KR101572629B1 - Net - Google Patents
Net Download PDFInfo
- Publication number
- KR101572629B1 KR101572629B1 KR1020130099318A KR20130099318A KR101572629B1 KR 101572629 B1 KR101572629 B1 KR 101572629B1 KR 1020130099318 A KR1020130099318 A KR 1020130099318A KR 20130099318 A KR20130099318 A KR 20130099318A KR 101572629 B1 KR101572629 B1 KR 101572629B1
- Authority
- KR
- South Korea
- Prior art keywords
- monofilament
- yarn
- monofilament yarn
- pvc
- coated
- Prior art date
Abstract
본 발명은 PVC코팅된 모노필라멘트사를 이용한 망 및 그 제조방법에 과한 것으로, PVC 코팅된 모노필라멘트사와 모노필라멘트사를 사용하여, 미세날벌레 침입을 막으면서 우수한 공간율로 통기성을 확보하고, 고광택을 위해 표면이 매끄러운 경질의 원사로 망을 형성하더라도 방충망틀 상에서 미끄러져 쉽게 이탈되는 현상을 방지하고, 사용중 고정력이 견고하게 유지되도록 하면서, 권취시에 네트 원단이 권취봉에 밀착되면서 권취되고, 재단 및 사용중에 올푸림이 방지되며, 경질의 합성수지 모노필라멘트사에 의하여 고광택이 가능하고, 생산원가가 부담되지 않는 미세망의 구현이 가능하도록 하는 PVC코팅된 모노필라멘트사를 이용한 망 및 그 제조방법에 관한 것이다.The present invention relates to a net using a PVC coated monofilament yarn and a method of manufacturing the same, and is characterized in that a PVC coated monofilament yarn and a monofilament yarn are used to ensure air permeability at a high spatial rate while preventing intrusion of fine insects, The net cloth is wound on the take-up stick while being wound tightly while being wound while preventing the phenomenon that the net is formed by the hard and smooth yarn whose surface is smooth and slip on the screen frame and is easily separated from the net, The present invention relates to a net using a PVC coated monofilament yarn and a method of manufacturing the same using a PVC coated monofilament yarn which is capable of high gloss by using a rigid synthetic resin monofilament yarn during use, will be.
Description
본 발명은 PVC코팅된 모노필라멘트사를 이용한 망 및 그 제조방법에 관한 것으로, 보다 상세하게는 방충망, 블라인드, 롤스크린 등에 사용되는 망을 제조함에 있어서 PVC 코팅된 모노필라멘트사를 사용하여, 미세날벌레 침입을 막으면서 우수한 공간율을 갖도록 하고, 권취봉에 밀착되면서 권취되고 고광택으로 미감이 향상되며 올풀림 및 조직변형이 발생되지 않고, 설치 및 사용중 미끄러짐으로 인한 이탈이 방지되며, 고강도를 갖는 PVC코팅된 모노필라멘트사를 이용한 망 및 그 제조방법에 관한 것이다.The present invention relates to a net using a PVC coated monofilament yarn and a method of manufacturing the same, and more particularly to a monofilament yarn using a PVC coated monofilament yarn to produce a net used for an insect control net, a blind, a roll screen, And is wound up while being closely attached to the winding rod to improve the aesthetics with high gloss and prevents the occurrence of artificial deformation and tissue deformation, prevents slippage due to installation and use, and prevents the PVC coated mono Filament yarn and a method of manufacturing the same.
가정이나 사무실과 같은 실내 공간에는 사생활을 보호하도록 시야를 가려주면서 통기성도 확보하고 햇빛을 차단하는 발, 롤스크린, 블라인드(수직, 수평블라인드 모두 포함)가 설치되며, 이외에도 통기성을 확보하면서 해충의 침입을 막는 방충망이 설치되며, 이러한 방충망, 발, 롤스크린, 블라인드(수직, 수평블라인드) 등은 모두 망 원단을 사용할 수 있고, 그 적용 목적에 따라 각각 다른 디바이스(프레임, 레일 등)에 의하여 창문에 설치된다.Inside the home such as a home or office, the ventilation is ensured while protecting the privacy, while the foot, roll screen, and blinds (including both vertical and horizontal blinds) that block the sunlight are installed. In addition, (Screen, rails, etc.) are installed in the windows according to the application purpose of the screen cloth, and the screen cloth, the screen, the roll screen, and the blind .
