KR101817385B1 - UV-curable ink composition for inkjetting having improved adhesiveness - Google Patents
UV-curable ink composition for inkjetting having improved adhesiveness Download PDFInfo
- Publication number
- KR101817385B1 KR101817385B1 KR1020140071574A KR20140071574A KR101817385B1 KR 101817385 B1 KR101817385 B1 KR 101817385B1 KR 1020140071574 A KR1020140071574 A KR 1020140071574A KR 20140071574 A KR20140071574 A KR 20140071574A KR 101817385 B1 KR101817385 B1 KR 101817385B1
- Authority
- KR
- South Korea
- Prior art keywords
- ink composition
- inkjet
- curable ink
- total weight
- weight
- Prior art date
Abstract
본 발명은 안료 분산액, 부착력 증진제로서 잉크 조성물의 총 중량에 대하여 7 ~ 20 중량%의 히드록시알킬 (메트)아크릴레이트, 바인더 용액, 다관능 모노머 및 광개시제를 포함하는 잉크젯용 자외선 경화형 잉크 조성물에 관한 것이다. 본 발명에 따른 잉크 조성물은 제팅 성능이 우수하고, 표면경도 및 부착성이 개선되어 터치패널 베젤을 형성하기 위한 자외선 경화형 방식의 잉크젯용 잉크 조성물로 적합하다. The present invention relates to a pigment dispersion, an ultraviolet curable ink composition for inkjet comprising a hydroxyalkyl (meth) acrylate, a binder solution, a polyfunctional monomer and a photoinitiator in an amount of 7 to 20% by weight based on the total weight of the ink composition as an adhesion promoting agent will be. The ink composition according to the present invention is excellent in jetting performance, improved in surface hardness and adhesion, and is suitable as an inkjet ink composition for ultraviolet curing type for forming a touch panel bezel.
Description
본 발명은 부착력이 개선된 잉크젯용 자외선 경화형 잉크 조성물, 보다 상세하게는 잉크젯 프린팅 기술을 이용해 터치패널 베젤(테두리부)을 형성하기 위한 부착력이 개선된 잉크젯용 자외선 경화형 잉크 조성물에 관한 것이다.The present invention relates to an ultraviolet ray curable ink composition for inkjet with improved adhesion, and more particularly to an ultraviolet (UV) curable ink composition for inkjet which has improved adhesion for forming a touch panel bezel (rim portion) using an inkjet printing technique.
터치패널 베젤(테두리부) 형성 공정은 기존에는 대부분 스크린 프린팅(screen printing) 방식으로 진행되어 왔으며 일정수준의 광학밀도를 나타내기 위해서는 10㎛ 수준의 두께로 베젤이 형성되어야 했다. 그러나 이러한 두께로 베젤이 형성된 기판 위에 전극을 형성하면, 베젤과 기판의 경계면에서 단선의 발생이 일어나는 문제점이 있었다. 이러한 문제를 해결하기 위해서 낮은 두께(2㎛수준)에서도 일정수준의 광학밀도(O.D. 5)를 나타내고, 표면경도 5H 이상, 부착력 5B의 성능을 나타내는 베젤의 형성 방법이 요구되고 있다.The process of forming the touch panel bezel (edge portion) has conventionally been performed by screen printing method. In order to achieve a certain level of optical density, a bezel has to be formed at a thickness of about 10 μm. However, when the electrode is formed on the substrate having the bezel with such a thickness, disconnection occurs at the interface between the bezel and the substrate. To solve such a problem, a method of forming a bezel that exhibits a certain optical density (OD 5) at a low thickness (2 탆 level) and exhibits a surface hardness of 5H or higher and an adhesive force of 5B is required.
또한, 현재 대부분의 베젤은 강화유리 위에 인쇄되고 있으나 여러 이유로 인해 강화유리 대신 필름이나 다양한 기재를 사용하는 시도가 이루어지고 있다. 강화유리 대신 필름이나 다양한 기재에 베젤을 인쇄하기 위해서는 기존 강화유리에 사용되었던 고온의 열 경화방식은 적용하기 어렵기 때문에 대신 자외선 경화형방식의 적용이 검토되고 있으며 이를 위한 자외선 경화형방식의 잉크의 개발이 필요하다.In addition, currently most bezels are printed on tempered glass, but attempts have been made to use films or various substrates instead of tempered glass for a variety of reasons. In order to print a bezel on a film or various substrates instead of a tempered glass, it is difficult to apply a high-temperature thermosetting method used in conventional tempered glass. Therefore, application of an ultraviolet ray curing type method has been studied instead. need.
특히 터치패널 베젤을 형성하기 위한 자외선 경화형 방식의 잉크젯용 잉크 조성물은 제팅 성능이 우수해야 하며, 표면경도 및 부착성이 개선되어야 하고 경화수축이 없어야 한다. In particular, an inkjet ink composition for ultraviolet curing type for forming a touch panel bezel should have excellent jetting performance, have improved surface hardness and adhesion, and should be free of curing shrinkage.
이와 관련하여 공개특허 10-2011-0072121에서는 에틸 아크릴레이트(Ethyl acrylate), 부틸 아크릴레이트(Butyl acrylate) 및 2-에틸헥실 아크릴레이트(2-Ethyl hexyl acrylate)로 이루어지는 군에서 선택된 1종 이상의 호모폴리머 또는 헤테로폴리머를 부착력 증진제로 사용하는 시도를 하였다. 그러나 상기 기술은 잉크젯용 잉크에 적용했을 때, 잉크 조성물의 표면경도, 부착성 등의 물성 개선효과가 미흡하였다.In this connection, in Patent Document 10-2011-0072121, at least one homopolymer selected from the group consisting of ethyl acrylate, butyl acrylate and 2-ethyl hexyl acrylate Or an attempt was made to use a heteropolymer as an adhesion promoting agent. However, when the above technology is applied to an inkjet ink, the effect of improving the physical properties such as surface hardness and adhesion of the ink composition is insufficient.
상기 종래 기술의 문제점을 해결하기 위하여, 본 발명은 터치패널 베젤(테두리부)을 형성하기 위한 표면경도 및 부착성이 개선된 잉크젯용 자외선 경화형 잉크 조성물을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art, it is an object of the present invention to provide an ink-jet ultraviolet curable ink composition having improved surface hardness and adhesion for forming a touch panel bezel (rim portion).
