KR102081263B1 - Functional ceramic accessories containing gold component and method of manufacture thereof - Google Patents

Functional ceramic accessories containing gold component and method of manufacture thereof Download PDF

Info

Publication number
KR102081263B1
KR102081263B1 KR1020190080333A KR20190080333A KR102081263B1 KR 102081263 B1 KR102081263 B1 KR 102081263B1 KR 1020190080333 A KR1020190080333 A KR 1020190080333A KR 20190080333 A KR20190080333 A KR 20190080333A KR 102081263 B1 KR102081263 B1 KR 102081263B1
Authority
KR
South Korea
Prior art keywords
weight
ceramic
gold
ceramic material
adhesive
Prior art date
Application number
KR1020190080333A
Other languages
Korean (ko)
Other versions
KR20190086636A (en
Inventor
신홍대
Original Assignee
신홍대
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 신홍대 filed Critical 신홍대
Priority to KR1020190080333A priority Critical patent/KR102081263B1/en
Publication of KR20190086636A publication Critical patent/KR20190086636A/en
Application granted granted Critical
Publication of KR102081263B1 publication Critical patent/KR102081263B1/en

Abstract

금이 포함된 팔, 침대용 매트리스의 상면에 부착하는 타일, 건물의 내장 타일에 적용할 수 있는 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법에 관한 것으로, (a) 세라믹 소재를 마련하는 단계, (b) 상기 세라믹 소재 상에 수금(liquid gold)을 도포하고, 800~830℃로 소성하는 단계, (c) 상기 단계 (b)에서 성형된 세라믹 소재의 표면에 남은 금(Gold)의 부분에 요업용 접착제를 도포하는 단계, (d) 상기 단계 (c)에서 접착제를 도포한 세라믹 소재의 상면에 유리 분말을 도포하고 646℃의 온도로 소성하여 투명한 유리 코팅층을 형성하는 단계를 포함하는 구성을 마련하여, 세라믹 액세서리를 간단하고 신속하게 제작할 수 있다.The present invention relates to a functional ceramic accessory including a gold-containing arm, a tile attached to an upper surface of a bed mattress, and a gold component applicable to an interior tile of a building, comprising the steps of: (a) preparing a ceramic material; (b) applying liquid gold on the ceramic material and firing at 800 to 830 ° C., and (c) a portion of gold remaining on the surface of the ceramic material formed in step (b). Applying a ceramic adhesive, (d) applying glass powder to the upper surface of the ceramic material to which the adhesive is applied in the step (c) and firing at a temperature of 646 ℃ to form a transparent glass coating layer In this way, the ceramic accessory can be produced simply and quickly.

Description

금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법{Functional ceramic accessories containing gold component and method of manufacture thereof} Functional ceramic accessories containing gold component and method of manufacture

본 발명은 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법에 관한 것으로, 특히 금이 포함된 팔찌에 주로 적용하지만, 예를 들어 침대용 매트리스의 상면에 부착하는 타일, 건물의 내장 타일에 적용할 수 있는 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법에 관한 것이다.The present invention relates to a functional ceramic accessory containing a gold component and a method for manufacturing the same, in particular, mainly applied to a bracelet containing gold, but can be applied to, for example, a tile attached to the upper surface of a bed mattress, a built-in tile of a building. The present invention relates to a functional ceramic accessory including a gold component and a method of manufacturing the same.

일반적으로, 세라믹 코팅재는 건축용 도료, 방수·방식용 도료, 중방 식용 도료, 전자제품용 코팅재, 특수 기능성 도료, 내유성 도료, 타일용 도료 등 다양한 분야에서 사용되고 있으며, 이에 따라, 세라믹 코팅재에 대하여, 내열성, 내식성, 내구성, 경도성, 내염수성, 부착성, 내염수성, 내용제성 및 내화학성 등 다양한 성능이 요구된다. Generally, ceramic coating materials are used in various fields such as construction paints, waterproofing and anticorrosive paints, middle coatings, electronic coatings, special functional paints, oil resistant paints, tile paints, and the like. Various performances such as corrosion resistance, durability, hardness, saline resistance, adhesion, saline resistance, solvent resistance and chemical resistance are required.

현재 다양한 세라믹과 금속 소재를 이용하여, 특정 분야에서의 적용을 위해 최적화된 세라믹 코팅재나 보다 성능이 개선된 다 기능성 세라믹 코팅재를 개발하기 위한 연구가 계속되고 있다.Currently, research is being conducted to develop a ceramic coating material optimized for application in a specific field or a multifunctional ceramic coating material having improved performance by using various ceramic and metal materials.

그러나 종래의 세라믹 코팅제는 중금속 및 환경 호르몬 물질을 포함하고 있거나, 예를 들어 코팅제를 매트릭스 표면에 도포 후, 경화를 위한 숙성(aging) 온도가 약 250 내지 300℃로 높고, 250℃보다 저온에서 실시할 경우 숙성에 긴 시간이 요구되어 과도한 에너지를 필요로 하는 문제가 있다.However, conventional ceramic coatings contain heavy metals and environmental hormonal materials, or, for example, after the coating is applied to the matrix surface, the aging temperature for curing is high, about 250 to 300 ° C., and is carried out at lower temperatures than 250 ° C. If you do need a long time for aging, there is a problem that requires excessive energy.

또 현재까지 사용되고 있는 세라믹 코팅재 조성물에는 바인더로서 에폭시, 우레탄, 아크릴 등의 유기 수지가 함유되어 있어 휘발성 유기 화합물과 같은 인체 유해 성분이 필수적으로 발생하여 인체와 환경에 악영향을 끼치는 문제점 및 유기 수지의 특성상 내열성이 좋지 않으며, 유기 수지를 건축 내외장재로 사용할 경우 대기 중의 오염물이 쉽게 부착되어 미관을 쉽게 해치는 문제점이 있다. 또한, 주방용 가열 조리기나 열 기기의 경우, 음식물 또는 음식물 조리에 필요한 양념류의 가열조리 과정 중에 탄화하여 눌어붙는 현상이 발생하여 세척하기가 곤란하다는 문제점이 있다.In addition, the ceramic coating composition used up to now contains organic resins such as epoxy, urethane, and acryl as binders, so that harmful substances such as volatile organic compounds are inevitably generated, which adversely affects the human body and the environment, and the characteristics of organic resins. The heat resistance is not good, there is a problem in that when the organic resin is used as the interior and exterior materials of the building, contaminants in the air are easily attached to harm the appearance. In addition, in the case of a cooking heater or a cooking appliance for a kitchen, there is a problem in that it is difficult to clean due to the phenomenon of carbonization and sticking during the heating cooking process of the food or seasoning required for cooking the food.

