KR101450764B1 - Composition of synthetic wood use for prevent sliding, property and preparing method thereof - Google Patents
Composition of synthetic wood use for prevent sliding, property and preparing method thereof Download PDFInfo
- Publication number
- KR101450764B1 KR101450764B1 KR1020140005564A KR20140005564A KR101450764B1 KR 101450764 B1 KR101450764 B1 KR 101450764B1 KR 1020140005564 A KR1020140005564 A KR 1020140005564A KR 20140005564 A KR20140005564 A KR 20140005564A KR 101450764 B1 KR101450764 B1 KR 101450764B1
- Authority
- KR
- South Korea
- Prior art keywords
- wood
- composition
- weight
- synthetic wood
- synthetic
- Prior art date
Abstract
Description
본 발명은, 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물 및 그의 제조방법에 관한 것으로,TECHNICAL FIELD The present invention relates to a synthetic wood composition having enhanced slip resistance and physical properties and a method for producing the same,
마루판 또는 천정판, 문짝, 문틀, 창호, 휀스(FENCE), 난간, 담장, 자전거 전용도로, 산책로와 같은 건축물의 외장재 또는 내장재로 사용되는, 목분 및 합성수지로 혼합 구성된 합성목재 조성물에 있어서;
1. A synthetic wood composition composed of wood flour and synthetic resin, which is used as an exterior material or an interior material of a building such as a flooring or ceiling plate, a door, a door frame, a window, a fence, a railing, a fence, a bicycle access road or a walkway;
본 발명 구성의 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물을 제공하여, It is an object of the present invention to provide a synthetic wood composition having enhanced anti-slip properties and physical properties,
특히, 완제품인 본 발명의 합성목재가 종래 기술의 천연목재 또는 합성목재에 비하여 내수성, 충격강도, 휨강도의 물성성능이 강화되고; Particularly, the synthetic wood of the present invention, which is an end product, has improved physical properties such as water resistance, impact strength and flexural strength as compared with natural wood or synthetic wood of the prior art;
미끄럼 방지 효과 및 난연 성능이 개선되고, 폐자원의 재활용이 가능하여 원가절감이 되는 동시에, 합성목재 표면층의 표면 질감이 향상되고; The slip prevention effect and the flame retardant performance are improved, the waste resources can be recycled and the cost is reduced, the surface texture of the synthetic wood surface layer is improved;
제조가 용이하여, 작업성이 향상된; 구성의, "미끄럼 방지 및 물성성능이 강화된 합성목재 조성물 및 그의 제조방법"에 관한 발명이다.Easy to manufacture and improved workability; , "Synthetic wood composition reinforced with anti-slip properties and physical properties, and method of producing the same ".
이하, 본 발명의 배경이 되는 기술에 대하여 설명키로 하며, 본 발명의 배경이 되는 기술은 본 출원인이 선출원한 특허 출원 제 10-2012-0083184호(2012. 07. 30. 출원) "미끄럼 방지 및 시인성이 우수한 합성목재 및 그의 제조방법"에 상세히 기재되어 있으며, The background art of the present invention is described in detail in Korean Patent Application No. 10-2012-0083184 filed by the present applicant (filed on Jul. 30, 2012) "Anti-slip and anti- Synthetic wood excellent in visibility and a process for producing the same "
본 특허와 관련된 기재분을 인용하여 발명의 배경이 되는 기술을 기재 및 종래기술의 추가 문제점을 기재하였다.
The description related to the present patent is cited to describe the technology as the background of the invention and further problems of the prior art are described.
