KR101574492B1 - Air insulation sheet with the function of preventing the loss of energy and the wrinkles - Google Patents
Air insulation sheet with the function of preventing the loss of energy and the wrinkles Download PDFInfo
- Publication number
- KR101574492B1 KR101574492B1 KR1020140070519A KR20140070519A KR101574492B1 KR 101574492 B1 KR101574492 B1 KR 101574492B1 KR 1020140070519 A KR1020140070519 A KR 1020140070519A KR 20140070519 A KR20140070519 A KR 20140070519A KR 101574492 B1 KR101574492 B1 KR 101574492B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- aluminum foil
- insulation
- heat insulating
- air
- Prior art date
Abstract
Description
본 발명은 건축물의 벽체나 천정 등 구조체의 외면 또는 창호의 유리 등에 부착시켜 단열효과를 높혀서 실내의 에너지 손실을 방지하기 위한 단열시트에 관한 것으로서, 특히 알루미늄 박에 의한 반사효율을 극대화시키고, 폐쇄공기층에 의한 단열효과를 높혀 건축물의 에너지 손실을 최소화시킬 수 있으면서 연질의 롤 타입으로 구성되어 적용성 및 운반성이 용이한 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트에 관한 것이다.
The present invention relates to a heat insulating sheet for preventing energy loss in a room by attaching to a wall of a building, an outer surface of a structure such as a ceiling or a glass of a window or the like to enhance the heat insulating effect, The present invention relates to an energy-saving and wrinkle-resistant air insulating sheet for a building, which can be easily applied and transported by being formed of a soft roll type while minimizing energy loss of a building by increasing the heat insulating effect by the heat-
수 백년에 걸친 화석연료의 사용은 지구 온난화를 야기시켜 이상기온에 따른 각종 자연재해를 유발하고 있어, 세계 각국에서는 온실가스의 배출량을 줄이고자 하는 노력이 지속되고 있다. 더욱이 우리나라는 2011년 기준으로 6억977만톤 온실가스 대량배출국가인 미국에 근접하고 있는바, 정부에서는 2014년에 625만톤의 온실가스를 감축하고 단계적으로 감축량을 늘려 2018년에는 그 9배 수준인 5,676만톤까지 줄인다는 계획을 가지고 있다.The use of fossil fuels over hundreds of years has caused global warming, causing various natural disasters due to abnormal temperatures, and efforts are being made to reduce greenhouse gas emissions around the world. In addition, Korea is close to the United States, which is the largest emitter of greenhouse gas at 607.77 million tons in 2011. The government will reduce greenhouse gas emissions by 6.25 million tons in 2014, Of the total.
다른 한편으로, 우리나라는 국내 에너지 수요의 97% 이상을 해외에 의존하고 있으며, 2013년 아시아개발은행은 한국을 비롯한 아시아 국가들이 20년 안에 에너지 부족에 시달릴 것이라는 전망을 내놓고 있다. 더욱이 영국의 최대기업인 석유회사 BP는 화석연료의 가채연수로 석유는 약 40년, 천연가스는 65년, 석탄은 약 155년으로 전망하고 있어 에너지 절약을 위한 노력이 매우 요구되고 있는 현실이다.On the other hand, Korea depends on foreign countries for more than 97% of domestic energy demand. In 2013, the Asian Development Bank is forecasting that Asian countries including Korea will suffer energy shortage within 20 years. In addition, BP, the largest oil company in the United Kingdom, is forecasting for 40 years for oil, 65 years for natural gas, and 155 years for coal due to the training of fossil fuels.
우리나라 전체의 에너지 소비량중 건축물부분이 차지하는 비율은 약 25%이상을 차지하고 있어, 건축물이 열성능을 향상시키는 것이 온실가스의 감축과 에너지 절약을 위한 지름길이라고 할 수 있다. 이에 정부는 2016년부터 건축물에 대하여도 에너지 등급을 표시하도록 하고, 2025년 제로에너지를 목표로 단열기준을 점차 강화시키고 있다.The percentage of energy consumption of the entire country accounts for more than 25% of the total energy consumption of the whole country, and it is a shortcut for reduction of greenhouse gas and energy conservation to improve the thermal performance of the building. Therefore, the government is obliged to display the energy grade for buildings from 2016, and the insulation standard is gradually strengthened with the goal of zero energy in 2025.
