KR101917425B1 - Preparation method of flexible electrode, flexible electrode fabricated according to said method and flexible dye-sensitized solar cell comprising said electrode - Google Patents
Preparation method of flexible electrode, flexible electrode fabricated according to said method and flexible dye-sensitized solar cell comprising said electrode Download PDFInfo
- Publication number
- KR101917425B1 KR101917425B1 KR1020160115475A KR20160115475A KR101917425B1 KR 101917425 B1 KR101917425 B1 KR 101917425B1 KR 1020160115475 A KR1020160115475 A KR 1020160115475A KR 20160115475 A KR20160115475 A KR 20160115475A KR 101917425 B1 KR101917425 B1 KR 101917425B1
- Authority
- KR
- South Korea
- Prior art keywords
- oxide
- nitride
- flexible
- dye
- group
- Prior art date
Abstract
본 발명은 저온소성용 염료감응 광전극과 그 제조방법, 및 이를 이용한 염료감응 태양전지에 관한 것으로, 더욱 상세하게는 ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬 알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계,; ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계 및; ⅲ)200℃ 이하의 온도에서 저온소성하여 다공질 제1금속산화물층을 형성하는 단계를 포함한 가요성 광전극 제조방법, 상기 방법에 의해 제조된 가요성 광전극 및 상기 가요성 광전극을 포함한 염료감응형 태양전지에 관한 것으로, 본 발명은 플렉서블 기판을 사용하여 저온소성이 요구되는 조건하에서도 가요성 광전극에 사용되는 금속산화물 입자 상호간 및 금속산화물 입자와 기판 사이에 상호 연결을 증가시켜 광전효율 및 안정성이 우수한 가요성 광전극 및 염료감응형 태양전지를 제조할 수 있다. The present invention relates to a dye-sensitized photoelectrode for low-temperature firing, a method for producing the same, and a dye-sensitized solar cell using the same. More particularly, the present invention relates to a dye- Mixing the first metal oxide nanoparticles in a solvent in a volume ratio of 1: 0.1 to 10 to prepare a paste; Ii) applying the paste onto the conductive flexible substrate; Iii) low-temperature baking at a temperature of 200 DEG C or less to form a porous first metal oxide layer; a method of manufacturing a flexible photoelectrode fabricated by the method and a dye- The present invention relates to a photovoltaic cell, and more particularly, to a photovoltaic cell in which a flexible substrate is used to increase interconnections between metal oxide particles used for flexible optical electrodes and between metal oxide particles and a substrate, The flexible optical electrode and the dye-sensitized solar cell excellent in stability can be produced.
Description
본 발명은 가요성 광전극 제조방법, 상기 방법에 의해 제조된 가요성 광전극 및 상기 가요성 광전극을 포함한 염료감응 태양전지에 관한 것으로, 보다 상세하게는 전도성 가요성 기재상에 형성되는 다공질 제1금속산화물층과 상기 다공질 제1금속산화물층상에 염료를 흡착한 구조를 포함한 가요성 광전극의 제조방법에 있어서, ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬 알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계,; ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계 및; ⅲ)200℃ 이하의 온도에서 저온소성하여 다공질 제1금속산화물층을 형성하는 단계를 포함한 가요성 광전극 제조방법, 상기 방법에 의해 제조된 가요성 광전극 및 상기 가요성 광전극을 포함한 염료감응형 태양전지에 관한 것이다.BACKGROUND OF THE
염료감응 태양전지(dye-sensitized photovoltaic cell)는 1991년 스위스의 그라첼(Gratzel) 등에 의하여 발표된 광전기화학 태양전지로 대표되는 것으로서, 일반적으로 가시광선을 흡수하는 감광성 염료, 넓은 밴드갭 에너지를 갖는 금속산화물 나노입자로 구성된 광전극, 백금(Pt)에 의해 촉매작용을 하는 상대전극(counter electrode), 그리고 그 사이에 채워진 전해질로 구성되어 있다. 염료감응형 태양전지는 기존의 실리콘 태양전지나 화합물 반도체 태양전지에 비해 그 제작비용이 저렴하고, 유기 태양전지에 비하여 그 효율이 높으며 이 외에도 친환경적이고 투명화가 가능하다는 장점을 가진다.The dye-sensitized photovoltaic cell is represented by a photovoltaic solar cell disclosed by Gratzel et al., 1991, and generally comprises a photosensitive dye that absorbs visible light, a dye having a wide band gap energy A photoelectrode composed of metal oxide nanoparticles, a counter electrode catalyzed by platinum (Pt), and an electrolyte filled therebetween. The dye-sensitized solar cell is advantageous in that its production cost is lower than that of a conventional silicon solar cell or a compound semiconductor solar cell, its efficiency is higher than that of an organic solar cell, and it is also environmentally friendly and transparent.
최근 유연기판(flexible substrate)을 갖는 반도체 전극을 사용하는 플렉서블 염료감응 태양전지는 휴대폰, 웨어러블 PC 등 차세대 PC 산업에 필요한 전원의 자가 충전이나 옷, 모자, 자동차 유리, 건물 등에 부착해 활용할 수 있다는 점에서 관심의 초점이 되고 있다.Recently, a flexible dye-sensitized solar cell using a semiconductor electrode having a flexible substrate can be used for self-charging of a power source necessary for a next-generation PC industry such as a mobile phone or a wearable PC, or attaching it to clothes, hats, Has become the focus of attention.
그러나, 이러한 유연기판을 갖는 반도체 전극의 제작에 필요한 플라스틱 기판은 고온에서 쉽게 변형이 일어나기 때문에 150℃ 이하의 저온에서 반도체 전극을 제작해야 하는 제한이 따른다. 즉, 일반적으로 유연기판인 플라스틱 기판에는 고온 열처리가 불가능하기 때문에 저온에서 TiO2와 같은 금속산화물을 소성시켜야 한다. 하지만, 상기 저온 소성의 경우는, TiO2 입자간 연결성이 부족하기 때문에 광전자 전달 능력이 현저히 떨어진다.However, the plastic substrate required for fabricating a semiconductor electrode having such a flexible substrate is easily deformed at high temperatures, and therefore, there is a limitation in manufacturing a semiconductor electrode at a low temperature of 150 캜 or less. That is, generally, a plastic substrate, which is a flexible substrate, can not be subjected to a high-temperature heat treatment, so that a metal oxide such as TiO 2 should be fired at a low temperature. However, in the case of the above-mentioned low-temperature firing, the capability of transferring photoelectrons is remarkably deteriorated due to the lack of connectivity between TiO 2 particles.
상기 플라스틱 기판을 적용한 반도체 전극을 제조하는 종래기술로는, 저온 소성이 가능한 페이스트를 기판에 인쇄하여 150℃ 미만에서 화학 소결(Chemical sintering), mechanical pressing, hydrothermal crystallization, electrophoretic deposition, microwave irradiation 방법 등이 있고, 광전극을 별도로 제조한 후 광전극을 플라스틱 기판에 부착하는 방법이 있다. 대한민국 특허 제1045849호에는 (a) 투명하고 구부림이 가능한 제1 전극이 처리된 제1 기판을 준비하는 단계; (b) 입자크기가 10-100 nm의 이산화티탄 나노입자, 에탄올, 아세틸아세톤을 혼합하여 분산시켜 입자크기가 10-100 nm의 이산화티탄 나노입자 콜로이드 용액을 제조하는 단계; (c) 티타늄 이소프로폭사이드, 에탄올, 물, 아세틸아세톤을 혼합하여 초음파 분산하고 교반하여 티타늄 전구체 용액을 제조하고, 상기 입자크기가 10-100 nm의 이산화티탄 나노입자 콜로이드 용액과 상기 티타늄 전구체 용액을 혼합하여 입자크기가 10-100 nm의 이산화티탄 페이스트를 제조하는 단계; (d) 상기 제1 전극의 상부에 상기 입자크기가 10-100 nm의 이산화티탄 페이스트를 도포하고 건조 후 소성하여 제1 무기 산화물층을 형성하는 단계; (e) 입자크기가 100-500 nm의 이산화티탄 나노입자, 에탄올, 아세틸아세톤을 혼합하여 분산시켜 입자크기가 100-500 nm의 이산화티탄 나노입자 콜로이드 용액을 제조하는 단계; (f) 티타늄 이소프로폭사이드, 에탄올, 물, 아세틸아세톤을 혼합하여 초음파 분산하고 교반하여 티타늄 전구체 용액을 제조하고, 상기 입자크기가 100-500 nm의 이산화티탄 나노입자 콜로이드 용액과 상기 티타늄 전구체 용액을 혼합하여 입자크기가 100-500 nm의 이산화티탄 페이스트를 제조하는 단계; (g) 상기 제1 무기 산화물층 상에 상기 입자크기가 100-500 nm의 이산화티탄 페이스트를 도포하고 건조 후 소성하여 제2 무기 산화물층을 형성하는 단계; (h) 상기 제2 무기 산화물층에 여기된 전자를 공급할 수 있는 염료를 흡착시키는 단계; (i) 고분자 전해질 용액을 제조하고 상기 염료가 흡착된 다층 무기 산화물층에 도포하여 전해질층을 형성하는 단계; 및 (j) 상기 전해질층이 도포된 제1 전극 기판에 투명한 제2 전극 및 제2 기판을 접합하는 단계를 포함하는 플렉시블 염료감응 태양전지의 제조방법이 개시되어 있다. 