KR102113222B1 - Coating composition for separator of secondary battery comprising P-doped graphitic carbon nitride, preparation method thereof and Li-S battery comprising the same - Google Patents

Coating composition for separator of secondary battery comprising P-doped graphitic carbon nitride, preparation method thereof and Li-S battery comprising the same Download PDF

Info

Publication number
KR102113222B1
KR102113222B1 KR1020180068089A KR20180068089A KR102113222B1 KR 102113222 B1 KR102113222 B1 KR 102113222B1 KR 1020180068089 A KR1020180068089 A KR 1020180068089A KR 20180068089 A KR20180068089 A KR 20180068089A KR 102113222 B1 KR102113222 B1 KR 102113222B1
Authority
KR
South Korea
Prior art keywords
secondary battery
carbon nitride
phosphorus
separator
coating
Prior art date
Application number
KR1020180068089A
Other languages
Korean (ko)
Other versions
KR20190141392A (en
Inventor
조원일
도반중
김문석
김민섭
나인욱
Original Assignee
한국과학기술연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국과학기술연구원 filed Critical 한국과학기술연구원
Priority to KR1020180068089A priority Critical patent/KR102113222B1/en
Publication of KR20190141392A publication Critical patent/KR20190141392A/en
Application granted granted Critical
Publication of KR102113222B1 publication Critical patent/KR102113222B1/en

Abstract

본 발명은 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물, 이의 제조방법 및 이를 포함하는 리튬-황 이차전지에 관한 것으로, 보다 상세하게는 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용할 수 있다.The present invention relates to a composition for coating a secondary battery separator comprising phosphorus-doped graphite carbon nitride, a method of manufacturing the same, and a lithium-sulfur secondary battery including the same, and more specifically, a secondary battery including phosphorus-doped graphite carbon nitride By coating the separator coating composition on the separator of a lithium-sulfur secondary battery, it is possible to prevent diffusion movement of polysulfide eluted from the positive electrode and to reversibly reuse it as an active material, thereby providing high coulomb efficiency and discharge capacity even under positive electrode conditions of high energy density. It can be applied as a lithium-sulfur secondary battery having a long life characteristic.

Description

인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물, 이의 제조방법 및 이를 포함하는 리튬-황 이차전지{Coating composition for separator of secondary battery comprising P-doped graphitic carbon nitride, preparation method thereof and Li-S battery comprising the same}A composition for coating a secondary battery separator containing phosphorus doped graphite carbon nitride, a method for manufacturing the same, and a lithium-sulfur secondary battery comprising the same P-doped graphitic carbon nitride, preparation method thereof and Li- S battery comprising the same}

본 발명은 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물, 이의 제조방법 및 이를 포함하는 리튬-황 이차전지에 관한 것으로, 보다 상세하게는 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용하는 기술에 관한 것이다.
The present invention relates to a composition for coating a secondary battery separator comprising phosphorus-doped graphite carbon nitride, a method of manufacturing the same, and a lithium-sulfur secondary battery including the same, and more specifically, a secondary battery including phosphorus-doped graphite carbon nitride By coating the separator coating composition on the separator of a lithium-sulfur secondary battery, it is possible to prevent diffusion movement of polysulfide eluted from the positive electrode and to reversibly reuse it as an active material, thereby providing high coulomb efficiency and discharge capacity even under positive electrode conditions of high energy density. It relates to a technology applied as a lithium-sulfur secondary battery having a long lifespan characteristic.

리튬이온 이차전지는 1991년 일본의 소니 (Sony)사에 의해 상용화가 이루어지고, 1990년대 이후 휴대용 전자기기의 필수불가결한 부품으로 자리잡게 되었다. 특히, 2000년대 후반부터 스마트폰, 디지털 카메라, 노트북 등과 같은 휴대용 전자기기의 사용량이 폭발적으로 증가하면서, 리튬이온 이차전지의 시장 및 중요성은 더더욱 성장하였다. 하지만 여기서 멈추지 않고, 근래에는 전기자동차 (Electric Vehicle, EV) 및 대용량 에너지저장시스템 (Energy Storage System) 분야까지 이차전지의 응용 분야가 확장하면서, 그 중요성은 다시 한 번 커지고 있다. Lithium-ion secondary batteries were commercialized in 1991 by Sony in Japan, and have become an integral part of portable electronic devices since the 1990s. In particular, since the use of portable electronic devices such as smart phones, digital cameras, and laptops has increased explosively since the late 2000s, the market and importance of lithium-ion secondary batteries have grown even more. However, it does not stop here, and in recent years, as the field of application of secondary batteries has expanded to the fields of electric vehicles (EVs) and large-capacity energy storage systems (Energy Storage Systems), its importance is growing once again.

하지만 지금까지 상용화된 리튬이온 이차전지 시스템에는, 현재 소형 전지 시스템에서의 커져가는 소비자의 요구와 가까운 미래에 다가올 전기자동차 시장 및 대용량 에너지저장시스템의 요구를 충족시키는 데에 태생적인 한계점이 존재한다. 그 태생적인 한계점은 바로 낮은 용량 (Capacity)이다. 기존의 리튬이온 이차전지는 ~ 270 mAh/g의 용량을 갖는 전이금속산화물 양극과 ~ 372 mAh/g의 용량을 갖는 흑연 음극으로 이루어져있다. 이러한 리튬이온의 단순한 삽입/탈리 (Intercalation/de-intercalation) 반응으로 나타나는 낮은 용량의 이차전지가 전기자동차에 적용될 경우, 한 번 충전으로 운행할 수 있는 거리가 매우 짧아 기존의 자동차 시장을 뛰어넘을 수 없게 된다.However, the commercially available lithium ion secondary battery system has inherent limitations in meeting the needs of the electric vehicle market and the large-capacity energy storage system, which will be approached in the near future with the growing consumer demand in the small battery system. Its inherent limitation is its low capacity. The existing lithium ion secondary battery is composed of a transition metal oxide positive electrode having a capacity of ~ 270 mAh / g and a graphite negative electrode having a capacity of ~ 372 mAh / g. When a low-capacity secondary battery, which is represented by a simple intercalation / de-intercalation reaction of lithium ion, is applied to an electric vehicle, the distance that can be operated by a single charge is very short, which can exceed the existing automobile market. There will be no.

리튬-황 이차전지는 이러한 기존의 리튬이온 이차전지의 낮은 용량 한계점을 뛰어넘는 차세대 이차전지의 대표주자이다. 리튬-황 이차전지는 황을 전기화학 반응의 활물질로 사용하고, ~1,675 mAh/g의 높은 이론 용량을 갖는 시스템이다. ~3,860 mAh/g의 이론 용량을 갖는 리튬금속을 음극으로 사용하여, 약 2,600 Wh/kg의 에너지 밀도를 나타내며, 이는 기존 리튬이온 이차전지 (LiCoO2/graphite) 시스템의 에너지 밀도 (~ 400 Wh/kg)보다 약 ~ 7, 8배 이상 큰 수치이다. 이러한 리튬-황 이차전지의 가능성은 1960년대에 이미 발표되었지만, 많은 어려움 탓에 최근까지 연구가 활발히 이루어지지 않았다. 그러나 2009년, 캐나다의 Linda F. Nazar 그룹에서 메조포러스 카본 (Mesoporous carbon)과 황의 복합체를 제조하여 리튬-황 이차전지의 특성을 향상시킨 연구 결과가 발표되면서 리튬-황 이차전지에 대한 연구가 전세계에서 폭발적으로 이뤄지고 있다.The lithium-sulfur secondary battery is a representative of the next generation secondary battery that surpasses the low capacity limit of the existing lithium ion secondary battery. The lithium-sulfur secondary battery is a system that uses sulfur as an active material in an electrochemical reaction and has a high theoretical capacity of ~ 1,675 mAh / g. Using a lithium metal with a theoretical capacity of ~ 3,860 mAh / g as a negative electrode, it shows an energy density of about 2,600 Wh / kg, which is the energy density of a conventional lithium ion secondary battery (LiCoO 2 / graphite) system (~ 400 Wh / It is about ~ 7, 8 times larger than kg). The possibility of such a lithium-sulfur secondary battery was already announced in the 1960s, but due to many difficulties, research has not been actively conducted until recently. However, in 2009, the Canadian Linda F. Nazar group published a study that improved the properties of lithium-sulfur secondary batteries by manufacturing a composite of mesoporous carbon and sulfur. In the explosion.

이러한 큰 장점에도 불구하고, 리튬-황 이차전지의 상용화를 위해선 해결해야 할 문제점이 존재한다. 리튬-황 이차전지의 첫 번째 문제점은 활물질로 사용하는 황의 매우 낮은 전기전도도이다. 황의 전기전도도는 5 x 10-30 S/cm으로 거의 부도체와 가깝고, 최종 방전물질인 Li2S 또한 전기적 부도체이다. 따라서 전자의 통로를 효과적으로 제공할 수 있는 도전재가 필수적이다. 두 번째 문제점은 충·방전 과정 사이에 발생하는 황의 부피 팽창이다. 활물질 황(S8)과 최종 방전물질인 Li2S는 각각 밀도가 2.07 g/cm3, 1.66 g/cm3으로, 약 80%의 부피 차이가 나타난다. 이러한 부피 팽창으로 인한 전극의 안정성 문제점을 해결하기 위해, 리튬-황 이차전지에 사용되는 도전재는 전자 통로 역할뿐만 아니라 동시에 부피 팽창 또한 완화시켜줄 수 있어야 한다. 세 번째 문제점은 소위 "셔틀 반응 (Shuttle reaction)"으로 알려진 현상이다. 방전 과정 중에 생성되는 반응 중간물질인 폴리설파이드 물질들 (Polysulfide species) 중, 긴 사슬(long chain) 폴리설파이드 형태인 Li2Sn (4 ≤ n ≤ 8) 물질은 에테르 (Ether) 계열의 전해질에 잘 용해되는 성질이 있다. 이렇게 용해되어 나온 폴리설파이드 물질은 양극으로부터 분리막을 통과하여 리튬금속 음극까지 확산되어 이동하게 되고, 리튬금속 음극과 화학적인 부반응 또한 일으키게 된다. 따라서 양극 내의 활물질 손실 및 리튬금속 음극 표면 상태 악화와 같은 심각한 문제점을 야기하여 결과적으로 리튬-황 이차전지의 수명 특성을 악화시킨다. 최근까지 셔틀 반응으로 인한 문제점을 억제하기 위하여, 양극의 탄소 구조체 개발과 분리막 표면 코팅, 전해질 개발 등을 통해 폴리설파이드의 확산을 막을 수 있도록 다양하게 노력하였다. 하지만 대부분 낮은 에너지 밀도의 양극을 바탕으로 가능성을 보여준 실험 결과들이 주를 이루었다. 앞으로 리튬-황 이차전지의 가장 큰 장점을 구현하기 위한, 실제 고에너지 밀도의 양극 조건에서는 셔틀 반응을 비롯한 문제점들이 더욱 심각하게 나타나게 된다.Despite these great advantages, there are problems to be solved for commercialization of lithium-sulfur secondary batteries. The first problem with lithium-sulfur secondary batteries is the very low electrical conductivity of sulfur used as an active material. The electrical conductivity of sulfur is 5 x 10 -30 S / cm, almost close to the non-conductor, and the final discharge material Li 2 S is also an electrical non-conductor. Therefore, a conductive material that can effectively provide electron passages is essential. The second problem is the volumetric expansion of sulfur that occurs between charge and discharge processes. The active material sulfur (S 8 ) and the final discharge material, Li 2 S, have densities of 2.07 g / cm 3 and 1.66 g / cm 3 , respectively, showing a volume difference of about 80%. In order to solve the stability problem of the electrode due to the volume expansion, the conductive material used in the lithium-sulfur secondary battery should be able to mitigate the volume expansion as well as the role of the electron passage. The third problem is a phenomenon known as the "Shuttle reaction". Among the polysulfide species, which are reaction intermediates generated during the discharging process, the long chain polysulfide Li 2 S n (4 ≤ n ≤ 8) material is added to the ether-based electrolyte. It has properties that dissolve well. The polysulfide material thus dissolved passes through the separator from the positive electrode to the lithium metal negative electrode and diffuses, and also causes a chemical side reaction with the lithium metal negative electrode. Therefore, it causes serious problems such as loss of the active material in the positive electrode and deterioration of the surface condition of the lithium metal negative electrode, resulting in deterioration of the life characteristics of the lithium-sulfur secondary battery. Until recently, in order to suppress the problems caused by the shuttle reaction, various efforts have been made to prevent diffusion of polysulfide through carbon structure development of the anode, surface coating of the separator, and development of electrolyte. However, most of the experiment results showed the possibility based on the anode with low energy density. In the future, in order to realize the greatest advantage of the lithium-sulfur secondary battery, problems including shuttle reaction will be more serious in an anode condition of a real high energy density.