건축물의 에너지 손실 중 가장 큰 비중을 차지하는 것은 외피를 통하여 이루어진다. 따라서, 건축물의 신축시에는 외피에 대한 적정단열이 이루어지도록 설계 및 시공이 이루어져야 하며, 기존 건축물에도 단열보강이 이루어지는 것이 요구된다.The largest portion of the energy loss of buildings is through the envelope. Therefore, it is required that the design and construction should be carried out so that the proper insulation is carried out for the outer shell when the building is expanded or contracted, and the thermal insulation reinforcement is also required in the existing building.
또한 에너지 손실의 경로는 전도, 대류 및 복사에 의해 이루어지나, 이중 복사에 의한 열손실은 지붕의 경우 전체의 93%, 벽의 경우 65~80%, 바닥의 경우 50~75%를 차지하여, 최우선적으로 복사에 의한 열손실을 방지하는 것이 가장 바람직한 것임을 알 수 있다.In addition, the path of energy loss is caused by conduction, convection, and radiation. However, heat loss due to duplication is 93% for the roof, 65 ~ 80% for the wall, and 50 ~ 75% It can be seen that it is the most preferable to prevent heat loss by radiation.
따라서 종래의 단열에서는 주로 스티로폴, 유리섬유 등의 저항형 단열재가 사용되어 왔으나, 최근에는 알루미늄 박판을 반사층으로 하는 반사형 단열재가 다양하게 개발·적용되고 있으며, 이러한 반사형 단열재는 일반적으로 알루미늄 박에 폴리에틸렌 폼이나 부직포를 부착시켜 구성시키고 있다.Therefore, in the conventional insulation, resistance type insulators such as styrofoam and glass fiber have been mainly used. However, in recent years, reflection type insulation materials using aluminum thin plate as a reflection layer have been developed and applied variously. Polyethylene foam or a nonwoven fabric is adhered thereto.
한편 반사형 단열재는 알루미늄 박판 등의 반사체가 복사형태로 열이 이동되는 공기층에 접하도록 사용될 때 그 기능이 제대로 발휘된다. 따라서 반사재인 알루미늄 박과 이에 수반되는 폴리에틸렌 폼 및 부직포 등의 단열부재를 어떻게 조합시키느냐, 또 알루미늄 박에 접하는 공기층의 형태 등은 반사형 단열재의 단열성을을 좌우하는 중요한 변수로 작용된다.On the other hand, the function of the reflection type heat insulator is exhibited when the reflector such as the aluminum thin plate is used to contact the air layer in which the heat is moved in the form of radiation. Therefore, how to combine an aluminum foil as a reflector with a heat insulating member such as a polyethylene foam and a nonwoven fabric, and a shape of an air layer in contact with the aluminum foil are important variables that determine the heat insulation property of the reflection heat insulator.
도 1은 2007년 7월 16일 등록번호 10-0741951호에 개시된 건축물용 내·외벽용 반사단열재에 관한 것으로서, 바깥쪽 양 측에 알루미늄 호일층(10a,10b)을 각각 위치하게 하고 그 사이에 폴리에스테르 부직포층(20), 에어버블층(2)(30), 폴리에틸렌 폼 층(40)을 순차로 적층시키고 있다.Fig. 1 is a perspective view of a reflective heat insulating material for interior and exterior walls for use in a building disclosed in Japanese Patent Registration No. 10-0741951 dated Jul. 16, 2007, wherein
상기 등록번호 10-0741951호의 반사단열재는, 그 내부에서는 양 방향의 복사에 의한 열 에너지 손실을 방지할 수 있으나 알루미늄 호일층에 접한 공기층은 완전하게 폐쇄되는 것이 아니어서 반사단열의 효율이 떨어질 뿐 아니라, 벽체에 부착되는 면의 알루미늄 호일층은 공기층에 접하고 있지 않기 때문에 복사에 의한 에너지 손실을 방지할 수 없고 오히려 높은 전도율에 의해 열 에너지 흐름의 통로 역할을 하는 문제점이 있다.The reflection heat insulator of the registration number 10-0741951 can prevent thermal energy loss due to radiation in both directions inside thereof, but the air layer in contact with the aluminum foil layer is not completely closed, , The aluminum foil layer on the surface of the wall attached to the wall is not in contact with the air layer, so that energy loss due to radiation can not be prevented, but rather has a problem in that it acts as a passage for heat energy flow due to a high conductivity.
