KR101743917B1 - Pigment composition for thermochromic mask pack and thermochromic mask pack using the same - Google Patents
Pigment composition for thermochromic mask pack and thermochromic mask pack using the same Download PDFInfo
- Publication number
- KR101743917B1 KR101743917B1 KR1020150120047A KR20150120047A KR101743917B1 KR 101743917 B1 KR101743917 B1 KR 101743917B1 KR 1020150120047 A KR1020150120047 A KR 1020150120047A KR 20150120047 A KR20150120047 A KR 20150120047A KR 101743917 B1 KR101743917 B1 KR 101743917B1
- Authority
- KR
- South Korea
- Prior art keywords
- pigment
- mask pack
- group
- thermochromic
- composition
- Prior art date
Abstract
본 발명은 열변색성 마스크 팩용 안료 조성물 및 열변색성 마스크 팩에 관한 것으로, 구체적으로 안료, 용매, 습윤제 및 분산제를 포함하고, 상기 안료는 착색안료 및 시온안료가 포함되는, 열변색성 마스크 팩용 안료 조성물 및 이를 포함하는 열변색성 마스크 팩에 관한 것이다.The present invention relates to a pigment composition for a thermochromic mask pack and a thermochromic mask pack, and more particularly to a thermochromic mask pack containing a pigment, a solvent, a wetting agent and a dispersing agent, Pigment compositions and thermochromic mask packs comprising the same.
Description
본 발명은 열변색성 마스크 팩용 안료 조성물 및 열변색성 마스크 팩에 관한 것이다.
The present invention relates to a pigment composition for a thermochromic mask pack and a thermochromic mask pack.
일반적으로 여성들은 얼굴을 아름답게 하기 위한 방법으로 피부가 거칠어지거나 햇볕에 타고 피로할 때 피부에 영양을 공급하여 얼굴 피부를 탄력 있게 가꾸기 위하여 세안 후 마사지를 행한다.
Generally, women use a method to beautify the face, and massage after cleansing in order to nourish the skin when the skin becomes rough or sunburned and tired, and to make the facial skin resilient.
이때, 손상된 피부에 영양을 공급하기 위하여 오이나 감귤 등의 천연 재료나 마사지용 크림, 영양 팩, 클린싱 팩, 표백 팩 등의 팩제를 바른 상태에서 얼굴에 미용 티슈나 기타 보조 수단을 사용하여 덮어줄 수 있다.
In order to supply nutrients to the damaged skin, cover with natural or natural materials such as citrus or citrus, massage cream, nutrition pack, cleansing pack, bleach pack, etc. with facial cosmetic tissue or other auxiliary means .
또한, 손쉽게 얼굴 마사지를 하기 위하여 최근에는 부직포, 미용 필름, 하이드로겔 등을 일정한 형태로 압축시켜서 마사지할 얼굴 부위에 덮어씌울 수 있도록 원형이나 얼굴 모양의 여러 가지 종류의 마스크 팩이 출시되고 있다.
In order to easily perform facial massage, various types of mask packs of circular or facial shapes have recently been introduced so that the nonwoven fabric, the cosmetic film, the hydrogel, etc. are compressed into a certain shape so as to cover the face portion to be massaged.
그렇지만, 종래의 마스크 팩은, 사용 시의 미용액의 온도가 적온인지를 표시할 수 있도록 한 것이 없었다. 이 때문에 사용자가 가열 또는 냉각한 마스크 팩의 온도가 적온 보다 너무 높거나 너무 낮은 경우가 있어, 충분한 미용 효과 및 기분 좋은 온감 또는 냉감을 확실히 얻을 수 없는 문제가 있다.
However, the conventional mask pack has not been able to indicate whether the temperature of the serum at the time of use is a proper temperature. For this reason, the temperature of the mask pack heated or cooled by the user may be too high or too low than the proper temperature, and there is a problem that a sufficient cosmetic effect and a pleasant warmth or cold feeling can not be surely obtained.
본 발명은, 주변의 온도 상태를 마스크 팩의 색상에 의하여 표현할 수 있도록 하여, 적정한 온도 아래에서 마스크 팩을 사용할 수 있어 충분한 미용효과뿐만 아니라, 기분 좋은 온감 또는 냉감을 얻을 수 있는 마스크 팩을 제공하는 것을 목적으로 한다.
The present invention provides a mask pack in which a mask pack can be used under a proper temperature by expressing the temperature state of the surroundings by the color of the mask pack, thereby providing not only a sufficient cosmetic effect but also a pleasant warmth or cold feeling .
또한, 상기 온도에 따라 다양한 색상 변화가 가능하고, 감각적 차별화를 부여할 수 있으며, 마스크의 사용시간과 제품의 유효시간을 시각적으로 나타낼 수 있는 열변색성 마스크 팩용 안료 조성물 및 열변색성 마스크 팩을 제공하는 것을 목적으로 한다.
In addition, a pigment composition for a thermochromic mask pack and a thermochromic mask pack, which can exhibit various color changes according to the temperature, can impart sensory differentiation, can visually indicate the use time of the mask and the effective time of the product, The purpose is to provide.
본 발명의 일 구현예는 조성물 총 중량에 대하여, 안료 0.5 내지 15중량%, 용매 30 내지 70중량%, 습윤제 10 내지 50중량% 및 분산제 0.1 내지 5중량%를 포함하고, 상기 안료는 착색안료 및 시온안료가 0:100 내지 40:60의 중량비로 포함되는, 열변색성 마스크 팩용 안료 조성물을 제공한다.One embodiment of the present invention includes a composition comprising 0.5 to 15% by weight of pigment, 30 to 70% by weight of a solvent, 10 to 50% by weight of a wetting agent and 0.1 to 5% by weight of a dispersing agent based on the total weight of the composition, The present invention provides a pigment composition for a thermochromic mask pack, wherein the zeolite pigment is contained in a weight ratio of 0: 100 to 40: 60.
상기 열변색성 마스크 팩용 안료 조성물은, 수성 고분자로, 우레탄기를 포함하는 중합체, 우레탄기를 포함하는 공중합체, 아크릴기를 포함하는 중합체 및 아크릴기를 포함하는 공중합체로 이루어진 군에서 선택되는 하나 이상을 더 포함하는 것이 바람직하다. The pigment composition for a thermochromic mask pack may further comprise at least one selected from the group consisting of an aqueous polymer, a polymer containing a urethane group, a copolymer containing a urethane group, a polymer containing an acrylic group, and a copolymer containing an acrylic group .
상기 수성 고분자는, 조성물 총 중량에 대하여 1 내지 30중량%를 포함하는 것이 바람직하다. The aqueous polymer preferably comprises 1 to 30% by weight based on the total weight of the composition.
