KR101651098B1 - Apparatus for Making Flame Resistant EPS Sandwich Pannel - Google Patents

Apparatus for Making Flame Resistant EPS Sandwich Pannel Download PDF

Info

Publication number
KR101651098B1
KR101651098B1 KR1020140178354A KR20140178354A KR101651098B1 KR 101651098 B1 KR101651098 B1 KR 101651098B1 KR 1020140178354 A KR1020140178354 A KR 1020140178354A KR 20140178354 A KR20140178354 A KR 20140178354A KR 101651098 B1 KR101651098 B1 KR 101651098B1
Authority
KR
South Korea
Prior art keywords
liquid
adhesive
eps
adhesive liquid
plate
Prior art date
Application number
KR1020140178354A
Other languages
Korean (ko)
Other versions
KR20160071080A (en
Inventor
김유석
김형주
Original Assignee
정우화인 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정우화인 주식회사 filed Critical 정우화인 주식회사
Priority to KR1020140178354A priority Critical patent/KR101651098B1/en
Publication of KR20160071080A publication Critical patent/KR20160071080A/en
Application granted granted Critical
Publication of KR101651098B1 publication Critical patent/KR101651098B1/en

Abstract

본 발명은 난연성 EPS 샌드위치 패널의 자동제조장치(100)를 제공한다.
본 발명은 제1 접착액 공급부에서 이소시아네이트 접착용액(A 액)을 공급받고, 제2 접착액 공급부에서 폴리올과 무기 난연제와 유기 바인더 및 첨가제로 구성된 폴리올 접착용액(B 액)을 공급받아서, 이들을 상면 철판(130)과 하면 철판(140)의 위에서 우레탄 반응을 시키고, 우레탄 반응에 의한 우레탄 접착제를 자동공정으로 EPS 보드(120)의 상면과 저면에 도포시킴과 동시에, 상기 상면 철판(130)과 EPS 보드(120)와 하면 철판(140)의 사이에 난연성 우레탄 접착제를 삽입시켜서 견고한 우레탄 결합을 형성한다.
본 발명은 상기 폴리올 접착용액(B 액) 중에 무기질 난연제를 포함하고 있음에도 불구하고, 공급관의 내부에서 막힘 현상이 발생되지 않으며, 균일한 난연성을 보장하고, 생산성과 경제성을 충족시킬 수 있게 된다. The present invention provides an apparatus (100) for automatic production of a flame-retardant EPS sandwich panel.
The present invention is characterized in that an isocyanate bonding solution (liquid A) is supplied from a first adhesive liquid supply portion and a polyol bonding solution (liquid B) comprising a polyol, an inorganic flame retardant, an organic binder and an additive is supplied to the second adhesive liquid supply portion, Urethane reaction is performed on the upper side of the steel plate 130 and the lower side of the steel plate 140 so that the urethane adhesive by the urethane reaction is applied to the upper and lower surfaces of the EPS board 120 by an automatic process, A flame-retardant urethane adhesive is inserted between the board 120 and the bottom steel plate 140 to form a rigid urethane bond.
Although the present invention includes the inorganic flame retardant in the polyol adhesive solution (liquid B), the clogging phenomenon does not occur in the inside of the supply pipe, uniform flame retardancy is ensured, and productivity and economy are satisfied.

Description

난연성 EPS 샌드위치 패널의 제조장치{Apparatus for Making Flame Resistant EPS Sandwich Pannel} FIELD OF THE INVENTION [0001] The present invention relates to a flame-retardant EPS sandwich panel,

본 발명은 난연성이 뛰어난 EPS 샌드위치 패널의 제조장치에 관한 것으로서, 더욱 상세하게는 샌드위치 패널로 알려진 발포폴리스티렌폼의 양면에 철판을 자동적으로 접착시키되, 난연성 우레탄 접착제를 사용하여 난연성과 접착강도를 동시에 향상시킬 수 있고, 자동 공정으로 가동시킬 수 있는 EPS 샌드위치 패널의 제조장치에 관한 것이다.
The present invention relates to an apparatus for manufacturing an EPS sandwich panel having excellent flame retardancy, and more particularly, to an apparatus for manufacturing an EPS sandwich panel having excellent flame retardancy, and more particularly, to an automatic sandwich panel To an apparatus for manufacturing an EPS sandwich panel which can be operated by an automatic process.

일반적으로 발포폴리스티렌(Expendable Polystyrene: EPS)은 희고 가벼우며 단열성이 좋고, 방음성과 성형가공성이 우수하므로, 각종 포장재료, 단열용 건축재료, 절연재료, 바다의 부표, 기타 장식품 등으로 사용되고 있다. In general, Expendable Polystyrene (EPS) is used as various packaging materials, building materials for insulation, insulation materials, sea buoys and other ornaments because it is white and light, has excellent heat insulation, and has excellent soundproofing and molding processability.

발포폴리스티렌(EPS)은 스티렌 단량체를 현탁중합시키면서 발포제를 동시에 가압첨가하여 발포성 비드를 만들고, 발포성 비드를 고온으로 가열하여 그 내부에 투입된 발포제가 팽창하도록 하면서, 그 팽창과정에서 연화된 스티렌중합체의 비드가 그 내부에 미세한 기포를 형성하도록 유도하여 제조되어진다. The foamed polystyrene (EPS) is produced by suspension polymerization of a styrene monomer and simultaneous pressurization of the foaming agent to produce a foamable bead, heating the foamable bead to a high temperature so that the foamed agent injected into the foamed bead expands, To form fine bubbles therein.

이러한 발포폴리스티렌은 그 체적의 약 98% 정도가 공기이고, 그 나머지 2 %가 스티렌수지로 이루어져 있으므로, 무엇보다 가볍고, 공기에 의한 단열성이 양호하며, 내수성과 완충성 및 방음성이 뛰어난 특성을 가지고 있다. 이와 같은 발포폴리스티렌의 특성을 이용하여, 건축물의 내외부 단열재로 각광을 받고 있으며, 다양한 형태의 단열재를 개발하여 사용하고 있다. Since about 98% of the volume of the foamed polystyrene is air and the remaining 2% is made of styrene resin, it has the characteristics of being lighter than anything, having good heat insulation by air, excellent in water resistance, cushioning and soundproofing . Using such properties of expanded polystyrene, it is widely used as an inner and outer insulation material of buildings, and various types of insulation materials have been developed and used.

그렇지만, 발포폴리스티렌 단열재는 열에 약해서 수축변형이 심하고, 전체적으로 열가소성수지로 구성되어 있어서, 화재에 노출되었을 경우, 순식간에 타버리는 단점이 있다. 이러한 단점은 발포폴리스티렌 수지에 난연성을 부가함으로써 극복될 수 있다. However, the foamed polystyrene insulation material is fragile due to heat and shrinking deformation, and is composed entirely of a thermoplastic resin, so that it is burned in an instant when it is exposed to fire. This disadvantage can be overcome by adding flame retardancy to the expanded polystyrene resin.

한편, 발포폴리스티렌의 뛰어난 단열성과 성형성 및 저렴한 생산비용은 건축재료의 용도로서 많은 장점을 가지고 있고, 다양한 형태로 사용되고 있다. On the other hand, excellent heat insulating properties, moldability and low production cost of expanded polystyrene have many advantages as the use of building materials and are used in various forms.

특히, 발포폴리스티렌 보드를 내부에 형성하고, 그 양면에 강철패널을 부착시킬 경우 소위 EPS 샌드위치 패널이 형성되어지게 된다. 이러한 EPS 샌드위치 패널은 뛰어난 단열성과 방음성 및 저렴한 생산비용에 기인하여, 냉동창고의 벽재, 보온보냉 창고, 조립식 건물, 또는 각종 축사 등에 널리 사용되고 있다. Particularly, when a foamed polystyrene board is formed inside and a steel panel is attached to both sides thereof, a so-called EPS sandwich panel is formed. These EPS sandwich panels are widely used in wall materials of refrigerated warehouses, refrigerated warehouses, prefabricated buildings, or various kinds of houses due to their excellent heat insulation, soundproofing and low production costs.

