KR102075439B1 - Fluorophosphate Glasses for Active Device with Strong Down- and Upconverstion Emission - Google Patents
Fluorophosphate Glasses for Active Device with Strong Down- and Upconverstion Emission Download PDFInfo
- Publication number
- KR102075439B1 KR102075439B1 KR1020180056420A KR20180056420A KR102075439B1 KR 102075439 B1 KR102075439 B1 KR 102075439B1 KR 1020180056420 A KR1020180056420 A KR 1020180056420A KR 20180056420 A KR20180056420 A KR 20180056420A KR 102075439 B1 KR102075439 B1 KR 102075439B1
- Authority
- KR
- South Korea
- Prior art keywords
- mol
- baf
- glass
- ybf
- erf
- Prior art date
Abstract
개시되는 능동소자용 불소인산염계 유리는, Al(PO3)3 포함하는 메타인산염(metaphosphate) 조성물; BaF2 및 SrF2를 포함하는 불소(fluoride) 조성물; 및 ErF3 및 YbF3로 마련되는 도펀트(dopant);를 포함하여 조성되며, 능동소자(예: 광섬유 레이저)용 유리 모재로 채용 가능한 열적, 기계적 특성을 가지면서도 높은 형광단면적 특성을 가지며, 강화된 하향 및 상향전이 방출 특성 및 극저온 환경에서 높은 민감도(S)를 가진다.Fluorine phosphate-based glass for the active device disclosed is a metaphosphate composition containing Al (PO 3 ) 3 ; Fluoride compositions comprising BaF 2 and SrF 2 ; And a dopant formed of ErF 3 and YbF 3 , and have a high fluorescence cross-sectional property while having thermal and mechanical properties that can be employed as a glass base material for an active device (eg, a fiber laser). Downward and upward transition emission characteristics and high sensitivity (S) in cryogenic environments.
Description
본 발명(Disclosure)은, 능동소자용 불소인산염계 유리(Fluorophosphate Glasses)에 관한 것으로, 특히 광섬유 레이저용 유리 모재로 채용 가능한 열적, 기계적 특성을 가지면서도 높은 형광단면적 특성을 가지며, 강화된 하향 및 상향전환 방출 특성 및 극저온 환경에서 높은 민감도(S)를 가지는 능동소자용 불소인산염계 유리의 조성에 관한 것이다.The present invention relates to fluorophosphate glasses for active devices, and in particular, has a high fluorescence cross-sectional property while having thermal and mechanical properties that can be employed as glass base materials for optical fiber lasers, and enhanced downward and upward directions. It relates to the composition of fluorine phosphate-based glass for active devices having a conversion emission characteristics and high sensitivity (S) in cryogenic environment.
여기서는, 본 발명에 관한 배경기술이 제공되며, 이들이 반드시 공지기술을 의미하는 것은 아니다(This section provides background information related to the present disclosure which is not necessarily prior art).This section provides background information related to the present disclosure which is not necessarily prior art.
일반적으로 어븀(Er) 도핑(doping)된 광섬유증폭기(erbium doped fiber amplifier, EDFA)는 파장분할방식(wavelength division multiplexing, WDM)방식의 통신 시스템은 물론이고 거의 대부분의 광 네트워크에서 주요한 장치로 사용되고 있는 광증폭기 장치로서, 유리재질의 광섬유에 어븀을 도핑하여 1530 내지 1610nm 사이의 파장을 갖는 빛을 증폭 시킨다.Generally, Erbium doped fiber amplifiers (EDF) are used as the main devices in almost all optical networks as well as in wavelength division multiplexing (WDM) communication systems. As an optical amplifier device, a glass fiber optical fiber is doped with erbium to amplify light having a wavelength between 1530 and 1610 nm.
불화물 유리(fluoride glass)에 인산염(phosphate)이 혼합된 불소인산염계 유리(fluorophosphate glass, FP)는 불화물 유리(fluoride glass)에 비하여 열적 안정성과 화학적 내구성이 뛰어나며, 포논 에너지(phonon energy가 낮고, 자외선에서 근적외선까지의 넓은 스펙트럼(spectrum) 영역에서의 광투과 특성 및 굴절률을 선형성이 우수하며, 희토류(RE, rare earth) 원소를 도펀트로 사용할 경우에, 다중 에너지 준위를 제공함으로써 높은 도펀트(dopant) 농도를 구현 할 수 있기 때문에, 짧은 길이 캐비티(cavity)를 이용하면서도 높은 효율을 얻을 수 있는 유리 모재이다. Fluorophosphate glass (FP) with phosphate mixed with fluoride glass has better thermal stability and chemical durability than fluoride glass, and has low phonon energy and low UV light. It has excellent linearity of light transmittance and refractive index in a broad spectrum region from to near infrared rays, and provides high energy dopant concentration by providing multiple energy levels when rare earth (RE) element is used as dopant. Because it can be implemented, a glass base material that can obtain a high efficiency while using a short length cavity (cavity).
한편 이터븀(Yb)은 980nm영역에서 월등히 높은 흡수단면적(absorption cross section)을 제공하며, 도너(2F5/2, Yb3+)의 에너지 준위(energy level)와 억셉터(4I11/2, Er3+)의 에너지 준위의 겹침(overlap)이 우수하기 때문에, 어븀(Er)과 함께 도핑(co-doping)됨으로써, 레이저 여기(laser excitation)의 증감제(sensitizer)로서 이용된다. Ytterbium (Yb), on the other hand, offers an extremely high absorption cross section in the 980 nm region, the energy level of the donors ( 2F 5/2 , Yb3 +) and the acceptor ( 4 I 11/2 , Since the overlap of the energy levels of
이러한 우수한 특성을 갖는 Er/Yb co-doping된 불소인산염계 유리는 앞서 설명한 우수한 성능을 활용하고자, 가시광 또는 적외선 레이저, 광섬유 증폭기, 광 저장 장치 및 해저 광통신망과 같은 기존의 응용 분야뿐만 아니라, 최근에는 라이다(LiDAR, Light Detection and Ranging)와 같이 고출력, eye-safe 광원(1550nm) 및 경량화가 요구되는 3차원 공간 관측 시스템에까지 그 응용 범위가 확대되고 있다. Er / Yb co-doping fluorophosphate-based glass having such excellent properties has recently been used to take advantage of the excellent performance described above, as well as existing applications such as visible or infrared lasers, fiber amplifiers, optical storage devices and subsea optical networks. The range of applications extends to 3D spatial observation systems, such as LiDAR (Light Detection and Ranging), which require high power, eye-safe light sources (1550 nm) and weight reduction.
또한, 바이오기술 및 데이터 저장과 같은 분야에서는 500nm 대역의 녹색과 600nm 대역의 적색 영역 파장을 이용한다. In addition, applications such as biotechnology and data storage use green wavelengths in the 500 nm band and red region wavelengths in the 600 nm band.
이와 같은 넓은 범위의 응용 분야에서 활용되기 위해서는, 장치의 크기가 축소되더라도 높은 펄스 출력을 구현할 수 있는 불소인산염계 유리 모재의 개발이 요구된다. 또한, 980nm의 레이저 여기 시스템을 이용하여, 500~600nm 대역의 파장을 방출하기 위해서는 상향전이(upconversion) 현상을 이용하여야 한다. In order to be utilized in such a wide range of applications, the development of a fluorophosphate-based glass base material that can realize a high pulse output even if the size of the device is reduced. In addition, using a 980nm laser excitation system, in order to emit a wavelength of 500 ~ 600nm band upconversion (upconversion) phenomenon should be used.
본 개시(Disclosure)는, 능동소자(예: 광섬유 레이저)용 유리 모재로 채용 가능한 열적, 기계적 특성을 가지면서도 높은 형광단면적 특성을 가지며, 강화된 하향 및 상향전이 방출 특성 및 극저온 환경에서 높은 민감도(S)를 가지는 능동소자용 불소인산염계 유리의 제공을 일 목적으로 한다.The present disclosure has thermal and mechanical properties that can be employed as a glass base material for active devices (eg, fiber lasers), but also has high fluorescence cross-sectional properties, enhanced down and up-transition emission characteristics, and high sensitivity in cryogenic environments. An object of the present invention is to provide a fluorophosphate-based glass for active elements having S).