상기 열변색성 마스크 팩용 안료 조성물은, 계면활성제, 살균제, 점도 조절제, pH 조절제, 완충제 및 산화 방지제로 이루어진 군에서 선택되는 하나 이상을 더 포함하는 것이 바람직하다. It is preferable that the pigment composition for a heat discolorable mask pack further comprises at least one selected from the group consisting of a surfactant, a bactericide, a viscosity adjusting agent, a pH adjusting agent, a buffer, and an antioxidant.
상기 시온안료는, 금속착염염료, 콜레스테릭 액정 및 메타모 컬러로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다. The zeolite pigment is preferably at least one selected from the group consisting of metal complex salt dyes, cholesteric liquid crystal and meta-color.
상기 착색안료는, 백연, 아연화, 황화아연, 이산화티탄, 군청, 감청, 코발트 블루, 산화크로늄, 피리지안, 크롬그린, 황연, 티탄예로우, 황색산화철, 몰립데이트오렌지, 카드뮴계 안료, 철흑, 티탄블랙, 카본 블랙, 알루미늄 가루, 브론즈 및 마이카로 이루어진 무기안료 및 아조계, 인단트론계, 인디고계, 티오인디고계, 프탈로시아닌계, 디옥사진계 및 피롤로피롤계로 이루어진 유기안료로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다. The coloring pigment is at least one selected from the group consisting of white pigments, zinc pigments, zinc sulfide, titanium dioxide, ultramarine blue, cobalt blue, chromium oxide, pyridine, chromium green, chrome yellow, titanium yellow oxide, , Organic pigments composed of an inorganic pigment composed of titanium black, carbon black, aluminum powder, bronze and mica, and an azo pigment, indanthrone pigment, indigo pigment, thioindigo pigment, phthalocyanine pigment, dioxazine pigment and pyrrolopyrrole pigment Or more.
상기 분산제는, 리그닌 설폰산의 염, 리그닌 설폰산의 포름알데히드 축합물, 알킬 나프탈렌 설폰산의 포름알데히드 축합물 및 크레오소트유(creosote oil) 설폰산의 포름알데히드 축합물로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다. The dispersant is at least one selected from the group consisting of a salt of lignin sulfonic acid, a formaldehyde condensate of lignin sulfonic acid, a formaldehyde condensate of alkyl naphthalene sulfonic acid, and a formaldehyde condensate of creosote oil sulfonic acid .
상기 습윤제는, 에틸렌 글리콜, 디에틸렌 글리콜, 트리에틸렌 글리콜, 프로필렌 글리콜, 테트라에틸렌 글리콜, 2-메틸-2,4-펜탄디올, 1,2,6-헥산트리올, 티오글리콜, 에틸렌 글리콜 모노-메틸 에테르, 에틸렌 글리콜 모노-에틸 에테르, 디에틸렌 글리콜 모노-메틸 에테르, 디에틸렌 글리콜 모노-에틸 에테르, 프로필렌 글리콜 모노-메틸 에테르, 프로필렌 글리콜 모노-에틸 에테르, 트리에틸렌 글리콜 모노-메틸 에테르, 트리에틸렌 글리콜 모노-에틸 에테르, 디에틸렌 글리콜 디-메틸 에테르, 디에틸렌 글리콜 디-에틸 에테르, 디에틸렌 글리콜 모노부틸 에테르, 글리세롤 및 설탕으로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다. The wetting agent may be at least one selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, tetraethylene glycol, 2-methyl-2,4-pentanediol, 1,2,6- hexanetriol, thioglycol, Methyl ether, ethylene glycol monoethyl ether, diethylene glycol mono-methyl ether, diethylene glycol mono-ethyl ether, propylene glycol mono-methyl ether, propylene glycol mono-ethyl ether, triethylene glycol mono-methyl ether, It is preferably at least one selected from the group consisting of glycol mono-ethyl ether, diethylene glycol di-methyl ether, diethylene glycol di-ethyl ether, diethylene glycol monobutyl ether, glycerol and sugar.
본 발명의 다른 구현예는 베이스 시트; 및 상기 베이스 시트의 어느 일면에 상기 열변색성 마스크 팩용 안료 조성물에 의해 형성되는 이미지부를 포함하는, 열변색성 마스크 팩을 제공한다.Another embodiment of the present invention is a base sheet comprising: a base sheet; And an image portion formed on either side of the base sheet by the pigment composition for the thermochromic mask pack.
상기 베이스 시트는, 고분자 수지, 천연섬유 또는 합성섬유 재질로 이루어진 직물 및 부직포로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다.The base sheet is preferably at least one selected from the group consisting of a fabric made of a polymer resin, a natural fiber, or a synthetic fiber, and a nonwoven fabric.
상기 베이스 시트는, 두께가 0.1 내지 5mm인 것이 바람직하다.The base sheet preferably has a thickness of 0.1 to 5 mm.
상기 열변색성 마스크 팩은, 화장료 조성물이 함침된 것이 바람직하다.
It is preferable that the thermochromic mask pack is impregnated with a cosmetic composition.
본 발명은, 마스크 팩 사용시 사용자 주변의 온도나 체온에 따라 본래 착색안료에 의한 마스크 팩의 색상이 그대로 연출되거나, 착색안료 및 시온안료의 혼합색상이 연출될 수 있어, 단일 마스크 팩에서 2종 이상의 색상이 연출될 수 있는 마스크 팩이 제공될 수 있다.
In the present invention, when the mask pack is used, the hue of the mask pack originally produced by the colored pigment can be directly produced or the mixed color of the colored pigment and the zeotropic pigment can be produced according to the temperature or the body temperature around the user, A mask pack in which colors can be produced can be provided.
또한, 사용자가 이동하여 주변 온도가 바뀌거나 체온 변화가 있는 경우, 마스크 팩의 색상이 반복적으로 변화될 수 있어 사용자 본인의 만족감을 크게 향상시키면서 동시에 주변의 흥미로움을 유발시킬 수 있어, 우수한 경쟁력을 부여할 수 있는 효과를 나타낸다.
In addition, when the user moves and the ambient temperature changes or the body temperature changes, the color of the mask pack can be repeatedly changed, thereby greatly improving the satisfaction of the user, and at the same time, And shows the effect that can be given.
또한, 주변의 온도 상태를 마스크 팩의 색상에 의하여 표현할 수 있도록 하여, 적정한 온도 아래에서 마스크 팩을 사용할 수 있어 충분한 미용 효과뿐만 아니라, 기분 좋은 온감 또는 냉감을 얻을 수 있는 마스크 팩을 제공할 수 있다.
In addition, it is possible to provide a mask pack which can use a mask pack under a proper temperature and can obtain a pleasant feeling of warmth or a cold feeling as well as a sufficient cosmetic effect by allowing the surrounding temperature state to be expressed by the color of the mask pack .
도 1은 본 발명의 열변색성 화장료 팩 시트가 온도에 따라 표면이 변화되는 형태를 나타낸 모식도이다.
도 2는 CIELAB 색 공간 시스템을 나타내는 모식도이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic view showing a form in which the surface of a thermochromic cosmetic pack sheet of the present invention changes with temperature. Fig.
