KR102322622B1 - Manufacturing method of fuel cell bipolar plate - Google Patents
Manufacturing method of fuel cell bipolar plate Download PDFInfo
- Publication number
- KR102322622B1 KR102322622B1 KR1020200010661A KR20200010661A KR102322622B1 KR 102322622 B1 KR102322622 B1 KR 102322622B1 KR 1020200010661 A KR1020200010661 A KR 1020200010661A KR 20200010661 A KR20200010661 A KR 20200010661A KR 102322622 B1 KR102322622 B1 KR 102322622B1
- Authority
- KR
- South Korea
- Prior art keywords
- fuel cell
- cell separator
- carbon composite
- thermoplastic resin
- channel
- Prior art date
Abstract
본 발명은 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련하는 단계, 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드를 마련하는 단계 및 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계를 포함하는 연료전지 분리판 제조방법을 제공한다.The present invention provides the steps of preparing a carbon composite plate including a thermoplastic resin containing conductive nanomaterials, providing a mold for forming a fuel cell separator having a channel shape therein, and applying the carbon composite plate to the fuel cell separator Provided is a method for manufacturing a fuel cell separator comprising the step of providing a fuel cell separator integrally formed with a channel by putting it into a molding mold.
Description
본 발명은 연료전지 분리판의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a fuel cell separator.
연료전지는 수소 또는 탄화수소 계열 원료와 산소로 대표되는 산화제의 전기화학 반응에 의해 전기 에너지를 얻는 에너지원으로서, 미래를 대비하는 가장 유망한 청정 에너지원 중의 하나로 최근 주목 받고 있다.A fuel cell is an energy source that obtains electric energy by an electrochemical reaction of an oxidizing agent represented by hydrogen or hydrocarbon-based raw material and oxygen, and has recently been attracting attention as one of the most promising clean energy sources for the future.
이러한 연료전지는 전기를 생성하는 스택, 스택으로 연료를 공급하는 연료 공급부 및 스택으로 산화제를 공급하는 산화제 공급부로 이루어진다. 또한, 이 스택은 막전극조립체(Membrane Electrode Assembly)와 분리판(Separator)이 순차적으로 적층된 구조를 이루며, 막전극조립체는 연료의 산화 및 환원제의 환원 반응을 통해 전기를 생성한다.Such a fuel cell includes a stack generating electricity, a fuel supply unit supplying fuel to the stack, and an oxidizer supply unit supplying an oxidizing agent to the stack. In addition, this stack has a structure in which a membrane electrode assembly and a separator are sequentially stacked, and the membrane electrode assembly generates electricity through oxidation of fuel and reduction reaction of a reducing agent.
다양한 방식의 연료전지 중, 고분자 전해질용 연료전지는 비교적 낮은 작동 온도와 스택의 소형화 가능성으로 수소용 전력원으로 활발이 연구되고 있으며, 현재 실용화 가능성이 높다고 평가받고 있다. 이러한 고분자 전해질형 연료전지는 그 내부에 여러 셀들의 연결이 포함되는데, 이러한 셀과 셀 간의 전기적인 연결은 분리판 또는 바이폴라플레이트(bipolar plate)에 의해 이루어지게 된다.Among various types of fuel cells, fuel cells for polymer electrolytes are being actively studied as a power source for hydrogen due to their relatively low operating temperature and the possibility of stack miniaturization, and are currently evaluated as having high potential for practical use. Such a polymer electrolyte fuel cell includes the connection of several cells therein, and the electrical connection between these cells and the cells is made by a separator or a bipolar plate.
분리판은 연료전지 스택에서 각 전지를 분리하고 있는 전도성 판으로, 인접한 두 전지에서 한 전지에서는 연료극판으로 다른 한 전지에서는 공기극판으로 기능한다. 분리판은 연료가스와 공기를 차단하는 역할 외에 연료가스와 공기의 유로 확보 및 외부 회로에 전류를 전달하는 역할을 하므로, 높은 전기 전도성, 내식성, 열전도성과 함께 낮은 기체 투과성이 요구된다.The separator is a conductive plate that separates each cell in a fuel cell stack, and functions as an anode plate in one cell and a cathode plate in the other cell in two adjacent cells. In addition to the role of blocking fuel gas and air, the separator serves to secure a flow path for fuel gas and air and transmit current to an external circuit, so high electrical conductivity, corrosion resistance, thermal conductivity and low gas permeability are required.