따라서, 본 발명자는 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용할 수 있음에 착안하여 본 발명을 완성하기에 이르렀다.
Therefore, the present inventors coated a composition for coating a secondary battery separator containing phosphorus doped graphite carbon nitride on a separator of a lithium-sulfur secondary battery, preventing diffusion movement of polysulfide eluted from the positive electrode and reversible reuse as an active material By doing so, the present invention has been completed by focusing on the fact that it can be applied as a lithium-sulfur secondary battery having high coulomb efficiency and discharge capacity even under high energy density anode conditions and having long life characteristics.

비특허문헌 1. Hu, Shaozheng, et al. Applied Surface Science 311 (2014): 164-171.Non-Patent Document 1. Hu, Shaozheng, et al. Applied Surface Science 311 (2014): 164-171. 비특허문헌 2. Zhang, Yuanjian, et al. Journal of the American Chemical Society 132.18 (2010): 6294-6295.Non-patent document 2. Zhang, Yuanjian, et al. Journal of the American Chemical Society 132.18 (2010): 6294-6295. 비특허문헌 3. Zhu, Yun-Pei, Tie-Zhen Ren, and Zhong-Yong Yuan. ACS applied materials & interfaces 7.30 (2015): 16850-16856.Non-patent document 3. Zhu, Yun-Pei, Tie-Zhen Ren, and Zhong-Yong Yuan. ACS applied materials & interfaces 7.30 (2015): 16850-16856. 비특허문헌 4. Ran, Jingrun, et al. Energy & Environmental Science 8.12 (2015): 3708-3717.Non-Patent Document 4. Ran, Jingrun, et al. Energy & Environmental Science 8.12 (2015): 3708-3717.

본 발명은 상기와 같은 문제점을 고려하여 안출된 것으로, 본 발명의 목적은 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용하고자 하는 것이다.
The present invention has been devised in consideration of the above problems, and an object of the present invention is to coat a composition for coating a secondary battery separator containing phosphorus doped graphite carbon nitride on a separator of a lithium-sulfur secondary battery and eluted from the positive electrode. It is intended to be applied as a lithium-sulfur secondary battery having high coulombic efficiency and discharge capacity even under high energy density anode conditions by enabling diffusion of polysulfide and preventing reversible reuse as an active material.

상기한 바와 같은 목적을 달성하기 위한 본 발명의 일 측면은 흑연질 탄소질화물(Graphitic Carbon Nitride, gCN)을 포함하는 이차전지 분리막 코팅용 조성물에 관한 것이다.One aspect of the present invention for achieving the object as described above relates to a composition for coating a secondary battery separator comprising a graphite carbon nitride (Graphitic Carbon Nitride, gCN).

본 발명의 다른 측면은 본 발명에 따른 이차전지 분리막 코팅용 조성물의 코팅층이 상기 분리막의 표면에 형성되어 있는 이차전지 분리막에 관한 것이다. Another aspect of the present invention relates to a secondary battery separator in which a coating layer of a composition for coating a secondary battery separator according to the present invention is formed on the surface of the separator.

본 발명의 또 다른 측면은 본 발명에 따른 이차전지 분리막을 포함하는 리튬-황 이차전지로서, 상기 코팅층은 상기 이차전지의 양극을 향하는 상기 분리막 일면의 표면에 형성되어 있는 것을 특징으로 하는 리튬-황 이차전지에 관한 것이다.Another aspect of the present invention is a lithium-sulfur secondary battery including a secondary battery separator according to the present invention, wherein the coating layer is formed on a surface of one surface of the separator facing the anode of the secondary battery. It relates to a secondary battery.

본 발명의 또 다른 측면은 본 발명에 따른 이차전지 분리막 코팅용 조성물을 포함하는 전기 디바이스로서, 상기 전기 디바이스는 전기자동차, 하이브리드 전기자동차, 플러그-인 하이브리드 전기자동차 및 전력 저장장치 중에서 선택되는 1종인 것을 특징으로 하는 전기 디바이스에 관한 것이다.Another aspect of the present invention is an electric device comprising a composition for coating a secondary battery separator according to the present invention, wherein the electric device is one selected from an electric vehicle, a hybrid electric vehicle, a plug-in hybrid electric vehicle and a power storage device. It relates to an electrical device characterized in that.

본 발명의 또 다른 측면은 멜라민 및 요소의 혼합물을 열처리하는 단계;를 포함하는 흑연질 탄소질화물의 제조방법에 관한 것이다.Another aspect of the present invention relates to a method for preparing a graphitic carbon nitride comprising; heat-treating a mixture of melamine and urea.

본 발명의 또 다른 측면은 멜라민, 요소 및 인 전구체의 혼합물을 열처리하는 단계;를 포함하는 인 도핑 흑연질 탄소질화물의 제조방법에 관한 것이다.
Another aspect of the present invention relates to a method for producing a phosphorus-doped graphitic carbon nitride comprising; heat-treating a mixture of melamine, urea and phosphorus precursors.

본 발명에 따르면, 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용할 수 있다.
According to the present invention, a composition for coating a secondary battery separation membrane containing phosphorus doped graphite carbon nitride is coated on a separation membrane of a lithium-sulfur secondary battery, preventing diffusion movement of polysulfide eluted from the positive electrode and reversible reuse as an active material By doing so, it can be applied as a lithium-sulfur secondary battery having high coulomb efficiency and discharge capacity even under high energy density anode conditions and having long life characteristics.

도 1은 본 발명의 실시예 1로부터 흑연질 탄소질화물(C3N4, CN) 합성 시 사용되는 두 가지 전구체인 멜라민과 요소의 중량비에 따른 BET 비표면적을 나타낸 (a) 표, (b) 그래프 및 (c) 특히, 3/7 중량비 조건의 그래프이다.
도 2는 본 발명의 실시예 2로부터 인 도핑 흑연질 탄소질화물(PgC3N4, PgCN) 합성 시 제2 인산암모늄의 함량에 따른 인 도핑 농도를 나타낸 표이다.
도 3은 (a) PgCN 합성의 반응 과정을 나타내는 모식도, (b) 합성된 gCN의 분말 이미지 및 (c) 합성된 PgCN의 분말 이미지이다.
도 4는 흑연질 탄소질화물 합성 시 사용되는 두 가지 전구체인 멜라민과 요소의 혼합이 최종 생성물 합성의 수득률에 미치는 효과를 보여주는 (a) 표와 (b) 이미지이다.
도 5는 본 발명의 실시예 1 및 2로부터 합성된 (a) gCN과 (b) PgCN의 전자주사현미경(SEM) 이미지이다.
도 6은 본 발명의 실시예 1 및 2로부터 합성된 (a) gCN과 PgCN의 열중량 분석 결과와 (b) PgCN의 EDX 분석 결과이다.
도 7은 1 M LiTFSI-DME/DOL(1:1, 부피비) 전해질 용액에, 본 발명의 실시예 1 및 2로부터 합성된 gCN과 PgCN 분말을 넣어, 시간 경과에 따른 폴리설파이드 흡착 효과를 시각적으로 확인하는 이미지이다.
도 8은 PgCN/C가 코팅된 분리막을 사용하여 실제 리튬-황 이차전지 시스템에 적용하여 1 C-rate에서의 전기화학적 수명 특성을 평가한 결과이다[(a) 사이클에 따른 방전용량, (b) 사이클에 따른 쿨롱 효율, (c) 용량-전압 변화].
1 is a table showing (a) BET specific surface area according to the weight ratio of melamine and urea, which are two precursors used in the synthesis of graphitic carbon nitride (C 3 N 4 , CN) from Example 1 of the present invention, (b) Graphs and (c) in particular, 3/7 weight ratio conditions.
Figure 2 is a table showing the phosphorus doping concentration according to the content of the second ammonium phosphate in the synthesis of phosphorus doped graphite carbon nitride (PgC 3 N 4 , PgCN) from Example 2 of the present invention.
3 is a schematic view showing the reaction process of (a) PgCN synthesis, (b) powder image of synthesized gCN and (c) powder image of synthesized PgCN.
FIG. 4 is a table (a) and (b) images showing the effect of mixing two precursors, melamine and urea, used in the synthesis of graphitic carbon nitride on the yield of final product synthesis.
5 is an electron scanning microscope (SEM) image of (a) gCN and (b) PgCN synthesized from Examples 1 and 2 of the present invention.
6 is a result of the thermogravimetric analysis of (a) gCN and PgCN synthesized from Examples 1 and 2 of the present invention and (b) EDX analysis of PgCN.
7 is a 1 M LiTFSI-DME / DOL (1: 1, volume ratio) electrolyte solution, gCN and PgCN powder synthesized from Examples 1 and 2 of the present invention, the visual effect of the polysulfide adsorption over time It is an image to check.
8 is a result of evaluating the electrochemical life characteristics at 1 C-rate by applying to a real lithium-sulfur secondary battery system using a PgCN / C coated separator ((a) discharge capacity according to cycle, (b ) Coulomb efficiency with cycle, (c) Capacity-voltage change].

