와 정제수의 혼합과정은 복수회에 걸쳐 이루어질 수도 있다. 예를 들어, 석회가루에 첫번째 정제수를 넣고 섞어주는 단계와, 두번째 정제수를 넣고 섞어주는 단계 등으로 복수회에 걸쳐 이루어질 수도 있다.The step of preparing a third mixture by mixing lime powder and purified water is a step of mixing lime powder and purified water. For example, the third mixture may be mixed in a ratio of 400 parts by weight to 800 parts by weight of purified water based on 100 parts by weight of lime powder. Since an exothermic phenomenon occurs in the mixing process of such lime powder and purified water, a step of aging for 60 to 80 hours may be additionally required. In some embodiments, the mixing process of lime powder and purified water may be performed multiple times. For example, the step of adding and mixing the first purified water to the lime powder and the step of adding and mixing the second purified water may be performed multiple times.

제3 혼합물에 첨가제를 첨가하여 제2 반죽을 제조하는 단계는 제3 혼합물에 접착제, 기포제거제, 윤활제, 중화제 등의 첨가제를 첨가하는 단계일 수 있다. 예를 들어, 제2 반죽은 제3 혼합물 100중량부에 대하여 접착제 3중량부 내지 6중량부, 기포제거제 1중량부 내지 3중량부, 윤활제 2중량부 내지 4중량부, 중화제 3중량부 내지 6중량부 비율로 혼합될 수 있다. 다만, 이에 한정되는 것은 아니며, 첨가제에는 추가적인 성분이 더 포함될 수 있으며, 상기 첨가제 중 일부는 생략될 수도 있다.The step of preparing the second dough by adding an additive to the third mixture may be a step of adding additives such as an adhesive, a defoaming agent, a lubricant, and a neutralizing agent to the third mixture. For example, the second dough is 3 parts by weight to 6 parts by weight of an adhesive, 1 part by weight to 3 parts by weight of a bubble remover, 2 parts by weight to 4 parts by weight of a lubricant, 3 parts by weight to 6 parts by weight of a neutralizer with respect to 100 parts by weight of the third mixture It may be mixed in a proportion by weight. However, the present invention is not limited thereto, and the additive may further include an additional component, and some of the additive may be omitted.

몇몇 실시예에서 제2 반죽은 숙성하는 단계를 더 포함할 수 있다. 예를 들어, 제2 반죽은 20℃ 내지 40℃에서 20시간 내지 30시간의 숙성과정을 포함할 수 있다.In some embodiments, the second dough may further include maturing. For example, the second dough may include an aging process of 20 to 30 hours at 20 to 40 °C.

제1 반죽과 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계(S30)는, 도 5와 같이 제1 반죽과 제2 반죽을 혼합하는 단계일 수 있다. 몇몇 실시예에서 제3 반죽은 제1 반죽 100중량부에 대하여 제2 반죽 150중량부 내지 300중량부 비율로 혼합될 수 있다.The step of preparing the third dough by mixing the first dough and the second dough ( S30 ) may be a step of mixing the first dough and the second dough as shown in FIG. 5 . In some embodiments, the third dough may be mixed in a ratio of 150 parts by weight to 300 parts by weight of the second dough with respect to 100 parts by weight of the first dough.

제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계(S40)는, 도 6과 같이 제 3 반죽에 목화솜을 넣고 섞어주는 단계일 수 있다. 몇몇 실시예에서 제4 반죽은 제3 반죽 100중량부에 대하여 목화솜 0.5중량부 내지 2중량부 비율로 혼합될 수 있다.The step of preparing the fourth dough by mixing the cotton wool with the third dough ( S40 ) may be a step of mixing cotton wool into the third dough as shown in FIG. 6 . In some embodiments, the fourth dough may be mixed in a ratio of 0.5 parts by weight to 2 parts by weight of cotton wool with respect to 100 parts by weight of the third dough.