분리판은 주로 수지 함침 흑연판, 탄소복합체판, 금속판 등으로 제작 되어지는데, 상기 분리판에는 유체의 흐름을 돕기 위해 유로가 형성되어 있다. 또한 분리판은 전지에서 발생된 열을 연료전지 스택 전체에 분배하는 역할도 수행하게 되는데, 과도하게 발생된 열은 공랭식 혹은 수냉식 열 교환을 통해 회수되어 버려지거나 사용할 수 있다.The separator is mainly made of a resin-impregnated graphite plate, a carbon composite plate, a metal plate, and the like, and a flow path is formed in the separator to help the fluid flow. In addition, the separator also serves to distribute the heat generated by the cell to the entire fuel cell stack, and the excessively generated heat can be recovered and discarded or used through air-cooled or water-cooled heat exchange.
지금까지 개발된 분리판 종류는 수지 함침 흑연판, 탄소복합체 분리판 및 금속 분리판으로 구분할 수 있다.The types of separators developed so far can be divided into resin-impregnated graphite plates, carbon composite separators, and metal separators.
이 중 수지 함침 흑연판은 흑연판에 수지(Resin)를 함침하여 기계 가공을 통해 기체 유로를 형성시킨 연료전지용 분리판이다. 전기 및 열전도성이 매우 높고, 부식에 매우 강하기 때문에 연료전지 연구개발 초기 단계부터 주로 사용되어 지고 있다.Among them, the resin-impregnated graphite plate is a fuel cell separator in which the graphite plate is impregnated with resin to form a gas flow path through machining. Because it has very high electrical and thermal conductivity and is very resistant to corrosion, it is mainly used from the initial stage of fuel cell research and development.
그러나, 수지 함침 흑연판은 흑연 분리판은 얇은 흑연판을 밀링 기계가공하여 성형하므로 제작시간 및 비용이 과다하게 소요되고, 충격에 의한 파손 가능성 큰 문제점이 있다.However, since the resin-impregnated graphite plate is molded by milling a thin graphite plate, the resin-impregnated graphite plate requires excessive manufacturing time and cost, and has a large problem of damage due to impact.
금속 분리판은 금속(주로 스테인리스 스틸)을 가공/주물/몰딩 함으로써 제작 되어지며, 전기 및 열전도성은 매우 높으나, 내부식성이 약한 단점이 있다.Metal separator is manufactured by processing/casting/molding metal (mainly stainless steel), and has very high electrical and thermal conductivity, but has a weak corrosion resistance.
한편, 금속 분리판은 내부식성을 위해 금속 자체에 부식을 막아주는 코팅이 필요하게 되는데, 이러한 코팅작업에 의해서 작업 시간이 길어질 뿐 아니라 제작 단가가 올라가고 코팅재에 의해 전기 전도성이 떨어지는 단점이 있다.On the other hand, the metal separator requires a coating to prevent corrosion on the metal itself for corrosion resistance, and this coating operation not only increases the working time, but also increases the manufacturing cost, and has disadvantages in that the electrical conductivity is lowered by the coating material.
탄소 복합체 분리판은 탄소와 수지를 섞은 상태에서 몰딩을 통해 분리판을 제작한 연료전지용 분리판으로, 수지함침 흑연판에 비해 다소 전기 전도성 및 열전도성이 낮아질 수 있는데, 수지의 선정 및 몰딩 방법의 최적화를 통해 수지 함침 흑연판과 유사한 수준의 연료전지 성능을 구현시켜야 하는 문제가 있다.Carbon composite separator is a separator for fuel cell manufactured by molding in a state where carbon and resin are mixed. Electrical and thermal conductivity may be somewhat lower than resin-impregnated graphite plate. There is a problem in that it is necessary to realize a fuel cell performance similar to that of a resin-impregnated graphite plate through optimization.
또한, 탄소 복합체 분리판은 탄소와 레진을 섞어서 분리판을 제작하기 때문에 몰딩시 작업 시간이 길어지며, 압축 또는 사출성형을 위하여 고분자를 고열로 용융시켜야 하며, 분리판 제작 이후 채널 형성을 위한 별도의 트리밍 공정이 필요해 공정이 과도하고 비용이 증가하는 문제가 있다.In addition, since the carbon composite separator is made by mixing carbon and resin to produce the separator, the working time is lengthened during molding, and the polymer must be melted at high heat for compression or injection molding, and a separate plate for channel formation after the separator is manufactured. There is a problem in that the process is excessive and the cost increases because a trimming process is required.
특히, 이러한 분리판의 표면에는 냉각수가 순환되는 냉각수 유로가 정밀하고 복잡하게 구성되는데, 이 냉각수 유로의 제작을 위해 분리판을 일체형으로 제작하기 어려운 문제가 있다.In particular, the cooling water flow path through which the cooling water is circulated is precisely and complicatedly formed on the surface of the separation plate, and there is a problem in that it is difficult to integrally manufacture the separation plate for manufacturing the cooling water flow path.
