KR101763370B1 - Cathode Active Material and Lithium Secondary Battery Comprising the Same and Method of Preparing the Same - Google Patents
Cathode Active Material and Lithium Secondary Battery Comprising the Same and Method of Preparing the Same Download PDFInfo
- Publication number
- KR101763370B1 KR101763370B1 KR1020160130043A KR20160130043A KR101763370B1 KR 101763370 B1 KR101763370 B1 KR 101763370B1 KR 1020160130043 A KR1020160130043 A KR 1020160130043A KR 20160130043 A KR20160130043 A KR 20160130043A KR 101763370 B1 KR101763370 B1 KR 101763370B1
- Authority
- KR
- South Korea
- Prior art keywords
- active material
- secondary battery
- lithium
- cathode active
- zro
- Prior art date
Abstract
본 발명은 양극 활물질 및 이를 포함하는 리튬 이차전지와 이의 제조방법으로서,
(a) 하기 화학식 1의 리튬 금속 산화물을 제조하는 단계; Li1+zNiaMnbCo1-(a+b)O2 (1)
(상기 식에서, 0≤z≤0.1, 0.1≤a≤0.8, 0.1≤b≤0.8 및 a+b<1이다.)
(b) 상기 리튬 금속 산화물과 지르코늄 및 불소 함유 전구체를 건식 혼합하는 단계; 및
(c) 단계(b)의 건식 혼합 후 열처리하여 지르코늄 및 불소 함유 전구체를 ZrO2로 변환시키고 산소(O) 음이온의 일부가 F로 치환되는 단계;
를 포함하는 것을 특징으로 하는, ZrO2 및 F가 코팅된 양극 활물질의 제조 방법 및 이를 사용하여 제조되는 양극 활물질을 제공한다.The present invention relates to a cathode active material, a lithium secondary battery comprising the same,
(a) preparing a lithium metal oxide represented by the following formula (1); Li 1 + z Ni a Mn b Co 1 - (a + b) O 2 (1)
(Where 0? Z? 0.1, 0.1? A? 0.8, 0.1? B? 0.8 and a + b <1).
(b) dry-blending the lithium metal oxide with zirconium and a fluorine-containing precursor; And
(c) heat-treating the zirconium and fluorine-containing precursor to ZrO 2 and converting a portion of the oxygen (O) anion to F;
The present invention also provides a method of producing a cathode active material coated with ZrO 2 and F and a cathode active material manufactured using the same.
Description
본 발명은 양극 활물질 및 이를 포함하는 리튬 이차전지와 이의 제조방법에 관한 것으로, 더욱 상세하게는, 소정의 리튬 금속 산화물을 제조하는 단계, 상기 리튬 금속 산화물과 지르코늄 및 불소 함유 전구체를 건식 혼합하는 단계, 및 이러한 건식 혼합 후 열처리하여 지르코늄 및 불소 함유 전구체를 ZrO2로 변환시키고 산소(O) 음이온의 일부가 F로 치환되는 단계를 포함하는 것을 특징으로 하는, ZrO2 및 F가 코팅된 양극 활물질의 제조 방법에 관한 것이다.The present invention relates to a cathode active material, a lithium secondary battery comprising the same, and a method of manufacturing the same. More particularly, the present invention relates to a lithium secondary battery comprising the steps of: preparing a predetermined lithium metal oxide; dry mixing the lithium metal oxide with zirconium and a fluorine- And a step of heat-treating the zirconium and fluorine-containing precursor after the dry-mixing to convert ZrO 2 and a part of the oxygen (O) anion to F. The positive electrode active material coated with ZrO 2 and F And a manufacturing method thereof.
리튬 이차전지는 높은 에너지 밀도와 작동 전위를 나타내고 사이클 수명이 길며 자기방전율이 낮아, 모바일 디바이스 뿐만 아니라, 전기자동차, 하이브리드 전기자동차, 전력저장 장치 등과 같은 중대형 디바이스 등에도 널리 사용되고 있다.Lithium secondary batteries exhibit high energy density and operating potential, have a long cycle life and low self-discharge rate, and are widely used not only for mobile devices, but also for medium and large-sized devices such as electric vehicles, hybrid electric vehicles, and electric power storage devices.
리튬 이차전지의 양극 활물질로는 리튬 함유 코발트 산화물 (LiCoMO2)이 주로 사용되고 있고, 그 외에도, 리튬 함유 니켈 산화물 (LiNiMO2), 층상 구조의 리튬 망간 산화물(LiMnMO2), 스피넬 구조의 리튬 망간 산화물(LiMn2MO4) 의 사용도 고려되고 있으며, 최근에는 LiMO2(M은 Co, Ni 및 Mn)이 사용되고 있다.Lithium-containing cobalt oxide (LiCoMO 2 ) is mainly used as a cathode active material of a lithium secondary battery, and lithium-containing nickel oxide (LiNiMO 2 ), lithium manganese oxide (LiMnMO 2 ) having a layered structure, lithium manganese oxide (LiMn 2 MO 4 ) is also considered, and recently, LiMO 2 (M is Co, Ni and Mn) is used.
이러한 LiMO2(M: Co, Ni, Mn) 표면에는 합성 과정 중에 다량의 Li 부산물이 발생하게 되고, 이들 Li 부산물의 대부분은 Li2CO3 및 LiOH의 화합물로 이루어져 있어서, 양극 페이스트의 제조시 젤(gel)화 되는 문제점과, 전극 제조 후 충방전 진행에 따른 가스 발생의 원인이 된다.On the surface of LiMO 2 (M: Co, Ni, Mn), a large amount of Li by-products are generated during the synthesis process. Most of these Li by-products are composed of compounds of Li 2 CO 3 and LiOH, and the generation of gas due to the progress of charge / discharge after manufacturing the electrode.