제4 반죽을 숙성하는 단계(S50)는 20℃ 내지 40℃에서 제4 반죽을 20시간 내지 30시간 숙성하는 하는 단계일 수 있다. 이와 같이 숙성과정을 거치면 스컬프쳐 페이스트가 완성된다. 스컬프쳐 페이스트는 제1 반죽과 제2 반죽이 혼합되어 제3 반죽 및 제4 반죽으로 변성되는 과정을 거치면서, 제1 반죽의 점성과 탄성을 제2 반죽이 적절히 제어하는 역할을 한다. 또한, 스컬프쳐 페이스트의 강도는 강해지고 표면이 유연해져 섬세한 표현이 가능하게 된다. 나아가, 도 7과 같이 목화솜이 첨가되어 독특한 질감을 표현할 수 있게 된다.The step of aging the fourth dough (S50) may be a step of aging the fourth dough at 20° C. to 40° C. for 20 to 30 hours. After this aging process, the sculpture paste is completed. The sculpture paste serves to appropriately control the viscosity and elasticity of the first dough while the first dough and the second dough are mixed and transformed into the third dough and the fourth dough. In addition, the strength of the sculpture paste becomes stronger and the surface becomes softer, enabling delicate expression. Furthermore, as shown in FIG. 7, cotton wool is added to express a unique texture.

다른 실시예에서 스컬프쳐 페이스트의 제1 반죽은 점토로 이루어질 수 있다. 점토는 인조 점토, 인조 점토의 점성을 조절하기 위한 점성 조절제 및 인조 점토와 점성 조절제의 혼합물의 경화속도를 촉진하기 위한 경화촉진제를 포함할 수 있다. 인조 점토는 합성수지(예를 들면, 초산비닐수지)를 주재료로 하고 물을 혼합한 강화제 등을 포함하는 인조 점토로 이루어지고, 상기 점성 조절제는 겔 미디엄(gel medium)이며, 상기 경화촉진제는 실리콘 경화제일 수 있다.In another embodiment, the first dough of the sculpture paste may be made of clay. The clay may include artificial clay, a viscosity modifier for controlling the viscosity of the artificial clay, and a hardening accelerator for accelerating the curing rate of the mixture of the artificial clay and the viscosity modifier. The artificial clay is made of synthetic resin (eg, vinyl acetate resin) as a main material and contains a reinforcing agent mixed with water, and the viscosity modifier is a gel medium, and the curing accelerator is a silicone curing agent. can be the best

몇몇 실시예에서 인조 점토와 겔 미디엄과 실리콘 경화제는 1:1:0.2의 비율로 배합될 수 있다. 겔 미디엄의 배합 비율이 1 미만인 경우에는 점성이 현저히 떨어지고 1 초과인 경우에는 점성이 너무 커져서 성형성 및 작업성이 좋지 못하고, 실리콘 경화제의 배합 비율이 0.2 미만인 경우에는 경화성에 전혀 영향을 주지 못하고, 0.2 초과인 경우에는 성형성에 영향을 줄 뿐만 아니라 급격한 경화 등에 의해 성형물에 크랙이 발생하는 등의 문제점이 있다.In some embodiments, the artificial clay, the gel medium, and the silicone curing agent may be mixed in a ratio of 1:1:0.2. When the mixing ratio of the gel medium is less than 1, the viscosity is significantly reduced, and when it is more than 1, the viscosity becomes too large, resulting in poor moldability and workability, and when the mixing ratio of the silicone curing agent is less than 0.2, it has no effect on curability If it exceeds 0.2, there is a problem that not only affects the moldability, but also cracks occur in the molded product due to rapid hardening.

이와 같이 제1 반죽이 점토로 이루어지는 경우 제1 반죽이 가벼워지고 부드러운 질감을 제공하는 이점이 있다.As such, when the first dough is made of clay, there is an advantage in that the first dough is light and provides a soft texture.

