KR101508926B1 - The packing materials with the function of dehumidification - Google Patents

The packing materials with the function of dehumidification Download PDF

Info

Publication number
KR101508926B1
KR101508926B1 KR20130151082A KR20130151082A KR101508926B1 KR 101508926 B1 KR101508926 B1 KR 101508926B1 KR 20130151082 A KR20130151082 A KR 20130151082A KR 20130151082 A KR20130151082 A KR 20130151082A KR 101508926 B1 KR101508926 B1 KR 101508926B1
Authority
KR
South Korea
Prior art keywords
layer
dehumidifying
packaging material
function
zeolite
Prior art date
Application number
KR20130151082A
Other languages
Korean (ko)
Inventor
김준열
Original Assignee
김준열
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김준열 filed Critical 김준열
Priority to KR20130151082A priority Critical patent/KR101508926B1/en
Application granted granted Critical
Publication of KR101508926B1 publication Critical patent/KR101508926B1/en

Abstract

The present invention relates to a packaging material having a dehumidification function to enable the packaging material to have a moisture absorption function and to enable the packaging material to be harmless to a human body and to reduce the costs. Therefore, the present invention includes: a surface printing layer (11) which is able to be printed and composed of a polyethylene terephthalate; a blocking layer (12) attached to adhere with the surface printing layer (11) and composed of an aluminum thin film blocking inner and outer portions; and a dehumidification sealing layer (13, 130) attached to adhere with the blocking layer (12) and performing moisture absorption function.

Description

제습 기능을 갖는 포장재{The packing materials with the function of dehumidification}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a packaging material having a dehumidifying function,

본 발명은 포장재에 관한 것으로서, 더욱 상세하게는 포장재 자체가 수분 흡수 기능을 갖도록 개선된 제습 기능을 갖는 포장재에 관한 것이다.
The present invention relates to a packaging material, and more particularly, to a packaging material having an improved dehumidifying function so that the packaging material itself has a water-absorbing function.

일반적으로 김과 같은 것을 포장하는 식품 포장지 내부에는 김의 식감을 유지하기 위하여 포장지 내부에 실리카겔과 같은 별도의 수분흡수제를 투입하여 포장지 내부에 있는 수분이 제거되도록 하고 있는 것이 이미 널리 알려진 사실이다.In general, it is well known that in order to maintain the texture of the kimchi in a food wrapping paper such as kimchi, a separate water absorbent such as silica gel is put into the inside of the wrapping paper to remove moisture inside the wrapping paper.

그러나 상기와 같이 실리카겔과 같은 별도의 수분흡수제가 포장지 내부에 별도로 들어 있게 되면 포장지 개봉시에 실리카겔의 포장이 파손되는 경우가 있어서 식품 오염이 되는 경우가 발생 될 수 있는 단점이 있을 뿐만 아니라 심한 경우에는 일부 소비자들은 실리카겔을 먹는 안전사고가 발생 됨으로써 항상 불안한 상태로 유통되는 문제점을 수반하고 있다.However, if a separate water absorbent such as silica gel is separately contained in the wrapping paper as described above, the packaging of the silica gel may be broken at the time of opening the wrapping paper, which may cause food contamination. In addition, Consumers are constantly in a state of insecurity because of safety accidents that eat silica gel.

또한, 식품 포장공정에서도 실리카겔을 투입하는 공정이 추가됨으로써 식품 제조원가를 상승시키는 문제점을 수반하고 있다.In addition, in the food packaging process, a process of adding silica gel is added, which raises a problem of raising the cost of food manufacturing.

따라서, 선행기술문헌에 기재된 선행기술에서는 인체에 극히 해롭지 않은 숯의 다공성을 이용하여 항균력, 습도조절능력, 곰팡이방지기능을 갖도록 한 코팅지가 개시되고 있으나 숯의 물질특성은 많으나 수분 흡수 효율이 그다지 높지 않아서 수분을 확실히 제거할 수 없는 한계가 있기 때문에 김과 같이 수분에 민감한 식품 포장재로서는 바람직하지 못한 문제점이 있다.Accordingly, in the prior art described in the prior art documents, a coated paper having antimicrobial activity, humidity control ability, and antifungal property using charcoal porosity which is not harmful to the human body is disclosed. However, charcoal has many material properties, but its water absorption efficiency is very high There is a problem that it is not preferable as a food packaging material susceptible to moisture such as Kim.

