KR102291015B1 - Vehicle descaling composition and its manufacturing method - Google Patents
Vehicle descaling composition and its manufacturing method Download PDFInfo
- Publication number
- KR102291015B1 KR102291015B1 KR1020200181959A KR20200181959A KR102291015B1 KR 102291015 B1 KR102291015 B1 KR 102291015B1 KR 1020200181959 A KR1020200181959 A KR 1020200181959A KR 20200181959 A KR20200181959 A KR 20200181959A KR 102291015 B1 KR102291015 B1 KR 102291015B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- vehicle
- present
- lime
- contamination
- Prior art date
Abstract
Description
아래 실시예들은 차량 석회 제거용 조성물 및 이의 제조방법에 관한 것이다.Examples below relate to a vehicle decalcification composition and a method for manufacturing the same.
노후된 아파트와 같은 건물로부터 발생되는 낙숫물로 인해 주차된 자동차의 피해가 발생되고 있다. 노후된 건물로부터 떨어지는 낙숫물에는 시멘트 가루와 같은 석회 성분, 페인트 가루, 철분, 타르 등이 포함되어 있는데, 이는 자동차 도장면에 심한 오염뿐만 아니라 상당한 손상을 일으키며 차량 내부로 침투할 경우 전자제품의 오작동을 유발할 위험성이 있다. Damage to parked cars is caused by dripping water from buildings such as old apartments. The dripping water from old buildings contains lime components such as cement powder, paint powder, iron, tar, etc., which cause significant damage as well as serious pollution to the car paint surface. There is a risk.
자동차의 외장, 도장 관련 조성물에 대한 종래 기술로서는 한국공개특허공보 제10-2019-0107870호의 유리막 코팅을 위한 전처리 조성물 및 이를 사용하는 자동차 외장에 대한 유리막 코팅 방법, 한국공개특허공보 제10-1999-0039956호의 연마기능을 갖는 자동차용 세척 및 광택제 조성물 등이 있으나, 차량 도장의 석회수로 인한 오염, 얼룩에 특화된 특허 기술은 없는 실정이다. As a prior art for automobile exterior and painting-related compositions, the pretreatment composition for glass film coating of Korean Patent Application Laid-Open No. 10-2019-0107870 and a glass film coating method for automobile exterior using the same, Korean Patent Application Laid-Open No. 10-1999- Although there is a cleaning and polishing agent composition for automobiles with abrasive function of No. 0039956, there is no patented technology specialized for contamination and stains caused by lime water on vehicle paints.
이러한 석회물로 인한 오염은 단순한 세차로는 제거가 어렵다. 인터넷 블로그 등에는 석회수 오염을 제거할 수 있는 방법으로서 티슈와 식초를 이용한 방법이 기재되어 있으나, 식초를 티슈나 휴지에 적신 후 오염된 부분 각각에 넓게 붙여야 하고 석회성분이 녹아 나올 때까지 상당한 시간을 기다려야 한다는 불편함이 있다. 한편, 자동차 도장면의 석회 물질 등의 오염 성분을 제거하기 위해 스크리퍼, 컴파운드 포함 용액, 광택제, 기스제 등이 사용되고 있으나 가격이 비싸고 환경 오염 가능성이 있다는 문제가 있다.Contamination caused by such lime is difficult to remove with a simple car wash. Internet blogs and the like describe a method using tissue and vinegar as a method to remove limewater contamination, but after soaking the tissue or tissue in vinegar, apply it to each contaminated area and take a considerable amount of time until the lime component dissolves. It is inconvenient to have to wait. On the other hand, a scraper, a compound containing solution, a polish, a grease agent, etc. are used in order to remove contaminants such as lime material from the car paint surface, but there is a problem that the price is high and there is a possibility of environmental pollution.
본 발명은 전해수, 염화수소, 아세트산을 포함하는, 차량 도장면의 석회 오염 제거용 조성물을 제공하고자 한다.An object of the present invention is to provide a composition for removing lime contamination from a vehicle paint surface, including electrolyzed water, hydrogen chloride, and acetic acid.
본 발명의 상기 및 다른 목적과 이점은 바람직한 실시예를 설명한 하기의 설명으로부터 분명해질 것이다.These and other objects and advantages of the present invention will become apparent from the following description of preferred embodiments.