이중 방충망은 가정이나 사무실과 같은 실내 공간에는 외부로부터 모기나 파리, 날파리 등의 곤충이 침입하는 것을 막으면서 통기성도 보장하기 위하여 약 0.15mm의 알루미늄, 스테인레스 등의 금속사로 이루어져 창문에 설치된다.The double insect screen is installed in a window made of metal such as aluminum and stainless steel of about 0.15 mm to ensure ventilation while preventing insects such as mosquitos, flies, and lynxes from entering the interior space such as a home or office.
그러나, 상기한 방충망의 경우 금속사로 이루어지고 외부와 접촉이 되는 환경이므로, 빗물 등에 의하여 사용 중 녹이 발생되고, 일조시간 동안은 외부의 열기가 그대로 실내로 전달되어 방충망을 주로 사용하는 여름에는 실내온도를 높이는 역할을 하며, 금속사로만 이루어져 있어서 외관이 좋지 않은 문제점이 있고, 설치에 있어서도 일반인이 용이하게 설치할 수 없고 전문 시공업자가 시공을 해야 하는 문제점이 있으며, 투시성 확보를 위하여 인치(inch)당 18~22개 사이의 금속사가 사용되므로 미세날벌레 침입이 가능하여 필터성이 저하되는 문제점이 있었다.However, in the case of the insect-control net described above, since it is made of metal and comes into contact with the outside, rust is generated due to rain or the like during the use, There is a problem that the appearance is not good because it is made only of a metal sheet and there is a problem that a public person can not easily install it in the installation and there is a problem that a professional contractor has to construct it. In order to secure visibility, ~ 22 pieces of metal yarn are used, so that it is possible to intrude micro-fly, resulting in deterioration of filterability.
이러한 금속사로 이루어진 방충망의 녹발생과 시공의 어려움 등을 해소하면서 외부에서 실내를 볼 때 실내가 훤히 들여다보이지 않도록 하여 사생활을 보호하고 고광택으로 외관을 향상한 네트 원단을 본 발명의 출원인은 특허출원 10-2010-0097113호에 제시하였으며, 그 내용을 살펴보면 합성수지 모노필라멘트사를 이용하여 제조된 네트의 일면에 금속나노코팅층을 형성함으로서, 금속나노코팅층에 의하여 난반사를 발생시켜 외부로부터 실내의 투시성을 차단하여 사생활을 보호하고, 녹이 발생되지 않도록 하며, 외부열이 내부로 전달되지 않도록 하고, 유해물질검출이 없는 친환경적이고 디자인이 우수하며 사생활보호가 가능하도록 하는 네트 및 그 제조방법을 제시하고 있다.The applicant of the present invention has applied the
상기한 본 발명 출원인의 선출원에서는 모노필라멘트사를 사용함으로서 고광택이 가능하지만, 상기 모노필라멘트사는 경질로서 표면이 매끄러워 현관, 창문 등에 사용되는 방충망에 적용시 가압고정된 단부가 방충망틀상에서 쉽게 이탈되는 문제점이 있었다.However, the monofilament yarn is hard and its surface is smooth. When applied to an insect screen used for a door, a window or the like, the press-fixed end is easily detached from the screen frame There was a problem.
즉, 방충망틀상에 형성되는 끼움홈에 네트의 가장자리부를 위치시키고, 가스켓을 롤러로 밀어서 두변부터 고정 후, 나머지 두변을 당기면서 시공하고 있지만, 네트의 주름을 제거하기 위해 나머지 두변을 당기는 과정에서 모노필라멘트사의 매끄러운 표면으로 인해 가스켓에 의해 미리 고정된 두변의 끼움부분이 빠지거나, 사용 중 미세외력에도 네트가 쉽게 이탈되는 폐단이 따랐다.In other words, although the edges of the net are positioned in the fitting grooves formed on the screen frame, the gasket is pushed by the rollers and fixed from the two sides, and the other two sides are pulled. However, in the process of pulling the remaining sides, Due to the smooth surface of the filament yarn, the fittings of the two sides previously fixed by the gasket were dislodged, or the net was easily separated from the micro-external force during use.