여기서는, 본 발명의 전체적인 요약(Summary)이 제공되며, 이것이 본 발명의 외연을 제한하는 것으로 이해되어서는 아니 된다(This section provides a general summary of the disclosure and is not a comprehensive disclosure of its full scope or all of its features).This section provides a general summary of the disclosure and is not a comprehensive disclosure of its full scope or all, provided that this is a summary of the present invention. of its features).
상기한 과제의 해결을 위해, 본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, Al(PO3)3 포함하는 메타인산염(metaphosphate) 조성물; BaF2 및 SrF2를 포함하는 불소(fluoride) 조성물; 및 ErF3 및 YbF3로 마련되는 도펀트(dopant);를 포함하여 조성된다. In order to solve the above problems, fluorophosphate-based glass for an active device according to an aspect of the present invention, a metaphosphate composition containing Al (PO 3 ) 3 ; Fluoride compositions comprising BaF 2 and SrF 2 ; And a dopant provided with ErF 3 and YbF 3 .
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 YbF3는 약 3mol% 내지 약 5mol%인 것을 특징으로 할 수 있다. In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, the YbF 3 may be characterized in that about 3 mol% to about 5 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 ErF3는 약 3mol%이며, 상기 YbF3는 약 3mol% 내지 약 5mol%인 것을 특징으로 할 수 있다. In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, the ErF 3 may be about 3 mol%, and the YbF 3 may be about 3 mol% to about 5 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 Al(PO3)3는 약 20mol% 내지 약 30mol%이며, 상기 BaF2는 약 10mol% 내지 약 60mol% 이며, 상기 SrF2는 약 10mol% 내지 약 70mol%인 것을 특징으로 할 수 있다.In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, Al (PO 3 ) 3 is about 20 mol% to about 30 mol%, and BaF 2 is about 10 mol% to about 60 mol%, SrF 2 may be characterized as about 10 mol% to about 70 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 Al(PO3)3는 약 20mol%이며, 상기 BaF2는 약 40mol% 내지 약 60mol% 이며, 상기 SrF2는 약 20mol% 내지 약 40mol%인 것을 특징으로 할 수 있다.One fluorine-phosphate glass for the active element according to the aspect (aspect) of the present invention, the Al (PO 3) 3 is about 20mol%, the BaF 2 is about 40mol% to about 60mol%, the SrF 2 is about 20 mol% to about 40 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 ErF3는 약 3mol%이며, 상기 YbF3는 약 3mol% 내지 약 5mol%인 것을 특징으로 할 수 있다. In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, the ErF 3 may be about 3 mol%, and the YbF 3 may be about 3 mol% to about 5 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 Al(PO3)3는 약 20mol%이며, 상기 BaF2는 약 60mol%이며, 상기 SrF2는 약 20mol%인 것을 특징으로 할 수 있다.One fluorine-phosphate glass for the active element according to the aspect (aspect) of the present invention, the Al (PO 3) 3 is about 20mol%, the BaF 2 is about 60mol%, the SrF 2 is to be about 20mol% It can be characterized.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 ErF3는 약 3mol%이며, 상기 YbF3는 약 3mol% 내지 약 5mol%인 것을 특징으로 할 수 있다. In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, the ErF 3 may be about 3 mol%, and the YbF 3 may be about 3 mol% to about 5 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 Al(PO3)3는 약 20mol%이며, 상기 BaF2는 약 50mol%이며, 상기 SrF2는 약 30mol%인 것을 특징으로 할 수 있다.One fluorine-phosphate glass for the active element according to the aspect (aspect) of the present invention, the Al (PO 3) 3 is about 20mol%, the BaF 2 is about 50mol%, the SrF 2 is to be about 30mol% It can be characterized.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 ErF3는 약 3mol%이며, 상기 YbF3는 약 3mol% 내지 약 5mol%인 것을 특징으로 할 수 있다. In the fluorine-phosphate-based glass for an active device according to an aspect of the present invention, the ErF 3 may be about 3 mol%, and the YbF 3 may be about 3 mol% to about 5 mol%.
본 발명의 일 태양(aspect)에 따른 능동소자용 불소인산염계 유리는, 상기 Al(PO3)3는 약 20mol%이며, 상기 BaF2는 약 40mol%이며, 상기 SrF2는 약 40mol%인 것을 특징으로 할 수 있다.One fluorine-phosphate glass for the active element according to the aspect (aspect) of the present invention, the Al (PO 3) 3 is about 20mol%, the BaF 2 is about 40mol%, the SrF 2 is to be about 40mol% It can be characterized.
본 개시에 따르면, 유리전이온도(tg) 및 피크온도(tp)를 포함하는 열적 특성, 열팽창계수(CTE)를 포함하는 열기계적 특성 및 유리경도(Knop Hardness)를 포함하는 기계적 특성이 개선되어 광섬유 레이저를 포함하는 능동소자의 제조 공정 상 장점을 제공한다.According to the present disclosure, the thermal properties including the glass transition temperature (tg) and the peak temperature (tp), the thermomechanical properties including the thermal expansion coefficient (CTE), and the mechanical properties including the glass hardness (Knop Hardness) are improved. It provides advantages in the manufacturing process of an active device including a laser.
본 개시에 따르면, 높은 형광단면적(emission cross-section) 특성을 구현하여, 장치의 크기가 축소되더라도, 높은 펄스 출력을 구현할 수 있는 효과를 가진다.According to the present disclosure, by implementing a high emission cross-section characteristic, even if the size of the device is reduced, there is an effect that can implement a high pulse output.
본 개시에 따르면, 도핑물질(예: Er, Yb)의 조성 최적화에 의해 유효한 에너지 전달(energy transfer) 현상으로 인해 유도방출(stimulated emission) 되는 준 안정상태(metastable state) 에너지 준위에서의 캐리어 수명이 연장되는 효과를 가진다.According to the present disclosure, carrier life at a metastable state energy level that is stimulated emission due to an effective energy transfer phenomenon by optimizing the composition of the doping material (eg, Er, Yb) is increased. Has an extended effect.
본 개시에 따르면, 도핑물질(예: Er, Yb)의 조성 최적화에 의해 하향전환(downconversion) 및 상향전환 (upconversion) 방출(emission) 특성이 강화되는 효과를 가진다.According to the present disclosure, downconversion and upconversion emission characteristics are enhanced by optimizing the composition of the doping materials (eg, Er and Yb).
본 개시에 따르면, 극저온에서도 민감도가 탁월한 능동소자용 유리 모재를 얻을 수 있다. 따라서 극저온 환경에서도 사용이 가능한 능동소자의 제공이 가능해진다.According to the present disclosure, it is possible to obtain a glass base material for active elements having excellent sensitivity even at cryogenic temperatures. Therefore, it is possible to provide an active device that can be used even in a cryogenic environment.
도 1a,1b,1c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리 조성 설계 도면이다.
도 2a,2b,2c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 열적 특성 평가에 대한 실험결과를 보인 도면이다.
도 3a,3b,3c는 ErF3-Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 열적 특성 평가에 대한 실험결과를 보인 도면이다.
도 4는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 조성 변화에 따른 열기계적 특성 평가에 대한 실험결과를 보인 도면이다.
도 5a,5b,5c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리조성 설계에 따른 기계적 특성 평가에 대한 실험결과를 보인 도면이다.
도 6a,6b,6c는 ErF3-Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리조성 설계에 따른 기계적 특성 평가에 대한 실험결과를 보인 도면이다.
도 7은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=3:ASB3E3Y, 4:ASB3E4Y, 5:ASB3E5Y)계 유리의 이터븀(Yb) 농도에 따른 흡수 스펙트럼을 보인 도면이다.
도 8은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=3:ASB3E3Y, 4:ASB3E4Y, 5:ASB3E5Y)계 유리의 이터븀(Yb) 농도에 따른 쥬드-오펠트 파라미터의 변화를 보인 도면이다.
도 9는 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 상향전이 스펙트럼을 보인 도면이다.
도 10은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 근적외선 방출 스펙트럼을 보인 도면이다.
도 11은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=4 mol%)계 유리의 파장에 따른 4I13/2 → 4I15/2 전이의 흡수(ACS) 및 방출(ECS) 단면적 변화에 대한 실험결과를 보인 도면이다.