상기 목적을 달성하기 위하여, 본 발명은 안료 분산액, 부착력 증진제로서 잉크 조성물의 총 중량에 대하여 7 ~ 20 중량%의 히드록시알킬 (메트)아크릴레이트, 바인더 용액, 다관능 모노머 및 광개시제를 포함하는 잉크젯용 자외선 경화형 잉크 조성물을 제공한다.In order to achieve the above object, the present invention provides a pigment dispersion, an ink-jet ink comprising a 7 to 20% by weight of a hydroxyalkyl (meth) acrylate, a binder solution, a polyfunctional monomer and a photoinitiator, Based ink composition.
본 발명에 따른 잉크 조성물은 제팅 성능이 우수하고, 표면경도 및 부착성이 개선되어 터치패널 베젤을 형성하기 위한 자외선 경화형 방식의 잉크젯용 잉크 조성물로 적합하다. The ink composition according to the present invention is excellent in jetting performance, improved in surface hardness and adhesion, and is suitable as an inkjet ink composition for ultraviolet curing type for forming a touch panel bezel.
터치패널 제작시 베젤 인쇄 후에 전극을 형성하기 위한 ITO 증착 및 에칭공정을 거치게 되는데, ITO etchant(45℃, 15s)에서 에칭을 하게 되면 내화학성이 좋지 않을 경우 표면경도 및 부착력이 낮아져 표면 박리가 일어날 수 있다. 그러나, 본 발명에 따른 잉크 조성물은 다관능 모노머 및 바인더 함량을 조절함으로써 jetting이 가능하면서 베젤 형성시 우수한 내화학성을 나타낼 수 있다. When manufacturing the touch panel, ITO is deposited and etched to form an electrode after printing the bezel. When the ITO etchant (45 ° C, 15s) is etched, if the chemical resistance is poor, the surface hardness and adhesion force are lowered, . However, the ink composition according to the present invention can jetting by controlling the content of the polyfunctional monomer and the binder, and exhibits excellent chemical resistance when forming the bezel.
이하, 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.
본 발명의 잉크젯용 자외선 경화형 잉크 조성물은 안료 분산액, 부착력 증진제로서 히드록시알킬 (메트)아크릴레이트, 바인더 용액, 다관능 모노머 및 광개시제를 포함한다.The ultraviolet curable ink composition for inkjet of the present invention comprises a pigment dispersion, a hydroxyalkyl (meth) acrylate, a binder solution, a polyfunctional monomer and a photoinitiator as an adhesion promoting agent.
상기 잉크젯용 자외선 경화형 잉크 조성물은 부착력 증진제를 잉크 조성물의 총 중량에 대하여 7 ~ 20 중량% 포함하는 것을 특징으로 한다.The ultraviolet-curable ink composition for inkjet comprises 7 to 20% by weight of an adhesion-promoting agent based on the total weight of the ink composition.
상기 안료 분산액은 카본 블랙(Carbon black) 안료, 분산제 및 제1 반응성 모노머를 포함한다. The pigment dispersion comprises a carbon black pigment, a dispersant and a first reactive monomer.
상기 카본 블랙(Carbon black) 안료는 차광 특성 확보를 위해 안료 분산액에 포함된다. The carbon black pigment is included in the pigment dispersion for securing the light shielding property.
본 발명의 잉크 조성물에 포함되는 상기 카본 블랙 안료로는 당업계에 알려진 1종 이상의 안료 또는 이들의 혼합물을 사용할 수 있다.As the carbon black pigment contained in the ink composition of the present invention, one or more pigments known in the art or a mixture thereof may be used.
구체적으로, 사용 가능한 카본 블랙의 예로는 시스토 5HIISAF-HS, 시스토 KH, 시스토 3HHAF-HS, 시스토 NH, 시스토 3M, 시스토 300HAF-LS, 시스토 116HMMAF-HS, 시스토 116MAF, 시스토 FMFEF-HS, 시스토 SOFEF, 시스토VGPF, 시스토 SVHSRF-HS 및 시스토 SSRF(동해카본 ㈜); 다이어그램 블랙 II, 다이어그램 블랙 N339, 다이어그램 블랙 SH, 다이어그램 블랙 H, 다이어그램 LH, 다이어그램 HA, 다이어그램 SF, 다이어그램 N550M, 다이어그램 M, 다이어그램 E, 다이어그램 G, 다이어그램 R, 다이어그램 N760M, 다이어그램 LR, #2700, #2600, #2400, #2350, #2300, #2200, #1000, #980, #900, MCF88, #52, #50, #47, #45, #45L, #25, #CF9, #95, #3030, #3050, MA7, MA77, MA8, MA11, MA100, MA40, OIL7B, OIL9B, OIL11B, OIL30B 및 OIL31B(미쯔비시화학㈜) ; PRINTEX-U, PRINTEX-V, PRINTEX-140U, PRINTEX-140V, PRINTEX-95, PRINTEX-85, PRINTEX-75, PRINTEX-55, PRINTEX-45, PRINTEX-300, PRINTEX-35, PRINTEX-25, PRINTEX-200, PRINTEX-40, PRINTEX-30, PRINTEX-3, PRINTEX-A, SPECIAL BLACK-550, SPECIAL BLACK-350, SPECIAL BLACK-250, SPECIAL BLACK-100, 및 LAMP BLACK-101(대구사㈜); RAVEN-1100ULTRA, RAVEN-1080ULTRA, RAVEN-1060ULTRA, RAVEN-1040, RAVEN-1035, RAVEN-1020, RAVEN-1000, RAVEN-890H, RAVEN-890, RAVEN-880ULTRA, RAVEN-860ULTRA, RAVEN-850, RAVEN-820, RAVEN-790ULTRA, RAVEN-780ULTRA, RAVEN-760ULTRA, RAVEN-520, RAVEN-500, RAVEN-460, RAVEN-450, RAVEN-430ULTRA, RAVEN-420, RAVEN-410, RAVEN-2500ULTRA, RAVEN-2000, RAVEN-1500, RAVEN-1255, RAVEN-1250, RAVEN-1200, RAVEN-1190ULTRA, 및 RAVEN-1170(콜롬비아 카본㈜) 등이 있다.Examples of usable carbon blacks include cysteine 5HIISAF-HS, cysteine KH, cysteo 3HHAF-HS, cysteo NH, cysteo 3M, cysteo 300HAF-LS, cysto 116HMMAF-HS, Cysto FMFEF-HS, Cysto