KR102147131B1 - Artificial leather used as a decorative material of cosmetic container and its decoration method - Google Patents
Artificial leather used as a decorative material of cosmetic container and its decoration method Download PDFInfo
- Publication number
- KR102147131B1 KR102147131B1 KR1020190121606A KR20190121606A KR102147131B1 KR 102147131 B1 KR102147131 B1 KR 102147131B1 KR 1020190121606 A KR1020190121606 A KR 1020190121606A KR 20190121606 A KR20190121606 A KR 20190121606A KR 102147131 B1 KR102147131 B1 KR 102147131B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- artificial leather
- foam
- decorative material
- polyurethane
- Prior art date
Abstract
Description
본 발명은 화장품 용기를 구성하는 뚜껑이나 덮개 등에 명판 용도를 비롯하여 각종 형태의 장식용도로 사용 가능하도록 한 화장품 용기의 장식재로 사용되는 인조피혁 및 그 가공 장식방법에 관한 것이다.The present invention relates to an artificial leather used as a decorative material for a cosmetic container and a method for processing the same so that it can be used for various types of decorative purposes, including nameplate use, such as a lid or cover constituting a cosmetic container.
일반적으로 화장품 용기는 화장(化粧)에 필요한 각종 성상(性狀)의 화장 내용물을 담아 휴대 보관 및 사용하기 위한 것이다. 이러한 용도의 화장품 용기는 그 기능이나 용도에 따라 다양한 형태 및 구조를 갖게 되는 것이며, 그 소재 또한 합성수지소재를 비롯하여 유리 등 다양한 소재가 이용 제작되어 진다.In general, cosmetic containers are intended for portable storage and use by containing cosmetic contents of various characteristics necessary for makeup. Cosmetic containers for this purpose will have various shapes and structures depending on their functions or uses, and their materials are also manufactured using various materials such as glass, including synthetic resin materials.
그러나 종래 제공되고 있는 합성수지소재로 제작되는 화장품 용기는 소재의 특성상 원하는 형태로 제조하기 용이하고, 또 인쇄 공정을 거쳐 다양한 색상과 느낌을 줄 수 있도록 하는 것이 가능하지만, 인공적인 소재의 사용 느낌을 지울 수가 없다는 소재 및 장식의 한계 있을수 밖에 없다.However, cosmetic containers made of synthetic resin materials that have been provided conventionally are easy to manufacture in a desired shape due to the nature of the material, and it is possible to give various colors and feelings through a printing process, but it is possible to remove the feeling of using artificial materials. There is no choice but to limit the material and decoration that cannot be used.
이러한 점을 감안하여 종래에는 천연소재로 제조한 것 처름 보이기 위해 나무결 무늬를 넣기도 하고, 또 용기에 대해 다양한 형상의 인조보석을 이용하여 다양하고 아름다운 무늬를 표출하는 방식의 화장품 용기(특허문헌 1 참조)가 제시되기도 하고 있는 실정이다In consideration of this, conventionally, a wooden grain pattern was added to make it look like it was made of natural materials, and a cosmetic container in a way that expresses various and beautiful patterns using artificial gemstones of various shapes for the container (see Patent Document 1). ) Is also being presented.
따라서, 본 발명은 종래와 같은 제반 문제점을 해결하기 위하여 발명한 것으로서, 본 발명의 목적은 주로 합성수지소재로 제작되는 화장품 용기의 장식소재에 적합하도록 천연가죽 질감을 제공하고, 동시에 탄성력과 볼륨감이 우수하며, 부드러운 촉감 및 터치감이 우수한 한 화장품 용기의 장식재로 사용되는 인조피혁을 제공함에 있다.Accordingly, the present invention has been invented to solve the problems as in the prior art, and an object of the present invention is to provide a natural leather texture suitable for a decorative material of a cosmetic container mainly made of a synthetic resin material, and at the same time, elasticity and volume It is to provide artificial leather that is used as a decoration material for cosmetic containers as long as it is excellent and has excellent soft touch and touch.
또한, 본 발명의 다른 목적은 인조피혁을 합성수지소재로 제작되는 화장품 용기의 장식에 따른 가공 정밀도가 향상되는 화장품 용기의 장식재로 사용되는 인조피혁을 이용한 가공 장식방법을 제공함에 있다.In addition, another object of the present invention is to provide a processing decoration method using artificial leather used as a decorative material for a cosmetic container in which the processing precision according to the decoration of a cosmetic container made of synthetic resin material is improved.
상기한 과제를 해결하기 위한 본 발명의 제1실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁은, 이면을 형성하는 필름층과, 상기 필름층의 상면에 구비되는 폼층과, 상기 폼층의 상면에 구비되는 백킹 클로스층과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층과, 상기 접착제층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층을 포함하여 구성됨을 특징으로 한다.The artificial leather used as a decorative material for a cosmetic container according to the first embodiment of the present invention for solving the above problems includes a film layer forming a back surface, a foam layer provided on an upper surface of the film layer, and an upper surface of the foam layer. A backing cloth layer provided in the backing cloth layer, an oil-based or water-based adhesive layer applied to the upper surface of the backing cloth layer, and an oil-based or water-based dry polyurethane skin layer provided on the upper surface of the adhesive layer to form a surface It characterized in that it is configured to include.
또한, 본 발명의 제2실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁은, 이면을 형성하는 필름층과, 상기 필름층의 상면에 구비되는 폼층과, 상기 폼층의 상면에 구비되는 백킹 클로스층과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층과, 상기 접착제 층의 상면에 구비되는 습식 폴리우레탄 은층과, 상기 습식 폴리우레탄(Polyurethane) 은층(Micro porous layer)의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층을 포함하여 구성됨을 특징으로 한다.In addition, the artificial leather used as a decoration material for a cosmetic container according to a second embodiment of the present invention includes a film layer forming a back surface, a foam layer provided on the upper surface of the film layer, and a backing cloth provided on the upper surface of the foam layer. A layer, an oily or water-based adhesive layer applied to the upper surface of the backing cloth layer, a wet polyurethane silver layer provided on the upper surface of the adhesive layer, and the upper surface of the wet polyurethane silver layer (Micro porous layer) It is characterized in that it comprises an oily or water-based dry polyurethane skin layer to form a surface.
또한, 본 발명의 제3실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁은, 이면을 형성하는 필름층과, 상기 필름층의 상면에 구비되는 폼층과, 상기 폼층의 상면에 구비되는 백킹 클로스층과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층과, 상기 접착제 층의 상면에 구비되는 1 액형 무용제 발포 폴리우레탄층과, 상기 1 액형 무용제 발포 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층을 포함하여 구성됨을 특징으로 한다.In addition, the artificial leather used as a decoration material for a cosmetic container according to a third embodiment of the present invention includes a film layer forming a back surface, a foam layer provided on the upper surface of the film layer, and a backing cloth provided on the upper surface of the foam layer. A layer, an oil-based or water-based adhesive layer applied to the upper surface of the backing cloth layer, a one-component non-solvent foamed polyurethane layer provided on the upper surface of the adhesive layer, and an upper surface of the one-component solvent-free foamed polyurethane layer It is characterized in that it comprises an oily or water-based dry polyurethane skin layer forming a surface.
또한, 본 발명의 제4실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁은, 이면을 형성하는 필름층과, 상기 필름층의 상면에 구비되는 폼층과, 상기 폼층의 상면에 구비되는 백킹 클로스층과, 상기 백킹 클로스층에 상면에 도포되는 2 액형 무용제 발포 폴리우레탄층과, 상기 2 액형 무용제 발포 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층을 포함하여 구성됨을 특징으로 한다.In addition, the artificial leather used as a decorative material for a cosmetic container according to a fourth embodiment of the present invention includes a film layer forming a back surface, a foam layer provided on the upper surface of the film layer, and a backing cloth provided on the upper surface of the foam layer. A layer, a two-component solvent-free foamed polyurethane layer applied on the upper surface of the backing cloth layer, and an oil-based or water-based dry polyurethane skin provided on the upper surface of the two-component solvent-free foamed polyurethane layer to form a surface (Polyurethane Skin) It is characterized in that it is composed of a layer.
