KR102327566B1 - Adhesive paper tape - Google Patents

Adhesive paper tape Download PDF

Info

Publication number
KR102327566B1
KR102327566B1 KR1020200077364A KR20200077364A KR102327566B1 KR 102327566 B1 KR102327566 B1 KR 102327566B1 KR 1020200077364 A KR1020200077364 A KR 1020200077364A KR 20200077364 A KR20200077364 A KR 20200077364A KR 102327566 B1 KR102327566 B1 KR 102327566B1
Authority
KR
South Korea
Prior art keywords
paper
base paper
adhesive
impregnated
layer
Prior art date
Application number
KR1020200077364A
Other languages
Korean (ko)
Inventor
두병호
김자경
조성은
Original Assignee
두병호
김자경
조성은
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 두병호, 김자경, 조성은 filed Critical 두병호
Priority to KR1020200077364A priority Critical patent/KR102327566B1/en
Application granted granted Critical
Publication of KR102327566B1 publication Critical patent/KR102327566B1/en

Abstract

The present invention relates to a functional paper adhesive tape that can reduce resource waste by eliminating the need to use a release paper discarded after peeling. Accordingly, the functional paper adhesive tape comprises: a base paper (1) wound in a roll form; an adhesive layer (2) formed on one side of the base paper (1); and an impregnated release layer (3) formed on the other side of the base paper (1), wherein the adhesive layer (2) is implemented by coating an adhesive composition on one side of the base paper (1), and the impregnated release layer (3) is implemented by impregnating the other side of the base paper (1) with a release composition consisting of an aqueous polyvinyl alcohol (PVA) solution and a water-soluble silicone resin.

Description

기능성 종이 점착테이프{Adhesive paper tape}Functional paper adhesive tape {Adhesive paper tape}

본 발명은 종이 점착테이프에 관한 것으로서, 더욱 상세하게는 반복적인 탈부착 과정에서도 초기의 점착 성능을 유지할 수 있는 기능성 종이 점착테이프에 관한 것이다. The present invention relates to a paper adhesive tape, and more particularly, to a functional paper adhesive tape capable of maintaining the initial adhesive performance even in the repeated attachment and detachment process.

일반적으로 포장물을 포장하기 위하여 PE 나 PP 필름에 접착제가 도포된 접착테이프를 사용하고 있다. 접착테이프는 그 자체의 접착력에 의하여 이종의 부재를 상호 연결할 수 있고, 와이어를 사용하지 않음으로써 포장하였을 때 완성도를 높일 수 있다. In general, an adhesive tape with an adhesive applied to a PE or PP film is used to package the package. The adhesive tape can interconnect different members by its own adhesive force, and by not using a wire, it can improve the degree of completeness when packaged.

그런데 접착테이프는 강력한 접착력을 가지기 때문에, 종이로 된 포장물이나 얇은 필름의 포장지로 포장된 포장물을 포장한 후 접착테이프를 떼어낼 때, 강한 접착력에 의하여 포장대상물이 파손되는 경우가 발생되었다. However, since the adhesive tape has a strong adhesive force, when the adhesive tape is peeled off after packaging the packaging made of paper or the packaging of a thin film, the packaging object is damaged due to the strong adhesive force.

또한 포장 과정에서, 접착테이프를 설정된 위치에 정확히 붙이지 못할 경우, 박리후 재부착이 불가능하였고, 이 경우 불완전한 포장 상태를 유지하여야 하였다. In addition, in the packaging process, if the adhesive tape could not be accurately attached to the set position, it was impossible to reattach after peeling. In this case, incomplete packaging had to be maintained.

또한 접착테이프는 모재가 수지 필름으로 되기 때문에 쉽게 절단되지 않고, 이에 따라 포장 과정에서 커터를 사용하여야 하는 번거로움이 있었다. In addition, the adhesive tape is not easily cut because the base material is made of a resin film, and thus there is a cumbersome need to use a cutter in the packaging process.

이에 따라, 종이원지의 일측면에 점착층 및 이형지로 구성되는 점착테이프가 개발되었으며, 이에 따라 포장대상물에서 반복적으로 점착 및 분리가 가능하고, 커터를 사용하지 않고도 절단이 가능하였다. Accordingly, an adhesive tape composed of an adhesive layer and a release paper on one side of the base paper was developed, and thus, it was possible to repeatedly adhere and separate from the packaging object and to cut it without using a cutter.

그런데 상기 점착테이프는 사용시 박리되어 폐기되는 이형지를 채용하였기 때문에, 이형지를 폐기물로 처리하는 과정에서 자원의 낭비 요소가 발생되었다.However, since the adhesive tape employs a release paper that is peeled off and discarded during use, a waste of resources is generated in the process of treating the release paper as a waste.

또한 커터를 사용하지 않고 절단이 가능하기는 하나, 절단된 면이 불규칙하여 포장대상물의 가치를 저하시킨다라는 문제점이 있었다. In addition, although it is possible to cut without using a cutter, there is a problem that the cut surface is irregular, thereby reducing the value of the packaging object.

본 발명은 상기와 같은 문제점을 해결하기 위하여 창출된 것으로서, 박리하여 폐기되는 이형지를 사용하지 않아도 되어, 자원의 낭비 요소를 줄일 수 있는, 기능성 종이 점착테이프를 제공하는 것을 목적으로 한다. An object of the present invention is to provide a functional paper adhesive tape, which has been created to solve the above problems, does not need to use a release paper to be peeled off and discarded, thereby reducing the waste of resources.

