KR101916351B1 - Decoration flexible sheet with printed patteren and embossed pattern matched and manufacturing method thereof - Google Patents

Decoration flexible sheet with printed patteren and embossed pattern matched and manufacturing method thereof Download PDF

Info

Publication number
KR101916351B1
KR101916351B1 KR1020180050447A KR20180050447A KR101916351B1 KR 101916351 B1 KR101916351 B1 KR 101916351B1 KR 1020180050447 A KR1020180050447 A KR 1020180050447A KR 20180050447 A KR20180050447 A KR 20180050447A KR 101916351 B1 KR101916351 B1 KR 101916351B1
Authority
KR
South Korea
Prior art keywords
sheet
base sheet
pattern
matched
printed
Prior art date
Application number
KR1020180050447A
Other languages
Korean (ko)
Inventor
김원호
Original Assignee
주식회사 금진
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 금진 filed Critical 주식회사 금진
Priority to KR1020180050447A priority Critical patent/KR101916351B1/en
Application granted granted Critical
Publication of KR101916351B1 publication Critical patent/KR101916351B1/en

Abstract

The present invention discloses a decoration sheet formed so that a three-dimensional shape formed on a decorative surface and an image corresponding to the three-dimensional shape are matched with each other, and a manufacturing method thereof. The disclosed decoration sheet with a printed pattern and an embossed pattern matched comprises: a base sheet provided with a synthetic resin capable of being deformed by heat, and provided with a sheet shape having a set width and a length; the printed pattern provided on the decorative surface defined by one surface of both surfaces in the thickness direction of the base sheet; the embossed pattern formed by convexly and concavely having the three-dimensional shape on the decorative surface, and formed to be matched with the printed pattern; and a stretching restriction sheet laminated and provided on a rear surface of the decorative surface among the both surfaces of the base sheet, provided with a material having a relatively smaller thermal strain rate than a thermal strain rate of the base sheet due to the heat applied when forming the embossed pattern, and restricting so that the base sheet is stretched in the longitudinal direction or the width direction.

Description

인쇄무늬와 엠보무늬가 일치된 데코시트 및 그 제조방법{Decoration flexible sheet with printed patteren and embossed pattern matched and manufacturing method thereof}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet having a printed pattern and an emboss pattern,

본 발명(Disclsoure)은, 바닥이나 벽면에 설치되어 다양한 미감을 제공할 수 있는 유연한(Flexible) 시트 형태의 데코시트 및 그 제조방법에 관한 것으로서, 구체적으로 장식면에 형성된 입체형상과 그 입체형상에 대응하는 이미지가 서로 매칭되도록 형성된 데코시트 및 그 제조방법에 관한 것이다.The present invention relates to a decorative sheet in the form of a flexible sheet which can be provided on a floor or a wall to provide a variety of aesthetics and a manufacturing method thereof. More particularly, the present invention relates to a three- The corresponding images are matched with each other, and a method of manufacturing the same.

여기서는, 본 발명에 관한 배경기술이 제공되며, 이들이 반드시 공지기술을 의미하는 것은 아니다(This section provides background information related to the present disclosure which is not necessarily prior art).Herein, the background art relating to the present invention is provided, and they are not necessarily referred to as known arts.

소비자의 취향이 날로 다각화 또는 고급화됨에 따라 실내 인테리어 분야는 유행에 민감한 분야가 되었으며, 미적 효과의 개선을 위한 매우 다양한 수단들이 제안되고 있는 실정이다. 실내 인테리어에 따라 해당 공간의 분위기를 크게 변화시킬 수 있으므로 그만큼 다양한 제품들이 출시되는 것은 당연하다. As consumer tastes diversify or become more advanced, interior decoration has become a trend - sensitive field, and various means for improving aesthetic effects have been proposed. It is natural that various products will be released because the atmosphere of the space can be changed greatly according to the interior of the room.

근간에는 건강이나 환경에 유익한 제품들이 많이 출시되었으며, 화재발생시에도 인명피해를 주지 않기 위한 제품도 출시되고 있다.In the meantime, many products that are beneficial to health and the environment have been released, and products are being released to prevent people from being injured in the event of a fire.

다른 한편 DIY 문화의 보급에 따라 개인이 스스로 시공할 수 있는 제품들도 출시되고 있다. On the other hand, according to the dissemination of DIY culture, there are also products that individuals can construct themselves.

이처럼 근래 제안되고 있는 인테리어 소재들은 단순한 미적 감흥을 넘어 다양한 기능적 내지 미적 특성을 가지고 있다.These recently proposed interior materials have various functional and aesthetic characteristics beyond merely aesthetic inspiration.

