KR101789283B1 - Indoor playground column cushioning material - Google Patents
Indoor playground column cushioning material Download PDFInfo
- Publication number
- KR101789283B1 KR101789283B1 KR1020170070904A KR20170070904A KR101789283B1 KR 101789283 B1 KR101789283 B1 KR 101789283B1 KR 1020170070904 A KR1020170070904 A KR 1020170070904A KR 20170070904 A KR20170070904 A KR 20170070904A KR 101789283 B1 KR101789283 B1 KR 101789283B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- cushioning material
- film
- flame retardant
- Prior art date
Abstract
본 발명은 실내놀이터용 기둥쿠션재에 관한 것으로, 보다 상세하게는 실내놀이시설을 지지 고정하는 기둥을 감싸 유아 또는 어린이들이 뛰어 놀 때 충돌에 의한 안전사고를 예방하기 위해 설치되는 쿠션재를 방염성과 항균성 및 내오염성을 갖도록 하여 항상 청결하게 유지되도록 하면서 화재 위험으로부터 안전성을 강화시키고 중금속을 비롯한 인체 유해물질 배출을 차단하여 어린이, 유아 등 성장기 아이들의 건강을 해치지 않도록 하면서 완충 쿠션기능도 강화시킨 실내놀이터용 기둥쿠션재에 관한 것이다.The present invention relates to a column cushioning material for an indoor playground, and more particularly, to a cushioning material for an indoor playground, which comprises a column for supporting and fixing an indoor playground, It has the stain resistance and keeps it clean at all times. It enhances the safety from the fire risk and prevents the emission of harmful substances such as heavy metals. It prevents the health of the growing children such as children and infants. Cushioning material.
Description
본 발명은 실내놀이터용 기둥쿠션재에 관한 것으로, 보다 상세하게는 실내놀이시설을 지지 고정하는 기둥을 감싸 유아 또는 어린이들이 뛰어 놀 때 충돌에 의한 안전사고를 예방하기 위해 설치되는 쿠션재를 방염성과 항균성 및 내오염성을 갖도록 하여 항상 청결하게 유지되도록 하면서 화재 위험으로부터 안전성을 강화시키고 중금속을 비롯한 인체 유해물질 배출을 차단하여 어린이, 유아 등 성장기 아이들의 건강을 해치지 않도록 하면서 완충 쿠션기능도 강화시킨 실내놀이터용 기둥쿠션재에 관한 것이다.The present invention relates to a column cushioning material for an indoor playground, and more particularly, to a cushioning material for an indoor playground, which comprises a column for supporting and fixing an indoor playground, It has the stain resistance and keeps it clean at all times. It enhances the safety from the fire risk and prevents the emission of harmful substances such as heavy metals. It prevents the health of the growing children such as children and infants. Cushioning material.
일반적으로 유치원이나 유아 놀이시설 및 체육관 등의 실내놀이시설의 바닥에는 충격 흡수를 통해 안전사고를 방지하기 위해 쿠션재가 설치된다.Generally, a cushioning material is installed on the floor of an indoor play facility such as a kindergarten, an infant play facility, and a gymnasium to prevent a safety accident through shock absorption.
이러한 쿠션재는 주로 폴리우레탄 발포재 또는 스펀지를 주로 사용하고 있다.Such a cushioning material mainly uses a polyurethane foam material or a sponge.
그리고, 실내놀이시설을 지지고정하기 위해 도 1의 예시와 같은 다수의 기둥이 설치되고, 기둥에는 도 2와 같은 완충용 쿠션재가 설치되어 유아 또는 어린이들이 충돌하였을 때 상해를 일으키지 않도록 보호하고 있다.In order to support and fix the indoor play facility, a plurality of pillars as shown in FIG. 1 are installed, and a cushioning cushion material as shown in FIG. 2 is installed on the pillars to protect the infant or children from being injured when they collide with each other.
그런데, 이러한 완충용 쿠션재는 대부분 일반 스펀지로 구성되기 때문에 장시간 사용시 스펀지가 쉽게 열화되어 부스러기가 많이 생기고 쿠션감이 떨어질 뿐만 아니라, 무엇보다도 항균성이 거의 없고, 단순히 비닐커버나 혹은 일반 레자(Leather)로 커버링되기 때문에 이들로부터 환경유해 물질이 배출되어 성장기의 아이들인 유아나 어린이들의 건강을 해치기도 한다.However, since most of these cushioning cushioning materials are made of ordinary sponge, when the cushioning material is used for a long time, the sponge is easily deteriorated to cause a lot of debris and cushion feeling, Because they are covered, environmentally harmful substances are emitted from them and harm the health of infants and children who are growing children.
뿐만 아니라, 스펀지나 레자는 방염성도 매우 취약하기 때문에 화재시 치명적인 유해물질(독성물질)을 방출은 물론 화재를 증폭시키는 심각한 문제도 있다.In addition, sponges and leathers are very vulnerable to flame retardants, which can cause serious harmful effects such as the emission of harmful substances (toxic substances) in the event of a fire, as well as the fire.