또한, 대한민국 특허 제1068440호에는 전도성 유리기판 상에 유기물질로 코팅하는 전처리공정을 수행하고, 상기 전처리된 전도성 유리기판 상에, 나노입자 산화물 페이스트를 도포하여 450℃ 이상조건으로 고온 소성하여 나노입자 산화물층으로 이루어진 반도체 전극층을 형성하고, 상기 형성된 반도체 전극층을 전도성 유리기판으로부터 분리하고, 상기 분리된 반도체 전극층을 전도성 플라스틱 기판에 접착시키는 공정을 포함하는 플렉서블 염료감응형 태양전지용 반도체 전극의 제조방법이 개시되어 있다.Conventional techniques for manufacturing a semiconductor electrode using the plastic substrate include a method in which a paste capable of low temperature firing is printed on a substrate and subjected to chemical sintering, mechanical pressing, hydrothermal crystallization, electrophoretic deposition, There is a method of separately manufacturing a photoelectrode and attaching the photoelectrode to a plastic substrate. Korean Patent No. 1045849 discloses a method comprising: (a) preparing a first substrate on which a transparent and bendable first electrode is processed; (b) dispersing titanium dioxide nanoparticles having a particle size of 10-100 nm, ethanol and acetylacetone to prepare a colloidal solution of titanium dioxide nanoparticles having a particle size of 10-100 nm; (c) titanium isopropoxide, ethanol, water, and acetylacetone are mixed and dispersed by ultrasonication and stirred to prepare a titanium precursor solution, and the titanium dioxide nanoparticle colloid solution having a particle size of 10-100 nm and the titanium precursor solution To prepare a titanium dioxide paste having a particle size of 10-100 nm; (d) applying a titanium dioxide paste having a particle size of 10-100 nm to an upper portion of the first electrode, and drying and firing the titanium dioxide paste to form a first inorganic oxide layer; (e) dispersing titanium dioxide nanoparticles having a particle size of 100-500 nm, ethanol and acetylacetone to prepare a colloidal solution of titanium dioxide nanoparticles having a particle size of 100-500 nm; (f) titanium isopropoxide, ethanol, water, and acetylacetone are mixed and dispersed by ultrasonication and stirred to prepare a titanium precursor solution, and the titanium dioxide nanoparticle colloid solution having a particle size of 100-500 nm and the titanium precursor solution To prepare a titanium dioxide paste having a particle size of 100 to 500 nm; (g) applying a titanium dioxide paste having a particle size of 100-500 nm to the first inorganic oxide layer, drying and firing the titanium dioxide paste to form a second inorganic oxide layer; (h) adsorbing a dye capable of supplying excited electrons to the second inorganic oxide layer; (i) preparing a polymer electrolyte solution and applying the solution to the multi-layered inorganic oxide layer on which the dye is adsorbed to form an electrolyte layer; And (j) bonding a transparent second electrode and a second substrate to the first electrode substrate coated with the electrolyte layer. Korean Patent No. 1068440 discloses a method in which a pretreatment process of coating an electroconductive glass substrate with an organic material is performed, a nanoparticle oxide paste is applied on the pretreated conductive glass substrate, and the nanoparticle is baked at a temperature of 450 ° C or higher, A method for manufacturing a semiconductor electrode for a flexible dye-sensitized solar cell, comprising: forming a semiconductor electrode layer made of an oxide layer, separating the formed semiconductor electrode layer from a conductive glass substrate, and bonding the separated semiconductor electrode layer to a conductive plastic substrate; Lt; / RTI >
그러나, 상기 문헌을 포함한 종래 기술에 개시된 가요성 광전극 내지 태양전지의 경우 광전극을 구성하는 금속산화물간 결합상태 내지 금속산화물과 기판 사이의 결합이 약해 태양전지의 광전효율과 막의 안정성이 떨어지는 문제가 있거나 복잡다단한 방법에 의해 제조되는 문제점 등이 있다. However, in the case of the flexible optical electrode or the solar cell disclosed in the prior art including the above document, the bonding between the metal oxide constituting the photoelectrode or the bond between the metal oxide and the substrate is weak and the photoelectric efficiency of the solar cell and the stability of the film are inferior Or a problem that is produced by a complicated and complicated method.
따라서 본 발명이 이루고자 하는 기술적 과제는 간단한 저온소성 공정으로도 가요성 광전극에 사용되는 TiO2 등의 금속산화물 입자간의 네트워크 또는 금속산화물 입자와 기판사이에 상호 연결을 획기적으로 증가시켜 태양전지의 광전효율 및 막의 안정성을 높인 가요성 광전극 제조방법과 상기 방법에 의해 제조된 가요성 광전극을 제공하는 것이다. SUMMARY OF THE INVENTION Accordingly, the present invention has been made in view of the above problems, and it is an object of the present invention to provide a method of manufacturing a photovoltaic cell in which the interconnection between metal oxide particles such as TiO 2 , The efficiency and the stability of the film are improved, and a flexible optical electrode manufactured by the above method.
본 발명의 또 다른 목적은 상기 가요성 광전극을 이용하여 염료감응 태양전지의 반도체 필름층의 안정성 확보와 높은 광전 효율을 갖는 태양전지를 제공하는 것이다.It is still another object of the present invention to provide a solar cell having a high photoelectric efficiency and securing the stability of a semiconductor film layer of a dye-sensitized solar cell using the flexible photoelectrode.
상기 기술적 과제를 달성하기 위하여 본 발명은 전도성 가요성 기재상에 형성되는 다공질 제1금속산화물층과 상기 다공질 제1금속산화물층상에 염료를 흡착한 구조를 포함한 가요성 광전극의 제조방법에 있어서, ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬 알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계,; ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계 및; ⅲ)200℃ 이하의 온도에서 저온소성하여 다공질 제1금속산화물층을 형성하는 단계를 포함한 가요성 광전극 제조방법을 제공한다.According to an aspect of the present invention, there is provided a method of manufacturing a flexible photoelectrode including a porous first metal oxide layer formed on a conductive flexible substrate and a structure in which a dye is adsorbed on the porous first metal oxide layer, I) incorporating the first metal oxide nanoparticles into a solvent containing a C6 to C12 linear or branched alkyl alcohol and C1 to C3 halogenated carbon in a volume ratio of 1: 0.1 to 10, to prepare a paste; Ii) applying the paste onto the conductive flexible substrate; And iii) low-temperature baking at a temperature of 200 ° C or lower to form a porous first metal oxide layer.
또한, 본 발명은 ⅳ)UV-O3을 이용하여 다공질 제1금속산화물층에 잔류한 유기물을 제거하는 단계를 더 포함한 가요성 광전극 제조방법을 제공한다.The present invention also provides a flexible photoelectrode manufacturing method further comprising: iv) removing organic matter remaining in the porous first metal oxide layer using UV-O 3 .
또한, 본 발명은 상기 전기전도성을 가진 가요성 기재가 플라스틱 기재상에 금속, 금속 질화물, 금속 산화물, 탄소화합물, 또는 전도성 고분자로 이루어진 평균 두께 1 내지 1000nm인 전도성 필름층을 형성하여 이루어진 것임을 특징으로 하는 가요성 광전극 제조방법을 제공한다.Further, the present invention is characterized in that the flexible substrate having electrical conductivity is formed by forming a conductive film layer having an average thickness of 1 to 1000 nm made of a metal, a metal nitride, a metal oxide, a carbon compound, or a conductive polymer on a plastic substrate The present invention also provides a method of manufacturing a flexible optical electrode.
또한, 본 발명은 상기 제1 및 제2금속산화물이 주석(Sn)산화물, 안티몬(Sb), 나이오븀(Nb) 또는 불소 도핑된 주석(Sn)산화물, 인듐(In)산화물, 주석 도핑된 인듐(In)산화물, 아연(Zn)산화물, 알루미늄(Al), 붕소(B), 갈륨(Ga), 수소(H), 인듐(In), 이트륨(Y), 타이타늄(Ti), 실리콘(Si) 또는 주석(Sn) 도핑된 아연(Zn)산화물, 마그네슘(Mg)산화물, 캐드뮴(Cd)산화물, 마그네슘아연(MgZn)산화물, 인듐아연(InZn)산화물, 구리알루미늄(CuAl)산화물, 실버(Ag)산화물, 갈륨(Ga)산화물, 아연주석산화물(ZnSnO), 타이타늄산화물(TiO2) 및 아연인듐주석(ZIS)산화물, 니켈(Ni)산화물, 로듐(Rh)산화물, 루세늄(Ru)산화물, 이리듐(Ir)산화물, 구리(Cu)산화물, 코발트(Co)산화물, 텅스텐(W)산화물, 티타늄(Ti)산화물, 지르코늄(Zr)산화물, 스트론튬(Sr)산화물, 란타넘(La)산화물, 바나듐(V)산화물, 몰리브데넘(Mo)산화물, 나이오븀(Nb)산화물, 알루미늄(Al)산화물, 이트늄(Y)산화물, 스칸듐(Sc)산화물, 사마륨(Sm)산화물, 스트론튬타이타늄(SrTi)산화물로 이루어진 군으로부터 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.Further, the present invention is characterized in that the first and second metal oxides are selected from the group consisting of tin (Sn) oxide, antimony (Sb), niobium (Nb) or fluorine doped tin (Sn) oxide, indium (In) oxide, zinc (Zn) oxide, aluminum (Al), boron (B), gallium (Ga), hydrogen (H), indium (In), yttrium (Y), titanium (Ti) Or tin (Sn) doped zinc oxide, magnesium oxide, cadmium oxide, magnesium zinc oxide, indium zinc oxide, copper aluminum oxide, silver ) Oxide, gallium (Ga) oxide, zinc tin oxide (ZnSnO), titanium oxide (TiO2) and zinc indium tin (ZIS) oxide, nickel oxide, rhodium oxide, ruthenium oxide, iridium (Ir) oxide, copper (Cu) oxide, cobalt (Co) oxide, tungsten (W) oxide, titanium (Ti) oxide, zirconium (Zr) oxide, strontium (Sr) oxide, lanthanum (La) oxide, vanadium V) oxide, molybdenum (Mo) oxide, Characterized in that it is at least one member selected from the group consisting of niobium (Nb) oxide, aluminum (Al) oxide, yttrium (Y) oxide, scandium (Sc) oxide, samarium (Sm) oxide, strontium titanium A method of manufacturing a photoelectrode is provided.