다른 실시예의 스컬프쳐 페이스트의 제2 반죽은 수성퍼티 조성물일 수 있다. 몇몇 실시예에서, 수성퍼티는 석회가루, 정제수, 접착제, 기포제거제, 윤활제, 중화제를 포함할 수 있다. 수성퍼티 조성물은 석회가루 100중량부에 대하여 정제수 20중량부 내지 40중량부, 접착제 1중량부 내지 3중량부, 기포제거제 2중량부 내지 4중량부, 윤활제 0.5중량부 내지 2중량부, 중화제 0.5중량부 내지 1.5중량부 비율로 혼합될 수 있다. 다만, 이에 한정되는 것은 아니다.The second dough of the sculpture paste of another embodiment may be an aqueous putty composition. In some embodiments, the aqueous putty may include lime powder, purified water, an adhesive, a defoaming agent, a lubricant, and a neutralizing agent. The aqueous putty composition contains 20 parts by weight to 40 parts by weight of purified water, 1 part by weight to 3 parts by weight of an adhesive, 2 parts by weight to 4 parts by weight of a bubble remover, 0.5 parts by weight to 2 parts by weight of a lubricant, and 0.5 parts by weight of a neutralizer based on 100 parts by weight of lime powder. It may be mixed in a ratio of 1.5 parts by weight to 1.5 parts by weight. However, the present invention is not limited thereto.

몇몇 실시예에서 제1 반죽이 상기 점토로 이루어지고, 제2 반죽이 상기 수성퍼티 조성물로 이루어진 경우에는 제1 반죽 100중량부에 대하여 제2 반죽 150중량부 내지 300중량부, 정제수 15중량부 내지 30중량부, 목화솜 0.5 중량부 내지 2중량부 비율로 혼합하여 스컬프쳐 페이스트를 제조할 수 있다.In some embodiments, when the first dough is made of the clay and the second dough is made of the aqueous putty composition, 150 parts by weight to 300 parts by weight of the second dough, 15 parts by weight to purified water based on 100 parts by weight of the first dough Sculpture paste can be prepared by mixing 30 parts by weight and 0.5 parts by weight to 2 parts by weight of cotton wool.

몇몇 실시예에서 스컬프쳐 페이스트에는 경화지연제가 더 포함될 수 있다. 경화지연제가 더 포함되는 경우 제1 반죽 100중량부에 대하여 제2 반죽 150중량부 내지 300중량부, 정제수 15중량부 내지 30중량부, 목화솜 0.5 중량부 내지 2중량부, 경화지연제 5중량부 내지 9중량부 비율로 혼합하여 스컬프쳐 페이스트를 제조할 수 있다.In some embodiments, the sculpture paste may further include a curing retardant. When a curing retardant is further included, 150 parts by weight to 300 parts by weight of the second dough, 15 parts by weight to 30 parts by weight of purified water, 0.5 parts by weight to 2 parts by weight of cotton wool, 5 parts by weight of the curing retardant with respect to 100 parts by weight of the first dough Sculpture paste can be prepared by mixing in a ratio of parts to 9 parts by weight.

좀 더 구체적으로 살펴보면, 점토로 이루어진 제1 반죽에 물을 넣어 혼합하는 제1 반죽물질을 제조하는 단계와, 제1 반죽물질에 수성퍼티 조성물로 이루어진 제2 반죽을 혼합하여 제2 반죽물질을 제조하는 단계와, 제2 반죽물질에 경화지연제를 혼합하여 제3 반죽물질을 제조하는 단계 및 제3 반죽물질에 목화솜을 혼합하여 스컬프쳐 페이스트를 제조하는 단계를 포함할 수 있다.More specifically, the steps of preparing a first dough material for mixing the first dough made of clay by adding water, and mixing the first dough material with a second dough made of an aqueous putty composition to prepare a second dough material It may include the steps of, preparing a third dough material by mixing a curing retardant with the second dough material, and preparing a sculptural paste by mixing cotton wool with the third dough material.

이와 같이 제1 반죽에 점토를 이용하고, 제2 반죽에 수성퍼티 조성물을 이용하여 스컬프쳐 페이스트를 제조하는 경우, 입체감과 질감 표현을 더욱 향상시킬 수 있다.As described above, when the sculptural paste is prepared by using the clay for the first dough and the aqueous putty composition for the second dough, three-dimensionality and texture expression can be further improved.

이상 첨부된 도면을 참조하여 본 발명의 실시예들을 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.Although embodiments of the present invention have been described above with reference to the accompanying drawings, those of ordinary skill in the art to which the present invention pertains may be embodied in other specific forms without changing the technical spirit or essential features of the present invention. you will be able to understand Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive.