본 발명은 상술한 바와 같은 종래 기술상의 제반 문제점들을 감안하여 이를 해결하고자 창출된 것으로, 실내놀이시설을 지지 고정하는 기둥을 감싸 유아 또는 어린이들이 뛰어 놀 때 충돌에 의한 안전사고를 예방하기 위해 설치되는 쿠션재를 방염성과 항균성 및 내오염성을 갖도록 하여 항상 청결하게 유지되도록 하면서 화재 위험으로부터 안전성을 강화시키고 중금속을 비롯한 인체 유해물질 배출을 차단하여 어린이, 유아 등 성장기 아이들의 건강을 해치지 않도록 하면서 완충 쿠션기능도 강화시킨 실내놀이터용 기둥쿠션재를 제공함에 그 주된 목적이 있다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide an indoor play facility, which is installed to prevent a safety accident caused by a collision when a child The cushioning material has flame retardancy, antimicrobial and stain resistance, so it is always kept clean, while the safety from the fire risk is strengthened and the emission of harmful substances such as heavy metals is blocked, so that the health of children, The present invention provides a cushioning material for an indoor playground, which is reinforced.
본 발명은 상기한 목적을 달성하기 위한 수단으로, 실내놀이터에 설치된 기둥(100)을 감싸 완충 기능을 수행하는 쿠션부재(200)로서, 상기 쿠션부재(200)는 기둥(100)에 밀착되는 발포체(210)와, 상기 발포체(210)의 외피를 이루는 필름(220)으로 이루어진 실내놀이터용 기둥쿠션재에 있어서; 상기 발포체(210)는 완충 흡수력을 가지면서 내열성, 내화성을 높여 방염성이 강화되도록 2-3cm의 길이를 갖는 글래스파이버 14중량%와, 세스키탄산나트륨(Sodium Sesqui Carbonate) 2.5중량%와, 모노글리세라이드(monoglyceride) 4.5중량%와, DBNPA(2,2-Dibromo-3-nitrilopropionamide) 8.5중량%와, 인슐래드 분말(Insuladd powder) 6.5중량%와, TOTM(Trioctyl Trimellitate) 2.5중량% 및 나머지 폴리스티렌수지로 이루어진 혼합물을 발포 성형하여 제조된 것을 특징으로 하는 실내놀이터용 기둥쿠션재를 제공한다.The present invention provides a cushioning member (200) for enclosing a column (100) installed on an indoor playground to perform a cushioning function, wherein the cushioning member (200) (210) and a film (220) constituting an outer shell of the foam (210); The
이때, 상기 필름(220)은 표면 보호 및 항균성과 방염성을 강화시키면서 유해물질 용출 차단을 위해 에틸렌-옥텐 러버(EOR) 80중량%와, 항균방염제 20중량%로 이루어진 수지조성물을 필름 형태로 성형한 것을 사용하되, 상기 항균방염제는 상기 에틸렌-옥텐 러버 100중량부를 기준으로 DBNPA(2,2-Dibromo-3-nitrilopropionamide)와 계지분말과 수근채(Oenanthe decumbens kpol) 추출액을 2:1:1의 중량비로 혼합한 항균제혼합물 25중량부와, 포타슘실리케이트 20중량부와, 아연스테아르산염 5중량부와, 1,4-부틸렌글리콜 3.5중량부 및 규산소다(Sodium Silicates) 5중량부로 이루어지는 것에도 그 특징이 있다.At this time, the
또한, 상기 에틸렌-옥텐 러버는 용융흐름지수가 20-25g/10min(100℃ 기준)인 것에도 그 특징이 있다.The ethylene-octene rubber has a melt flow index of 20-25 g / 10 min (at 100 ° C).
또한, 상기 필름(220)의 표면에는 코팅액이 스프레이되어 0.2-0.4mm의 두께로 방염코팅층이 더 형성되며, 상기 방염코팅층을 형성하는 코팅액은 PVC솔(PVC Sol) 80중량%와, 첨가제 20중량%로 이루어지되, 상기 첨가제는 상기 PVC솔 100중량부를 기준으로 팽창흑연 8중량부와, 수산화알루미늄 1.5중량부와, 지르코늄 4중량부와, 뮬라이트 6중량부 및 DOTP 10중량부로 이루어진 것에도 그 특징이 있다.A coating solution is sprayed on the surface of the
본 발명에 따르면, 실내놀이시설을 지지 고정하는 기둥을 감싸 유아 또는 어린이들이 뛰어 놀 때 충돌에 의한 안전사고를 예방하기 위해 설치되는 쿠션재를 방염성과 항균성 및 내오염성을 갖도록 하여 항상 청결하게 유지되도록 하면서 화재 위험으로부터 안전성을 강화시키고 중금속을 비롯한 인체 유해물질 배출을 차단하여 어린이, 유아 등 성장기 아이들의 건강을 해치지 않도록 하면서 완충 쿠션기능도 강화시키는 효과를 얻을 수 있다.According to the present invention, a cushioning material installed to prevent a safety accident caused by a collision when a child or a child jumps around a pole supporting and fixing the indoor play facility is provided with flame retardancy, antimicrobial property and stain resistance, It enhances safety from fire risk and prevents the emission of harmful substances including heavy metals, thereby enhancing the buffer cushion function while preventing the health of the growing children such as children and infants.
