KR101692960B1

KR101692960B1 - Scratch Repair sticker and manufacturing method

Info

Publication number: KR101692960B1
Application number: KR1020160081035A
Authority: KR
Inventors: 김정린
Original assignee: 김정린
Priority date: 2016-06-28
Filing date: 2016-06-28
Publication date: 2017-01-04
Also published as: WO2018004112A1

Abstract

The present invention relates to a sticker for repairing defects including scratches on the surfaces of vehicles and home appliances, and more specifically, to a sticker for repairing scratches on vehicles and home appliances and to a method of producing the same, wherein the sticker, when used for repairing minor defects on the painted and coated exterior of a vehicle or an electronic product, allows anyone to conveniently repair the defective site while reducing the time and cost required for the repair work, and particularly, enables a surface quality of the repaired surface to be maximally similar to the original surface, and also, enables repaired colors to be preserved over long periods of time by providing protection to the repaired surface.

Description

{Scratch repair sticker and manufacturing method}

본 발명은 차량 및 가전제품의 표면에 발생되는 스크래치 등의 흠집을 보수하기 위한 스티커에 관한 것으로, 더욱 상세하게는 도장 및 코팅 형성된 차량이나 전자제품에 흠집이 발생시 스크래치를 보수함에 있어, 누구나 간편하면서도 신속한 보수가 가능하게 하면서도, 보수에 소요되는 시간과 비용의 절감을 가져오는 등 매우 효율적으로 사용할 수 있게 하는 차량 및 가전제품 스크래치 보수 스티커 및 그 보수 스티커 제조방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sticker for repairing scratches such as scratches on a surface of a vehicle and an electric appliances. More particularly, the present invention relates to a sticker for repairing a scratch when a paint or a coating- And more particularly, to a vehicle and household appliance scratch repair sticker and a method for manufacturing the repair sticker, which enable a user to use the vehicle scratch repair sticker with high efficiency while reducing the time and cost required for repairing while allowing quick repair.

일반적으로 전자제품이나 차량의 경우 그 외관에는 도장 및 코팅 형성되어 외관상의 미려함을 도모하고 있다.Generally, in the case of an electronic product or a vehicle, a coating and a coating are formed on the outer surface thereof to achieve a beautiful appearance.

한편, 근자에 들어서는 산업기술의 발달로 인한 전자제품이나 자동차의 발달이 상당한 수준에 도달되어 있는 상태이며, 이러한 기술의 발달로 차량이나 전자제품이 고급화되어 있는 실정이다.On the other hand, the development of electronic products and automobiles due to the development of industrial technologies in recent years has reached a considerable level, and the development of such technologies has resulted in the upgrading of vehicles and electronic products.

이에, 이러한 차량이나 전자제품의 경우 내구 구성은 물론, 외관상으로도 그 미려함이 한층 더해지고 있는 실정이다.Thus, in the case of such vehicles and electronic products, not only the durability but also the appearance thereof are becoming more and more beautiful.

이러한 차량이나 전자제품의 경우 사용중 외부요인의 충돌 등으로 인해 도장면이 손상되는 스크래치가 발생하고 있었다.In the case of such a vehicle or an electronic product, a scratch has occurred in which the paint surface is damaged due to external factors such as impact.

그러나, 전자제품의 경우 이러한 스크래치 등을 보수하기 위한 보수방법이 마땅히 준비되지 않아 사용자로 하여금 부득이 그대로 방치 사용하여야 하는 문제점이 있었다.However, in the case of electronic products, there is a problem in that a maintenance method for repairing such scratches and the like is not properly prepared, and therefore, the user must use the product unavoidably.

또한, 차량의 경우에는 외부요인에 상당히 노출되어 있는 것인바, 본인의 부주의로 인한 경미한 접촉사고나 주차중 옆 차량의 도어를 개방시 크고 작은 스크래치나 도장의 벗겨짐 등 흠집이 빈번히 발생하고 있는 실정으로, 이러한 흠집이 발생시 수분 등의 외부 요인으로 인한 부식 등 2차적인 손상을 방지하기 위해 반드시 보수를 수행하여야 한다.In addition, in the case of a vehicle, it is exposed to external factors considerably. In the case of a slight contact accident due to carelessness of the user, scratches such as large and small scratches or peeling of the paint frequently occur when the door of the vehicle is opened during parking , Repair must be performed to prevent secondary damage such as corrosion due to external factors such as moisture when such scratches occur.

한편, 이러한 차량의 경우 그 흡집이 중한 경우 판금 등의 단계를 거쳐 다시 도장하여 보수하는 것이 대부분인 것으로, 이러한 보수방법은, 자동차의 흠집부분을 청결하게 하는 단계, 상기 흠집부분을 사포 등으로 연마하여 평탄화하는 단계, 주위에 서페이서를 도포하고 이를 부드럽게 연마하는 단계, 이물질과 왁스를 제거한 다음 원래의 도장 색과 동일한 도료를 도포하는 단계, 클리어를 도포하는 단계, 클리어와 블렌딩 시너의 혼합물을 도포하는 단계, 블렌딩 시너를 도포하는 단계 및 건조하여 마무리하는 단계로 구성되는 것이 일반적이다.On the other hand, in the case of such a vehicle, in most cases, when the adsorbent is heavy, it is mostly painted and repainted through a step such as a sheet metal. Such a repair method includes a step of cleaning a scratched portion of an automobile, Applying a coating of the same color as the original coating color, applying a clearing, applying a mixture of clearing and blending thinner, removing the wax and removing the foreign substance and wax, , A step of applying a blending thinner, and a step of drying and finishing.