또한, 본 발명은 상기 금속질화물이 질화타이타늄(Ti), 질화지르코늄(Zr), 질화하프늄, 질화나이오븀(Nb), 질화탄탈륨(Ta), 질화바나듐, 질화크롬(Cr), 질화몰리브데늄(Mo),질화텅스텐(W), 질화알루미늄(Al), 질화갈륨(Ga), 질화인듐(In), 질화실리콘(Si) 및 질화게르마늄(Ge)으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.Further, the present invention is characterized in that the metal nitride is selected from the group consisting of titanium nitride (Ti), zirconium nitride (Zr), hafnium nitride, niobium nitride, tantalum nitride (Ta), vanadium nitride, chromium (Cr), molybdenum nitride At least one selected from the group consisting of molybdenum (Mo), tungsten nitride (W), aluminum nitride (Al), gallium nitride (Ga), indium nitride (In), silicon nitride (Si), and germanium nitride The present invention also provides a method of manufacturing a flexible optical electrode.
또한, 본 발명은 상기 탄소화합물이 활성탄, 흑연, 카본 나노튜브, 카본블랙, 그라펜으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.The present invention also provides a method of manufacturing a flexible photoelectrode characterized in that the carbon compound is at least one selected from the group consisting of activated carbon, graphite, carbon nanotube, carbon black and graphene.
또한, 본 발명은 상기 전도성 고분자가 PEDOT (폴리(3,4-에틸렌디옥시티오펜))- PSS(폴리(스티렌설포네이트)), 폴리아닐린-CSA, 펜타센, 폴리아세틸렌, P3HT(폴리(3-헥실티오펜), 폴리실록산 카르바졸, 폴리아닐린, 폴리에틸렌 옥사이드, (폴리(1-메톡시-4-(0-디스퍼스레드1)-2,5-페닐렌-비닐렌), 폴리인돌, 폴리카르바졸, 폴리피리디아진, 폴리이소티아나프탈렌, 폴리페닐렌 설파이드, 폴리비닐피리딘, 폴리티오펜, 폴리플루오렌, 폴리피리딘, 폴리피롤, 폴리설퍼나이트라이드 및 이들의 공중합체로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.The present invention also provides a method for producing a conductive polymer, wherein the conductive polymer is at least one selected from the group consisting of PEDOT (poly (3,4-ethylenedioxythiophene) -PSS (poly (styrenesulfonate)), polyaniline-CSA, pentacene, polyacetylene, Hexylthiophene), polysiloxane carbazole, polyaniline, polyethylene oxide, (poly (1-methoxy-4- (0 -dispersed red) At least one member selected from the group consisting of polypyridazines, polyisothianaphthalenes, polyphenylene sulfides, polyvinylpyridines, polythiophenes, polyfluorenes, polypyridines, polypyrroles, polysulfuronitrides, and copolymers thereof The present invention also provides a method of manufacturing a flexible photoelectrode.
또한, 본 발명은 상기 알킬 알콜이 C7 내지 C10의 직쇄 알킬알콜인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.The present invention also provides a process for producing a flexible photoelectrode characterized in that the alkyl alcohol is a C7 to C10 linear alkyl alcohol.
또한, 본 발명은 상기 할로겐화탄소가 사염화탄소, 옥살릴 염화물(C2Cl2O2), Chloroacetyl chloride(C2H2Cl2O), Thionyl chloride(SOCl2), Tetrachloroethylene(C2Cl4), 1,1,2,2-Tetrachloroethane(C2H2Cl4), 2,3-Dichloropropionyl chloride(C3H3Cl3O), Dichloroacetyl chloride(C2HCl3O), 3-Chloropropionyl chloride(C3H4Cl2O) 및 2,3-Dichloropropionyl chloride(CH2ClCHClCOCl)로 구성된 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법을 제공한다.The present invention also relates to a process for the preparation of the above-mentioned halogenated carbons, wherein the halogenated carbon is at least one selected from the group consisting of carbon tetrachloride, oxalyl chloride (C2Cl2O2), chloroacetyl chloride (C2H2Cl2O), thionyl chloride (SOCl2), tetrachlorethylene (C2Cl4), 1,1,2,2- 3-Dichloropropionyl chloride (C3H3Cl3O), Dichloroacetyl chloride (C2HCl3O), 3-Chloropropionyl chloride (C3H4Cl2O) and 2,3-Dichloropropionyl chloride (CH 2 ClCHClCOCl ) flexible optical electrode produced, characterized in that at least one member selected from the group consisting of ≪ / RTI >
본 발명의 다른 목적을 달성하기 위하여, 본 발명은 상기 방법으로 제조된 가요성 광전극을 제공한다.According to another aspect of the present invention, there is provided a flexible photoelectrode fabricated by the above method.
본 발명의 또 다른 목적을 달성하기 위하여 본 발명은 상기 가요성 광전극을 포함한 염료감응형 태양전지를 제공한다. According to another aspect of the present invention, there is provided a dye-sensitized solar cell including the flexible photoelectrode.
본 발명은 플렉서블 기판을 사용하여 저온소성이 요구되는 조건하에서도 가요성 광전극에 사용되는 금속산화물 입자 상호간 및 금속산화물 입자와 기판 사이에 상호 연결을 증가시켜 광전효율 및 안정성이 우수한 가요성 광전극 및 염료감응형 태양전지를 제조할 수 있다. The present invention relates to a method of manufacturing a flexible photoelectrode, which uses a flexible substrate to increase interconnection between metal oxide particles used for flexible optical electrodes and between metal oxide particles and a substrate under conditions requiring low temperature firing, And a dye-sensitized solar cell.
도 1은 본 발명에 따른 가요성 광전극 및 염료감응형 태양전지의 제조방법을 설명하기 위한 공정의 개략도
도 2는 본 발명의 실시예 1과 비교예 1에서 제조한 페이스트의 점도 및 흐름성을 대비한 사진
도 3은 본 발명에 따른 UV-O3을 처리함으로서 다공질막 사이에 불순물이 없고 더 투명한 가요성 광전극의 사진
도 4는 본 발명에서 1-Octanol과 사염화 탄소로 인해 TiO2끼리 화학적 결합을 나타낸 모식도
도 5은 본 발명의 실시예 1 및 비교예 1에 따른 염료감응 태양전지의 전류-전압 곡선을 비교하여 도시한 그래프1 is a schematic view of a process for explaining a method of manufacturing a flexible photoelectrode and a dye-sensitized solar cell according to the present invention
2 is a photograph showing the viscosity and flowability of the paste prepared in Example 1 of the present invention and Comparative Example 1
Figure 3 is a photograph of a more transparent flexible photo electrode without impurities between the porous films by treating UV-O 3 according to the present invention
4 is a schematic view showing chemical bonding between TiO 2 due to 1-Octanol and carbon tetrachloride in the present invention.
5 is a graph showing a comparison of current-voltage curves of the dye-sensitized solar cell according to Example 1 and Comparative Example 1 of the present invention
이하에서 본 명세서에 첨부된 도면을 참조하여 본 발명을 상세히 설명한다. 본 명세서에서 "나노"라는 용어는 0.1 내지 1,000 nm 범위의 나노 스케일을 의미하며, 명세서에 기재된 "나노 입자"라는 용어는 평균입도가 나노 스케일인 모든 형태의 입자를 포함하며, '저온소성' 또는 '저온소결'의 용어는 200℃ 이하의 온도에서 화학적 소결(chemical sintering)반응을 수행함을 의미한다. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described in detail with reference to the drawings attached hereto. As used herein, the term "nano" refers to nanoscale in the range of 0.1 to 1,000 nm, and the term "nanoparticle" as used in the specification includes all types of particles having an average particle size of nanoscale, The term 'low-temperature sintering' means that a chemical sintering reaction is performed at a temperature of 200 ° C or lower.
도 1은 본 발명에 따른 가요성 광전극 및 염료감응형 태양전지의 제조방법을 설명하기 위한 공정의 개략도이다. 도 1에서 볼 수 있는 바와 같이, 본 발명은 가요성 광전극 제조방법은 전도성 가요성 기재상에 형성되는 다공질 제1금속산화물층과 상기 다공질 제1금속산화물층상에 염료를 흡착한 구조를 포함한 광전극의 제조방법에 있어서, ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬 알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계,; ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계 및; ⅲ)200℃ 이하의 온도에서 저온소결하여 다공질 제1금속산화물층을 형성하는 단계를 포함한다.1 is a schematic view of a process for explaining a method of manufacturing a flexible photoelectrode and a dye-sensitized solar cell according to the present invention. As shown in FIG. 1, the present invention provides a method for manufacturing a flexible photoelectrode, comprising the steps of: forming a first porous metal oxide layer on a conductive flexible substrate; and a second porous metal oxide layer on the porous first metal oxide layer, The first metal oxide nanoparticles are mixed in a solvent containing i) a straight chain or branched alkyl alcohol of C6 to C12 and C1 to C3 halogenated carbon in a volume ratio of 1: 0.1 to 10, A manufacturing step; Ii) applying the paste onto the conductive flexible substrate; And iii) low-temperature sintering at a temperature of 200 DEG C or less to form a porous first metal oxide layer.
