KR102256924B1 - Pouch having enhanced concealment function of white ink and producing method therefor - Google Patents
Pouch having enhanced concealment function of white ink and producing method therefor Download PDFInfo
- Publication number
- KR102256924B1 KR102256924B1 KR1020200135758A KR20200135758A KR102256924B1 KR 102256924 B1 KR102256924 B1 KR 102256924B1 KR 1020200135758 A KR1020200135758 A KR 1020200135758A KR 20200135758 A KR20200135758 A KR 20200135758A KR 102256924 B1 KR102256924 B1 KR 102256924B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive
- film
- pouch
- white ink
- weight
- Prior art date
Abstract
Description
본 발명은 고상 또는 액상의 내용물을 수용하는 파우치 및 그 제조방법에 관한 것으로서, 보다 상세하게는, CPP 필름과, 상기 CPP필름의 상측에 부착되는 나일론필름과, 상기 나일론필름의 상측에 부착되는 PET필름과, 상기 CPP 필름)과 나일론필름의 사이에 형성되되 백색잉크가 함유된 접착제가 경화되어 이루어진 제 1 접착층과, 상기 나일론필름과 PET 필름의 사이에 형성되되 백색잉크가 함유된 접착제가 경화되어 이루어진 제 2 접착층을 포함하여 구성되는 파우치 및 그 제조방법에 관한 것이다. The present invention relates to a pouch for accommodating solid or liquid contents and a method for manufacturing the same, and more particularly, a CPP film, a nylon film attached to the upper side of the CPP film, and a PET attached to the upper side of the nylon film. The first adhesive layer formed between the film and the CPP film) and the nylon film, wherein the adhesive containing white ink is cured, and the adhesive formed between the nylon film and the PET film, and the adhesive containing white ink is cured. It relates to a pouch comprising a second adhesive layer made and a method of manufacturing the same.
일반적으로, 파우치(pouch)란 고상 또는 액상의 내용물을 수용하는 용기로서, 주로 가열 살균된 음식물을 보관하는 용도로 널리 이용되고 있으며, 소위 레토르트 파우치(retort pouch)라고도 불리운다.In general, a pouch is a container that accommodates solid or liquid contents, and is widely used mainly for storing heat-sterilized food, and is also called a so-called retort pouch.
이러한 파우치는 살균 처리에 견딜 수 있는 내열성, 내부에 수용되는 내용물의 보존이 가능하도록 산소나 수증기와의 차단성 및 외부의 광선으로부터의 차광성이 요구되며, 파우치의 용도에 따라서 고온의 물에 데워지는 용도의 파우치와 전자레인지의 마이크로웨이브(microwave)에 의하여 데워지는 용도의 파우치의 두가지 종류로 대분된다. These pouches require heat resistance to withstand sterilization treatment, barrier properties to oxygen or water vapor, and light shielding from external rays to enable preservation of the contents contained in the pouch. Depending on the use of the pouch, it is heated in high temperature water. It is largely divided into two types: pouches for paper use and pouches for use heated by microwaves in a microwave oven.
도 1 및 도 2 는 상술한 두가지 종류의 파우치의 단면모식도를 나타낸다.1 and 2 are schematic cross-sectional views of the two types of pouches described above.
먼저, 도 1 을 참조하여 고온의 물에 데워지는 용도의 파우치를 설명하면, 고온용 물에 사용되는 파우치(10)는 내용물에 직접 접촉되는 투명상의 CPP(cast poly propylene: 무연신폴리프로필렌) 필름(11)과, CPP필름(11)의 상측에 부착되는 나일론필름(12)과, 상기 나일론필름(12)의 상측에 부착되는 알루미늄박(13)과, 상기 알루미늄박(13)의 상측에 부착되는 PET필름(14)으로 이루어진 4 중지의 구성이며, 각 필름들은 접착제를 사용하여 접착되며, 접착제층의 도시는 생략된 상태이다.First, referring to FIG. 1, a pouch for heating in high temperature water will be described. The pouch 10 used for high temperature water is a transparent CPP (cast poly propylene) film in direct contact with the contents. (11) And, a nylon film 12 attached to the upper side of the CPP film 11, an aluminum foil 13 attached to the upper side of the nylon film 12, and attached to the upper side of the aluminum foil 13 It is a configuration of four layers made of PET film 14, and each of the films is adhered using an adhesive, and the illustration of the adhesive layer is omitted.
이와 같은 고온용 물에 사용되는 파우치(10)는 알루미늄박(13)의 색상이 불투명하기 때문에 파우치의 내부에 수용된 내용물이 파우치의 외부로 노출되지 않게 되므로, 파우치의 내용물의 색상이 파우치의 표면에 인쇄되는 색상과 중첩되지 않도록 하는 백색잉크 은폐력이 요구되지 않는다.In the pouch 10 used for such high-temperature water, since the color of the aluminum foil 13 is opaque, the contents contained in the pouch are not exposed to the outside of the pouch. No white ink hiding power is required so that it does not overlap with the color being printed.
또한, 도 2 를 참조하여 전자레인지의 마이크로웨이브용 파우치를 설명하면, 전자레인지용 파우치(20)는 도 1 에 도시된 고온의 물에 사용되는 파우치(10)와 비교하여 전자레인지의 마이크로웨이브에 사용이 불가한 알루미늄박(13)을 제거한 구성으로서, 내용물에 직접 접촉되는 투명상의 CPP(cast poly propylene: 무연신폴리프로필렌) 필름(21)과, CPP필름(21)의 상측에 부착되는 나일론필름(22)과, 상기 나일론필름(22)의 상측에 부착되는 PET필름(23)으로 이루어진 3 중지의 구성이며, 각 필름들은 접착제를 사용하여 접착되며, 접착제층의 도시는 생략된 상태이다.In addition, referring to FIG. 2, when a microwave pouch for a microwave oven is described, the pouch for a microwave oven 20 is compared with the pouch 10 used for high temperature water shown in FIG. 1. A configuration in which the unusable aluminum foil 13 has been removed, and a transparent CPP (cast poly propylene) film 21 in direct contact with the contents and a nylon film attached to the upper side of the CPP film 21 It is a configuration of three layers consisting of (22) and a PET film 23 attached to the upper side of the nylon film 22, and each of the films is adhered using an adhesive, and the illustration of the adhesive layer is omitted.