본 발명의 다른 목적은, 커터등의 도구를 이용하지 않고도 깔끔한 절단을 가능하게 할 수 있어 포장대상물의 가치를 높일 수 있는. 기능성 종이 점착테이프를 제공하는 것을 목적으로 한다. Another object of the present invention is to enable clean cutting without using tools such as cutters, thereby increasing the value of the packaging object. An object of the present invention is to provide a functional paper adhesive tape.

본 발명의 또 다른 목적은, 점착은 물론 필요에 따라 강하게 접착될 수 있도록 하여 분리되지 않도록 할 수 있는, 기능성 종이 점착테이프를 제공하는 것이다. Another object of the present invention is to provide a functional paper adhesive tape that can not be separated by enabling strong adhesion as well as adhesion as necessary.

상기와 같은 목적을 달성하기 위하여, 본 발명에 따른 기능성 종이 점착테이프는,롤 형태로 말려지는 종이원지(1); 상기 종이원지(1)의 일측면에 형성된 점착층(2); 상기 종이원지(1)의 타측면에 형성된 함침이형층(3); 및 상기 점착층(2)의 가장자리에서 내측에 형성된 것으로서 상기 종이원지(1)로 인가되는 압력에 연동되어 접착제를 방출하는 가압접착층(7);을 포함하고; 상기 점착층(2)은, 점착조성물이 상기 종이원지(1)의 일측면에 코팅됨으로써 구현되고; 상기 함침이형층(3)은 PVA(폴리비닐알코올(Polyvinyl alcohol)) 수용액과 수용성 실리콘 수지로 이루어진 이형조성물이 상기 종이원지(1)의 타측면에 함침되어 구현되고; 상기 가압접착층(7)은, 가압될 때 파괴되는 캡슐(7b)에 충진된 접착제(7c)로 이루어지는 마이크로 크기의 다수의 접착제캡슐(7a)로 구성되고; 상기 함침이형층(3)의 표면에 형성된 것으로서 필기도구로 필기를 가능하게 하기 위한 펄프노출면(4)이 형성되되, 상기 펄프노출면(4)은 상기 함침이형층(3) 표면을 니들 브러쉬로 식각함으로써 형성된 것;을 특징으로 한다. In order to achieve the above object, the functional paper adhesive tape according to the present invention, Paper base paper (1) rolled in the form of a roll; an adhesive layer (2) formed on one side of the base paper (1); an impregnated release layer (3) formed on the other side of the base paper (1); and a pressure-sensitive adhesive layer (7) formed on the inside from the edge of the adhesive layer (2) and releasing the adhesive in association with the pressure applied to the base paper (1); The adhesive layer (2) is implemented by coating the adhesive composition on one side of the base paper (1); The impregnated release layer 3 is implemented by impregnating the other side of the base paper 1 with a release composition composed of an aqueous solution of PVA (Polyvinyl alcohol) and a water-soluble silicone resin; The pressure-adhesive layer 7 is composed of a plurality of micro-sized adhesive capsules 7a made of an adhesive 7c filled in the capsule 7b which is destroyed when pressed; As formed on the surface of the impregnated release layer 3, a pulp exposed surface 4 for enabling writing with a writing instrument is formed, and the pulp exposed surface 4 is formed on the surface of the impregnated release layer 3 with a needle brush. It is characterized by a; formed by etching with

본 발명에 있어서, 상기 이형조성물은, 상기 PVA 수용액 100 중량부를 기준으로 실리콘 수지가 300~800 중량부 비율로 혼합되어 구현된다.In the present invention, the release composition is implemented by mixing the silicone resin in a ratio of 300 to 800 parts by weight based on 100 parts by weight of the PVA aqueous solution.

본 발명에 있어서, 상기 이형조성물을 건조시키기 위하여, 상기 이형조성물이 함침된 종이원지(1)를 90~120℃ 의 온도조건에서 120~240초 동안 유지시킨다.In the present invention, in order to dry the release composition, the base paper 1 impregnated with the release composition is maintained at a temperature of 90 to 120° C. for 120 to 240 seconds.

삭제delete

본 발명에 있어서, 상기 종이원지(1)의 양 가장자리를 따라 일정한 간격으로 형성되는 다수의 절단가이드홈(5)(5')을 더 포함한다.In the present invention, it further includes a plurality of cutting guide grooves (5, 5') formed at regular intervals along both edges of the paper base paper (1).

본 발명에 있어서, 상기 절단가이드홈(5)(5') 사이에서 상기 종이원지(1)의 표면에 형성되는 스크래치라인(6)을 더 포함한다. In the present invention, it further includes a scratch line (6) formed on the surface of the base paper (1) between the cutting guide grooves (5, 5').

본 발명에 따르면, 종이원지(1) 일측면에 점착층(2)이 형성되고 타측면에 함침이형층(3)이 형성됨으로서, 종이원지(1)를 롤 형태로 권회하였을 때 점착층(2)은 함침이형층(3)에 점착되어 완벽한 롤 형태를 이룰 수 있고, 이에 따라 사용을 위해 종이원지(1)를 롤 형태로부터 잡아당길 때 점착층(2)은 함침이형층(3)에서 쉽게 이형될 수 있다. According to the present invention, the adhesive layer 2 is formed on one side of the base paper 1 and the impregnated release layer 3 is formed on the other side, so that when the base paper 1 is wound in a roll shape, the adhesive layer 2 ) can be adhered to the impregnated release layer 3 to form a perfect roll, and thus, when the base paper 1 is pulled from the roll form for use, the adhesive layer 2 is easily removed from the impregnated release layer 3 can be demolded.

