KR102026372B1 - Adhesive for restoring pottery - Google Patents
Adhesive for restoring pottery Download PDFInfo
- Publication number
- KR102026372B1 KR102026372B1 KR1020170144710A KR20170144710A KR102026372B1 KR 102026372 B1 KR102026372 B1 KR 102026372B1 KR 1020170144710 A KR1020170144710 A KR 1020170144710A KR 20170144710 A KR20170144710 A KR 20170144710A KR 102026372 B1 KR102026372 B1 KR 102026372B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive
- porcelain
- weight
- parts
- restoring
- Prior art date
Abstract
본 발명은 도자기 유물(문화재)의 복원을 위한 접착제에 대한 것으로, 더욱 상세하게는 아교 30 내지 50 중량부, 생옻 추출물 50 내지 70 중량부, 생강 0.5 내지 2 중량부, 우뭇가사리 2 내지 4 중량부, 청각 2 내지 4 중량부를 포함하여, 도자기 복원에 적합한 접착 강도를 가져 적절하게 도자기를 복원하고 2차 손상을 방지하고 시간이 지남에 따라 색상의 변화가 없고 수분에 강하며 건조환경 및 건조시간을 개선할 수 있어 도자기 복원에 최적화되고, 천연물질로 이루어져 휘발성 유해물질을 배출하지 않아 친환경성을 도모할 수 있으면서 나쁜 냄새가 나지 않고 쉽게 부패하지 않는 도자기 복원용 접착제에 대한 것이다.The present invention relates to an adhesive for restoring porcelain relics (cultural assets), more specifically, 30 to 50 parts by weight of glue, 50 to 70 parts by weight of fresh lacquer extract, 0.5 to 2 parts by weight of ginger, 2 to 4 parts by weight of starfish, Acoustic strength, suitable for restoring porcelain, including 2 to 4 parts by weight, to properly restore porcelain, prevent secondary damage, resist color change over time, resist moisture, improve drying environment and drying time It can be optimized for porcelain restoration, and made of natural materials to promote eco-friendliness without emitting volatile harmful substances, but it does not have a bad smell and does not easily rot for porcelain restoration.
Description
본 발명은 도자기 유물(문화재)의 복원을 위한 접착제에 대한 것으로, 더욱 상세하게는 아교 30 내지 50 중량부, 생옻 추출물 50 내지 70 중량부, 생강 0.5 내지 2 중량부, 우뭇가사리 2 내지 4 중량부, 청각 0.5 내지 2 중량부를 포함하여, 도자기 복원에 적합한 접착 강도를 가져 적절하게 도자기를 복원하고 2차 손상을 방지하고 시간이 지남에 따라 색상이 검은색으로 변화하지 않고 수분에 강하며 건조환경 및 건조시간을 개선할 수 있어 도자기 복원에 최적화되고, 천연물질로 이루어져 휘발성 유해물질을 배출하지 않아 친환경성을 도모할 수 있으면서 나쁜 냄새가 나지 않고 쉽게 부패하지 않는 도자기 복원용 접착제에 대한 것이다.The present invention relates to an adhesive for restoring porcelain relics (cultural assets), more specifically, 30 to 50 parts by weight of glue, 50 to 70 parts by weight of fresh lacquer extract, 0.5 to 2 parts by weight of ginger, 2 to 4 parts by weight of starfish, Acoustic strength, suitable for restoration of porcelain, including 0.5 to 2 parts by weight, to properly restore porcelain, prevent secondary damage, color does not turn black over time, is resistant to moisture, dry environment and drying It is optimized for porcelain restoration because it can improve the time, and it is made of natural materials and does not emit volatile harmful substances, so that it can promote eco-friendliness and does not smell bad and does not easily rot.
도자기는 도기, 자기, 사기, 토기, 질그릇 따위를 통틀어 말하는데, 우리나라에서는 대략 서기 전 6000∼5000년경에 토기를 만들기 시작하여 고려, 조선을 거치면서 청자, 분청사기, 백자 등으로 발전하여, 많은 도자기 유물이 발견되고 있다. 발굴된 도자기 유물은 온전한 형태보다 여러 조각으로 부서진 체로 발견되는 것이 대부분이어서, 부서진 조각을 하기의 특허문헌과 같은 합성수지 접착제를 이용하여 붙여 복원이 이루어지고 있다.Pottery refers to pottery, porcelain, pottery, earthenware, earthenware, etc. In Korea, about 6,000-5000 years ago, pottery began to be made. Artifacts are being found. Excavated porcelain artifacts are mostly found in a broken body in several pieces rather than intact forms, and the broken pieces are restored using a synthetic resin adhesive such as the following patent document.
(특허문헌)(Patent literature)
특허 제10-0848538호(2008. 07. 21. 등록) "도자기질 타일용 접착제 조성물"Patent No. 10-0848538 (registered July 21, 2008) "Adhesive composition for ceramic tiles"
하지만, 종래 합성수지 접착제는 휘발성 유기용제를 방출하고, 시간이 지남에 따라 구성 고분자의 화학적 변화와 분해로 인해 물리적 변화 즉 수축·팽창의 결함 등의 문제가 발생한다. 이와 같은 합성수지 접착제의 단점을 극복하기 위해 아교 등을 주성분으로 하는 기존의 천연 접착제가 사용되어 유해한 유기용제를 방출하지 않고 시간이 지남에 따라 생기는 물리적 변화를 최소화할 수 있으나, 종래의 천연 접착제는 도자기에 맞추어서 생산된 것이 아니어서 도자기 복원에 접합하지 않은 문제가 있다.However, conventional synthetic resin adhesives release volatile organic solvents, and as time passes, problems such as physical changes, that is, defects in shrinkage and expansion, occur due to chemical changes and decomposition of constituent polymers. In order to overcome the drawbacks of synthetic resin adhesives, conventional natural adhesives, including glues, can be used to minimize physical changes occurring over time without releasing harmful organic solvents. There was a problem in that it was not produced in accordance with the process, so it was not bonded to ceramic restoration.