그러나, 상기와 같은 보수방법은 상당한 시간과 비용이 소요되며, 특히 보험처리시 할증 적용으로 인한 보험료가 인상되는 등 2차적인 손실이 발생하게 되는 것인바, 비교적 중한 흠집의 경우 당연히 실시하여야 하지만, 비교적 경미한 흠집의 경우 이러한 시간과 비용을 지출하기에는 상당한 부담이 있었다.However, the above-mentioned repair method takes considerable time and expense, and in particular, a secondary loss such as an increase in insurance premium due to application of an insurance premium is caused. In the case of relatively serious flaws, In the case of relatively minor scratches, there was a considerable burden to spend such time and money.

이에, 근자에 들어 상기와 같은 제반 문제점을 해결하기 위해 비교적 경미한 흠집의 경우 소비자가 직접 보수를 수행할 수 있도록 다양한 수단이 적용되고 있는 것으로, 대표적으로 터치펜 타입을 들 수 있다.Accordingly, in order to solve the above-mentioned problems, various means have been applied so that a consumer can perform repair in the case of relatively minor scratches. Typically, the touch pen type is exemplified.

그러나, 상기와 같은 종래의 터치펜을 이용한 보수는 미세한 흠집의 보수를 수행할 수는 있었으나, 터치 위치가 정교하지 못할경우 자칫 타 부분에 도료가 묻어나는 등 오히려 차량의 외관을 해치고, 특히 기존의 도장면과 표면이 고르지 못한 문제점이 있었다.However, in the conventional repair using the touch pen, it is possible to perform repair with minute scratches. However, if the touch position is not precise, the paint is applied to other parts of the touch panel, There is a problem that the coating surface and the surface are uneven.

또한, 상기와 같은 보수방법은, 그 터치펜의 도료가 최초 차량의 도료과 다른 성분으로 조성되어 있으면서도 도장의 열처리가 불가한 건인바, 기간이 경과시 그 도장 부분의 색상이 변화되는 문제점이 있었다.In addition, the above-described repair method has a problem that the paint of the touch pen is composed of components different from those of the paint of the first vehicle, but the paint can not be heat-treated.

대한민국실용신안등록 제20-0200143호.Korea Utility Model Registration No. 20-0200143.

본 발명은 상기와 같은 제반 문제점을 해결하기 위해 창안된 것으로, 차량이나 전자제품의 도장 및 코팅된 외관의 경미한 흡집을 보수함에 있어, 누구나 간편하게 흠집부분에 대한 보수가 가능하게 하면서도, 보수작업에 소요되는 시간과 비용의 절감을 가져오며, 특히, 보수면에 대하여 기존의 도장면과 최대한 유사한 표면도를 얻을 수 있으며, 보험처리시 할증 적용으로 인한 보험료가 인상되는 등 2차적인 손실이 발생되는 것을 방지하기 위한 차량 및 가전제품 스크래치 보수 스티커 및 그 보수 스티커 제조방법을 제공함에 본 발명의 목적이 있는 것이다.Disclosure of the Invention The present invention was conceived in order to solve the above-mentioned problems, and it is an object of the present invention to provide a method and apparatus for repairing a slight absorption of a coating of a vehicle or an electronic product, In particular, it is possible to obtain a surface roughness that is as close as possible to that of the existing coating surface with respect to the repair surface, and a secondary loss such as an increase in insurance premium due to the application of the premium may occur A scratch repair sticker for a vehicle, an electric appliance scratch repair sticker, and a repair sticker manufacturing method, which are objects of the present invention.

또한, 보수된 표면에 대하여 보호가 가능하게 하여, 장기간이 경과하더라도 보수된 색상의 유지가 가능하게 하기 위한 차량 및 가전제품 스크래치 보수 스티커 및 그 보수 스티커 제조방법을 제공함에 본 발명의 목적이 있는 것이다.It is another object of the present invention to provide a vehicle and household appliance scratch repair sticker and a repair sticker manufacturing method for enabling maintenance of a repaired surface and enabling maintenance of a color to be maintained even after a long period of time has elapsed .

상기 목적을 달성하기 위한 구체적인 수단으로는, 보호지;As a specific means for achieving the above object,

보호지의 일면에 형성되는 도장층;A coating layer formed on one side of the protective paper;

도장층의 표면에 형성되는 접착층 및An adhesive layer formed on the surface of the paint layer and

접착층을 보호하는 이형지를 포함하여 구성하며,And a release paper for protecting the adhesive layer,

권취되어 롤지로 된 보호지를 구비하되, 보호지의 일면에 도장층을 형성하는 도장층 형성단계;A coating layer forming step of forming a coating layer on one side of the protective paper, the protective layer being wound and rolled;

도장층의 표면에 접착제를 도포하여 접착층을 형성하는 접착층 형성단계;An adhesive layer forming step of forming an adhesive layer by applying an adhesive to the surface of the paint layer;

접착층의 표면에 이형지를 점착 형성하는 이형지 형성단계; 및A release paper forming step of adhering a release paper to the surface of the adhesive layer; And

이형지까지 형성된 보호지를 타발하는 타발단계을 수행함으로 달성할 수 있는 것이다.And a punching step of punching a protective paper formed up to the release paper.

이상과 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커 및 그 보수 스티커 제조방법은, 접착층을 갖는 도장층이 형성되어 있어, 도장이 벗겨지거나 스크래치 등의 경미한 흠집에 대하여 간편하게 접착 사용이 가능하여, 누구나 간편하게 흠집의 보수가 가능하게 하면서도, 비교적 저렴한 제작이 가능하여 보수에 따른 시간과 비용의 절감을 가져오며, 특히, 보수면에 대하여 기존의 도장면과 최대한 유사한 표면도를 얻을 수 있으며, 보험처리시 할증 적용으로 인한 보험료가 인상되는 등 2차적인 손실이 발생되는 것을 방지하게 되는 등 매우 효율적으로 사용할 수 있는 효과를 얻을 수 있는 것이다.INDUSTRIAL APPLICABILITY As described above, the vehicle of the present invention, the household electric appliance scratch repair sticker and the method of manufacturing the repair sticker have the coating layer having the adhesive layer formed thereon, so that the coating can be easily peeled off or can be easily used for minor scratches such as scratches. It is possible to make the maintenance of the scratches comparatively inexpensive, thereby saving time and cost in repairing, and in particular, it is possible to obtain a surface similar to the existing coating surface to the repair surface, It is possible to prevent a secondary loss such as an increase in the insurance premium due to the application.