본 발명의 가요성 광전극 제조방법은 전도성 가요성 기재상에 형성되는 다공질 제1금속산화물층과 상기 다공질 제1금속산화물층상에 염료를 흡착한 구조를 포함한 광전극을 제조하는 방법이다. 본 발명에 있어서 전도성 가요성 기재(103)는 통상 전도성을 가지고 있으면서 가요성인 재질, 예를 들면 금속 또는 비전도성이고 가요성인 플라스틱 등과 같은 기재(101)상에 전도성층(102)을 형성한 구조의 것을 사용할 수 있다. 또한 전도성층(102)은 FTO (F-doped SnO2:SnO2:F),ITO,평균 두께가 1 내지 1000 nm인 금속, 금속 질화물, 제2금속 산화물, 탄소화합물, 또는 전도성 고분자를 포함하는 전도성 필름이 코팅될 수 있다. 따라서, 도 1에 도시된 것처럼, 상기 광전극(110)은 가요성 기판(101), 상기 가요성 기판(101) 위에 형성된 전도성 필름(102) 및 염료가 흡착된 다공질 제1금속산화물층(107)을 포함할 수 있다.The method of manufacturing a flexible photoelectrode according to the present invention is a method of manufacturing a photoelectrode including a porous first metal oxide layer formed on a conductive flexible substrate and a structure in which a dye is adsorbed on the porous first metal oxide layer. In the present invention, the conductive
본 발명에서 상기 전도성층으로 사용가능한 금속은 특별히 제한되지 않으며 통상의 금속이 적용될 수 있으며, 금속 질화물은 IVB족 금속원소의 질화물, VB족 금속원소의 질화물, VIB족 금속원소의 질화물, 질화알루미늄, 질화갈륨, 질화인듐, 질화실리콘, 질화게르마늄으로 이루어진 군으로부터 1종 이상을 선택할 수 있다. The metal that can be used as the conductive layer in the present invention is not particularly limited and a normal metal may be used. The metal nitride may be a nitride of a group IVB metal element, a nitride of a group VB metal element, a nitride of a group VIB metal element, At least one selected from the group consisting of gallium nitride, indium nitride, silicon nitride, and germanium nitride.
또한 본 발명에서 사용될 수 있는 제1 및 제2금속산화물은 주석(Sn)산화물, 안티몬(Sb), 나이오븀(Nb) 또는 불소 도핑된 주석(Sn)산화물, 인듐(In)산화물, 주석 도핑된 인듐(In)산화물, 아연(Zn)산화물, 알루미늄(Al), 붕소(B), 갈륨(Ga), 수소(H), 인듐(In), 이트륨(Y), 타이타늄(Ti), 실리콘(Si) 또는 주석(Sn) 도핑된 아연(Zn)산화물, 마그네슘(Mg)산화물, 캐드뮴(Cd)산화물, 마그네슘아연(MgZn)산화물, 인듐아연(InZn)산화물, 구리알루미늄(CuAl)산화물, 실버(Ag)산화물, 갈륨(Ga)산화물, 아연주석산화물(ZnSnO), 타이타늄산화물(TiO2) 및 아연인듐주석(ZIS)산화물, 니켈(Ni)산화물, 로듐(Rh)산화물, 루세늄(Ru)산화물, 이리듐(Ir)산화물, 구리(Cu)산화물, 코발트(Co)산화물, 텅스텐(W)산화물, 티타늄(Ti)산화물, 지르코늄(Zr)산화물, 스트론튬(Sr)산화물, 란타넘(La)산화물, 바나듐(V)산화물, 몰리브데넘(Mo)산화물, 나이오븀(Nb)산화물, 알루미늄(Al)산화물, 이트늄(Y)산화물, 스칸듐(Sc)산화물, 사마륨(Sm)산화물, 스트론튬타이타늄(SrTi)산화물로 이루어진 군에서 선택된 1종 이상을 사용할 수 있고, 바람직하게는 티타늄산화물을 사용한다.The first and second metal oxides that may be used in the present invention may also be selected from the group consisting of tin (Sn) oxide, antimony (Sb), niobium (Nb) or fluorine doped tin (Sn) (Al), boron (B), gallium (Ga), hydrogen (H), indium (In), yttrium (Y), titanium (Ti), silicon (Si), indium (In) ) Or tin (Sn) -doped zinc oxide, magnesium oxide, cadmium oxide, magnesium zinc oxide, indium zinc oxide, copper aluminum oxide, silver (Ag) oxide, gallium (Ga) oxide, zinc tin oxide (ZnSnO), titanium oxide (TiO2) and zinc indium tin (ZIS) oxide, nickel oxide, rhodium oxide, ruthenium oxide, A rare earth element such as iridium (Ir) oxide, copper (Cu) oxide, cobalt (Co) oxide, tungsten (W) oxide, titanium (Ti) oxide, zirconium (Zr) oxide, strontium (Sr) (V) oxide, molybdenum (1) selected from the group consisting of a metal oxide (Mo) oxide, a niobium (Nb) oxide, an aluminum (Al) oxide, an yttrium (Y) oxide, a scandium (Sc) oxide, a samarium (Sm) oxide and a strontium titanium Or more, and titanium oxide is preferably used.
또한, 본 발명에서 사용가능한 탄소화합물로는 활성탄, 흑연, 카본 나노튜브, 카본블랙, 그라펜 또는 이들의 혼합물 등을 들 수 있으나, 이에 제한되는 것은 아니다. 또한 전도성 고분자로는 PEDOT (폴리(3,4-에틸렌디옥시티오펜))- PSS(폴리(스티렌설포네이트)), 폴리아닐린-CSA, 펜타센, 폴리아세틸렌, P3HT(폴리(3-헥실티오펜), 폴리실록산 카르바졸, 폴리아닐린, 폴리에틸렌 옥사이드, (폴리(1-메톡시-4-(0-디스퍼스레드1)-2,5-페닐렌-비닐렌), 폴리인돌, 폴리카르바졸, 폴리피리디아진, 폴리이소티아나프탈렌, 폴리페닐렌 설파이드, 폴리비닐피리딘, 폴리티오펜, 폴리플루오렌, 폴리피리딘, 폴리피롤, 폴리설퍼나이트라이드 및 이들의 공중합체로 이루어진 군으로부터 1종 이상 선택하여 사용할 수 있다.Examples of carbon compounds usable in the present invention include, but are not limited to, activated carbon, graphite, carbon nanotubes, carbon black, graphene, and mixtures thereof. Examples of the conductive polymer include PEDOT (poly (3,4-ethylenedioxythiophene) -PSS (poly (styrenesulfonate)), polyaniline-CSA, pentacene, polyacetylene, P3HT (poly (3-hexylthiophene) , Polysiloxane carbazole, polyaniline, polyethylene oxide, (poly (1-methoxy-4- (0 -dispersed 1) -2,5-phenylene-vinylene), polyindole, polycarbazole, At least one selected from the group consisting of polyisoprene, polyisoprenesulfone, polyisothianaphthalene, polyphenylene sulfide, polyvinylpyridine, polythiophene, polyfluorene, polypyridine, polypyrrole, polysulfuron nitride and copolymers thereof .
본 발명의 가요성 광전극 제조방법은 ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계를 포함한다. 상기 알킬알콜과 할로겐화탄소를 포함한 용매는 제1금속산화물 나노입자와 혼합되어 페이스트상으로 만들어지며 타 용매 대비시 동일 농도하에서 페이스트의 점도를 높인다. 상기 용매를 적용한 페이스트의 상대적으로 높은 점도는 할로겐화탄소의 할로겐원소와 제1금속산화물 나노입자의 표면에 존재하는 히드록시기(-OH)간 수소결합으로 인한 것으로 추정된다. 할로겐화탄소와 제1금속산화물간 수소결합으로 인해 점도의 상승과 함께 제1금속산화물간 거리가 보다 가까워져 알킬알콜 및 할로겐화탄소의 반응으로 수행되는 화학적 소결반응시 제1금속산화물 상호간 및 제1금속산화물과 전도성 가요성 기재와의 결합력을 높일 수 있고 광전환효율을 보다 높일 수 있다. 또한, 이러한 페이스트의 높은 점도는 전도성 가요성 기재상에 페이스트를 도포할 경우 도포층의 두께조절을 용이하게 해준다. 도 2는 본 발명의 실시예 1과 비교예 1에서 제조한 페이스트의 점도 및 흐름성을 대비한 사진이다. 도 2에서 볼 수 있는 바와 같이, 알킬알콜과 할로겐화탄소의 혼합용매를 적용한 페이스트의 점도가 알킬알콜만을 사용한 경우보다 점도가 높고 퍼짐성이 낮음을 알 수 있다. The method for producing a flexible photoelectrode of the present invention comprises the steps of (i) mixing a first metal oxide nanoparticle into a solvent containing a C6 to C12 linear or branched alkyl alcohol and C1 to C3 halogenated carbon in a volume ratio of 1: 0.1 to 10 Thereby producing a paste. The solvent containing the alkyl alcohol and the halogenated carbon is mixed with the first metal oxide nanoparticles to form a paste, and the viscosity of the paste is increased under the same concentration as the other solvents. The relatively high viscosity of the paste to which the solvent is applied is presumably due to the hydrogen bonding between the halogen element of the halogenated carbon and the hydroxyl group (-OH) existing on the surface of the first metal oxide nanoparticle. The distance between the first metal oxides becomes closer with the increase of the viscosity due to the hydrogen bonding between the halogenated carbon and the first metal oxide, so that in the chemical sintering reaction performed by the reaction of the alkyl alcohol and the halogenated carbon, And the conductive flexible substrate can be increased and the light conversion efficiency can be further increased. The high viscosity of such a paste also facilitates the adjustment of the thickness of the applied layer when the paste is applied on the conductive flexible substrate. FIG. 2 is a photograph showing the viscosity and flowability of the paste prepared in Example 1 of the present invention and Comparative Example 1. As can be seen from FIG. 2, the viscosity of the paste to which the mixed solvent of alkyl alcohol and halogenated carbon is applied is higher and the spreadability is lower than when the alkyl alcohol alone is used.
