KR101928867B1 - Waterproof fabrics for covering construction wastes collecting and carrying vehicle and manufacturing method of the same - Google Patents
Waterproof fabrics for covering construction wastes collecting and carrying vehicle and manufacturing method of the same Download PDFInfo
- Publication number
- KR101928867B1 KR101928867B1 KR1020170061652A KR20170061652A KR101928867B1 KR 101928867 B1 KR101928867 B1 KR 101928867B1 KR 1020170061652 A KR1020170061652 A KR 1020170061652A KR 20170061652 A KR20170061652 A KR 20170061652A KR 101928867 B1 KR101928867 B1 KR 101928867B1
- Authority
- KR
- South Korea
- Prior art keywords
- fabric
- weft
- strand
- water repellent
- warp
- Prior art date
Abstract
본 발명에 따른 건설폐기물 수집운반 차량 덮개용 방수 직물의 제조방법은 경사와 위사를 2*2 옥스포드(oxford) 구조로 교차시켜 직물을 제직하는 단계; 및 불소 중합체 성분의 발수 약제를 포함하는 디핑액을 상기 제직된 직물에 부착하는 열처리 단계를 포함하는 것을 특징으로 한다. A method for fabricating a waterproof fabric for a construction waste carrier transportation vehicle lid according to the present invention includes steps of weaving a fabric by crossing warp and weft with a 2 * 2 oxford structure; And a heat treatment step of attaching a dipping solution containing a fluoropolymer component water repellent agent to the woven fabric.
Description
본 발명은 건설폐기물 수집운반 차량 덮개용 방수 직물 및 그의 제조방법에 관한 것으로, 상세하게는 기존 경사/위사 조직 구성 방식을 변경하고 열처리 디핑 (Dipping)액 조제 방법을 변경하여 방수 기능을 부여한 건설폐기물 수집운반 차량 덮개용 직물 및 그 제조방법에 관한 것이다.[0001] The present invention relates to a waterproof fabric for a construction waste cover transportation vehicle cover and a method of manufacturing the same, and more particularly, to a waterproof fabric for a construction waste which is provided with a waterproof function by changing the existing slope / And more particularly, to a fabrics for collecting and transporting vehicle covers and fabrication methods thereof.
산업용 컨베이어 벨트에 사용하고 있는 직물 보강재인 EP (경사 Polyester, 위사 Nylon) 벨트지 제품을 건설 폐기물을 수집·운반하는 차량에 덮개용으로 일부 판매를 하고 있으나, 2016년 7월 환경부에서 건설 폐기물 수집·운반차량 덮개 재질에 관한 요구 사항을 지정함에 따라 방수 기능을 추가로 필요로 하게 되었다{참고: 건설폐기물 수집·운반차량 덮개 재질에 관한 고시(2016. 7. 1. 시행)}.We sell some of EP (Belt) products, which are fabric reinforcing materials used in industrial conveyor belts, for covering and collecting construction waste. However, in July 2016, the Ministry of Environment By specifying requirements for the material of the vehicle hatch cover, additional waterproofing is required. (Note: Notice of construction waste hatch cover material (enforced on July 1, 2016)).
상기 환경부 고시에 따르면, 건설폐기물 수집·운반차량 덮개 재질로서 그밖에 금속에 준하는 재질이란 한국산업표준 KS M ISO527 인장시험(시험편의 좁은 평행면 부분의 폭은 10mm로 함)을 적용하여 측정한 인장하중이 500N 이상인 것으로 방수기능을 갖추고 있는 재질을 말한다.According to the Ministry of the Environment notification, the materials that are used as construction cover materials for construction waste collection and transportation vehicles are tensile load measured by KS M ISO527 tensile test (width of narrow parallel portion of test specimen is 10mm) It is a material with waterproof function that is more than 500N.
통상적으로, 벨트지는 경사, 위사로 구성된 직물로 각각 원사를 꼬아서 연사품(Raw Cord)을 만들고, 이것을 제직하여 직물 형태로 만든 생지(Raw Fabric)를 열처리하여 딥지(Dip Fabric)을 만들게 되는데, 기존 EP 벨트 규격의 경우, 소재 자체에 방수 기능이 없고, 경사/위사로 구성된 직물로 밀도가 낮아 직물에 공극이 존재하기 때문에 방수는 불가능한 구조이다. Generally, a yarn is twisted with a fabric composed of a belt, a warp, and a weft, respectively, to make a raw cord, and the fabric is weaved to heat the raw fabric to form a dip fabric. In the case of the existing EP belt standard, there is no waterproof function in the material itself, and the density is low due to a fabric composed of warp / weft.
