KR101597252B1 - Tile for saltpan floor board using the tile composition using foreshore - Google Patents

Tile for saltpan floor board using the tile composition using foreshore Download PDF

Info

Publication number
KR101597252B1
KR101597252B1 KR1020140051544A KR20140051544A KR101597252B1 KR 101597252 B1 KR101597252 B1 KR 101597252B1 KR 1020140051544 A KR1020140051544 A KR 1020140051544A KR 20140051544 A KR20140051544 A KR 20140051544A KR 101597252 B1 KR101597252 B1 KR 101597252B1
Authority
KR
South Korea
Prior art keywords
tile
weight
parts
tidal flats
body portion
Prior art date
Application number
KR1020140051544A
Other languages
Korean (ko)
Other versions
KR20150124697A (en
Inventor
민경철
민귀성
민재오
민경순
Original Assignee
민경철
민귀성
민재오
민경순
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 민경철, 민귀성, 민재오, 민경순 filed Critical 민경철
Priority to KR1020140051544A priority Critical patent/KR101597252B1/en
Publication of KR20150124697A publication Critical patent/KR20150124697A/en
Application granted granted Critical
Publication of KR101597252B1 publication Critical patent/KR101597252B1/en

Abstract

본 발명은 갯벌과 상기 갯벌 100중량부 대비 혼화재 30중량부를 이용하여 조성되되, 상기 혼화재는 상기 갯벌 100중량부 대비 모래 8~9중량부, 석탄 5중량부, 불포화 폴리에스테르 액상수지 15중량부 및 유기과산화물 1~2중량부가 혼합된 것을 특징으로 하는 갯벌을 이용한 타일 조성물에 관한 것이다.
또한 본 발명은 타일 조성물을 형틀에 주입한 후 양생과정을 거쳐 제작되는 염전바닥용 타일에서, 상변이 평평한 형태의 입체 형상으로 구성되는 몸체부; 상기 몸체부의 가장자리에 하부방향으로 경사를 이루며 발톱형태로 돌출연장되는 고정부; 및, 상기 몸체부의 하부로 각 변의 중심과의 동일선상을 양단으로 하여 돌출되게 설치되는 보강부;를 포함하여 구성되는 것을 특징으로 한다.The present invention relates to a tidal flats and a tidal flats, which are prepared by using 30 parts by weight of an admixture to 100 parts by weight of the tidal flats, wherein the admixture comprises 8 to 9 parts by weight of sand relative to 100 parts by weight of the tidal flats, 5 parts by weight of coal, 15 parts by weight of an unsaturated polyester liquid resin, And 1 to 2 parts by weight of an organic peroxide is mixed with the tile.
The present invention also relates to a tile for tile flooring, which is manufactured by injecting a tile composition into a mold and then curing it, a body portion having a three-dimensional shape of a flat top; A fixing unit which is inclined downwardly at an edge of the body and protrudes and extends in a claw shape; And a reinforcing portion protruding from the lower portion of the body portion with both ends thereof coaxially aligned with the center of each side.

Description

갯벌을 이용한 타일 조성물을 이용하여 제작된 염전바닥용 타일{Tile for saltpan floor board using the tile composition using foreshore}TECHNICAL FIELD [0001] The present invention relates to a tile for floor tiles,

본 발명은 갯벌을 이용한 타일 조성물 및 이를 이용하여 제작된 염전바닥용 타일에 관한 것으로, 더욱 상세하게는 갯벌과 모래, 석탄, 불포화 폴리에스테르 액상수지 및 유기과산화물로 구성되는 혼화재를 혼합하여 형성된 타일 조성물과 이를 바람직하게 이용하여 제작된 구조적으로 우수하고 친환경적인 염전바닥용 타일에 관한 것이다.The present invention relates to a tile composition using a tidal flats and a tile for a tidal floor made using the tidal flats. More particularly, the present invention relates to a tile composition formed by mixing a tidal flat with an admixture composed of sand, coal, an unsaturated polyester liquid resin and an organic peroxide And a tile for tile flooring which is structurally excellent and environmentally friendly, which is produced by using it preferably.

전 세계적으로 갯벌이 조성되어 있는 나라는 많지 않지만, 우리나라는 서해안을 중심으로 넓은 갯벌이 조성되어 있으며, 특히 지역에 따라 다양한 성분의 갯벌이 분포되어 있다.Although there are not many countries where tidal-flats are formed all over the world, Korea has wide tidal-flats centered on the west coast, and various tidal-flats are distributed especially according to the region.

국토의 효율적인 개발을 위해 바다의 갯벌을 막아 농지로 사용하거나 또는 대규모 산업 단지 등을 조성하기 위한 간척사업이 시행되고 있는 실정이나, 이와 같은 갯벌에 존재하는 갯벌은 염분을 다량함유하고 있어 건물 등의 부식을 유발하거나 농작물의 생육을 저하하게 되어 그와 같은 갯벌의 처리가 사회적인 문제로 떠오르고 있는 실정이다.For the efficient development of the country, reclamation projects are being implemented to prevent sea tidal flats from being used as agricultural land or to build large-scale industrial complexes. However, the tidal flats that exist in these tidal flats contain a large amount of salt, It causes corrosion and degradation of crops, and the disposal of such tidal flats is becoming a social problem.

특히, 이와 같은 갯벌에 대한 재활용이 제대로 이루어지지 못해 불법으로 땅속에 매설시에 빗물이 침투되어 침출수가 발생하는 경우 인근 토양의 2차 환경오염을 유발하는 문제점도 있다.Particularly, recycling of such tidal flats is not performed properly, and when rainwater is infiltrated when it is illegally buried in the ground and leachate is generated, there is a problem of causing secondary environmental pollution of the nearby soil.