이에 따라 본 발명의 출원인은 대한민국 실용신안등록출원 20-2012-0001451호에서 모노필라멘트사를 이용하는 원단에 있어서, PVC 코팅된 멀티필라멘트사를 상기 모노필라멘트사 사이에 투입한 미끄럼방지 네트에 대한 기술을 출원하였으나, 상기 멀티필라멘트사는 0.3~0.35mm 직경으로 실제조기 1대당 1일 생산량이 100kg정도의 생산량을 갖는다면 0.2mm 직경의 실을 제조할 경우 잘 끊어져서 사출장력을 높일 수 없고 이로 인하여 분당 사속이 낮아짐으로 20kg정도밖에 생산을 할 수가 없어서 생산성이 낮아지므로 원사가격이 상승하게되어 미세직경의 원사는 현실적으로 생산이 어려운 문제점이 있었다.Accordingly, the applicant of the present invention has proposed a technique for a non-slip net in which a PVC coated multifilament yarn is inserted between monofilament yarns in a fabric using a monofilament yarn in Korean utility model registration application No. 20-2012-0001451 However, if the production amount of the multifilament yarn is 0.3 to 0.35 mm in diameter and the production amount per one minute of the actual production per one day is about 100 kg, if the yarn having a diameter of 0.2 mm is manufactured, the yarn can not be broken easily and the injection tension can not be increased. It is impossible to produce only about 20 kg due to the lowering of the productivity, so that the productivity is lowered, so that the price of the yarn is increased.
그리고, 공기가 통하면서 미세 날벌레 등을 저지하기 위해서는 네트 원단의 통공 사이즈가 0.5mm정도 되어야 하고 이를 위해서는 원사의 직경이 0.2mm정도가 되어야 하지만 상기한 바와 같이 PVC코팅용 멀티필라멘트 원사는 0.2mm정도의 직경으로는 사실상 생산이 어렵기 때문에, 통공 사이즈가 0.5mm 미만의 미세망을 구현하기 위해서는 가격이 매우 높아지고, 가격을 현실화하기 위해서는 0.5mm 미만의 미세망은 구현이 불가능한 문제점이 있었다.
In order to block the micro flysch while the air passes through, the diameter of the thread should be about 0.2 mm in order to achieve a through hole size of about 0.5 mm. However, as described above, the multifilament yarn for PVC coating has a diameter of about 0.2 mm It is difficult to produce a fine mesh of less than 0.5 mm in order to realize a price, and the price is too high to realize a fine mesh having a through hole size of less than 0.5 mm.
한편, 상기한 특허출원 10-2010-0097113호에서는 모노필라멘트사를 사용함으로서 고광택이 가능하지만, 상기 모노필라멘트사는 경질이므로 최근 현관, 창문 등에 사용되는 권취형 방충망(관련선행기술 : 공개특허 특2002-0021655, 등록실용 20-0398773, 등록실용 20-0398812 등)에 적용시, 올풀림 및 조직변형이 발생됨은 물론 도 1에 나타내는 바와 같이 네트원단(12)이 권취봉(14)에 밀착되어 권취되지 않고 경질섬유의 특성에 의하여 펼쳐지려고 함으로서 유격을 가지고 권취되어 권취봉이 설치되는 하우징의 크기가 커지게 되고, 특히 네트원단이 2m~2.4m정도의 길이가 요구되는 경우 권취봉이 설치되는 하우징의 크기가 너무 커지게 되어 적용할 수 없는 문제점이 있었다.Meanwhile, in the above-mentioned patent application 10-2010-0097113, it is possible to obtain a high gloss by using monofilament yarn. However, since the monofilament yarn is hard, the winding-type insect screening net used in the front porch, When the
이에 따라 본 발명의 출원인은 대한민국 실용신안등록출원 20-2012-0001450호 및 20-2011-0008555호에서 네트 원단의 권취방향 원사는 유연성을 갖는 연질의 합성수지 원사를 사용하고, 네트원단의 권취방향에 수직방향의 원사는 경질의 합성수지 모노필라멘트사, 또는 상기 경질의 합성수지 모노필라멘트사와 PVC코팅사를 사용한 기술을 제시하였으나, 상기 연질의 합성수지 원사는 광택이 없어서 고광택이 불가능하고, 모노필라멘트사와 결합력이 없어서 성형시 올풀림이 발생될 수 있으며, 이러한 올풀림을 방지하기 위하여 PVC코팅사를 임의의 간격으로 사용하였으나 충분한 광택을 갖지 못하고 원하는 공간율을 확보하기는 용이하지 않았다.Accordingly, the applicant of the present invention has found that in the utility model registration application 20-2012-0001450 and 20-2011-0008555, the yarn in the winding direction of the net fabric is made of soft synthetic resin yarn having flexibility, In the case of a vertical yarn, a technique of using a hard synthetic fiber monofilament yarn or a hard synthetic resin monofilament yarn and a PVC coated yarn has been proposed. However, the soft synthetic resin yarn is not glossy and can not have high gloss, In order to prevent this occurrence, PVC coated yarns were used at an arbitrary interval, but they did not have sufficient gloss and it was not easy to obtain a desired space factor.