한편, 리튬 이차전지에는 이온을 전달하는 매개체로서 전해질이 필수적이고, 상기 전해질은 일반적으로 용매와 리튬염으로 구성되어 있으며, 상기 리튬염으로는 염의 용해도와 화학적 안정성 등의 관계에서 4불화붕산리튬(LiBF4), 6불화인산리튬(6LiPF6) 등이 주로 사용되고 있다. 그러나, 상기와 같이 불소(F)를 포함하는 리튬염을 용해시킨 전해질은 전해질 내의 미량의 수분과 반응하여 불산(HF)을 형성하고, 상기 불산은 전극을 분해하는 문제점을 초래한다.On the other hand, in the lithium secondary battery, an electrolyte is essential as an agent for transferring ions, and the electrolyte is generally composed of a solvent and a lithium salt. In the lithium salt, lithium tetrafluoroborate LiBF 4 ), lithium hexafluorophosphate (6LiPF 6 ), and the like are mainly used. However, as described above, the electrolyte in which the lithium salt containing fluorine (F) is dissolved reacts with a trace amount of moisture in the electrolyte to form hydrofluoric acid (HF), and the hydrofluoric acid causes a problem of decomposing the electrode.
또한, 탄산 리튬(Li2CO3)은 비수용성 순수용매에서는 용출되지 않고 안정하게 존재하지만, 불산(HF)과 반응하는 경우에는 전해질로 용출되어 이산화탄소(CO2)를 발생시키기 때문에, 저장 또는 사이클 동안 과량의 가스가 발생하는 단점이 있다. 그에 따라, 전지의 스웰링(swelling) 현상을 유발하며, 고온 안전성을 저하시키는 문제점을 가지고 있다.Also, lithium carbonate (Li 2 CO 3), since, if there stably without being eluted in the water-insoluble pure solvent, hydrofluoric acid (HF) and the reaction is eluted with the electrolyte to produce a carbon dioxide (CO 2), storage or cycles There is a disadvantage in that an excessive amount of gas is generated. Thereby causing swelling of the battery and deteriorating high-temperature safety.
본 발명은 상기와 같은 종래기술의 문제점과 과거로부터 요청되어온 기술적 과제를 해결하는 것을 목적으로 한다.SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-mentioned problems of the prior art and the technical problems required from the past.
구체적으로, 본 발명의 목적은, ZrO2 및 F 코팅층에 의해 양극 활물질의 표면에 존재하는 불순물(Li2CO3, LiOH)과 전해질내의 불산(HF)과의 접촉을 막고, ZrO2이 전해질 내의 불산(HF)와 반응하여 안정한 물질을 생성함으로써 안전성과 사이클 특성이 우수한 양극 활물질의 제조방법을 제공하는 것이다.Specifically, in the object of the present invention, ZrO 2, and F by the coating layers of impurities existing on the surface of the positive electrode active material to prevent contact with the hydrofluoric acid (HF) in the (Li 2 CO 3, LiOH) and the electrolyte, ZrO 2 the electrolyte The present invention provides a method for producing a cathode active material having excellent safety and cycle characteristics by reacting with hydrofluoric acid (HF) to produce a stable material.
본 발명의 또 다른 목적은 상기 방법으로 제조된 새로운 구조의 양극 활물질을 제공하는 것이다.Another object of the present invention is to provide a cathode active material of a novel structure manufactured by the above method.
이러한 목적을 달성하기 위한 본 발명에 양극 활물질의 제조방법은,In order to achieve the above object, the present invention provides a method for producing a cathode active material,
(a) 하기 화학식 1의 리튬 금속 산화물을 제조하는 단계, Li1+zNiaMnbCo1-(a+b)O2 (1)(a) preparing a lithium metal oxide represented by the following formula (1), Li 1 + z Ni a Mn b Co 1- (a + b) O 2
(상기 식에서, 0≤z≤0.1, 0.1≤a≤0.8, 0.1≤b≤0.8 및 a+b<1이다);(Where 0? Z? 0.1, 0.1? A? 0.8, 0.1? B? 0.8 and a + b <1);
(b) 상기 리튬 금속 산화물과 지르코늄 및 불소 함유 전구체를 건식 혼합하는 단계; 및(b) dry-blending the lithium metal oxide with zirconium and a fluorine-containing precursor; And
(c) 단계(b)의 건식 혼합 후 열처리하여 지르코늄 및 불소 함유 전구체를 ZrO2로 변환시키고 산소(O) 음이온의 일부가 F로 치환되는 단계;(c) heat-treating the zirconium and fluorine-containing precursor to ZrO 2 and converting a portion of the oxygen (O) anion to F;
를 포함하고 있어서, ZrO2 및 F가 코팅된 양극 활물질을 제공한다.To thereby provide a cathode active material coated with ZrO 2 and F.