또한, 본 발명의 제5실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁은, 이면을 형성하는 필름층과, 상기 필름층의 상면에 구비되는 폼층과, 상기 폼층의 상면에 구비되는 백킹 클로스층과, 상기 백킹 클로스층의 상면에 구비되어 표면을 형성하는 폴리비닐클로라이드(PVC) 또는 열가소성폴리우레탄(TPU) 스킨층을 포함하여 구성됨을 특징으로 한다.In addition, the artificial leather used as a decorative material for a cosmetic container according to a fifth embodiment of the present invention includes a film layer forming a back surface, a foam layer provided on the upper surface of the film layer, and a backing cloth provided on the upper surface of the foam layer. It is characterized in that it comprises a layer and a polyvinyl chloride (PVC) or thermoplastic polyurethane (TPU) skin layer provided on the upper surface of the backing cloth layer to form a surface.
본 발명의 제1 내지 제5의 실시 예에서 갖추어지는 필름층은, 폴리프로필렌(PP), 폴리카보네이트(PC), 폴리에틸렌(PE), 폴리에틸렌테레프탈레이트(PET) 중 어느 하나가 선택 사용될 수 있고, 또, 그 두께는 10~300㎛의 두께(T) 범위 내로 이루어짐을 특징으로 한다.The film layer provided in the first to fifth embodiments of the present invention may be selected from any one of polypropylene (PP), polycarbonate (PC), polyethylene (PE), and polyethylene terephthalate (PET), In addition, the thickness is characterized in that it is made within the thickness (T) range of 10 ~ 300㎛.
본 발명의 제1 내지 제5의 실시 예에서 갖추어지는 폼층은, 폴리우레탄 습식 PLU FORM), 고밀도 건식 발포우레탄 폼(PORON), 올레핀 폼(OLEFINFROM), 열가소성폴리 올레핀(TPO: Thermoplastic Olefin), 열가소성엘라스토머(TPE: Thermoplastic Elastomer), PUD Foam(수성), 아크릴 폼, TPU폼 중 어느 하나가 선택 사용될 수 있고, 또 그 두께는 50~500㎛의 두께(T) 범위 내로 이루어짐을 특징으로 한다.The foam layers provided in the first to fifth embodiments of the present invention are polyurethane wet PLU FORM), high density dry foam urethane foam (PORON), olefin foam (OLEFINFROM), thermoplastic polyolefin (TPO: Thermoplastic Olefin), thermoplastic Elastomer (TPE: Thermoplastic Elastomer), PUD Foam (aqueous), acrylic foam, TPU foam can be used to select any one, and the thickness is characterized in that it is made in the range of 50 ~ 500㎛ thickness (T).
본 발명의 제1 내지 제5의 실시 예에서 갖추어지는 백킹 클로스층은, 직물, 편물, 극세사, 부직포, 함침포 중 어느 하나가 사용됨을 특징으로 한다.The backing cloth layer provided in the first to fifth embodiments of the present invention is characterized in that any one of a woven fabric, a knitted fabric, a microfiber, a nonwoven fabric, and an impregnated fabric is used.
본 발명의 제1 내지 제5의 실시 예에서 필름층 및 폼층을 제외한 나머지 층의 두께는 10~300㎛의 두께(T) 범위 내로 이루어짐을 특징으로 한다.In the first to fifth embodiments of the present invention, the thickness of the remaining layers excluding the film layer and the foam layer is in the range of 10 to 300 μm in thickness (T).
본 발명의 제1 내지 제5의 실시 예에 따른 상기 인조피혁의 표면으로는 리얼 스티칭 방식이나, 또는 고주파 퀄팅 방식(누비는 방식)에 의해 다양한 형태의 패턴이 더 형성되어 짐을 특징으로 한다The surface of the artificial leather according to the first to fifth embodiments of the present invention is characterized in that various types of patterns are further formed by a real stitching method or a high frequency qualifying method (quilting method).
본 발명의 제1 내지 제5 실시 예에 따른 인조피혁은 화장품 용기의 장식재로 사용됨을 특징으로 한다.Artificial leather according to the first to fifth embodiments of the present invention is characterized in that it is used as a decorative material for cosmetic containers.
상기한 과제를 해결하기 위한 본 발명의 화장품 용기의 장식재로 사용되는 인조피혁 가공 장식방법은, 적정한 크기로 재단된 시트 상의 인조피혁에 대하여 작업 테이블에 형성된 가이드 핀에 맞추어 가이드 핀 홀을 형성하는 제1단계; 상기 시트 상의 인조피혁에 형성된 가이드 핀 홀을 이용하여 인조피혁을 가이드 핀이 형성된 작업 테이블에 배치 고정하는 제2단계; 상기 작업 테이블에 배치 고정된 인조피혁의 표면에 문양을 형성하는 제3단계; 상기 문양에 맞도록 별도로 제작된 휘장의 고정핀에 대응되는 홀을 형성하는 제4단계; 상기 인조피혁의 가장자리를 화장품 용기의 부착공간의 형태와 높이에 맞추어 가압 커팅하는 제5단계; 상기 문양에 대해 휘장을 끼워 고정하는 제6단계; 를 포함하여 구성됨을 특징으로 한다.The artificial leather processing decoration method used as a decorative material for a cosmetic container according to the present invention for solving the above problems is a method of forming a guide pin hole in accordance with a guide pin formed on a work table for artificial leather on a sheet cut to an appropriate size. Level 1; A second step of placing and fixing the artificial leather on a work table on which a guide pin is formed by using a guide pin hole formed in the artificial leather on the sheet; A third step of forming a pattern on the surface of the artificial leather disposed and fixed on the work table; A fourth step of forming a hole corresponding to the fixing pin of the insignia separately manufactured to fit the pattern; A fifth step of pressing and cutting the edge of the artificial leather according to the shape and height of the attachment space of the cosmetic container; A sixth step of inserting and fixing a badge with respect to the pattern; It characterized in that it is configured to include.
본 발명에 따른 인조피혁은 주로 합성수지소재로 제작되는 화장품 용기의 장식재에 적합하도록 천연가죽 질감을 제공하고, 또 탄성력과 볼륨감이 우수하며, 부드러운 촉감 및 터치감을 제공하게 되는 이점이 있다.The artificial leather according to the present invention has the advantage of providing a natural leather texture suitable for decoration of cosmetic containers mainly made of synthetic resin materials, and has excellent elasticity and volume, and provides a soft touch and touch.
또한, 본 발명 인조피혁의 가공 장식방법에 따르면, 화장품 용기의 장식 부착에 따른 가공 정밀도가 향상되어 인조피혁의 부착 작업을 신속 용이하게 할 수 있고, 또 부착 외관이 미려하게 되는 이점을 제공하게 된다.In addition, according to the method for processing and decorating the artificial leather of the present invention, the processing precision according to the decoration of the cosmetic container is improved, so that the attachment of the artificial leather can be quickly and easily, and the appearance of the attachment is beautiful. .
또한, 본 발명에 따른 인조피혁은 회사 로그나 휘장, 이름 등을 가공하여 화장품 용기의 장식재로 사용됨으로 인해 회사 선전 및 광고 효과의 극대화가 가능하고 또 화장품 용기의 고급화가 가능하게되는 이점을 제공하게 된다.In addition, the artificial leather according to the present invention is used as a decorative material for cosmetic containers by processing company logs, emblems, names, etc., so that it is possible to maximize the effect of company advertisement and advertisement, and to provide the advantage of enabling the luxury of cosmetic containers. do.
도 1은 본 발명의 제1실시 예에 따른 인조피혁 구조를 보인 단면도이다.
도 2는 본 발명의 제2실시 예에 따른 인조피혁 구조를 보인 단면도이다.
도 3은 본 발명의 제3실시 예에 따른 인조피혁 구조를 보인 단면도이다.
도 4는 본 발명의 제4실시 예에 따른 인조피혁 구조를 보인 단면도이다.
도 5는 본 발명의 제5실시 예에 따른 인조피혁 구조를 보인 단면도이다.