상기 목적은, 전해수, 염화수소, 아세트산을 포함하는, 차량 도장면의 석회 오염 제거용 조성물에 의해 달성될 수 있다.The above object, including electrolyzed water, hydrogen chloride, acetic acid, can be achieved by a composition for removing lime stains from a vehicle paint surface.
구체적으로, 상기 전해수, 염화수소, 아세트산은 30 : 15 : 15의 중량비로 혼합된 것을 특징으로 하는 것일 수 있다.Specifically, the electrolyzed water, hydrogen chloride, and acetic acid may be mixed in a weight ratio of 30:15:15.
구체적으로, 상기 조성물은 5.5 내지 6.5의 pH를 갖는 것일 수 있다.Specifically, the composition may have a pH of 5.5 to 6.5.
구체적으로, 상기 조성물은 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소를 추가로 포함하는 것일 수 있다.Specifically, the composition may further include sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, and silicon dioxide.
구체적으로, 상기 조성물은 지황 추출물, 복령 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올, 락토바실러스 파라파라지니스 배양액 및 락토바실러스 플란타럼 배양액을 추가로 포함하는 것일 수 있다.Specifically, the composition may be one that further comprises a rehmannia extract, bokryeong extract, phenoxyethanol, sodium citrate, sodium phosphate, propanediol, Lactobacillus paraparagini culture medium and Lactobacillus plantarum culture medium.
본 발명에 따른 조성물은 차량 도장면의 석회 등 오염물질을 빠른 시간 내에 효과적으로 제거하면서도 도장면의 손상을 방지할 수 있다. 또한 본 발명의 제조방법은 여러 화합물과 천연 유래 추출물을 적절한 공정으로 조합하여 제조함으로써 효과가 우수한 차량 도장면의 석회 오염 제거용 조성물을 제조할 수 있다.The composition according to the present invention can effectively remove contaminants such as lime from the paint surface of a vehicle in a short time while preventing damage to the paint surface. In addition, the manufacturing method of the present invention can prepare a composition for removing lime contamination of a vehicle paint surface with excellent effect by preparing a combination of various compounds and a naturally-derived extract in an appropriate process.
다만, 본 발명의 효과들은 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the effects of the present invention are not limited to the above-mentioned effects, and other effects not mentioned will be clearly understood by those skilled in the art from the following description.
도 1은 일 실시예에 따른, 석회 오염 제거용 조성물을 차량 도장면의 석회 오염 물질에 처리하여 세척한 경우의 세척 효과에 관한 것이다.1 relates to a cleaning effect when the composition for removing lime contamination according to an embodiment is treated and washed with lime pollutants on a vehicle painted surface.
이하에서, 첨부된 도면을 참조하여 실시예들을 상세하게 설명한다. 그러나, 실시예들에는 다양한 변경이 가해질 수 있어서 특허출원의 권리 범위가 이러한 실시예들에 의해 제한되거나 한정되는 것은 아니다. 실시예들에 대한 모든 변경, 균등물 내지 대체물이 권리 범위에 포함되는 것으로 이해되어야 한다.Hereinafter, embodiments will be described in detail with reference to the accompanying drawings. However, since various changes may be made to the embodiments, the scope of the patent application is not limited or limited by these embodiments. It should be understood that all modifications, equivalents and substitutes for the embodiments are included in the scope of the rights.
실시예들에 대한 특정한 구조적 또는 기능적 설명들은 단지 예시를 위한 목적으로 개시된 것으로서, 다양한 형태로 변경되어 실시될 수 있다. 따라서, 실시예들은 특정한 개시형태로 한정되는 것이 아니며, 본 명세서의 범위는 기술적 사상에 포함되는 변경, 균등물, 또는 대체물을 포함한다.Specific structural or functional descriptions of the embodiments are disclosed for purposes of illustration only, and may be changed and implemented in various forms. Accordingly, the embodiments are not limited to a specific disclosure form, and the scope of the present specification includes changes, equivalents, or substitutes included in the technical spirit.
제1 또는 제2 등의 용어를 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이런 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 해석되어야 한다. 예를 들어, 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소는 제1 구성요소로도 명명될 수 있다.Although terms such as first or second may be used to describe various components, these terms should be interpreted only for the purpose of distinguishing one component from another. For example, a first component may be termed a second component, and similarly, a second component may also be termed a first component.
어떤 구성요소가 다른 구성요소에 "연결되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다.When a component is referred to as being “connected to” another component, it may be directly connected or connected to the other component, but it should be understood that another component may exist in between.
