KR101980243B1 - 고 강인성 고 탄성률 초고분자량 폴리에틸렌 섬유 및 그 제조방법 - Google Patents

고 강인성 고 탄성률 초고분자량 폴리에틸렌 섬유 및 그 제조방법 Download PDF

Info

Publication number
KR101980243B1
KR101980243B1 KR1020147023561A KR20147023561A KR101980243B1 KR 101980243 B1 KR101980243 B1 KR 101980243B1 KR 1020147023561 A KR1020147023561 A KR 1020147023561A KR 20147023561 A KR20147023561 A KR 20147023561A KR 101980243 B1 KR101980243 B1 KR 101980243B1
Authority
KR
South Korea
Prior art keywords
yarn
uhmw
polymer
solution
intrinsic viscosity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
KR1020147023561A
Other languages
English (en)
Korean (ko)
Other versions
KR20140129050A (ko
Inventor
토마스 탬
존 암스트롱 영
랄프 클레인
마크 탈렌트
헨리 제라드 아디프
Original Assignee
허니웰 인터내셔널 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 허니웰 인터내셔널 인코포레이티드 filed Critical 허니웰 인터내셔널 인코포레이티드
Publication of KR20140129050A publication Critical patent/KR20140129050A/ko
Application granted granted Critical
Publication of KR101980243B1 publication Critical patent/KR101980243B1/ko
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F6/04—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyolefins
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
    • D02G3/00—Yarns or threads, e.g. fancy yarns; Processes or apparatus for the production thereof, not otherwise provided for
    • D02G3/02—Yarns or threads characterised by the material or by the materials from which they are made
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/58—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives
    • D04H1/593—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives to layered webs
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/70—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres characterised by the method of forming fleeces or layers, e.g. reorientation of fibres
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/06—Wet spinning methods
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H13/00—Other non-woven fabrics
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/02—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins
    • D10B2321/021—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polyethylene
    • D10B2321/0211—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polyethylene high-strength or high-molecular-weight polyethylene, e.g. ultra-high molecular weight polyethylene [UHMWPE]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/298—Physical dimension
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2008—Fabric composed of a fiber or strand which is of specific structural definition

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Artificial Filaments (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
KR1020147023561A 2012-02-24 2013-02-14 고 강인성 고 탄성률 초고분자량 폴리에틸렌 섬유 및 그 제조방법 Active KR101980243B1 (ko)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
US201261602963P 2012-02-24 2012-02-24
US61/602,963 2012-02-24
US13/766,112 2013-02-13
US13/766,112 US9169581B2 (en) 2012-02-24 2013-02-13 High tenacity high modulus UHMW PE fiber and the process of making
PCT/US2013/026124 WO2013126268A1 (en) 2012-02-24 2013-02-14 High tenacity high modulus uhmwpe fiber and the process of making

Publications (2)

Publication Number Publication Date
KR20140129050A KR20140129050A (ko) 2014-11-06
KR101980243B1 true KR101980243B1 (ko) 2019-05-21

Family

ID=49003347

Family Applications (1)

Application Number Title Priority Date Filing Date
KR1020147023561A Active KR101980243B1 (ko) 2012-02-24 2013-02-14 고 강인성 고 탄성률 초고분자량 폴리에틸렌 섬유 및 그 제조방법

Country Status (13)

Country Link
US (3) US9169581B2 (cg-RX-API-DMAC10.html)
EP (1) EP2817440B1 (cg-RX-API-DMAC10.html)
JP (1) JP6392124B2 (cg-RX-API-DMAC10.html)
KR (1) KR101980243B1 (cg-RX-API-DMAC10.html)
CN (1) CN104246036B (cg-RX-API-DMAC10.html)
BR (1) BR112014020344B1 (cg-RX-API-DMAC10.html)
CA (1) CA2864551C (cg-RX-API-DMAC10.html)
ES (1) ES2780364T3 (cg-RX-API-DMAC10.html)
IL (1) IL234117B (cg-RX-API-DMAC10.html)
IN (1) IN2014DN06759A (cg-RX-API-DMAC10.html)
MX (1) MX347676B (cg-RX-API-DMAC10.html)
RU (1) RU2612714C2 (cg-RX-API-DMAC10.html)
WO (1) WO2013126268A1 (cg-RX-API-DMAC10.html)