수소연료전지에서 분리판의 비중은 계속 증가하고 있는 실정으로서, 연료전지에서 분리판이 차지하는 비용 역시 증가하고 있는 실정이므로, 분리판 제작시 시간과 비용을 절감할 수 있는 연구가 필요한 실정이다.The proportion of the separator in the hydrogen fuel cell is continuously increasing, and the cost occupied by the separator in the fuel cell is also increasing. Therefore, there is a need for research to reduce time and cost when manufacturing the separator.
본 발명은 연료전지 분리판 제조방법에 관한 것이다. The present invention relates to a method for manufacturing a fuel cell separator.
본 발명의 일 실시형태에 따르면, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련하는 단계, 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드를 마련하는 단계 및 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계를 포함하는 연료전지 분리판 제조방법을 제공한다.According to an embodiment of the present invention, the steps of preparing a carbon composite plate including a thermoplastic resin containing conductive nanomaterials, providing a mold for forming a fuel cell separator having a channel shape therein, and the carbon composite plate It provides a method for manufacturing a fuel cell separator comprising the step of preparing a fuel cell separator in which channels are integrally formed by inputting the into the mold for forming the fuel cell separator.
본 발명의 일 실시형태에 따르면, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드 내부에서 핫 프레스 공법에 의해 고온 압축함으로써, 채널이 일체로 형성된 연료전지 분리판을 용이하게 제작할 수 있다.According to an embodiment of the present invention, by high-temperature compression of a carbon composite plate including a thermoplastic resin containing conductive nanomaterials in a mold for molding a fuel cell separator having a channel shape therein by a hot press method, the channels are formed An integrally formed fuel cell separator can be easily manufactured.
특히, 본 발명의 일 실시형태에 따르면, 탄소 복합재 평판을 열가소성 수지에 탄소 재료 및 전도성 나노물질이 혼합된 형태로 제작하기 때문에, 핫 프레스 공법에 의해 분리판 제작시 낮은 온도에서 수행될 수 있으며, 재사용이 가능한 장점이 있다. In particular, according to one embodiment of the present invention, since the carbon composite plate is manufactured in the form of a mixture of a carbon material and a conductive nanomaterial in a thermoplastic resin, it can be performed at a low temperature when manufacturing a separator by a hot press method, It has the advantage of being reusable.
또한, 열가소성 수지를 포함하는 탄소 복합재 평판을 이용하기 때문에, 불량 발생시에도 재사용이 가능하므로, 시간과 비용의 절감 효과가 있다. In addition, since a carbon composite plate including a thermoplastic resin is used, it can be reused even when a defect occurs, thereby reducing time and cost.
도 1은 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법을 나타낸 공정도이다.
도 2는 도 1의 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법에 의해 제조된 연료전지 분리판을 나타낸 모식도이다. 1 is a process diagram illustrating a method for manufacturing a fuel cell separator according to an embodiment of the present invention.
FIG. 2 is a schematic diagram illustrating a fuel cell separator manufactured by the method for manufacturing a fuel cell separator according to an embodiment of the present invention of FIG. 1 .
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시 형태를 설명한다. 그러나, 본 발명의 실시 형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시 형태로 한정되는 것은 아니다. Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. However, the embodiment of the present invention may be modified in various other forms, and the scope of the present invention is not limited to the embodiments described below.
도 1은 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법을 나타낸 공정도이다. 1 is a process diagram illustrating a method for manufacturing a fuel cell separator according to an embodiment of the present invention.
도 2는 도 1의 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법에 의해 제조된 연료전지 분리판을 나타낸 모식도이다.FIG. 2 is a schematic diagram illustrating a fuel cell separator manufactured by the method for manufacturing a fuel cell separator according to an embodiment of the present invention of FIG. 1 .
도 1에 나타난 바와 같이, 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법은 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련하는 단계, 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드를 마련하는 단계 및 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계를 포함한다.As shown in FIG. 1 , the method for manufacturing a fuel cell separator according to an embodiment of the present invention includes the steps of preparing a carbon composite plate including a thermoplastic resin containing conductive nanomaterials, separating a fuel cell having a channel shape therein providing a mold for forming a plate; and inserting the carbon composite plate into the mold for forming the fuel cell separator to prepare a fuel cell separator in which a channel is integrally formed.
본 발명의 일 실시형태에 따른 연료전지 분리판을 제조하기 위하여 우선, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련한다.In order to manufacture a fuel cell separator according to an embodiment of the present invention, first, a carbon composite plate including a thermoplastic resin containing conductive nanomaterials is prepared.
상기 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련하는 방법은 특별히 제한되지 않으며, 예를 들면 반경화 시트 상태의 프리프레그 형태로 제작될 수도 있으며, 완전 경화시킨 형태로 제작될 수도 있다.The method of preparing the carbon composite plate including the thermoplastic resin containing the conductive nanomaterial is not particularly limited, and for example, it may be manufactured in the form of a semi-cured sheet prepreg, or it may be manufactured in a fully cured form. have.