상기와 같은 갯벌을 재활용할 수 있는 노력이 경주되고 있으며, 이와 관련된 선행기술로써 한국공개특허 2010-0049219호에 갯벌을 이용하여 건축용 블럭을 제조하는 기술이 개시되어 있으나, 단순히 갯벌에서 점토와 모래성분만을 분리하여 반죽해서 성형 및 건조해서 벽돌이나 보도블럭의 블럭을 만드는 것에 불과하다.As a prior art related to this, there has been disclosed a technique for manufacturing a building block using a tidal flats in Korean Patent Publication No. 2010-0049219. However, in the tidal flats, clay and sand castings , Kneading, molding and drying to make blocks of bricks and sidewalk blocks.

일반적으로 천일염이라 함은 태양과 풍력 등의 자연력을 이용하여 바닷물을 증발, 농축하는 시설을 말하는 것으로 우리나라에서는 수면이 낮은 서해안과 남해안에 널리 분포되어 있다.In general, the term "solar salt" refers to a facility for evaporating and concentrating seawater by using the natural forces such as the sun and wind, and is widely distributed in the west coast and the southern coast where the water is low in Korea.

이러한 천일염전의 결정지에는 채염을 위한 기반시설에서 발생한 녹, 보온덮개의 부스러기, 모래알갱이, 해충, 식물체와 같은 이물질, 해안의 갯벌에서와 저류지(低流地)의 갯벌에서 유입된 불용분, 오염된 바닷물의 오염물질이 지반에 섞여 있게 되는데, 이러한 이물질이 채염용으로 수집해둔 바닷물이나 소금에 혼입(混入)되는 것을 방지시키기 위해 합성수지재의 장판 또는 도자기재의 타일 등과 같은 바닥마감부재로 결정지의 지면을 덮어서 사용하고 있다.The determination site before the sunshine includes rust, insect coverings, sand grains, pests, plant-like debris from infrastructure for compaction, insoluble matter from coastal tidal flats and tidal flats of lowland, In order to prevent these contaminants from being mixed into seawater or salt collected for the purpose of compaction, a floor covering material such as tiles of synthetic resin material or ceramic tiles is used as the ground surface of the determined ground. It is covered and used.

특히 도 1은 종래의 합성수지재 장판을 염전바닥용으로 이용한 사진인데, 국내 염전의 80%정도가 합성수지재 중의 하나인 PVC 장판을 이용하고 있다. 이는 가격이 저렴하고 내약품성 등이 우수하다는 장점이 있다. 그러나 PVC 장판은 신축성과 접착성을 좋게 하기 위하여 다량의 가소제를 첨가하는데, 여기에는 내분비계장애물질 등의 유해한 물질이 포함된 것으로 알려져 있다. 또한 도 1에 도시된 바와 같이 PVC 장판을 장기간 고무래 등과 같은 도구를 사용하여 바닥면을 긁게 되면, 코팅부가 벗겨져 환경호르몬이 배출됨으로써 인체에 유해한 영향을 줄 수 있다는 문제가 있다. 아울러 자외선에 의한 짧은 수명, 여름철의 태풍에 의한 취약성 및 겨울철 동파에 의한 파손 등의 한계가 있으며 장판을 고정하기 위하여 설치되는 못 또는 스크류를 장기간 사용할 경우 산화되어 생성되는 소금에 함유되는 문제점과 PVC 장판이 햇빛과 통풍을 차단하여 바닥의 갯벌이 썩어가는 환경문제가 있다는 점도 간과해서는 안 된다.Particularly, FIG. 1 is a photograph using a conventional synthetic resin revetment for a tumbling floor, in which about 80% of domestic tumblers use a PVC laminate, which is one of synthetic resin materials. This is advantageous in that the price is low and the chemical resistance is excellent. However, the PVC laminate adds a large amount of plasticizer in order to improve elasticity and adhesion, which is known to contain harmful substances such as endocrine disruptors. Also, as shown in FIG. 1, when the bottom of a PVC sheet is scratched by using a tool such as a rubber strip for a long time, the coating part is peeled off and the environmental hormone is discharged, thereby adversely affecting the human body. In addition, there are limitations such as short life due to ultraviolet rays, vulnerability due to typhoons in summer, and breakage due to freezing in winter. Also, when a nail or a screw installed for fixing a long plate is used for a long time, It should not be underestimated that there is an environmental problem that cuts off the sunlight and ventilation and rotates the bottom of the tidal flats.

또한 염전바닥용으로 타일을 이용하는데, 이는 평탄도가 우수하나 고가라는 점과 내충격성 및 내마모성이 약하여 쉽게 깨어진다는 특징이 있다. 그러기에 잦은 보수에 따른 소금생산량 차질 및 유지관리비가 가중부담되는 문제점이 발생한다. 아울러 종래의 타일은 염전에서 밀대에 힘을 가하여 소금을 생산할 경우 타일이 자주 이탈되는 현상이 발생하였으며, 타일을 이용하여 바닥을 시공하는 경우 시멘트를 사용하여야 하므로 인체에 유해한 환경호르몬이 배출되는 문제점이 있다.
In addition, tile is used for tile floor, which is excellent in flatness, but it is expensive, and its impact resistance and abrasion resistance are weak, so it is easily broken. As a result, there is a problem that the disruption of salt production due to frequent maintenance and the maintenance cost are burdened. In addition, the conventional tile has a tendency that the tile is often detached when the salt is produced by applying a force to the tongs in the tongue, and when the floor is constructed using the tile, the cement is used so that harmful environmental hormones are discharged to the human body have.