오늘날 일반적으로 사용되고 있는 EPS 샌드위치 패널은 그 중앙에 발포폴리스티렌 보드 또는 난연성 발포폴리스티렌 보드를 위치시키고, 그 양측면에 강철판재를 갖다 대고, 상기 발포폴리스티렌 보드와 상기 강철판재의 사이에 접착제를 개입시켜서, 단단한 판재 구조물로 형성되어 있다. 이때, 상기 접착제는 일반적으로 유기접착성 재질로 형성된 것이어서, 외부에서 화염이 도달하게 되면 쉽게 타버리는 가연성 유기물질로 구성되어 있다. An EPS sandwich panel commonly used today has a foamed polystyrene board or a flame-retardant foamed polystyrene board placed at the center thereof, a steel plate is placed on both sides thereof, an adhesive is interposed between the foamed polystyrene board and the steel plate, And is formed as a plate material structure. At this time, the adhesive is generally formed of an organic adhesive material, and is composed of a flammable organic material that burns easily when a flame reaches the outside.

유기물 접착제의 이러한 성질은 난연성 EPS 샌드위치 패널의 난연성을 오히려 떨어뜨리게 되는 하나의 요인으로 작용할 수 있다. 이러한 단점을 개선하기 위해 불연성 첨가제를 배합하는 등 난연성을 높이기 위한 다양한 연구가 진행되고 있으나, 만족할 만한 수준에 이르지는 못하고 있는 것으로 여겨진다. This property of the organic adhesive can serve as a factor in reducing the flame retardancy of the flame retardant EPS sandwich panel. In order to improve these disadvantages, various studies have been carried out to improve the flame retardancy, such as blending incombustible additives, but it is considered that they are not satisfactory.

유기물 접착제에 난연성 무기재료를 첨가할 경우, 난연성 측면에서 향상된 경향을 보여주고 있지만, 무기재료에 의하여 오히려 접착성능이 떨어지게 되고, 이로 인하여 접착제로서의 본래적 기능을 기대하기 어려운 점이 존재하고 있다. 난연성 향상을 위하여, 접착성을 훼손하게 될 경우, 난연성 EPS 샌드위치 패널은 접착력 저하로 인하여 제품의 품질에 심각한 문제를 발생하게 되고, 특히 계절에 따른 기후 및 습도의 변화에 따라 건축물의 안정성이 문제될 수 있다. The addition of the flame retardant inorganic material to the organic adhesive exhibits an improved tendency in terms of flame retardancy, but the adhesive property is rather deteriorated by the inorganic material, which makes it difficult to expect the original function as an adhesive. In order to improve the flame retardancy, the flame-retardant EPS sandwich panel is seriously problematic in the quality of the product due to the deterioration of the adhesive strength when the adhesiveness is deteriorated. In particular, the stability of the building is problematic due to seasonal changes in climate and humidity .

또한, 이러한 난연성 접착제를 개발완료하였을 경우에도, 그러한 난연성 접착제를 이용하여 자동공정으로 작업을 수행할 수 없다면, 제품의 품질 및 제품의 생산성 측면에서 볼 때 불완전한 기술 개발이라고 하지 않을 수 없을 것이다. Even if such a flame-retardant adhesive has been developed, if such a flame-retardant adhesive can not be used in an automatic process, it would be an incomplete technology development in terms of product quality and product productivity.

결과적으로, 본 발명자들은 유기물 접착제에 난연성 부여와 접착력 향상이 서로 상반된 측면을 가지고 있는 것이지만, 이러한 한계점을 해결한 난연성 접착제를 개발하여 이미 특허출원을 진행한 바 있고, 금번에는 상기 난연성 접착제를 이용하여 난연성 EPS(Expandible Polystyrene) 샌드위치 패널을 자동공정으로 제조할 수 있는 제조장치 설비를 개발하게 됨으로써, 본 발명을 완성하게 된 것이다.
As a result, the inventors of the present invention have contradicted each other with respect to imparting flame retardancy to the organic adhesive agent and enhancing the adhesive strength. However, the present inventors have already developed a flame-retardant adhesive that solves these limitations and have already filed a patent application. The inventors of the present invention have completed the present invention by developing an equipment for manufacturing a flame-retardant EPS (Expandable Polystyrene) sandwich panel by an automatic process.

대한민국 등록특허 제10-528608호 "폴리우레탄 접착제 조성물 및 그의 제조방법" (2005. 11. 8.);Korean Patent No. 10-528608 entitled " Polyurethane Adhesive Composition and Method for Producing the Same "(2005. 8. 8.); 대한민국 등록특허 제10-1093528호 "폴리우레탄 접착제 조성물 및 그의 제조방법" (2011. 12. 7.);Korean Patent No. 10-1093528 entitled "Polyurethane Adhesive Composition and Process for its Preparation" (December 7, 2011); 대한민국 등록특허 제10-1025248호 "팽창흑연 및/또는 황토 접착액을 이용한 발포폴리스티렌폼의 난연 처리방법" (2011. 3. 21.);Korean Patent No. 10-1025248 entitled "Flame Retardant Treatment Method of Expanded Polystyrene Foam Using Expanded Graphite and / or Loess Adhesive Liquid" (Mar. 21, 2011); 대한민국 등록특허 제10-1179943호 "인계 난연제와 팽창흑연을 이용한 발포 폴리스티렌폼의 난연방법" (2012. 8. 30.).Korean Patent No. 10-1179943 "Flame retarding method of expanded polystyrene foam using phosphorus flame retardant and expanded graphite" (Aug. 30, 2012).

본 발명은, 상기 종래기술의 제반 문제점을 해결하기 위한 것으로, 샌드위치 패널로 알려진 발포폴리스티렌폼의 양면에 철판을 자동적으로 접착시키되, 난연성 우레탄 접착제를 사용하여 난연성과 접착강도를 동시에 향상시킬 수 있고, 자동 공정으로 가동시킬 수 있는 난연성 EPS 샌드위치 패널의 제조장치를 제공하는데 그 목적이 있다.
Disclosure of Invention Technical Problem [8] The present invention has been made in view of the above problems, and it is an object of the present invention to provide a method for automatically bonding an iron plate to both surfaces of a foamed polystyrene foam known as a sandwich panel, And to provide a manufacturing apparatus of a flame retardant EPS sandwich panel which can be operated by an automatic process.

본 발명은, 상기 목적을 달성하기 위하여, The present invention, in order to achieve the above object,

이소시아네이트 접착용액을 보관하고 공급하는 제1 접착액(A 액) 공급부와 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제를 보관하고 공급하는 제2 접착액(B 액) 공급부로 구성된 접착제 원료공급부와; And a second adhesive liquid (liquid B) supply part for storing and supplying the first adhesive liquid (liquid A) supply part for storing and supplying the isocyanate bonding solution and the additives such as polyol, inorganic flame retardant, Wow;

난연성 발포폴리스티렌(EPS: Expandible Polystyrene) 보드를 받쳐주고 위에서 아래 방향으로 공급해주는 경사받침판으로 형성된 EPS 보드 공급부와;An EPS board supply unit formed of an inclined support plate for supporting a flame-retardant expandable polystyrene (EPS) board and supplying the EPS board in a downward direction;

상기 EPS 보드의 상면에 접착되는 상면 철판을 권취된 상태에서 풀어 공급하는 제1 언코일러와, 상기 상면 철판의 회전방향을 변경시켜서 계속 공급하는 원판 회전로울러로 구성된 제1 패널 공급부와; A first panel feeder configured by a first uncoiler that unwinds and feeds an upper surface iron plate adhered to an upper surface of the EPS board in a wound state, and a disk rotating roller that changes the rotation direction of the upper surface iron plate and supplies the same;