그리고 숯을 나노 입자로 가공하여 코팅하여야 하므로 원가상승이 초래되어 제품가격을 상승시키는 문제점을 수반하고 있다.
And since the charcoal must be coated and processed into nanoparticles, the cost is increased and the product cost is increased.

KR 20-0232882 Y1 2001.09.25KR 20-0232882 Y1 2001.09.25 KR 10-1194897 B1 2012.10.25KR 10-1194897 B1 2012.10.25

본 발명은 포장재 자체가 수분 흡수 기능을 갖도록 개선된 제습 기능을 갖는 포장재를 제공하려는데 그 목적이 있다.An object of the present invention is to provide a packaging material having an improved dehumidification function so that the packaging material itself has a water absorption function.

본 발명의 다른 목적은, 수분 흡수기능을 갖는 포장재가 인체에 해롭지 않도록 구현시킨 제습 기능을 갖는 포장재를 제공하려는데 있다.Another object of the present invention is to provide a packaging material having a dehumidifying function which is implemented so that a packaging material having a moisture absorption function is not harmful to the human body.

본 발명의 또 다른 목적은, 포장재 자체가 수분 흡수 기능을 갖도록 하면서도 원가절감이 도모될 수 있도록 하려는데 있다.
It is another object of the present invention to provide a packaging material that can have a water-absorbing function while reducing cost.

본 발명은, 인쇄가 되고 폴리에틸렌 테레프탈레이트로 이루어지는 표면인쇄층)과, 상기 표면인쇄층과 접착되게 부착되고 내외부를 차단하는 기능을 하는 알루미늄박막으로 이루어지는 차단층을 포함하고, 상기 차단층에 접착되게 부착되고 수분 흡착 기능을 하는 제습실링층을 포함하여 이루어지는 것을 그 특징으로 한다.The present invention provides a surface printing layer comprising a surface printed layer made of polyethylene terephthalate which is printed, and a barrier layer made of an aluminum thin film adhered to the surface print layer and having a function of blocking the inside and the outside, And a dehumidifying sealing layer adhered and having a water adsorption function.

상기 제습실링층은, 차단층에 부착되고 폴리프로필렌이나 폴리에틸렌 중 어느 하나로 이루어지는 외면접착층)과, 수분 흡착 기능을 하는 제습층과, 상기 제습층 외면을 덮도록 접착되어 은폐되게 하고 폴리프로필렌이나 폴리에틸렌 중 어느 하나로 이루어지는 내면접착층을 갖도록 이루어지는 것을 다른 특징으로 한다.The dehumidifying sealing layer is adhered to the blocking layer and is an outer surface adhesive layer made of either polypropylene or polyethylene.), A dehumidifying layer having a moisture adsorption function, and a dehydrating layer which is adhered to cover the outer surface of the dehumidifying layer, And an inner surface adhesive layer made of any one of them.

상기 제습실링층 및 제습층은 폴리프로필렌 80-95wt%나 폴리에틸렌 80-95wt% 중에 어느 하나와 제올라이트 5-20wt%의 성분으로 이루어지도록 한 것을 또 다른 특징으로 한다.
The dehumidifying sealing layer and the dehumidifying layer are characterized in that the dehumidifying sealing layer and the dehumidifying layer are composed of 80-95 wt% of polypropylene or 80-95 wt% of polyethylene and 5-20 wt% of zeolite.

본 발명은 월등한 수분 흡착 기능이 있는 포장재를 제공하게 되는 효과가 있을 뿐만 아니라 포장되는 식품의 식감 유지가 매우 뛰어난 효과가 있다.The present invention has an effect of providing a packaging material having a superior moisture adsorption function and also has an excellent effect of maintaining the texture of the food to be packaged.

또한, 본 발명은 포장재 자체가 제습 작용을 하므로 예전과 같이 실리카겔과 같은 수분흡착제를 별도 투입하지 않아도 되기 때문에 실리카겔 투입 공정이 없어도 되므로 원가절감이 도모되게 하는 효과가 있다.In addition, since the packaging material itself acts as a dehumidifying agent, it is not necessary to separately add a moisture adsorbent such as silica gel as in the prior art, thereby eliminating the need for a silica gel injecting step, thereby reducing cost.