본 발명은 상기의 문제점을 해결하기 위해 안출된 것으로,The present invention has been made to solve the above problems,
본 발명은 도자기 복원에 최적화된 도자기 복원용 접착제를 제공하는데 그 목적이 있다.It is an object of the present invention to provide an adhesive for restoration of ceramics optimized for ceramic restoration.
또한, 본 발명은 도자기 복원에 적합한 접착 강도를 가져 적절하게 도자기를 복원하고 2차 손상을 방지하고, 천연물질로 이루어져 휘발성 유해물질을 배출하지 않아 친환경성을 도모할 수 있는 도자기 복원용 접착제를 제공하는데 그 목적이 있다.In addition, the present invention provides an adhesive for restoring porcelain which has an adhesive strength suitable for restoring porcelain to properly restore porcelain, prevent secondary damage, and promote eco-friendliness by releasing volatile harmful substances made of natural materials. Its purpose is to.
또한, 본 발명은 시간이 지남에 따라 색상이 검은색으로 변화하지 않고, 수분에 강하며, 건조환경 및 건조시간을 개선할 수 있는 도자기 복원용 접착제를 제공하는데 그 목적이 있다.In addition, an object of the present invention is to provide an adhesive for restoring porcelain that does not change color over time, is resistant to moisture, and improves the drying environment and drying time.
또한, 본 발명은 천연물질로만 이루어졌음에도 나쁜 냄새가 나지 않고 쉽게 부패하지 않는 도자기 복원용 접착제를 제공하는데 그 목적이 있다.In addition, an object of the present invention is to provide an adhesive for restoring porcelain which does not smell bad and does not easily rot even though it is made of only natural materials.
본 발명은 앞서 본 목적을 달성하기 위해서 다음과 같은 구성을 가진 실시예에 의해서 구현된다.The present invention is implemented by the embodiment having the following configuration to achieve the above object.
본 발명의 일 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제는 아교 30 내지 50 중량부 및 생옻 추출물 50 내지 70 중량부를 포함하는 것을 특징으로 한다.According to one embodiment of the invention, the adhesive for restoring porcelain according to the invention is characterized in that it comprises 30 to 50 parts by weight of glue and 50 to 70 parts by weight of fresh lacquer extract.
본 발명의 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제에 있어서 상기 생옻 추출물은 정제하지 않은 옻나무의 진을 의미하는 생옻을 유기 용제에 혼합하여 혼합용액을 형성하고 교반하는 혼합교반단계와, 상기 혼합교반단계 후 일정 온도에서 일정 시간 정치하여 유기용제에 용해되는 부분과 용해되지 않은 부분으로 층분리하는 분리단계와, 상기 분리단계에서 유기용제에 용해되는 부분인 상층액을 분리하여 감압 증발을 통해 유기용제를 증발시켜 생옻 추출물을 추출하는 증발단계를 거쳐 얻어지는 것을 특징으로 한다.According to another embodiment of the present invention, in the adhesive for restoring porcelain according to the present invention, the raw lacquer extract is a mixed stirring step of forming a mixed solution by mixing raw lacquer, which means gin of unrefined lacquer, with an organic solvent and stirring. After the mixing and stirring step, the mixture is allowed to stand at a certain temperature for a certain time to separate the layer into a part that is dissolved in an organic solvent and a part that is not dissolved, and the supernatant that is a part that is dissolved in an organic solvent in the separation step is separated and evaporated under reduced pressure. It is characterized in that it is obtained through an evaporation step of extracting the raw lacquer extract by evaporating the organic solvent through.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제는 생강 0.5 내지 2 중량부 및 우뭇가사리 2 내지 4 중량부를 추가로 포함하는 것을 특징으로 한다.According to another embodiment of the present invention, the adhesive for restoring porcelain according to the present invention is characterized in that it further comprises 0.5 to 2 parts by weight of ginger and 2 to 4 parts by weight of loot.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제는 청각 0.5 내지 2 중량부를 추가로 포함하는 것을 특징으로 한다.According to another embodiment of the present invention, the adhesive for restoring porcelain according to the present invention is characterized in that it further comprises 0.5 to 2 parts by weight of hearing.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제에 있어서 상기 분리단계에서는 생옻이 유기용제에 용해되는 부분인 상측의 상층액과, 생옻이 유기용제에 용해되지 않는 부분인 분말형태의 하측의 침전물층으로 분리되는 것을 특징으로 한다.According to another embodiment of the present invention, in the separation step in the adhesive for restoring porcelain according to the present invention, the supernatant of the upper side of which the raw lacquer is dissolved in an organic solvent, and the powder of the raw lacquer is a part which is not soluble in the organic solvent. Characterized in that separated into the bottom sediment layer of the form.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제에 있어서 상기 생강, 우뭇가사리 및 청각은 건조 후 분쇄된 분말이 사용되는 것을 특징으로 한다.According to another embodiment of the present invention, in the adhesive for restoring porcelain according to the present invention, the ginger, wood star and auditory are characterized in that the powder pulverized after drying is used.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제에 있어서 상기 혼합교반단계에서는 혼합용액을 초음파 처리하고 교반하여 이루어지는 것을 특징으로 한다.According to another embodiment of the present invention, the ceramic stirring adhesive according to the present invention is characterized in that the mixing and stirring step is made by sonicating and stirring the mixed solution.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제는 돌외잎추출분말 0.1 내지 0.5 중량부를 추가로 포함하며, 상기 돌외잎추출분말은 돌외잎을 식초에 담지하여 일정 온도에서 일정 시간 유지하고 건더기를 제거 후 얻은 추출액을 동결건조하여 얻어지게 되는 것을 특징으로 한다.According to another embodiment of the present invention, the adhesive for restoring porcelain according to the present invention further comprises 0.1 to 0.5 parts by weight of the stone extract leaf, the stone extract leaf powder is fixed at a certain temperature by supporting the stone extract in vinegar It is characterized in that it is obtained by lyophilizing the extract obtained after maintaining the time and removing the dust.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제는 감껍질추출분말 0.5 내지 2 중량부를 추가로 포함하며, 상기 감껍질추출분말은 감껍질을 건조하여 분쇄한 분말을 에탄올에 침지하고 일정 온도에서 일정 시간 유지하고 여과를 통해 감껍질 분말을 제거하고 여과액을 동결건조하여 얻어지게 되는 것을 특징으로 한다.According to another embodiment of the present invention, the adhesive for restoring porcelain according to the present invention further comprises 0.5 to 2 parts by weight of persimmon peel extract powder, wherein the persimmon peel extract powder is dried and ground to powder ethanol into ethanol. It is characterized in that it is obtained by immersing and maintaining at a constant temperature for a certain time, and removing persimmon powder through filtration and freeze-drying the filtrate.