상기 EPS 보드의 하면에 접착되는 하면 철판을 권취된 상태에서 풀어 공급하는 제2 언코일러와, 상기 하면 철판의 표면에 가압 압착가공해주는 철판 압착머신으로 구성된 제2 패널 공급부와; A second panel feeder configured by a second uncoiler for unwinding and feeding the lower backing plate adhered to the lower surface of the EPS board in a wound state, and a pressing machine for pressing the surface of the lower backing plate;

상기 상면 철판의 상부 표면 위에 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 B액분사관과, 상기 상면 철판의 상부 표면 위에 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 A액분사관과, 상기 상면 철판의 상부 표면 위에서 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합하여 신속한 반응을 유도하는 제1 믹싱플레이트로 구성된 제1 접착원료 혼합부와; A first B liquid distributing pipe for dropping or spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the upper surface iron plate; and a second B liquid distributor for dropping or spraying the first adhesive liquid (liquid A) (B liquid) and the first adhesive liquid (liquid A) on the upper surface of the upper surface iron plate to induce a rapid reaction, and a second mixing plate A first adhesive raw material mixing portion composed of a first adhesive raw material mixing portion;

상기 하면 철판의 상부 표면 위에 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 B액분사관과, 상기 하면 철판의 상부 표면 위에 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 A액분사관과, 상기 하면 철판의 상부 표면 위에서 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합하여 신속한 반응을 유도하는 제2 믹싱플레이트로 구성된 제2 접착원료 혼합부; 를 포함하고 있는 난연성 EPS 샌드위치 패널의 자동제조장치를 제공한다. A second B liquid dispersion pipe for dropping or spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the lower metal plate; and a second B liquid distributing pipe for dropping or spraying the first adhesive liquid (liquid A) (B liquid) and the first adhesive liquid (liquid A) on the upper surface of the lower backing plate to induce a rapid reaction, and a second mixing plate A second adhesive raw material mixing portion constituted by the first adhesive raw material mixing portion; The present invention provides an apparatus for automatically manufacturing a flame-retardant EPS sandwich panel.

본 발명에 있어서, 상기 제1 접착액(A 액) 공급부는 이소시아네이트 원료를 저장하여 보관하고 필요시 공급하는 공급탱크와, 상기 이소시아네이트 원료를 라인을 따라 공급시키는 공급펌프를 포함하고 있다. In the present invention, the first adhesive liquid (liquid A) supply section includes a supply tank for storing and storing the isocyanate material, and a supply pump for supplying the isocyanate material along the line.

본 발명에 있어서, 상기 제2 접착액(B 액) 공급부는 폴리올과 무기 난연제와 반응촉매 등의 첨가제를 저장하여 보관하고 필요시 공급하는 공급탱크와, 상기 폴리올과 무기 난연제와 반응촉매 등을 혼련시키고 균일한 조성을 유도하는 교반 날개와, 상기 교반 날개에 대한 회전 동력을 발생시키는 모터와, 상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제를 포함한 제2 접착액(B 액)을 라인을 따라 공급시키는 공급 펌프를 포함하고 있는 것이 바람직하다. In the present invention, the second adhesive liquid (liquid B) supply unit may include a supply tank for storing and storing additive such as polyol, an inorganic flame retardant, and a reaction catalyst, and a supply tank for kneading the polyol, the inorganic flame retardant, And a second adhesive liquid (liquid B) containing additives such as polyol, inorganic flame retardant, organic binder, and reaction catalyst is introduced into a line And a feed pump for feeding the feed pump.

본 발명에 있어서, 상기 제1 B액분사관은 원통형 관으로 형성되어 있고 상기 라인으로 부터 상기 제2 접착액(B 액)을 공급받게 되는 원통형 공급관과, 상기 원통형 공급관의 내부에서 서서히 회전하면서 상기 제2 접착액(B 액)을 교반시켜주는 스프링 믹서와, 상기 스프링 믹서에 회전동력을 제공하는 회전모터와, 상기 원통형 공급관의 저면에 다수 형성되어 있고 상기 제2 접착액(B 액)을 아래쪽으로 뿌려주는 노즐구멍을 포함하고 있는 것이 바람직하다. In the present invention, it is preferable that the first B liquid crystal distribution tube is a cylindrical tube and has a cylindrical supply tube for receiving the second adhesive liquid (liquid B) from the line, A plurality of second adhesive liquids (liquid B) which are formed on the bottom surface of the cylindrical supply pipe and which are arranged in a downward direction It is preferable to include a nozzle hole for spraying.

본 발명에 있어서, 상기 제2 B액분사관의 기능 및 구조는 상기 제1 B액분사관의 기능 및 구조와 동일하다.
In the present invention, the function and structure of the second B liquid crystal panel are the same as those of the first B liquid crystal panel.

본 발명에 의한 난연성 EPS 샌드위치 패널의 제조장치를 이용할 경우, 난연성 접착제를 사용하여 EPS 샌드위치 패널을 자동공정으로 제조할 수 있는 장점이 있다. When the flame retardant EPS sandwich panel manufacturing apparatus according to the present invention is used, the EPS sandwich panel can be manufactured by an automatic process using a flame-retardant adhesive.

또한, 본 발명에 의한 난연성 EPS 샌드위치 패널의 제조장치는, 접착제 원료 자체에 포함된 무기 난연제의 존재 여부에 상관없이, 상기 접착제 원료를 샌드위치 패널의 철판 위에 계속적으로 균일하게 공급할 수 있으므로, 난연성 EPS 샌드위치 패널의 접착력을 더욱 향상시킬 수 있고, 최종적인 제품의 난연성 및 품질의 고급화를 기할 수 있는 장점도 있다. In addition, the apparatus for producing a flame-retardant EPS sandwich panel according to the present invention can continuously and uniformly supply the adhesive raw material on the iron plate of the sandwich panel regardless of the presence or absence of the inorganic flame retardant contained in the adhesive raw material itself. The adhesive strength of the panel can be further improved, and the final product can be improved in flame retardancy and quality.

또한, 본 발명에 의한 난연성 EPS 샌드위치 패널의 제조장치는, 접착제 원료 자체에 무기질 난연제가 존재함에도 불구하고, 여전히 자동화 공정으로 진행될 수 있으므로, 제품의 생산성을 향상시킬 수 있고, 제품의 경쟁력을 더욱 배가시킬 수 있는 특장점이 있다.
In addition, the apparatus for manufacturing a flame-retardant EPS sandwich panel according to the present invention can still proceed to an automated process in spite of the presence of an inorganic flame retardant in the adhesive raw material itself, thereby improving the productivity of the product, There are special features that can be made.

도 1은 본 발명의 난연성 EPS 샌드위치 패널의 제조장치(100)에 관한 개략적인 전개도이고,
도 2는 본 발명의 기술적 특징을 구성하는 제2 접착액(B 액)의 분사관에 관한 개략적인 개념도이다. 1 is a schematic development view of an apparatus 100 for manufacturing a flame retardant EPS sandwich panel of the present invention,
Fig. 2 is a schematic conceptual view of a spray tube of a second adhesive liquid (liquid B) which constitutes a technical feature of the present invention.

이하, 본 발명의 바람직한 실시예를 예시도면에 의거하여 상세히 설명한다. 다만, 첨부된 도면은 본 발명의 기술사상을 보다 상세하게 설명하기 위한 것일 뿐이며, 본 발명의 기술사상이 이에 한정되는 것이 아니며, 다양한 변형이 가능함을 미리 밝혀둔다. 또한, 본 발명의 명세서에 있어서, 동일한 부분에 대해서는 동일한 참조번호를 사용하기로 하며, 이 기술분야에서 공지된 것으로서 통상의 기술을 가진 자에 의해 용이하게 창작될 수 있는 부분에 대해서는 상세한 설명을 생략하기로 한다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. It is to be noted that the accompanying drawings are only for explaining the technical idea of the present invention in detail and that the technical idea of the present invention is not limited thereto and that various modifications are possible. In the description of the present invention, the same reference numerals are used for the same parts, and parts that can be easily created by those having ordinary skill in the art are omitted in the description of the present invention .