또한, 보수된 표면이 코팅 형성되어 장기간 기간이 경과하더라도 보수면에 대한 색상의 변화 및 번겨짐이 방지되는 등 내구성의 향상을 가져오는 효과를 얻을 수 있는 것이다.In addition, even if the maintenance surface is coated and formed over a long period of time, the effect of improving the durability can be obtained, for example, the change in color and repulsion of the maintenance surface is prevented.

도 1은 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제1 실시예 단면도.
도 2는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제1 실시예에 따른 다른 실시예도.
도 3는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제2 실시예 단면도.
도 4은 본 발명 차량 및 가전제품 스크래치 보수 스티커 제조방법의 전체 공정도.
도 5는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제1 실시예에 따른 사용상태도.
도 6는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제2 실시예에 따른 사용상태도.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a sectional view of a first embodiment of a vehicle according to the present invention and a household electrical appliance scratch repair sticker. Fig.
2 shows another embodiment according to the first embodiment of the inventive vehicle and household appliance scratch repair sticker.
3 is a sectional view of a vehicle according to the present invention and a second embodiment of a household electric appliance scratch repair sticker.
4 is an overall process diagram of the vehicle of the present invention and a method for manufacturing a scratch repair sticker for household appliances.
5 is a state of use according to a first embodiment of a vehicle of the present invention and a household appliance scratch repair sticker.
6 is a use state diagram according to a second embodiment of the inventive vehicle and household appliance scratch repair sticker.

본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms and words used in the present specification and claims should not be construed as limited to ordinary or dictionary terms and the inventor may appropriately define the concept of the term in order to best describe its invention It should be construed as meaning and concept consistent with the technical idea of the present invention.

따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.Therefore, the embodiments described in the present specification and the configurations shown in the drawings are merely the most preferred embodiments of the present invention, and not all of the technical ideas of the present invention are described. Therefore, It should be understood that various equivalents and modifications may be present.

이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

먼저, 본 발명 차량 및 가전제품 스크래치 보수 스티커를 살펴보면,First, the car of the present invention and the scratch repair sticker of household appliances,

도 1은 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제1 실시예 단면도이고, 도 2는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제1 실시예에 따른 다른 실시예도이며, 도 3는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제2 실시예 단면도이다.Fig. 1 is a sectional view of a vehicle according to a first embodiment of the present invention and a scratch repair sticker for household appliances, Fig. 2 is another embodiment according to the first embodiment of the vehicle of the present invention and a scratch repair sticker for household appliances, And a household electric appliance scratch repair sticker according to a second embodiment of the present invention.

도 1 내지 도 3의 도시와 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커(1)는, 보호지(100)와, 도장층(200)과, 접착층(300)과, 이형지(400)로 구성된 것으로, 이때 보호지(100)와 도장층(200)은 다양하게 구성할 수 있다.1 to 3, the vehicle of the present invention and the scratch repair sticker 1 for household appliances comprise a protective paper 100, a coating layer 200, an adhesive layer 300, and a release paper 400, At this time, the protective paper 100 and the coating layer 200 can be configured in various ways.

먼저, 본 발명 차량 및 가전제품 스크래치 보수 스티커(1)의 제1 실시예를 살펴보면,First, referring to the first embodiment of the vehicle of the present invention and the household electrical appliance scratch repair sticker 1,

도 1의 도시와 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커(1)의 제1 실시예는, 보호지(100)와, 도장층(200)과, 접착층(300)과, 이형지(400)로 구성된다.1, the vehicle of the present invention and the scratch repair sticker 1 of household appliances are constructed of a protective paper 100, a paint layer 200, an adhesive layer 300, and a release paper 400 do.

여기서, 보호지(100)는, 수지재로 된 투명의 코팅비닐(110)로 구성할 수 있는 것으로, 이때 코팅비닐(110)은 하기하는 도장층(200)의 보호 및 광택도를 가지게 구성된다.Here, the protective paper 100 may be formed of a transparent coating vinyl 110 made of a resin material. In this case, the coating vinyl 110 is configured to have the protection and gloss of the coating layer 200 described below.

이때, 코팅비닐(110)을 이루는 수지재는 한정되는 것이 아니고, 통상의 PE(polyethylene), PP(polypropylene), PET(Polyethylene phthalate) 중 어느 하나로 된 투명의 수지를 비닐지로 형성한 것이면 가능할 것이며, 이때 코팅비닐(110)의 두께는 최소 0.05mm 이하를 이루게 구성함이 가장 바람직할 것이다.The resin material constituting the coated vinyl 110 is not limited and may be any material as long as a transparent resin made of any one of ordinary polyethylene (PE), polypropylene (PP), and polyethylene phthalate (PET) is formed of vinyl paper. It is most preferable that the thickness of the coated vinyl 110 is 0.05 mm or less.

상기 도장층(200)은, 코팅비닐(110)의 일면에 형성되며, 흠집난 외관을 보수하여 도장면을 이루게 구성된 것으로, 제1 실시예에서는 도장층(200)이 코팅비닐(110)의 일면에 0.05~0.1mm의 두께로 도료가 형성된 도료층(211)을 이루게 구성된다.The coating layer 200 is formed on one side of the coating vinyl 110 and is formed to repair the scratched outer surface to form a coating surface. In the first embodiment, the coating layer 200 is formed on one surface of the coating vinyl 110 A paint layer 211 having a thickness of 0.05 to 0.1 mm is formed.

