KR102042225B1 - Waterproof double-sided adhesive tape having improved fracture resistant - Google Patents
Waterproof double-sided adhesive tape having improved fracture resistant Download PDFInfo
- Publication number
- KR102042225B1 KR102042225B1 KR1020180053550A KR20180053550A KR102042225B1 KR 102042225 B1 KR102042225 B1 KR 102042225B1 KR 1020180053550 A KR1020180053550 A KR 1020180053550A KR 20180053550 A KR20180053550 A KR 20180053550A KR 102042225 B1 KR102042225 B1 KR 102042225B1
- Authority
- KR
- South Korea
- Prior art keywords
- sided tape
- buffer layer
- double
- storage modulus
- waterproof double
- Prior art date
Abstract
Description
개시된 내용은 내파괴성이 우수한 방수 양면테이프에 관한 것으로, 더욱 상세하게는 방수성능이 우수할 뿐만 아니라, 저장탄성률이 우수한 수지가 함유된 완충층과 점착층이 형성되어, 우수한 내파괴성을 나타내는 내파괴성이 우수한 방수 양면테이프에 관한 것이다.
The present disclosure relates to a waterproof double-sided tape having excellent fracture resistance, and more particularly, a buffer layer and a pressure-sensitive adhesive layer containing a resin having excellent waterproof modulus and excellent storage modulus are formed, and thus have excellent fracture resistance. An excellent waterproof double sided tape.
화상 표시 장치 또는 입력 장치를 탑재한 전자 기기에는 조립을 위해 양면 점착 테이프가 주로 사용되고 있는데, 구체적으로는, 전자 기기의 표면을 보호하기 위한 커버 패널을 터치 패널 모듈 또는 디스플레이 패널 모듈에 접착하거나, 터치 패널 모듈과 디스플레이 패널 모듈을 접착하기 위해 양면 점착 테이프가 사용되고 있다.Double-sided adhesive tape is mainly used for assembling electronic devices equipped with an image display device or an input device. Specifically, a cover panel for protecting the surface of the electronic device is attached to the touch panel module or the display panel module, or touched. Double-sided adhesive tape is used to bond the panel module and the display panel module.
종래에 양면 점착 테이프는, 액자상 등의 형상으로 타발되고, 표시 화면의 주변에 배치되도록 하여 사용되는데, 최근에는 전자 기기의 소형화, 표시 화면의 대화면화에 따라 개구부 면적이 증대되고 있고, 그것에 의해 표시 화면주변의 접합 고정 부분이 협폭화되고 있다. 이 때문에, 점착 테이프는 해마다 점착면적이 줄어들고 있고, 점착면적이 좁아짐에 따라 더욱 우수한 점착성능이 요구되고 있다.Conventionally, a double-sided adhesive tape is punched into a shape of a picture frame or the like and used to be disposed around the display screen. In recent years, the opening area has been increased due to the miniaturization of electronic devices and the large screen of the display screen. The joint fixing part around the display screen is narrowing. For this reason, the adhesive area of adhesive tape is decreasing year by year, and as adhesive area becomes narrow, further excellent adhesive performance is calculated | required.
또한, 최근에는 스마트폰이나 디지털카메라와 같은 휴대용 전자기기의 두께가 점차 얇아짐에 따라 양면 점착 테이프의 두께가 박막화되고 있으며, 점착성능 외에도 휴대용 전자기기의 방수성능에 대한 소비자의 요구가 증가함에 따라 시장에서의 경쟁 우위성을 확보하기 위해 방수성능이 부여된 양면테이프에 대한 개발이 이루어지고 있다.In addition, recently, as the thickness of portable electronic devices such as smartphones and digital cameras is becoming thinner, the thickness of double-sided adhesive tapes is becoming thinner, and in addition to adhesive performance, as consumer demand for waterproof performance of portable electronic devices increases, In order to secure a competitive advantage in the market, the development of double-sided tape with waterproof performance is being made.
그러나, 종래에 개발된 양면 점착 테이프의 경우에는 평소에는 양면 점착 테이프에 형성된 점착층의 방수성능이 유지되지만, 외부로부터 충격이 가해질 경우, 점착층에 균열이 발생하여 방수성능이 손실되는 문제점이 있었다.
However, in the case of the conventionally developed double-sided adhesive tape, the waterproof performance of the adhesive layer formed on the double-sided adhesive tape is usually maintained, but when an impact is applied from the outside, there is a problem in that the adhesive layer is cracked and the waterproof performance is lost. .
