KR101839594B1 - Carboxylate acrylonitril styrene butadiene copolymer of synthesis rubber latex for reforming semi-rigid pavement and polymer cement and method thereof and modified concrete composition comprising the same - Google Patents
Carboxylate acrylonitril styrene butadiene copolymer of synthesis rubber latex for reforming semi-rigid pavement and polymer cement and method thereof and modified concrete composition comprising the same Download PDFInfo
- Publication number
- KR101839594B1 KR101839594B1 KR1020170092496A KR20170092496A KR101839594B1 KR 101839594 B1 KR101839594 B1 KR 101839594B1 KR 1020170092496 A KR1020170092496 A KR 1020170092496A KR 20170092496 A KR20170092496 A KR 20170092496A KR 101839594 B1 KR101839594 B1 KR 101839594B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- latex
- monomer
- semi
- Prior art date
Abstract
Description
본 발명은 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 및 그의 제조방법 및 그를 포함하는 개질 콘크리트 조성물에 관한 것이다.The present invention relates to a synthetic rubber latex of carboxylate acrylonitrile styrene butadiene copolymer for semi-rigid packaging and polymer cement modification, a process for producing the same, and a modified concrete composition comprising the same.
현재 사용되고 있는 콘크리트 교면포장 및 폴리머 시멘트 몰탈 조성물은 보통 콘크리트의 제반 성능을 개선시키기 위해 콘크리트에 스티렌 부타디엔 라텍스, 카르복실레이트 스틸렌 부타디엔 라텍스, 폴리아크릴 에멀젼 또는 에틸렌 비닐아세테이트, 에폭시 수지 등과 같은 종류의 개질제를 시공 목적에 맞게 혼합시켜 제조한 콘크리트 및 시멘트 몰탈이다. 특히 도로의 교면 포장, 보수, 보강, 표면보호, 교량방수에 있어서는 분산성, 접착성, 방수성 등이 우수한 스티렌 부타디엔 라텍스를 혼합시킨 개질콘크리트 및 시멘트 몰탈이 주로 사용되고 있다.Currently used concrete bridge pavement and polymer cement mortar compositions usually contain modifiers such as styrene butadiene latex, carboxylate styrene butadiene latex, polyacrylic emulsion or ethylene vinyl acetate, epoxy resin and the like to the concrete in order to improve general performance of the concrete It is a concrete and cement mortar produced by mixing according to the purpose of construction. In particular, modified concrete and cement mortar mixed with styrene butadiene latex, which is excellent in dispersibility, adhesiveness, waterproofness, etc., are mainly used in bridge pavement, repair, reinforcement, surface protection and bridge waterproofing of roads.
최근 교량 및 건설구조물의 효과적인 유지관리를 통해 사용수명 연장하는 것에 대한 관심이 높아지고 있다. 특히 콘크리트의 경우 내구성이 우수한 건축 토목재료로 알려져 왔지만 최근 지구 온난화로 인한 잦은 폭설과 과다한 제설제 살포 콘크리트 구조물 손상, 동결융해, 염화물 등에 의해 열화 및 노후화가 진행되어 이에 대한 보수보강이 요구되고 있다. 즉, 내구성 약화로 인해 특히 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성이 열악해지는 문제의 해결이 요구되고 있다. Recent interest in extending service life through effective maintenance of bridges and construction structures is increasing. Especially, concrete has been known as a durable construction civil engineering material. However, recently, it has been required to repair and reinforce it due to frequent heavy snowfalls due to global warming, deterioration and deterioration due to excessive snowing concrete structure damage, freezing and thawing, and chloride. That is, it is required to solve the problem that the oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance are deteriorated due to the durability deterioration.
종래의 콘크리트용 개질제인 스티렌 부타디엔 라텍스의 제조방법으로는 대한민국 등록특허공보 제441055호(2004. 7. 9 등록)에 개시된 것을 들 수 있다. 즉, 상기 특허에서는 부타디엔 단량체, 스티렌 단량체 등을 이용하여 전환율 80~90%에서 70℃로 승온시켜 반응을 완료시키는 것을 특징으로 하는 개질콘크리트 제조용 스티렌-부타디엔 공중합체 라텍스의 제조방법을 소개하고 있다.A conventional method for producing styrene butadiene latex as a modifier for concrete includes those disclosed in Korean Registered Patent No. 441055 (registered on July 7, 2004). That is, the patent discloses a method for preparing a styrene-butadiene copolymer latex for the production of modified concrete, wherein the reaction is completed by raising the conversion from 80 to 90% to 70 ° C. by using a butadiene monomer, a styrene monomer or the like.
그러나, 상기와 같은 방법은 부타디엔 단량체 및 스티렌 단량체를 고압반응기를 이용하여 고온에서 3-5기압의 고압으로 합성시킴에 따라 제조설비가 복잡해짐에 따라 설비의 가동이 까다롭고, 그에 따른 제조설비의 비용이 과다 소요되며, 또한 반응시간이 20시간 이상 소요되는 단점이 있다. 또한, 상기와 같은 단점에도 불구하고 미반응 물질이 많이 잔류하여 스티렌-부타디엔 공중합체 라텍스의 농도가 40-43 중량%에 지나지 않고 고농도의 합성라텍스를 얻기 위해 농축공정이 필요한 문제점이 있었다.However, since the butadiene monomer and the styrene monomer are synthesized at a high pressure of 3 to 5 atm at a high temperature using a high-pressure reactor, the operation of the equipment is complicated as the manufacturing facility becomes complicated, There is a disadvantage that the cost is excessive and the reaction time is more than 20 hours. In addition, despite the disadvantages mentioned above, unreacted materials remain to a great extent, and the concentration of the styrene-butadiene copolymer latex is only 40-43 wt%, and a concentration process is required to obtain a high-concentration synthetic latex.
일반적으로 아스콘 및 콘크리트 포장은 차량에 의해 발생되는 교통하중 및 기후변화에 의한 환경하중 등의 작용으로 여러 형태의 열화 및 파손이 발생한다. 이러한 노후된 아스콘 및 콘크리트 포장은 보수 및 보강이 필수적이다. 공용 중인 도로의 교통차단을 전제로 하는 보수공사는 도로정체와 더불어 이용자의 많은 불편을 야기하므로, 주로 교통량이 적은 야간이나 새벽 시간에 시공이 이루어지고 있으며, 특히 공사개시 후 3~5 시간 내에 교통을 개방해야 하기 때문에 초속경 콘크리트가 사용된다.Generally, various kinds of deterioration and breakage of the ascon and concrete pavement occur due to the action of environmental load due to traffic load and climate change generated by the vehicle. Maintenance and reinforcement of these aged ascon and concrete pavements are essential. Since repair work on the premise of blocking the traffic on the public road leads to many inconveniences of the user along with the road congestion, the construction is carried out at nighttime or at dawn hours where the traffic volume is low. Especially, Speed concrete is used.
그러나 초속경 콘크리트는 강도발현이 빠른 장점이 있지만, 초속경 시멘트의 구성광물 특성상 내수성, 내동해성, 장기내구성 등이 취약해 보수 후에도 다시 재보수를 해야 하는 경우가 자주 발생하는 문제점이 있다. 이에 따라 최근에는 콘크리트의 내구성을 보완하기 위해 수성 폴리머의 일종인 기존에 알려진 SBR 라텍스를 사용한 라텍스 개질 초속경 콘크리트가 보수재료로서 활발히 이용되고 있다.However, the concrete with quick speed is advantageous in that the strength is rapidly developed, but the water resistance, anti-freeze, and long-term durability are poor due to the characteristics of the constituent minerals of the quick-speed cement. Recently, latex modified quick-setting concrete using SBR latex, which is a kind of water-based polymer, has been actively used as a maintenance material to supplement the durability of concrete.
이러한 라텍스를 이용한 콘크리트는 동결융해와 스켈링(scaling)에 대한 저항성이 우수하고 방수성과 부착성이 높아 초속경 시멘트와 물, 골재만을 사용할 때의 단점을 크게 보완하고 도로 보수공사의 품질을 높이는데 크게 기여하였다.These latex-based concrete has excellent resistance to freezing and thawing and scaling, and has high water resistance and adhesion. It greatly improves the shortcomings of using cement, water and aggregate at the first speed and improves the quality of road repair work. Contributed.
그러나 기존의 SBR 라텍스를 첨가하는 경우에 시멘트와의 혼화성과 작업성을 부여하기 위해 다량의 친수성 유화제를 사용하게 되는데, 이는 라텍스 자체의 저장안정성을 떨어뜨려 장기 저장 시, 라텍스 입자의 상분리 발생의 원인이 된다. 또한 이로 인해 기존 SBR 라텍스 개질 초속경 콘크리트에서 시멘트와의 혼화성, 소성크랙, 포설된 부위별 방수성, 내구성에 편차가 발생할 수 있는 문제점이 있다. 한편 기존 SBR 라텍스 개질 초속경 콘크리트는 동절기 저온 경화성능이 떨어져 조기교통개방이 어려울 뿐만 아니라, 양생을 위한 별도의 난방이 필요하기 때문에 시공비 상승 및 품질관리가 어려운 문제점이 있다.However, in the case of adding the existing SBR latex, a large amount of hydrophilic emulsifier is used in order to impart compatibility with the cement and workability. This is because the storage stability of the latex itself is lowered, . In addition, the conventional SBR latex modified quick-speed concrete has a problem that miscibility with cement, plastic crack, waterproof property and durability may be varied. On the other hand, the existing SBR latex modified quick-speed concrete has poor low temperature curing ability during the winter season, and it is difficult to open early traffic, and since heating for curing is required separately, it is difficult to increase the construction cost and quality control.
따라서 앞으로 급증할 노후될 포장 물량을 생각할 때 우리나라도 노후 포장의 근본적인 보수재료 개발이 시급한 상황이다.Therefore, it is urgent for Korea to develop basic repair materials for aging packaging considering the rapidly aging packaging materials.
본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위하여 안출된 것으로서,SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems of the prior art,
본 발명은 포름알데히드가 검출되지 않고, 휘발성 유기화합물의 함량이 낮고, 중금속(납, 크롬, 카드늄, 수은)이 검출되지 않아 친환경적인 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 제공하는 것을 목적으로 한다. The present invention relates to an environmentally friendly semi-rigid packaging and a polymeric cement-modifying carboxylate acrylonitrile styrene butadiene (CIC) resin, which is free of formaldehyde, low in volatile organic compounds and heavy metals (lead, chromium, cadmium, mercury) Copolymer The object of the present invention is to provide a synthetic rubber latex.