이때, 상기와 같이 코팅비닐(110)의 일면에 도료층(211)을 구성함에 있어, 다양한 실시예의 적용 가능한 것으로, 먼저 도 1을 참조하여 코팅비닐(110)의 전체면에 구성할 수 있다.In this case, the coating layer 211 may be formed on one side of the coated vinyl 110 as described above. The coating layer 211 may be formed on the entire surface of the coated vinyl 110 with reference to FIG.

또한, 도료층(211)을 구성함에 있어, 도 2를 참조하여 코팅비닐(110)의 일면 주변에 테두리부(111)두되, 그 테두리부(111)를 제외한 코팅비닐(110)의 중앙에만 구성할 수 있다.2, a frame 111 is formed around one side of the coated vinyl 110, and only the center of the coated vinyl 110 except the edge 111 is formed. can do.

이때, 도료층(211)을 구성함에 있어 그 색상은 한정되는 것이 아니고, 본 발명 보수 스티커(1)가 사용되는 차량이나 전자제품의 도장 색상과 동일하게 다양한 색상으로의 적용 가능할 것으로, 일예로 차량의 경우 그 도장의 색상은 영문의 조합 또는 영문과 숫자의 조합으로 된 다양한 색상코드를 이루고 있는 것인바, 이러한 색상 코드에 해당하는 색상으로 다양하게 적용될 것이다.In this case, the color of the paint layer 211 is not limited, and it may be applied to various colors in the same manner as the paint color of a vehicle or an electronic product in which the repair sticker 1 of the present invention is used. For example, The color of the paint may be various combinations of English characters or a combination of alphanumeric characters and various colors corresponding to these color codes.

상기 접착층(300)은, 본 발명 보수 스티커(1)를 흠집부분에 접착 가능하게 구성된 것으로, 이때, 접착층(300)은, 전술한 도료층(211)의 형성에 따라 다양하게 적용할 수 있다.The adhesive layer 300 is configured to be adherable to a scratch portion of the present repair sticker 1. The adhesive layer 300 can be variously applied according to the formation of the paint layer 211 described above.

먼저, 접착층(300)은, 도 1을 참조하여 도료층(211)을 코팅비닐(110)의 전체면에 구성시에는, 도료층(211)의 전체면에 도포 형성되게 구성할 수 있다.Referring to FIG. 1, the adhesive layer 300 may be formed on the entire surface of the coating layer 211 when the coating layer 211 is formed on the entire surface of the coating vinyl 110.

또한 접착층(300)은, 도 2를 참조하여 도료층(211)을 코팅비닐(110)의 테두리부(111)을 제외한 중앙부에 형성시에는, 그 테두리부(111)에 해당하게만 도포 형성되게 구성할 수 있다.2, when the paint layer 211 is formed at the central portion of the coating vinyl 110 except for the edge portion 111, the adhesive layer 300 is applied only to the edge portion 111 Can be configured.

이때, 적용되는 접착층(300)은, 한정되는 것이 아니고 통상의 스티커 등에 적용되는 접착제의 적용 가능할 것이다.At this time, the adhesive layer 300 to be applied is not limited, and an adhesive applied to an ordinary sticker or the like may be applicable.

상기 이형지(400)는, 접착층(300)을 보호하게 구성된 것으로, 이형지(400)는, 한정되는 것이 아니고 통상의 코팅종이 등으로 구성되어 접착층(300)을 포함한 도료층(211) 전체를 덮어 마감하며, 사용시 접착층(300)으로부터 제거 가능하게 구성된다.The release paper 400 is configured to protect the adhesive layer 300. The release paper 400 is not limited and covers the entire paint layer 211 including the adhesive layer 300, And is removable from the adhesive layer 300 in use.

또한, 본 발명 차량 및 가전제품 스크래치 보수 스티커(1)의 제2 실시예를 살펴보면,In addition, according to the second embodiment of the vehicle of the present invention and the household electrical appliance scratch repair sticker 1,

도 3의 도시와 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커(1)의 제2 실시예는, As shown in Fig. 3, the vehicle of the present invention and the second embodiment of the scratch repair sticker 1 of household appliance,

상기 보호지(100)를 구성함에 있어, 그 보호지(100)를 물과 접촉시 불려져 제거 가능한 종이지로 구성할 수 있다.In forming the protective paper 100, the protective paper 100 may be composed of paper that can be removed when the paper is contacted with water.

그리고 상기 도장층(200)은, 종이지(120)의 일면에 형성되며, 흠집난 외관을 보수하여 도장면을 이루게 구성된 것으로, 제2 실시예에서는 유리막(221)과 도료층(222)으로 구성된다.The coating layer 200 is formed on one side of the paper paper 120 to repair the scratched outer surface to form a coating surface. In the second embodiment, the coating layer 200 is composed of the glass film 221 and the coating layer 222 do.

먼저, 유리막(221)은, 0.05.mm의 두께를 이루게 보호지(100)의 일면에 형성되게 구성된 것으로, 하기하는 도료층(222)의 보호 및 광택도를 가지게 구성된다.First, the glass film 221 is formed on one side of the protective paper 100 so as to have a thickness of 0.05 mm. The glass film 221 has the protection and gloss of the following paint layer 222.

그리고 도료층(222)은, 유리막(221)에 도료가 0.05~0.1mm 두께를 이루게 도포 형성되어 구성된다.The coating layer 222 is formed by coating a glass film 221 with a thickness of 0.05 to 0.1 mm.

이때, 도료층(222)을 구성함에 있어 그 색상은 한정되는 것이 아니고, 본 발명 보수 스티커(1)가 사용되는 차량이나 전자제품의 도장 색상과 동일하게 다양한 색상으로의 적용 가능할 것으로, 일예로 차량의 경우 그 도장의 색상은 영문의 조합 또는 영문과 숫자의 조합으로 된 다양한 색상코드를 이루고 있는 것인바, 이러한 색상 코드에 해당하는 색상으로 적용됨이 바람직할 것이다.In this case, the color of the paint layer 222 is not limited, but may be applied to various colors such as the paint color of a vehicle or an electronic product in which the repair sticker 1 of the present invention is used. For example, It is preferable that the color of the paint is applied to a color corresponding to the color code, such as a combination of English or a combination of letters and numbers.