개시된 내용은 방수성능이 우수할 뿐만 아니라, 저장탄성률이 우수한 수지가 함유된 완충층과 점착층이 형성되어, 우수한 내파괴성을 나타내는 방수 양면테이프를 제공하는 것이다.
Disclosed is to provide a waterproof double-sided tape showing excellent fracture resistance by forming a buffer layer and a pressure-sensitive adhesive layer containing a resin having excellent waterproof performance and excellent storage modulus.
하나의 일 실시예로서 이 개시의 내용은 기재층, 상기 기재층의 일면에 형성되며, 저장탄성률이 40000 내지 90000Pa인 수지가 함유되는 완충층 및 상기 완충층이 형성된 상기 기재층의 상부면 및 하부면에 형성되는 점착층으로 이루어지는 것을 특징으로 하는 내파괴성이 우수한 방수 양면테이프에 대해 기술하고 있다.As an example, the contents of the present disclosure are formed on a base layer, one surface of the base layer, a buffer layer containing a resin having a storage modulus of 40000 to 90000 Pa, and a top surface and a bottom surface of the base layer on which the buffer layer is formed. It describes the waterproof double-sided tape excellent in fracture resistance, characterized in that the adhesive layer formed.
바람직하기로는, 상기 기재층은 25 내지 100 마이크로미터 두께의 폴리에틸렌테레프탈레이트로 이루어질 수 있다.Preferably, the substrate layer may be made of polyethylene terephthalate having a thickness of 25 to 100 micrometers.
더 바람직하기로는, 상기 완충층은 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부, 충전제 0.1 내지 10 중량부 및 경화제 0.1 내지 10 중량부로 이루어질 수 있다.More preferably, the buffer layer may be composed of 100 parts by weight of an acrylic resin or urethane resin having a storage modulus of 40000 to 90000 Pa, 0.1 to 10 parts by weight of a filler, and 0.1 to 10 parts by weight of a curing agent.
더욱 바람직하기로는, 상기 충전제는 0.001 내지 50 마이크로미터의 입자크기를 나타내며, 폴리메틸메타아크릴레이트, 탄화수소, 탄산칼슘 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어질 수 있다.More preferably, the filler has a particle size of 0.001 to 50 micrometers, and may be made of one selected from the group consisting of polymethylmethacrylate, hydrocarbons, calcium carbonate and silica.
더욱 더 바람직하기로는, 상기 완충층은 10 내지 200 마이크로미터의 두께로 형성될 수 있다.Even more preferably, the buffer layer may be formed to a thickness of 10 to 200 micrometers.
더욱 더 바람직하기로는, 상기 점착층은 10 내지 200 마이크로미터의 두께로 형성되며, 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부 및 경화제 0.1 내지 10 중량부로 이루어질 수 있다.
Even more preferably, the pressure-sensitive adhesive layer is formed to a thickness of 10 to 200 micrometers, it may be composed of 100 parts by weight of acrylic resin or urethane resin having a storage modulus of 40000 to 90000 Pa and 0.1 to 10 parts by weight of a curing agent.
이상에서와 같은 내파괴성이 우수한 방수 양면테이프는 방수성능이 우수할 뿐만 아니라, 저장탄성률이 우수한 수지가 함유된 완충층과 점착층이 형성되어, 우수한 내파괴성을 나타내는 양면테이프를 제공하는 탁월한 효과를 나타낸다.
As described above, the waterproof double-coated tape having excellent fracture resistance not only has excellent waterproofing performance but also has a buffer layer and an adhesive layer containing a resin having excellent storage modulus, thereby providing an excellent double-sided tape showing excellent fracture resistance. .
도 1은 개시된 일 실시예에 따른 내파괴성이 우수한 방수 양면테이프를 나타낸 분해사시도이다.1 is an exploded perspective view showing a waterproof double-sided tape having excellent fracture resistance according to one embodiment disclosed.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
In the following, preferred embodiments of the present invention and the physical properties of each component will be described in detail, which is intended to explain in detail enough to be able to easily carry out the invention by one of ordinary skill in the art, This does not mean that the technical spirit and scope of the present invention is limited.
개시된 내파괴성이 우수한 방수 양면테이프는 기재층(10), 상기 기재층(10)의 일면에 형성되며, 저장탄성률이 40000 내지 90000Pa인 수지가 함유되는 완충층(20) 및 상기 완충층(20)이 형성된 상기 기재층(10)의 상부면 및 하부면에 형성되는 점착층(30)으로 이루어진다.
