KR101773055B1 - Bullet proof fabric preventing radiation of heat and manufacturing method thereof - Google Patents

Bullet proof fabric preventing radiation of heat and manufacturing method thereof Download PDF

Info

Publication number
KR101773055B1
KR101773055B1 KR1020140071164A KR20140071164A KR101773055B1 KR 101773055 B1 KR101773055 B1 KR 101773055B1 KR 1020140071164 A KR1020140071164 A KR 1020140071164A KR 20140071164 A KR20140071164 A KR 20140071164A KR 101773055 B1 KR101773055 B1 KR 101773055B1
Authority
KR
South Korea
Prior art keywords
heat
fiber
layer
present
manufacturing
Prior art date
Application number
KR1020140071164A
Other languages
Korean (ko)
Other versions
KR20150142403A (en
Inventor
정기수
나주연
Original Assignee
한국생산기술연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국생산기술연구원 filed Critical 한국생산기술연구원
Priority to KR1020140071164A priority Critical patent/KR101773055B1/en
Publication of KR20150142403A publication Critical patent/KR20150142403A/en
Application granted granted Critical
Publication of KR101773055B1 publication Critical patent/KR101773055B1/en

Abstract

본 발명은 방탄 섬유의 직조에 의해 형성되는 방탄 섬유층 및 방탄 섬유층 표면에 형성되는 방열층을 포함하는 방열 가능한 방탄 섬유 및 이를 제조하는 방법에 관한 것이다. The present invention relates to a heat-resistant anti-fogging fiber including a protective layer formed by woven fabric of anti-fogging fibers and a heat-releasing layer formed on the surface of the anti-fogging fabric layer, and a method of manufacturing the same.

Description

방열 가능한 방탄 섬유 및 이를 제조하는 방법 {BULLET PROOF FABRIC PREVENTING RADIATION OF HEAT AND MANUFACTURING METHOD THEREOF}FIELD OF THE INVENTION [0001] The present invention relates to a bulletproof fiber,

본 발명은 방열 가능한 방탄 섬유 및 이를 제조하는 방법에 관한 것이다.
The present invention relates to a heat-resistant anti-armor fiber and a method of manufacturing the same.

방탄복이란, 방탄 가능한 섬유를 직조하여 의복 형태로 만든 것으로, 총탄으로부터 착용자를 보호할 수 있다. 이러한 방탄복은 무게가 가벼우면서도, 사격 및 열충격에 대한 저항 능력이 우수하여 이와 같은 외부 충격 시 구조적 변형이 적어야 하는 특징을 가지고 있다. 따라서 고강력, 고탄성, 고내열, 저비중의 섬유가 사용되고 있다. A body armor is a garment made by weaving an armor-resistant fiber, which protects the wearer from bullets. Such a Kevlar is light in weight, has excellent resistance to shooting and thermal shock, and has a characteristic that structural deformation is small in such an external impact. Therefore, high strength, high elasticity, high heat resistance and low specific gravity fibers are used.

한편, 겨울과 같이 외부의 환경이 극저온인 경우, 착용자들은 보온을 위하여 별도의 의복을 추가적으로 갖추어야 한다. 이러한 경우, 착용자들은 두터운 의복의 착용으로 인해 움직임이 둔해지고, 이로 인해 위험에 쉽게 노출될 수 있다. On the other hand, if the outside environment is extremely low, such as winter, the wearer should additionally provide separate garments for keeping warm. In such a case, wearers may feel dulled by wear of thick clothing, which can easily expose them to danger.

따라서, 착용자의 체온을 유지할 수 있으면서도, 방탄 작용이 가능한 섬유의 개발이 필요한 실정이다.
Therefore, it is necessary to develop a fiber capable of maintaining the body temperature of the wearer while being able to perform a bulletproof operation.

본 발명의 목적은 사용자의 피부로부터 발생된 열이 외부로 방출되는 것을 방지할 수 있는 방열 가능한 방탄 섬유 및 이를 제조하는 방법을 제공하는 것이다. An object of the present invention is to provide a heat-resistant anti-fogging fiber capable of preventing heat generated from a user's skin from being released to the outside, and a method of manufacturing the same.

