A resin composition comprising a metal foil and a layer of a resin composition formed on at least one side of the metal foil without interposing an adhesive layer, the layer of the resin composition comprising a polyester resin (A) and a water-soluble resin (B) Wherein the content of the polyester resin (A) in the layer of the composition is 40 parts by mass or more and 70 parts by mass or less based on 100 parts by mass in total of the polyester resin (A) and the water-soluble resin (B) Wherein the polyester resin (A) is a copolymer containing a tricarboxylic acid-derived structural unit and a polyol-derived structural unit.

Description

Drill hole entry sheet, and drill drilling method using same

The present invention relates to an entry sheet for a drill hole used in a drilling process of a laminated plate or a multilayer plate, and a drill drilling method using the same.

As a method for drilling a laminated board or a multilayer board used for a printed wiring board material, generally, a laminate or a multilayer board is generally laminated one on top of the other, and an uppermost portion of the laminate board is laminated on an aluminum foil or aluminum foil There has been adopted a method in which a sheet on which a layer of a resin composition is formed (hereinafter referred to as " sheet " in the present specification is referred to as " drill hole entry sheet ") is subjected to drilling.

In recent years, with the demand for improvement of the reliability of the printed wiring board and the progress of high density, drilling of a laminated board or a multilayer board is required to drill high quality drills such as improvement of hole position accuracy and reduction of hole wall roughness have.

For example, in the patent document 1, a perforating process using a sheet made of a water-soluble resin such as polyethylene glycol has been proposed in order to cope with the above-described demand for improvement in hole position accuracy and reduction in hole wall roughness. Patent Document 2 proposes a perforated liner sheet in which a water-soluble resin layer is formed on a metal foil. Patent Document 3 proposes a perforated entry sheet in which a water-soluble resin layer is formed on an aluminum foil on which a thin film of a thermosetting resin is formed. Further, Patent Document 4 proposes a perforated liner sheet in which a lubricant resin composition is mixed with a non-halogen colorant.

As one form of the drill hole common entry sheet, there has been proposed a form comprising a metal foil and a layer of a resin composition formed on at least one side of the metal foil. However, in the structure of the drill hole entry sheet in which the metal foil and the layer of the resin composition are directly in contact with each other, the layer of the metal foil and the resin composition has weak adhesive strength, and the layer of the resin composition is peeled off during drilling, The layer of the resin composition was stepped on the drill, leading to deterioration of hole position accuracy and deterioration of frequency of breakage of the drill. The drill hole common entry sheet is usually disposed on both sides of a plurality of laminated plates or multilayer boards and is used as a set of fixing tapes for drilling. However, the fixing tape is peeled together with the resin composition layer, The position of the sheet may be shifted. Practically, for the purpose of improving the bonding strength between the metal foil and the layer of the resin composition, a urethane compound, a vinyl acetate compound, a vinyl chloride compound, a polyester compound and / (Adhesive film) composed of a polymer, an epoxy compound, a cyanate compound, or the like is formed on the surface of the substrate (see, for example, Patent Document 5).

Japanese Patent Application Laid-Open No. 4-92494 Japanese Patent Application Laid-Open No. 5-169400 Japanese Patent Application Laid-Open No. 2003-136485 Japanese Laid-Open Patent Publication No. 2004-230470 Japanese Laid-Open Patent Publication No. 2011-183548

On the other hand, when the adhesive layer is formed between the metal foil and the resin composition layer, the adhesive layer interferes with the lubrication effect of the resin composition, so that the hole position accuracy, which is an important characteristic required for the drill hole entry sheet, has been deteriorated. Therefore, there is a desperate need to develop an entry sheet for a drill hole having a high bonding strength between the metal foil and the resin composition layer without forming an adhesive layer between the metal foil and the layer of the resin composition, and having excellent hole position accuracy.

SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and an object of the present invention is to provide an entry sheet comprising a metal foil and a layer of a resin composition formed on at least one surface of the metal foil without an adhesive layer interposed therebetween, It is an object of the present invention to provide an entry sheet for a drill hole having a high adhesion strength between a metal foil and a layer of a resin composition even when the adhesive layer is not present, .

DISCLOSURE OF THE INVENTION As a result of various investigations to solve the above problems, the present inventors have found that a resin composition containing a metal foil and a polyester resin (A) and a water-soluble resin (B) formed on at least one surface of the metal foil without interposing an adhesive layer Wherein the content of the polyester resin (A) in the layer of the resin composition is within a specific range, and the content of the polyester resin (A) And that the drill hole common entry sheet, which is a copolymer containing the derived constituent unit, can solve the above problems, and has completed the present invention.

That is, the present invention is as follows.

[One]

A metal foil comprising a metal foil and a layer of a resin composition formed on at least one side of the metal foil without interposing an adhesive layer,

The layer of the resin composition contains a polyester resin (A) and a water-soluble resin (B)

The content of the polyester resin (A) in the layer of the resin composition is 40 parts by mass or more and 70 parts by mass or less based on 100 parts by mass in total of the polyester resin (A) and the water-soluble resin (B) ,

Wherein the polyester resin (A) is a copolymer comprising a tricarboxylic acid-derived structural unit and a polyol-derived structural unit,

Drill cloth entry sheet.

[2]

Wherein the content of the water-soluble resin (B) in the layer of the resin composition is 30 parts by mass or more and 60 parts by mass or less based on 100 parts by mass in total of the polyester resin (A) and the water-soluble resin (B)

The drill hole entry sheet described in [1].

[3]

Wherein the tricarboxylic acid is trimellitic acid,

The drill hole entry sheet according to [1] or [2].

[4]

Wherein the polyester resin (A) has a structural unit represented by the following general formula (1)

The drill hole entry sheet described in [3].

[Chemical Formula 1]

(In the formula (1), each R independently represents a -CH ₂ -CH ₂ -O-CH ₂ -CH ₂ - group or a - (CH ₂ ) ₆ - group, and n is an integer of 1 or more .

[5]

Based on the total amount of 100 mol% of the molar number of the tricarboxylic acid-derived structural unit and the molar amount of the structural unit derived from the polyol,

Wherein the molar ratio of the tricarboxylic acid-derived structural unit is 40 to 80 mol%

Wherein the molar ratio of the polyol-derived structural unit is 20 to 60 mol%

The drill hole entry sheet according to any one of [1] to [4].

[6]

Wherein the polyester resin (A) has a number average molecular weight of 5,000 or more and 50,000 or less,

The drill hole entry sheet according to any one of [1] to [5].

[7]

Wherein the water-soluble resin (B) is at least one selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinyl pyrrolidone, cellulose derivatives, polyethylene glycol, polypropylene glycol, polytetramethylene glycol, polyoxyethylene monoether compounds, polyoxyethylene monostearate , Polyoxyethylene sorbitan monostearate, polyglycerin monostearate compound, polyethylene oxide-polypropylene oxide copolymer, and derivatives thereof.

The drill hole entry sheet according to any one of [1] to [6].

[8]

Soluble resin (b1) having a weight average molecular weight of 50,000 or more and 1,500,000 or less and a low-molecular water-soluble resin (b2) having a weight-average molecular weight of 1,000 or more and 30,000 or less,

Wherein the polymeric water-soluble resin (b1) contains at least one member selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinylpyrrolidone, and cellulose derivatives,

Wherein the low-molecular water-soluble resin (b2) is selected from the group consisting of polyethylene glycol, polypropylene glycol, polytetramethylene glycol, polyoxyethylene monoether compounds, polyoxyethylene monostearate, polyoxyethylene sorbitan monostearate, polyethylene oxide- Oxide copolymers, and derivatives thereof, and at least one compound selected from the group consisting of

The drill hole entry sheet described in [7].

