KR101673743B1 - Fermentation accelerator and manufacturing method thereof - Google Patents
Fermentation accelerator and manufacturing method thereof Download PDFInfo
- Publication number
- KR101673743B1 KR101673743B1 KR1020150015121A KR20150015121A KR101673743B1 KR 101673743 B1 KR101673743 B1 KR 101673743B1 KR 1020150015121 A KR1020150015121 A KR 1020150015121A KR 20150015121 A KR20150015121 A KR 20150015121A KR 101673743 B1 KR101673743 B1 KR 101673743B1
- Authority
- KR
- South Korea
- Prior art keywords
- ash
- fly ash
- fermentation accelerator
- present
- activated carbon
- Prior art date
Abstract
본 발명은 발효촉진제에 있어서,석탄회, 플라이애시, 제지소각재, 석고, 석회석, 활성탄 및 산화제를 포함하는 것을 특징으로 하는 발효촉진제에 관한 것으로, 본 발명에 따른 발효촉진제를 축분 또는 음식물폐기물과 톱밥, 왕겨, 수피 등 수분조절제의 혼합물에 첨가하여 발효시키는 경우 톱밥의 부숙기간을 포함하여 퇴비화 기간을 단축시킬수 있으며, 석탄회, 활성탄에 의해 악취발생을 저감시킬수 있는 특징이 있다.The present invention relates to a fermentation accelerator, which comprises coal fly ash, fly ash, paper ash ash, gypsum, limestone, activated carbon and an oxidizing agent, wherein the fermentation accelerator according to the present invention is used as a fermentation accelerator, When the fermentation is performed by adding to a mixture of water regulators such as rice hulls and bark, the composting period can be shortened including the compaction period of the sawdust, and odor generation can be reduced by coal fly ash and activated carbon.
Description
본 발명은 발효촉진제 및 이의 제조방법에 관한 것으로, 보다 상세하게는 석탄회, 활성탄의 다공성에 의한 흡수, 흡착특성과 플라이애시의 흡수, 수화반응에 의한 발열특성을 이용하여 축분이나 음식물폐기물의 퇴비화를 촉진시키는 발효촉진제 및 이의 제조방법에 관한 것이다.
More particularly, the present invention relates to a fermentation accelerator and a method for producing the fermentation accelerator, and more particularly to a fermentation accelerator and a method for producing the fermentation accelerator. And a method for producing the same.
가축의 축분이나 음식물폐기물 등을 톱밥, 수피, 왕겨 등을 수분조절제로 사용하여 퇴비를 제조할때 퇴비 제조기간을 단축하기 위해 사용되는 발효촉진제에 관한 것으로, 퇴비제조는 호기성 미생물의 작용에 의해서 가축분뇨나 음식물폐기물 속의 유기물이 분해되는 과정이다. 따라서 퇴비 제조기간을 단축하기 위해서는 미생물의 활동을 활성화시킴으로서 달성할 수 있으며, 이를 위해 퇴비제조 초기단계에 수분조절제와 함께 발효촉진제를 첨가함으로써 초기 미생물의 활성화를 촉진시킬수 있으며, 그 결과로서 퇴비제조 기간을 단축시킬수 있다. The present invention relates to a fermentation accelerator used for shortening the composting period when compost is produced by using sawdust, bark, rice hull, etc. as a moisture regulator for livestock flour and food waste. The production of compost is controlled by the action of aerobic microorganisms It is the decomposition process of organic matter in manure or food wastes. Therefore, in order to shorten the composting period, it can be achieved by activating the activity of the microorganisms. To this end, the activation of the microorganisms can be promoted by adding the fermentation accelerator together with the moisture control agent at the initial stage of the composting. As a result, Can be shortened.
하지만 종래의 퇴비 발효촉진제는 발효촉진기능과 악취기능을 동시에 갖추지 못하여 적용시 실용성이 떨어지는 문제가 있으며, 발효촉진제를 통해 수분조절제의 통기성 향상 및 퇴비화의 촉진을 통한 퇴비의 제조기간을 단축시킬 수 있는 새로운 퇴비 발효촉진제의 개발이 필요한 실정이다.