도 6은 본 발명의 제2실시 예에 따른 인조피혁에 있어서, 습식 풀레우레탄 은층의 단면 구조를 보인 도면이다.
도 7은 본 발명의 각 실시 예에 따른 인조피혁에 리얼 스티치 방식으로 패턴이 형성된 예를 보인 평면도이다.
도 8은 본 발명에 따른 인조피혁의 가공 장식과정을 설명하기 위한 작업 공정도이다.
도 9는 도 8의 공정도에 있어서, 제1단계 과정을 설명하기 위한 도면이다.
도 10은 도 8의 공정도에 있어서, 제2단계 과정을 설명하기 위한 도면이다.
도 11은 도 8의 공정도에 있어서, 제3단계 과정을 설명하기 위한 도면이다.
도 12는 도 8의 공정도에 있어서, 제4단계 과정을 설명하기 위한 도면이다.
도 13은 도 8의 공정도에 있어서, 제5단계 과정을 설명하기 위한 도면이다.
도 14는 도 8의 공정도에 있어서, 제6단계 과정을 설명하기 위한 도면이다.
도 15는 본 발명에 따른 인조피혁의 장식재가 화장품 용기에 부착되기 전의 예시 사진이다.
도 16은 본 발명에 따른 인조피혁의 장식재가 화장품 용기에 부착된 예를 보인 사진이다.1 is a cross-sectional view showing an artificial leather structure according to a first embodiment of the present invention.
2 is a cross-sectional view showing an artificial leather structure according to a second embodiment of the present invention.
3 is a cross-sectional view showing an artificial leather structure according to a third embodiment of the present invention.
4 is a cross-sectional view showing an artificial leather structure according to a fourth embodiment of the present invention.
5 is a cross-sectional view showing an artificial leather structure according to a fifth embodiment of the present invention.
6 is a view showing a cross-sectional structure of a wet polyurethane silver layer in the artificial leather according to the second embodiment of the present invention.
7 is a plan view showing an example in which a pattern is formed in a real stitch method on artificial leather according to each embodiment of the present invention.
Figure 8 is a working flow chart for explaining the processing and decoration process of the artificial leather according to the present invention.
9 is a diagram illustrating a first step process in the process diagram of FIG. 8.
10 is a diagram illustrating a second step process in the process diagram of FIG. 8.
11 is a diagram illustrating a third step process in the process diagram of FIG. 8.
12 is a view for explaining a fourth step process in the process diagram of FIG. 8.
13 is a diagram illustrating a fifth step process in the process chart of FIG. 8.
14 is a diagram illustrating a sixth step process in the process diagram of FIG. 8.
15 is an exemplary photograph before the decorative material of artificial leather according to the present invention is attached to a cosmetic container.
16 is a photograph showing an example in which the decorative material of artificial leather according to the present invention is attached to a cosmetic container.
이하, 본 발명에 따른 바람직한 실시 예를 첨부된 도면을 참조하여 보다 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments according to the present invention will be described in more detail with reference to the accompanying drawings.
본 발명의 제1 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)에 대하여 설명하면 다음과 같다.The artificial leather (A1) used as a decorative material for a cosmetic container according to the first embodiment of the present invention will be described as follows.
도 1을 참조하면, 제1 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)은, 이면을 형성하는 필름층(110)과, 상기 필름층의 상면에 구비되는 폼층(120)과, 상기 폼층의 상면에 구비되는 백킹 클로스층(130)과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과, 상기 접착제층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성된다.Referring to Figure 1, the artificial leather (A1) used as a decoration material of the cosmetic container according to the first embodiment, a
필름층(110)은 실질적으로 베이스 기능을 하게 되는 것으로서, 부착이 요구되는 화장품 용기에 대한 접합을 안정되게 유지 제공하는 기능을 하게 된다.The
필름층의 소재는 다양하게 적용될 수 있을 것이다. 그 두께 또한 일정 범위 내에서 다양하게 적용될 수 있다.The material of the film layer may be applied in various ways. Its thickness can also be applied in various ways within a certain range.
상술하면, 상기 필름층(110)은 폴리우레탄수지라면 특별히 제한되지 않으나, 바람직하게는 폴리프로필렌(PP), 폴리카보네이트(PC), 폴리에틸렌(PE), 폴리에틸렌테레프탈레이트(PET) 중 어느 하나가 선택 사용될 수 있고, 또, 그 두께는 10~300㎛의 두께(T) 범위 내로 이루어짐이 바람직할 것이다.In detail, the
필름층(110)의 두께가 상기 범위를 벗어나는 경우에는 너무 딱딱하게 되거나 너무 부드러워 장식재로 접착시, 베이스 기능을 상실하게 되는 문제가 발생될 수 있다.When the thickness of the
폼층(120)은 큐션 정도를 제공하기 위한 하나의 층을 구성한다.The
폼층(120)은 다양한 종류의 폼이 사용될 수 있을 것이다. 그 두께 또한 일정 범위 내에서 다양하게 적용될 수 있다.As the
상술하면, 상기 폼층(120)은 폴리우레탄 습식 폼(PU FORM), 고밀도 건식 발포우레탄 폼(PORON), 올레핀 폼(OLEFINFROM), 열가소성폴리올레핀(TPO: Thermoplastic Olefin), 열가소성엘라스토머(TPE: Thermoplastic Elastomer), PUD Foam(수성), 아크릴 폼, TPU폼 중 어느 하나가 선택 사용될 수 있고, 또 그 두께는 50~500㎛의 두께(T) 범위 내로 이루어짐이 바람직할 것이다. In detail, the
상기 폼층(120)의 두께가 상기 범위를 벗어나는 경우에는 과도하거나 미약한 큐선력이 제공되는 문제가 발생될 수 있다.When the thickness of the
백킹 클로스층(130)은 실질적으로 기재(원단)층을 구성한다. 백킹 클로스층(130) 역시 다양한 소재가 이용될 수 있다. 그 두께 또한 일정 범위 내에서 다양하게 적용될 수 있다.The
상술하면, 백킹 클로스층(130)은, 직물, 편물, 극세사, 부직포, 함침포 중 어느 하나가 사용될 수 있다. 바람직하기로는 부직포(Non-Woven)가 가장 좋을 것이다, 부직포는 섬유간 강한 교락이 존재하고, 높은 기계적 물성을 가짐에 따라 폴리우레탄 인공피혁의 기재로 매우 적합하다.In detail, as the
건식 폴리우레탄 스킨(Polyurethane Skin)층(150)은, 피혁의 표면을 구성하는 것으로서, 유성 또는 수성, 무용제로도 이루어질 수 있는바, 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 유성으로 형성하는 경우에는, 가격 경쟁력이 매우 높아질 수 있는 이점이 있고, 또 수성으로 형성하는 경우에는 친환경적이며, 대기 오염물질로서 발암성을 가진 독성화학물질인 VOCs(휘발성 유기화합물)가 발생하지 않는 이점이 있다.The dry
여기서, 유성으로 제조되는 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)은 폴리우레탄수지와 혼합하여 사용하는 용제 중 물(Wwater)을 제외한 솔벤트(solvent)를 사용하여 제조되는 것을 말하며, 수성으로 제조되는 건식 폴리우레탄 스킨(Polyurethane Skin)층은 물을 솔벤트로 사용하여 제조된 것을 말한다.Here, the dry
또한, 무용제는 A액, B액을 이용하여 물, 용제를 사용하지 않는 100% 고형분의 우레탄 수지(Resine)를 말한다. 여기서 무용제로 이용되는 A액은 과량의 이소시아네이트(MDI,TDI,HDI,IPID 등)+폴리올 일 수 있고, B액은 폴리올+기타 첨가제(Polyester 혹은 Polyol, 쇄 연장제, 발포제, 정포제(셀 안정제) 등) 일 수 있다, 상기한 A액 및 B액은 촉매의 화학적 발포를 통해 폴리우레탄 스킨 층을 형성할 수 있게 된다.In addition, a solvent-free agent refers to a 100% solid urethane resin (resine) that uses liquid A and liquid B and does not use water or solvent. Solution A used as a solvent-free agent may be an excessive amount of isocyanate (MDI, TDI, HDR, IPID, etc.) + polyol, and Solution B is polyol + other additives (Polyester or Polyol, chain extender, foaming agent, foam stabilizer (cell stabilizer ), etc.), the above-described solutions A and B can form a polyurethane skin layer through chemical foaming of a catalyst.