Families Citing this family (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USRE50459E1 (en) 2011-12-14 2025-06-17 Avient Protective Materials B.V. Ultra high molecular weight polyethylene multifilament yarn
US9169581B2 (en) * 2012-02-24 2015-10-27 Honeywell International Inc. High tenacity high modulus UHMW PE fiber and the process of making
JP6436091B2 (ja) * 2012-12-20 2018-12-12 東洋紡株式会社 ポリオレフィン糸条及び製造方法
BR122020002315B1 (pt) * 2013-10-29 2021-06-15 Braskem S.A. Método e sistema de pré-recuperação mecânica de pelo menos um líquido em pelo menos um fio polimérico
US20150164158A1 (en) * 2013-12-13 2015-06-18 Honeywell International Inc. Protective overglove for glove-box gloves
WO2015125064A1 (en) * 2014-02-20 2015-08-27 Reliance Industries Limited High strength and high modulus ultra-high molecular weight polyethylene fibers
KR102224261B1 (ko) * 2014-03-28 2021-03-05 도요보 가부시키가이샤 멀티필라멘트 및 끈목
CN106164347A (zh) * 2014-03-28 2016-11-23 东洋纺株式会社 复丝及编带
US9816211B2 (en) * 2014-10-29 2017-11-14 Honeywell International Inc. Optimized braid construction
US9834872B2 (en) 2014-10-29 2017-12-05 Honeywell International Inc. High strength small diameter fishing line
BR112017011660B1 (pt) 2014-12-02 2021-10-19 Braskem S.A. Método e sistema contínuo para a produção de pelo menos um fio polimérico, fio polimérico, e, uso de um fio polimérico
US20160174616A1 (en) * 2014-12-18 2016-06-23 Adidas Ag Athletic jersey with cut-resistant portion
WO2016133102A1 (ja) 2015-02-20 2016-08-25 東洋紡株式会社 マルチフィラメント及びそれを用いた組紐
US20170145596A1 (en) * 2015-10-27 2017-05-25 Tosha Hays Systems and articles of manufacture employing long-term cooling material in woven and non-woven fabrics and processes to generate the long-term cooling material and articles of manufacture
CA3109972C (en) 2016-03-04 2023-12-12 Bauer Hockey Ltd. 3d weaving material and method of 3d weaving for sporting implements
US11471736B2 (en) 2016-03-04 2022-10-18 Bauer Hockey, Llc 3D braiding materials and 3D braiding methods for sporting implements
US10704866B2 (en) 2016-09-15 2020-07-07 Honeywell International Inc. High kinetic energy absorption with low back face deformation ballistic composites
CN107988632B (zh) * 2017-11-24 2020-04-24 龙游龙纤新材料有限公司 一种实现连续均匀喂料的uhmwpe纤维生产配料方法
US11306432B2 (en) * 2018-11-05 2022-04-19 Honeywell International Inc. HMPE fiber with improved bending fatigue performance
CZ2018647A3 (cs) * 2018-11-23 2020-06-03 Reifenhäuser GmbH & Co. KG Maschinenfabrik Objemná netkaná textilie se zvýšenou stlačitelností a zlepšenou schopností regenerace
EP3921589B1 (en) * 2019-02-06 2025-07-09 Barrday Corporation Ballistic-resistant composite with blocked isocyanate
MY206320A (en) 2019-12-27 2024-12-09 Kolon Inc Polyethylene yarn, method for manufacturing the same, and skin cooling fabric comprising the same
US20210321700A1 (en) * 2020-04-15 2021-10-21 Chris TREVINO Protective Glove
RU2734546C1 (ru) * 2020-04-16 2020-10-20 Роман Валерьевич Платонов Ткань трикотажная для использования при самообороне в боевых контактах и искусствах
CN114481343A (zh) * 2020-10-23 2022-05-13 中国石油化工股份有限公司 一种纤维纺丝方法和聚乙烯纺丝纤维
CN118201769A (zh) 2021-11-10 2024-06-14 杜邦安全与建筑公司 由不含非织造纤维的机械缠结的织造织物制成的防弹材料及其制造方法
US20230193518A1 (en) * 2021-12-17 2023-06-22 Honeywell International Inc. Ultra-fine denier uhmw pe fiber
CN117802607A (zh) * 2022-09-30 2024-04-02 中国石油化工股份有限公司 纺丝用超高分子量聚乙烯组合物、超高分子量聚乙烯纤维及其制备方法与应用
KR102506254B1 (ko) 2022-10-28 2023-03-07 (주)유원기술 공기청정기능 및 환기기능을 구현하는 냉방제습기