종래의 벨트 직물 제조방법은 경사 Polyester 1000d 1가닥, 위사 Nylon-6 840d 2가닥에 각각 꼬임을 부여하고, 경사, 위사를 1*1 평직(Plain) 구조로 교차시켜 제직하는 과정, Dipping액을 부착하는 열처리 과정을 거쳐 최종적으로 벨트 직물을 얻게 된다.The conventional method of fabricating a belt fabric includes twisting a warp yarn and weft yarn in a 1 * 1 plain weave structure by applying a twist to each strand of warp polyester 1000d and weft yarn Nylon-6 840d, And finally a belt fabric is obtained.
이와 같은 과정을 거쳐 얻게 된 벨트 직물의 경우, 직물 구조 상 공극이 크고 Dipping액 자체에 방수 기능이 없기 때문에 한국산업표준 KS K 0590 발수도 4급 이상 조건을 만족할 수 없었다.In the case of the belt fabric obtained through such a process, since the pore size is large in the fabric structure and the dipping liquid itself does not have a waterproof function, the KS K 0590 water repellency of KS K 0590 or more can not be satisfied.
따라서, 방수 기능을 갖추고 있는 건설폐기물 수집운반 차량 덮개용 직물에 대한 필요성이 현실적으로 대두되고 있다.Therefore, there is a real need for a construction waste water collection and transportation vehicle covering fabric having a waterproof function.
본 발명에 관련된 종래기술로는, KR 2012-0151705 A은 고기능성의 라미네이팅 투습방수포에 관한 것으로, 박리강도 및 세탁 내구성이 우수한 고기능성 투습방수포를 제공하기 위해 소수성 폴리 우레탄 피막을 적용하여 친수성 필름 층의 팽윤에 따른 문제를 해결하고, 고투습성을 부여하기 위해 흡습성이 우수한 나노 상태의 미립자 성분을 투입하며 나노 사이즈의 미세기공을 형성할 수 있는 첨가제를 투입하였다는 기술적 특징을 가지고 있다. KR 2012-0151705 A discloses a highly functional laminating moisture permeable protective film. To provide a highly functional moisture permeable protective film having excellent peel strength and washing durability, a hydrophobic polyurethane film is applied to form a hydrophilic film layer The present invention has the technical feature that an additive capable of forming nano-sized micropores is added to the nanostructured fine particle component having excellent hygroscopicity in order to solve the problem caused by the swelling of the nanostructure.
EP 01789627 B는 이송 벨트 및 프레스 직물 분야에서 사용하기 위한 제지업자 직물에 관한 것으로, 다수의 층들을 소정의 방식으로 배열하는 단계로, 적어도 하나의 층은 제직하거나, 뜨개질하거나, 짠 재료로 이루어지고, 제 1의 융점을 가지며, 나머지 층들 중 각 층은 상기 제1의 융점보다 높은 융점을 갖는 단계 및 상기 나머지 층들이 용해됨이 없이 상기 적어도 하나의 층이 용해되도록 한다는 기술적 특징이 있다. EP 01789627 B relates to a papermaker's fabric for use in a conveying belt and press fabric field, comprising arranging a plurality of layers in a predetermined manner, wherein at least one layer is made of a woven, knitted or woven material , A first melting point, each of the remaining layers having a melting point higher than the first melting point, and the at least one layer dissolving without dissolving the remaining layers.