도 1은 일반적인 실내놀이시설의 예시적인 사진이다.
도 2는 일반적인 실내놀이시설의 기둥에 설치되는 종래 기둥쿠션재의 예시적인 사진이다.
도 3은 본 발명에 따른 실내놀이터용 기둥쿠션재의 예시적인 단면도이다.Figure 1 is an exemplary photograph of a typical indoor play facility.
2 is an exemplary photograph of a conventional column cushioning material installed in a column of a general indoor play facility.
3 is an exemplary sectional view of a column cushioning material for an indoor playground according to the present invention.
이하에서는, 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.Hereinafter, preferred embodiments according to the present invention will be described in detail.
본 발명 설명에 앞서, 이하의 특정한 구조 내지 기능적 설명들은 단지 본 발명의 개념에 따른 실시예를 설명하기 위한 목적으로 예시된 것으로, 본 발명의 개념에 따른 실시예들은 다양한 형태로 실시될 수 있으며, 본 명세서에 설명된 실시예들에 한정되는 것으로 해석되어서는 아니된다.Before describing the present invention, the following specific structural or functional descriptions are merely illustrative for the purpose of describing an embodiment according to the concept of the present invention, and embodiments according to the concept of the present invention may be embodied in various forms, And should not be construed as limited to the embodiments described herein.
또한, 본 발명의 개념에 따른 실시예는 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있으므로, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경물, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.In addition, it should be understood that the embodiments according to the concept of the present invention include various modifications, equivalents, and alternatives included in the spirit and technical scope of the present invention, .
도 3에 도시된 바와 같이, 본 발명에 따른 실내놀이터용 기둥쿠션재는 기둥(100)을 감싸 완충 기능을 수행하는 쿠션부재(200)로서, 상기 쿠션부재(200)는 기둥(100)에 밀착되는 발포체(210)와, 상기 발포체(210)의 외피를 이루는 필름(220)으로 이루어진다.3, the column cushioning material for an indoor playground according to the present invention is a
이때, 상기 쿠션부재(200)는 필름(220)과 일체로 발포체(210)를 발포하여 판상, 즉 일정 두께를 갖는 시트상으로 제조된 후 원통으로 권취 마감하여 기둥(100)을 감싸도록 기둥(100)이 삽입되게 배치됨으로써 실내놀이터용 기둥쿠션재를 완성하게 된다.The
여기에서, 상기 발포체(210)는 종래 스펀지처럼 완충 흡수력을 가지면서 내열성, 내화성을 높여 방염성이 강화되도록 2-3cm의 길이를 갖는 글래스파이버 14중량%와, 세스키탄산나트륨(Sodium Sesqui Carbonate) 2.5중량%와, 모노글리세라이드(monoglyceride) 4.5중량%와, DBNPA(2,2-Dibromo-3-nitrilopropionamide) 8.5중량%와, 인슐래드 분말(Insuladd powder) 6.5중량%와, TOTM(Trioctyl Trimellitate) 2.5중량% 및 나머지 폴리스티렌수지로 이루어진 혼합물을 발포 성형하여 제조된다.Here, the
여기에서, 상기 글래스파이버는 치수안정화와 인장강도 증대를 위해 첨가된다. 다만, 14중량%를 초과하면 성형 후 표면에 미소크랙 발생 우려가 있으므로 상기 범위로 한정해야 한다.Here, the glass fiber is added for dimensional stabilization and increase in tensile strength. However, if it exceeds 14% by weight, there is a risk of microcracks on the surface after molding, so the range should be limited to the above range.
또한, 상기 세스키탄산나트륨(Sodium Sesqui Carbonate)은 천연 알칼리제로서 Na2CO3ㆍNaHCO3ㆍ2H2O로 표현되며, 천연 무기물로서 수질오염이나 환경오염을 유발하지 않으면서 인체에 무해하고(피부자극 없음), 물에 쉽게 녹는 특성이 있으며, 수용액은 약알카리성을 띄기 때문에 본 발명에서는 변질, 변색을 방지하기 위해 첨가된다.Sodium sesquicarbonate is a natural alkali agent expressed as Na 2 CO 3 .NaHCO 3 .2H 2 O. It is a natural inorganic substance and does not cause water pollution or environmental pollution and is harmless to the human body ), Easily soluble in water. Since the aqueous solution is slightly alkaline, it is added in order to prevent deterioration and discoloration in the present invention.
그리고, 상기 모노글리세라이드는 유화를 촉진하여 표면에 이물질이 부착되는 것을 억제하므로 방오성을 강화시키기 위해 첨가된다.The monoglyceride is added to enhance the antifouling property by promoting emulsification and inhibiting the adherence of foreign matter to the surface.
또한, 상기 DBNPA는 대표적인 액상 항균제로서 알카리 환경에서도 항균 특성이 우수한 물질이며, 특히 포도상구균, 대장균, 폐렴균 및 진드기와 곰팡이에 대한 항균특성이 매우 우수한 것으로 알려져 있다.DBNPA is a typical liquid antimicrobial agent having excellent antibacterial properties even in an alkaline environment. It is known that DBNPA has excellent antimicrobial properties especially against Staphylococcus, Escherichia coli, Pneumococcus and mite and mold.