본 발명은 상기와 같은 문제점을 해결하기 위하여 개발된 것으로서, 시멘트 및 골재 대신에 갯벌이 주재료로 이용되는 친환경적이고 강도가 우수한 타일 조성물을 제공하는데 그 목적이 있다.The present invention has been developed in order to solve the above-mentioned problems, and it is an object of the present invention to provide an environmentally friendly tile composition having high strength, in which tidal flats are used as a main material instead of cement and aggregate.

본 발명의 다른 목적은 가장자리에 소정의 각도로 꺾인 발톱형상의 고정부를 통하여 지지력을 증가시키고, 저면의 중앙부에 형성된 빔(beam) 형태의 보강부를 통하여 상부 하중에 대한 지지력이 향상되는 갯벌을 이용한 타일 조성물을 이용하여 제작된 염전바닥용 타일을 제공하는데 그 목적이 있다.Another object of the present invention is to provide a tidal flatshaving increased supporting force through a toe-shaped fixing portion bent at a predetermined angle to an edge and enhanced supporting force against an upper load through a beam-shaped reinforcing portion formed at a central portion of the bottom surface It is an object of the present invention to provide a tile for a pre-tile floor made using a tile composition.

상기 목적을 달성하기 위한 본 발명은 갯벌과 상기 갯벌 100중량부 대비 혼화재 30중량부를 이용하여 조성되되, 상기 혼화재는 상기 갯벌 100중량부 대비 모래 8~9중량부, 석탄 5중량부, 불포화 폴리에스테르 액상수지 15중량부 및 유기과산화물 1~2중량부가 혼합된 것을 특징으로 하는 갯벌을 이용한 타일 조성물을 제공한다.In order to accomplish the above object, the present invention is achieved by using the tidal flats and 30 parts by weight of an admixture to 100 parts by weight of the tidal flats, wherein the admixture comprises 8 to 9 parts by weight of sand relative to 100 parts by weight of the tidal flats, 5 parts by weight of coal, 15 parts by weight of a liquid resin and 1 to 2 parts by weight of an organic peroxide are mixed with each other.

또한 본 발명은 타일 조성물을 형틀에 주입한 후 양생과정을 거쳐 제작되는 염전바닥용 타일에서, 상변이 평평한 형태의 입체 형상으로 구성되는 몸체부; 상기 몸체부의 가장자리에 하방향으로 경사를 이루며 발톱형태로 돌출연장되는 고정부; 및, 상기 몸체부의 하부로 각 변의 중심과의 동일선상을 양단으로 하여 돌출되게 설치되는 보강부;를 포함하여 구성되는 것을 특징으로 하는 염전바닥용 타일을 제공한다.The present invention also relates to a tile for tile flooring, which is manufactured by injecting a tile composition into a mold and then curing it, a body portion having a three-dimensional shape of a flat top; A fixing portion that is inclined downwardly at an edge of the body portion and protrudes and extends in a claw shape; And a reinforcing portion protruding from the lower portion of the body portion with both ends thereof coaxially aligned with the center of each side of the tile.

본 발명의 갯벌을 이용한 타일 조성물에 따르면, 타일 조성물로써 시멘트와 골재 대신에 갯벌을 이용함으로써 친환경적이고, 내구성 및 내화성이 우수한 장점이 있을 뿐만 아니라, 녹색사업성장의 일환으로 갯벌을 자원화하여 환경오염을 방지하는 동시에 수익을 창출할 수 있다.According to the tile composition using the tidal flats of the present invention, tidal flats are used instead of cement and aggregates as tile compositions, which are environmentally friendly, durable and fire resistant. In addition, as a part of green business growth, While at the same time generating revenue.

또한 본 발명의 갯벌을 이용한 타일 조성물을 이용하여 제작된 염전바닥용 타일에 따르면, 하부에 형성된 발톱 형상의 고정부 및 빔 형태의 보강부로 인하여 밀대의 충격, 작업자의 무게 및 소금의 무게 때문에 타일이 밀리거나 쉽게 파손되는 것을 방지할 수 있으며, 별도의 접착제와 시멘트 등의 결합용 약제가 필요 없으므로 인체에 유해한 환경호르몬이 방출되지 않는 효과가 있다.
In addition, according to the tile for tile floor using the tile composition of the present invention, due to the impact of the tile, the weight of the worker and the weight of the salt due to the claw- It can be prevented from being pushed or easily broken, and there is no need for a separate adhesive and a binding agent such as cement, so that an environmental hormone harmful to the human body is not released.

도 1는 종래에 합성수지재 장판을 염전바닥용으로 이용한 현장사진이다.
도 2는 본 발명에 따른 갯벌을 이용한 타일 조성물을 이용하여 염전바닥용 타일을 제조하는 방법을 도시한 공정도이다.
도 3(a)와 (b)는 본 발명에 따른 염전바닥용 타일의 제1실시예를 나타낸 사시도 및 단면도이다.
도 4(a)와 (b)는 본 발명에 따른 염전바닥용 타일의 제2실시예를 나타낸 사시도 및 단면도이다.
도 5(a)와 (b)는 본 발명에 따른 염전바닥용 타일의 제3실시예를 나타낸 사시도 및 단면도이다.
도 6(a) 내지 (c)는 본 발명에 따른 염전바닥용 타일의 제1,2,3실시예를 이용한 시공방법을 나타낸 것이다.FIG. 1 is a photograph of a site where a conventional synthetic resin revetment plate is used for a salt float floor.
FIG. 2 is a process diagram showing a method of manufacturing a tile for a salt tile floor using a tile composition using the tidal flats according to the present invention.
3 (a) and 3 (b) are a perspective view and a cross-sectional view showing a first embodiment of a tile for floatation according to the present invention.
4 (a) and 4 (b) are a perspective view and a cross-sectional view showing a tile according to a second embodiment of the present invention.
5 (a) and 5 (b) are a perspective view and a cross-sectional view showing a third embodiment of the tile for floatation according to the present invention.
6 (a) to 6 (c) illustrate a construction method using the tile according to the first, second, and third embodiments of the present invention.