2 is a schematic diagram showing a CIELAB color space system.
이하, 본 발명의 바람직한 실시 형태를 설명한다. 그러나, 본 발명의 실시 형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시 형태로 한정되는 것은 아니다.Hereinafter, preferred embodiments of the present invention will be described. However, the embodiments of the present invention can be modified into various other forms, and the scope of the present invention is not limited to the embodiments described below.
본 발명의 일 구현예는, 조성물 총 중량에 대하여, 안료 0.5 내지 15중량%, 용매 30 내지 70중량%, 습윤제 10 내지 50중량% 및 분산제 0.1 내지 5중량%를 포함하고, 상기 안료는 착색안료 및 시온안료가 0:100 내지 40:60의 중량비로 포함되는, 열변색성 마스크 팩용 안료 조성물을 제공한다.
An embodiment of the present invention comprises a composition comprising 0.5 to 15% by weight of pigment, 30 to 70% by weight of a solvent, 10 to 50% by weight of a wetting agent and 0.1 to 5% by weight of a dispersing agent based on the total weight of the composition, And a zeotropic pigment are contained in a weight ratio of 0: 100 to 40:60.
또한, 본 발명의 다른 구현예는, 베이스 시트; 및 상기 베이스 시트의 어느 일면에 상기 열변색성 마스크 팩용 안료 조성물에 의해 형성되는 이미지부를 포함하는, 열변색성 마스크 팩을 제공한다.
Further, another embodiment of the present invention is a base sheet comprising: a base sheet; And an image portion formed on either side of the base sheet by the pigment composition for the thermochromic mask pack.
도 1은, 본 발명의 열변색성 마스크 팩용 안료 조성물에 의하여 형성되는 이미지부를 포함하는 열변색성 마스크 팩의 일 구현예를 나타낸 것으로, 온도 변화에 따라 가역적으로 색상이 변화는 형태를 나타내는 모식도이다. 예를 들어, 마스크 팩 (a)의 경우 주변 온도 10℃에서의 색상을 나타내고 있으며, 마스크 팩 (b)의 경우 주변 온도 25℃에서의 색상을 나타내고 있는 것으로, 이는 온도 변화에 따라 가역적으로 변화될 수 있음을 나타내고 있으며, 따라서 마스크 팩의 온도를 시각적으로 확인할 수 있다.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view showing an embodiment of a thermochromic mask pack including an image portion formed by a pigment composition for a thermochromic mask pack of the present invention, wherein a color reversibly changes in accordance with a temperature change . For example, in the case of the mask pack (a), the hue indicates the color at an ambient temperature of 10 ° C. In the case of the mask pack (b), the hue indicates the hue at an ambient temperature of 25 ° C, And thus the temperature of the mask pack can be visually confirmed.
이하, 본 발명의 열변색성 마스크 팩용 안료 조성물과 이를 포함하는 열변색성 마스크 팩을 보다 구체적으로 설명한다.
Hereinafter, the pigment composition for the thermochromic mask pack of the present invention and the thermochromic mask pack containing the same will be described in more detail.
상기 열변색성 마스크 팩용 안료 조성물은, 마스크 팩에 인쇄되어 온도에 따라 다양한 색상 변화를 나타낼 수 있도록 하는 안료 조성물로, 상기 안료는 착색안료와 함께 온도에 따라 색상이 바뀌는 열변색안료, 즉 시온안료를 포함하는 것이 바람직하다.
The pigment composition for a heat-discoloring mask pack is a pigment composition printed on a mask pack to exhibit various color changes depending on temperature. The pigment is a heat-discoloring pigment whose color changes depending on temperature together with a coloring pigment, .
상기 안료 중 착색안료는, 무기안료 및 유기안료 중 필요에 따라 선택적으로 사용할 수 있으며, 예를 들어, 무기안료로 백연, 아연화, 황화아연, 이산화티탄 등의 백색안료, 군청, 감청, 코발트 블루 등의 청색안료, 산화크로늄, 피리지안, 크롬그린 등의 녹색안료, 황연, 티탄예로우, 황색산화철, 몰립데이트오렌지, 카드뮴계 안료 등의 노랑 또는 적색안료, 철흑, 티탄블랙, 카본 블랙 등의 흑색안료, 알루미늄 가루, 브론즈 등의 금속안료 및 마이카 등의 펄 안료일 수 있다. 또한, 유기안료로 아조계, 인단트론계, 인디고계, 티오인디고계, 프탈로시아닌계, 디옥사진계 및 피롤로피롤계 등이 사용될 수 있으나, 이에 한정되는 것은 아니다.
Among the above pigments, the color pigments can be selectively used as required among inorganic pigments and organic pigments. For example, white pigments such as white pigments, zinc pigments, zinc sulfide, and titanium dioxide, Green pigments such as chromium oxide, pyridine and chrome green, yellow or red pigments such as chrome yellow, titanium yellow, yellow iron oxide, molybdate orange and cadmium pigments, iron black, titanium black and carbon black Metal pigments such as black pigment, aluminum powder, bronze, and the like, and pearl pigments such as mica. Examples of the organic pigments include, but are not limited to, azo pigments, indanthrone pigments, indigo pigments, thioindigo pigments, phthalocyanine pigments, dioxazine pigments, and pyrrolopyrrole pigments.
한편, 상기 시온안료는, 온도에 따라 색상이 변화는 온도 감응 안료로, 일반적으로 기준 온도에 도달함에 따라 색깔이 없어지기 시작했다가 기준 온도에 도달하면 투명해지고, 다시 온도가 내려가면 원래의 색깔로 되돌아 가는지 여부에 따라서 가역성 또는 비가역성으로 나눌 수 있다. 본 발명에서 바람직한 온도변화 범위는 20℃ 내지 45℃이며, 보다 바람직하게는 30℃ 내지 40℃에서 색상이 변하는 것이 좋다.
On the other hand, the above-mentioned zeolite pigment is a temperature-sensitive pigment which changes in color depending on the temperature. As the pigment reaches a reference temperature, the color begins to disappear. When the reference temperature is reached, the color becomes transparent. Or reversible or irreversible, depending on whether or not it is returned to < RTI ID = 0.0 > a < / RTI > The preferred range of the temperature change in the present invention is 20 占 폚 to 45 占 폚, more preferably 30 占 폚 to 40 占 폚.
본 발명의 열변색성 마스크 팩용 안료 조성물에 포함되는 시온안료는, 온도에 따라 본래의 색상을 유지 또는 상실을 반복할 수 있는 가역성 온도 감응 안료인 것이 바람직하며, 이때 상기 시온안료는, 금속착염염료, 콜레스테릭 액정 및 메타모 컬러로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하지만, 이에 한정되는 것은 아니다. 상기 금속착염염료로는 이산화티탄을 사용하는 것이 바람직하다.