KR 1049257 B는 투습방수용 코팅조성물, 투습방수직물에 관한 것으로, 구체적으로 투습도 및 내수도가 우수하며 생산성이 좋고, 환경친화적인 섬유가공 기술개발에 관한 것으로, 발수가공 및 시레가공된 직물과 친수무공형의 폴리우레탄 아크릴레이트가 포함된 코팅층을 사용하여 전체 직물의 우수한 유연성, 투습방수성을 나타내고, 메쉬구조를 갖는 직물을 함께 구성함으로써 투습성을 향상시킨다는 특징을 가지고 있다. KR 1049257 B relates to a coating composition for breathable and waterproofing, and a breathable and waterproof fabric, and more particularly relates to the development of an environmentally friendly textile processing technology having excellent water vapor permeability and water resistance, good productivity and water repellency, Type polyurethane acrylate is used to exhibit excellent flexibility, moisture permeability and waterproofness of the whole fabric, and a fabric having a mesh structure is formed together to improve the moisture permeability.
KR 1386428 B는 고강도 직물의 발수처리 방법에 관한 것으로, 고강도 직물을 발수제 조성물 내에 디핑시켜 고강도 직물내에 발수제 조성물을 함침시킨 후 건조 및 열처리 하기 전에 공기흡입장치로 고강도 직물내에 함침된 발수제 조성물중 일부를 제거해 주는 것을 특징으로 하고 있다. KR 1386428 B relates to a method of water repellent treatment of high strength fabrics in which a high strength fabric is dipped into a water repellent composition to impregnate a water repellent composition in a high strength fabric and then a part of the water repellent composition impregnated in the high strength fabric And the like.
그러나, 상기 선행기술들은 경사, 위사 공극을 최소화하기 위해 직물 조직을 2*2 Oxford 조직으로 구성하여 KS K 0590 발수도 4급 이상 조건을 만족하지도 않고, 나아가, 건설 폐기물 수집운반하는 차량의 덮개용으로도 사용되지 않았다. However, the above-mentioned prior arts do not satisfy the conditions of KS K 0590
이에 상기한 문제점을 해결하기 위하여 본 발명은 건설 폐기물 수집·운반하는 차량에 덮개용으로 사용하고 있는 직물 및 그 제조 방법에 관한 것으로, 경사/위사 조직 구성 방식을 변경하고 열처리 Dipping 액(Resorcinol Formalin Latex, 일종의 접착액) 조제 방법을 변경하여 방수 기능을 부여하는 건설 폐기물 수집·운반하는 차량에 덮개용으로 사용하고 있는 직물 및 그 제조 방법을 제공하는 것을 목적으로 한다.In order to solve the above-mentioned problems, the present invention relates to a fabric used as a lid for a vehicle for collecting and transporting construction waste, and a method of manufacturing the same, wherein the inclined / , A kind of adhesive liquid), and to provide a fabric used for a cover for a vehicle for collecting and transporting construction waste that imparts a waterproof function, and a method of manufacturing the same.
상기한 기술적 과제는, 본 발명의 바람직한 실시예에 따르면, 경사와 위사를 2*2 옥스포드(oxford) 구조로 교차시켜 직물을 제직하는 단계; 및 불소 중합체 성분의 발수 약제를 포함하는 디핑액을 상기 제직된 직물에 부착하는 열처리 단계를 포함하는 것을 특징으로 하는 건설폐기물 수집운반 차량 덮개용 방수 직물의 제조방법에 의해 해결된다.According to a preferred embodiment of the present invention, the above-mentioned technical problem is solved by a yarn manufacturing method comprising: weaving a fabric by crossing a warp and a weft in a 2 * 2 oxford structure; And a heat treatment step of adhering a dipping liquid containing a fluoropolymer component water repellent agent to the woven fabric. The method of manufacturing a waterproof fabric for a construction waste cover transportation vehicle cover according to claim 1,
상기 경사와 위사는, 경사 폴리에스테르 1000d 1가닥, 위사 폴리에스테르 1000d 1가닥에 각각 꼬임을 부여한 것이 바람직하다.It is preferable that the warp yarns and the warp yarns are each provided with a twist on one strand of the warp polyester 1000d and one strand of the weft polyester 1000d.
상기 디핑액은 R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물} 90 내지 97 중량%에 불소 중합체 성분의 발수 약제를 3 내지 10% 중량%를 포함하는 것이 바람직하다. The dipping solution contains 3 to 10% by weight of a water repellent agent of a fluoropolymer component in 90 to 97% by weight of RFL (Resorcinol, Formalin, Latex, Isocyanate mixture) .