그리고 본 발명은 포장재 자체가 제습 기능을 갖게 되므로 부주의에 의해 실리카겔과 같은 수분흡수제를 섭취하게 되는 것을 미연에 방지하게 되므로 안전사고 발생의 위험이 완전히 배제되게 하는 안전한 포장지를 제공하게 되는 효과가 있는 것이다.
In addition, since the packaging material itself has a dehumidifying function, the present invention prevents the risk of accidental ingestion of the water absorbent such as silica gel due to carelessness, thereby providing a safe wrapping paper that completely eliminates the risk of a safety accident .

도 1은 본 발명에 의한 일실시예의 포장재 단면 구성도,
도 2의 (a),(b)는 본 발명에 따른 다른 실시예 포장재의 분리단면도 및 결합단면 구성도,
도 3의 (a),(b)는 본 발명의 일실시예 및 다른 실시예의 포장재에 의해 제조되는 포장지의 단면 구성도이다.1 is a cross-sectional view of a packaging material according to an embodiment of the present invention,
2 (a) and 2 (b) are a sectional view and a cross-sectional view of a packaging material according to another embodiment of the present invention,
3 (a) and 3 (b) are cross-sectional structural views of a packaging paper produced by the packaging material of one embodiment and another embodiment of the present invention.

본 발명을 첨부된 바람직한 실시도면에 의거하여 보다 상세히 설명하면 다음과 같다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in more detail with reference to the accompanying drawings.

도 1은 본 발명의 일실시예를 나타낸 것으로서, 본 발명의 일실시예의 포장재(10)는 상면부터 표면인쇄층(11)과 차단층(12)과 제습실링층(13)으로 이루어지게 된다.FIG. 1 shows an embodiment of the present invention. The packaging material 10 of the embodiment of the present invention comprises a surface printing layer 11, a barrier layer 12, and a dehumidifying sealing layer 13 from an upper surface.

상기 표면인쇄층(11)은 외피지 역할을 하는 것으로서 인쇄가 되는 층이며, 폴리에틸렌 테레프탈레이트(polyethylene terephthalate)에 의해 이루어지게 된다.The surface print layer 11 serves as an outer film and is a layer to be printed, and is made of polyethylene terephthalate.

차단층(12)은, 포장지 내부와 외부가 차단되게 하여 가스나 수분을 차단하는 층으로서, 알루미늄박막에 의해 이루어지게 된다.The barrier layer 12 is made of an aluminum thin film as a layer that blocks gas and moisture by blocking the inside and the outside of the wrapping paper.

그리고 제습실링층(13)은, 포장지를 만들 때 테두리부분이나 입구 부분이 융융되어 융착될 수 있도록 하는 층이다.The dehumidifying sealing layer 13 is a layer which allows the rim and the inlet portion to be melted and fused when making the wrapping paper.

상기 제습실링층(13)은 폴리프로필렌(polypropylene)이나 폴리에틸렌(polyethylene) 중에 어느 하나의 성분에 제올라이트(zeolite)가 혼합되어 구성된다.The dehumidifying sealing layer 13 is formed by mixing zeolite with any one of polypropylene and polyethylene.

따라서, 제습실링층(13)은 필름 형태로 제조되어 차단층(12)에 부착되는 것으로서, 폴리프로필렌이나 폴리에틸렌 중 어느 하나의 마스터 배치(mastr batch)에 제올라이트 마스터 배치가 혼합되어 용융된 상태에서 필름 형태로 제조된 다음에 차단층(12)에 부착되게 하는 것이다. 상기 표면인쇄층(11)과 차단층(12)과 제습실링층(13)이 부착되게 하는 것은 접착 방법이 주로 이용되고 있으며 이미 알려진 것이므로 상세한 설명은 생략하는 것으로 한다.Therefore, the dehumidifying sealing layer 13 is formed in the form of a film and adhered to the barrier layer 12, in which a zeolite master batch is mixed with a master batch of either polypropylene or polyethylene, And then to be attached to the barrier layer 12. The adhesion of the surface printing layer 11, the barrier layer 12, and the dehumidifying sealing layer 13 is mainly performed using a bonding method, and a detailed description thereof will be omitted.