본 발명은 난연성 접착제를 사용하여 EPS 샌드위치 패널을 자동공정으로 제조할 수 있는 EPS 샌드위치 패널의 제조장치(100)를 제공한다. The present invention provides an apparatus (100) for manufacturing an EPS sandwich panel, which can be used to manufacture an EPS sandwich panel by an automatic process using a flame-retardant adhesive.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 이소시아네이트 접착용액을 보관하고 공급하는 제1 접착액(A 액) 공급부와, 폴리올과 무기 난연제와 반응촉매 등의 첨가제를 보관하고 공급하는 제2 접착액(B 액) 공급부로 구성된 접착제 원료공급부를 포함하고 있다. An apparatus 100 for manufacturing an EPS sandwich panel according to the present invention includes a first adhesive liquid (liquid A) supply part for storing and supplying an isocyanate bonding solution, a second adhesive liquid (liquid A) supplying part for storing and supplying additives such as polyol, And an adhesive material supply portion composed of an adhesive liquid (liquid B) supply portion.

본 발명에 있어서, 상기 제1 접착액(A 액) 공급부는 이소시아네이트 원료를 저장하여 보관하고 필요시 공급하는 공급탱크(111)와, 상기 이소시아네이트 원료를 라인(10)을 따라 공급시키는 공급펌프(113)를 포함하고 있다. 상기 이소시아네이트 원료는 우레탄 반응에서 필요로 하는 이소시아네이트기를 가진 성분을 의미하고, 상기 공급탱크(111)에 저장되었다가, 상기 공급펌프(113)에 의하여 라인(10)을 따라 접착원료 혼합부로 이동하게 된다. 상기 이소시아네이트 원료는 이 기술분야에서 통상적으로 사용되고 있는 것을 이용하고 있고, 또한 우레탄 반응은 일반적으로 잘 알려져 있는 것이므로, 상세한 설명을 생략한다. In the present invention, the first adhesive liquid (liquid A) supply unit may include a supply tank 111 for storing and storing the isocyanate material, if necessary, and a supply pump 113 for supplying the isocyanate material along the line 10 ). The isocyanate material refers to a component having an isocyanate group required for the urethane reaction and is stored in the supply tank 111 and is moved to the adhesive material mixing portion along the line 10 by the supply pump 113 . The isocyanate raw materials are those commonly used in this technical field, and the urethane reaction is generally well known, and thus a detailed description thereof will be omitted.

본 발명에 있어서, 상기 제2 접착액(B 액) 공급부는 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제를 저장하여 보관하고 필요시 공급하는 공급탱크(112)와, 상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등을 혼련시키고 균일한 조성을 유도하는 교반 날개(114)와, 상기 교반 날개에 대한 회전 동력을 발생시키는 모터(116)와, 상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제를 포함한 제2 접착액(B 액)을 라인(10)을 따라 공급시키는 공급 펌프(118)를 포함하고 있는 것이 바람직하다. In the present invention, the second adhesive liquid (liquid B) supply unit may include a supply tank 112 for storing and storing additives such as polyol, inorganic flame retardant, organic binder, and reaction catalyst, if necessary, A stirring blade 114 for kneading an organic binder and a reaction catalyst and inducing a uniform composition, a motor 116 for generating a rotational power for the stirring blade, an organic binder such as an organic binder and a reaction catalyst And a supply pump 118 for supplying the second adhesive liquid (liquid B) containing the additive of the additive along the line 10.

상기 제2 접착액(B 액) 공급부는 상기 제2 접착액(B 액) 중에 무기 난연제 성분이 포함되어 있고, 상기 무기 난연제 성분은 미세한 분말상의 입자로 형성되어 있고, 상기 액상의 폴리올 성분에 비하여 그 비중이 더 높은 것이므로 상기 교반 날개(114)에 의하여 혼합시켜주지 않을 경우, 상기 액상의 제2 접착액 중에 침전되어지는 경향을 보이게 된다. 이와 같은 제반 사정을 고려하여, 상기 제2 접착액(B 액) 공급부를 상면 철판(130)과 하면 철판(140)의 위치보다 더 높은 위치에 설치하는 것이 바람직하다. Wherein the second adhesive liquid (liquid B) supply portion includes an inorganic flame retardant component in the second adhesive liquid (liquid B), the inorganic flame retardant component is formed of fine powder particles, It tends to be precipitated in the liquid second adhesive liquid unless it is mixed by the stirring vane 114 because the specific gravity is higher. It is preferable that the second adhesive liquid (liquid B) supply unit is provided at a higher position than the upper surface iron plate 130 and the lower surface of the lower plate 140, considering all of the above circumstances.

상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제는 제2 접착액(B 액)을 형성하게 된다. 상기 폴리올은 이 기술분야에서 우레탄 접착제를 제조할 때 통상적으로 사용하는 것을 그대로 활용하여 사용할 수 있다. The additive such as the polyol, the inorganic flame retardant, the organic binder and the reaction catalyst forms the second adhesive liquid (liquid B). The polyol may be used as it is in the art in the production of urethane adhesives.

상기 무기 난연제는 화재 발생시 고온에서 팽창하여 보호 피막을 형성하는 것으로서 초기 부피의 250 배 내지 350 배 정도로 팽창될 수 있는 팽창 흑연을 사용하는 것이 바람직하다. 상기 팽창 흑연은 화재 발생시 고온에서 팽창하여 차단막(Char)을 형성하게 되고, 상기 팽창 흑연의 차단막이 화염의 진행을 막게 됨으로써 우레탄 접착제 및 샌드위치 패널에 대해 난연성을 부여하는 것이다. 상기 팽창 흑연은 단독으로 사용될 수 있고, 좀더 효율적인 난연 성능을 발휘하기 위하여, 무기질 난연제 또는 유기질 난연제로 형성된 난연 보조재료를 첨가할 수 있다. The inorganic flame retardant is preferably expanded graphite which expands at a high temperature in the event of a fire to form a protective coating and can expand to about 250 to 350 times its initial volume. The expanded graphite expands at a high temperature when a fire occurs to form a shielding film Char. The shielding film of the expanded graphite prevents flame propagation, thereby imparting flame retardancy to the urethane adhesive and the sandwich panel. The expanded graphite may be used alone, and in order to exhibit more efficient flame retardant performance, a flame retardant auxiliary material formed of an inorganic flame retardant or an organic flame retardant may be added.

상기 무기질 난연제 또는 유기질 난연제는 그 효과 측면에서 살펴볼 때, 냉각효과, 보호막(Char)효과, 희석소화효과, 활성라디칼 흡수효과로 나뉘어 구분될 수 있다. 본 발명은 상기 냉각효과, 보호막(Char)효과, 희석소화효과, 활성라디칼 흡수효과를 달성할 수 있는 각종 난연제를 단독으로, 또는 상기 팽창 흑연과 함께 사용할 수 있다. The inorganic flame retardant or the organic flame retardant can be divided into a cooling effect, a Char effect, a diluting effect and an active radical absorption effect in terms of the effect. The present invention can be used alone or in combination with the expanded graphite to achieve the cooling effect, the protective effect (Char), the diluting effect and the active radical absorption effect.

