KR101806998B1 - Bulletproof matter for women's bulletproof jacket and a manufacturing method thereof - Google Patents

Bulletproof matter for women's bulletproof jacket and a manufacturing method thereof Download PDF

Info

Publication number
KR101806998B1
KR101806998B1 KR1020170060851A KR20170060851A KR101806998B1 KR 101806998 B1 KR101806998 B1 KR 101806998B1 KR 1020170060851 A KR1020170060851 A KR 1020170060851A KR 20170060851 A KR20170060851 A KR 20170060851A KR 101806998 B1 KR101806998 B1 KR 101806998B1
Authority
KR
South Korea
Prior art keywords
material layer
bulletproof
bulletproof material
cover cup
cup portion
Prior art date
Application number
KR1020170060851A
Other languages
Korean (ko)
Inventor
김천수
손영익
인원교
강지만
Original Assignee
김천수
(주)보광직물
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김천수, (주)보광직물 filed Critical 김천수
Priority to KR1020170060851A priority Critical patent/KR101806998B1/en
Application granted granted Critical
Publication of KR101806998B1 publication Critical patent/KR101806998B1/en

Abstract

The present invention provides a bulletproof material for a bulletproof jacket for women and a manufacturing method thereof. A ceramic bulletproof panel for a bulletproof jacket comprises: a ceramic plate formed to have curvature; a bulletproof material layer formed by laminating a plurality of polyethylene sheets cut in a shape corresponding to the ceramic plate, and laminated on an inner surface of the ceramic plate; an adhesion sheet laminated between the ceramic plate and the bulletproof material layer to affix the ceramic plate and the bulletproof material layer; a scattering prevention sheet which is affixed to an outer surface of the ceramic plate, and prevents the ceramic plate from scattering while the ceramic plate is broken by an impact applied to the ceramic plate; and a twisting prevention unit which is affixed to a side of the scattering prevention sheet, the bulletproof material layer, and the ceramic plate, and prevents the scattering prevention sheet, the bulletproof material layer, and the ceramic plate from twisting.

Description

여성 방탄복용 방탄재 및 이의 제작방법{BULLETPROOF MATTER FOR WOMEN'S BULLETPROOF JACKET AND A MANUFACTURING METHOD THEREOF}FIELD OF THE INVENTION [0001] The present invention relates to a bulletproof material for a female bullet-

본 발명은 여성 방탄복용 방탄재 및 이의 제작방법에 관한 것으로, 여성의 가슴을 커버하도록 가슴커버컵부를 형성하여 착용감을 향상시킬 수 있음은 물론 가슴에 가해지는 압박을 방지하여 오랜 시간 착용이 가능한 여성 방탄복용 방탄재 및 이의 제작방법에 관한 것이다.
The present invention relates to a bulletproof bullet material for female bulletproofing and a method of manufacturing the bulletproof bulletproof material for female bulletproofing. The bullet cover cup part can be formed to cover a woman's chest to improve the fit feeling, To a bullet-proof bulletproof material and a manufacturing method thereof.

일반적으로, 총기류로부터 발사되는 탄두 또는 칼, 송곳, 죽창과 같은 날카로운 끝단을 갖는 흉기에 의한 공격에 대해서, 선체, 차체, 인체 등의 "피보호체"를 보호하고자 하는 방탄 또는 방검용의 "보호 패널" 또는 "보호 구조재"가 널리 공지되어 있다.In general, protection against bullets or defenses intended to protect a "protected body", such as a hull, body, or body, against an attack by a weapon having a sharp end, such as a warhead or a sharp end, such as a knife, Panel "or" protective structure material "are widely known.

이러한 보호 패널 또는 보호 구조재는 방탄복에 사용될 수 있으며, 통상의 방탄복은 탄환 및 포탄 파편으로 인한 부상을 줄이려는 목적으로 만들어진 의류이다. 이와 같은 방탄복은 군인, 경찰, 사설 경호원들이 주로 착용하여 교전 상황에서 실탄 및 폭발물의 파편으로부터 신체를 보호하는데 사용된다.Such protective panels or protective structures may be used in body armor, and typical body armor is a garment intended to reduce injury due to bullets and shell debris. Such armor is mainly used by soldiers, police, and private security guards to protect the body from fragments of bullets and explosives in an engagement situation.