더욱이 상기 반사단열재는 에어버블층(2)(30)을 중간에 두고 그 양측에 폴리에스테르 부직포층(20)과 폴리에틸렌폼 층(40)을 부착시키는 등 5개의 층으로 이루어져 있어 반사단열재의 두께가 두꺼울 수 밖에 없고, 양 측에는 모두 신축성이 부족한 알루미늄 호일층이 위치하고 있어, 보관·운반 및 작업의 용이성을 도모하기 위하여 롤 형태로 감아지는 상기 반사단열재는 직경의 차이로 인해 내측 알루미늄 호일층이 심한 주름을 형성하면서 이에 부착되었던 폴리에스테르 부직포층 또는 폴리에틸렌폼 층과 분리되거나, 경우에 따라서는 인장력에 의해 외측 알루미늄 호일층이 파손될 우려가 있다.
The reflective heat insulating material is composed of five layers such that the polyester
본 발명은 상기한 종래기술이 가지는 문제점을 해결하기 위한 것으로서, 각 단열부재들을 효율적으로 배치시킴으로써 최소한의 부재로 양 방향에 대하여 복사 및 전도에 의한 열에너지의 이동을 최대한 억제시킬 수 있는 고효율의 에어 단열 시트를 제공함에 그 목적이 있다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide a heat- The purpose of the sheet is to provide.
또한 본 발명은 상기와 같이 최소한의 부재를 사용하여 단열시트의 두께를 줄여 줌으로써 롤 형태로 감더라도 외측에 지나친 인장력이 작용하지 않고, 내측에 주름방지수단을 구비하여 충분한 유연성으로 굴곡진 부분 등 다양한 형상의 부위에 대한 시공을 용이하게 할 뿐 아니라, 어떠한 경우에도 외장부분에 주름이 발생되지 않아 외관이 저해되지 않는 주름방지 기능의 에어 단열 시트를 제공함에 또 다른 목적이 있다.
Further, according to the present invention, since the thickness of the heat insulating sheet is reduced by using the minimum number of members as described above, even when rolled in the form of roll, excessive tensile force does not act on the outside, Another object of the present invention is to provide an airtight insulating sheet having a wrinkle-preventing function that not only facilitates construction of a portion of a shape but also does not cause wrinkles on the outer portion and thus does not hinder the appearance.
상기한 과제를 해결하기 위한 본 발명의 바람직한 실시예에 의하면, 다수의 독립된 밀폐공기셀로 이루어지는 에어버블층과, 표면처리된 알루미늄 박으로 이루어지는 반사층과, 가교 폴리에틸렌 폼으로 이루어지는 다공성의 부피단열층을 순차로 적층시켜 단열부를 형성시키되; 부피단열층이 위치한 상기 단열부의 외면측에는 인쇄필름층이 구비되고, 가교 폴리에틸렌 폼의 양면 중 알루미늄 박이 부착된 면에는 주름방지수단이 구비되는 것을 특징으로 하는 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트가 제공된다.According to a preferred embodiment of the present invention for solving the above problems, an air bubble layer composed of a plurality of independent closed air cells, a reflection layer made of a surface-treated aluminum foil, and a porous volume insulating layer made of a crosslinked polyethylene foam are sequentially To form a heat insulating portion; A heat insulating and wrinkle preventing thermal insulation sheet for a building, characterized in that a print film layer is provided on the outer surface side of the heat insulating portion on which the volumetric insulation layer is disposed, and wrinkle preventing means is provided on a surface of the cross- / RTI >
본 발명의 또 다른 실시예에 의하면, 상기 표면처리된 알루미늄 박은, 순수 알루미늄 박에 PET 박막 코팅한 것과 순수 알루미늄 박에 PET필름을 접착한 것 및 PET필름에 알루미늄을 증착시킨 것 중 어느 하나로 이루어지는 것을 특징으로 하는 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트가 제공된다.According to another embodiment of the present invention, the surface-treated aluminum foil may be formed by coating a thin PET film on a pure aluminum foil, bonding a PET film to a pure aluminum foil, or depositing aluminum on a PET film A heat insulating sheet for energy loss prevention and wrinkle prevention for buildings is provided.
본 발명의 또 다른 실시예에 의하면, 상기 가교 폴리에틸렌 폼은 35배 발표의 가교 폼인 것을 특징으로 하는 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트가 제공된다.According to another embodiment of the present invention, there is provided an air insulation sheet for preventing energy loss and wrinkles for buildings, wherein the crosslinked polyethylene foam is a crosslinked foam having a release ratio of 35 times.
이때, 상기 주름방지수단은 단열부의 내면에 반복적으로 구비되는 길이홈으로서, 상기 길이홈은 마름모 또는 육각형상이 반복되도록 하여 물결무늬의 형상으로 이루어지는 것을 특징으로 하는 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트가 제공된다.Wherein the wrinkle preventing means is a longitudinal groove repeatedly provided on the inner surface of the heat insulating portion, wherein the longitudinal groove is formed in a wavy pattern so as to repeat rhombic or hexagonal phase. A sheet is provided.