SOFEF, Cysto VGPF, Cysto SVHSRF-HS and Cysto SSRF (Donghae Carbon Co., Ltd.); Diagram Black II, Diagram Black N339, Diagram Black SH, Diagram Black H, Diagram LH, Diagram HA, Diagram SF, Diagram N550M, Diagram M, Diagram E Diagram G Diagram R Diagram N760M Diagram LR, # 2700, # 25, # 45, # 45, # 45, # 45, # 45, # 25, # CF9, # 95, # 20, # 2300, # 2350, # 2300, # 2200, # 1000, # 980, # 900, 3030, # 3050, MA7, MA77, MA8, MA11, MA100, MA40, OIL7B, OIL9B, OIL11B, OIL30B and OIL31B (Mitsubishi Chemical); PRINTEX-25, PRINTEX-25, PRINTEX-55, PRINTEX-55, PRINTEX-45, PRINTEX-35, PRINTEX- 200, PRINTEX-40, PRINTEX-30, PRINTEX-3, PRINTEX-A, SPECIAL BLACK-550, SPECIAL BLACK-350, SPECIAL BLACK-250, SPECIAL BLACK-100 and LAMP BLACK-101 (Daegu; 890, RAVEN-880ULTRA, RAVEN-880ULTRA, RAVEN-850R, RAVEN-1080ULTRA, RAVEN-1080ULTRA, RAVEN-1080ULTRA, RAVEN-1080ULTRA, RAVEN-1040ULTRA, RAVEN-1040, RAVEN-1035, RAVEN-1020, RAVEN- 820, RAVEN-790ULTRA, RAVEN-780ULTRA, RAVEN-760ULTRA, RAVEN-520, RAVEN-500, RAVEN-460, RAVEN-450, RAVEN-430ULTRA, RAVEN- RAVEN-1500, RAVEN-1255, RAVEN-1250, RAVEN-1200, RAVEN-1190ULTRA and RAVEN-1170 (Colombia Carbon).
상기 카본 블랙 안료는 상기 안료 분산액의 총 중량에 대하여 10 ~ 30 중량%로 포함되는 것이 바람직하다. 또한, 잉크 조성물의 총 중량에 대하여 5 ~ 40 중량%로 포함되는 것이 바람직하다. 5 중량% 미만이면 차광특성이 미흡하고, 40 중량% 초과이면 분산이 어려울 수 있다.The carbon black pigment is preferably contained in an amount of 10 to 30% by weight based on the total weight of the pigment dispersion. Further, it is preferably contained in an amount of 5 to 40% by weight based on the total weight of the ink composition. If it is less than 5% by weight, the light-shielding property is insufficient. If it is more than 40% by weight, dispersion may be difficult.
상기 분산제로는 고분자형, 비이온성, 음이온성, 또는 양이온성 분산제를 사용할 수 있으며, 그 예로는 폴리알킬렌글리콜 및 이의 에스테르, 폴리옥시알킬렌 다가알콜, 에스테르알킬렌 옥사이드 부가물, 알코올알킬렌옥사이드 부가물, 설폰산 에스테르, 설폰산염, 카르복실산에스테르, 카르복실산염, 알킬아미드알킬렌옥사이드 부가물, 또는 알킬아민 등이 있다. 이들은 단독으로 첨가하거나 2 이상 혼합하여 사용할 수 있다.As the dispersing agent, a polymer type, a nonionic, an anionic, or a cationic dispersing agent can be used. Examples thereof include polyalkylene glycols and esters thereof, polyoxyalkylene polyhydric alcohols, ester alkylene oxide adducts, Oxide adducts, sulfonic acid esters, sulfonates, carboxylic acid esters, carboxylic acid salts, alkylamide alkylene oxide adducts, or alkylamines. These may be added alone or in combination of two or more.
상기 분산제의 함량은 상기 안료 분산액의 총 중량에 대하여 2 ~ 6 중량%로 포함되는 것이 바람직하다.The content of the dispersing agent is preferably 2 to 6% by weight based on the total weight of the pigment dispersion.
상기 제1 반응성 모노머는 자외선 경화형 잉크 조성물에 일반적으로 사용되는 것을 사용할 수 있으나, 예를 들면 관능성기가 2 또는 3개인 것이 바람직하다. 본 발명에는 1,6-헥산디올 디아크릴레이트, 네오펜틸글리콜 히드록시피발레이트(neopentylglycol hydroxypivalate), 트리메틸올프로판 트리아크릴레이트(trimethylolpropane triacrylate: TMPTA), 펜타에리스리톨 트리아크릴레이트, 트리메틸렌프로판 트리아크릴레이트, 펜타에리스톨 트리아크릴레이트, 트리메틸렌 프로필 트리아크릴레이트, 프로폭시레이티드 글리세롤 트리아크릴레이트 등을 단독 또는 혼합하여 사용하는 것이 바람직하다. The first reactive monomer may be one generally used in an ultraviolet curable ink composition. For example, the first reactive monomer preferably has 2 or 3 functional groups. In the present invention, it is preferable to use a copolymer of 1,6-hexanediol diacrylate, neopentylglycol hydroxypivalate, trimethylolpropane triacrylate (TMPTA), pentaerythritol triacrylate, trimethylene propane triacrylate , Pentaerythritol triacrylate, trimethylene propyl triacrylate, propoxylated glycerol triacrylate, and the like are preferably used alone or in combination.
상기 제1 반응성 모노머의 함량은 상기 안료 분산액의 총 중량에 대하여 65 ~ 85 중량%로 포함되는 것이 바람직하다..The content of the first reactive monomer is preferably 65 to 85% by weight based on the total weight of the pigment dispersion.
상기 안료 분산액은 잉크 조성물의 총 중량에 대하여 50 ~ 65 중량%로 포함되는 것이 바람직하다. 50 중량% 미만이면 차광특성이 미흡하고, 65 중량% 초과이면 잉크의 점도가 너무 높아 잉크젯 공정의 적용이 어렵다.The pigment dispersion is preferably contained in an amount of 50 to 65% by weight based on the total weight of the ink composition. When the amount is less than 50% by weight, the light-shielding property is insufficient. When the amount is more than 65% by weight, the viscosity of the ink is too high.