[9]

Wherein the thickness of the layer of the resin composition is 0.02 to 0.3 mm,

The drill hole entry sheet according to any one of [1] to [8].

[10]

Wherein the metal foil has a thickness of 0.05 mm to 0.5 mm,

The drill hole entry sheet according to any one of [1] to [9].

[11]

A drill hole entry sheet as described in any one of [1] to [10], wherein the drill hole entry sheet has a hole forming step of forming holes in a laminated plate or a multilayer plate,

Drill drilling method.

According to the present invention, there is provided an entry sheet for a drill hole in the form of a metal foil and a layer of a resin composition formed on at least one side of the metal foil without interposing an adhesive layer between the metal foil and the resin composition layer, It is possible to provide an entry sheet for a drill hole having a strong adhesive strength to a layer of a metal foil and a resin composition, and moreover, an hole position accuracy at drilling processing, and a drilling processing method using the same. Further, an entry sheet for a drill hole without an adhesive layer is economical in terms of both the raw material and the manufacturing process of the entry sheet.

Hereinafter, a mode for carrying out the present embodiment (hereinafter referred to as " present embodiment ") will be described in detail, but the present embodiment is not limited to this, and various modifications This is possible.

[I: drill hole common entry sheet]

The drill hole entry sheet of the present embodiment comprises a metal foil and a layer of a resin composition formed on at least one side of the metal foil without interposing an adhesive layer, Wherein the content of the polyester resin (A) in the resin composition layer is 100 parts by mass or less per 100 parts by mass of the total of the polyester resin (A) and the water-soluble resin (B) Is 40 parts by mass or more and 70 parts by mass or less, and the polyester resin (A) is a copolymer containing a tricarboxylic acid-derived structural unit and a polyol-derived structural unit.

The drill hole entry sheet of the present embodiment comprises a metal foil and a layer of a resin composition formed on the metal foil without interposing an adhesive layer therebetween. That is, the metal foil does not have an adhesive layer (resin coating or the like) for bonding the metal foil and the resin composition between the metal foil and the resin composition layer, and the metal foil and the resin composition layer are in direct contact with each other. Wherein the layer of the resin composition contains the polyester resin (A) and the water-soluble resin (B), the content of the polyester resin (A) in the resin composition layer is in the above- ) Is a copolymer containing a tricarboxylic acid-derived structural unit having three or more carboxyl groups in the molecule and a structural unit derived from a polyol so that the metal foil and the resin composition The strength of the adhesive strength of the layer of the drill hole is high and the hole position accuracy at drilling is excellent.

Since the drill hole entry sheet according to the present embodiment does not require an adhesive layer to be interposed, it is possible to suppress the raw material cost and omit the step of forming the adhesive layer. Thus, compared with the conventional drill hole entry sheet, great. The layer of the resin composition may be formed on one surface of the metal foil or on both surfaces thereof. When a layer of the resin composition is formed on both sides, the composition of the resin composition of the layer may be the same or different.

[II: Polyester resin (A)]

The polyester resin (A) is a copolymer containing a tricarboxylic acid-derived constituent unit and a polyol-derived constituent unit. The copolymer is not particularly limited as long as it is a copolymer containing a tricarboxylic acid-derived structural unit and a polyol-derived structural unit as components.

"Tricarboxylic acid-derived constituent unit" refers to a constituent unit (skeleton) in a polymer derived from a tricarboxylic acid, which is used as a raw material for a polymerization reaction when a polymer is used, and "constituent unit derived from a polyol" Refers to a structural unit (skeleton) in a polymer derived from a polyol used as a raw material for a polymerization reaction when a polymer is used. That is, a copolymer containing a tricarboxylic acid-derived constituent unit and a polyol-derived constituent unit is composed of at least a tricarboxylic acid-containing structural unit derived from a tricarboxylic acid and a structural unit derived from a polyol To give a polyol. In other words, it is a copolymer having a plurality of carboxyl groups as side chains.

Since the polyester resin (A) is a copolymer containing a constituent unit derived from a tricarboxylic acid and a constituent unit derived from a polyol, the drill hole entry sheet according to the present embodiment is characterized in that the adhesive strength between the metal foil and the resin composition layer is And there is a tendency that hole position accuracy in drilling processing is excellent. The reason is described below, but the present invention is not limited thereto. The carboxyl group has a relatively strong interaction with the surface of the metal. Therefore, the copolymer constituting the polyester resin (A) contained in the resin composition layer contains a tricarboxylic acid-derived structural unit, so that the bonding strength between the metal foil and the resin composition layer becomes strong. Further, by containing the tricarboxylic acid-derived constituent unit, the core-forming property to the drill bit can be further improved and the cutting debris generated at the time of machining can be efficiently discharged, It is considered that the hole position accuracy at the time of processing is excellent. On the other hand, when a polycarboxylic acid having four or more carboxyl groups in the molecule is used, the structure of the obtained polyester resin (A) becomes rigid and low in flexibility, and the bonding strength between the metal foil and the layer of the resin composition is lowered. Further, since the copolymer contains a constituent unit derived from a polyol, the layer of the resin composition can exhibit lubricity. It is also considered that the hole position accuracy at the time of drilling is excellent. In the present embodiment, " centrifugal " refers to a property (force) toward the rotation center when the drill bit rotates.

The tricarboxylic acid giving the tricarboxylic acid-derived constituent unit is not particularly limited as long as it is an organic compound having three carboxyl groups (COOH groups) in the molecule, and may be a monomer or a polymer. Examples of such compounds include, but are not limited to, trimellitic acid, 2,5,7-naphthalenetricarboxylic acid, 1,2,4-naphthalenetricarboxylic acid, 1,2,4- Carboxylic acid, 1,2,5-hexanetricarboxylic acid, 1,3-dicarboxyl-2-methyl-2-methylenecarboxypropane and 1,2,4-cyclohexanetricarboxylic acid . Among them, trimellitic acid is preferable. These tricarboxylic acids may be used singly or in combination of two or more.

The polyol to which the polyol-derived constituent unit is added is not particularly limited as long as it is an organic compound having two or more hydroxyl groups (OH groups) in the molecule, and may be a monomer or a polymer. Examples of such compounds include, but are not limited to, ethylene glycol, diethylene glycol, 1,3-propanediol, 1,2-propanediol, triethylene glycol, 2- Propane diol, 1,4-butanediol, 2-methyl-1,4-butanediol, 2-methyl-3- Methyl-1,4-butanediol, 3-methyl-1,5-pentanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol and 1,6-hexanediol. Among them, ethylene glycol, diethylene glycol, 1,4-butanediol and 1,6-hexanediol are preferable, and diethylene glycol and 1,6-hexanediol are particularly preferable. These polyols may be used singly or in combination of two or more.

Based on the total of 100 mol% of the molar number of the tricarboxylic acid-derived constituent unit and the molar amount of the constituent unit derived from the polyol in the copolymer containing the tricarboxylic acid-derived constituent unit and the polyol-derived constituent unit, The molar ratio of the carboxylic acid-derived structural units is preferably 40 to 80 mol%, more preferably 45 to 75 mol%, still more preferably 50 to 70 mol%, still more preferably 55 to 70 mol% 70 mol%, and still more preferably 55 mol% to 65 mol%. The molar ratio of the polyol-derived constituent unit to the total of 100 mol% of the molar number of the tricarboxylic acid-derived constituent unit and the molar number of the constituent unit derived from the polyol is preferably 20 to 60 mol% Is 25 to 55 mol%, more preferably 30 to 50 mol%, still more preferably 30 to 45 mol%, and still more preferably 35 to 45 mol%. When the molar ratio of the tricarboxylic acid-derived structural unit is 40 mol% or more, the bonding strength between the layer of the resin composition and the metal foil is further improved, and the layer of the resin composition is not easily peeled off during drilling processing, Tends to be better. On the other hand, when the molar ratio of the polyol-derived structural units is 20 mol% or more, the layer of the resin composition is efficiently melted during the drilling process, so that the dischargeability of the cutting chips generated by the processing is good, Good and / or drilling process life tends to be prolonged.