한편, 종래 벽면을 장식하는 부재로는, 벽지와 같이 일면에 장식문양이 인쇄된 시트지가 주를 이루었으나, 최근 들어 실제와 같은 문양, 즉 3차원 형상을 가지는 장식문양이 형성된 장식 부재가 종종 소개되고 있다.On the other hand, as a member for decorating a conventional wall, a sheet having a decorative pattern printed on one side such as wallpaper is mainly made. Recently, however, a decorative member having a decorative pattern having a three- .

그러나 장식을 위한 면에 3차원 형상이 형성된 것들은 3차원 형상과 그것에 대응되는 이미지가 서로 일치하지 않아 이미지의 고급화가 미흡한 문제가 있었다. However, in the case where the three-dimensional shape is formed on the surface for decoration, the three-dimensional shape and the corresponding image do not coincide with each other, so that there is a problem in that the quality of the image is insufficient.

1. 한국 공개특허공보 제10-2017-0109802호1. Korean Patent Publication No. 10-2017-0109802

본 발명(Discloure)은, 장식면에 형성된 입체형상과 그 입체형상에 대응하는 이미지가 서로 매칭되도록 형성된 데코시트 및 그 제조방법의 제공을 일 목적으로 한다.The object of the present invention is to provide a decorative sheet formed so that a three-dimensional shape formed on a decorative surface and an image corresponding to the three-dimensional shape match each other and a manufacturing method thereof.

여기서는, 본 발명의 전체적인 요약(Summary)이 제공되며, 이것이 본 발명의 외연을 제한하는 것으로 이해되어서는 아니 된다(This section provides a general summary of the disclosure and is not a comprehensive disclosure of its full scope or all of its features).The present invention is not intended to be exhaustive or to limit the scope of the present invention to the full scope of the present invention. of its features).

상기한 과제의 해결을 위해, 본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트는, 열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 시트형상으로 구비되는 베이스 시트; 상기 베이스 시트의 두께방향으로 양면 중 일면으로 정의되는 장식면에 구비되는 인쇄무늬; 상기 장식면에 볼록 또는 오목하게 3차원 형상을 가지며 형성되되, 상기 인쇄무늬와 정합 되도록 형성되는 엠보무늬; 및 상기 베이스 시트의 양면 중 상기 장식면의 배면에 합지되어 구비되며, 상기 엠보무늬의 형성시 가해지는 열에 의한 상기 베이스 시트의 열 변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비되어, 상기 베이스 시트가 그 길이방향 또는 폭방향으로 연신되는 것을 제한하는 연신 제한시트;를 포함한다.In order to solve the above-mentioned problems, a decor sheet having a printed pattern and an emboss pattern in accordance with an aspect of the present invention is provided with a synthetic resin capable of being deformed by heat, and has a sheet shape having a set width and a length A base sheet; A printed pattern provided on a decorative surface defined as one of both surfaces in a thickness direction of the base sheet; An emboss pattern formed to have a convex or concave three-dimensional shape on the decorative surface, and to be matched with the print pattern; And a base sheet having a thermal deformation rate that is less than a thermal deformation rate of the base sheet due to heat applied when the emboss pattern is formed, And a stretching limit sheet for restricting stretching in the longitudinal direction or the width direction.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 연신 제한시트는, 상기 엠보무늬 형성이 완료된 후 상기 베이스 시트로부터 분리 가능하게 구비되는 것을 특징으로 한다.In a decor sheet having a printed pattern and an emboss pattern matched with each other according to an aspect of the present invention, the drawing sheet is detachably provided from the base sheet after the emboss pattern formation is completed.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 연신 제한시트는, PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 중 어느 하나의 재질로 구비되는 것을 특징으로 한다.In the decorative sheet in which the printed pattern and the emboss pattern match each other according to an aspect of the present invention, the stretching limit sheet is made of a material selected from the group consisting of polyethylene terephthalate (PET), polypropylene (PP), cloth, nonwoven fabric, As shown in FIG.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 연신 제한시트는, 상기 베이스 시트에 부착되는 면에 코팅되어 구비되되, 설정된 온도 이상에서는 상기 베이스 시트와 접착력을 유지하고, 상기 설정된 온도 이하로 낮아짐에 따라 상기 베이스 시트와의 접착력이 약해지는 재질로 구비되는 이형층을 가지는 것을 특징으로 한다.In the decorative sheet according to an aspect of the present invention, the stretch limiting sheet is coated on the surface to be adhered to the base sheet. When the stretch sheet is adhered to the base sheet at a predetermined temperature or higher, And a releasing layer formed of a material which weakens the adhesive force with the base sheet as the temperature is lowered below the set temperature.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 이형층은, 연화점이 55℃ 이하인 고분자 수지로 구비되는 것을 특징으로 한다.In a decor sheet in which a printed pattern and an emboss pattern match each other according to an aspect of the present invention, the release layer is characterized by being made of a polymer resin having a softening point of 55 캜 or less.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 이형층은, PE(polyethylene) 재질로 구비되는 것을 특징으로 한다.In a decor sheet having a printed pattern and an emboss pattern in accordance with an aspect of the present invention, the release layer is made of polyethylene (PE).