또한 함침이형층(3)에 펄프노출면(4)을 형성함으로서 연필에 의하여 자유로운 필기가 가능하며, 이에 따라 포장 도중에 필요한 정보를 용이하고 완벽하게 기재할 수 있다. In addition, by forming the pulp exposed surface 4 on the impregnated release layer 3, free writing is possible with a pencil, and accordingly, necessary information can be easily and completely written during packaging.

또한 종이원지(1)의 양 가장자리를 따라 다수의 절단가이드홈(5)(5')를 형성하고, 절단가이드홈(5)(5') 사이에서 종이원지(1)의 표면에 스크래치라인(6)을 형성함으로써, 커터등의 도구를 이용하지 않고도 깔끔한 절단을 가능하게 할 수 있으며, 이에 따라 포장대상물의 가치를 높일 수 있다. In addition, a plurality of cutting guide grooves 5 and 5' are formed along both edges of the base paper 1, and scratch lines ( 6), it is possible to make a clean cut without using a tool such as a cutter, thereby increasing the value of the packaging object.

그리고 가압접착층(7)을 채용함으로서, 포장된 종이원지(1)의 중앙을 따라 가압하였을 때 가압접착층(7)을 구성하는 접착제캡슐(7a)을 파괴할 수 있고, 이 경우, 접착제(7c)기 캡슐(7b)로부터 빠져나와 종이원지(1)와 포장대상물 사이를 강하게 접착시킬 수 있고, 이에 따라 본 발명의 기능성 종이 점착테이프(10)를 포장대상물로부터 분리되지 않도록 강제 접착시킬 수 있다. And by employing the pressure-adhesive layer 7, when pressed along the center of the packed paper base 1, the adhesive capsule 7a constituting the pressure-adhesive layer 7 can be destroyed, and in this case, the adhesive 7c It can come out from the base capsule 7b and strongly adhere between the base paper 1 and the packaging object, and thus the functional paper adhesive tape 10 of the present invention can be forcibly adhered so as not to be separated from the packaging object.

도 1은 본 발명에 따른 기능성 종이 점착테이프의 사시도,
도 2는 도 1의 II-II' 선을 따른 단면도,
도 3은 도 1의 종이 점착테이프에 절단가이드홈, 스크래치라인 및 가압접착층이 형성된 것을 설명하기 위한 도면,
도 4는 도 3의 IV-IV' 선을 따른 단면도로서, 스크래치라인의 구조를 설명하기 위한 도면,
도 5는 도 3의 가압접착층을 구성하는 접착제캡슐을 설명하기 위한 도면.1 is a perspective view of a functional paper adhesive tape according to the present invention;
2 is a cross-sectional view taken along the line II-II' of FIG. 1;
3 is a view for explaining that a cutting guide groove, a scratch line and a pressure adhesive layer are formed on the paper adhesive tape of FIG. 1;
4 is a cross-sectional view taken along line IV-IV' of FIG. 3, a view for explaining the structure of a scratch line;
5 is a view for explaining an adhesive capsule constituting the pressure-sensitive adhesive layer of FIG.

이하, 본 발명에 따른 기능성 종이 점착테이프를 첨부된 도면들을 참조하여 상세히 설명한다. Hereinafter, the functional paper adhesive tape according to the present invention will be described in detail with reference to the accompanying drawings.

이하에서, "상부" 나 "상"이라고 기재된 것은 접촉하여 바로 위에 있는 것뿐만 아니라 비접촉으로 위에 있는 것도 포함할 수 있다. 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 구성요소들은 용어들에 의해 한정 되어서는 안 된다. 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. 또한, 명세서에 기재된 "...부", "모듈" 등의 용어는 적어도 하나의 기능이나 동작을 처리하는 단위를 의미한다.Hereinafter, what is described as "upper" or "upper" may include not only those directly above in contact, but also those above in non-contact. Terms such as first, second, etc. may be used to describe various elements, but the elements should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another. The singular expression includes the plural expression unless the context clearly dictates otherwise. In addition, when a part "includes" a certain component, this means that other components may be further included, rather than excluding other components, unless otherwise stated. In addition, terms such as "...unit" and "module" described in the specification mean a unit that processes at least one function or operation.

도 1은 본 발명에 따른 기능성 종이 점착테이프의 사시도이고, 도 2는 도 1의 II-II' 선을 따른 단면도이다. 1 is a perspective view of a functional paper adhesive tape according to the present invention, and FIG. 2 is a cross-sectional view taken along line II-II' of FIG. 1 .

도시된 바와 같이, 본 발명에 따른 기능성 종이 점착테이프는, 롤 형태로 말려지는 종이원지(1)와; 종이원지(1)의 일측면에 형성된 점착층(2)과; 종이원지(1)의 타측면에 형성된 함침이형층(3)과; 함침이형층(3)의 표면에 형성된 것으로서 필기도구로 필기를 가능하게 하기 위한 펄프노출면(4);을 포함한다. As shown, the functional paper adhesive tape according to the present invention includes a paper base paper 1 rolled in a roll form; an adhesive layer 2 formed on one side of the paper base 1; an impregnated release layer (3) formed on the other side of the base paper (1); and a pulp exposed surface 4 formed on the surface of the impregnated release layer 3 to enable writing with a writing instrument.