본 발명은 반사층의 양쪽면에 밀폐된 공기층과 다공성의 부피단열층을 형성시킴으로써, 하나의 반사층만으로도 양 방향으로의 복사에 의한 에너지 손실을 방지하고 알루미늄 박에 의한 열전도가 발생하지 않도록 함으로서 두께를 최소화시키면서 단열효과를 극대화시킬 수 있게 된다.By forming an air layer and a porous volume insulating layer on both sides of the reflective layer, energy loss due to radiation in both directions is prevented by using only one reflective layer and heat conduction by the aluminum foil is prevented from occurring, It is possible to maximize the adiabatic effect.
또한 본 발명은 롤 형상으로 제작되어 운반성, 보관성 및 시공성을 매우 양호하게 할 수 있게 하면서도, 얇은 두께와 일면에 구비되는 주름방지수단 및 외측에 형성되는 에어버블층(2)은 평탄면의 시공시 외면에 주름이 발생하는 등의 하자가 발생되지 않게 한다.In addition, the present invention can be manufactured in a roll shape, so that the
아울러 본 발명은 외면에 인쇄필름층에 의한 마감문양이 형성되어 있어 별도의 마감작업을 필요로 하지 아니하며, 피접부재에 부착되는 에어버블층(2)의 외면에는 접착층과 이형지가 구비되어 있어 전문가가 아니더라도 누구나 쉽게 기존 건축물에 시공할 수 있는 범용성을 발휘하게 한다.
In addition, the present invention is characterized in that a finish pattern is formed on the outer surface by a printing film layer, so that no separate finishing operation is required, and an adhesive layer and a release paper are provided on the outer surface of the
도 1은 종래기술에 의한 반사단열시트에 관한 설명도이다.
도 2는 본 발명의 일 실시예에 의한 에어 단열 시트의 구성을 전체적으로 나타내는 설명도이다.
도 3은 본 발명의 주름방지수단을 나타낸 일 실시예에 관한 것으로서, (a)는 단열부의 에어버블층을 제외시킨 상태에서의 사시도이고, (b)는 도 2의 A-A' 단면도이다.
도 4는 주름이 발생된 상태를 보여주는 일반적인 단열시트의 사진이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is an explanatory view of a conventional reflective heat-insulating sheet; FIG.
2 is an explanatory view showing the entire construction of an air insulating sheet according to an embodiment of the present invention.
Fig. 3 is a perspective view of a wrinkle preventing device according to an embodiment of the present invention. Fig. 3 (a) is a perspective view of the heat insulating portion with the air bubble layer removed. Fig. 3 (b) is a sectional view taken along the line AA 'in Fig.
Fig. 4 is a photograph of a general heat insulating sheet showing a state where wrinkles are generated.
이하에서는 본 발명의 실시 예를 첨부된 도면을 참조하여 상세히 설명한다. 그러나 본 발명을 설명함에 있어 공지의 구성을 구체적으로 설명함으로 인하여 본 발명의 기술적 사상을 흐리게 하거나 불명료하게 하는 경우에는 위 공지의 구성에 관하여는 그 설명을 생략하기로 한다.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following description of the present invention, however, it is to be understood that the present invention is not limited to the disclosed embodiments.
도 2는 본 발명의 일 실시예에 의한 에어 단열 시트(S)의 구성을 전체적으로 나타내는 설명도이다.2 is an explanatory view showing the entire construction of the air insulating sheet S according to the embodiment of the present invention.
상기한 본 발명의 에어 단열 시트(S)는 신축 건축물은 물론 기존 건축물의 벽체에 간편하게 부착 시공할 수 있도록 롤 형상으로 제조되며, 양면 모두가 낮은 표면방사율을 가지는 반사층(1)을 사이에 두고, 공기의 흐름이 완전 차단된 밀폐 공기층과 다공성의 부피단열재가 상기 반사층(1)의 양면에 직접 면하도록 부착되는 단열구조를 포함하여 이루어진다.The heat insulating sheet S according to the present invention is manufactured in a roll shape so that it can be easily attached to a wall of an existing building as well as a new construction and a new building and has a
여기에서 표면방사율이라 함은 반사율과 대응되는 것으로서, 물질의 표면이 반사 에너지를 발산하는 정도를 의미한다. 따라서 표면방사율이 낮을수록 그 표면에서 방출되는 열이 적어지므로 반사형 단열재로서는 기능성은 높아진다.Here, the surface emissivity refers to the degree to which the surface of the material emits the reflected energy, corresponding to the reflectance. Therefore, the lower the surface emissivity, the less heat is released from the surface, so that the functionality of the reflective insulation increases.