따라서, 상기와 같은 제1실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)은, 경제적이며, 고 내열성이 우수하며 고주파나 열 몰딩 성형이 우수하고, 원단의 꺽임 및 주름이 거의 발생되지 않은 구조상의 특징을 가질 수 있다.Therefore, the artificial leather (A1) used as a decorative material for a cosmetic container according to the first embodiment as described above is economical, has excellent high heat resistance, is excellent in high frequency or thermal molding, and almost causes bending and wrinkles of the fabric. It may have structural features that are not.
제1실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)의 각 층을 형성하는 과정은, 먼저 이형지에 대하여 유성으로 제조되는 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 형성하고, 그 위에 유성 또는 수성의 접착제층(140)이 도포돠고, 또 백킹 클로스층(130)과, 폼층(120) 및 필름층(110)이 순차적으로 적층 형성되어 지는 방법으로 이루어질 수 있다.In the process of forming each layer of artificial leather (A1) used as a decoration material for a cosmetic container according to the first embodiment, first, a dry
다음으로, 본 발명의 제2 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A2)에 대하여 설명하면 다음과 같다. 제2실시 예를 설명함에 있어서, 제1실시 예와 동일한 구성에 대해서는 동일한 부호를 부여하여 설명하고, 중복 설명은 생략한다.Next, an artificial leather (A2) used as a decorative material for a cosmetic container according to a second embodiment of the present invention will be described as follows. In describing the second embodiment, the same components as those of the first embodiment are denoted by the same reference numerals, and redundant descriptions are omitted.
도 2를 참조하면, 제2 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A2)은, 이면을 형성하는 필름층(110)과, 상기 필름층의 상면에 구비되는 폼층(120)과, 상기 폼층의 상면에 구비되는 백킹 클로스층(130)과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과, 상기 접착제 층의 상면에 구비되는 습식 폴리우레탄 은층(160)과, 상기 습식 폴리우레탄(Polyurethane) 은층(Micro porous layer)의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성된 것이다.Referring to Figure 2, the artificial leather (A2) used as a decorative material of the cosmetic container according to the second embodiment, a
상기 제2실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A2)은 제1 실시 예의 인조피혁(A1)과 비교하여 유성 또는 수성의 접착제층(140)과, 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150) 사이에 습식 폴리우레탄 은층(160)이 더 갖추어진 구성의 차이만을 가진다.The artificial leather (A2) used as a decorative material for the cosmetic container according to the second embodiment has an oil-based or water-based
따라서, 제2 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A2)을 설명함에 있어서, 습식 폴리우레탄층(160)에 대해서만 상세하게 설명하고, 나머지 구성에 대해서는 설명을 생략한다.Therefore, in describing the artificial leather (A2) used as a decoration material for a cosmetic container according to the second embodiment, only the
상기 제2 실시 예에서 습식 폴리우레탄 은층(160)을 구비함으로 인해 폴리우레탄에 형성되는 다공층으로 인해 제품의 볼륨상 및 내구성 및 물리적 물성이 향상되어 질 수 있다.In the second embodiment, since the wet
여기서, 습식 폴리우레탄 은층(160)에 다공층의 형성은, 열경화성 폴리우레탄 수지를 포함하는 폴리우레탄수지 조성물에 첨가제를 혼합한 코팅 배합액을 교반한 후 평활성 및 코팅의 균일성을 위한 기포를 제거하는 단계와, 원단에 코팅 배합액을 도포하는 코팅단계를 거친 후 상기 폴리우레탄 배합액으로 원단에 코팅하여 전처리 가공을 거쳐 코팅된 원단을 응고조 조건범위 내에서(용제 농도와 온도) 응고하는 단계를 거치며, 이후, 코팅 배합액으로 코팅하여 응고조 조건 범위 내에서 응고시킨다.Here, the formation of the porous layer on the wet
이때 용제 농도가 높으면 응고가 늦어지고 균일한 기공이 형성되지 안게되고, 낮으면 기공이 너무 커져 제품으로서 활용할 수 없게 되는 까닭에 적정한 용제 농도 및 온도 설정이 중요하다고 하겠다. 폴리우레탄 코팅 배합액에 혼합되어 있는 첨가제는 응고단계에서는 상기 폴리우레탄수지 조성물 내에 잔류하고 있으며, 수세단계에서 물에 용해되어 제거되는 동시에 미세한 다공을 형성하며, 이때 다공은 균일하게 되고, 제품 내 기계/화학적 물성은 저하되지 않는 특성을 가지게 된다.At this time, if the solvent concentration is high, coagulation is delayed and uniform pores are not formed, and if the solvent concentration is low, the pores become too large to be used as a product. Therefore, it is important to set an appropriate solvent concentration and temperature. The additives mixed in the polyurethane coating formulation remain in the polyurethane resin composition in the solidification step, and are dissolved in water and removed in the water washing step, and at the same time form fine pores, the porosity becomes uniform, and the machine in the product /The chemical properties have a property that does not deteriorate.
상기한 방법으로 제조되는 습식 폴리우레탄 은층(160)의 다공층 구조는 도 6에 나타낸 바와 같다.The porous layer structure of the wet
제2실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A2)의 각 층을 형성하는 과정은, 제1실시 예와 같은 방법으로 이루어질 수 있다.The process of forming each layer of the artificial leather (A2) used as a decoration material for a cosmetic container according to the second embodiment may be performed in the same manner as in the first embodiment.
다음으로, 본 발명의 제3실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A3)에 대하여 설명하면 다음과 같다. 제3실시 예를 설명함에 있어서, 제1실시 예와 동일한 구성에 대해서는 동일한 부호를 부여하여 설명하고, 중복 설명은 생략한다.Next, the artificial leather (A3) used as a decorative material for a cosmetic container according to a third embodiment of the present invention will be described as follows. In describing the third embodiment, the same components as those of the first embodiment are denoted by the same reference numerals, and redundant descriptions are omitted.
도 3을 참조하면, 제3 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A3)은, 이면을 형성하는 필름층(110)과, 상기 필름층의 상면에 구비되는 폼층(120)과, 상기 폼층의 상면에 구비되는 백킹 클로스층(130)과, 상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과, 상기 접착제 층의 상면에 구비되는 1 액형 무용제 발포 폴리우레탄층(170)과, 상기 1 액형 무용제 발포 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성된 것이다.Referring to FIG. 3, artificial leather (A3) used as a decorative material for a cosmetic container according to the third embodiment includes a
상기 제3실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A3)은 제1 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)과 비교하여 유성 또는 수성의 접착제층(140)과, 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150) 사이에 1액형 무용제 발포 폴리우레탄층(170)이 개재된 구성의 차이만을 가진다.The artificial leather (A3) used as a decorative material for a cosmetic container according to the third embodiment is an oily or water-based
따라서, 제3 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A3)을 설명함에 있어서, 1액형 무용제 발포 폴리우레탄층(170)에 대해서만 상세하게 설명하고, 나머지 구성에 대해서는 설명을 생략한다.Therefore, in describing the artificial leather (A3) used as a decorative material for a cosmetic container according to the third embodiment, only the one-component solvent-free
여기서, 1액형 무용제 발포 폴리우레탄층(170)의 폴리우레탄수지는 초경량 폴리우레탄 하이솔리드수지를 사용하게 된다. 본 발명에서 사용되는 폴리우레탄 수지는 유기 용제가 포함되지 않은 무용제 타입으로, 휘발성 유기화합물(VOC) 방출의Here, the polyurethane resin of the one-component solvent-free
염려가 없는 친환경 소재이면서 탄성력과 내구성이 우수하다. 바람직하기로는 상기 1액형 타입의 블록킹된 폴리우레탄 하이솔리드수지는 폴리올 60 ∼ 80 중량%와 이소시아네이트 화합물 15 ∼ 30 중량% 및 블로킹제 5 ∼10 중량%를 포함할 수 있다.It is an eco-friendly material that has no worries, but has excellent elasticity and durability. Preferably, the one-pack type blocked polyurethane high-solid resin may include 60 to 80% by weight of polyol, 15 to 30% by weight of an isocyanate compound, and 5 to 10% by weight of a blocking agent.