종이원지(1)는 인장강도, 인열강도, 신장도등이 다른 지류에 비하여 특히 우수한 크라프트 종이로 된다. 이러한 크라프트 종이로 된 종이원지(1)는 70, 80, 90g/m2 등 세가지 평량에 대하여 인열강도는 세로 82, 95, 107g, 가로 93, 108, 122g 으로 규정되고, 인장강도는 세로 6.3, 6.8, 7.6kg/15mm 이상, 가로 3.3, 3.5, 3.8kg/15mm 이상으로 규정된 것을 사용한다. The paper base paper 1 is made of kraft paper which is particularly excellent in tensile strength, tear strength, elongation, etc. compared to other papers. The paper base (1) made of such kraft paper has a tear strength of 82, 95, 107g, 93, 108, and 122g for three basis weights such as 70, 80, and 90g/m2, and the tensile strength is 6.3, Use those specified for 6.8, 7.6kg/15mm or more, and 3.3, 3.5, 3.8kg/15mm or more in width.

점착층(2)은 종이원지(1)의 일측면에 형성되는 것으로서, 종이원지(1)를 포장대상물(미도시)에 점착시키거나, 종이원지(1)의 타측면에 형성된 함침이형층(3)에 이형 가능하게 점착될 수 있게 한다. 이러한 점착층(2)은, 아크릴 산(acrylic acid), 부틸 아크릴레이트 모노머(Butyl Acrylate Monomer) 및 옥수수 전분(cornstarch)으로 구성된 점착조성물이 종이원지(1)에 코팅됨으로써 구현되고, 35 ㅁ 5 마이크로미터의 두께를 가진다.The adhesive layer 2 is formed on one side of the base paper 1, and the base paper 1 is adhered to the packaging object (not shown), or an impregnated release layer formed on the other side of the base paper 1 ( 3) so that it can be releasably attached to it. This adhesive layer (2) is implemented by coating the adhesive composition composed of acrylic acid, butyl acrylate monomer, and cornstarch on the paper base paper (1), 35 ㅁ 5 micro has a thickness of meters.

함침이형층(3)은 종이원지(1)의 타측면에 형성된 것으로서, 종이원지(1)를 롤 형태로 권회할 때 점착층(2)이 점착되도록 함과 동시에 원활이 분리되도록 한다. 이러한 함침이형층(3)은 PVA 수용액과 수용성 실리콘 수지로 이루어진 이형조성물이 종이원지(1)의 타측면에 함침되어 한 몸체를 이룬다. The impregnated release layer 3 is formed on the other side of the base paper 1, and when the base paper 1 is wound in a roll shape, the adhesive layer 2 is adhered and at the same time is smoothly separated. This impregnated release layer (3) forms a body by impregnating the other side of the base paper (1) with a release composition composed of an aqueous PVA solution and a water-soluble silicone resin.

함침이형층(3)은, 종이원지(1)의 일측 표면을 거칠게 표면 처리하고, 이후 표면 처리된 종이원지(1) 표면에 이형조성물을 도포하고 건조시킴으로써 구현된다. The impregnated release layer 3 is implemented by rough surface-treating one surface of the base paper 1, and then applying a release composition to the surface-treated surface of the base paper 1 and drying.

종이원지(1)의 표면 처리는, 고속으로 회전되는 니들 브러쉬롤러에 표면이 접촉되게 종이원지(1)를 상대 이송시킴으로써 구현된다. 이에 따라 니들 브러쉬롤러는 종이원지(1) 표면에서 돌출되는 펄프 조직을 형성할 수 있고, 이 상태에서 후술할 이형조성물을 도포하면 이형조성물은 거칠어진 펄프 조직으로 함침된다. 즉, 종이원지(1) 표면에서 펄프조직이 거칠게 부풀어지도록 함으로써 후술할 이형조성물이 효과적으로 흡수 및 함침되는 것이다. The surface treatment of the base paper 1 is implemented by relatively transferring the base paper 1 so that the surface is in contact with the needle brush roller rotated at high speed. Accordingly, the needle brush roller can form a pulp structure protruding from the surface of the base paper 1, and in this state, when a release composition to be described later is applied, the release composition is impregnated with a rough pulp structure. That is, the release composition to be described later is effectively absorbed and impregnated by making the pulp texture rough on the surface of the paper base paper 1 .

이형조성물은, PVA(폴리비닐알코올(Polyvinyl alcohol)) 수용액 100 중량부를 기준으로 실리콘 수지가 300~800 중량부 비율로 혼합되어 구현된다. The release composition is implemented by mixing a silicone resin in a ratio of 300 to 800 parts by weight based on 100 parts by weight of a PVA (polyvinyl alcohol) aqueous solution.