또한, 본 발명은 개질 콘크리트 조성물에 포함되어 혼화성, 접착성, 강도, 방수성, 내구성 등의 성능을 향상시키며, 특히 콘크리트의 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 현저히 향상시킬 수 있는 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 제공하는 것을 목적으로 한다. The present invention also provides a method for improving the performance of concrete such as miscibility, adhesion, strength, water resistance and durability, and particularly improving oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance of concrete A semi-rigid packaging and a polymeric cement modifying carboxylate acrylonitrile styrene-butadiene copolymer synthetic rubber latex.
또한, 본 발명은 반응온도 낮은 온도(대략 45℃) 낮은 반응압력인 0.1~0.3 기압(물 포화증기압)의 조건하에서 유화중합시킴으로써, 고온, 고압반응기를 사용할 필요가 없어서 제조설비가 간단하며, 폭발 위험성이 없어 안전하며, 반응시간이 짧아 생산성이 높고, 생성물의 농도가 높은 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 제조방법을 제공하는 것을 목적으로 한다.In addition, the present invention is characterized in that it is not necessary to use a high-temperature and high-pressure reactor by emulsion polymerization under the condition of a reaction pressure of 0.1 to 0.3 atm (water saturation vapor pressure) which is a low reaction temperature (about 45 ° C) It is an object of the present invention to provide a process for preparing a semi-rigid packaging and a carboxylate acrylonitrile styrene-butadiene copolymer synthetic rubber latex for polymer cement reforming, which is safe because of no risk, .
또한, 본 발명은 상기 합성고무라텍스를 포함함으로써 우수한 혼화성, 접착성, 강도, 방수성, 내구성 등의 성능을 제공하며, 특히 우수한 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 제공하는 개질 콘크리트 조성물을 제공하는 것을 목적으로 한다. Further, the present invention provides a rubber composition containing the synthetic rubber latex, which provides performance such as excellent compatibility, adhesion, strength, water resistance and durability, and in particular, a modifier for providing excellent oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance It is an object of the present invention to provide a concrete composition.
또한, 본 발명은 상기 합성고무라텍스를 포함함으로써 시멘트와의 혼화성이 우수하여 초속경 콘크리트 제조 작업이 용이하게 되며, 가사기간이 충분히 확보되어 콘크리트 면의 평탄성을 확보할 수 있으며, 타설 후 4시간 이내에 기준치 이상인 25 MPa 이상의 압축강도를 발현하고, 방수성과 염분침투저항성, 동결융해저항 성능이 우수하여 슬래브 및 콘크리트 내의 철근의 부식을 막고 내구성능을 개선하여 구조물의 수명을 연장할 수 있는 개질 콘크리트 조성물을 제공하는 것을 목적으로 한다.In addition, since the present invention includes the synthetic rubber latex, it is excellent in compatibility with cement to facilitate construction work of quick-speed concrete, securing the flatness of the concrete surface sufficiently and ensuring the flatness of the concrete surface. Modified concrete composition capable of extending the life of the structure by improving the durability and preventing the corrosion of the reinforcing bars in the slab and concrete by exhibiting the compressive strength of 25 MPa or more which is higher than the reference value and being excellent in the waterproof property, the salt penetration resistance and the freezing- And to provide the above objects.
상기의 목적을 달성하기 위하여, 본 발명은In order to achieve the above object,
시드(seed) 라텍스 10~20 중량부, 폴리부타디엔 라텍스 30~40 중량부, 아크릴로니트릴 모노머 20~50 중량부, 스티렌 모노머 10~30 중량부, 불포화 카르복실산 단량체 2~8 중량부, 아크릴레이트 단량체 2~8 중량부, 유화제 3~8 중량부, 반응개시제 2~5 중량부, 및 첨가제 1~15 중량부를 반응기에 일괄 투입하여, 0.2~0.5 기압, 35~55℃의 조건에서 4~8 시간 동안 유화중합 및 그라프트 반응시켜 합성시켜서 제조된 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 제공한다.10 to 20 parts by weight of a seed latex, 30 to 40 parts by weight of a polybutadiene latex, 20 to 50 parts by weight of an acrylonitrile monomer, 10 to 30 parts by weight of a styrene monomer, 2 to 8 parts by weight of an unsaturated carboxylic acid monomer, 2 to 8 parts by weight of a monomer, 3 to 8 parts by weight of an emulsifier, 2 to 5 parts by weight of a reaction initiator and 1 to 15 parts by weight of an additive are fed into a reactor at a total pressure of 0.2 to 0.5 atm, Styrene-butadiene copolymer synthetic rubber latex for semi-rigid packaging and polymer cement reforming, which is prepared by emulsion polymerization and grafting reaction for 8 hours.
상기 합성고무라텍스는 고형분이 40~60 중량%이고, pH가 10~11.5이며, 점도가 50~100 cps이며, 평균입자경이 1200~2000Å인 특징을 가질 수 있다. The synthetic rubber latex may have a solid content of 40 to 60 wt%, a pH of 10 to 11.5, a viscosity of 50 to 100 cps, and an average particle size of 1200 to 2000 ANGSTROM.
본 발명은 또한,The present invention also relates to
시드(seed) 라텍스 10~20 중량부, 폴리부타디엔 라텍스 10~20 중량부, 아크릴로니트릴 모노머 20~50 중량부, 스티렌 모노머 10~35 중량부, 불포화 카르복실산 단량체 2~8 중량부, 아크릴레이트 단량체 2~8 중량부, 유화제 3~8 중량부, 반응개시제 2~5 중량부, 및 첨가제 1~15 중량부를 반응기에 일괄 투입하는 단계; 및10 to 20 parts by weight of a seed latex, 10 to 20 parts by weight of a polybutadiene latex, 20 to 50 parts by weight of an acrylonitrile monomer, 10 to 35 parts by weight of a styrene monomer, 2 to 8 parts by weight of an unsaturated carboxylic acid monomer, 2 to 8 parts by weight of a monomer, 3 to 8 parts by weight of an emulsifier, 2 to 5 parts by weight of a reaction initiator and 1 to 15 parts by weight of an additive in a reactor; And
0.2~0.5 기압, 35~55℃의 조건에서 4~8 시간 동안 유화중합 및 그라프트 반응을 진행하는 단계;를 포함하는 것을 특징으로 하는 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 제조방법을 제공한다.And carrying out emulsion polymerization and grafting reaction for 4 to 8 hours under the conditions of 0.2 to 0.5 atm and 35 to 55 ° C. The semi-rigid packaging and polymer cement modifying carboxylate acrylonitrile styrene Butadiene copolymer rubber latex.
본 발명은 또한,The present invention also relates to
상기 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 전체 콘크리트 조성물 총 중량에 대하여 10~30 중량%로 포함하는 것을 특징으로 하는 개질 콘크리트 조성물을 제공한다.The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex is contained in an amount of 10 to 30% by weight based on the total weight of the concrete composition.
상기 개질 콘크리트 조성물에는 하기 화학식 1로 표시되는 화합물을 1~5 중량%가 더 포함될 수 있다:The modified concrete composition may further comprise 1 to 5% by weight of a compound represented by the following Formula 1:
[화학식 1][Chemical Formula 1]
상기 식에서 n은 1~10의 자연수이다.In the above formula, n is a natural number of 1 to 10.
상기 개질 콘크리트 조성물에는 염해를 방지하기 위해 하기 화학식 2 및 화학식 3으로 표시되는 화합물 중에서 선택되는 1종 이상이 1~3 중량% 더 포함될 수 있다:The modified concrete composition may further contain 1 to 3% by weight of at least one compound selected from compounds represented by the following formulas (2) and (3)
[[ 화학식2(2) ]]
[화학식 3](3)
본 발명의 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스는 포름알데히드가 검출되지 않고, 휘발성 유기화합물의 함량이 낮고, 중금속(납, 크롬, 카드늄, 수은)이 검출되지 않아 친환경적이다. The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene-butadiene copolymer synthetic rubber latex of the present invention is characterized in that formaldehyde is not detected and the content of volatile organic compounds is low and heavy metals (lead, chromium, cadmium, mercury) Is not detected and is environmentally friendly.
또한, 상기 합성고무라텍스는 개질 콘크리트 조성물에 포함되어 혼화성, 접착성, 강도, 방수성, 내구성 등의 성능을 향상시키며, 특히 콘크리트의 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 현저히 향상시키는 효과를 제공한다. In addition, the synthetic rubber latex is included in the modified concrete composition to improve performance such as miscibility, adhesiveness, strength, water resistance, durability and the like, and particularly remarkably improves the oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance of concrete .
또한, 본 발명의 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 제조방법은 반응온도 낮은 온도(대략 45℃) 낮은 반응압력인 0.1~0.3 기압(물 포화증기압)의 조건하에서 유화중합시킴으로써, 고온, 고압반응기를 사용할 필요가 없어서 제조설비가 간단하며, 폭발 위험성이 없어 안전하며, 반응시간이 짧아 생산성이 높고, 생성물의 농도가 높다.In addition, the process for preparing a semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex of the present invention is characterized in that the reaction temperature is low (about 45 ° C) and the reaction pressure is 0.1 to 0.3 atm Vapor pressure), it is not necessary to use a high-temperature and high-pressure reactor, so that the production facility is simple, the explosion is not dangerous, the reaction time is short, the productivity is high, and the product concentration is high.
또한, 본 발명의 개질 콘크리트 조성물은 상기 합성고무라텍스를 포함함으로써 우수한 혼화성, 접착성, 강도, 방수성, 내구성 등의 성능을 제공하며, 특히 우수한 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 제공한다. In addition, the modified concrete composition of the present invention provides excellent compatibility, adhesion, strength, water resistance and durability by including the synthetic rubber latex. In particular, it has excellent oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance, ozone resistance .