The zeolite pigment included in the pigment composition for a thermochromic mask pack of the present invention is preferably a reversible temperature-sensitive pigment which can maintain or lose its original hue according to temperature, wherein the zeolite pigment is a metal complex salt dye , Cholesteric liquid crystal, and meta-color. However, the present invention is not limited thereto. As the metal complex salt dye, it is preferable to use titanium dioxide.
한편, 상기 시온안료는, 무기화합물계로 Hg, Ag, Cu, Pb 등의 중금속의 요오드화물 또는 이들의 착염을 포함하는 것이 바람직하다. 이때, 예를 들어 안료 조성이 Ag2HgI4 및 Cu2HgI4인 시온안료는 각각 50℃ 및 70℃의 온도에서 변색이 가능하며, 혼합하는 경우 50 내지 70℃ 사이에서 변색 온도 설정이 가능하다.
On the other hand, the zeolite pigment preferably contains an iodide of a heavy metal such as Hg, Ag, Cu, Pb or a complex thereof in an inorganic compound system. At this time, for example, the cyan pigment having a pigment composition of Ag 2 HgI 4 and Cu 2 HgI 4 can be discolored at a temperature of 50 ° C and 70 ° C, respectively, and in case of mixing, a discoloration temperature can be set between 50 ° C and 70 ° C .
나아가, 상기 시온안료는 유기화합물계로, 스피로피란류 등을 포함할 수 있으며, 이를 가열 용융하면 가역적으로 무색에서 유색으로 변화시킬 수 있다.
Further, the zeolite pigment may include organic compounds such as spiropyran and the like, and when heated and melted, it can be reversibly changed from colorless to colored.
한편, 상기 시온안료는 예를 들어 카멜케미칼사에서 시판되는 시온안료로, 노랑(yellow), 오렌지(orange), 마젠타(magenta), 로즈 레드(rose red), 스카이 블루(sky blue), 다크 블루(dark blue), 패스트 블루(fast blue), 보라(violet), 터키 블루(Turkish blue), 그린(green), 블랙(black) 등의 색상이 사용될 수 있으며, 이에 한정되는 것은 아니다.
On the other hand, the zeolite pigment is, for example, a zeolite pigment commercially available from Camell Chemical Company, and is a yellow pigment such as yellow, orange, magenta, rose red, sky blue, colors such as dark blue, fast blue, violet, Turkish blue, green, and black may be used, but the present invention is not limited thereto.
한편, 상기 착색안료 및 시온안료를 포함하는 안료를 이용함으로써, 주변의 온도에 따라 색상의 변화가 가능한 마스크 팩을 제조할 수 있다.
On the other hand, by using the pigment containing the colored pigment and the zeotropic pigment, it is possible to produce a mask pack capable of changing the color depending on the ambient temperature.
예를 들어, 상기 시온안료가 25℃ 이상에서 고유색이 표출되는 안료인 경우, 상기 착색안료 및 시온안료가 혼합된 상태에서 고유 색상을 갖는 마스크 팩은, 25℃ 미만의 온도에서 상기 시온안료는 투명하게 표현되기 때문에, 상기 착색안료에 의한 색상만을 연출하게 된다.
For example, when the zeolite pigment is a pigment exhibiting an intrinsic color at 25 ° C or higher, the mask pack having the intrinsic hue in a state where the color pigment and the zeolite pigment are mixed, So that only the color by the colored pigment is produced.
이와 같은 상태에서, 사용자가 마스크 팩을 사용하게 되면, 사용자의 체온으로부터 영향을 받아 상기 마스크 팩이 25℃ 이상으로 상승하게 되고, 상기 시온안료 고유색이 표출되면서 본래 착색안료와 혼합된 독특한 색상을 연출하게 된다.
In such a state, when the user uses the mask pack, the mask pack rises to 25 ° C or higher under the influence of the body temperature of the user, and a distinctive color mixed with the coloring pigment is displayed .
다른 예로, 상기 시온안료가 25℃ 미만에서만 고유색이 표현되도록 착색안료 및 시온안료가 혼합된 안료를 포함하는 열변색성 마스크 팩의 경우, 25℃ 이상의 온도 조건에서는 시온안료가 무색으로, 착색안료에 의한 색상만이 마스크 팩에 표현되게 된다.
As another example, in the case of a thermochromic mask pack comprising a pigment in which a color pigment and a zeotropin pigment are mixed such that the zeolite pigment exhibits an intrinsic color only at less than 25 캜, the zeolite pigment is colorless at a temperature of 25 캜 or higher, Only the color by the mask pack is expressed in the mask pack.
즉, 사용자가 마스크 팩을 사용하여 사용자의 체온에 의하여 상기 마스크 팩이 25℃ 이상의 온도로 상승하게 되면, 시온안료의 고유색이 소멸하면서 착색안료에 의한 색상이 마스크 팩 상에 연출된다. 또한, 상기 마스크 팩을 사용하는 사용자가 25℃ 미만의 환경에 노출되는 경우, 상기 시온안료가 나타내는 색상이 표현되면서, 상기 착색안료 및 시온안료의 혼합된 색상이 연출되어, 두 가지 색상을 갖는 마스크 팩을 사용하는 것과 같은 효과를 얻을 수 있다.
That is, when the user uses the mask pack to raise the temperature of the mask pack to a temperature of 25 ° C or more due to the body temperature of the user, the color of the color pigment is directed on the mask pack while the unique color of the zeolite pigment disappears. When the user using the mask pack is exposed to an environment of less than 25 캜, the color represented by the zeolite pigment is expressed, so that the mixed color of the color pigment and the zeolite pigment is produced, The same effect as using a pack can be obtained.
상기 안료는, 열변색성 마스크 팩용 안료 조성물 총 중량에 대하여, 0.5 내지 15중량%로 포함되는 것이 바람직하며, 보다 바람직하게는 1 내지 10중량%로 포함될 수 있다. 이때, 상기 안료의 함량이 0.5중량% 미만인 경우 베이스 시트에 인쇄 후 색상을 선명하게 나타내기 어려우며, 상기 함량이 15중량%를 초과하는 경우 조성물에 분산되기 어려워 색상이 고르게 표현되지 않는 문제점이 있다.
The pigment is preferably contained in an amount of 0.5 to 15% by weight, more preferably 1 to 10% by weight, based on the total weight of the pigment composition for a thermochromic mask pack. If the content of the pigment is less than 0.5% by weight, it is difficult to clearly show the color on the base sheet after printing. If the content is more than 15% by weight, the pigment is hardly dispersed in the composition.
특히, 상기와 같은 시온안료를 사용함에 따라 서로 다른 변색 온도를 갖는 두 가지 이상의 색상으로 된 시온안료를 일정한 비율로 혼합 사용하는 경우, 사용자가 위치한 주변의 온도에 따라 마스크 팩의 색상이 다양하게 변화될 수 있어, 환상적인 아름다움을 연출할 수 있다.