이러한 문제를 해결하기 위한 기술의 일 예가 하기 특허문헌 1 내지 3 등에 개시되어 있다.An example of the technique for solving such a problem is disclosed by following patent documents 1-3 etc.

예를 들어, 하기 특허문헌 1에는 도 1에 도시된 바와 같이, 세라믹소재를 성형하여 형성되는 고융점 세라믹성형물(1), 상기 고융점 세라믹성형물의 상면에 도포되는 요업용 접착제(2), 상기 접착제의 상면에 울퉁불퉁하게 요철형태로 증착되는 것으로 상기 고융점 세라믹성형물보다 낮은 용융온도를 가지는 저융점세라믹 및 베트로사(3), 상기 저융점세라믹 및 베트로사의 상면에 증착되는 귀금속층(4), 상기 귀금속층의 상면에 귀금속층을 보호하기 위해 증착되는 보호피막(5)을 포함하되, 상기 접착제는 고융점 세라믹성형물의 상면에 부분적으로 도포되며, 상기 귀금속층은 저융점세라믹 및 베트로사의 상면과 접착제가 도포되지 않은 고융점 세라믹성형물의 상면에 증착되는 귀금속층이 형성되는 세라믹 성형물(10)에 대해 개시되어 있다.For example, Patent Document 1, as shown in Figure 1, a high melting point ceramic molding (1) formed by molding a ceramic material, a ceramic adhesive (2) applied to the upper surface of the high melting point ceramic molding, Unevenly deposited on the upper surface of the adhesive in a concave-convex shape having a lower melting temperature than that of the high-melting-point ceramic molding (3) and the low-melting ceramic and Betrosa (3), the precious metal layer (4) deposited on the top And a protective film 5 deposited on the upper surface of the noble metal layer to protect the noble metal layer, wherein the adhesive is partially applied on the upper surface of the high-melting-point ceramic molding, and the noble metal layer is formed of low-melting-point ceramic and Betrosa. A ceramic molding 10 is disclosed in which a precious metal layer is deposited on a top surface and a top surface of a high melting point ceramic molding to which an adhesive is not applied.

또 하기 특허문헌 2에는 에폭시실란 100 중량%, 에폭시실란 중량 대비 130 ~ 190 중량%의 에틸알코올 또는 이소프로필알코올 중 선택된 1 내지 2종, 에폭시실란 중량 대비 20 ~ 40 중량%의 증류수와 에폭시실란 중량 대비 30 ~ 50 중량%의 테크라프로필오르소티타넌트 또는 테크라이소프로필티타네이트 또는 티타늄에틸아세토아세테이트 또는 티타늄 아세틸아세토네이트 또는 테트라노르말부틸티타네이트 또는 테트라티타늄이소프로폭사이드 중 선택된 1 내지 6종이 졸-겔 합성법을 통해 제조된 금속 표면용 세라믹 코팅제에 대해 개시되어 있다.In addition, Patent Document 2, 100% by weight of epoxysilane, 130 to 190% by weight of the weight of the epoxy silane 1 to 2 selected from ethyl alcohol or isopropyl alcohol, 20 to 40% by weight of distilled water and epoxy silane weight of the weight of epoxy silane 1 to 6 selected from 30 to 50% by weight of techlapropyl ortho titanate or techisopropyl titanate or titanium ethyl acetoacetate or titanium acetylacetonate or tetranormalbutyl titanate or tetratitanium isopropoxide A ceramic coating for metal surfaces prepared via sol-gel synthesis is disclosed.

한편, 하기 특허문헌 3에는 금, 유황, 산화 비스무드 및 붕산 납을 포함하는 수금 혼합액을 제조하는 제1 단계, 연단(납)과 규사, 평산 두 가지 물질 중의 적어도 하나 이상의 재료를 주원료로 하는 코팅재를 제조하는 제2 단계, 흙(정제된 점토)을 반죽하여 제조코자 하는 형상으로 모양을 형성한 도자기류를 밀폐된 가마 속에 넣고 920∼980℃로 8∼12시간 동안 초벌 소성하고 서서히 실온으로 냉각시키는 제3 단계, 상기 제3 단계에서 초벌 소성된 도자기류의 표면에 상기 제1 단계에서 제조된 수금 혼합액을 이용하여 원하는 문양을 붓으로 그리거나 스크린 인쇄 또는 전사대지 인쇄하여 다시 밀폐된 가마 속에 넣고 500∼850℃에서 8∼15시간 동안 1차 소성한 후 냉각시키는 제4 단계 및 상기 제4 단계의 1차 소성된 도자기류 표면상에 상기 제2 단계에서 제조된 코팅제를 붓으로 코팅하거나 스크린 인쇄 또는 전사대지 인쇄한 다음, 이를 가마에 넣어 490∼840℃에서 5∼8시간 동안 2차 소성시키는 제5 단계를 포함하는 수금으로 코팅된 도자기류의 제조방법에 대해 개시되어 있다.On the other hand, Patent Document 3, the first step of producing a molten liquid mixture containing gold, sulfur, bismuth oxide and lead borate, a coating material containing at least one material of two materials such as podium (lead) and silica sand, Pyeongsan as a main raw material In the second step of preparing the clay, the clay (purified clay) was kneaded and placed in a closed kiln into a closed kiln for 8 to 12 hours at 920 to 980 ° C and gradually cooled to room temperature. In the third step, the desired pattern is drawn on the surface of the porcelain first fired in the third step by using a collection of liquids prepared in the first step with a brush or by screen printing or transfer sheet printing and placed in a closed kiln. The fourth step of the first firing at 500 ~ 850 ℃ for 8 to 15 hours and then cooled and the second step on the first fired porcelain surface of the fourth step Coating method of the coating agent with a brush or screen printing or transfer sheet printing, and then put it in a kiln for the method of manufacturing ceramics coated with the harp including the fifth step of secondary firing at 490 ~ 840 ℃ for 5 to 8 hours Is disclosed.