종래기술의 마루판 또는 천정판, 문짝, 문틀, 창호, 휀스(FENCE), 난간, 담장과 같은 건축물의 내,외장재로 사용되는 합성목재는;
Synthetic timbers used as interior and exterior materials of buildings such as floorboards, ceiling panels, doors, door frames, window frames, fences, railings, fences of the prior art;
건축물의 내, 외장재로 사용시에, 열가소성 수지가 다량 함유된 합성목재의 재질에 의한 표면층이 미끄러워 보행자가 보행시에 미끄러짐으로 인한 안전사고가 발생되고 있으며;
When used as an interior or exterior material of a building, a surface layer formed of a synthetic wood material containing a large amount of thermoplastic resin is slippery, causing a safety accident due to slipping of the pedestrian during walking;
자전거 전용도로 또는 산책로와 같은 건축물의 외장재로 합성목재가 사용시에, 야간에 시인성 향상을 목적으로 사용자의 안전을 위하여 상기 합성목재의 외부에 형광물질이 투입된 조성의 축광도료를 도포 사용하고 있으나, A phosphorescent paint having a composition in which a phosphor is added to the outside of the synthetic wood is applied for the purpose of improving the visibility at night when synthetic wood is used as the exterior material of a building such as a bicycle exclusive road or a walkway,
이 또한, 축광도료의 고유성분에 의한 축광도료가 도포된 도포층이 매우 미끄러워, 자전거 전용도로 또는 산책로에 사용시에 자전거의 제동거리가 길어짐으로 인한 제동력의 저하 및, 보행자가 보행시에 미끄러짐으로 인한 자전거 또는 보행자의 안전사고가 빈번히 발생되고 있으며, This is also because the applied layer coated with the phosphorescent paint by the intrinsic component of the phosphorescent paint is very slippery and the braking force caused by the increase in the braking distance of the bicycle when the bicycle is used on the road for exclusive use on the bicycle or on the promenade and the slippery The safety of bicycles or pedestrians due to frequent occurrence of accidents,
축광도료가 도포된 도포층인 형광 플라스틱의 부식에 의한 내구성이 저하되어 사용이 불가한 문제점이 발생되고 있는 실정이다.
There is a problem that the durability of the fluorescent plastic coated with the phosphorescent coating is lowered due to corrosion of the fluorescent plastic.
또한, 일반적으로 마루판 또는 천정판, 문짝, 문틀, 창호, 휀스(FENCE), 난간, 담장과 같은 건축물의 내,외장재는 천연목재가 주로 사용 되고 있다.In general, natural wood is mainly used for interior and exterior materials of buildings such as floorboards, ceiling panels, doors, door frames, window frames, fences, railings and fences.
상기한 건축물의 내,외장재로 천연목재가 주로 사용되고 있는 이유로는, 원목에 대한 소비자의 선호도 증가와 천연 질감에 의한 미관이 향상되기 때문이다.The reason why natural wood is mainly used as the interior and exterior materials of the above-mentioned building is that the consumer's preference for the wood is improved and the beauty due to the natural texture is improved.
그러나, 상기한 천연목재를 사용한 건축물의 내,외장재는 목재의 벌목에 따른 산림 훼손과, 화재시에 유해물질 방출로 인한 환경파괴의 문제점이 발생되고 있으며;
However, the above-mentioned interior and exterior materials of buildings using natural wood have suffered from the problems of deforestation due to logging of wood and environmental destruction due to the release of harmful substances in case of fire;
특히, 목재의 고유 물성에 의한 내수성, 내열성, 충격강도, 휨강도, 칫수안정성, 난연성, 내후성, 항균성 물성이 저하되어 건축물의 내,외장재로 사용이 곤란한 문제점과; Particularly, there is a problem that it is difficult to use the wood as an inner or outer material of a building because of its low water resistance, heat resistance, impact strength, bending strength, dimensional stability, flame retardancy, weatherability and antimicrobial properties due to inherent physical properties of wood.
목재 재질에 의한 항균성이 저하되어 수명이 단축되며, 상기 항균성 강화를 위한 용도의 구리, 비소, 크롬 계통의 방부제(일명 CCA 방부제라고 함)가 혼입, 사용 됨으로 인한, 화재 발생시에 상기 구리, 비소, 크롬 계통의 방부제 연소에 의한 유독물질이 배출되어 인체에 유해하며, 난연기능이 없어 화재가 번지는 문제점이 발생되고 있는 실정이다.