본 발명의 잉크 조성물은 부착력 증진제로서 히드록시알킬 (메트)아크릴레이트를 포함한다.The ink composition of the present invention includes hydroxyalkyl (meth) acrylate as an adhesion promoting agent.
본 발명에서 "(메트)아크릴레이트"란 아크릴레이트와 메트아크릴레이트 화합물을 총체적으로 칭하는 것이다.In the present invention, "(meth) acrylate" refers collectively to acrylate and methacrylate compounds.
상기 히드록시알킬 (메트)아크릴레이트는 기재와 인쇄층의 부착력을 향상시키는 역할을 한다.The hydroxyalkyl (meth) acrylate serves to improve adhesion between the substrate and the print layer.
상기 부착력 증진제는 2-히드록시에틸 아크릴레이트(2-hydroxyethyl acrylate, 2-HEA), 히드록시프로필 아크릴레이트(hydroxypropyl acrylate, HPMA), 2-히드록시에틸 메타크릴레이트(2-hydroxyethyl methacrylate, 2-HEMA) 및 히드록시프로필 메타크릴레이트(hydroxypropyl methacrylate, HPMA)로 이루어지는 군에서 선택된 1종 이상의 모노머일 수 있다. 바람직하게는 2-히드록시에틸 아크릴레이트(2-hydroxyethyl acrylate, 2-HEA)의 모노머일 수 있다.The adhesion promoting agent may be selected from the group consisting of 2-hydroxyethyl acrylate (2-HEA), hydroxypropyl acrylate (HPMA), 2-hydroxyethyl methacrylate, 2- HEMA), and hydroxypropyl methacrylate (HPMA). Preferably, it may be a monomer of 2-hydroxyethyl acrylate (2-HEA).
상기 부착력 증진제는 잉크 조성물의 총 중량에 대하여 7~ 20 중량%, 보다 바람직하게는 10 ~ 15 중량%로 포함되는 것이 바람직하다. 7 중량% 미만이면 부착력이 부족하고 20 중량% 초과이면 다관능 모노머 및 바인더 함량이 줄어 표면경도 및 부착력이 충분하지 않을 수 있다.The adhesion-promoting agent is preferably contained in an amount of 7 to 20% by weight, more preferably 10 to 15% by weight, based on the total weight of the ink composition. If the content is less than 7% by weight, the adhesive strength is insufficient. If the content is more than 20% by weight, the content of the polyfunctional monomer and the binder may be decreased, and the surface hardness and adhesion may not be sufficient.
상기 바인더 용액은 에폭시계 수지와 제2 반응성 모노머로 구성된다.The binder solution is composed of an epoxy resin and a second reactive monomer.
상기 에폭시계 수지는 바인더 용액의 총 중량에 대하여 1 ~ 10 중량%로 포함되는 것이 바람직하다.The epoxy resin is preferably contained in an amount of 1 to 10% by weight based on the total weight of the binder solution.
상기 제2 반응성 모노머로 아크릴레이트계 모노머를 사용할 수 있다.As the second reactive monomer, an acrylate-based monomer may be used.
상기 아크릴레이트계 모노머는 아크릴레이트 뿐만 아니라 메타크릴레이트, 또는 아크릴레이트나 메타크릴레이트에 치환기가 도입된 유도체를 모두 의미한다.The acrylate-based monomer means not only acrylate but also methacrylate, or a derivative having a substituent introduced into acrylate or methacrylate.
상기 아크릴레이트계 모노머는 히드록시에틸 아크릴레이트(HEA), 히드록시에틸메타크릴레이트(HEMA), 헥산디올디아크릴레이트(HDDA), 페놀아크릴레이트(PHEA), 디프로필렌글리콜 디아크릴레이트(DPGDA), 트리프로필렌글리콜 디아크릴레이트(TPGDA) 및 에틸렌글리콜 디아크릴레이트(EGDA)로 이루어진 군으로부터 1종 이상 선택하여 단독 또는 혼합하여 사용할 수 있으나, 반드시 이에 제한되지는 않는다. The acrylate-based monomer may be at least one selected from the group consisting of hydroxyethyl acrylate (HEA), hydroxyethyl methacrylate (HEMA), hexanediol diacrylate (HDDA), phenol acrylate (PHEA), dipropylene glycol diacrylate , Tripropylene glycol diacrylate (TPGDA), and ethylene glycol diacrylate (EGDA) may be used singly or in combination, but not always limited thereto.
상기 아크릴레이트계 모노머는 바인더 용액의 총 중량에 대하여 90 ~ 99 중량%로 포함되는 것이 바람직하다.The acrylate-based monomer is preferably contained in an amount of 90 to 99% by weight based on the total weight of the binder solution.
상기 바인더 용액은 잉크 조성물의 총 중량에 대하여 5 ~ 20 중량%로 포함되는 것이 바람직하다. 바인더 용액의 함량이 5 중량% 미만이면 기재와 인쇄 층의 부착력 및 막강도가 충분하지 않고 20 중량% 초과이면 잉크의 점도가 너무 높아 잉크젯 공정이 어려울 수 있다.The binder solution is preferably contained in an amount of 5 to 20% by weight based on the total weight of the ink composition. When the content of the binder solution is less than 5% by weight, the adhesive strength and the film strength of the substrate and the print layer are insufficient, and when the content is more than 20% by weight, the viscosity of the ink is too high.
상기 다관능 모노머는 자외선 경화형을 통해 가교결합을 일으켜 인쇄 층의 막강도를 증가시키는 역할을 한다. The polyfunctional monomer is crosslinked through ultraviolet curing type to increase the film strength of the printing layer.
다관능 모노머로는 예를 들면 관능성기가 3 내지 6 이상인 것이 바람직하며, 상기 관능성기의 예로는 아크릴레이트, 카르복시기 등을 들 수 있으나 이에 한정되는 것은 아니다. As the polyfunctional monomer, for example, it is preferable that the functional group is 3 to 6 or more, and examples of the functional group include acrylate, carboxyl group and the like, but are not limited thereto.