뿐만 아니라, 상기 인슐래드 분말은 알루미늄 실리케이트를 주성분으로 한 30~100 마이크론 크기의 미세중공체(microscopic hollow sphere) 분말로서 폐쇄 공기층의 세라믹 피막을 형성하여 탁월한 열반사와 열저항 효과를 발휘하며, 8대 유해 중금속은 물론 휘발성유기화합물(VOC) 및 독성이 전혀 없는 환경 친화적인 소재로서, 용융점이 약 1,800℃인 불연소재이며, 피막의 압축강도가 3,000N/㎤ 정도로서 매우 단단한 구조로 이루어져 있어 내구성이 뛰어나므로 본 발명에서는 방염성을 강화시키기 위해 첨가된다.In addition, the insulin powder is a microscopic hollow spherical powder having a size of 30 to 100 microns mainly composed of aluminum silicate and forms a ceramic coating of a closed air layer, exhibiting excellent heat radiation and thermal resistance, It is a non-combustible material with a melting point of about 1,800 ° C and has a compressive strength of about 3,000 N / cm 3 because it is an environmentally friendly material with no heavy metal, VOC and toxicity. In the present invention, it is added to enhance flame retardancy.
그리고, 상기 TOTM(Trioctyl Trimellitate)은 수지의 가소화를 촉진시키고 내열성을 강화시켜 열화방지, 내열성을 증대시키기 위해 첨가된다.The above-mentioned TOTM (Trioctyl Trimellitate) is added to promote the plasticization of the resin and enhance the heat resistance to prevent deterioration and increase the heat resistance.
또한, 상기 폴리스티렌수지는 대표적인 내화성 수지로서, 발포를 통해 내충격성도 강화시키면서 방염성도 강화시키기 위한 베이스 수지로 첨가된다.In addition, the polystyrene resin is a typical refractory resin, and is added as a base resin for enhancing flame resistance while strengthening impact resistance through foaming.
아울러, 상기 필름(220)은 표면 보호 및 항균성과 방염성을 강화시키면서 유해물질 용출 차단을 위해 용융흐름지수가 20-25g/10min(100℃ 기준)인 에틸렌-옥텐 러버(EOR) 80중량%와, 항균방염제 20중량%로 이루어지되, 상기 항균방염제는 상기 에틸렌-옥텐 러버 100중량부를 기준으로 DBNPA(2,2-Dibromo-3-nitrilopropionamide)와 계지분말과 수근채(Oenanthe decumbens kpol) 추출액을 2:1:1의 중량비로 혼합한 항균제혼합물 25중량부와, 포타슘실리케이트 20중량부와, 아연스테아르산염 5중량부와, 1,4-부틸렌글리콜 3.5중량부 및 규산소다(Sodium Silicates) 5중량부를 첨가하여 조성된다.The
이때, 상기 에틸렌-옥텐 러버는 흐름성을 좋게 하기 위해 용융흐름지수가 20-25g/10min(100℃ 기준)을 유지해야 하며, 탄성력을 갖추어 충돌흡수력을 높이면서 충돌시 내스크래치성을 확보하기 위해 첨가된다.In order to improve the flowability, the ethylene-octene rubber should have a melt flow index of 20-25 g / 10 min (based on 100 ° C.) .
그리고, 상기 DBNPA는 우수한 액상 항균제이고, 계지분말은 전통적인 친환경성 천연 항균제로서 계피나무 줄기를 증숙한 후 말려 분쇄한 것이며, 수근채(Oenanthe decumbens kpol)는 플라보노이드 성분을 가지고 있어 항균·항바이러스 활성이 뛰어난 천연물질로서 수근채 잎과 뿌리를 채취한 후 증숙한 다음 짜서 얻은 추출액을 사용한다.DBNPA is an excellent liquid antimicrobial agent, and the egg yolk powder is a natural eco-friendly natural antimicrobial agent, which is obtained by pulverizing cinnamon trunks after drying, and Oenanthe decumbens kpol has a flavonoid component and thus has antibacterial and antiviral activity As an excellent natural substance, extract the roots and roots of water root and boil them, then use the extract obtained from squeezing.
특히, 이들은 항균성 강화를 위해 분말 형태인 계지분말과 추출물 형태인 수근채 추출액을 먼저 1:1의 중량비로 혼합하여 걸쭉하게 만든 다음 여기에서 액상 항균제인 DBNPA를 상기 계지분말 혹은 수근채 추출액의 첨가량 보다 2배 이상 희석되게 하여 걸쭉한 상태로 유동성이 끈 액상으로 바꾸어 첨가하도록 함이 바람직하다.In order to enhance the antimicrobial activity, they prepared a mixture of powdered egg yolk powder and water extract, which is in the form of an extract, in a weight ratio of 1: 1 and then thickened. Then, the liquid antimicrobial DBNPA was added to the above- It is preferable that the liquid is diluted twice or more and added in a liquid state in a thick state in which the fluidity is changed.