최근에는 방탄복의 성능을 개선하기 위하여 세라믹을 사용하는 방탄복의 보급이 점차 증가하고 있는 추세이다. 이처럼 세라믹을 이용한 방탄복은 현재 완전히 규명되지 않은 상태이나 총탄 또는 발사체의 파편이 초기 세라믹 플레이트와 충돌할 때, 세라믹 플레이트를 여러 조각으로 파손하면서 대부분의 운동에너지를 이 세라믹 파편 조각들에게 분산 흡수하고 뾰족한 선단부가 버섯모양으로 변형되거나, 여러 조각으로 분할되어 접촉면이 증가된 상태로 진행하면서 적층된 방탄섬유에 남은 에너지를 다 흡수하면서 통과하지 못한다고 알려져 있다.In recent years, the use of ceramics has been increasing in order to improve the performance of the body armor. This type of ceramic armor is now completely unidentified, but when a piece of bullet or projectile collides with an initial ceramic plate, the ceramic plate is broken into several pieces, and most of the kinetic energy is dispersed and absorbed by the pieces of ceramic fragments. It is known that the tip is deformed into mushroom shape or divided into several pieces to increase the contact surface and absorb the energy remaining in the laminated bulletproof fiber and fail to pass through.

그러나, 상기와 같은 종래의 세라믹을 이용한 방탄복은 방호를 위한 방탄패널이 평탄하게 형성되므로, 여성이 착용하였을 때 여성의 가슴부위에 과도한 압박이 가해져 착용감이 현저하게 저하됨은 물론 오랜 시간 동안 착용하기가 매우 어려운 문제점이 있다.However, since the bulletproof panel for protecting is flatly formed in the conventional ceramic body using the ceramic as described above, excessive pressure is applied to the female's bust when the female wears it, so that the feeling of wearing is remarkably lowered, There is a very difficult problem.

따라서, 이를 개선할 필요성이 요청된다.Therefore, there is a need to improve this.

한편, 국내 등록특허공보 제10-1364337호(등록일:2014년02월11일)에는 "이중타일 결합구조를 갖는 방탄용 세라믹 복합체"가 개시되어 있다.
On the other hand, Korean Patent Registration No. 10-1364337 (filed on Feb. 11, 2014) discloses a "ceramic composite for bullet-proof having a double-tile bonding structure ".

본 발명은 상기와 같은 필요성에 의해 창출된 것으로서, 여성의 가슴을 커버하도록 가슴커버컵부를 형성하여 착용감을 향상시킬 수 있을 뿐만 아니라, 가슴에 가해지는 압박을 방지함으로써, 활동이 용이하고 오랜 시간 편안하게 착용할 수 있는 여성 방탄복용 방탄재 및 이의 제작방법을 제공하는데 그 목적이 있다.
The present invention has been made in view of the above needs. It is an object of the present invention to provide a chest cover cup portion for covering a woman's chest to improve the fit feeling and prevent pressure applied to the chest, And a method for manufacturing the same.

상기한 목적을 달성하기 위하여 본 발명의 일 측면에 따른 여성 방탄복용 방탄재는, 합성수지시트가 복수개 적층되는 방탄재층과, 상기 방탄재층의 특정부분이 열성형을 통해 상기 방탄재층의 일측으로 돌출 및 경화되어 여성의 가슴부위를 커버하는 가슴커버컵부와, 상기 방탄재층이 삽입되는 외피부를 포함하는 것을 특징으로 한다.In order to attain the above object, the present invention provides a bulletproof bulletproof material for female bullets, comprising: a bulletproof material layer in which a plurality of synthetic resin sheets are laminated; a bulky material layer protruded and hardened to one side of the bulletproof material layer by thermoforming; A chest cover cup portion covering the chest area of the woman, and an outer skin into which the bulletproof material layer is inserted.

또한, 상기 방탄재층은, 총탄의 타격시 상기 합성수지시트가 개별적으로 말리는 것이 방지되도록 테두리부에 재봉 또는 열압착을 통해 접착라인이 형성되는 것을 특징으로 한다.Further, the bulletproof material layer is characterized in that an adhesive line is formed through sewing or thermocompression bonding at the rims so that the synthetic resin sheets are prevented from being dried individually when the bullet is hit.

또한, 상기 합성수지시트는, 폴리에틸렌 수지인 것을 특징으로 한다.Further, the synthetic resin sheet is characterized by being a polyethylene resin.

또한, 상기 합성수지시트는, 섬유질방향이 교차하도록 적층되어 상기 방탄재층을 형성하는 것을 특징으로 한다.Further, the synthetic resin sheet is laminated so that the fiber direction crosses to form the bulletproof material layer.

또한, 상기 가슴커버컵부는, 열프레스에 의해 130 ~135℃에서 압축 성형되는 것을 특징으로 한다.Further, the chest cover cup portion is compression-molded at 130 to 135 占 폚 by a hot press.