본 발명의 제조방법에 따라 형성된 ZrO2 및 F 피막은 양극 활물질 표면에 존재하는 불순물(Li2CO3, LiOH)과 전해질 내의 불산(HF)의 접촉을 막을 수 있고, 또한, 상기 ZrO2 피막은 전해질 내의 불산(HF)과 반응하여 안정한 형태의 ZrO2ㅇ5HFㅇH2O를 형성할 수 있어 양극 활물질의 표면을 안정화시키는 작용을 한다.ZrO 2 and F film formed in accordance with the production method of the present invention can prevent the contact of the hydrofluoric acid (HF) in which the impurity (Li 2 CO 3, LiOH) and the electrolyte present in the cathode active material surface, and the ZrO 2 film is And reacts with hydrofluoric acid (HF) in the electrolyte to form a stable form of ZrO 2 ㅇ 5HF ㅇ H 2 O, thereby stabilizing the surface of the cathode active material.
따라서, 본 발명에 따라 제조되는 양극 활물질은 전해액과 접촉으로 인한 양극 활물질의 구조 붕괴 및 부반응 산물로서 이산화탄소의 발생을 억제할 수 있으므로, 이를 포함하는 리튬 이차전지는 스웰링 현상의 최소화로 인해 향상된 안전성을 갖고, 사이클 특성이 향상되는 효과를 발휘한다.Therefore, the cathode active material produced according to the present invention can suppress the structural collapse of the cathode active material due to contact with the electrolyte and the generation of carbon dioxide as a side reaction product. Therefore, the lithium secondary battery including the lithium secondary battery has improved safety And exhibits an effect of improving cycle characteristics.
상기 화학식 1의 리튬 금속 산화물은 니켈의 함량(a) 및 망간의 함량(b)이, 상세하게는, 각각 0.1 이상 내지 0.8 이하일 수 있고, 더욱 상세하게는, 상기 화학식 1의 리튬 금속 산화물은 Li1Ni1/3Mn1/3Co1/3O2 또는 LiNi0.5Mn0.3Co0.2O2일 수 있다.More specifically, the lithium metal oxide of Formula 1 may be Li (Li), Li (Li), Li (Li) 1 Ni 1/3 Mn 1/3 Co 1/3 O 2 or LiNi 0.5 Mn 0.3 Co 0.2 O 2 .
이러한 리튬 전이금속 산화물 입자는 고상법, 공침법 등 당업계에서 공지된 제조방법에 따라 준비될 수 있으므로, 이에 대한 자세한 설명은 생략 하기로 한다.The lithium transition metal oxide particles can be prepared by a solid-phase method, a co-precipitation method, and the like, which are well-known in the art, and thus a detailed description thereof will be omitted.
본 발명에 따른 제조방법에서, 상기 지르코늄 및 불소 함유 전구체는, Zr 및 F를 제공할 수 있는 화합물로서, 특별히 제한되는 것은 아니나, 구체적으로는 ZrF4일 수 있다.In the production method according to the present invention, the zirconium and the fluorine-containing precursor are compounds capable of providing Zr and F, but are not particularly limited, but may be specifically ZrF 4 .
하나의 구체적인 예에서, 상기 단계(b)에서 리튬 전이금속 산화물에 코팅되는 ZrO2 및 F의 양이 양극 활물질 전체 중량을 기준으로 0.001 내지 0.100 중량%가 되도록, 리튬 전이금속 산화물의 양을 조절하여 혼합할 수 있고, 상세하게는 0.001 내지 0.010 중량%가 되도록 혼합할 수 있다.In one specific example, the amount of the lithium transition metal oxide is adjusted so that the amount of ZrO 2 and F coated on the lithium transition metal oxide in the step (b) is 0.001 to 0.100 wt% based on the total weight of the cathode active material And may be mixed in an amount of 0.001 to 0.010% by weight.
상기 ZrO2 및 F의 양이 지나치게 작을 경우 소망하는 효과를 발휘하기 어렵고, 지나치게 많을 경우 비용량(specific capacity)이 감소될 수 있어 바람직하지 않다.If the amount of ZrO 2 and F is too small, it is difficult to exhibit the desired effect, and if it is too large, the specific capacity may be decreased.
상기 단계(b)의 건식 혼합은, 예를 들어, 단순 혼합 또는 고에너지 밀링(high energy milling)에 의해 이루어질 수 있다. 특히, 고에너지 밀링(high energy milling)은 예컨대 메카노퓨전 장치, 또는 노빌타 장치 등을 이용하여 달성할 수 있고, 상기 메카노 퓨전은 건식 상태에서 강한 물리적인 회전력에 의해 혼합물을 형성시키는 방법으로, 구성물질들 간의 정전기적인 결착력이 형성되는 방법이다.The dry mixing of step (b) may be accomplished by, for example, simple mixing or high energy milling. Particularly, high energy milling can be achieved by using, for example, a mechanofusion apparatus or a novilla apparatus, and the mechanofusion is a method of forming a mixture by a strong physical rotational force in a dry state , And the electrostatic binding force between constituent materials is formed.
상기 열처리는, 예를 들어, 400 내지 1000℃의 온도에서 4 시간 내지 10시간 동안 공기 분위기 하에서 수행될 수 있으며, 이러한 열처리로 지르코늄 및 불소 함유 전구체가 ZrO2로 변환되고 산소(O) 음이온의 일부가 F로 치환되어 ZrO2 및 F가 코팅된 리튬 전이금속 산화물을 제조할 수 있다.The heat treatment can be performed, for example, at a temperature of 400 to 1000 ° C. for 4 to 10 hours under an air atmosphere, and the zirconium and fluorine-containing precursor is converted into ZrO 2 by this heat treatment and a part of the oxygen (O) Can be replaced with F to produce a lithium-transition metal oxide coated with ZrO 2 and F.