실시예에서 사용한 용어는 단지 설명을 목적으로 사용된 것으로, 한정하려는 의도로 해석되어서는 안된다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terms used in the examples are used for description purposes only, and should not be construed as limiting. The singular expression includes the plural expression unless the context clearly dictates otherwise. In the present specification, terms such as “comprise” or “have” are intended to designate that a feature, number, step, operation, component, part, or combination thereof described in the specification exists, but one or more other features It should be understood that this does not preclude the existence or addition of numbers, steps, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 실시예가 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which the embodiment belongs. Terms such as those defined in commonly used dictionaries should be interpreted as having a meaning consistent with the meaning in the context of the related art, and should not be interpreted in an ideal or excessively formal meaning unless explicitly defined in the present application. does not
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.Advantages and features of the present invention and methods of achieving them will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in a variety of different forms, and only these embodiments allow the disclosure of the present invention to be complete, and common knowledge in the technical field to which the present invention belongs It is provided to fully inform the possessor of the scope of the invention, and the present invention is only defined by the scope of the claims.
본 발명의 실시예들에서, 별도로 다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 발명의 실시예에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.In the embodiments of the present invention, unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which the present invention belongs. have meaning Terms such as those defined in a commonly used dictionary should be interpreted as having a meaning consistent with the meaning in the context of the related art, and unless explicitly defined in an embodiment of the present invention, an ideal or excessively formal meaning is not interpreted as
본 발명의 실시예를 설명하기 위한 도면에 개시된 형상, 크기, 비율, 각도, 개수 등은 예시적인 것이므로 본 발명이 도시된 사항에 한정되는 것은 아니다. 또한, 본 발명을 설명함에 있어서, 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명은 생략한다. 본 명세서 상에서 언급된 '포함한다', '갖는다', '이루어진다' 등이 사용되는 경우 '~만'이 사용되지 않는 이상 다른 부분이 추가될 수 있다. 구성 요소를 단수로 표현한 경우에 특별히 명시적인 기재 사항이 없는 한 복수를 포함하는 경우를 포함한다.The shapes, sizes, proportions, angles, numbers, etc. disclosed in the drawings for explaining the embodiments of the present invention are exemplary, and thus the present invention is not limited to the illustrated matters. In addition, in describing the present invention, if it is determined that a detailed description of a related known technology may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted. When 'including', 'having', 'consisting', etc. mentioned in this specification are used, other parts may be added unless 'only' is used. When a component is expressed in the singular, the case in which the plural is included is included unless otherwise explicitly stated.
구성 요소를 해석함에 있어서, 별도의 명시적 기재가 없더라도 오차 범위를 포함하는 것으로 해석한다.In interpreting the components, it is interpreted as including an error range even if there is no separate explicit description.
도면에서 나타난 각 구성의 크기 및 두께는 설명의 편의를 위해 도시된 것이며, 본 발명이 도시된 구성의 크기 및 두께에 반드시 한정되는 것은 아니다.The size and thickness of each component shown in the drawings are illustrated for convenience of description, and the present invention is not necessarily limited to the size and thickness of the illustrated component.
본 발명의 여러 실시예들의 각각 특징들이 부분적으로 또는 전체적으로 서로 결합 또는 조합 가능하며, 당업자가 충분히 이해할 수 있듯이 기술적으로 다양한 연동 및 구동이 가능하며, 각 실시예들이 서로에 대하여 독립적으로 실시 가능할 수도 있고 연관 관계로 함께 실시 가능할 수도 있다.Each feature of the various embodiments of the present invention may be partially or wholly combined or combined with each other, and technically various interlocking and driving are possible, as will be fully understood by those skilled in the art, and each embodiment may be independently implemented with respect to each other, It may be possible to implement together in a related relationship.
본 발명의 일 측면은, 전해수, 염화수소, 아세트산을 포함하는, 차량 도장면의 석회 오염 제거용 조성물을 제공한다.One aspect of the present invention provides a composition for removing lime stains from a vehicle paint surface, comprising electrolyzed water, hydrogen chloride, and acetic acid.
일 실시예에 있어서, 상기 전해수, 이온수는 물에 전기를 가하여 얻어지는 물로, 산성이온수와 알칼리이온수를 모두 포함하나 구체적으로는 알칼리이온수일 수 있다. 전해수는 석회 오염 세척을 위한 물질들의 용해와 조성물의 pH 조절에 필요하다.In an embodiment, the electrolyzed water and ionized water are water obtained by applying electricity to water, and include both acidic ionized water and alkaline ionized water, but may specifically be alkaline ionized water. Electrolyzed water is necessary for dissolving substances for cleaning lime contamination and for adjusting the pH of the composition.