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트에서, 상기 연신 제한시트는, 상기 베이스 시트에 상기 엠보무늬를 형성한 후 냉각시키는 과정에서 상기 베이스 시트로부터 분리가능하게 구비되는 것을 특징으로 한다.In a decor sheet having a printed pattern and an emboss pattern in accordance with an aspect of the present invention, the stretch sheet may be separated from the base sheet in a process of forming the emboss pattern on the base sheet and cooling the emboss pattern .

한편, 본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법은, 열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 시트형상으로 구비되는 베이스 시트를 준비하는 제1 단계; 상기 베이스 시트의 열변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비되어, 상기 베이스 시트가 그 길이방향 또는 폭방향으로 연신되는 것을 제한하는 연신 제한시트를 상기 베이스 시트의 일면에 합치하는 제2 단계; 상기 베이스 시트의 양면 중 상기 연신 제한시트의 배면으로 정의되는 장식면에 인쇄무늬를 형성하는 제3 단계; 상기 베이스 시트에 열을 가하여 상기 장식면에 상기 인쇄무늬와 정합되도록 볼록 또는 오목하게 3차원 형상을 가지는 엠보무늬를 형성하는 제4 단계; 및 상기 인쇄무늬와 상기 엠보무늬가 형성된 상기 베이스 시트를 냉각한 후 상기 연신 제한시트를 분리하는 제5 단계;를 포함한다.A method of manufacturing a decorative sheet in which a printed pattern and an emboss pattern match each other according to an aspect of the present invention includes a synthetic resin capable of being deformed by heat, A first step of preparing a first step; A second step of fitting a stretching restricting sheet provided with a material having a thermal deformation rate relatively smaller than the thermal deformation rate of the base sheet to restrict the stretching of the base sheet in the longitudinal direction or the width direction to one surface of the base sheet; ; A third step of forming a printed pattern on the decorative surface defined by the back surface of the stretch limit sheet in the both sides of the base sheet; A fourth step of applying heat to the base sheet to form an emboss pattern having a convex or concave three-dimensional shape on the decorative surface to match the printed pattern; And a fifth step of cooling the base sheet having the print pattern and the emboss pattern, and then separating the stretch limit sheet.

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법에서, 상기 제3 단계는, 상기 인쇄무늬가 일면에 인쇄된 장식시트를 상기 장식면에 합지하는 것을 특징으로 한다.In a method of manufacturing a decor sheet in which a printed pattern and an emboss pattern match each other according to an aspect of the present invention, in the third step, a decorative sheet printed on one side of the printed pattern is laminated on the decorative surface .

본 발명의 일 태양(aspect)에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법에서, 상기 연신 제한시트는, PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 중 어느 하나의 재질로 구비되며, 상기 베이스 시트에 부착되는 면에 PE(polyethylene) 재질로 구비되는 이형층을 가지는 것을 특징으로 한다.In the method of manufacturing a decor sheet having a printed pattern and an emboss pattern matched with each other according to an aspect of the present invention, the stretching sheet is made of PET (polyethylene terephthalate), PP (polypropylene), cloth, nonwoven fabric, And a release layer provided on a surface of the base sheet, the release layer being made of polyethylene (PE).

본 발명에 따르면, 열변형율의 차이를 이용하여 연신 제한시트에 의해 베이스 시트가 열에 의해 연신되는 것을 방지함으로써, 인쇄무늬와 엠보무늬가 정합된 데코시트를 제조할 수 있다.According to the present invention, the base sheet is prevented from being stretched by heat by the stretching restraining sheet using the difference in thermal strain, whereby a decoupled sheet in which the printed pattern and the embossed pattern are matched can be manufactured.

본 발명에 따르면, 열변형율의 차이를 이용하여 인쇄무늬와 엠보무늬가 형성된 베이스 시트로부터 연신 제한시트의 분리가 용이하게 되며, 이에 의해 연신 제한시트의 반복사용(또는 재사용)이 가능한 이점을 가진다.According to the present invention, it is easy to separate the stretch restraint sheet from the base sheet on which the printed pattern and the emboss pattern are formed by utilizing the difference in the thermal strain rate, whereby the stretch sheet can be repeatedly used (or reused).