Claims (10)

제1 반죽을 제조하는 단계;
제2 반죽을 제조하는 단계;
상기 제1 반죽과 상기 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계;
상기 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계 및 제4 반죽을 숙성하는 단계를 포함하고,
상기 제1 반죽을 제조하는 단계는, 붕사물을 제조하는 단계와, PVA풀과 정제수를 혼합하여 제1 혼합물을 제조하는 단계와, 상기 제1 혼합물에 소다를 첨가하여 제2 혼합물을 제조하는 단계와, 상기 제2 혼합물에 상기 붕사물을 혼합하는 단계를 포함하고,
상기 제1 반죽은 상기 PVA풀 100중량부에 대하여 상기 정제수 30중량부 내지 40중량부, 상기 소다 2중량부 내지 6중량부, 상기 붕사물 20중량부 내지 30중량부 비율로 혼합되며,
상기 제2 반죽을 제조하는 단계는, 석회가루와 정제수를 혼합하여 제3 혼합물을 제조하는 단계 및 상기 제3 혼합물에 첨가제를 첨가하는 단계를 포함하고,
상기 제3 혼합물은, 상기 석회가루 100중량부에 대하여 상기 정제수 400중량부 내지 800중량부 비율로 혼합되며,
상기 첨가제는, 접착제와, 기포제거제와, 윤활제 및 중화제를 포함하고,
상기 제2 반죽은 상기 제3 혼합물 100중량부에 대하여 상기 접착제 3중량부 내지 6중량부, 상기 기포제거제 1중량부 내지 3중량부, 상기 윤활제 2중량부 내지 4중량부, 상기 중화제 3중량부 내지 6중량부 비율로 혼합되는 스컬프쳐 페이스트의 제조방법.
preparing a first dough;
preparing a second dough;
preparing a third dough by mixing the first dough and the second dough;
Including the steps of preparing a fourth dough by mixing cotton wool with the third dough and aging the fourth dough,
Preparing the first dough, preparing a borax, preparing a first mixture by mixing PVA grass and purified water, and adding soda to the first mixture to prepare a second mixture And, comprising the step of mixing the borax in the second mixture,
The first dough is mixed in a ratio of 30 parts by weight to 40 parts by weight of the purified water, 2 parts by weight to 6 parts by weight of the soda, 20 parts by weight to 30 parts by weight of the borax with respect to 100 parts by weight of the PVA paste,
The step of preparing the second dough comprises preparing a third mixture by mixing lime powder and purified water and adding an additive to the third mixture,
The third mixture is mixed in a ratio of 400 parts by weight to 800 parts by weight of the purified water with respect to 100 parts by weight of the lime powder,
The additive includes an adhesive, a defoaming agent, a lubricant and a neutralizing agent,
The second dough is 3 parts by weight to 6 parts by weight of the adhesive, 1 part by weight to 3 parts by weight of the bubble remover, 2 parts by weight to 4 parts by weight of the lubricant, 3 parts by weight of the neutralizer with respect to 100 parts by weight of the third mixture A method of producing a sculptural paste that is mixed in a ratio of to 6 parts by weight.
삭제delete 삭제delete 제1 항에 있어서,
상기 제1 반죽과 상기 제2 반죽을 혼합하여 제3 반죽을 제조하는 단계는,
상기 제1 반죽 100중량부에 대하여 제2 반죽 150중량부 내지 300중량부 비율로 혼합되는 단계를 포함하는 스컬프쳐 페이스트의 제조방법.
According to claim 1,
The step of preparing a third dough by mixing the first dough and the second dough,
A method of producing a sculpture paste comprising the step of mixing 150 parts by weight to 300 parts by weight of the second dough with respect to 100 parts by weight of the first dough.
제4 항에 있어서,
상기 제3 반죽에 목화솜을 혼합하여 제4 반죽을 제조하는 단계는,
제3 반죽 100중량부에 대하여 목화솜 0.5중량부 내지 2중량부 비율로 혼합하는 단계를 포함하는 스컬프쳐 페이스트의 제조방법.
5. The method of claim 4,