본 발명은 갯벌을 이용하여 형성되는 타일(10) 조성물에서, 갯벌과 상기 갯벌 100중량부 대비 혼화재 30중량부를 이용하여 조성되되, 상기 혼화재는 상기 갯벌 100중량부 대비 모래 8~9중량부, 석탄 5중량부, 불포화 폴리에스테르 액상수지 15중량부 및 유기과산화물 1~2중량부가 혼합된 것을 특징으로 한다.The present invention relates to a tile (10) comprising tidal flats, comprising: a tidal flats and 30 parts by weight of an admixture to 100 parts by weight of the tidal flats, wherein the admixture comprises 8 to 9 parts by weight of sand relative to 100 parts by weight of the tidal flats, 5 parts by weight of an unsaturated polyester liquid resin, 15 parts by weight of an unsaturated polyester liquid resin and 1 to 2 parts by weight of an organic peroxide.

또한 본 발명은 상기 혼화재는 석탄 대신에 숯가루로 구성되는 것을 특징으로 한다.In addition, the present invention is characterized in that the admixture is made of charcoal powder instead of coal.

이하 첨부한 도면과 함께 상기와 같은 본 발명의 개념이 바람직하게 구현된 실시예를 통하여 본 발명을 더욱 상세하게 설명한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 2는 본 발명에 따른 갯벌을 이용한 타일(10) 조성물을 이용하여 염전바닥용 타일(10)을 제조하는 방법을 도시한 공정도이다.FIG. 2 is a process drawing showing a method for manufacturing a tile 10 for tile floor using a tile 10 composition according to the present invention.

본 발명의 타일(10) 조성물은 도 2에 도시된 바와 같이 갯벌, 모래, 석탄 또는 숯가루, 불포화 폴리에스테르 액상수지 및 유기과산화물을 혼합하게 된다.The tile (10) composition of the present invention mixes tidal flats, sand, coal or charcoal powder, unsaturated polyester liquid resin and organic peroxide as shown in FIG.

갯벌은 바닷물이 드나드는 모래톱 또는 그 주변의 넓은 땅에 형성된 것이다. 특히 본 발명은 염전 현장에서 직접 깨끗한 갯벌을 채취하여 적용될 수 있으며, 갯벌 표면으로부터 50~100cm의 범위 내에서 채취하는 것이 바람직하다. 50cm 미만의 표면에 가까운 갯벌은 성분의 편차가 상이하며 외부환경에 따라 불순물이 다수 포함될 수 있으며, 100cm를 초과한 깊이에서는 채취가 용이하지 않고 지형에 변화를 일으킬 수 있기 때문이다. 또한 본 발명은 갯벌의 염분을 제거하기 위해 갯벌을 물속에서 충분히 교반 및 분산시키는 통상의 방법이 이용될 수 있다.The tidal flats are formed on the sandy beach where the waters come and go, or on the wide land around them. In particular, the present invention can be applied by collecting clean tidal flats directly from the salt field, and it is preferable to collect the tidal flats within a range of 50 to 100 cm from the surface of the tidal flats. Tidal flats near the surface of less than 50 cm have different deviations from each other and may contain many impurities depending on the external environment. It is not easy to collect at depths exceeding 100 cm and can cause changes in the terrain. Further, in the present invention, a conventional method of sufficiently stirring and dispersing the tidal flats in water to remove the saltiness of the tidal flats can be used.

모래는 지름 2~0.02㎜ 사이의 암석편, 광석편으로서, 통상의 콘크리트용 재료를 의미한다.Sand is a rock piece or ore piece having a diameter of 2 to 0.02 mm and means a usual concrete material.

석탄은 지질시대의 육생식물이나 수생식물이 수중에 퇴적하여 매몰된 후 가열과 가압작용을 받아 변질하여 생성된 흑갈색의 가연성 암석을 의미하며, 본 발명은 이 중에 탄화가 잘되어 연기를 내지 않고 연소하며 휘발분이 3~7%로 적은 무연탄이 이용된다. 이러한 석탄은 높은 경도로 인해 골재의 역할을 수행함으로써 다른 잔골재 및 굵은골재의 혼합을 생략가능케 할 수 있다. 이때, 염전바닥의 지반이 초연약화인 경우와 그 우려가 있을 경우와 같이 상부 자재의 중량물을 지탱하기 어려운 지지력으로 구성된 경우 석탄 대신에 숯가루로 대체해서 사용하는 것이 바람직하다.Coal is a blackish-brown flammable rock produced by sedimentation and burial of geophysical plants or aquatic plants in water after undergoing heating and pressurization. The present invention is characterized in that carbonization is well performed, And anthracite coal having a volatile content of 3 to 7% is used. Such coal can play a role of aggregate due to its high hardness, thereby making it possible to omit mixing of fine aggregates and coarse aggregates. In this case, it is preferable to use charcoal instead of coal in the case where the foundation of the salt floor is composed of a bearing which is difficult to support the weight of the upper material, such as the case where the superficial weakening is weakened.