The disclosed waterproof double-coated tape having excellent fracture resistance is formed on the
상기 기재층(10)은 개시된 내파괴성이 우수한 방수 양면테이프의 기재가 되는 층으로, 25 내지 100 마이크로미터 두께의 폴리에틸렌테레프탈레이트로 이루어지는데, 외력에 의해 개시된 방수 양면테이프가 변형되지 않고 일정한 형태를 유지할 수 있도록 하는 역할을 한다.The
상기 기재층(10)의 두께가 25 마이크로미터 미만이면 외력에 의해 개시된 방수 양면테이프가 쉽게 변형되거나 파손될 수 있고, 상기 기재층(10)의 두께가 100 마이크로미터를 초과하게 되면 상기의 효과는 크게 향상되지 않으면서 양면테이프의 두께가 지나치게 증가하여 소형화 및 박막화되고 있는 전자제품에 적용이 곤란해진다.
When the thickness of the
상기 완충층(20)은 상기 기재층(10)의 일면에 10 내지 200 마이크로미터의 두께로 형성되며, 저장탄성률이 40000 내지 90000Pa인 수지가 함유되는데, 상기 수지는 아크릴 또는 우레탄이 사용될 수 있고, 더욱 상세하게는 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부, 충전제 0.1 내지 10 중량부 및 경화제 0.1 내지 10 중량부로 이루어진다.The
상기의 두께 및 성분으로 이루어지는 완충층(20)이 형성된 양면테이프는 저장탄성율이 우수한 수지가 적용되어 우수한 내파괴성을 나타내는데, 상기 완충층(20)의 두께가 10 마이크로미터 미만이면 상기의 효과가 미미하며, 상기 완충층(20)의 두께가 200 마이크로미터를 초과하게 되면 상기의 효과는 크게 향상되지 않으면서 양면테이프의 두께가 지나치게 증가하여 바람직하지 못하다.The double-sided tape on which the
또한, 상기 완충층(20)을 구성하는 아크릴 수지 또는 우레탄 수지의 저장탄성률이 40000Pa 미만이면 완충층(20)으로 인해 발생하는 내파괴성 향상효과가 미미하다.In addition, when the storage modulus of the acrylic resin or the urethane resin constituting the
이때, 상기 완충층(20)에 사용되는 충전제는 완충층의 기계적 물성을 향상시키는 역할을 하는데, 아크릴 수지나 우레탄 수지에 적용할 수 있는 것이면, 특별히 한정되지 않고 어떠한 것이든 사용가능하나, 상기 충전제는 0.001 내지 50 마이크로미터의 입자크기를 나타내며, 폴리메틸메타아크릴레이트, 탄화수소, 탄산칼슘 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어지는 것이 바람직하다.At this time, the filler used in the
이때, 상기 충전제로 폴리메틸메타아크릴레이트나 탄산칼슘을 사용하는 경우에는 입자크기가 1 내지 50 마이크로미터인 것을 사용하는 것이 바람직하며, 상기 충전제로 실리카를 사용하는 경우에는 0.001 내지 50 마이크로미터의 입자크기를 나타내는 것을 사용하는 것이 바람직하다.In this case, when polymethyl methacrylate or calcium carbonate is used as the filler, it is preferable to use a particle size of 1 to 50 micrometers, and when silica is used as the filler, particles of 0.001 to 50 micrometers are used. It is preferable to use what indicates the size.
또한, 상기 경화제는 이소시아네이트, 에폭시 및 킬레이트로 이루어진 그룹에서 선택된 하나로 이루어지는 것이 바람직하다.
In addition, the curing agent is preferably made of one selected from the group consisting of isocyanate, epoxy and chelate.