순수 알루미늄 박의 표면방사율은 0.03 정도로서 표면방사율이 0.12인 강판 등에 비해 매우 낮은 표면방사율을 가지고 있어 반사형 단열재의 반사층으로서는 최적의 것이라고 할 수 있다. The surface emissivity of the pure aluminum foil is about 0.03, which is very suitable for the reflection layer of the reflection type insulator because it has a very low surface emissivity compared with the steel plate having the surface emissivity of 0.12.
그러나 이러한 순수 알루미늄 박은 알칼리에 매우 약하기 때문에 이를 그대로 알칼리성을 가지는 시멘트 콘크리트 벽체에 사용하는 경우 쉽게 부식되어 내구성이 떨어지는 문제점이 있다.However, since such pure aluminum foil is very weak to alkali, when it is used in a cement concrete wall having alkalinity as it is, it is easily corroded to deteriorate durability.
따라서 본 발명에서 사용되는 반사층(1)은 내부식성을 증가시키기 위한 표면처리가 이루어진 알루미늄 박으로 이루어진다. 상기한 표면처리방법은 순수 알루미늄 박에 PET필름을 접착하거나 PET필름에 알루미늄을 증착시키는 방법으로 이루어질 수도 있으나, 순수 알루미늄 박에 PET 박막 코팅의 방법으로 표면처리하는 것이 바람직하다. PET 박막 코팅하는 경우에는 PET필름을 접착하거나 증착시키는 것에 비해 방사율이 그다지 높아지지 않아 반사단열에 더욱 유리하다.Therefore, the
반사층에는 열이 이동되는 공기층이 접하고 있을 때 그 기능이 제대로 발휘되며, 이러한 공기층을 위한 독립 공기셀의 확보와 그 크기는 단열성능의 극대화를 위한 중요한 변수로 작용하게 된다.The function of the reflective layer is exhibited when the air layer to which the heat moves is in contact with the air layer. The size and the size of the independent air cell for the air layer serve as important parameters for maximizing the heat insulation performance.
이를 위해 본 발명의 알루미늄 박 일면, 보다 구체적으로는 본 발명의 에어 단열 시트(S)의 양 면중 유리나 벽구조체 등의 피접부재(이들을 통칭하여 '벽체'라 한다)에 접하는 면에는 다수의 독립된 밀폐공기셀로 이루어지는 에어버블(속칭 '에어캡'으로 불리는 것을 말한다)층이 형성된다.To this end, the surfaces of the aluminum foil of the present invention, more specifically, the surfaces contacting the contact members (collectively referred to as "walls") such as glass or wall structures on both surfaces of the heat insulating sheet S of the present invention, An air bubble (referred to as an 'air cap') layer made of an air cell is formed.
공기의 열전도율은 온도에 따라 다소 달라지나 0.0203 Kcal/m.h℃ 정도로서, 장섬유 중공부직포의 0.31 Kcal/m.h℃ 내지 폴리에틸레 폼의 0.043~0.050 Kcal/m.h℃에 비해 현저히 낮다.The thermal conductivity of air varies slightly depending on the temperature, but is about 0.0203 Kcal / m.h ° C, which is significantly lower than 0.31 Kcal / m.h ° for long fiber hollow nonwoven fabric and 0.043-0.050 Kcal / m.h ° for polyethylform.
또 독립된 에어버블층(2)의 밀폐공기셀에 충진된 공기층은, 부직포나 발포폼에 형성된 공극에 충진된 공기층에 비해 밀폐성이 높아 공기의 흐름이 완전 차단되는 밀폐공기층(2a)을 형성시킴과 아울러, 공기층의 크기가 월등하기 때문에 반사층에 의한 복사열 차단효과가 훨씬 높다.The air layer filled in the closed air cell of the independent
따라서 벽체에 부착된 에어버블층(2)은 벽체로부터 들어오는 열이 단열시트(S) 내부로 전달되는 것을 최대한 억제시키면서 반사단열의 효율을 극대화시킨다.Therefore, the
이와 함께 유연성이 매우 좋은 에어버블층(2)을 벽체에 부착되는 면에 둠으로써 후술하는 주름방지수단과 함께, 에어 단열 시트(S)를 권취하거나 굴곡부위에 시공할 때에 마감층이 되는 에어 단열 시트(S) 외면측의 인쇄필름층(4)에 과다한 인장력이 가해지지 않도록 하여 하자 발생률을 줄여줌과 아울러 양호한 시공성을 가지게 한다.In addition, the
표면처리된 알루미늄 박의 타면, 구체적으로 실내(내단열의 경우) 또는 실외(외단열의 경우)의 외기에 노출되는 면쪽에는 가교 폴리에틸렌 폼으로 이루어지는 다공성의 부피단열층(3)이 위치한다.A porous
폴리에틸렌 폼은 열전도율이 0.043~0.050 Kcal/m.h℃으로 낮으면서 무독성으로, 열에 강해 열화현상이 쉽게 발생되지 않으면서 열융착 등 가공에 유리하다. 더욱이 다공성을 이루는 기포는 이방성을 가지고 있어 시트의 연신성이 높다는 장점이 있다.The polyethylene foam has a low thermal conductivity of 0.043 to 0.050 Kcal / m.h ° C, is non-toxic, and is resistant to heat and is not easily deteriorated. Furthermore, the porous bubble has an anisotropic property and has an advantage that the sheet has high elongation.