본 발명은 상기한 문제점을 해결하기 위한 것으로, 방충망, 블라인드, 롤스크린 등에 사용되는 망을 제조함에 있어서 PVC 코팅된 모노필라멘트사와 모노필라멘트사를 사용하여, 미세날벌레 침입을 막으면서 우수한 공간율로 통기성을 확보하고, 고광택을 위해 표면이 매끄러운 경질의 원사로 망을 형성하더라도 방충망틀 상에서 미끄러져 쉽게 이탈되는 현상을 방지하고, 사용중 고정력이 견고하게 유지되도록 하면서, 권취시에 네트 원단이 권취봉에 밀착되면서 권취되고, 재단 및 사용중에 올푸림이 방지되며, 경질의 합성수지 모노필라멘트사에 의하여 고광택이 가능하고, 생산원가가 부담되지 않는 미세망의 구현이 가능하도록 하는 PVC코팅된 모노필라멘트사를 이용한 망 및 그 제조방법을 제공하는 데 목적이 있다.DISCLOSURE OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a net for use in insect screens, blinds, roll screens, etc. by using PVC coated monofilament yarns and monofilament yarns, The net fabric is tightly adhered to the winding rod at the time of winding while preventing the phenomenon that the web is slid off easily on the screen frame even if the net is made of a hard and hard surface yarn for high gloss, A monofilament made of PVC coated monofilament yarn which is wrapped, prevented from coming off during cutting and use, capable of high gloss by hard synthetic fiber monofilament yarn, and capable of realizing a fine network that does not incur a production cost And a manufacturing method thereof.
상기한 목적을 달성하기 위한 본 발명의 특징은, 모노필라멘트사와 PVC 코팅된 모노필라멘트사로 제직된 망에 있다.In order to accomplish the above object, the present invention is characterized in that a monofilament yarn and a PVC coated monofilament yarn are woven into a net.
상기에서 망은 모노필라멘트사로 이루어진 경사 또는 위사 또는 경사와 위사 배열 사이사이에 PVC 코팅된 모노필라멘트사를 삽입하여 망을 형성한다.In this case, the mesh is formed by inserting a monofilament yarn made of monofilament yarn or a PVC-coated monofilament yarn between warp or weft yarns and weft yarns.
또한, 상기 망은 그 권취방향으로는 PVC 코팅된 모노필라멘트사를 사용하고, 망의 권취방향에 수직방향으로는 PVC 코팅된 모노필라멘트사와 멀티필라멘트사를 혼합 배치하여 사용하는데, 상기 모노필라멘트사와 PVC 코팅된 모노필라멘트사는 10~20:1의 비율로 배치되어 망이 형성된다.The monofilament yarn of PVC coated monofilament yarn is used in the winding direction of the web, and the monofilament yarn and the multifilament yarn of PVC coated monofilament yarn are mixed and disposed in a direction perpendicular to the winding direction of the web. The coated monofilament yarns are arranged at a ratio of 10 to 20: 1 to form a mesh.
한편, 상기 모노필라멘트사(10)는 검정계열로 형성되어 밀도 28-50EA/Inch, 개구사이즈 450-1000㎛로 망을 형성하는 것을 특징으로 한다.Meanwhile, the
한편, 본 발명의 다른 특징은 모노필라멘트사와 PVC 코팅된 모노필라멘트사로 망을 제직한 후, 160~220도에서 20-60m/분의 속도로 텐터가공을 통해 열융착하는 망 제조방법에 있다.In another aspect of the present invention, there is provided a method for manufacturing a mesh which is manufactured by weaving a mesh with a monofilament yarn and a PVC coated monofilament yarn, and then thermally fusing the yarn at a speed of 20 to 60 m / min at 160 to 220 degrees.
이와 같이 구성된 본 발명에 의하면 모노필라멘트사와 PVC 코팅된 모노필라멘트사로 망이 제직됨으로서, 망을 형성하는 섬유의 직경이 작아서 미세날벌레의 침입을 방지하면서 충분한 공간율을 확보하게 되어 통기성이 우수한 방충망을 제공할 수 있게 되고, 우수한 강도를 갖는 망을 제공할 수 있게 된다.According to the present invention constructed as described above, since the mesh is formed by the monofilament yarn and the PVC coated monofilament yarn, the diameter of the fibers forming the mesh is small, thereby securing a sufficient space ratio while preventing the invasion of the microscopic beads, thereby providing an insect- It becomes possible to provide a network having excellent strength.