상기 점착층(30)은 상기 완충층(20)이 형성된 상기 기재층(10)의 상부면 및 하부면에 10 내지 200 마이크로미터의 두께로 형성되며, 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부에 경화제 0.1 내지 10 중량부를 혼합하여 이루어지는데, 개시된 양면테이프에 점착성능을 부여할 뿐만 아니라, 저장탄성률이 우수한 아크릴 수지나 우레탄 수지가 사용되어 외력에 의해 점착층이 쉽게 손상되지 않기 때문에, 점착 대상으로부터 양면테이프가 쉽게 분리되지 않도록 하는 역할을 한다.The
상기 점착층(30)의 두께가 40 마이크로미터 미만이면 점착층(30)의 점착력이나 내파괴성이 저하되며, 상가 점착층(30)의 두께가 60 마이크로미터를 초과하게 되면 상기의 효과는 크게 향상되지 않으면서 양면테이프의 두께가 지나치게 두터워져 바람직하지 못하다.When the thickness of the
이때, 상기 점착층(30)을 구성하는 아크릴 수지 또는 우레탄 수지의 저장탄성계수는 상기 완충층(20)에 적용된 아크릴 수지 또는 우레탄 수지의 저장탄성계수보다 작거나 같은 것이 바람직한데, 점착층(30)을 구성하는 아크릴 수지 또는 우레탄 수지의 저장탄성계수가 상기 완충층(20)에 적용된 아크릴 수지 또는 우레탄 수지의 저장탄성계수보다 큰 경우에는 양면테이프의 내파괴성이 저하된다.At this time, the storage modulus of the acrylic resin or urethane resin constituting the
이때, 점착층에 사용되는 경화제는 이소시아네이트, 에폭시 및 킬레이트로 이루어진 그룹에서 선택된 하나로 이루어지는 것이 바람직하다.
At this time, the curing agent used in the pressure-sensitive adhesive layer is preferably made of one selected from the group consisting of isocyanate, epoxy and chelate.
또한, 상기 완충층(20)이나 상기 점착층(30)에 사용되는 아크릴 수지나, 우레탄 수지는 아래 표 1에 나타낸 비율을 통해 원하는 저장탄성률을 갖도록 제조할 수 있다.In addition, the acrylic resin or urethane resin used in the
<표 1>TABLE 1
위에 표 1에 나타낸 것처럼, 아크릴 수지나 우레탄 수지의 저장탄성률은 모노머의 혼합비율과 분자량의 조절을 통해 다양하게 도출할 수 있다.
As shown in Table 1 above, the storage modulus of the acrylic resin or urethane resin can be derived variously by controlling the mixing ratio and molecular weight of the monomer.
이하에서는, 개시된 내파괴성이 우수한 방수 양면테이프의 제조방법 및 그 제조방법을 통해 제조된 양면테이프의 물성을 실시예를 들어 설명하기로 한다.
Hereinafter, the physical properties of the double-sided tape manufactured by the method of manufacturing a waterproof double-sided tape having excellent fracture resistance and the manufacturing method will be described with reference to Examples.
<실시예 1><Example 1>
50 마이크로미터 두께의 폴리에틸렌테레프탈레이트 필름으로 기재층을 형성하고, 상기 기재층의 상부면에 저장탄성률이 40000Pa(TA Instruments사, 모델명 AR2000 레오미터, 조건 1 rad/s)인 아크릴수지 100 중량부, 충전제(30 마이크로미터의 입자크기를 갖는 폴리메틸메타크릴레이트) 5 중량부, 경화제(이소시아네이트) 2 중량부 및 용매(메틸에틸케톤) 100 중량부로 이루어진 혼합물을 콤마코팅 기를 이용하여 50 마이크로미터 두께로 코팅하여 완충층을 형성하고, 상기 완충층이 형성된 상기 기재층의 상부면 및 하부면에 저장탄성률이 40,000Pa인 아크릴수지 100 중량부, 경화제(이소시아네이트) 2 중량부 및 용매(메틸에틸케톤) 100 중량부로 이루어진 혼합물 콤마코팅기를 이용하여 50 마이크로미터의 두께로 코팅하여 방수 양면테이프를 제조하였다.
A substrate layer is formed of a polyethylene terephthalate film having a thickness of 50 micrometers, 100 parts by weight of an acrylic resin having a storage modulus of 40000 Pa (TA Instruments, model AR2000 rheometer, condition 1 rad / s) on an upper surface of the substrate layer, A mixture of 5 parts by weight of a filler (polymethylmethacrylate having a particle size of 30 micrometers), 2 parts by weight of a curing agent (isocyanate) and 100 parts by weight of a solvent (methylethylketone) to a thickness of 50 micrometers using a comma coating machine Coating to form a buffer layer, 100 parts by weight of an acrylic resin having a storage modulus of 40,000 Pa, 2 parts by weight of a curing agent (isocyanate) and 100 parts by weight of a solvent (methyl ethyl ketone) on the upper and lower surfaces of the base layer on which the buffer layer is formed. It was coated to a thickness of 50 micrometers using a mixture comma coater made of a waterproof double-sided tape.