대한민국 등록특허공보 제10-1315344호(2013.09.30 등록)Republic of Korea Patent Publication No. 10-1315344 (2013.09.30 registration) 대한민국 공개특허공보 제2009-0006695호(2009.01.15 공개)Republic of Korea Patent Publication No. 2009-0006695 (published Jan. 15, 2009) 대한민국 등록특허공보 제10-0446477호(2004.08.20 등록)Republic of Korea Patent Publication No. 10-0446477 (registered Aug. 20, 2004)

상술한 바와 같은 특허문헌 1에 개시된 기술은 본 발명자가 발명하여 등록된 것으로서, 도 1에 도시된 바와 같이 타일 양각 인쇄용 유리분말로 사용되는 베트로사(Vetrosa)와 저융점세라믹을 요철 형태로 증착하는 구조를 마련하여 가열하는 공정이 필요하므로, 제조 과정이 번잡하고 이에 따라 제조 비용이 증가한다는 문제가 있었다.The technique disclosed in Patent Document 1 as described above has been invented and registered by the present inventors, and as shown in FIG. 1, the method of depositing Vetrosa and low melting point ceramics, which are used as a glass powder for embossed printing of tiles, in an uneven form Since the process of preparing and heating the structure is necessary, there is a problem that the manufacturing process is complicated and the manufacturing cost increases accordingly.

상기 특허문헌 2에 개시된 기술은 유해가스, 습기 또는 유기물질 등으로 쉽게 변색, 부식되는 금속류를 졸-겔 합성법을 통해 제조한 수용성 친환경 세라믹 코팅제로 처리함으로써 내후성 및 내식성뿐만 아니라 알코올 등으로 간단한 탈지처리를 통해 피착체와의 접착력 및 표면경도를 부여할 수 있는 것으로서, 금, 은과 같은 귀금속에는 적용할 수 없다는 문제가 있었다.The technique disclosed in the Patent Document 2 is a simple degreasing treatment by using a water-soluble eco-friendly ceramic coating prepared by the sol-gel synthesis method of metals that easily discolor and corrode with harmful gases, moisture or organic substances, as well as weather resistance and corrosion resistance As it is possible to give the adhesion and surface hardness to the adherend through, there was a problem that can not be applied to precious metals such as gold, silver.

또한, 상기 특허문헌 3에 개시된 기술에서는 수금을 이용하여 원하는 문양을 붓으로 그리거나 스크린 인쇄 또는 전사 대지 인쇄하고, 도자기류의 표면을 수금으로 전반적으로 코팅시킨 후 소성하고, 코팅된 도자기류 표면상에 코팅제를 붓으로 코팅하거나 스크린 인쇄 또는 전사대지 인쇄를 하는 과정을 거치므로, 상기 특허문헌 1과 같이, 제조 과정이 번잡하고 이에 따라 제조 비용이 증가한다는 문제가 있었다.In addition, in the technique disclosed in Patent Document 3, a desired pattern is drawn with a brush, or screen-printed or transferred to a printed sheet, and the surface of the ceramics is coated with a metal sheet in general, followed by sintering. Since the coating is coated with a brush or screen printing or transfer sheet printing is carried out, there is a problem that the manufacturing process is complicated and the manufacturing cost increases accordingly, as in Patent Document 1.

본 발명의 목적은 상술한 바와 같은 문제점을 해결하기 위해 이루어진 것으로서, 팔찌와 같은 고급스러운 세라믹 액세서리를 간단하고 신속하게 제작할 수 있는 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법을 제공하는 것이다.An object of the present invention is to solve the problems as described above, to provide a functional ceramic accessory and a method for manufacturing the same containing a gold component that can easily and quickly produce a high-quality ceramic accessories such as bracelets.

본 발명의 다른 목적은 제조 공정의 단순화에 의해 저렴하게 세라믹 액세서리를 제작할 수 있는 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법을 제공하는 것이다.It is another object of the present invention to provide a functional ceramic accessory and a method for manufacturing the same, which contain a gold component which can be manufactured at low cost by simplifying the manufacturing process.

상기 목적을 달성하기 위해 본 발명에 따른 기능성 세라믹 액세서리의 제조방법은 금 성분이 포함되는 기능성 세라믹 액세서리를 제조하는 방법으로서, (a) 세라믹 소재를 마련하는 단계, (b) 상기 세라믹 소재 상에 수금(liquid gold)을 도포하고, 800~830℃로 소성하는 단계, (c) 상기 단계 (b)에서 성형된 세라믹 소재의 표면에 남은 금(Gold)의 부분에 요업용 접착제를 도포하는 단계, (d) 상기 단계 (c)에서 접착제를 도포한 세라믹 소재의 상면에 한국 세라믹에서 제조·판매되는 제품명 크린클(Crinkle)(이하“유리 분말”이라 한다)을 도포하고 646℃의 온도로 소성하여 투명한 유리 코팅층을 형성하는 단계를 포함하고, 상기 수금은 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어지고, 상기 유리 코팅층은 유리 분말, 장석, 용융 조절제의 혼합물이고, 상기 유리 분말은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 1~10 중량%, 소다회 10~20 중량%, 탄산 바륨 1~5 중량%, 알루미나 5~10 중량%로 이루어지는 것을 특징으로 한다.In order to achieve the above object, a method of manufacturing a functional ceramic accessory according to the present invention is a method of manufacturing a functional ceramic accessory including a gold component, comprising: (a) preparing a ceramic material, and (b) collecting water on the ceramic material (liquid gold) and firing at 800 ~ 830 ℃, (c) applying a ceramic adhesive to the portion of the gold (Gold) remaining on the surface of the ceramic material formed in the step (b), ( d) Applying the product name Crinkle (hereinafter referred to as “glass powder”) manufactured and sold in Korean ceramics on the upper surface of the ceramic material coated with the adhesive in the step (c), and baking it at a temperature of 646 ° C. Forming a glass coating layer, wherein the collection is gold powder (Gold powder) 4% by weight, gold sulforedinate 18% by weight, platinum oxide (Platinum oxide) 26% by weight, rhodium oxide (Rhodium oxide) 1 % By weight, bismuth jade 2 wt% Bismuth octylate, 31 wt% Rosin, 6 wt% Turpentine oil, 6 wt% Camphor oil, 3-methoxy-3-methyl-1-butanol (3-methoxy-3-methyl-1-butanol) 6 wt%, the glass coating layer is a mixture of glass powder, feldspar, melt control agent, the glass powder is 50 to 60 wt% of silica sand, 20 to 30 boric acid It is characterized by consisting of 1% by weight, 1-10% by weight of carbonate, 10-20% by weight of soda ash, 1-5% by weight of barium carbonate, 5-10% by weight of alumina.