상기 유기 바인더는 난연 첨가제를 사용함으로써 필연적으로 감소되는 접착력을 보강하고 증진시켜주는 물질로써, EPS 접착제와 난연 첨가제의 배합 및 분산안정성 증대와 연소시 난연 첨가제의 물성을 도와주는 여러 가지 성능 면에서 매우 중요한 물질이다. 상기 유기 바인더로서는 GUM류가 바람직하고, 이는 수소결합, 공유결합, 분자간 인력을 모두 발현하여 물질간의 접착력을 크게 상승시켜주기 때문이다. The organic binder is a material that reinforces and enhances the adhesive force which is inevitably decreased by using a flame retardant additive. It is a material which improves the blending and dispersion stability of the EPS adhesive and the flame retardant additive and improves the properties of the flame- It is an important material. The organic binder is preferably GUM, because it exhibits both hydrogen bonding, covalent bonding, and intermolecular attraction, thereby greatly increasing the adhesion between the materials.

상기 난연제와 상기 유기 바인더 성분들을 투입함으로 인한 반응성 저하를 방지하고 분산성과 양호한 물성을 유지시켜주는 기타 첨가제 성분을 통상적인 방식으로 포함할 수 있다. 상기 기타 첨가제는 이 기술분야에서 우레탄 반응시에 통상적으로 사용되는 물, 정포제, 분산제, 반응 개시제 등을 의미하고, 이 기술분야에서 통상적으로 사용되는 분량만큼 사용되어진다. 따라서, 이에 대해서는 상세한 설명을 생략하기로 한다. Other additives may be added in a conventional manner to prevent deterioration of reactivity due to the addition of the flame retardant and the organic binder components and to maintain dispersibility and good physical properties. The above-mentioned other additive means water, a foam stabilizer, a dispersant, a reaction initiator and the like commonly used in the urethane reaction in this technical field, and is used in an amount commonly used in this technical field. Therefore, a detailed description thereof will be omitted.

상기 공급탱크(112)의 내부에 존재하는 교반 날개(114)는 모터(116)에 의해 서서히 회전하면서, 상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등을 혼련시키고 균일한 조성을 유도한다. 특히, 상기 무기 난연제가 포함되어 있으므로, 그의 침강을 방지하기 위하여, 상기 교반 날개(114)를 반드시 필요한 것임을 언급한다. The stirring vanes 114 existing in the supply tank 112 are slowly rotated by the motor 116 to knead the polyol, the inorganic flame retardant, the organic binder, the reaction catalyst, and the like to induce a uniform composition. In particular, since the above inorganic flame retardant is included, it is mentioned that the stirring vane 114 is indispensable in order to prevent its settling.

상기 공급 펌프(118)는 액상의 제2 접착액(B 액)을 라인(10)을 따라 이송시키는 것으로서, 상기 제2 접착액(B 액)의 내부에 미세한 입자형태의 무기 난연제가 혼합되어 있는 점을 고려하여, 통상의 펌프를 사용할 수도 있지만, 박막을 이용한 다이아프램 펌프를 사용하는 것이 더욱 좋다.
The supply pump 118 feeds a liquid second adhesive liquid (liquid B) along the line 10, and an inorganic flame retardant in the form of fine particles is mixed in the second adhesive liquid (liquid B) In consideration of the point, a normal pump can be used, but it is better to use a diaphragm pump using a thin film.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 난연성 EPS 보드(120)를 받쳐주고 위에서 아래 방향으로 공급해주는 경사받침판(122)으로 형성된 EPS 보드 공급부를 포함하고 있다. The apparatus 100 for manufacturing an EPS sandwich panel according to the present invention includes an EPS board supply unit formed of an inclined support plate 122 for supporting the flame-retardant EPS board 120 and supplying the flame-retardant EPS board 120 downward.

상기 경사받침판(122)은 상부에서 EPS 보드(120)를 붙잡은 상태에서 놓아주면 EPS 보드(120)가 아래 방향으로 미끄러져 내려갈 정도로 경사면을 이루고 있도록 하는 것이 바람직하다. 상기 EPS 보드(120)는 발포제를 함침시킨 폴리스티렌 입자를 성형기의 내부에서 고온으로 발포시켜서 블록형 발포폴리스티렌을 얻고, 이것을 보드 형태로 절단하여 만든 단열재용 EPS 판재를 말한다. 상기 EPS 보드(120)는 KS 규격에 합격된 제품을 사용하는 것이 바람직하다.
The inclined support plate 122 may be inclined so that the EPS board 120 slides downward when the EPS board 120 is held in a state where the EPS board 120 is held on the upper side. The EPS board 120 refers to an EPS plate for thermal insulation material obtained by foaming polystyrene particles impregnated with a foaming agent into a molding machine at a high temperature to obtain block-type expanded polystyrene and cutting the same into a board form. It is preferable that the EPS board 120 uses a product that conforms to the KS standard.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 상기 EPS 보드(120)의 상면에 접착되는 상면 철판(130)을 공급하는 제1 패널 공급부를 포함하고 있다. The apparatus 100 for manufacturing an EPS sandwich panel according to the present invention includes a first panel supply unit for supplying an upper surface iron plate 130 adhered to an upper surface of the EPS board 120.

상기 제1 패널 공급부는 상기 상면 철판(130)을 권취시키고 있고 작업시 상기 상면 철판(130)을 서서히 풀어서 공급하는 제1 언코일러(132)와, 상기 상면 철판(130)의 회전방향을 최초 공급시의 방향과 반대방향으로 변경시켜서 계속 공급하는 원판 회전로울러(134)를 포함하여 구성하고 있다. 상기 제1 언코일러(132)는 EPS 보드(120)의 상면에 접착되는 상면 철판(130)을 권취시키고 있는데 반하여, 제2 언코일러(142)는 상기 EPS 보드(120)의 반대편 하면에 접착되는 하면 철판(140)을 권취시키고 있다. 상기 원판 회전로울러(134)는 상기 상면 철판(130)의 표면이 뒤집어진 상태로 상기 EPS 보드(120)의 윗면에 접촉되어지도록 하기 위하여, 회전되면서 상기 상면 철판(130)을 서서히 최초의 공급되는 방향으로부터 반대 방향으로 변경시켜주게 된다.
The first panel supply unit includes a first uncoiler 132 for winding up the upper surface iron plate 130 and gradually releasing and supplying the upper surface iron plate 130 in operation and a second uncoiler 132 for rotating the upper surface iron plate 130 for the first time And a disc rotating roller 134 for changing the direction of rotation of the disc rotating rollers 134 in the opposite direction. The first uncoiler 132 winds the upper surface iron plate 130 attached to the upper surface of the EPS board 120 while the second uncoiler 142 is attached to the lower surface of the opposite side of the EPS board 120 And the lower surface iron plate 140 is wound. The disc rotating rollers 134 are rotated so that the upper surface iron plate 130 is in contact with the upper surface of the EPS board 120 while the surface of the upper surface iron plate 130 is turned upside down, Direction to the opposite direction.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 상기 EPS 보드(120)의 하면에 접착되는 하면 철판(140)을 공급하는 제2 패널 공급부를 포함하고 있다. The apparatus 100 for manufacturing an EPS sandwich panel according to the present invention includes a second panel supply unit for supplying a bottom plate 140 adhered to a lower surface of the EPS board 120.

상기 제2 패널 공급부는 상기 EPS 보드(120)의 하면에 접착되는 하면 철판(140)을 권취된 상태에서 풀어 공급하는 제2 언코일러(142)를 포함하고 있고, 상기 하면 철판(140)의 표면에 가압 압착가공해주는 철판 압착머신(144)을 더욱 포함하고 있는 것이 바람직하다. 상기 제2 언코일러(142)는 이미 설명한 바와 같이, 상기 EPS 보드(120)의 반대편 하면에 접착되는 하면 철판(140)을 권취시키고 있고, 작업시 이를 서서히 풀어주게 된다. 상기 철판 압착머신(144)은 상기 제2 언코일러(142)에서 공급되는 하면 철판(140)의 표면에 각종 인쇄 방식이나 부분 가압 처리 방식으로 가공하는 일련의 표면가공 설비를 의미한다.
The second panel feeder includes a second uncoiler 142 that unwinds and feeds a bottom plate 140 adhered to a bottom surface of the EPS board 120. The bottom surface of the bottom plate 140 And a press machine 144 for press-pressing the work piece. As described above, the second uncoiler 142 winds the bottom plate 140 adhered to the opposite bottom surface of the EPS board 120, and gradually releases the bottom plate 140 during operation. The iron plate pressing machine 144 refers to a series of surface processing equipment that is processed on the surface of the bottom steel plate 140 supplied from the second uncoiler 142 by various printing methods or partial pressure processing methods.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 상기 상면 철판(130)의 상부 표면 위에서 상기 제1 접착액(A 액)과 상기 제2 접착액(B 액)을 혼합하여 반응시키는 제1 접착원료 혼합부를 포함하고 있다. The apparatus 100 for manufacturing an EPS sandwich panel according to the present invention is characterized in that the first adhesive liquid (liquid A) and the second adhesive liquid (liquid B) are mixed and reacted on the upper surface of the upper surface iron plate 130 And an adhesive raw material mixing portion.