불포화 폴리에스테르 액상수지는 비교적 낮은 점도의 액상 수지이며 실내온도에서도 경화되고 또한 경화될 때에 많은 열경화성 수지와 같은 가스를 발생하지 않기 때문에 성형에는 거의 압력을 가할 필요가 없다는 특징이 있다. 또한 불포화 폴리에스테르 액상수지는 구조를 치밀하게 하여 강도와 내수성을 부여한다. 또한 상술한 바와 같이 불포화 폴리에스테르 액상수지를 갯벌 100중량부 대비 15중량부를 혼합함으로써 타일(10) 조성물이 강한 내구성과 내마모성을 가지도록 하는 것이 바람직하다.The unsaturated polyester liquid resin is a liquid resin having a relatively low viscosity and is characterized in that it does not need to apply a little pressure to the molding since it hardens at room temperature and does not generate much gas like a thermosetting resin when it is cured. In addition, the unsaturated polyester liquid resin is dense in structure to impart strength and water resistance. In addition, as described above, it is preferable that the tile 10 composition has strong durability and abrasion resistance by mixing 15 parts by weight of the unsaturated polyester liquid resin with respect to 100 parts by weight of the tidal flats.

유기과산화물은 과산화수소(HOOH)의 수소원자 1개 또는 2개를 “R group”으로 치환시킨 과산화수소 유도체로 ROOR’의 구조를 가지며, 특징적으로 가지고 있는 ＂-O-O-＂ 결합은 용이하게 자유라디칼(-Oㆍ)을 발생하여 monomer의 중합반응에 효과적인 것을 특징으로 한다. 본 발명은 갯벌 100중량부 대비 1~2중량부의 유기과산화물이 혼합됨으로써 제작되는 타일(10)의 표면을 코팅시킨다.The organic peroxide is a hydrogen peroxide derivative in which one or two hydrogen atoms of hydrogen peroxide (HOOH) are replaced with an "R group". The ROOO 'structure is characteristic. The characteristic "-OO-" O < - >) is generated and is effective for the polymerization reaction of the monomer. The present invention coats the surface of the tile 10 produced by mixing 1 to 2 parts by weight of organic peroxide with respect to 100 parts by weight of tidal flats.

즉 본 발명의 타일(10) 조성물은 상술한 바와 같은 갯벌과 모래, 석탄, 불포화 폴리에스테르 액상수지 및 유기과산화물으로 구성된 혼화재가 혼합되며, 모래는 갯벌 100중량부 대비 8~9중량부로, 석탄은 갯벌 100중량부 대비 5중량부로, 불포화 폴리에스테르 액상수지는 갯벌 100중량부 대비 15중량부로, 유기과산화물은 갯벌 100중량부 대비 1~2중량부로 구성된다. 또한 본 발명은 상술한 중량부로 구성된 타일(10) 조성물을 형틀에 투입하고 양생한 후, 일정한 두께로 절단하여 타일(10)을 제조한다.That is, the tile (10) composition of the present invention is prepared by mixing the above-described tidal flats with an admixture composed of sand, coal, unsaturated polyester liquid resin and organic peroxide, sand is 8 to 9 parts by weight relative to 100 parts by weight of tidal flats, 5 parts by weight relative to 100 parts by weight of tidal flats, 15 parts by weight of unsaturated polyester liquid resin with respect to 100 parts by weight of tidal flats, and 1 to 2 parts by weight of organic peroxides relative to 100 parts by weight of tidal flats. In addition, the present invention is a method for manufacturing a tile (10) by putting a tile (10) composition composed of the above-mentioned weight portion into a mold and curing it, and then cutting it to a predetermined thickness.

본 발명은 상술한 방식으로 혼합된 타일(10) 조성물을 형틀에 주입한 후 양생과정을 거쳐 제작되는 염전바닥용 타일(10)에서, 상변이 평평한 형태의 입체 형상으로 구성되는 몸체부(12); 상기 몸체부(12)의 가장자리에 하부방향으로 경사를 이루며 발톱형태로 돌출연장되는 고정부(14); 및, 상기 몸체부(12)의 하부로 각 변의 중심과의 동일선상을 양단으로 하여 돌출되게 설치되는 보강부(16);를 포함하여 구성되는 것을 특징으로 한다.The present invention relates to a tile (10) for tile flooring, which is prepared by injecting a tile composition (10) mixed in the above-described manner into a mold and then curing the body, a body part (12) having a three- ; A fixing part 14 which is inclined downward at the edge of the body part 12 and protrudes and extends in the form of a claw; And a reinforcing portion 16 protruding from the lower portion of the body portion 12 so as to be in line with the center of the sides of the body portion 12 at both ends thereof.

즉 본 발명의 염전바닥용 타일(10)은 몸체부(12), 고정부(14), 보강부(16)로 구성된다.That is, the tile 10 for tile flooring according to the present invention comprises a body portion 12, a fixing portion 14, and a reinforcing portion 16.

몸체부(12)는 염전용 밀대(소금을 모으는 도구)가 접촉되는 부분이 상부면으로 이루어지는 입체형상의 구성요소로서, 사각형을 포함한 다각형의 단면으로 구성될 수 있다. 또한 몸체부(12)는 밀대로 힘을 가할 때 걸리지 않도록 상부면이 평평하게 구성되어야 하며, 측면도 인접한 염전바닥용 타일(10)이 밀착되게 결합되기 위해서 반듯한 표면으로 구성되어야 한다.The body portion 12 may be a three-dimensional shaped component having a top surface in contact with a salt-extinguishing plate (a tool for collecting salt), and may have a polygonal cross-section including a quadrangle. Also, the upper surface of the body 12 should be flat so as not to be touched when a force is applied to the body, and the side surface should be formed of a flat surface so that the adjacent tile 10 for tile bottom is tightly engaged.

