Abstract

The present invention provides a cosmetic composition for lip tattooing which not only has excellent color formation and good durability, but also has good moisturizing effects. Further, the present invention relates to a method of preparing a cosmetic composition for lip tattooing, which enables such a cosmetic composition for lip tattooing to be prepared through a simpler process. A method of preparing a cosmetic composition for lip tattooing according to the present invention comprises: process A of mixing glycerin with acid water at a temperature of 75 to 80C; process B of mixing polyvinyl alcohol with purified water at a temperature of 75 to 80C; process C of injecting the mixture passed through the process B into the mixture passed through the process A to mix the mixtures; and process D of injecting a preservative, a PEG/PPG-17/6 copolymer, ethanol, a coloring pigment, and incense into the mixture passed through the process C. Specifically, the cosmetic composition for lip tattooing comprises glycerin which is dissolved into acid water, and polyvinyl alcohol, a PEG/PPG-17/6 copolymer, ethanol, a coloring pigment, and incense which are dissolved into purified water.

Description

BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a cosmetic composition for lip tat,

The present invention relates to a cosmetic composition for lip tattoo and a method for producing the composition, and more particularly, to a cosmetic composition for lip tat with excellent color development, good durability and good moisturizing power, And to a process for producing the composition.

In recent years, natural make-up has been spotlighted by women, but instead, concentrated lips are expressing bright red lips that look like babies.

Of course, as the aging progresses, the lips of the lustrous lips become tangled, the color of the lips becomes dull and dark, the elasticity of the lips is reduced, and the wrinkles of the lips are highlighted. Cosmetics and makeup techniques It is the subject of interest.

Lipstick, lipgloss and lipstick are the products that make up the color of the lips depending on the type and package type of the contents. Lipstick and lipgloss make up cosmetics.

In general, a lipstick or lipgloss is intended to give a luster to the lips or to moisturize the lips while simultaneously expressing color in the mouth. The composition is composed of waxes that maintain a solid shape, various oils and pigments, and the like do. Other ingredients such as polybutene, lanolin, and vaseline are also used for the purpose of improving adhesion and gloss when used on lips.

However, these products were easily buried in the food or lips, so they were easily buried or erased, so that they continued to wear lipsticks. When lipstick was peeled off, there was a problem that the lips were dirty.

Recently, lips tattoo stickers have been attracting attention because of these problems, which give various colors and patterns to lips and to show temporary tattoo effect. Such a lip tattoo sticker has an advantage that it has excellent durability, but it has a problem that it is harmful to the human body and the lips are easily dried because an adhesive or the like is used to apply various colors to the lips.

Accordingly, such a lip tattoo sticker limit is problematic, and a tattoo lip cosmetic composition in which a lip is tattoo-like colored is disclosed in Patent Documents 10-1367817 (Registered on 2014.02.20) and No. 10-1378789 (Registered on Mar. 31, 2014) However,

The present invention also proposes a cosmetic composition for lips tattooing, in which tattoos and temporary coloring are applied to the lips to overcome the problems of the lip tattoo sticker and conventional lipstick to lip gloss, and a method of manufacturing the composition.

That is, in both of the inventions, the composition applied to the lips after applying the cosmetic composition composed of specific ingredients to the lips absorbs color on the lips and forms a thin film while being dried so that the user removes the film, This is about lips tattooing on the lips.

However, the cosmetic compositions for lip tattoos disclosed in Japanese Patent Application Nos. 10-1367817 and 10-1378789 and the compositions of the present invention to be described below are different from each other in composition, and also have a different method of producing them.

That is, in the case of the manufacturing method disclosed in Japanese Patent Application Nos. 10-1367817 and 10-1378789, the cooling process must be performed at a specific temperature for each step, and then the pH is separately adjusted.

Accordingly, it is an object of the present invention to provide a cosmetic composition for lip tat with excellent lip coloration and durability,

It is an object of the present invention to provide a cosmetic composition for lip tat with a composition which simplifies the manufacturing process as compared with the conventional art and provides a simplified manufacturing process.

Technical Solution In order to accomplish the above object, the present invention provides a cosmetic composition for lip tattoo comprising glycerin dissolved in water, polyvinyl alcohol dissolved in purified water, SPG176, ethanol, a coloring pigment and a perfume.

Furthermore, the cosmetic composition for lip tattoo described above preferably contains 35 to 40 wt% of acidic water, 0.1 to 0.3 wt% of glycerin, 33 to 38 wt% of purified water, 14 to 16 wt% of polyvinyl alcohol, 0.2 to 0.7 wt% of preservative, 0.7 to 10% by weight of ethanol, 0.01 to 0.08% by weight of a color pigment, and 0.03 to 0.08% by weight of a perfume.