다관능 모노머의 바람직한 예로 비스페놀 에톡실레이트 디아크릴레이트, 에톡실레이트 페놀 모노아크릴레이트, 트리프로필렌글리콜 디아크릴레이트, 트리메틸 프로판 트리아크릴레이트(TMPTA), 폴리 에틸렌글리콜 디아크릴레이트, 펜타에리스리톨 테트라아크릴레이트(PETA), 디펜타에리스리톨 헥사아크릴레이트(DPHA), 헥산디올디아크릴레이트(HDDA), 부탄디올 디아크릴레이트, 헥산디올 디아크릴레이트, 에톡실레이트 노닐페놀 아크릴레이트 및 페녹시에틸 아크릴레이트 군으로 이루어진 군에서 선택되는 1종 또는 2종 이상의 혼합물을 사용할 수 있다. 더욱 바람직하게는 트리메틸올프로판 트리아크릴레이트(TMPTA) 및 디펜타에리스리톨 헥사아크릴레이트(DPHA) 중 적어도 하나를 사용할 수 있다.Preferable examples of the polyfunctional monomer include bisphenol ethoxylate diacrylate, ethoxylate phenol monoacrylate, tripropylene glycol diacrylate, trimethylpropane triacrylate (TMPTA), polyethyleneglycol diacrylate, pentaerythritol tetraacrylate (PETA), dipentaerythritol hexaacrylate (DPHA), hexanediol diacrylate (HDDA), butanediol diacrylate, hexanediol diacrylate, ethoxylated nonylphenol acrylate, and phenoxyethyl acrylate groups Or a mixture of two or more of them may be used. More preferably, at least one of trimethylolpropane triacrylate (TMPTA) and dipentaerythritol hexaacrylate (DPHA) can be used.
상기 다관능 모노머는 잉크 조성물의 총 중량에 대하여 1 ~ 40 중량%로 포함되는 것이 바람직하다. 1 중량% 미만이면 막의 강도가 충분하지 않고 40 중량% 초과이면 잉크의 점도가 너무 높아져서 공정이 불가능할 수 있다.The multifunctional monomer is preferably contained in an amount of 1 to 40% by weight based on the total weight of the ink composition. When the content is less than 1% by weight, the strength of the film is not sufficient. If the content is more than 40% by weight, the viscosity of the ink becomes too high and the process may not be possible.
상기 광개시제는 자외선 경화형 과정에서 잉크에 함유된 불포화 이중결합을 갖는 모노머가 반응하여 고분자를 형성하는 경화 반응을 개시하는 역할을 한다.The photoinitiator has a role of initiating a curing reaction in which a monomer having an unsaturated double bond contained in the ink reacts to form a polymer in an ultraviolet curing type process.
본 발명의 일 실시예에 따르면, 상기 광 개시제의 예로는 1-히드록시-시클로헥실-페닐 케톤, 2-히드록시-2-메틸-1-페닐-1-프로판온, 2-히드록시-1-[4-(2-히드록시에톡시)페닐]-2-메틸-1-프로판온, 메틸벤조일포르메이트, α-디메톡시-α-페닐아세토페논, 2-벤조일-2-(디메틸아미노)-1-[4-(4-모포린일)페닐]-1-부타논, 2-메틸-1-[4-(메틸씨오)페닐]-2-(4-몰포린일)-1-프로판온 디페닐(2,4,6-트리메틸벤조일)-포스핀옥사이드, 또는 비스(2,4,6-트리메틸벤조일)-페닐포스핀옥사이드 등을 들 수 있으나, 반드시 이에 제한되지는 않는다. 또한 현재 시판되고 있는 상품으로는 Irgacure 184, Irgacure 500, Irgacure 651, Irgacure 369, Irgacure 907, Darocur 1173, DarocurMBF, Irgacure 819, Darocur TPO, Irgacure 907, Esacure KIP 100F 등을 들 수 있다. 이들 광 개시제는 단독으로 또는 서로 다른 2종 이상을 혼합하여 사용할 수 있다.According to one embodiment of the present invention, examples of the photoinitiator include 1-hydroxy-cyclohexyl-phenylketone, 2-hydroxy-2-methyl- Methylbenzoylformate,? -Dimethoxy-? -Phenylacetophenone, 2-benzoyl-2- (dimethylamino) -1- [4- (4-morpholinyl) phenyl] -1-butanone, 2- (2,4,6-trimethylbenzoyl) -phosphine oxide, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide, and the like, but the present invention is not limited thereto. Examples of commercially available products include Irgacure 184, Irgacure 500, Irgacure 651, Irgacure 369, Irgacure 907, Darocur 1173, Darocur MBF, Irgacure 819, Darocur TPO, Irgacure 907 and Esacure KIP 100F. These photoinitiators may be used alone or in combination of two or more.
상기 광개시제는 잉크 조성물의 총 중량에 대하여 0.1 ~ 10 중량%로 포함되는 것이 바람직하다. 광개시제의 함량이 0.1 중량% 미만이면 경화 반응이 충분하지 않고 10 중량% 초과이면 모두 용해되지 않을 수 있다.The photoinitiator is preferably contained in an amount of 0.1 to 10% by weight based on the total weight of the ink composition. When the content of the photoinitiator is less than 0.1% by weight, the curing reaction is not sufficient. If the content is more than 10% by weight, the curing reaction may not be completely dissolved.
본 발명의 잉크 조성물은 추가로 중합억제제, 계면활성제 등의 첨가제를 잔량 포함할 수 있다.The ink composition of the present invention may further contain residual amounts of additives such as a polymerization inhibitor and a surfactant.
상기 중합억제제는 잉크가 상온에서 보관하는 동안 경화반응이 일어나지 않도록 하는 역할을 한다. The polymerization inhibitor serves to prevent the curing reaction from occurring during storage of the ink at room temperature.
상기 중합억제제로는 하이드로퀴논(MEHQ), 벤조퀴논, 카테콜, 페노티아진, N-니트로소페닐히드록시아민 및 2,2,6,6-테트라메틸피페리딘-1-옥실 유리 라디칼 및 이들의 유도체로부터 선택된 1종 이상을 사용할 수 있다.Examples of the polymerization inhibitor include hydroquinone (MEHQ), benzoquinone, catechol, phenothiazine, N-nitrosophenylhydroxyamine and 2,2,6,6-tetramethylpiperidine-1-oxyl free radical and And at least one selected from these derivatives can be used.
상기 계면활성제는 잉크의 표면장력을 조절하여 제팅이 원활하게 일어나게 하며 유리 기판에서 잉크가 적절하게 퍼지도록 하는 역할을 한다.The surfactant adjusts the surface tension of the ink to smoothly perform the jetting and to cause the ink to properly spread on the glass substrate.