도 12는 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=4 mol%)계 유리의 파장과 반전분포비율에 따른 이득상수 변화에 대한 실험결과를 보인 도면.
도 13은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 4I13/2 에너지 준위에서의 캐리어 감쇄곡선을 보인 도면.
도 14a는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8번에서 도펀트 ErF3의 농도가 3 mol%일 때 이터븀(Yb) 농도에 따른 캐리어 형광단면적 변화에 대한 실험결과를 보인 도면이다.
도 14b는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 9번에서 도펀트 ErF3의 농도가 3 mol%일 때 이터븀(Yb) 농도에 따른 캐리어 형광단면적 변화에 대한 실험결과를 보인 도면이다.
도 14c는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 10번에서 도펀트 ErF3의 농도가 3 mol%일 때 이터븀(Yb) 농도에 따른 캐리어 형광단면적 변화에 대한 실험결과를 보인 도면이다.
도 15a는 Er/Yb 시스템에서 광자의 흡수 및 하향전이에 따른 광자 방출현상을 설명하는 에너지 준위(energy level) 도면이다.
도 15b는 Er/Yb 시스템에서 광자의 흡수 및 상향전이에 따른 광자 방출현상을 설명하는 에너지 준위(energy level) 도면이다.
도 16은 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%, YbF3의 농도가 5 mol% 일 때, 저온 상향전이 방출 스펙트럼을 설명하는 도면이다.
도 17a는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%, YbF3의 농도가 5 mol% 일 때, 녹색 방출(green emissions)의 불소화 강도비율(FIR)의 온도에 따른 변화를 나타내는 도면이다.
도 17b는 도 17a의 유리계의 감도(sensitivity, S)의 온도에 따른 변화를 설명하는 도면이다.1A, 1B, and 1C are glass composition design diagrams of an Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
2a, 2b, and 2c are diagrams showing experimental results for evaluation of thermal properties of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
3A, 3B, and 3C are diagrams showing experimental results for evaluating thermal characteristics of ErF 3 -Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
4 is a view showing the experimental results for the evaluation of the thermomechanical characteristics according to the composition change of the Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
5a, 5b, and 5c show experimental results for evaluation of mechanical properties according to the glass composition design of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
6a, 6b, and 6c are diagrams showing the experimental results for the evaluation of mechanical properties according to the glass composition design of ErF 3 -Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
7 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
Figure 8 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
9 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
10 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
11 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
12 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
13 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -3mol%
FIG. 14A illustrates changes in carrier fluorescence cross-sectional area according to ytterbium (Yb) concentration when the concentration of dopant ErF 3 is 3 mol% in
FIG. 14B illustrates changes in carrier fluorescence cross-sectional area according to ytterbium (Yb) concentration when the concentration of dopant ErF 3 is 3 mol% in
FIG. 14C illustrates the change in carrier fluorescence cross-sectional area according to ytterbium (Yb) concentration when the concentration of dopant ErF 3 is 3 mol% in
FIG. 15A is an energy level diagram illustrating photon emission due to absorption and downward transition of photons in an Er / Yb system.
15B is an energy level diagram illustrating photon emission due to absorption and upward transition of photons in an Er / Yb system.
When 16 is in Fig. 1c Al (PO 3) 3 -BaF 2 is -SrF 2 concentration of the sample composition based dopant ErF 3 from 8, 9, 10, one of the
Figure 17a is the Figure 1c Al (PO 3) 3 -BaF 2 -
It is a figure explaining the change with the temperature of the sensitivity (S) of the glass system of FIG. 17A.
이하, 본 발명에 따른 능동소자용 불소인산염계 유리를 구현한 실시형태를 도면을 참조하여 자세히 설명한다.Hereinafter, an embodiment of implementing a fluorophosphate-based glass for an active device according to the present invention will be described in detail with reference to the drawings.
다만, 본 발명의 사상은 이하에서 설명되는 실시형태에 의해 그 실시 가능 형태가 제한된다고 할 수는 없고, 본 발명의 사상을 이해하는 통상의 기술자는 본 개시와 동일한 기술적 사상의 범위 내에 포함되는 다양한 실시 형태를 치환 또는 변경의 방법으로 용이하게 제안할 수 있을 것이나, 이 또한 본 발명의 기술적 사상에 포함됨을 밝힌다.However, the spirit of the present invention is not to be limited by the embodiments described below, the possible embodiments thereof, and those skilled in the art who understand the spirit of the present invention are included within the scope of the same technical idea as the present disclosure. Embodiments may be easily proposed by a method of substitution or change, but this is also included in the technical spirit of the present invention.
또한, 이하에서 사용되는 용어는 설명의 편의를 위하여 선택한 것이므로, 본 발명의 기술적 내용을 파악하는 데 있어서, 사전적 의미에 제한되지 않고 본 발명의 기술적 사상에 부합되는 의미로 적절히 해석되어야 할 것이다. In addition, the terms used below are selected for convenience of description, and therefore, in grasping the technical contents of the present invention, they should be appropriately interpreted as meanings corresponding to the technical idea of the present invention without being limited to the dictionary meanings.
본 실시형태에 따른 능동소자용 불소인산염계 유리는, Al(PO3)3-BaF2-(Sr, Ca, Mg)F2를 기재(base material)로 하여 구성된다. 구체적으로 본 발명자들은 ErF3-YbF3-Al(PO3)3-BaF2-SrF2로 구성되거나, 이들 조성을 기재로 하여 구성되는 불소인산염계 유리의 조성을 본 발명의 특징으로 한다.The fluorophosphate-based glass for active elements according to the present embodiment is composed of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 as a base material. Specifically, the present inventors characterize the composition of the fluorine phosphate-based glass composed of ErF 3 -YbF 3 -Al (PO 3 ) 3 -BaF 2 -SrF 2 or based on these compositions.
이에 의하면, Al(PO3)3-BaF2-SrF2계 유리의 경우, 능동소자용(예: 광섬유 레이저) 유리에 적용될 수 있는 열적, 기계적 특성 조건을 만족시키면서도, Er3 + 및 Yb3 +로 구성되는 도핑물질의 조성비율(mol%)을 최적화함으로써, 높은 형광단면적(emission cross-section) 특성을 구현하여, 장치의 크기가 축소되더라도, 높은 펄스 출력을 구현할 수 있는 효과를 도출할 수 있게 된다.According to this, in the case of Al (PO 3 ) 3 -BaF 2 -SrF 2 -based glass, Er 3 + and Yb 3 + , while satisfying the thermal and mechanical properties that can be applied to glass for active devices (eg fiber lasers) By optimizing the composition ratio (mol%) of the dopant, the high fluorescence cross-section characteristic is realized, so that even if the size of the device is reduced, a high pulse output can be obtained. do.
도 1a,1b,1c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리 조성 설계 도면이다. 1A, 1B, and 1C are glass composition design diagrams of an Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
도 1a,1b,1c를 참조하면, Al(PO3)3를 인산염으로 사용하며, 스트론튬(Sr)과 칼슘(Ca) 및 마그네슘(Mg)각각의 불소화합물로 사용하는 불소인산염계 유리의 물질 조합에서 유리 형성 영역을 기준으로 정해진 샘플조성(sample composition)을 확인할 수 있다. Referring to FIGS. 1A, 1B, and 1C, a combination of materials of fluorophosphate-based glass using Al (PO 3 ) 3 as a phosphate and used as a fluorine compound of strontium (Sr), calcium (Ca), and magnesium (Mg), respectively In the sample can be determined a sample composition (sample composition) based on the glass forming region.
도 1a,1b,1c에서 흑색 테두리(폐곡선) 내부에 위치되는 샘플조성이 그것이며, 샘플조성에서 각 조성물의 조성비율(mol%) 변화에 따른 열적, 기계적 특성 변화를 분석하여 능동소자용 유리 모재로서의 적합성을 확인하였다. 1A, 1B, and 1C are sample compositions located inside black borders (closed curves), and the glass base materials for active devices are analyzed by analyzing thermal and mechanical properties according to the composition ratio (mol%) of each composition in the sample composition. Suitability was confirmed as.