따라서, 상기 폴리프로필렌이나 폴리에틸렌은 포장지를 만들 때 열을 가하면 융융되어 포장지의 테두리부분이나 입구 부분이 상호 융착되게 하는 역할을 하게 되고, 제올라이트는 물질 특성상 특유의 다공성 형태를 가지므로 향(냄새)이나 수분을 흡착하는 기능을 수행하게 된다.Therefore, the polypropylene or polyethylene is melted when heat is applied to the wrapping paper so that the rim portion or the inlet portion of the wrapping paper is fused to each other. Since the zeolite has a porous form unique to the material, And performs a function of adsorbing moisture.

따라서, 본 발명의 포장재(10)를 이용하여 도 3의 (a)와 같이 포장지 상태로 만들어지게 되면 제습실링층(13)이 포장지 내면에 위치하게 되어 밀봉된 상태의 포장지 내부에 존재하는 냄새나 습기를 제습실링층(13)에서 흡수하여 제거하게 되는 것이다.3 (a) using the packaging material 10 of the present invention, the dehumidifying sealing layer 13 is located on the inner surface of the wrapping paper so that the odor and the odor existing in the sealed packaging paper Moisture is absorbed and removed by the dehumidifying sealing layer 13.

그리고 상기한 포장재(10)는 제습실링층(13)이 밀봉된 상태의 포장지 내부에 포장된 제품과 접촉되는 상태가 되므로 가령 제습이 필요한 전자제품이나 인체와 상관이 없는 제품을 포장하는 포장재(10)로 사용하는 것이 바람직하다.Since the dehumidifying sealing layer 13 of the packaging material 10 is brought into a state of being in contact with the packaged product in the sealed packaging material, the packaging material 10 for packaging the electronic product or the product which is not related to the human body ) Is preferably used.

그러나 경우에 따라서는 도면으로 도시하지는 않았으나 상기 제습실링층(13) 외면에 폴리프로필렌이나 폴리에틸렌 중에 어느 하나로 이루어지는 실링층이 더 부착되게 구성되도록 할 수도 있다.However, although not shown in the drawings, a sealing layer made of any one of polypropylene and polyethylene may be further attached to the outer surface of the dehumidifying sealing layer 13.

도 2는 본 발명의 다른 실시예를 나타낸 것으로서, 상기 실시예의 포장재(10')는 표면인쇄층(11)과 차단층(12)과 제습실링층(130)으로 이루어지게 된다.FIG. 2 shows another embodiment of the present invention. The packaging material 10 'of the embodiment includes the surface printing layer 11, the barrier layer 12, and the dehumidifying sealing layer 130.

상기 표면인쇄층(11)과 차단층(12)은 이미 앞서 설명된 일실시예의 표면인쇄층(11)과 차단층(12)과 동일한 것이므로 상세한 설명은 생략하는 것으로 한다.The surface print layer 11 and the barrier layer 12 are the same as those of the surface print layer 11 and the barrier layer 12 of the embodiment described above and will not be described in detail.

따라서, 본 발명은 상기 표면인쇄층(11)과 차단층(12)은 필름형태로 제조되어 상호 접착되게 부착되는 것이고, 아울러서 제습실링층(130)도 별도의 필름 형태로 제조되어 차단층(12)에 접착되게 부착되는 것이다.Therefore, in the present invention, the surface printing layer 11 and the barrier layer 12 are formed in the form of a film and adhered to each other, and the dehumidifying sealing layer 130 is also formed in a separate film form, As shown in Fig.

도 2의 (a)를 참조하면, 상기 제습실링층(130)은 폴리프로필렌이나 폴리에틸렌 중에 어느 하나로 이루어지는 외면접착층(131)이 있고, 상기 외면접착층(131)에는 폴리프로필렌이나 폴리에틸렌 중에 어느 하나의 성분에 제올라이트(zeolite)가 혼합되어 구성된 제습층(132)이 부착되고, 상기 제습층(132)에는 폴리프로필렌이나 폴리에틸렌 중에 어느 하나로 이루어지는 내면접착층(133)이 층착 되도록 이루어지게 된다.2 (a), the dehumidifying sealing layer 130 has an outer surface bonding layer 131 made of either polypropylene or polyethylene, and the outer surface bonding layer 131 is formed of one of polypropylene and polyethylene And a dehumidifying layer 132 composed of a mixture of zeolite and deionized water is attached to the dehumidifying layer 132. An inner adhesive layer 133 made of polypropylene or polyethylene is stacked on the dehumidifying layer 132. [