상기 열처리 온도 범위는 본 발명에서 소망하는 양극 활물질을 얻을 수 있는 최적의 범위로서, 상기 열처리 온도가 지나치게 높거나 낮은 경우, 불순물, 결정 결합, 시편 깨짐 등의 문제점이 발생할 수 있어 바람직하지 않다.The heat treatment temperature range is an optimum range for obtaining the desired cathode active material in the present invention. If the heat treatment temperature is excessively high or low, problems such as impurities, crystal bonds, specimen breakage, etc. may occur.
본 발명은, 또한, 상기 제조 방법을 사용하여 제조한 ZrO2 및 F가 코팅되어 있는 것을 특징으로 하는 이차전지용 양극 활물질을 제공한다.The present invention also provides a cathode active material for a secondary battery, which is coated with ZrO 2 and F produced by the above production method.
상기 코팅층의 두께는 구체적으로는 0.01 내지 0.1 ㎛일 수 있고, 더욱 구체적으로는 0.01 내지 0.05 ㎛일 수 있다. 상기 코팅층의 두께가 지나치게 얇을 경우에는 전해액과의 접촉을 방지할 수 없거나 전지의 작동 과정에서 손상되기 쉬울 수 있고, 지나치게 두꺼운 경우에는 비용량(specific capacity)이 감소될 수 있어 바람직하지 않다.The thickness of the coating layer may be specifically 0.01 to 0.1 mu m, more specifically 0.01 to 0.05 mu m. If the thickness of the coating layer is too small, contact with the electrolyte can not be prevented or the battery may be damaged during operation. If the coating layer is too thick, the specific capacity may be reduced.
상기 ZrO2 및 F는 양극 활물질의 표면적을 기준으로, 예를 들어, 60 내지 100%의 코팅 면적으로 도포될 수 있고, 구체적으로는 80 내지 100%의 코팅 면적으로 도포될 수 있다. 상기 코팅층의 면적이 지나치게 작은 경우, 양극 활물질과 전해액과의 접촉 면적이 늘어날 수 있어 바람직하지 않다.The ZrO 2 and F may be applied with a coating area of, for example, 60 to 100% based on the surface area of the cathode active material, and specifically, a coating area of 80 to 100%. If the area of the coating layer is excessively small, the contact area between the positive electrode active material and the electrolytic solution may increase, which is not preferable.
본 발명은 또한 상기와 같은 양극 활물질이 포함하는 이차전지용 양극 합체 및 상기 양극 합체를 도포되어 있는 이차전지용 양극을 제공한다.The present invention also provides a positive electrode composite for a secondary battery comprising the above-mentioned positive electrode active material and a positive electrode for a secondary battery coated with the positive electrode composite.
상기 양극 합제에는 상기 양극 활물질 이외에, 선택적으로 도전재, 바인더, 충진제 등이 포함될 수 있다.In addition to the positive electrode active material, the positive electrode mixture may optionally contain a conductive material, a binder, a filler, and the like.
상기 도전재는 통상적으로 양극 활물질을 포함한 혼합물 전체 중량을 기준으로 1 내지 30 중량%로 첨가된다. 이러한 도전재는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 천연 흑연이나 인조 흑연 등의 흑연; 카본블랙, 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙 등의 카본블랙; 탄소 섬유나 금속 섬유 등의 도전성 섬유; 불화 카본, 알루미늄, 니켈 분말 등의 금속 분말; 산화아연, 티탄산 칼륨 등의 도전성 위스키; 산화 티탄 등의 도전성 금속 산화물; 폴리페닐렌 유도체 등의 도전성 소재 등이 사용될 수 있다. The conductive material is usually added in an amount of 1 to 30% by weight based on the total weight of the mixture including the cathode active material. Such a conductive material is not particularly limited as long as it has electrical conductivity without causing chemical changes in the battery, for example, graphite such as natural graphite or artificial graphite; Carbon black such as carbon black, acetylene black, ketjen black, channel black, furnace black, lamp black, and summer black; Conductive fibers such as carbon fiber and metal fiber; Metal powders such as carbon fluoride, aluminum, and nickel powder; Conductive whiskey such as zinc oxide and potassium titanate; Conductive metal oxides such as titanium oxide; Conductive materials such as polyphenylene derivatives and the like can be used.
상기 바인더는 활물질과 도전제 등의 결합과 집전체에 대한 결합에 조력하는 성분으로서, 통상적으로 양극 활물질을 포함하는 혼합물 전체 중량을 기준으로 1 내지 30 중량%로 첨가된다. 이러한 바인더의 예로는, 폴리불화비닐리덴, 폴리비닐알코올, 카르복시메틸셀룰로우즈(CMC), 전분, 히드록시프로필셀룰로우즈, 재생 셀룰로우즈, 폴리비닐피롤리돈, 테트라플루오로에틸렌, 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌-디엔 테르 폴리머(EPDM), 술폰화 EPDM, 스티렌 브티렌 고무, 불소 고무, 다양한 공중합제 등을 들 수 있다.The binder is added to the binder in an amount of 1 to 30% by weight, based on the total weight of the mixture containing the cathode active material, as a component that assists in bonding between the active material and the conductive agent and bonding to the current collector. Examples of such binders include polyvinylidene fluoride, polyvinyl alcohol, carboxymethylcellulose (CMC), starch, hydroxypropylcellulose, regenerated cellulose, polyvinylpyrrolidone, tetrafluoroethylene, polyethylene , Polypropylene, ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrene butylene rubber, fluorine rubber, and various copolymers.