또한, 본 발명이 해결하고자 하는 기술적 과제는 이상에서 언급한 기술적 과제로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are not intended to limit the invention to the precise form disclosed. It can be understood.

상기 목적은, 본 발명의 일 실시예에 따라, 방탄 소재용 실의 직조에 의해 형성되는 방탄 섬유층 및 방탄 섬유층 표면에 형성되는 방열층을 포함하는 방열 가능한 방탄 섬유에 의해 제공될 수 있다. The above object can be provided by a heat-resistant armor-proof fiber including a ballistic fiber layer formed by weaving a yarn for a bulletproof material and a heat-radiating layer formed on the surface of the ballistic-resistant fiber layer, according to an embodiment of the present invention.

방열층은, 방탄 소재용 실의 표면에 코팅되는 방열 소재에 의해 형성될 수 있다. The heat-radiating layer may be formed by a heat-radiating material coated on the surface of the room for the bulletproof material.

이때, 방열 소재는 알루미늄을 포함할 수 있다. At this time, the heat dissipation material may include aluminum.

한편, 방열층은, 방탄 섬유층의 양면에 형성될 수 있다. On the other hand, the heat-radiating layer can be formed on both sides of the anti-fogging fiber layer.

한편, 상기 목적은, 본 발명의 다른 실시예에 따라, 방탄 소재용 실을 직조하여 방탄 섬유층을 형성하고, 방탄 섬유층 표면에 형성되는 방열층을 포함하는 방열 가능한 방탄 섬유의 제조 방법에 의해 제공될 수 있다. On the other hand, the above object can be achieved by a method for producing a heat-resistant armored fiber including a heat-resistant layer formed on the surface of a ballistic-resistant fibrous layer by forming a ballistic-resistant fiber layer by woven yarn for a ballistic material according to another embodiment of the present invention .

방열층은, 방탄 섬유층 상에 방열 소재가 적층되어 형성되거나, 혹은 표면에 방열 소재가 코팅된 방탄 소재용 실의 직조에 의해 형성될 수 있다. The heat-radiating layer may be formed by laminating a heat-radiating material on the anti-fogging fiber layer or by weaving a room for a bulletproof material coated with a heat-radiating material on the surface.

이때, 방열층은, 방열 소재는 알루미늄을 포함할 수 있다. At this time, the heat-radiating material may include aluminum.

한편, 방열층은, 방탄 섬유층의 양면에 형성될 수 있다.
On the other hand, the heat-radiating layer can be formed on both sides of the anti-fogging fiber layer.

본 발명에 의하면, 사용자의 피부로부터 발생된 열이 외부로 방출되는 것을 방지할 수 있는 방열 가능한 방탄 섬유 및 이를 제조하는 방법을 제공할 수 있게 된다.
According to the present invention, it is possible to provide a heat-resistant anti-fogging fiber capable of preventing heat generated from a user's skin from being emitted to the outside, and a method of manufacturing the same.

도 1은 본 발명의 일 실시예에 따른 방열 가능한 방탄 섬유를 나타낸 도면이다.
도 2는 본 발명의 다른 실시예에 따른 방열 가능한 방탄 섬유를 나타낸 도면이다. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view showing a heat-resistant anti-armor fiber according to an embodiment of the present invention. FIG.
Fig. 2 is a view showing a heat-resistant anti-armor fiber according to another embodiment of the present invention.

본 발명은 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.BRIEF DESCRIPTION OF THE DRAWINGS The present invention is capable of various modifications and various embodiments, and specific embodiments are illustrated in the drawings and described in detail in the detailed description. It is to be understood, however, that the invention is not to be limited to the specific embodiments, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.

도 1은 본 발명의 일 실시예에 따른 방열 가능한 방탄 섬유(10)를 나타낸 도면이며, 도 2는 본 발명의 다른 실시예에 따른 방열 가능한 방탄 섬유(10)를 나타낸 도면이다. FIG. 1 is a view showing a heat-resistant anti-armor fiber 10 according to an embodiment of the present invention, and FIG. 2 is a view showing a heat-resistant anti-armor fiber 10 according to another embodiment of the present invention.