고정부(14)는 몸체부(12)의 가장자리에서 아래 방향으로 돌출 연장되는 구성요소로서, 소정의 각도를 이루도록 꺾인 형상으로 이루어져 지면에 견고히 박히도록 하는 스파이크(spike)의 역할을 하는 것이다. 즉 고정부(14)는 본 발명의 염전바닥용 타일(10) 위에서 밀대로 힘을 가해 소금을 생산할 때, 상기 염전바닥용 타일(10)이 뒤집히거나 뒤틀리지 않도록 해준다. 이와 같은 고정부(14)는 단면상 삼각형으로 구성될 수 있으나, 이에 제한되지는 않으며 지면에 박혀 움직이지 않도록 할 수 있다면 다양한 형태로 구성될 수 있다. 또한 고정부(14)는 지면과 이루는 각도가 45°로 구성됨으로써, 장차 기계화시공에 대하여 대비하고 구조적 안정성을 증대시킬 수 있다.The fixing part 14 is a component that protrudes downward from the edge of the body part 12 and serves as a spike which is formed in a bent shape to form a predetermined angle and is firmly embedded in the ground surface. That is, the fixing portion 14 prevents the tile 10 for tile 10 from being turned upside down or twisted when producing a salt by applying a pushing force on the tile 10 of the present invention. The fixing portion 14 may have a triangular shape in cross section, but it is not limited thereto. The fixing portion 14 may be formed in various shapes as long as it can be prevented from being pinched and moved on the ground. Further, since the fixing portion 14 is formed at an angle of 45 degrees with the ground, it can be prepared against mechanical construction in the future and the structural stability can be increased.

보강부(16)는 몸체부(12)의 저면에 연장결합되는 구성요소로서, 각 변의 중앙점의 동일선상을 양단으로 하여 아래로 돌출된 형태로 결합된다. 이러한 보강부(16)는 본 발명의 염전바닥용 타일(10)의 저면이 갯벌과 맞닿을 때 빔(beam)의 역할을 하여 상부의 하중을 분산 지탱하도록 한다.The reinforcing portion 16 is a component that is extended and joined to the bottom surface of the body portion 12 and is coupled in a projected shape with both ends of the center line of each side being on the same line. The reinforcing portion 16 serves as a beam when the bottom surface of the tile 10 for salt float according to the present invention abuts the tidal flats so as to disperse and support the upper load.

이하 타일(10)의 형태에 따른 각 실시예에 따라 설명하기로 한다.Hereinafter, a description will be given of each embodiment according to the shape of the tile 10.

<< 제1실시예First Embodiment >>

도 3(a)와 (b)는 본 발명에 따른 염전바닥용 타일(10)의 제1실시예를 나타낸 사시도 및 단면도이다.3 (a) and 3 (b) are a perspective view and a cross-sectional view showing a first embodiment of a tile 10 for tumbling according to the present invention.

제1실시예는, 도 3(a)에 도시된 바와 같이 상기 몸체부(12)는 직사각형의 단면으로 구성되고, 상기 고정부(14)는 상기 몸체부(12)의 양측 길이방향으로 형성되며, 상기 보강부(16)는 상기 몸체부(12)의 하부로 각 변의 중심과의 동일선상을 양단으로 하여 돌출되게 설치되는 것에 추가로 상기 몸체부(12)의 길이방향의 일정 간격마다 상기 몸체부(12)의 길이방향과 직교되는 방향으로 더 설치되어 전체적으로 격자형상으로 배치되는 것을 특징으로 한다.3 (a), the body part 12 has a rectangular cross-section, and the fixing part 14 is formed in both longitudinal sides of the body part 12 The reinforcing portion 16 is provided so as to protrude from the lower portion of the body portion 12 with both ends of the same line with the center of each side of the body portion 12 in the longitudinal direction of the body portion 12, Are further provided in a direction orthogonal to the longitudinal direction of the part (12) and are arranged in a lattice form as a whole.

본 발명에 따른 염전바닥용 타일(10)의 제1실시예는 전체적으로 직육면체의 외형으로 보이며, 단변 방향의 측면을 정면으로 보았을 때 하부가 'M'형상의 단면으로 개구된 형태가 된다. 즉 단변방향의 단면만 개구된 형태가 나타나며, 길이방향의 단면은 직사각 형태로 폐쇄된 구조를 이룬다. 이때 제1실시예는 개구된 형태 상 양측에 일정 각도 절곡된 부분이 고정부(14)가 되며, 중앙에 하부로 소정 길이 돌출된 부분이 보강부(16)가 되는 것이다. 그리고 보강부(16)는 도 3(b)에 도시된 바와 같이 단변과 장변의 중앙점을 양단으로 하는 것 이 외에도 길이방향으로 일정 간격마다 추가로 형성됨으로써 전체적인 배치가 격자형태로 나타나게 되는데, 이는 더욱 안정적으로 상부 하중에 대한 저항력을 높일 수 있다.The tile 10 according to the first embodiment of the present invention is formed as a rectangular parallelepiped with an overall shape of a rectangular parallelepiped. That is, only the section in the short side direction is opened, and the section in the longitudinal direction is closed in a rectangular shape. In this case, in the first embodiment, a portion bent at a predetermined angle on both sides of the opened shape becomes the fixing portion 14, and a portion protruding downward by a predetermined length at the center becomes the reinforcing portion 16. As shown in FIG. 3 (b), the reinforcing portion 16 is formed at both ends of the central portion of the short side and the long side, and is further formed at regular intervals in the longitudinal direction, so that the overall arrangement appears in a lattice form. The resistance against the upper load can be more stably increased.

<< 제2실시예Second Embodiment >>

도 4(a)와 (b)는 본 발명에 따른 염전바닥용 타일(10)의 제2실시예를 나타낸 사시도 및 단면도이다.4 (a) and 4 (b) are a perspective view and a cross-sectional view showing a second embodiment of the tile 10 for tumbling according to the present invention.