The step of preparing a fourth dough by mixing cotton wool with the third dough,
A method for producing a sculpture paste comprising the step of mixing 0.5 parts by weight to 2 parts by weight of cotton wool with respect to 100 parts by weight of the third dough.
제1 반죽에 정제수를 넣어 혼합하는 제1 반죽물질을 제조하는 단계;
상기 제1 반죽물질에 제2 반죽을 혼합하여 제2 반죽물질을 제조하는 단계;
상기 제2 반죽물질에 경화지연제를 혼합하여 제3 반죽물질을 제조하는 단계; 및
상기 제3 반죽물질에 목화솜을 혼합하는 단계를 포함하고,
상기 제1 반죽은 점토로 이루어지고, 상기 제2 반죽은 수성퍼티 조성물로 이루어진 스컬프쳐 페이스트의 제조방법.
preparing a first dough material for mixing the first dough with purified water;
preparing a second dough material by mixing a second dough material with the first dough material;
preparing a third dough material by mixing a curing retardant with the second dough material; and
Including the step of mixing cotton wool with the third dough material,
The first dough is made of clay, and the second dough is a method of manufacturing a sculpture paste made of an aqueous putty composition.
제6 항에 있어서,
상기 점토는, 인조점토와, 겔 미디엄 및 실리콘 경화제를 포함하되,
상기 인조점토와 상기 겔 미디엄 및 상기 실리콘 경화제는 1:1:0.2 비율로 배합된 스컬프쳐 페이스트의 제조방법.
7. The method of claim 6,
The clay includes artificial clay, a gel medium and a silicone curing agent,
The method for producing a sculpture paste in which the artificial clay, the gel medium, and the silicone curing agent are mixed in a ratio of 1:1:0.2.
제7 항에 있어서,
상기 수성퍼티 조성물은, 석회가루와, 정제수와, 접착제와, 기포제거제와, 윤활제 및 중화제를 포함하되,
상기 석회가루 100중량부에 대하여 상기 정제수 20중량부 내지 40중량부, 상기 접착제 1중량부 내지 3중량부, 상기 기포제거제 2중량부 내지 4중량부, 상기 윤활제 0.5중량부 내지 2중량부, 상기 중화제 0.5중량부 내지 1.5중량부 비율로 혼합된 스컬프쳐 페이스트의 제조방법.
8. The method of claim 7,
The aqueous putty composition includes lime powder, purified water, an adhesive, a defoaming agent, a lubricant and a neutralizing agent,
Based on 100 parts by weight of the lime powder, 20 parts by weight to 40 parts by weight of the purified water, 1 parts by weight to 3 parts by weight of the adhesive, 2 parts by weight to 4 parts by weight of the bubble remover, 0.5 parts by weight to 2 parts by weight of the lubricant, the A method of producing a sculpture paste mixed in a ratio of 0.5 parts by weight to 1.5 parts by weight of a neutralizing agent.
제8 항에 있어서,
상기 제1 반죽 100중량부에 대하여 상기 제2 반죽 150중량부 내지 300중량부, 상기 정제수 15중량부 내지 30중량부, 상기 목화솜 0.5중량부 내지 2중량부, 상기 경화지연제 5중량부 내지 9중량부 비율로 혼합된 스컬프쳐 페이스트의 제조방법.
9. The method of claim 8,
150 parts by weight to 300 parts by weight of the second dough with respect to 100 parts by weight of the first dough, 15 parts by weight to 30 parts by weight of the purified water, 0.5 parts by weight to 2 parts by weight of the cotton wool, 5 parts by weight to the curing retardant A method of producing a sculptural paste mixed in a ratio of 9 parts by weight.
제6 항 내지 제9 항 중 어느 한 항의 제조방법에 의하여 제조된 스컬프쳐 페이스트.
[Claim 10] The sculpture paste prepared by the manufacturing method of any one of claims 6 to 9.
KR1020200057242A 2020-05-13 2020-05-13 sculpture paste and its manufacturing method KR102351902B1 (en)