본 발명의 또 다른 실시예에 따르면, 본 발명에 따른 도자기 복원용 접착제에 있어서 상기 감껍질은 잘 익은 감보다 덜 익은 풋감이 이용되는 것을 특징으로 한다.According to another embodiment of the present invention, in the adhesive for restoring porcelain according to the present invention, the persimmon peel is characterized by using a less ripe foot than the ripe persimmon.
본 발명은 앞서 본 실시예에 의해 다음과 같은 효과를 얻을 수 있다.The present invention can obtain the following effects by the above embodiment.
본 발명은 도자기 복원에 최적화된 도자기 복원용 접착제를 제공하는 효과가 있다.The present invention has the effect of providing an adhesive for restoration of ceramics optimized for ceramic restoration.
또한, 본 발명은 도자기 복원에 적합한 접착 강도를 가져 적절하게 도자기를 복원하고 2차 손상을 방지하고, 천연물질로 이루어져 휘발성 유해물질을 배출하지 않아 친환경성을 도모할 수 있는 효과가 있다.In addition, the present invention has an adhesive strength suitable for restoring porcelain appropriately restore the porcelain and prevent secondary damage, and made of natural materials do not discharge volatile harmful substances, there is an effect that can be eco-friendly.
또한, 본 발명은 시간이 지남에 따라 색상의 변화가 없고, 수분에 강하며, 건조환경 및 건조시간을 개선할 수 있는 효과가 있다.In addition, the present invention does not change color over time, is resistant to moisture, and has the effect of improving the drying environment and drying time.
또한, 본 발명은 천연물질로만 이루어졌음에도 나쁜 냄새가 나지 않고 쉽게 부패하지 않는 효과가 있다.In addition, the present invention has an effect that does not smell bad and easily rot even though it is made of only natural materials.
이하에서는 본 발명에 따른 도자기 복원용 접착제를 첨부된 도면을 참조하여 상세히 설명한다. 특별한 정의가 없는 한 본 명세서의 모든 용어는 본 발명이 속하는 기술분야의 통상의 지식을 가진 기술자가 이해하는 당해 용어의 일반적 의미와 동일하고 만약 본 명세서에 사용된 용어의 의미와 충돌하는 경우에는 본 명세서에 사용된 정의에 따른다. 또한, 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대해 상세한 설명은 생략한다. 명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.Hereinafter, with reference to the accompanying drawings, the adhesive for restoration of porcelain according to the present invention will be described in detail. Unless otherwise defined, all terms in this specification are equivalent to the general meaning of the terms understood by those of ordinary skill in the art to which the present invention pertains and, if they conflict with the meanings of the terms used herein, Follow the definition used in the specification. In addition, detailed description of well-known functions and configurations that may unnecessarily obscure the subject matter of the present invention will be omitted. Throughout the specification, when a part is said to "include" a certain component, it means that it may further include other components, without excluding other components unless specifically stated otherwise.
본 발명의 일 실시예에 따른 도자기 복원용 접착제는 아교 30 내지 50 중량부, 생옻 추출물 50 내지 70 중량부, 생강 0.5 내지 2 중량부, 우뭇가사리 2 내지 4 중량부, 청각 0.5 내지 2 중량부 등을 포함한다.Adhesive for restoring porcelain according to an embodiment of the present invention is 30 to 50 parts by weight of glue, 50 to 70 parts by weight of fresh lacquer extract, 0.5 to 2 parts by weight of ginger, 2 to 4 parts by weight of starfish, 0.5 to 2 parts by weight of hearing Include.
상기 아교는 상기 도자기 복원용 접착제의 주성분으로, 30 내지 50 중량부 범위에서 사용되는 것이 바람직하며, 30 중량부 미만으로 사용되는 경우 접착제의 접착강도가 떨어지며 50 중량부를 초과하여 사용되는 경우 접착제의 접착강도가 너무 강해 복원된 도자기의 2차 손상이 발생할 수 있다. 아교는 일반 시중에서 판매되는 아교가 사용될 수 있으며, 그 제형은 제한되는 것이 아니다. 도자기 복원에서 접착제의 접착강도는 가장 중요한 요소인데, 접착제의 접착강도가 너무 낮으면 도자기의 접착 부위가 약해 손상이 일어날 수 있고 접착강도가 너무 높으면 도자기가 손상될 수 있어 본 발명은 도자기 복원에 사용되는 종래의 합성수지 접착제의 접착 강도와 유사한 수준의 접착강도를 제공하도록 한다.The glue is a main component of the adhesive for restoring porcelain, preferably used in the range of 30 to 50 parts by weight, and when used in less than 30 parts by weight, the adhesive strength of the adhesive is lowered and the adhesion of the adhesive when used in excess of 50 parts by weight. The strength is so strong that secondary damage to the restored pottery can occur. Glue may be used commercially available glue, the formulation is not limited. Adhesive strength of the adhesive in the restoration of porcelain is the most important factor, if the adhesive strength of the adhesive is too low, the adhesive portion of the porcelain may be damaged and damage may occur if the adhesive strength is too high, the present invention is used in ceramic restoration To provide a level of adhesion similar to that of conventional synthetic resin adhesives.