상기 제1 접착원료 혼합부는 상기 상면 철판(130)의 상부 표면 위에서 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 B액분사관(152)과, 상기 상면 철판(130)의 상부 표면 위에 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 A액분사관(154)과, 상기 상면 철판(130)의 상부 표면 위에서 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합하여 신속한 반응을 유도하는 제1 믹싱플레이트(156)로 구성되어 있다. The first adhesive material mixing portion includes a first B liquid distributing pipe 152 for dropping or spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the upper surface iron plate 130, (B liquid) on the upper surface of the upper surface iron plate 130, and a second A liquid distributing pipe 154 for dropping or spraying or spraying the first adhesive liquid (liquid A) And a first mixing plate 156 for mixing the first adhesive liquid (liquid A) and inducing a quick reaction.

상기 제1 B액분사관(152)은 상기 라인(10)을 통하여 상기 B액의 공급탱크(112)로부터 상기 제2 접착액(B 액)을 공급받게 되는 원통형 공급관(172)을 포함하고 있다. 상기 원통형 공급관(172)은 그 단면이 원통형 관으로 형성되어 있고, 그 내부에는 서서히 회전하면서 상기 제2 접착액(B 액)을 교반시켜주는 스프링 믹서(174)를 포함하고 있다. 상기 스프링 믹서(174)는 회전모터(176)에 의하여 회전동력을 제공받게 되고, 상기 원통형 공급관(172)의 내부에서 무기질 난연제 등이 관의 내부에서 침전되어 액상 접착용액의 유동을 방해하는 현상을 방지하게 된다. 또한, 상기 원통형 공급관(172)의 저면에는 다수의 노즐구멍(178)이 형성되어 있어서, 상기 원통형 공급관(172)의 내부로 공급된 상기 제2 접착액(B 액)을 아래쪽으로 분사시키거나 뿌려주거나 적하시키게 된다. 일반적으로, 상기 원통형 공급관(172)은 외부에서 가압된 정도에 따라, 상기 다수의 노즐구멍(178)을 통하여 액상의 접착용액을 세차게 분사시키거나 약하게 뿌려주거나 자연스럽게 자유낙하 방식으로 떨어뜨려서 적하시키게 된다. The first B liquid dispensing pipe 152 includes a cylindrical supply pipe 172 for receiving the second adhesive liquid (liquid B) from the supply tank 112 of the liquid B through the line 10. [ The cylindrical supply pipe 172 is formed in a cylindrical tube with a cross section and includes a spring mixer 174 which slowly rotates while stirring the second adhesive liquid (liquid B). The spring mixer 174 is supplied with rotational power by a rotation motor 176 and the inorganic flame retardant or the like is precipitated in the inside of the cylindrical supply pipe 172 to interfere with the flow of the liquid bonding solution . A plurality of nozzle holes 178 are formed in the bottom surface of the cylindrical supply pipe 172 so that the second adhesive liquid B supplied to the inside of the cylindrical supply pipe 172 is sprayed downward Or drop. Generally, the cylindrical supply pipe 172 is sprayed with a weak liquid or sprinkled weakly through the plurality of nozzle holes 178 according to the degree of external pressurization, or naturally dropped in a free-fall manner .

상기 제1 A액분사관(154)은 상기 라인(10)을 통하여 상기 A액의 공급탱크(111)로부터 상기 제1 접착액(A 액)을 공급받게 되는 원통형 공급관(도시되지 않음)과 상기 원통형 공급관의 저면에 형성된 다수의 분사노즐(도시되지 않음)로 구성되는 것이 바람직하다. 이러한 구조는 상기 제1 B액분사관(152)의 구조 및 기능과 대동소이하고, 다만 상기 스프링 믹서(174)가 존재하지 않는 점에서만 차이가 있는 것이므로, 구체적인 설명을 생략하기로 한다. The first A liquid dispensing pipe 154 is connected to a cylindrical supply pipe (not shown) through which the first adhesive liquid (liquid A) is supplied from the supply tank 111 of the liquid A through the line 10, And a plurality of injection nozzles (not shown) formed on the bottom surface of the supply pipe. This structure differs from the structure and function of the first B liquid crystal distribution pipe 152 only in that there is no spring mixer 174, so a detailed description thereof will be omitted.

상기 제1 믹싱플레이트(156)는 상면 철판(130)의 상부 표면 위에서 상기 제1 접착액(A 액)과 상기 제2 접착액(B 액)을 서로 혼합시켜주는 기구로서, 상기 상면 철판(130)의 진행방향에 대해 직각 방향으로 전ㆍ후진운동을 반복적으로 번갈아가면서 수행하게 된다. The first mixing plate 156 is a mechanism for mixing the first adhesive liquid (liquid A) and the second adhesive liquid (liquid B) on the upper surface of the upper surface iron plate 130, In the direction perpendicular to the traveling direction of the vehicle.

본 발명에 의한 EPS 샌드위치 패널의 제조장치(100)는 상기 하면 철판(140)의 상부 표면 위에서 상기 제1 접착액(A 액)과 상기 제2 접착액(B 액)을 혼합하여 반응시키는 제2 접착원료 혼합부를 포함하고 있다. The apparatus 100 for manufacturing an EPS sandwich panel according to the present invention is characterized in that an upper surface of the lower steel plate 140 is coated with a second adhesive liquid (liquid A) and a second adhesive liquid (liquid B) And an adhesive raw material mixing portion.

상기 제2 접착원료 혼합부는 상기 하면 철판(140)의 상부 표면 위에서 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 B액분사관(162)과, 상기 하면 철판(140)의 상부 표면 위에 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 A액분사관(164)과, 상기 하면 철판(140)의 상부 표면 위에서 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합하여 신속한 반응을 유도하는 제2 믹싱플레이트(166)로 구성되어 있다. The second adhesive material mixing portion includes a second B liquid distributing pipe 162 for dropping, spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the lower steel plate 140, A second A liquid distributing pipe 164 for dropping or spraying or spraying the first adhesive liquid A on the upper surface of the lower iron plate 140; And a second mixing plate 166 for mixing the first adhesive liquid (liquid A) and inducing a quick reaction.

본 발명에 있어서, 상기 제2 B액분사관(162)의 기능 및 구조는 상기 제1 B액분사관(152)의 기능 및 구조와 동일하고, 상기 제2 A액분사관(164)의 기능 및 구조는 상기 제1 A액분사관(154)의 기능 및 구조와 동일하며, 상기 제2 믹싱플레이트(166)의 기능 및 구조는 상기 제1 믹싱플레이트(156)의 기능 및 구조와 동일하다. 따라서, 이들에 대한 상세한 설명은 생략하기로 한다.
In the present invention, the function and structure of the second B liquid crystal distribution pipe (162) are the same as the function and structure of the first B liquid crystal distribution pipe (152), and the function and structure of the second A liquid crystal liquid distribution pipe And the function and structure of the second mixing plate 166 are the same as those of the first mixing plate 156. Therefore, a detailed description thereof will be omitted.