도 2a,2b,2c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 열적 특성 평가에 대한 실험결과를 보인 도면이며, 도 3a,3b,3c는 ErF3-Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 열적 특성 평가에 대한 실험결과를 보인 도면이다.2a, 2b and 2c show experimental results for the evaluation of thermal properties of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system, and FIGS. 3a, 3b and 3c show ErF 3 −. The experimental results for the evaluation of the thermal properties of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
잉곳(ingot) 형태로 제조된 유리 모재를 일정한 온도로 재가열 하면서 일정한 속도로 인선함으로써 광섬유를 제조하게 된다. An optical fiber is manufactured by cutting a glass base material manufactured in an ingot form at a constant speed while reheating it to a constant temperature.
따라서 광섬유 생산용 유리 모재는 유리전이온도(Tg)와 피크온도(Tp)가 공정의 난이도와 수율을 결정하는 주요한 요소가 된다.Therefore, in the glass base material for optical fiber production, the glass transition temperature (Tg) and peak temperature (Tp) are the major factors that determine the difficulty and yield of the process.
도 2a,2b,2c를 참조하면, Al(PO3)3-BaF2-MgF2계 유리에서 BaF2 대신 MgF2 함량이 증가함에 따라 Tg(glass transition temperature)의 변화가 크지 않음을 알 수 있고, Al(PO3)3-BaF2-CaF2계 유리에서도 sample composition (6)에서 (7)로 BaF2 대신 CaF2 함량이 증가함에 따라 Tg(glass transition temperature)의 변화는 미미함을 확인할 수 있다.Referring to Figure 2a, 2b, 2c, Al ( PO 3) 3 -
또한, Al(PO3)3-BaF2-SrF2계 유리조성 후보에서 sample composition (8)에서 (14)로 BaF2 대신 SrF2 함량이 20 mol%에서 70 mol%로 증가함에 따라 열특성 변위 거동 경향성은 나타나지 않아 상대적으로 미미한 것으로 판단된다.In addition, Al (PO 3) 3 -BaF 2 -
따라서 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계 유리의 경우, 그 조성 변화가 광섬유 제조시 인선 공정에서의 난이도 및 수율에 미치는 영향이 낮으므로, 그 외의 다른 특성 조절을 위한 조성 최적화가 가능한 이점을 가지게 된다.Therefore, in the case of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 -based glass, the effect of the composition change on the difficulty and yield in the cutting process during fiber manufacturing is low, The composition optimization for adjustment has the advantage of being possible.
한편, 망상조직 형성 성분(Network former, 網狀組織形成成分)인 Al(PO3)3 함량이 20 mol%에서 30 mol%로 증가함에 따라 상대적으로 강성구조(structure of rigidity)가 증가하여 유리전이온도는 증가하는 것을 확인할 수 있으며, 이는 Al(PO3)3 함량의 조성변화 범위는 제한이 필요하게 된다.Meanwhile, as the content of Al (PO 3 ) 3 , which is a network former, increases from 20 mol% to 30 mol%, the structure of rigidity increases, resulting in a glass transition. It can be seen that the temperature increases, which requires a limited range of composition change of the Al (PO 3 ) 3 content.
도 3a,3b,3c를 참조하면 (1, 2) mol% ErF3-Al(PO3)3-BaF2-MgF2계 유리에서 ErF3가 증가함에 따라 상대적으로 유리전이온도가 선형적으로 감소함이 확인되는데, (1, 2)mol% ErF3-Al(PO3)3-BaF2-CaF2계와 (1, 2)mol% ErF3-Al(PO3)3-BaF2-SrF2계 유리에서도 동일한 경향성을 확인할 수 있다. 3a, 3b, and 3c, the glass transition temperature decreases linearly with increasing ErF 3 in (1, 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -MgF 2 glass. (1, 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -CaF 2 system and (1, 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -SrF The same tendency can be confirmed also in 2 type glass.
일반적으로 희토류 물질 이온(rare earth ion)이 첨가될 경우 상대적으로 유리전이온도는 증가시키는 현상과 반대 현상을 나타낸다.In general, when the rare earth material ion (rare earth ion) is added, the glass transition temperature is relatively opposite to the phenomenon of increasing.
또한, (1, 2)mol% ErF3-Al(PO3)3-BaF2-MgF2계 유리에서 ErF3가 증가함에 따라 상대적으로 유리전이온도가 선형적으로 감소함을 보였으며, (1, 2)mol% ErF3-Al(PO3)3-BaF2-CaF2계와 (1, 2)mol% ErF3-Al(PO3)3-BaF2-SrF2계 유리에서도 동일한 경향성을 확인할 수 있다. In addition, the glass transition temperature of the (1, 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -MgF 2 glass decreased linearly with increasing ErF 3 , (1 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -CaF 2 and (1, 2) mol% ErF 3 -Al (PO 3 ) 3 -BaF 2 -SrF 2 glass You can check it.
도 4는 ErF3 doped Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 조성 변화에 따른 열적, 기계적 특성에 대한 실험결과를 보인 도면이다.4 is a view showing the experimental results for the thermal and mechanical properties according to the composition change of the ErF 3 doped Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
광섬유가 외부 온도에 따라 팽창하거나 수축하게 되면, 통신 시스템에서 전송 특성이 나빠짐은 물론이고, 광섬유레이저 또는 광섬유 증폭기에서는 이득 특성의 변화를 야기하게 되므로, 열팽창 계수는 작은 것이 바람직하다.When the optical fiber expands or contracts according to the external temperature, not only the transmission characteristics of the communication system deteriorate but also the change of the gain characteristics of the optical fiber laser or the optical fiber amplifier. Therefore, the thermal expansion coefficient is preferably small.
도 4를 참조하면, Er3 +도핑에 의한 열팽창 계수(Coefficient of Thermal Expansion; CTE)의 변화는 Al(PO3)3-BaF2-MgF2계 유리, Al(PO3)3-BaF2-CaF2계 유리에서 Er3 +도핑 양의 변화에 따른 열팽창 계수의 변화 경향성이 Al(PO3)3-BaF2-SrF2계 유리에서도 유사하게 나타남을 확인할 수 있다. 이로부터 Al(PO3)3-BaF2-SrF2계 유리를 광섬유레이저 또는 광섬유 증폭기에 적용하는 경우 코어와 클래딩의 계면접합에 유리한 특성을 가질 것임을 확인할 수 있다. 4, the thermal expansion coefficient due to Er + 3 doped; change in (Coefficient of Thermal Expansion CTE) is Al (PO 3) 3 -BaF 2 -
도 5a,5b,5c는 Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리조성 설계에 따른 기계적 특성에 대한 실험결과를 보인 도면이며, 도 6a,6b,6c는 ErF3-Al(PO3)3-BaF2-(Sr, Ca, Mg)F2계의 유리조성 설계에 따른 기계적 특성에 대한 실험결과를 보인 도면이다.5a, 5b and 5c show experimental results of mechanical properties according to the glass composition design of Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system, and FIGS. 6a, 6b and 6c. Shows the experimental results of the mechanical properties of the glass composition of ErF 3 -Al (PO 3 ) 3 -BaF 2- (Sr, Ca, Mg) F 2 system.
도 5a,5b,5c를 참조하면, Al(PO3)3-BaF2-MgF2계 유리의 경도변화는 20 mol% Al(P03)3에서 BaF2 mol%가 70에서 30으로 감소, 즉 MgF2 mol%는 20에서 50으로 증가함에 따라 경도는 선형적으로 증가함을 알 수 있다. Referring to Figure 5a, 5b, 5c, Al ( PO 3) 3-BaF 2 -MgF 2 -based change in hardness of the glass is 20 mol% Al (P0 3) 3 in mol% BaF 2 is reduced from 70 to 30, that is It can be seen that the hardness increases linearly as MgF 2 mol% increases from 20 to 50.
한편, sample composition 4번 조성의 경우, 상대적으로 경도가 낮은데, Al(P03)3의 mol% 조성비가 10으로 낮아진 것이 원인으로 판단된다.On the other hand, in the case of sample composition No. 4, the hardness is relatively low, it is determined that the mol% composition ratio of Al (P0 3 ) 3 is lowered to 10.
따라서, Al(PO3)3-BaF2-MgF2계 유리에서 Al(P03)3의 조성비가 증가함에 따라 경도는 선형적으로 증가함을 확인할 수 있다.Therefore, it can be seen that the hardness increases linearly as the composition ratio of Al (PO 3 ) 3 increases in the Al (PO 3 ) 3 -BaF 2 -MgF 2 -based glass.