이러한 전자레인지용 파우치(20)는 알루미늄박의 사용이 불가하므로 내용물의 색상이 파우치의 표면에 인쇄되는 색상과 중첩되지 않도록 적합한 정도의 백색잉크 은폐력이 요구된다.Since the use of aluminum foil is not possible for the microwave pouch 20, a suitable level of white ink hiding power is required so that the color of the contents does not overlap with the color printed on the surface of the pouch.
그러므로, 종래에는 전자레인지용 파우치(20)의 백색잉크 은폐력을 부여하기 위하여, CPP 필름(21)과 나일론필름(22) 사이에 유백색의 PET 필름을 추가적으로 게재시키거나, 또는 상기 CPP필름(21)을 유백색의 CPP 필름으로 대체하여 사용하였다. Therefore, in the prior art, in order to impart the white ink hiding power of the microwave pouch 20, a milky PET film is additionally placed between the CPP film 21 and the nylon film 22, or the CPP film 21 Was used by replacing it with a milky white CPP film.
그러나, 유백색의 PET 필름을 사용하는 방법은 유백색 PET 필름이 비교적 고가이므로 파우치의 제조원가가 증가되는 단점이 있었으며, 유백색의 CPP 필름을 사용하는 방법은 파우치의 유통 과정에서 유백색의 CPP 필름이 오렌지 색상으로 변색되거나 탈색될 우려가 있어 시간이 경과될수록 파우치의 상품성이 저하되는 문제점이 있었다.However, the method of using the milky white PET film had the disadvantage of increasing the manufacturing cost of the pouch because the milky white PET film was relatively expensive. There is a problem of discoloration or discoloration, and thus the marketability of the pouch decreases as time elapses.
한편, 상술한 바와같은 파우치의 제조기술에 관한 선행기술로서, 대한민국특허공고 제 794472 호의 내용물로부터의 색소 침착에 기인한 변색 감지를 방지할 수 있는 파우치의 기술이 공지되어 있다.On the other hand, as a prior art related to the manufacturing technology of a pouch as described above, a technique of a pouch capable of preventing the detection of discoloration due to pigmentation from the contents of Korean Patent Publication No. 794472 is known.
본 발명은 상술한 바와 같은 종래의 제반 문제점을 해소하기 위하여 창안된 것으로서, 제조원가를 상승시키지 않고 탈색이나 변색의 가능성이 낮추면서도 파우치 내부에 수용된 내용물의 색상과 파우치의 표면에 인쇄되는 색상과의 중첩이 일어나지 않도록 적합한 정도의 백색잉크 은폐력을 가지는 파우치의 구성과 그 제조방법을 제공하는데에 본 발명의 기술적 과제가 있다.The present invention was devised to solve the problems of the prior art as described above, and overlapping the color of the contents contained in the pouch with the color printed on the surface of the pouch while reducing the possibility of discoloration or discoloration without increasing the manufacturing cost. In order to prevent this from occurring, there is a technical problem of the present invention to provide a configuration of a pouch having an appropriate degree of hiding power of white ink and a method of manufacturing the same.
상기와 같은 기술적 과제를 달성하기 위한 본 발명의 향상된 백색잉크 은폐력을 가지는 파우치 및 그 제조방법은, 각 필름을 부착시키는 접착제에 백색잉크를 혼합하고, 백색잉크가 혼합된 접착제를 사용하여 파우치를 이루는 각 필름을 접착시키는 구성을 특징으로 한다.A pouch having an improved white ink hiding power of the present invention for achieving the above technical problem and a method for manufacturing the same include mixing white ink with an adhesive for attaching each film, and forming a pouch using an adhesive mixed with white ink. It features a configuration to bond each film.
상기와 같이 구성되는 본 발명의 향상된 백색잉크 은폐력을 가지는 파우치 및 그 제조방법은 종래의 3중지 구조를 그대로 이용하므로 종래의 유백색 필름을 사용하는 방법과 비교하여 제조원가가 저렴한 장점을 가지게 되었다.Since the pouch having the improved white ink hiding power of the present invention and its manufacturing method configured as described above uses the conventional triple-layer structure as it is, the manufacturing cost is inexpensive compared to the method using the conventional milky white film.
또한, 백색잉크 혼합된 접착제를 사용하므로 종래 유백색 필름의 탈색이나 변색의 가능성을 낮추면서도 수용된 내용물의 색상이 파우치의 인쇄물 색상을 중첩하지 않을 정도의 적합한 백색잉크 은폐력을 보유하게 된 효과를 발현한다.In addition, since an adhesive mixed with white ink is used, the color of the contained contents does not overlap the print color of the pouch while reducing the possibility of discoloration or discoloration of the conventional milky white film.
도 1 및 도 2 는 종래의 파우치의 구성을 나타내는 도면으로서, 도 1 은 고온의 물에 사용되는 파우치의 단면모식도, 도 2 는 전자레인지에 사용되는 파우치의 단면모식도,
도 3 은 본 발명의 전자레인지용 파우치의 구성을 나타내는 단면모식도,
도 4 는 본 발명의 전자레인지용 파우치의 제조방법의 순서도,
도 5 는 본 발명의 전자레인지용 파우치와 종래 전자레인지용 파우치를 비교한 사진도면이다.1 and 2 are diagrams showing the configuration of a conventional pouch, FIG. 1 is a schematic cross-sectional view of a pouch used for hot water, and FIG. 2 is a schematic cross-sectional view of a pouch used for a microwave oven;
3 is a schematic cross-sectional view showing the configuration of a pouch for a microwave oven of the present invention;
4 is a flow chart of a method of manufacturing a pouch for a microwave oven of the present invention,
5 is a photographic view comparing a pouch for a microwave oven according to the present invention and a pouch for a conventional microwave oven.
본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 구현예(態樣, aspect)(또는 실시예)들을 본문에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.The present invention will be described in detail in the text of the bar, implementation (態樣, aspect) (or embodiment) that can apply various changes and have various forms. However, this is not intended to limit the present invention to a specific form of disclosure, and it should be understood to include all changes, equivalents, and substitutes included in the spirit and scope of the present invention.