The total number of moles of the constituent unit derived from the tricarboxylic acid and the constituent unit derived from the polyol is preferably 95 to 100 mol% based on the total 100 mol% of the total molar amounts of the constituent units constituting the polyester resin (A) , And more preferably 97 to 100 mol%.

The copolymer containing a tricarboxylic acid-derived constituent unit and a polyol-derived constituent unit may be copolymerized with a constitutional unit derived from a tricarboxylic acid and a constitutional unit other than the polyol-derived constitutional unit (hereinafter, May also be referred to as " other constituent units "). That is, a copolymer containing a tricarboxylic acid-derived constituent unit and a polyol-derived constituent unit is preferably a copolymer comprising a tricarboxylic acid which gives a tricarboxylic acid-derived constituent unit and a polyol- Or a copolymer obtained by a copolymerization reaction of a polyol and a compound giving another structural unit, if necessary.

The other constitutional unit is not particularly limited, and examples thereof include oxalic acid, succinic acid, adipic acid, pimelic acid, sebacic acid, 1,2,4-butanetricarboxylic acid, 1,2,5- Tricarboxylic acid, 1,3-dicarboxyl-2-methyl-2-methylenecarboxypropane, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, A structural unit derived from a polycarboxylic acid other than a tricarboxylic acid such as hexanedicarboxylic acid, pyromellitic acid, tetra (methylenecarboxyl) methane, and 1,2,7,8-octatetracarboxylic acid; Structural units derived from olefin such as ethylene, propylene, 1-butene, 2-butene, 1,3-butadiene, 1-pentene, 3-pentene, 1,3-pentadiene and 1,5-pentadiene; And structural units derived from unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic acid, and fumaric acid.

In the copolymer containing a tricarboxylic acid-derived constituent unit, a polyol-derived constituent unit and other constituent units, the combination of these constituent units is not particularly limited. As the polyester resin (A), a copolymer containing a tricarboxylic acid-derived constituent unit, a polyol-derived constituent unit and, if necessary, another constituent unit may be used singly, Two or more types may be used in combination.

The molar ratio of the other constituent units to the total of 100 mol% of the molar number of the tricarboxylic acid-derived constituent unit, the molar number of the constituent unit derived from the polyol and the molar amount of the other constituent unit is preferably 0 to 5 mol% , More preferably 0 to 3 mol%.

In the present embodiment, the polyester resin (A) is preferably a copolymer composed of a tricarboxylic acid-derived structural unit and a polyol-derived structural unit. If the polyester resin (A) is a copolymer comprising a constituent unit derived from a tricarboxylic acid and a constituent unit derived from a polyol, the drill hole entry sheet according to the present embodiment is characterized in that the adhesive strength between the metal foil and the resin composition layer is The drill bits have a good aperturbability and the cutting debris generated at the time of machining can be efficiently discharged, so that the hole position accuracy at the time of drilling is better.

The copolymer composed of a tricarboxylic acid-derived constituent unit and a polyol-derived constituent unit is not particularly limited and includes, for example, a tricarboxylic acid giving the tricarboxylic acid-derived constituent unit described above, And a copolymer obtained by copolymerization reaction of a polyol which gives a constituent unit derived from one polyol. In the copolymer comprising a tricarboxylic acid-derived structural unit and a polyol-derived structural unit, the combination of the tricarboxylic acid-derived structural unit and the polyol-derived structural unit is not particularly limited. As the polyester resin (A), a copolymer comprising a tricarboxylic acid-derived structural unit and a polyol-derived structural unit may be used alone or in combination of two or more.

Based on the total amount of 100 mol% of the molar number of the tricarboxylic acid-derived constituent unit and the molar amount of the constituent unit derived from the polyol in the copolymer comprising the tricarboxylic acid-derived constituent unit and the polyol-derived constituent unit, The molar ratio of the acid-derived constituent units is preferably 40 to 80 mol%, more preferably 45 to 75 mol%, still more preferably 50 to 70 mol%, still more preferably 55 to 70 mol% %, And still more preferably from 55 to 65 mol%. The molar ratio of the polyol-derived constituent unit to the total of 100 mol% of the molar number of the tricarboxylic acid-derived constituent unit and the molar number of the constituent unit derived from the polyol is preferably 20 to 60 mol% Is 25 to 55 mol%, more preferably 30 to 50 mol%, still more preferably 30 to 45 mol%, and still more preferably 35 to 45 mol%. When the molar ratio of the tricarboxylic acid-derived structural unit is 40 mol% or more, the bonding strength between the layer of the resin composition and the metal foil is further improved, and the layer of the resin composition is not easily peeled off during drilling processing, Tends to be better. On the other hand, when the molar ratio of the polyol-derived structural units is 20 mol% or more, the layer of the resin composition is efficiently melted during the drilling process, so that the dischargeability of the cutting chips generated by the processing is good, Good and / or drilling process life tends to be prolonged.

In the present embodiment, the polyester resin (A) is a copolymer composed of the constituent unit derived from the above-mentioned tricarboxylic acid and the constituent unit derived from the polyol, the constituent unit derived from trimellitic acid and the constituent unit derived from polyol , That is, a trimellitic acid-polyol copolymer.

The trimellitic acid-polyol copolymer is not particularly limited and, for example, a copolymer obtained by a copolymerization reaction of a trimellitic acid with a polyol imparting the aforementioned structural unit derived from a polyol. Among them, one kind selected from the group consisting of trimellitic acid-diethylene glycol copolymer, trimellitic acid-1,6-hexanediol copolymer, trimellitic acid-diethylene glycol-1,6-hexanediol copolymer Or two or more kinds are preferable. These copolymers may be used alone or in combination of two or more. If the polyester resin (A) is a copolymer of these, the drill hole entry sheet of the present embodiment is advantageous in that the adhesion strength between the metal foil and the resin composition layer is stronger and the percibility of the drill bit is good, It is possible to efficiently discharge the cutting chips. Therefore, the accuracy of the hole position at the time of drilling processing tends to be better.

In the trimellitic acid-polyol copolymer, the molar ratio of trimellitic acid-derived structural units to the total of 100 mol% of the molar number of the trimellitic acid-derived structural units and the polyol-derived structural units is preferably 40 To 80 mol%, more preferably 45 mol% to 75 mol%, still more preferably 50 mol% to 70 mol%, still more preferably 55 mol% to 70 mol%, and still more preferably 55 mol% to 65 mol% . The molar ratio of the polyol-derived structural units to the total amount of 100 mol% of the number of moles of the trimellitic acid-derived structural units and the number of the structural units derived from the polyol is preferably 20 to 60 mol% Is 25 to 55 mol%, more preferably 30 to 50 mol%, still more preferably 30 to 45 mol%, and still more preferably 35 to 45 mol%. Since the molar ratio of the constituent units derived from trimellitic acid is 40 mol% or more, the bonding strength between the layer of the resin composition and the metal foil is further improved, and the layer of the resin composition is not easily peeled off during drilling processing, There is an excellent tendency. On the other hand, when the ratio of the number of moles of the polyol-derived constituent units is 20 mol% or more, the layer of the resin composition is efficiently melted at the time of drilling, so that the dischargeability of cutting debris generated by the processing is good, And / or the drilling process life tends to be prolonged. In particular, the molar ratio of the trimellitic acid-derived structural unit in the trimellitic acid-polyol copolymer is 55 to 70 mol% and the molar ratio of the polyol-derived structural unit is 30 to 45 mol% The accuracy tends to be more excellent.