<실시예 2><Example 2>
상기 실시예 1과 동일하게 진행하되, 저장탄성률 60000Pa인 아크릴 수지를 완충층과 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, by applying an acrylic resin having a storage modulus of 60000 Pa to the buffer layer and the adhesive layer to prepare a waterproof double-sided tape.
<실시예 3><Example 3>
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 90000Pa인 아크릴 수지를 완충층과 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 90000 Pa was applied to the buffer layer and the adhesive layer to prepare a waterproof double-sided tape.
<실시예 4><Example 4>
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 60000Pa인 아크릴 수지를 사용하여 완충층에 적용하고, 저장탄성률이 40000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, using an acrylic resin having a storage modulus of 60000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 40000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<실시예 5>Example 5
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 90000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 40000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 90000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 40000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<실시예 6><Example 6>
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 90000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 60000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 90000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 60000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<실시예 7><Example 7>
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 50000Pa인 우레탄 수지를 완충층에 적용하고, 저장탄성률이 40000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, a urethane resin having a storage modulus of 50000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 40000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<비교예 1>Comparative Example 1
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 30000Pa인 아크릴 수지를 완충층과 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 30000 Pa was applied to the buffer layer and the adhesive layer to prepare a waterproof double-sided tape.
<비교예 2>Comparative Example 2
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 40000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 60000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 40000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 60000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<비교예 3>Comparative Example 3
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 40000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 90000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 40000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 90000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<비교예 4><Comparative Example 4>
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 60000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 90000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 60000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 90000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<비교예 5>Comparative Example 5
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 30000Pa인 아크릴 수지를 완충층에 적용하고, 저장탄성률이 40000Pa인 아크릴 수지를 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, an acrylic resin having a storage modulus of 30000 Pa was applied to the buffer layer, and an acrylic resin having a storage modulus of 40000 Pa was applied to the adhesive layer to prepare a waterproof double-sided tape.
<비교예 6>Comparative Example 6
상기 실시예 1과 동일하게 진행하되, 저장탄성률이 50000Pa인 우레탄 수지를 완충층에 적용하고, 저장탄성률이 90000Pa인 아크릴 수지 점착층에 적용하여 방수 양면테이프를 제조하였다.
Proceed in the same manner as in Example 1, applying a urethane resin having a storage modulus of 50000 Pa to the buffer layer, and applied to an acrylic resin adhesive layer having a storage modulus of 90000 Pa to prepare a waterproof double-sided tape.
상기 실시예 1 내지 7 및 상기 비교예 1 내지 6을 통해 제조된 방수 양면테이프의 내파괴성 및 방수성을 측정하여 아래 표 2에 나타내었다.Destructive resistance and waterproofness of the waterproof double-sided tape prepared through Examples 1 to 7 and Comparative Examples 1 to 6 were measured and shown in Table 2 below.
{단, 내파괴성은 압출하중평가와 낙하분리평가를 통해 측정하였다.{However, fracture resistance was measured by extrusion load evaluation and drop separation evaluation.
압출하중평가 - 방수 양면테이프를 가로 15.5mm × 세로 15.5mm로 자른 후 내부를 가로 14.8mm × 세로 14.8mm 잘라내어 살폭이 0.7mm인 사각틀 모양의 샘플을 준비한 후에, 가운데 10φ 크기로 구멍이 있는 가로 50mm × 세로 50mm × 두께 3.5mm 마그네슘(Mg) 플레이트와 동일 크기의 폴리카보네이트(PC) 플레이트 위에 테이프 샘플을 부착시킨 후 그 위에 가로 20mm × 세로 20mm × 두께 2.8mm 유리 플레이트를 부착시켰다. 그 후에 준비된 샘플을 24℃에서 30분 방치시킨 후 만능 인장 시험기를 사용해서 10φ 구멍에 뽀쪽한 팁으로 누르면서 유리 플레이트와 마그네슘 플레이트(또는 폴리카보네이트 플레이트)가 분리될 때의 하중 값(kgf)을 획득 했다. 이렇게 획득된 값은 양면 테이프가 외부로 부터의 주어진 힘을 견디는 정도(저항성)를 나타내며 값이 높을 수록 내파괴성이 우수한 것을 의미한다.Extrusion Load Evaluation-After cutting the waterproof double-sided tape into 15.5mm × 15.5mm, cut the inside 14.8mm × 14.8mm and cut a square frame sample with 0.7mm flesh. A tape sample was attached onto a polycarbonate (PC) plate of the same size as a 50 mm long 3.5 mm magnesium (Mg) plate, and then a 20 mm wide 20 mm long 2.8 mm thick glass plate was attached thereto. Thereafter, the prepared sample was allowed to stand at 24 ° C. for 30 minutes, and then obtained a load value (kgf) when the glass plate and the magnesium plate (or polycarbonate plate) were separated while pressing with a pointed tip in a 10φ hole using a universal tensile tester. did. The value thus obtained indicates the degree (resistance) of the double-sided tape to withstand a given force from the outside, and the higher the value, the better the fracture resistance.