상기 계면활성제로는 불소계 계면활성제가 바람직하다. 상기 불소계 계면활성제의 구체적인 예로는 DIC(DaiNippon Ink & Chemicals) 사의 F-114, F-177, F-410, F-411, F-450, F-493, F-494, F-443, F-444, F-445, F-446, F-470, F-471, F-472SF, F-474, F-475, F-477, F-478, F-479, F-480SF, F-482, F-483, F-484, F-486, F-487, F-172D, MCF-350SF, TF-1025SF, TF-1117SF, TF-1026SF, TF-1128, TF-1127, TF-1129, TF-1126, TF-1130, TF-1116SF, TF-1131, TF1132, TF1027SF, TF-1441, TF-1442, TF-1752 등이 있으나, 이에만 한정되는 것은 아니다. The surfactant is preferably a fluorine-based surfactant. Specific examples of the fluorochemical surfactant include F-114, F-177, F-410, F-411, F-450, F-493, F-494, F- 444, F-445, F-446, F-470, F-471, F-472SF, F-474, F-475, F-477, F- TF-1129, TF-1129, TF-1129, TF-1127, TF-1027SF, TF- 1126, TF-1130, TF-1116SF, TF-1131, TF1132, TF1027SF, TF-1441, TF-1442 and TF-1752.
본 발명에 따른 잉크 조성물은 부착력 증진을 위해 종래 기술과 같이 butyl carbitol acetate 등의 용매를 포함하지 않고 부착력 증진제로 2-HEA를 잉크 조성물의 총 중량에 대하여 7 ~ 20 중량% 포함함으로써 부착력 뿐만 아니라 표면경도를 증진시킬 수 있다.The ink composition according to the present invention does not contain a solvent such as butyl carbitol acetate as in the prior art, and contains 2 to 7 wt.% Of 2-HEA as an adhesion promoter in an amount of 7 to 20 wt% The hardness can be improved.
본 발명에 따른 잉크젯용 자외선 경화형 잉크 조성물은 광학밀도(O.D.) 4 이상, 표면경도 5H 이상, 부착력 5B 등의 물성을 나타낼 수 있다. 따라서 본 발명의 잉크 조성물은 베젤 형성을 위한 조성물로 적합하게 사용될 수 있다.The ultraviolet curable ink composition for inkjet according to the present invention can exhibit physical properties such as an optical density (OD) of 4 or more, a surface hardness of 5H or more, and an adhesive force of 5B. Accordingly, the ink composition of the present invention can be suitably used as a composition for forming a bezel.
또한, 본 발명은 전술한 잉크젯용 자외선 경화형 잉크 조성물을 이용하여 형성된 패턴을 제공한다.Further, the present invention provides a pattern formed using the above-described ultraviolet curable ink composition for inkjet.
여기서, 패턴은 목적하는 용도에서 요구되는 형태를 갖는 것을 의미한다.Here, the pattern means that it has a form required for the intended use.
본 발명에 따른 잉크젯용 자외선 경화형 잉크 조성물의 각 성분은 본 명세서에 기재된 패턴의 제조 공정을 위하여 적용된 조건, 예컨대 건조 및/또는 경화 조건 하에서 변형될 수 있다.Each component of the inkjet UV curable ink composition according to the present invention can be modified under the conditions applied for the production process of the pattern described herein, such as drying and / or curing conditions.
또한, 본 발명에 따른 패턴은 상기 조성물의 각 성분이 상기 조건 하에서 가능한 변형이 된 상태를 포함할 수 있다.The pattern according to the present invention may also include a state in which each component of the composition has been modified as far as possible under the above conditions.
상기 패턴은 터치 패널의 베젤 패턴인 것이 바람직하다.The pattern is preferably a bezel pattern of the touch panel.
또한, 본 발명은 전술한 패턴을 포함하는 전자소자를 제공한다. 상기 전자소자는 액정표시장치, 디스플레이, 터치 패널 등일 수 있으나, 이에 한정되는 것은 아니며, 터치 패널인 것이 바람직하다. 터치 패널용 패턴은 액정표시장치용 블랙 매트릭스 패턴에 비하여 매우 단순하여 잉크젯 프린팅 공정을 통하여 쉽게 형성할 수 있기 때문이다.The present invention also provides an electronic device comprising the above-described pattern. The electronic device may be a liquid crystal display device, a display, a touch panel, or the like, but is not limited thereto, and is preferably a touch panel. This is because the pattern for the touch panel is very simple as compared with the black matrix pattern for a liquid crystal display and can be easily formed through an inkjet printing process.
본 발명에 따른 전자소자는 전술한 본 발명에 따른 패턴을 포함하는 것을 제외하고는 당기술 분야에 알려진 구성을 가질 수 있다.
The electronic device according to the present invention may have a configuration known in the art, except that it includes the pattern according to the invention described above.
이하 실시예 및 비교예를 통하여 본 발명을 더욱 상세하게 설명한다. 그러나, 이하의 실시예 및 비교예는 본 발명을 예시하기 위한 것이며, 이에 의하여 본 발명의 범위가 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, the following examples and comparative examples are provided for illustrating the present invention, and thus the scope of the present invention is not limited thereto.
<실시예 1>≪ Example 1 >
전체 잉크 조성물 총 중량에 대하여 안료분산액 60 중량%(Carbon black 20 중량%, 분산제 4 중량%, TMPTA 76 중량%), 부착력 증진제로서 2-hydroxyethyl acrylate 10 중량%, 바인더 용액(바인더 용액 총 중량에 대하여 epoxy PD7610 5 중량%, TPGDA 65 중량%, DPGDA 30 중량%) 12.5중량%, 다관능 모노머로서 DPHA 10 중량%, 광개시제로서 Irgacure 819 3 중량%, Irgacure 907 3 중량%, 및 ITX 1 중량%, 및 중합억제제(중합억제제 총 중량에 대하여 MEHQ(monomethylether hydroquinone) 10 중량% 및 Butyl Carbitol 90 중량%) 0.5 중량%를 혼합하였으며, 상기 혼합물을 5시간 동안 교반하여 자외선 경화형 잉크 조성물을 제조하였다.