또한, 본 발명의 개질 콘크리트 조성물은 상기 합성고무라텍스를 포함함으로써 시멘트와의 혼화성이 우수하여 초속경 콘크리트 제조 작업이 용이하게 되며, 가사기간이 충분히 확보되어 콘크리트 면의 평탄성을 확보할 수 있다. 또한, 상기 초속경 콘크리트의 타설 후 4시간 이내에 기준치 이상인 25 MPa 이상의 압축강도를 발현하고, 방수성과 염분침투저항성, 동결융해저항 성능이 우수하여 슬래브 및 콘크리트 내의 철근의 부식을 막고 내구성능을 개선하여 구조물의 수명을 연장하는 효과를 제공한다. Also, the modified concrete composition of the present invention is excellent in compatibility with cement due to the synthetic rubber latex, facilitating the work of preparing quick-speed concrete, and ensuring the flatness of the concrete surface. Also, it exhibits a compressive strength of 25 MPa or more, which is higher than the reference value within 4 hours after the above-mentioned quick-speed concrete is poured, and is excellent in waterproof property, salt penetration resistance and freezing and thawing resistance performance to prevent corrosion of reinforcing bars in slabs and concrete, Thereby providing an effect of extending the life of the structure.
이하에서 본 발명을 자세히 설명한다.Hereinafter, the present invention will be described in detail.
본 발명은 시드(seed) 라텍스 10~20 중량부, 폴리부타디엔 라텍스 30~40 중량부, 아크릴로니트릴 모노머 20~50 중량부, 스티렌 모노머 10~30 중량부, 불포화 카르복실산 단량체 2~8 중량부, 아크릴레이트 단량체 2~8 중량부, 유화제 3~8 중량부, 반응개시제 2~5 중량부, 및 첨가제 1~15 중량부를 반응기에 일괄 투입하여, 0.2~0.5 기압, 35~55℃의 조건에서 4~8 시간 동안 유화중합 및 그라프트 반응시켜 합성시켜서 제조된 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스에 관한 것이다.The present invention relates to a thermoplastic resin composition comprising 10 to 20 parts by weight of seed latex, 30 to 40 parts by weight of polybutadiene latex, 20 to 50 parts by weight of acrylonitrile monomer, 10 to 30 parts by weight of styrene monomer, 2 to 8 parts by weight of unsaturated carboxylic acid monomer 2 to 8 parts by weight of an acrylate monomer, 3 to 8 parts by weight of an emulsifier, 2 to 5 parts by weight of a reaction initiator and 1 to 15 parts by weight of an additive are fed into a reactor under the conditions of 0.2 to 0.5 atm and 35 to 55 ° C For 4 to 8 hours by emulsion polymerization and grafting. The present invention also relates to a synthetic rubber latex for carboxylate acrylonitrile styrene butadiene copolymer for polymer cement modification.
상기 합성고무라텍스는 고형분이 40~60 중량%이고, pH가 10~11.5이며, 점도가 50~100 cps이며, 평균입자경이 1200~2000Å인 특징을 가질 수 있다. The synthetic rubber latex may have a solid content of 40 to 60 wt%, a pH of 10 to 11.5, a viscosity of 50 to 100 cps, and an average particle size of 1200 to 2000 ANGSTROM.
본 발명에서 상기 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스는 주로 일반 콘크리트와 시멘트 몰탈 조성물의 물성을 향상시키기 위해 콘크리트와 시멘트 몰탈 조성물의 개질용으로 사용된다. 이렇게 개질된 개질콘크리트와 시멘트 몰탈 조성물은 굳지 않은 상태에서는 유동성이 크게 향상되고 재료분리 저항성이 우수하며, 경화 후에는 라텍스 입자가 콘크리트 및 시멘트 몰탈 조성물 내부의 미세공극을 채워 충진재 역할을 함과 동시에 필름 막을 형성하여 방수 역할을 하므로, 인장강도 및 부착강도가 매우 크고, 그리고 균열저항성이 좋아진다. 또한, 이렇게 개질된 개질콘크리트와 시멘트 몰탈 조성물은 제반 성능이 크게 개선되고 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성이 우수한 것이 특징이다. In the present invention, the semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex is mainly used for modifying concrete and cement mortar composition to improve physical properties of general concrete and cement mortar composition . The modified concrete and the cement mortar composition thus improved greatly in fluidity and excellent resistance to material separation in the uncured state. After the curing, the latex particles fill the micro voids in the concrete and cement mortar composition, Since it forms a film and plays a waterproof function, its tensile strength and adhesion strength are very high, and crack resistance is improved. Also, the modified concrete and cement mortar composition thus modified are remarkably improved in performance and excellent in oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance.
상기 시드(seed) 라텍스는, 폴리부타디엔 라텍스를 중합하여 합성할 때 중합체의 입자를 성장시키기 위해 중합 전 첨가하는 라텍스로서, 시드(seed) 라텍스의 첨가량이 상기에서 정한 범위보다 적게 첨가될 경우 폴리부타디엔 라텍스, 아크릴로니트릴, 스틸렌 모노머의 과량으로 인해 중합 라텍스의 시드(seed)에 엉김 현상이 발생되거나 또는 미반응의 폴리부타디엔 라텍스와 아크릴로니트릴, 스틸렌 모노머가 잔류하여 전화율이 낮아질 우려가 있다. 또한, 시드(seed) 라텍스의 첨가량이 상기에서 정한 범위보다 많을 경우에는 시드(seed) 라텍스의 첨가량에 비해 폴리부타디엔 라텍스, 아크릴로니트릴, 스틸렌 모노머의 첨가량이 부족하므로 SNBR 합성라텍스 시드(seed)가 제대로 성장하지 못할 우려가 있다. The seed latex is a latex to be added before polymerization to grow polymer particles when synthesized by polymerization of polybutadiene latex. When the addition amount of the seed latex is less than the range defined above, the polybutadiene There is a possibility that the seed of the polymerization latex tends to flocculate due to an excess amount of latex, acrylonitrile and styrene monomer, or unreacted polybutadiene latex, acrylonitrile and styrene monomer remain, resulting in lower conversion rate. When the addition amount of the seed latex is larger than the range defined above, the addition amount of the polybutadiene latex, acrylonitrile and styrene monomer is less than the addition amount of the seed latex, so that the SNBR synthetic latex seed There is concern that it will not grow properly.
본 발명에서 시드(seed) 라텍스 입자의 크기는 600 ~ 1,000Å인 것이 바람직하다. 시드(seed) 라텍스 입자의 크기가 600Å 미만이 될 경우에는 라텍스의 최종입자경이 작아 점도가 높고, 교반이 어렵고, 시멘트 혼합성이 어려울 수 가 있고, 시드(seed) 라텍스 입자의 크기가 1,000Å를 초과할 경우에는 최종입자경이커서 라텍스 응고물이 다량발생 할 우려가 있다. In the present invention, the size of the seed latex particles is preferably 600 to 1,000 angstroms. When the size of the seed latex particles is less than 600 ANGSTROM, the final particle diameter of the latex is small and viscosity is high, stirring is difficult, cement mixing is difficult, and seed latex particles have a size of 1,000 ANGSTROM There is a possibility that a large amount of latex coagulated product is generated due to a large final particle diameter.
본 발명에서 주제인 폴리부타디엔 라텍스의 기본물성은 고형분 38~41 중량%, 반응전환율 98%, 점도 70cps, 표면장력 45dyne/㎝, 입자 크기 600~1,000Å, 겔 함량 70~85 중량%, 응고물 0.2 중량% 이하인 것이 바람직하다. The basic physical properties of the polybutadiene latex as a subject of the present invention are as follows: a solid content of 38 to 41 wt%, a reaction conversion rate of 98%, a viscosity of 70 cps, a surface tension of 45 dyne / cm, a particle size of 600 to 1,000 ANGSTROM, a gel content of 70 to 85 wt% And preferably 0.2% by weight or less.
폴리부타디엔 라텍스의 입자경이 상기에서 정한 크기의 범위보다 작을 경우에는 폴리부타디엔 라텍스의 입자의 크가가 적어 개질콘크리트의 제반 물성이 저하할 우려가 있고, 상기에서 정한 크기의 범위보다 클 경우에는 아크릴로니트릴, 스티렌 모노머와의 그라프트 공중합시 SNBR 합성라텍스를 균일하게 형성시키기가 어려워 개질콘크리트의 제반 물성의 저하를 초래할 우려가 있다. 그리고 고형분 또는 겔의 함량이 상기에서 정한 함량의 범위보다 적을 경우에는 그라프트 단량체가 증가하면서 중합속도가 빨라짐에 따라 중합 안정성이 저하되어 응고물이 다량 생성될 우려가 있고, 상기에서 정한 함량의 범위보다 클 경우에는 그라프트 단량체가 감소되어 그라프트반응이 불균일하게 진행되어 SNBR 합성라텍스의 물성이 저하될 우려가 있다.When the particle size of the polybutadiene latex is smaller than the range defined above, the physical properties of the modified concrete may be lowered because the particle size of the polybutadiene latex is small. When the particle size of the polybutadiene latex is larger than the range defined above, It is difficult to uniformly form the SNBR synthetic latex upon graft copolymerization with nitrile and styrene monomer, which may result in deterioration of the physical properties of the modified concrete. When the content of the solid or gel is less than the content defined above, the polymerization stability is lowered as the graft monomer is increased and the polymerization stability is lowered. Thus, a large amount of solidification product may be produced. , The graft monomer may be decreased and the graft reaction may proceed unevenly, which may lower the physical properties of the SNBR synthetic latex.
본 발명에서 아크릴로니트릴 모노머, 스티렌 모노머의 조성비는 폴리부타디엔 라텍스와 공중합시키기 위한 조성비로써, 폴리부타디엔 라텍스 30~40 중량부, 아크릴로니트릴 모노머 20~50 중량부, 스티렌 모노머 10~30 중량부의 함량비로 반응시키는 것이 바람직하다. 폴리부타디엔 라텍스와 아크릴로니트릴, 스티렌 모노머의 함량비가 상기에서 정한 범위를 벗어날 경우에는 미반응된 폴리부타디엔 라텍스와 아크릴로니트릴, 스티렌 모노머의 잔류 물질로 인하여 합성라텍스의 농도가 저하될 우려가 있다. 본 발명에 가장 중요한 구성성분인 아크릴로니트릴 모노머는 수용성, 친수성이고 반응성이 우수하기 때문에 단독으로 사용할 경우 반응속도조절이 매우 어렵고, 소량 사용할 경우 콘크리트, 시멘트 몰탈 조성물의 내유성 등의 제반물성을 악화시킨다.In the present invention, the composition ratio of acrylonitrile monomer and styrene monomer is 30 to 40 parts by weight of polybutadiene latex, 20 to 50 parts by weight of acrylonitrile monomer, 10 to 30 parts by weight of styrene monomer Is preferable. When the content ratio of the polybutadiene latex, acrylonitrile, and styrene monomer is out of the range defined above, there is a possibility that the concentration of the synthetic latex is lowered due to unreacted polybutadiene latex, acrylonitrile, and styrene monomer. Since the acrylonitrile monomer, which is the most important constituent of the present invention, is water-soluble, hydrophilic and excellent in reactivity, it is very difficult to control the reaction rate when used alone, and when used in a small amount, the physical properties such as oil resistance of concrete and cement mortar composition are deteriorated .