In particular, when two or more colors of zeotropic pigments having different coloring temperatures are mixed and used at a certain ratio by using the zeotropic pigment, the color of the mask pack varies in accordance with the temperature around the user And can produce a fantastic beauty.
특히, 상기 안료에 포함되는 착색안료 및 시온안료는, 0:100 내지 40:60의 중량비로 포함되는 것이 바람직하며, 보다 바람직하게는 0:100 내지 20:80의 중량비로 포함될 수 있다. 즉, 상기 착색안료에 시온안료만을 포함할 수 있으며, 착색안료 및 시온안료를 혼합하는 경우 중량비가 0:100 내지 40:60이며, 이를 벗어나는 경우 온도 변화에 따른 색상 변화를 뚜렷하게 나타내기 어려운 문제점이 있다.
In particular, the color pigment and the zeotropic pigment contained in the pigment are preferably contained in a weight ratio of 0: 100 to 40:60, more preferably 0: 100 to 20:80. That is, the coloring pigment may contain only the zeolite pigment, and when the coloring pigment and the zeolite pigment are mixed, the weight ratio is 0: 100 to 40:60. When the coloring pigment and the zeolite pigment are removed, have.
한편, 열변색성 마스크 팩용 안료 조성물에 의하여, 열변색성 마스크 팩에 표현되는 색상은, 시온안료 단독, 착색안료 단독, 또는 착색안료 및 시온안료가 혼합된 색상으로 표현이 가능하며, 그 색상 변화는 도 2에 나타낸 바와 같이, CIELAB 색 공간 시스템에서, L=0~100, a=±127, b=±127의 범위에 걸쳐 표현될 수 있으며, 예를 들어, 주변 온도에 따라 L이 70이상 범위로 진행되는 가변성 마스크 팩인 것이 바람직하다. 또한, 시온안료에 의하여 무색, 즉 투명하게 색상을 표현할 수도 있으며, 이를 통해 착색안료와 시온안료를 혼합하여 사용할 때, 착색안료 고유의 색상을 표현할 수 있다.
On the other hand, due to the pigment composition for a thermochromic mask pack, the hue expressed in the thermochromic mask pack can be expressed as a mixture of a zeotropic pigment, a colored pigment alone, or a colored pigment and a zeotropic pigment, Can be expressed over a range of L = 0 to 100, a = ± 127, b = ± 127 in the CIELAB color space system as shown in FIG. 2. For example, if L is 70 or more It is preferable that the mask pack is a variable mask pack. In addition, color can be expressed by a zeolite pigment, that is, in a transparent manner. Thus, when a colored pigment is mixed with a zeolite pigment, the color of the colored pigment can be expressed.
한편, 상기 열변색성 마스크 팩용 안료 조성물은, 수성 고분자로, 우레탄기를 포함하는 중합체, 우레탄기를 포함하는 공중합체, 아크릴기를 포함하는 중합체 및 아크릴기를 포함하는 공중합체로 이루어진 군에서 선택되는 하나 이상을 더 포함하는 것이 바람직하다. 구체적으로, 우레탄 함유 공중합체, 아크릴 중합체, 아크릴 중합체와 블렌딩된 우레탄 아크릴 공중합체, 1종 이상의 폴리우레탄 중합체와 1종 이상의 아크릴 중합체의 블렌드, 2종 이상의 아크릴 중합체의 블렌드 또는 이들의 블렌드인 것이 바람직하지만, 이에 한정되는 것은 아니다.
On the other hand, the pigment composition for a heat-discoloring mask pack is preferably a water-soluble polymer which comprises at least one member selected from the group consisting of a polymer containing a urethane group, a copolymer containing a urethane group, a polymer containing an acrylic group, . Specifically, a urethane-containing copolymer, an acrylic polymer, a urethane acrylic copolymer blended with an acrylic polymer, a blend of at least one polyurethane polymer and at least one acrylic polymer, a blend of at least two acrylic polymers, or a blend thereof However, the present invention is not limited thereto.
나아가, 상기 수성 고분자는, 상기 열변색성 마스크 팩용 안료 조성물 총 중량에 대하여, 1 내지 30중량%로 포함되는 것이 바람직하고, 보다 바람직하게는 10 내지 20중량%로 포함될 수 있다. 이때, 상기 수성 고분자의 함량이 1중량% 미만인 경우 상기 열변색성 마스크 팩용 안료 조성물의 분산성이 불량해질 수 있고, 조성물의 층이 분리되는 문제점이 있을 수 있으며, 30중량%를 초과하는 경우, 조성물의 점도가 증가하고, 안료 조성물의 건조 속도가 증가하는 문제가 있을 수 있다.
Furthermore, the water-soluble polymer is preferably contained in an amount of 1 to 30% by weight, more preferably 10 to 20% by weight, based on the total weight of the pigment composition for a thermochromic mask pack. If the content of the aqueous polymer is less than 1% by weight, the pigment composition for the thermochromic mask pack may have poor dispersibility, and the composition layer may be separated. When the content of the aqueous polymer is more than 30% by weight, There may be a problem that the viscosity of the composition increases and the drying speed of the pigment composition increases.
나아가, 상기 열변색성 마스크 팩용 안료 조성물은, 계면활성제, 살균제, 점도 조절제, pH 조절제, 완충제 및 산화 방지제로 이루어진 군에서 선택되는 하나 이상을 더 포함하는 것이 바람직하지만, 추가 가능한 성분이 이에 한정되는 것은 아니며, 베이스 시트에 이미지부를 형성하여 마스크 팩을 제조하는데 필요한 성분을 추가할 수 있다.
Further, it is preferable that the pigment composition for the thermochromic mask pack further comprises at least one selected from the group consisting of a surfactant, a bactericide, a viscosity adjusting agent, a pH adjusting agent, a buffer and an antioxidant, And it is possible to add the components necessary for manufacturing the mask pack by forming the image portion on the base sheet.
한편, 상기 열변색성 마스크 팩용 안료 조성물에 포함되는 분산제는, 리그닌 설폰산염, 리그닌 설폰산 포름알데히드 축합물, 알킬 나프탈렌 설폰산 포름알데히드 축합물 및 크레오소트유(creosote oil) 설폰산 포름알데히드 축합물로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하며, 상기 분산제는 음이온계 분산제인 것이 바람직하다.
Meanwhile, the dispersant contained in the pigment composition for the thermochromic mask pack may be selected from the group consisting of a lignin sulfonate, a lignin sulfonic acid formaldehyde condensate, an alkyl naphthalene sulfonic acid formaldehyde condensate and a creosote oil sulfonic acid formaldehyde condensate , And the dispersing agent is preferably an anionic dispersing agent.