만약, 실리콘 수지가 300 중량부 이하일 경우, 이형조성물은 되게 되어 종이원지(1)에 표면으로 잘 흡수되지 못하게 되고, 이에 따라 완성되는 함침이형층(3)의 이형능력이 완벽하지 않게 된다. 이는 후술할 점착층(2) 및 가압접착층(7)이 함침이형층(3)에서 쉽게 이형되지 못하게 되는 원인이 된다. 또한 실리콘 수지가 800 중량부 이상일 경우 완성되는 이형조성물은 너물 묽게 되어 건조과정에서 많은 시간이 소요되고, 이에 따라 완성되는 함침이형층(3) 표면이 거칠게 된다. 이 경우에도 후술할 점착층(2)이 함침이형층(3) 및 가압접착층(7)이 쉽게 이형되지 못하게 된다. If the amount of the silicone resin is 300 parts by weight or less, the release composition is not well absorbed to the surface of the paper base paper 1, and thus the release ability of the finished impregnated release layer 3 is not perfect. This causes the pressure-sensitive adhesive layer 2 and the pressure-sensitive adhesive layer 7 to be described later from being easily released from the impregnated release layer 3 . In addition, when the amount of the silicone resin is 800 parts by weight or more, the finished release composition becomes too thin and takes a lot of time in the drying process, and thus the surface of the finished impregnated release layer 3 becomes rough. Even in this case, the pressure-sensitive adhesive layer 2 to be described later is not easily released by the impregnated release layer 3 and the pressure-sensitive adhesive layer 7 .

한편, 도포된 이형조성물을 건조시키기 위하여, 이형조성물이 함침된 종이원지(1)를 90~120℃ 의 온도조건에서 120~240초 동안 유지시킨다.Meanwhile, in order to dry the applied release composition, the base paper 1 impregnated with the release composition is maintained at a temperature of 90 to 120° C. for 120 to 240 seconds.

만약 건조 온도가 90℃이하이고 120초 이하일 경우 완벽한 건조가 이루어지지 못하게 되고, 120℃ 온도 이상이고 240초 이상일 경우 이형조성물의 물성 변화가 발생된다. If the drying temperature is less than 90 ℃ and less than 120 seconds, perfect drying cannot be achieved, and if the temperature is more than 120 ℃ and more than 240 seconds, a change in the physical properties of the mold release composition occurs.

이와 같이, 펄프 조직이 부풀어지도록 거칠게 표면 처리된 종이원지(1) 표면으로 이형조성물이 함침 및 건조됨으로서 함침이형층(3)이 구현되고, 이러한 함침이형층(3)에 의하여, 점착층(2)이 형성된 종이원지(1)를 롤 형태로 권회하였을 때 점착층(2)은 함침이형층(3)에 점착되어 완벽한 롤 형태를 이룰 수 있다. 그리고 사용을 위해 종이원지(1)를 잡아당기면 점착층(2)은 함침이형층(3)에서 쉽게 이형되면서 종이원지(1)를 롤 형태에서 길게 풀어진다. As described above, the impregnated release layer 3 is realized by impregnating and drying the release composition on the surface of the rough surface-treated paper base 1 so that the pulp tissue swells, and by this impregnated release layer 3, the adhesive layer 2 ), when the formed paper base 1 is wound in a roll shape, the adhesive layer 2 is adhered to the impregnated release layer 3 to form a perfect roll shape. And when the base paper 1 is pulled for use, the adhesive layer 2 is easily released from the impregnated release layer 3 and the base paper 1 is long released from the roll shape.

여기서, 함침이형층(3)을 형성함으로써, 별도의 이형지와 같은 구성을 채용하지 않아도 되고, 이에 따라 이형지를 처리하는 과정에서 발생되는 자원낭비 요소를 줄일 수 있고, 환경이 오염되는 것을 방지할 수 있다. Here, by forming the impregnated release layer 3, it is not necessary to employ a configuration such as a separate release paper, and thus it is possible to reduce the resource wasting factor generated in the process of processing the release paper, and to prevent pollution of the environment. have.

펄프노출면(4)은, 도 2에 도시된 바와 같이, 종이 펄프 단면(1a)을 함침이형층(3) 표면으로부터 노출시킨 면이다. 이러한 펄프노출면(4)을 형성하기 위하여, 함침이형층(3) 표면을 날카로운 니들 브러쉬와 접촉된 상태로 상대 이송시키며, 이 과정을 통하여 실리콘 수지로 덮여진 함침이형층(3)이 표면이 식각되고 이에 따라 종이원지(1)를 구성하는 펄프 단면(1a)이 노출된다. 즉, 펄프노출면(4)을 통하여 실리콘 수지로 덮여진 함침이형층(3) 표면에서 종이 펄프단면(1a)을 노출시키는 것이며, 이에 따라 연필을 이용하여 자유로운 필기가 가능해진다. The pulp exposed surface 4 is a surface exposed from the surface of the impregnated release layer 3 to the paper pulp end surface 1a, as shown in FIG. 2 . In order to form such a pulp exposed surface 4, the surface of the impregnated release layer 3 is relatively transferred in contact with a sharp needle brush, and through this process, the impregnated release layer 3 covered with a silicone resin becomes the surface The etched section exposes the pulp cross section 1a constituting the base paper 1 as a result. That is, the paper pulp end surface 1a is exposed on the surface of the impregnated release layer 3 covered with the silicone resin through the pulp exposed surface 4, and thus free writing is possible using a pencil.

만약, 펄프노출면(4)을 형성하지 않을 경우, 함침이형층(3)의 표면은 실리콘 수지에 의하여 덮여진 상태이기 때문에, 연필로 필기할 경우 필기하기가 상당히 어렵거나 필기가 되지 않게 된다. If the pulp exposed surface 4 is not formed, since the surface of the impregnated release layer 3 is covered with a silicone resin, it is very difficult or impossible to write with a pencil.