종래 낮은 에너지 밀도를 갖는 얇은 전극을 사용한 리튬-황 이차전지의 성능은 다양한 양극 물질 개발이나 분리막 개질 등을 통해 좋은 전지 특성을 갖게 되었다. 하지만 현재 상용화된 리튬이온 이차전지를 뛰어넘기 위해서는 리튬-황 이차전지가 고에너지 밀도의 양극을 사용해야 한다. 고에너지 밀도의 양극을 개발하기 위해 양극 성분 중 황 활물질의 조성이 증가하거나 양극이 두꺼워지면서 양극 내 황의 로딩양이 크게 증가하고, 결국 태생적인 리튬-황 이차전지의 문제점이 재발하여 제어하기 어려워지게 된다. 특히 셔틀 반응을 일으키는 폴리설파이드의 절대적인 용출량이 매우 증가하기 때문에 이를 적절히 제어하지 못할 경우, 양극 내 활물질의 손실과 리튬 음극의 부식으로 인한 전지의 쿨롱 효율 및 수명 저하가 급격하게 일어나게 된다. 본 발명에 따르면 강한 극성 물질과 탄소 물질의 조합으로 표면이 코팅된 분리막 개질 방법을 통하여 위의 쿨롱 효율 및 수명 저하 현상을 해결할 수 있다.The performance of a lithium-sulfur secondary battery using a thin electrode having a low energy density in the related art has good battery characteristics through development of various positive electrode materials or membrane modification. However, in order to overcome the current commercially available lithium ion secondary batteries, lithium-sulfur secondary batteries need to use high energy density anodes. In order to develop a positive electrode with high energy density, the amount of sulfur in the positive electrode increases significantly as the composition of the sulfur active material among the positive electrode components increases or the positive electrode thickens, and eventually the problem of the native lithium-sulfur secondary battery recurs and becomes difficult to control. do. In particular, since the absolute elution amount of polysulfide that causes a shuttle reaction is very increased, if it is not properly controlled, the coulombic efficiency and lifespan of the battery due to the loss of the active material in the positive electrode and corrosion of the lithium negative electrode rapidly occur. According to the present invention, it is possible to solve the above phenomenon of Coulomb efficiency and lifetime reduction through a method of reforming a membrane coated with a strong polar material and a carbon material.

이하에서, 본 발명의 여러 측면 및 다양한 구현예에 대해 더욱 구체적으로 설명한다.Hereinafter, various aspects and various embodiments of the present invention will be described in more detail.

본 발명의 일 측면은 흑연질 탄소질화물(Graphitic Carbon Nitride, gCN)을 포함하는 이차전지 분리막 코팅용 조성물에 관한 것이다.One aspect of the present invention relates to a composition for coating a secondary battery separation membrane comprising graphite carbon nitride (gCN).

상기 흑연질 탄소질화물을 포함하는 분리막 코팅용 조성물이 적용된 리튬-황 이차전지의 경우, 양극에서 용출된 폴리설파이드의 확산 이동 방지에 효과적이며, 이를 통하여 리튬 음극의 안정성 또한 향상시킬 수 있기 때문에, 전체적인 리튬-황 이차전지의 장수명 특성을 확보할 수 있다.In the case of the lithium-sulfur secondary battery to which the composition for coating a separator containing the graphite carbon nitride is applied, it is effective in preventing diffusion movement of polysulfide eluted from the positive electrode, and through this, stability of the lithium negative electrode can also be improved. Long life characteristics of the lithium-sulfur secondary battery can be secured.

특이하게도, 본 발명에 따른 이차전지 분리막 코팅용 조성물을 이차전지의 분리막 상에 코팅할 경우에는 황의 용융온도 이상의 고온(60 내지 80 ℃ 이상)에서도 황이 전지의 전극 외부로 전혀 누설되지 않는 것을 확인하였다. 반면, 분리막이 아닌 음극 또는 양극 상에 코팅하거나, 상기 코팅용 조성물의 코팅층이 상기 분리막과 상기 음극 또는 양극 사이에 존재하거나, 또는 상기 코팅용 조성물이 전해질 상에 함유되어 있는 경우에는 60 내지 80 ℃ 이상에서 황이 전극 외부로 누설됨을 확인하였다.Specifically, when coating the composition for coating a secondary battery separator according to the present invention on a separator of a secondary battery, it was confirmed that sulfur is not leaked to the outside of the electrode of the battery even at a high temperature (60 to 80 ° C. or higher) above the melting temperature of sulfur. . On the other hand, when coating on a cathode or an anode, not a separator, a coating layer of the coating composition is present between the separator and the cathode or anode, or when the coating composition is contained on the electrolyte, 60 to 80 ° C From the above, it was confirmed that sulfur leaked out of the electrode.

일 구현예에 따르면, 상기 분리막은 폴리프로필렌, 폴리올레핀 및 부직포 중에서 선택되는 1종 이상일 수 있으며, 이에 한정되는 것은 아니다. 바람직하게는 폴리프로필렌일 수 있다.According to one embodiment, the separator may be at least one selected from polypropylene, polyolefin, and nonwoven fabric, but is not limited thereto. It may be preferably polypropylene.

다른 구현예에 따르면, 상기 흑연질 탄소질화물은 인 도핑된, 인 도핑 흑연질 탄소질화물(P-doped Graphitic Carbon Nitride, PgCN)일 수 있다.According to another embodiment, the graphite carbon nitride may be phosphorus doped, phosphorus doped graphite carbon nitride (P-doped Graphitic Carbon Nitride, PgCN).

특히, 상기 gCN과 달리 인이 도핑된 경우, 도핑된 인은 폴리설파이드 물질과 화학적 결합을 통해 화학적 흡착을 할 수 있다. 이는 반데르발스 힘과 같은 정전기력에 의한 단순 물리적 흡착에 비해 화학적 결합을 형성하여 화학적 흡착이 일어나기 때문에 폴리설파이드의 확산을 더욱 효과적으로 포집해둘 수 있다.In particular, unlike the gCN, when phosphorus is doped, the doped phosphorus can be chemically adsorbed through chemical bonding with a polysulfide material. This is because the chemical adsorption occurs due to the formation of chemical bonds compared to simple physical adsorption by electrostatic forces such as van der Waals forces, so that the diffusion of polysulfide can be more effectively captured.

또 다른 구현예에 따르면, 상기 인의 함량은 상기 인 도핑 흑연질 탄소질화물 전체 중량을 기준으로 1 내지 50 at%, 바람직하게는 10 내지 40 at%, 더욱 바람직하게는 20 내지 25 at%일 수 있다.According to another embodiment, the content of the phosphorus may be 1 to 50 at%, preferably 10 to 40 at%, more preferably 20 to 25 at%, based on the total weight of the phosphorus doped graphite carbon nitride. .

상기 인의 도핑 함량이 상기 수치 범위(1 내지 50 at%)를 벗어나는 경우에는 인 도핑 흑연질 탄소질화물의 2차 입자가 서로 응집(agglomeration)되어 폴리설파이드의 포집 효과가 저하됨을 확인하였다.When the doping content of the phosphorus was outside the numerical range (1 to 50 at%), it was confirmed that secondary particles of the phosphorus doped graphite carbon nitride were agglomerated with each other to reduce the collection effect of polysulfide.

또 다른 구현예에 따르면, 상기 인 도핑 흑연질 탄소질화물은 복수 개의 1차 입자가 응집된 형태의 2차 입자로 형성되고, 상기 1차 입자의 입경은 1 내지 120 nm이며, 상기 2차 입자의 입경은 200 내지 600 nm인 것일 수 있다.According to another embodiment, the phosphorus-doped graphitic carbon nitride is formed of secondary particles having a plurality of primary particles aggregated, the primary particles have a particle diameter of 1 to 120 nm, and the secondary particles The particle size may be 200 to 600 nm.

특이하게도, 상기 인의 도핑 함량이 상기 수치 범위(1 내지 50 at%)임과 동시에, 상기 1차 입경 및 2차 입경이 상기 수치범위(1 내지 140 nm의 1차 입경 및 200 내지 600 nm의 2차 입경)일 경우에는 상온에서 인 도핑 흑연질 탄소질화물의 2차 입자가 서로 응집되는 현상이 전혀 발생하지 않았다. 반면, 상기 수치 범위(1 내지 50 at%)를 벗어나거나, 상기 인의 도핑 함량이 상기 수치 범위(1 내지 50 at%)를 벗어남과 동시에 상기 1차 입경 및 2차 입경이 상기 수치범위(1 내지 140 nm의 1차 입경 및 200 내지 600 nm의 2차 입경)를 벗어나는 경우에는 상온에서도 인 도핑 흑연질 탄소질화물의 2차 입자가 서로 응집되어 폴리설파이드의 포집 효과가 저하됨을 확인하였다.Specifically, while the doping content of the phosphorus is within the numerical range (1 to 50 at%), the primary particle size and the secondary particle size are the numerical range (primary particle size of 1 to 140 nm and 2 of 200 to 600 nm). In the case of secondary particle size), the phenomenon in which secondary particles of phosphorus doped graphite carbon nitride aggregated with each other at room temperature did not occur at all. On the other hand, the primary particle size and the secondary particle diameter are out of the numerical range (1 to 50 at%) or the doping content of the phosphorus is out of the numerical range (1 to 50 at%). When it was out of the primary particle size of 140 nm and the secondary particle size of 200 to 600 nm), it was confirmed that the secondary particles of phosphorus doped graphite carbon nitride aggregated with each other even at room temperature to degrade the collection effect of polysulfide.

또 다른 구현예에 따르면, 상기 이차전지 분리막 코팅용 조성물은 탄소 도전재 또는, 탄소 도전재 및 결합제를 더욱 포함할 수 있다. According to another embodiment, the composition for coating a secondary battery separator may further include a carbon conductive material, or a carbon conductive material and a binder.

상기 탄소 도전재를 더욱 포함하는 경우, 상위 제2 집전체 기능을 통한 가역적인 활물질 재사용이 가능한 효과가 있다.When the carbon conductive material is further included, reversible active materials can be reused through the upper second current collector function.

또 다른 구현예에 따르면, 상기 탄소 도전재는 Super-P, rGO(환원된 산화 그래핀), VGCF(기상성장탄소섬유), 그래핀, AB(아세틸렌블랙), KB(케천블랙), CNT 및 MWCNT 중에서 선택되는 1종 이상일 수 있으며, 이에 한정되는 것은 아니다.According to another embodiment, the carbon conductive material is Super-P, rGO (reduced graphene oxide), VGCF (weather growth carbon fiber), graphene, AB (acetylene black), KB (kecheon black), CNT and MWCNT It may be one or more selected from, but is not limited thereto.

또 다른 구현예에 따르면, 상기 탄소 도전재는 Super-P, rGO 및 VGCF의 혼합물이고, 상기 Super-P, rGO 및 VGCF의 중량비는 1 : 0.1 내지 0.5 : 0.1 내지 0.5일 수 있다.According to another embodiment, the carbon conductive material is a mixture of Super-P, rGO and VGCF, and the weight ratio of Super-P, rGO and VGCF may be 1: 0.1 to 0.5: 0.1 to 0.5.