Arsenic and chromium-based preservatives (also referred to as CCA preservatives) for the purpose of enhancing the antimicrobial properties of the copper or arsenic, Toxic substances are emitted by the chromium-based preservative burning and are harmful to the human body, and there is a problem that the fire does not have a flame-retarding function.
상기와 같은 문제점을 해결하기 위하여, 최근 천연목재와 유사한 질감 및 외관을 가진 주성분이 목분과 염화비닐수지(PVC)로 구성된 합성목재가 건축물의 내,외장재로 널리 사용되고 있어, 천연목재에 비하여 내수성과 내열성, 칫수안정성물성이 향상되며, 가격이 저렴하여 제조원가가 절감되는 효과는 있으나,
In order to solve the above problems, synthetic wood having a texture and appearance similar to those of natural wood and composed mainly of wood and PVC is widely used as an interior and exterior material of a building, Heat resistance, dimensional stability, physical properties are improved, the cost is low, and the manufacturing cost is reduced. However,
이 또한, 건축물의 내,외장재로 설치 사용시에, 특히 상기 재질 특성에 의한 강도 저하로 휨강도와 충격강도의 물성이 저하되고, 만족할만한 수준의 내수성이 유지되지 못하여 합성목재의 수명이 단축되는 문제점과;In addition, when installed and used as an inner and outer material of a building, in particular, the strength of bending strength and impact strength is lowered due to the decrease in strength due to the above material properties, and the water resistance of a satisfactory level is not maintained. ;
화재 발생시에 난연성 저하로 인한 화재가 번지는 문제점과, 염소 가스가 외부로 배출되어 인체에 유해한 문제점과;There is a problem that a fire occurs due to a decrease in flame retardancy when a fire occurs, and a problem that chlorine gas is discharged to the outside and is harmful to the human body;
천연목재에 비하여, 합성목재 표면층의 표면 질감이 현저히 저하된 문제점이 발생되고 있는 실정이다. There is a problem that the surface texture of the synthetic wood surface layer is remarkably lowered compared to natural wood.
본 발명의 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물의 제조방법에 의하여; By the method for producing a synthetic wood composition having enhanced non-slip properties and physical properties of the present invention;
종래기술 합성목재의 문제점을 해결 및,
[0002] Conventionally,
특히, 완제품인 본 발명의 합성목재가, 종래 기술의 천연목재 또는 합성목재에 비하여 내수성, 충격강도, 휨강도의 물성성능이 강화되고;
Particularly, the synthetic wood of the present invention, which is an article of finished product, has improved physical properties such as water resistance, impact strength and flexural strength as compared with natural wood or synthetic wood of the prior art;
미끄럼 방지 및 난연 성능이 개선되고, 폐자원의 재활용이 가능하여 원가절감이 되는 동시에, 합성목재 표면층의 표면 질감이 향상되며; Slip prevention and flame retardant performance are improved, waste resources can be recycled, cost is reduced, surface texture of the synthetic wood surface layer is improved;
제조가 용이하여, 작업성이 향상된 구성의; "미끄럼 방지 및 물성성능이 향상된 합성목재 조성물 및 그의 제조방법"을 제공 함을, 본 발명의 목적 및 본 발명의 해결하고저 하는 과제로 한다.Which is easy to manufacture and improved in workability; It is an object of the present invention to solve the problems of the present invention and to provide a synthetic wood composition and a method for producing the same which have improved slip resistance and physical properties.