한편, 상기 함침이형층(3)의 식각은, 니들 브러쉬를 함침이형층(3) 표면에 밀착시킨 상태에서 왕복 이송시킴으로써 이루어지거나, 니들 브러쉬를 가지는 브러쉬롤러를 고속 회전시키면서 함침이형층(3) 표면으로 상대 이송시킴으로써 이루어질 수 있다. On the other hand, the etching of the impregnated release layer (3) is made by reciprocating a needle brush in a state in close contact with the impregnated release layer (3), or by rotating a brush roller having a needle brush at high speed while the impregnated release layer (3) This can be done by relative transfer to the surface.

도 3은 도 1의 종이 점착테이프에 절단가이드홈, 스크래치라인 및 가압접착층이 형성된 것을 설명하기 위한 도면이고, 도 4는 도 3의 IV-IV' 선을 따른 단면도로서, 스크래치라인의 구조를 설명하기 위한 도면이며, 도 5는 도 3의 가압접착층을 구성하는 접착제캡슐을 설명하기 위한 도면이다.FIG. 3 is a view for explaining that a cutting guide groove, a scratch line, and a pressure adhesive layer are formed in the paper adhesive tape of FIG. 1, and FIG. 4 is a cross-sectional view taken along line IV-IV' of FIG. 3, explaining the structure of the scratch line FIG. 5 is a view for explaining an adhesive capsule constituting the pressure-sensitive adhesive layer of FIG. 3 .

본 발명의 종이 점착테이프(10)는, 종이원지(1)의 양 가장자리를 따라 일정한 간격으로 형성되는 다수의 절단가이드홈(5)(5')과; 절단가이드홈(5)(5') 사이에서 종이원지(1)의 표면에 형성되는 스크래치라인(6)과; 점착층(2)에 내장된 것으로서 종이원지(1)로 인가되는 압력에 연동되어 접착제를 방출하는 가압접착층(7);을 더 포함할 수 있다. The paper adhesive tape 10 of the present invention includes a plurality of cutting guide grooves 5 and 5 ′ formed at regular intervals along both edges of the paper base paper 1 ; a scratch line 6 formed on the surface of the base paper 1 between the cutting guide grooves 5 and 5'; A pressure-sensitive adhesive layer 7 embedded in the adhesive layer 2 to release the adhesive in association with the pressure applied to the base paper 1; may further include.

절단가이드홈(5)(5')은 종이원지(1)의 양 가장자리에 일정한 간격으로 형성된 패어진 홈이다. 이러한 절단가이드홈(5)(5')에 의하여, 사용자는 포장 도중에 특정 절단가이드홈 근처에서 종이원지(1)를 잡아당기면, 커터를 사용하지 않고도 용이하게 절단할 수 있다. The cutting guide grooves 5 and 5' are grooves formed at regular intervals on both edges of the base paper 1 . With these cutting guide grooves 5 and 5', if a user pulls the paper stock 1 near a specific cutting guide groove during packaging, it can be easily cut without using a cutter.

스크래치라인(6)은, 도 4에 도시된 바와 같이, 절단가이드홈(5)(5') 사이에서 종이원지(1)의 표면에 홈이 라인 형태로 형성됨으로써 구현된다. 즉, 스크래치라인(6)은 종이원지(1)를 절단하는 것이 아닌, 종이원지(1) 표면에 형성되는 홈인 것이다. 스크래치라인(6)은 절단가이드홈(5)(5')과 일직선상에 위치되고, 이에 따라 특정 절단가이드홈을 찢으면서 잡아당기면, 종이원지(1)는 스크래치라인(6)을 따라 깔끔하게 절단된다. The scratch line 6 is implemented by forming a groove on the surface of the base paper 1 in the form of a line between the cutting guide grooves 5 and 5', as shown in FIG. 4 . That is, the scratch line 6 is a groove formed on the surface of the base paper 1 rather than cutting the base paper 1 . The scratch line 6 is positioned on a straight line with the cutting guide grooves 5 and 5 ', and accordingly, when the specific cutting guide groove is torn and pulled, the base paper 1 is neatly cut along the scratch line 6 do.

이러한 스크래치라인(6)은 종이원지(1) 절단하지 않고 표면에 홈을 형성함으로써 구현되기 때문에 종이원지(1)는 충분한 인장강도를 유지할 수 있고, 절단을 하고자 할 경우 종이원지(1)는 스크래치라인(6)을 따라 깔끔하게 절단될 수 있는 것이다. 이에 따라 점착테이프(10)의 절단면이 커터로 절단한 것처럼 깔끔하게 마감되어 포장대상물의 가치를 높여준다. Since the scratch line 6 is implemented by forming a groove on the surface of the base paper 1 without cutting it, the base paper 1 can maintain sufficient tensile strength, and when cutting, the base paper 1 is scratched. It can be cut neatly along the line (6). Accordingly, the cut surface of the adhesive tape 10 is neatly finished as if cut with a cutter, thereby increasing the value of the packaging object.