도 1 및 도 2는 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 실시형태를 보인 도면.
도 3 내지 도 5는 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법을 설명하기 위한 도면.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 and Fig. 2 show an embodiment of a decor sheet according to the present invention in which a printed pattern and an emboss pattern are matched. Fig.
Figs. 3 to 5 are diagrams for explaining a method of manufacturing a decor sheet in which the emboss pattern is matched with the emboss pattern according to the present invention. Fig.

이하, 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트 및 그 제조방법을 구현한 실시형태를 도면을 참조하여 자세히 설명한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a decorative sheet in which a printed pattern and an emboss pattern match each other according to the present invention and embodiments in which the method of manufacturing the same is implemented will be described in detail with reference to the drawings.

다만, 본 발명의 사상은 이하에서 설명되는 실시형태에 의해 그 실시 가능 형태가 제한된다고 할 수는 없고, 본 발명의 사상을 이해하는 통상의 기술자는 본 개시와 동일한 기술적 사상의 범위 내에 포함되는 다양한 실시 형태를 치환 또는 변경의 방법으로 용이하게 제안할 수 있을 것이나, 이 또한 본 발명의 기술적 사상에 포함됨을 밝힌다.It is to be understood, however, that the scope of the present invention is not limited to the embodiments described below, and those skilled in the art of the present invention, other than the scope of the present invention, It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the invention.

또한, 이하에서 사용되는 용어는 설명의 편의를 위하여 선택한 것이므로, 본 발명의 기술적 내용을 파악하는 데 있어서, 사전적 의미에 제한되지 않고 본 발명의 기술적 사상에 부합되는 의미로 적절히 해석되어야 할 것이다. In addition, the terms used below are selected for convenience of explanation. Therefore, the technical meaning of the present invention should not be limited to the prior meaning, but should be properly interpreted in accordance with the technical idea of the present invention.

먼저, 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 실시형태에 대하여 설명한다.First, a description will be given of an embodiment of a decorative sheet in which the print pattern and the emboss pattern match each other according to the present invention.

도 1 및 도 2는 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 실시형태를 보인 도면이다.1 and 2 are views showing an embodiment of a decorative sheet in which a printed pattern and an emboss pattern are matched according to the present invention.

도 1 및 도 2를 참조하면, 본 실시형태에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트(100)는, 베이스 시트(110), 인쇄무늬(120), 엠보무늬(130) 및 연신 제한시트(140)를 가진다.1 and 2, a decor sheet 100 having a printed pattern and an emboss pattern matched with each other according to the present embodiment includes a base sheet 110, a printed pattern 120, an emboss pattern 130, (140).

베이스 시트(110)는, 본 실시형태에 따른 데코시트(100)의 몸체를 이루는 부분으로서, 열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 시트형상으로 구비된다. The base sheet 110 is a part of a body of the decor sheet 100 according to the present embodiment, and is formed of synthetic resin capable of being deformed by heat, and is formed in a sheet shape having a predetermined width and length.

본 실시형태에서, 베이스 시트(110)와 후술하는 연신 제한시트(140)는 각각 롤 형상으로 감겨져 거치되며, 이들은 합지를 위해 적어도 한 쌍의 롤러 사이를 통과하면서 가열 압착된다.In the present embodiment, the base sheet 110 and a stretching and restraining sheet 140 described below are wound and mounted in rolls, respectively, and they are heat-pressed while passing between at least a pair of rollers for joining.

베이스 시트(110)는, 열에 의한 변형이 가능하도록 열가소성 수지 재질로 구비될 수 있다.The base sheet 110 may be made of a thermoplastic resin so as to be deformable by heat.

베이스 시트(110)는, 충격 또는 소음 완화 효과를 위해 탄성력을 가지는 재질로 구비될 수 있다.The base sheet 110 may be made of a material having an elastic force for an impact or noise reduction effect.

인쇄무늬(120)는, 베이스 시트(110)의 두께방향으로 양면 중 일면으로 정의되는 장식면(111)에 구비된다.The printed pattern 120 is provided on the decorative surface 111, which is defined as one of both surfaces in the thickness direction of the base sheet 110. [

인쇄무늬(120)는, 제조자에 의해 선택되는 것으로 패턴의 종류는 제한되지 않는다.The print pattern 120 is selected by the manufacturer and the type of pattern is not limited.

인쇄무늬(120)는, 베이스 시트(110)의 장식면(111)에 인쇄되어 구비될 수도 있고, 인쇄무늬(120)가 인쇄된 장식시트가 베이스 시트(110)의 장식면(111)에 합지되어 구비될 수도 있다.The printed pattern 120 may be printed on the decorative surface 111 of the base sheet 110 or may be provided on the decorative surface 111 of the base sheet 110, .

엠보무늬(130)는. 장식면(111)에 볼록 또는 오목하게 3차원 형상을 가지며 형성되되, 인쇄무늬와 정합 되도록 형성된다.The emboss pattern (130) Is formed to have a convex or concave three-dimensional shape on the decorative surface (111), and is formed to be matched with the printed pattern.