However, conventional compost fermentation accelerators fail to provide both fermentation promoting function and malodor function, so that they are inferior in practicality when applied. The fermentation accelerator can improve the permeability of the moisture control agent and shorten the manufacturing period of compost through promotion of composting It is necessary to develop a new compost fermentation accelerator.
따라서, 본 발명이 해결하고자 하는 과제는 축산분뇨 및 음식물 폐기물의 퇴비화 기간을 단축시킬수 있으며, 석탄회와 활성탄에 의해 악취발생을 저감시킬수 있는 발효촉진제 및 이의 제조방법을 제공하는 것이다.
Accordingly, a problem to be solved by the present invention is to provide a fermentation accelerator capable of shortening the composting period of animal manure and food wastes, reducing odor generation by fly ash and activated carbon, and a method for producing the same.
상기 과제를 해결하기 위하여, 본 발명은 발효촉진제에 있어서, 석탄회, 플라이애시, 제지소각재, 석고, 석회석, 활성탄 및 산화제를 포함하는 것을 특징으로 하는 발효촉진제를 제공할 수 있다.In order to solve the above problems, the present invention can provide a fermentation accelerator which comprises coal fly ash, fly ash, paper ash ash, gypsum, limestone, activated carbon and an oxidizing agent as a fermentation accelerator.
본 발명의 일 실시예로 상기 석탄회는 25 내지 35 중량%, 상기 플라이 애시는 15 내지 25 중량%, 상기 제지 소각재는 15 내지 25 중량%, 상기 석고는 15 내지 20 중량%, 상기 석회석은 2 내지 10 중량%, 상기 활성탄은 2 내지 7 중량% 및 상기 산화제는 2 내지 5 중량%인 것을 특징으로 하는 발효촉진제를 제공할 수 있다.In one embodiment of the present invention, the fly ash is 15 to 25 wt%, the paper ash ash is 15 to 25 wt%, the gypsum is 15 to 20 wt%, the limestone is 2 to 20 wt% 10% by weight of the active carbon, 2 to 7% by weight of the activated carbon and 2 to 5% by weight of the oxidizing agent.
본 발명의 일 실시예에서 상기 플라이애시, 제지소각재 및 석고는 수화반응을 하여 수산화칼슘(Ca(OH)2)과 에트린자이트(3CaOAl2O33CaSO432H2O)를 생성하며, 상기 산화제는 황산알루미늄인 것을 특징으로 하는 발효촉진제를 제공할 수 있다.In one embodiment of the present invention, the fly ash, paper ash ash, and gypsum hydrate to produce calcium hydroxide (Ca (OH) 2 ) and etrinite (3CaOAl 2 O 3 3CaSO 4 32H 2 O) A fermentation accelerator which is characterized by being aluminum sulfate.
또한, 본 발명은 발효촉진제 제조방법에 있어서, 석탄회 및 활성탄을 분쇄하는 단계; 상기 분쇄된 석탄회 및 활성탄을 분급하는 단계; 상기 분급된 석탄회 및 활성탄에 플라이애시, 제지소각재, 석회석, 석고 및 산화제를 계량한 후 혼합하는 단계를 포함하는 발효촉진제 제조방법을 제공할 수 있다.According to another aspect of the present invention, there is provided a method for producing a fermentation accelerator, comprising the steps of: pulverizing fly ash and activated carbon; Classifying the pulverized fly ash and activated carbon; A method for manufacturing a fermentation accelerator comprising the steps of weighing fly ash, paper ash, ash, limestone, gypsum and an oxidizing agent and then mixing the classified fly ash and activated carbon.