In the present embodiment, the polyester resin (A) is a copolymer of trimellitic acid-diethylene glycol copolymer, trimellitic acid-1,6-hexanediol copolymer, trimellitic acid-diethylene glycol- Hexanediol copolymer preferably contains a copolymer having a structural unit represented by the following general formula (1). By using such a polyester resin (A), the adhesive strength between the metal foil and the layer of the resin composition of the drill hole entry sheet of the present embodiment is stronger, the perforation of the drill bit is good, and the The cutting chips can be discharged more efficiently, so that the hole position accuracy at drilling processing tends to be better.

(2)

(In the formula (1), each independently, R represents -CH ₂ -CH ₂ -O-CH ₂ -CH ₂ - group or - (CH ₂ ) ₆ group, and n represents an integer of 1 or more.

In the trimellitic acid-polyol copolymer having the structure of the general formula (1), R is each independently -CH ₂ -CH ₂ -O-CH ₂ -CH ₂ - group or - (CH ₂ ) ₆ - is a group. n is an integer of 1 or more, preferably 18 or more. The upper limit of n is not particularly limited, but is preferably 188 or less. As the polyester resin (A), two or more trimellitic acid-polyol copolymers differing in R and n may be contained.

When the polyester resin (A) is a trimellitic acid-polyol copolymer represented by the general formula (1), the ratio of the constitutional unit derived from trimellitic acid to the constitutional unit derived from polyol is not particularly limited, but trimellitic acid- Derived from the polyol is preferably in the range of 40:60 to 80:20, more preferably in the range of 50:50 to 70:30, and more preferably in the range of 55:45 To 70: 30. When the molar ratio of the constitutional unit derived from trimellitic acid is 40 or more, the adhesive strength between the layer of the resin composition and the metal foil is sufficient, and the layer of the resin composition is not easily peeled during drilling processing, have. On the other hand, when the molar ratio of the polyol-derived constituent units is 20 or more, the layer of the resin composition is efficiently melted during drilling processing, so that the dischargeability of cutting debris generated by the processing is good, And / or the drilling process life tends to be long. If the ratio (molar ratio) of the molar number of the trimellitic acid-derived constituent unit to the molar number of the constitutional unit derived from the polyol in the copolymer is in the range of 55:45 to 70:30, the accuracy of the hole position in drilling processing tends to be even better have.

The content of the polyester resin (A) in the layer of the resin composition of the drill hole entry sheet of the present embodiment is preferably 40 to 40 parts by mass based on 100 parts by mass of the total amount of the polyester resin (A) and a water- Not less than 70 parts by mass, preferably not less than 40 parts by mass and not more than 60 parts by mass, and more preferably not less than 40 parts by mass and not more than 50 parts by mass. When the content of the polyester resin (A) is 40 parts by mass or more, the adhesion strength between the metal foil and the resin composition layer is further improved, and the layer of the resin composition Since the peeling does not occur easily, the hole positioning accuracy is excellent and the drilling processing life is long. On the other hand, when the content of the polyester resin (A) is 70 parts by mass or less, the content of the water-soluble resin (B) in the layer of the resin composition can be adjusted to a sufficient amount of lubricity for drilling, The precision of the hole position of the hole is better. Particularly, when the content of the polyester resin (A) is 40 parts by mass or more and 60 parts by mass or less, both the adhesion strength of the layer of the metal foil and the resin composition and the accuracy of the hole position at the time of perforation tends to be excellent.

The number average molecular weight of the polyester resin (A) is not particularly limited, but is preferably 5,000 or more and 50,000 or less, more preferably 5,000 or more and 30,000 or less, still more preferably 5,000 or more and 25,000 or less. When the number average molecular weight is 5,000 or more, occurrence of blocking can be suppressed, and the handling property tends to be further improved. In addition, the number average molecular weight of 50,000 or less makes it possible to further improve the dischargeability of cutting debris at the time of drill drilling, to improve hole position accuracy, and to suppress the occurrence of drill breakage. The number average molecular weight of the polyester resin (A) can be measured using polystyrene as a standard substance by using a GPC column according to a regular method.

The acid value of the polyester resin (A) is not particularly limited, but is preferably 0 to 2.8 mgKOH / g, and more preferably 0 to 2.6 mgKOH / g. When the acid value of the polyester resin (A) is within the above range, there is a tendency that both the bonding strength between the metal foil and the resin composition layer and the accuracy of the hole position at the time of the perforation process are excellent. Further, the acid value was obtained by weighing 0.2 g of the sample, dissolving in 20 mL of chloroform, and titrating with 0.01 N potassium hydroxide (ethanol solution). For the indicator, phenolphthalein was used.

The production method and production conditions of the polyester resin (A) are not particularly limited, and known methods and conditions can be used. For example, a tricarboxylic acid such as trimellitic acid and a polyol such as diethylene glycol or 1,6-hexanediol may be copolymerized by a known method. Examples of the raw materials that can be used in the production of the polyester resin (A) include tricarboxylic acid to give the tricarboxylic acid-derived constituent unit, polyol to give the constituent unit derived from the polyol, . ≪ / RTI >

The polyester resin (A) may contain ingredients such as raw materials, catalysts, and solvents used in the production of the copolymer. It may contain a stabilizer for a product such as water or an amine, or a component of a dispersant.

The polyester resin (A) is preferably used in the form of an aqueous dispersion when forming the resin composition layer of the drill hole entry sheet of the present embodiment. That is, the mode of the polyester resin (A) in forming the layer of the resin composition is not particularly limited, but it is preferable that the polyester resin (A) is in the form of an aqueous dispersion. The production method of the aqueous dispersion of the polyester resin (A) is not particularly limited, and a known method can be used. For example, the polyester resin (A) described above, an aqueous solvent, and, if necessary, other components such as a base and an emulsifier may be stirred using a solid-liquid stirring apparatus or the like.

A commercially available product may be used as the aqueous dispersion of the polyester resin (A). Examples of commercial products of the water dispersion of the polyester resin (A) include Bayern MD1335 (trimellitic acid-diethylene glycol-1,6-hexanediol copolymer, number average molecular weight 8,000; trimellitic acid-derived The ratio of the number of moles of constituent units: the number of moles of constituent units derived from polyol = 59: 41).

[III: Water-soluble resin (B)]

The water-soluble resin (B) contained in the layer of the resin composition of the drill hole entry sheet of the present embodiment is not particularly limited as long as it is a water-soluble resin, and the combination of the high- and low-molecular water-soluble resin (b2) desirable. The "water-soluble resin" refers to a resin which is dissolved in an amount of 1 g or more per 100 g of water at 25 ° C. and 1 atm.

The polymer water-soluble resin (b1) is not particularly limited, and is preferably one or more kinds selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinyl pyrrolidone, and cellulose derivatives, Of these, polyvinyl pyrrolidone is particularly preferable. These compounds may be used singly or in combination of two or more. These compounds have a sheet-forming property, so that the use of these compounds tends to make the composition and thickness of the resin composition layer of the drill hole entry sheet of the present embodiment uniform. The weight average molecular weight of the polymer water-soluble resin (b1) is not particularly limited, but is preferably from 50,000 to 1,500,000 from the viewpoint of the film formability of the layer of the resin composition in producing the drill hole entry sheet. The weight average molecular weight can be measured by a general method such as liquid chromatography with a GPC column.