구체적으로, 상기 탄소복합재 평판은 열가소성 수지를 베이스로 하여, 탄소 소재 및 전도성 나노물질로 강화된 반경화 시트 상태의 프리프레그 형태를 갖도록 제작될 수 있다.Specifically, the carbon composite plate may be manufactured to have a prepreg form in the form of a semi-hardened sheet reinforced with a carbon material and a conductive nanomaterial based on a thermoplastic resin.
상기 탄소복합재 평판을 프리프레그 형태로 제작할 경우, 통상의 방법으로 제작될 수 있으며, PE 필름 등의 이형필름이 감겨진 롤(roll)에서 이형필름을 연속적으로 공급하며, 이형필름 위로 시트 형상의 탄소 소재 및 전도성 나노 물질을 연속 투입하여 적층하고, 이어 열가소성 수지를 함침시킨다.When the carbon composite flat plate is manufactured in the form of a prepreg, it can be manufactured by a conventional method, and the release film is continuously supplied from a roll on which a release film such as a PE film is wound, and a sheet-shaped carbon on the release film The material and the conductive nanomaterial are continuously added to be laminated, and then the thermoplastic resin is impregnated.
다음으로, 소정 온도로 가열함으로써, 반경화 상태의 프리프레그 형태로 제작할 수 있으며, 롤 형태로 사용할 수 있다.Next, by heating to a predetermined temperature, it can be produced in the form of a prepreg in a semi-cured state, and can be used in the form of a roll.
다른 방법으로서는, 상기 탄소복합재 평판은 열가소성 수지에 탄소 소재 및 전도성 나노물질을 투입하여 완전 경화시킨 형태를 갖도록 제작될 수 있다.As another method, the carbon composite plate may be manufactured to have a fully cured form by adding a carbon material and a conductive nanomaterial to a thermoplastic resin.
상기 탄소복합재 평판이 완전 경화 형태로 제작될 경우에는, 열가소성 수지에 탄소 소재 및 전도성 나노물질을 투입한 이후 150 ℃ 내지 250 ℃ 정도의 온도에서 완전 경화시켜 제작할 수 있다.When the carbon composite plate is manufactured in a fully cured form, it can be manufactured by adding a carbon material and a conductive nanomaterial to a thermoplastic resin and then completely curing it at a temperature of about 150°C to 250°C.
열가소성 수지로 제작된 탄소복합재 평판은 후술하는 바와 같이, 종래의 열경화성 프리프레그와 달리 재사용이 가능하고, 완전 경화 이후에도 소정의 열을 가할 경우, 추가의 가공이 가능하기 때문에, 분리판 제조시 시간과 비용이 절감되는 효과가 있다.As will be described later, the carbon composite plate made of a thermoplastic resin can be reused, unlike conventional thermosetting prepregs, and when a predetermined heat is applied even after complete curing, additional processing is possible. It has the effect of reducing costs.
상기 탄소 소재는 일반적으로 사용되는 탄소 재료가 적용될 수 있으며, 이중에서도 보강성 및 가공성 면에서 흑연이 바람직할 수 있다. 또, 상기 흑연은 천연 흑연 또는 합성 흑연일 수 있으며, 상기 합성 흑연은 구상 또는 팽창 흑연일 수 있다.As the carbon material, a commonly used carbon material may be applied, and among them, graphite may be preferable in terms of reinforcing properties and workability. In addition, the graphite may be natural graphite or synthetic graphite, and the synthetic graphite may be spherical or expanded graphite.
상기 전도성 나노물질은 탄소나노튜브(Carbon Nano Tube, CNT), 그래핀, 흑연 및 이들의 혼합물로 이루어진 군으로부터 선택된 어느 하나 이상일 수 있으나, 반드시 이에 제한되는 것은 아니다.The conductive nanomaterial may be at least one selected from the group consisting of carbon nanotubes (CNT), graphene, graphite, and mixtures thereof, but is not necessarily limited thereto.
구체적으로, 상기 전도성 나노물질은 탄소나노튜브(Carbon Nano Tube, CNT), 그래핀, 흑연일 수 있으며, 이들 중 1종 단독 또는 2종 이상의 혼합물이 사용될 수 있다. Specifically, the conductive nanomaterial may be a carbon nanotube (CNT), graphene, or graphite, and one or a mixture of two or more thereof may be used.