본 발명에 있어서 상기 알킬알콜은 C6 내지 C12의 직쇄 또는 분지쇄 알킬알콜인 것이 바람직하고, C7 내지 C10의 직쇄 알킬알콜인 것이 더욱 바람직하다. 상기 알킬알콜은 화학적 소결시 탈수반응을 통해 제1금속산화물 입자간 및 제1금속산화물과 전도성 가요성 기재간 결합을 이루어지게 한다. 상기 알킬알콜의 경우 화학적 소결시 반응성을 높이기 위하여 온도가 높아야 하기 때문에 높은 끓는점을 갖는 것이 바람직하다. 다만, 통상 투명 플라스틱 소재인 가요성 기재의 변형이나 발화를 방지하기 위하여 소결이 200℃ 이하, 보다 바람직하게는 150℃ 이하의 온도에서 수행되는 것을 고려하면 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 적절한 점도와 물성을 갖는 알킬알콜을 선택할 수 있을 것이다.In the present invention, the alkyl alcohol is preferably a C6 to C12 linear or branched alkyl alcohol, more preferably a C7 to C10 linear alkyl alcohol. The alkyl alcohol causes a bond between the first metal oxide particles and the first metal oxide and the conductive flexible substrate through a dehydration reaction during chemical sintering. In the case of the above-mentioned alkyl alcohol, it is preferable to have a high boiling point because the temperature must be high in order to increase the reactivity in chemical sintering. However, considering that sintering is carried out at a temperature of 200 ° C or less, more preferably 150 ° C or less in order to prevent deformation or ignition of a flexible substrate, which is a transparent plastic material, ordinary knowledge in the technical field of the present invention The person skilled in the art will be able to select alkyl alcohols having appropriate viscosity and physical properties.
또한, 본 발명에 있어서 상기 할로겐화탄소는 C1 내지 C3의 할로겐화탄소인 것이 바람직하고, 구체적으로 상기 할로겐화탄소의 예로는 사염화탄소, 옥살릴 염화물(C2Cl2O2), Chloroacetyl chloride(C2H2Cl2O), Thionyl chloride(SOCl2), Tetrachloroethylene(C2Cl4), 1,1,2,2-Tetrachloroethane(C2H2Cl4), 2,3-Dichloropropionyl chloride(C3H3Cl3O), Dichloroacetyl chloride(C2HCl3O), 3-Chloropropionyl chloride(C3H4Cl2O) 및 2,3-Dichloropropionyl chloride(CH2ClCHClCOCl)로 구성된 군으로부터 선택된 1종 이상인 것이 가장 바람직하다. 전술한 바와 같이 제1금속산화물 입자간 및 제1금속산화물 입자와 전도성 가요성 기재 중 전도성층과 수소결합을 통해 입자간 거리를 가깝게 하고 페이스트의 점도를 높여 도포성을 개선하는 역할을 수행한다. In the present invention, the halogenated carbon is preferably a C1 to C3 halogenated carbon. Examples of the halogenated carbon include carbon tetrachloride, oxalyl chloride (C2Cl2O2), chlorooacetyl chloride (C2H2Cl2O), thionyl chloride (SOCl2) Dichloroacetyl chloride (C2HCl3O), 3-Chloropropionyl chloride (C3H4Cl2O) and 2,3-Dichloropropionyl chloride (CH 2 < RTI ID = 0.0 > ClCHClCOCl). ≪ / RTI > As described above, the first metal oxide particles and the first metal oxide particles and the conductive layer of the conductive flexible substrate are brought close to each other through hydrogen bonding to increase the viscosity of the paste, thereby improving the coatability.
본 발명에 있어서 제1금속산화물과 용매의 배합비율은 특별히 제한되는 것은 아니며, 제1금속산화물의 입도, 페이스트의 점도 및 저온소성 후 형성되는 제1금속산화물층의 두께 및 공극비율을 고려하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 적절히 조절할 수 있을 것이다. 본 발명의 실시예에서는 제1금속산화물 분말과 용매의 비율은 무게비로 1:0.1 내지 10 범위로 조절을 하였다. In the present invention, the compounding ratio of the first metal oxide and the solvent is not particularly limited, and the mixing ratio of the first metal oxide and the solvent is determined in consideration of the particle size of the first metal oxide, the viscosity of the paste, the thickness of the first metal oxide layer formed after the low- Those skilled in the art will appreciate that those skilled in the art may appropriately control the invention. In the embodiment of the present invention, the ratio of the first metal oxide powder to the solvent is adjusted in the range of 1: 0.1 to 10 by weight.
본 발명의 가요성 광전극 제조방법은 ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계를 포함한다. 도포방법은 공지의 페이스트 도포방법, 예를 들면 닥터블레이드 등을 통해 수행될 수 있다. The method for producing a flexible photoelectrode of the present invention comprises the step of: (ii) applying the paste onto the conductive flexible substrate. The application method can be carried out by a known paste application method, for example, a doctor blade or the like.
본 발명의 가요성 광전극 제조방법은 ⅲ)200℃ 이하의 온도에서 저온소결하여 다공질 제1금속산화물층을 형성하는 단계를 포함한다. FTO나 ITO같은 TCO(Transparent conductive oxide)(103) 기판 위에 코팅 한 후(104) 150 ℃ 이하 저온 소성하여 금속산화물 나노입자를 포함하는 다공질막 필름(105)을 제조하게 된다. The method of manufacturing a flexible photoelectrode of the present invention includes the step of iii) low temperature sintering at a temperature of 200 DEG C or less to form a porous first metal oxide layer. (104) such as FTO or ITO (104) and then baked at a low temperature of 150 DEG C or less to produce a porous film film (105) containing metal oxide nanoparticles.
본 발명의 가요성 광전극 제조방법은 ⅳ)다공질 제1금속산화물층에 잔류한 유기물을 제거하는 단계를 더 포함할 수 있다. 유기물 제거는 공지의 유기물 분해공정인 UV-O3을 처리함으로서 다공질막 필름내에 잔류한 불순물을 제거하게 된다. 이렇게 불순물이 제거된 필름은 도 3에서 보듯이 좀 더 투명한 제1금속산화물 다공질막 필름(106)을 제조할 수 있다. 그런 다음 감광성 염료를 흡착시켜 염료가 흡착된 제1금속산화물층(107)을 형성하여 광전극(110)을 제조한다. 상대전극에 필요한 전도성 기판위(103)에 촉매전극 물질을(121) 코팅하고 소성하여 제작한 후 상대전극(120)을 제조한다. 그런 다음 광전극과 상대전극을 열융착 필름(140)을 이용하여 붙인 다음 그사이에 전해질(130)을 주입하여 태양전지를 제조한다. The flexible photoelectrode manufacturing method of the present invention may further comprise the step of iv) removing the organic matter remaining in the porous first metal oxide layer. Removal of organic substances removes impurities remaining in the porous film by treating UV-O 3 , a known organic decomposition process. The impurity-removed film can produce a more transparent first metal oxide
한편 상기 염료흡착 제1금속산화물 다공질막(107)은 금속산화물 나노입자층 포함한 광전극을 이루는 부분을 형성하기 위해서, TiO2등을 이용하여 나노입자 필름을 형성한 것을 의미한다. 이때 상기 광전극에 형성된 다공질막의 두께도 특별히 한정되지 않으나, 바람직하게 1 내지 40 ㎛ 일 수 있다. On the other hand, the dye-adsorbing first metal oxide
또한 상기 감광성 염료는 밴드갭 (Band Gap) 이 1.55 eV 내지 3.1 eV을 가져 가시광선을 흡수할 수 있는 염료를 사용할 수 있으며, 예를 들면 금속 또는 금속 복합체를 포함하는 유-무기 복합염료, 유기 염료 또는 이들의 혼합물을 포함할 수 있다. 상기 유-무기 복합염료의 예로는 알루미늄(Al), 백금(Pt), 팔라듐(Pd), 유로퓸(Eu), 납(Pb), 이리듐(Ir), 루테늄(Ru) 및 이들의 복합체로 이루어지는 군에서 선택된 원소를 포함하는 유-무기 복합염료일 수 있다.The photosensitive dye may have a band gap of 1.55 eV to 3.1 eV and may absorb visible light. Examples of the dye include organic-inorganic composite dyes including metals or metal complexes, organic dyes Or mixtures thereof. Examples of the organic-inorganic composite dye include a group consisting of aluminum (Al), platinum (Pt), palladium (Pd), europium (Eu), lead (Pb), iridium (Ir), ruthenium Inorganic hybrid dyes including the elements selected from the group consisting of the following.
상대전극(counter electrode, 120)을 이루는 부분을 형성하기 위해서 Pt 등을 이용한 나노입자금속필름을 이용하여 형성시킨다. 상대전극을 이루는 상기 나노입자금속으로는 백금(Pt), 활성탄(activated carbon), 흑연(graphite), 카본 나노튜브, 카본블랙, p-형 반도체, PEDOT (폴리(3,4-에틸렌디옥시티오펜))- PSS(폴리(스티렌설포네이트)), 폴리아닐린-CSA, 펜타센, 폴리아세틸렌, P3HT(폴리(3-헥실티오펜), 폴리실록산 카르바졸, 폴리아닐린, 폴리에틸렌 옥사이드, (폴리(1-메톡시-4-(0-디스퍼스레드1)-2,5-페닐렌-비닐렌), 폴리인돌, 폴리카르바졸, 폴리피리디아진, 폴리이소티아나프탈렌, 폴리페닐렌 설파이드, 폴리비닐피리딘, 폴리티오펜, 폴리플루오렌, 폴리피리딘, 폴리피롤, 폴리설퍼나이트라이드 및 이들의 유도체 및 이들의 공중합체 또는 이들의 복합체로 이루어진 군으로부터 1종 이상 선택되는 것이 바람직하다.And is formed using a nanoparticle metal film using Pt or the like to form a counter electrode (120). Examples of the nanoparticle metal forming the counter electrode include platinum (Pt), activated carbon, graphite, carbon nanotube, carbon black, p-type semiconductor, PEDOT (poly (3,4- ) -PSS (poly (styrenesulfonate)), polyaniline-CSA, pentacene, polyacetylene, P3HT (poly (3-hexylthiophene), polysiloxane carbazole, polyaniline, polyethylene oxide, Polyphenylenevinylene), poly (vinylidene fluoride), poly (vinylidene fluoride), poly (vinylidene fluoride), poly At least one selected from the group consisting of thiophene, polyfluorene, polypyridine, polypyrrole, polysulfuron nitride and derivatives thereof and copolymers thereof or a complex thereof.