상기 방수 직물은 한국산업표준 KS K 0590 발수도 4급 이상 조건을 만족하는 것이 바람직하다. It is preferable that the waterproof fabric satisfies the Korean Industrial Standard KS K 0590
본 발명은 건설 폐기물 수집·운반하는 차량에 덮개용으로 사용하는 직물은, 경사, 위사 공극을 최소화하기 위해 직물 조직을 2*2 Oxford 조직으로 구성하여, 기존 직물 대비 경사, 위사의 밀도를 70~100% 이상 추가하여 직물을 조밀하게 제직을 하고, Dipping액 조제 시 Fluoropolymer 성분의 발수 약제를 추가함으로써 방수 기능이 확보되었다. In the present invention, a fabric used for a cover for a vehicle for collecting and transporting construction waste is made of 2 * 2 Oxford fabric so as to minimize warpage and weft voids, and the density of warp and weft is 70 ~ 100% or more was added to weave the fabric densely, and water repellent function was secured by adding a fluoropolymer water repellent agent when preparing the dipping solution.
도 1은 본 발명에 따라 제조되는 방수 직물의 변경 구조 예시도로서, 좌측은 종래기술 구조, 우측은 본 발명 구조,
도 2는 발수도(KS K 0590) 평가 등급 기준 조견도.Fig. 1 is a view showing a modified structure of a waterproof fabric manufactured according to the present invention, wherein the left side is a prior art structure, the right side is a structure of the present invention,
Fig. 2 is a diagram based on the water repellency (KS K 0590) evaluation grade.
이하, 실시예를 통해 본 발명을 구체적으로 설명한다. 그러나 이들 실시예는 본 발명의 이해를 돕기 위한 것일 뿐 어떠한 의미로든 본 발명의 범위가 이들 실시예로 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail by way of examples. However, these examples are provided only for the understanding of the present invention, and the scope of the present invention is not limited to these examples in any sense.
본 발명을 설명함에 있어서, 본 발명과 관련된 공지기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략하기로 한다. 그리고, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례 등에 따라 달라질 수 있다. 그러므로 그 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.In the following description, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. The following terms are defined in consideration of the functions of the present invention, and may be changed according to the intention or custom of the user, the operator, and the like. Therefore, the definition should be based on the contents throughout this specification.
본 발명의 기술적 사상은 청구범위에 의해 결정되며, 이하의 실시예는 본 발명의 기술적 사상을 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 효율적으로 설명하기 위한 일 수단일 뿐이다. The technical idea of the present invention is determined by the claims, and the following embodiments are merely a means for effectively explaining the technical idea of the present invention to a person having ordinary skill in the art to which the present invention belongs.
종래기술에 따른 건설폐기물 수집운반 차량 덮개용 직물은 경사 Polyester 1000d 1가닥, 위사 Nylon-6 840d 2가닥에 각각 꼬임을 부여하고, 경사, 위사를 1*1 평직(Plain) 구조로 교차시켜 제직하는 과정(도 1(좌측) 참조), Dipping액을 부착하는 열처리 과정을 거쳐 최종적으로 벨트 직물을 얻게 된다. 그러나, 이와 같은 과정을 거쳐 얻게 된 벨트 직물의 경우, 직물 구조 상 공극이 크고 Dipping액 자체에 방수 기능이 없기 때문에 한국산업표준 KS K 0590 발수도 4급 이상 조건을 만족할 수 없었다.The fabric for construction waste cover according to the prior art has twisted yarns on one strand of warp polyester 1000d and two strands of weft yarn Nylon-6 840d and weaving warp yarns and weft yarns in a 1 * 1 plain structure (See FIG. 1 (left)), the belt fabric is finally obtained through a heat treatment process for attaching the dipping solution. However, in the case of the belt fabric obtained through such a process, since the pore structure is large in the fabric structure and the dipping liquid itself does not have a waterproof function, the KS K 0590 water repellency of KS K 0590 or more can not be satisfied.