또 다른 구현예에 따르면, 상기 결합제는 폴리비닐리덴플루오라이드(PVDF), 폴리헥사플루오로프로필렌-폴리비닐리덴플루오라이드의 공중합체(PVDF/HFP), 폴리(비닐아세테이트), 폴리비닐알코올, 폴리에틸렌옥사이드, 폴리비닐피롤리돈, 알킬화 폴리에틸렌옥사이드, 폴리비닐에테르, 폴리(메틸메타크릴레이트), 폴리(에틸아크릴레이트), 폴리테트라플루오로에틸렌 (PTFE), 폴리비닐클로라이드, 폴리아크릴로니트릴, 폴리비닐피리딘, 스티렌-부타디엔 고무, 아크릴로니트릴-부타디엔 고무 및 에틸렌프로필렌디엔모노머(EPDM) 중에서 선택되는 1종 이상일 수 있으며, 이에 한정되는 것은 아니다. 바람직하게는 PVDF일 수 있다.According to another embodiment, the binder is polyvinylidene fluoride (PVDF), a copolymer of polyhexafluoropropylene-polyvinylidene fluoride (PVDF / HFP), poly (vinyl acetate), polyvinyl alcohol, polyethylene Oxide, polyvinylpyrrolidone, alkylated polyethylene oxide, polyvinyl ether, poly (methyl methacrylate), poly (ethyl acrylate), polytetrafluoroethylene (PTFE), polyvinyl chloride, polyacrylonitrile, poly It may be one or more selected from vinyl pyridine, styrene-butadiene rubber, acrylonitrile-butadiene rubber, and ethylene propylene diene monomer (EPDM), but is not limited thereto. It may preferably be PVDF.

또 다른 구현예에 따르면, 상기 인 도핑 흑연질 탄소질화물은 상기 인 도핑 흑연질 탄소질화물, 탄소 도전재 및 결합제 전체 100 중량부를 기준으로 40 내지 80 중량부, 바람직하게는 50 내지 70 중량부, 더욱 바람직하게는 55 내지 65 중량부 포함할 수 있다.According to another embodiment, the phosphorus doped graphite carbon nitride is 40 to 80 parts by weight, preferably 50 to 70 parts by weight, more preferably, based on 100 parts by weight of the phosphorus doped graphite carbon nitride, carbon conductive material and binder Preferably it may contain 55 to 65 parts by weight.

상기 인 도핑 흑연질 탄소질화물의 함량이 상기 수치 범위의 하한값(40 중량부) 미만인 경우에는 폴리설파이드의 흡착 효과가 미미할 수 있고, 상한 값(80 중량부)을 초과하는 경우에는 도전재 혼합물에 의한 제2 집전체 역할 효과가 감소하여 전극의 용량 구현이 줄어들 수 있어 바람직하지 않다.When the content of the phosphorus doped graphite carbon nitride is less than the lower limit (40 parts by weight) of the numerical range, the adsorption effect of polysulfide may be insignificant, and when it exceeds the upper limit (80 parts by weight), the conductive material mixture may The effect of the role of the second current collector is reduced, and thus the capacity of the electrode can be reduced, which is undesirable.

특히, 하기 실시예 또는 비교예 등에는 명시적으로 기재하지는 않았지만, 본 발명에 따른, 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물에 있어서, 상기 인의 함량, 상기 인 도핑 흑연질 탄소질화물 입자의 입경, 탄소 도전재와 결합제를 더욱 포함 시 탄소 도전재의 조성과 인 도핑 흑연질 탄소 질화물의 함량, 결합제의 종류 및 분리막의 종류가 변화된 이차전지 분리막 코팅용 조성물을 각각 리튬-황 이차전지의 분리막에 코팅하여 500 시간 동안 고온(60 ℃)의 LiTFSI와 LiFSI 이중염을 사용한 리튬-황전지에서 작동한 후, 상기 리튬-황 이차전지의 분리막에 대하여 그 절단면 및 상기 코팅층의 유실 여부를 주사전자현미경(SEM) 분석을 통해 확인하였다.In particular, although not explicitly described in the following Examples or Comparative Examples, in the composition for coating a secondary battery separator comprising phosphorus doped graphite carbon nitride according to the present invention, the phosphorus content, the phosphorus doped graphite carbon When the particle size of the nitride particles, the carbon conductive material and the binder are further included, the composition of the carbon conductive material, the content of the phosphorus doped graphite carbon nitride, the type of the binder, and the type of the separator are changed. After coating the separator on the lithium-sulfur battery using high-temperature (60 ° C) LiTFSI and LiFSI double salts for 500 hours, the separator of the lithium-sulfur secondary battery was scanned for loss of the cut surface and the coating layer. It was confirmed through an electron microscope (SEM) analysis.

그 결과, 다른 조건 및 다른 수치 범위에서와는 달리, 아래 조건이 모두 만족하였을 때 500 시간 동안 고온에서 작동한 후에도 상기 분리막과 상기 코팅층 사이 계면에 빈 공간이 발생하지 않았고, 또한 상기 분리막에 코팅된, 인 도핑 흑연질 탄소질화물 코팅층의 유실이 전혀 관찰되지 않았다.As a result, unlike in other conditions and other numerical ranges, no voids were generated at the interface between the separator and the coating layer even after operating at high temperature for 500 hours when all of the following conditions were satisfied, and No loss of the doped graphite carbon nitride coating layer was observed.

(ⅰ) 인의 함량은 상기 인 도핑 흑연질 탄소질화물 전체 중량을 기준으로 1 내지 50 at%, (ⅱ) 인 도핑 흑연질 탄소질화물은 1 내지 120 nm 입경의 1차 입자 및 200 내지 600 nm의 입경의 2차 입자로 형성, (ⅲ) 탄소 도전재 및 결합제를 더욱 포함, (ⅳ) 탄소 도전재는 Super-P, rGO 및 VGCF의 혼합물, (ⅴ) Super-P, rGO 및 VGCF의 중량비는 1 : 0.1 내지 0.5 : 0.1 내지 0.5, (ⅵ) 결합제는 PVDF, (ⅶ) 인 도핑 흑연질 탄소질화물은 상기 인 도핑 흑연질 탄소질화물, 탄소 도전재 및 결합제 전체 100 중량부를 기준으로 40 내지 80 중량부 포함, (ⅷ) 분리막은 폴리프로필렌.(I) The content of phosphorus is 1 to 50 at% based on the total weight of the phosphorus doped graphite carbon nitride, (ii) the phosphorus doped graphite carbon nitride has primary particles having a particle diameter of 1 to 120 nm and particle diameters of 200 to 600 nm. Formed with the secondary particles of (i) further comprising a carbon conductive material and a binder, (i) the carbon conductive material is a mixture of Super-P, rGO and VGCF, and (i) the weight ratio of Super-P, rGO and VGCF is 1: 0.1 to 0.5: 0.1 to 0.5, (i) the binder is PVDF, (i) phosphorus doped graphite carbon nitride includes 40 to 80 parts by weight based on 100 parts by weight of the phosphorus doped graphite carbon nitride, carbon conductive material and binder , (I) The separator is polypropylene.

다만, 상기 조건 중 어느 하나라도 충족되지 않는 경우에는 500 시간 동안 고온에서 작동한 후에 상기 분리막과 상기 코팅층 사이 계면 중 적지 않은 부분에 빈 공간이 형성될 뿐만 아니라, 상기 분리막에 코팅된, 인 도핑 흑연질 탄소질화물의 유실이 현저하게 나타남을 확인하였다.However, if any one of the above conditions is not satisfied, after operating at high temperature for 500 hours, not only an empty space is formed at a small portion of the interface between the separator and the coating layer, but also coated with the separator, phosphorus doped graphite It was confirmed that the loss of vaginal carbon nitride was remarkable.

본 발명의 다른 측면은 본 발명에 따른 이차전지 분리막 코팅용 조성물의 코팅층이 상기 분리막의 표면에 형성되어 있는 이차전지 분리막에 관한 것이다. Another aspect of the present invention relates to a secondary battery separator in which a coating layer of a composition for coating a secondary battery separator according to the present invention is formed on the surface of the separator.

일 구현예에 따르면, 상기 코팅된 분리막의 건조는 40 내지 60 ℃에서 수행된 것일 수 있으며, 특이하게도 상기 온도 범위 외에서 건조가 이루어지는 경우 건조 동안 분리막의 수축이 일어남을 확인하였다. 이 경우 리튬-황 이차전지용 분리막으로 사용될 수 없는 문제점이 발생한다.According to one embodiment, drying of the coated separator may be performed at 40 to 60 ° C. Specifically, when drying is performed outside the temperature range, it is confirmed that shrinkage of the separator occurs during drying. In this case, a problem that cannot be used as a separator for a lithium-sulfur secondary battery occurs.

본 발명의 또 다른 측면은 본 발명에 따른 이차전지 분리막을 포함하는 리튬-황 이차전지로서, 상기 코팅층은 상기 이차전지의 양극을 향하는 상기 분리막 일면의 표면에 형성되어 있는 것을 특징으로 하는 리튬-황 이차전지에 관한 것이다.Another aspect of the present invention is a lithium-sulfur secondary battery including a secondary battery separator according to the present invention, wherein the coating layer is formed on a surface of one surface of the separator facing the anode of the secondary battery. It relates to a secondary battery.

일 구현예에 따르면, 상기 리튬-황 이차전지의 양극은 KB(케천블랙)과 황의 화합물, Super-P 도전재, 그리고 Polyvinyl pyrrolidone(PVP), Carboxymethyl cellulose(CMC), Poly(ethylene oxide)(PEO) 3 가지 조합 시스템의 수계 결합제로 구성될 수 있으며, 이에 한정되는 것은 아니다.According to one embodiment, the positive electrode of the lithium-sulfur secondary battery is a compound of KB (Kecheon Black) and sulfur, a Super-P conductive material, and Polyvinyl pyrrolidone (PVP), Carboxymethyl cellulose (CMC), Poly (ethylene oxide) (PEO ) It may be composed of a water-based binder of three combination systems, but is not limited thereto.

본 발명의 또 다른 측면은 본 발명에 따른 이차전지 분리막 코팅용 조성물을 포함하는 전기 디바이스로서, 상기 전기 디바이스는 전기자동차, 하이브리드 전기자동차, 플러그-인 하이브리드 전기자동차 및 전력 저장장치 중에서 선택되는 1종인 것을 특징으로 하는 전기 디바이스에 관한 것이다.Another aspect of the present invention is an electric device comprising a composition for coating a secondary battery separator according to the present invention, wherein the electric device is one selected from an electric vehicle, a hybrid electric vehicle, a plug-in hybrid electric vehicle and a power storage device. It relates to an electrical device characterized in that.

본 발명의 또 다른 측면은 멜라민 및 요소의 혼합물을 열처리하는 단계;를 포함하는 흑연질 탄소질화물의 제조방법에 관한 것이다.Another aspect of the present invention relates to a method for preparing a graphitic carbon nitride comprising; heat-treating a mixture of melamine and urea.