상기 외면접착층(131)과 제습층(132) 및 내면접착층(133)에 있어서도 일실시예와 같이 각각 필름 형태로 제조되어 접착제로 부착되어 하나의 제습실링층(130)을 구성하게 되는 것이고, 상기와 같이 필름 형태로 제조된 제습실링층(130)을 표면인쇄층(11)과 접착된 차단층(12)에 접착시켜 부착되게 하는 것으로서, 상기와 같이 각각의 필름을 접착시켜 부착되게 하는 것은 이미 알려진 기술이므로 상세한 설명은 생략하는 것으로 한다.The outer surface adhesive layer 131, the dehumidifying layer 132, and the inner surface adhesive layer 133 may be formed in the form of a film and adhered with an adhesive to form a single dehumidifying sealing layer 130, The dehumidifying sealing layer 130 made in the form of a film is adhered to the surface printing layer 11 and the adhesive layer 12 adhered to the surface printing layer 11, The detailed description thereof will be omitted.

따라서, 상기 제습층(132)은 필름 형태로 제조되어 외면접착층(131)과 내면접착층(133) 사이에 부착되는 것으로서, 폴리프로필렌이나 폴리에틸렌 중 어느 하나의 마스터 배치(mastr batch)에 제올라이트 마스터 배치가 혼합되어 용융된 상태에서 필름 형태로 제조된 다음에 외면접착층(131)과 내면접착층(133) 사이에 접착되게 부착되는 것이다.Therefore, the dehumidifying layer 132 is formed in the form of a film and attached between the outer surface adhesive layer 131 and the inner surface adhesive layer 133. In the mastr batch of any one of polypropylene and polyethylene, a zeolite master batch And is adhered and adhered between the outer surface adhesive layer 131 and the inner surface adhesive layer 133. [

따라서, 상기 내면접착층(133)은 포장지를 만들 때 열을 가하면 융융되어 포장지의 테두리부분이나 입구 부분이 상호 융착되게 하는 역할을 하게 되고, 제습층(132)에 함유하고 있는 제올라이트는 물질 특성상 특유의 다공성 형태를 가지므로 향이나 수분을 흡착하는 기능을 수행하는 역할을 하게 된다.Accordingly, the inner surface adhesive layer 133 functions to melt the outer surface of the wrapping paper and to fuse the outer surface of the wrapping paper when the wrapping paper is heated. The zeolite contained in the dehumidifying layer 132 has a characteristic Since it has a porous form, it plays a role of adsorbing fragrance and moisture.

그러므로 본 발명의 포장재(10')를 이용하여 도 3의 (b)와 같이 포장지 상태로 만들어지게 되면 제습층(132)이 포장지 내면 쪽에 위치하게 되어 밀봉된 상태의 포장지 내부에 존재하는 냄새나 습기를 흡수하여 제거하게 되는 것이다.3 (b), the dehumidifying layer 132 is positioned on the inner surface of the wrapping paper, and the odor and moisture present in the sealed wrapping paper As shown in FIG.

그리고 상기한 포장재(10')는 제습층(132) 외면에 내면접착층(133)이 있기 때문에 밀봉된 상태의 포장지 내부에 포장된 제품이 제습층(132)에 직접 접촉되지 않게 되는 상태가 되므로 가령 김과 같은 식품이나 의약품 등과 같이 사람이 섭취하는 제품을 포장하는 포장재(10')로 사용하는 것이 바람직하다.
Since the packaging material 10 'has an inner surface adhesive layer 133 on the outer surface of the dehumidifying layer 132, the packaged product in the sealed package does not directly contact the dehumidifying layer 132, It is preferable to use it as a packaging material 10 'for wrapping a product consumed by a person such as a food or a medicament such as roast.

[[ 실시예Example 1] One]

따라서, 본 발명에 실시되는 제올라이트를 마스터배치 상태(분말상태)에서 수분이 흡착되는 실험을 하였으며, 아래의 [표1]은 그 실험표를 나타낸 것으로서, 여기서 마스터배치는 M/B라는 약호를 사용하여 표기하였다.Thus, experiments were conducted in which water was adsorbed in the master batch state (powder state) of the zeolite according to the present invention, and the following Table 1 shows the experiment table, wherein the master batch uses the abbreviation M / B Respectively.