그리고, 상기 포타슘실리케이트는 무기질로서 방염성을 강화시키기 위해 첨가되며, 곰팡이 서식도 차단하는 효과를 얻을 수 있다.The potassium silicate is added as an inorganic substance to enhance the flame retardancy, and the effect of blocking fungus habit can be obtained.
뿐만 아니라, 상기 아연스테아르산염은 열적 안정제로서, 내열성을 강화시키기 위해 첨가된다.In addition, the zinc stearate is added as a thermal stabilizer to enhance heat resistance.
또한, 상기 1,4-부틸렌글리콜과 규산소다(Sodium Silicates)는 필름(220)과 발포체(210) 간의 부착력을 강화시켜 박리가능성을 극소화시키기 위해 첨가된다.In addition, the 1,4-butylene glycol and sodium silicates are added to enhance the adhesion between the
다른 한편, 본 발명에서는 상기 필름(220)의 표면에 0.2-0.4mm의 두께로 방염코팅층을 더 형성할 수 있는데, 상기 방염코팅층을 형성하는 코팅액은 PVC솔(PVC Sol) 80중량%와, 첨가제 20중량%로 이루어질 수 있다.On the other hand, in the present invention, a flame retardant coating layer may be further formed on the surface of the
이 경우, 상기 첨가제는 상기 PVC솔 100중량부를 기준으로 팽창흑연 8중량부와, 수산화알루미늄 1.5중량부와, 지르코늄 4중량부와, 뮬라이트 6중량부 및 DOTP 10중량부로 이루어진다.In this case, the additive is composed of 8 parts by weight of expanded graphite, 1.5 parts by weight of aluminum hydroxide, 4 parts by weight of zirconium, 6 parts by weight of mullite and 10 parts by weight of DOTP based on 100 parts by weight of the PVC brush.
여기에서, 상기 팽창흑연(Exandable Graphite)은 그라파이트의 층상 구조를 갖기 때문에 그 층상 사이에 원자나 작은 분자를 집어 넣고 열을 가할 경우 아코디언처럼 분리가 되면서 입자가 수 백배 팽창하게 되는 현상을 이용하여 난연성, 방염성을 강화시킨다.Since the Exandable Graphite has a layered structure of graphite, when particles or small molecules are inserted between the layers and heat is applied, particles are expanded by several hundreds of times as they are separated like an accordion. , And enhances flame resistance.
그리고, 상기 수산화알루미늄은 PVC솔의 소수화를 막고 친수화를 유도하여 결합력을 높이기 위해 첨가된다.The aluminum hydroxide is added to prevent hydrophobization of the PVC brush and to induce hydrophilization to increase the binding force.
또한, 상기 지르코늄은 화재발생시 공기중의 산소와 결합하여 산화물 또는 질소화물로 된 보호피막을 형성하여 내화성, 내식성, 난연성을 증대시키기 위해 첨가된다.The zirconium is added to increase the fire resistance, the corrosion resistance and the flame retardancy by forming a protective coating made of an oxide or a nitrogen by bonding with oxygen in the air when a fire occurs.
뿐만 아니라, 상기 뮬라이트는 1500℃ 부근까지 고융점화시켜 방염성을 강화시키기 위해 첨가된다.In addition, the mullite is added to increase the melting point to about 1500 ° C to enhance the flame resistance.
아울러, 상기 DOTP는 PVC 가소제이다.In addition, the DOTP is a PVC plasticizer.
이에 더하여, 상기 방염코팅층 위해 1-2mm 두께로 쿨링스킨층이 더 형성될 수 있다.In addition, a cooling skin layer may be formed to a thickness of 1-2 mm for the flame retardant coating layer.
상기 쿨링스킨층은 아이들이 피부와 접촉할 때 시원한 느낌이 들도록 하여 체온을 떨어뜨림으로써 아이들이 좀 더 활동적으로 놀이할 수 있도록 유도하는 장점을 갖추기 위한 것이다.The cooling skin layer is designed to have a cool feeling when children contact the skin, thereby lowering the body temperature, thereby inducing children to play more actively.
이러한 쿨링스킨층은 쿨링코팅액을 스프레이 코팅하여 이루어지는데, 상기 쿨링코팅액은 PVC솔 80중량%와 쿨링성첨가물 20중량%로 이루어질 수 있으며, 쿨링성첨가물은 PVC솔 100중량부를 기준으로 자일리톨과 에리스리톨이 1:1의 중량비로 혼합된 제1혼합물 10중량부, 멘톨(Menthol)과 DL-Camphor(DL-캄파)가 1:1의 중량비로 혼합된 제2혼합물 5중량부, 빙초산(Glacial Acetic Acide) 10중량부, 황산가돌리늄 5중량부 및 소디움 메틸실리코네이트 15중량부로 이루어진다. The cooling coating layer may be formed by spray coating a cooling coating solution. The cooling coating solution may be composed of 80 wt% of a PVC sole and 20 wt% of a cooling additive. The cooling additive may include xylitol and erythritol 10 parts by weight of a first mixture mixed at a weight ratio of 1: 1, 5 parts by weight of a second mixture in which Menthol and DL-Camphor (DL-Kamp) were mixed at a weight ratio of 1: 1, Glacial Acetic Acid, 10 parts by weight, gadolinium sulfate 5 parts by weight and sodium methyl silicate 15 parts by weight.