In addition, the present invention provides a method for preparing a cosmetic composition for lip tat,

After the step A, in which glycerin is mixed with the acidic water at a temperature of 75 to 80 ° C, and the step B, in which polyvinyl alcohol is mixed with the purified water at a temperature of 75 to 80 ° C., the mixture obtained through step B is subjected to step A After the addition, the mixture is subjected to a C step,

C process, and then adding preservative, SPG176, ethanol, coloring pigment, and dye to the mixture, and mixing the resultant mixture through D process.

Further, the mixing in the C and D steps is performed in an agitation homogenizer (AGI) at 2500 rpm for 10 minutes.

According to the present invention, it is possible to obtain a cosmetic composition for lips and tattoos, which can solve the problems of lip makeup products including conventional lipsticks and can keep color and / or deposit in the lips clearly and continuously, Lt; / RTI >

In addition, since the manufacturing process can be easily performed in manufacturing the cosmetic composition for lip tattoo, the productivity can be improved compared to the conventional art.

BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view schematically illustrating a process for producing a cosmetic composition for lip tattoo according to the present invention. FIG.

Hereinafter, a cosmetic composition for lip tattoo according to the present invention and a method for producing the same will be described in detail.

The present invention solves the problems of conventional lipsticks (lip gloss) and lip tattoo stickers. When a certain amount is applied to the lips as in the above-described conventional patent, the color is deposited on the lips, Is to remove the membrane.

In other words, it is as convenient as lipstick (lip gloss), it can guarantee long-lasting durability, can enhance moisturizing effect on lips and obtain vivid color, and has the advantage of being less harmful to human than lip tattoo sticker.

According to the present invention,

Acid water, glycerin, purified water, polyvinyl alcohol, preservative, PEG / PPG-17/6 Copolymer, ethanol, coloring pigments, and fragrances. .

It is especially with the polyvinyl alcohol in the composition that forms the film after application to the lips. That is, the polyvinyl alcohol acts as a water-soluble film forming agent. When the composition according to the present invention is applied to the lips and then the film is dried, a thin film is formed, and the user can remove the easily formed film by hand.

In the process of applying to the lips and forming a film, a certain color is deposited on the lips, so that the lipstick can be applied and the lips are moisturized. This effect is expected by dissolving glycerin in the acidic water.

The pH of the acidic water is set to 5 or less. The acidic water functions to facilitate the deposition of the coloring pigment to be applied to the lips at a later time. By dissolving glycerin, which moisturizes the lipid, A cosmetic composition in which the colored state can be maintained for a long time while maintaining moisturization is obtained.

Next, the cosmetic composition for lip tattoo according to the present invention comprises a preservative and a pigment / PPE-17/6 copolymer (PEG / PPG-17/6 Copolymer)

The preservative may be selected from the group consisting of hexylene glycol, 1,3-butanediol, decane-1,2-diol, ethylhexyl glycerine, And Totarol, and more preferably,

The component ratio of each component was 30% by weight of hexylene glycol, 5% by weight of 1,3-butanediol, 30% by weight of decane-1,2-diol 30 weight%. 30% by weight of ethylhexyl glycerine, and 5% by weight of Totarol.

Totarol is an oil product that acts as a key to the preservative. Hexylene glycols and 1,3-butanediol are used to supplement the moisturizing properties of the ingredients. .

The PEG / PPG-17/6 copolymer (PEG / PPG-17/6 Copolymer) was mixed with the above preservative in a ratio of 1: 17/6 Copolymer) functions to maximize the moisturizing function of the above-mentioned glycerin, which is added to provide moisture.

That is, mixing a small amount of a PEG / PPE-17/6 copolymer (PEG / PPG-17/6 Copolymer) with glycerin rather than using the required amount of glycerin to provide the desired moisture retention reduces the amount of glycerin But it can give more effect to moisturizing effect.

Depending on the situation, juice extracts may be added to the mixture of the preservative and the PEG / PPE-17/6 copolymer (PEG / PPG-17/6 Copolymer). Citric acid is considered as a juice extract.

Next, the cosmetic composition for lip tattoo according to the present invention comprises ethanol, coloring pigment, and perfume in addition to the above-mentioned composition.

The cosmetic composition for lips and tattoos according to the present invention having such components is characterized in that it comprises 35 to 40 wt% of acidic water, 0.1 to 0.3 wt% of glycerin, 33 to 38 wt% of purified water, 14 to 16 wt% of polyvinyl alcohol, 0.2 to 0.7 wt% 0.2 to 0.7% by weight of a copolymer of PEG / PPG-17/6 Copolymer, 7 to 10% by weight of ethanol, 0.01 to 0.08% by weight of a coloring pigment and 0.03 to 0.08% It is possible to impart color to the lips so that the lips remain sharp and at the same time to sufficiently supply the moisture.