상기 충진제는 양극의 팽창을 억제하는 성분으로서 선택적으로 사용되며, 당해 전지에 화학적 변화를 유발하지 않으면서 섬유상 재료라면 특별히 제한되는 것은 아니며, 예를 들어, 폴리에틸렌, 폴리프로필렌 등의 올리핀계 중합제; 유리섬유, 탄소섬유 등의 섬유상 물질이 사용된다.The filler is optionally used as a component for suppressing expansion of the anode, and is not particularly limited as long as it is a fibrous material without causing a chemical change in the battery. Examples of the filler include olefin-based polymerizers such as polyethylene and polypropylene; Fibrous materials such as glass fibers and carbon fibers are used.
본 발명에 따른 양극은 상기와 같은 화합물들을 포함하는 양극 합제를 NMP 등의 용매에 혼합하여 만들어진 슬러리를 양극 집전체 상에 도포한 후 건조 및 압연하여 제조될 수 있다.The positive electrode according to the present invention can be prepared by applying a slurry prepared by mixing a positive electrode mixture containing the above-described compounds to a solvent such as NMP, applying the slurry on the positive electrode collector, followed by drying and rolling.
상기 양극 집전체는 일반적으로 3 내지 500 ㎛의 두께로 만들어진다. 이러한 양극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 또는 알루미늄이나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면 처리한 것 등이 사용될 수 있다. 집전체는 그것의 표면에 미세한 요철을 형성하여 양극 활물질의 접착력을 높일 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태가 가능하다.The cathode current collector is generally made to have a thickness of 3 to 500 mu m. Such a positive electrode collector is not particularly limited as long as it has conductivity without causing chemical change to the battery, and may be formed on the surface of stainless steel, aluminum, nickel, titanium, sintered carbon or aluminum or stainless steel Carbon, nickel, titanium, silver, or the like may be used. The current collector may have fine irregularities on the surface thereof to increase the adhesive force of the cathode active material, and various forms such as a film, a sheet, a foil, a net, a porous body, a foam, and a nonwoven fabric are possible.
본 발명은 또한 상기 양극과, 음극, 분리막, 및 리튬염 함유 비수 전해액으로 구성된 리튬 이차전지를 제공한다. The present invention also provides a lithium secondary battery comprising the positive electrode, the negative electrode, the separator, and a non-aqueous electrolyte containing a lithium salt.
상기 음극은, 예를 들어, 음극 집전체 상에 음극 활물질을 포함하고 있는 음극 합제를 도포한 후 건조하여 제조되며, 상기 음극 합제에는, 필요에 따라, 앞서 설명한 바와 같은 성분들이 포함될 수 있다.The negative electrode is prepared, for example, by coating a negative electrode mixture containing a negative electrode active material on a negative electrode collector and then drying the mixture. The negative electrode mixture may contain the above-described components as required.
상기 음극 활물질은, 예를 들어, 난흑연화 탄소, 흑연계 탄소 등의 탄소; LixFe2O3(0≤x≤1), LixWO2(0≤x≤1), SnxMe1-xMe'yOz (Me: Mn, Fe, Pb, Ge; Me': Al, B, P, Si, 주기율표의 1족, 2족, 3족 원소, 할로겐; 0<x≤1; 1≤y≤3; 1≤z≤8) 등의 금속 복합 산화물; 리튬 금속; 리튬 합금; 규소계 합금; 주석계 합금; SnO, SnO2, PbO, PbO2, Pb2O3, Pb3O4, Sb2O3, Sb2O4, Sb2O5, GeO, GeO2, Bi2O3, Bi2O4, and Bi2O5 등의 금속 산화물; 폴리아세틸렌 등의 도전성 고분자; Li-Co-Ni 계 재료 등을 사용할 수 있다.The negative electrode active material may include, for example, carbon such as non-graphitized carbon or graphite carbon; Li x Fe 2 O 3 (0≤x≤1 ), Li x WO 2 (0≤x≤1), Sn x Me 1-x Me 'y O z (Me: Mn, Fe, Pb, Ge; Me' : Metal complex oxides such as Al, B, P, Si, Group 1, Group 2, Group 3 elements of the periodic table, Halogen, 0 < x < Lithium metal; Lithium alloy; Silicon-based alloys; Tin alloy; SnO, SnO 2, PbO, PbO 2, Pb 2 O 3, Pb 3 O 4, Sb 2 O 3, Sb 2 O 4, Sb 2 O 5, GeO, GeO 2, Bi 2 O 3, Bi 2 O 4, and Bi 2 O 5 ; Conductive polymers such as polyacetylene; Li-Co-Ni-based materials and the like can be used.
상기 음극 집전체는 일반적으로 3 내지 500 ㎛의 두께로 만든다. 이러한 음극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 높은 도전성을 가지는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 구리, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 구리나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다. 또한, 양극 집전체와 마찬가지로, 표면에 미세한 요철을 형성하여 음극 활물질의 결합력을 강화시킬 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.The negative electrode collector is generally made to have a thickness of 3 to 500 mu m. Such an anode current collector is not particularly limited as long as it has high conductivity without causing chemical changes in the battery, and examples thereof include copper, stainless steel, aluminum, nickel, titanium, sintered carbon, copper or stainless steel Surface-treated with carbon, nickel, titanium, silver or the like, aluminum-cadmium alloy, or the like can be used. In addition, like the positive electrode collector, fine unevenness can be formed on the surface to enhance the bonding force of the negative electrode active material, and it can be used in various forms such as films, sheets, foils, nets, porous bodies, foams and nonwoven fabrics.