예를 들어, 상기 분산제는, 고분자계 설폰산일 수 있으며, 바람직하게는, 방향족 설폰산 포르말린 축합물, 리그닌 설폰산 포르말린 축합물 등일 수 있다. 또한, 상기 방향족 설폰산 포르말린 축합물로, 크레오소트유 설폰산 포르말린 축합물, 크레졸 설폰산 포르말린 축합물, 페놀 설폰산 포르말린 축합물, β-나프톨 설폰산 포르말린 축합물, β-나프탈린 설폰산과 β-나프톨 설폰산 포르말린 축합물, 크레졸 설폰산과 2-나프톨-6-설폰산 포르말린 축합물인 것이 바람직하지만 이에 한정되는 것은 아니다. 또한, 상기 축합물은 나트륨염과 같은 염을 포함하며, 보다 바람직하게는 크레오소트유 설폰산 포르말린 축합물, 나프탈렌 설폰산 포르말린 축합물, 리그닌 설폰산 포르말린 축합물 등일 수 있다.
For example, the dispersant may be a polymeric sulfonic acid, preferably an aromatic sulfonic acid formalin condensate, a lignin sulfonic acid formalin condensate, and the like. Also, as the aromatic sulfonic acid formalin condensate, there may be mentioned a condensate of a formalin of creosote, a condensate of cresol sulfonic acid, a formalin condensate of phenol sulfonic acid, a condensate of formalin of β-naphthol sulfonic acid, a condensate of β-naphthalene sulfonic acid, Naphthol sulfonic acid formalin condensate, and cresol sulfonic acid and 2-naphthol-6-sulfonic acid formalin condensate, but are not limited thereto. In addition, the condensate may include a salt such as sodium salt, more preferably a creosote-ethylsulfonic acid formalin condensate, a naphthalenesulfonic acid formalin condensate, a lignin sulfonic acid formalin condensate, and the like.
또한, 상기 분산제는, 시판품으로 입수될 수 있으며, 방향족 설폰산 포르말린 축합물로, 예를 들어 DEMOL N(카오사 제품), DEMOL C(카오사 제품), 특수 방향족 설폰산 포르말린 축합물의 나트륨 염인, DEMOL SNB(카오사 제품) 등을 사용할 수 있으나, 이에 한정되는 것은 아니다.
The dispersant may be a commercially available product and may be an aromatic sulfonic acid formalin condensate such as DEMOL N (manufactured by Kao Corporation), DEMOL C (manufactured by KAO Corporation), sodium salt of a special aromatic sulfonic acid formalin condensate, DEMOL SNB (manufactured by Kao Corporation), and the like, but the present invention is not limited thereto.
이때, 상기 분산제는 열변색성 마스크 팩용 안료 조성물 총 중량에 대하여, 0.1 내지 5중량%로 포함되는 것이 바람직하고, 보다 바람직하게는 1 내지 3중량%일 수 있다. 상기 분산제의 함량이 0.1중량% 미만인 경우 분산성이 떨어지고 조성물의 층이 분리될 수 있으며, 상기 함량이 5중량%를 초과하는 경우, 안료의 분산성이 떨어져 색상이 균일하지 못한 문제점이 있다.
At this time, the dispersant is preferably contained in an amount of 0.1 to 5% by weight, more preferably 1 to 3% by weight based on the total weight of the pigment composition for a thermochromic mask pack. When the content of the dispersant is less than 0.1% by weight, the dispersibility of the composition may be deteriorated and the composition layer may be separated. When the content of the dispersant is more than 5% by weight, the dispersibility of the pigment may be poor.
상기 열변색성 마스크 팩용 안료 조성물에 포함되는 습윤제는, 에틸렌 글리콜, 디에틸렌 글리콜, 트리에틸렌 글리콜, 프로필렌 글리콜, 테트라에틸렌 글리콜, 2-메틸-2,4-펜탄디올, 1,2,6-헥산트리올, 티오글리콜, 에틸렌 글리콜 모노-메틸 에테르, 에틸렌 글리콜 모노-에틸 에테르, 디에틸렌 글리콜 모노-메틸 에테르, 디에틸렌 글리콜 모노-에틸 에테르, 프로필렌 글리콜 모노-메틸 에테르, 프로필렌 글리콜 모노-에틸 에테르, 트리에틸렌 글리콜 모노-메틸 에테르, 트리에틸렌 글리콜 모노-에틸 에테르, 디에틸렌 글리콜 디-메틸 에테르, 디에틸렌 글리콜 디-에틸 에테르, 디에틸렌 글리콜 모노부틸 에테르, 글리세롤 및 설탕으로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다.
The wetting agent contained in the pigment composition for a thermochromic mask pack may be at least one selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, tetraethylene glycol, 2-methyl-2,4-pentanediol, Diethylene glycol mono-methyl ether, propylene glycol mono-methyl ether, propylene glycol mono-ethyl ether, propylene glycol mono-diethyl ether, diethylene glycol mono-diethyl ether, diethylene glycol mono- At least one compound selected from the group consisting of triethylene glycol mono-methyl ether, triethylene glycol mono-methyl ether, triethylene glycol mono-ethyl ether, diethylene glycol di-methyl ether, diethylene glycol di-ethyl ether, diethylene glycol monobutyl ether, glycerol and sugar .
또한, 상기 습윤제는, 열변색성 마스크 팩용 안료 조성물의 총 중량에 대하여, 10 내지 50중량%로 포함되는 것이 바람직하며, 보다 바람직하게는 20 내지 40중량%로 포함될 수 있다. 이때, 상기 습윤제의 함량이 10중량% 미만인 경우 안료 조성물의 건조 속도가 증가되어, 잉크젯을 이용하여 베이스 시트 상에 이미지부를 형성함에 있어 잉크젯 헤드 내의 노즐에서 건조가 일어나 노즐 막힘 등의 문제가 발생될 수 있으며, 상기 함량이 50중량%를 초과하는 경우 조성물의 점도가 상승되어 분산성에 열위해지는 문제점이 있다.
The wetting agent is preferably contained in an amount of 10 to 50% by weight, more preferably 20 to 40% by weight, based on the total weight of the pigment composition for a thermochromic mask pack. When the content of the wetting agent is less than 10% by weight, the drying speed of the pigment composition is increased. In forming the image portion on the base sheet using the inkjet, drying in the nozzle in the inkjet head may cause problems such as nozzle clogging When the content is more than 50% by weight, the viscosity of the composition is increased and the dispersibility is disadvantageously lowered.
상기 용매는, 열변색성 마스크 팩용 안료 조성물 총 중량에 대하여, 30 내지 70중량%로 포함되는 것이 바람직하며, 보다 바람직하게는 40 내지 50중량%로 포함될 수 있다. 상기 용매는 물, 예를 들어 정제수 또는 탈이온수 등이 사용될 수 있으며, 나아가 물에 혼합되는 수혼합성 유기용매를 포함할 수 있지만, 이에 한정되는 것은 아니다.
The solvent is preferably contained in an amount of 30 to 70% by weight, more preferably 40 to 50% by weight, based on the total weight of the pigment composition for a thermochromic mask pack. The solvent may include water, such as purified water or deionized water, and may further include a water-miscible organic solvent mixed with water, but is not limited thereto.