상기 전해질(130)은 도 1에서 설명의 편의상 간단히 채워진 상태로 도시되어 있지만, 실제로는 광전극(110) 및 상대전극(120) 사이의 공간에서 다공질막(106)인 제1금속산화물 나노입자층의 내부에 균일하게 분산될 수 있다. 상기 전해질은 산화-환원에 의해 상대전극으로부터 전자를 받아 광전극의 염료에 전달하는 역할을 하는 산화-환원 유도체 포함하며, 통상의 염료감응 태양전지에 사용가능한 것이면 특히 한정되지 않는다. 구체적으로 산화-환원 유도체는 요오드(I)계, 브롬(Br)계, 코발트(Co)계, 황화시안(SCN-)계, 셀레늄화시안(SeCN-)계를 함유하는 전해질로 이루어진 군으로부터 1종 이상 선택되는 것이 바람직하다. 또한 상기 전해질은 폴리비닐리덴플로라이드-co-폴리헥사플루오르프로필렌, 폴리아크릴로니트릴, 폴리에틸렌옥사이드 및 폴리알킬아크릴레이트로 이루어진 군에서 선택된 하나 이상의 고분자를 함유할 수 있다. 또한, 상기 전해질은 실리카 및 TiO2 나노입자로 이루어진 군에서 선택된 하나 이상의 무기입자를 함유하는 고분자 겔 전해질일 수 있다.1, the
또한 상기 태양전지는 상기 반도체 전극과 상대전극을 봉합하기 위한 열융착 고분자 필름 또는 페이스트인 접착제를 더욱 포함할 수 있으며, 이때 사용되는 접착제는 통상의 물질을 사용할 수 있으므로 그 종류가 특별히 한정되지는 않는다.In addition, the solar cell may further include a thermally fusible polymer film or an adhesive, which is a paste, for sealing the semiconductor electrode and the counter electrode. The type of adhesive used is not particularly limited as the adhesive can be made of conventional materials .
이하 실시예를 통해 본 발명을 보다 상세히 설명한다. 그러나 하기 실시예는 본 발명의 이해를 돕기 위한 예시적인 것으로서, 본 발명의 범위가 이에 한정되는 것은 아니다. Hereinafter, the present invention will be described in more detail with reference to examples. However, the following examples are provided for illustrative purposes only, and the scope of the present invention is not limited thereto.
저온소성용 금속산화물 페이스트 준비(TiOPreparation of metal oxide paste for low-temperature firing (TiO 22 paste 제조) paste manufacture)
상용 TiO2 powder(Degussa,P25)의 입자 응결 방지와 수분 및 유기물 제거를 위해Acetylacetone (Sigma-Aldrich)를 1:1로 혼합 후 500 ℃에서 소성하였다. 그 후 전처리 된 TiO2 분말, 1-Octanol(Sigma-Aldrich), CCl4(Sigma-Aldrich)를 각각 1 g. l㎖, l㎖의 비율로 혼합 후 10 ~ 20분 Ultrasound homogenizer (Ulsso hitech co,ltd, USA)처리 후 70℃, 500 rpm/s에서 12시간 교반하여 페이스트를 제조하였다(Paste-B, 실시예 1용). Acetylacetone (Sigma-Aldrich) was mixed at a ratio of 1: 1 to prevent particle coagulation of the commercially available TiO 2 powder (Degussa, P25) and to remove water and organic matter. The pretreated TiO 2 powder, 1-Octanol (Sigma-Aldrich), and CCl 4 (Sigma-Aldrich) (Paste-B, manufactured by Paste-B Co., Ltd., USA), and the mixture was stirred for 10 to 20 minutes at 70 ° C and 500 rpm / s for 12 hours with an ultrasonic homogenizer (Ulsso hitech co, 1).
이와 별개로 CCl4첨가 유/무에 따른 점도변화를 측정하기 위해 TiO2 분말 1g과 1-Octanol 2㎖만을 사용한 것을 제외하고는 동일한 조건으로 페이스트를 제조하였다(Paste-A, 비교예 1용). Separately, a paste was prepared under the same conditions except that only 1 g of TiO 2 powder and 2 ml of 1-octanol were used to measure the viscosity change depending on the presence / absence of CCl 4 (Paste-A, for Comparative Example 1) .
비교예 1Comparative Example 1
(광전극의 제조)(Fabrication of photoelectrode)
본 발명의 가요성 광전극의 제조는 원래 전도성 가요성 기판을 사용하여야 하나 가요성을 제외하고는 전기화학적 특성이 다를 이유가 없으므로 광전극에 사용되는 기판으로는 비가요성 전도성 기판인 fluorine doped tin oxide glass(8 Ω/Sq., Pilkington, USA)을 사용하였다. FTO glass에 유기물을 제거하기 위하여 (1)Mucasol(Sigma-Aldrich), (2)유기용매 세척, (3)UV-03표면처리 순서로 클리닝하였다. 세척이 끝난 FTO glass 위에 닥터 블레이드 방법을 이용하여 태양전지의 면적은 0.25㎠로 하고 위에서 만든 paste A를 코팅하고 전기로를 이용하여 150℃에서 30분 소결 , TiO2 전극은 UV-O3표먼처리를 진행하였다. 챔버 안에 UV light (wavelength k = 185, 254 nm)를 일정간격 유지후 30분동안 유지시켜주었다. 그 후 TiO2 전극막이 코팅된 FTO glass는 N-719 (0.5 mM ethanolic solution of cis-diisothioc yanato-bis(2,2'-bipyridyl-4,4'-dicarboxylato) ruthenium(II) bis-tetrabutylammonium) 염료 용액에 넣었다. 전극 막 위에 염료가 충분히 흡착하도록 약 18시간동안 유지하였다. 18시간 후 염료가 흡착된 광전극은 Ethanol로 씻어낸 후 질소 가스로 건조시켰다Since the flexible optical electrode of the present invention is originally made of a conductive flexible substrate, there is no reason for its electrochemical characteristics to be different except for flexibility. Therefore, a fluorine doped tin oxide glass (8 Ω / Sq., Pilkington, USA) was used. (1) Mucasol (Sigma-Aldrich), (2) organic solvent washing, and (3) UV-0 3 surface treatment to remove organic substances in FTO glass. On the cleaned FTO glass, the area of the solar cell was adjusted to 0.25
(상대전극의 제조)(Preparation of counter electrode)
상대전극을 만들기 위해 광전극을 만들 때 사용되었던 동일한 FTO glass가 사용되었다. FTO glass에 드릴을 이용하여 두 개의 구멍을 뚫었다. 구멍을 뚫은 유리를 에탄올(혹은 아세톤)용액에 초음파 세척 후 질소가스로 건조하였다. 건조 후 FTO glass 표면전체에 Pt solution (5 mM ethanolic solution of chloroplatinic acid hexahydrate (H2PtCl6·6H2O))을 drop coating하여 전기로에서 400℃의 온도에서 20분 소결하여 Pt상대전극을 제작하였다.The same FTO glass that was used to make the photoelectrode to make the counter electrode was used. Two holes were drilled in the FTO glass using a drill. The perforated glass was ultrasonically washed with ethanol (or acetone) solution and then dried with nitrogen gas. After drying, a Pt solution (5 mM ethanolic solution of chloroplatinic acid hexahydrate (H 2 PtCl 6 .6H 2 O)) was dropped on the entire surface of the FTO glass and sintered at 400 ° C. for 20 minutes in an electric furnace to prepare a Pt counter electrode .
(전해질 주입 및 봉합)(Electrolyte injection and sealing)
앞서 제조한 광전극과 상대전극 사이의 공간에 DMPII (1,2-dimethyl-3-propylimidazolium iodide, 0.6 M), LiI(0.1 M), I2(0.1 M), 4-tert-butylpyridine(tBP, 0.5 M), 4′,6-diamidino-2-phenylindole (DAPI, 1 mM) 를 포함하는 3-methoxypropionitrile (MPN) 전해질을 주입하고 통상의 고분자 수지로 봉합하여 도 3의 구조의 염료감응 태양전지를 제조하였다.(2-dimethyl-3-propylimidazolium iodide, 0.6 M), LiI (0.1 M), I 2 (0.1 M), and 4-tert-butylpyridine (tBP) were added to the space between the photo- 3-methoxypropionitrile (MPN) electrolyte containing 4%, 6-diamidino-2-phenylindole (DAPI, 1 mM) was injected and sealed with a conventional polymer resin to obtain a dye- .