이때, 상기 자일리톨과 에리스리톨은 당알코올로 수분과 반응하여 흡열반응을 일으켜 주변의 열을 빼앗아 쿨링성을 느끼게 하며, 또한 피부와 접촉시에는 강한 청량감(시원한 느낌)을 주므로 이러한 청량감 확보와 흡열에 따른 쿨링성 확보를 위해 첨가된다.At this time, the xylitol and erythritol react with moisture with sugar alcohol to cause an endothermic reaction, thereby depriving the surrounding heat of cooling, and giving a strong cooling sensation (cool feeling) upon contact with the skin. It is added for securing the cooling property.
아울러, 상기 멘톨(Menthol)과 DL-Camphor(DL-캄파)는 혈관을 확장시켜 시원한 느낌을 주는 청량감을 강화시킴으로써 쿨링기능을 증대시키기 위해 첨가된다.In addition, Menthol and DL-Camphor (DL-Camphor) are added to enhance the cooling function by strengthening the cooling sensation that extends the blood vessels and gives a cool feeling.
뿐만 아니라, 상기 빙초산은 어느점이 14.5℃ 이상으로서 상온에서도 어는 특성이 있어 쿨링성을 강화시킨다.In addition, the glacial acetic acid has a characteristic of freezing at 14.5 DEG C or higher at room temperature, thereby enhancing the cooling property.
아울러, 상기 황산가돌리늄은 희토류 원소인 가돌리늄(Gd)의 황산화물로서, 가돌리늄은 주기율표 3족에 속하는 희토류(稀土類) 전이금속이며, 연성(延性)이 있는 은백색의 원소로 산소·물과 서서히 반응하고, 17℃ 이하에서는 강자성(强磁性)을, 아주 낮은 온도에서는 초전도성(超傳導性)을 띤다. 이러한 가돌리늄의 황산화물은 자기냉각특성이 있어 쿨링성을 강화시킨다.The gadolinium sulfate is a rare earth transition metal belonging to Group 3 of the periodic table. It is a silver-white element having ductility and gradually reacts with oxygen and water. Ferromagnetism at 17 ° C or less, and superconductivity at a very low temperature. These gadolinium sulfates have self-cooling properties, which enhances cooling.
그리고, 상기 소디움 메틸실리코네이트는 강한 발수 기능을 위해 첨가되어 통풍성을 강화시키는데 유용하다.And, the sodium methylsiliconate is added for strong water repellency and is useful for enhancing ventilation.
이하, 실시예에 대하여 설명한다.Hereinafter, examples will be described.
[실시예 1][Example 1]
본 발명에 따라 발포체와 그 외피를 이루는 필름으로 이루어진 쿠션부재를 제조하되, 발포체는 2cm의 길이를 갖는 글래스파이버 14중량%와, 세스키탄산나트륨 2.5중량%와, 모노글리세라이드 4.5중량%와, DBNPA 8.5중량%와, 인슐래드 분말 6.5중량%와, TOTM 2.5중량% 및 나머지 폴리스티렌수지로 이루어진 혼합물을 발포 성형하여 제조하였으며; 필름은 에틸렌-옥텐 러버(EOR) 80중량%와, 항균방염제 20중량%로 구성하되, 상기 항균방염제는 상기 에틸렌-옥텐 러버 100중량부를 기준으로 DBNPA와 계지분말과 수근채 추출액을 2:1:1의 중량비로 혼합한 항균제혼합물 25중량부와, 포타슘실리케이트 20중량부와, 아연스테아르산염 5중량부와, 1,4-부틸렌글리콜 3.5중량부 및 규산소다(Sodium Silicates) 5중량부로 조성하여 만든 것을 사용하였다.According to the present invention, a cushioning member made of a foam and a film constituting its shell is produced, wherein the foam comprises 14 wt% of glass fiber having a length of 2 cm, 2.5 wt% of sodium sesquicarbonate, 4.5 wt% of monoglyceride, DBNPA 8.5% by weight, 6.5% by weight of insulin powder, 2.5% by weight of TOTM and the balance polystyrene resin; The film is composed of 80% by weight of ethylene-octene rubber (EOR) and 20% by weight of an antibacterial flame retardant, wherein the antibacterial flame retardant is prepared by mixing DBNPA, 25 parts by weight of a mixture of antimicrobial agents mixed at a weight ratio of 1: 1, 20 parts by weight of potassium silicate, 5 parts by weight of zinc stearate, 3.5 parts by weight of 1,4-butylene glycol and 5 parts by weight of sodium silicates Were used.
[실시예 2][Example 2]
실시예 1과 동일하게 하되, 필름 표면에 0.3mm의 두께로 방염코팅층을 더 형성하되, 상기 방염코팅층은 PVC솔(PVC Sol) 80중량%와, 첨가제 20중량%로 이루어진 코팅액을 스프레이 코팅하여 형성하였다.A flame retardant coating layer was formed on the surface of the film in the same manner as in Example 1 except that the flame retardant coating layer was formed by spray coating a coating solution composed of 80% by weight of PVC sol and 20% Respectively.