상기 접착층(300)은, 본 발명 보수 스티커(1)를 흠집부분에 접착 형성하게 구성된 것으로, 도장층(200)을 이루는 도료층(222)의 표면에 도포 형성되며, 이때 적용되는 접착층(300)은, 한정되는 것이 아니고 통상의 스티커 등에 적용되는 접착제의 적용 가능할 것이다.The adhesive layer 300 is formed by adhering the repair sticker 1 of the present invention to a flaw portion and is formed on the surface of the paint layer 222 forming the paint layer 200. The adhesive layer 300, The present invention is not limited to this, and an adhesive applied to ordinary stickers or the like may be applicable.

상기 이형지(400)는, 접착층(300)을 보호하게 구성된 것으로, 이형지(400)는, 한정되는 것이 아니고 통상의 코팅종이 등으로 구성되어 접착층(300)을 덮어 마감하며, 사용시 접착층(300)으로부터 제거 가능하게 구성된다.The release paper 400 is configured to protect the adhesive layer 300. The release paper 400 is not limited to a typical coated paper and covers the adhesive layer 300 to cover the adhesive layer 300. In use, Removable.

이하, 상기와 같은 구성을 갖는 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제조방법을 살펴보면,Hereinafter, the vehicle of the present invention having the above-described structure and the manufacturing method of the scratch repair sticker for household appliances will be described.

도 4은 본 발명 차량 및 가전제품 스크래치 보수 스티커 제조방법의 전체 공정도이다.4 is an overall process diagram of a vehicle of the present invention and a method of manufacturing a household electric appliance scratch repair sticker.

도 4의 도시와 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커 제조방법은, 도장층 형성단계(S100)와, 접착층 형성단계(S200)와, 이형지 형성단계(S300)와, 타발단계(S400)를 수행하여 가능하다.4, the vehicle of the present invention and the method for manufacturing a scratch repair sticker of an electric appliance according to the present invention include a coating layer forming step S100, an adhesive layer forming step S200, a release paper sheet forming step S300, and a punching step S400 .

도 1 내지 도 3을 참조하여 먼저, 도장층 형성단계(S100)는, 1 to 3, a coating layer forming step (S100)

보호지(100)를 구비하되, 보호지(100)는 귄취된 롤지 형태로 구비되며, 그 보호지(100)가 권해되어 이동하는 과정에서 보호지(100)의 일면에 도장층(200)을 형성하게 된다.The protective paper 100 is provided in the form of rolled paper and the paint layer 200 is formed on one side of the protective paper 100 during the movement of the protective paper 100.

접착층 형성단계(S200)는, In the adhesive layer forming step (S200)

도장층(200)이 형성된 보호지(100)가 이동하는 과정에서 통상의 도포롤(도면중 미도시함)을 이용하여 표면에 접착제를 도포 형성하게 되는 것으로, 그 도장층(200)을 흡집난 외관에 접착이 가능하도록 접착층(300)을 형성하게 된다.An adhesive is applied to the surface of the protective layer 100 using a conventional application roll (not shown) during the movement of the protective layer 100 formed with the paint layer 200, The adhesive layer 300 is formed so that the adhesive layer 300 can be adhered.

이형지 형성단계(S300)는, In the release paper forming step S300,

접착층(300)의 표면에 코팅종이재로 된 이형지(400)를 점착 형성하되, 이는 권취된 롤지 형태의 이형지(400)를 이동하는 보호지(100)의 접착층(300)에 중첩되게 한 상태에서 가압롤(도면중 미도시함)을 이용하여 가압 점착시켜 접착층(300)을 보호하게 된다. A release paper 400 made of a coated paper material is adhered and formed on the surface of the adhesive layer 300 so that the release paper 400 in the form of rolled paper is superimposed on the adhesive layer 300 of the moving paper 100, The adhesive layer 300 is protected by pressure-bonding using a roll (not shown).

타발단계(S400)는,In the step S400,

상기와 같이 보호지(100)는 롤지 형태로 연속하여 공급되며, 그 보호지(100)에 도장층(200)과, 접착층(300)과, 이형지(400)가 연속하여 형성되는 것인바, 이형지(400)가 형성된 상태에서 프레스 타발(도면중 미도시함)에 의해 다양한 크기와 형상을 이루게하면 되는 것으로, 본 발명 보수 스티커(1)의 제조가 가능하게 된다.The protective paper 100 is continuously supplied in the form of a roll paper and the coating layer 200, the adhesive layer 300 and the release paper 400 are continuously formed on the protective paper 100. The release paper 400 (Not shown in the figure) in a state in which they are formed with various sizes and shapes, it becomes possible to manufacture the repair sticker 1 of the present invention.

한편, 상기와 같은 일련의 과정에 의해 제조되는 본 발명 보수 스티커 제조방법을 각각의 제1,2 실시예에 따라 상세히 살펴보면,Meanwhile, according to the first and second embodiments of the present invention,

먼저, 도 1을 참조하여 제1 실시예에 따른 보수 스티커 제조방법을 살펴보면, First, referring to FIG. 1, a method of manufacturing a repair sticker according to the first embodiment will be described.

도장층 형성단계(S100)에서,In the paint layer formation step (S100)

제1 실시예의 보수 스티커(1)를 제조하기 위해서는 보호지(100)가 구비되는 것으로, 이때 구비되는 보호지(100)는 압출 성형된 수지재로 된 투명의 코팅비닐(110)을 적용하되, 그 두께는 0.05mm 이하의 두께를 이루게 형성함이 가장 바람직할 것이다.In order to manufacture the maintenance sticker 1 of the first embodiment, a protective paper 100 is provided. In this case, the protective paper 100 is formed by applying a transparent coating vinyl 110 made of an extruded resin material, A thickness of 0.05 mm or less is most preferable.