일 실시예에 있어서, 상기 전해수, 염화수소, 아세트산은 30 : 15 : 15의 중량비로 혼합된 것을 특징으로 하는 것일 수 있다. 염화수소, 아세트산은 모두 산성 물질로서 적절한 중량비로 포함되지 않으면 pH가 지나치게 낮아지거나 세척 효과가 감소될 수 있다.In an embodiment, the electrolyzed water, hydrogen chloride, and acetic acid may be mixed in a weight ratio of 30:15:15. Hydrogen chloride and acetic acid are both acidic substances, and if they are not included in an appropriate weight ratio, the pH may become excessively low or the washing effect may be reduced.
일 실시예에 있어서, 상기 아세트산은 양조식초로부터 유래된 것일 수 있고, 상기 조성물은 양조식초를 추가로 포함할 수 있다.In one embodiment, the acetic acid may be derived from brewed vinegar, and the composition may further include brewed vinegar.
일 실시예에 있어서, 상기 조성물은 5.5 내지 6.5의 pH를 갖는 것일 수 있다. 본 발명의 차량 도장면의 석회 오염 제거용 조성물은 적절한 약산성~중성의 pH를 가짐으로써 사용자의 안전을 보호하면서도 효율적으로 석회 오염물질을 제거, 세척할 수 있다.In one embodiment, the composition may have a pH of 5.5 to 6.5. The composition for removing lime contamination of a vehicle paint surface of the present invention can efficiently remove and wash lime contaminants while protecting the user's safety by having an appropriate slightly acidic to neutral pH.
일 실시예에 있어서, 상기 조성물은 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소를 추가로 포함하는 것일 수 있다. 또한, 상기 조성물은 지황 추출물, 복령 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올, 락토바실러스 파라파라지니스 배양액 및 락토바실러스 플란타럼 배양액을 추가로 포함하는 것일 수 있다. 이는 본 발명의 조성물이 차량 도장면에 단단하게 굳은 석회수 오염 물질을 효율적으로 용해, 제거하는 데에 도움을 줄 수 있는 물질로서, 본 발명의 조성물에 추가적으로 첨가될 수 있다. 상기 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소는 차량 도장면의 석회 오염 제거용 조성물 전체 중량 대비 각각 1 내지 5, 0.5 내지 3, 0.1 내지 2 중량%로 포함되는 것일 수 있고, 지황 추출물, 복령 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올, 락토바실러스 파라파라지니스 배양액 및 락토바실러스 플란타럼 배양액은 각각 차량 도장면의 석회 오염 제거용 조성물 전체 중량 대비 7 내지 9, 7 내지 9, 3 내지 6, 0.1 내지 3, 0.5 내지 1, 10 내지 15, 0.1 내지 5, 0.1 내지 5의 중량%로 포함되는 것일 수 있다. 각 물질의 중량%가 상기 범위를 넘어설 경우 석회 오염물질 제거 효과가 낮아지고 안정성에 문제가 있을 수 있다.In one embodiment, the composition may further include sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, and silicon dioxide. In addition, the composition may be one that further comprises a rehmannia extract, bokryeong extract, phenoxyethanol, sodium citrate, sodium phosphate, propanediol, Lactobacillus paraparagini culture medium and Lactobacillus plantarum culture medium. This is a material that can help the composition of the present invention efficiently dissolve and remove limewater contaminants that are hardened on the vehicle paint surface, and may be additionally added to the composition of the present invention. The sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, and silicon dioxide may be included in an amount of 1 to 5, 0.5 to 3, and 0.1 to 2% by weight, respectively, based on the total weight of the composition for removing lime contamination on a vehicle paint surface. In addition, Rehmannia Root extract, Bokryeong extract, phenoxyethanol, sodium citrate, sodium phosphate, propanediol, Lactobacillus paraparagini culture medium, and Lactobacillus plantarum culture medium are respectively compared to the total weight of the composition for removing lime contamination of vehicle paint surfaces 7 to 9, 7 to 9, 3 to 6, 0.1 to 3, 0.5 to 1, 10 to 15, 0.1 to 5, may be included in an amount of 0.1 to 5 by weight. When the weight % of each material exceeds the above range, the effect of removing lime contaminants is lowered and there may be a problem in stability.