이때, 첨가제는 상기 PVC솔 100중량부를 기준으로 팽창흑연 8중량부와, 수산화알루미늄 1.5중량부와, 지르코늄 4중량부와, 뮬라이트 6중량부 및 DOTP 10중량부로 조성하였다.The additive was composed of 8 parts by weight of expanded graphite, 1.5 parts by weight of aluminum hydroxide, 4 parts by weight of zirconium, 6 parts by weight of mullite and 10 parts by weight of DOTP based on 100 parts by weight of the PVC brush.
[실시예 3][Example 3]
실시예 2와 동일하게 하되, 방염코팅층 위에 1.5mm 두께로 쿨링스킨층을 더 형성하되, 상기 쿨링스킨층은 PVC솔 80중량%와, 쿨링성첨가물 20중량%로 이루어진 쿨링성코팅액을 스프레이 코팅하여 형성하였다.A cooling skin layer having a thickness of 1.5 mm was formed on the flame retardant coating layer in the same manner as in Example 2. The cooling skin layer was formed by spray coating a cooling coating solution composed of 80% by weight of a PVC brush and 20% by weight of a cooling additive .
이때, 쿨링성첨가물은 PVC솔 100중량부를 기준으로 자일리톨과 에리스리톨이 1:1의 중량비로 혼합된 제1혼합물 10중량부와, 멘톨(Menthol)과 DL-Camphor(DL-캄파)가 1:1의 중량비로 혼합된 제2혼합물 5중량부와, 빙초산(Glacial Acetic Acide) 10중량부와, 황산가돌리늄 5중량부 및 소디움 메틸실리코네이트 15중량부로 조성하였다. The cooling additive was prepared by mixing 10 parts by weight of a first mixture of xylitol and erythritol in a weight ratio of 1: 1 based on 100 parts by weight of a PVC brush, 10 parts by weight of menthol and DL-Camphor (DL-camp) , 5 parts by weight of a second mixture mixed with 10 parts by weight of glacial acetic acid, 5 parts by weight of gadolinium sulfate and 15 parts by weight of sodium methyl silicate.
그런 다음, [실시예 1,2,3]에 대해 유해물질 용출실험을 통해 중금속의 용출이 있는지 확인하였으나, [실시예 1,2,3] 모두 중금속 용출이 없었다.Then, it was confirmed that there was leaching of heavy metals through experiments for dissolving toxic substances in [Examples 1, 2, and 3], but no heavy metal elution was observed in all of [Examples 1, 2, and 3].
또한, 방염성을 확인하기 위해 [실시예 1,2,3]에 대해 난연성 시험방법(KS F2271)에 따라 방염성을 테스트한 결과, 양자 모두 준불연성으로 방염성이 우수한 것으로 판정되었다.Further, in order to confirm the flame retardancy, the flame resistance was tested according to the flame resistance test method (KS F2271) for [Examples 1, 2 and 3].
아울러, 항균성을 테스트하기 위해 [실시예 1,2,3]의 쿠션부재 표면의 동일 부위에 곰팡이 균주를 각각 1㎖씩 떨어뜨린 후 5일, 10일, 15일간 자연 상태로 방치하여 항균 활성여부를 체크하였다.To test the antimicrobial activity, 1 ml of each of the fungal strains was dropped on the same surface of the cushion member of Examples 1, 2, and 3, and allowed to stand for 5 days, 10 days, and 15 days in a natural state. .
이때, 시험방법은 ASTMG-21에 따랐고, 활성여부는 배양된 균주의 성장 유무로 확인하였으며, 시험한 곰팡이 균주는 아스퍼질러스 나이거(Aspergillus niger) ATCC 9642, 페니실리움 피노필럼(Penicillium pinophilum) ATCC 11797, 캐토미움 글로보솜(Chaetomium globosom) ATCC 6205 였다.At this time, the test method was according to ASTMG-21, and the activity was confirmed by the presence or absence of the growth of the cultured strain. The tested fungus strains were Aspergillus niger ATCC 9642, Penicillium pinophilum, ATCC 11797, Chaetomium globosom ATCC 6205.
시험 결과, 5일, 10일, 15일간 시료 모두에서 균주의 성장이 관찰되지 않았다. 이를 통해, 항균성(항곰팡이성)이 있는 것으로 확인되었다.As a result of the test, no growth of the strain was observed in all the samples for 5 days, 10 days and 15 days. As a result, it was confirmed that there was antibacterial (antifungal) property.
뿐만 아니라, [실시예 3]의 쿨링성을 평가하기 위해 열풍에 의해 30℃로 유지되는 항습실에 [실시예 3]의 시료를 투입한 상태에서 열풍을 끄고 50분간 유지되게 하여 자연 냉각시켰다.In addition, in order to evaluate the cooling performance of [Example 3], the sample of Example 3 was put in a humidity chamber maintained at 30 占 폚 by hot air, the hot air was turned off and kept for 50 minutes and naturally cooled.
그런 다음, 적외선 온도계를 시료 표면에 조사하여 쿨링 여부를 확인하였다.Then, an infrared thermometer was irradiated on the surface of the sample to confirm whether it was cooled.