상기 생옻 추출물은 아교와 함께 상기 도자기 복원용 접착제의 주성분을 이루는 구성으로, 아교가 가지는 단점인 수분에 약하고 쉽게 부패되고 나쁜 냄새가 나는 것을 보완한다. 상기 생옻 추출물은 50 내지 70 중량부 범위에서 사용되는 것이 바람직하며, 50 중량부 미만으로 사용되는 경우 아교의 상대적인 비율이 커 접착제의 접착강도 너무 강해 복원된 도자기의 훼손이 발생할 수 있으며 70 중량부를 초과하여 사용되는 경우 접착제의 접착강도가 떨어지는 문제가 있다. 상기 생옻 추출물은 정제하지 않은 옻나무의 진을 의미하는 생옻을 유기 용제에 혼합하여 혼합용액을 형성하고 교반하는 혼합교반단계와, 상기 혼합교반단계 후 일정 온도에서 일정 시간 정치하여 유기용제에 용해되는 부분과 용해되지 않은 부분으로 층분리하는 분리단계와, 상기 분리단계에서 유기용제에 용해되는 부분인 상층액을 분리하여 감압회전증발기를 이용하여 유기용제를 증발시켜 생옻 추출물을 추출하는 증발단계를 거쳐 얻어지게 된다. 상기 생옻은 생칠이라고도 하며 시판 중인 제품이 사용될 수 있으며, 상기 유기용제는 예컨대 아세톤 등이 사용될 수 있고, 상기 분리단계에서는 생옻이 유기용제에 용해되는 부분인 상측의 상층액과, 생옻이 유기용제에 용해되지 않는 부분인 분말형태의 하측의 침전물층으로 분리되게 된다. 생옻 자체를 사용하는 경우 제조된 접착제가 시간이 경과함에 따라 색상이 검은색으로 변화하여 복원된 도자기의 미관을 해하고 높은 점도로 인해 도포성이 떨어지는데 반해, 상기 접찹제는 생옻이 아니라 생옻 추출물이 사용되어, 점도를 낮추어 도포성을 향상시키고 도자기 도포 후 시간이 경과하여도 색상이 검은색으로 변화하지 않고 오히려 투명성이 증가하여 미관을 저해하지 않게 된다. 상기 생옻 추출물은 얻는 과정의 일 단계인 상기 혼합교반단계에서 혼합용액을 초음파 처리하고 교반하는 경우 생옻 추출물의 추출 효율을 향상시키킬 수 있다. 상기 초음파 처리는 초음파 분산기를 이용하여 수행될 수 있다.The raw lacquer extract is composed of the main component of the adhesive for restoring the porcelain with glue, to compensate for the weakness of the glue is weak and easily rot and bad smell. The raw lacquer extract is preferably used in the range of 50 to 70 parts by weight, and when used in less than 50 parts by weight, the relative ratio of glue is large, the adhesive strength of the adhesive is too strong may cause damage to the restored porcelain and exceeds 70 parts by weight If used, there is a problem that the adhesive strength of the adhesive falls. The raw lacquer extract is a mixed stirring step of forming a mixed solution by mixing the raw lacquer, which means the pure lacquer gin in an organic solvent and stirring, and a part which is allowed to stand at a certain temperature for a certain time after the mixing stirring step to dissolve in the organic solvent A separation step of separating the layers into undissolved parts, and a supernatant which is a part dissolved in the organic solvent in the separation step, and then evaporating the organic solvent by using a reduced pressure rotary evaporator to obtain a raw lacquer extract. You lose. The raw lacquer is also known as raw lacquer may be used commercially available products, the organic solvent may be used, for example, acetone, etc. In the separation step, the upper supernatant liquid is a portion of the raw lacquer dissolved in the organic solvent, and the raw lacquer in the organic solvent It is separated into a sediment layer below in the form of powder, which is an insoluble part. In the case of using the raw lacquer itself, the color of the prepared adhesive changes to black as time passes, which damages the aesthetics of the restored porcelain and is poor in applicability due to its high viscosity. It can be used to lower the viscosity to improve the applicability and the color does not change to black even after the application of porcelain, but rather the transparency is increased so as not to impair the aesthetics. The raw lacquer extract may improve the extraction efficiency of the raw lacquer extract when the mixed solution is sonicated and stirred in the mixing and stirring step of obtaining a step. The sonication may be performed using an ultrasonic disperser.
상기 생강은 도자기 복원용 접착제의 나쁜 냄새를 제거하기 위한 구성으로, 0.5 내지 2 중량부 범위에서 사용되는 것이 바람직하며, 0.5 중량부 미만으로 사용되는 경우 냄새 제거의 효과가 미미하고 2 중량부를 초과하여 사용되는 경우 접착제에 요구되는 물성을 저하하게 된다.The ginger is a component for removing bad odor of the adhesive for restoring porcelain, preferably used in the range of 0.5 to 2 parts by weight, and when used in less than 0.5 parts by weight, the effect of removing the odor is insignificant and in excess of 2 parts by weight. When used, the physical properties required for the adhesive are lowered.
상기 우뭇가사리는 도자기 복원용 접착제의 건조시간을 단축하고 투명도를 높이기 위해 사용되는 구성으로, 2 내지 4 중량부 범위에서 사용되는 것이 바람직하며 2 중량부 미만으로 사용되는 경우 그 효과가 미비하고 4 중량부를 초과하여 사용되는 경우 접착제에 요구되는 물성을 저하하게 된다.The wood starfish is used to shorten the drying time of the adhesive for restoring porcelain and increase the transparency, preferably used in the range of 2 to 4 parts by weight, and when used in less than 2 parts by weight, the effect is insignificant and 4 parts by weight. When used in excess, the physical properties required for the adhesive are lowered.