상기 1액형 타입의 블록킹된 폴리우레탄 하이솔리드수지를 구성하는 폴리올 성분으로서 폴리에테르폴리올, 폴리에스테르폴리올, 글리콜 또는 이들의 혼합물을 사용할 수 있다. 상기 폴리에테르폴리올은 중량평균분자량이 400 ∼ 6,000 범위이고, 히드록실값(OH value)이 26 ∼ 30 mgKOH/g인 것이 바람직하다. 상기 폴리에테르폴리올의 중량평균분자량과 히드록실값이 상기에서 한정한 범위 미만이 될 경우에는 반응이 빠르게 진행되어 폴리우레탄의 물리적 물성이 저하할 우려가 있고, 히드록실값과 중량평균분자량이 상기에서 한정한 범위를 초과할 경우에는 점도가 너무 높아 폴리우레탄 반응시 물성이 저하할 우려가 있다. 상기 폴리에테르폴리올은 구체적으로 폴리에틸렌글리콜(PEG), 폴리카보네이트디올(PCD), 폴리프로필렌글리콜(PPG), 폴리테트라메틸렌에테르글리콜(PTMEG) 등으로부터 선택된 1종 이상을 사용할 수 있다. 특히 바람직하기로는 폴리카보네이트디올(PCD)을 사용하는 것이다.Polyether polyol, polyester polyol, glycol, or a mixture thereof may be used as a polyol component constituting the one-pack type blocked polyurethane high solid resin. The polyether polyol preferably has a weight average molecular weight in the range of 400 to 6,000 and a hydroxyl value of 26 to 30 mgKOH/g. When the weight average molecular weight and hydroxyl value of the polyether polyol are less than the ranges defined above, the reaction proceeds rapidly and there is a concern that the physical properties of the polyurethane may decrease, and the hydroxyl value and the weight average molecular weight are When it exceeds the limited range, the viscosity is too high, and there is a concern that physical properties may decrease during the polyurethane reaction. Specifically, the polyether polyol may be one or more selected from polyethylene glycol (PEG), polycarbonate diol (PCD), polypropylene glycol (PPG), polytetramethylene ether glycol (PTMEG), and the like. Particularly preferably, polycarbonate diol (PCD) is used.
상기 폴리에스테르폴리올은 폴리우레탄 반응의 고분자 우레탄의 내구성과 가수분해성을 조절하는 폴리올로서 첨가량에 따라 탄성과 유연성을 결정하면서 내가수분해 물성에 작용한다. 상기 폴리에스테르폴리올은 평균분자량이 1,700 ∼ 2,500 범위이고, 히드록실값(OH value)이 51 ∼ 57 mgKOH/g인 것이 바람직하다. 상기 폴리에스테르폴리올의 중량평균분자량과 히드록실값이 상기에서 한정한 범위 미만이 될 경우에는 반응이 빠르게 진행되어 폴리우레탄의 물리적 물성이 저하할 우려가 있고, 히드록실값과 중량평균분자량이 상기에서 한정한 범위를 초과할 경우에는 점도가 너무 높아 폴리우레탄 반응시 물성이 저하할 우려가 있다. 상기 폴리에스테르 폴리올은 구체적으로 아디프산과 네오펜틸글리콜을 1:1 몰비로 반응시켜 제조될 수 있다.The polyester polyol is a polyol that controls the durability and hydrolysis properties of a polymer urethane in a polyurethane reaction, and acts on hydrolysis resistance while determining elasticity and flexibility according to the amount added. The polyester polyol preferably has an average molecular weight in the range of 1,700 to 2,500 and a hydroxyl value of 51 to 57 mgKOH/g. When the weight average molecular weight and hydroxyl value of the polyester polyol are less than the ranges defined above, the reaction proceeds rapidly and there is a concern that the physical properties of the polyurethane may decrease, and the hydroxyl value and the weight average molecular weight are When it exceeds the limited range, the viscosity is too high, and there is a concern that physical properties may decrease during the polyurethane reaction. The polyester polyol may be specifically prepared by reacting adipic acid and neopentyl glycol in a 1:1 molar ratio.
상기 글리콜은 모듈러스 조절과 촉감을 조절하는 작용을 하며, 1,6-헥산디올, 에틸렌 글리콜, 디에틸렌 글리콜 등으로부터 선택된 1종 이상을 사용할 수 있다.The glycol functions to control modulus and touch, and at least one selected from 1,6-hexanediol, ethylene glycol, diethylene glycol, and the like may be used.
상기 1액형 타입의 블록킹된 폴리우레탄 하이솔리드수지의 구성성분으로서 폴리올은 60 ∼ 80 중량% 범위로 포함되는데, 그 함량이 60 중량% 미만이면 제품의 감촉의 딱딱하고 굴곡성능이 저하될 수 있고, 80 중량%를 초과하면 물리, 화학적 물성이 저하하는 문제가 있다.As a constituent component of the one-pack type blocked polyurethane high-solid resin, polyol is included in the range of 60 to 80% by weight, and if the content is less than 60% by weight, the stiffness of the product and the bending performance may be reduced, If it exceeds 80% by weight, there is a problem that physical and chemical properties are deteriorated.
상기 이소시아네이트 화합물은 폴리우레탄 제조를 위해 통상적으로 사용되는 지방족 또는 방향족 이소시아네이트 화합물을 사용할 수 있으며, 본 발명은 이의 선택에 특별한 제한을 두지 않는다. 상기 지방족 이소시아네이트 화합물은 구체적으로 헥사메틸렌 디이소시아네이트, 이소프렌 디이소시아네이트, 디시클로헥실메탄 디이소시아네이트 등으로 이루어진 군으로부터 선택된 1종 이상을 사용할 수 있다.As the isocyanate compound, an aliphatic or aromatic isocyanate compound commonly used for preparing polyurethane may be used, and the present invention does not place any particular limitation on its selection. Specifically, the aliphatic isocyanate compound may be one or more selected from the group consisting of hexamethylene diisocyanate, isoprene diisocyanate, dicyclohexylmethane diisocyanate, and the like.
상기 방향족 이소시아네이트 화합물은 구체적으로 디페닐메탄 디이소시아네이트, 나프탈렌-1,5-디이소시아네이트, 폴리페닐렌폴리메틸렌 폴리이소시아네이트, 2,4-톨릴렌 디이소시아네이트, 2,6-톨릴렌 디이소시아네이트로 이루어진 군으로부터 선택된 1종 이상을 사용할 수 있다. 특히 바람직하기로는 디페닐메탄 디이소시아네이트(MDI), 헥사메틸렌 디이소시아네이트(HDI), 이소프렌 디이소시아네이트(IPDI) 및 디시클로헥실메탄 디이소시아네이트(DCMDI)으로 이루어진 군으로부터 선택된 1종 이상을 사용할 수 있다.The aromatic isocyanate compound is specifically a group consisting of diphenylmethane diisocyanate, naphthalene-1,5-diisocyanate, polyphenylenepolymethylene polyisocyanate, 2,4-tolylene diisocyanate, and 2,6-tolylene diisocyanate At least one selected from can be used. Particularly preferably, at least one selected from the group consisting of diphenylmethane diisocyanate (MDI), hexamethylene diisocyanate (HDI), isoprene diisocyanate (IPDI), and dicyclohexylmethane diisocyanate (DCMDI) may be used.
상기 1액형 타입의 블록킹된 폴리우레탄 하이솔리드수지의 구성성분으로서 이소시아네이트 화합물은 15 ∼ 30중량% 범위로 포함되는데, 그 함량이 15 중량% 미만이면 표피층 형성이 어려울 수 있고, 30 중량%를 초과하면 점도의 상승과 제품이 딱딱해지는 문제가 있다.As a component of the one-pack type blocked polyurethane high solid resin, the isocyanate compound is included in the range of 15 to 30% by weight.If the content is less than 15% by weight, it may be difficult to form a skin layer, and if it exceeds 30% by weight There is a problem that the viscosity increases and the product becomes hard.