이를 개선하기 위해, 본 발명에 따르면, 도 1(우측)에 도시된 바와 같이, 경사, 위사 공극을 최소화하기 위해 직물 조직을 2*2 Oxford 조직으로 구성하여, 기존 직물 대비 경사, 위사의 밀도를 70~100% 이상 추가하여 직물을 조밀하게 제직을 하고, Dipping액 조제시 Fluoropolymer 성분의 발수 약제를 추가함으로써 방수 기능을 확보하도록 하였다. 직물 구성 밀도나 발수 약제 함량 등은 요구 수준에 따라 변경이 가능하다.In order to improve this, according to the present invention, as shown in Fig. 1 (right), in order to minimize warpage and weft voids, the fabric structure is made of 2 * 2 Oxford tissue and the density of warp and weft 70 ~ 100% of the fabric is densely woven, and the water repellent function is ensured by adding the water repellent agent of the fluoropolymer component when preparing the dipping solution. Fabric composition density and water repellent agent content can be changed according to demand level.
본 발명에 사용한 발수 약제는 아래와 같다. The water repellent agent used in the present invention is as follows.
- 구조식 : 
- 상품명 : Lurol FC-L624 - Product name: Lurol FC-L624
- 제조사 : Goulston Technologies, Inc.- Manufacturer: Goulston Technologies, Inc.
- 물성 : 하기 표 1과 같다. - Physical properties: The results are shown in Table 1 below.
상기 디핑액 조제시 R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물} 90 내지 97 중량%에 불소 중합체 성분의 발수 약제를 3 내지 10 중량%를 포함한 것이 바람직하다. 발수 약제의 함량이 3 중량% 미만인 경우에는 원하는 수준의 방수 기능을 확보하기 어려우며, 10 중량%를 초과하는 경우에는 열처리 시 발수 코팅막이 두꺼워져 디핑액의 균일 도포 측면에서 불리하므로 방수 효과가 저하될 수 있다.When preparing the dippling solution, 90 to 97% by weight of RFL (Resorcinol, Formalin, Latex, Isocyanate mixture) contains 3 to 10% by weight of a water repellent agent of a fluoropolymer component . When the content of the water repellent agent is less than 3% by weight, it is difficult to secure a desired level of waterproof function. When the content of the water repellent agent exceeds 10% by weight, the water repellent coating film becomes thicker during heat treatment, .
그럼, 본 발명을 실시예 및 비교예를 통해 비교, 설명하기로 한다.Hereinafter, the present invention will be described by way of examples and comparative examples.
[실시예 1][Example 1]
경사 폴리에스테르(Polyester) 1000d 1가닥, 위사 폴리에스테르 (Polyester) 1000d 1가닥에 각각 꼬임을 부여하고, 경사와 위사를 2*2 옥스포드(oxford) 구조로 교차시켜 직물을 제직하고, R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물} 97 중량%에 불소 중합체(Fluoropolymer) 성분의 발수 약제를 3 중량%를 추가하여 디핑(Dipping)액을 조제한 후, 상기 직물에 상기 디핑액을 부착하는 열처리 단계를 거쳐 최종적으로 벨트 직물을 제조하였다. One strand of Polyester 1000d and one strand of Polyester 1000d were each twisted and the fabric was weaved by crossing the warp and weft with a 2x2 oxford structure and RFL { A dipping solution was prepared by adding 3 wt% of a water repellent agent of a fluoropolymer component to 97 wt% of Resorcinol, Formalin, Latex, Isocyanate mixture, A belt fabric was finally made through a heat treatment step of attaching the dipping solution to the fabric.
[실시예 2][Example 2]
상기 실시예 1의 디핑액 조제시 R.F.L 90 중량%에 발수 약제를 10 중량%를 추가한 것을 제외하고는 상기 실시예 1과 동일하게 실시하였다.The procedure of Example 1 was repeated except that 10 wt% of water repellent agent was added to 90 wt% of R.F.L in preparing the dipening solution of Example 1. [
[비교예 1][Comparative Example 1]
경사 폴리에스테르 1000d 1가닥, 위사 나일론-6 840d 2가닥에 각각 꼬임을 부여하고, 경사와 위사를 1*1 평직(plain) 구조로 교차시켜 직물을 제직하고, R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물}을 디핑(Dipping)액으로 하여 상기 직물에 부착하는 열처리 단계를 거쳐 벨트 직물을 제조하였다.One strand of the warp polyester and one strand of weft nylon-6 840d were each twisted, and the warp and weft were crossed in a 1 * 1 plain structure to weave the fabric, and RFL {Resorcinol, A belt fabric was manufactured through a heat treatment step of attaching to a fabric a dipping solution of formalin, latex and isocyanate mixture.