상기 전도성 나노물질은 입자형, 판형, 인편상 등 그 형상이 특별히 한정되는 것은 아니지만, 1 내지 200 ㎛의 평균 입자 직경을 갖는 입자인 것이 바람직하다. 전도성 나노물질의 평균 입자 직경이 1 ㎛ 미만이면 전도성 나노물질끼리의 응집 우려가 있고, 전도성 나노물질의 평균 입자 크기가 200 ㎛를 초과하면 성형 및 기체 밀폐도가 저하될 우려가 있다.Although the shape of the conductive nanomaterial is not particularly limited, such as a particle shape, a plate shape, and a scale shape, it is preferable that the conductive nanomaterial be particles having an average particle diameter of 1 to 200 μm. If the average particle diameter of the conductive nanomaterial is less than 1 μm, there is a risk of aggregation of the conductive nanomaterials, and when the average particle size of the conductive nanomaterial exceeds 200 μm, there is a risk of lowering the degree of molding and gas sealing.
상기 전도성 나노물질의 함량은 특별히 제한되지 않으며, 예를 들어 탄소복합재 100 wt%에 대하여, 40 내지 60 wt%의 함량으로 포함될 수 있다.The content of the conductive nanomaterial is not particularly limited, and for example, may be included in an amount of 40 to 60 wt% based on 100 wt% of the carbon composite material.
상기 열가소성 수지는 특별히 제한되지 않으며, 폴리알킬렌 (예를 들면, 폴리프로필렌(Polypropylene, PP), 폴리에틸렌(Polyethylene, PE) 등), 불소계 중합체(예를 들면, 폴리비닐리덴 플루오라이드(Polyvinylidene Fluoride, PVDF) 등), 아크릴 중합체(예를 들면, 폴리메틸메타크릴레이트(Polymethyl methacrylate, PMMA) 등), 폴리카보네이트(Polycarbonate), 폴리페닐렌설파이드(Polyphenylene sulfide), 폴리에테르에테르케톤(Poly ether ether ketone) 또는 폴리에테르설폰(Polyether sulfone) 등일 수 있다.The thermoplastic resin is not particularly limited, and polyalkylene (for example, polypropylene (PP), polyethylene (PE), etc.), fluorine-based polymer (for example, polyvinylidene fluoride, PVDF), etc.), acrylic polymers (eg, polymethyl methacrylate, PMMA, etc.), polycarbonate, polyphenylene sulfide, poly ether ether ketone ) or polyether sulfone, and the like.
상기 열가소성 수지의 함량은 특별히 제한되지 않으며, 예를 들어 탄소복합재 100 wt%에 대하여, 10 내지 30 wt%의 함량으로 포함될 수 있다.The content of the thermoplastic resin is not particularly limited, and for example, may be included in an amount of 10 to 30 wt% based on 100 wt% of the carbon composite material.
다음으로, 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드를 마련하는 단계가 수행된다.Next, a step of preparing a mold for forming a fuel cell separator having a channel shape therein is performed.
상기 연료전지 분리판 성형용 몰드의 상부 및 하부 내측에는 양각의 채널 패턴이 형성될 수 있으며, 다음 단계로서, 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련한다.An embossed channel pattern may be formed on the upper and lower inner sides of the mold for forming the fuel cell separator plate, and as a next step, the carbon composite plate is put into the mold for forming the fuel cell separator plate and the channel is integrally formed. Prepare a battery separator.
본 발명의 일 실시형태에 따르면, 상기 연료전지 분리판 성형용 몰드의 상부 및 하부 내측에 양각의 채널 패턴을 미리 형성하고, 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 핫 프레스 또는 마이크로웨이브 성형 공정 등에 의해 채널이 일체로 형성된 연료전지 분리판을 제작할 수 있다.According to an embodiment of the present invention, embossed channel patterns are formed in advance on the upper and lower inner sides of the mold for forming the fuel cell separator plate, and the carbon composite plate is put into the mold for forming the fuel cell separator plate by hot pressing. Alternatively, a fuel cell separator in which channels are integrally formed by a microwave molding process or the like may be manufactured.
특히, 본 발명의 일 실시형태에서는 상기 탄소복합재 평판이 열가소성 수지를 포함하여 제작되기 때문에, 낮은 온도에서도 채널이 일체로 형성된 연료전지 분리판을 제작할 수 있으며, 열가소성 수지의 특성으로 인해 종래 열경화성 수지를 포함하는 프리프레그와 달리 재사용이 가능한 장점이 있다.In particular, in one embodiment of the present invention, since the carbon composite plate is manufactured including a thermoplastic resin, a fuel cell separator in which a channel is integrally formed can be manufactured even at a low temperature, and due to the characteristics of the thermoplastic resin, conventional thermosetting resin It has the advantage of being reusable unlike the prepreg it contains.
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계는 핫 프레스 공법으로 수행될 수 있다.The step of preparing the fuel cell separator in which the channel is integrally formed may be performed by a hot press method.
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계가 핫 프레스 공법으로 수행될 경우, 50 ℃ 내지 150 ℃의 온도에서 수행될 수 있다.When the step of preparing the fuel cell separator in which the channel is integrally formed is performed by a hot press method, it may be performed at a temperature of 50°C to 150°C.