가압접착층(7)은 점착층(2)의 가장자리에서 내측에 형성된 것으로서 종이원지(1)로 인가되는 압력에 연동되어 접착제를 방출한다. 가압접착층(7)은 점착층(2)의 내측에 캡슐(7b)에 충진된 접착제(7c)로 이루어지는 마이크로 크기 단위의 접착제캡슐(7a)이 내장됨으로 구현된다. 여기서 접착제캡슐(7a)은, 옥수수 전분으로 된 구형의 캡슐(7b)에 접착제(7c)가 내장되어 구현되며, 접착제(7c)는 일반 접착테이프에서 사용되는 접착제로 된다. The pressure-sensitive adhesive layer 7 is formed on the inside at the edge of the adhesive layer 2 and is interlocked with the pressure applied to the base paper 1 to release the adhesive. The pressure-sensitive adhesive layer 7 is implemented by embedding an adhesive capsule 7a in a micro size unit made of an adhesive 7c filled in the capsule 7b inside the adhesive layer 2 . Here, the adhesive capsule 7a is implemented by embedding an adhesive 7c in a spherical capsule 7b made of corn starch, and the adhesive 7c is an adhesive used in a general adhesive tape.

이러한 가압접착층(7)에 의하여, 점착테이프(10)가 포장대상물을 포장한 이후, 점착테이프를 포장대상물에 완전히 접착시키고자 할 경우 가압접착층(7)의 반대면에서 손톱등으로 종이원지(1)를 가압한다. 그러면 옥수수 전분으로 된 캡슐(7b)이 인가되는 압력에 의하여 파괴되면서 접착제(7c)가 흘러나와 종이원지(1)와 포장대상물을 접착시키고, 이 상태에서 점착테이프(10)를 포장대상물로부터 분리되지 않게 된다. 즉, 가압접착층(7)을 채용함으로써, 포장대상물에서 점착테이프(10)가 분리되지 않게 할 수 있으며, 이에 따라 포장대상물이 불법적인 목적으로 개방되는 것을 방지할 수 있다. By means of this pressure-adhesive layer 7, after the adhesive tape 10 packs the packaging object, when it is desired to completely adhere the adhesive tape to the packaging object, use a nail or the like on the opposite side of the pressure-sensitive adhesive layer 7 to use the paper base paper (1). ) is pressurized. Then, while the corn starch capsule 7b is destroyed by the applied pressure, the adhesive 7c flows out and adheres the base paper 1 and the packaging object, and in this state, the adhesive tape 10 is not separated from the packaging object. won't That is, by employing the pressure-sensitive adhesive layer 7, it is possible to prevent the adhesive tape 10 from being separated from the packaging object, thereby preventing the packaging object from being opened for illegal purposes.

이와 같이, 본 발명에 따르면, 종이원지(1) 일측면에 점착층(2)이 형성되고 타측면에 함침이형층(3)이 형성됨으로서, 종이원지(1)를 롤 형태로 권회하였을 때 점착층(2)은 함침이형층(3)에 점착되어 완벽한 롤 형태를 이룰 수 있다. 이에 따라 사용을 위해 종이원지(1)를 롤 형태로부터 잡아당길 때 점착층(2)은 함침이형층(3)에서 쉽게 이형될 수 있다. 이에 따라 박리되어 폐기되는 이형지를 사용하지 않아도 되어, 자원의 낭비 요소를 줄일 수 있다. As described above, according to the present invention, the adhesive layer 2 is formed on one side of the base paper 1 and the impregnated release layer 3 is formed on the other side. The layer 2 may be adhered to the impregnated release layer 3 to form a perfect roll. Accordingly, when the base paper 1 is pulled from the roll form for use, the adhesive layer 2 can be easily released from the impregnated release layer 3 . Accordingly, there is no need to use a release paper that is peeled off and discarded, thereby reducing the waste of resources.

또한 함침이형층(3)에 펄프노출면(4)을 형성함으로서 연필을 이용하여 자유로운 필기가 가능하며, 포장 도중에 필요한 정보를 용이하고 완벽하게 기재할 수 있다. In addition, by forming the pulp exposed surface 4 on the impregnated release layer 3, free writing is possible using a pencil, and necessary information can be easily and completely written during packaging.

또한 종이원지(1)의 양 가장자리를 따라 다수의 절단가이드홈(5)(5')를 형성하고, 절단가이드홈(5)(5') 사이에서 종이원지(1)의 표면에 스크래치라인(6)을 형성함으로써, 커터등의 도구를 이용하지 않고도 깔끔한 절단을 가능하게 할 수 있다. 이에 따라 포장대상물의 가치를 높일 수 있다. In addition, a plurality of cutting guide grooves 5 and 5' are formed along both edges of the base paper 1, and scratch lines ( 6), it is possible to make a clean cut without using a tool such as a cutter. Accordingly, the value of the packaging object can be increased.

그리고 가압접착층(7)을 채용함으로서, 포장된 종이원지(1)의 중앙을 따라 가압하였을 때 가압접착층(7)을 구성하는 접착제캡슐(7a)을 파괴할 수 있다. 이 경우, 접착제(7c)기 캡슐(7b)로부터 빠져나와 종이원지(1)와 포장대상물 사이를 강하게 접착시킬 수 있고, 이에 따라 본 발명의 기능성 종이 점착테이프(10)를 포장대상물로부터 분리되지 않도록 강제 접착시킬 수 있다. And by employing the pressure-adhesive layer 7, it is possible to destroy the adhesive capsule 7a constituting the pressure-adhesive layer 7 when pressed along the center of the packed paper base 1 . In this case, the adhesive 7c can come out from the capsule 7b and strongly adhere between the base paper 1 and the packaging object, so that the functional paper adhesive tape 10 of the present invention is not separated from the packaging object. It can be force-bonded.