For reference, the table is as follows.

Name % 1 group
Acid water 35 to 40 glycerin 0.1 to 0.3 2 groups
Purified water 33 ~ 38 Polyvinyl alcohol 14-16

3 groups

antiseptic 0.2 to 0.7 PP / PE-17/6 Copolymer 0.2 to 0.7 ethanol 7 to 10 Colored pigment 0.01 to 0.08 Spices 0.01 to 0.08

For reference, when the juice extract is further added,

(PEG / PPG-17/6 Copolymer) 0.5% by weight, acidic water 39.71% by weight, glycerin 0.2% by weight, purified water 35% by weight, polyvinyl alcohol 15% By weight, 1% by weight of extract, 8% by weight of ethanol, 0.04% by weight of color pigment and 0.05% by weight of perfume.

Next, a method for producing the lip cosmetic composition for lip tattoos as described above will be described with reference to Fig.

The method of manufacturing a cosmetic composition for lip tattoo according to the present invention is divided into four processes, and it has an advantage that a separate cooling step is not required to be performed step by step unlike the existing registered prior arts, and the stirring process is also simple.

First, glycerin for providing moisture and polyvinyl alcohol for film formation are mixed with each acidic water and purified water, and the mixing temperature is preferably 75 to 80 ° C.

Each of the above steps is referred to as step A (mixing glycerin to acidic water at a temperature of 75 to 80 캜) and step B (mixing polyvinyl alcohol to purified water at a temperature of 75 to 80 캜).

In particular, in the step A, the pH is already adjusted so that it is not necessary to carry out a separate pH adjustment step.

Next, the mixture obtained through the B step, that is, the purified water mixture in which the polyvinyl alcohol is dissolved, is subjected to the C step in which the mixture obtained by the A step, that is, glycerin is dissolved in the acidic water and stirred together.

In the case of step C, the mixture is agitated with an agitation homogenizer (AGI) for 10 minutes. It is preferable to stir at 2500 rpm at a high speed.

When the preservative, the PEG / PPG-17/6 copolymer, ethanol, the coloring pigment, and the perfume are added to the mixture after the following C step and stirred (D process ) The desired lip cosmetic composition for tattooing is completed.

For reference, the addition of a PEG / PPE-17/6 copolymer (PEG / PPG-17/6 Copolymer) enhances the moisture retention with glycerin.

Also, in the above-mentioned step (D), stirring is preferably performed with an agitation homogenizer (AGI) for 10 minutes, and stirring is preferably performed at 2500 rpm.

Of course, the composition ratio of the above-mentioned ingredients is 35 to 40% by weight of acidic water, 0.1 to 0.3% by weight of glycerin, 33 to 38% by weight of purified water, 14 to 16% by weight of polyvinyl alcohol, 0.2 to 0.7% 0.2 to 0.7% by weight of a PEG / PPGI-17/6 copolymer (PEG / PPG-17/6 Copolymer), 7 to 10% by weight of ethanol, 0.01 to 0.08% by weight of a colored pigment and 0.03 to 0.08% .

While the present invention has been described in connection with the preferred embodiments thereof, it will be apparent to those skilled in the art that various modifications, substitutions and substitutions are possible, Should be interpreted as belonging to.

Claims (4)

delete delete An A step of mixing glycerin with acidic water at a temperature of 75 to 80 캜,
After a B step of mixing polyvinyl alcohol with purified water at a temperature of 75 to 80 占 폚,
The mixture obtained by the B step is introduced into the mixture obtained through the A step, and the resulting mixture is subjected to a C step.
C, and then D is added to the mixture obtained by mixing the preservative, the PEG / PPG-17/6 copolymer (PEG / PPG-17/6 Copolymer), ethanol,
The composition ratio of the components to be added to each of the above steps is 35 to 40% by weight of acidic water, 0.1 to 0.3% by weight of glycerin, 33 to 38% by weight of purified water, 14 to 16% by weight of polyvinyl alcohol, 0.2 to 0.7% (PEG / PPG-17/6 Copolymer), 7 to 10% by weight of ethanol, 0.01 to 0.08% by weight of a color pigment and 0.03 to 0.08% by weight of a perfume,
The preservative is 30% by weight of hexylene glycol, 5% by weight of 1,3-butanediol, and 30% by weight of decane-1,2-diol. 30% by weight of Ethyl Hexyl Glycerine and 5% by weight of Totarol,
PPG-17/6 copolymer (PEG / PPG-17/6 copolymer) is prepared by mixing 1: 1 of the preservative and a charge /
Wherein the mixing in the C and D steps is carried out at 2500 rpm for 10 minutes in an agitation homogenizer (AGI).