다음으로, Al(PO3)3-BaF2-CaF2계 유리의 경도변화는 20mol% Al(P03)3에서 BaF2 mol%는 70에서 40으로 감소 즉 CaF2 mol%는 10에서 40으로 증가함에 따라 경도는 선형적으로 증가하였으며 30 mol% Al(P03)3에서도 동일한 경도 증가의 경향을 나타냄을 확인할 수 있다. Next, the hardness change of Al (PO 3 ) 3 -BaF 2 -CaF 2 glass is reduced from 20 mol% Al (P0 3 ) 3 to 2 mol% BaF from 70 to 40, that is, CaF 2 mol% from 10 to 40 As the hardness increases, the hardness increases linearly, and it can be seen that the same hardness tends to increase even at 30 mol% Al (P0 3 ) 3 .
또한 Al(P03)3가 증가할 경우 상대적으로 경도가 증가하여 본 실험에서는 6번 14번으로 조성이 변할 경우 경도는 선형적으로 증가함을 확인할 수 있다.In addition, when Al (P0 3 ) 3 increases, the hardness increases relatively. In this experiment, the hardness increases linearly when the composition changes to No. 6 and No. 14.
다음으로, Al(PO3)3-BaF2-SrF2계 유리의 경도변화에서는, 첫째 8번과 14번 조성시편의 경우처럼 BaF2 조성몰비가 60 mol%로 상대적으로 많이 차지하는 경우 경도가 매우 약함을 나타내었다.Next, in the hardness change of Al (PO 3 ) 3 -BaF 2 -SrF 2 glass, the hardness is very high when the molar ratio of BaF 2 composition is 60 mol%, as in the case of the first 8 and 14 specimens. It was weak.
특이한 점은 Al(PO3)3-BaF2-SrF2계 유리에서는 Al(P03)3의 mol%가 증가에도 크게 영향을 받지 않는 것을 확인할 수 있다. In particular, in the Al (PO 3 ) 3 -BaF 2 -SrF 2 type glass, it can be seen that the mol% of Al (P0 3 ) 3 is not significantly affected by the increase.
한편, 20 mol% Al(P03)3로 고정되고 9번에서 13번 조성으로 즉 SrF2 mol%가 40에서 70으로 증가함에 따라 경도는 선형적으로 증가하는데, 이는 Al(PO3)3-BaF2-(Ca, Mg, Sr)F2 불소인산염계 유리경도 변화 동향을 정리하면 BaF2 많은 조성비가 많은 영역에서는 경도가 약하며 BaF2대비 CaF2 ,MgF2 또는 SrF2 조성비가 증가함에 따라 경도는 일반적으로 증가함을 의미하며, 또한 용융온도가 높은 인산염의 증가는 경도의 향상을 가져오는 것으로 사료된다.On the other hand, the hardness increases linearly as 20 mol% Al (P0 3 ) 3 is fixed and the composition from Nos. 9 to 13, ie, SrF 2 mol% increases from 40 to 70, which is Al (PO 3 ) 3 − BaF 2 - (Ca, Mg, Sr)
한편, 도 6a,6b,6c를 참조하면, Al(PO3)3-BaF2-(Mg, Ca, Sr)F2계 유리에 각각 (1, 2) mol% ErF3 첨가함에 따라 Knoop경도의 선형적으로 증가함을 확인할 수 있다. Meanwhile, referring to FIGS. 6A, 6B, and 6C, (1, 2) mol% ErF 3 was added to Al (PO 3 ) 3 -BaF 2- (Mg, Ca, Sr) F 2 glass, respectively, to determine the Knoop hardness. It can be seen that the linear increase.
실질적으로 1 mol% ErF3 농도로 첨가될 경우, 휘발현상에 의한 Er3+ 이온이 유리 결정 내부에 균질하게 분포되지 못하는 점을 감안하더라도 상대적으로 희토류 원소이온(rare earth ion)이 첨가될 경우 Er 이온 주변 리간드(Ligand)와 공유결합성이 증가하여 상대적으로 유리전이온도의 증가와 더불어 경도 향상도 예상된다.When added at substantially 1 mol% ErF 3 concentration, even when rare earth ions are added, Er 3+ ions due to volatilization are not uniformly distributed inside the glass crystal. Covalent bonds with the ligands around the ions increase, so that the glass transition temperature is increased and the hardness is improved.
도 7은 20mol% Al(PO3)3 - (40-x)mol% BaF2 - 40mol% SrF2 - 3mol% ErF3/(y)YbF3 (y=3:ASB3E3Y, 4:ASB3E4Y, 5:ASB3E5Y)계 유리의 이터븀(Yb) 농도에 따른 흡수 스펙트럼을 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.7 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 - 40mol% SrF 2 -
도 7를 참조하면, YbF3가 3mol%에서 5mol%로 증가함에 따라서, 2F7/2→2F5/ 2 전이 강도(intensity)는 계속 증가한다. 4I15 /2→ 4I13 /2의 전이 강도는 YbF3가 증가함에 따라 증가 후 포화된다. 또한, 4I13 /2의 감소된 강도 및 그로부터 여기된 에너지 준위는 상향전환 현상이 나타나고 있음을 나타낸다.Referring to Figure 7, YbF 3 as the increase in 3mol% to 5mol% Thus, 2 F 7/2 → 2 F 5 /2 transition intensity (intensity) is increasing. 4 transition intensity of I 15/2 → 4 I 13 /2 is saturated and then increases as the increase YbF 3. In addition, 4 I 13 / the reduced strength of the second and the energy level from which here indicates that appears and the up-conversion phenomenon.
한편, 진동 강도(oscillation strengths)와 강도 파라미트(intensity parameter), 자연방출 확률(spontaneous emission probabilities), 분기 확륙(branching ratio) 및 발광성 수명(radiative lifetime)를 산출하기 위해, 쥬드 오펠트 이론(Judd-Ofelt Theory)에 도 7의 흡수 스펙트럼을 적용하였다.On the other hand, in order to calculate oscillation strengths and intensity parameters, spontaneous emission probabilities, branching ratios and radiative lifetimes, Jude Opelt (Judd) The absorption spectrum of FIG. 7 was applied to -Ofelt Theory.
도 8은, 20mol% Al(PO3)3 - (40-x)mol% BaF2 - 40mol% SrF2 - 3mol% ErF3/(y)YbF3 (y=3:ASB3E3Y, 4:ASB3E4Y, 5:ASB3E5Y)계 유리의 이터븀(Yb) 농도에 따른 쥬드-오펠트 파라미터의 변화를 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.Figure 8 is, 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 - 40mol% SrF 2 -
도 8을 참조하면, 쥬드-오펠트 분석은, YbF3가 증가함에 따라서, JO 파라미터 Ωλ가 연속적으로 증가하고 있음을 확인할 수 있다. 이것은, YbF3의 증가에 따라서 Er3+ 이온의 평균 대칭은 감소하며, Er-O 결합 사이의 공유원자가(covalency, 共有原子價)는 증가함을 의미한다. 따라서, y=5 일때, 종래의 기술에 비해서, 대략 2.04배 높은 성능 인자를 가지며, 따라서 y=5일 때, 레이저 이득 매체로 사용될 수 있는 가능성이 높다. Referring to FIG. 8, the jude-ofeldt analysis may confirm that the JO parameter Ω λ continuously increases as YbF 3 increases. This means that as the YbF 3 increases, the average symmetry of the
도 9는 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 상향전이 스펙트럼을 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.9 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
도 9을 참조하면, 두 개의 강력한 녹색 방출 피크(peak)가 525nm(2H11 /2 → 4I15 / 2)와 545nm(4S3 /2 → 4I15/2)에서 나타나며, 약한 하나의 적색 방출 피크가 651nm(4F9/2 → 4I15 / 2)에서 나타난다. 즉, YbF3의 농도가 증가함에 따라서, 녹색 방출과 적색 방출 강도(intensity)가 단조 증가하고 있음을 알 수 있다. Referring to Figure 9, appears in two strong green emission peak (peak) is 525nm (2 H 11/2 → 4 I 15/2) and 545nm (4 S 3/2 → 4 I 15/2), one weak the red emission peak appears at 651nm (4 F 9/2 → 4 I 15/2). That is, as the concentration of YbF 3 increases, it can be seen that the green emission and the red emission intensity monotonically increase.