이에, 도장층 형성단계(S100)는,Accordingly, the coating layer forming step (S100)

준비된 코팅비닐(110)의 일측면에 도료를 0.05~0.1mm의 두께로 스프레이 분사하여 도료층(211)을 형성하고, 그 형성된 도료층(211)은 자연 건조하여 완전 경화시켜 경화된 도료층(211)으로 된 도장층(200)을 얻을 수 있다.A paint layer 211 is formed by spraying a paint to a thickness of 0.05-0.1 mm on one side of the prepared coated vinyl 110. The formed paint layer 211 is naturally dried and completely cured to form a cured paint layer 211 can be obtained.

이때, 상기 도료층(211)을 코팅비닐(110)에 형성함에 있어서는, 다양하게 적용 가능한 것으로, 먼저 도 1을 참조하여 코팅비닐(110)의 전체면에 도료를 분사하여 도료층(211)을 형성할 수 있다.Referring to FIG. 1, the paint layer 211 may be formed by spraying a paint on the entire surface of the coated vinyl 110. The paint layer 211 may be formed on the entire surface of the coated vinyl 110, .

또한, 도료층(211)을 구성함에 있어, 도 2를 참조하여 코팅비닐(110)의 일면 주변에 테두리부(111)두되, 그 테두리부(111)를 제외한 코팅비닐(110)의 중앙에만 도료를 분사하여 도료층(211)을 형성할 수 있다.2, a frame 111 is formed around one side of the coated vinyl 110, and only the center of the coated vinyl 110 except the edge 111 is coated with a coating material So that the paint layer 211 can be formed.

이때, 상기와 같이 테두리부(111)를 두고 도료층(211)을 형성함에 있어서는, 코팅비닐(110)에 도료를 분사하기에 앞서 별도로 각각의 보수 스티커(1)의 테두리부(111)에 해당하는 지그(도면중 미도시함)를 두고 분사 형성함이 바람직할 것이다.At this time, in forming the paint layer 211 with the rim portion 111 as described above, it is necessary to separately coat the rim portion 111 of each of the maintenance stickers 1 before spraying the paint on the coating vinyl 110 (Not shown in the figure) may be disposed.

이후, 접착층 형성단계(S200)에서는, 먼저 도 1을 참조하여 코팅비닐(110)의 전체면에 도료층(211)을 형성시에는 그 도료층(211) 전체면에 접착제를 도포하여 접착층(300)을 형성하면 될 것이고, 도 2를 참조하여 테두리부(111)를 두고 도료층(211)을 형성시에는 그 테두리부(111)에 해당하게만 도료층(211)에 별도의 지그(도면중 미도시함)를 두고 접착제를 도포하여 접착층(300)을 형성하면 될 것이다.1, when the paint layer 211 is formed on the entire surface of the coating vinyl 110, an adhesive is applied to the entire surface of the paint layer 211 to form an adhesive layer 300 2, when the coating layer 211 is formed with the rim 111, a separate jig (not shown) is formed in the coating layer 211 corresponding to the rim 111, The adhesive layer 300 may be formed by applying an adhesive.

또한, 도 3을 참조하여 제2 실시예에 따른 보수 스티커 제조방법을 살펴보면,Referring to FIG. 3, a method of manufacturing a repair sticker according to a second embodiment of the present invention will now be described.

제2 실시예의 보수 스티커(1)를 제조하기 위해서는 보호지(100)가 구비되는 것으로, 이때 구비되는 보호지(100)는 물이 접촉시 불려져 제거가 가능한 종이지(120)를 적용한다.In order to manufacture the maintenance sticker 1 of the second embodiment, a protective paper 100 is provided. In this case, the protective paper 100 to be used at this time is paper paper 120 that can be removed when water is contacted.

종이지(120)의 표면에 유리막(221) 및 도료층(222)을 형성하여 되는 것으로, 먼저 유리막(221)을 형성하기 위해서는 종이지(120)의 표면에 투명의 유리막 코팅재를 스프레이 분사하여 종이지(120)의 표면에 유리막(221)을 형성하게 된다.A glass film 221 and a paint layer 222 are formed on the surface of the paper paper 120. In order to form the glass film 221, a transparent glass film coating material is sprayed onto the surface of the paper paper 120, A glass film 221 is formed on the surface of the paper 120.

이때, 유리막(221)에 분사되는 유리막 코팅재는 0.05.mm 이하로 막을 이루게 함이 가장 바람직할 것이다.At this time, it is most preferable that the glass coating material sprayed on the glass coating 221 has a film thickness of 0.05 mm or less.

한편, 상기에서 적용되는 유리막 코팅재는 한정되는 것이 아니고, 유리 등의 표면을 코팅하여 얇은 막을 이루는 것이면 가능할 것이다.Meanwhile, the glass coating material to be applied in the above is not limited, and it may be a material that forms a thin film by coating the surface of glass or the like.

이후, 도료층(222)을 형성하되, 도료층(222)을 형성시에는 상기 스프레이 분사된 유리막(221)이 완전히 경화되기 전 즉 50~60% 정도의 경화도를 이룬 상태에서 그 유리막(221)의 표면에 0.05~0.1mm 두께로 도료를 스프레이 분사하여 유리막(221) 표면에 도료층(222)을 형성하면 되는 것으로, 이에 유리막(221)과 도료층(222)을 이루는 도장층(200)을 얻을 수 있다.When the coating layer 222 is formed, the glass layer 221 is sprayed onto the glass layer 221 in a state where the sprayed glass layer 221 has a degree of curing of about 50 to 60% The paint layer 222 is formed on the surface of the glass film 221 by spraying the paint to a thickness of 0.05 to 0.1 mm on the surface of the glass film 221. The paint film 200 constituting the glass film 221 and the paint layer 222 Can be obtained.