본 발명의 일 실시형태에 따르면, 상기 탄소복합재 평판이 열가소성 수지를 포함하여 제작되기 때문에, 상기 열가소성 수지가 경화될 수 있는 온도와 압력만 제공되면, 채널이 일체로 형성된 연료전지 분리판을 제작할 수 있기 때문에, 50 ℃ 내지 150 ℃의 온도에서 수행될 수 있다.According to one embodiment of the present invention, since the carbon composite plate is manufactured including the thermoplastic resin, if only the temperature and pressure at which the thermoplastic resin can be cured are provided, a fuel cell separator in which the channel is integrally formed can be manufactured. Therefore, it can be carried out at a temperature of 50 ℃ to 150 ℃.
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계가 50 ℃ 미만에서 수행될 경우, 미경화로 인하여 불량이 발생할 수 있다.When the step of preparing the fuel cell separator in which the channel is integrally formed is performed at less than 50° C., defects may occur due to non-curing.
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계는 150 ℃의 온도를 초과하여 수행될 수도 있으나, 고온에서 수행할 경우 고비용이 발생할 수 있으며, 분리판의 치수 변형의 문제가 생길 수 있어, 150 ℃ 이하의 온도에서 수행되는 것이 바람직하다.The step of preparing the fuel cell separator in which the channel is integrally formed may be performed exceeding a temperature of 150 ° C. However, if it is performed at a high temperature, high cost may occur, and a problem of dimensional deformation of the separator may occur, It is preferably carried out at a temperature of 150° C. or lower.
핫프레스 공법에서 인가되는 압력은 특별히 제한되는 것은 아니며, 예를 들어 500 kg/cm2 ~ 30,000 kg/cm2 조건에서 수행될 수 있다.The pressure applied in the hot press method is not particularly limited, and for example, 500 kg/cm 2 to 30,000 kg/cm 2 may be performed under conditions.
본 발명의 일 실시형태에 따르면, 상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계는 마이크로웨이브 공법으로 수행될 수도 있다.According to an embodiment of the present invention, the step of preparing the fuel cell separator in which the channel is integrally formed may be performed by a microwave method.
본 발명의 일 실시형태에 따르면, 상기 탄소복합재 평판이 열가소성 수지를 포함하여 제작되기 때문에, 연료전지 분리판 제작시 고온 및 과도한 압력이 요구되는 것이 아니므로, 마이크로웨이브 공법으로 수행될 수도 있다.According to an embodiment of the present invention, since the carbon composite plate is manufactured by including a thermoplastic resin, high temperature and excessive pressure are not required when manufacturing the fuel cell separator, and thus it may be performed by the microwave method.
본 발명의 일 실시형태에 따르면, 종래 열경화성 수지를 포함하는 프리프레그와 달리 열가소성 수지를 포함하는 탄소복합재를 이용하여 연료전지 분리판을 제조하기 때문에, 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계가 마이크로웨이브 공법으로 수행될 수 있다는 점에 특징이 있다.According to an embodiment of the present invention, since the fuel cell separator is manufactured using a carbon composite including a thermoplastic resin, unlike a conventional prepreg including a thermosetting resin, the carbon composite plate is used for molding the fuel cell separator. It is characterized in that the step of providing the fuel cell separator in which the channel is integrally formed by being put into the mold can be performed by the microwave method.
상기 마이크로웨이브 공법은 2000 MHz 이상의 마이크로웨이브(전자기파)를 조사하여, 열가소성 수지를 포함하는 탄소 복합재가 경화되며, 상기 마이크로웨이브에 의해 상기 열가소성 수지의 화학 반응을 유도하여 경화가 일어나게 된다.The microwave method is irradiated with a microwave (electromagnetic wave) of 2000 MHz or higher, the carbon composite material including the thermoplastic resin is cured, and curing occurs by inducing a chemical reaction of the thermoplastic resin by the microwave.
특히, 자기 공명 흡수에 의한 자체 발열로 인하여, 상기 열가소성 수지의 화학 반응을 유도하며, 이로써 열가소성 수지를 포함하는 탄소 복합재가 경화되며, 채널이 일체로 형성된 연료전지 분리판을 제작할 수 있다.In particular, due to self-heating due to magnetic resonance absorption, a chemical reaction of the thermoplastic resin is induced, whereby the carbon composite material including the thermoplastic resin is cured, and a fuel cell separator in which a channel is integrally formed can be manufactured.
본 발명의 일 실시형태와 같이, 상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계가 마이크로웨이브 공법으로 수행될 경우, 고온 및 고압 공정이 필요하지 않아 시간과 비용 절감의 효과가 있다.As in one embodiment of the present invention, when the step of preparing the fuel cell separator in which the channel is integrally formed by putting the carbon composite plate into the mold for forming the fuel cell separator is performed by the microwave method, high temperature and high pressure Since no process is required, there is an effect of saving time and cost.