상기 불포화 카르복실산 단량체는 수용액 상에 현탁된 합성라텍스 입자의 껍질부에 친수성 유화제와 함께 카르복시기(-COOH)를 결합시켜 SNBR 합성라텍스의 유동성, 접착성, 방수성, 내구성 등과 같은 물성을 향상시켜주는 역할을 한다. 상기 불포화 카르복실산 단량체로는 아크릴산, 메타크릴산, 퓨마릭산, 및 이타콘산 등으로 이루어진 군으로부터 선택되는 1종 이상의 것을 들 수 있으며, The unsaturated carboxylic acid monomer may be prepared by binding a carboxyl group (-COOH) together with a hydrophilic emulsifier to the shell of synthetic latex particles suspended in an aqueous solution to improve physical properties such as fluidity, adhesiveness, water resistance and durability of the SNBR synthetic latex It plays a role. Examples of the unsaturated carboxylic acid monomer include at least one selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, and itaconic acid,
상기 아크릴레이트 단량체로는 메틸메타크릴레이트, 메틸아크릴레이트, 에틸아크릴레이트, 부틸아크릴레이트, 2-에틸헥실아크릴레이트, 라우릴메타크릴레이트, 하이드록시 알킬 아크릴레이트, 및 글리시딜 메타아크릴레이트 등으로 이루어진 군으로부터 선택되는 1종 이상의 것을 들 수 있으며, 특히 메틸메타크릴레이트가 바람직하게 사용될 수 있다.Examples of the acrylate monomers include methyl methacrylate, methyl acrylate, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, lauryl methacrylate, hydroxyalkyl acrylate, and glycidyl methacrylate , And methyl methacrylate is particularly preferably used.
본 발명에서 사용하는 불포화 카르복실산 단량체는 메타아크릴산메틸(methyl methacrylate), 메타크릴산(methacrylic acid), 이타코닉산(itaconic acid), 및 퓨마릭산을 모두 포함하는 것이 더욱 바람직하며, 이들은 1~2 : 1~2 : 1~2 : 1~2의 중량비로 포함될 수 있다.The unsaturated carboxylic acid monomer used in the present invention is more preferably all of methyl methacrylate, methacrylic acid, itaconic acid, and fumaric acid, 2: 1 ~ 2: 1 ~ 2: 1 ~ 2.
상기에서 메틸메타크릴레이트(methyl methacrylate)는 상기에서 정한 첨가량의 범위보다 적게 첨가할 경우에는 반응속도가 늦어지고 내구성 물성이 저하될 우려가 있고, 상기에서 정한 첨가량의 범위보다 많이 첨가할 경우에 반응속도가 빨라 반응속도조절이 어렵게 될 우려가 있다. If methyl methacrylate is added in an amount less than the above-defined range, the reaction rate will be slower and the durability property may be deteriorated. If the amount of methyl methacrylate is more than the range of the addition amount, There is a fear that it is difficult to control the reaction rate because the speed is high.
그리고 메타크릴산(methacrylic acid)은 상기에서 정한 첨가량의 범위보다 적게 첨가할 경우에는 반응속도가 늦고, 상기에서 정한 첨가량의 범위보다 많이 첨가할 경우에 라텍스 안정성이 부족하여 응고물이 다량 발생할 우려가 있다. When methacrylic acid is added in an amount less than the above defined range, the reaction rate is slow. When the amount of methacrylic acid added is more than the range of the amount added, the stability of the latex is insufficient, have.
또한, 이타코닉산(itaconic acid)은 상기에서 정한 첨가량의 범위보다 적게 첨가할 경우에는 중합안정성 떨어지고, 상기에서 정한 첨가량의 범위보다 많이 첨가할 경우에 내수성, 방수성이 떨어질 우려가 있다. When itaconic acid is added in an amount less than the above-defined range, the polymerization stability is deteriorated, and when it is added in an amount exceeding the above-defined range, the water resistance and water resistance may deteriorate.
또한, 퓨마릭산(fumaric acid)은 상기에서 정한 첨가량의 범위보다 적게 첨가할 경우에는 라텍스 안정성이 떨어져 pH를 조정할 때 점도가 급상승할 우려가 있고, 상기에서 정한 첨가량의 범위보다 많이 첨가할 경우에 점도조절이 용이하다. When fumaric acid is added in an amount less than the above-defined range, there is a risk that the viscosity of the latex becomes poor when the pH is adjusted because of the low stability of the latex. Adjustment is easy.
또한, 본 발명에서 사용 가능한 유화제로는 소디움도데실벤젠설포네이트, 소디움라우릴설페이트, 소디움옥틸설페이트, 소디움톨루엔설포네이트, 포타슘스테아릴포스페이트, 포타슘스테아레이트 중에서 선택되는 1종 또는 2종 이상을 들 수 있다. 상기 음이온 유화제의 첨가량은 상기에서 정한 범위보다 적게 첨가하면 중합속도가 느려지고 중합안정성이 저하되어 다량의 응고체가 형성되어 생산성이 저하할 우려가 있고, 그리고 상기에서 정한 범위보다 많이 첨가하면 중합속도가 빨라지고 안정성이 높은 장점이 있는 반면에 과도한 유화제의 사용으로 인해 다량의 거품(foam) 발생과 최종 제품의 가공물성에 나쁜 영향을 미칠 우려가 있다. As the emulsifier usable in the present invention, one or two or more selected from sodium dodecylbenzene sulfonate, sodium lauryl sulfate, sodium octyl sulfate, sodium toluene sulfonate, potassium stearyl phosphate, and potassium stearate may be used. . If the addition amount of the anionic emulsifier is less than the range defined above, the polymerization rate will be slower and the polymerization stability will be lowered to cause a large amount of solidification product to be formed and the productivity will be lowered. While there is a high stability advantage, excessive use of emulsifier may cause a large amount of foam and adversely affect processing properties of final product.
본 발명에서 사용 가능한 반응개시제로는 벤조일퍼옥사이드, 테트라 부틸퍼옥사이드, 디이소프로필벤젠하이드로퍼옥사이드, 암모늄퍼설페이트, 포타슘퍼설페이트, 아세틸퍼옥사이드, 및 큐멘하이드로퍼옥사이드 등으로 이루어진 군으로부터 선택되는 1종 또는 2종 이상을 들 수 있다. 상기 반응개시제의 첨가량은 상기에서 정한 범위보다 적게 첨가하면 반응 속도가 느려 미반응 단량체가 다량 잔류하여 생산성이 저하할 우려가 있고, 그리고 상기에서 정한 범위보다 많이 첨가하면 급격한 반응에 의한 중합체의 안정성이 저하할 우려가 있다.The reaction initiator usable in the present invention is selected from the group consisting of benzoyl peroxide, tetrabutyl peroxide, diisopropylbenzene hydroperoxide, ammonium persulfate, potassium persulfate, acetyl peroxide, cumene hydroperoxide and the like One kind or two kinds or more of them may be mentioned. If the addition amount of the reaction initiator is less than the range defined above, the reaction rate will be slow, resulting in a large amount of unreacted monomers remaining, resulting in a decrease in productivity. If the addition amount is more than the range defined above, the stability of the polymer There is a risk of degradation.
상기 첨가제로는 분자량조절제, 가교제, 및 안정제 등으로 이루어진 군에서 선택되는 1종 이상의 것을 들 수 있다. Examples of the additive include at least one selected from the group consisting of a molecular weight modifier, a crosslinking agent, and a stabilizer.
본 발명에서 사용 가능한 분자량 조절제로는 n-도데실메르캅탄, t-도데실 메르캅탄, n-옥틸메르캅탄 중에서 선택되는 1종 또는 2종 이상을 들 수 있다. 상기 분자량 조절제는 첨가제 100 중량부를 기준으로 1~50 중량부로 포함될 수 있다. 상기에서 정한 범위보다 적게 첨가하면 그라프트율이 낮아 합성라텍스의 물성을 얻기 어려울 우려가 있고, 그리고 상기에서 정한 범위보다 많이 첨가하면 과도한 그라프트율에 의해 도리어 합성라텍스의 물성을 얻기 어려울 우려가 있다. Examples of the molecular weight modifier that can be used in the present invention include one or more selected from n-dodecyl mercaptan, t-dodecyl mercaptan, and n-octyl mercaptan. The molecular weight modifier may be included in an amount of 1 to 50 parts by weight based on 100 parts by weight of the additive. If the amount is less than the above-defined range, the grafting rate is low, which may make it difficult to obtain the physical properties of the synthetic latex. If the amount is larger than the above-specified range, it may be difficult to obtain the physical properties of the synthetic latex due to excessive grafting.
본 발명에서 사용 가능한 가교제로는 디비닐벤젠, 1,3-부탄디올 아크릴레이트, 1,3-부탄디올 디메타크릴레이트, 1,4-부탄디올 디아크릴레이트, 1,4-부탄디올 디메타크릴레이트, 아릴 아크릴레이트, 아릴 메타크릴레이트, 테트라에틸렌글리코올 디아크릴레이트, 테트라에티렌글리콜 디메타크릴레이트로 이루어진 군에서 선택되는 1종 또는 2종 이상을 들 수 있다. 상기 가교제는 첨가제 100 중량부를 기준으로 1~50 중량부로 포함될 수 있다. 상기에서 정한 범위보다 적게 첨가하면 충분한 가교가 일어나지 않을 우려가 있고, 그리고 상기에서 정한 범위보다 많이 첨가하면 글라스 전이온도 높아 휨 강도가 높아질 우려가 있다.Examples of the crosslinking agent usable in the present invention include divinylbenzene, 1,3-butanediol acrylate, 1,3-butanediol dimethacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, Acrylate, aryl methacrylate, tetraethylene glycol diacrylate, tetraethylene glycol dimethacrylate, and the like. The crosslinking agent may be contained in an amount of 1 to 50 parts by weight based on 100 parts by weight of the additive. If it is added in an amount less than the range defined above, there is a fear that sufficient crosslinking does not occur, and if it is added in an amount exceeding the range defined above, the glass transition temperature may be high and the bending strength may increase.