또한, 상기 여성 방탄복용 방탄재는, 상기 가슴커버컵부의 성형으로 인하여 발생하는 취약부위를 보강하도록 상기 가슴커버컵부에 적층되어 상기 가슴커버컵부와 함께 성형되는 보강시트를 더 포함하는 것을 특징으로 한다.The bulletproof material for women's bullets-proofing may further include a reinforcing sheet laminated on the breast cover cup part to be reinforced with a weak part caused by the molding of the breast cover cup part and formed together with the breast cover cup part.

상기한 목적을 달성하기 위하여 본 발명의 다른 측면에 따른 여성 방탄복용 방탄재 제조방법은, 폴리에틸렌 수지를 절단하여 합성수지시트를 형성하고, 상기 합성수지시트를 20장 ~ 40장을 적층하여 방탄재층을 제작하는 제1공정과, 상기 방탄재층을 열프레스에 투입하여 상기 방탄재층의 특정부위를 130 ~135℃로 열압착하여 가슴커버컵부를 성형한 후, 상기 가슴커버컵부를 상기 열프레스에서 냉각하는 제2공정과, 상기 가슴커버컵부를 상기 열프레스에서 냉각시켜 이형하고, 열성형된 상기 방탄재층을 외피에 삽입하는 제3공정을 포함하는 것을 특징으로 한다.According to another aspect of the present invention, there is provided a method for manufacturing a bulletproof material for female bulletproofing, comprising the steps of: cutting a polyethylene resin to form a synthetic resin sheet; laminating 20 to 40 sheets of the synthetic resin sheet to form a bulletproof material layer A step of putting the bulletproof material layer in a hot press to thermally press a specific region of the bulletproof material layer at 130 to 135 DEG C to form a chest cover cup portion, And a third step of cooling the chest cover cup portion by the hot press to release the thermally-formed bulletproof material layer into the envelope.

또한, 상기 제1공정에서는, 상기 가슴커버컵부를 형성하는 부위에 보강시트를 적어도 2장이상 더 적층하여 상기 가슴커버컵부를 보강하는 것을 특징으로 한다.
In addition, in the first step, at least two reinforcing sheets are laminated at a portion where the chest cover cup portion is formed to reinforce the chest cover cup portion.

이상에서 설명한 바와 같이, 본 발명에 따른 여성 방탄복용 방탄재 및 이의 제작방법은 종래기술과는 달리 여성의 돌출된 가슴을 커버하도록 가슴커버컵부를 형성하여 착용감을 향상시킬 수 있을 뿐만 아니라, 가슴커버컵부에 의해 방탄재층의 적층된 상태가 안정되게 유지되므로 취급이 용이한 효과를 가진다.As described above, according to the bulletproof bullet material for female bulletproofing and the method of manufacturing the bulletproof bulb material according to the present invention, it is possible to improve the fit feeling by forming the breast cover cup part to cover the protruding breast of the woman, Since the laminated state of the ballistic material layer is stably maintained by the cup portion, it is easy to handle.

또한, 본 발명에 따른 여성 방탄복용 방탄재 및 이의 제작방법은 가슴커버컵부에 의해 착용감이 향상되므로, 가슴에 가해지는 압박이 방지되어 오랜 시간 착용할 수 있는 효과를 가진다.Further, the bulletproof material for a female bullet-proof bulb according to the present invention and the method of manufacturing the bulletproof bulb material according to the present invention have an effect of being worn for a long time because the feeling of fit is improved by the breast cover cup part,

또한, 본 발명에 따른 여성 방탄복용 방탄재 및 이의 제작방법은, 보강시트를 이용하여 가슴커버컵부 성형에 따른 취약부위를 커버하므로, 성능저하를 방지할 수 있는 효과를 가진다.
In addition, the bulletproof material for female bulletproofing according to the present invention and the method for manufacturing the bulletproof material for women's bulletproof covering have the effect of preventing a performance deterioration because they cover a vulnerable portion due to the forming of a breast cover cup part by using a reinforcing sheet.

도 1은 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 사시도이다.
도 2는 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 도 1의 A-A선 단면도이다.
도 3은 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 도 1의 B-B선 단면도이다.
도 4는 본 발명의 일 실시예에 따른 방탄재층의 적층 상태를 나타낸 사시도이다.
도 5는 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재 제조방법을 설명하기 위한 공정도이다.1 is a perspective view showing a bullet-proof bullet-proof material according to an embodiment of the present invention.
FIG. 2 is a cross-sectional view taken along the line AA of FIG. 1 showing a bulletproof material for a female bulletproof control according to an embodiment of the present invention.
3 is a cross-sectional view taken along the line BB of Fig. 1 showing a bulletproof material for a female bulletproof control according to an embodiment of the present invention.
4 is a perspective view showing a laminated state of the bulletproof material layer according to an embodiment of the present invention.
5 is a process diagram for explaining a method for manufacturing a bulletproof material for a female bulletproofing according to an embodiment of the present invention.