상기 제조방법에서 상기 석탄회는 25 내지 35 중량%, 상기 플라이 애시는 15 내지 25 중량%, 상기 제지 소각재는 15 내지 25 중량%, 상기 석고는 15 내지 20 중량%, 상기 석회석은 2 내지 10 중량%, 상기 활성탄은 2 내지 7 중량% 및 상기 산화제는 2 내지 5 중량%인 것이 바람직하다.Wherein the fly ash is 15 to 25 wt%, the paper ash ash is 15 to 25 wt%, the gypsum is 15 to 20 wt%, the limestone is 2 to 10 wt% , 2 to 7% by weight of the activated carbon and 2 to 5% by weight of the oxidizing agent.
본 발명의 일 실시예는 상기 혼합된 원료에 비수계 결합제 5 내지 20 중량%를 첨가하여 성형하는 단계를 더 포함하는 것을 특징으로 하는 발효촉진제 제조방법을 제공할 수 있다.One embodiment of the present invention may further comprise a step of adding 5 to 20% by weight of a non-aqueous binder to the mixed raw material to form a fermentation accelerator.
본 발명의 일 실시예는 상기 분급된 석탄회의 입자크기는 0.8 mm 이하이고, 분급된 활성탄의 입자크기가 0.6 mm 이하인 것을 특징으로 하는 발효촉진제 제조방법을 제공할 수 있다.In an embodiment of the present invention, the particle size of the classified fly ash is 0.8 mm or less, and the particle size of the classified activated carbon is 0.6 mm or less.
본 발명의 일 실시예는 상기 비수계 결합제를 첨가하여 성형된 발효촉진제는 지름이 1 내지 7 mm 과립형태인 것을 특징으로 하는 발효촉진제 제조방법을 제공할 수 있다.In one embodiment of the present invention, the fermentation accelerator formed by adding the non-aqueous binder may be in the form of granules having a diameter of 1 to 7 mm.
한편, 본 발명은 상기의 제조방법에 의해 제조된 발효촉진제를 제공할 수 있다.
Meanwhile, the present invention can provide a fermentation accelerator prepared by the above-mentioned production method.
본 발명에 따른 발효촉진제를 축분 또는 음식물폐기물과 톱밥, 왕겨, 수피 등 수분조절제의 혼합물에 첨가하여 발효시키는 경우 톱밥의 부숙기간을 포함하여 퇴비화 기간을 단축시킬수 있으며, 석탄회, 활성탄에 의해 악취발생을 저감시킬수 있다.
When the fermentation accelerator according to the present invention is added to a mixture of a starch or a food waste and a moisture control agent such as sawdust, rice hull or bark to ferment, the composting period can be shortened including the ripening period of the sawdust. Can be reduced.
도 1은 본 발명의 일 실시예에 따른 발효촉진제의 제조공정을 나타내는 단계도이다.
도 2는 본 발명의 실시예 및 비교예 1,2에 따른 발효촉진제 수화 발열온도를 대조군과 비교하여 나타내는 그래프이다.
도 3은 본 발명의 실시예, 비교예 1,2 및 대조구(발효촉진제 사용하지 않음)의 퇴비 발효단계의 온도변화를 나타내는 그래프이다.
도 4는 본 발명의 실시예 및 비교예 1,2에 따라 제조된 퇴비 시험성적서를 나타낸다.
도 5는 발 명의 일 실시예에 따라 발효촉진제와 이에 의해 제조된 퇴비를 나타내는 사진이다. FIG. 1 is a view illustrating a process for producing a fermentation accelerator according to an embodiment of the present invention.
FIG. 2 is a graph showing the hydration heating temperature of the fermentation accelerator according to the present invention and Comparative Examples 1 and 2, in comparison with the control group.
FIG. 3 is a graph showing changes in temperature in the compost fermentation step of Examples of the present invention, Comparative Examples 1 and 2, and a control (no fermentation accelerator is used).
Fig. 4 shows a compost test report prepared according to Examples of the present invention and Comparative Examples 1 and 2. Fig.