또 본 발명에 따른 기능성 세라믹 액세서리의 제조방법은 금 성분이 포함되는 기능성 세라믹 액세서리를 제조하는 방법으로서, (a) 세라믹 소재를 마련하는 단계, (b) 상기 세라믹 소재의 상면에 요업용 접착제를 도포하는 단계, (c) 상기 단계 (b)에서 접착제가 도포된 세라믹 소재의 표면에 한국 세라믹에서 제조·판매되는 제품명 크린클(Crinkle)(이하“유리 분말”이라 한다)을 도포한 뒤에 950~1050℃의 온도로 소성하는 단계, (d) 상기 단계 (c)에서 소성된 유리 분말의 상면에 수금(liquid gold)을 도포하고, 800~830℃로 소성하는 단계, (e) 상기 단계 (d)에서 금이 소성된 상면에 표면보호 피막층을 형성하는 단계를 포함하고, 상기 유리 분말은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 1~10 중량%, 소다회 10~20 중량%, 탄산 바륨 1~5 중량%, 알루미나 5~10 중량%로 이루어지며, 상기 수금은 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어지고, 상기 표면보호 피막층은 1차 표면보호 피막층을 형성하는 제1 세라믹코팅제와 상기 1차 표면보호 피막층의 상면에 도포된 세라믹 표면코팅제로 이루어지고, 상기 세라믹 표면코팅제는 주제로서 상기 제1 세라믹코팅제와 경화제로서 제2 세라믹코팅제가 14:4의 중량비로 혼합하여 구성된 것을 특징으로 한다.In addition, the method of manufacturing a functional ceramic accessory according to the present invention is a method of manufacturing a functional ceramic accessory containing a gold component, (a) preparing a ceramic material, (b) applying a ceramic adhesive on the upper surface of the ceramic material Step (c) after applying the product name Crinkle (hereinafter referred to as “glass powder”) manufactured and sold in Korean ceramics on the surface of the ceramic material to which the adhesive is applied in step (b), 950 to 1050. Calcining at a temperature of (° C.), (d) applying liquid gold to the upper surface of the glass powder calcined in the step (c), and calcining at 800 to 830 ° C., (e) the step (d) Forming a surface protective film layer on the upper surface is calcined from gold, wherein the glass powder is 50 to 60% by weight of silica sand, 20 to 30% by weight boric acid, 1 to 10% by weight carbonate, 10 to 20% by weight soda ash Consisting of 1 to 5% by weight of barium carbonate and 5 to 10% by weight of alumina The collection is 4% by weight of gold powder (Gold powder), 18% by weight of gold sulforedinate, 26% by weight of platinum oxide, 1% by weight of rhodium oxide, Bismuth octylate (Bismuth octylate 2% by weight, rosin 31% by weight, 6% by weight turpentine oil, 6% by weight camphor oil, 3-methoxy-3-methyl-1-butanol (3- methoxy-3-methyl-1-butanol) 6 wt%, wherein the surface protective coating layer is a first ceramic coating agent forming a primary surface protection coating layer and a ceramic surface coating agent applied to an upper surface of the primary surface protection coating layer. The ceramic surface coating agent is composed of a first ceramic coating agent and a second ceramic coating agent as a curing agent in a weight ratio of 14: 4.

또한, 본 발명에 따른 기능성 세라믹 액세서리는 상술한 기능성 세라믹 액세서리의 제조방법에 의해 제조된 것을 특징으로 한다.In addition, the functional ceramic accessory according to the invention is characterized in that it is manufactured by the method for producing a functional ceramic accessory described above.

상술한 바와 같이, 본 발명에 따른 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법에 의하면, 접착제를 도포한 세라믹 소재의 상면에 유리 분말을 도포하고 646℃의 온도로 소성하여 투명한 유리 코팅층을 형성하므로, 세라믹 액세서리를 간단하고 신속하게 제작할 수 있다는 효과가 얻어진다.As described above, according to the functional ceramic accessory including the gold component according to the present invention and a method for manufacturing the same, glass powder is coated on the upper surface of the ceramic material coated with an adhesive and baked at a temperature of 646 ° C. to form a transparent glass coating layer. Therefore, the effect that the ceramic accessory can be manufactured simply and quickly is obtained.

또 본 발명에 따른 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법에 의하면, 세라믹 소재의 표면에 유리 분말을 소성하고, 금이 소성된 상면에 표면보호 피막층을 형성하므로, 액세서리에서 금 부분의 입체감을 마련함과 동시에 마모를 최소화할 수 있다는 효과도 얻어진다.In addition, according to the functional ceramic accessory including the gold component according to the present invention and the manufacturing method thereof, glass powder is fired on the surface of the ceramic material, and a surface protective film layer is formed on the upper surface of the fired gold, so that the three-dimensional impression of the gold portion in the accessory At the same time, the effect of minimizing wear can be obtained.