본 발명에서 사용되는 폴리에틸렌 폼은 가교된 것이 사용된다. 가교된 폴리에틸렌 폼은 무가교 폼에 비해 열전도율이 낮으며 유연성이 월등한다. 상기 본 발명의 가교 폴리에틸렌 폼은 다양한 배율로 발포될 수는 있으나 바람직하게는 35배 발포된 것을 사용한다. 40배로 발포된 폴리에틸렌 폼은 열전도율이 0.048 Kcal/m.h℃임에 비해 35배로 발포된 폴리에틸렌 폼은 0.043 Kcal/m.h℃로 더 낮은 열전도율을 가지고 있다.The polyethylene foam used in the present invention is crosslinked. Cross-linked polyethylene foam has lower thermal conductivity and superior flexibility than uncoated foam. The crosslinked polyethylene foam of the present invention may be foamed at various magnifications, but preferably 35 times foamed foamed foam is used. The polyethylene foam foamed at a magnification of 40 times has a lower thermal conductivity of 0.043 Kcal / m.h ° C than that of polyethylene foam foamed at 35 times the thermal conductivity of 0.048 Kcal / m.h ° C.
상기 폴리에틸렌 폼은 에어 단열 시트(S)의 형상성을 유지시키면서 그 내부에 형성된 독립기포층을 이용하여 반사층(1)이 반사단열의 기능을 충분히 수행할 수 있게 하며, 자체적으로는 대류현상을 감소시켜 열이 전달되는 것을 방지하는 저항형 단열재로서의 기능을 한다.
The polyethylene foam enables the
이와 같이 다수의 독립된 밀폐공기셀로 이루어지는 에어버블층(2), 표면처리된 알루미늄 박으로 이루어지는 반사층(1) 및, 가교 폴리에틸렌 폼으로 이루어지는 부피단열층(3)을 순차로 적층하여 단열부를 구성하게 되는 바, 상기 단열부의 양 면중 외기에 면하는 외면측인 폴리에틸렌 폼의 일면에는 인쇄필름층(4)이 구비된다.In this manner, the
인쇄필름층(4)은 외장 마감층을 구성하는 것으로서, 바람직하게는 PET(Polyethylene Terephthalate) 필름이 사용된다. 상기 PET 필름은 플라스틱 필름 중에서 인장강도가 가장 크고, 수증기나 기체의 투과율이 낮아 방습성이 우수하다.The
또 PET 필름의 내면에는 알루미늄을 증착시키는 것이 바람직하다. 이러한 알루미늄 증착면은 인쇄필름층(4)의 강성을 더욱 증가시킬 뿐 아니라 또 하나의 반사층을 형성시킴으로써 앞서 설명한 단열부를 통과하는 아주 적은 양에 대하여 또 다시 열적 흐름을 차단시킴으로써 본 발명의 에어 단열 시트(S)에 대한 전체적인 단열성능을 향상시키게 한다.It is also preferable to deposit aluminum on the inner surface of the PET film. This aluminum deposition surface not only increases the rigidity of the
상기한 인쇄필름층(4)에는 다양한 무늬의 문양을 인쇄함으로써 단열시공 후 별도의 마감작업을 필요하지 않게 하여, 기존 건축물의 벽체에 대하여 누구나 간편하게 단열시공 내지 보강작업을 할 수 있게 한다.