실시예 1(광전극의 제조)Example 1 (Production of photoelectrode)
광전극에 사용되는 투명 전도성 기판은 fluorine doped tin oxide glass(8 Ω/Sq., Pilkington, USA)을 사용하였다. FTO glass에 유기물을 제거하기 위하여 (1)Mucasol(Sigma-Aldrich), (2)유기용매 세척, (3)UV-03표면처리 순서로 클리닝하였다. 세척이 끝난 FTO glass 위에 닥터 블레이드 방법을 이용하여 태양전지의 면적은 0.25㎠로 하고 위에서 만든 paste A를 코팅하고 전기로를 이용하여 150℃에서 30분 소결 , TiO2전극은 UV-O3 표먼처리를 진행하였다. 챔버 안에 UV light (wavelength k = 185, 254 nm)를 일정간격 유지 후 30분 동안 유지시켜주었다. 그 후 TiO2 전극막이 코팅된 FTO glass는 N-719 (0.5 mM ethanolic solution of cis-diisothioc yanato-bis(2,2'-bipyridyl-4,4'-dicarboxylato) ruthenium(II) bis-tetrabutylammonium) 염료 용액에 넣었다. 전극 막 위에 염료가 충분히 흡착하도록 약 18시간동안 유지하였다. 18시간 후 염료가 흡착된 광전극은 Ethanol로 씻어낸 후 질소 가스로 건조시켰다Fluorine doped tin oxide glass (8 Ω / Sq., Pilkington, USA) was used as a transparent conductive substrate for the photoelectrode. (1) Mucasol (Sigma-Aldrich), (2) organic solvent washing, and (3) UV-03 surface treatment to remove organic substances in FTO glass. On the cleaned FTO glass, the area of the solar cell was adjusted to 0.25
(상대전극의 제조)(Preparation of counter electrode)
상대전극을 만들기 위해 광전극을 만들 때 사용되었던 동일한 FTO glass가 사용되었다. FTO glass에 드릴을 이용하여 두 개의 구멍을 뚫었다. 구멍을 뚫은 유리를 에탄올 용액에 초음파 세척 후 질소가스로 건조하였다. 건조 후 FTO glass 표면전체에 Pt solution (5 mM ethanolic solution of chloroplatinic acid hexahydrate (H2PtCl6·6H2O))을 drop coating하여 전기로에서 400℃의 온도에서 20분 소결하여 Pt상대전극을 제작하였다. The same FTO glass that was used to make the photoelectrode to make the counter electrode was used. Two holes were drilled in the FTO glass using a drill. The perforated glass was ultrasonically washed with ethanol solution and then dried with nitrogen gas. After drying, a Pt solution (5 mM ethanolic solution of chloroplatinic acid hexahydrate (H 2 PtCl 6 .6H 2 O)) was dropped on the entire surface of the FTO glass and sintered at 400 ° C. for 20 minutes in an electric furnace to prepare a Pt counter electrode .
(전해질 주입 및 봉합)(Electrolyte injection and sealing)
앞서 제조한 광전극과 상대전극 사이의 공간에 DMPII(1,2-dimethyl-3-propylimidazolium iodide, 0.6 M), LiI(0.1 M), I2(0.1 M), 4-tert-butylpyridine(tBP, 0.5 M), 4′,6-diamidino-2-phenylindole (DAPI, 1 mM) 를 포함하는 3-methoxypropionitrile (MPN) 전해질을 주입하고 통상의 고분자 수지로 봉합하여 도 3의 구조의 염료감응 태양전지를 제조하였다.(2-dimethyl-3-propylimidazolium iodide, 0.6 M), LiI (0.1 M), I 2 (0.1 M), and 4-tert-butylpyridine (tBP) were added to the space between the photo- 3-methoxypropionitrile (MPN) electrolyte containing 4%, 6-diamidino-2-phenylindole (DAPI, 1 mM) was injected and sealed with a conventional polymer resin to obtain a dye- .
상기 실시예 1 및 비교예 1에서 각각 제조한 염료감응 태양전지에 대하여 하기와 같은 방법으로 개방전압, 광전류밀도, 에너지 변환효율(energy conversion efficiency), 및 충진계수(fill factor)를 측정하였으며, 그 결과를 하기 표 1에 정리하였다. 또한, 도 5 에는 AM 1.5G 1 Sun 조건에서 얻은 실시예 1 및 비교예 1의 태양전지의 전류-전압 곡선의 그래프를 도시하였다.The dye-sensitized solar cell prepared in Example 1 and Comparative Example 1 was measured for open-circuit voltage, photocurrent density, energy conversion efficiency, and fill factor in the following manner. The results are summarized in Table 1 below. 5 shows a graph of current-voltage curves of the solar cells of Example 1 and Comparative Example 1 obtained under the condition of AM 1.5
(1) 개방전압(V) 및 광전류밀도(㎃/㎠)(1) Open-circuit voltage (V) and photocurrent density (mA / cm 2)
: 개방전압과 광전류 밀도는 Keithley SMU2400 을 이용하여 측정하였다.: Open-circuit voltage and photocurrent density were measured using a Keithley SMU2400.
(2) 에너지 변환효율(%) 및 충진계수(%)(2) Energy conversion efficiency (%) and fill factor (%)
: 에너지 변환효율의 측정은 1.5AM 100mW/cm2의 솔라 시뮬레이터(Xe 램프[200W, PolaronixㄾK201,McScience,Korea], AM1.5 filter로 구성됨)를 이용하였고, 충진계수는 앞서 얻은 변환효율 및 하기 계산식을 이용하여 계산하였다.: The energy conversion efficiency was measured using a solar simulator (Xe lamp [200 W, Polaronix ㄾ K201, McScience, Korea], AM1.5 filter) at 1.5 AM 100 mW / cm 2 , Was calculated using the following formula.
[계산식][formula]
상기 계산식에서, J는 변환효율 곡선의 Y축 값이고, V는 변환효율 곡선의 X축 값이며, Jsc및 Voc는 각 축의 절편 값이다.In the above equation, J is the Y-axis value of the conversion efficiency curve, V is the X-axis value of the conversion efficiency curve, and Jsc and Voc are the intercept values of the respective axes.
(㎃/cm2)Jsc
(MA / cm 2)
(V)Voc
(V)
(%)FF
(%)
(%)efficiency
(%)
(㎠) Area
(㎠)
상기 표 1 및 도 5에 나타낸 바와 같이, 1-Octanol과 사염화 탄소(CCl4)를 용매로 사용한 실시예 1의 태양전지의 경우 기존 1-Octanol만 넣은 비교예 1의 염료감응 태양전지보다 높은 효율을 나타내는 것을 확인할 수 있었다. 따라서, 본 발명의 태양전지는 용매 중에 분산된 TiO2 나노 입자에 바인더 역할을 할 수 있는 1-Octanol과 CCl4를 일정 몰비율로 혼합하여 TiO2 나노입자간의 네트워크를 향상시켜 저온 소성이 가능하고 균일한 TiO2전극막을 형성 할 수 있으며 비교적 높은 에너지변환효율(η)을 나타낼 수 있고 저온에서 소성이 가능하므로 유연성을 요구하는 다양한 전자 산업이나 전원이 필요한 분야에 활용될 수 있다.As shown in Table 1 and FIG. 5, the solar cell of Example 1 using 1-Octanol and carbon tetrachloride (CCl 4 ) as a solvent showed higher efficiency than the dye-sensitized solar cell of Comparative Example 1 containing only conventional 1-Octanol . ≪ / RTI > Therefore, the solar cell of the present invention can improve the network between TiO 2 nanoparticles by mixing 1-Octanol and CCl 4 , which can serve as a binder for TiO 2 nanoparticles dispersed in a solvent, at a constant molar ratio, Can form a uniform TiO 2 electrode film and can exhibit a relatively high energy conversion efficiency (η) and can be fired at a low temperature, so that it can be used in a variety of electronic industries requiring power and in fields requiring power supply.
앞에서 설명된 본 발명의 일실시예는 본 발명의 기술적 사상을 한정하는 것으로 해석되어서는 안 된다. 본 발명의 보호범위는 청구범위에 기재된 사항에 의하여만 제한되고, 본 발명의 기술 분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상을 다양한 형태로 개량 변경하는 것이 가능하다. 따라서 이러한 개량 및 변경은 통상의 지식을 가진 자에게 자명한 것인 한 본 발명의 보호범위에 속하게 될 것이다.The embodiments of the present invention described above should not be construed as limiting the technical idea of the present invention. The scope of protection of the present invention is limited only by the matters described in the claims, and those skilled in the art will be able to modify the technical idea of the present invention in various forms. Accordingly, such improvements and modifications will fall within the scope of the present invention as long as they are obvious to those skilled in the art.
101: 플라스틱 기판
102: 전도성 필름
103 : 전도성 가요성 기재
104 : 저온소성용 금속산화물 나노입자를 포함하는 다공질막
105 : 150℃ 이하에서 소성한 저온소성용 금속산화물 나노입자를 포함하는 다공질막
106 : UV-O3을 처리한 금속산화물 나노입자를 포함하는 다공질막
107 : 염료를 흡착한 금속산화물 나노입자를 포함하는 다공질막
110 : 광전극
120: 상대전극
121: Pt 촉매층
130: 전해질
140: 고분자 접착제층101: plastic substrate
102: Conductive film
103: Conductive flexible substrate
104: Porous film containing metal oxide nanoparticles for low-temperature firing
105: A porous film comprising metal oxide nanoparticles for low-temperature calcination baked at 150 ° C or lower
106: Porous film containing metal oxide nanoparticles treated with UV-O 3
107: Porous film containing metal oxide nano-particles adsorbing dye
110: photoelectrode
120: counter electrode
121: Pt catalyst layer
130: electrolyte
140: polymer adhesive layer
Claims (12)
ⅰ)C6 내지 C12의 직쇄 또는 분지쇄 알킬 알콜 및 C1 내지 C3의 할로겐화탄소를 체적비로 1:0.1 내지 10 범위로 포함한 용매에 제1금속산화물 나노입자를 혼입하여 페이스트를 제조하는 단계,;
ⅱ)상기 전도성 가요성 기재상에 상기 페이스트를 도포하는 단계 및;
ⅲ)200℃ 이하의 온도에서 저온소결하여 다공질 제1금속산화물층을 형성하는 단계를 포함한 가요성 광전극 제조방법. A method of manufacturing a photoelectrode including a porous first metal oxide layer formed on a conductive flexible substrate and a structure in which a dye is adsorbed on the porous first metal oxide layer,
I) incorporating the first metal oxide nanoparticles into a solvent containing a C6 to C12 linear or branched alkyl alcohol and C1 to C3 halogenated carbon in a volume ratio of 1: 0.1 to 10, to prepare a paste;
Ii) applying the paste onto the conductive flexible substrate;
And iii) low temperature sintering at a temperature of 200 DEG C or less to form a porous first metal oxide layer.