상기 청각은 도자기 복원용 접착제의 나쁜 냄새를 제거하고 부패를 방지하기 위한 구성으로, 0.5 내지 2 중량부 범위에서 사용되는 것이 바람직하며, 0.5 중량부 미만으로 사용되는 경우 냄새 제거 및 부패 방지의 효과가 미미하고 2 중량부를 초과하여 사용되는 경우 접착제에 요구되는 물성을 저하하게 된다. 상기 생강, 우뭇가사리 및 청각은 건조 후 분쇄된 분말이 사용되게 된다. 상기 접착제 조성물은 동물에서 얻은 아교를 주성분으로 하므로, 그 냄새와 빠른 부패가 문제되는데 생옻 추출물이 함께 혼합되어 이에 대한 문제를 해결하고, 추가로 생강, 청각이 혼합되어 더욱 나쁜 냄새를 제거하고 부패를 방지하게 된다. 한편, 동일 양으로 생강 또는 청각을 각각 사용하는 것보다 생강 및 청각을 함께 사용하는 경우 냄새 제거의 효과가 향상되게 된다.The hearing is configured to remove the bad smell of the porcelain restoration adhesive and to prevent decay, it is preferably used in the range of 0.5 to 2 parts by weight, when used in less than 0.5 parts by weight has the effect of removing the odor and anti-corruption Insignificant and when used in excess of 2 parts by weight will lower the physical properties required for the adhesive. The ginger, wood starch and hearing are to be used after crushed powder drying. Since the adhesive composition is mainly composed of glue obtained from the animal, its smell and rapid decay are a problem, and the raw lacquer extract is mixed together to solve the problem. In addition, ginger and hearing are mixed to remove even worse odor and decay. Will be prevented. On the other hand, when using ginger and hearing together than using ginger or hearing in the same amount, respectively, the effect of odor removal is improved.
상기 도자기 복원용 접착제는 돌외잎추출분말 0.1 내지 0.5 중량부 및 감껍질추출분말 0.5 내지 2 중량부를 추가로 포함할 수 있다. 상기 돌외잎추출분말은 도자기 복원용 접착제의 부패를 방지하기 위해 추가로 첨가되는 구성으로, 돌외잎을 식초에 담지하여 일정 온도에서 일정 시간 유지하고 건더기를 제거 후 얻은 추출액을 동결건조하여 얻어지게 된다. 상기 감추출액은 도자기 복원용 접착제의 방수성을 증가시키기 위해 추가로 첨가되는 구성으로, 감껍질을 건조하여 분쇄한 분말을 에탄올에 침지하고 일정 온도에서 일정 시간 유지하고 여과를 통해 감껍질 분말을 제거하고 여과액을 동결건조하여 얻어지게 된다. 잘 익은 감보다 덜 익은 풋감을 사용하는 경우 방수성을 더욱 향상시킬 수 있다.The porcelain restoration adhesive may further comprise 0.1 to 0.5 parts by weight of the stone extract leaf powder and 0.5 to 2 parts by weight of persimmon extract powder. The outer leaf extract powder is added to prevent the decay of the adhesive for restoring porcelain, and is obtained by holding the outer leaf in vinegar to maintain a certain temperature at a certain temperature and freeze-drying the extract obtained after removing dry . The persimmon extract is added to increase the waterproofness of the adhesive for restoring porcelain, the dried persimmon bark powder is immersed in ethanol and maintained at a constant temperature for a certain time, and filtration to remove persimmon skin The filtrate is obtained by lyophilization. If you use less ripe than a ripe persimmon, you can further improve the waterproofness.
이하, 실시예를 통해서 본 발명을 보다 상세히 설명하기로 한다. 하지만, 이들은 본 발명을 보다 상세하게 설명하기 위한 것일 뿐, 본 발명의 권리범위가 이에 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples. However, these are only for explaining the present invention in more detail, the scope of the present invention is not limited thereto.
<실시예 1 및 2> 생옻 추출물의 제조<Examples 1 and 2> Preparation of fresh lacquer extract
(1) 실시예 1(1) Example 1
시판 중인 생옻을 유기용제인 아세톤(생옻 100g당 아세톤 500ml 사용)에 혼합하고 1시간 교반한 후, 상온에서 24시간 동안 정치하여 유기용제에 용해되는 부분인 상측액과 유기용제에 용해되지 않은 부분인 침전물층으로 층분리를 수행하고, 감압증발기를 사용하여 분리된 상측액에서 유기용제를 증발시켜 액체 상태의 생옻 추출물을 얻었다.Commercially available raw lacquer is mixed with organic solvent acetone (500 ml of acetone per 100 g of fresh lacquer), stirred for 1 hour, and left to stand at room temperature for 24 hours to dissolve in the organic solvent and the supernatant and the organic solvent. Layer separation was carried out with the precipitate layer, and the organic solvent was evaporated from the separated supernatant using a reduced pressure evaporator to obtain a liquid lacquer extract.
(2) 실시예 2(2) Example 2
실시예 1에서 생옻과 아세톤을 혼합하고 초음파 분산기를 이용하여 10분간 초음파 처리한 후 교반한 것을 제외하고는 다른 조건을 실시예 1과 동일하게 하여 생옻 추출물을 얻었다.The raw lacquer extract was obtained in the same manner as in Example 1 except that the raw lacquer and acetone were mixed in Example 1 and sonicated for 10 minutes using an ultrasonic disperser, followed by stirring.