상기 분리막은 양극과 음극 사이에 개재되며, 높은 이온 투과도와 기계적 강도를 가지는 절연성의 얇은 박막이 사용된다. 분리막의 기공 직경은 일반적으로 0.01 ~ 10 ㎛이고, 두께는 일반적으로 5 ~ 300 ㎛이다. 이러한 분리막으로는, 예를 들어, 내화학성 및 소수성의 폴리프로필렌 등의 올레핀계 폴리머; 유리섬유 또는 폴리에틸렌 등으로 만들어진 시트나 부직포 등이 사용된다. 전해질로서 폴리머 등의 고체 전해질이 사용되는 경우에는 고체 전해질이 분리막을 겸할 수도 있다.The separation membrane is interposed between the anode and the cathode, and an insulating thin film having high ion permeability and mechanical strength is used. The pore diameter of the separator is generally 0.01 to 10 mu m and the thickness is generally 5 to 300 mu m. Such separation membranes include, for example, olefinic polymers such as polypropylene, which are chemically resistant and hydrophobic; A sheet or nonwoven fabric made of glass fiber, polyethylene or the like is used. When a solid electrolyte such as a polymer is used as an electrolyte, the solid electrolyte may also serve as a separation membrane.
상기 리튬염 함유 비수계 전해액은 전해액과 리튬염으로 이루어져 있으며, 상기 전해액으로는 비수계 유기용매, 유기 고체 전해질, 무기 고체 전해질 등이 사용된다.The lithium salt-containing nonaqueous electrolyte solution is composed of an electrolyte solution and a lithium salt. As the electrolyte solution, a nonaqueous organic solvent, an organic solid electrolyte, and an inorganic solid electrolyte may be used.
상기 비수계 유기용매로는, 예를 들어, N-메틸-2-피롤리디논, 프로필렌 카르보네이트, 에틸렌 카르보네이트, 부틸렌 카르보네이트, 디메틸 카르보네이트, 디에틸 카르보네이트, 감마-부틸로 락톤, 1,2-디메톡시 에탄, 테트라히드록시 프랑(franc), 2-메틸 테트라하이드로푸란, 디메틸술폭시드, 1,3-디옥소런, 포름아미드, 디메틸포름아미드, 디옥소런, 아세토니트릴, 니트로메탄, 포름산 메틸, 초산메틸, 인산 트리에스테르, 트리메톡시 메탄, 디옥소런 유도체, 설포란, 메틸 설포란, 1,3-디메틸-2-이미다졸리디논, 프로필렌 카르보네이트 유도체, 테트라하이드로푸란 유도체, 에테르, 피로피온산 메틸, 프로피온산 에틸 등의 비양자성 유기용매가 사용될 수 있다.Examples of the non-aqueous organic solvent include N-methyl-2-pyrrolidinone, propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, gamma -Butyrolactone, 1,2-dimethoxyethane, tetrahydroxyfuran, 2-methyltetrahydrofuran, dimethylsulfoxide, 1,3-dioxolane, formamide, dimethylformamide, dioxolane , Acetonitrile, nitromethane, methyl formate, methyl acetate, triester phosphate, trimethoxymethane, dioxolane derivatives, sulfolane, methylsulfolane, 1,3-dimethyl-2-imidazolidinone, propylene carbonate Nonionic organic solvents such as tetrahydrofuran derivatives, ethers, methyl pyrophosphate, ethyl propionate and the like can be used.
상기 유기 고체 전해질로는, 예를 들어, 폴리에틸렌 유도체, 폴리에틸렌 옥사이드 유도체, 폴리프로필렌 옥사이드 유도체, 인산 에스테르 폴리머, 폴리 에지테이션 리신(agitation lysine), 폴리에스테르 술파이드, 폴리비닐 알코올, 폴리 불화 비닐리덴, 이온성 해리기를 포함하는 중합제 등이 사용될 수 있다.Examples of the organic solid electrolyte include a polymer electrolyte such as a polyethylene derivative, a polyethylene oxide derivative, a polypropylene oxide derivative, a phosphate ester polymer, an agitation lysine, a polyester sulfide, a polyvinyl alcohol, a polyvinylidene fluoride, A polymer containing an ionic dissociation group and the like may be used.
상기 무기 고체 전해질로는, 예를 들어, Li3N, LiI, Li5NI2, Li3N-LiI-LiOH, LiSiO4, LiSiO4-LiI-LiOH, Li2SiS3, Li4SiO4, Li4SiO4-LiI-LiOH, Li3PO4-Li2S-SiS2 등의 Li의 질화물, 할로겐화물, 황산염 등이 사용될 수 있다.Examples of the inorganic solid electrolyte include Li 3 N, LiI, Li 5 NI 2 , Li 3 N-LiI-LiOH, LiSiO 4 , LiSiO 4 -LiI-LiOH, Li 2 SiS 3 , Li 4 SiO 4 , Nitrides, halides and sulfates of Li such as Li 4 SiO 4 -LiI-LiOH and Li 3 PO 4 -Li 2 S-SiS 2 can be used.