ⅳ)다공질 제1금속산화물층에 잔류한 유기물을 제거하는 단계를 더 포함한 가요성 광전극 제조방법. The method according to claim 1,
Iv) removing the organic matter remaining in the first porous metal oxide layer.
상기 전기전도성을 가진 가요성 기재는 플라스틱 기재상에 금속, 금속 질화물, 제2금속산화물, 탄소화합물, 또는 전도성 고분자로 이루어진 평균 두께 1 내지 1000nm인 전도성 필름층을 형성하여 이루어진 것임을 특징으로 하는 가요성 광전극 제조방법. The method according to claim 1,
Wherein the flexible substrate having electrical conductivity is formed by forming a conductive film layer of an average thickness of 1 to 1000 nm made of a metal, a metal nitride, a second metal oxide, a carbon compound, or a conductive polymer on a plastic substrate. A method of manufacturing a photoelectrode.
상기 제1금속산화물은 주석(Sn)산화물, 안티몬(Sb), 나이오븀(Nb) 또는 불소 도핑된 주석(Sn)산화물, 인듐(In)산화물, 주석 도핑된 인듐(In)산화물, 아연(Zn)산화물, 알루미늄(Al), 붕소(B), 갈륨(Ga), 수소(H), 인듐(In), 이트륨(Y), 타이타늄(Ti), 실리콘(Si) 또는 주석(Sn) 도핑된 아연(Zn)산화물, 마그네슘(Mg)산화물, 캐드뮴(Cd)산화물, 마그네슘아연(MgZn)산화물, 인듐아연(InZn)산화물, 구리알루미늄(CuAl)산화물, 실버(Ag)산화물, 갈륨(Ga)산화물, 아연주석산화물(ZnSnO), 타이타늄산화물(TiO2) 및 아연인듐주석(ZIS)산화물, 니켈(Ni)산화물, 로듐(Rh)산화물, 루세늄(Ru)산화물, 이리듐(Ir)산화물, 구리(Cu)산화물, 코발트(Co)산화물, 텅스텐(W)산화물, 티타늄(Ti)산화물, 지르코늄(Zr)산화물, 스트론튬(Sr)산화물, 란타넘(La)산화물, 바나듐(V)산화물, 몰리브데넘(Mo)산화물, 나이오븀(Nb)산화물, 알루미늄(Al)산화물, 이트늄(Y)산화물, 스칸듐(Sc)산화물, 사마륨(Sm)산화물, 스트론튬타이타늄(SrTi)산화물로 이루어진 군으로부터 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법.The method according to claim 1,
The first metal oxide may be selected from the group consisting of tin (Sn) oxide, antimony (Sb), niobium (Nb) or fluorine doped tin (Sn) oxide, indium (In) oxide, tin doped indium ) Oxide, aluminum (Al), boron (B), gallium (Ga), hydrogen (H), indium (In), yttrium (Y), titanium (Ti), silicon (Si) or tin (Zn) oxide, magnesium oxide, cadmium oxide, magnesium zinc oxide, indium zinc oxide, copper aluminum oxide, silver oxide, gallium oxide, , Zinc tin oxide (ZnSnO), titanium oxide (TiO2) and zinc indium tin (ZIS) oxide, nickel oxide, rhodium oxide, ruthenium oxide, iridium oxide, copper ) Oxide, cobalt (Co) oxide, tungsten (W) oxide, titanium (Ti) oxide, zirconium (Zr) oxide, strontium (Sr) oxide, lanthanum (La) oxide, vanadium Mo) oxide, niobium (Nb) oxide, Minyum (Al) oxide, the teunyum (Y) oxide, scandium (Sc) oxide, samarium (Sm) oxide, strontium titanium (SrTi) flexible optical electrode method, characterized in that at least one member from the group consisting of oxide.
상기 금속질화물은 질화타이타늄(Ti), 질화지르코늄(Zr), 질화하프늄, 질화나이오븀(Nb), 질화탄탈륨(Ta), 질화바나듐, 질화크롬(Cr), 질화몰리브데늄(Mo),질화텅스텐(W), 질화알루미늄(Al), 질화갈륨(Ga), 질화인듐(In), 질화실리콘(Si) 및 질화게르마늄(Ge)으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법.The method of claim 3,
The metal nitride may be at least one selected from the group consisting of titanium nitride (Ti), zirconium nitride (Zr), hafnium nitride, niobium nitride, tantalum nitride, vanadium nitride, chromium (Cr), molybdenum nitride Wherein at least one selected from the group consisting of tungsten (W), aluminum nitride (Al), gallium nitride (Ga), indium nitride (In), silicon nitride (Si), and germanium nitride (Ge) Gt;
상기 제2금속산화물은 주석(Sn)산화물, 안티몬(Sb), 나이오븀(Nb) 또는 불소 도핑된 주석(Sn)산화물, 인듐(In)산화물, 주석 도핑된 인듐(In)산화물, 아연(Zn)산화물, 알루미늄(Al), 붕소(B), 갈륨(Ga), 수소(H), 인듐(In), 이트륨(Y), 타이타늄(Ti), 실리콘(Si) 또는 주석(Sn) 도핑된 아연(Zn)산화물, 마그네슘(Mg)산화물, 캐드뮴(Cd)산화물, 마그네슘아연(MgZn)산화물, 인듐아연(InZn)산화물, 구리알루미늄(CuAl)산화물, 실버(Ag)산화물, 갈륨(Ga)산화물, 아연주석산화물(ZNSNO), 타이타늄산화물(TiO2) 및 아연인듐주석(ZIS)산화물, 니켈(Ni)산화물, 로듐(Rh)산화물, 루세늄(Ru)산화물, 이리듐(Ir)산화물, 구리(Cu)산화물, 코발트(Co)산화물, 텅스텐(W)산화물, 티타늄(Ti)산화물로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법.The method of claim 3,
Wherein the second metal oxide is selected from the group consisting of tin (Sn) oxide, antimony (Sb), niobium (Nb) or fluorine doped tin (Sn) oxide, indium (In) oxide, tin doped indium ) Oxide, aluminum (Al), boron (B), gallium (Ga), hydrogen (H), indium (In), yttrium (Y), titanium (Ti), silicon (Si) or tin (Zn) oxide, magnesium oxide, cadmium oxide, magnesium zinc oxide, indium zinc oxide, copper aluminum oxide, silver oxide, gallium oxide, , Zinc tin oxide (ZNSNO), titanium oxide (TiO 2 ) and zinc indium tin (ZIS) oxide, nickel (Ni) oxide, rhodium (Rh) oxide, ruthenium (Ru) oxide, iridium Wherein at least one selected from the group consisting of copper (Cu) oxide, cobalt (Co) oxide, tungsten (W) oxide, and titanium (Ti) oxide.
상기 탄소화합물은 활성탄, 흑연, 카본 나노튜브, 카본블랙, 그라펜으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법.The method of claim 3,
Wherein the carbon compound is at least one selected from the group consisting of activated carbon, graphite, carbon nanotube, carbon black, and graphene.
상기 전도성 고분자는 PEDOT (폴리(3,4-에틸렌디옥시티오펜))- PSS(폴리(스티렌설포네이트)), 폴리아닐린-CSA, 펜타센, 폴리아세틸렌, P3HT(폴리(3-헥실티오펜), 폴리실록산 카르바졸, 폴리아닐린, 폴리에틸렌 옥사이드, (폴리(1-메톡시-4-(0-디스퍼스레드1)-2,5-페닐렌-비닐렌), 폴리인돌, 폴리카르바졸, 폴리피리디아진, 폴리이소티아나프탈렌, 폴리페닐렌 설파이드, 폴리비닐피리딘, 폴리티오펜, 폴리플루오렌, 폴리피리딘, 폴리피롤, 폴리설퍼나이트라이드 및 이들의 공중합체로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 가요성 광전극 제조방법.The method of claim 3,
The conductive polymer may be selected from the group consisting of PEDOT (poly (3,4-ethylenedioxythiophene) -PSS (poly (styrene sulfonate)), polyaniline-CSA, pentacene, polyacetylene, P3HT Polysiloxane carbazole, polyaniline, polyethylene oxide, (poly (1-methoxy-4- (0 -dispersed 1) -2,5-phenylene-vinylene), polyindole, polycarbazole, Characterized in that it is at least one member selected from the group consisting of polyisoprenesulfone, polyisothianaphthalene, polyphenylene sulfide, polyvinylpyridine, polythiophene, polyfluorene, polypyridine, polypyrrole, polysulfuron nitride and copolymers thereof (Method for manufacturing a photoelectrode).
상기 알킬 알콜은 C7 내지 C10의 직쇄 알킬알콜인 것을 특징으로 하는 가요성 광전극 제조방법.The method according to claim 1,
Wherein the alkyl alcohol is a C7 to C10 straight chain alkyl alcohol.