낙하분리평가 - 방수 양면테이프를 가로 48mm × 세로 48mm 로 자른 후 가로 내부를 47.3mm × 세로 47.3mm 잘라내어 살폭이 0.7mm인 사각틀 모양의 샘플을 준비한 후에 가로 60mm × 세로 60mm × 두께 6.5mm 알루미늄(Al) 플레이트 위에 샘플을 부착시키고, 가로 50mm × 세로 50mm × 두께 2.8mm 유리 플레이트를 부착시켰다. 준비된 샘플을 24℃에서 30분 방치 후 1.5m 자유 낙하시키되, 알루미늄 플레이트와 유리플레이트가 분리될 때까지 반복 낙하시켰다. 알루미늄 플레이트와 유리플레이트가 분리될 때의 횟수와 분리면에서의 점착제가 남은 정도를 확인하여 점착제 잔사를 구했으며, 알루미늄 플레이트 또는 유리 플레이트에서 방수 양면테이프의 점착층을 구성하는 점착제 성분이 한쪽면에만 존재할 경우 잔사를 0%로 표기하였고 테이프가 파괴되어 알루미늄 플레이트와 유리 플레이트 양면에 점착제가 동일하게 존재하는 경우에는 잔사를 100%로 표기하였다. 분리될 때가지 낙하되는 횟수가 많고 잔사가 0%에 가까울수록 방수 양면테이프의 내파괴성이 우수한 것을 의미한다.Drop Separation Evaluation-After cutting the waterproof double-sided tape into 48mm × 48mm, cut the inside of the horizontal 47.3mm × 47.3mm, prepare a sample of 0.7mm in width, and then prepare 60mm × 60mm × 6.5mm thick aluminum (Al A sample was attached onto the plate and a glass plate of 50 mm long by 50 mm long and 2.8 mm thick was attached. The prepared sample was allowed to drop freely for 1.5 m after being left at 24 ° C. for 30 minutes, and then repeatedly dropped until the aluminum plate and the glass plate were separated. The adhesive residue was obtained by checking the number of times when the aluminum plate and the glass plate were separated and the degree of the adhesive remaining on the separating surface, and the adhesive component constituting the adhesive layer of the waterproof double-sided tape on the aluminum plate or the glass plate was found on only one side. If present, the residue was marked as 0%, and if the adhesive was present on both sides of the aluminum plate and the glass plate because the tape was broken, the residue was marked as 100%. The more the number of drops falling until the separation and the residue is closer to 0%, the better the fracture resistance of the waterproof double-sided tape.
또한, 방수성은 방수 양면테이프를 가로 48mm × 세로 48mm 로 자른 후 가로 내부를 47.3mm × 세로 47.3mm 잘라내어 살폭이 0.7mm인 사각틀 모양의 샘플을 준비한 후에, 가로 60mm × 세로 60mm × 두께 6.5mm 마그네슘(Mg) 플레이트와 동일 크기의 폴리카보네이트(PC) 플레이트 위에 샘플을 부착시키고, 가로 50mm × 세로 50mm × 두께 2.8mm인 유리 플레이트를 부착시켰다. 준비된 샘플을 24℃에서 72시간 방치시킨 후에 물이 2m 높이로 채워진 수조에 투입하고 144시간 경과 후 샘플을 수거하여 누수의 유/무를 육안으로 확인하였다. 누수가 없는 샘플은 Pass로 표기 하였고 누수된 샘플은 NG로 표기하였다.}
In addition, after the waterproof double-coated tape was cut into 48 mm × 48 mm lengths, the inside was cut into 47.3 mm × 47.3 mm widths, and a 0.7 mm-thick square frame sample was prepared.Then, 60 mm × 60 mm × 6.5 mm magnesium ( A sample was attached onto a polycarbonate (PC) plate of the same size as the Mg) plate, and a glass plate 50 mm x 50 mm x 2.8 mm thick was attached. After the prepared sample was left at 24 ° C. for 72 hours, water was placed in a water tank filled with 2 m height, and after 144 hours, the samples were collected to visually check whether water leaked or not. Leak-free samples are labeled Pass and leaky samples are labeled NG.}
<표 2>TABLE 2
위에 표 2에 나타낸 것처럼, 개시된 실시예 1 내지 7을 통해 제조된 방수 양면테이프는 비교예 1 내지 6을 통해 제조된 방수 양면테이프에 비해, 내파괴성과 방수성능이 우수한 것을 알 수 있다.