본 발명은 도면에 도시된 일 실시예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. Although the present invention has been described with reference to one embodiment shown in the drawings, which is only exemplary, those skilled in the art will understand that various modifications and equivalent other embodiments are possible therefrom.

10 ... 점착테이프
1 ... 종이원지 2 ... 점착층
3 ... 함침이형층 4 ... 펄프노출면
5, 5' ... 절단가이드홈 6 ... 스크래치라임
7 ... 가압접착층 7a ... 접착제캡슐
7b ... 캡슐 7c ... 접착제10 ... adhesive tape
1 ... Paper base 2 ... Adhesive layer
3 ... impregnated release layer 4 ... pulp exposed surface
5, 5' ... Cutting guide groove 6 ... Scratch lime
7 ... pressure adhesive layer 7a ... adhesive capsule
7b ... Capsule 7c ... Glue

Claims (6)

롤 형태로 말려지는 종이원지(1);
상기 종이원지(1)의 일측면에 형성된 점착층(2);
상기 종이원지(1)의 타측면에 형성된 함침이형층(3); 및
상기 점착층(2)의 가장자리에서 내측에 형성된 것으로서 상기 종이원지(1)로 인가되는 압력에 연동되어 접착제를 방출하는 가압접착층(7);을 포함하고;
상기 점착층(2)은, 점착조성물이 상기 종이원지(1)의 일측면에 코팅됨으로써 구현되고;
상기 함침이형층(3)은 PVA(폴리비닐알코올(Polyvinyl alcohol)) 수용액과 수용성 실리콘 수지로 이루어진 이형조성물이 상기 종이원지(1)의 타측면에 함침되어 구현되고;
상기 가압접착층(7)은, 가압될 때 파괴되는 캡슐(7b)에 충진된 접착제(7c)로 이루어지는 마이크로 크기의 다수의 접착제캡슐(7a)로 구성되고;
상기 함침이형층(3)의 표면에 형성된 것으로서 필기도구로 필기를 가능하게 하기 위한 펄프노출면(4)이 형성되되, 상기 펄프노출면(4)은 상기 함침이형층(3) 표면을 니들 브러쉬로 식각함으로써 형성된 것;을 특징으로 하는 기능성 종이 점착테이프.Paper base paper (1) rolled in the form of a roll;
an adhesive layer (2) formed on one side of the base paper (1);
an impregnated release layer (3) formed on the other side of the base paper (1); and
and a pressure-sensitive adhesive layer (7) formed on the inside from the edge of the adhesive layer (2) and releasing the adhesive in association with the pressure applied to the base paper (1);
The adhesive layer (2) is implemented by coating the adhesive composition on one side of the base paper (1);
The impregnated release layer 3 is implemented by impregnating the other side of the base paper 1 with a release composition composed of an aqueous solution of PVA (Polyvinyl alcohol) and a water-soluble silicone resin;
The pressure-sensitive adhesive layer 7 is composed of a plurality of micro-sized adhesive capsules (7a) made of an adhesive (7c) filled in the capsule (7b) that is destroyed when pressed;
As formed on the surface of the impregnated release layer 3, a pulp exposed surface 4 for enabling writing with a writing instrument is formed, and the pulp exposed surface 4 is formed on the surface of the impregnated release layer 3 with a needle brush. Functional paper adhesive tape, characterized in that; formed by etching with 제1항에 있어서,
상기 이형조성물은, 상기PVA 수용액 100 중량부를 기준으로 실리콘 수지가 300~800 중량부 비율로 혼합되어 구현된 것을 특징으로 하는 기능성 종이 점착테이프.According to claim 1,
The release composition is a functional paper adhesive tape, characterized in that the silicone resin is mixed in a ratio of 300 to 800 parts by weight based on 100 parts by weight of the PVA aqueous solution. 제2항에 있어서,
상기 이형조성물을 건조시키기 위하여, 상기 이형조성물이 함침된 종이원지(1)를 90~120℃ 의 온도조건에서 120~240초 동안 유지시키는 것을 특징으로 하는 기능성 종이 점착테이프.3. The method of claim 2,
In order to dry the release composition, the functional paper adhesive tape, characterized in that the paper base paper (1) impregnated with the release composition is maintained for 120-240 seconds at a temperature of 90-120°C. 삭제delete 제1항에 있어서,
상기 종이원지(1)의 양 가장자리를 따라 일정한 간격으로 형성되는 다수의 절단가이드홈(5)(5')을 더 포함하는 것을 특징으로 하는 기능성 종이 점착테이프.According to claim 1,
Functional paper adhesive tape, characterized in that it further comprises a plurality of cutting guide grooves (5, 5') formed at regular intervals along both edges of the paper base paper (1). 제5항에 있어서,
상기 절단가이드홈(5)(5') 사이에서 상기 종이원지(1)의 표면에 형성되는 스크래치라인(6)을 더 포함하는 것을 특징으로 하는 기능성 종이 점착테이프.6. The method of claim 5,
Functional paper adhesive tape, characterized in that it further comprises a scratch line (6) formed on the surface of the base paper (1) between the cutting guide grooves (5, 5').
KR1020200077364A 2020-06-24 2020-06-24 Adhesive paper tape KR102327566B1 (en)