이와 같이 구성된 본 발명은 다음과 같은 방식으로 작동되어진다. The present invention configured in this manner is operated in the following manner.

작업자는 상기 공급탱크(111)에 우레탄 반응에 필요한 이소시아네이트 접착용액(A 액)을 저장하여 보관하고, 상기 공급탱크(121)에 우레탄 반응에 필요한 폴리올과 무기 난연제와 유기 바인더 및 반응촉매 등의 첨가제를 계량하여 투입하고, 상기 모터(116)를 가동하여 서서히 교반시켜서 폴리올 접착용액(B 액)을 형성함으로써, 난연용 EPS 샌드위치 패널의 제조작업을 준비한다.The operator stores and stores the isocyanate bonding solution (liquid A) required for the urethane reaction in the supply tank 111. In the supply tank 121, an additive such as a polyol, an inorganic flame retardant, an organic binder and a reaction catalyst And the motor 116 is actuated and stirred to form a polyol adhesive solution (liquid B), thereby preparing an EPS sandwich panel for flame retardancy.

작업자는 EPS 보드(120)를 상기 경사받침판(122)에서 아래쪽으로 밀어 내리고, 상기 제1 언코일러(132)에서는 상기 EPS 보드(120)의 상면에 접착되어질 상면 철판(130)을 공급시키고, 상기 제2 언코일러(142)에서는 상기 EPS 보드(120)의 하면에 접착되어질 하면 철판(140)을 공급시킨다. The operator pushes down the EPS board 120 downward from the inclined support plate 122 and feeds the upper surface steel plate 130 to be bonded to the upper surface of the EPS board 120 in the first uncoiler 132, In the second uncoiler 142, the steel plate 140 is adhered to the lower surface of the EPS board 120.

작업자는 라인(10)상의 밸브(20)들을 열고, 상기 공급탱크(121)에서 폴리올 접착용액(B 액)을 상기 제1 B액분사관(152)(162)으로 이송시키고, 상기 공급탱크(111)에서 이소시아네이트 접착용액(A 액)을 상기 제1 A액분사관(154)(164)으로 이송시킨다. The operator opens the valves 20 on the line 10 and transfers the polyol bonding solution (liquid B) from the supply tank 121 to the first B liquid distributing pipe 152 (162) , The isocyanate bonding solution (liquid A) is transferred to the first A liquid distributing pipe 154 (164).

이때, 상기 제1 B액분사관(152)(162)에서는 회전모터(176)에 의해 스프링 믹서(174)가 회전하고 있으므로, 상기 폴리올 접착용액(B 액)은 비교적 무거운 입자상의 무기질 난연제를 포함하고 있음에도 불구하고, 관의 내부에서 침적되지 아니한다. 상기 폴리올 접착용액(B 액)은 상기 제1 B액분사관(152)(162)을 통하여, 철판의 상면으로 떨어뜨려져서 적하되어지고, 그 뒤를 이어서, 또한, 상기 이소시아네이트 접착용액(A 액)이 상기 제1 A액분사관(154)(164)을 통하여 철판의 상면으로 떨어뜨려져서 적하되어지므로, 상기 폴리올 접착용액(B 액)의 위쪽에 떨어지게 되는 것이다. At this time, since the spring mixer 174 is rotated by the rotary motor 176 in the first B liquid crystal distribution pipes 152 and 162, the polyol adhesive solution (liquid B) contains a relatively heavy particulate inorganic flame retardant In spite of this, it is not immersed in the inside of the pipe. The polyol adhesive solution (liquid B) was dropped onto the upper surface of the iron plate through the first B liquid distributing pipes 152 and 162 and then dropped thereon. Then, the isocyanate bonding solution (liquid A) Is dropped onto the upper surface of the steel plate through the first A liquid distributing pipe (164), and dropped onto the upper side of the polyol adhesive solution (liquid B).

상기 폴리올 접착용액(B 액) 중의 폴리올 성분과 상기 이소시아네이트 접착용액(A 액) 중의 이소시아네이트 성분은 서로 반응하게 되고, 그 결과 상기 철판의 상면에서 우레탄 결합을 신속하게 진행하게 된다. The polyol component in the polyol adhesive solution (solution B) and the isocyanate component in the isocyanate bonding solution (solution A) react with each other, and as a result, the urethane bonding proceeds rapidly on the upper surface of the steel sheet.

상기 믹싱플레이트(156)(166)는 진행 방향에 대해 직각 방향으로 전진 및 후진 운동을 반복함으로써, 상기 폴리올 접착용액(B 액)과 상기 이소시아네이트 접착용액(A 액)의 혼합을 유도하고, 신속한 우레탄 반응을 유도하게 된다. The mixing plates 156 and 166 repeat the forward and backward movements in the direction perpendicular to the advancing direction to induce mixing of the polyol adhesive solution (liquid B) and the isocyanate bonding solution (liquid A) Thereby inducing the reaction.

상기 폴리올 접착용액(B 액) 중에는 무기 난연제로서 팽창 흑연성분이 포함되어 있으므로, 우레탄 반응에 의한 우레탄 접착제는 필연적으로 난연성을 가지게 되고, 난연성 접착제를 형성하게 되는 것이다. 상기 우레탄 반응은 통상적인 것이므로, 구체적인 설명을 생략한다. Since the polyol adhesive solution (liquid B) contains an expanded graphite component as an inorganic flame retardant, the urethane adhesive by the urethane reaction necessarily has flame retardancy and forms a flame-retardant adhesive. Since the urethane reaction is conventional, a detailed description thereof will be omitted.

이때, 상기 상면 철판(130)을 살펴보면, 상기 우레탄 반응에 의해 우레탄 접착제가 형성되어짐과 동시에, 상기 상면 철판(130)은 상기 원판 회전로울러(134)의 표면을 따라 반원으로 회전하면서 최초의 방향과 반대 방향으로 이송되어지게 된다. 그 결과, 상기 상면 철판(130)의 윗면에 형성된 우레탄 접착제는 아래쪽으로 전환된 상태에서, 상기 EPS 보드(120)의 상면으로 투입되어지게 된다. The urethane adhesive is formed by the urethane reaction and the upper surface iron plate 130 is rotated in a semicircular shape along the surface of the disk rotating roller 134, It is conveyed in the opposite direction. As a result, the urethane adhesive formed on the upper surface of the upper surface iron plate 130 is inserted into the upper surface of the EPS board 120 in a state of being downwardly shifted.

한편, 상기 하면 철판(140)을 살펴보면, 상기 우레탄 반응에 의해 우레탄 접착제가 형성되어짐과 동시에, 상기 하면 철판(140)은 그 상태로 최초의 방향과 동일하 방향으로 이송되어지게 된다. 그 결과, 상기 하면 철판(140)의 윗면에 형성된 우레탄 접착제는 상기 EPS 보드(120)의 하면으로 투입되어지게 된다. Meanwhile, the urethane adhesive is formed by the urethane reaction and the bottom steel plate 140 is transported in the same direction as the initial direction. As a result, the urethane adhesive formed on the upper surface of the lower metal plate 140 is inserted into the lower surface of the EPS board 120.

결과적으로, 최종적인 제품은 상면 철판(130)과 EPS 보드(120)와 하면 철판(140)의 사이에 상기 우레탄 반응에 의해 형성된 난연성 우레탄 접착제를 자동 공정으로 형성한 것임을 알 수 있다.
As a result, it can be understood that the final product is formed by the automatic process of the flame-retardant urethane adhesive formed by the urethane reaction between the upper surface iron plate 130, the EPS board 120 and the lower surface iron plate 140.

이상에서 본 발명에 의한 EPS 샌드위치 패널의 제조장치(100) 및 그 작동방법을 구체적으로 설명하였으나, 이는 본 발명의 가장 바람직한 실시양태를 기재한 것일 뿐, 본 발명이 이에 한정되는 것은 아니며, 첨부된 특허청구범위에 의해서 그 범위가 결정되어지고 한정되어진다. While the present invention has been particularly shown and described with respect to preferred embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, And the range is determined and limited by the claims.