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006045755A (ja) * 2004-07-08 2006-02-16 Toyobo Co Ltd 高強度ポリエチレン繊維
WO2011076914A1 (en) * 2009-12-23 2011-06-30 Teijin Aramid B.V. Ballistic-resistant articles

Family Cites Families (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4413110A (en) 1981-04-30 1983-11-01 Allied Corporation High tenacity, high modulus polyethylene and polypropylene fibers and intermediates therefore
US4457985A (en) 1982-03-19 1984-07-03 Allied Corporation Ballistic-resistant article
US4403012A (en) 1982-03-19 1983-09-06 Allied Corporation Ballistic-resistant article
US4536536A (en) 1982-03-19 1985-08-20 Allied Corporation High tenacity, high modulus polyethylene and polypropylene fibers and intermediates therefore
US4551296A (en) 1982-03-19 1985-11-05 Allied Corporation Producing high tenacity, high modulus crystalline article such as fiber or film
US4440711A (en) * 1982-09-30 1984-04-03 Allied Corporation Method of preparing high strength and modulus polyvinyl alcohol fibers
JPS59216912A (ja) 1983-05-20 1984-12-07 Toyobo Co Ltd 高強度・高弾性率ポリエチレン繊維の製造方法
US4663101A (en) 1985-01-11 1987-05-05 Allied Corporation Shaped polyethylene articles of intermediate molecular weight and high modulus
US4623574A (en) 1985-01-14 1986-11-18 Allied Corporation Ballistic-resistant composite article
US4748064A (en) 1985-01-14 1988-05-31 Allied Corporation Ballistic-resistant composite article
JPH06102847B2 (ja) * 1985-05-31 1994-12-14 三井石油化学工業株式会社 プラスチツクワイヤ−及びその製造方法
US4650710A (en) 1985-02-25 1987-03-17 Allied Corporation Ballistic-resistant fabric article
US4737402A (en) 1985-02-28 1988-04-12 Allied Corporation Complex composite article having improved impact resistance
JPS61282417A (ja) * 1985-06-05 1986-12-12 Toray Ind Inc ポリエチレンマルチフイラメントヤ−ン
EP0205960B1 (en) 1985-06-17 1990-10-24 AlliedSignal Inc. Very low creep, ultra high moduls, low shrink, high tenacity polyolefin fiber having good strength retention at high temperatures and method to produce such fiber
US5032338A (en) 1985-08-19 1991-07-16 Allied-Signal Inc. Method to prepare high strength ultrahigh molecular weight polyolefin articles by dissolving particles and shaping the solution
US4916000A (en) 1987-07-13 1990-04-10 Allied-Signal Inc. Ballistic-resistant composite article
US5552208A (en) 1993-10-29 1996-09-03 Alliedsignal Inc. High strength composite
JP2699319B2 (ja) 1993-12-16 1998-01-19 東洋紡績株式会社 高強度ポリエチレン繊維
US6448359B1 (en) 2000-03-27 2002-09-10 Honeywell International Inc. High tenacity, high modulus filament
US6642159B1 (en) 2000-08-16 2003-11-04 Honeywell International Inc. Impact resistant rigid composite and method for manufacture
US6846758B2 (en) 2002-04-19 2005-01-25 Honeywell International Inc. Ballistic fabric laminates