<실시예 3 내지 12> 접착제의 제조Examples 3 to 12 Preparation of Adhesive
(1) 실시예 3(1) Example 3
아교 40중량부와 물 50중량부가 혼합되어 형성된 아교 수용액, 실시예 1에서 제조된 생옻 추출물 60중량부, 생강 분말 1중량부, 우뭇가사리 분말 3 중량부, 청각 분말 1 중량부를 혼합하여 접착제를 제조하였다.An adhesive was prepared by mixing a glue aqueous solution formed by mixing 40 parts by weight of glue and 50 parts by weight of water, 60 parts by weight of fresh lacquer extract prepared in Example 1, 1 part by weight of ginger powder, 3 parts by weight of wheat starch powder, and 1 part by weight of hearing powder. .
(2) 실시예 4(2) Example 4
실시예 1에서 제조된 생옻 추출물 대시에 실시예 2에서 제조된 생옻 추출물을 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared in the same manner as in Example 3 except that the raw lacquer extract prepared in Example 2 was used in the raw lacquer extract dash prepared in Example 1.
(3) 실시예 5(3) Example 5
돌외잎추출분말 0.3 중량부가 추가로 사용된 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다. 상기 돌외잎추출분말은 건조한 돌외잎을 식초(돌외잎 100g당 식초 200ml)에 담지하여 12℃에서 48시간 유지하고 건더기를 제거 후 얻은 추출액을 동결건조하여 얻었다.An adhesive was prepared under the same conditions as in Example 3 except that 0.3 part by weight of the extra-leaf extract powder was additionally used. The dorsal leaf extract powder was obtained by holding the dried dorsal leaves in vinegar (200 ml of vinegar per 100 g of dolvine leaves) and maintaining them at 12 ° C. for 48 hours.
(4) 실시예 6(4) Example 6
감껍질추출분말 1 중량부를 추가로 사용된 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다. 상기 감껍질추출분말은 8월에 수확한 단감(완전히 익지 않은 풋감)의 껍질을 건조하여 분쇄한 분말을 에탄올(껍질 100g당 에탄올 300ml)에 침지하고 24℃에서 48시간 유지하고 여과를 통해 감껍질 분말을 제거하고 여과액을 동결건조하여 얻었다.An adhesive was prepared in the same manner as in Example 3 except that 1 part by weight of persimmon extract powder was used. The persimmon extract powder is dried by drying the skin of sweet persimmon (completely raw green persimmon) harvested in August, immersed in ethanol (300ml of ethanol per 100g shell) and maintained for 48 hours at 24 ℃ and persimmon through filtration The powder was removed and the filtrate was obtained by lyophilization.
(5) 실시예 7(5) Example 7
8월에 수확한 단감(완전히 익지 않은 풋감)의 껍질 대신에 10월에 수확한 단감(완전히 익은 감)의 껍질을 사용한 것을 제외하고는 다른 조건을 실시예 6과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared in the same manner as in Example 6, except that the peel of sweet persimmon (completely ripe persimmon) harvested in October was used instead of the peel of sweet persimmon (full ripe persimmon) harvested in August.
(6) 실시예 8(6) Example 8
청각 분말을 사용하지 않고 생강 분말 2 중량부를 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared under the same conditions as in Example 3 except that 2 parts by weight of ginger powder was not used for the auditory powder.
(7) 실시예 9(7) Example 9
생강 분말을 사용하지 않고 청강 분말 2 중량부를 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared in the same manner as in Example 3, except that 2 parts by weight of the diamond powder was used without the ginger powder.
(8) 실시예 10(8) Example 10
아교 40 중량부 대신에 아교 20 중량부를 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared under the same conditions as in Example 3 except that 20 parts by weight of glue were used instead of 40 parts by weight of glue.
(8) 실시예 11(8) Example 11
아교 40 중량부 대신에 아교 80 중량부를 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared under the same conditions as in Example 3 except that 80 parts by weight of the glue was used instead of 40 parts by weight of the glue.
(9) 실시예 12(9) Example 12
생옻 조성물 대신에 생옻을 사용한 것을 제외하고는 다른 조건을 실시예 3과 동일하게 하여 접착제를 제조하였다.An adhesive was prepared in the same manner as in Example 3 except that the fresh lacquer was used instead of the fresh lacquer composition.
<실험예 1> 접착강도의 측정Experimental Example 1 Measurement of Adhesive Strength
(1) 접착제의 접착강도 측정을 위해 토기를 피착제로 하여 시편을 제작하고 KS M 3734에 따라 인장전단 접착강도(N/mm2)를 측정하였다. 실시예 3 내지 7, 10 및 11에서 제조된 접착제 및 도자기 복원에 사용되는 대표적인 합성수지 접착제인 Paraloid B-72(P. B-72)를 그 대상으로 하였으며 그 결과를 표 1에 나타내었다.(1) In order to measure the adhesive strength of the adhesive, a specimen was prepared using earthenware as an adherend, and tensile shear adhesive strength (N / mm 2 ) was measured according to KS M 3734. Paraloid B-72 (P. B-72), which is a representative synthetic resin adhesive used for restoring the adhesives and porcelains prepared in Examples 3 to 7, 10, and 11, was subjected to the test, and the results are shown in Table 1.
(2) 표 1을 보면, 실시예 3 내지 7에서 제조된 접착제와 Paraloid B-72가 유사한 접착강도를 가지며, 실시예 10에서 제조된 접착제는 상대적으로 접착강도가 떨어지고 실시예 11에서 제조된 접착제는 상대적으로 접착강도가 강함을 알 수 있어, 본 발명의 접착제는 도자기 복원에 적합한 접착 강도를 가져 적절하게 도자기를 복원하고 2차 손상을 방지할 수 있음을 알 수 있다.(2) Referring to Table 1, the adhesives prepared in Examples 3 to 7 and Paraloid B-72 have similar adhesive strengths, and the adhesive prepared in Example 10 is relatively inferior in adhesive strength and the adhesive prepared in Example 11 It can be seen that the relatively strong adhesive strength, the adhesive of the present invention has a suitable adhesive strength for restoring porcelain can be properly restored porcelain and prevent secondary damage.