도 1에 도시된 것과 같이, 본 발명의 일 실시예에 따른 방열 가능한 방탄 섬유(10)는 방탄 섬유층(11) 및 방열층(12)을 포함할 수 있다. As shown in FIG. 1, the heat-resistant anti-armor fiber 10 according to an embodiment of the present invention may include the anti-fogging fiber layer 11 and the heat radiation layer 12.

방탄 섬유층(11)은 방탄 소재용 실의 직조에 의해 형성된다. The armor-proof fibrous layer 11 is formed by weaving yarn for a bulletproof material.

본 실시예에 따른 방탄 소재용 실은 파라 아라미드 또는 고강도 폴리에틸렌과 같은 고분자로 이루어지며, 이러한 고분자 이외에도 방탄 소재용 실로 사용될 수 있는 것이라면 어떠한 것이라도 사용될 수 있다.The yarn for a bulletproof material according to the present embodiment is made of a polymer such as para-aramid or high-strength polyethylene, and any yarn can be used as long as it can be used as a thread for a bulletproof material in addition to such a polymer.

방열층(12)은 본 실시예에 따른 방탄 섬유(10)에 의해 제조된 방탄복을 착용한 착용자의 피부로부터 발생되는 열이 외부로 방출되는 것을 방지하기 위하여 방탄 섬유층(11)의 표면에 형성된다. The heat-radiating layer 12 is formed on the surface of the anti-fogging fiber layer 11 in order to prevent heat generated from the skin of the wearer wearing the body armor fabricated by the anti-fogging fiber 10 according to the present embodiment from being discharged to the outside .

이때, 본 실시예에 따른 방열층(12)은, 도 1에 도시된 것과 같이, 방탄 섬유층(11)을 이루는 방탄 소재용 실의 표면에 코팅된 방열 소재에 의해 형성될 수 있다. At this time, the heat-radiating layer 12 according to the present embodiment may be formed by a heat-radiating material coated on the surface of the room for the bulletproof material, which constitutes the bulletproof fiber layer 11, as shown in Fig.

본 실시예에 따라, 방탄 소재용 실의 표면에 코팅되는 방열 소재는, 열의 반사 기능이 우수한 알루미늄을 포함할 수 있다. According to the present embodiment, the heat-radiating material coated on the surface of the room for the bulletproof material may include aluminum having excellent heat reflecting function.

이와 같이 방열 소재가 코팅된 방탄 소재용 실의 직조에 의해 방탄 섬유(10)가 제공될 수 있기 때문에, 본 실시예에 따르면, 방탄 섬유층(11)의 양면에 방열층(12)이 형성된 방탄 섬유(10)를 제공할 수 있게 된다. Since the armor fiber 10 can be provided by woven yarn for a bulletproof material coated with a heat dissipation material as described above, according to this embodiment, the bulletproof fiber material 11 having the heat radiation layer 12 formed on both surfaces thereof (10).

이상에서는 본 발명의 일 실시예에 따른 방열 가능한 방탄 섬유(10)에 대하여 설명하였다. 본 발명에 따른 방탄 섬유(10)에 의하면, 착용자의 피부로부터 발생되는 열이 알루미늄을 포함하여 형성된 방열층(12)에 의하여 반사됨으로써 외부로의 열의 방출이 방지될 수 있는 방열 가능한 방탄 섬유(10)를 제공할 수 있게 된다. The heat-resistant anti-armor fiber 10 according to the embodiment of the present invention has been described above. According to the anti-armor fiber 10 of the present invention, the heat generated from the skin of the wearer is reflected by the heat-radiating layer 12 including aluminum, so that the heat- ). ≪ / RTI >

한편, 이하에서는 본 발명의 다른 실시예에 따른 방열 가능한 방탄 섬유의 제조 방법에 대해 설명하기로 한다. Hereinafter, a method of manufacturing a heat-resistant armored fiber according to another embodiment of the present invention will be described.

본 실시예에 따른 방열 가능한 방탄 섬유의 제조 방법은, 방탄 소재용 실을 직조하여 방탄 섬유층(11)을 형성하고, 방탄 섬유층(11) 표면에 형성되는 방열층(12)을 포함한다. The method for manufacturing heat-resistant armor-resistant fibers according to the present embodiment includes a heat-radiating layer 12 formed on the surface of the armor-fiber layer 11 by woven a yarn for a bulletproof material to form a bulletproof fiber layer 11.