이하, 첨부된 도면들을 참조하여 본 발명에 따른 여성 방탄복용 방탄재 및 이의 제작방법의 바람직한 실시예를 설명한다. 이 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다.DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of a bulletproof material for female bulldozer according to the present invention and a method of manufacturing the same will be described with reference to the accompanying drawings. In this process, the thicknesses of the lines and the sizes of the components shown in the drawings may be exaggerated for clarity and convenience of explanation.

또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다. 그러므로, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.
In addition, the terms described below are defined in consideration of the functions of the present invention, which may vary depending on the intention or custom of the user, the operator. Therefore, definitions of these terms should be made based on the contents throughout this specification.

도 1은 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 사시도이고, 도 2는 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 도 1의 A-A선 단면도이고, 도 3은 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재를 나타낸 도 1의 B-B선 단면도이다.2 is a cross-sectional view taken along line AA of FIG. 1 showing a female bullet-proof bulletproof material according to an embodiment of the present invention, and FIG. 3 is a cross- 1 is a sectional view taken along line BB of Fig. 1 showing a bulletproof material for a female bulletproofing according to an embodiment of the present invention.

또한, 도 4는 본 발명의 일 실시예에 따른 방탄재층의 적층 상태를 나타낸 사시도이고, 도 5는 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재 제조방법을 설명하기 위한 공정도이다.
4 is a perspective view illustrating a laminate structure of a bulletproof material layer according to an embodiment of the present invention, and FIG. 5 is a process diagram illustrating a method of manufacturing a bulletproof material for a female bulletproof barrier according to an embodiment of the present invention.

도 1 내지 도 4에 도시된 바와 같이, 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재(100)는, 여성의 가슴을 안정적으로 커버할 수 있도록 방탄재층(110)과, 방탄재층(110)에서 돌출 형성되는 가슴커버컵부(120)와, 방탄재층(110)을 보호하기 위한 외피부(150)와, 가슴커버컵부(120)를 보강하기 위한 보강시트(130)를 포함한다.1 to 4, a female bulletproof wearing bulletproof material 100 according to an embodiment of the present invention includes a bulletproof material layer 110 and a bulletproof material layer 110 And a reinforcing sheet 130 for reinforcing the bust cover cup portion 120. The bust cover cup portion 120 protrudes from the bust cover cup portion 120. The bust cover cup portion 120 protrudes from the bust cover cup portion 120,

이러한, 여성 방탄복용 방탄재(100)는 여성이 방탄복을 착용하게 되면 가슴커버컵부(120)에 여성의 가슴부위가 삽입되어 안착되므로, 가슴에 가해지는 압박이 방지되어 착용감이 향상된다.When the female body armor is worn by the female bullet-proof bulletproof material 100, since the female breast part is inserted and seated in the chest cover cup part 120, the pressure applied to the chest is prevented, thereby improving the fit feeling.

방탄재층(110)은 합성수지시트(111)가 복수개 예를 들어 20 ~ 40장이 적층되며, 중앙부에 가슴커버컵부(120)가 형성된다. 또한, 방탄재층(110)은 취급이 용이하도록 테두리부에 접착라인(113)이 형성된다. 이러한, 방탄재층(110)은 가슴커버컵부(120)가 성형될 때 접착라인(113)이 열압착을 통해 함께 형성될 수 있다. 접착라인(113)은 방탄재층(110)에 탄환이 맞을 경우 합성수지시트(111)가 개별적으로 말리거나 들리는 것을 방지한다.In the ballistic material layer 110, 20 to 40 sheets of synthetic resin sheet 111 are stacked, for example, and a chest cover cup portion 120 is formed at the center. Further, the ballistic material layer 110 is formed with an adhesive line 113 at a rim portion to facilitate handling. The bulletproof material layer 110 may be formed together with the adhesive lines 113 by thermocompression when the chest cover cup portion 120 is formed. The adhesive line 113 prevents the synthetic resin sheet 111 from being individually dried or lifted when the bulletproof material layer 110 is hit by a bullet.