Examples of the low-molecular water-soluble resin (b2) include, but are not limited to, glycol compounds such as polyethylene glycol, polypropylene glycol and polytetramethylene glycol; Monoether compounds of polyoxyethylene such as polyoxyethylene oleyl ether, polyoxyethylene cetyl ether, polyoxyethylene stearyl ether, polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether and polyoxyethylene octylphenyl ether; Polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyglycerin monostearate compound, polyethylene oxide-polypropylene oxide copolymer and derivatives thereof . These compounds or copolymers may be used singly or in combination of two or more. By using these compounds, the drill hole entry sheet of the present embodiment tends to be able to sufficiently exhibit the effect of lubricity at drilling processing. The weight average molecular weight of the low-molecular water-soluble resin (b2) is not particularly limited, but is preferably from 1,000 to 30,000 from the viewpoint of improvement in lubricity during drilling. The weight average molecular weight can be measured by a general method such as liquid chromatography with a GPC column.

Among the above-mentioned water-soluble resins (B), examples of the water-soluble resin (B) include polyethylene oxide, polypropylene oxide, polyvinylpyrrolidone, cellulose derivatives, polyethylene glycol, polypropylene glycol, polytetramethylene glycol, Polyoxyethylene sorbitan monostearate, polyglycerin monostearate compound, polyethylene oxide-polypropylene oxide copolymer, and derivatives thereof, in addition to the above-mentioned one or two or more kinds selected from the group consisting of polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan monostearate, desirable. The use of such a water-soluble resin (B) tends to further improve the film composition of the resin composition layer and the accuracy of the hole position.

Particularly when the water-soluble resin (B) contains a water-soluble polymer (b1) having a weight average molecular weight of 50,000 or more and 1,500,000 or less and a low-molecular water-soluble resin (b2) having a weight-average molecular weight of 1,000 to 30,000, (b2) is at least one selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinylpyrrolidone, and cellulose derivatives, wherein the low-molecular water-soluble resin (b2) is at least one selected from the group consisting of polyethylene glycol, polypropylene glycol, At least one member selected from the group consisting of methylene glycol, monoether compounds of polyoxyethylene, polyoxyethylene monostearate, polyoxyethylene sorbitan monostearate, polyethylene oxide-polypropylene oxide copolymer, and derivatives thereof . The use of such a water-soluble resin (B) tends to further improve the film composition of the resin composition layer and the accuracy of the hole position.

The content of the water-soluble resin (B) in the layer of the resin composition is not particularly limited, but is preferably 30 parts by mass or more and 60 parts by mass or less per 100 parts by mass of the total amount of the polyester resin (A) More preferably 40 parts by mass or more and 60 parts by mass or less, and still more preferably 50 parts by mass or more and 60 parts by mass or less. Since the content of the water-soluble resin (B) is 50 parts by mass or more, a layer of a uniform resin composition can be formed, and sufficient lubricity for drilling processing can be imparted to the resin composition layer. The precision tends to be excellent. On the other hand, when the content of the water-soluble resin (B) is 60 parts by mass or less, the content of the polyester resin (A) in the layer of the resin composition can be adjusted to such an extent that the adhesion strength between the metal foil and the resin composition layer becomes good , There is a tendency that hole position accuracy in drilling processing is excellent.

The content of the polymer water-soluble resin (b1) in the layer of the resin composition is not particularly limited as long as it is within the range of the content of the water-soluble resin (B) in the resin composition layer described above, Is preferably 5 parts by mass or more and 30 parts by mass or less, more preferably 5 parts by mass or more and 10 parts by mass or less, and still more preferably 5 parts by mass or more and 7 parts by mass or less, based on 100 parts by mass of the total amount of the water- Do. When the content of the polymer water-soluble resin (b1) is within the above range, the film composition of the resin composition layer and the hole position accuracy tend to be further improved.

The content of the low-molecular water-soluble resin (b2) in the layer of the resin composition is not particularly limited as long as it is within the range of the content of the water-soluble resin (B) in the layer of the resin composition described above, Is preferably 35 parts by mass or more and 55 parts by mass or less, more preferably 40 parts by mass or more and 55 parts by mass or less, further preferably 45 parts by mass or more and 55 parts by mass or less, more preferably 100 parts by mass or less per 100 parts by mass of the total amount of the water- Do. When the content of the low-molecular water-soluble resin (b2) is within the above range, there is a tendency that both the bonding strength between the metal foil and the resin composition layer and the accuracy of the hole position at the time of drilling are superior.

[IV: Other components]

The layer of the resin composition in the drill hole entry sheet of the present embodiment may contain an additive, if necessary. The type of the additive is not particularly limited, and examples thereof include a surface conditioner, a leveling agent, an antistatic agent, an emulsifier, a defoamer, a wax additive, a coupling agent, a rheology control agent, an antiseptic agent, A nucleating agent such as Na, a solid lubricant such as graphite, an organic filler, an inorganic filler, a heat stabilizer, and a coloring agent

The thickness of the layer of the resin composition in the present embodiment is appropriately determined depending on the diameter of the drill bit used for drilling and the configuration of the material to be drilled (for example, a printed wiring board material such as a laminate or a multilayer board) It is preferably 0.02 to 0.3 mm, more preferably 0.02 to 0.2 mm, and even more preferably 0.02 to 0.1 mm. When the layer thickness of the resin composition is 0.02 mm or more, a sufficient lubrication effect is obtained and the load on the drill bit is reduced, so that the cutting of the drill bit tends to be further suppressed. Further, when the thickness of the layer of the resin composition is 0.3 mm or less, there is a tendency to suppress the winding of the resin composition on the drill bit.

[V: metal foil]

The metal foil to be used in the drill hole entry sheet of the present embodiment is not particularly limited, but it is preferable that the metal foil has high adhesion with the layer of the resin composition and can withstand a shock caused by a drill bit. The metal species of the metal foil includes, for example, aluminum from the viewpoints of availability, cost and processability. As the material of the aluminum foil, aluminum having a purity of 95% or more is preferable. As such aluminum foil, for example, 5052, 3004, 3003, 1N30, 1N99, 1050, 1070, 1085, 8021 specified in JIS- . By using an aluminum foil having an aluminum purity of 95% or more for the metal foil, the impact caused by the drill bit is alleviated and the sticking sound to the tip of the drill bit is improved. In addition to the lubrication effect of the drill bit by the resin composition, The positional accuracy can be further increased.

The thickness of the metal foil is not particularly limited, but is preferably 0.05 to 0.5 mm, and more preferably 0.05 to 0.3 mm. When the thickness of the metal foil is 0.05 mm or more, occurrence of burrs in the perforated object (for example, a laminated plate) at drilling processing can be suppressed. When the thickness of the metal foil is 0.5 mm or less, it is easier to discharge the cutting powder generated during drilling.

The thickness of each layer constituting the drill hole entry sheet of the present embodiment is measured as follows. First, an entry sheet was prepared by using a cross-section polisher (trade name "CROSS-SECTION POLISHER SM-09010" manufactured by Nippon Electronic Datum Co., Ltd.) or an ultra-microtome (product name "EM UC7" And cut in the lamination direction. Thereafter, the cross section was observed from a vertical direction with respect to the section shown by cutting using SEM (Scanning Electron Microscope, product number " VE-7800 " manufactured by KEYENCE) The thickness of the layer of the metal foil and the resin composition is measured. For one field of view, the thickness of the five points is measured, and the average value is taken as the thickness of each layer.