방탄 섬유층(11)은, 앞서 설명한 것과 같이, 방탄 소재용 실의 직조에 의해 형성되며, 본 실시예에 따른 방탄 소재용 실은 파라 아라미드 또는 고강도 폴리에틸렌과 같은 고분자로 이루어지며, 이러한 고분자 이외에도 방탄 소재용 실로 사용될 수 있는 것이라면 어떠한 것이라도 사용될 수 있다.As described above, the armor fiber layer 11 is formed by weaving a yarn for a bulletproof material, and the yarn for a bulletproof material according to this embodiment is made of a polymer such as para aramid or high strength polyethylene. In addition to such a polymer, Anything that can actually be used can be used.

방열층(12) 역시 앞서 설명한 것과 같이, 본 실시예에 따른 방탄 섬유(10)에 의해 제조된 방탄복을 착용한 착용자의 피부로부터 발생되는 열이 외부로 방출되는 것을 방지하기 위하여 방탄 섬유층(11)의 표면에 형성된다.As described above, the heat-radiating layer 12 also has a bulletproof fiber layer 11 to prevent heat generated from the skin of the wearer wearing the bulletproof fabric manufactured by the bulletproof fiber 10 according to the present embodiment from being discharged to the outside, As shown in FIG.

이때 본 실시예에 따른 방열층(12)은, 도 1에 도시된 것과 같이, 표면에 방열 소재가 코팅된 방탄 소재용 실의 직조에 의해 형성될 수 있다. At this time, the heat-radiating layer 12 according to the present embodiment may be formed by weaving a room for a bulletproof material having a surface coated with a heat-radiating material, as shown in Fig.

한편, 본 실시예의 변형예에 따른 방열층(12)은, 도 2에 도시된 것과 같이, 방탄 섬유층(11) 상에 방열 소재가 적층되어 형성될 수 있다. On the other hand, the heat-radiating layer 12 according to the modification of this embodiment may be formed by laminating a heat-radiating material on the anti-fogging fiber layer 11, as shown in Fig.

이때, 본 실시예의 변형예에 따르면, 방열 소재는 필름 형태로 마련되어 방탄 섬유층(11) 상에 부착됨으로써 방열층(12)을 형성할 수 있으며, 혹은 분말 형태로 제작되어 방탄 섬유층(11) 상에 증착됨으로써 방열층(12)을 형성할 수 있을 것이다. 또한, 페이스트 형태의 방열 소재가 방탄 섬유층(11) 상에 도포되어 방열층(12)을 형성할 수 있을 것이다. According to a modification of this embodiment, the heat-radiating material may be provided in the form of a film and attached to the anti-fogging fiber layer 11 to form the heat-releasing layer 12, or may be formed in powder form, The heat dissipation layer 12 can be formed by vapor deposition. In addition, a heat-dissipating material in the form of a paste may be coated on the anti-fogging fiber layer 11 to form the heat-radiating layer 12.

이 외에도 다양한 방법으로 도 2에 도시된 것과 같이, 방열층(12)이 적층된 방탄 섬유(10)를 제공될 수 있다. 따라서, 본 발명의 실시 범위는 방열 소재의 형태 및 방열 소재를 방탄 섬유층(11)에 적층하는 방법에 의해서는 제한되지 않으며, 앞서 서술되지 않은 방열 소재의 형태 및 이를 방탄 섬유층(11) 상에 적층하는 방법이라 할지라도 방탄 섬유층(11)의 표면 상에 형성된 방열층(12)을 포함하는 방탄 섬유의 제조 방법에 관해서는 본 발명의 권리범위가 미칠 수 있을 것이다. In addition, as shown in Fig. 2 in various ways, the anti-fogging fiber 10 in which the heat-radiating layer 12 is laminated can be provided. Therefore, the scope of the present invention is not limited by the shape of the heat-radiating material and the method of laminating the heat-radiating material on the anti-fogging fiber layer 11, and the shape of the heat- The method of manufacturing the armored fiber including the heat-radiating layer 12 formed on the surface of the anti-fogging fiber layer 11 may have the scope of the present invention.