본 명세서에서 사용한 용어는 단지 특정한 구현예(태양, 態樣, aspect)(또는 실시예)를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, ~포함하다~ 또는 ~이루어진다~ 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terms used in this specification are only used to describe specific embodiments (sun, 態樣, aspect) (or embodiments), and are not intended to limit the present invention. Singular expressions include plural expressions unless the context clearly indicates otherwise. In the present application, terms such as ~comprise~ or ~consist~ are intended to designate the existence of features, numbers, steps, actions, components, parts, or a combination thereof described in the specification, but one or more other features It is to be understood that the presence or addition of elements or numbers, steps, actions, components, parts, or combinations thereof, does not preclude in advance the possibility of the presence or addition.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless otherwise defined, all terms used herein including technical or scientific terms have the same meaning as commonly understood by one of ordinary skill in the art to which the present invention belongs. Terms as defined in a commonly used dictionary should be interpreted as having a meaning consistent with the meaning in the context of the related technology, and should not be interpreted as an ideal or excessively formal meaning unless explicitly defined in the present application. Does not.
이하, 도면을 참조하여 본 발명의 향상된 백색잉크 은폐력을 가지는 파우치 및 그 제조방법을 상세하게 설명한다.Hereinafter, a pouch having an improved white ink hiding power of the present invention and a method of manufacturing the same will be described in detail with reference to the drawings.
단, 개시된 도면들은 당업자에게 본 발명의 사상이 충분하게 전달될 수 있도록 하기 위한 예로서 제공되는 것이다. 따라서, 본 발명은 이하 제시되는 도면들에 한정되지 않고 다른 태양으로 구체화될 수도 있다.However, the disclosed drawings are provided as an example to sufficiently convey the spirit of the present invention to those skilled in the art. Accordingly, the present invention is not limited to the drawings presented below and may be embodied in other aspects.
또한, 본 발명 명세서에서 사용되는 용어에 있어서 다른 정의가 없다면, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략한다.In addition, unless otherwise defined in terms of the terms used in the present specification, they have the meanings commonly understood by those of ordinary skill in the art to which the present invention pertains, and the gist of the present invention in the following description and accompanying drawings. Detailed descriptions of known functions and configurations that may be unnecessarily obscure will be omitted.
도 3 은 본 발명의 전자레인지용 파우치의 구성을 나타내는 단면모식도이다. 여기서, 설명의 편의상 종래 도 1 과 도 2 에서 그 도시가 생략된 접착층을 본 발명의 단면모식도는 이들을 개별적으로 도시하여 설명하기로 한다.3 is a schematic cross-sectional view showing the configuration of a pouch for a microwave oven according to the present invention. Here, for convenience of explanation, a schematic cross-sectional view of the adhesive layer, which is not illustrated in FIGS. 1 and 2 in the related art, will be described by individually showing them.
본 발명의 전자레인지용 파우치(100)는 내용물에 직접 접촉되는 투명상의 CPP(cast poly propylene: 무연신폴리프로필렌) 필름(110)과, CPP필름(110)의 상측에 부착되는 나일론필름(120)과, 상기 나일론필름(120)의 상측에 부착되는 PET필름(130)으로 이루어진 3 중지의 구성이며, 상기 CPP 필름(110)과 나일론필름(120)의 사이에 백색잉크가 함유된 접착제가 경화되어 이루어진 제 1 접착층(140)이 형성되고, 상기 나일론필름(120)과 PET 필름(130)의 사이에 백색잉크가 함유된 접착제가 경화되어 이루어진 제 2 접착층(150)이 형성된 구성이다.The microwave pouch 100 of the present invention includes a transparent CPP (cast poly propylene) film 110 in direct contact with the contents, and a nylon film 120 attached to the upper side of the CPP film 110 And, it is a configuration of three layers consisting of a PET film 130 attached to the upper side of the nylon film 120, the adhesive containing white ink between the CPP film 110 and the nylon film 120 is cured The first adhesive layer 140 is formed, and the second adhesive layer 150 is formed by curing an adhesive containing white ink between the nylon film 120 and the PET film 130.
상기 제 1 접착층(140)과 제 2 접착층(150)은 전자렌지용 파우치(100)의 제조공정중 각 필름(110,120,130)을 합지시키는 공정에서 백색잉크를 혼합시킨 접착제를 이용하여 각 필름들을 상호 부착시키는 과정에서 형성된다.The first adhesive layer 140 and the second adhesive layer 150 are attached to each other using an adhesive mixed with white ink in the process of laminating each of the films 110, 120, 130 during the manufacturing process of the microwave pouch 100 It is formed in the process of making.
이러한 제 1 접착층(140)과 제 2 접착층(150)을 형성한 본 발명의 파우치(100)는 각 접착층(140,150)에 혼합된 백색잉크에 의하여 파우치의 내용물의 색상이 파우치의 표면에 인쇄되는 색상과 중첩되지 않도록 적합한 정도의 백색잉크 은폐력을 가지게 된다.In the pouch 100 of the present invention in which the first adhesive layer 140 and the second adhesive layer 150 are formed, the color of the contents of the pouch is printed on the surface of the pouch by the white ink mixed with each of the adhesive layers 140 and 150 It has a suitable level of white ink hiding power so that it does not overlap with.
이때, 본 발명의 전자레인지용 파우치(100)에 이용되는 접착제에 대한 백색잉크의 혼합비에 따른 파우치의 필름의 박리강도를 하기 표 1 과 같이 실시하였다. At this time, the peel strength of the film of the pouch according to the mixing ratio of the white ink to the adhesive used in the microwave pouch 100 of the present invention was carried out as shown in Table 1 below.
(표 1) 접착제에 대한 백색잉크의 혼합비에 따른 파우치의 필름의 박리강도 측정(Table 1) Measurement of the peel strength of the film of the pouch according to the mixing ratio of the white ink to the adhesive
* 측정기기: INSTRON (만능물성시험기)* Measuring equipment: INSTRON (Universal Property Tester)
* 측정스피드: 100mm/min* Measurement speed: 100mm/min
* 접착강도 단위: gf/15mm* Adhesion Strength Unit: gf/15mm
본 발명의 실시예의 파우치(100)는 접착제로서 통상의 우레탄수지 접착제를 사용하였으며, 백색잉크는 Deer's M 社(대한민국 소재)의 알코올 타입 백색잉크를 사용하였다. The pouch 100 of the embodiment of the present invention used a conventional urethane resin adhesive as an adhesive, and an alcohol-type white ink of Deer's M Company (Korea Material) was used as the white ink.