확인결과 10분 경과시 시료 표면온도는 26.8℃였고, 20분 경과시에는 24.3℃였으며, 30분 경과시에는 22.1℃였다.After 10 minutes, the surface temperature of the sample was 26.8 ℃, and it was 24.3 ℃ for 20 minutes and 22.1 ℃ for 30 minutes.
이를 통해, 시간이 경과할수록 온도가 떨어지면서 쿨링기능을 발현함을 확인할 수 있었다.As a result, it was confirmed that the cooling function was exhibited as the temperature dropped with time.
100: 기둥
200: 쿠션부재
210: 발포체
220: 필름100: Column
200: Cushion member
210: foam
220: Film
Claims (4)
상기 발포체(210)는 완충 흡수력을 가지면서 내열성, 내화성을 높여 방염성이 강화되도록 2-3cm의 길이를 갖는 글래스파이버 14중량%와, 세스키탄산나트륨(Sodium Sesqui Carbonate) 2.5중량%와, 모노글리세라이드(monoglyceride) 4.5중량%와, DBNPA(2,2-Dibromo-3-nitrilopropionamide) 8.5중량%와, 인슐래드 분말(Insuladd powder) 6.5중량%와, TOTM(Trioctyl Trimellitate) 2.5중량% 및 나머지 폴리스티렌수지로 이루어진 혼합물을 발포 성형하여 제조된 것을 특징으로 하는 실내놀이터용 기둥쿠션재.
A cushioning member (200) for wrapping a column (100) installed on an indoor playground and performing a cushioning function. The cushioning member (200) comprises a foam body (210) And a film (220) formed on the upper surface of the upper portion of the cushioning material.
The foamed body 210 is composed of 14% by weight of glass fiber having a length of 2-3 cm, 2.5% by weight of sodium sesqui carbonate, 2.5% by weight of sodium sesquicarbonate, 4.5% by weight of monoglyceride, 8.5% by weight of 2,2-Dibromo-3-nitrilopropionamide, 6.5% by weight of insuladd powder, 2.5% by weight of TOTM (Trioctyl trimellitate) And the mixture is foam-molded.
상기 필름(220)은 표면 보호 및 항균성과 방염성을 강화시키면서 유해물질 용출 차단을 위해 에틸렌-옥텐 러버(EOR) 80중량%와, 항균방염제 20중량%로 이루어진 수지조성물을 필름 형태로 성형한 것을 사용하되,
상기 항균방염제는 상기 에틸렌-옥텐 러버 100중량부를 기준으로 DBNPA(2,2-Dibromo-3-nitrilopropionamide)와 계지분말과 수근채(Oenanthe decumbens kpol) 추출액을 2:1:1의 중량비로 혼합한 항균제혼합물 25중량부와, 포타슘실리케이트 20중량부와, 아연스테아르산염 5중량부와, 1,4-부틸렌글리콜 3.5중량부 및 규산소다(Sodium Silicates) 5중량부로 이루어지는 것을 특징으로 하는 실내놀이터용 기둥쿠션재.
The method according to claim 1,
The film 220 is formed by molding a resin composition consisting of 80% by weight of ethylene-octene rubber (EOR) and 20% by weight of an antibacterial flame retardant in the form of a film to enhance surface protection, antibacterial properties and flame retardancy, However,
The antimicrobial flame retardant is prepared by mixing DBNPA (2,2-Dibromo-3-nitrilopropionamide), an adhesive powder and an extract of Oenanthe decumbens kpol at a weight ratio of 2: 1: 1 on the basis of 100 parts by weight of the ethylene- 25 parts by weight of the mixture, 20 parts by weight of potassium silicate, 5 parts by weight of zinc stearate, 3.5 parts by weight of 1,4-butylene glycol and 5 parts by weight of sodium silicates. Cushioning material.
상기 에틸렌-옥텐 러버는 용융흐름지수가 20-25g/10min(100℃ 기준)인 것을 특징으로 하는 실내놀이터용 기둥쿠션재.
The method of claim 2,
Wherein the ethylene-octene rubber has a melt flow index of 20-25 g / 10 min (at 100 占 폚).
상기 필름(220)의 표면에는 코팅액이 스프레이되어 0.2-0.4mm의 두께로 방염코팅층이 더 형성되며, 상기 방염코팅층을 형성하는 코팅액은 PVC솔(PVC Sol) 80중량%와, 첨가제 20중량%로 이루어지되, 상기 첨가제는 상기 PVC솔 100중량부를 기준으로 팽창흑연 8중량부와, 수산화알루미늄 1.5중량부와, 지르코늄 4중량부와, 뮬라이트 6중량부 및 DOTP 10중량부로 이루어진 것을 특징으로 하는 실내놀이터용 기둥쿠션재.
The method of claim 2,
A coating solution is sprayed on the surface of the film 220 to form a flame retardant coating layer having a thickness of 0.2-0.4 mm. The coating solution for forming the flame retardant coating layer is composed of 80% by weight of PVC sol and 20% Wherein the additive comprises 8 parts by weight of expanded graphite, 1.5 parts by weight of aluminum hydroxide, 4 parts by weight of zirconium, 6 parts by weight of mullite and 10 parts by weight of DOTP based on 100 parts by weight of the PVC brush. Column cushioning material.