[비교예 2][Comparative Example 2]
경사 폴리에스테르 1000d 1가닥, 위사 나일론-6 840d 2가닥에 각각 꼬임을 부여하고, 경사와 위사를 1*1 평직(plain) 구조로 교차시켜 직물을 제직하고, R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물} 97 중량%에 불소 중합체(fluoropolymer) 성분의 발수 약제를 3 중량%를 추가하여 디핑(Dipping)액을 조제한 후, 상기 직물에 상기 디핑액을 부착하는 열처리 단계를 거쳐 최종적으로 벨트 직물을 제조하였다. One strand of the warp polyester and one strand of weft nylon-6 840d were each twisted, and the warp and weft were crossed in a 1 * 1 plain structure to weave the fabric, and RFL {Resorcinol, 3% by weight of a water repellent agent of a fluoropolymer component is added to 97% by weight of a mixture of formaldehyde, formalin, latex and isocyanate to prepare a dipping solution, The belt fabric was finally made through a heat treatment step of adhering the zine solution.
[비교예 3][Comparative Example 3]
경사 폴리에스테르(Polyester) 1000d 1가닥, 위사 폴리에스테르 (Polyester) 1000d 1가닥에 각각 꼬임을 부여하고, 경사와 위사를 2*2 옥스포드(oxford) 구조로 교차시켜 직물을 제직하고, R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물}을 디핑(Dipping)액으로 하여 상기 직물에 부착하는 열처리 단계를 거쳐 벨트 직물을 제조하였다.One strand of Polyester 1000d and one strand of Polyester 1000d were each twisted and the fabric was weaved by crossing the warp and weft with a 2x2 oxford structure and RFL { A belt fabric was manufactured through a heat treatment step of applying Resorcinol, Formalin, Latex, Isocyanate mixture as a dipping solution to the fabric.
[비교예 4][Comparative Example 4]
상기 실시예 1의 디핑액 조제시 R.F.L 98 중량%에 발수 약제를 2 중량%를 추가한 것을 제외하고는 상기 실시예 1과 동일하게 실시하였다.The procedure of Example 1 was repeated except that 2 wt% of water repellent agent was added to 98 wt% of R.F.L in the preparation of the dipening solution of Example 1 above.
평가evaluation
상기 실시예 1 내지 2 및 비교예 1 내지 4에서 제조된 벨트 직물의 물성을 아래와 같은 방법으로 평가하였으며, 그 결과를 표 2에 나타내었다. The physical properties of the belt fabric prepared in Examples 1 to 2 and Comparative Examples 1 to 4 were evaluated by the following methods, and the results are shown in Table 2.
1) 밀도1) Density
직물 5cm 당 경사 또는 위사의 가닥 수로 측정하였다.And the number of strands of warp or weft per 5 cm of fabric.
2) 발수도2) Water repellency
한국산업표준 KS K 0590(직물의 발수도 시험 방법: 스프레이법)에 따라 발수도를 시험하였다. 이후 도 2에 따라 그 결과를 평가하였다. 발수도는 1급에서 5급으로 평가되며 숫자가 클수록 방수기능이 좋음을 뜻한다.The water repellency was tested according to Korean Industrial Standard KS K 0590 (water repellency test method: spray method). The results were evaluated according to Fig. The water footage is evaluated as first to fifth grade. The larger the number, the better the waterproof function.
구성textile
Configuration
발수제(3 중량%)RFL +
Water repellent agent (3% by weight)
발수제(2 중량%)RFL +
Water repellent agent (2% by weight)
발수제(3 중량%)RFL +
Water repellent agent (3% by weight)
발수제(10 중량%)RFL +
Water repellent agent (10% by weight)
(KS K 0590)Water repellency evaluation result
(KS K 0590)
상기 표 1에서 알 수 있는 바와 같이, 본 발명의 실시예 1, 2에서 제조된 벨트 직물은 발수도 평가 결과 4급으로, 비교예 1 내지 4 에서 제조된 벨트 직물과 달리 방수 기능이 확보되었음을 알 수 있다. As can be seen from the above Table 1, the belt fabrics manufactured in Examples 1 and 2 of the present invention had water repellency rating of 4, indicating that the waterproof function was secured unlike the belt fabric prepared in Comparative Examples 1 to 4 .