상기 블록킹제(blocking agent)는 이소시아네이트 화합물의 말단 NCO기를 블록킹시키기 위한 것이다. 이러한 블록킹제는 구체적으로 카프로락탐, 3,5-디메틸피라졸, 1,2,4-트리아졸, 이미다졸, 2-부타닌디에틸말로네이트, 에틸 아세토아세테이트, 메틸에틸케톡심으로 이루어지는 군에서 1종 이상을 선택하여 사용하는 것이 바람직하다.The blocking agent is for blocking the terminal NCO group of the isocyanate compound. These blocking agents are specifically in the group consisting of caprolactam, 3,5-dimethylpyrazole, 1,2,4-triazole, imidazole, 2-butaninediethylmalonate, ethyl acetoacetate, and methylethylketoxime. It is preferable to select and use at least one type.
상기 1액형 타입의 블록킹된 폴리우레탄 하이솔리드수지의 구성성분으로서 블로킹제는 5 ∼ 10 중량% 범위로 사용되는데, 그 함량이 5 중량% 미만이면 이소시아네이트 화합물의 NCO기가 충분히 블록킹되지 않을 우려가 있고, 10 중량%를 초과하여 과량이 포함되는 우레탄 경화가 느려지고, 물성이 저하될 우려가 있다.As a component of the one-pack type blocked polyurethane high solid resin, the blocking agent is used in the range of 5 to 10% by weight, and if the content is less than 5% by weight, there is a concern that the NCO group of the isocyanate compound may not be sufficiently blocked, Curing of urethane containing an excess of more than 10% by weight slows down, and there is a concern that physical properties may be deteriorated.
따라서, 본 발명의 제3 실시 예에서, 1액형 무용제 발포 폴리우레탄층(170)을 형성함에 있어서, 초경량 폴리우레탄 하이솔리드수지를 사용함으로써, 물성 및 촉감(Softness)이 우수하고, 균일한 셀(Cell)을 형성하여 일반 폴리우레탄 수지보다 높은 후도(두께)를 형성하여 볼륨감과 밀도를 낮추는 효과가 있고, 또한, 무용제 수지로서 친환경적이며, VOCs가 발생하지 않게 되는 현저한 이점을 갖는다.Therefore, in the third embodiment of the present invention, in forming the one-component solvent-free
제3실시 예에 따른 인조피혁(A3)의 각 층을 형성하는 과정은, 제1실시 예와 같은 방법으로 이루어질 수 있다.The process of forming each layer of the artificial leather A3 according to the third embodiment may be performed in the same manner as in the first embodiment.
다음으로, 본 발명의 제4실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A4)에 대하여 설명하면 다음과 같다. 제4실시 예를 설명함에 있어서, 제1실시 예와 동일한 구성에 대해서는 동일한 부호를 부여하여 설명하고, 중복 설명은 생략한다.Next, the artificial leather (A4) used as a decorative material for a cosmetic container according to a fourth embodiment of the present invention will be described as follows. In describing the fourth embodiment, the same components as those of the first embodiment are denoted by the same reference numerals, and redundant descriptions are omitted.
도 4를 참조하면, 제4 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A3)은, 이면을 형성하는 필름층(110)과, 상기 필름층의 상면에 구비되는 폼층(120)과, 상기 폼층의 상면에 구비되는 백킹 클로스층(130)과, 상기 백킹 클로스층에 상면에 도포되는 2액형 무용제 폴리우레탄층(180)과, 상기 2액형 무용제 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성된 것이다.Referring to FIG. 4, artificial leather (A3) used as a decorative material for a cosmetic container according to the fourth embodiment includes a
상기 제4실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A4)은 제1 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)과 비교하여 유성 또는 수성의 접착제층(140) 대신 2 액형 무용제 폴리우레탄층(180)이 개재된 구성의 차이만을 가진다.The artificial leather (A4) used as a decorative material for a cosmetic container according to the fourth embodiment is an oily or water-based
따라서, 제4실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A4)은 2 액형 무용제 폴리우레탄층(180)을 사용함으로써 제품의 생산성이 우수하며, 친환경적이며, 인체에 무해하고, 일반 제품에 비해 다양한 제품의 두께감을 구현할 수 있을 뿐 아니라 꺽임 및 주름이 발생하지 않으며, 이로 인해 볼륨감 및 복원력이 우수한 제품을 제공할 수 있게 된다.Therefore, the artificial leather (A4) used as a decorative material for a cosmetic container according to the fourth embodiment has excellent product productivity, eco-friendly, harmless to the human body, and a general product by using a two-component solvent-
제4실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A4)의 각 층을 형성하는 과정은, 제1실시 예와 같은 방법으로 이루어질 수 있다.The process of forming each layer of the artificial leather A4 used as a decorative material for a cosmetic container according to the fourth embodiment may be performed in the same manner as in the first embodiment.
다음으로, 본 발명의 제5실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A5)에 대하여 설명하면 다음과 같다. 제5실시 예를 설명함에 있어서, 제1실시 예와 동일한 구성에 대해서는 동일한 부호를 부여하여 설명하고, 중복 설명은 생략한다.Next, the artificial leather (A5) used as a decorative material for a cosmetic container according to a fifth embodiment of the present invention will be described as follows. In describing the fifth embodiment, the same components as those of the first embodiment are denoted by the same reference numerals, and redundant descriptions are omitted.
도 5를 참조하면, 제5 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A5)은, 이면을 형성하는 필름층(110)과, 상기 필름층의 상면에 구비되는 폼층(120)과, 상기 폼층의 상면에 구비되는 백킹 클로스층(130)과, 상기 백킹 클로스층에 상면에 구비되는 PVC / TPU 스킨(Skin)층(190)을 포함하여 구성된 것이다.Referring to FIG. 5, the artificial leather A5 used as a decorative material for a cosmetic container according to the fifth embodiment includes a
상기 제5실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A5)은 제1 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1)과 비교하여 유성 또는 수성의 접착제층(140) 및 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 제거하고, 대신에 PVC(폴리비닐클로라이드) 또는 TPU(열가소성폴리우레탄) 스킨(Skin)층(190)을 갖도록 구성된 차이만을 가진다.The artificial leather (A5) used as a decorative material for a cosmetic container according to the fifth embodiment is an oily or water-based
따라서, 제5실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A5)은, PVC(폴리비닐클로라이드) 또는 TPU(열가소성폴리우레탄) 스킨(Skin)층(190)을 가짐에 따라 경제적이며, 화장품 용기 감싸기시 꺽임 주름이 전혀 발생하지 않아 생산성이 우수하게 되는 이점을 제공하게 된다.Therefore, the artificial leather (A5) used as a decorative material for a cosmetic container according to the fifth embodiment is economical as it has a PVC (polyvinyl chloride) or TPU (thermoplastic polyurethane)
특히, PVC(폴리비닐클로라이드) 또는 TPU(열가소성폴리우레탄) 수지를 이용하여 스킨층(190)을 형성하는 인조피혁은 천연가죽이나 폴리우레탄 인조가죽에 비하여 매우 저렴한 특성을 가진다.In particular, the artificial leather forming the
제5실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A5)의 각 층을 형성하는 과정은, 제1실시 예와 같은 방법으로 이루어질 수 있다.The process of forming each layer of the artificial leather A5 used as a decoration material for a cosmetic container according to the fifth embodiment may be performed in the same manner as in the first embodiment.