또한, 본 발명 실시예의 파우치(100)는 접착제와 백색잉크와의 혼합비를 접착제 18Kg 에 백색잉크 3Kg 로서 설정하여 대략 접착제 84 중량부에 백색잉크 16 중량부의 조성비로서 혼합하였으며, 백색잉크의 양을 증가시킬 경우에는 백색잉크 은폐력은 증가되나 접착력이 저하되게 되므로 파우치(100)에 수용될 내용물의 색상에 따라서 백색잉크의 함량을 조절하는 것이 바람직하다.In addition, in the pouch 100 of the present invention, the mixing ratio of the adhesive and the white ink was set as 18Kg of the adhesive and 3Kg of the white ink, and were mixed as a composition ratio of approximately 84 parts by weight of the adhesive and 16 parts by weight of white ink, and the amount of white ink was increased. In this case, since the white ink hiding power is increased but the adhesion is lowered, it is preferable to adjust the content of the white ink according to the color of the contents to be accommodated in the pouch 100.
상기와 같이 구성되는 본 발명의 전자레인지용 파우치의 제조방법을 도 4 를 참조하여 개조식으로 설명한다.A method of manufacturing a pouch for a microwave oven configured as described above will be described in a modified manner with reference to FIG. 4.
1) 필름의 제단 및 준비 단계(S1)1) Film cutting and preparation step (S1)
본 발명의 전자레인지용 파우치(100)를 구성하는 투명상의 CPP(cast poly propylene: 무연신폴리프로필렌) 필름(110)과, 나일론필름(120)과, PET필름(130)을 합지기의 사이즈에 맞도록 일정한 길이로 재단하고 합지기에 투입할 준비를 수행하는 단계이다.The transparent CPP (cast poly propylene) film 110 constituting the microwave oven pouch 100 of the present invention, the nylon film 120, and the PET film 130 are combined in the size of the laminating machine. This is the step of preparing to cut into a certain length so that it fits and put it into the paper machine.
본 발명의 파우치(100)는, 상기 투명상의 CPP 필름(110)으로서 70-90 ㎛ 두께의 필름을 사용하며, 실시예의 파우치는 80 ㎛ 두께의 투명상의 CPP 필름을 사용한다. The pouch 100 of the present invention uses a film having a thickness of 70-90 μm as the transparent CPP film 110, and the pouch of the embodiment uses a transparent CPP film having a thickness of 80 μm.
또한, 본 발명의 파우치(100)는 상기 나일론 필름(120)으로서 5-15 ㎛ 두께의 필름을 사용하며, 실시예의 파우치는 10 ㎛ 두께의 나일론 필름을 사용한다.In addition, the pouch 100 of the present invention uses a 5-15 μm thick film as the nylon film 120, and the pouch of the embodiment uses a 10 μm thick nylon film.
또한, 본 발명의 파우치(100)는 상기 PET 필름(130)으로서 10-14 ㎛ 두께의 필름을 사용하며, 실시예의 파우치는 12 ㎛ 두께의 PET 필름을 사용한다.In addition, the pouch 100 of the present invention uses a film having a thickness of 10-14 µm as the PET film 130, and the pouch of the embodiment uses a PET film having a thickness of 12 µm.
2) 백색잉크와 접착제의 혼합단계(S2)2) Mixing step of white ink and adhesive (S2)
본 발명의 파우치(100)의 제 1 접착층(140) 및 제 2 접착층(150)을 형성하기 위하여 접착제에 백색잉크를 혼합하는 단계이다.This is a step of mixing white ink with the adhesive to form the first adhesive layer 140 and the second adhesive layer 150 of the pouch 100 of the present invention.
상술한 바와 같이, 본 발명의 실시예의 파우치(100)는 접착제로서 통상의 우레탄수지 접착제를 사용하고, 백색잉크는 Deer's M 社(대한민국 소재)의 알코올 타입 백색잉크를 사용하고, 접착제 18Kg 에 백색잉크 3Kg 을 혼합조에서 혼합시키고 균일하게 교반하여 백색잉크가 함유된 접착제를 제조한다.As described above, the pouch 100 of the embodiment of the present invention uses a conventional urethane resin adhesive as an adhesive, and the white ink uses an alcohol-type white ink of Deer's M (Korea Material), and 18Kg of the adhesive is white ink. 3Kg was mixed in a mixing tank and stirred uniformly to prepare an adhesive containing white ink.
바람직하게는, 상기 우레탄수지 접착제로서 이액형 폴리우레탄계 접착제를 사용하는 것이 좋다. Preferably, it is preferable to use a two-component polyurethane-based adhesive as the urethane resin adhesive.
상기 이액형 폴리우레탄계접착제는 폴리우레탄계 수지를 주제로 하며 경화제로서 폴리이소시아네이트를 사용하고 희석용제로서는 에틸아세테이트를 사용한다. The two-component polyurethane-based adhesive is based on a polyurethane-based resin, and polyisocyanate is used as a curing agent, and ethyl acetate is used as a diluent.
또한, 상기 이액형 폴리우레탄계접착제는 고형분의 함량이 약 30중량%인 것을 사용하는 것이 바람직하다.In addition, it is preferable to use the two-part polyurethane-based adhesive having a solid content of about 30% by weight.
3) 제 1 합지단계(S3)3) The first lamination step (S3)
상기 백색잉크와 접착제의 혼합단계(S2)에서 제조된 백색잉크 함유 접착제를 이용하여 본 발명의 전자레인지용 파우치(100)를 구성하는 투명상의 CPP필름(110)과 나일론필름(120)을 상호 부착시키는 단계이다.The transparent CPP film 110 and the nylon film 120 constituting the microwave pouch 100 of the present invention are attached to each other by using the white ink-containing adhesive prepared in the mixing step (S2) of the white ink and the adhesive. This is the step to make.
구체적으로, 합지기에 권취된 CPP 필름(110)을 인출하면서 인출되는 CPP 필름(110)의 상측으로 상기 S2 단계에서 제조된 백색잉크 함유 접착제를 도포하면서 CPP필름(110)과 나일론필름(120)을 상호 부착시킨다. 바람직하게는, 본 발명의 백색잉크 함유 접착제의 도포량은 약 3.5g/m2 로 조절하였다. Specifically, the CPP film 110 and the nylon film 120 while applying the white ink-containing adhesive prepared in step S2 to the upper side of the CPP film 110 that is drawn out while drawing the CPP film 110 wound on the paper machine. Are mutually attached. Preferably, the applied amount of the white ink-containing adhesive of the present invention was adjusted to about 3.5 g/m2.