또한, 강도가 우수한 모노필라멘트사에 PVC코팅을 함으로서 PVC코팅과정에서 원사의 절단에 대한 염려가 종래 멀티필라멘트사에 비하여 대폭 감소되므로, 직경이 작은 PVC코팅된 모노필라멘트사의 제작이 용이할 뿐 아니라 그 사출속도도 우수하여 대량생산에 적당한 생산속도를 확보할 수 있게되는 효과가 있다.In addition, PVC coated monofilament yarn having high strength is greatly reduced in concern about cutting of yarn during PVC coating process compared with conventional multifilament yarns. Therefore, it is easy to fabricate monofilament yarn of PVC coated with a small diameter, The injection speed is also excellent, so that it is possible to secure a suitable production speed for mass production.
또한, 모노필라멘트사에의하여 고광택을 유지하면서, PVC 코팅된 필라멘트사에 의해 방충망틀 상에 미끄러지지 않고 고정력이 견고하게 유지되어 설치 및 사용중 이탈이 방지되는 효과가 있다.In addition, while the high-gloss is maintained by the monofilament yarn, the PVC-coated filament yarn is not slipped on the screen frame, and the fixing force is firmly maintained.
아울러, PVC코팅으로 모노 필라멘트사가 유연성을 갖게 되므로 권취형 방충망으로 가공이 가능하게 되고, 권취과정에서도 롤에 밀착하면서 권취가 가능하게 되어 하우징의 크기가 커지는 문제점이 발생하지 않게 되는 효과가 있다.In addition, since the monofilament yarn is made flexible by the PVC coating, it can be processed into a winding-type insect-proofing net, and the winding can be performed while closely adhering to the roll in the winding process, thereby avoiding the problem of increasing the size of the housing.
도 1 및 도 2는 본 발명에 따른 PVC코팅된 모노필라멘트사를 이용한 망을 나타내는 구성도.
도 3은 본 발명에 따른 망을 방충망틀에 설치하는 상태를 나타내는 구성도.
도 4는 본 발명에 따른 망의 권취예를 나타내는 도면BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view showing a network using a PVC coated monofilament yarn according to the present invention. FIG.
3 is a block diagram showing a state in which a network according to the present invention is installed in a screen frame.
4 is a view showing an example of winding a net according to the present invention;
이하 본 발명의 실시예를 첨부한 도면을 참조하여 살펴보며, 본 발명의 실시 예에서 네트는 방충망에 적용된 것을 예로서 살펴본다.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. In an embodiment of the present invention, a net is applied to an insect screen as an example.
본 발명에 따른 PVC코팅된 모노필라멘트사를 이용한 망은 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)를 사용하여 제직된다.The net using the PVC coated monofilament yarn according to the present invention is woven using the
상기에서 모노필라멘트사(10)는 고광택 효과를 높이기 위해 경질의 합성수지사로서, 통상 PET, PP, 나일론, PE 등을 사용하고, 그 사경은 0.15~0.25mm이다.The
그리고, 상기 PVC를 코팅한 모노필라멘트사(20)는 상기 모노필라멘트사를 중심에 위치시키고 그 주변으로 PVC가 코팅되도록 압출기를 사용하여 제조되므로 모노필라멘트사 대비 유연성이 우수하여 형상변형이 용이함과 더불어 외피를 형성하는 PVC 코팅에 의해 마찰력이 향상된다.