FIG. 5 is a photograph showing a fermentation accelerator and compost produced thereby according to an embodiment of the present invention;
이하, 본 발명의 바람직한 실시예를 첨부한 도면을 참조하여 당해 분야의 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 설명하기로 한다. 또한, 본 발명을 설명함에 있어 관련된 공지의 기능 또는 공지의 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략하기로 한다. 그리고 도면에 제시된 어떤 특징들은 설명의 용이함을 위해 확대 또는 축소 또는 단순화된 것이고, 도면 및 그 구성요소들이 반드시 적절한 비율로 도시되어 있지는 않다. 그러나 당업자라면 이러한 상세 사항들을 쉽게 이해할 것이다.Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. And certain features shown in the drawings are to be enlarged or reduced or simplified for ease of explanation, and the drawings and their components are not necessarily drawn to scale. However, those skilled in the art will readily understand these details.
본 발명은 가축분뇨나 음식물폐기물을 수분조절제를 사용하여 퇴비를 제조할때 악취 발생을 억제하고 퇴비화 기간을 단축시키기 위한 것이다. 이를 위하여 본 발명은 석탄회, 플라이애시, 제지소각재, 석고, 석회석, 활성탄 및 산화제를 혼합한 원료 및 비수계 결합제를 포함하는 발효촉진제를 제공한다. 본 발명의 일 실시예에서 상기 석탄회는 25 내지 35 중량%, 상기 플라이 애시는 15 내지 25 중량%, 상기 제지 소각재는 15 내지 25 중량%, 상기 석고는 15 내지 20 중량%, 상기 석회석은 2 내지 10 중량%, 상기 활성탄은 2 내지 7 중량% 및 상기 산화제는 2 내지 5 중량%인 혼합된 원료에 상기 비수계 결합제를 5 내지 20 중량%를 포함하는 것이 바람직하나 반드시 이에 한정되는 것은 아니다. The present invention aims at suppressing odor generation and shortening the composting period when compost is produced using a moisture control agent for livestock manure or food wastes. To this end, the present invention provides a fermentation accelerator comprising a raw material in which coal fly ash, fly ash, paper ash, ash, gypsum, limestone, activated carbon and oxidizer are mixed and a non-aqueous binder. In one embodiment of the present invention, the fly ash is 15 to 25 wt%, the paper ash is 15 to 25 wt%, the gypsum is 15 to 20 wt%, the limestone is 2 to 20 wt% And the non-aqueous binder is contained in an amount of 5 to 20% by weight in a mixed raw material of 10 to 10% by weight, the activated carbon in an amount of 2 to 7% by weight and the oxidizing agent in an amount of 2 to 5% by weight.
한편, 본 발명에 사용되는 플라이애시, 제지소각재, 석고에는 CaO, CaSO4와 같은 성분이 포함되어 있으며, 이와같은 CaO, CaSO4 성분과 가축분뇨 또는 음식물폐기물에 포함되어 있는 수분과 수화반응을 하여 수산화칼슘(Ca(OH)2)과 에트린자이트(3CaOAl2O33CaSO432H2O)를 생성하며, 이때 가축분뇨나 음식물폐기물에 포함되어 있는 수분을 저감시키며, 수화반응이 일어날때 악취를 일으키는 NH3, H2S 등 물질이 에트린자이트 결정에 둘러쌓여 악취 비산을 방지한다. On the other hand, there is fly ash, paper ash, gypsum to be used in the present invention includes the components such as CaO, CaSO 4, in such a CaO, CaSO 4 component and the manure or are included in the food waste water and the hydration reaction in It produces calcium hydroxide (Ca (OH) 2 ) and etrinite (3CaOAl 2 O 3 3CaSO 4 32H 2 O), which reduces moisture contained in livestock manure or food wastes, The substances such as NH 3 and H 2 S are surrounded by the ettringite crystals to prevent the spread of odors.
또한 석탄회와 활성탄은 미세한 기공을 다량으로 함유하고 있어 이러한 기공에 의해 악취를 발생하는 물질이 기공내부로 흡착되어 악취발생을 막아주는 기능을 한다.In addition, the coal fly ash and activated carbon contain a large amount of fine pores, and the substances generating odor due to these pores are adsorbed into the pores to prevent the generation of odors.