일 실시예에 있어서, 상기 조성물은 바인더, 점증제, 계면활성제, 유화제, 코팅제 연마제, 분산제를 추가로 포함할 수 있다.In one embodiment, the composition may further include a binder, a thickener, a surfactant, an emulsifier, an abrasive coating agent, and a dispersant.
일 실시예에 있어서, 상기 조성물은 이소파라핀, 옥사이드, 왁스, 아민 옥사이드, 설팜산, 토르마린, 질산 은, 과산화수소 및 유기 카복시산을 추가로 포함할 수 있다.In one embodiment, the composition may further include isoparaffin, oxide, wax, amine oxide, sulfamic acid, tourmaline, silver nitrate, hydrogen peroxide and organic carboxylic acid.
본 발명의 다른 일 측면은, 차량 도장면의 석회 오염 제거용 조성물의 제조방법을 제공한다.Another aspect of the present invention provides a method for preparing a composition for removing lime contamination from a vehicle painted surface.
상기 제조방법의 각 단계, 유효물질 등의 구성에 대해서는 상술한 바와 같다.Each step of the manufacturing method, the composition of the active material, etc. are as described above.
일 실시예에 있어서, 전해수, 염화수소, 아세트산을 30 : 15 : 15의 중량비로 혼합하는 단계; 상기 혼합물의 온도를 30 ~ 35℃로 30~60분 간 유지하는 단계; 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소를 조성물 전체 중량 대비 각각 1 내지 5, 0.5 내지 3, 0.1 내지 2 중량%로 첨가하는 단계; 지황 추출물, 복령 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올을 조성물 전체 중량 대비 7 내지 9, 7 내지 9, 3 내지 6, 0.1 내지 3, 0.5 내지 1, 10 내지 15로 첨가하는 단계; 및 밀폐된 용기에 보관하는 단계;를 포함하는 차량 도장면의 석회 오염 제거용 조성물의 제조방법을 제공한다.In one embodiment, electrolyzed water, hydrogen chloride, and acetic acid 30: 15: mixing the weight ratio of 15; maintaining the temperature of the mixture at 30 to 35° C. for 30 to 60 minutes; adding sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, and silicon dioxide in an amount of 1 to 5, 0.5 to 3, and 0.1 to 2% by weight, respectively, based on the total weight of the composition; Rehmannia glutinosa extract, bokryeong extract, phenoxyethanol, sodium citrate, sodium phosphate, and propanediol are added in an amount of 7 to 9, 7 to 9, 3 to 6, 0.1 to 3, 0.5 to 1, 10 to 15 based on the total weight of the composition. to do; and storing in a sealed container; provides a method for producing a composition for removing lime contamination from a vehicle painted surface, including.
일 실시예에 있어서, 상기 차량 도장면의 석회 오염 제거용 조성물의 제조방법은 상기 지황 추출물 등의 첨가 이후, 락토바실러스 파라파라지니스 배양액 및 락토바실러스 플란타럼 배양액을 조성물 전체 중량 대비 0.1 내지 5, 0.1 내지 5의 중량%로 첨가하는 단계를 포함할 수 있다. 이러한 미생물 배양액이 미량 포함됨으로써 견고하게 굳은 석회 오염 물질을 효과적으로 제거할 수 있다.In one embodiment, the method for preparing the composition for removing lime contamination from the vehicle paint surface is after the addition of the rehmannia glutinosa extract, etc., Lactobacillus paraparaginis culture solution and Lactobacillus plantarum culture solution 0.1 to 5, relative to the total weight of the composition, It may include adding in an amount of 0.1 to 5% by weight. By containing a trace amount of such a microbial culture solution, it is possible to effectively remove the solidified lime contaminants.
이하, 구체적인 실시예와 비교예를 통하여 본 발명의 구성 및 그에 따른 효과를 보다 상세히 설명하고자 한다. 그러나, 본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.Hereinafter, the configuration of the present invention and its effects will be described in more detail through specific examples and comparative examples. However, these examples are for explaining the present invention in more detail, and the scope of the present invention is not limited to these examples.