US6841492B2 (en) 2002-06-07 2005-01-11 Honeywell International Inc. Bi-directional and multi-axial fabrics and fabric composites
US7344668B2 (en) 2003-10-31 2008-03-18 Honeywell International Inc. Process for drawing gel-spun polyethylene yarns
US6969553B1 (en) 2004-09-03 2005-11-29 Honeywell International Inc. Drawn gel-spun polyethylene yarns and process for drawing
DE602005023231D1 (de) * 2004-09-03 2010-10-07 Honeywell Int Inc Polyethylengarne
US7147807B2 (en) 2005-01-03 2006-12-12 Honeywell International Inc. Solution spinning of UHMW poly (alpha-olefin) with recovery and recycling of volatile spinning solvent
EP1746187A1 (en) * 2005-07-18 2007-01-24 DSM IP Assets B.V. Polyethylene multi-filament yarn
US7370395B2 (en) 2005-12-20 2008-05-13 Honeywell International Inc. Heating apparatus and process for drawing polyolefin fibers
US8444898B2 (en) 2006-03-30 2013-05-21 Honeywell International Inc High molecular weight poly(alpha-olefin) solutions and articles made therefrom
US7674409B1 (en) * 2006-09-25 2010-03-09 Honeywell International Inc. Process for making uniform high strength yarns and fibrous sheets
JP2010525184A (ja) * 2007-05-01 2010-07-22 ディーエスエム アイピー アセッツ ビー．ブイ． Ｕｈｍｗｐｅ繊維およびその製造方法
BRPI0702313A2 (pt) * 2007-05-24 2009-01-13 Profil Ltda Braskem S A processo para a preparaÇço de fios polimÉricos a partir de homopolÍmeros ou copolimeros de ultra alto peso molecular, fios polimÉricos, artigos polimÉricos moldados, e, uso de fios polimÉricos
US7638191B2 (en) 2007-06-08 2009-12-29 Honeywell International Inc. High tenacity polyethylene yarn
US9365953B2 (en) 2007-06-08 2016-06-14 Honeywell International Inc. Ultra-high strength UHMWPE fibers and products
US8889049B2 (en) 2010-04-30 2014-11-18 Honeywell International Inc Process and product of high strength UHMW PE fibers
US8747715B2 (en) 2007-06-08 2014-06-10 Honeywell International Inc Ultra-high strength UHMW PE fibers and products
US9005753B2 (en) 2007-10-05 2015-04-14 Dsm Ip Assets B.V. Fibers of UHMWPE and a process for producing thereof
BRPI0820787A2 (pt) 2007-12-17 2015-06-16 Dsm Ip Assets Bv Processo de fiação de peuapm, fios de múltiplos filamentos de peuapm produzidos e o seu uso
CN101230499B (zh) 2008-02-26 2010-10-06 山东爱地高分子材料有限公司 一种有颜色的高强聚乙烯纤维及其制造方法
CN101230501B (zh) * 2008-02-26 2010-06-02 山东爱地高分子材料有限公司 一种采用超高分子量聚乙烯与低密度聚乙烯共混熔融制备高强聚乙烯纤维的方法
CN102308035A (zh) * 2009-02-09 2012-01-04 帝斯曼知识产权资产管理有限公司 耐切割的复合纱线
LT2462275T (lt) 2009-08-04 2016-10-10 Dsm Ip Assets B.V. Padengti aukšto stiprumo pluoštas, gijos ir lynai bei jų gamybos būdas
US8236119B2 (en) * 2009-08-11 2012-08-07 Honeywell International Inc. High strength ultra-high molecular weight polyethylene tape articles
US9169581B2 (en) * 2012-02-24 2015-10-27 Honeywell International Inc. High tenacity high modulus UHMW PE fiber and the process of making