본 발명에서 사용가능한 암포트릭(amphoteric) 안정제로는 노닐페닐에테르술폰산염 및 노닐폐닐에테르술폰산 암모늄 중에서 선택되는 1종 또는 2종 이상을 들 수 있다. 상기 암포트릭(amphoteric) 안정제는 첨가제 100 중량부를 기준으로 1~50 중량부로 포함될 수 있다. 상기에서 의 첨가량은 상기에서 정한 범위보다 적게 첨가하면 반응계의 pH가 산성계열로 변하여 중합안정성, 라텍스 안정성이 떨어져 응고물이 다량 발생할 우려가 있고, 그리고 상기에서 정한 범위보다 많이 첨가하면 콘크리트 내구성, 접착성, 방수성 물성을 저하시킬 우려가 있다.Examples of the amphoteric stabilizer usable in the present invention include at least one selected from nonyl phenyl ether sulfonate and ammonium nonyl ether sulfonate. The amphoteric stabilizer may be included in an amount of 1 to 50 parts by weight based on 100 parts by weight of the additive. If the addition amount is less than the above-defined range, the pH of the reaction system may be changed to an acidic system, resulting in a decrease in polymerization stability and latex stability, and a large amount of solidification product may be generated. There is a possibility of deteriorating physical properties such as water resistance and water resistance.
상기 첨가제로는 이 분야에 공지되어 있는 전해질도 사용될 수 있다. As the additive, an electrolyte known in the art may also be used.
본 발명에 있어서, 상기 시드(seed) 라텍스로는 부타디엔 단량체 및 스티렌 단량체를 6~9.5 : 0.5~4 중량부로 포함하는 유화중합체를 사용하는 것이 바람직하다. 즉, 부타디엔 단량체 및 스티렌 단량체를 유화중합시켜서 제조되는 것이 사용될 수 있다. 이 때, 상기에서 설명된 불포화 카르복실산, 메틸메타크릴레트같은 다른 단량체, 반응개시제, 그 밖에 분자량 조절제, 가교제 등을 첨가하여 유화중합을 실시할 수 있다.In the present invention, it is preferable to use an emulsion polymer containing 6 to 9.5: 0.5 to 4 parts by weight of a butadiene monomer and a styrene monomer as the seed latex. That is, those prepared by emulsion polymerization of a butadiene monomer and a styrene monomer can be used. At this time, emulsion polymerization can be carried out by adding the above-described unsaturated carboxylic acid, other monomers such as methyl methacrylate, a reaction initiator, a molecular weight regulator, a crosslinking agent and the like.
구체적인 방법은 상기 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 제조방법과 동일하게 할 수 있다. A specific method may be the same as the method for producing the carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex.
본 발명의 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스는 예를 들어, 수용액 상에 현탁된 합성라텍스 입자의 시드(seed)에 디비닐벤젠과 같은 가교제를 넣어 가교 구조를 갖게 하고, 스틸렌 모노머대신 아크릴로니트릴 모노머로 대체하고, 시드(seed)의 껍질부는 메틸메타아크릴레이트, 메타크릴산, 이타코닉산, 퓨마릭산과 같은 불포화카르복실산을 결합킴으로써 합성라텍스의 유동성, 접착성, 방수성, 내구성 등과 같은 물성을 향상시킴과 동시에 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 향상시킨 것을 특징으로 한다.Carboxylate acrylonitrile styrene butadiene copolymer of the present invention Synthetic rubber latex can be obtained, for example, by adding a crosslinking agent such as divinylbenzene to a seed of synthetic latex particles suspended in an aqueous solution to obtain a crosslinked structure, The shell of the seed is replaced with an acrylonitrile monomer in place of the monomer and an unsaturated carboxylic acid such as methylmethacrylate, methacrylic acid, itaconic acid or fumaric acid is bonded to the synthetic latex to improve the fluidity, Water resistance, durability and the like, and at the same time, has improved oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance.
본 발명의 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 콘크리트에 혼합시키면, 수용액 상에 현탁된 합성라텍스 입자의 껍질부에 친수성 유화제와 카르복시기(-COOH)와 극성기를 지닌 니트릴기(-C≡N) 를 결합시켜 합성라텍스의 물성을 향상시켜주므로 콘크리트의 제반 성능인 혼화성, 접착성, 강도, 방수성, 내구성 등을 향상시킬 수 있고, 특히 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 향상시킨다. Carboxylate acrylonitrile styrene butadiene copolymer of the present invention When a synthetic rubber latex is mixed with concrete, a hydrophilic emulsifier, a carboxyl group (-COOH) and a nitrile group (--COOH) having a polar group are added to the shell of synthetic latex particles suspended in an aqueous solution. C≡N) to improve the physical properties of the synthetic latex. Therefore, it is possible to improve the miscibility, adhesiveness, strength, water resistance and durability of various concrete properties, and in particular, to improve oil resistance, heat resistance, cold resistance, chemical resistance, Thereby improving ozone resistance.
본 발명은 또한,The present invention also relates to
시드(seed) 라텍스 10~20 중량부, 폴리부타디엔 라텍스 10~20 중량부, 아크릴로니트릴 모노머 20~50 중량부, 스티렌 모노머 10~35 중량부, 불포화 카르복실산 단량체 2~8 중량부, 아크릴레이트 단량체 2~8 중량부, 유화제 3~8 중량부, 반응개시제 2~5 중량부, 및 첨가제 1~15 중량부를 반응기에 일괄 투입하는 단계; 및10 to 20 parts by weight of a seed latex, 10 to 20 parts by weight of a polybutadiene latex, 20 to 50 parts by weight of an acrylonitrile monomer, 10 to 35 parts by weight of a styrene monomer, 2 to 8 parts by weight of an unsaturated carboxylic acid monomer, 2 to 8 parts by weight of a monomer, 3 to 8 parts by weight of an emulsifier, 2 to 5 parts by weight of a reaction initiator and 1 to 15 parts by weight of an additive in a reactor; And
0.2~0.5 기압, 35~55℃의 조건에서 4~8 시간 동안 유화중합 및 그라프트 반응을 진행하는 단계;를 포함하는 것을 특징으로 하는 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 제조방법에 관한 것이다.And carrying out emulsion polymerization and grafting reaction for 4 to 8 hours under the conditions of 0.2 to 0.5 atm and 35 to 55 ° C. The semi-rigid packaging and polymer cement modifying carboxylate acrylonitrile styrene Butadiene copolymer rubber latex.
상기에서 정한 반응압력, 반응온도 및 반응시간 범위보다 압력이나 온도나 반응시간이 짧을 경우에는 충분한 합성 반응이 일어나지 아니하여 미반응 물질이 많이 잔류함으로써 생산성이 저하될 우려가 있고, 그리고 상기에서 정한 범위보다 압력과 온도가 높거나 또는 반응시간이 길 경우에는 불록중합이 일어나 라텍스의 안정성이 나빠지고, 겔화가 될 우려가 있다. If the pressure, temperature, or reaction time is shorter than the reaction pressure, reaction temperature, and reaction time range set forth above, sufficient synthesis reaction does not occur and there is a risk that the unreacted materials remain in a large amount and productivity is lowered. When the pressure and the temperature are higher or the reaction time is longer, block polymerization occurs and the stability of the latex is deteriorated and gelation may occur.
종래의 방법이 고압반응기를 이용하여 70℃ 이상의 고온 조건에서 20시간 이상 반응시키는데 비해 본 발명에 따른 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 제조방법은 0.1-0.3 기압의 압력과 45±5℃의 저온에서 반응을 실시함으로써, 고압반응기를 사용하지 않음에 따라 종래의 설비에 비해 폭발 위험성이 없어 안전하고, 제조설비가 간단하여 운전하기 쉬우며, 그리고 반응시간이 6±0.5 시간에 지나지 않아 종래의 방법에 비해 생산성이 높은 것이 특징이다.The conventional method is performed for 20 hours or more at a high temperature of 70 ° C or higher using a high pressure reactor, whereas the method for preparing a synthetic rubber latex of a carboxylate acrylonitrile styrene-butadiene copolymer for semi-rigid packaging and polymer cement modification according to the present invention is 0.1 The reaction is carried out at a pressure of -0.3 atm and a low temperature of 45 + -5 deg. C, so that there is no danger of explosion compared with the conventional equipment, and the production facility is simple, Since the time is not shorter than 6 ± 0.5 hours, the productivity is higher than the conventional method.
본 발명의 합성고무라텍스의 제조방법은 가소제를 전혀 사용하지 않고, 유화제를 과다 사용하지 않고, 스틸렌 모노머의사용량을 대폭 줄이는 대신 수용성모노머인 아크릴로니트릴 모노머의 량을 증가시켜 투입하고, 메틸메타아크릴레이트, 불포화 카르복실산을 이용하여 유화중합반응시킴으로써, 화학적, 기계적,물리적 안정성이 우수할 뿐 아니라 포름알데히드가 검출되지 않고, 휘발성 유기화합물의 함량이 낮고, 중금속이 검출되지 않아서 친환경적인 특징을 갖는다.The method of producing the synthetic rubber latex of the present invention is a method in which the amount of the acrylonitrile monomer as the water soluble monomer is increased and the amount of the styrene monomer is increased without using any plasticizer and no excessive use of the emulsifier, Rate and unsaturated carboxylic acid, it is excellent in chemical, mechanical and physical stability, and is free from formaldehyde, low in volatile organic compounds, and free from heavy metals, thus being eco-friendly .
본 발명의 제조방법에 의해 합성고무라텍스는 예를 들어, 수용액 상에 현탁된 합성라텍스 입자의 시드(seed)에 디비닐벤젠과 같은 가교제를 넣어 가교 구조를 갖게 하고, 스틸렌 모노머대신 아크릴로니트릴 모노머로 대체하고, 시드(seed)의 껍질부는 메틸메타아크릴레이트, 메타크릴산, 이타코닉산, 퓨마릭산과 같은 불포화카르복실산을 결합시켜 합성라텍스의 유동성, 접착성, 방수성, 내구성 등과 같은 물성을 향상시킴과 동시에 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성을 향상시킨 것을 특징으로 한다.The synthetic rubber latex according to the present invention can be obtained, for example, by adding a crosslinking agent such as divinylbenzene to a seed of a synthetic latex suspended in an aqueous solution to have a crosslinking structure, and to use an acrylonitrile monomer And the shell of the seed is bonded with an unsaturated carboxylic acid such as methyl methacrylate, methacrylic acid, itaconic acid or fumaric acid to improve physical properties such as fluidity, adhesiveness, water resistance and durability of the synthetic latex And at the same time, has improved oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance.