한편, 상기와 같이 도료층(222)을 형성함에 있어 유리막(221)이 완전 경화되기 전 스프레이 분사 형성함은 유리막(221)이 완전 경화시 그 우수한 표면도에 의해 도료의 접착력이 저하될 수 있는 것인바, 이에, 그 유리막(221)이 경화되기전 형성함으로 그 유리막(221)에 도료가 소정 함침되어 유리막(221)과 긴밀하게 고착될 수 있다.In forming the paint layer 222 as described above, when the glass film 221 is sprayed before being completely cured, the adhesion of the paint may be deteriorated due to the excellent surface appearance when the glass film 221 is completely cured The glass film 221 is formed before the glass film 221 is cured, so that the glass film 221 can be impregnated with a paint to be tightly fixed to the glass film 221.

이후, 도장층(200)에 수행되는 접착층 형성단계(S200)는, 도료층(222)의 표면에 도포하면 된다.Thereafter, the adhesive layer forming step (S200) performed on the paint layer 200 may be performed on the surface of the paint layer 222. [

이에, 상기와 같은 일련의 과정을 통해 제1,2 실시예에 따른 본 발명 차량 및 가전제품 스크래치 보수 스티커의 제조가 가능하게 된다.Thus, it is possible to manufacture the vehicle of the present invention and the scratch repair sticker of household appliances according to the first and second embodiments through the above-described series of processes.

이하, 상기와 같이 제조된 본 발명 차량 및 가전제품 스크래치 보수 스티커의 작용을 첨부된 도면을 참조하여 상세히 설명한다.Hereinafter, the operation of the vehicle of the present invention and the scratch repair sticker of household appliances manufactured as described above will be described in detail with reference to the accompanying drawings.

한편, 본 발명의 사용상태의 실시예에서는 차량의 외관에 사용상태를 그 실시예로 적용한다.On the other hand, in the embodiment of the use state of the present invention, the use state is applied to the exterior of the vehicle as an embodiment thereof.

먼저, 상기와 같이 구성된 제1 실시예의 보수 스티커(1)는, 도 1 및 도 2를 참조하여 도 5의 도시와 같이 코팅비닐(110)로 된 보호지(100)의 표면에 도료층(211)으로 된 도장층(200)과 접착층(300)과 이형지(400)가 적층 형성된 구조를 이루게 구성된 것인바, 사용시 접착층(300)으로부터 이형지(400)를 제거한 상태에서, 접착층(300)을 통해 차량(10)의 흠집부분에 접착 사용하면 되는 것으로, 이렇게 접착된 보수 스티커(1)는, 도장층(200)을 이루는 도료층(211)을 통해 흠집의 보수가 가능하게 된다.1 and 2, the maintenance sticker 1 according to the first embodiment of the present invention has a coating layer 211 on the surface of a protective paper 100 made of a coating vinyl 110 as shown in FIG. The release layer 400 is removed from the adhesive layer 300 when the adhesive layer 300 is removed from the adhesive layer 300 and the release layer 400 is removed from the adhesive layer 300. [ The repair sticker 1 thus adhered can repair the scratches through the paint layer 211 constituting the paint layer 200. In this case,

이에, 보수된 도료층(211)은, 투명의 수지로 된 보호지(100)를 이루는 코팅비닐(110)을 통해 투시되어 기존 도장면(흠집 주변부)과의 동일한 색상을 이루게 보수되는 한편, 코팅비닐(110)의 코팅에 의해 보호되게 된다.Thus, the repaired paint layer 211 is transparent through the coating vinyl 110 forming the protective paper 100 made of a transparent resin so as to have the same color as the existing paint surface (flaw peripheral portion) Lt; RTI ID = 0.0 > 110 < / RTI >

이때, 도료층(211)을 형성함에 있어, 도 1을 참조하여 코팅비닐(110) 전체면에 접착층(300)을 형성시에는 도료층(211) 전체면이 접착되어 차량(10)에 긴밀한 접착이 가능할 것이고, 도 2를 참조하여 테두리부(111)에 해당하게 접착층(300)을 형성시에는 그 코팅비닐(110)의 두께가 보다 축소되어 접착시 차량의 외관과 근접한 표면도를 얻을 수 있을 것이다.1, when the adhesive layer 300 is formed on the entire surface of the coated vinyl 110, the entire surface of the paint layer 211 is adhered to the vehicle 10, 2, when the adhesive layer 300 is formed to correspond to the rim 111, the thickness of the coating vinyl 110 may be reduced to obtain a surface close to the appearance of the vehicle at the time of adhering will be.

또한, 상기와 같이 구성된 제2 실시예의 보수 스티커(1)는, 도 3을 참조하여 도 6의 도시와 같이 종이지(120)로 된 보호지(100)의 표면에 유리막(221)과 도료층(222)으로 된 도장층(200)과 접착층(300)과 이형지(400)가 적층 형성된 구조를 이루는 것인바, 사용시 먼저 접착층(300)으로부터 이형지(400)를 제거한 상태에서, 접착층(300)을 통해 차량(10)의 흠집부분에 접착 사용하면 되는 것으로, 도장층(200)을 통해 흠집의 보수가 가능하게 된다.3, the maintenance sticker 1 according to the second embodiment having the above-described structure is provided with a glass film 221 and a coating layer (not shown) on the surface of the protective paper 100 made of paper paper 120, The release layer 400 is removed from the adhesive layer 300 at the time of using the adhesive layer 300 and the adhesive layer 300 and the release layer 400 are stacked on the adhesive layer 300. [ It is possible to repair the scratches through the paint layer 200 by adhering to the scratches of the vehicle 10. [

이후, 종이지(120)를 제거하되, 이때 종이지(120)는 물을 가해 불린 상태에서 제거하면 되는 것으로, 이렇게 보호지(100)를 제거함으로 도장층(200)이 노출되는 것인바, 그 도장층(200)의 유리막(221)을 통해 도료층(222)이 투시되어 보수가 가능하게 되는 한편, 유리막(221)을 통해 도료층(222)이 코팅된 상태를 이루어 도료층(222)이 보호되게 된다.Then, the paper sheet 120 is removed. At this time, the paper sheet 120 is removed from the state where the paper sheet 120 is filled with water. Thus, the paint layer 200 is exposed by removing the protective paper 100, The paint layer 222 can be repaired through the glass layer 221 of the layer 200 and the paint layer 222 is coated through the glass layer 221 so that the paint layer 222 is protected .