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006045755A (ja) * 2004-07-08 2006-02-16 Toyobo Co Ltd 高強度ポリエチレン繊維
WO2011076914A1 (en) * 2009-12-23 2011-06-30 Teijin Aramid B.V. Ballistic-resistant articles

Also Published As

Publication number Publication date
BR112014020344A2 (pt) 2017-06-20
US9169581B2 (en) 2015-10-27
KR20140129050A (ko) 2014-11-06
US9765447B2 (en) 2017-09-19
CA2864551C (en) 2020-03-10
JP6392124B2 (ja) 2018-09-19
WO2013126268A1 (en) 2013-08-29
ES2780364T3 (es) 2020-08-25
EP2817440B1 (en) 2020-01-01
CA2864551A1 (en) 2013-08-29
JP2015508849A (ja) 2015-03-23
US20180016710A1 (en) 2018-01-18
BR112014020344B1 (pt) 2021-09-21
EP2817440A4 (en) 2016-01-06
CN104246036A (zh) 2014-12-24
RU2014137552A (ru) 2016-04-10
CN104246036B (zh) 2017-03-08
MX2014009998A (es) 2014-09-12
RU2612714C2 (ru) 2017-03-13
MX347676B (es) 2017-05-09
EP2817440A1 (en) 2014-12-31
IL234117B (en) 2018-12-31
IN2014DN06759A (cg-RX-API-DMAC10.html) 2015-05-22
US20160130730A1 (en) 2016-05-12
US20130225022A1 (en) 2013-08-29
US10450676B2 (en) 2019-10-22

Similar Documents

Publication Publication Date Title
KR20140129050A (ko) 고 강인성 고 탄성률 초고분자량 폴리에틸렌 섬유 및 그 제조방법
CN103608502B (zh) 超高强度uhmw pe纤维和产品
CN102933758B (zh) 增强的防弹性能的聚合物纤维
TWI602962B (zh) 混合纖維單向帶及複合層合物
CN100503908C (zh) 用于制造高性能聚乙烯多丝纱的方法
US9631898B2 (en) Protective helmets
CN103998661B (zh) 超高分子量聚乙烯复丝纱线
KR101979238B1 (ko) 고성능 라미네이티드 테이프 및 탄도 적용 관련 제품
EP0397696A1 (en) COMPOSITE ARTICLE RESISTANT TO PROJECTILES.

Legal Events

Date Code Title Description
PA0105 International application

Patent event date: 20140822

Patent event code: PA01051R01D

Comment text: International Patent Application

PG1501 Laying open of application
A201 Request for examination
PA0201 Request for examination

Patent event code: PA02012R01D

Patent event date: 20180212

Comment text: Request for Examination of Application

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

Comment text: Notification of reason for refusal

Patent event date: 20181022

Patent event code: PE09021S01D

E701 Decision to grant or registration of patent right
PE0701 Decision of registration

Patent event code: PE07011S01D

Comment text: Decision to Grant Registration

Patent event date: 20190410

GRNT Written decision to grant
PR0701 Registration of establishment

Comment text: Registration of Establishment

Patent event date: 20190514

Patent event code: PR07011E01D

PR1002 Payment of registration fee

Payment date: 20190515

End annual number: 3

Start annual number: 1

PG1601 Publication of registration
FPAY Annual fee payment

Payment date: 20220503

Year of fee payment: 4

PR1001 Payment of annual fee

Payment date: 20220503

Start annual number: 4

End annual number: 4