도 10은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 근적외선 방출 스펙트럼을 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.10 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
도 10을 참조하면, 1540nm 파장의 방출현상은 넓은 대역을 갖는 여기된 Er3+이온에 대해 4I15 /2 및 4I13/2 매니폴드 사이에 있는 내부-4f 전환의 특성 대역임을 확인할 수 있다. 즉, YbF3가 1.0mol%에서 3.0mol%로 증가함에 따라서 1540 nm 파장의 방출 강도가 증가하며, YbF3 농도가 3.0mol% 이상으로 증가하면 1540 nm 파장의 방출 강도는 감소한다. Referring to Figure 10, the discharge phenomenon of the wavelength 1540nm is found to be 4 I 15/2 and 4 I 13/2 transition in characteristics of the inside -4f between manifold band for the Er3 + ion here has a wide band. That is, as YbF 3 increases from 1.0 mol% to 3.0 mol%, the emission intensity of 1540 nm wavelength increases, and when the YbF 3 concentration increases to 3.0 mol% or more, the emission intensity of 1540 nm wavelength decreases.
또한, 반치폭(FWHM, full width at half maximum)은 YbF3가 1.0mol%에서 4.0mol%로 증가함에 따라서 67nm에서 78nm로 증가하며, YbF3 농도가 5.0mol%일 경우에 감소한다. 이러한 YbF3 농도가 5.0mol% 일때, 방출강도와 반치폭은, 클러스터 포메이션(cluster formation)에 기인하는 비발광성 프로세스(non-radiative process)에 의하여 감소한다. In addition, the full width at half maximum (FWHM) increases from 67 nm to 78 nm as YbF 3 increases from 1.0 mol% to 4.0 mol%, and decreases when YbF 3 concentration is 5.0 mol%. When this YbF 3 concentration is 5.0 mol%, the emission intensity and half width are reduced by a non-radiative process due to cluster formation.
도 11은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=4 mol%)계 유리의 파장에 따른 4I13/2 → 4I15/2 전이의 흡수(ACS) 및 방출(ECS) 단면적 변화에 대한 실험결과를 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.11 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
도 11을 참조하면, YbF3의 농도에 증가에 따라서, 흡수 단면적과 방출단면적은 감소한다. 그러나, YbF3가 4.0mol%에서는, Yb3 + 에서 Er3 +로의 효과적인 공진 에너지 전환(resonant energy transfer)을 유도할 수 있는, 적절한 Er/Yb 농도 비율 때문에, 흡수단면적 및 방출단면적이 증가한다. Referring to Fig. 11, as the concentration of YbF 3 increases, the absorption cross section and emission cross section decrease. However, YbF 3 is in 4.0mol%, and because the effective resonance energy transition to Er + 3 at the Yb 3 + (resonant energy transfer) the induction, suitable Er / Yb concentration ratio which can increase the absorption and emission cross-sectional area.
도 12는 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=4 mol%)계 유리의 파장과 반전분포비율에 따른 이득상수 변화에 대한 실험결과를 보인 도면이다.12 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
도 12를 참조하면, 반전분포 비율(γ)가 0.4이상일 때, 1540nm에서의 이득 상수가 양의 값을 가질 수 있음을 알 수 있다. 이런 현상은 , 4I13 /2 → 4I15 /2 전이의 레이저 작동을 위해서 낮은 펌프 임계값이 요구됨을 확인할 수 있다. Referring to FIG. 12, it can be seen that when the inversion distribution ratio γ is 0.4 or more, the gain constant at 1540 nm may have a positive value. These effects are, for the laser operation of the 4 I 13/2 → 4 I 15/2 transition can be found a low pump threshold is required.
반전분포 비율(γ)가 0.4이상일 때, 레이저 방출 파장은 단파장으로 이동한다. 더우기, 반전분포 비율(γ)가 0.4일 때 대역폭(bandwidth)는 74nnm 이며, 이는 일반적인 실리케이트(silicated) 어븀도핑 파이버 증폭기(erbium doped fiber amplifier)의 대역폭에 비교하여 매우 넓다.When the inversion distribution ratio γ is 0.4 or more, the laser emission wavelength shifts to a shorter wavelength. Furthermore, when the inversion distribution ratio γ is 0.4, the bandwidth is 74 nnm, which is very wide compared to the bandwidth of a conventional silicate erbium doped fiber amplifier.
반전분포 비율(γ)가 0.4이상일 때, 광통신 윈도우의 C(1530-1565nm)와 L(1565-1625nm) 밴드를 포함하는 1490nm 에서 1620nm 범위에서 평탄 이득 특성을 나타낸다. 따라서, 파장 분할 다중 통신망(wavelength division multiplex networks)에서, 더 많은 채널(channel)을 수용할 수 있다. When the inversion distribution ratio γ is more than 0.4, flat gain characteristics are exhibited in the range of 1490 nm to 1620 nm including the C (1530-1565 nm) and L (1565-1625 nm) bands of the optical communication window. Thus, in wavelength division multiplex networks, more channels can be accommodated.
도 13은 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리의 이터븀(Yb) 농도에 따른 4I13/2 에너지 준위에서의 캐리어 감쇄곡선을 보인 도면이다. 여기서 x는 ErF3와 YbF3의 mol%의 합이다.13 is 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
도 13을 참조하면, YbF3의 농도가 1.0 mol%에서 5.0mol%로 증가할때, 4I13 /2 에너지 준위에서의 캐리어 수명 τexp는 각각 8.73, 11.85, 11.55, 12,37, 그리고 10.47ms로 결정된다. YbF3 농도가 1.0mol%에서 4.0mol%로 증가함에 따라서, τexp는 8.73ms에서 12.37ms로 증가하며, YbF3 농도가 5.0mol%로 증가하면, τexp는10.47ms로 감소한다.13, when the concentration of YbF 3 to increase from 1.0 mol% to 5.0mol%, 4 I 13/2 lifetime of the carrier in the energy level τ exp, respectively 8.73, 11.85, 11.55, 12,37 and 10.47 Determined by ms. YbF 3 As the concentration increases from 1.0 mol% to 4.0 mol%, τ exp increases from 8.73 ms to 12.37 ms and YbF 3 When the concentration increases to 5.0 mol%, τ exp decreases to 10.47 ms.
YbF3 농도가 1.0mol%에서 4.0mol%로 증가함에 따라서, τexp가 증가하는 것은, YbF3의 농도 증가에 따른 에너지 전환을 통한 여기(exitation)와, ErF3에 의한 분산(dispersion)이 증가하기 때문이다. 또한, YbF3 농도가 5.0mol%로 증가함에 따라서 τexp가 감소하는 것은, 클러스터 포메이션에 기인하는 비발광성 손실이 증가하기 때문이다. 따라서, 20mol% Al(PO3)3-(40-x)mol% BaF2-40mol% SrF2-3mol% ErF3/(y)YbF3 (y=1,2,3,4,5 mol%)계 유리에서 y=2 내지 5 일때의 τexp는, 종래의 불소인산염계 유리 및 Al(PO3)3를 기반으로 하는 불소인산염계 유리에 비해, 더 길다. YbF 3 The concentration of the thus increases from 1.0mol% to 4.0mol%, increasing τ exp, YbF because here (exitation) with energy conversion according to the increase in the concentration of 3, a dispersion (dispersion) by ErF 3 Increases to be. In addition, YbF 3 Τ exp decreases as the concentration increases to 5.0 mol% because the non-luminescent loss due to the cluster formation increases. Thus, 20mol% Al (PO 3) 3 - (40-x) mol% BaF 2 -40mol% SrF 2 -
다음으로, 본 실시형태에 따른 능동소자용 불소인산염계 유리의 형광단면적 특성에 대해 설명한다.Next, the fluorescence cross-sectional area characteristics of the fluorophosphate-based glass for active elements according to the present embodiment will be described.
도 14a 내지 도 14c는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%일 때 이터븀(Yb) 농도에 따른 형광단면적 변화에 대한 실험결과를 보인 도면이다.
여기서, 도펀트 ErF3와 YbF3 mol%의 합 만큼 BaF2의 mol% 는 감소된다.14A to 14C show the ytterbium (Yb) concentration when the concentration of the dopant ErF 3 is 3 mol% in
Here, the mol% of BaF 2 is reduced by the sum of the dopants ErF 3 and 3 mol% of YbF.