한편, 제2 실시예에서와 같이 보수 스티커(1)를, 보호지(100)를 제거하는 구조를 이루게 함은, 유리막(221)은 스프레이 분사에 의해 비교적 얇은 두께로의 제작이 가능하게 되는 것인바, 외관에 접착 형성되는 보수 스티커(1)의 두께를 최소화시켜 기존 도장면과의 단차를 최소화 시킬 수 있게 된다.On the other hand, when the maintenance sticker 1 is structured to remove the protective paper 100 as in the second embodiment, the glass film 221 can be manufactured with a relatively thin thickness by spraying, , It is possible to minimize the thickness of the repair sticker 1 adhered to the outer surface and to minimize the step with the existing paint surface.

이상에서와 같이 본 발명 차량 및 가전제품 스크래치 보수 스티커는, 차량 또는 전자제품의 외관에 비교적 경미한 흠집이 발생시 남녀 누구나 간편하게 접착 방식을 통해 보수가 가능하게 되는 등 사용상의 편리함을 가져오면서도 저렴한 비용으로 외관의 보수가 가능하다.As described above, the vehicle of the present invention and the scratch repair sticker for household appliances can be easily remedied by a bonding method when a relatively minor scratch on the exterior of a vehicle or an electronic product occurs, Appearance can be repaired.

또한, 보수된 도장면이 코팅 형성된 것인바, 도장층을 구성함에 있어 도장층에 대한 열처리를 수행하지 않더라도 도장면의 장기간 보호가 가능하게 된다.In addition, since the repaired coating surface is coated, it is possible to protect the coating surface for a long period of time without performing heat treatment on the coating layer in forming the coating layer.

한편, 상기에서는 본 발명 보수 스티커의 사용을 차량 및 전자제품에 적용함을 설명하였으나, 이는 그 사용함에 있어 한정되는 것이 아니고 차량 및 전자제품은 물론 도장 및 코팅층을 이루는 다양한 물품에 적용 가능할 것이다.In the above description, the use of the repair sticker according to the present invention is applied to a vehicle and an electronic product. However, the present invention is not limited to the use of the sticker, but may be applied to a variety of articles including paint and coating layers as well as vehicles and electronic products.

100 : 보호지 110 : 코팅비닐
120 : 종이지 200 : 도장층
211 : 도료층 221 : 유리막
222 : 도료층 300 : 접착층
400 : 이형지
S100 : 도장층 형성단계 S200 : 접착층 형성단계
S300 : 이형지 형성단계 S400 : 타발단계100: Protective paper 110: Coated vinyl
120: paper stock 200: paint layer
211: paint layer 221: glass film
222: paint layer 300: adhesive layer
400: release paper
S100: paint layer formation step S200: adhesive layer formation step
S300: release paper forming step S400: punching step

Claims

A protective paper 100;
A coating layer (200) formed on one surface of the protective paper (100);
An adhesive layer 300 formed on the surface of the paint layer 200; And
A release paper (400) for protecting the adhesive layer (300);
, &Lt; / RTI &
The protective paper 100,
And a water-absorbing paper sheet (120)
The coating layer (200)
A transparent glass film 221 having a thickness of 0.05 mm or less; And
A coating layer 222 having a coating of a thickness of 0.05 to 0.1 mm on the glass film 221;
Respectively,
The adhesive layer (300)
Is formed on the surface of the paint layer (222).

The method according to claim 1,
The protective paper 100,
And a transparent coating vinyl 110 made of a resin material having a thickness of 0.05 mm or less,
The coating layer (200)
And a coating layer 211 formed on the entire surface of the coated vinyl 110 with a coating thickness of 0.05-0.1 mm.
The adhesive layer (300)
Is formed on the surface of the paint layer (211).

delete

A coating layer forming step (S100) for forming a coating layer (200) on one side of the protective paper (100), the protective paper being wound and rolled;
An adhesive layer forming step (S200) of forming an adhesive layer (300) for adhering the protective paper (100);
A release paper forming step (S300) of forming a release paper (400) on the surface of the adhesive layer (300); And
A punching step (S400) of tapping the protective paper 100 formed up to the release paper 400;
, &Lt; / RTI &
The protective paper 100,
And a removable paper sheet 120, which is called upon contact with water,
The coating layer forming step (S100)
A transparent glass coating material is sprayed onto the surface of the paper paper 120 to form a glass film 221 having a thickness of 0.05 mm or less,
A coating layer 222 having a thickness of 0.05 to 0.1 mm is formed by spraying the coating material onto the glass coating 221 in a state where the glass coating 221 is cured by 50 to 60% to form the glass coating 221 and the coating layer 222, The coating layer 200 is formed,
In the adhesive layer forming step (S200)
Wherein the coating layer (222) is applied to the surface of the paint layer (222).

6. The method of claim 5,
In the paint layer formation step (S100)
The protective paper 100,
And a transparent coating vinyl 110 made of resin material extruded to have a thickness of 0.05 mm or less,
The coating layer forming step (S100)
The coating material is sprayed and completely cured to a thickness of 0.05 to 0.1 mm at the center with the rim 111 around the entire surface or one surface of one side of the coating vinyl 110 to form a coating layer 211,
In the adhesive layer forming step (S200)
Wherein an adhesive is applied to the entire surface of the paint layer (200) or one side edge (111) of the protective paper (100).

delete