위에서 설명한 본 발명의 제1 내지 제5 실시 예에 따른 화장품 용기의 장식재로 사용되는 인조피혁(A1~A5)은 도 16에 예시된 바와 같이 화장품 용기(200)의 장식재(400)로 사용될 수 있을 것이다.Artificial leather (A1 to A5) used as a decoration material for a cosmetic container according to the first to fifth embodiments of the present invention described above may be used as a
한편, 본 발명의 각 실시 예에 따른 화장품 용기의 장식재(400)로 사용되는 인조피혁(A1~A5)에 따르면, 인조피혁의 표면으로는 리얼 스티칭(stitching) 방식이나, 고주파 퀄팅(quilting) 방식(누비는 방식)에 의해 다양한 형태의 패턴(P)이 형성되어 질 수 있다.On the other hand, according to the artificial leather (A1 to A5) used as the
상기 패턴(P)은 고주파 방식으로 형성되어 질 수도 있으나, 더욱 바람직하게는 자동 스티치 머신을 이용하여 리얼 스티칭 방식으로 인조피혁에 형성함으로써 패턴의 다양한 디자인 구현이 정교하게 이루어질 수 있고, 실 두께 및 땀수 구현의 자유로움을 제공할 수 있을 것이다.The pattern P may be formed by a high frequency method, but more preferably, by forming it on the artificial leather by a real stitching method using an automatic stitching machine, various designs of the pattern can be elaborated, and the thread thickness and number of stitches It will be able to provide freedom of implementation.
도 7에 리얼 스티칭 방식으로 인조피혁에 다양한 형태의 패턴(P)이 형성된 예를 나타내었다.Fig. 7 shows an example in which various types of patterns P are formed on artificial leather by a real stitching method.
한편, 본 발명에 따른 화장품 용기의 장식재로 사용되는 인조피혁 가공 장식방법에 대하여 설명한다. 도 8은 가공장식과정을 나타내는 것이며, 도 9 내지 도 12는 각 단계별 공정에 따른 가공 상태를 설명하기 위한 도면들이다.On the other hand, the artificial leather processing decoration method used as a decoration material for a cosmetic container according to the present invention will be described. 8 shows a processing decoration process, and FIGS. 9 to 12 are views for explaining a processing state according to each step process.
도 8 및 도 9 내지 도 14를 참조하면, 화장품 용기의 장식재로 사용되는 제1 내지 제5실시 예의 인조피혁을 이용한 장식재의 가공 장식방법은,8 and 9 to 14, the processing and decoration method of a decorative material using artificial leather of the first to fifth embodiments used as a decorative material for a cosmetic container,
적정한 크기로 재단된 시트 상의 인조피혁(A1~A5)에 대하여 작업 테이블(324)에 형성된 가이드 핀(322)에 맞추어 가이드 핀 홀(312)을 형성하는 제1단계(310);A
상기 시트 상의 인조피혁(A1~A5)에 형성된 가이드 핀 홀(312)을 이용하여 인조피혁을 가이드 핀(322)이 형성된 작업 테이블(324)에 배치 고정하는 제2단계(320);A second step (320) of placing and fixing the artificial leather on the work table 324 on which the guide pins 322 are formed using the guide pin holes 312 formed in the artificial leather (A1 to A5) on the sheet;
상기 작업 테이블에 배치 고정된 인조피혁의 표면에 문양(332)을 형성하는 제3단계(330);A third step (330) of forming a pattern (332) on the surface of the artificial leather disposed and fixed on the work table;
상기 문양(332)에 맞도록 별도로 제작된 휘장(342)의 고정핀(342a)에 대응되는 홀(344)을 형성하는 제4단계(340);A
상기 인조피혁의 가장자리(352)를 화장품 용기(200)의 부착공간(220)의 형태와 높이에 맞추어 장식재(400)를 각각 가압 커팅하는 제5단계(350);A fifth step (350) of pressing and cutting the
상기 문양(332)에 대해 휘장(342)을 끼워 고정하는 제6단계(360); 를 포함하여 이루어질 수 있다.A sixth step (360) of inserting and fixing a
상기 과정에서, 인조피혁의 표면에 형성되는 문양(332)이나 휘장(342)은 표현과는 달리 각종 선전 문구일 수도 있고, 특정 형태나 형상에서 벗어나 매우 다양하고 다양한 형태로 제작될 수 있다.In the above process, the
따라서, 본 발명에 따른 인조피혁 가공 장식방법에 따르면, 화장품 용기의 장식 부착에 따른 가공 정밀도가 향상되어 각 실시 예의 인조피혁을 이용하여 가공 제작되는 장식재(400)의 부착 작업을 신속 용이하게 할 수 있고, 또 부착 외관이 미려하게 되는 이점을 제공함은 물론 회사 로그나 휘장, 이름 등을 가공하여 화장품 용기의 장식재로 사용됨으로 인해 회사 선전 및 광고 효과의 극대화가 가능하고 또 화장품 용기의 고급화가 가능하게되는 이점을 제공하게 된다.Therefore, according to the artificial leather processing decoration method according to the present invention, the processing precision according to the decoration attachment of the cosmetic container is improved, so that the attachment operation of the
한편, 각 실시 예의 인조피혁(A1~A5)을 이용하여 상기와 같은 가공 장식방법에 의해 가공된 장식재(400)는 도 15에 예시된 바와 같이 화장품 용기(200)의 부착 공간(210)에 접착되어 질 수 있고, 도 16과 같이 화장품 용기(200)의 장식재(400)로 부착 사용되어 질 수 있다.Meanwhile, the
상기한 과정을 통해 인조피혁(A1~A5)이 장식재(400)로 가공되어진 각 장식재가 부착되어지는 화장품 용기(200)의 부착공간은 다양한 위치에 형성되어 질 수 있다. Through the above-described process, artificial leather (A1 to A5) is processed into the
예컨대, 화장품 용기의 사용시, 외관상 잘 보이는 내부 뚜껑이나 외부뚜껑의 상면에 형성되어 질 수도 있고, 또 내부용기나 외부용기의 측면 등 장식이 요구되는 부분에 다양하게 형성되어 질 수 있을 것이다.For example, when a cosmetic container is used, it may be formed on an inner lid or an upper surface of an outer lid that is clearly visible in appearance, and may be variously formed on a part requiring decoration, such as an inner container or a side of an outer container.
비록, 본 발명에 첨부된 도면을 참조하여 설명되었을지라도, 본 발명은 이에 한정되지 아니하고, 하기의 특허청구범위를 벗어나지 않는 범위 내에서 많은 수정 및 변경이 있을 수 있음은 당연하다.Although described with reference to the accompanying drawings, the present invention is not limited thereto, and it is natural that many modifications and changes can be made without departing from the scope of the following claims.
본 발명에 따른 인조피혁(A1~A5)은 화장품 용기의 장식재(400)로 적합하며, 상기한 화장품 용기(200)의 장식용도로 사용됨으로써 기존의 화장품 용기에 적용되었던 인쇄 부착 등의 방법에 비하여 매우 고급스러운 장식성을 제공하게 되는 것이다. The artificial leather (A1 to A5) according to the present invention is suitable as a
110: 필름층 120: 폼층
130: 백킹 클로스층 140: 유성 또는 수성의 접착제층
150: 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층
160: 습식 폴리우레탄 은층 170: 1 액형 무용제 발포 폴리우레탄층
180: 2 액형 무용제 폴리우레탄층 190: PVC / TPU 스킨(Skin)층
200: 화장품 용기 310~360: 제1 내지 제6단계
400: 장식재 P1: 패턴110: film layer 120: foam layer
130: backing cloth layer 140: oil-based or water-based adhesive layer
150: oil-based or water-based dry polyurethane skin (Polyurethane Skin) layer
160: wet polyurethane silver layer 170: one-component solvent-free foamed polyurethane layer
180: 2-component solvent-free polyurethane layer 190: PVC / TPU skin layer
200:
400: decorative material P1: pattern
Claims (11)
상기 필름층의 상면에 구비되는 폼층(120)과,
상기 폼층의 상면에 구비되는 백킹 클로스층(130)과,
상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과,
상기 접착제층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150), 을 포함하여 구성됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The film layer 110 forming the back surface,
A foam layer 120 provided on the upper surface of the film layer,
A backing cloth layer 130 provided on the upper surface of the foam layer,
An oil-based or water-based adhesive layer 140 applied to the upper surface of the backing cloth layer,
Artificial leather used as a decorative material for a cosmetic container, comprising an oily or water-based dry polyurethane skin layer 150 provided on the upper surface of the adhesive layer to form a surface.