그리고 [표1]를 참조하면 본 실험에서 제올라이트 함량(농도)은 50wt% 및 30wt%의 마스터배치가 각각 함유된 상태에서 포장지(용기)의 용적별로 실험하였다.In Table 1, zeolite content (concentration) was tested for each volume of wrapping paper (container) with 50wt% and 30wt% masterbatch, respectively.

Figure 112013111750339-pat00001
Figure 112013111750339-pat00001

상기 [표1]에서 대각선으로 나타낸 실험라인 중에 윗쪽 실험라인(청색라인)은 제올라이트 함량(농도) 50wt% 상태가 실험되어 나타낸 실험라인이고, 아래쪽 실험라인(적라인)은 제올라이트 함량(농도) 30wt% 상태가 실험되어 나타낸 실험라인을 나타낸 것으로서, 제올라이트 농도 및 포장지(용기)의 용적에 따라 제올라이트의 필요로되는 양을 알 수 있었고, 이를 토대로 하여 포장재(10,10')에 적용시킬 바람직한 제올라이트의 함량을 설정할 수 있었다.
The upper experimental line (blue line) in the diagonal line in Table 1 is the experimental line in which the zeolite content (concentration) of 50 wt% was experimentally tested and the lower experimental line (enemy line) was the zeolite content (concentration) of 30 wt % State. The amount of zeolite needed was determined according to the zeolite concentration and the volume of the wrapping paper (container). Based on this, it was found that the preferable zeolite to be applied to the packaging material 10, 10 ' The content could be set.

[[ 실시예Example 2] 2]

그리고 기존에 수분흡착제로 쓰이던 실리카겔과 본 발명에 실시되는 제올라이트의 수분 흡착 능력 실험을 하였으며, 아래의 [표2]는 그 실험결과표를 나타낸 것이다. 그리고 실험 대상은 김을 대상을 하여 습도별로 실험하였다.The moisture adsorption capacity of the silica gel used as a moisture adsorbent and the zeolite used in the present invention was tested. The following Table 2 shows the results of the experiment. Experiments were carried out on the Kimchi and humidity.

Figure 112013111750339-pat00002
Figure 112013111750339-pat00002

따라서, 상기 [표2]에 의하면 제올라이트(적색라인참조)가 실리카겔(청색라인참조)보다는 수분 흡착량이 상대적으로 훨씬 우수한 것으로 나타났으며, 그로 인해 제올라이트 성분을 포장재(10,10')에 함유되게 하여도 기존의 실리카겔보다는 매우 우수한 수분흡착능력을 발휘할 수 있다는 것을 확인할 수 있었다.
Therefore, according to the above Table 2, it was found that the zeolite (see the red line) had a much higher moisture adsorption amount than the silica gel (see the blue line), and thus the zeolite component was contained in the packaging materials 10 and 10 ' It is possible to exert a water adsorption ability which is superior to that of the conventional silica gel.

[실시예 3][Example 3]

본 발명이 포장재(10')를 다수 제조하여 이를 가지고 포장지를 만들어서 김을 맛을 비교하는 실험을 하였다.The present invention was conducted to prepare a plurality of wrapping materials 10 'and to prepare a wrapping paper to compare the taste of the wrapping material 10'.

그리고 상기 포장재(10')에서 제습층(132)은 폴리에틸렌과 제올라이트가 혼합된 것을 제조하여 실험하였고, 이때 제올라이트 마스터 배치 함량이 2wt%, 5wt%, 10wt%가 혼합된 것을 각각 제조하여 실험하였다.The dehumidifying layer 132 of the packaging material 10 'was prepared by mixing a mixture of polyethylene and zeolite. At this time, a mixture of 2 wt%, 5 wt% and 10 wt% of zeolite master batch was prepared and tested.

또한, 통상적으로 포장된 김의 유통기한은 제조일로부터 6개월이므로, 1개월부터 6개월까지 각각 구분하여 김 맛에 대한 관능 실험을 하였다.In addition, since the shelf life of packaged steaming kim was usually 6 months from the date of manufacture, sensory evaluation of kimchi taste was performed for 1 month to 6 months.