상기 흑연질 탄소질화물을 합성하는데 사용되는 4 가지 전구체는 티오요소(Thiourea), 디시안디아미드(Dicyandiamide), 멜라민(Melamine), 요소(Urea)이다. 각 전구체의 가격은 3906 $/t, 1538 $/t, 2025 $/t, 450 $/t으로, 요소의 가격이 매우 저렴하고, 반수치사량(LD50)은 125 mg/kg, 4000 mg/kg, 3248 mg/kg, 8500 mg/kg으로, 요소의 독성이 가장 안정하다. 이러한 요소를 단독 전구체로 사용하여 탄소질화물을 합성하면 가장 높은 비표면적을 갖게 되지만, 수율이 약 1% 정도로 매우 낮아 거의 사용되지 않는다. 하지만 본 발명에서는 가장 저렴하고 독성이 가장 적은 요소와 함께 멜라민을 전구체로 조합하여 요소 전구체에 비해 획기적으로 증가한 수득률을 기록하였다.The four precursors used to synthesize the graphitic carbon nitride are thiourea, dicyandiamide, melamine, and urea. The price of each precursor is 3906 $ / t, 1538 $ / t, 2025 $ / t, 450 $ / t, and the price of urea is very low, and the half mortality (LD50) is 125 mg / kg, 4000 mg / kg, At 3248 mg / kg and 8500 mg / kg, urea toxicity is the most stable. When carbon nitride is synthesized using these elements as a single precursor, it has the highest specific surface area, but its yield is very low, about 1%, and is rarely used. However, in the present invention, by combining melamine as a precursor with the cheapest and least toxic element, a significantly increased yield compared to the urea precursor was recorded.

본 발명의 또 다른 측면은 멜라민, 요소 및 인 전구체의 혼합물을 열처리하는 단계;를 포함하는 인 도핑 흑연질 탄소질화물의 제조방법에 관한 것이다.Another aspect of the present invention relates to a method for producing a phosphorus-doped graphitic carbon nitride comprising; heat-treating a mixture of melamine, urea and phosphorus precursors.

일 구현예에 따르면, 상기 멜라민 대 요소의 중량비는 1 : 9 내지 3 : 7일 수 있다.According to one embodiment, the weight ratio of the melamine to urea may be 1: 9 to 3: 7.

상기 중량비 범위 내에서는 상기 중량비를 벗어날 경우에 비하여 인 도핑된 흑연질 탄소질화물의 비표면적의 크기가 현저히 향상되어, 폴리설파이드의 흡착 효과가 현저히 우수함을 확인하였다.Within the weight ratio range, the size of the specific surface area of the phosphorus doped graphite carbon nitride is significantly improved compared to the case where it exceeds the weight ratio, and it was confirmed that the adsorption effect of polysulfide is remarkably excellent.

다른 구현예에 따르면, 상기 인 전구체는 제2 인산암모늄이고, 상기 제2 인산암모늄은 상기 멜라민 및 요소의 혼합물 100 중량부를 기준으로 10 내지 50 중량부, 바람직하게는 20 내지 40 중량부, 더욱 바람직하게는 25 내지 35 중량부 혼합될 수 있다.According to another embodiment, the phosphorus precursor is a second ammonium phosphate, the second ammonium phosphate is 10 to 50 parts by weight, preferably 20 to 40 parts by weight, more preferably based on 100 parts by weight of the mixture of melamine and urea It may be mixed 25 to 35 parts by weight.

상기 제2 인산암모늄의 함량이 상기 하한치(10 중량부) 미만인 경우에는 폴리설파이드의 흡착 효과가 미미할 수 있고, 상기 상한치(50 중량부) 초과인 경우에는 흑연질 탄소질화물의 구조를 유지하지 못하게 되어, 바람직하지 않다.When the content of the second ammonium phosphate is less than the lower limit (10 parts by weight), the adsorption effect of polysulfide may be insignificant, and when it is more than the upper limit (50 parts by weight), the structure of graphite carbon nitride cannot be maintained. , Is not preferred.

또 다른 구현예에 따르면, 상기 열처리는 1 내지 10 ℃/min, 바람직하게는 3 내지 8 ℃/min, 더욱 바람직하게는 4 내지 6 ℃/min의 승온속도로 400 내지 700 ℃, 바람직하게는 450 내지 650 ℃, 더욱 바람직하게는 500 내지 600 ℃로 승온시킨 후 1 내지 10 시간, 바람직하게는 2 내지 8 시간, 더욱 바람직하게는 3 내지 5 시간 동안 유지하여 수행될 수 있다.According to another embodiment, the heat treatment is 1 to 10 ℃ / min, preferably 3 to 8 ℃ / min, more preferably 400 to 700 ℃ at a heating rate of 4 to 6 ℃ / min, preferably 450 It may be carried out by heating for 1 to 10 hours, preferably 2 to 8 hours, and more preferably 3 to 5 hours after heating up to 650 ° C, more preferably 500 to 600 ° C.

특히, 하기 실시예 또는 비교예 등에는 명시적으로 기재하지는 않았지만, 본 발명에 따른 인 도핑 흑연질 탄소질화물의 제조방법에 있어서, 멜라민 대 요소의 중량비, 인 전구체의 종류, 혼합물 중 인 전구체의 함량, 및 열처리 조건을 달리하여 제조된 인 도핑 흑연질 탄소 질화물을, 탄소 도전재 및 결합제와 혼합하여 슬러리를 제조한 후, 리튬-황 이차전지의 분리막에 코팅하여, 800 시간 동안 60 ℃의 LiTFSI와 LiFSI 이중염을 사용한 리튬-황전지에서 작동한 후, 상기 분리막의 형태를 주사전자현미경(SEM)을 분석을 통해 확인하였다. In particular, although not explicitly described in the following Examples or Comparative Examples, in the method for preparing phosphorus doped graphite carbon nitride according to the present invention, the weight ratio of melamine to urea, the type of phosphorus precursor, and the content of phosphorus precursor in the mixture , And by mixing the phosphorus doped graphite carbon nitride prepared by different heat treatment conditions, and a carbon conductive material and a binder to prepare a slurry, and then coated on a separator of a lithium-sulfur secondary battery, LiTFSI at 60 ℃ for 800 hours After operating in a lithium-sulfur battery using a LiFSI double salt, the morphology of the separator was confirmed by analysis of a scanning electron microscope (SEM).

그 결과, 다른 조건 및 다른 수치 범위에서와는 달리, 아래 조건이 모두 만족하였을 때 800 시간 동안 60 ℃의 고온에서 작동한 후에도 상기 분리막에 코팅된 상기 인 도핑 흑연질 탄소질화물 2차 입자의 응집이 전혀 발생하지 않아 열적 안정성이 매우 우수함을 확인하였고,As a result, unlike in other conditions and other numerical ranges, aggregation of the phosphorous doped graphite carbon nitride secondary particles occurred on the separator even after operating at a high temperature of 60 ° C. for 800 hours when all of the following conditions were satisfied. It was confirmed that the thermal stability is not very good,

(ⅰ) 멜라민 대 요소의 중량비는 1 : 9 내지 3 : 7, (ⅱ) 인 전구체는 제2 인산암모늄, (ⅲ) 제2 인산암모늄은 상기 멜라민 및 요소의 혼합물 100 중량부를 기준으로 10 내지 50 중량부 혼합, (ⅳ) 열처리는 1 내지 10 ℃/min의 승온속도로 400 내지 700 ℃로 승온시킨 후 1 내지 10 시간 동안 유지하여 수행, (ⅴ) 탄소 도전재는 Super-P, rGO 및 VGCF의 혼합물, (ⅵ) Super-P, rGO 및 VGCF의 중량비는 1 : 0.1 내지 0.5 : 0.1 내지 0.5, (ⅶ) 결합제는 PVDF, (ⅷ) 인 도핑 흑연질 탄소질화물은 상기 인 도핑 흑연질 탄소질화물, 탄소 도전재 및 결합제 전체 100 중량부를 기준으로 40 내지 80 중량부 포함, (ⅸ) 분리막은 폴리프로필렌.(I) The weight ratio of melamine to urea is 1: 9 to 3: 7, (ii) the phosphorus precursor is diammonium phosphate, (i) the second ammonium phosphate is 10 to 50 based on 100 parts by weight of the mixture of melamine and urea. Mixing by weight, (ⅳ) heat treatment is performed by heating to 400 to 700 ° C. at a heating rate of 1 to 10 ° C./min and maintaining for 1 to 10 hours. (Ⅴ) Carbon conductive materials of Super-P, rGO and VGCF The weight ratio of the mixture, (i) Super-P, rGO and VGCF is 1: 0.1 to 0.5: 0.1 to 0.5, (i) the binder is PVDF, (i) phosphorous doped graphite carbon nitride, the phosphorus doped graphite carbon nitride, 40 to 80 parts by weight based on 100 parts by weight of the total of the carbon conductive material and the binder, (i) the separation membrane is polypropylene.

다만, 상기 조건 중 어느 하나라도 충족되지 않는 경우에는 800 시간 동안 60 ℃의 고온에서 작동한 후에 상기 분리막 상에 코팅된 인 도핑 흑연질 탄소질화물 2차 입자의 응집이 현저히 발생하는 것을 확인하였다.
However, when any one of the above conditions is not satisfied, it was confirmed that aggregation of phosphorous doped graphite carbon nitride secondary particles coated on the separator occurs remarkably after operating at a high temperature of 60 ° C. for 800 hours.

이하에서 실시예 등을 통해 본 발명을 더욱 상세히 설명하고자 하며, 다만 이하에 실시예 등에 의해 본 발명의 범위와 내용이 축소되거나 제한되어 해석될 수 없다. 또한, 이하의 실시예를 포함한 본 발명의 개시 내용에 기초한다면, 구체적으로 실험 결과가 제시되지 않은 본 발명을 통상의 기술자가 용이하게 실시할 수 있음은 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구 범위에 속하는 것도 당연하다.Hereinafter, the present invention will be described in more detail through examples and the like, but the scope and content of the present invention may be reduced or limited by the following examples and the like and cannot be interpreted. In addition, if it is based on the disclosure of the present invention including the following examples, it is obvious that a person skilled in the art can easily carry out the present invention in which experimental results are not specifically presented, and patents to which such modifications and corrections are attached Naturally, it is within the scope of the claims.

또한 이하에서 제시되는 실험 결과는 상기 실시예 및 비교예의 대표적인 실험 결과만을 기재한 것이며, 아래에서 명시적으로 제시하지 않은 본 발명의 여러 구현예의 각각의 효과는 해당 부분에서 구체적으로 기재하도록 한다.
In addition, the experimental results presented below are only representative of experimental results of the examples and comparative examples, and the effects of various embodiments of the present invention, which are not explicitly presented below, will be described in detail in the corresponding parts.