제조예 1: 차량 석회 제거용 조성물의 제조Preparation Example 1: Preparation of a composition for vehicle descaling
전해수, 염화수소, 아세트산 용액을 30 : 15 : 15의 중량비로 준비하여 교반기에 첨가 후 혼합하였다. 혼합물이 균일하게 안정화될 수 있도록 30 ~ 35℃로 40분 간 유지시켰다. 이후, 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소 분말을 전체 조성물 대비 각각 각각 3, 2, 1 중량%로 첨가하였다. Electrolyzed water, hydrogen chloride, and acetic acid solution were prepared in a weight ratio of 30:15:15, added to a stirrer, and then mixed. The mixture was maintained at 30-35° C. for 40 minutes to be uniformly stabilized. Thereafter, sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, and silicon dioxide powder were added in an amount of 3, 2, and 1 wt%, respectively, based on the total composition, respectively.
상기 첨가물이 고르게 혼합된 이후, 지황 에탄올 추출물, 복령 에탄올 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올을 조성물 전체 중량 대비 각각 8, 8, 5, 2, 1, 12 중량%로 추가로 첨가하였다.After the additives are evenly mixed, 8, 8, 5, 2, 1, 12% by weight of each of Rehmannia ethanol extract, Bokryeong ethanol extract, phenoxyethanol, sodium citrate, sodium phosphate, and propanediol based on the total weight of the composition further added.
락토바실러스 파라파라지니스(Lactobacillus parafarraginis) 균주와 락토바실러스 플란타럼(Lactobacillus plantarum) 균주를 기탁 기관에서 분양 받아, DMEM 배지에서 3일간 배양한 후 용해하여 배양액을 추출하였다. 각 균주의 배양액을 석회 제거 조성물 전체 중량 대비 3 중량%로 첨가하였으며, 이를 밀폐된 용기에 보관하여 차량 석회 제거용 조성물을 제조하였다.Lactobacillus parafarraginis (Lactobacillus parafarraginis) strain and Lactobacillus plantarum (Lactobacillus plantarum) strain were received from the depository institution, cultured in DMEM medium for 3 days, then dissolved and the culture solution was extracted. The culture solution of each strain was added in an amount of 3% by weight based on the total weight of the descaling composition, and it was stored in an airtight container to prepare a vehicle descaling composition.
한편, 상기 제조예 1과 동일한 방법으로 제조하되, 염화수소, 아세트산의 비율을 10 : 20으로 하여 제조예 2의 차량 석회 제거용 조성물을 제조하였고, 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 및 이산화규소 분말을 첨가하지 않고 제조예 3의 차량 석회 제거용 조성물을 제조하였으며, 균주 배양액을 첨가하지 않고 제조예 4의 차량 석회 제거용 조성물을 제조하였다.On the other hand, it was prepared in the same manner as in Preparation Example 1, except that the ratio of hydrogen chloride and acetic acid was 10: 20 to prepare the vehicle descaling composition of Preparation Example 2, sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate , and without adding silicon dioxide powder, the composition for removing vehicle decalcification of Preparation Example 3 was prepared, and without adding a strain culture solution, the composition for removing vehicle decalcification of Preparation Example 4 was prepared.
실험예 1: 차량 석회 제거용 조성물의 pH 확인Experimental Example 1: Checking the pH of the composition for vehicle descaling
상기 제조된 차량 석회 제거용 조성물 각각의 pH 수치를 확인하였다. 구체적으로, 비교예 1 내지 4의 조성물을 300g 용기에 담은 후 휴대용 pH 측정기를 이용하여 pH 수치를 측정하였다.The pH value of each of the prepared vehicle descaling compositions was confirmed. Specifically, the composition of Comparative Examples 1 to 4 was placed in a 300 g container, and then the pH value was measured using a portable pH meter.
그 결과 상기 표 1과 같이, 제조예 2의 경우 비교적 산성이 강하게 나타난 반면, 제조예 1, 3, 4의 차량 석회 제거용 조성물은 약산성에서 중성 사이의 pH 수치를 가져, 석회 오염 제거에 적합하면서도 사용하기에 안전한 물질임을 확인하였다.As a result, as shown in Table 1 above, in the case of Preparation Example 2, relatively strong acidity was shown, whereas the compositions for removing decalcification for vehicles of Preparation Examples 1, 3, and 4 had a pH value between weak acidity and neutrality, making them suitable for removing lime contamination. It was confirmed that the material was safe for use.