연신 제한시트(140)는, 인쇄무늬(120)와 엠보무늬(130)의 정합이 가능하도록 구비되는 것이다.The stretch limiting sheet 140 is provided so as to be able to match the printed pattern 120 and the embossed pattern 130. [

연신 제한시트(140)는, 베이스 시트(110)의 양면 중 장식면(111)의 배면에 부착되어 구비되어 엠보무늬(130)의 형성시 가해지는 열에 의해 베이스 시트(110)가 연신되는 것을 제한하여 엠보무늬(130)가 인쇄무늬(120)와 일치되게 형성되도록 한다. The stretch limiting sheet 140 is attached to the back surface of the decorative surface 111 on both sides of the base sheet 110 so as to restrict the stretching of the base sheet 110 due to the heat applied when the emboss pattern 130 is formed So that the emboss pattern 130 is formed so as to coincide with the print pattern 120.

이를 위해, 연신 제한시트(140)는, 엠보무늬(130)의 형성시 가해지는 열에 의한 베이스 시트(110)의 열 변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비된다.For this purpose, the stretch limiting sheet 140 is formed of a material having a thermal deformation rate relatively smaller than the thermal deformation rate of the base sheet 110 due to the heat applied when the emboss pattern 130 is formed.

베이스 시트(110)가 열에 의해 그 길이방향 또는 폭방향으로 연신되는 것을 열변형율이 작은 연신 제한시트(140)가 억제하는 구조이다.The stretch limiting sheet 140 having a small thermal strain rate inhibits the base sheet 110 from being stretched in the longitudinal direction or the width direction by heat.

이를 위해, 연신 제한시트(140)는 열변형율은 거의 없거나 매우 작은 재질로 구비되는 것이 바람직하다.To this end, the stretch limiting sheet 140 is preferably made of a material having little or very little thermal strain.

연신 제한시트(140)는, PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 등을 예로 들 수 있을 것이나, 이에 제한되지 않고 열변형율의 차이로 인해 열에 의해 베이스 시트(110)의 연신을 제한할 수 있는 것이라면 본 발명의 사상에 포함되는 것임을 의심할 여지가 없다.The stretch limit sheet 140 may be made of PET (polyethylene terephthalate), PP (polypropylene), cloth, nonwoven fabric, glass paper, paper and the like, but the present invention is not limited thereto. There is no doubt that it is included in the idea of the present invention.

본 실시형태에서, 연신 제한시트(140)는, 베이스 시트(110)의 양면 중 장식면(111)의 배면 전체에 부착되는 시트형상으로 구비되는 것이 바람직하다.In the present embodiment, it is preferable that the stretching restraint sheet 140 be provided in a sheet shape attached to the entire rear surface of the decorative surface 111 on both sides of the base sheet 110. [

한편, 본 실시형태에서, 연신 제한시트(140)는, 엠보무늬(130) 형성이 완료된 후 베이스 시트(110)로부터 분리 가능하게 구비된다.On the other hand, in the present embodiment, the stretch limiting sheet 140 is detachably provided from the base sheet 110 after the emboss pattern 130 is formed.

이는 엠보무늬(130) 형성 후 베이스 시트(110)의 냉각과정에서 발생 되는 열 변형율에 의해 서로 분리 가능하게 되는 원리를 이용할 수 있다.It is possible to use the principle that they can be separated from each other by the thermal deformation rate generated in the cooling process of the base sheet 110 after the emboss pattern 130 is formed.

다만, 엠보무늬(130) 형성 후 베이스 시트(110)의 냉각과정에서 베이스 시트(110)와 연신 제한시트(140)의 분리 또는 박리를 원활하게 하기 위해, 연신 제한시트(140)는, 베이스 시트(110)에 부착되는 면에 베이스 시트(110)와 동일한 재질로 구비되는 이형층(150)을 가지는 것이 바람직하다.In order to smoothly separate or peel off the base sheet 110 and the stretch-limiting sheet 140 during the cooling process of the base sheet 110 after the emboss pattern 130 is formed, the stretch- It is preferable that the release layer 150 is made of the same material as that of the base sheet 110 on the surface of the base sheet 110 attached to the base sheet 110.

이형층(150)은, 연신 제한시트(140)의 일면에 코팅되어 구비되어 열변형율이 연신 제한시트(140)와 사실상 동일하게 구속되며, 엠보무늬(130)의 형성 시 가해지는 열에 의해 동일 재질인 베이스 시트(110)에 부착이 쉽게 이루어진다.The releasing layer 150 is coated on one side of the stretching restriction sheet 140 so that the heat distortion rate is substantially the same as that of the stretching restriction sheet 140. The release layer 150 is made of the same material The base sheet 110 can be easily attached.