<실험예 2> 건조 및 색상변화 관측Experimental Example 2 Drying and Color Change Observation
(1) 실시예 3 내지 12에서 제조된 접착제 각각을 유리판에 도포하고 24시간이 지난 후 접착제가 완전히 건조되었는지와 색상변화를 관측하였다.(1) Each of the adhesives prepared in Examples 3 to 12 was applied to a glass plate, and after 24 hours, the adhesive was completely dried and the color change was observed.
(2) 실시예 3 내지 11에서 제조된 접착제는 24시간 후 완전히 건조되었고, 전체적으로 투명하고 옅은 갈색을 가진 원래 색상에서 24시간 후 투명도가 더욱 증가하였으나, 실시예 12에서 제조된 접착제는 24시간 후 완전히 건조되지 않았고 검은 색상을 띠었다.(2) The adhesives prepared in Examples 3 to 11 were completely dried after 24 hours and the transparency was further increased after 24 hours in the original color with overall transparent and light brown color, but the adhesives prepared in Example 12 were after 24 hours It was not completely dry and black in color.
<실험예 3> 물에 강한 정도 평가Experimental Example 3 Evaluation of the Strongness to Water
(1) 토기를 두 조각으로 절단하고 실시예 2, 3, 6 및 7에서 제조된 접착제 각각을 이용하여 두 조각을 서로 붙이고 24시간 건조를 수행한 후, 물속에 담가 조각이 떨어지는 시간을 측정하여, 그 결과를 표 2에 나타내었다.(1) cut the earthenware into two pieces, attach the two pieces to each other using the adhesives prepared in Examples 2, 3, 6 and 7, and perform drying for 24 hours, and then measure the time that the pieces fall in water The results are shown in Table 2.
(2) 표 2를 보면, 실시예 6에서 제조된 접착제가 가장 나중에 떨어지는 것으로 보아, 완전히 익지 않은 감의 껍질을 이용하여 추출한 분말을 사용하여 접착제를 제조하는 경우 방수성을 향상시킬 수 있음을 알 수 있다.(2) From Table 2, it can be seen that the adhesive prepared in Example 6 falls off last, so that the waterproofing property can be improved when the adhesive is prepared using powder extracted using a shell of raw persimmon. have.
<실험예 4> 부패 방지 효과 평가Experimental Example 4 Evaluation of Anti-Corruption Effect
(1) 실시예 3 내지 6 및 9에서 제조된 접착제 각각을 상면이 개방된 용기에 넣고 온도 30℃ 및 습도 70%인 인위적인 환경에 방치하여 부패가 발생하는 시간을 측정하여, 그 결과를 표 3에 나타내었다. 원래의 냄새와는 다른 역한 냄새가 나고 접착제의 외면에 곰팡이 같은 것이 형성되어 외관이 현저하게 달라진 경우, 부패가 발생한 것으로 평가하였다.(1) Each of the adhesives prepared in Examples 3 to 6 and 9 was placed in an open top container and left in an artificial environment having a temperature of 30 ° C. and a humidity of 70% to measure the time for decay to occur, and the results are shown in Table 3 below. Shown in It was evaluated that the decay occurred when the appearance was changed significantly due to an inverse odor different from the original smell and the appearance of mold on the outer surface of the adhesive.
(2) 표 3을 보면, 실시예 5 및 9에서 제조된 접착제가 실시예 3, 4 및 6에서 제조된 접착제에 비해서 부패가 늦게 일어나고, 실시예 9에 제조된 접착제에 비해서 실시예 5에서 제조된 접착제가 부패가 늦게 일어나는 것을 확인할 수 있어, 돌외잎추출분말 및 청각분말은 부패를 방지하며, 특히 돌외잎추출분말이 현저한 부패 방지효과가 있음을 알 수 있다./(2) Table 3 shows that the adhesives prepared in Examples 5 and 9 had a late decay as compared to the adhesives prepared in Examples 3, 4 and 6, and produced in Example 5 compared to the adhesives prepared in Example 9 It can be seen that the adhesive decay occurs late, the outer stone extract powder and hearing powder to prevent the decay, in particular, the outer leaf extract powder can be seen that the anti-corruption has a significant anti-corruption effect.
<실험예 5> 냄새 제거 효가 평가Experimental Example 5 Evaluation of Odor Removal Effectiveness
실시예 3 내지 6, 8 및 9에서 제조된 접착제 각각에 대하여 냄새에 대한 관능 평가 실시하여 그 결과를 표 4에 나타내었다. 패널은 10명을 대상으로 하였으며, 5점 항목 척도를 사용하여 평가하였고, 좋으면 5점, 나쁘면 1점으로 하여 평가하였다.For each of the adhesives prepared in Examples 3 to 6, 8 and 9, the sensory evaluation on the smell was carried out and the results are shown in Table 4. The panel of 10 subjects was evaluated using the 5-point scale, and 5 points for good and 1 point for bad.
(2) 표 4를 보면, 실시예 2 내지 6에서 제조된 접착제가 실시예 8 및 9에서 제조된 접착제보다 좋은 점수를 받은 것으로 보아, 생강 및 청각을 각각 사용하는 것보다 함께 사용하는 경우 나쁜 냄새 제거 효과가 큼을 알 수 있다.(2) Table 4 shows that the adhesives prepared in Examples 2 to 6 scored better than the adhesives prepared in Examples 8 and 9, resulting in a bad odor when used together with ginger and hearing, respectively. The removal effect is large.