이때, 본 실시예에 따른 방열층(12)은 열을 반사하는 성질이 우수한 알루미늄을 포함하는 방열 소재에 의해 형성될 수 있다. At this time, the heat dissipation layer 12 according to the present embodiment may be formed of a heat dissipation material including aluminum, which is excellent in heat reflecting properties.

한편, 본 실시예에 따른 방열층(12)은 방탄 섬유층(11)의 양면에 형성될 수 있다. 도 1에 도시된 것과 같이, 표면 상에 방열 소재가 코팅된 방탄 소재용 실의 직조에 의해 방탄 섬유(10)의 경우, 방탄 섬유층(11)의 양면에 자연스럽게 방열층(12)이 형성될 수 있다. 또한, 도 2에 도시된 실시예의 변형예로써, 도 2에 도시되지는 않았지만, 도 2에서 방탄 섬유층(11)의 일면에만 방열층(12)이, 방탄 섬유층(11)의 타면에도 형성될 수 있다. On the other hand, the heat-radiating layer 12 according to this embodiment can be formed on both sides of the anti- As shown in Fig. 1, in the case of the anti-armor fiber 10, the heat radiation layer 12 can be formed naturally on both sides of the anti-fogging fiber layer 11 by woven yarn for the anti- have. 2, the heat dissipation layer 12 may be formed on the other side of the anti-fouling fibrous layer 11 only on one side of the anti-fog fibrous layer 11 in Fig. 2 (not shown in Fig. 2) have.

이상에서는 본 발명의 다른 실시예에 따른 방열 가능한 방탄 섬유의 제조 방법에 대해 설명하였다. 본 발명에 따른 방탄 섬유의 제조 방법에 의하면, 착용자의 피부로부터 발생되는 열이 알루미늄을 포함하여 형성된 방열층(12)에 의하여 반사됨으로써 외부로의 열의 방출이 방지될 수 있는 방열 가능한 방탄 섬유(10)를 제공할 수 있게 된다. The method of manufacturing the heat-resistant armored fiber according to another embodiment of the present invention has been described above. According to the method for manufacturing the armored fiber according to the present invention, the heat generated from the wearer's skin is reflected by the heat-radiating layer 12 including aluminum, so that the heat- ). ≪ / RTI >

앞에서, 본 발명의 특정한 실시예가 설명되고 도시되었지만 본 발명은 기재된 실시예에 한정되는 것이 아니고, 본 발명의 사상 및 범위를 벗어나지 않고 다양하게 수정 및 변형할 수 있음은 이 기술의 분야에서 통상의 지식을 가진 자에게 자명한 일이다. 따라서, 그러한 수정예 또는 변형예들은 본 발명의 기술적 사상이나 관점으로부터 개별적으로 이해되어서는 안되며, 변형된 실시예들은 본 발명의 특허청구범위에 속한다 하여야 할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It is obvious to those who have. Accordingly, it should be understood that such modifications or alterations should not be understood individually from the technical spirit and viewpoint of the present invention, and that modified embodiments fall within the scope of the claims of the present invention.

10: 방탄 섬유
11: 방탄 섬유층
12: 방열층10: Bulletproof fiber
11:
12:

Claims (9)

방탄 소재용 실을 직조하여 방탄 섬유층을 형성하고,
상기 방탄 섬유층 표면에 형성되는 방열층을 포함하며,
상기 방열층은 알루미늄을 포함하는 페이스트를 상기 방탄 섬유층 상에 도포하여 형성되는,
방열 가능한 방탄 섬유의 제조 방법.
A yarn for a bulletproof material is woven to form a bulletproof fiber layer,
And a heat dissipation layer formed on the surface of the anti-
Wherein the heat dissipation layer is formed by applying a paste containing aluminum on the anti-
Method of manufacturing heat - resistant armored fiber.
제1항에 있어서,
상기 방열층은,
상기 방탄 섬유층의 양면에 형성되는 것을 특징으로 하는,
방열 가능한 방탄 섬유의 제조 방법.
The method according to claim 1,
The heat-
Wherein the protective layer is formed on both sides of the anti-
Method of manufacturing heat - resistant armored fiber.
삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete
KR1020140071164A 2014-06-12 2014-06-12 Bullet proof fabric preventing radiation of heat and manufacturing method thereof KR101773055B1 (en)