실시예 1: 흑연질 탄소질화물(gCExample 1: Graphitic carbon nitride (gC 33 NN 44 , gCN)의 합성, gCN)

6 g의 멜라민(C3H6N6) 분말을 1000 mL 증류수가 담긴 비커에 넣고, 100 ℃로 설정된 핫플레이트 위에서 멜라민이 완전히 녹을 때 까지 60분 동안 교반하였다. 그 다음 60% 농도의 질산 용액을 5 mL 넣고, 용매가 모두 증발하여 건조한 분말 형태로 얻어질 때까지 용액을 계속해서 가열하며 교반한다. 분말 형태로 얻어진 뒤, 14 g의 요소(Urea, (NH2)2CO)를 넣고 유발을 사용하여 섞어주었다. 이 혼합물을 세라믹 재질의 뚜껑이 닫힌 도가니 안에 넣고, 분당 5 ℃의 승온 속도로 550 ℃의 박스형 전기로에서 3 시간 동안 열분해를 하였다. 열분해 뒤 얻어지는 분말은 증류수로 3 번의 세척 후 에탄올로 한번 세척한 후, 80 ℃의 오븐에서 12 시간 동안 건조하였다.
6 g of melamine (C 3 H 6 N 6 ) powder was placed in a beaker containing 1000 mL of distilled water and stirred for 60 minutes on a hot plate set at 100 ° C. until melamine was completely dissolved. Then, 5 mL of a nitric acid solution having a concentration of 60% was added, and the solution was continuously heated and stirred until all of the solvent evaporated to obtain a dry powder. After being obtained in powder form, 14 g of urea (Urea, (NH 2 ) 2 CO) was added and mixed using a mortar. This mixture was placed in a crucible with a ceramic lid closed, and thermally decomposed for 3 hours in a box-type electric furnace at 550 ° C at a heating rate of 5 ° C per minute. The powder obtained after thermal decomposition was washed 3 times with distilled water and then washed once with ethanol, and then dried in an oven at 80 ° C. for 12 hours.

실시예 2: 인 도핑 흑연질 탄소질화물 (PgCExample 2: Phosphorus doped graphite carbon nitride (PgC 33 NN 44 , PgCN)의 합성, PgCN)

6 g의 멜라민(C3H6N6) 분말을 1000 mL 증류수가 담긴 비커에 넣고, 100 ℃로 설정된 핫플레이트 위에서 멜라민이 완전히 녹을 때 까지 60 분 동안 교반하였다. 그 다음 60% 농도의 질산 용액을 5 mL 넣고, 용매가 모두 증발하여 건조한 분말 형태로 얻어질 때까지 용액을 계속해서 가열하며 교반하였다. 분말 형태로 얻어진 뒤, 14 g의 요소(Urea, (NH2)2CO)와 6 g의 제2 인산암모늄((NH4)2HPO4)을 추가로 넣고 유발을 사용하여 섞어주었다. 이 혼합물을 세라믹 재질의 뚜껑이 닫힌 도가니 안에 넣고, 분당 5 ℃의 승온 속도로 550 ℃의 박스형 전기로에서 3 시간 동안 열분해 하였다. 열분해 뒤 얻어지는 분말은 증류수로 3 번의 세척 후 에탄올로 한번 세척한 후, 80 ℃의 오븐에서 12 시간 동안 건조하였다. 인 도핑 농도는 제2 인산암모늄의 양을 통해 조절하여 PgCN 물질을 합성하였다.
6 g of melamine (C 3 H 6 N 6 ) powder was placed in a beaker containing 1000 mL of distilled water, and stirred for 60 minutes on a hot plate set at 100 ° C. until melamine was completely dissolved. Then, 5 mL of a nitric acid solution having a concentration of 60% was added, and the solution was continuously heated and stirred until all of the solvent evaporated to obtain a dry powder. After being obtained in powder form, 14 g of urea (Urea, (NH 2 ) 2 CO) and 6 g of second ammonium phosphate ((NH 4 ) 2 HPO 4 ) were additionally added and mixed using a mortar. This mixture was placed in a crucible with a ceramic lid closed, and thermally decomposed for 3 hours in a box-type electric furnace at 550 ° C at a heating rate of 5 ° C per minute. The powder obtained after thermal decomposition was washed 3 times with distilled water and then washed once with ethanol, and then dried in an oven at 80 ° C. for 12 hours. PgCN material was synthesized by adjusting the phosphorus doping concentration through the amount of diammonium phosphate.

실시예 3 내지 4: PgCN/C 또는 gCN/C이 코팅된 분리막의 제조Examples 3 to 4: Preparation of PgCN / C or gCN / C coated separator

(1) 먼저 슬러리 전체 중량을 기준으로 60 중량%의 PgCN(또는 gCN)과 30 중량%의 탄소 혼합물, 10 중량%의 PVDF 바인더 조성으로 이루어진 슬러리를 30 분의 볼 밀링을 통해 제조하였다. 여기서 30 중량%의 탄소 혼합물의 세부 조성은 제조된 전체 슬러리 100 중량부 기준으로 20 중량부의 Super-P, 5 중량부의 VGCF(Vapor Grown Carbon Fiber), 5 중량부의 rGO(Reduced Graphene Oxide)로 하였다.
(1) First, a slurry composed of 60% by weight PgCN (or gCN) and 30% by weight carbon mixture, and 10% by weight PVDF binder composition based on the total weight of the slurry was prepared through ball milling for 30 minutes. Here, the detailed composition of the 30% by weight carbon mixture was 20 parts by weight of Super-P, 5 parts by weight of VGCF (Vapor Grown Carbon Fiber), and 5 parts by weight of Reduced Graphene Oxide (rGO) based on 100 parts by weight of the total slurry prepared.

(2) 이렇게 제조된 슬러리를 닥터 블레이드 방식으로 분리막(폴리프로필렌) 한쪽 표면 위에 캐스팅한 뒤, 40 ~ 50 ℃의 오븐에서 12 시간 동안 건조하여 PgCN/C 코팅된 분리막을 제작하였다. gCN/C 코팅된 분리막 제작 방법은 PgCN/C 대신 gCN/C 물질을 사용하고, 나머지 절차는 동일하다.
(2) The prepared slurry was cast on one surface of a separator (polypropylene) by a doctor blade method, and then dried in an oven at 40 to 50 ° C. for 12 hours to prepare a PgCN / C coated separator. The method of manufacturing the gCN / C coated separator uses gCN / C material instead of PgCN / C, and the rest of the procedure is the same.

실시예 5: 리튬-황 이차전지의 제작Example 5: Preparation of lithium-sulfur secondary battery

KB/S 화합물(1:4 질량비)과 Super-P 도전재, PVP/CMC/PEO 조합의 수계 졀합제로 제작된 양극과 리튬금속 호일 음극을 사용하고, 전해질은 1 M LiTFSI 리튬염과 0.25 M LiNO3 첨가제가 DME:DOL(1:1 부피비)에 녹아있는 용액을 사용하여 코인셀을 제작하였다. 양극과 음극 사이의 위치하는 분리막을 기존의 분리막(폴리프로필렌) 또는 PgCN 코팅된 분리막 또는 gCN 코팅된 분리막을 사용하고, 코팅된 분리막의 경우에는 코팅된 쪽이 양극을 바라보는 방향으로 놓고 코인셀을 제작하였다. 전지 타입은 2032 코인셀을 사용하였다. 충방전 장비는 마커 4000 시리즈를 사용하였고, 1.7 ~ 2.8 V (Li/Li+) 전압 범위에서 1 C 전류밀도로 수명 특성을 측정하였다. 여기서 1 C = 1,675 mAh/g을 기준으로 하였다.
A positive electrode and a lithium metal foil negative electrode made of an aqueous mixture of a KB / S compound (1: 4 mass ratio), a Super-P conductive material, and a PVP / CMC / PEO combination are used, and the electrolyte is 1 M LiTFSI lithium salt and 0.25 M. A coin cell was prepared using a solution in which the LiNO 3 additive was dissolved in DME: DOL (1: 1 volume ratio). The separation membrane positioned between the anode and the cathode uses a conventional separation membrane (polypropylene) or a PgCN-coated separation membrane or a gCN-coated separation membrane, and in the case of a coated separation membrane, the coated side is placed in a direction facing the anode, and the coin cell is placed. It was produced. The battery type used a 2032 coin cell. Marker 4000 series was used as the charging / discharging equipment, and the life characteristics were measured at a current density of 1 C in the voltage range of 1.7 to 2.8 V (Li / Li + ). Here, it was based on 1 C = 1,675 mAh / g.

도 1은 본 발명의 실시예 1로부터 흑연질 탄소질화물(C3N4, CN) 합성 시 사용되는 두 가지 전구체인 멜라민과 요소의 중량비에 따른 BET 비표면적을 나타낸 (a) 표, (b) 그래프 및 (c) 특히, 3/7 중량비 조건의 그래프이다.1 is a table showing the specific surface area of BET according to the weight ratio of melamine and urea, which are two precursors used when synthesizing graphite carbon nitride (C 3 N 4 , CN) from Example 1 of the present invention, (a) table, (b) Graphs and (c) in particular, 3/7 weight ratio conditions.

먼저 도 1a 의 표는 멜라민/요소의 9/1 질량비부터 1/9 질량비까지 변화하며 합성을 진행한 후, N2-isotherm BET 분석을 통하여 측정한 비표면적 결과를 보여준다. First, the table of FIG. 1A shows the specific surface area results measured through N 2 -isotherm BET analysis after synthesis was performed while changing from 9/1 mass ratio of melamine / urea to 1/9 mass ratio.

도 1b 및 1c의 그래프는 BET 분석에서 얻어지는 N2-isotherm 그래프이다. 여기서 멜라민/요소의 3/7 질량비와 1/9 질량비 조건에서 가장 높은 52 m2/g과 53 m2/g의 비표면적 결과가 나타났고, 따라서 본 발명에서는 멜라민/요소의 질량비를 3/7로 고정하여 물질을 합성하였다.
1B and 1C are graphs of N 2 -isotherm obtained from BET analysis. Here, the specific surface area results of 52 m 2 / g and 53 m 2 / g, which were the highest in the 3/7 mass ratio of the melamine / urea and the 1/9 mass ratio, were obtained, and accordingly, in the present invention, the mass ratio of the melamine / urea was 3/7. The material was synthesized by fixing with.

도 2는 본 발명의 실시예 2로부터 인 도핑 흑연질 탄소질화물(PgC3N4, PgCN) 합성 시 제2 인산암모늄의 함량에 따른 인 도핑 농도를 나타낸 표이다. Figure 2 is a table showing the phosphorus doping concentration according to the content of the second ammonium phosphate in the synthesis of phosphorus doped graphite carbon nitride (PgC 3 N 4 , PgCN) from Example 2 of the present invention.

멜라민/요소의 비율은 3/7 질량비인 6 g/14 g으로 고정한 후, 인 도핑 전구체 역할을 수행하는 제2 인산암모늄의 양을 2 g에서 9 g까지 늘려가며 실험을 진행하였다. 그 결과 인 도핑 농도가 최종 PgCN을 100 중량부로 봤을 때, 7.2 중량부에서 최대 36 중량부까지 제2 인산암모늄의 첨가 양에 비례하여 증가하는 것을 확인할 수 있다.
After the ratio of melamine / urea was fixed at 3/7 mass ratio of 6 g / 14 g, the experiment was conducted while increasing the amount of ammonium phosphate 2 serving as a phosphorus doping precursor from 2 g to 9 g. As a result, when the final phosphorus doping concentration is 100 parts by weight of the final PgCN, it can be confirmed that the proportion increases from 7.2 parts by weight to 36 parts by weight of ammonium diphosphate.