이어서, 상호 부착된 상태의 CPP 필름(110)과 나일론필름(120)을 대략 80℃의 라미네이션롤을 통과시키면서 접착제를 건조시키면서 라미네이션을 수행하게 되면, 상기 CPP필름(110)과 나일론필름(120) 사이에 도포된 접착제가 건조되면서 백색잉크가 함유된 접착제가 경화되어 이루어진 제 1 접착층(140)이 형성된다.Subsequently, when lamination is performed while drying the adhesive while passing the CPP film 110 and the nylon film 120 in a state of being attached to each other through a lamination roll of approximately 80° C., the CPP film 110 and the nylon film 120 As the adhesive applied therebetween is dried, the first adhesive layer 140 formed by curing the adhesive containing white ink is formed.
4) 제 2 합지단계(S4)4) The second lamination step (S4)
상기 백색잉크와 접착제의 혼합단계(S2)에서 제조된 백색잉크 함유 접착제를 이용하여 상기 제 1 합지단계(S3)에서 제조된 CPP 필름(110)과 나일론필름(120)의 접합체상에 본 발명의 전자레인지용 파우치(100)를 구성하는 PET 필름(130)을 부착시키는 단계이다.Using the white ink-containing adhesive prepared in the mixing step (S2) of the white ink and the adhesive, on the bonded body of the CPP film 110 and the nylon film 120 prepared in the first laminating step (S3) This is a step of attaching the PET film 130 constituting the microwave pouch 100.
구체적으로, 합지기에 권취된 상태의 CPP필름(110)과 나일론필름(120)의 접합체를 인출하면서 인출되는 나일론필름(120)의 상측으로 상기 S2 단계에서 제조된 백색잉크 함유 접착제를 도포하면서 나일론필름(120)의 상측으로 PET 필름(130)을 을 부착시킨다. 바람직하게는, 본 발명의 백색잉크 함유 접착제의 도포량은 약 3.5g/m2 로 조절하였다.Specifically, nylon while applying the white ink-containing adhesive prepared in step S2 to the upper side of the nylon film 120 that is drawn out while drawing out the bonded body of the CPP film 110 and the nylon film 120 in a state wound on a paper machine. A PET film 130 is attached to the upper side of the film 120. Preferably, the applied amount of the white ink-containing adhesive of the present invention was adjusted to about 3.5 g/m2.
그렇게 되면, CPP 필름(110)과 나일론필름(120)의 접합체 상에 PET 필름(130)이 부착되고, 이 상태에서 필름들(110,120,130)의 부착체를 대략 80℃의 라미네이션롤을 통과시키면서 접착제를 건조시키면서 라미네이션을 수행하게 되면, 상기 나일론필름(120)과 PET필름(130) 사이에 도포된 접착제가 건조되면서 백색잉크가 함유된 접착제가 경화되어 이루어진 제 2 접착층(150)이 형성된다.Then, the PET film 130 is attached on the bonding body of the CPP film 110 and the nylon film 120, and in this state, the adhesive is applied while passing the attachment body of the films 110, 120, 130 through a lamination roll of approximately 80°C. When lamination is performed while drying, the adhesive applied between the nylon film 120 and the PET film 130 is dried to form a second adhesive layer 150 formed by curing the adhesive containing white ink.
이러한 제 1 접착층(140)과 제 2 접착층(150)을 형성한 본 발명의 파우치(100)는 각 접착층(140,150)에 혼합된 백색잉크에 의하여 파우치의 내용물의 색상이 파우치의 표면에 인쇄되는 색상과 중첩되지 않도록 적합한 정도의 백색잉크 은폐력을 가지게 된다.In the pouch 100 of the present invention in which the first adhesive layer 140 and the second adhesive layer 150 are formed, the color of the contents of the pouch is printed on the surface of the pouch by the white ink mixed with each of the adhesive layers 140 and 150 It has a suitable level of white ink hiding power so that it does not overlap with.
5) 인쇄 및 절단 단계(S5)5) Printing and cutting step (S5)
상술한 바와 같은 각 단계를 통하여 제조된 본 발명의 파우치의 PET 필름(130)의 표면에 파우치의 내용물을 표시하는 문자나 도안을 다양한 색상을 이용하여 인쇄기에 의하여 인쇄한 후, 절단기를 이용하여 필요한 사이즈로 절단하여 본 발명의 파우치(100)의 제조를 완료한다. 제조된 파우치(100)는 육안으로 품질 검사를 실시한 후 유통을 위하여 출하한다.After printing a character or a pattern indicating the contents of the pouch on the surface of the PET film 130 of the pouch manufactured through each step as described above by a printer using various colors, it is necessary to use a cutting machine. It is cut to size to complete the manufacture of the pouch 100 of the present invention. The manufactured pouch 100 is shipped for distribution after a quality inspection is performed with the naked eye.
도 5 는 본 발명의 전자레인지용 파우치와 종래 전자레인지용 파우치를 비교한 사진도면이다.5 is a photographic view comparing a pouch for a microwave oven according to the present invention and a pouch for a conventional microwave oven.
도면을 참조하면, 좌측 (a)에 도시된 파우치는 도 2 를 통하여 설명한 종래의 전자레인지의 마이크로웨이브용 파우치이고, 우측 (b)에 도시된 파우치는 본 발명의 실시예의 파우치이다.Referring to the drawings, the pouch shown in left (a) is a microwave pouch of a conventional microwave oven described with reference to FIG. 2, and the pouch shown in right (b) is a pouch according to an embodiment of the present invention.
종래 파우치와 본 발명 실시예의 파우칭에 동일한 용량의 적색의 침투액을 수용시키고 동일 용량의 물을 첨가하여 침투액을 희석시여 관찰한 결과, 좌측의 종래의 파우치는 수용된 적색의 침투액이 선명하게 노출이 되나, 우측의 본 발명의 파우치는 수용된 적색의 침투액이 종래의 파우치보다는 어둡게 노출됨으로써, 본 발명의 파우치가 향상된 백색잉크 은폐력을 보유하게 되었음을 파악할 수 있다.As a result of diluting the penetrating solution by accommodating the same volume of red penetrant to the conventional pouch and the pouch of the embodiment of the present invention and diluting the penetrating solution by adding the same amount of water, the conventional pouch on the left clearly exposed the received red penetrating solution. , It can be seen that the pouch of the present invention on the right is exposed to darker than the conventional pouch, so that the pouch of the present invention has improved white ink hiding power.
한편, 본 발명의 파우치(100)는 장기간 보관 및 사용 시 외면에 세균이 증식될 수 있고, 이러한 경우 본 발명의 파우치(100)를 사용하는 자에게 세균이 전파되거나 본 발명의 파우치(100)가 세균과 같은 미생물에 의해 분해되어 수명이 저하될 수 있다.On the other hand, when the pouch 100 of the present invention is stored and used for a long period of time, bacteria may proliferate on the outer surface, and in this case, the bacteria may spread to the person who uses the pouch 100 of the present invention or the pouch 100 of the present invention It can be decomposed by microorganisms such as bacteria and shorten its lifespan.