합성수지시트(111)는 폴리에틸렌 수지에 의해 특정형상으로 재단되어 형성되며, 일정한 패턴의 방향성을 가지는 섬유질(140)을 포함한다. 이러한 합성수지시트(111)는 섬유질(140)의 방향성이 교차하도록 상호 적층되어 방탄재층(110)을 형성하게 된다. 이로 인하여 방탄재층(110)의 방탄 성능이 향상된다.The synthetic resin sheet 111 is formed by being cut into a specific shape by a polyethylene resin and includes fibers 140 having a predetermined pattern of directionality. The synthetic resin sheets 111 are laminated to each other such that the fibers 140 cross each other to form a bulletproof material layer 110. This improves the bulletproof performance of the bulletproof material layer 110.

본 실시예에서는 합성수지시트(111)가 폴리에틸렌(Polyethylene)에 의해 제작되는 것을 예를 들어 설명하고 있지만, 합성수지시트(111)를 아라미드 직물, 아라미드 라미네이팅 직물, 초고분자량 폴리에틸렌(UHMWPE, Ultra High Molecular Weight Poly-Ethylene) UD, 초고분자량 폴리에틸렌(UHMWPE, Ultra High Molecular Weight Poly-Ethylene) 섬유 중 선택된 어느 하나에 의해 제작될 수도 있다.The synthetic resin sheet 111 is made of aramid fabric, aramid laminating fabric, ultra high molecular weight polyethylene (UHMWPE, Ultra High Molecular Weight Poly -Ethylene UD, Ultra High Molecular Weight Poly-Ethylene (UHMWPE) fibers.

가슴커버컵부(120)는 방탄재층(110)의 특정부분에 열과 압력이 가해져서 형성되며, 여성의 가슴이 삽입되는 공간을 확보하게 된다. 이러한 가슴커버컵부(120)는 열프레스를 통해 특정부분에 열과 압력이 가해지면 방탄재층(110)의 일측으로 돌출 및 경화된다.The chest cover cup portion 120 is formed by applying heat and pressure to a specific portion of the bulletproof material layer 110, thereby securing a space for inserting a woman's chest. The bust cover cup portion 120 protrudes and hardens to one side of the bulletproof material layer 110 when heat and pressure are applied to a specific portion through a hot press.

본 실시예에 따른 가슴커버컵부(120)는 열프레스에 의해 130 ~ 135℃에서 압축 성형될 수 있다. 여기서, 가슴커버컵부(120)를 성형할 때 성형 온도가 130℃ 미만이면 가슴커버컵부(120)의 성형성이 저하되고, 성형 온도가 135℃를 초과하면 방탄재층(110)의 성질이 변화되어 방호 성능이 저하된다.The chest cover cup portion 120 according to the present embodiment can be compression-molded at 130 to 135 ° C by a hot press. If the forming temperature is less than 130 캜 when forming the chest cover cup portion 120, the moldability of the chest cover cup portion 120 is lowered. If the forming temperature exceeds 135 캜, the properties of the ballistic material layer 110 are changed The protection performance deteriorates.

또한, 가슴커버컵부(120)의 열 성형시 방탄재층(110)에서 굴곡되는 부분에 취약부위(121)가 발생하게 되는데, 이 취약부위(121)가 보강시트(130)에 의해 보강된다.The fragile portion 121 is formed in the portion of the bulletproof material layer 110 bent at the time of thermoforming of the chest cover cup portion 120. The fragile portion 121 is reinforced by the reinforcing sheet 130.

보강시트(130)는 합성수지시트(111)가 가슴커버컵부(120) 형상으로 절단되어 사용되며, 가슴커버컵부(120)가 성형되는 부위에 위치하도록 방탄재층(110)에 적어도 2겹 이상으로 적층된다. 또한, 보강시트(130)는 방탄재층(110)에 적층될 때 섬유질(140)의 방향성이 교차하도록 적층된다.The reinforcing sheet 130 is used to cut the synthetic resin sheet 111 into the shape of the chest cover cup part 120 and to stack the bulletproof material layer 110 in at least two or more layers do. Further, the reinforcing sheet 130 is stacked so that the direction of the fibers 140 crosses when stacked on the ballistic material layer 110.

이러한, 보강시트(130)는 가슴커버컵부(120)의 열 성형으로 인하여 발생하는 취약부위(121)를 보강하도록 방탄재층(110)에 적층되어 가슴커버컵부(120)와 함께 열 성형된다.The reinforcing sheet 130 is laminated to the bulletproof material layer 110 and thermoformed together with the chest cover part 120 so as to reinforce the fragile area 121 caused by the thermoforming of the chest cover part 120.

외피부(150)는 방탄재(100)의 취급이 용이하도록 가슴커버컵부(120)의 성형이 완료된 방탄재층(110)이 삽입되며, 마감을 위하여 테두리부가 재봉처리된다.The outer skin 150 is inserted with the bulletproof material layer 110 of the bust cover cup part 120 to facilitate handling of the bulletproof material 100 and the frame part is sewn to finish.