[VI: Manufacturing Method of Drill Beam Common Entry Sheet]

The manufacturing method of the drill hole common entry sheet of the present embodiment is not particularly limited, and a general manufacturing method can be used. For example, a drill hole entry sheet can be manufactured as follows. The drill hole entry sheet of the present embodiment is produced by forming a layer of a resin composition on at least one surface of a metal foil. The method for forming the layer of the resin composition is not particularly limited, and a known method can be used. In such a method, for example, a solution of a resin composition obtained by dissolving or dispersing an aqueous dispersion of the polyester resin (A), a water-soluble resin (B) and an additive agent, A method of coating the metal foil and further drying and / or cooling and solidifying the metal foil may be mentioned.

When a solution of the resin composition is coated on a metal foil by a coating method and dried to form a layer of the resin composition, the solvent used in the solution of the resin composition is a mixed solution of water and a solvent having a boiling point lower than that of water . Use of a mixed solution of water and a solvent having a lower boiling point than water can effectively reduce residual bubbles in the layer of the resin composition. The type of the solvent having a lower boiling point than water is not particularly limited, and examples thereof include alcohol compounds such as ethanol, methanol and isopropyl alcohol, and low boiling point solvents such as methyl ethyl ketone and acetone can also be used. As other solvent, it is possible to use, for example, a solvent in which tetrahydrofuran or acetonitrile is partially mixed with water or an alcohol compound highly compatible with the resin composition.

[VII: drilling process]

The drilling processing method of the present embodiment has a hole forming step of forming holes in the laminated board or the multilayer board using the above-described drill hole shared entry sheet. The drill hole common entry sheet may be arranged so that the metal foil side is in contact with the laminated plate or the multilayer plate, or the layer side of the resin composition is placed in contact with the laminated plate or the multilayer plate. Among them, it is preferable to arrange the layer side of the resin composition of the drill hole common entry sheet so as to be in contact with the laminate or the multilayer plate, and to form the hole from the metal layer side.

In addition, the drill boring can more effectively and reliably achieve the object of the present embodiment, provided that the drill boring is performed by a drill bit having a diameter (drill bit diameter) of 0.30 mm or less. Particularly, it is preferable to use a drill bit having a diameter of 0.05 mm to 0.30 mm and a diameter of 0.05 mm to 0.20 mm, in which the accuracy of the hole position becomes important, from the viewpoint of drastically improving hole position accuracy and drill life Do. Further, the drill bit diameter of 0.05 mm? Is the lower limit of the available drill bit diameter, and is not limited to the above as long as a drill bit of smaller diameter is available. Further, there is no problem in adopting the drill hole common use entry sheet of the present embodiment in the drill drilling using a drill bit having a diameter exceeding 0.30 mm ?. In general, a "copper clad laminate" is often used as the laminate, but the laminate of this embodiment may be a laminate without a copper foil on the outer layer. In the present embodiment, unless otherwise specified, the laminate refers to a " copper clad laminate " and / or " a laminate without a copper foil on the outer layer ".

The drill hole entry sheet of the present embodiment can be suitably used, for example, when drilling a printed wiring board material, more specifically, a laminated board or multilayer board. Specifically, a drill / drill hole entry sheet is disposed on at least the uppermost surface of a laminate or multilayer plate (printed wiring board material) in which the metal foil side is in contact with the printed wiring board material, and the upper surface The layer side of the resin composition).

The embodiment for carrying out the present embodiment has been described above, but the present embodiment is not limited to the above embodiment. In the present embodiment, various modifications can be made without departing from the gist of the present invention.

Example

The effects of the embodiment of the present embodiment will be described below in comparison with a comparative example deviating from the scope of the present embodiment. Further, "polyethylene glycol" may be abbreviated as "PEG" and "polyethylene oxide" may be abbreviated as "PEO".

Hereinafter, a method of measuring the adhesive force and a method of measuring the hole position accuracy in the examples and the comparative examples will be described.

<Method of Measuring Adhesive Force>

The adhesion between the metal foil and the layer of the resin composition was measured in the following manner. First, three drill-milled entry sheets prepared in Examples and Comparative Examples were cut into 3 mm width and 100 mm length. Next, a double-sided tape was pasted on the entire surface of the resin composition layer of the sample. Thereafter, one end of a sample to which the double-sided tape was pasted was peeled off by 10 mm, and a jig for mounting the spring balance was attached to the metal foil portion of the peeled sample. A spring balance (manufactured by SANKO, a maximum measurable value of 1000 gf) was attached to the jig and pulled at a speed of 1 cm / sec to read the numerical value indicated by the spring scale. The measurement was carried out on three samples, and the average value of three times was taken as the numerical value of the adhesive force. &Quot; 1000 &quot; when the metal foil and the resin composition layer were not peeled off.

<Measurement of hole position accuracy>

The hole position accuracy was measured in the following manner. On the upper surface of a copper clad laminate in which five copper clad laminate plates (trade name: HL832, thickness of copper foil: 12 mu m, double-sided plate, manufactured by Mitsubishi Gas Chemical Co., Ltd.) having a thickness of 0.2 mm were piled up and piled, The sheet was placed so that the layer side of the resin composition was on the upper side, and a folding plate (paper phenol laminate PS1160-G, manufactured by Risho Co., Ltd.) having a thickness of 1.5 mm was disposed on the backside (bottom surface) of the lowest plate of the superposed copper clad laminate. At a drill bit of 3,000 holes per one drill bit, the total number of drill bits was set to 1, and the number of drill bits was set at 3,000 holes per one drill bit (trade name: C-CFU020S, manufactured by Tangalai Co., Ltd.) at a revolution of 200,000 rpm, a feed rate of 2.6 m / 6000 holes were drilled.

For the hole of 3000 holes (the first drill bit) and the hole of 6000 holes (the second drill bit), the position of the holes in the bottom face (bottom face) of the lowermost plate of the copper clad laminate piled up is shifted from the designated coordinates Using an analyzer (model number: HA-1AM, Hitachi Biomechanics Co., Ltd.). For each drill bit, the average value and the standard deviation (?) Were calculated for the deviation, and the "average value + 3σ" was calculated. Thereafter, an average value was calculated for each of the "average value + 3σ" for the two drill bits used as the hole position accuracy of the entire drill drilling. The formula used to calculate the hole position accuracy is as follows.

(Where n represents the number of used drills)

<Materials>

Table 1 shows the specifications of polyester resin (A), water-soluble resin (B), additive, solvent and metal foil used in the production of the drill hole common entry sheet of Examples and Comparative Examples, and the manufacturer.

Table 2 shows specifications of the polyester resin (A) used in Examples and Comparative Examples. The ratio (molar ratio) of the molar number of the polycarboxylic acid-derived constituent unit to the molar number of the constituent unit derived from the polyol in Table 2 was calculated from the ¹ H-NMR method and the DQF-COZY method, which are one of the nuclear magnetic resonance spectroscopy methods. The number average molecular weight was measured by the method described later. The resin solid content concentration represents the amount (mass%) of the resin solid content in the aqueous dispersion of the polyester resin (A) used in the form of an aqueous dispersion.

Bioron MD1335 has a constitutional unit derived from trimellitic acid as a constitutional unit derived from a tricarboxylic acid, and contains a constitutional unit derived from diethylene glycol and a constitutional unit derived from 1,6-hexanediol as a constitutional unit derived from polyol Is a trimellitic acid-polyol copolymer. The ratio of the number of moles of the constitutional unit derived from trimellitic acid to the number of moles of the constitutional unit derived from polyol (ratio of the constitutional unit derived from trimellitic acid to the constitutional unit derived from polyol) in mole of the constitutional unit derived from trimellitic acid: Was 59: 41. Here, the number of moles of the constituent unit derived from the polyol unit is the sum of the number of moles of the constituent unit derived from diethylene glycol and the number of moles of the constituent unit derived from 1,6-hexanediol.