By printing patterns of various patterns on the
단열부와 인쇄필름층(4)으로 구성되는 본 발명의 에어 단열 시트(S)는 롤 타입으로 제작 및 관리되며 작업현장으로 이송된다. 롤 타입의 단열시트는 판상 타입의 단열패널에 비하여 운반성 및 보관성이 뛰어나며, 유연성으로 기둥, 보, 벽면의 모서리 등 꺽임부분에 대하여도 시공성이 뛰어나다.The heat insulating sheet S of the present invention constituted by the heat insulating portion and the
그러나 이러한 롤 형태로 권취되는 일반적인 단열시트는 앞서 설명한 바와 같이, 감겨진 롤에서의 위치하는 내경과 외경의 차이로 인하여 단열시트의 단면 중심축을 기준으로 내측에는 압축응력이 발생하게 되어 주름이 발생하게 되고 심한 경우에는 부재들간에 분리현상이 발생될 우려가 있다.However, as described above, since a general heat insulating sheet wound in the form of rolls is subjected to a compressive stress in the inner side relative to the center axis of the end face of the heat insulating sheet due to the difference between the inner diameter and the outer diameter, In severe cases, separation phenomenon may occur between the members.
이와 반대로 단열시트의 단면 중심축을 기준으로 외측에는 인장응력이 발생하면서 외면의 부재를 신장시키게 되는 바, 이러한 상태로 장시간 경과하게 되면 상기한 외면 부재는 롤 형상의 단열시트를 풀어 평탄하게 놓아 상기한 응력들을 제거하더라도 신장된 길이가 줄어들지 않게 되며, 이러한 현상은 권취된 롤의 중심부분으로 갈수록 더욱 심하게 나타난다.On the other hand, tensile stress is generated on the outside of the heat insulating sheet with respect to the center axis of the heat insulating sheet, and the member on the outer surface is stretched. When the state of the outer surface has elapsed for a long time, Eliminating the stresses does not reduce the elongated length, and this phenomenon becomes even more severe as the roll is moved toward the center of the wound roll.
따라서 롤 타입으로 권취된 상태로 보관되고 운반된 단열시트를 유리면이나 벽면 등의 평탄면에 시공하게 되면 그동안 신장된 부분이 주름을 형성하게 되므로 별도의 마감층을 시공해야 하는 번거로움이 발생하게 되며, 이와 더불어 본 발명의 경우에서와 같이 외장 마감층을 구비시킨 경우에는 외관의 저해되는 불량시공의 우려가 있게 된다. 도 4는 상기와 같은 주름이 발생된 단열시트의 일 예의 사진이다.Therefore, if the heat-insulating sheet stored and transported in a rolled-up state is applied to a flat surface such as a glass surface or a wall surface, since the elongated portion forms wrinkles in the meantime, it is troublesome to construct a separate finish layer In addition, when the exterior finishing layer is provided as in the case of the present invention, there is a fear of poor construction that the appearance is inhibited. 4 is a photograph of an example of the heat-insulating sheet in which the wrinkles are generated as described above.
본 발명은 단열부의 내면측에 주름방지수단을 구비시킴으로써 상기한 문제점을 해결한다. 도 3은 상기한 주름방지수단의 일 실시예를 나타낸 것으로서, (a)는 단열부의 에어버블층(2)을 제외시킨 상태에서의 사시도이고, (b)는 도 2의의 A-A' 단면도이다.The present invention solves the above problem by providing wrinkle preventing means on the inner surface side of the heat insulating portion. FIG. 3 is a perspective view of the wrinkle preventing means in the state where the
상기한 주름방지수단은 단열부의 내면에, 보다 구체적으로는 도 3의 (b)에서와 같이 가교 폴리에틸렌 폼의 양면 중 알루미늄 박이 부착된 면에 길이홈(3a)을 반복 형성시킴으로써 이루어진다.The wrinkle preventing means described above is formed on the inner surface of the heat insulating portion, more specifically, as shown in Fig. 3 (b), by repeatedly forming the
이와 같이 알루미늄 박에 부착된 가교 폴리에틸렌 폼에 형성된 길이홈(3a)은 에어 단열 시트(S)가 권취될 때 내측이 쉽게 접어지게 함으로써 알루미늄 박과 가교 폴리에틸렌 폼간의 분리 가능성을 제거해 주며, 반대측에 위치한 인쇄필름층(4)에 발생하는 인장응력의 크기를 감소시켜 평탄면 시공후 표면에 주름이 발생될 수 있는 여지를 최소화시킨다.The
상기한 길이홈(3a)은 벽체에 접착되는 면에 구비되므로 시공후에는 감추어져 외관을 저해하지 않을 뿐 더러, 반사층(1) 전면의 또 다른 공기층을 형성하여 단열성능 향상에 기여하게 된다.Since the
주름방지수단의 길이홈(3a)은 에어 단열 시트(S)의 폭방향으로 다수 개를 평행하게 구성시킬 수도 있으나, 보다 바람직하게는 도 3의 (a)에 나타낸 바와 같이 마름모 형상이 반복되도록 형성시킨다. 이러한 마름모 형상의 길이홈(3a)은 현장여건에 따라 여러 방향으로 접어져 보관되는 경우에도 각 방향 모두에 대하여 주름이 발생하는 것을 방지할 수 있게 한다.The
단열부의 에어버블층(2)의 외면에는 점착층(5)과 이형지(6)를 순차로 구비시켜 시공의 용이성을 보다 향상시킬 수 있다.The
따라서 유연성이 매우 좋은 본 발명의 에어 단열 시트(S)는 상기 이형지(6)만을 제거하고 단열부위에 부착함으로써 시공이 완료되는 것이므로, 전문가가 아니더라도 누구나 손쉽게 사용할 수 있는 범용성이 있다.