한편, 본 발명의 열변색성 마스크 팩에 포함되는 베이스 시트는, 고분자 수지, 천연섬유 또는 합성섬유 재질로 이루어진 직물 및 부직포로 이루어진 군에서 선택되는 하나 이상인 것이 바람직하다. 이때, 상기 천연섬유는 예를 들어, 레이온, 실크, 면, 마 등일 수 있으며, 상기 합성 섬유는 나일론, 폴리프로필렌, 폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트, 폴리부타디엔, 폴리아마이드, 폴리에틸렌, 폴리비닐알콜, 폴리비닐클로라이드, 폴리아크릴로니트릴, 폴리우레탄, 폴리락틱에시드 등일 수 있다. 바람직하게는 셀룰로오즈계 레이온, 면 등과 같은 재질로 이루어진 직물 또는 부직포일 수 있다.
Meanwhile, the base sheet included in the thermochromic mask pack of the present invention is preferably at least one selected from the group consisting of a fabric made of a polymer resin, a natural fiber, or a synthetic fiber, and a nonwoven fabric. The synthetic fibers may be selected from the group consisting of nylon, polypropylene, polyethylene terephthalate, polybutylene terephthalate, polybutadiene, polyamide, polyethylene, polyvinyl Alcohol, polyvinyl chloride, polyacrylonitrile, polyurethane, polylactic acid, and the like. Preferably a fabric made of a material such as a cellulosic rayon, a cotton, or the like or a nonwoven fabric.
상기 베이스 시트의 두께는 0.1 내지 5mm인 것이 바람직하며, 상기 베이스 시트의 두께가 0.1mm 미만인 경우 보관, 운반 및 사용 과정에서 베이스 시트가 쉽게 파손될 수 있으며, 상기 두께가 5mm를 초과하는 경우 패 시트의 두께가 전체적으로 두꺼워져 피부에 밀착 및 부착이 어려운 문제점이 있다.
If the thickness of the base sheet is less than 0.1 mm, the base sheet may be easily broken during storage, transportation and use. If the thickness of the base sheet is more than 5 mm, There is a problem that the thickness becomes thick as a whole and it is difficult to adhere and adhere to the skin.
상기 열변색성 마스크 팩은, 베이스 시트의 일면에 화장료 조성물 층이 적응되거나 또는 베이스 시트가 화장료 조성물에 함침된 것일 수 있고, 이 중 화장료 조성물이 함침된 것이 바람직하며, 이때 상기 화장료 조성물은, 예를 들어 에센스 화장료 조성물일 수 있지만, 이에 한정되는 것은 아니다.
In the thermochromic mask pack, the cosmetic composition layer may be adapted to one side of the base sheet, or the base sheet may be impregnated with the cosmetic composition, and the cosmetic composition may be impregnated with the base sheet. For example, but are not limited to, an essence cosmetic composition.
이하, 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나, 하기의 실시예는 본 발명을 구체적으로 설명하기 위한 것으로, 이들 실시예에 의하여 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail with reference to Examples. However, the following examples are intended to illustrate the present invention in detail and should not be construed as limiting the scope of the present invention.
<< 실시예Example 및 And 비교예Comparative Example >>
<< 실시예Example 1> 1>
조성물 총 중량에 대하여, 안료 1중량%, 습윤제로 에틸렌 글리콜 10중량% 및 분산제로 나프탈렌 설폰산 포르말린 축합물 1중량%, 잔부의 용매로 정제수를 포함하고, 상기 안료는 25℃ 미만에서는 선명한 적색이었다가 25℃ 이상에서는 무색으로 변색되는 시온안료인 25type rose red(카멜케미칼사)을 포함하는 열변색성 화장료 팩 시트용 안료 조성물을 준비하였다.
1% by weight of pigment, 10% by weight of ethylene glycol as a wetting agent and 1% by weight of naphthalenesulfonic acid formalin condensate as a dispersing agent, and purified water as a solvent of the rest, based on the total weight of the composition, A pigment composition for a thermochromic cosmetic pack sheet containing 25type rose red (Carmel Chemicals), which is a zeolite pigment that discolors at 25 占 폚 or higher, was prepared.
이후, 상기 안료 조성물을 베이스 시트로 준비된 2mm 두께의 부직포의 일면에 실크 스크린 방식에 의하여 인쇄하여, 이미지부를 형성하여, 화장료 팩 시트를 제조하였다.
Thereafter, the pigment composition was printed on one surface of a nonwoven fabric having a thickness of 2 mm prepared as a base sheet by a silk screen method to form an image portion to prepare a cosmetic pack sheet.
<< 실시예Example 2> 2>
상기 실시예 1에 있어서, 상기 안료는, 25℃ 미만에서는 선명한 적색이었다가 25℃ 이상에서는 무색으로 변색되는 시온안료인 25 type rose red(카멜케미칼사)와 남색의 착색안료인 Blue #607(현대케미칼사)이 중량비 5:2로 혼합된 안료인 것을 제외하고, 상기 실시예 1과 동일하게 화장료 팩 시트를 제조하였다.
In Example 1, the pigment was a mixture of a 25 type rose red (Carmel Chemicals) and a blue coloring pigment such as Blue # 607 (manufactured by Kamel Chemical Co., Ltd.), which are clear red at 25 ° C and discolored at 25 ° C or higher, Chemicals Co., Ltd.) were mixed in a weight ratio of 5: 2 to prepare a cosmetic pack sheet in the same manner as in Example 1 above.
<< 비교예Comparative Example 1> 1>
상기 실시예 1에 있어서, 상기 안료는, 남색의 착색안료인 Blue #607(현대케미칼사)인 것을 제외하고, 상기 실시예 1과 동일하게 화장료 팩 시트를 제조하였다.
A cosmetic pack sheet was prepared in the same manner as in Example 1, except that the pigment in Example 1 was Blue # 607 (Hyundai Chemical Company), which is a navy coloring pigment.
<< 실험예Experimental Example >>
상기 제조된 실시예 1, 2 및 비교예 1의 화장료 팩 시트를 피부에 부착하기 전(25℃ 미만), 피부에 부착하고 5분 경과 후(25℃) 및 피부에 부착하고 10분 경과 후(25℃ 이상) 색상의 변화를 관찰하였고, 그 결과를 하기 표 1에 나타내었다.After the cosmetic pack sheets of Examples 1 and 2 and Comparative Example 1 prepared above were adhered to the skin before adhering to the skin (less than 25 ° C), adhered to the skin for 5 minutes (at 25 ° C) 25 deg. C or more), and the results are shown in Table 1 below.