도 1은 종래의 기술에 따른 세라믹 성형물의 단면도,
도 2는 본 발명의 제1 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리의 제조 과정을 설명하기 위한 단면도,
도 3은 본 발명의 제2 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리의 제조 과정을 설명하기 위한 단면도.1 is a cross-sectional view of a ceramic molding according to the prior art,
2 is a cross-sectional view illustrating a manufacturing process of a functional ceramic accessory including a gold component according to a first embodiment of the present invention;
3 is a cross-sectional view illustrating a manufacturing process of a functional ceramic accessory including a gold component according to a second embodiment of the present invention.

본 발명의 상기 및 그 밖의 목적과 새로운 특징은 본 명세서의 기술 및 첨부 도면에 의해 더욱 명확하게 될 것이다.The above and other objects and novel features of the present invention will become more apparent from the description of the specification and the accompanying drawings.

[ 제1 실시 예 ]First Embodiment

이하, 본 발명에 따른 제1 실시 예를 도 2에 따라 설명한다.Hereinafter, a first embodiment according to the present invention will be described with reference to FIG.

도 2는 본 발명의 제1 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리의 제조 과정을 설명하기 위한 단면도 이다.2 is a cross-sectional view for describing a manufacturing process of a functional ceramic accessory including a gold component according to a first embodiment of the present invention.

본 발명의 제1 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리는 도 2에 도시된 바와 같이, 먼저 세라믹 소재(100)를 마련한다. 이 세라믹 소재(100)는 예를 들어 맥반석으로 마련될 수 있다. 그러나 이에 한정되는 것은 아니고, 점토, 고령토, 장석, 규석 등을 사용할 수도 있다.In the functional ceramic accessory including the gold component according to the first embodiment of the present invention, as shown in FIG. 2, a ceramic material 100 is first prepared. The ceramic material 100 may be made of, for example, elvan. However, the present invention is not limited thereto, and clay, kaolin, feldspar, silica, and the like can also be used.

다음에 상기 세라믹 소재(100) 상에 수금(liquid gold, 200)을 도포한다. 이 수금(200)은 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어진다. Next, a liquid gold 200 is coated on the ceramic material 100. This collection 200 is composed of 4% by weight of gold powder, 18% by weight of gold sulforedinate, 26% by weight of platinum oxide, 1% by weight of rhodium oxide, bismuth octylate ( 2% by weight Bismuth octylate, 31% by weight Rosin, 6% by weight Turpentine oil, 6% by weight Camphor oil, 3-methoxy-3-methyl-1-butanol (3 -methoxy-3-methyl-1-butanol).

이후, 세라믹 소재(100) 상에 수금(200)이 도포된 상태에서 800~830℃로 소성하고 냉각시키면, 수금(200)에 함유된 이물질은 휘발 되고 순수 금(Gold)만 남게 된다. Subsequently, when the calciner 200 is coated on the ceramic material 100 and then cooled to 800 to 830 ° C., the foreign matter contained in the scaffold 200 is volatilized and only pure gold remains.

이어서 성형된 세라믹 소재(100)의 표면에 남은 금(Gold)의 부분에 요업용 접착제(300)를 도포한다. 상기 요업용 접착제(300)는 고분자 접착제로서, 상용의 접착제를 사용할 수 있다. Next, the ceramic adhesive 300 is applied to a portion of gold remaining on the surface of the molded ceramic material 100. The ceramic adhesive 300 may be a commercial adhesive as a polymer adhesive.

다음에, 접착제(300)를 도포한 세라믹 소재(100)의 상면에 유리 코팅층(400)을 형성하는 유리 분말을 도포하고 646℃의 온도로 소성하여 투명한 유리 코팅층(400)을 형성한다.Next, the glass powder forming the glass coating layer 400 is applied to the upper surface of the ceramic material 100 to which the adhesive 300 is applied and baked at a temperature of 646 ° C. to form a transparent glass coating layer 400.

상기 유리 코팅층(400)은 유리 분말, 장석, 용융 조절제를 혼합하여 형성할 수 있다. 이때, 작업자의 의도한 대로 유리 분말을 세라믹 소재(100)의 전체 면에 균일한 두께, 예를 들어 1㎜로 도포한 뒤에 646℃의 온도로 소성하면 세라믹 소재(100)의 전체면에 평면으로 표면이 형성된다.The glass coating layer 400 may be formed by mixing glass powder, feldspar, and melting control agent. At this time, the glass powder is applied to the entire surface of the ceramic material 100 at a uniform thickness, for example, 1 mm, and then fired at a temperature of 646 ° C. as the worker intended, and the surface of the ceramic material 100 is flat. The surface is formed.

또 상기 유리 분말은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 0~10 중량%, 소다회 10~20 중량%, 탄산 바륨 0~5 중량%, 알루미나 5~10 중량%을 포함할 수 있다.In addition, the glass powder includes 50 to 60% by weight of silica sand, 20 to 30% by weight of boric acid, 0 to 10% by weight of carbonate carbonate, 10 to 20% by weight of soda ash, 0 to 5% by weight of barium carbonate, and 5 to 10% by weight of alumina. can do.

상술한 바와 같은 유리 코팅층(400)은 표면을 매끈하여 미려하게 함과 아울러 금의 마모를 방지하고, 금 특유의 고급스러운 컬러가 외부로 나타나게 한다.As described above, the glass coating layer 400 smoothes the surface and prevents abrasion of the gold, and causes the exclusive color of the gold to appear to the outside.

한편, 상기 실시 예에서는 유리 분말을 1㎜로 균일하게 도포한 구조로 설명을 하였지만, 이에 한정되는 것은 아니고, 상기 유리 분말을 1~2㎜의 두께로 부분적으로 울퉁불퉁하게 요철 형태로 증착시켜 소성하면, 금의 상면이 울퉁불퉁한 요철 형태로 형성된다. 이와 같은 요철 형상에 의해 요철부가 금 덩어리처럼 보이게 할 수 있다.In the above embodiment, the glass powder is uniformly coated at 1 mm, but the present invention is not limited thereto. When the glass powder is partially unevenly deposited at a thickness of 1 mm to 2 mm, the sintered shape is baked. , The upper surface of the gold is formed in the form of irregular bumps. This uneven shape can make the uneven portion look like a lump of gold.