본 발명의 일 실시형태에 따르면, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드 내부에서 핫 프레스 공법 또는 마이크로웨이브 공법에 의해 고온 압축함으로써, 채널이 일체로 형성된 연료전지 분리판을 용이하게 제작할 수 있다.According to an embodiment of the present invention, a carbon composite flat plate including a thermoplastic resin containing conductive nanomaterials is compressed at a high temperature by a hot press method or a microwave method in a mold for molding a fuel cell separator having a channel shape therein. By doing so, the fuel cell separator in which the channel is integrally formed can be easily manufactured.
특히, 본 발명의 일 실시형태에 따르면, 탄소 복합재 평판을 열가소성 수지에 탄소 재료 및 전도성 나노물질이 혼합된 형태로 제작하기 때문에, 핫 프레스 공법 또는 마이크로웨이브 공법에 의해 분리판 제작시 낮은 온도에서 수행될 수 있으며, 재사용이 가능한 장점이 있다. In particular, according to an embodiment of the present invention, since the carbon composite plate is manufactured in a form in which a carbon material and a conductive nanomaterial are mixed in a thermoplastic resin, the separation plate is manufactured by the hot press method or the microwave method at a low temperature. It can be used and has the advantage of being reusable.
또한, 열가소성 수지를 포함하는 탄소 복합재 평판을 이용하기 때문에, 불량 발생시에도 재사용이 가능하므로, 시간과 비용의 절감 효과가 있다. In addition, since a carbon composite plate including a thermoplastic resin is used, it can be reused even when a defect occurs, thereby reducing time and cost.
도 2는 도 1의 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법에 의해 제조된 연료전지 분리판을 나타낸 모식도이다.FIG. 2 is a schematic diagram illustrating a fuel cell separator manufactured by the method for manufacturing a fuel cell separator according to an embodiment of the present invention of FIG. 1 .
도 2를 참조하면, 본 발명의 일 실시형태에 따른 연료전지 분리판 제조방법에 의해 제조된 연료전지 분리판(100)은 탄소복합재 평판을 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드에 투입하여 채널(110)이 일체로 형성된 구조를 갖는다.Referring to FIG. 2 , the
즉, 본 발명의 일 실시형태에 따르면, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드 내부에서 핫 프레스 공법 또는 마이크로웨이브 공법에 의해 고온 압축함으로써, 채널이 일체로 형성된 연료전지 분리판을 용이하게 제작할 수 있다.That is, according to an embodiment of the present invention, a carbon composite plate including a thermoplastic resin containing conductive nanomaterials is formed in a mold for forming a fuel cell separator having a channel shape therein by a hot press method or a microwave method. By high-temperature compression, a fuel cell separator in which channels are integrally formed can be easily manufactured.
특히, 본 발명의 일 실시형태에 따르면, 탄소 복합재 평판을 열가소성 수지에 탄소 재료 및 전도성 나노물질이 혼합된 형태로 제작하기 때문에, 핫 프레스 공법 또는 마이크로웨이브 공법에 의해 분리판 제작시 낮은 온도에서 수행될 수 있으며, 재사용이 가능한 장점이 있다. In particular, according to an embodiment of the present invention, since the carbon composite plate is manufactured in a form in which a carbon material and a conductive nanomaterial are mixed in a thermoplastic resin, the separation plate is manufactured by the hot press method or the microwave method at a low temperature. It can be used and has the advantage of being reusable.
또한, 열가소성 수지를 포함하는 탄소 복합재 평판을 이용하기 때문에, 불량 발생시에도 재사용이 가능하므로, 시간과 비용의 절감 효과가 있다.In addition, since a carbon composite material flat plate containing a thermoplastic resin is used, it can be reused even when a defect occurs, thereby reducing time and cost.
이하 본 발명의 실시예에 따라 본 발명을 보다 구체적으로 설명하나 이에 제한되는 것은 아니다.Hereinafter, the present invention will be described in more detail according to embodiments of the present invention, but the present invention is not limited thereto.
본 발명의 일 실시형태에 따른 채널이 일체로 형성된 연료전지 분리판을 제조하기 위하여 우선, 전도성 나노물질이 함유된 열가소성 수지를 포함하는 탄소복합재 평판을 마련한다.In order to manufacture the fuel cell separator in which the channel is integrally formed according to an embodiment of the present invention, first, a carbon composite plate including a thermoplastic resin containing conductive nanomaterials is prepared.