도 14a를 참조하면, 도 1c의 유리의 삼성분계 조성 8('ABS-8'라 함)의 경우, 3 mol% ErF3/ 5 mol% YbF3에서 형광단면적 4.841x10-21cm2으로 가장 높은 값을 나타내는 것을 확인할 수 있다.14a to FIG. If, in the case of the ternary composition 8 (referred to as 'ABS-8') of the glass of Figure 1c, 3 mol% ErF 3/ 5 mol% YbF 3 in cross-section fluorescence 4.841x10 -21 cm 2 at the highest You can see that it represents a value.
도 14b를 참조하면, 도 1c의 유리의 삼성분계 조성 9('ABS-9'라 함)의 경우, 3 mol% ErF3/ 4 mol% YbF3에서 형광단면적 4.2412x10-21cm2으로 가장 높은 값을 나타내는 것을 확인할 수 있다.Reference to Figure 14b when, in the case of ternary compositions 9 (referred to as 'ABS-9') of the glass of Figure 1c, 3 mol% ErF 3/ 4 mol% YbF 3 in cross-section fluorescence 4.2412x10 -21 cm 2 at the highest You can see that it represents a value.
도 14c를 참조하면, 도 1c의 유리의 삼성분계 조성 10('ABS-10'라 함)의 경우, 3 mol% ErF3/ 3 mol% YbF3에서 형광단면적 4.145x10-21cm2으로 가장 높은 값을 나타내는 것을 확인할 수 있다.See Figure 14c when, in the case of the ternary composition 10 (referred to as 'ABS-10') of the glass of Figure 1c, 3 mol% ErF 3/ 3 mol% YbF 3 in cross-section fluorescence 4.145x10 -21 cm 2 at the highest You can see that it represents a value.
이들 결과를 정리하면, 이는 희토류 원소가 에너지 전이 및 multiphonon relaxation 등과 같은 quenching effect가 상대적으로 적은 비율에 기인한 것으로 사료된다. These results suggest that the rare earth elements are due to the relatively low ratio of quenching effects such as energy transfer and multiphonon relaxation.
또한, 모재 조성변화에 따라 BaF2 대신 SrF2의 함량이 증가시, 즉 sample composition ABS-8에서 ABS-10으로 증가시, 상대적으로 가장 높은 형광단면적은 ErF3:YbF3 의 mol%가 3:3~3:5 비율에서 나타났으며 이는 지금까지 연구된 비율인 1:3보다 상대적으로 매우 낮은 YbF3의 함량에 의해서도 높은 형광단면적을 구현할 수 있게 된다.In addition, as the base material composition change BaF 2 instead SrF upon the amount of 2 is increased, i.e. sample by increasing the ABS-10 in the composition ABS-8, relative to the highest fluorescence cross-sectional area is ErF 3: mol% of YbF 3 is 3: The 3 ~ 3: 5 ratio is shown, which makes it possible to realize a high fluorescence cross-section by the YbF 3 content, which is much lower than the ratio of 1: 3.
도 15a는 Er/Yb 시스템에서 광자의 흡수 및 하향전이에 따른 광자 방출현상을 설명하는 에너지 준위(energy level) 도면이고, 도 15b는 Er/Yb 시스템에서 광자의 흡수 및 상향전이에 따른 광자 방출현상을 설명하는 에너지 준위(energy level) 도면이다.15A is an energy level diagram illustrating photon emission due to absorption and downward transition of photons in an Er / Yb system, and FIG. 15B is photon emission phenomenon due to absorption and upward transition of photons in an Er / Yb system. Is an energy level diagram.
우선, 도 15a를 참조하여, 하향전이(downconversion)을 설명하면, Er/Yb가 함께 도핑(co-doping)되면 3개의 에너지 준위를 통해 동작(three level laser)함을 확인할 수 있다. First, referring to FIG. 15A, when downconversion is described, it can be seen that when Er / Yb is doped together, three level lasers operate.
이때 이터븀(Yb)의 2F7/2 2F5/2 전이(transition)와 어븀(Er)의 4I15 / 2 4I11 /2 전이(transition) 상호 간에 에너지 전이현상이 발생하며, 어븀(Er)의 4I11 / 2 4I13 / 2 로의 비발광성 전이 현상이 복합적으로 나타남으로써, 4I13/2에서의 캐리어 수명에 영향을 미치고 있음을 알 수 있다. At this time, and the energy transfer phenomenon occurs between the
이터븀(Yb)의 농도가 증가하는 상황에서는 이터븀(Yb)의 2F7/2 2F5/2 전이(transition)와 어븀(Er)의 4I15/2 4I11/2전이(transition)가 중첩(overlap)되어 이터븀(Yb)으로부터 어븀(Er)으로의 에너지 전달(energy transfer) 현상이 증가하게 되며, 앞서 설명한 바와 같이 이터븀(Yb) 이온이 어븀(Er) 이온의 비 발광성 프로세스를 감소시키는 효과가 커지기 때문에, 4I13/2에너지 준위에서의 캐리어 수명이 늘어나게 된다.In a situation where the concentration of ytterbium (Yb) increases, the 2 F 7/2 2 F 5/2 transition of ytterbium (Yb) and the 4 I 15/2 4 I 11/2 transition of erbium (Er) ( As the transition overlaps, the energy transfer phenomenon from ytterbium (Yb) to erbium (Er) increases. As described above, the ytterbium (Yb) ion is a ratio of the erbium (Er) ion. Since the effect of reducing the luminescent process is increased, the carrier life at the 4 I 13/2 energy level is increased.
다음으로 상향전이(upconversion)을 설명한다. Next, upconversion is described.
상향전이(upconversion)는 매우 제한된 상황에서 발생하고 자연계에서는 거의 관찰되지 않는다, Upconversion occurs in very limited situations and is rarely observed in nature.
상향전이 현상은 단일 광자에 의해서가 아니라 2개 이상의 광자에 의해서, 광자 하나의 에너지보다 더 높은 에너지 준위로 여기되는 현상이다. 이를 안티-스톡스 방출(anti-Stokes-emission)이라고도 한다. Upward transitions are excited by two or more photons, not by a single photon, at higher energy levels than a single photon. This is also known as anti-Stokes-emission.
상향전이 현상은, 1차로 광자를 전자가 흡수하여 높은 에어지 준위로 여기된 후, 기저상태로 떨어지기 전에 다시 또 다른 광자를 흡수해야한다. 따라서 일차적인 광자 흡수에 의해 여기된 전자는, 이차적으로 광자를 흡수하기 전까지, 1차로 여기된 에너지 준위에서 존재하여야 한다.The upward transition phenomenon involves first absorbing photons by electrons, exciting them to a high air level, and then again absorbing another photon before falling to the ground state. Therefore, the electrons excited by primary photon absorption must exist at the primary excited energy level until the secondary photons are absorbed.
도 15b를 참조하면, 상술한 바와 같이 4I15 /2→4I11 /2 에너지 전이(energy transition)되어 4I11 /2 에 여기된 캐리어중 일부는, 비발광성 재결합으로 4I13/2로 이동한후 발광성 재결합으로 4I15/2로 이동하게 된다. Referring to Figure 15b, some of the 4 I 15/2 → 4 I 11/2 energy transfer (energy transition) is a carrier where the 4 I 11/2 as described above, a non-luminescent recombination 4 I 13/2 After migrating to 4 I 15/2 by luminescent recombination.
이때, 4I11 /2에 잔류하고 있는 또 다른 캐리어는, 또 다른 4I15 /2→4I11 /2 에너지 전이(energy transfer)에 의해서, 4F7/2 또는 4F9/2로 여기되는 여기상태 흡수(exited-state absorption)현상이 나타남으로써 상향전이된다. At this time, another carrier remaining in 4 I 11/2 is, in another 4 I 15/2 → 4 I 11/2 energy transfer, 4 F 7/2 or 4 F 9/2 by (energy transfer) It is up-converted by the appearance of excited-state absorption.