또한, 베이스 시트(110)의 열변형을 억제하게 된다.Further, thermal deformation of the base sheet 110 is suppressed.

한편, 엠보무늬(130)의 형성이 완료된 후 냉각과정에서 베이스 시트(110)와 연신 제한시트(140)의 열변형율 차이에 의해 베이스 시트(110)로부터 이형층(150)의 분리가 가능하게 된다.After the formation of the emboss pattern 130 is completed, the release layer 150 can be separated from the base sheet 110 due to the difference in thermal strain between the base sheet 110 and the stretch limit sheet 140 during the cooling process .

한편, 본 실시형태에서, 이형층(150)은, 베이스 시트(110)의 재질에 관계없이 PE(polyethylene) 재질로 구비될 수 있다. Meanwhile, in this embodiment, the release layer 150 may be made of polyethylene (PE) regardless of the material of the base sheet 110.

또한, 본 실시형태에서, 연신 제한시트(140)는, 베이스 시트(110)에 부착되는 면에 코팅되어 구비되되, 설정된 온도 이상에서는 베이스 시트(110)와 접착력을 유지하고, 설정된 온도 이하로 낮아짐에 따라 베이스 시트(110)와의 접착력이 약해지는 재질로 구비되는 이형층(150)을 가진다.In addition, in the present embodiment, the stretching restraint sheet 140 is coated on the surface of the base sheet 110, and maintains the adhesive strength with the base sheet 110 at a set temperature or higher, And a releasing layer 150 made of a material which weakens the adhesive force of the base sheet 110 with respect to the base sheet 110.

이때, 이형층(150)은, 연화점이 55℃ 이하인 고분자 수지로 구비되는 것이 바람직하다.At this time, the release layer 150 is preferably made of a polymer resin having a softening point of 55 ° C or less.

다음으로, 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법의 실시형태에 대하여 설명한다.Next, a description will be given of an embodiment of a method for manufacturing a decor sheet having a printed pattern and an emboss pattern matched with each other according to the present invention.

도 3 내지 도 5는 본 발명에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법을 설명하기 위한 도면이다.FIGS. 3 to 5 are views for explaining a method for manufacturing a decor sheet having a printed pattern and an emboss pattern matched with each other according to the present invention.

도 3 내지 도 5를 참조하면, 본 실시형태에 따른 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법(S10)은, 베이스 시트 준비단계(S11), 연신 제한시트 합지단계(S12), 인쇄무늬 형성단계(S13), 엠보무늬 형성단계(S14), 연신 제한시트 분리단계(S15)를 포함한다.3 to 5, a method (S10) for producing a decor sheet having a printed pattern and an emboss pattern matched with each other according to the present embodiment includes a base sheet preparing step (S11), a stretching limit sheet lining step (S12) A pattern forming step S13, an embroidery pattern forming step S14, and a stretching restraining sheet separating step S15.

베이스 시트 준비단계(S11)는, 열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 유연한 시트형상으로 구비되되, 롤에 감겨진 상태로 베이스 시트(110)를 준비하는 단계이다. 여기서 베이스 시트(110)에 대한 자세한 설명은 앞선 설명으로 대신한다.The base sheet preparation step S11 is a step of preparing the base sheet 110 in the form of a flexible sheet having a predetermined width and length and being wound on a roll, which is provided with a synthetic resin capable of being deformed by heat. Here, the detailed description of the base sheet 110 is replaced by the foregoing description.

연신 제한시트 합지단계(S12)는, 베이스 시트(110)의 열변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비되어, 베이스 시트(110)가 그 길이방향 또는 폭방향으로 연신되는 것을 제한하는 연신 제한시트(140)를 베이스 시트(110)와 마찬가지로 롤에 감겨진 상태로 준비한 후, 베이스 시트(110)와 연신 제한시트(140)를 합지하는 단계이다.The stretching-restraint sheet lining step S12 is provided with a material having a thermal deformation rate relatively smaller than the thermal deformation rate of the base sheet 110 so as to prevent the base sheet 110 from being stretched in the longitudinal direction or the width direction, The step of preparing the limiting sheet 140 in a state of being wound on the roll like the base sheet 110 and then laminating the base sheet 110 and the stretching restraining sheet 140 together.

여기서 연신 제한시트(140)에 대한 자세한 설명은 앞선 설명으로 대신한다.Here, the detailed description of the stretch limiting sheet 140 is replaced with the preceding description.