본 발명의 파우치(100)는 상기와 같은 문제점을 해결하기 위한 수단으로 외면에 구비되는 보호제을 포함할 수 있다.The pouch 100 of the present invention may include a protective agent provided on the outer surface as a means for solving the above problems.
보호제는 무기화합물 및 티르리 오일을 포함하는 살균제 100 중량부를 포함하는데, 무기화합물은 살균제로서 통상적으로 사용되는 것으로서, 예시적으로 황산구리, 산화아연, 붕산 등일 수 있다. 티트리 오일(Tea tree oil)은 티트리 잎과 잔가지에서 추출한 에센셜 오일로 박테리아, 진균류에 효과적으로 작용하는 것이다. 티트리 오일은 보호제의 용매로서 작용할 수 있다.The protective agent includes 100 parts by weight of a disinfectant including an inorganic compound and a tyric oil, and the inorganic compound is commonly used as a disinfectant, and may be, for example, copper sulfate, zinc oxide, boric acid, and the like. Tea tree oil is an essential oil extracted from tea tree leaves and twigs and works effectively against bacteria and fungi. Tea tree oil can act as a solvent for a protective agent.
보호제는 4-디시안메틸렌-2-메틸-6-(p-디메틸아미노스티릴)-4H-피란(DCM), 6-프로피오닐-2-(디메틸아미노)나프탈렌(PRODAN) 및 N-메틸-2-니트로아닐린(NM2NA)을 포함하는 균반응제 20 중량부를 포함할 수 있다.The protective agent is 4-dicyanmethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran (DCM), 6-propionyl-2-(dimethylamino)naphthalene (PRODAN) and N-methyl- It may contain 20 parts by weight of a bacterial reaction agent including 2-nitroaniline (NM2NA).
상기한 균반응제는 용매에 용해된 상태로 용매를 제1색상(예시적으로 청색)으로 유지시킨다. 이후에 상기 균반응제가 균, 미생물 등과 접촉할 경우, 제1색상의 용매를 약 10초 이내에 제2색상(예시적으로 무색)으로 변화시킨다.The above-described mycobacterial reactant maintains the solvent in the first color (e.g., blue) while being dissolved in the solvent. Thereafter, when the fungicide reactants come into contact with bacteria, microorganisms, etc., the solvent of the first color is changed to a second color (eg, colorless) within about 10 seconds.
균반응제는 상기 본 발명의 파우치(100)에서 균들이 있는 부분을 용매의 색상 변화를 통해 사용자가 인지할 수 있도록 하기 위한 용도로 사용되었으며, 균반응제가 20 중량부 미만일 경우, 균반응제가 균과 접촉 하여도 색상의 변화가 뚜렷하지 않고, 균반응제가 20 중량부를 초과할 경우 경제적이지 않다.The bacterial reaction agent was used for the purpose of allowing the user to recognize the portion of the pouch 100 of the present invention with bacteria through the color change of the solvent. When the bacterial reaction agent is less than 20 parts by weight, the bacterial reaction agent Even in contact with, the color change is not apparent, and it is not economical if the microbial reaction agent exceeds 20 parts by weight.
균반응제는 4-디시안메틸렌-2-메틸-6-(p-디메틸아미노스티릴)-4H-피란(DCM) 10 중량부 대비 6-프로피오닐-2-(디메틸아미노)나프탈렌(PRODAN) 5 중량부, N-메틸-2-니트로아닐린(NM2NA) 5 중량부가 포함되는 것이 바람직하다.Bacterial reaction agent is 4-dicyanmethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran (DCM) 10 parts by weight of 6-propionyl-2-(dimethylamino)naphthalene (PRODAN) It is preferable that 5 parts by weight and 5 parts by weight of N-methyl-2-nitroaniline (NM2NA) are included.
한편, 보호제는 용매가 소량 휘발될 경우, 상기한 균반응제가 균과 접촉하여도 용매의 색상 변화 시간이 보다 오래 소요되며, 용매의 색상 변화의 차이가 크지 않고, 균반응제의 감도가 저하될 수 있다.On the other hand, when the solvent is volatilized in a small amount, the protective agent takes a longer time to change the color of the solvent even when the above-described microbial reactant contacts the microbe, the difference in the color change of the solvent is not large, and the sensitivity of the microbial reagent decreases I can.
건식유지제는 균반응제의 상기한 문제 발생을 억제하기 위한 것으로, 균반응제가 세균과 접촉된 상태에서, 용매가 소량 휘발할 경우에도 상기한 균반응제의 감도와 색상 대비의 차이를 유지하고, 용매의 색상 변화 시간을 유지할 수 있다.The dry maintenance agent is to suppress the occurrence of the above-described problem of the fungicide, and maintains the difference between the sensitivity and color contrast of the fungicide, even when a small amount of solvent volatilizes while the fungicide is in contact with bacteria. , Can maintain the color change time of the solvent.
건식유지제가 1 중량부 미만일 경우, 용매가 소량 증발될 경우에 균반응제의 성능을 충분히 유지할 수 없다는 문제점이 있다.When the dry-retaining agent is less than 1 part by weight, there is a problem in that the performance of the bacteriostatic agent cannot be sufficiently maintained when a small amount of the solvent is evaporated.
균반응제는 염소산 나트륨, 염소, 황산나트륨 등과 같은 불순물과 접촉할 경우, 균과 접촉하지 않아도 색상이 변화될 수 있다.When the disinfectant reacts with impurities such as sodium chlorate, chlorine, and sodium sulfate, the color may change even without contact with the bacteria.
선별향상제는 상기한 균반응제의 문제점을 극복하기 위한 것인데, 2,2 ', 5,5'- 테트라메틸벤지딘(Tetramethylbenzidin)은 무색의 상태에서 염소 또는 염소산 나트륨과 접촉하여 빨간색으로 변화하며, 전분과 요오드는 염소산염과 반응하여 흑색으로 변화한다.The selection enhancer is to overcome the problems of the above-described microbial reaction agent, and 2,2', 5,5'-tetramethylbenzidin changes to red by contact with chlorine or sodium chlorate in a colorless state And iodine reacts with chlorate and turns black.