또한, 이 기술분야에서 통상의 지식을 가진 자라면 누구나 본 발명의 명세서의 기재내용에 의하여 다양한 변형 및 모방을 행할 수 있을 것이나, 이 역시 본 발명의 범위를 벗어난 것이 아님은 명백하다고 할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope of the present invention.

100 : EPS 샌드위치 패널의 제조장치,
111, 112: 원료 공급탱크, 113, 118 : 공급 펌프,
114 : 교반 날개, 116 : 모터,
120 : EPS 보드, 122 : 경사받침판,
130 : 상면 철판, 132, 142 : 언코일러,
134 : 원판 회전로울러, 140 : 하면 철판,
144 : 가공처리 장비, 152, 162 : B액 분사관,
154, 164 : A액 분사관, 156, 166 : 믹싱플레이트100: EPS sandwich panel manufacturing equipment,
111, 112: raw material supply tank, 113, 118: feed pump,
114: stirring blade, 116: motor,
120: an EPS board, 122: an inclined support plate,
130: Upper plate, 132, 142: Uncoiler,
134: disc rotating roller, 140: lower iron plate,
144: processing equipment, 152, 162: liquid dispenser B,
154, 164: A liquid spray tube, 156, 166: mixing plate

Claims (5)

이소시아네이트 접착용액을 보관하고 공급하는 제1 접착액(A 액) 공급부와;
폴리올과 무기 난연제와 유기 바인더 및 반응촉매의 첨가제를 저장하여 보관하고 필요시 공급하는 공급탱크(112)와, 상기 폴리올과 무기 난연제와 반응촉매 등을 혼련시키고 균일한 조성을 유도하는 교반 날개(114)와, 상기 교반 날개에 대한 회전 동력을 발생시키는 모터(116)와, 상기 폴리올과 무기 난연제와 유기 바인더 및 반응촉매의 첨가제를 포함한 제2 접착액(B 액)을 이송시키는 공급 펌프(118)로 구성된 제2 접착액(B 액) 공급부와;
EPS 보드(120)를 받쳐주고 위에서 아래 방향으로 공급해주는 경사받침판(122)으로 형성된 EPS 보드 공급부와;
상기 EPS 보드(120)의 상면에 접착되는 상면 철판(130)을 권취된 상태에서 풀어 공급하는 제1 언코일러(132)와, 상기 상면 철판(130)의 회전방향을 변경시켜서 계속 공급하는 원판 회전로울러(134)로 구성된 제1 패널 공급부와;
상기 EPS 보드(120)의 하면에 접착되는 하면 철판(140)을 권취된 상태에서 풀어 공급하는 제2 언코일러(142)로 구성된 제2 패널 공급부와;
상기 상면 철판(130)의 상부 표면 위에서, 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 B액분사관(152)과, 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제1 A액분사관(154)과, 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합시키는 제1 믹싱플레이트(156)로 구성된 제1 접착원료 혼합부와;
상기 하면 철판(140)의 상부 표면 위에서, 상기 제2 접착액(B 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 B액분사관(162)과, 상기 제1 접착액(A 액)을 떨어뜨리거나 뿌려주거나 분사시키는 제2 A액분사관(164)과, 상기 제2 접착액(B 액)과 상기 제1 접착액(A 액)을 혼합시키는 제2 믹싱플레이트(166)로 구성된 제2 접착원료 혼합부; 를
포함하고 있는, 난연성 EPS 샌드위치 패널의 자동제조장치(100).
A first adhesive liquid (liquid A) supply part for storing and supplying the isocyanate adhesive solution;
A feed tank 112 for storing and storing additives such as a polyol, an inorganic flame retardant, an organic binder, and a reaction catalyst; a stirring blade 114 for kneading the polyol, the inorganic flame retardant and a reaction catalyst and inducing a uniform composition; And a feed pump 118 for feeding the second adhesive liquid (liquid B) containing the additive of the polyol, the inorganic flame retardant, the organic binder and the reaction catalyst to the stirring blade A second adhesive liquid (liquid B) supply unit;
An EPS board supply unit formed of an inclined support plate 122 that supports the EPS board 120 and supplies the EPS board 120 downward;
A first uncoiler 132 which unwinds and feeds an upper surface iron plate 130 adhered to the upper surface of the EPS board 120 in a wound state and a first disk changer 132 which changes the rotation direction of the upper surface iron plate 130 and supplies A first panel supply part composed of a roller 134;
And a second uncoiler 142 for uncoiling and feeding the bottom steel plate 140 attached to the lower surface of the EPS board 120 in a wound state;
A first B liquid distributing pipe 152 for dropping, spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the upper surface iron plate 130; And a first mixing plate 156 for mixing the second adhesive liquid (liquid B) and the first adhesive liquid (liquid A). The first adhesive liquid 154 is mixed with the first adhesive liquid A mixing portion;
A second B liquid dispersion pipe 162 for dropping, spraying or spraying the second adhesive liquid (liquid B) on the upper surface of the lower metal plate 140; and a second B liquid distributing pipe 162 for dropping the first adhesive liquid And a second mixing plate (166) for mixing the second adhesive liquid (liquid B) and the first adhesive liquid (liquid A), and a second adhesive material Mixing portion; To
(100) of a flame retardant EPS sandwich panel.
삭제delete 제 1 항에 있어서,
상기 제2 접착액(B 액) 공급부는 상면 철판(130)과 하면 철판(140)의 위치보다 더 높은 위치에 설치되는 것을 특징으로 한, 난연성 EPS 샌드위치 패널의 자동제조장치(100).
The method according to claim 1,
Wherein the second adhesive liquid (B liquid) supply unit is installed at a position higher than the position of the upper surface iron plate (130) and the lower surface iron plate (140).
제 1 항에 있어서,
상기 공급 펌프(118)는, 액상의 제2 접착액(B 액)을 상기 제2 접착액(B 액) 공급부로부터 이송시키는 펌프로서, 박막을 이용한 다이아프램 펌프인 것을 특징으로 한, 난연성 EPS 샌드위치 패널의 자동제조장치(100).
The method according to claim 1,
Wherein the feed pump (118) is a diaphragm pump using a thin film as a pump for feeding a liquid second adhesive liquid (liquid B) from the second adhesive liquid (liquid B) Automatic manufacturing equipment for panels (100).
제 1 항에 있어서,
상기 제1 B액분사관(152)은 원통형 관으로 형성되어 있고 상기 제2 접착액(B 액)을 공급받게 되는 원통형 공급관(172)과, 상기 원통형 공급관의 내부에서 서서히 회전하면서 상기 제2 접착액(B 액)을 교반시켜주는 스프링 믹서(174)와, 상기 스프링 믹서에 회전동력을 제공하는 회전모터(176)와, 상기 원통형 공급관(172)의 저면에 다수 형성되어 있고 상기 제2 접착액(B 액)을 아래쪽으로 뿌려주는 노즐구멍(178)을 포함하고 있는 것을 특징으로 한, 난연성 EPS 샌드위치 패널의 자동제조장치(100).


The method according to claim 1,
The first B liquid-distributing pipe 152 is formed of a cylindrical tube and has a cylindrical supply pipe 172 for receiving the second adhesive liquid (liquid B) A rotary motor 176 for providing a rotational power to the spring mixer, and a plurality of second adhesive liquids 174 which are formed on the bottom surface of the cylindrical supply pipe 172, And a nozzle hole (178) for spraying the liquid (B liquid) downward. The automatic apparatus (100) for manufacturing a flame-retardant EPS sandwich panel according to claim 1,


KR1020140178354A 2014-12-11 2014-12-11 Apparatus for Making Flame Resistant EPS Sandwich Pannel KR101651098B1 (en)