본 발명은 또한,The present invention also relates to
본 발명의 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 전체 콘크리트 조성물 총 중량에 대하여 10~30 중량%로 포함하는 것을 특징으로 하는 개질 콘크리트 조성물에 관한 것이다.The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex of the present invention is contained in an amount of 10 to 30% by weight based on the total weight of the entire concrete composition .
상기 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 첨가에 의해 본 발명의 개질 콘크리트 조성물은 보통 콘크리트 조성물의 물성에 비해 혼화성, 접착성, 강도, 방수성, 내구성 등과 같은 제반 물성이 향상되고 특히 내유성, 내열성, 내한성, 내화학성, 내마모성, 내오존성이 우수해진다. The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene-butadiene copolymer The addition of the synthetic rubber latex allows the modified concrete composition of the present invention to have improved compatibility, adhesion, strength, water resistance, Durability and the like, and particularly excellent in oil resistance, heat resistance, cold resistance, chemical resistance, abrasion resistance and ozone resistance.
상기 개질 콘크리트 조성물은 시멘트 결합재 100 중량부; C12A7 10~30 중량부; 잔골재 150~250 중량부; 물 10 중량부; 및 실시예 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 29~154 중량부;를 포함할 수 있다.The modified concrete composition comprises 100 parts by weight of a cement binder; 10 to 30 parts by weight of C12A7; 150 to 250 parts by weight of fine aggregate; 10 parts by weight of water; And Examples Carbonate for semi-rigid packaging and polymer cement modification Acrylonitrile styrene butadiene copolymer 29 to 154 parts by weight of a synthetic rubber latex.
상기 개질 콘크리트 조성물의 추가 성분으로는 이분야에 공지된 성분이 제한 없이 사용될 수 있다. As the additional components of the modified concrete composition, components known in this field can be used without limitation.
상기 개질 콘크리트 조성물에는 하기 화학식 1로 표시되는 화합물이 1~5 중량% 더 포함될 수 있다. 상기 화학식 1의 화합물은 우레탄 골격의 양말단에 3개씩의 비닐기를 도입한 구조를 갖는다. 하기 화학식 1의 화합물은 상기와 같은 구조적 특성으로 인해 아크릴수지, 실록산수지, 라텍스 등의 유기성분뿐만 아니라, 시멘트, 골재 등의 무기성분과도 강하게 결합하여 3차원적 망상구조를 형성하므로 개질 콘크리트 조성물의 강도 및 내구성을 크게 향상시킨다. The modified concrete composition may further contain 1 to 5% by weight of a compound represented by the following formula (1). The compound of formula (1) has a structure in which three vinyl groups are introduced at both ends of the urethane skeleton. Due to the above-mentioned structural characteristics, the compound of the following formula 1 strongly bonds with not only organic components such as acrylic resin, siloxane resin and latex but also inorganic components such as cement and aggregate to form a three-dimensional network structure. Thereby significantly improving the strength and durability.
[화학식 1][Chemical Formula 1]
상기 식에서 n은 1~10의 자연수이다.In the above formula, n is a natural number of 1 to 10.
상기 개질 콘크리트 조성물에는 염해를 방지하기 위해 하기 화학식 2 및 화학식 3으로 표시되는 화합물 중에서 선택되는 1종 이상의 화합물이 1~3 중량% 더 포함될 수 있다:The modified concrete composition may further contain 1 to 3% by weight of at least one compound selected from compounds represented by the following general formulas (2) and (3)
[화학식 2](2)
[화학식 3](3)
염화물에 의한 콘크리트의 열화는 염화물이 시멘트 수화생성물인 Ca(OH)2와 반응하여 CaO·CaCl2·2H2O및 Mg2(OH)3Cl·4H2O와 같은 결정물들을 생성하여 용적을 팽창시키며, 일부는 외부로 용출됨에 따른 공극증가로 인하여 이루어진다. 그러나 이러한 화학 작용에 의한 콘크리트 자체의 열화보다도 염화물이온(Cl-)이 콘크리트 내부로 침투하여 나타나는 열화가 더 크다.The deterioration of concrete caused by chloride reacts with Ca (OH) 2, which is a cement hydration product, to produce crystals such as CaO · CaCl 2 · 2H 2 O and Mg 2 (OH) 3 Cl · 4H 2 O, This is because of the increase in porosity as the elution occurs. However, deterioration of chloride ion (Cl-) penetration into concrete is greater than deterioration of concrete itself due to such chemical action.
상기 화학식 2 또는 화학식 3의 화합물은 Cl-이온과 반응하여 Cl-이온을 고정함으로써 Cl-이온이 콘크리트 구조물로 침입하는 것을 방지한다.The compound of formula (2) or (3) reacts with Cl - ions to fix Cl - ions, thereby preventing Cl - ions from entering the concrete structure.
특히, 상기 화학식 2 또는 화학식 3의 화합물은 유기 성분과 무기 성분(Si 등)을 모두 포함함으로써 콘크리트 조성물 내에 견고하고, 안정하고, 균일하게 혼합될 수 있으므로 더욱 바람직한 효과를 나타낸다. In particular, the compound of formula (2) or (3) may contain both an organic component and an inorganic component (Si or the like), thereby exhibiting a more preferable effect because it can be firmly, stably and uniformly mixed in the concrete composition.
이하에서, 실시예를 통하여 본 발명을 보다 상세히 설명한다. 그러나, 하기의 실시예는 본 발명을 더욱 구체적으로 설명하기 위한 것으로서, 본 발명의 범위가 하기의 실시예에 의하여 한정되는 것은 아니다. 하기의 실시예는 본 발명의 범위 내에서 당업자에 의해 적절히 수정, 변경될 수 있다. Hereinafter, the present invention will be described in more detail by way of examples. However, the following examples are intended to further illustrate the present invention, and the scope of the present invention is not limited by the following examples. The following examples can be appropriately modified and changed by those skilled in the art within the scope of the present invention.
제조예 1: 시드(seed)의 합성Production Example 1 Synthesis of Seed
고압반응기에 이온수 165 중량부에 부타디엔 단량체 90 중량부, 스티렌 단량체 10.0 중량부; 유화제인 소디움도데실벤젠설포네이트 1.5 중량부와 포타슘하이드록사이드 0.7 중량부; 분자량 조절제인 n-도데실메르캅탄 0.5 중량부; 안정제인 노닐페닐에테르설폰산염 0.3 중량부를 일괄투입하여 40℃에서 1시간 정도 교반한 다음 섞이게 한 후 소듐바이설페이트(sodium bisulfate) 0.2 중량부를 투입하여 50℃로 승온시켜 2시간 반응 시켜서 시드라텍스 입자를 제조하였다. 합성된 시드(seed)는 입자경은 1,000 Å, 고형분의 함량 38 중량%, 겔 함량이 70 중량%이었다.To 165 parts by weight of ionized water, 90 parts by weight of a butadiene monomer, 10.0 parts by weight of a styrene monomer, 1.5 parts by weight of an emulsifier sodium dodecylbenzenesulfonate and 0.7 parts by weight of potassium hydroxide; 0.5 part by weight of n-dodecyl mercaptan as a molecular weight regulator; And 0.3 part by weight of nonylphenyl ether sulfonate, which is a stabilizer, were added to the mixture at 40 ° C. for about 1 hour. Then, 0.2 part by weight of sodium bisulfate was added to the mixture and the mixture was heated to 50 ° C. for 2 hours to prepare seed latex particles . The synthesized seed had a particle diameter of 1,000 Å, a solid content of 38% by weight, and a gel content of 70% by weight.
제조예 2: 화학식 1로 표시되는 화합물의 제조Production Example 2: Preparation of a compound represented by the formula (1)
3구 반응기에 기계식 교반기, 온도센서, 온도센서와 연결되어있는 가열 장치에 Kopex-PEG-400 (한농화성) 112.6g, 디부틸 틴 라우레이트 0.1g를 투입하고 상온에서 교반했다. 헥사메틸렌디이소시아네이트(HMDI) 64.9g를 넣고 반응시켰다. 상기 반응액에 펜타에리스리톨트리아크릴레이트(Sigma-Aldrich 사 제조, CAS Number 3524-68-3) 322.1g, 0.2g의 메톡시하이드로큐논을 투입하고 반응온도 75℃로 유지하고 3시간 반응시켰다. 적외선 스펙트럼의 이소시아네이트의 특성피크인 2260cm-1가 완전히 소멸된 시점에 반응이 완료된 것으로 판단하였다. 상기 반응이 종료된 후, 3-트리메톡시실릴프로필글리시딜 에테르 224g을 넣고 1시간 동안 교반하면서 3-트리메톡시실릴프로필글리시딜 에테르의 에폭시기와 우레탄 구조에 포함된 아민기 간의 반응을 진행시켜서 목적화합물을 제조하였다.In a three-necked reactor, Kopex-PEG-400 (concentrate) 112.6 g and dibutyltinlaurate 0.1 g were added to a heating device connected to a mechanical stirrer, a temperature sensor and a temperature sensor, and stirred at room temperature. And 64.9 g of hexamethylene diisocyanate (HMDI) were placed and reacted. 322.1 g of pentaerythritol triacrylate (CAS Number 3524-68-3, manufactured by Sigma-Aldrich) and 0.2 g of methoxyhydroquinone were added to the reaction solution, and the reaction temperature was maintained at 75 캜 for 3 hours. It was judged that the reaction was completed when the characteristic peak of isocyanate of 2260 cm -1 in the infrared spectrum completely disappeared. After the completion of the reaction, 224 g of 3-trimethoxysilylpropyl glycidyl ether was added and the reaction between the epoxy group of 3-trimethoxysilylpropyl glycidyl ether and the amine group contained in the urethane structure was carried out with stirring for 1 hour To proceed the desired compound.
[화학식 1][Chemical Formula 1]
상기 식에서 n은 6이다.In the above formula, n is 6.