(20% by weight of carbon black, 4% by weight of dispersant and 76% by weight of TMPTA), 10% by weight of 2-hydroxyethyl acrylate as an adhesion promoting agent, 10% by weight of binder solution (based on the total weight of the binder solution 10 wt% of DPHA as a polyfunctional monomer, 3 wt% of Irgacure 819 as a photoinitiator, 3 wt% of Irgacure 907, and 1 wt% of ITX as a polyfunctional monomer, and 0.5% by weight of polymerization inhibitor (10% by weight of monomethylether hydroquinone (MEHQ) and 90% by weight of butyl carbitol) based on the total weight of the polymerization inhibitor were mixed and the mixture was stirred for 5 hours to prepare an ultraviolet curable ink composition.
<실시예 2>≪ Example 2 >
전체 잉크 조성물 총 중량에 대하여 안료분산액 55 중량%(Carbon black 20 중량%, 분산제 4 중량%, TMPTA 76 중량%), 부착력 증진제로서 2-hydroxyethyl acrylate 15 중량%, 바인더 용액(바인더 용액 총 중량에 대하여 epoxy PD1700 5 중량%, TPGDA 65 중량%, DPGDA 30 중량%) 12.5중량%, 다관능 모노머로서 DPHA 10 중량%, 광개시제로서 Irgacure 819 3 중량%, Irgacure 907 3 중량%, 및 ITX 1 중량%, 및 반응억제제(반응억제제 총 중량에 대하여 MEHQ(monomethylether hydroquinone) 10 중량%, Butyl Carbitol 90 중량%) 0.5 중량%를 혼합하였으며, 상기 혼합물을 5시간 동안 교반하여 자외선 경화형 잉크 조성물을 제조하였다.(20% by weight of carbon black, 4% by weight of dispersant and 76% by weight of TMPTA), 15% by weight of 2-hydroxyethyl acrylate as an adhesion promoting agent, a binder solution 10 wt% DPHA as a polyfunctional monomer, 3 wt% Irgacure 819 as a photoinitiator, 3 wt% Irgacure 907, and 1 wt% ITX as a polyfunctional monomer, and 10 wt% 0.5% by weight of a reaction inhibitor (10% by weight of monomethylether hydroquinone (MEHQ) and 90% by weight of butyl carbitol) based on the total weight of the reaction inhibitor were mixed and the mixture was stirred for 5 hours to prepare an ultraviolet curable ink composition.
<비교예 1>≪ Comparative Example 1 &
안료분산액의 TMPTA 함량을 줄이면서 butyl carbitol acetate 용매 15 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다An ultraviolet curable ink composition was prepared in the same manner as in Example 1 except that 15 wt% of butyl carbitol acetate solvent was added while reducing the TMPTA content of the pigment dispersion
<비교예 2>≪ Comparative Example 2 &
안료분산액의 TMPTA 함량을 줄이면서 butyl carbitol acetate 용매 15 중량%, 부착력 증진제로 2-히드록시에틸 아크릴레이트 대신 Butyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다.Except that 15 wt% of butyl carbitol acetate solvent and 10 wt% of butyl acrylate instead of 2-hydroxyethyl acrylate were added to the pigment dispersion while reducing the TMPTA content of the pigment dispersion, the ultraviolet curable ink A composition was prepared.
<비교예 3>≪ Comparative Example 3 &
안료분산액의 TMPTA 함량을 줄이면서 butyl carbitol acetate 용매 15 중량%, 부착력 증진제로 2-히드록시에틸 아크릴레이트 대신 Ethyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다.Except that 15 wt% of butyl carbitol acetate solvent and 10 wt% of ethyl acrylate instead of 2-hydroxyethyl acrylate were added to the pigment dispersion while reducing the TMPTA content of the pigment dispersion, the ultraviolet curable ink A composition was prepared.
<비교예 4>≪ Comparative Example 4 &
안료분산액의 TMPTA 함량을 줄이면서 butyl carbitol acetate 용매 15 중량%, 부착력 증진제로 2-히드록시에틸 아크릴레이트 대신 2-Ethyl hexyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다.Except that 15 wt% of butyl carbitol acetate solvent and 10 wt% of 2-ethyl hexyl acrylate instead of 2-hydroxyethyl acrylate as the adhesion promoter were added while reducing the TMPTA content of the pigment dispersion, An ultraviolet curable ink composition was prepared.
<비교예 5>≪ Comparative Example 5 &
부착력 증진제 2-hydroxyethyl acrylate를 첨가하지 않은 것을 제외하고는, 실시예 1과 동일하게 자외선 경화형 잉크 조성물을 제조하였다. An ultraviolet curable ink composition was prepared in the same manner as in Example 1, except that 2-hydroxyethyl acrylate was not added.
<비교예 6>≪ Comparative Example 6 >
부착력 증진제로 2-hydroxyethyl acrylate 5 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다. An ultraviolet curable ink composition was prepared in the same manner as in Example 1 except that 5% by weight of 2-hydroxyethyl acrylate was added as an adhesion promoting agent.
<비교예 7>≪ Comparative Example 7 &
부착력 증진제로 Butyl acrylate 5 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다. An ultraviolet curable ink composition was prepared in the same manner as in Example 1 except that 5% by weight of butylacrylate was added as an adhesion promoting agent.
<비교예 8>≪ Comparative Example 8 >
부착력 증진제로 Butyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다. An ultraviolet curable ink composition was prepared in the same manner as in Example 1, except that 10% by weight of butylacrylate was added as an adhesion promoting agent.
<비교예 9>≪ Comparative Example 9 &
부착력 증진제로 Ethyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다. An ultraviolet curable ink composition was prepared in the same manner as in Example 1, except that 10% by weight of ethyl acrylate was added as an adhesion promoting agent.
<비교예 10>≪ Comparative Example 10 &
부착력 증진제로 2-Ethyl hexyl acrylate 10 중량%를 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 자외선 경화형 잉크 조성물을 제조하였다.
An ultraviolet curable ink composition was prepared in the same manner as in Example 1 except that 10% by weight of 2-ethyl hexyl acrylate was added as an adhesion promoting agent.