비교예 1과 비교예 2를 비교해 보면, 비교예 2의 경우 디핑 방식에 발수제가 첨가되었음에도 발수도 평가 결과가 나아지지 않았는데, 이는 1*1 평직 구조의 경우 경사, 위사의 밀도가 낮아 직물에 공극이 존재하기 때문에 디핑 방식에서 발수제를 첨가하였음에도 방수 기능이 확보되지 못한 것으로 평가된다.Comparing Comparative Example 1 with Comparative Example 2, the water repellency evaluation result was not improved even though the water repellent agent was added to the dipping system in Comparative Example 2 because the density of warp and weft was low in the case of a 1 * 1 plain weave structure, It is estimated that the waterproof function can not be secured even though the water repellent is added in the dipping method.
또한, 비교예 3과 비교예 1을 비교해 보면, 2*2 옥스포드 구조의 경우 경사, 위사의 밀도가 높아 직물이 조밀하게 제직되어 1*1 평직 구조에 비해 발수도 평가 결과가 나아짐을 확인할 수 있다.Further, when comparing Comparative Example 3 and Comparative Example 1, it can be confirmed that the density of the warp and weft yarns in the 2 * 2 oxford structure is so high that the fabric is densely woven, and the water repellency evaluation result is better than that of the 1 * 1 plain weave structure .
비교예 3 내지 4와 실시예 1, 2를 비교해 보면, 2*2 옥스포드 구조 직물에다가 디핑 방식에 발수제가 3 내지 10 중량% 첨가될 경우, 발수도 평가 결과가 4급 이상 확보됨을 확인할 수 있다.Comparing Comparative Examples 3 to 4 with Examples 1 and 2, it can be confirmed that water repellency evaluation results of
따라서 본 발명의 직물 제조방법에 있어, ① 직물 제직 구조를 옥스포드 조직을 적용하는 것과 ② 열처리 시 발수 약제를 추가하는 것을 특징으로 하여 방수 기능이 있는(KS K 0590 발수도 4급 이상) 직물을 제조할 수 있음을 알 수 있다. Therefore, in the fabric manufacturing method of the present invention, (1) fabrics having a waterproof function (KS K 0590
Claims (4)
불소 중합체 성분의 발수 약제를 포함하는 디핑액을 상기 제직된 직물에 부착하는 열처리 단계를 포함하고,
상기 디핑액은 R.F.L{레조르시놀(Resorcinol), 포르말린(Formalin), 라텍스(Latex), 이소시아네이트(Isocyanate) 혼합물} 90 내지 97 중량%에 불소 중합체 성분의 발수 약제를 3 내지 10 중량%를 포함한 것을 특징으로 하는 건설폐기물 수집운반 차량 덮개용 방수 직물의 제조방법.Crossing a weft of 1000 d 1 strand having a density of 143 to 147 ea / 5 cm and a weft of 1000 d 1 strand having a density of 61 to 65 ea / 5 cm in a 2 * 2 oxford structure; And
And a heat treatment step of attaching a dipping solution containing a water repellent agent of a fluoropolymer component to the woven fabric,
The dipping solution may contain 3 to 10% by weight of a water repellent agent of fluoropolymer component in 90 to 97% by weight of RFL (Resorcinol, Formalin, Latex, Isocyanate mixture) A method for manufacturing a waterproof fabric for a construction waste collector transportation vehicle lid.
상기 경사와 위사는, 경사 폴리에스테르 1000d 1가닥, 위사 폴리에스테르 1000d 1가닥에 각각 꼬임을 부여한 것을 특징으로 하는 건설폐기물 수집운반 차량 덮개용 방수 직물의 제조방법.The method according to claim 1,
Wherein said warp and weft yarns are each provided with a twist on one strand of warp polyester 1000d and one strand of weft polyester 1000d.
A waterproof fabric made by the method of paragraph 1 and covering the construction industry waste water transport vehicle cover which satisfies the KS K 0590 water repellency grade 4 or above of the Korean industry standard.