인쇄무늬 형성단계(S13)는, 베이스 시트(110)의 양면 중 연신 제한시트(140)의 배면으로 정의되는 장식면(111)에 인쇄무늬(120)를 형성하는 단계이다. The printed pattern forming step S13 is a step of forming the printed pattern 120 on the decorative surface 111 defined by the back surface of the stretch limit sheet 140 on both sides of the base sheet 110. [

인쇄무늬 형성단계(S13)는, 독립적인 공정으로 준비될 수도 있으나, 이에 한정되지 않고, 베이스 시트(110)가 일면에 인쇄무늬(120)가 형성(또는 인쇄)된 상태로 준비될 수 있다.The print pattern forming step S13 may be prepared by an independent process, but the present invention is not limited thereto. The base sheet 110 may be prepared in a state in which the print pattern 120 is formed (or printed) on one surface.

여기서 인쇄무늬(120)에 대한 자세한 설명은 앞선 설명으로 대신한다.Here, the detailed description of the print pattern 120 is replaced by the foregoing description.

엠보무늬 형성단계(S14)는, 베이스 시트(110)에 열을 가하여 장식면(111)에 인쇄무늬(120)와 정합되도록 볼록 또는 오목하게 3차원 형상을 가지는 엠보무늬(130)를 형성하는 단계이다. 이는 금형을 이용하여 열과 함께 가압하는 방법으로 수행될 수 있다.The emboss pattern formation step S14 includes the steps of forming an emboss pattern 130 having a convex or concave three-dimensional shape so as to match the printed pattern 120 on the decorative surface 111 by applying heat to the base sheet 110 to be. This can be performed by pressurizing with heat using a mold.

여기서 엠보무늬(130)에 대한 자세한 설명은 앞선 설명으로 대신한다.Here, the detailed description of the emboss pattern 130 is replaced with the foregoing description.

연신 제한시트 분리단계(S15)는, 인쇄무늬(120)와 엠보무늬(130)가 형성된 베이스 시트(110)를 냉각한 후 연신 제한시트(140)를 분리하는 단계이다.The stretching limit sheet separation step S15 is a step of cooling the base sheet 110 on which the print pattern 120 and the emboss pattern 130 are formed and then separating the stretch limit sheet 140. [

여기서, 냉각은 상온 또는 그 이하의 온도 환경을 의미한다.Here, cooling refers to a temperature environment at room temperature or lower.

한편, 본 실시형태에서, 인쇄무늬(120)가 일면에 인쇄된 장식시트를 장식면(111)에 합지할 수 있음은 앞서 설명한 것과 같다.On the other hand, in the present embodiment, the decorative sheet printed on one side of the printed pattern 120 can be joined to the decorative surface 111 as described above.

또한, 본 실시형태에서, 연신 제한시트(140)는, PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 중 어느 하나의 재질로 구비되며, 베이스 시트(110)에 부착되는 면에 PE(polyethylene) 재질로 구비되는 이형층(150)을 가지는 것으로 구비될 수 있다.In the present embodiment, the stretching restriction sheet 140 is made of any one material selected from the group consisting of polyethylene terephthalate (PET), polypropylene (PP), cloth, nonwoven fabric, glass paper and paper, And a release layer 150 made of polyethylene (PE).

Claims (10)