상기 리튬염은 상기 비수계 전해질에 용해되기 좋은 물질로서, 예를 들어, LiCl, LiBr, LiI, LiClO4, LiBF4, LiB10Cl10, LiPF6, LiCF3SO3, LiCF3CO2, LiAsF6, LiSbF6, LiAlCl4, CH3SO3Li, CF3SO3Li, (CF3SO2)2NLi, 클로로 보란 리튬, 저급 지방족 카르본산 리튬, 4 페닐 붕산 리튬, 이미드 등이 사용될 수 있다.The lithium salt is a material that is readily soluble in the non-aqueous electrolyte, for example, LiCl, LiBr, LiI, LiClO 4, LiBF 4,
또한, 전해액에는 충방전 특성, 난연성 등의 개선을 목적으로, 예를 들어, 피리딘, 트리에틸포스파이트, 트리에탄올아민, 환상 에테르, 에틸렌 디아민, n-글라임(glyme), 헥사 인산 트리 아미드, 니트로벤젠 유도체, 유황, 퀴논 이민 염료, N-치환 옥사졸리디논, N,N-치환 이미다졸리딘, 에틸렌 글리콜 디알킬 에테르, 암모늄염, 피롤, 2-메톡시 에탄올, 삼염화 알루미늄 등이 첨가될 수도 있다. 경우에 따라서는, 불연성을 부여하기 위하여, 사염화탄소, 삼불화에틸렌 등의 할로겐 함유 용매를 더 포함시킬 수도 있고, 고온 보존 특성을 향상시키기 위하여 이산화탄산 가스를 더 포함시킬 수도 있으며, FEC(Fluoro-Ethylene carbonate), PRS(Propene sultone), FPC(Fluoro-Propylene carbonate) 등을 더 포함시킬 수 있다.For the purpose of improving the charge / discharge characteristics and the flame retardancy, the electrolytic solution is preferably mixed with an organic solvent such as pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylenediamine, glyme, Benzene derivatives, sulfur, quinone imine dyes, N-substituted oxazolidinones, N, N-substituted imidazolidines, ethylene glycol dialkyl ethers, ammonium salts, pyrrole, 2-methoxyethanol, . In some cases, halogen-containing solvents such as carbon tetrachloride and ethylene trifluoride may be further added to impart nonflammability. In order to improve the high-temperature storage characteristics, carbon dioxide gas may be further added. FEC (Fluoro-Ethylene carbonate, PRS (propene sultone), FPC (fluoro-propylene carbonate), and the like.
본 발명에 따른 이차전지는 소형 디바이스의 전원으로 사용되는 전지셀에 사용될 수 있을 뿐만 아니라, 다수의 전지셀들을 포함하는 중대형 전지 모듈에 단위전지로도 바람직하게 사용될 수 있다.The secondary battery according to the present invention can be used not only in a battery cell used as a power source for a small device but also as a unit cell in a middle or large battery module including a plurality of battery cells.
또한, 본 발명은 상기 전지모듈을 중대형 디바이스의 전원으로 포함하는 전지팩을 제공하고, 상기 중대형 디바이스는 전기자동차(Electric Vehicle, EV), 하이브리드 전기자동차(Hybrid Electric Vehicle, HEV), 플러그-인 하이브리드 전기자동차(Plug-in Hybrid Electric Vehicle PHEV) 등을 포함하는 전기차 및 전력 저장장치 등을 들 수 있으나, 이에 한정되는 것은 아니다.Also, the present invention provides a battery pack including the battery module as a power source of a middle- or large-sized device, wherein the middle- or large-sized device is an electric vehicle (EV), a hybrid electric vehicle (HEV) An electric vehicle including a Plug-in Hybrid Electric Vehicle (PHEV), and a power storage device, but the present invention is not limited thereto.
이상에서 설명한 바와 같이, 본 발명에 따른 양극 활물질의 제조방법은 지르코늄 및 불소 함유 전구체와 리튬 전이금속 산화물을 건식 혼합 후 열처리하는 단계를 포함함으로써, 이에 따라 제조되는 양극 활물질 표면에 ZrO2 및 F가 코팅되어, 전해질 내의 불산(HF)과 반응하여 안정한 물질을 생성할 수 있다.As described above, the method for producing a cathode active material according to the present invention includes a step of dry-blending zirconium and a fluorine-containing precursor with a lithium transition metal oxide and then heat-treating the ZrO 2 and F on the surface of the cathode active material Can be coated and react with hydrofluoric acid (HF) in the electrolyte to produce a stable material.
따라서, 전해액과의 접촉으로 인한 양극 활물질의 구조 붕괴 및 부반응 산물로서 이산화탄소의 발생을 억제할 수 있고, 이를 포함하는 리튬 이차전지는 스웰링 현상의 최소화로 인해 향상된 안전성을 가지며, 사이클 특성이 향상되는 효과를 발휘한다.Therefore, it is possible to suppress the structural collapse of the cathode active material due to contact with the electrolyte and the generation of carbon dioxide as a side reaction product, and the lithium secondary battery including the lithium secondary battery has improved safety due to minimization of the swelling phenomenon, Effect.
도 1은 본 발명에 따른 하나의 실시예에서 얻어진 전이금속 산화물의 전자현미경 사진이다.
도 2는 실험예 1에 따른 수명특성을 나타내는 그래프이다.1 is an electron micrograph of a transition metal oxide obtained in one embodiment according to the present invention.
2 is a graph showing lifetime characteristics according to Experimental Example 1. FIG.