[ 제2 실시 예 ]Second Embodiment

이하, 본 발명에 따른 제2 실시 예를 도 3에 따라 설명한다.Hereinafter, a second embodiment according to the present invention will be described with reference to FIG. 3.

도 3은 본 발명의 제2 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리의 제조 과정을 설명하기 위한 단면도 이다.3 is a cross-sectional view illustrating a manufacturing process of a functional ceramic accessory including a gold component according to a second embodiment of the present invention.

본 발명의 제2 실시 예에 따른 금 성분이 포함되는 기능성 세라믹 액세서리는 도 3에 도시된 바와 같이, 먼저 세라믹 소재(100)를 마련한다. 이 세라믹 소재(100)는 상술한 제1 실시 예와 같이, 예를 들어 맥반석으로 마련될 수 있다. 그러나 이에 한정되는 것은 아니고, 점토, 고령토, 장석, 규석 등을 사용할 수도 있다.In the functional ceramic accessory including the gold component according to the second embodiment of the present invention, as shown in FIG. 3, a ceramic material 100 is first prepared. The ceramic material 100 may be made of, for example, elvan, as in the first embodiment described above. However, the present invention is not limited thereto, and clay, kaolin, feldspar, silica, and the like can also be used.

다음에 상기 세라믹 소재(100)의 상면에 요업용 접착제(310)를 도포한다. 상기 요업용 접착제(310)는 고분자 접착제로서, 상용의 접착제를 사용할 수 있다. Next, the ceramic adhesive 310 is applied to the upper surface of the ceramic material 100. The ceramic adhesive 310 may be a commercial adhesive as a polymer adhesive.

그리고 상면에 접착제가 도포된 세라믹 소재(100)의 표면에 한국 세라믹에서 제조·판매되는 유리 분말(500)[제품명 : 크린클(Crinkle)]를 도포한 뒤에 950~1050℃의 온도로 소성한다.Then, the glass powder 500 (product name: Crinkle) manufactured and sold in Korean ceramics is coated on the surface of the ceramic material 100 having the adhesive applied to the upper surface, and then fired at a temperature of 950 to 1050 ° C.

상기 유리 분말(500)은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 0~10 중량%, 소다회 10~20 중량%, 탄산 바륨 0~5 중량%, 알루미나 5~10 중량%을 포함할 수 있다.The glass powder 500 is 50 to 60% by weight of silica sand, 20 to 30% by weight boric acid, 0 to 10% by weight of carbonic carbonate, 10 to 20% by weight of soda ash, 0 to 5% by weight of barium carbonate, 5 to 10% by weight of alumina It may include.

한편, 작업자의 의도에 따라 접착제(310) 상면에 유리 분말(500)을 균일, 예를 들어 1㎜ 두께로 균일하게 도포 후 소성하면, 세라믹 소재(100) 상면에 평탄한 유광이 형성되고, 유리 분말(500)을 울퉁불퉁하게 부분적으로 1~2㎜의 두께로 도포하고 소성하면 울퉁불퉁한 요철부가 형성된다.On the other hand, when the glass powder 500 is uniformly applied, for example, 1 mm thick and uniformly baked on the upper surface of the adhesive 310 according to the intention of the operator, a flat gloss is formed on the upper surface of the ceramic material 100, and the glass powder When the 500 is unevenly partially coated with a thickness of 1 to 2 mm and fired, an uneven portion is formed.

이후, 유리 분말(500)이 도포되고 소성된 상면에 접착제(320)를 도포한 다음 수금(200)을 도포하고 800~830℃로 소성하면 수금(200)에 함유된 이물질은 휘발 되고 순수 금(Gold)만 남게 된다.Subsequently, the glass powder 500 is coated and then coated with an adhesive 320 on the fired top surface, then the collection 200 is applied, and when fired at 800 to 830 ° C., foreign matter contained in the collection 200 is volatilized and pure gold ( Only Gold) remains.

상기 수금(200)은 상술한 제1 실시 예와 같이, 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어진다. As in the first embodiment, the collection 200 is 4% by weight of gold powder, 4% by weight of gold sulforedinate, 18% by weight of platinum oxide, and 26% by weight of rhodium oxide. ) 1% by weight, Bismuth octylate 2% by weight, Rosin 31% by weight, 6% by weight Turpentine oil, 6% by weight Camphor oil, 3-methoxy- It consists of 6% by weight of 3-methyl-1-butanol.

이어서, 상기 금이 소성된 상면에 표면보호 피막층(600)을 형성한다. Subsequently, a surface protective film layer 600 is formed on the upper surface of the gold fired.

상기 표면보호 피막층(600)은 1차 표면보호 피막층을 형성하는 제1 세라믹코팅제와 상기 1차 표면보호 피막층의 상면에 도포된 세라믹 표면코팅제로 이루어진다.The surface protective film layer 600 includes a first ceramic coating agent for forming a first surface protection film layer and a ceramic surface coating agent applied to an upper surface of the first surface protection film layer.

상기 제1 세라믹코팅제는 예를 들어, 대한민국 공개특허공보 제2016-0113359호(2016.09.29 공개)에 기재된 바와 같이, (A) 용매 100 중량부를 기준으로, 실리카(SiO2) 20~80 중량부, 알루미나(Al2O3) 3~15 중량부, 지르코니아(ZrO2), 티타니아(TiO2), 이트리아(Yi2O3) 및 이들의 혼합물로 이루어진 군으로부터 선택되는 성분 2~10 중량부, 실리콘 오일 중합체 0.1~3 중량부를 포함하여 이루어지는 조성물 (A) 및 (B) MTMS(methyl tri-methoxy silane) 100 중량부를 기준으로 GPTMS(Glycidoxy propyl tri-methoxy silane) 20~60 중량부를 포함하는 조성물 (B)를 포함하며, 상기 조성물 (A) 100 중량부를 기준으로 상기 조성물 (B) 60~140 중량부를 혼합하고, 15 내지 25℃의 온도에서 10~50시간 동안 프리에이징(preaging) 하여 이루어진 세라믹 코팅제를 사용할 수 있으며, 이 제1 세라믹코팅제를 도포하고 330℃로 소성하면 단단하고 표면이 거친 1차 표면보호 피막층이 형성된다.The first ceramic coating agent, for example, as described in Republic of Korea Patent Publication No. 2016-0113359 (published on September 29, 2016), based on 100 parts by weight of the solvent (A), 20 to 80 parts by weight of silica (SiO 2), 3 to 15 parts by weight of alumina (Al 2 O 3 ), 2 to 10 parts by weight of a component selected from the group consisting of zirconia (ZrO 2 ), titania (TiO 2 ), yttria (Yi 2 O 3 ), and mixtures thereof, Composition comprising 20 to 60 parts by weight of GPTMS (Glycidoxy propyl tri-methoxy silane) based on 100 parts by weight of the composition (A) and (B) MTMS (methyl tri-methoxy silane) comprising 0.1 to 3 parts by weight of a silicone oil polymer ( B), a ceramic coating comprising 60 to 140 parts by weight of the composition (B) based on 100 parts by weight of the composition (A) and preaging at a temperature of 15 to 25 ° C. for 10 to 50 hours. The first ceramic coating agent may be applied and then cooled to 330 ° C. If the surface is hard to form a rough primary surface protective coating layer.