Bioron MD1985 has a constitutional unit derived from terephthalic acid and a constitutional unit derived from adipic acid as a constitutional unit derived from a dicarboxylic acid instead of a constitutional unit derived from a tricarboxylic acid, -Butanediol. &Lt; / RTI &gt;

Bioron MD1480 has a constitutional unit derived from an isophthalic acid as a constitutional unit derived from a dicarboxylic acid instead of a constitutional unit derived from a tricarboxylic acid and having a constitutional unit derived from a polyol having a constitutional unit derived from diethylene glycol Lt; / RTI &gt; acid-polyol copolymer.

The synthetic polyester resin of the present invention has a structural unit derived from a tetracarboxylic acid and a structural unit derived from a pyromellitic acid as a structural unit derived from a tetracarboxylic acid and having a constitutional unit derived from polyethylene glycol 10,000) units of a tetracarboxylic acid-polyol copolymer. The ratio of the molar number of the constitutional unit derived from pyromellitic acid to the molar number of the constitutional unit derived from polyol (the ratio of the constitutional unit derived from pyromellitic acid to the constitutional unit derived from polyol) of the constitutional unit derived from pyromellitic acid: Was 42: 58.

A method for synthesizing the above-mentioned synthetic polyester resin is as follows. A 500 g three-necked flask was charged with 150 parts of polyethylene glycol having a number average molecular weight of 10,000 and 1,08 parts of calcium carbonate, and subjected to vacuum degassing at 130 占 폚 for 90 minutes. Subsequently, 2.36 parts of 2-anhydrous pyromellitic acid was poured in a nitrogen atmosphere, and a chain extension reaction was carried out at 150 ° C for 2 hours under atmospheric pressure in a nitrogen atmosphere to obtain a polyester resin. The number average molecular weight of the obtained polyester resin was 35,000. Separately, in order to measure the acid value, a polyester resin was obtained in the same manner without injecting calcium carbonate. As a result, the number average molecular weight of the polyester resin was almost the same and the acid value was 7.5 mgKOH / g. The polyester resin was acidified.

The Hydran ADS110 used as the polyurethane resin is an aqueous dispersion having a resin solid content concentration of 30 mass%.

&Lt; Method of measuring number average molecular weight of polyester resin (A) >

The number average molecular weight of the polyester resin (A) was measured using polystyrene as a standard substance using liquid chromatography (manufactured by Shimadzu Corporation) equipped with a GPC column, and the relative average molecular weight was calculated. The equipment used and the analysis conditions are shown below.

(Equipment used)

Shimadzu High Performance Liquid Chromatograph Prominence LIQUID

System Controller: CBM-20A

Liquid Unit: LC-20AD

Online DDE: DGU-20A3

Auto sampler: SIL-20AHT

Column oven: CTO-20A

Differential refractive index detector: RID-10A

LC Workstation: LCSolution

(Analysis condition)

Column: Phenogel 5 占 10E5A 7.8 占 300 占 1, Phenogel 5 占 10E4A 7.8 占 300 占 1, Phenogel 5 占 10E3A 7.8 占 300 占 1, manufactured by Phenomenex

Guard column: Phenogel guard column 7.8 × 50 × 1, manufactured by Phenomenex

Eluent: Tetrahydrofuran for high-performance liquid chromatography Manufactured by Kanto Kagaku Co., Ltd.

Flow rate: 1.00 ml / min

Column temperature: 45 ° C

(Polystyrene for calibration curve)

Showa major Manufacture Shodex standard SL105, SM105

Polystyrene having a number average molecular weight of 580, 1390, 2750, 6790, 13200, 18500, 50600, 123000, 259000, 639000, 1320000, 2480000

Hereinafter, a method of manufacturing an entry sheet for drill holes in the examples and the comparative examples will be described.

&Lt; Example 1 >

As the polyester resin (A), an aqueous dispersion of a trimellitic acid-polyol copolymer (trade name: Bioron MD1335, number average molecular weight 8,000, number of moles of the constituent unit derived from trimellitic acid: number of moles of the constituent unit derived from polyol = 59 (Trade name: Alcox E-45, weight average molecular weight: 560,000, manufactured by Meisei Chemical Industry Co., Ltd.) as the polymer water-soluble resin (b1), 120 parts by mass ), And 54.0 parts by mass of polyethylene glycol (trade name: PEG4000S, weight average molecular weight: 3,300, manufactured by Sanyo Chemical Industries, Ltd.) as a low-molecular water-soluble resin (b2) were dissolved in a water / methanol mixed solvent (mass ratio 50/50) A solution having a solid content concentration of 30% by mass as a composition was prepared.

1.2 parts by mass of a surface conditioner (BYK349, manufactured by Big Chem Co., Ltd.) was added to 100 parts by mass of the solid content of the resin composition in this solution, and further 0.25 parts by mass of sodium formate (Manufactured by Mitsubishi Gas Chemical Co., Ltd.) was added and uniformly dispersed to obtain a resin composition solution for forming a resin composition layer.

The obtained solution of the resin composition was applied to an aluminum foil (using aluminum foil: JIS-A1100H1.80, thickness 0.1 mm, Mitsubishi Aluminum Co., Ltd.) with a bar coater to a thickness of the resin composition layer after drying and solidification of 0.05 mm . Subsequently, the sheet was dried at 120 DEG C for 3 minutes by using a drier, and then cooled and solidified to prepare an entry sheet for drilling.

The adhesive strength between the metal foil of the drill hole entry sheet and the layer of the resin composition was measured three times by the above-described method, and the average value thereof was determined. Subsequently, the drilling process was carried out by the above-described method to measure hole position accuracy. Table 3 shows these results.

&Lt; Examples 2 to 5 >

A solution of the resin composition was prepared in accordance with the type and blend amount of the raw materials shown in Table 3 in accordance with Example 1 to prepare a drill hole blanking sheet having a layer thickness of the resin composition after drying and solidification of 0.05 mm. With respect to the obtained drill hole common entry sheet, the adhesion of the metal foil and the layer of the resin composition and the hole position accuracy were measured. Table 3 shows these results.

&Lt; Comparative Examples 1 to 10 &

A solution of the resin composition was prepared in accordance with the type and blend amount of the raw materials shown in Table 3 in accordance with Example 1 to prepare a drill hole blanking sheet having a layer thickness of the resin composition after drying and solidification of 0.05 mm. With respect to the obtained drill hole common entry sheet, the adhesion between the metal foil and the layer of the resin composition and the hole position accuracy were measured. Table 3 shows these results.

<Criteria>

The evaluation criteria of the adhesion shown in Table 3 are as follows. In drilling processing, the load during processing is applied to the entry sheet. If the adhesion between the metal foil and the resin composition layer is weak, the resin composition layer is peeled off. As a result of intensive studies, the present inventors have found that when the adhesive force is 200 gf or more, it is found that the layer of the resin composition does not peel off during drilling processing. Quot; x &quot;.

The criterion of hole position accuracy shown in Table 3 is as follows. When the hole position accuracy calculated by the equation (2) is 17 占 퐉 or less, it is marked with "?" When the characteristic is excellent, and when it is greater than 17 占 퐉.

The comprehensive judgment shown in Table 3 is as follows. When both the adhesion determination and the hole position accuracy determination are &quot;? &Quot;, the bonding strength between the metal foil and the resin composition layer is strong and the hole position accuracy is excellent. Quot; x &quot; as a comprehensive judgment when at least one of them is &quot; x &quot;.

From Examples 1 to 5 in Table 3, it is found that the polyester resin (A) in the layer of the resin composition of the drill hole common entry sheet is a copolymer (A) containing a constituent unit derived from a tricarboxylic acid and a constituent unit derived from a polyol And the content of the polyester resin (A) is 40 parts by mass or more and 70 parts by mass or less based on 100 parts by mass of the total amount of the polyester resin (A) and the water-soluble resin (B), the metal foil of the drill- The adhesive strength of the layer of the composition is strong and the hole position accuracy in the drilling using the entry sheet is good.