한편 본 실시예에 따른 여성 방탄복용 방탄재(100)는 가슴커버컵부(120)가 경화된 상태로 제공되고, 가슴커버컵부(120)를 제외한 다른 부위가 플렉시블한 상태를 유지하게 된다. 이로 인하여, 방탄복을 착용하였을 때 여성 방탄복용 방탄재(100)가 착용자의 몸에 맞게 휘어지므로, 착용감이 향상됨은 물론 착용을 용이하게 할 수 있다.
Meanwhile, the bulletproof bullet material 100 for a female bulldozer according to the present embodiment is provided in a cured state of the chest cover cup portion 120, and other portions except for the chest cover cup portion 120 are maintained in a flexible state. As a result, when the bulletproof vest 100 is warped to fit the body of the wearer when the bulletproof vest is worn, the wearing comfort can be improved and the wearer can be easily worn.

상기와 같이 구성되는 본 발명의 일 실시예에 따른 여성 방탄복용 방탄재의 제조방법을 설명한다.A method of manufacturing a bulletproof material for female bulletproofing according to an embodiment of the present invention will be described.

도 1 내지 도 5에 도시된 바와 같이, 본 실시예에 따른 방탄복용 방탄체의 제조방법은, 합성수지시트(111)를 적층하여 방탄재층(110)을 형성하는 제1공정(S10)과, 방탄재층(110)을 열을 이용하여 가슴커버컵부(120)를 가공하는 제2공정(S20)과, 열 가공된 방탄재층(110)을 탈형하는 제3공정(S30)을 포함한다.1 to 5, the method for manufacturing a bullet-proof carcass according to the present embodiment includes a first step (S10) of laminating a synthetic resin sheet 111 to form a bulletproof material layer 110, A second step S20 of processing the chest cover cup portion 120 by using the material layer 110 as a heat and a third step S30 of demolding the thermally processed ballistic material layer 110 as shown in FIG.

제1공정(S10)은 시트 형태로 제공되는 폴리에틸렌 수지를 재단하여 특정형태의 합성수지시트(111)를 제작하고(S11), 합성수지시트(111)를 20 ~ 40장을 적층하여 방탄재층(110)을 제작한다(S13).In the first step S10, a polyethylene resin provided in a sheet form is cut to produce a specific type of synthetic resin sheet 111 (S11), 20 to 40 sheets of the synthetic resin sheet 111 are laminated to form a bulletproof material layer 110, (S13).

그리고, 제1공정(S10)에서는 폴리에틸렌 수지를 재단할 때 합성수지시트(111)의 섬유질(140) 방향이 다른 방향을 가지도록 재단하며, 합성수지시트(111)의 섬유질(140) 방향이 교차하도록 적층한다.In the first step S10, the synthetic resin sheet 111 is cut so that the direction of the fibers 140 of the synthetic resin sheet 111 is different from that of the synthetic resin sheet 111 when cutting the polyethylene resin, do.

특히 제1공정(S10)에서는 가슴커버컵부(120)를 형성함에 따라 발생하는 취약부위(121)를 보강하도록 방탄재층(110)에 보강시트(130)를 2장 이상 더 적층한다(S15). 이때, 보강시트(130)의 섬유질(140) 또한 서로 교차하도록 적층한다.More particularly, in the first step S10, two or more sheets of the reinforcing sheet 130 are laminated on the bulletproof material layer 110 so as to reinforce the weakened portions 121 generated by forming the bust cover cup portion 120 (S15). At this time, the fibers 140 of the reinforcing sheet 130 are also laminated so as to cross each other.

제2공정(S20)은 보강시트(130)를 적층한 방탄재층(110)을 열프레스에 투입한 후, 보강시트(130)가 적층된 방탄재층(110)의 특정부위를 130 ~ 135℃로 열압착하여 가슴커버컵부(120)를 성형한다(S21). 가슴커버컵부 성형단계(S20)에서는 방탄재층(110)의 일측으로 돌출되어 경화되도록 가슴커버컵부(120)의 성형부위를 6 ~ 20 kg/cm2의 압력으로 열압착한다.In the second step S20, the ballistic material layer 110 in which the reinforcing sheet 130 is laminated is placed in a hot press, and then a specific portion of the ballistic material layer 110 in which the reinforcing sheet 130 is laminated is heated to 130 to 135 占 폚 And the chest cover cup portion 120 is formed by thermocompression (S21). In the chest cover cup forming step S20, the molding portion of the chest cover cup portion 120 is thermocompression-bonded at a pressure of 6 to 20 kg / cm2 so as to protrude to one side of the bulletproof material layer 110 and be cured.