구체적으로, 탄소 소재로서, 탄소 섬유 10 wt%, 전도성 나노물질로서, 탄소나노튜브 60wt%의 혼합재를 폴리프로필렌 재질 열가소성 수지 필름 30 wt%에 함침시킨 후 탄소 복합재 평판을 마련하였다. Specifically, as a carbon material, 10 wt% of carbon fiber, and as a conductive nanomaterial, a mixture of 60 wt% of carbon nanotubes was impregnated into 30 wt% of a polypropylene thermoplastic resin film, and then a carbon composite plate was prepared.
다음으로, 상부 금형과 하부 금형 내측에 양각의 채널 패턴이 형성된 연료전지 분리판 성형용 몰드를 제작하고, 상기 탄소 복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입한다.Next, a mold for forming a fuel cell separator in which an embossed channel pattern is formed inside the upper mold and the lower mold is manufactured, and the carbon composite plate is put into the mold for forming the fuel cell separator.
다음으로, 온도 150 ℃ 및 압력 1000 kg/cm2의 조건에서 핫 프레스 공법을 적용하여 상기 열가소성 수지 포함 탄소 복합재 평판을 성형한다. Next, by applying a hot press method under the conditions of a temperature of 150 ℃ and a pressure of 1000 kg / cm 2 to mold the carbon composite material including the thermoplastic resin flat plate.
이로써, 상기 열가소성 수지 포함 탄소 복합재 평판을 이용하여 채널이 일체로 형성된 연료전지 분리판을 제작하였다.Thus, a fuel cell separator in which a channel is integrally formed was manufactured using the carbon composite material plate including the thermoplastic resin.
본 발명의 일 실시형태에 따르면, 탄소 복합재 평판을 열가소성 수지에 탄소 재료 및 전도성 나노물질이 혼합된 형태로 제작하기 때문에, 핫 프레스 공법에 의해 분리판 제작시 낮은 온도에서 수행될 수 있으며, 재사용이 가능한 장점이 있다. According to an embodiment of the present invention, since the carbon composite plate is manufactured in a form in which a carbon material and a conductive nanomaterial are mixed in a thermoplastic resin, it can be performed at a low temperature when the separator is manufactured by the hot press method, and reuse is not possible. There are possible advantages.
또한, 열가소성 수지를 포함하는 탄소 복합재 평판을 이용하기 때문에, 불량 발생시에도 재사용이 가능하므로, 시간과 비용의 절감 효과가 있다.In addition, since a carbon composite plate including a thermoplastic resin is used, it can be reused even when a defect occurs, thereby reducing time and cost.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고, 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 수정 및 변형이 가능하다는 것은 당 기술분야의 통상의 지식을 가진 자에게는 자명할 것이다.Although the embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and variations are possible within the scope without departing from the technical spirit of the present invention described in the claims. It will be apparent to those of ordinary skill in the art.
100: 연료전지 분리판
110: 채널100: fuel cell separator
110: channel
Claims (5)
내부에 채널 형상을 갖는 연료전지 분리판 성형용 몰드를 마련하는 단계; 및
상기 탄소복합재 평판을 상기 연료전지 분리판 성형용 몰드에 투입하여 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계를 포함하되,
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계는 핫 프레스 공법으로 수행되고,
상기 채널이 일체로 형성된 연료전지 분리판을 마련하는 단계는 마이크로웨이브 공법으로 수행되되,
상기 탄소복합재 평판을 마련하는 단계는,
탄소 소재로서, 탄소 섬유 10 wt%, 전도성 나노물질로서, 탄소나노튜브 60wt%의 혼합재를 폴리프로필렌 재질 열가소성 수지 필름 30 wt%에 함침시킨 후 탄소 복합재 평판을 마련하고,
온도 150 ℃ 및 압력 1000 kg/cm2의 조건에서 핫 프레스 공법을 적용하여 상기 열가소성 수지 포함 탄소 복합재 평판을 성형하는 것을 특징으로 하는 연료전지 분리판 제조방법.
preparing a carbon composite plate including a thermoplastic resin containing conductive nanomaterials;
providing a mold for forming a fuel cell separator having a channel shape therein; and
Preparing a fuel cell separator in which the channel is integrally formed by putting the carbon composite plate into a mold for forming the fuel cell separator;
The step of preparing the fuel cell separator in which the channel is integrally formed is performed by a hot press method,
The step of preparing the fuel cell separator in which the channel is integrally formed is performed by a microwave method,
The step of preparing the carbon composite flat plate,
As a carbon material, 10 wt% of carbon fiber, as a conductive nanomaterial, a mixture of 60 wt% of carbon nanotubes was impregnated into 30 wt% of a polypropylene thermoplastic resin film, and then a carbon composite plate was prepared,
A method for manufacturing a fuel cell separator, characterized in that the carbon composite plate containing the thermoplastic resin is molded by applying a hot press method at a temperature of 150° C. and a pressure of 1000 kg/cm 2 .