아래의 [표3]은 상기와 같이 실험한 김 맛에 대한 관능 실험표를 나타낸 것으로서, [표3]에서 제올라이트 마스터 배치 표시는 M/B라는 약호를 사용하여 표기하였다.[Table 3] shows the sensory test table for the taste of kimchi as described above. In Table 3, the zeolite master batch display is indicated by the abbreviation M / B.

보존기간Retention period M/B 함량 M / B content 1개월 1 month 2개월  2 months 3개월 3 months 4개월 4 months 6개월 6 months M/B 2wt% M / B 2 wt% ◎   ◎ ◎   ◎ ○  ○ △   △ X  X M/B 5wt% M / B 5 wt% ◎   ◎ ◎   ◎ ◎  ◎ ○   ○ ○  ○ M/B 10wt% M / B 10wt% ◎   ◎ ◎   ◎ ◎  ◎ ◎   ◎ ○  ○

◎:매우 좋음, ○:좋음, △:보통, X:나쁨       ?: Very good,?: Good,?: Fair, X: poor

상기 김에 대한 보관기간별로 관능 테스트를 한 결과 제올라이트 마스터 배치 함량이 높을수록 수분 흡착력이 좋아져서 김의 바삭함을 오래 지속할 수 있는 것으로 나타났다.As a result of the sensory test for the storage period of the above Kim, the higher the content of the zeolite master batch, the better the moisture absorption ability was, and the crispness of Kim could be maintained for a long time.

그리고 제올라이트 함량은 5wt% 이상으로 함유되게 하면 6개월까지 양호한 제습능력을 갖는 것으로 확인되었다.It was confirmed that when the content of zeolite is 5 wt% or more, it has a good dehumidifying ability up to 6 months.

따라서, 일실시예의 제습실링층(13) 및 다른 실시예의 제습층(132)은 폴리프로필렌 80-95wt%나 폴리에틸렌 80-95wt% 중에 어느 하나와 제올라이트 5-20wt%의 비율이 되도록 하여 이루어지게 하는 것이 바람직한 것으로 판단된다.Accordingly, the dehumidifying sealing layer 13 of one embodiment and the dehumidifying layer 132 of another embodiment are made to have a ratio of either 80-95 wt% of polypropylene or 80-95 wt% of polypropylene and 5-20 wt% of zeolite Is preferable.

그리고 포장 김에 들어가는 기름이 장시간 경과 되면 산화되어 좋지 않은 냄새가 발생 되는데, 본 발명은 제올라이트의 특유의 다공성 성질로 향(냄새) 흡착력까지 있어서 기름이 산화되어 나게 되는 좋지 않은 기름냄새까지도 흡착하는 것으로 나타났다.In addition, when the oil entering the pavement is oxidized for a long time, it is oxidized and a bad smell is generated. The present invention shows that even a poor smell of oil, which is oxidized by oil even up to incense (odor) adsorption ability due to peculiar porous property of zeolite, .

한편, 실시예 3에서 제습층(132) 외면에 내면접착층(131')이 있는 포장재(10')만 제조하여 실험한 것은 상기 내면접착층(131')이 없는 일실시예의 포장재(10)도 상기 내면접착층(131')이 있는 포장재(10') 보다는 더욱 우수하거나 또는 동일한 실험 결과가 나올 것이란 것 때문이다.On the other hand, only the packaging material 10 'having the inner surface bonding layer 131' on the outer surface of the dehumidifying layer 132 in Example 3 was tested and the packaging material 10 of one embodiment without the inner surface bonding layer 131 ' Is superior to the packaging material 10 'with the inner adhesive layer 131' or the same experimental result will be obtained.

따라서, 본 발명의 포장재(10,10')는 월등한 수분 흡착 기능이 있는 것으로 실험되었을 뿐만 아니라 수분 흡착에 의한 김의 식감 유지가 도모되는 것이 실험결과 입증되었다.Therefore, it has been experimentally proven that the packaging materials 10 and 10 'of the present invention not only have been tested to have superior water adsorption function, but also maintain the texture of the Kim by moisture adsorption.