On the other hand, from the comparative examples 1 to 4, even when the polyester resin (A) was not used, or the polyester resin (A) containing the tricarboxylic acid-derived constituent unit and the polyol-containing constituent unit was used, When the content of the ester resin (A) is less than 40 parts by mass based on the total 100 parts by mass of the polyester resin (A) and the water-soluble resin (B), the adhesive strength between the metal foil and the resin composition layer of the drill- , It was found that in the punching process using the entry sheet, the layer of the resin composition peeled off and the hole position accuracy was bad.

In Comparative Example 5 in which the content of the polyester resin (A) in the resin composition layer was more than 70 parts by mass, the adhesion strength between the metal foil and the resin composition layer of the drill hole entry sheet was strong, Since the content of the water-soluble resin (B) is small, the dischargeability of cutting debris during drilling processing is deteriorated, and the hole position accuracy is poor.

In Comparative Example 6 using a copolymer containing a structural unit derived from terephthalic acid or adipic acid, which is a dicarboxylic acid, and a structural unit derived from a polyol, as the polyester resin in the layer of the resin composition, the content of the polyester resin Is not less than 40 parts by mass and not more than 70 parts by mass with respect to 100 parts by mass of the total of the polyester resin and the water-soluble resin (B), the adhesive strength between the metal foil and the resin composition layer of the drill- In drilling processing, it was found that the hole position accuracy is poor. In Comparative Example 7, although the adhesive force between the metal foil and the layer of the resin composition of the drill hole entry sheet was strong, the perforation of the drill was poor, and in drilling processing using the entry sheet, the hole position accuracy was poor.

In Comparative Example 8 using a copolymer containing a constituent unit derived from isophthalic acid as a dicarboxylic acid and a constituent unit derived from a polyol as a polyester resin in the layer of the resin composition, the content of the polyester resin in the polyester Even in the case where the amount of the metal foil is less than 40 parts by mass and not more than 70 parts by mass based on 100 parts by mass of the total amount of the resin and the water-soluble resin (B), the adhesion between the metal foil and the resin composition layer is weak, , And the hole position accuracy was found to be bad.

In Comparative Example 9 using a copolymer containing a constituent unit derived from a pyromellitic acid which is a tetracarboxylic acid and a constituent unit derived from a polyol as a polyester resin in the layer of the resin composition, Even when the amount is from 40 parts by mass or more to 70 parts by mass or less based on 100 parts by mass of the total of the ester resin and the water-soluble resin (B), the adhesive strength between the metal foil and the resin composition layer of the drill- , The hole position accuracy was found to be poor.

Comparative Example 10 using a polyurethane resin instead of the polyester resin (A) contained 40 parts by mass or more and 70 parts by mass or less of the polyurethane resin with respect to 100 parts by mass of the total of the polyurethane resin and the water-soluble resin (B) The adhesion of the metal foil of the drill hole common entry sheet to the layer of the resin composition is weak and it is found that hole position accuracy is poor in drilling processing using the entry sheet.

It has been found from the above that the content of the polyester resin (A) in the layer of the resin composition constituting the drill hole common entry sheet is 40 parts by mass per 100 parts by mass of the total of the polyester resin (A) and the water-soluble resin (B) Is not less than 70 parts by mass and the polyester resin (A) is a copolymer containing a constituent unit derived from a tricarboxylic acid and a constituent unit derived from a polyol, a metal foil of the drill- It can be seen that the adhesive strength is strong and the hole position accuracy in the drilling using the entry sheet is also good.

According to the present invention, compared with the conventional drill hole entry sheet, hole position accuracy is excellent and the occurrence of drill breakage due to peeling of the metal foil and the resin composition layer is suppressed, It is possible to provide an excellent drill hole common entry sheet.

The present application is based on Japanese Patent Application (Japanese Patent Application No. 2016-49334) filed on March 14, 2016 with the Japanese Patent Office, the contents of which are incorporated herein by reference.

Industrial availability

INDUSTRIAL APPLICABILITY The drill hole common entry sheet of the present invention is used for drilling drilling of a laminate or multilayer plate, and has industrial applicability.

Claims (11)

A metal foil comprising a metal foil and a layer of a resin composition formed on at least one side of the metal foil without interposing an adhesive layer,
The layer of the resin composition contains a polyester resin (A) and a water-soluble resin (B)
The content of the polyester resin (A) in the layer of the resin composition is 40 parts by mass or more and 70 parts by mass or less based on 100 parts by mass in total of the polyester resin (A) and the water-soluble resin (B) ,
Wherein the polyester resin (A) is a copolymer containing a tricarboxylic acid-derived structural unit and a polyol-derived structural unit. The method according to claim 1,
Wherein the content of the water-soluble resin (B) in the layer of the resin composition is 30 parts by mass or more and 60 parts by mass or less based on 100 parts by mass in total of the polyester resin (A) and the water-soluble resin (B) Porcelain entry sheet. 3. The method according to claim 1 or 2,
Wherein the tricarboxylic acid is trimellitic acid. The method of claim 3,
Wherein the polyester resin (A) has a constitutional unit represented by the following general formula (1).
[Chemical Formula 1]

(In the formula (1), each R independently represents a -CH ₂ -CH ₂ -O-CH ₂ -CH ₂ - group or a - (CH ₂ ) ₆ - group.) 3. The method according to claim 1 or 2,
Based on the total amount of 100 mol% of the molar number of the tricarboxylic acid-derived structural unit and the molar amount of the structural unit derived from the polyol,
Wherein the molar ratio of the tricarboxylic acid-derived structural unit is 40 to 80 mol%
And the molar ratio of the polyol-derived structural unit is 20 to 60 mol%. 3. The method according to claim 1 or 2,
The number average molecular weight of the polyester resin (A) is 5,000 or more and 50,000 or less. 3. The method according to claim 1 or 2,
Wherein the water-soluble resin (B) is at least one selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinyl pyrrolidone, cellulose derivatives, polyethylene glycol, polypropylene glycol, polytetramethylene glycol, polyoxyethylene monoether compounds, polyoxyethylene monostearate , Polyoxyethylene sorbitan monostearate, polyglycerin monostearate compound, polyethylene oxide-polypropylene oxide copolymer, and derivatives thereof. The present invention relates to a drill / 8. The method of claim 7,
Soluble resin (b1) having a weight average molecular weight of 50,000 or more and 1,500,000 or less and a low-molecular water-soluble resin (b2) having a weight-average molecular weight of 1,000 or more and 30,000 or less,
Wherein the polymeric water-soluble resin (b1) contains at least one member selected from the group consisting of polyethylene oxide, polypropylene oxide, polyvinylpyrrolidone, and cellulose derivatives,
Wherein the low-molecular water-soluble resin (b2) is selected from the group consisting of polyethylene glycol, polypropylene glycol, polytetramethylene glycol, polyoxyethylene monoether compounds, polyoxyethylene monostearate, polyoxyethylene sorbitan monostearate, polyethylene oxide- An oxide copolymer, and an oxide thereof, and a derivative thereof. 3. The method according to claim 1 or 2,
Wherein the thickness of the layer of the resin composition is 0.02 to 0.3 mm. 3. The method according to claim 1 or 2,
Wherein the metal foil has a thickness of 0.05 mm to 0.5 mm. A drill hole drilling method having a hole forming step of forming holes in a laminated plate or a multilayer plate by using the drill hole entry sheet according to claim 1 or 2.