또한, 제2공정(S20)에서는 가슴커버컵부(120)를 형성할 때 방탄재층(110)에 접착라인(113)을 함께 열 성형한다. 이는 방탄체(100)의 방호성능을 유지하면서 취급성 및 착용성을 향상시키기 위함이다.Further, in the second step S20, the adhesive line 113 is thermally formed on the ballistic material layer 110 when forming the chest cover cup portion 120. [ This is for improving the handleability and wearability while maintaining the protective performance of the bulletproof body 100.

그리고, 가슴커버컵부(120)의 열 성형이 완료되면(S21), 열프레스에 냉각수를 순환시키는 수냉방식을 이용하여 가슴커버컵부(120)를 급냉시킨다(S23). Then, when thermoforming of the chest cover cup portion 120 is completed (S21), the chest cover cup portion 120 is quenched by using a water-cooling method for circulating cooling water to the hot press (S23).

이처럼 제2공정(S20)을 통해 가슴커버컵부(120)를 압착하여 경화하면 취급성 및 착용성이 향상된다. 예를 들어 본 실시예에 따른 방탄체(100)가 적용된 방탄복을 착용할 때 경화된 가슴커버컵부(120)에 여성의 가슴부위가 삽입되고, 나머지 부분이 착용자의 체형에 따라 변형되면서 몸에 밀착된다.As described above, when the chest cover cup portion 120 is pressed and hardened through the second step S20, handling and wearability are improved. For example, when the body armor to which the bulletproof body 100 according to the present embodiment is applied is worn, the chest part of the woman is inserted into the cured chest cover cup part 120 and the remaining part is deformed according to the body shape of the wearer, do.

더하여, 제2공정(S20)에서 열성형된 방탄재층(110)을 급냉시키는 것은 생산성을 향상시키기 위함이다.In addition, it is desirable to quench the thermally-formed ballistic material layer 110 in the second step S20 to improve productivity.

제3공정(S30)은 냉각된 방탄재층(110)을 분리하여 외피부(150)에 삽입하고, 외피부(150)의 개방부를 재봉하여 밀폐하여 방탄재층(110)을 감싸준다.In the third step S30, the cooled bulletproof material layer 110 is separated and inserted into the outer skin 150, and the opening of the outer skin 150 is sewed to seal the bulletproof material layer 110.

상기와 같은 본 발명은 여성의 가슴을 커버하도록 가슴커버컵부(120)를 방탄재층(110)의 일측으로 돌출 및 경화시키므로, 본 실시예에 따른 방탄체(100)를 이용하는 방탄복을 착용하였을 때 여성의 가슴이 가슴커버컵부(120)에 삽입된다. 이로 인하여, 방탄복의 착용감이 향상된다.In the present invention, the chest cover cup portion 120 is protruded and hardened to one side of the bulletproof material layer 110 so as to cover the chest of a woman. Therefore, when the bulletproof material using the bulletproof material 100 according to the present embodiment is worn, The chest cover cup portion 120 is inserted into the chest. As a result, the feeling of wearing of the body armor is improved.

또한, 본 발명은 합성수지시트(111)가 적층된 방탄재층(110)의 가슴커버컵부(120)가 일체로 접합되면서 접착라인(113)에 의해 고정되므로, 방탄재층(110)의 합성수지시트(111)가 분리되는 것이 방지되고 적층된 상태가 안정되게 유지되어 제작과정에서 취급을 용이할 수 있다.Since the bust cover part 120 of the bulletproof material layer 110 in which the synthetic resin sheet 111 is laminated is fixed by the adhesive line 113 while integrally joining the bust cover material part 110 to the synthetic resin sheet 111 of the bulletproof material layer 110 Is prevented from being separated and the laminated state can be stably maintained, thereby facilitating handling in the manufacturing process.

또한, 본 발명은 여성의 가슴이 가슴커버컵부(120)에 삽입되어 착용감이 향상되므로, 가슴에 가해지는 압박이 없어 불편함 없이 오랜 시간 착용할 수 있다.In addition, since the female chest is inserted into the chest cover cup portion 120 to improve the fit feeling, the present invention can be worn for a long time without inconvenience because there is no pressing on the chest.

또한, 본 발명은 보강시트(130)를 이용하여 가슴커버컵부(120) 성형에 따른 취약부위(121)를 커버하므로, 성능저하를 방지할 수 있다.In addition, the present invention covers the vulnerable portion 121 due to the formation of the chest cover cup portion 120 by using the reinforcing sheet 130, so that it is possible to prevent performance deterioration.