상기 표 1에 나타낸 바와 같이, 시온안료를 포함하고 있지 않은 비교예 1의 마스크 팩의 경우, 피부 부착에 의한 온도 변화에 영향을 받지 않고, 착색안료 고유의 색을 유지하고 있는 반면, 본 발명의 열변색성 마스크 팩용 조성물로 이미지부가 형성된 마스크 팩인 실시예 1 및 2의 경우, 피부 부착에 의한 온도 변화에 영향으로 다양한 색상을 구현하고 있음을 확인할 수 있다.
As shown in Table 1, in the case of the mask pack of Comparative Example 1 which does not contain a zeotropic pigment, the color inherent to the color pigment is maintained without being affected by temperature change due to skin adhesion, In the case of the mask packs 1 and 2 in which the image portion is formed of the composition for the thermochromic mask pack, it can be confirmed that various colors are implemented due to the temperature change due to skin adhesion.
<< 실시예Example 3 내지 7 및 3 to 7 and 비교예Comparative Example 2 내지 5> 2 to 5>
하기 표 2의 조성과 같이, 착색안료 및 시온안료가 혼합된 안료 100g, 습윤제로 에틸렌 글리콜 1,000g 분산제로 나프탈렌 설폰산 포르말린 축합물 10g 및 용매로 정제수를 혼합하여 화장료 팩 시트용 안료 조성물을 준비하였다.
100 g of a pigment mixed with a coloring pigment and a sion pigment, 10 g of a naphthalenesulfonic acid formalin condensate as a wetting agent, 1,000 g of ethylene glycol as a dispersant, and purified water as a solvent were mixed to prepare a pigment composition for a cosmetic pack sheet, .
이후, 상기 안료 조성물을 베이스 시트로 준비된 2mm 두께의 부직포의 일면에 실크 스크린 방식에 의하여 인쇄하여, 이미지부를 형성하여, 화장료 팩 시트를 제조하였다.
Thereafter, the pigment composition was printed on one surface of a nonwoven fabric having a thickness of 2 mm prepared as a base sheet by a silk screen method to form an image portion to prepare a cosmetic pack sheet.
이후, 제조된 화장료 팩 시트의 온도 변화에 따른 색상 변화와, 변색에 걸린 시간을 측정하여, 하기 표 2에 기재하였다.
Thereafter, the color change according to the temperature change and the time taken for the color change of the prepared cosmetic pack sheet were measured and are shown in Table 2 below.
상기 비교예 2 내지 5에서와 같이, 시온안료의 함량이 착색안료의 함량과 동일하거나 또는 적을 경우, 변색까지 걸리는 시간이 10분 이상으로 변색까지 시간이 다소 오래 걸리는 반면, 시온안료의 함량이, 시온안료와 착색안료의 함량비 6:4 이상 포함되는 경우, 변색까지 걸리는 시간이 50초 이하로 짧은 시간 안에 변색될 수 있음을 확인할 수 있다.As in Comparative Examples 2 to 5, when the content of the zeotropic pigment is equal to or less than the content of the colored pigment, the time required for discoloration takes longer than 10 minutes, When the content ratio of the zeotropic pigment to the color pigment is 6: 4 or more, it can be confirmed that the time required for discoloration can be discolored within a short time of 50 seconds or less.
Claims (12)
상기 베이스 시트의 어느 일 면에 열변색성 마스크 팩용 안료 조성물에 의해 형성되는 이미지부를 포함하며,
상기 열변색성 마스크 팩용 안료 조성물은 조성물 총 중량에 대하여, 착색안료와 시온안료가 0:100 내지 40:60의 중량비로 포함된 안료 0.5 내지 15중량%, 용매 30 내지 70중량%, 습윤제 10 내지 50중량% 및 분산제 0.1 내지 5중량%를 포함하고, 변색 시간이 50초 이내인, 열변색성 마스크 팩.
A base sheet; And
An image portion formed on one side of the base sheet by a pigment composition for a thermochromic mask pack,
Wherein the pigment composition for a thermochromic mask pack comprises 0.5 to 15% by weight of a pigment containing a color pigment and a zeotropic pigment in a weight ratio of 0: 100 to 40:60, 30 to 70% by weight of a solvent, 10 to 30% 50% by weight and a dispersant in an amount of 0.1 to 5% by weight, the discoloration time being within 50 seconds.
The pigment composition for a thermochromic mask pack according to claim 1, wherein the pigment composition for a thermochromic mask pack is selected from the group consisting of an aqueous polymer, a polymer containing a urethane group, a copolymer containing a urethane group, a polymer containing an acrylic group, A thermochromic mask pack further comprising at least one aqueous polymer.
The thermochromic mask pack according to claim 2, wherein the aqueous polymer is contained in an amount of 1 to 30% by weight based on the total weight of the composition.
The thermochromic mask pack of claim 1, wherein the pigment composition for a thermochromic mask pack further comprises at least one selected from the group consisting of a surfactant, a bactericide, a viscosity modifier, a pH adjuster, a buffer, and an antioxidant.
The thermochromic mask pack according to claim 1, wherein the zeolite pigment is at least one selected from the group consisting of metal complex salt dyes, cholesteric liquid crystal, and meta-color.
The method according to claim 1, wherein the coloring pigment is at least one selected from the group consisting of white pigments, zincations, zinc sulfide, titanium dioxide, ultramarine blue, persimmon, cobalt blue, chromium oxide, pyridine, chrome green, chrome, titanium yellow, An organic pigment consisting of an inorganic pigment composed of a cadmium pigment, iron black, titanium black, carbon black, an aluminum powder, a bronze and a mica and an azo pigment, an indanthrone pigment, an indigo pigment, a thioindigo pigment, a phthalocyanine pigment, a dioxazine pigment and a pyrrolopyrrole pigment Wherein the heat-discoloring mask pack is at least one selected from the group consisting of:
The dispersant of claim 1, wherein the dispersant is selected from the group consisting of a salt of lignin sulfonic acid, a formaldehyde condensate of lignin sulfonic acid, a formaldehyde condensate of alkyl naphthalene sulfonic acid, and a formaldehyde condensate of creosote oil sulfonic acid At least one selected from the group consisting of:
The composition according to claim 1, wherein the wetting agent is selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, tetraethylene glycol, 2-methyl-2,4-pentanediol, 1,2,6-hexanetriol, , Ethylene glycol mono-methyl ether, ethylene glycol mono-ethyl ether, diethylene glycol mono-methyl ether, diethylene glycol mono-ethyl ether, propylene glycol mono-methyl ether, propylene glycol monoethyl ether, Which is at least one selected from the group consisting of methyl ether, triethylene glycol monoethyl ether, diethylene glycol di-methyl ether, diethylene glycol di-ethyl ether, diethylene glycol monobutyl ether, glycerol and sugar, pack.
The thermochromic mask pack according to claim 1, wherein the base sheet is at least one selected from the group consisting of a fabric made of a polymer resin, a natural fiber, or a synthetic fiber, and a nonwoven fabric.
The thermochromic mask pack according to claim 1, wherein the base sheet has a thickness of 0.1 to 5 mm.