열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 시트형상으로 구비되는 베이스 시트;
상기 베이스 시트의 두께방향으로 양면 중 일면으로 정의되는 장식면에 구비되는 인쇄무늬;
상기 장식면에 볼록 또는 오목하게 3차원 형상을 가지며 형성되되, 상기 인쇄무늬와 정합 되도록 형성되는 엠보무늬; 및
상기 베이스 시트의 양면 중 상기 장식면의 배면에 합지되어 구비되며, 상기 엠보무늬의 형성시 가해지는 열에 의한 상기 베이스 시트의 열 변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비되어, 상기 베이스 시트가 그 길이방향 또는 폭방향으로 연신되는 것을 제한하는 연신 제한시트;를 포함하고,
상기 연신 제한시트는, 상기 엠보무늬 형성이 완료된 후 상기 베이스 시트로부터 분리 가능하게 구비되며,
상기 연신 제한시트는, PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 중 어느 하나의 재질로 구비되고,
상기 연신 제한시트는, 상기 베이스 시트에 부착되는 면에 코팅되어 구비되되, 설정된 온도 이상에서는 상기 베이스 시트와 접착력을 유지하고, 상기 설정된 온도 이하로 낮아짐에 따라 상기 베이스 시트와의 접착력이 약해지는 재질로 구비되는 이형층을 가지는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트.A base sheet provided with a synthetic resin capable of being deformed by heat, the base sheet having a predetermined width and length;
A printed pattern provided on a decorative surface defined as one of both surfaces in a thickness direction of the base sheet;
An emboss pattern formed to have a convex or concave three-dimensional shape on the decorative surface, and to be matched with the print pattern; And
Wherein the base sheet is made of a material having a thermal deformation rate that is less than a thermal deformation rate of the base sheet due to heat applied at the time of forming the emboss pattern, And a stretching limit sheet for restricting stretching in the longitudinal direction or the width direction,
The stretch limiting sheet is detachably provided from the base sheet after the emboss pattern formation is completed,
The stretch limiting sheet may be made of any one material selected from the group consisting of polyethylene terephthalate (PET), polypropylene (PP), cloth, nonwoven fabric, glass paper,
Wherein the stretch limiting sheet is coated on a surface of the base sheet to maintain an adhesive force with the base sheet at a predetermined temperature or higher and is made of a material having a weak adhesive force with the base sheet And a release layer provided on the decorative sheet. 삭제delete 삭제delete 삭제delete 청구항 1에 있어서,
상기 이형층은, 연화점이 55℃ 이하인 고분자 수지로 구비되는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트.The method according to claim 1,
Characterized in that the releasing layer is made of a polymer resin having a softening point of 55 캜 or less, and the printed pattern and the embossed pattern are matched with each other. 청구항 1에 있어서,
상기 이형층은, PE(polyethylene) 재질로 구비되는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트.The method according to claim 1,
Characterized in that the release layer is made of polyethylene (PE) material, and the printed pattern and the embossed pattern are matched. 청구항 1에 있어서,
상기 연신 제한시트는, 상기 베이스 시트에 상기 엠보무늬를 형성한 후 냉각시키는 과정에서 상기 베이스 시트로부터 분리가능하게 구비되는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트.The method according to claim 1,
Wherein the stretch limiting sheet is detachably attached to the base sheet in a process of forming the emboss pattern on the base sheet and cooling the embossing pattern. 열에 의한 변형이 가능한 합성수지로 구비되되, 설정된 폭과 길이를 가지는 시트형상으로 구비되며, 장식면으로 정의되는 일면에 인쇄무늬를 가지는 베이스 시트를 준비하는 제1 단계;
상기 베이스 시트의 열변형율 보다 상대적으로 작은 열변형율을 가지는 소재로 구비되어, 상기 베이스 시트가 그 길이방향 또는 폭방향으로 연신되는 것을 제한하는 연신 제한시트를 상기 베이스 시트의 일면에 합치하는 제2 단계;
상기 베이스 시트에 열을 가하여 상기 장식면에 상기 인쇄무늬와 정합되도록 볼록 또는 오목하게 3차원 형상을 가지는 엠보무늬를 형성하는 제4 단계; 및
상기 인쇄무늬와 상기 엠보무늬가 형성된 상기 베이스 시트를 냉각한 후 상기 연신 제한시트를 분리하는 제5 단계;를 포함하는 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법.A first step of preparing a base sheet provided with a synthetic resin capable of being deformed by heat, the base sheet being provided in a sheet shape having a predetermined width and length and having a printed pattern on one surface defined as a decorative surface;
A second step of fitting a stretching restricting sheet provided with a material having a thermal deformation rate relatively smaller than the thermal deformation rate of the base sheet to restrict the stretching of the base sheet in the longitudinal direction or the width direction to one surface of the base sheet; ;
A fourth step of applying heat to the base sheet to form an emboss pattern having a convex or concave three-dimensional shape on the decorative surface to match the printed pattern; And
And a fifth step of cooling the base sheet on which the embossed pattern and the embossed pattern are formed, and then separating the stretch-limiting sheet. 청구항 8에 있어서,
상기 인쇄무늬는, 상기 베이스 시트와 상기 연신 제한시트가 합지된 상태에서 상기 장식면에 형성되는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법.The method of claim 8,
Wherein the printed pattern is formed on the decorative surface in a state in which the base sheet and the stretch restricting sheet are laminated with each other, the printed pattern and the embossed pattern are matched with each other. 청구항 8에 있어서,
상기 연신 제한시트는,
PET(Polyethylene terephthalate), PP(polypropylene), 천, 부직포, 그라스페이퍼, 종이 중 어느 하나의 재질로 구비되며,
상기 베이스 시트에 부착되는 면에 PE(polyethylene) 재질로 구비되는 이형층을 가지는 것을 특징으로 하는 인쇄무늬와 엠보무늬가 일치된 데코시트의 제조방법.
The method of claim 8,
The stretch limiting sheet may be formed by stretching,
(Polyethylene terephthalate), PP (polypropylene), cloth, non-woven fabric, glass paper, and paper,
And a release layer provided on the surface of the base sheet, the release layer being made of polyethylene (PE) material, the embossed pattern being matched with the printed pattern.
KR1020180050447A 2018-05-02 2018-05-02 Decoration flexible sheet with printed patteren and embossed pattern matched and manufacturing method thereof KR101916351B1 (en)