산화제로 사용되는 황산알루미늄은 가축분뇨 또는 음식물폐기물중의 수분과 반응하여 [H]+를 생성하고, 생성된 [H]+는 플라이애시, 제지소각재 등에 포함되어 있는 CaO에 의한 pH의 상승을 억제하여 암모니아 발생을 저감시키는 역할을 한다.Aluminum sulfate is used as the oxidizing agent produces a [H] + reacts with the moisture in the animal waste or food waste, and suppress an increase in the pH due to the CaO that is generated [H] + is embedded in a fly ash, paper ash Thereby reducing the generation of ammonia.
도 1은 본 발명의 일실시예에 따른 발효촉진제의 제조공정을 나타내는 단계도이다.FIG. 1 is a view illustrating a process for producing a fermentation accelerator according to an embodiment of the present invention.
도 1을 참조하면, 본 발명은 석탄회 및 활성탄을 핀밀 또는 해머밀 또는 이와 같은 기능을 하는 분쇄기로 공급하여 분쇄하는 단계; 분쇄된 석탄회와 활성탄을 진동스크린과 같은 분급장치를 통해 입도분리하는 단계; 석탄회, 플라이애시, 제지소각재, 석회석, 석고, 산화제를 계량하여 혼합기에 투입하는 단계; 혼합된 원료에 비수계의 결합제를 첨가하여 결합제와 발효촉진제 원료를 혼합하는 단계 및 비수계 결합제와 혼합된 발효촉진제 원료를 과립기에 공급하여 과립을 제조하는 단계를 포함하여 발효촉진제를 제조할 수 있다.Referring to FIG. 1, the present invention provides a method for manufacturing a carbon nanotube, comprising the steps of: supplying coal fly ash and activated carbon to a pin mill, a hammer mill or a pulverizer having such a function; Separating the pulverized fly ash and activated carbon through a classification device such as a vibration screen; Weighing fly ash, fly ash, paper ash, limestone, gypsum and oxidizing agent into a mixer; Adding a non-aqueous binder to the mixed raw material to mix the binder and the fermentation accelerator raw material, and feeding the raw material of the fermentation enhancer mixed with the non-aqueous binder to a granulator to prepare granules, thereby producing a fermentation accelerator .
상기 석탄회 및 활성탄을 분쇄하는 단계에서 석탄회는 분쇄한 후, 분급을 하여 입자크기가 0.8 mm 이하, 폐활성탄은 입상 폐활성탄을 분쇄한후 분급을 하여 입자크기가 0.6 mm 이하인 것이 바람직하다. 석탄회의 입자크기가 0.8 mm 및 폐활성탄의 입자크기가 0.6 mm가 초과하는 경우에는 다공성에 의한 흡수, 흡착특성이 떨어지게 되어 본 발명의 특성을 저감시키는 결과를 초래하게 된다. In the step of pulverizing the coal fly ash and the activated carbon, it is preferable that the coal fly ash is pulverized and classified to have a particle size of 0.8 mm or less, and the pulverized activated carbon is pulverized after granular activated carbon is pulverized to have a particle size of 0.6 mm or less. When the particle size of the fly ash is 0.8 mm and the particle size of the activated carbon is more than 0.6 mm, the absorption and adsorption characteristics due to porosity are lowered, resulting in the reduction of the characteristics of the present invention.
또한, 상기 비수계 결합제와 혼합하여 제조된 발효촉진제는 지름이 1 내지 7 mm의 과립형태인 것이 바람직 하나 반드시 이에 한정되는 것은 아니다. The fermentation accelerator prepared by mixing with the non-aqueous binder is preferably in the form of granules having a diameter of 1 to 7 mm, but is not limited thereto.