제2실시예는, 도 4(a)에 도시된 바와 같이 상기 몸체부(12)는 정사각형의 단면으로 구성되고, 상기 고정부(14)는 상기 몸체부(12)의 각 모서리의 하부방향으로 형성되며, 상기 보강부(16)는 전체적으로 십자형상으로 배치되는 것을 특징으로 한다.4 (a), the body portion 12 has a square cross-section, and the fixing portion 14 is formed in a lower portion of each corner of the body portion 12 And the reinforcement portions 16 are arranged in a cross shape as a whole.

본 발명에 따른 염전바닥용 타일(10)의 제2실시예는 전체적으로 정육면체의 외형으로 보이며, 각 변마다 정면상으로 하부가 'M'형상으로 개구되도록 구성된다. 이때 제2실시예도 제1실시예와 마찬가지로 개구된 형태 상 양측에 일정 각도 절곡된 부분이 고정부(14)가 되며, 중앙에 하부로 소정 길이 돌출된 부분이 보강부(16)가 되는 것이다. 특히 제1실시예와는 달리 4개의 측면모두 단면상 고정부(14)와 보강부(16)가 나타나도록 구성된다. 그리고 보강부(16)는 각 변의 중앙점을 양단으로 하여 서로 연장 형성되기에 그 배치된 형태가 십자형상으로 나타난다.The tile 10 according to the second embodiment of the present invention may be seen as an external shape of a cube, and may be formed to open in a 'M' shape on the front surface and a lower surface on each side. At this time, in the second embodiment as well as in the first embodiment, a portion bent at a predetermined angle on both sides in the opened form becomes the fixing portion 14, and a portion protruding downward by a predetermined length at the center becomes the reinforcing portion 16. In particular, unlike the first embodiment, the reinforcing portion 16 and the reinforcing portion 14 are formed in a cross-sectional view on all four sides. Since the reinforcing portion 16 is formed so as to extend at both ends of the central point of each side, the reinforcing portion 16 appears in a cross shape.

<< 제3실시예Third Embodiment >>

도 5(a)와 (b)는 본 발명에 따른 염전바닥용 타일(10)의 제3실시예를 나타낸 사시도 및 단면도이다.5 (a) and 5 (b) are a perspective view and a cross-sectional view showing a third embodiment of the tile 10 for tumbling according to the present invention.

제3실시예는, 도 5(a)에 도시된 바와 같이 상기 몸체부(12)는 정육각형의 단면으로 구성되고, 상기 고정부(14)는 상기 몸체부(12)의 각 모서리의 하부방향으로 형성되며, 상기 보강부(16)는 전체적으로 별형상으로 배치되는 것을 특징으로 한다.5 (a), the body part 12 has a regular hexagonal cross section, and the fixing part 14 is formed in a lower direction of each corner of the body part 12 , And the reinforcing part (16) is arranged in a star shape as a whole.

본 발명에 따른 염전바닥용 타일(10)의 제3실시예는 상하부면이 정육면체로 구성되고, 모든 측면이 상하부면에 평평하게 수직된 면으로 연결되는 팔면체로 보이며, 각 변마다 정면상으로 볼 때 하부가 'M'형상으로 개구된다. 이때 제3실시예도 제1,2실시예와 마찬가지로 개구된 형태 상 양측에 일정 각도 절곡된 부분이 고정부(14)가 되며, 중앙에 하부로 소정 길이 돌출된 부분이 보강부(16)가 된다. 그리고 보강부(16)는 각 변의 중앙과의 동일선상을 양단으로 하여 서로 연장 형성되기에 그 배치된 형태가 별형상(눈꽃형상)으로 나타난다.The third embodiment of the tile 10 for tile floors according to the present invention is characterized in that the upper and lower surfaces are formed as a cube and all side surfaces are seen as octahedrons connected to the upper and lower surfaces by flat vertical surfaces, The lower portion is opened in the shape of "M". In this case, as in the first and second embodiments, the third embodiment also has the fixed part 14 bent at both sides of the opened shape on both sides thereof, and the part protruding downward by a predetermined length at the center becomes the reinforcing part 16 . Since the reinforcement portions 16 are formed so as to extend at the both ends in the same line with the center of each side, the arrangement of the reinforcement portions 16 appears as a star shape (snowball shape).

도 6(a) 내지 (c)는 본 발명에 따른 염전바닥용 타일(10)의 제1,2,3실시예를 이용한 시공방법을 나타낸 것이다.6 (a) to 6 (c) illustrate a construction method using the first, second, and third embodiments of the tile 10 for floatation according to the present invention.

본 발명의 염전바닥용 타일(10)은 갯벌을 이용한 타일(10) 조성물을 형틀에 주입하고 양생한 후, 단위 크기에 맞춰 절단하여 이용된다. 이때, 각 단위 크기의 염전바닥용 타일(10)은 본 발명의 각 실시예에 따라 까는 방법이 상이하게 적용될 수 있는데, 도 6(a) 내지 (c)가 이를 나타낸 것이다. 자세히 말해서, 도 6(a)는 본 발명의 제1실시예에 따른 직사각형 단면의 염전바닥용 타일(10)을 서로 엇갈리는 형태로 배치하는 것을 나타낸 것이고, 도 6(b)는 본 발명의 제2실시예에 따른 정사각형 단면의 염전바닥용 타일(10)을 서로 평행한 형태로 배치하는 것을 나타낸 것이며, 도 6(c)는 본 발명의 제3실시예 따른 정육면체 단면의 염전바닥용 타일(10)을 벌집형태(봉소구조)로 배치하는 것을 나타낸 것이다. 물론 본 발명은 상기한 방법으로 염전바닥용 타일(10)을 배치하는 것에 제한되지는 않으며, 현장 상황에 맞게 다양한 형태로 배치될 수도 있다.The tile (10) for salt floors according to the present invention is used by cutting a tile (10) composition using the tidal flats in accordance with the unit size after pouring the tile (10) composition into a mold. In this case, the tile 10 for the tile 10 of each unit size can be applied differently according to each embodiment of the present invention, which is shown in Figs. 6 (a) to 6 (c). More specifically, FIG. 6 (a) shows arranging the tiles 10 having a rectangular cross section according to the first embodiment of the present invention in a staggered manner, FIG. 6 (b) 6 (c) is a perspective view of a tile 10 for a tile floor of a cubic cross-section according to a third embodiment of the present invention, (Honeycomb structure). Of course, the present invention is not limited to disposing the tile 10 for tile flooring in the above-described manner, and may be arranged in various forms according to the field conditions.