실시예Example 1: One: 반강성포장Semi-rigid packaging 및 And 폴리머Polymer 시멘트 cement 개질용For reforming 카르복실레이트Carboxylate 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 합성 Synthesis of acrylonitrile styrene butadiene copolymer synthetic rubber latex
상기 제조예 1의 고압반응기에서 합성시킨 시드(seed) 라텍스 15 중량부에 폴리부타디엔 라텍스 30 중량부, 아크릴로니트릴 단량체 50 중량부, 스티렌 단량체 10 중량부, 아크릴산 2 중량부, 메타크릴산 1 중량부, 퓨마릭산 1중량부, 및 이타콘산 1 중량부, 메틸메타아크릴레이트 5 중량부, 유화제로서 소디움도데실벤젠설포네 7 중량부, 반응개시제로는 벤조일퍼옥사이드 3 중량부, 분자량 조절제로서 n-도데실메르캅탄 1 중량부, 가교제로 디비닐벤젠 1 중량부를 반응기에 투입한 다음, 0.3 기압, 45℃에서 6시간 동안 유화중합 및 그라프트 반응시켰다. 반응이 완료된 후, 고형분이 50±2 중량%, pH 10.5±0.5, 점도 80 cps, 입자경 1500~1800Å, 미반응 모노머 100 ppm 이하의 콘크리트 교면포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 얻었다.30 parts by weight of polybutadiene latex, 50 parts by weight of acrylonitrile monomer, 10 parts by weight of styrene monomer, 2 parts by weight of acrylic acid, and 1 part by weight of methacrylic acid were added to 15 parts by weight of seed latex synthesized in the high- 1 part by weight of fumaric acid, 1 part by weight of itaconic acid, 5 parts by weight of methyl methacrylate, 7 parts by weight of sodium dodecylbenzene sulfone as an emulsifier, 3 parts by weight of benzoyl peroxide as a reaction initiator, n 1 part by weight of dodecylmercaptan and 1 part by weight of divinylbenzene as a crosslinking agent were charged in the reactor and subjected to emulsion polymerization and grafting reaction at 0.3 atm and 45 ° C for 6 hours. After completion of the reaction, a concrete cross-linked pavement having a solid content of 50 ± 2 wt%, a pH of 10.5 ± 0.5, a viscosity of 80 cps, a particle diameter of 1500 to 1800 Å, an unreacted monomer of 100 ppm or less, and a carboxylate acrylonitrile styrene butadiene A copolymer rubber latex was obtained.
실시예Example 2 내지 4: 2 to 4: 반강성포장Semi-rigid packaging 및 And 폴리머Polymer 시멘트 cement 개질용For reforming 카르복실레이트Carboxylate 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스의 합성 Synthesis of acrylonitrile styrene butadiene copolymer synthetic rubber latex
상기 실시예 1에서 폴리부타디엔 라텍스, 아크릴로니트릴 단량체, 스티렌 단량체의 함량을 하기 표 1에 기재된 함량으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스를 합성하였다.In the same manner as in Example 1 except that the content of polybutadiene latex, acrylonitrile monomer and styrene monomer in Example 1 was changed to the content shown in the following Table 1, the semi-rigid packaging and the polymer cement- Late acrylonitrile styrene butadiene copolymer Synthetic rubber latex was synthesized.
비교예Comparative Example 1: One: 반강성포장Semi-rigid packaging 및 And 폴리머Polymer 시멘트 cement 개질용For reforming 카르복실레이트Carboxylate 스티렌 부타디엔 Styrene butadiene 공중합물Copolymer 합성고무라텍스의 합성 Synthesis of synthetic rubber latex
상기 1의 고압반응기에서 합성시킨 시드(seed) 라텍스 15 중량부에 부타디엔 단량체 35 중량부, 스티렌 단량체 55 중량부, 아크릴산 단량체 5 중량부, 메틸메타아크릴레이트 5 중량부, 터셔리도데실머캅탄 0.9 중량부, 로진염 0.7 중량부, 폴리옥시에틸렌알킬에테르계 비이온 염 4.5 중량부를 투입한 다음, 55℃에서 개시하여 초기 반응이 완료되는 2시간 후에 55℃에서 60℃로 승온시켜 6시간 반응시킨 다음 65℃에서 12시간 반응시킨 후 70℃로 활성화시켜 반응을 종료하고,라텍스 고형분이 낮아(43.1%) 농축 및 증류하였다.To 15 parts by weight of seed latex synthesized in the above 1 high pressure reactor were added 35 parts by weight of butadiene monomer, 55 parts by weight of styrene monomer, 5 parts by weight of acrylic acid monomer, 5 parts by weight of methyl methacrylate, 0.9 by weight of tertiary dodecylmercaptan , 0.7 part by weight of rosin salt and 4.5 parts by weight of polyoxyethylene alkyl ether nonionic salt were charged and then heated at 55 ° C. and elevated to 60 ° C. for 2 hours after the completion of the initial reaction at 55 ° C. for 6 hours After reacting at 65 ° C for 12 hours, the reaction was terminated by activation at 70 ° C, and the latex solid was low (43.1%) and concentrated and distilled.
시험예 1: 합성고무라텍스의 기본물성 및 라텍스 필름물성 평가Test Example 1: Evaluation of basic physical properties and latex film properties of synthetic rubber latex
상기 실시예 1 내지 4의 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스와 및 비교예 1의 카르복실레이트 스틸렌 부타디엔 합성고무라텍스의 기본물성 및 라텍스 필름물성을 측정하고, 그 결과를 하기 표 1에 나타내었다.The basic properties and latex film properties of the semi-rigid packaging and polymer cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex of Examples 1 to 4 and the carboxylate styrene butadiene synthetic rubber latex of Comparative Example 1 And the results are shown in Table 1 below.
표 1에 나타낸 각 항목의 특성은 라텍스 혼합개질 콘크리트, 시멘트 몰탈 조성물, 방수제의 물성에 중요한 인자이다. 그 특성을 설명하면 다음과 같다.Properties of each item shown in Table 1 are important factors in the physical properties of latex mixed modified concrete, cement mortar composition and waterproofing agent. The characteristics are as follows.
1.부타디엔 함유량1. Butadiene content
카르복실레이트 아크릴로니트릴 스티렌 부타디엔의 총 중량에 대한 부타디엔 중량비는 라텍스혼합 개질콘크리트, 시멘트 몰탈 조성물, 방수제의 휨, 부착강도, 탄성, 균열저항성 등의 영향을 미치는 인자이다. 부타디엔 함유량이 높으면 인장력과 신율 탄성은 우수하고 휨강도가 낮아지고, 낮으면 압축강도가 높아지고, 취성적인 성질이 나타낸다.Carboxylate The weight ratio of butadiene to the total weight of acrylonitrile styrene butadiene is a factor affecting the flexure, adhesion strength, elasticity, crack resistance, etc. of latex mixed modified concrete, cement mortar composition and waterproofing agent. If the butadiene content is high, the tensile strength and elongation elasticity are excellent and the flexural strength is low, and when the butadiene content is low, the compressive strength is high and brittle properties are exhibited.
2, 전 고형분 함유량2, the total solid content
라텍스 총 중량에 대한 고형분의 중량으로서 라덱스의 점도에 영향을 미치고 라텍스혼합 개질콘크리트, 시멘트 몰탈 조성물, 방수제의 부착력, 휨, 인장강도, 투수성, 방수성, 내구성 등에 영향을 미치는 주요인자이다. 고형분 함유량이 많을수록 라텍스의 점도는 증가하게 되고, 허용 고형분보다 적을 경우 라텍스혼합 개질콘크리트, 시멘트 몰탈 조성물, 방수제의 성능이 급격히 저하된다. 따라서 시멘트 폴리머 비율을 15-20%, 고형분은 45-50%가 가장 적절하다.It is a weight of solid content with respect to the total weight of latex and affects the viscosity of the latex and is a main factor affecting the adhesion, bending, tensile strength, permeability, water resistance and durability of latex mixed modified concrete, cement mortar composition and waterproofing agent. The higher the solids content, the greater the viscosity of the latex. If the solids content is less than the permissible solids content, the performance of the latex mixed modified concrete, cement mortar composition and waterproofing agent is drastically reduced. Therefore, the ratio of cement polymer is 15-20% and the solid content is 45-50%.
3. pH3. pH
pH 8-10이 가장 적절하다. 그 이유는 카르복실기와 pH 조정제의 금속이온 칼륨, 나트륨이온과 에스테르반응으로 라텍스 점도가 급상승하여 시멘트와 라텍스간의 혼화력 분산력이 저하되어 강도 및 제반 물성이 떨어진다. pH 8-10 is the most appropriate. The reason is that latex viscosity increases sharply due to ester reaction with potassium ion and sodium ion of carboxyl group and metal ion of pH adjuster, resulting in poor mixing power dissipation between cement and latex, resulting in poor strength and various physical properties.
4.점도4. Viscosity
점도가 높으면 모빌믹서의 교반시간이 짧아 시멘트와 라텍스의 혼화력이 급격히 저하되어 개질콘크리트의 제반물성이 떨어지고 모빌믹서의 라텍스 이송라인이 적어 이송펌프에 부하가 걸려 정량투입이 어렵다. 따라서 점도는 100cps 이하가 적정하다.When the viscosity is high, the mixing time of the mobile mixer is short, and the mixing power of the cement and latex rapidly decreases. Therefore, the physical properties of the modified concrete deteriorate and the latex transfer line of the mobile mixer is low. Therefore, it is appropriate that the viscosity is 100 cps or less.
5.표면장력5. Surface tension
표면장력이 높으면 시멘트와 라텍스의 혼화 분산성이 떨어지고 개질콘크리트 및 시멘트 몰탈 조성물의 제반물성을 저하되고, 낮으면 분산력 혼화성이 좋아져서 유동성 가사시간이 좋아지고 개질콘크리트 및 시멘트 몰탈 조성물의 제반물성이 향상된다. 따라서 40 이하가 적정하다.When the surface tension is high, the miscible dispersibility of the cement and latex is lowered, and the physical properties of the modified concrete and the cement mortar composition are lowered. When the surface tension is low, the dispersibility of the modified concrete and the cement mortar composition is lowered. . Therefore, 40 or less is appropriate.