이하, 본 발명을 구체적인 실시예에 의해 보다 더 상세히 설명하고자 한다. 하지만, 본 발명은 하기 실시예에 의해 한정되는 것은 아니며, 본 발명의 사상과 범위 내에서 여러가지 변형 또는 수정할 수 있음은 이 분야에서 당업자에게 명백할 것이다. Hereinafter, the present invention will be described in more detail by way of specific examples. It will be apparent to those skilled in the art that the present invention is not limited by the following examples, but can be variously modified or changed within the spirit and scope of the present invention.
실시예 Example
아래의 표 1은 본 발명의 실시예 및 비교예 1,2에 따른 발효촉진제의 원료배합비를 나태나는 표이다.Table 1 below shows the mixing ratio of raw materials of the fermentation accelerator according to Examples of the present invention and Comparative Examples 1 and 2.
도 2는 본 발명의 실시예 및 비교예 1,2에 따른 발효촉진제가 물과 접촉했을때 수화 발열온도의 변화 특성을 대조군과 비교하여 나타내는 그래프이다.FIG. 2 is a graph showing changes in the hydration heat generation temperature when the fermentation accelerator is contacted with water according to Examples of the present invention and Comparative Examples 1 and 2, in comparison with the control group.
또한, 아래의 표 2는 본 발명의 본발명의 실시예 및 비교예 1,2에 따른 발효촉진제의 물리적인 특성(pH 및 흡수율)을 나타내는 표이다.Table 2 below shows the physical properties (pH and absorption rate) of the fermentation accelerator according to Examples of the present invention and Comparative Examples 1 and 2 of the present invention.
도 2와 표 2의 결과를 살펴보면, 비교예 1 및 2와 달리 제지소각재 및 석고를 포함하는 실시예에 의해 제조된 발효촉진제가 수화반응에 의한 발열특성 및 흡수율 특성이 우수함을 알 수 있다.2 and Table 2, it can be seen that the fermentation accelerator prepared by the examples including the papermaking ashes and the gypsum, in contrast to the comparative examples 1 and 2, is excellent in heat generation characteristics and water absorption characteristics by hydration reaction.
아래의 표 3은 위 실시예 및 비교예 1,2와 같은 조성을 가진 발효촉진제를 가축분뇨에 수분조절제로서 톱밥을 사용하여 퇴비를 제조할 때 발효촉진제를 5 중량% 첨가하여 제조된 퇴비의 분석결과를 나타낸다. 이때 가축분뇨와 수분조절제로서 톱밥의 혼합후 함수율은 55 %로 조절하였다.Table 3 below shows the results of analysis of the compost produced by adding 5% by weight of a fermentation accelerator when preparing compost using sawdust as a moisture control agent for livestock manure, . At this time, the moisture content after mixing of livestock manure and sawdust as moisture control agent was adjusted to 55%.
도 3은 축분과 수분조절제 중량에 대해서 본 발명의 실시예 및 비교예 1,2의 발효촉진제를 5 중량% 첨가한 퇴비의 발효가 진행되는 초기단계에서 미생물의 활성화에 의한 발효촉진 효과를 나타내기 위한 온도상승 상태를 기록한 그래프이다. 도 3에서 나타나는 대조구는 발효촉진제를 사용하지 않은 퇴비를 나타낸다. Fig. 3 shows the effect of accelerating the fermentation by microbial activation at the initial stage of fermentation of the compost containing 5 wt% of the fermentation accelerator of the example of the present invention and the fermentation accelerator of the comparative examples 1 and 2, And the temperature rise state for the temperature rise. The control shown in Fig. 3 represents a compost without using a fermentation accelerator.
도 3을 살펴보면 본 발명의 실시예에 의한 발효촉진제를 첨가한 퇴비는 발효촉진제를 사용하지 않는(대조구) 퇴비보다 뚜렷한 온도상승 효과를 나타내고 있어, 본 발명에 의한 발효촉진제는 퇴비화 기간을 탄축시킬 수 있음을 알 수 있다.
As shown in FIG. 3, the compost with the fermentation accelerator according to the embodiment of the present invention exhibits a distinct temperature increasing effect compared to the compost without the fermentation accelerator (control). Therefore, the fermentation accelerator according to the present invention can calm the composting period .