실험예 2: 차량 석회 오염물질의 제거 효과 확인Experimental Example 2: Confirmation of the removal effect of vehicle lime pollutants
정제수에 석회(CaO), 실리카(SiO2), 카본 분말, 산화철 분말을 첨가하여 석회수 오염 시료를 준비한 후, 차량 도장면에 두껍게 도포한 후 3일간 경화시켰다. 이후, 시판 중인 컴파운드 기반의 차량용 세척제(비교예) 또는 제조예 1 내지 4의 차량 석회 오염 제거용 조성물을 미량으로 5ml 분무한 후 부드러운 천으로 닦아 석회 오염 물질이 세척되는 정도를 10명의 사용자가 육안으로 비교하여 점수화하였다. Lime (CaO), silica (SiO 2 ), carbon powder, and iron oxide powder were added to purified water to prepare a sample contaminated with lime water, and then thickly applied to the vehicle paint surface and cured for 3 days. After that, after spraying 5 ml of a commercially available compound-based vehicle cleaner (comparative example) or the composition for removing lime contamination of Preparation Examples 1 to 4 in a trace amount, wipe with a soft cloth to see how much lime contaminants are washed by 10 users. were compared to score.
- 1점: 세척력이 낮음- 10점: 세척력이 높음- 1 point: low cleaning power - 10 points: high cleaning power
상기 10명의 사용자가 부여한 점수를 평균으로 하여 비교한 결과, 표 2와 같이 제조예 1 내지 4의 조성물 모두 석회 오염의 제거가 가능하였으며, 그 중 제조예 1의 조성물은 시판 중인 컴파운드 기반의 비교예와 실질적으로 동등한 세척 효과를 나타내어, 적은 양의 세척액으로도 효과적으로 석회 성분의 오염 제거가 가능함을 확인하였다.As a result of comparing the scores given by the 10 users as an average, as shown in Table 2, all of the compositions of Preparation Examples 1 to 4 were able to remove lime contamination, and among them, the composition of Preparation Example 1 was a commercially available compound-based comparative example. It was confirmed that it was possible to effectively remove the contamination of the lime component even with a small amount of cleaning solution by showing a cleaning effect substantially equivalent to that of
제조예 1의 석회 오염 제거 효과를 도 1에 나타내었다.The lime contamination removal effect of Preparation Example 1 is shown in FIG. 1 .
이상 첨부된 도면을 참조하여 본 발명의 실시예들을 더욱 상세하게 설명하였으나, 본 발명은 반드시 이러한 실시예로 국한되는 것은 아니고, 본 발명의 기술사상을 벗어나지 않는 범위 내에서 다양하게 변형 실시될 수 있다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.Although the embodiments of the present invention have been described in more detail with reference to the accompanying drawings, the present invention is not necessarily limited to these embodiments, and various modifications may be made within the scope without departing from the technical spirit of the present invention. . Accordingly, the embodiments disclosed in the present invention are not intended to limit the technical spirit of the present invention, but to explain, and the scope of the technical spirit of the present invention is not limited by these embodiments. Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive. The protection scope of the present invention should be construed by the following claims, and all technical ideas within the equivalent range should be construed as being included in the scope of the present invention.
그러므로, 다른 구현들, 다른 실시예들 및 특허청구범위와 균등한 것들도 후술하는 청구범위의 범위에 속한다.Therefore, other implementations, other embodiments, and equivalents to the claims are also within the scope of the following claims.
Claims (3)
상기 조성물은 5.5 내지 6.5의 pH를 갖는 것이고,
이산화규소 분말, 불소인산나트륨, 아미노카프론산, 테트라소듐파이로포스페이트, 지황 추출물, 복령 추출물, 페녹시에탄올, 소듐시트레이트, 소듐포스페이트, 프로판다이올, 락토바실러스 파라파라지니스 배양액 및 락토바실러스 플란타럼 배양액을 추가로 포함하는, 차량 도장면의 석회 오염 제거용 조성물.
As a composition for removing lime stains from a vehicle paint surface, comprising electrolyzed water, hydrogen chloride, and acetic acid,
The composition has a pH of 5.5 to 6.5,
Silicon dioxide powder, sodium fluorophosphate, aminocaproic acid, tetrasodium pyrophosphate, rehubar extract, bokryeong extract, phenoxyethanol, sodium citrate, sodium phosphate, propanediol, Lactobacillus paraparaginis culture medium and Lactobacillus planta A composition for removing lime contamination from a vehicle paint surface, further comprising a rum culture solution.