6.입자경6. Drop Diameter
입자경은 작으면 시멘트입자에 흡착이 많아 접착력 휨강도 방수성능이 우수하고, 크면 분포도가 적어 개질콘크리트 및 시멘트 몰탈 조성물 제반성능을 저하시키고, 라텍스의 저장 안정성이 떨어진다. 따라서 1300-1800Å이 가장 적절하다.When the particle size is small, the cement particles adsorb much, and the adhesive strength and bending strength are excellent in waterproof performance. When the particle size is small, the distribution performance of the modified concrete and cement mortar composition is decreased and the storage stability of the latex is deteriorated. Therefore, 1300-1800 Å is most appropriate.
7.응고량7. Coagulation amount
응고량이 높으면 라텍스의 물리적 화학적 안정성이 떨어져서 개질 콘크리트 및 시멘트 몰탈 조성물의물성을 저하시키고, 모빌믹서의 여과기 막힘현상으로 라텍스의 정량투입이 어렵고 제반물성을 저하시킨다. 따라서 응고량은 0.1%이하가 적정하다.If the coagulation amount is high, the physical and chemical stability of the latex deteriorates, which deteriorates the physical properties of the modified concrete and cement mortar composition, and the clogging of the filter of the mobile mixer is difficult to quantitatively inject latex and deteriorate various physical properties. Therefore, the amount of solidification should be 0.1% or less.
실시예 5: 개질 콘크리트 조성물 제조Example 5: Preparation of modified concrete composition
보통 포틀랜드 시멘트 60중량%, 바텀애쉬(bottom ash) 35중량%, 플라이애쉬 5중량%를 포함한 시멘트 결합재 100 중량부; C12A7 20 중량부; 잔골재 200 중량부;를 강제믹서에서 교반시킨 후, 물 10 중량부; 및 실시예 1에서 제조된 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 60 중량부;를 추가로 혼입하고 3분 동안 교반하여 개질 콘크리트 조성물을 제조하였다.100 parts by weight of a cement binder including 60% by weight of Portland cement, 35% by weight of bottom ash, and 5% by weight of fly ash; 20 parts by weight of C12A7; 200 parts by weight of fine aggregate was stirred in a forced mixer, 10 parts by weight of water, And 60 parts by weight of the semi-rigid packaging and polymer cement modifying carboxylate acrylonitrile styrene butadiene copolymer synthetic rubber latex prepared in Example 1 were further mixed and stirred for 3 minutes to prepare a modified concrete composition.
실시예 6: 개질 콘크리트 조성물 제조Example 6: Preparation of modified concrete composition
보통 포틀랜드 시멘트 60중량%, 바텀애쉬(bottom ash) 35중량% 및 플라이애쉬 5중량%를 포함한 시멘트 결합재 100 중량부; C12A7 20 중량부; 및 잔골재 200 중량부;를 강제믹서에서 교반시킨 후, 물 10 중량부; 실시예 1에서 제조된 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 60 중량부; 및 제조예 2에서 제조된 화학식 1의 화합물 5 중량부를 추가로 혼입하고 3분 동안 교반하여 개질 콘크리트 조성물을 제조하였다.100 parts by weight of a cementitious binder comprising 60% by weight of Portland cement, 35% by weight of bottom ash and 5% by weight of fly ash; 20 parts by weight of C12A7; And fine aggregate 200 parts by weight were stirred in a forced mixer, and then 10 parts by weight of water; The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer prepared in Example 1 60 parts by weight of synthetic rubber latex; And 5 parts by weight of the compound of Formula 1 prepared in Preparation Example 2 were further mixed and stirred for 3 minutes to prepare a modified concrete composition.
실시예 7: 개질 콘크리트 조성물 제조Example 7: Preparation of modified concrete composition
보통 포틀랜드 시멘트 60중량%, 바텀애쉬(bottom ash) 35중량% 및 플라이애쉬 5중량%를 포함한 시멘트 결합재 100 중량부; C12A7 20 중량부; 및 잔골재 200 중량부;를 강제믹서에서 교반시킨 후, 물 10 중량부; 실시예 1에서 제조된 반강성포장 및 폴리머 시멘트 개질용 카르복실레이트 아크릴로니트릴 스티렌 부타디엔 공중합물 합성고무라텍스 60중량부; 제조예 2에서 제조된 화학식 1의 화합물 5 중량부; 및 하기 화학식 2의 화합물 3 중량부를 혼입하고 3분 동안 교반하여 개질 콘크리트 조성물을 제조하였다.100 parts by weight of a cementitious binder comprising 60% by weight of Portland cement, 35% by weight of bottom ash and 5% by weight of fly ash; 20 parts by weight of C12A7; And fine aggregate 200 parts by weight were stirred in a forced mixer, and then 10 parts by weight of water; The semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene butadiene copolymer prepared in Example 1 60 parts by weight of synthetic rubber latex; 5 parts by weight of the compound of formula (I) prepared in Preparation Example 2; And 3 parts by weight of a compound represented by the following formula (2) were mixed and stirred for 3 minutes to prepare a modified concrete composition.
[화학식 2] (2)
시험예 2: 개질 콘크리트 조성물의 물성 평가Test Example 2: Property Evaluation of Modified Concrete Composition
상기에서 제조된 실시예 5 내지 7의 개질 콘크리트 조성물을 KS F 2405(모르타르의 압축강도 시험방법)에 의한 압축강도 시험을 수행하였고, 그 결과를 하기 표 2에 나타내었다. 또한, KS F 2408(모르타르의 휨강도 시험방법)에 의하여 휨강도 시험을 수행하였고, KS F 2423(모르타르의 인장강도 시험방법)에 의하여 인장강도 시험을 수행하였으며, JIS A 6916 (마무리 도장재용 바탕 조정재)에 의하여 공시체의 접착강도를 측정하여 각각의 결과를 하기 표 2에 나타내었다.The modified concrete compositions of Examples 5 to 7 prepared above were subjected to a compressive strength test by KS F 2405 (Mortar's compressive strength test method), and the results are shown in Table 2 below. Bending strength test was carried out by KS F 2408 (Bending strength test method of mortar), Tensile strength test was conducted by KS F 2423 (Tensile strength test method of mortar), JIS A 6916 (Tension adjustment material for finishing paint) The results are shown in Table 2 below.
(kgf/㎠)burglar
(kgf / cm2)
시험예 3: 개질 콘크리트 조성물의 염해방지성능 평가Test Example 3: Evaluation of the prevention of salt corrosion of the modified concrete composition
염소이온 침투 저항성을 시험하기 위해 상기 실시예 5 및 7에서 제조된 콘크리트를 5cm두께로 포설한 후 재령 28일이 된 것을 시험편으로 하여 시험을 실시하였다. To test the chloride ion penetration resistance, the concrete prepared in Examples 5 and 7 was installed at a thickness of 5 cm, and then the test pieces were tested at 28 days old.
상기 시험편으로 확산셀을 구성하여 60V의 직류전원을 6시간동안 통전한 조건에서 매 30분마다 측정한 전류를 시간에 대해 적분하여 구한통과전하량을구하여 하기 표 3에 나타내었다. The diffusion cell was constructed with the above test piece, and the current measured every 30 minutes under the condition that a direct current power of 60 V was applied for 6 hours was integrated with respect to time.
Claims (9)
상기 불포화 카르복실산 단량체는 아크릴산, 메타크릴산, 퓨마릭산, 및 이타콘산으로 이루어진 군으로부터 선택되는 1종 이상의 것이며,
상기 아크릴레이트 단량체는 메틸메타크릴레이트, 메틸아크릴레이트, 에틸아크릴레이트, 부틸아크릴레이트, 2-에틸헥실아크릴레이트, 라우릴메타크릴레이트, 하이드록시 알킬 아크릴레이트, 및 글리시딜 메타아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상의 것이며,
하기 화학식 1로 표시되는 화합물을 1~5 중량% 더 포함하는 것을 특징으로 하는 개질 콘크리트 조성물:
[화학식 1]
상기 식에서 n은 1~10의 자연수이다.10 to 20 parts by weight of a seed latex, 30 to 40 parts by weight of a polybutadiene latex, 20 to 50 parts by weight of an acrylonitrile monomer, 10 to 30 parts by weight of a styrene monomer, 2 to 8 parts by weight of an unsaturated carboxylic acid monomer, 2 to 8 parts by weight of an unsaturated monomer, 3 to 8 parts by weight of an emulsifier, 2 to 5 parts by weight of a reaction initiator and 1 to 15 parts by weight of an additive are fed into a reactor at a total pressure of 0.2 to 0.5 atm, A semi-rigid packaging and polymeric cement modifying carboxylate acrylonitrile styrene-butadiene copolymer prepared by emulsion polymerization and grafting reaction for 8 hours is contained in an amount of 10 to 30% by weight based on the total weight of the entire concrete composition In addition,
The unsaturated carboxylic acid monomer is at least one selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, and itaconic acid,
Wherein the acrylate monomer is selected from the group consisting of methyl methacrylate, methyl acrylate, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, lauryl methacrylate, hydroxyalkyl acrylate, and glycidyl methacrylate. And at least one selected from the group consisting of
1. A modified concrete composition comprising 1 to 5% by weight of a compound represented by the following formula (1)
[Chemical Formula 1]
In the above formula, n is a natural number of 1 to 10.
시드(seed) 라텍스는 부타디엔 단량체 및 스티렌 단량체를 6~9.5 : 0.5~4 중량부로 포함하는 유화중합체인 것을 특징으로 하는 개질 콘크리트 조성물.The method according to claim 1,
Wherein the seed latex is an emulsion polymer comprising 6 to 9.5: 0.5 to 4 parts by weight of a butadiene monomer and a styrene monomer.
상기 첨가제는 안정제, 분자량조절제, 및 가교제 중에서 선택되는 1종 이상의 것임을 특징으로 하는 개질 콘크리트 조성물.The method according to claim 1,
Wherein the additive is at least one selected from a stabilizer, a molecular weight modifier, and a crosslinking agent.
염해를 방지하기 위해 하기 화학식 2 및 화학식 3으로 표시되는 화합물 중에서 선택되는 1종 이상을 1~3 중량% 더 포함하는 것을 특징으로 하는 개질 콘크리트 조성물:
[화학식2]
[화학식 3]
The method according to claim 1,
And 1 to 3% by weight of at least one compound selected from the group consisting of compounds represented by the following formulas (2) and (3) to prevent salt corrosion:
(2)
(3)