계속해서 상기 1차 표면보호 피막층의 상면에 세라믹 표면코팅제를 도포하고, 80~100℃로 소성하면 거친 1차 표면보호 피막층의 표면에 세라믹 표면코팅제가 접착이 잘되어 견고한 매끄러운 표면보호 피막층(600)이 형성되고, 이 표면보호 피막층(600)이 벗겨지지 않게 된다.Subsequently, the ceramic surface coating agent is applied to the upper surface of the first surface protective film layer, and when fired at 80 to 100 ° C., the ceramic surface coating agent is well adhered to the surface of the rough primary surface protective film layer, thereby providing a firm and smooth surface protective film layer 600. Is formed and the surface protective film layer 600 is not peeled off.

상기 세라믹 표면코팅제는 상술한 제1 세라믹코팅제(주제)와 제2 세라믹코팅제(경화제)를 14:4의 중량비로 혼합하여 구성된다.The ceramic surface coating agent is formed by mixing the aforementioned first ceramic coating agent (topic) and the second ceramic coating agent (curing agent) in a weight ratio of 14: 4.

이 제2 세라믹 코팅제로서는 예를 들어, 대한민국 등록특허공보 제10-1400911호(2014.05.22 등록)에 기재된 바와 같이, 용제로서 콜로이드 실리카 수용액, 티타니아 수용액, 지르코니아 수용액, 메탄올, 이소프로필알코올(IPA), 메틸하이드로겐 실리콘 오일, 불소실란, 기능성 충전제 및 안료를 포함하는 제1 용액 및 결합제로서 메틸트리메톡시실란(MTMS(methyltrimethoxysilane)), 글리시독시프로필 트리메톡시실란(GPTMS(glycidoxypropyl trimethoxysilane)) 및 촉매를 포함하는 제2 용액을 포함하는 세라믹 코팅제 조성물을 사용할 수 있다.As this second ceramic coating agent, for example, as described in Korean Patent Publication No. 10-1400911 (registered on May 22, 2014), a colloidal silica aqueous solution, a titania aqueous solution, a zirconia aqueous solution, methanol, and isopropyl alcohol (IPA) are used as a solvent. And methyltrimethoxysilane (MTMS), glycidoxypropyl trimethoxysilane (GPTMS) as a first solution and binder comprising methylhydrogen silicone oil, fluorinesilane, functional filler and pigment And it can be used a ceramic coating composition comprising a second solution comprising a catalyst.

상술한 제2 실시 예에서는 유리 분말(500)이 도포되고 소성된 상면에 수금(200)이 마련되고, 이 수금 상에 표면보호 피막층(600)이 형성되므로, 제1 실시 예에 비해 더욱 더 입체감을 향상시킬 수 있다In the above-described second embodiment, since the collection 200 is provided on the top surface of which the glass powder 500 is coated and fired, and the surface protective film layer 600 is formed on the collection, the three-dimensional effect is further increased compared to the first embodiment. Can improve

또한, 상술한 제2 실시 예에서도 제1 실시 예와 동일하게 세라믹 완성품의 표면을 평탄하고 매끄럽게 형성하거나 또는 금의 상면이 울퉁불퉁한 요철 형태로 형성된다. 따라서, 요철 형상에 의해 요철부가 금덩어리처럼 보이게 한다.In addition, in the second embodiment described above, similarly to the first embodiment, the surface of the ceramic finished product is formed flat and smooth, or the upper surface of the gold is formed in an uneven shape. Therefore, the uneven portion makes the uneven portion look like a lump of gold.

이상 본 발명자에 의해서 이루어진 발명을 상기 실시 예에 따라 구체적으로 설명하였지만, 본 발명은 상기 실시 예에 한정되는 것은 아니고 그 요지를 이탈하지 않는 범위에서 여러 가지로 변경 가능한 것은 물론이다.As mentioned above, although the invention made by the present inventor was demonstrated concretely according to the said Example, this invention is not limited to the said Example and can be variously changed in the range which does not deviate from the summary.

본 발명에 따른 금 성분이 포함되는 기능성 세라믹 액세서리 및 그 제조방법을 사용하는 것에 의해 세라믹 액세서리를 간단하고 신속하게 제작할 수 있다.By using the functional ceramic accessory containing the gold component and the manufacturing method thereof according to the present invention, the ceramic accessory can be produced simply and quickly.