예를 들어 선별향상제는 2,2 ', 5,5'- 테트라메틸벤지딘(Tetramethylbenzidin) 0.5 중량부 전분 및 요오드의 혼합물이 0.5 중량부를 포함할 수 있다.For example, the selection enhancer may include 0.5 parts by weight of a mixture of 2,2 ′, 5,5 ′-tetramethylbenzidin and 0.5 parts by weight of a starch and iodine mixture.
상기 혼합물이 0.5 중량부를 초과하는 경우 선별향상제가 염소(또는 염소산 나트륨) 및 염소산염과 동시에 반응하였을 때 염소의 검출이 어려울 수 있으며, 상기 혼합물이 0.5 중량부 미만일 경우, 선별향상제가 염소 및 염소산염과 동시에 반응하였을 때 염소산염의 검출이 어려울 수 있다.When the mixture exceeds 0.5 parts by weight, detection of chlorine may be difficult when the selection enhancer reacts with chlorine (or sodium chlorate) and chlorate at the same time, and when the mixture is less than 0.5 parts by weight, the selection enhancer is simultaneously with chlorine and chlorate. When reacted, it may be difficult to detect chlorate.
점도가변제는 시간이 흐름에 따라 보호제의 점도를 향상시키기 위한 용도로 사용되었다. 점도가변제는 예를 들어 보호제의 각 성분(상기 점도가변제를 제외한 성분)의 혼합 과정에서는 배제되어, 보호제의 점도를 낮게 유지함으로써 보호제에 포함되는 각 성분(상기 점도가변제를 제외한 성분)들이 혼합이 잘 이루어지도록 한다.Viscosity modifiers were used to improve the viscosity of the protective agent over time. Viscosity modifiers are excluded from the mixing process of each component (components other than the viscosity modifier) of the protectant, for example, and each component (components excluding the viscosity modifier) included in the protectant by keeping the viscosity of the protectant low Make sure to mix well.
보호제의 혼합 이후에, 점도가변제가 첨가되고 점도가변제에 전단력이 발생되는 경우, 시간이 지남에 따라 점도가 향상되는데, 상기한 전단력은 분무 장치의 노즐과의 접촉 또는 본 발명의 파우치(100)와의 접촉 등에 의해 발생되는 것일 수 있다.After mixing of the protective agent, when the viscosity modifier is added and a shear force is generated in the viscosity modifier, the viscosity increases over time, and the shear force is in contact with the nozzle of the spray device or the pouch 100 of the present invention. ) May be caused by contact with.
또한 공정 상 보호제의 각 성분이 혼합되는 과정에서 점도가변제가 첨가될 수도 있는데, 점도가변제는 시간이 흐름에 따라 점도가 증가하는 것으로 혼합 과정에서 초기에 보호제의 점도를 낮게 유지하여 혼합을 용이하게 하고 혼합 공정 이후에는 점도를 향상시키도록 해 보호제가 본 발명의 파우치(100)에 보다 쉽게 도포되도록 할 수 있다.In addition, a viscosity modifier may be added while each component of the protective agent is mixed in the process, and the viscosity modifier increases with the passage of time. This makes mixing easier by keeping the viscosity of the protective agent low at the beginning of the mixing process. And, after the mixing process, the viscosity is improved so that the protective agent can be more easily applied to the pouch 100 of the present invention.
이와 같이, 점도가변제가 시간이 지남에 따라 보호제의 점도를 증가시킴으로써, 보호제가 본 발명의 파우치(100)에 도포된 상태에서 쉽게 흘러내리지 않게 되고, 따라서 보호제의 기능을 장시간 유지할 수 있다.In this way, by increasing the viscosity of the protective agent as the viscosity modifier increases over time, the protective agent does not easily flow down while being applied to the pouch 100 of the present invention, and thus the function of the protective agent can be maintained for a long time.
특히 보호제가 점도가변제에 의해 점도가 증가됨에 따라 본 발명의 파우치(100)와의 접촉력이 향상됨으로써, 보호제에 포함되어 있는 균반응제 또한 균과 장시간 용이하게 접촉할 수 있고, 따라서 본 발명의 파우치(100)에서 균이 증식된 부분을 보다 용이하게 파악할 수 있다.In particular, as the viscosity of the protective agent is increased by the viscosity modifier, the contact force with the pouch 100 of the present invention is improved, so that the bacterial reaction agent contained in the protective agent can also easily contact the bacteria for a long time, and thus the pouch of the present invention In (100), it is possible to more easily identify the area where the bacteria have grown.
본 발명의 파우치(100)에서 균반응제에 의해 색상이 변한 부분은 세균이 많이 있는 곳으로 인지되고, 이후에 세균이 많다고 파악되는 부분에 보호제를 더 살포하여 효과적으로 살균을 수행할 수 있다.In the pouch 100 of the present invention, a portion of the pouch 100 whose color is changed by the bacterial reaction agent is recognized as a place where there are a lot of bacteria, and then a protective agent is further sprayed on a portion where a lot of bacteria are found to be effectively sterilized.
이상에서 첨부된 도면을 참조하여 설명한 본 발명은 통상의 기술자에 의하여 다양한 변형 및 변경이 가능하고, 이러한 변형 및 변경은 본 발명의 권리범위에 포함되는 것으로 해석되어야 한다.The present invention described above with reference to the accompanying drawings can be variously modified and changed by a person skilled in the art, and such modifications and changes should be construed as being included in the scope of the present invention.