이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.
Claims (10)
석탄회, 플라이애시, 제지소각재, 석고, 석회석, 활성탄 및 산화제를 포함하며,
상기 석탄회는 25 내지 35 중량%, 상기 플라이 애시는 15 내지 25 중량%, 상기 제지 소각재는 15 내지 25 중량%, 상기 석고는 15 내지 20 중량%, 상기 석회석은 2 내지 10 중량%, 상기 활성탄은 2 내지 7 중량% 및 상기 산화제는 2 내지 5 중량%이며,
상기 산화제는 황산알루미늄인 것을 특징으로 하는 발효촉진제.In the fermentation accelerator,
Coal ash, fly ash, paper ash, gypsum, limestone, activated carbon and oxidants,
Wherein the fly ash is 15 to 25 wt.%, The paper ash ash is 15 to 25 wt.%, The gypsum is 15 to 20 wt.%, The limestone is 2 to 10 wt.%, 2 to 7 wt%, and the oxidizing agent is 2 to 5 wt%
Wherein the oxidizing agent is aluminum sulfate.
상기 플라이애시, 제지소각재 및 석고는 수화반응을 하여 수산화칼슘(Ca(OH)2)과 에트린자이트(3CaOAl2O33CaSO432H2O)를 생성하는 것을 특징으로 하는 발효촉진제.The method according to claim 1,
Wherein the fly ash, paper ash ash, and gypsum are hydrated to produce calcium hydroxide (Ca (OH) 2 ) and etrinite (3CaOAl 2 O 3 3CaSO 4 32H 2 O).
(a) 석탄회 및 활성탄을 분쇄하는 단계;
(b) 상기 분쇄된 석탄회 및 활성탄을 분급하는 단계;
(c) 상기 분급된 석탄회 및 활성탄에 플라이애시, 제지소각재, 석회석, 석고 및 산화제를 계량한 후 혼합하는 단계를 포함하며,
상기 석탄회는 25 내지 35 중량%, 상기 플라이 애시는 15 내지 25 중량%, 상기 제지 소각재는 15 내지 25 중량%, 상기 석고는 15 내지 20 중량%, 상기 석회석은 2 내지 10 중량%, 상기 활성탄은 2 내지 7 중량% 및 상기 산화제는 2 내지 5 중량%이며,
상기 (c)단계에서 혼합된 원료에 비수계 결합제 5 내지 20 중량%를 첨가하여 성형하는 단계를 더 포함하는 것을 특징으로 하는 발효촉진제 제조방법.In the method for producing a fermentation accelerator,
(a) pulverizing fly ash and activated carbon;
(b) classifying the pulverized fly ash and activated carbon;
(c) weighing fly ash, paper ash ash, limestone, gypsum and oxidizing agent to the classified fly ash and activated carbon, and mixing,
Wherein the fly ash is 15 to 25 wt.%, The paper ash ash is 15 to 25 wt.%, The gypsum is 15 to 20 wt.%, The limestone is 2 to 10 wt.%, 2 to 7 wt%, and the oxidizing agent is 2 to 5 wt%
Further comprising the step of adding 5 to 20% by weight of a non-aqueous binder to the raw material mixed in the step (c) and then molding the fermentation accelerator.
상기 (b)단계에서 분급된 석탄회의 입자크기는 0.8 mm 이하이고, 분급된 활성탄의 입자크기가 0.6 mm 이하인 것을 특징으로 하는 발효촉진제 제조방법.6. The method of claim 5,
Wherein the particle size of the fly ash classified in the step (b) is 0.8 mm or less, and the particle size of the classified activated carbon is 0.6 mm or less.
상기 비수계 결합제를 첨가하여 성형된 발효촉진제는 지름이 1 내지 7 mm 과립형태인 것을 특징으로 하는 발효촉진제 제조방법.6. The method of claim 5,
Wherein the fermentation accelerator formed by adding the non-aqueous binder is a granule having a diameter of 1 to 7 mm.