그러므로 본 발명은 제습 기능을 하는 포장재(10,10')를 제공하게 되는 것일 뿐만 아니라 포장재(10,10') 자체가 제습 기능을 하므로 예전과 같이 실리카겔과 같은 수분흡착제를 별도 투입하지 않아도 되기 때문에 실리카겔 투입 공정이 없어지게 됨으로써 원가절감이 도모되는 것이다.Therefore, the present invention not only provides the packaging material 10, 10 'having a dehumidifying function but also the moisture absorbent such as silica gel does not need to be separately supplied as in the prior art because the packaging material 10, 10' The silica gel injecting process is eliminated, thereby reducing the cost.

또한, 본 발명은 포장재(10,10') 자체가 제습 기능을 갖게 되므로 식품 포장시에 별도의 수분흡수제를 투입하지 않아도 되므로 예전과 같이 부주의에 의해 실리카겔과 같은 수분흡수제를 섭취하지 않게 되므로 안전사고 발생의 위험이 전혀 발생 되지 않게 되는 것이다.In addition, since the packaging material (10, 10 ') itself has a dehumidifying function, it is not necessary to add a separate water absorbent at the time of food packaging, so that the water absorbent such as silica gel is not taken carelessly as in the past, There is no risk of occurrence.

한편, 본 발명은 도면으로 도시되지는 않았지만 일실시예의 포장재(10)에 있어서 제습실링층(13) 외면에 또다른 접착층을 구비하도록 할 수도 있고, 다른 실시예의 포장재(10')에 있어서는 외면접착층(131)을 제거하고 제습층(132)이 차단층(12)에 직접적으로 접착되게 부착시켜 구성되도록 할 수도 있는 것이다.Although the present invention is not shown in the drawings, it is also possible to provide another adhesive layer on the outer surface of the dehumidifying sealing layer 13 in the packaging material 10 of one embodiment. In the packaging material 10 'of another embodiment, The dehumidifying layer 132 may be adhered to the barrier layer 12 so as to be directly adhered thereto.

따라서, 본 발명은 도면으로 도시되고 설명된 실시예에 반드시 국한되는 것은 아니고 본 발명 기술분야에서 통상의 지식을 가진자에 의해서 여러 가지 형태로 변형 실시될 수도 있는 것이므로 청구범위를 크게 벗어나지 않는 한 폭넓게 보호되어야 하는 것은 자명한 것이다.
Therefore, the present invention is not limited to the embodiments shown in the drawings, but may be modified in various ways by those skilled in the art. Accordingly, It is self-evident to be protected.

10,10:포장재 11:표면인쇄층
12:차단층 13,130:제습실링층
131:외면접착층 131':내면접착층
132:제습층10, 10: packing material 11: surface printing layer
12: barrier layer 13, 130: dehumidifying sealing layer
131: outer adhesive layer 131 ': inner adhesive layer
132: dehumidifying layer

Claims (3)

삭제delete 인쇄가 되고 폴리에틸렌 테레프탈레이트로 이루어지는 표면인쇄층(11)과, 상기 표면인쇄층(11)과 접착되게 부착되고 내외부를 차단하는 기능을 하는 알루미늄박막으로 이루어지는 차단층(12)을 갖는 것에 있어서;
상기 차단층(12)에 부착되고 폴리프로필렌으로 이루어지는 외면접착층(131)과, 수분 흡착 기능을 하는 제습층(132)과, 상기 제습층(132) 외면을 덮도록 접착되어 은폐되게 하고 폴리프로필렌으로 이루어지는 내면접착층(131')을 갖는 제습실링층(130)을 포함하여 이루어지게 하되 상기 제습층(132)이 폴리프로필렌 80-95wt%과 제올라이트 5-20wt%의 성분으로 이루어지도록 한 것을 특징으로 하는 제습 기능을 갖는 포장재.

A surface printing layer 11 made of polyethylene terephthalate to be printed and a barrier layer 12 made of an aluminum foil adhered to the surface printing layer 11 and functioning to block the inside and the outside;
An outer surface adhesive layer 131 attached to the barrier layer 12 and made of polypropylene, a dehumidifying layer 132 having a function of adsorbing water and an outer surface of the dehumidifying layer 132, Wherein the dehumidifying layer (132) comprises 80-95 wt% of polypropylene and 5-20 wt% of zeolite, wherein the dehumidifying sealing layer (130) comprises an inner adhesive layer (131 ' Packing material with dehumidification function.

삭제delete
KR20130151082A 2013-12-06 2013-12-06 The packing materials with the function of dehumidification KR101508926B1 (en)