<물성평가>≪ Evaluation of physical properties &
상기 제조된 자외선 경화형 잉크 조성물을 가로 50mm, 세로 50mm, 두께 100㎛의 크기의 정사각형 모양의 PET 필름에 5㎛의 두께로 잉크젯 프린팅하여 시편을 제작하였다. 제작한 시편을 100℃ 오븐에서 2 분 이상 가열한 뒤 UV경화를 실시하였다. 이후 상기 시편에 대해서 표면경도 측정 실험 및 부착력 측정 실험을 수행하여 그 결과를 표 1 및 2에 나타냈다.The ultraviolet curable ink composition prepared above was inkjet printed on a square PET film having a size of 50 mm in width, 50 mm in length and 100 탆 in thickness to a thickness of 5 탆. The specimens were heated in a 100 ℃ oven for 2 minutes and then UV cured. Then, the surface hardness measurement test and the adhesion force measurement test were performed on the specimens, and the results are shown in Tables 1 and 2.
표면경도 측정은 연필경도계로 측정하였으며, 긁기각도 45도, 하중 500g 조건에서 측정하였다(규격 : ASTM D3363).The surface hardness was measured with a pencil hardness tester and measured at a scratch angle of 45 degrees and a load of 500 g (specification: ASTM D3363).
부착력 측정은 cross cut test을 실시하여 측정하여 0B~5B로 평가하였다(규격 : ASTM D3359).
Adhesion strength was measured by cross cut test and evaluated as 0B to 5B (Specification: ASTM D3359).
2-HEA: 2-hydroxyethyl acrylate2-HEA: 2-hydroxyethyl acrylate
B.A.: Butyl acrylateB.A .: Butyl acrylate
E.A.: Ethyl acrylateE.A .: Ethyl acrylate
2-EHA: 2-Ethyl hexyl acrylate
2-EHA: 2-Ethyl hexyl acrylate
상기 표 1에서 보는 바와 같이, 부착력 개선을 위해 butyl carbitol acetate 용매를 첨가한 비교예 1, 비교예 2, 비교예 3 및 비교예 4의 잉크 조성물은 표면경도가 HB, 부착력이 2B~4B 수준으로 낮게 나타났다, As shown in Table 1, the ink compositions of Comparative Example 1, Comparative Example 2, Comparative Example 3 and Comparative Example 4 in which the butyl carbitol acetate solvent was added to improve the adhesion strength showed HB with a surface hardness of 2B to 4B Respectively,
상기 표 2에서 보는 바와 같이, 용매를 첨가하지 않은 비교예 5의 잉크 조성물은 부착력은 0B로 상당히 낮았고, 비교예 7 내지 10의 잉크 조성물은 표면경도가 용매를 첨가하지 않았을 때보다 개선되었지만 여전히 부족하였고 부착력도 3B~4B수준으로 낮게 나타났다.As shown in Table 2, the ink composition of Comparative Example 5, to which no solvent was added, had a very low adhesive force of 0B, and the ink compositions of Comparative Examples 7 to 10 showed improvement in surface hardness as compared with the case where the solvent was not added, And the adhesive strength was low as 3B ~ 4B level.
또한, 부착력 증진제 2-HEA를 5 중량% 첨가한 비교예 6의 잉크 조성물은 표면경도가 3H이고, 부착력은 3B이어서 표면경도 및 부착력이 미흡하였다.In addition, the ink composition of Comparative Example 6 in which 5% by weight of the adhesion promoter 2-HEA was added had a surface hardness of 3H and an adhesion force of 3B, which was insufficient in surface hardness and adhesion.
반면, 본 발명에 따라 부착력 증진제로 2-HEA를 10 ~ 15 중량% 첨가한 실시예 1 내지 2의 잉크 조성물은 표면경도가 8H이고, 부착력은 5B이어서 가장 우수한 물성을 나타냈다.On the other hand, according to the present invention, the ink compositions of Examples 1 and 2 containing 10 to 15 wt% of 2-HEA as an adhesion promoter exhibited the best physical properties with a surface hardness of 8H and an adhesive strength of 5B.
Claims (17)
상기 안료 분산액은 카본 블랙(Carbon black) 안료, 분산제 및 제1 반응성 모노머를 포함하며,
상기 카본 블랙 안료는 상기 안료 분산액의 총 중량에 대하여 10 ~ 30중량% 또는 잉크 조성물의 총 중량에 대하여 5 ~ 40 중량%로 포함되고,
상기 분산제의 함량은 상기 안료 분산액의 총 중량에 대하여 2 ~ 6 중량%로 포함되며,
상기 안료 분산액은 잉크 조성물의 총 중량에 대하여 50 ~ 65 중량%로 포함되고,
상기 제1 반응성 모노머의 함량은 상기 안료 분산액의 총 중량에 대하여 65 ~ 85 중량%로 포함되며,
상기 제1 반응성 모노머는 1,6-헥산디올 디아크릴레이트, 네오펜틸글리콜 히드록시피발레이트(neopentylglycol hydroxypivalate), 트리메틸올프로판 트리아크릴레이트(trimethylolpropane triacrylate:TMPTA), 펜타에리스리톨 트리아크릴레이트, 트리메틸렌프로판 트리아크릴레이트, 펜타에리스톨 트리아크릴레이트, 트리메틸렌 프로필 트리아크릴레이트 및 프로폭시레이티드 글리세롤 트리아크릴레이트로 이루어진 군으로부터 선택되는 1종 또는 2종 이상의 혼합물인 것을 특징으로 하는 잉크젯용 자외선 경화형 잉크 조성물.A pigment dispersion, a 7 to 20 wt% hydroxyalkyl (meth) acrylate, a binder solution, a polyfunctional monomer and a photoinitiator as an adhesion promoting agent based on the total weight of the ink composition,
Wherein the pigment dispersion comprises a carbon black pigment, a dispersant and a first reactive monomer,
The carbon black pigment is contained in an amount of 10 to 30% by weight based on the total weight of the pigment dispersion or 5 to 40% by weight based on the total weight of the ink composition,
The content of the dispersing agent is 2 to 6% by weight based on the total weight of the pigment dispersion,
The pigment dispersion is contained in an amount of 50 to 65% by weight based on the total weight of the ink composition,
The content of the first reactive monomer is 65 to 85% by weight based on the total weight of the pigment dispersion,
The first reactive monomer may be selected from the group consisting of 1,6-hexanediol diacrylate, neopentylglycol hydroxypivalate, trimethylolpropane triacrylate (TMPTA), pentaerythritol triacrylate, trimethylene propane An ultraviolet curable ink composition for inkjet, which is a mixture of at least one selected from the group consisting of triacrylate, pentaerythritol triacrylate, trimethylene propyl triacrylate and propoxylated glycerol triacrylate .