상기 필름층의 상면에 구비되는 폼층(120)과,
상기 폼층의 상면에 구비되는 백킹 클로스층(130)과,
상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과,
상기 접착제 층의 상면에 구비되는 습식 폴리우레탄 은층(160)과,
상기 습식 폴리우레탄(Polyurethane) 은층(Micro porous layer)의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The film layer 110 forming the back surface,
A foam layer 120 provided on the upper surface of the film layer,
A backing cloth layer 130 provided on the upper surface of the foam layer,
An oil-based or water-based adhesive layer 140 applied to the upper surface of the backing cloth layer,
A wet polyurethane silver layer 160 provided on the upper surface of the adhesive layer,
A cosmetic container decorative material comprising an oily or water-based dry polyurethane skin layer 150 provided on the upper surface of the wet polyurethane silver layer to form the surface. Artificial leather used as.
상기 필름층의 상면에 구비되는 폼층(120)과,
상기 폼층의 상면에 구비되는 백킹 클로스층(130)과,
상기 백킹 클로스층에 상면에 도포되는 유성 또는 수성의 접착제층(140)과,
상기 접착제 층의 상면에 구비되는 1 액형 무용제 발포 폴리우레탄층(170)과,
상기 1 액형 무용제 발포 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The film layer 110 forming the back surface,
A foam layer 120 provided on the upper surface of the film layer,
A backing cloth layer 130 provided on the upper surface of the foam layer,
An oil-based or water-based adhesive layer 140 applied to the upper surface of the backing cloth layer,
A one-component solvent-free foamed polyurethane layer 170 provided on the upper surface of the adhesive layer,
Artificial leather used as a decorative material for cosmetic containers, characterized in that it comprises an oily or water-based dry polyurethane skin layer 150 provided on the upper surface of the one-component solvent-free foamed polyurethane layer to form the surface .
상기 필름층의 상면에 구비되는 폼층(120)과,
상기 폼층의 상면에 구비되는 백킹 클로스층(130)과,
상기 백킹 클로스층에 상면에 도포되는 2 액형 무용제 폴리우레탄층(180)과,
상기 2 액형 무용제 폴리우레탄층의 상면에 구비되어 표면을 형성하는 유성 또는 수성의 건식 폴리우레탄 스킨(Polyurethane Skin)층(150)을 포함하여 구성됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The film layer 110 forming the back surface,
A foam layer 120 provided on the upper surface of the film layer,
A backing cloth layer 130 provided on the upper surface of the foam layer,
A two-component solvent-free polyurethane layer 180 applied to the upper surface of the backing cloth layer,
Artificial leather used as a decorative material for cosmetic containers, characterized in that it comprises an oily or water-based dry polyurethane skin layer 150 provided on the upper surface of the two-component solvent-free polyurethane layer to form the surface.
상기 필름층의 상면에 구비되는 폼층(120)과,
상기 폼층의 상면에 구비되는 백킹 클로스층(130)과,
상기 백킹 클로스층에 상면에 구비되는 PVC / TPU 스킨(Skin)층(190)을 포함하여 구성됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The film layer 110 forming the back surface,
A foam layer 120 provided on the upper surface of the film layer,
A backing cloth layer 130 provided on the upper surface of the foam layer,
Artificial leather used as a decoration material for a cosmetic container, characterized in that it comprises a PVC / TPU skin layer (190) provided on the upper surface of the backing cloth layer.
상기 필름층(110)은 폴리프로필렌(PP), 폴리카보네이트(PC), 폴리에틸렌(PE), 폴리에틸렌테레프탈레이트(PET) 중 어느 하나가 선택 사용되어 지고, 그 두께는 10~300㎛의 두께(T) 범위 내로 이루어짐을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The method according to any one of claims 1 to 5,
The film layer 110 is selected from one of polypropylene (PP), polycarbonate (PC), polyethylene (PE), and polyethylene terephthalate (PET), and the thickness is 10 to 300 μm (T ) Artificial leather used as a decorative material for cosmetic containers, characterized in that it is made within the range.
상기 폼층(120)은 폴리우레탄 습식 폼(PU FORM), 고밀도 건식 발포우레탄 폼(PORON), 올레핀 폼(OLEFINFROM), 열가소성폴리올레핀(TPO: Thermoplastic Olefin), 열가소성엘라스토머(TPE: Thermoplastic Elastomer), PUD Foam(수성), 아크릴 폼, TPU폼 중 어느 하나가 선택 사용되어지고, 그 두께는 50~500㎛의 두께(T) 범위 내로 이루어짐을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The method according to any one of claims 1 to 5,
The foam layer 120 is polyurethane wet foam (PU FORM), high density dry foam urethane foam (PORON), olefin foam (OLEFINFROM), thermoplastic polyolefin (TPO: Thermoplastic Olefin), thermoplastic elastomer (TPE: Thermoplastic Elastomer), PUD Foam Artificial leather used as a decorative material for cosmetic containers, characterized in that any one of (aqueous), acrylic foam, and TPU foam is selected and the thickness is within a thickness (T) range of 50 to 500 μm.
상기 백킹 클로스층(130)은, 직물, 편물, 극세사, 부직포, 함침포 중 어느 하나가 사용됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The method according to any one of claims 1 to 5,
The backing cloth layer 130 is artificial leather used as a decorative material for a cosmetic container, characterized in that any one of fabric, knitted fabric, microfiber, nonwoven fabric, and impregnated fabric is used.
상기 인조피혁의 표면으로는 리얼 스티칭 방식이나, 또는 고주파 퀄팅 방식(누비는 방식)에 의해 다양한 형태의 패턴(P)이 더 형성되어 짐을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁.The method according to any one of claims 1 to 5,
Artificial leather used as a decorative material for cosmetic containers, characterized in that various patterns P are further formed on the surface of the artificial leather by a real stitching method or a high frequency qualifying method (quilting method).
적정한 크기로 재단된 시트 상의 인조피혁(A1~A5)에 대하여 작업 테이블(322)에 형성된 가이드 핀(324)에 맞추어 가이드 핀 홀(312)을 형성하는 제1단계(310);
상기 시트 상의 인조피혁(A1~A5)에 형성된 가이드 핀 홀(312)을 이용하여 인조피혁을 가이드 핀(324)이 형성된 작업 테이블(322)에 배치 고정하는 제2단계(320);
상기 작업 테이블에 배치 고정된 인조피혁의 표면에 문양(332)을 형성하는 제3단계(330);
상기 문양(332)에 맞도록 별도로 제작된 휘장(342)의 고정핀(342a)에 대응되는 홀(344)을 형성하는 제4단계(340);
상기 인조피혁의 가장자리(352)를 화장품 용기(200)의 부착공간(210)의 형태와 높이에 맞추어 각각의 장식재(400)로 가압 커팅하는 제5단계(350);
상기 문양(332)에 대해 휘장(342)을 끼워 고정하는 제6단계(360); 를 포함하여 가공 장식됨을 특징으로 하는 화장품 용기의 장식재로 사용되는 인조피혁의 가공 장식방법.A method for processing and decorating artificial leather used as a decoration material for cosmetic containers falling under any one of claims 1 to 5,
A first step 310 of forming a guide pin hole 312 in conformity with the guide pin 324 formed on the work table 322 with respect to the artificial leather (A1 to A5) on the sheet cut to an appropriate size;
A second step (320) of placing and fixing the artificial leather on the work table 322 on which the guide pins 324 are formed using the guide pin holes 312 formed in the artificial leather (A1 to A5) on the sheet;
A third step (330) of forming a pattern (332) on the surface of the artificial leather disposed and fixed on the work table;
A fourth step 340 of forming a hole 344 corresponding to the fixing pin 342a of the insignia 342 separately manufactured to fit the pattern 332;
A fifth step (350) of pressing and cutting the edge 352 of the artificial leather with each decorative material 400 according to the shape and height of the attachment space 210 of the cosmetic container 200;
A sixth step (360) of inserting and fixing a drapery 342 with respect to the pattern 332; Processing and decoration method of artificial leather used as a decorative material of a cosmetic container, characterized in that the processing and decoration including.