4F7/2 또는 4F9/2로 상향전이된 캐리어들은, 비발광성 재결합하여 2H11 /2, 4S3 / 2,및 4F9/2로 떨어지게 된다. 2H11 /2, 4S3 / 2,및 4F9/2로 떨어진 캐리더들은 다시 4I15 /2로 떨어지면서 발광성 재결합하여, 523nm 와 545nm의 광자(photon)와 651nm 광자를 방출한다. 4 F 7/2 to 4 F 9/2 or a transition-up carriers, and non-luminescent recombination will drop to 2 H 11/2, 4 S 3/2, and 4 F 9/2. 11 H 2/2, 4 S 3/2, and carry away more to the 4 F 9/2 4 I are back to fall to 15/2 luminance recombined to emit photon (photon) and 651nm photons of 523nm and 545nm .
도 16은 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%, YbF3의 농도가 5 mol% 일 때, 저온 상향전이 방출 스펙트럼을 설명하는 도면이다.When 16 is in Fig. 1c Al (PO 3) 3 -BaF 2 is -SrF 2 concentration of the sample composition based dopant ErF 3 from 8, 9, 10, one of the
도 16을 참조하면, 온도가 증가함에 따라 비발광성 감쇄 비율이 증가하므로, 측정된 전체 파장영역에서 발광강도(luminescence intensity)는 낮아진다. 그러나, 521nm(2H11 /2 → 4I15 /2) 대역의 강도는 증가한다. 이러한 현상은, 4S3 / 2준위로 부터 2H11 / 2준위로 캐리어가 열적 여기됨으로써, YbF3비율이 농도가 증가하기 때문이다.Referring to FIG. 16, since the non-luminescence attenuation ratio increases with increasing temperature, luminescence intensity is lowered in the entire measured wavelength range. However, 521nm and (2 H 11/2 → 4 I 15/2) to increase the strength of the band. This phenomenon, due 4 S 3/2 being 2 H carrier is thermally excited by 11/2 level from the level, to the YbF 3 ratio increases the concentration.
따라서, Al(PO3)3-(1-x)BaF2-SrF2-(0.03)ErF3/(x)YbF3계 유리의 열적 결합 준위(thermally coupled levels)에 대한 온도의 영향을, 불소화 온도 감지 방법으로 분석할 수 있음을 나타낸다.Thus, the influence of temperature on the thermally coupled levels of Al (PO 3 ) 3- (1-x) BaF 2 -SrF 2- (0.03) ErF 3 / (x) YbF 3 -based glass, It can be analyzed by the temperature sensing method.
도 17a는 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%, YbF3의 농도가 5 mol% 일 때, 녹색 방출(green emissions)의 불소화 강도비율(FIR)의 온도에 따른 변화를 나타내는 도면이고, 도 17b는 감도(sensitivity, S)의 온도에 따른 변화를 설명하는 도면이다.Figure 17a is the Figure 1c Al (PO 3) 3 -BaF 2 -
여기서, 감도(Sensitivity, S)는, 불소화 강도 비율(Fluorescence intensity ratio, FIR, 이하 R)의 시간에 따른 변화율이다. Here, Sensitivity (S) is the rate of change over time of Fluorescence Intensity Ratio (FIR, hereinafter R).
도 17a를 참조하면, 본 실시형태에 따른 능동소자용 불소인산염계 유리는 극저온(예: 100K 이하)에서도, 온도에 따라 불소화 강도비율(FIR)의 변화 정도가 분해 가능하게 나타나고 있음을 확인할 수 있다. Referring to FIG. 17A, it can be seen that the fluorinated phosphate-based glass for active elements according to the present embodiment exhibits a degradable degree of change in fluorinated strength ratio (FIR) depending on temperature even at cryogenic temperatures (eg, 100 K or less). .
이에 의해, 도 17b에서 확인되는 바와 같이 극저온에서 민감도(S)가 높게 나타난다.As a result, as shown in FIG. 17B, the sensitivity S is high at cryogenic temperatures.
표 1에, 도 17a 내지 도 17b를 기반으로 하여 산출된 S 및 최대 감지감도(Maximum sensor sensitivity, Tmax)를 나타내었다. In Table 1, S and the maximum sensor sensitivity (Tmax) calculated based on FIGS. 17A to 17B are shown.
표 1을 참조하면, 본 실시형태에 따른 불소인산염계 유리(특히, 도 1c의 Al(PO3)3-BaF2-SrF2계 유리의 sample composition 8,9,10번에서 도펀트 ErF3의 농도가 3 mol%, YbF3의 농도가 5 mol% 인 유리)는 S가 22.4×10-4 이고, Tmax는 123K 이다. Referring to Table 1, the concentration of the dopant ErF 3 in the sample composition Nos. 8, 9 and 10 of the fluorophosphate-based glass (particularly, Al (PO 3 ) 3 -BaF 2 -SrF 2 based glass of FIG. 1C) Is 3 mol%, glass having a concentration of YbF 3 is 5 mol%), S is 22.4 × 10 −4 , and T max is 123 K.
따라서, 본 실시형태에 따른 불소인산염계 유리는 다른 어떠한 유리모재에도 확인되지 않는 극저온(123K)에서 높은 민감도(S)를 보이고 있음을 확인할 수 있다. Therefore, it can be seen that the fluorophosphate-based glass according to the present embodiment shows high sensitivity (S) at cryogenic temperatures (123K), which are not found in any other glass base material.
Claims (11)
BaF2 및 SrF2를 포함하는 불소(fluoride) 조성물; 및
ErF3 및 YbF3로 마련되는 도펀트(dopant);를 포함하되,
상기 Al(PO3)3는 20mol%이며,
상기 BaF2는 (40-x)mol% 내지 (60-x)mol% 이며,
상기 SrF2는 20mol% 내지 40mol% 이고,
상기 x는 상기 ErF3와 상기 YbF3의 mol%를 합한 값으로 조성되는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.Metaphosphate compositions comprising Al (PO 3 ) 3 ;
Fluoride compositions comprising BaF 2 and SrF 2 ; And
Dopant provided with ErF 3 and YbF 3 ; Including,
Al (PO 3 ) 3 is 20 mol%,
BaF 2 is (40-x) mol% to (60-x) mol%,
SrF 2 is 20 mol% to 40 mol%,
X is a fluorine phosphate-based glass for an active element having enhanced down and up-conversion emission characteristics, which are formed by adding mol% of the ErF 3 and the YbF 3 .
상기 YbF3는 3mol% 내지 5mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 1,
YbF 3 is 3 mol% to 5 mol%, characterized in that the fluorine phosphate-based glass for the active element having enhanced down and up-conversion release characteristics.
상기 ErF3는 3mol%이며, 상기 YbF3는 3mol% 내지 5mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 2,
Wherein said ErF 3 is 3 mol% and said YbF 3 is 3 mol% to 5 mol%.
상기 Al(PO3)3는 20mol%이며,
상기 BaF2는 (60-x)mol%이며,
상기 SrF2는 20mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 1,
Al (PO 3 ) 3 is 20 mol%,
BaF 2 is (60-x) mol%,
SrF 2 is 20 mol% characterized in that the fluorine phosphate-based glass for the active element having enhanced down- and up-conversion emission characteristics.
상기 ErF3는 3mol%이며, 상기 YbF3는 3mol% 내지 5mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 7, wherein
Wherein said ErF 3 is 3 mol% and said YbF 3 is 3 mol% to 5 mol%.
상기 Al(PO3)3는 20mol%이며,
상기 BaF2는 (50-x)mol%이며,
상기 SrF2는 30mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 1,
Al (PO 3 ) 3 is 20 mol%,
BaF 2 is (50-x) mol%,
SrF 2 is 30 mol%, characterized in that the fluorine phosphate-based glass for the active element having enhanced down- and up-conversion emission characteristics.
상기 ErF3는 3mol%이며, 상기 YbF3는 3mol% 내지 5mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 9,
Wherein said ErF 3 is 3 mol% and said YbF 3 is 3 mol% to 5 mol%.
상기 Al(PO3)3는 20mol%이며,
상기 BaF2는 (40-x)mol%이며,
상기 SrF2는 40mol%인 것을 특징으로 하는 강화된 하향 및 상향전환 방출 특성을 갖는 능동소자용 불소인산염계 유리.The method of claim 1,
Al (PO 3 ) 3 is 20 mol%,
BaF 2 is (40-x) mol%,
SrF 2 is 40 mol%, characterized in that the fluorine phosphate-based glass for the active element having enhanced down- and up-conversion emission characteristics.