이하, 실시예를 통해 본 발명을 더욱 상술하지만, 하기 실시예는 본 발명을 예시하기 위한 것이며, 본 발명의 범주가 이들만으로 한정되는 것은 아니다.Hereinafter, the present invention will be described in further detail with reference to the following examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
<실시예 1>≪ Example 1 >
삼성분계 리튬 전이금속 산화물로 Li1+zNiaMnbCo1-(a+b)O2 (0≤z≤0.1, 0.1≤a≤0.8, 0.1≤b≤0.8 및 a+b<1)를 사용하고, 0.01 내지 0.20 중량%의 ZrF4를 혼합한 후, 300 내지 700℃의 온도에서 3 내지 10 시간 동안 열처리 하여, 도 1에서 보는 바와 같이, 표면에 ZrF가 코팅된 양극 활물질을 합성하였다.A ternary lithium-transition Li 1 + z Ni a Mn b Co 1- a metal oxide (a + b) O2 (0≤z≤0.1 , 0.1≤a≤0.8, 0.1≤b≤0.8 , and a + b <1) And 0.01 to 0.20 wt% of ZrF 4 were mixed and then heat-treated at 300 to 700 ° C for 3 to 10 hours to synthesize ZrF-coated cathode active material as shown in FIG.
상기 양극 활물질을 활물질, 도전제 및 바인더의 비율을 95 : 2.5 : 2.5로 하여 슬러리를 만들고 두께 20 ㎛의 Al-foil 위에 코팅한 후 코인 형태의 전지를 제작하였다. 음극으로는 Li-metal을 사용하였으며, 전해액으로 EC : EMC : DEC(1 : 2 : 1)에 LiPF6 1M을 사용하였다. A slurry was prepared from the above cathode active material at a ratio of active material, a conductive agent and a binder of 95: 2.5: 2.5, and coated on an Al foil having a thickness of 20 탆 to prepare a coin-shaped battery. Li-metal was used for the cathode, and LiPF 6 1M was used for the electrolyte EC: EMC: DEC (1: 2: 1).
<비교예 1>≪ Comparative Example 1 &
상기 리튬 전이금속 산화물로 LiNi3/5Mn1/5Co1/5O2 로 표시되는 리튬 금속 산화물을 사용한 것을 제외하고는 양극 제조 및 전지의 제조방법에 있어서는 상기 실시예 1과 동일한 방법으로 코인형 전지를 제작하였다.Except that a lithium metal oxide represented by LiNi 3/5 Mn 1/5 Co 1/5 O 2 was used as the lithium transition metal oxide, the same procedure as in Example 1 was applied to the preparation of a positive electrode and the production of a battery, A doll battery was made.
<실험예 1><Experimental Example 1>
상기 실시예 및 비교예 1에서 제조된 전지를 45℃ 에서 200 사이클 진행 후 수명특성을 분석하여 도 2 에 나타내었다.The battery manufactured in the above Examples and Comparative Example 1 was subjected to 200 cycles at 45 ° C, and its life characteristics were analyzed and shown in FIG.
실험 결과, 도 2 에서 보는 바와 같이, 본 발명에 따른 실시예 1의 전지의 경우 비교예 1의 전지에 비하여 수명특성이 크게 향상되는 것을 볼 수 있다. 이는 전지 표면의 코팅층으로 인해 전지의 수명특성 및 용량특성을 현저하게 향상시키는 효과가 있음을 확인할 수 있다.As shown in FIG. 2, it can be seen that the battery of Example 1 according to the present invention has a significantly improved life characteristic as compared with the battery of Comparative Example 1. This shows that the coating layer on the surface of the battery has an effect of remarkably improving the life characteristics and the capacity characteristics of the battery.
본 발명이 속한 분양에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주내에서 다양한 응용 및 변형을 수행하는 것이 가능할 것이다.It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.
Claims (13)
(a) 하기 화학식 1의 리튬 금속 산화물을 제조하는 단계; Li1+zNiaMnbCo1-(a+b)O2 (1)
(상기 식에서, 0≤z≤0.1, 0.1≤a≤0.8, 0.1≤b≤0.8 및 a+b<1이다.)
(b) 상기 리튬 금속 산화물과 지르코늄 및 불소 함유 전구체를 건식 혼합하는 단계; 및
(c) 단계(b)의 건식 혼합 후 열처리하여 지르코늄 및 불소 함유 전구체를 ZrO2로 변환시키고 산소(O) 음이온의 일부가 F로 치환되는 단계;
를 포함하고,
상기 단계(b)에서 리튬 전이금속 산화물에 코팅되는 ZrO2 및 F의 총량이 양극 활물질 전체 중량을 기준으로 0.001 내지 0.010 중량%가 되도록 리튬 전이금속 산화물의 양을 조절하여 혼합하는 것을 특징으로 하는, ZrO2 및 F가 코팅된 양극 활물질의 제조 방법.A method for producing a cathode active material for a secondary battery,
(a) preparing a lithium metal oxide represented by the following formula (1); Li 1 + z Ni a Mn b Co 1 - (a + b) O 2 (1)
(Where 0? Z? 0.1, 0.1? A? 0.8, 0.1? B? 0.8 and a + b <1).
(b) dry-blending the lithium metal oxide with zirconium and a fluorine-containing precursor; And
(c) heat-treating the zirconium and fluorine-containing precursor to ZrO 2 and converting a portion of the oxygen (O) anion to F;
Lt; / RTI >
Wherein the amount of the lithium transition metal oxide is adjusted so that the total amount of ZrO 2 and F coated on the lithium transition metal oxide in the step (b) is 0.001 to 0.010 wt% based on the total weight of the cathode active material. Lt; / RTI > coated with ZrO2 and < RTI ID = 0.0 > F. < / RTI >