도 3은 (a) PgCN 합성의 반응 과정을 나타내는 모식도, (b) 합성된 gCN의 분말 이미지 및 (c) 합성된 PgCN의 분말 이미지이다. 3 is a schematic view showing the reaction process of (a) PgCN synthesis, (b) powder image of synthesized gCN and (c) powder image of synthesized PgCN.

멜라민/요소와 제2 인산암모늄을 첨가한 뒤 550 ℃ 열분해 과정을 통하여 간단하게 PgCN 물질을 합성할 수 있었다.
After adding melamine / urea and ammonium phosphate, PgCN materials could be synthesized simply through a pyrolysis process at 550 ° C.

도 4는 흑연질 탄소질화물 합성 시 사용되는 두 가지 전구체인 멜라민과 요소의 혼합이 최종 생성물 합성의 수득률에 미치는 효과를 보여주는 (a) 표와 (b) 이미지이다. FIG. 4 is a table (a) and (b) images showing the effect of mixing two precursors, melamine and urea, used in the synthesis of graphitic carbon nitride on the yield of final product synthesis.

요소만 사용하여 탄소질화물을 합성할 경우의 수득률은 0.2%이고, 멜라민만 사용하여 합성할 경우에는 수득률이 48.9%였다. 하지만 멜라민과 요소의 조합으로 탄소질화물을 합성할 경우, 수득률이 34.3%를 나타내었다. 또한 같은 조합으로 인 도핑 탄소질화물을 합성할 시 30.6%의 수득률을 기록하였다. 따라서 탄소질화물 합성의 전구체로 멜라민과 요소의 조합을 사용할 경우, 멜라민의 수득률에는 미치지 못하지만 요소의 수득률 보다는 크게 증가하는 것을 확인할 수 있다.
When the carbon nitride was synthesized using only urea, the yield was 0.2%, and when synthesized using only melamine, the yield was 48.9%. However, when carbon nitride was synthesized using a combination of melamine and urea, the yield was 34.3%. In addition, when synthesizing phosphorus doped carbon nitride in the same combination, a yield of 30.6% was recorded. Therefore, when using a combination of melamine and urea as a precursor for the synthesis of carbon nitride, it can be seen that although it does not reach the yield of melamine, it increases significantly more than the yield of urea.

도 5는 본 발명의 실시예 1 및 2로부터 합성된 (a) gCN과 (b) PgCN의 전자주사현미경(SEM) 이미지이다. 5 is an electron scanning microscope (SEM) image of (a) gCN and (b) PgCN synthesized from Examples 1 and 2 of the present invention.

도 5를 참조하면, 두 시료 모두 1차 입자의 크기는 약 60 ~ 90 nm 정도의 크기를 갖고, 2차 입자의 크기는 약 400 nm 내외 인 것으로 확인되었다. gCN과 PgCN은 서로 유사한 입자 형상을 보여준다.
5, in both samples, the size of the primary particles was about 60 to 90 nm, and the size of the secondary particles was found to be around 400 nm. gCN and PgCN show similar particle shape to each other.

도 6은 본 발명의 실시예 1 및 2로부터 합성된 (a) gCN과 PgCN의 열중량 분석 결과와 (b) PgCN의 EDX 분석 결과이다. 6 is a result of the thermogravimetric analysis of (a) gCN and PgCN synthesized from Examples 1 and 2 of the present invention and (b) EDX analysis of PgCN.

도 6을 참조하면, 두 시료 모두 400 ℃ 이상의 온도에서 열분해가 시작하여 약 700℃ 부근에서 질량 감소가 끝나는 것을 확인할 수 있다. 이 구간의 온도에서 나타나는 질량 감소는 탄소질화물 (C3N4, CN)의 분해로 인한 것이다. 따라서 PgCN의 경우 800 ℃ 이상에서 남아있는 약 50%의 질량은 P-N 결합 또는 인 산화물(Phosphorus oxide) 형태이다. 여기서 인 원소만의 도핑 농도를 조금 더 정확히 확인하기 위하여 추가로 SEM EDX 분석을 진행하였다. 그 결과 약 22%의 인 성분이 검출되어 인 도핑 농도를 결정할 수 있었다.
Referring to FIG. 6, it can be seen that both samples start pyrolysis at a temperature of 400 ° C. or higher, and the mass reduction ends at around 700 ° C. The decrease in mass at the temperature in this section is due to the decomposition of carbon nitride (C 3 N 4 , CN). Therefore, in the case of PgCN, about 50% of the mass remaining above 800 ° C is in the form of PN bond or phosphorus oxide. Here, in order to confirm the doping concentration only for the phosphorus element more accurately, an SEM EDX analysis was further performed. As a result, about 22% of the phosphorus component was detected and the phosphorus doping concentration could be determined.

도 7은 1 M LiTFSI-DME/DOL(1:1, 부피비) 전해질 용액에, 본 발명의 실시예 1 및 2로부터 합성된 gCN과 PgCN 분말을 넣어, 시간 경과에 따른 폴리설파이드 흡착 효과를 시각적으로 확인하는 이미지이다. 7 is a 1 M LiTFSI-DME / DOL (1: 1, volume ratio) electrolyte solution, gCN and PgCN powder synthesized from Examples 1 and 2 of the present invention, the visual effect of the polysulfide adsorption over time It is an image to check.

먼저, Li2S + 5S → Li2S6 반응식에 따라 0.92 g (0.01 mol)의 Li2S와 3.2 g(0.05 mol)의 황 분말을 20 mL DME와 20 mL DOL가 섞여있는 용매에 넣고 80 내지 90 ℃로 설정된 핫플레이트 위에서 12 시간 내지 24 시간 교반하여 최종적으로 0.01 mol의 Li2S6를 제조하였다. 최종적으로 이렇게 제조된 폴리설파이드 용액의 농도는 0.25 M이다.First, Li 2 S + 5S → Li 2 S 6 Put 0.92 g (0.01 mol) of Li 2 S and 3.2 g (0.05 mol) of sulfur powder in a solvent mixed with 20 mL DME and 20 mL DOL according to the reaction formula 80 The mixture was stirred for 12 hours to 24 hours on a hot plate set to 90 ° C. to finally prepare 0.01 mol of Li 2 S 6 . Finally, the concentration of the polysulfide solution thus prepared is 0.25 M.

도 7을 참조하면, a)에서와 같이 준비된 각 전해질 용액(3 mL)에 0.25 M 농도의 Li2S6, 폴리설파이드(2 mL)를 넣고 가만히 두면, 시간이 지날수록 PgCN(100 mg)이 들어있는 시료의 용액의 색깔이 점차 투명하게 변하는 것을 확인할 수 있다. 이는 용액 속의 PgCN 분말이 용액 속에 녹아있던 폴리설파이드를 효과적으로 흡착하기 때문이다. 따라서 PgCN이 gCN(100 mg)보다 더욱 효과적으로 폴리설파이드를 흡착할 수 있다. 이는 도핑된 인이 폴리설파이드와 단순 물리적 흡착이 아닌 화학결합을 통한 화학적 흡착을 이루기 때문이다.
Referring to FIG. 7, when 0.25 M concentration of Li 2 S 6 and polysulfide (2 mL) was added to each electrolyte solution (3 mL) prepared as in a), PgCN (100 mg) was added over time. It can be seen that the color of the solution of the sample contained gradually changes to be transparent. This is because the PgCN powder in the solution effectively adsorbs the polysulfide dissolved in the solution. Therefore, PgCN can adsorb polysulfide more effectively than gCN (100 mg). This is because the doped phosphorus forms chemical adsorption through chemical bonding rather than simple physical adsorption with polysulfide.

도 8은 PgCN/C가 코팅된 분리막을 사용하여 실제 리튬-황 이차전지 시스템에 적용하여 1 C-rate에서의 전기화학적 수명 특성을 평가한 결과이다[(a) 사이클에 따른 방전용량, (b) 사이클에 따른 쿨롱 효율, (c) 용량-전압 변화]. 8 is a result of evaluating the electrochemical life characteristics at 1 C-rate by applying to a real lithium-sulfur secondary battery system using a PgCN / C coated separator ((a) discharge capacity according to cycle, (b ) Coulomb efficiency with cycle, (c) Capacity-voltage change].

황의 로딩양이 2.5 mg/cm2인 전극을 제작하여 양극으로, 1 M LiTFSI와 0.25 M LiNO3가 녹아있는 전해질을 사용하였다. 먼저 방전 용량 측면에서 비교했을 때, PgCN/C가 코팅된 분리막을 사용하였을 때 가장 높은 방전 용량을 나타냈고, 충방전 곡선 또한 안정적으로 나타났다. 기존의 일반 분리막(Prisinte saparator)은 폴리설파이드를 전혀 가둬둘 수 없어, 용출된 폴리설파이드의 재사용이 불가능하기 때문에 가장 낮은 방전 용량을 보여주었다. PgCN/C가 코팅된 분리막(PgCN/C-separator)은 gCN/C가 코팅된 분리막(gCN/C-separator)보다 좋은 효과를 보여주었는데, 이는 PgCN의 폴리설파이드 흡착 능력이 gCN보다 더욱 강력하기 때문이다. 하지만 gCN/C 코팅의 경우 C 코팅(C-separator)보다 우수한 방정 용량을 기록하였다. 카본은 기본적으로 무극성 분자이기 때문에 폴리설파이드와 어떠한 상호작용이 없지만, 상용 카본의 낮은 결정도에서 야기되는 결함(defect)과 표면의 작용기, 또는 매우 큰 비표면적 효과로 인해 어느 정도의 폴리설파이드를 흡착할 수 있다. 하지만 그 정도가 gCN 또는 PgCN보다 떨어지기 때문에, 폴리설파이드의 재사용 정도가 적고, 그 결과 방전 용량 또한 작아지게 된다. 이러한 경향에 일치하는 결과를 쿨롱 효율 비교 그래프에서 다시 확인할 수 있다. 폴리설파이드의 흡착 능력이 클수록 쿨롱 효율이 PgCN/C > gCN/C > C > Pristine 분리막 순서로 높게 나타나는 것을 확인할 수 있다.
An electrode having a loading amount of sulfur of 2.5 mg / cm 2 was prepared and an electrolyte in which 1 M LiTFSI and 0.25 M LiNO 3 were dissolved as an anode was used. First, when compared in terms of discharge capacity, when using a separator coated with PgCN / C, it showed the highest discharge capacity, and the charge / discharge curve was also stable. The existing ordinary separator (Prisinte saparator) showed the lowest discharge capacity because polysulfide could not be confined at all and reuse of the eluted polysulfide was impossible. PgCN / C-coated separator (PgCN / C-separator) showed better effect than gCN / C-coated separator (gCN / C-separator) because PgCN's polysulfide adsorption capacity is stronger than gCN. to be. However, in the case of gCN / C coating, a better anticorrosive capacity was recorded than C-separator. Since carbon is basically a non-polar molecule, it does not have any interaction with polysulfide, but due to defects caused by low crystallinity of commercial carbon and functional groups on the surface, or a very large specific surface area effect, it can adsorb polysulfide to some extent. Can be. However, since the degree is lower than that of gCN or PgCN, the degree of reuse of polysulfide is small, and as a result, the discharge capacity is also reduced. The results consistent with this trend can be confirmed again in the Coulomb efficiency comparison graph. It can be seen that the higher the adsorption capacity of polysulfide, the higher the Coulomb efficiency is in the order of PgCN / C> gCN / C>C> Pristine separation membrane.