The PVC-coated
상기한 망원단의 제직예로서, 위사 혹은 경사 중 일측을 모두 모노필라멘트사(10)를 이용하고, 타측은 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)를 혼용하여 제직하거나, 위사 혹은 경사 중 일측을 모두 PVC 코팅된 모노필라멘트사(20)로 배치하고 타측은 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)를 혼용하여 제직할 수도 있으며, 경사와 위사 모두를 PVC 코팅된 모노필라멘트사(20)로 제직할 수도 있다.In the weaving of the telephoto end,
상기에서 제단과정에서 올풀림을 방지하기 위해서는 PVC 코팅된 모노필라멘트사(20)는 위사와 경사에 각각 배치되어 서로 교차되도록 제직하는 것이 바람직하며, 이 경우 상기 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)는 10~20:1의 비율로 배치되는 것이 바람직하다. The
상기에서 PVC 코팅된 모노필라멘트사(20)의 비율이 높아지면 모노필라멘트사(10)에 의한 망(1) 전체의 광택효과가 저하되고, PVC 코팅된 모노필라멘트사(20)의 비율이 낮아지면 망(1)의 미끄럼방지기능이 저하되므로, 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)를 13:1의 비율로 배치되는 것이 바람직하다.(도 1에서는 13:1의 비율로 배치된 상태를 도시)When the ratio of the PVC coated
또한, 상기 모노필라멘트사는 검정계열로 형성되어 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 망을 형성된다. 모노필라멘트사가 검정색으로서, 상기 검정색은 빛을 흡수하기 때문에 인치당 가닥수가 많아지더라도 시야 확보가 용이하고, 이와 같이 인치당 가닥수를 많이 할 수 있으므로 개구 사이즈가 450-700㎛가 되어 개구사이즈를 550㎛미만으로 할 경우 미세날벌레(국내최소크기 550-600㎛)를 완벽하게 차단할 수 있다.
In addition, the monofilament yarns are formed in a black system and have a net density of 28-50EA / inch and an opening size of 450-700 μm. Since the monofilament yarn is black, the black color absorbs light, so that even if the number of strands per inch is increased, it is easy to ensure visibility, and since the number of strands per inch can be increased, the opening size becomes 450-700 μm, It is possible to completely block the micro-fly (domestic minimum size of 550-600 mu m).
상기한 바와 같이 제직된 원단은 텐터기에서 160~220도에서 20-60m/분의 속도로 텐터가공을 통해 열융착하는 것이 바람직하다.As described above, the fabric is preferably thermally fused at a speed of 20 to 60 m / min at 160 to 220 degrees in a tenter machine through tentering.
상기에서 온도가 설정온도보다 낮거나 처리속도가 설정속도보다 높은 경우 열융착이 이루어지지 않고, 설정온도보다 높거나 처리속도가 설정속도보다 낮을 경우 가스가 나오면서 제품불량이 발생된다.
If the temperature is lower than the set temperature or the processing speed is higher than the set speed, the thermal fusion is not performed. If the set temperature is higher than the set temperature or the processing speed is lower than the set speed, gas is generated and the product is defective.
이와 같이 제직된 네트(1)를 사용하는 경우, 도 3에 나타내는 바와 같이 상기 모노필라멘트사(10)와 PVC 코팅된 모노필라멘트사(20)로 제직된 망(10)을 방충망틀상에 끼움 고정시, PVC 코팅된 모노필라멘트사(20)가 방충망틀(F)의 끼움홈(F1) 및 가스켓(G)의 형상을 따라 유연하게 형상 변형되면서 PVC 코팅층(P)의 마찰력으로 인해 미끄럼이 방지됨에 따라 망(1)을 설치 및 사용하는 중에 이탈이 방지된다.3, when the
또한, 상기한 PVC 코팅된 모노필라멘트사(20)를 망의 권취방향으로 배치하고, 망의 권취방향에 수직방향으로 모노필라멘트사 또는 모노필라멘트사와 PVC 코팅된 모노필라멘트사를 배치할 경우, PVC 코팅된 모노필라멘트사(20)에 의하여 유연성이 우수해지므로, 도 4에 나타내는 바와 같이 권취과정에서 망이 롤러에 밀착되면서 권취될 수 있게 된다.When the
10 : 모노필라멘트사 20 : PVC 코팅된 모노필라멘트사10: Monofilament yarn 20: PVC coated monofilament yarn
Claims (4)
상기 모노필라멘트사와 PVC 코팅된 모노필라멘트사는 경사와 위사 각각 10~20:1의 비율로 배치되는 것을 특징으로 하는 PVC코팅된 모노필라멘트사를 이용한 망 제조방법.It is composed of monofilament of 0.15 ~ 0.25mm in diameter and monofilament of PVC coated monofilament, weft of monofilament of 0.15 ~ 0.25mm in diameter and monofilament of PVC coated monofilament, weaving net with opening size of 450-700㎛ Coated monofilament yarns were wefted so as to intersect with each other at an arbitrary interval as warp and weft, heat-sealed at a rate of 20 to 60 m / min at 160 to 220 degrees,
Wherein the monofilament yarns and the PVC coated monofilament yarns are disposed at a ratio of 10 to 20: 1, respectively, of warp and weft.