* 도면의 주요 부분에 대한 부호의 설명 *
100; 본 발명의 파우치
110; CPP필름
120; 나일론필름
130; PET필름
140; 제 1 접착층
150; 제 2 접착층* Description of symbols for the main parts of the drawing
100; Pouch of the present invention
110; CPP film
120; Nylon film
130; PET film
140; First adhesive layer
150; 2nd adhesive layer
Claims (4)
상기 CPP필름(110)의 상측에 부착되는 나일론필름(120)과,
상기 나일론필름(120)의 상측에 부착되는 PET필름(130)과,
상기 CPP 필름(110)과 나일론필름(120)의 사이에 형성되되 백색잉크가 함유된 접착제가 경화되어 이루어진 제 1 접착층(140)과,
상기 나일론필름(120)과 PET 필름(130)의 사이에 형성되되 백색잉크가 함유된 접착제가 경화되어 이루어진 제 2 접착층(150)을 포함하여 구성되고,
제 1 접착층(140)과 제 2 접착층(150)을 형성하는 백색잉크 함유 접착제는, 접착제 84 중량부에 백색잉크 16 중량부의 조성비로 혼합되어 이루어지고,
상기 제 1 접착층(140)과 제 2 접착층(150)을 형성하는 접착제는, 우레탄수지 접착제이고,
외면에 구비되는 보호제를 더 포함하되,
상기 보호제는 무기화합물 및 티트리 오일을 포함하는 살균제 100 중량부,
4-디시안메틸렌-2-메틸-6-(p-디메틸아미노스티릴)-4H-피란(DCM), 6-프로피오닐-2-(디메틸아미노)나프탈렌(PRODAN) 및 N-메틸-2-니트로아닐린(NM2NA)을 포함하는 균반응제 20 중량부, 및
2,2 ', 5,5'- 테트라메틸벤지딘(Tetramethylbenzidin) 0.5 중량부 및, 전분 및 요오드 0.5 중량부를 포함하는 선별향상제 1 중량부를 포함하는 것을 특징으로 하는 파우치.CPP film 110,
A nylon film 120 attached to the upper side of the CPP film 110,
PET film 130 attached to the upper side of the nylon film 120,
A first adhesive layer 140 formed between the CPP film 110 and the nylon film 120 and formed by curing an adhesive containing white ink
It is formed between the nylon film 120 and the PET film 130, and comprises a second adhesive layer 150 formed by curing an adhesive containing white ink,
The white ink-containing adhesive forming the first adhesive layer 140 and the second adhesive layer 150 is formed by mixing 84 parts by weight of the adhesive in a composition ratio of 16 parts by weight of white ink,
The adhesive forming the first adhesive layer 140 and the second adhesive layer 150 is a urethane resin adhesive,
Further comprising a protective agent provided on the outer surface,
The protective agent 100 parts by weight of a fungicide containing an inorganic compound and tea tree oil,
4-dicyanmethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran (DCM), 6-propionyl-2-(dimethylamino)naphthalene (PRODAN) and N-methyl-2- 20 parts by weight of a fungicide containing nitroaniline (NM2NA), and
2,2', 5,5'- tetramethylbenzidin (Tetramethylbenzidin) 0.5 parts by weight, and a pouch comprising 1 part by weight of a selection enhancer containing 0.5 parts by weight of starch and iodine.
투명상의 CPP 필름(110)과, 나일론필름(120)과, PET필름(130)을 합지기의 사이즈에 맞도록 일정한 길이로 재단하고 합지기에 투입할 준비를 수행하는 필름의 제단 및 준비 단계(S1);
상기 CPP 필름(110), 상기 나일론필름(120), 상기 PET필름(130)들을 부착시키기 위한 접착제에 백색잉크를 혼합하는 백색잉크와 접착제의 혼합단계(S2);
상기 백색잉크 함유 접착제를 이용하여 상기 CPP필름(110)과 나일론필름(120)을 상호 부착시키고 건조시켜 CPP필름(110)과 나일론필름(120) 사이에 백색잉크가 함유된 접착제가 경화되어 이루어진 제 1 접착층(140)을 형성하는 제 1 합지단계(S3);
상기 백색잉크 함유 접착제를 이용하여 상기 제 1 합지단계(S3)에서 제조된 CPP 필름(110)과 나일론필름(120)의 접합체상에 PET 필름(130)을 상호 부착시키고 건조시켜 상기 나일론필름(120)과 PET필름(130) 사이에 백색잉크가 함유된 접착제가 경화되어 이루어진 제 2 접착층(150)을 형성하는 제 2 합지단계(S4);
를 포함하여 구성되고,
상기 파우치(100)의 제 1 접착층(140)과 제 2 접착층(150)을 형성하는 백색잉크 함유 접착제는, 접착제 84 중량부에 백색잉크 16 중량부의 조성비로 혼합되고,
상기 제 1 접착층(140)과 제 2 접착층(150)을 형성하는 접착제는, 우레탄수지 접착제이고,
외면에 보호제를 도포하는 단계를 더 포함하되,
상기 보호제는 상기 보호제는 무기화합물 및 티트리 오일을 포함하는 살균제 100 중량부,
4-디시안메틸렌-2-메틸-6-(p-디메틸아미노스티릴)-4H-피란(DCM), 6-프로피오닐-2-(디메틸아미노)나프탈렌(PRODAN) 및 N-메틸-2-니트로아닐린(NM2NA)을 포함하는 균반응제 20 중량부, 및
2,2 ', 5,5'- 테트라메틸벤지딘(Tetramethylbenzidin) 0.5 중량부 및, 전분 및 요오드 0.5 중량부를 포함하는 선별향상제 1 중량부를 포함하는 것을 특징으로 하는 파우치의 제조방법.In the method of manufacturing a pouch,
The transparent CPP film 110, the nylon film 120, and the PET film 130 are cut to a certain length to fit the size of the laminating machine, and the film cutting and preparation step ( S1);
Mixing step of white ink and adhesive (S2) of mixing white ink with the adhesive for attaching the CPP film 110, the nylon film 120, and the PET film 130;
Using the white ink-containing adhesive, the CPP film 110 and the nylon film 120 are attached to each other and dried to cure the white ink-containing adhesive between the CPP film 110 and the nylon film 120. A first laminating step (S3) of forming an adhesive layer 140;
The white ink-containing adhesive is used to attach the PET film 130 to the bonded body of the CPP film 110 and the nylon film 120 prepared in the first lamination step (S3) and dry the nylon film 120 ) And a second laminating step (S4) of forming a second adhesive layer 150 formed by curing an adhesive containing white ink between the PET film 130;
Consisting of including,
The white ink-containing adhesive forming the first adhesive layer 140 and the second adhesive layer 150 of the pouch 100 is mixed with 84 parts by weight of the adhesive in a composition ratio of 16 parts by weight of white ink,
The adhesive forming the first adhesive layer 140 and the second adhesive layer 150 is a urethane resin adhesive,
Further comprising the step of applying a protective agent to the outer surface,
The protective agent is the protective agent 100 parts by weight of a fungicide containing an inorganic compound and tea tree oil,
4-dicyanmethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran (DCM), 6-propionyl-2-(dimethylamino)naphthalene (PRODAN) and N-methyl-2- 20 parts by weight of a fungicide containing nitroaniline (NM2NA), and
2,2', 5,5'- Tetramethylbenzidin (Tetramethylbenzidin) 0.5 parts by weight, and a method of manufacturing a pouch comprising 1 part by weight of a selection enhancer containing 0.5 parts by weight of starch and iodine.