그러므로 본 발명에 따르면, 인 도핑 흑연질 탄소질화물을 포함하는 이차전지 분리막 코팅용 조성물을 리튬-황 이차전지의 분리막에 코팅하여, 양극에서 용출된 폴리설파이드의 확산 이동 방지 및 활물질로써의 가역적 재사용을 가능하게 함으로써, 고에너지 밀도의 양극 조건에서도 높은 쿨롱 효율과 방전 용량을 기록하며 장수명 특성을 갖는 리튬-황 이차전지로 응용할 수 있다.Therefore, according to the present invention, the composition for coating a secondary battery separator containing phosphorus doped graphite carbon nitride is coated on a separator of a lithium-sulfur secondary battery, preventing diffusion movement of polysulfide eluted from the positive electrode and reversible reuse as an active material By making it possible, it can be applied as a lithium-sulfur secondary battery having high coulomb efficiency and discharge capacity even under high energy density anode conditions and having long life characteristics.

Claims (17)

흑연질 탄소질화물(Graphitic Carbon Nitride, gCN)을 포함하고,
상기 흑연질 탄소질화물은 인 도핑된, 인 도핑 흑연질 탄소질화물(P-doped Graphitic Carbon Nitride, PgCN)이고,
상기 인 도핑 흑연질 탄소질화물은 멜라민, 요소 및 인 전구체의 혼합물을 열처리하여 수득된 것이고,
상기 멜라민 대 요소의 중량비는 1 : 9 내지 3 : 7이고,
상기 인 전구체는 상기 멜라민 및 요소의 혼합물 100 중량부를 기준으로 20 내지 40 중량부 혼합되고,
상기 인의 함량은 상기 인 도핑 흑연질 탄소질화물 전체 중량을 기준으로 10 내지 40 at%인 것인 이차전지 분리막 코팅용 조성물.
Graphitic Carbon Nitride (gCN), and
The graphite carbon nitride is phosphorus doped, phosphorus doped graphite carbon nitride (P-doped Graphitic Carbon Nitride, PgCN),
The phosphorus doped graphite carbon nitride is obtained by heat-treating a mixture of melamine, urea and phosphorus precursors,
The weight ratio of the melamine to urea is 1: 9 to 3: 7:
The phosphorus precursor is mixed with 20 to 40 parts by weight based on 100 parts by weight of the mixture of melamine and urea,
The content of the phosphorus is a secondary battery separator coating composition that is 10 to 40 at% based on the total weight of the phosphorus doped graphite carbon nitride.
삭제delete 삭제delete 제1항에 있어서,
상기 인 도핑 흑연질 탄소질화물은 복수 개의 1차 입자가 응집된 형태의 2차 입자로 형성되고,
상기 1차 입자의 입경은 1 내지 120 nm이며,
상기 2차 입자의 입경은 200 내지 600 nm인 것을 특징으로 하는 이차전지 분리막 코팅용 조성물.
According to claim 1,
The phosphorus doped graphite carbon nitride is formed of secondary particles in a form of a plurality of primary particles aggregated,
The particle size of the primary particles is 1 to 120 nm,
The composition for secondary battery separator coating, characterized in that the secondary particles have a particle diameter of 200 to 600 nm.
제1항 또는 제4항에 있어서,
상기 이차전지 분리막 코팅용 조성물은 탄소 도전재 또는, 탄소 도전재 및 결합제를 더욱 포함하는 것을 특징으로 하는 이차전지 분리막 코팅용 조성물.
The method of claim 1 or 4,
The composition for coating a secondary battery separator further comprises a carbon conductive material, or a carbon conductive material and a binder.
제5항에 있어서,
상기 탄소 도전재는 Super-P, rGO(환원된 산화 그래핀) 및 VGCF(기상성장탄소섬유)의 혼합물이고,
상기 Super-P, rGO 및 VGCF의 중량비는 1 : 0.1 내지 0.5 : 0.1 내지 0.5인 것을 특징으로 하는 이차전지 분리막 코팅용 조성물.
The method of claim 5,
The carbon conductive material is a mixture of Super-P, rGO (reduced graphene oxide) and VGCF (Weather Growth Carbon Fiber),
The weight ratio of the Super-P, rGO and VGCF is 1: 0.1 to 0.5: 0.1 to 0.5 composition for secondary battery separator coating.
제5항에 있어서,
상기 인 도핑 흑연질 탄소질화물은 상기 인 도핑 흑연질 탄소질화물, 탄소 도전재 및 결합제 전체 100 중량부를 기준으로 40 내지 80 중량부 포함하는 것을 특징으로 하는 이차전지 분리막 코팅용 조성물.
The method of claim 5,
The phosphorus doped graphite carbon nitride composition for secondary battery separation membrane coating, characterized in that it comprises 40 to 80 parts by weight based on 100 parts by weight of the phosphorus doped graphite carbon nitride, a carbon conductive material and a binder.
제1항에 있어서,
상기 인 도핑 흑연질 탄소질화물은 1 내지 120 nm 입경의 1차 입자 및 200 내지 600 nm의 입경의 2차 입자로 형성된 것이며,
상기 이차전지 분리막 코팅용 조성물은 탄소 도전재 및 결합제를 더욱 포함하며,
상기 탄소 도전재는 Super-P, rGO 및 VGCF의 혼합물이며,
상기 Super-P, rGO 및 VGCF의 중량비는 1 : 0.1 내지 0.5 : 0.1 내지 0.5이며,
상기 결합제는 PVDF이며,
상기 인 도핑 흑연질 탄소질화물은 상기 인 도핑 흑연질 탄소질화물, 탄소 도전재 및 결합제 전체 100 중량부를 기준으로 40 내지 80 중량부 포함하며,
상기 분리막은 폴리프로필렌인 것을 특징으로 하는 이차전지 분리막 코팅용 조성물.
According to claim 1,
The phosphorus doped graphite carbon nitride is formed of primary particles having a particle diameter of 1 to 120 nm and secondary particles having a particle diameter of 200 to 600 nm,
The composition for coating a secondary battery separator further includes a carbon conductive material and a binder,
The carbon conductive material is a mixture of Super-P, rGO and VGCF,
The weight ratio of the Super-P, rGO and VGCF is 1: 0.1 to 0.5: 0.1 to 0.5,
The binder is PVDF,
The phosphorus doped graphite carbon nitride includes 40 to 80 parts by weight based on 100 parts by weight of the phosphorus doped graphite carbon nitride, carbon conductive material and binder,
The separator is a composition for coating a secondary battery separator, characterized in that polypropylene.
제1항에 따른 이차전지 분리막 코팅용 조성물의 코팅층이 상기 분리막의 표면에 형성되어 있는 이차전지 분리막.A secondary battery separator in which a coating layer of the composition for coating a secondary battery separator according to claim 1 is formed on the surface of the separator. 제9항에 따른 이차전지 분리막을 포함하는 리튬-황 이차전지로서,
상기 코팅층은 상기 이차전지의 양극을 향하는 상기 분리막 일면의 표면에 형성되어 있는 것을 특징으로 하는 리튬-황 이차전지.
A lithium-sulfur secondary battery comprising the secondary battery separator according to claim 9,
The coating layer is a lithium-sulfur secondary battery, characterized in that formed on the surface of one surface of the separator toward the anode of the secondary battery.
제1항에 따른 이차전지 분리막 코팅용 조성물을 포함하는 전기 디바이스로서,
상기 전기 디바이스는 전기자동차, 하이브리드 전기자동차, 플러그-인 하이브리드 전기자동차 및 전력 저장장치 중에서 선택되는 1종인 것을 특징으로 하는 전기 디바이스.
An electrical device comprising the composition for coating a secondary battery separator according to claim 1,
The electric device is an electric device, characterized in that one selected from an electric vehicle, a hybrid electric vehicle, a plug-in hybrid electric vehicle and a power storage device.
삭제delete 멜라민, 요소 및 인 전구체의 혼합물을 열처리하는 단계;를 포함하는 인 도핑 흑연질 탄소질화물(P-doped Graphitic Carbon Nitride, PgCN)에 대하여,
상기 멜라민 대 요소의 중량비는 1 : 9 내지 3 : 7이고,
상기 인 전구체는 상기 멜라민 및 요소의 혼합물 100 중량부를 기준으로 20 내지 40 중량부 혼합되고,
상기 인의 함량은 상기 인 도핑 흑연질 탄소질화물 전체 중량을 기준으로 10 내지 40 at%인 것인 인 도핑 흑연질 탄소질화물의 제조방법.
Heat treatment of the mixture of melamine, urea and phosphorus precursors; for phosphorus doped graphite carbon nitride (P-doped Graphitic Carbon Nitride, PgCN),
The weight ratio of the melamine to urea is 1: 9 to 3: 7:
The phosphorus precursor is mixed with 20 to 40 parts by weight based on 100 parts by weight of the mixture of melamine and urea,
The phosphorus-doped graphitic carbon nitride production method of 10 to 40 at% based on the total weight of the phosphorus-doped graphite carbon nitride.
삭제delete 제13항에 있어서,
상기 인 전구체는 제2 인산암모늄인 것을 특징으로 하는 인 도핑 흑연질 탄소질화물의 제조방법.
The method of claim 13,
The phosphorus precursor is a method for producing a phosphorus doped graphite carbon nitride, characterized in that the second ammonium phosphate.
제13항에 있어서,
상기 열처리는 1 내지 10 ℃/min의 승온속도로 400 내지 700 ℃로 승온시킨 후 1 내지 10 시간 동안 유지하여 수행되는 것을 특징으로 하는 인 도핑 흑연질 탄소질화물의 제조방법.
The method of claim 13,
The heat treatment is a method of producing a phosphorus doped graphite carbon nitride, characterized in that is performed by heating for 1 to 10 hours after heating to 400 to 700 ° C at a heating rate of 1 to 10 ° C / min.
제13항에 있어서,
상기 인 전구체는 제2 인산암모늄이며,
상기 열처리는 1 내지 10 ℃/min의 승온속도로 400 내지 700 ℃로 승온시킨 후 1 내지 10 시간 동안 유지하여 수행되는 것을 특징으로 하는 인 도핑 흑연질 탄소질화물의 제조방법.
The method of claim 13,
The phosphorus precursor is diammonium phosphate,
The heat treatment is a method of producing a phosphorus doped graphite carbon nitride, characterized in that is performed by heating for 1 to 10 hours after heating to 400 to 700 ° C at a heating rate of 1 to 10 ° C / min.
KR1020180068089A 2018-06-14 2018-06-14 Coating composition for separator of secondary battery comprising P-doped graphitic carbon nitride, preparation method thereof and Li-S battery comprising the same KR102113222B1 (en)