본 발명은 상기에서 언급한 바와 같이 바람직한 실시예와 관련하여 설명되었으나, 본 발명의 요지를 벗어남이 없는 범위 내에서 다양한 수정 및 변형이 가능하며, 다양한 분야에서 사용 가능하다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the invention.

따라서 본 발명의 청구범위는 이건 발명의 진정한 범위 내에 속하는 수정 및 변형을 포함한다.
It is therefore intended that the appended claims cover such modifications and variations as fall within the true scope of the invention.

10: 타일 12: 몸체부
14: 고정부 16: 보강부10: tile 12: body part
14: fixing part 16: reinforcing part

Claims (7)

갯벌을 이용하여 형성되는 타일(10) 조성물을 형틀에 주입한 후 양생과정을 거쳐 제작되는 염전바닥용 타일(10)에서,
상변이 평평한 형태의 입체 형상으로 구성되는 몸체부(12);
상기 몸체부(12)의 가장자리에 하부방향으로 경사를 이루며 발톱형태로 돌출연장되는 고정부(14); 및,
상기 몸체부(12)의 하부로 각 변의 중심과의 동일선상을 양단으로 하여 돌출되게 설치되는 보강부(16);
를 포함하여 구성되되,
상기 타일(10) 조성물은 갯벌과 상기 갯벌 100중량부 대비 혼화재 30중량부를 이용하여 조성되되, 상기 혼화재는 상기 갯벌 100중량부 대비 모래 8~9중량부, 석탄 5중량부, 불포화 폴리에스테르 액상수지 15중량부 및 유기과산화물 1~2중량부가 혼합된 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.In a tile (10) for a tile floor after a tile (10) composition formed by using tidal flats is injected into a mold and cured,
A body portion 12 formed in a three-dimensional shape of a flat top;
A fixing part 14 which is inclined downward at the edge of the body part 12 and protrudes and extends in the form of a claw; And
A reinforcing portion 16 protruding from the lower portion of the body portion 12 so as to be in line with the center of the sides of the body portion 12;
, &Lt; / RTI &gt;
The composition of the tile (10) is prepared using tidal flats and 30 parts by weight of an admixture relative to 100 parts by weight of the tidal flats, wherein the admixture comprises 8 to 9 parts by weight of sand relative to 100 parts by weight of the tidal flats, 5 parts by weight of coal, 15 parts by weight of an organic peroxide and 1 to 2 parts by weight of an organic peroxide are mixed in the tile. 제1항에서,
상기 혼화재는 석탄 대신에 숯가루로 구성되는 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.The method of claim 1,
Wherein the admixture is composed of charcoal powder instead of coal. 삭제delete 제1항 또는 제2항에서,
상기 몸체부(12)는 직사각형의 단면으로 구성되고,
상기 고정부(14)는 상기 몸체부(12)의 양측 길이방향으로 형성되며,
상기 보강부(16)는 상기 몸체부(12)의 길이방향의 일정 간격마다 상기 몸체부(12)의 길이방향과 직교되는 방향으로 더 설치되어 전체적으로 격자형상으로 배치되는 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.3. The method according to claim 1 or 2,
The body portion 12 has a rectangular cross section,
The fixing portion 14 is formed in the longitudinal direction of both sides of the body portion 12,
The reinforcing part (16) is further provided in a grid-like shape in a direction orthogonal to the longitudinal direction of the body part (12) at regular intervals in the longitudinal direction of the body part (12) Tiles for tile flooring made using tile composition. 제1항 또는 제2항에서,
상기 몸체부(12)는 정사각형의 단면으로 구성되고,
상기 고정부(14)는 상기 몸체부(12)의 각 모서리의 하부방향으로 형성되며,
상기 보강부(16)는 전체적으로 십자형상으로 배치되는 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.3. The method according to claim 1 or 2,
The body portion 12 has a square cross section,
The fixing portion 14 is formed in a lower direction of each corner of the body portion 12,
Wherein the reinforcing portion (16) is disposed in a cross shape as a whole. 제1항 또는 제2항에서,
상기 몸체부(12)는 정육각형의 단면으로 구성되고,
상기 고정부(14)는 상기 몸체부(12)의 각 모서리의 하부방향으로 형성되며,
상기 보강부(16)는 전체적으로 별형상으로 배치되는 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.3. The method according to claim 1 or 2,
The body portion 12 has a regular hexagonal cross section,
The fixing portion 14 is formed in a lower direction of each corner of the body portion 12,
Wherein the reinforcing portion (16) is arranged in a star shape as a whole. 제1항 또는 제2항에서,
상기 고정부(14)는 삼각형의 단면으로 구성되고, 지면과 이루는 각도가 45°로 구성되는 것을 특징으로 하는 갯벌을 이용한 타일조성물을 이용하여 제작된 염전바닥용 타일.
3. The method according to claim 1 or 2,
Wherein the fixing portion (14) has a triangular cross section, and the angle between the fixing portion (14) and the ground surface is 45 °.
KR1020140051544A 2014-04-29 2014-04-29 Tile for saltpan floor board using the tile composition using foreshore KR101597252B1 (en)