As shown in Table 2 above, it can be seen that the waterproof double-coated tape produced through the disclosed Examples 1 to 7 has excellent fracture resistance and waterproof performance, compared to the waterproof double-coated tape prepared through Comparative Examples 1 to 6.
따라서, 개시된 내파괴성이 우수한 방수 양면테이프는 방수성능이 우수할 뿐만 아니라, 저장탄성률이 우수한 수지가 함유된 완충층과 점착층이 형성되어, 우수한 내파괴성을 나타낸다.
Therefore, the disclosed waterproof double-coated tape having excellent fracture resistance not only has excellent waterproof performance, but also a buffer layer and an adhesive layer containing a resin having excellent storage modulus are formed, thereby exhibiting excellent fracture resistance.
10 ; 기재층
20 ; 완충층
30 ; 점착층10; Substrate layer
20; Buffer layer
30; Adhesive layer
Claims (6)
상기 기재층의 일면에 형성되며, 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부, 충전제 0.1 내지 10 중량부 및 경화제 0.1 내지 10 중량부로 이루어지는 완충층; 및
상기 완충층이 형성된 상기 기재층의 상부면 및 하부면에 형성되는 점착층; 으로 이루어지고,
상기 충전제는 0.001 내지 50 마이크로미터의 입자크기를 나타내며, 폴리메틸메타아크릴레이트, 탄화수소, 탄산칼슘 및 실리카로 이루어진 그룹에서 선택된 하나로 이루어지며,
상기 점착층은 저장탄성률이 40000 내지 90000Pa인 아크릴 수지 또는 우레탄 수지 100 중량부 및 경화제 0.1 내지 10 중량부로 이루어지는 것을 특징으로 하는 내파괴성이 우수한 방수 양면테이프.
Base layer;
A buffer layer formed on one surface of the base layer, the buffer layer including 100 parts by weight of an acrylic resin or a urethane resin having a storage modulus of 40000 to 90000 Pa, 0.1 to 10 parts by weight of a filler, and 0.1 to 10 parts by weight of a curing agent; And
An adhesive layer formed on upper and lower surfaces of the base layer on which the buffer layer is formed; Made of
The filler has a particle size of 0.001 to 50 micrometers, and consists of one selected from the group consisting of polymethylmethacrylate, hydrocarbons, calcium carbonate and silica,
The adhesive layer is a waterproof double-coated tape having excellent fracture resistance, characterized in that the storage elastic modulus is composed of 100 parts by weight of acrylic resin or urethane resin of 40000 to 90000 Pa and 0.1 to 10 parts by weight of a curing agent.
상기 기재층은 25 내지 100 마이크로미터 두께의 폴리에틸렌테레프탈레이트로 이루어지는 것을 특징으로 하는 내파괴성이 우수한 방수 양면테이프.
The method according to claim 1,
The base layer is a waterproof double-sided tape having excellent fracture resistance, characterized in that consisting of polyethylene terephthalate having a thickness of 25 to 100 micrometers.
상기 완충층은 10 내지 200 마이크로미터의 두께로 형성되는 것을 특징으로 하는 내파괴성이 우수한 방수 양면테이프.
The method according to claim 1,
The buffer layer is a waterproof double-sided tape having excellent fracture resistance, characterized in that formed in a thickness of 10 to 200 micrometers.
상기 점착층은 10 내지 200 마이크로미터의 두께로 형성되는 것을 특징으로 하는 내파괴성이 우수한 방수 양면테이프.The method according to claim 1,
The adhesive layer is a waterproof double-sided tape having excellent fracture resistance, characterized in that formed in a thickness of 10 to 200 micrometers.