Accordingly, since the air insulation sheet S of the present invention is very flexible, the construction is completed by removing only the
이상에서 본 발명은 구체적인 실시 예를 참조하여 상세히 설명하였으나, 상기 실시 예는 본 발명을 이해하기 쉽도록 하기 위한 예시에 불과한 것이므로, 이 분야에서 통상의 지식을 가진 자라면 본 발명의 기술적 사상의 범위 내에서 이를 다양하게 변형하여 실시할 수 있을 것임은 자명한 것이다. 따라서 그러한 변형 예들은 청구범위에 기재된 바에 의해 본 발명의 권리범위에 속한다고 할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the scope of the invention is not limited to the disclosed embodiments, but, on the contrary, It is obvious that it will be possible to carry out various modifications thereof. It is therefore intended that such modifications are within the scope of the invention as set forth in the claims.
1: 반사층 2: 에어버블층
2a: 밀폐공기층 3: 부피단열층
3a: 길이홈 4: 인쇄필름층
5: 점착층 6: 이형지
S: 에어 단열 시트1: reflection layer 2: air bubble layer
2a: airtight air layer 3: volume insulation layer
3a: longitudinal groove 4: printing film layer
5: Adhesive layer 6: Release paper
S: Air insulation sheet
Claims (7)
상기 단열시트는 다수의 독립된 밀폐공기셀로 이루어지는 에어버블층(2)과, 표면처리된 알루미늄 박으로 이루어지는 반사층(1)과, 가교 폴리에틸렌 폼으로 이루어지는 다공성의 부피단열층(3)을 순차로 적층시켜 단열부를 형성시키되; 부피단열층(3)이 위치한 상기 단열부의 외면측에는 인쇄필름층(4)이 구비되고, 가교 폴리에틸렌 폼의 양면 중 알루미늄 박이 부착된 면에는 주름방지수단이 구비되는 것으로서, 상기 주름방지수단은 마름모 또는 육각형상이 반복되어 물결무늬의 형상이 이루어지도록 하는 길이홈(3a)인 것을 특징으로 하는 건축물용 에너지손실 방지 및 주름방지 에어 단열 시트.
A heat-insulating sheet attached to a wall of a building,
The heat insulating sheet is formed by sequentially laminating an air bubble layer 2 made of a plurality of independent closed air cells, a reflection layer 1 made of a surface-treated aluminum foil, and a porous volume heat insulating layer 3 made of a crosslinked polyethylene foam Forming an insulating portion; A printing film layer (4) is provided on the outer surface side of the heat insulation part (3) on which the volumetric insulating layer (3) is placed, and wrinkle preventing means is provided on the surface of the crosslinked polyethylene foam on which the aluminum foil is attached, Wherein the longitudinal groove (3a) is a longitudinal groove (3a) in which a wavy pattern is formed by repeating the phase of the wrinkle preventing airfoil.
The structure according to claim 1, wherein the surface-treated aluminum foil is one of a pure aluminum foil coated with a PET thin film, a pure aluminum foil bonded with a PET film, and a PET film vapor-deposited with aluminum Energy loss prevention and anti-wrinkle air insulation sheet.
The heat insulating sheet according to claim 1, wherein the crosslinked polyethylene foam is a crosslinked foam having a release ratio of 35 times.
The heat insulating and anti-wrinkle heat insulating sheet for a building according to claim 1, wherein the printing film layer (4) is formed by depositing aluminum on the inner surface of a PET film.
The air-insulating sheet according to claim 1, wherein an adhesive layer (5) and a release paper (6) are sequentially formed on an outer surface of the air bubble layer (2).