<실험예 6> 생옻 추출물의 추출 효율 평가Experimental Example 6 Evaluation of Extraction Efficiency of Fresh Lacquer Extract
(1) 실시예 1 및 2에서 얻은 생옻 추출물의 무게를 측정하여 원래의 생옻 무게와 대비하여, 생옻 추출물의 추출 효율을 평가하였다.(1) The weight of the raw lacquer extract obtained in Examples 1 and 2 was measured, and the extraction efficiency of the raw lacquer extract was evaluated in comparison with the original raw lacquer weight.
(2) 실시예 1에서 제조된 생옻 추출물은 70%의 추출 효율(생옻 100g당 생옻 추출물 70g을 얻을 수 있음을 의미함)을 가지나, 실시예 2에서 제조된 생옻 추출물은 83%의 추출 효율을 가져, 추출과정에서 초음파 처리를 하는 경우 생옻 추출물의 추출 효율을 증가시킬 수 있음을 알 수 있다.(2) The raw lacquer extract prepared in Example 1 has an extraction efficiency of 70% (meaning that 70 g of the raw lacquer extract can be obtained per 100 g of fresh lacquer), but the raw lacquer extract prepared in Example 2 has an extraction efficiency of 83%. Taken, when the ultrasonication in the extraction process it can be seen that the extraction efficiency of the raw lacquer extract can be increased.
이상에서, 본 발명의 바람직한 실시예들을 설명하였지만, 이와 같은 실시예들은 본 발명의 기술적 사상을 구현하는 일 실시예일 뿐이며 본 발명의 기술적 사상을 구현하는 한 어떠한 변경예 또는 수정예도 본 발명의 범위에 속하는 것으로 해석되어야 한다.In the above, preferred embodiments of the present invention have been described, but these embodiments are only one embodiment for implementing the technical idea of the present invention, and any changes or modifications may be made within the scope of the present invention as long as the technical idea of the present invention is implemented. Should be interpreted as belonging.
Claims (10)
상기 생옻 추출물은 정제하지 않은 옻나무의 진을 의미하는 생옻을 유기 용제에 혼합하여 혼합용액을 형성하고 교반하는 혼합교반단계와, 상기 혼합교반단계 후 일정 온도에서 일정 시간 정치하여 유기용제에 용해되는 부분과 용해되지 않은 부분으로 층분리하는 분리단계와, 상기 분리단계에서 유기용제에 용해되는 부분인 상층액을 분리하여 감압 증발을 통해 유기용제를 증발시켜 생옻 추출물을 추출하는 증발단계를 거쳐 얻어지는 것을 특징으로 하는 도자기 복원용 접착제.In the adhesive for restoring porcelain comprising 30 to 50 parts by weight of glue, 50 to 70 parts by weight of fresh lacquer extract, 0.5 to 2 parts by weight of ginger and 2 to 4 parts by weight of loot,
The raw lacquer extract is a mixed stirring step of forming a mixed solution by mixing the raw lacquer, which means the pure lacquer gin in an organic solvent and stirring, and a part which is allowed to stand at a certain temperature for a certain time after the mixing stirring step to dissolve in the organic solvent Separation step of separating the layer into an undissolved portion, and the supernatant which is a part dissolved in the organic solvent in the separation step is obtained through the evaporation step of extracting the raw lacquer extract by evaporating the organic solvent through a reduced pressure evaporation. Adhesive for ceramic restoration.
청각 0.5 내지 2 중량부를 추가로 포함하는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 3, wherein the adhesive for restoring porcelain
Adhesive for restoring porcelain further comprising 0.5-2 parts by weight of hearing.
상기 분리단계에서는 생옻이 유기용제에 용해되는 부분인 상측의 상층액과, 생옻이 유기용제에 용해되지 않는 부분인 분말형태의 하측의 침전물층으로 분리되는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 4, wherein
In the separation step, the adhesive for porcelain restoration, characterized in that the raw liquid is separated into an upper supernatant, which is a part in which the organic solvent is dissolved in the organic solvent, and a lower precipitate layer in powder form, in which the raw lacquer is not dissolved in the organic solvent.
상기 생강, 우뭇가사리 및 청각은 건조 후 분쇄된 분말이 사용되는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 4, wherein
The ginger, wood starch and hearing are porcelain restoration adhesive, characterized in that the powder is used after crushed dry.
상기 혼합교반단계에서는 혼합용액을 초음파 처리하고 교반하여 이루어지는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 5,
In the mixing and stirring step, the ceramic restoration adhesive, characterized in that made by ultrasonication and stirring the mixed solution.
돌외잎추출분말 0.1 내지 0.5 중량부를 추가로 포함하며, 상기 돌외잎추출분말은 돌외잎을 식초에 담지하여 일정 온도에서 일정 시간 유지하고 건더기를 제거 후 얻은 추출액을 동결건조하여 얻어지게 되는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 4, wherein the porcelain restoration adhesive
Further comprising 0.1 to 0.5 parts by weight of the outer leaf extract powder, the outer leaf extract powder is characterized in that obtained by lyophilizing the extract obtained after holding the outer leaf in vinegar for a certain time and removing the dry matter Adhesive for ceramic restoration.
감껍질추출분말 0.5 내지 2 중량부를 추가로 포함하며, 상기 감껍질추출분말은 감껍질을 건조하여 분쇄한 분말을 에탄올에 침지하고 일정 온도에서 일정 시간 유지하고 여과를 통해 감껍질 분말을 제거하고 여과액을 동결건조하여 얻어지게 되는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 4, wherein the porcelain restoration adhesive
The persimmon extract powder further comprises 0.5 to 2 parts by weight, wherein the persimmon extract powder is dried persimmon peel dried powder immersed in ethanol, maintained at a constant temperature for a certain time, and filtered to remove persimmon powder and filtered Adhesive for restoring porcelain obtained by lyophilizing a liquid.
잘 익은 감보다 덜 익은 풋감이 이용되는 것을 특징으로 하는 도자기 복원용 접착제.The method of claim 9, wherein the persimmon peel
An adhesive for restoring porcelain, in which a less ripe foot is used than a ripe persimmon.