본 발명은 도면에 도시된 실시예를 참고로 하여 설명되었으나, 이는 예시적인 것에 불과하며, 당해 기술이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. I will understand.

따라서, 본 발명의 진정한 기술적 보호범위는 특허청구범위에 의해서 정하여져야 할 것이다.
Accordingly, the true scope of protection of the present invention should be defined by the claims.

100 : 여성 방탄복용 방탄재 110 : 방탄재층
120 : 가슴커버컵부 130 : 외피부
140 : 섬유질100: Female bullet-proof bulletproof material 110: Bulletproof material layer
120: chest cover cup part 130: outer skin
140: Fiber

Claims (6)

합성수지시트가 복수개 적층되는 방탄재층; 상기 방탄재층의 특정부분이 열성형을 통해 상기 방탄재층의 일측으로 돌출 및 경화되어 여성의 가슴부위를 커버하는 가슴커버컵부; 상기 방탄재층이 삽입되는 외피부; 및 상기 가슴커버컵부의 성형으로 인하여 발생하는 취약부위를 보강하도록 상기 가슴커버컵부에 적층되어 상기 가슴커버컵부와 함께 성형되는 보강시트;를 포함하며,
상기 방탄재층은, 재봉 또는 열압착을 통해 테두리부에 접착라인이 형성되는고,
상기 가슴커버컵부는, 열프레스에 의해 130 ~135℃에서 압축 성형되고,
상기 보강시트는 상기 합성수지시트의 섬유질 방향성이 교차하도록 2겹 이상 적층되는 것을 특징으로 하는 여성 방탄복용 방탄재.
A bulletproof material layer in which a plurality of synthetic resin sheets are laminated; A chest cover cup part which covers a chest part of the female so as to protrude and harden to one side of the bulletproof material layer by thermoforming a specific part of the bulletproof material layer; An outer skin into which the bulletproof material layer is inserted; And a reinforcing sheet which is laminated on the chest cover cup portion and is formed together with the chest cover cup portion so as to reinforce the fragile portion caused by the molding of the chest cover cup portion,
The bulletproof material layer may have an adhesive line formed on the rim through sewing or thermocompression,
The chest cover cup portion is compression-molded at 130 to 135 DEG C by a hot press,
Wherein the reinforcing sheet is laminated in two or more layers so that the fiber direction of the synthetic resin sheet crosses.
제 1 항에 있어서,
상기 합성수지시트는, 폴리에틸렌 수지인 것을 특징으로 하는 여성 방탄복용 방탄재.
The method according to claim 1,
Wherein the synthetic resin sheet is a polyethylene resin.
삭제delete 삭제delete 폴리에틸렌 수지를 재단하여 합성수지시트를 형성하고, 상기 합성수지시트를 20장 ~ 40장을 적층하여 방탄재층을 제작하는 제1공정; 상기 방탄재층을 열프레스에 투입하여 상기 방탄재층의 특정부위를 130 ~135℃로 열압착하여 가슴커버컵부를 성형하고, 상기 가슴커버컵부를 상기 열프레스에서 냉각하는 제2공정; 및 열성형된 상기 방탄재층을 탈형하여 외피에 삽입하는 제3공정;을 포함하며,
상기 제1공정에서는, 상기 가슴커버컵부를 형성하는 부위에 보강시트를 적어도 2장 이상 적층하되, 상기 보강시트의 섬유질 방향이 교차하도록 적층하고,
상기 제2공정에서는, 상기 가슴커버컵부의 성형부위를 6 ~ 20 kg/cm2의 압력으로 열압착하면서 상기 방탄재층에 접착라인을 함께 성형하는 것을 특징으로 하는 여성 방탄복용 방탄재 제조방법.A first step of cutting a polyethylene resin to form a synthetic resin sheet, and laminating 20 to 40 sheets of the synthetic resin sheet to form a bulletproof material layer; A second step of putting the bulletproof material layer into a hot press to thermally press a specific region of the bulletproof material layer at 130 to 135 DEG C to form a chest cover cup portion and cooling the chest cover cup portion in the heat press; And a third step of demolding the thermally-formed bulletproof material layer and inserting it into the envelope,
In the first step, at least two reinforcing sheets are stacked in a region where the bust cover cup portion is formed, the reinforcing sheet is laminated so that the fiber direction of the reinforcing sheet crosses,
Wherein in the second step, an adhesive line is formed together with the bulletproof material layer by thermocompression bonding the molding part of the chest cover cup part at a pressure of 6 to 20 kg / cm < 2 >. 삭제delete
KR1020170060851A 2017-05-17 2017-05-17 Bulletproof matter for women's bulletproof jacket and a manufacturing method thereof KR101806998B1 (en)