100 : 세라믹 소재
200 : 수금
300 : 요업용 접착제
400 : 유리 코팅층100: ceramic material
200: collection
300: ceramic adhesive
400: glass coating layer

Claims (3)

금 성분이 포함되는 기능성 세라믹 액세서리를 제조하는 방법으로서,
(a) 세라믹 소재를 마련하는 단계,
(b) 상기 세라믹 소재 상에 수금(liquid gold)을 도포하고, 800~830℃로 소성하는 단계,
(c) 상기 단계 (b)에서 성형된 세라믹 소재의 표면에 남은 금(Gold)의 부분에 요업용 접착제를 도포하는 단계,
(d) 상기 단계 (c)에서 접착제를 도포한 세라믹 소재의 상면에 유리 분말을 도포하고 646℃의 온도로 소성하여 투명한 유리 코팅층을 형성하는 단계를 포함하고,
상기 수금은 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어지고,
상기 유리 코팅층은 유리 분말, 장석, 용융 조절제의 혼합물이고,
상기 유리 분말은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 1~10 중량%, 소다회 10~20 중량%, 탄산 바륨 1~5 중량%, 알루미나 5~10 중량%로 이루어지는 것을 특징으로 하는 금 성분이 포함되는 기능성 세라믹 액세서리의 제조방법.As a method of manufacturing a functional ceramic accessory containing a gold component,
(a) preparing a ceramic material,
(b) applying liquid gold on the ceramic material and firing at 800 to 830 ° C.,
(c) applying a ceramic adhesive to a portion of gold remaining on the surface of the ceramic material molded in step (b),
(d) applying glass powder to the upper surface of the ceramic material to which the adhesive is applied in step (c) and baking at a temperature of 646 ° C. to form a transparent glass coating layer,
The collection is 4% by weight of gold powder (Gold powder), 18% by weight of gold sulforedinate, 26% by weight of platinum oxide, 1% by weight of rhodium oxide, Bismuth octylate (Bismuth octylate) 2% by weight, 31% by weight Rosin, 6% by weight Turpentine oil, 6% by weight Camphor oil, 3-methoxy-3-methyl-1-butanol 3-methyl-1-butanol) 6 wt%
The glass coating layer is a mixture of glass powder, feldspar, melt control agent,
The glass powder is composed of 50 to 60% by weight of silica sand, 20 to 30% by weight boric acid, 1 to 10% by weight of carbonic carbonate, 10 to 20% by weight of soda ash, 1 to 5% by weight of barium carbonate, and 5 to 10% by weight of alumina. A method for producing a functional ceramic accessory comprising a gold component. 금 성분이 포함되는 기능성 세라믹 액세서리를 제조하는 방법으로서,
(a) 세라믹 소재를 마련하는 단계,
(b) 상기 세라믹 소재의 상면에 요업용 접착제를 도포하는 단계,
(c) 상기 단계 (b)에서 접착제가 도포된 세라믹 소재의 표면에 유리 분말을 도포한 뒤에 950~1050℃의 온도로 소성하는 단계,
(d) 상기 단계 (c)에서 소성된 유리 분말의 상면에 수금(liquid gold)을 도포하고, 800~830℃로 소성하는 단계,
(e) 상기 단계 (d)에서 금이 소성된 상면에 표면보호 피막층을 형성하는 단계를 포함하고,
상기 유리 분말은 규사 50~60 중량%, 붕산 20~30 중량%, 탄산카리 1~10 중량%, 소다회 10~20 중량%, 탄산 바륨 1~5 중량%, 알루미나 5~10 중량%로 이루어지며,
상기 수금은 금 분말(Gold powder) 4 중량%, 황산 금(Gold sulforedinate) 18 중량%, 산화백금(Platinum oxide) 26 중량%, 산화로듐(Rhodium oxide) 1 중량%, 비스무트 옥틸레이트(Bismuth octylate) 2 중량%, 로진(Rosin) 31 중량%, 터펜틴 오일(Turpentine oil) 6 중량%, 캠퍼 오일(Camphor oil) 6 중량%, 3-메톡시-3-메틸-1-부탄올(3-methoxy-3-methyl-1-butanol) 6 중량%로 이루어지고,
상기 표면보호 피막층은 1차 표면보호 피막층을 형성하는 제1 세라믹코팅제와 상기 1차 표면보호 피막층의 상면에 도포된 세라믹 표면코팅제로 이루어지고,
상기 세라믹 표면코팅제는 주제로서 상기 제1 세라믹코팅제와 경화제로서 제2 세라믹코팅제가 14:4의 중량비로 혼합하여 구성된 것을 특징으로 하는 금 성분이 포함되는 기능성 세라믹 액세서리의 제조방법.As a method of manufacturing a functional ceramic accessory containing a gold component,
(a) preparing a ceramic material,
(b) applying a ceramic adhesive to the upper surface of the ceramic material,
(c) applying glass powder to the surface of the ceramic material to which the adhesive is applied in step (b) and then baking at a temperature of 950 to 1050 ° C.,
(d) applying liquid gold to the upper surface of the glass powder calcined in the step (c) and calcining at 800 to 830 ° C.,
(e) forming a surface protective film layer on the upper surface of which gold is calcined in step (d),
The glass powder is composed of 50 to 60% by weight of silica sand, 20 to 30% by weight of boric acid, 1 to 10% by weight of carbonate, 10 to 20% by weight of soda ash, 1 to 5% by weight of barium carbonate, and 5 to 10% by weight of alumina. ,
The collection is 4% by weight of gold powder (Gold powder), 18% by weight of gold sulforedinate, 26% by weight of platinum oxide, 1% by weight of rhodium oxide, Bismuth octylate (Bismuth octylate) 2 wt%, 31 wt% Rosin, 6 wt% Turpentine oil, 6 wt% Camphor oil, 3-methoxy-3-methyl-1-butanol 3-methyl-1-butanol) 6% by weight,
The surface protective film layer is composed of a first ceramic coating agent to form a first surface protective film layer and a ceramic surface coating agent applied to the upper surface of the first surface protective film layer,
The ceramic surface coating agent is a method of manufacturing a functional ceramic accessory comprising a gold component, characterized in that the first ceramic coating agent as a subject and a second ceramic coating agent as a curing agent is mixed in a weight ratio of 14: 4. 청구항 제1항 또는 청구항 제2항의 금 성분이 포함되는 기능성 세라믹 액세서리의 제조방법에 의해 제조된 것을 특징으로 하는 금 성분이 포함되는 기능성 세라믹 액세서리.A functional ceramic accessory comprising a gold component, which is produced by a method for producing a functional ceramic accessory containing the gold component of claim 1.
KR1020190080333A 2019-07-03 2019-07-03 Functional ceramic accessories containing gold component and method of manufacture thereof KR102081263B1 (en)