본 발명 구성의 "미끄럼 방지 및 물성성능이 향상된 합성목재 조성물 및 그의 제조방법"에 의하여, 상기 과제를 해결코저 한다.The above problems will be solved by a "synthetic wood composition having improved slip resistance and physical properties and a method for producing the same "
본 발명의, 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물 및 그의 제조방법에 의하여; By using the synthetic wood composition of the present invention with enhanced anti-slip and physical properties and a method of manufacturing the same;
종래기술 합성목재의 문제점을 해결 및,
[0002] Conventionally,
특히, 완제품인 본 발명의 합성목재가, 종래 기술의 천연목재 또는 합성목재에 비하여 내수성, 충격강도, 휨강도의 물성성능이 강화된 효과와;Particularly, the synthetic wood of the present invention, which is an end product, has the effect of enhancing the physical properties of water resistance, impact strength and flexural strength compared with the prior art natural wood or synthetic wood;
미끄럼 방지 효과 및 난연 성능이 개선된 효과와;An anti-slip effect and an improved flame retardancy;
폐자원의 재활용이 가능하여, 원가절감 효과와;It is possible to recycle waste resources, thereby reducing costs;
합성목재 표면층의 표면 질감이 향상된 효과와;An improved surface texture of the synthetic wood surface layer;
제조가 용이하여, 작업성이 향상된 효과를 가져오는, 매우 유용한 발명이다.It is a very useful invention which brings about an effect that the manufacturing is easy and the workability is improved.
도 1은, 본 발명 합성목재 조성물로 가공된 합성목재 구성의 건축물인 펜스의 도면대용 사시 사진,
도 2는 본 발명 합성목재 조성물의 제조방법을 단계적으로 도시한 FLOW-SHEET,
도 3은 본 발명 합성목재 조성물이 합성목재로 가공되는 제조장치를 개략적으로 도시한 개략도.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view of a fence as a structure of a synthetic wood structure processed with a synthetic wood composition according to the present invention,
FIG. 2 is a flow diagram of a process for preparing a synthetic wood composition according to the present invention,
3 is a schematic view schematically showing a manufacturing apparatus in which a synthetic wood composition of the present invention is processed into synthetic wood.
본 발명은, 마루판 또는 천정판, 문짝, 문틀, 창호, 휀스(FENCE), 난간, 담장, 자전거 전용도로, 산책로와 같은 건축물의 외장재 또는 내장재로 사용되는, 목분 및 합성수지로 혼합 구성된 합성목재 조성물에 있어서;
The present invention relates to a synthetic wood composition composed of wood flour and synthetic resin, which is used as an exterior material or an interior material of a building such as a floorboard or ceiling plate, door, door frame, window, fence, railings, ;
본 발명 구성의 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물을 제공하여, It is an object of the present invention to provide a synthetic wood composition having enhanced anti-slip properties and physical properties,
특히, 완제품인 본 발명의 합성목재가 종래 기술의 천연목재 또는 합성목재에 비하여 내수성, 충격강도, 휨강도의 물성성능이 강화되고; Particularly, the synthetic wood of the present invention, which is an end product, has improved physical properties such as water resistance, impact strength and flexural strength as compared with natural wood or synthetic wood of the prior art;
미끄럼 방지 효과 및 난연 성능이 개선되고, 폐자원의 재활용이 가능하여 원가절감이 되는 동시에, 합성목재 표면층의 표면 질감이 향상되며;The slip prevention effect and the flame retardant performance are improved, the waste resources can be recycled, the cost is reduced, the surface texture of the synthetic wood surface layer is improved,
제조가 용이하여, 작업성이 향상된; 구성의, "미끄럼 방지 및 물성성능이 강화된 합성목재 조성물 및 그의 제조방법"에 관한 발명이다.
Easy to manufacture and improved workability; , "Synthetic wood composition reinforced with anti-slip properties and physical properties, and method of producing the same ".
또한, 본 발명에 언급된 물성성능은; In addition, the physical properties mentioned in the present invention are:
본 발명의 합성목재 조성물로 가공된 완제품인 합성목재의 내수성, 충격강도, 휨강도, 난연성의 물성성능에 관한 것으로, 이를 물성성능으로 한정 기재한 것으로서, 불명확한 표현이 아님을 분명히 하며,
The present invention relates to water resistance, impact strength, flexural strength, and flame retardancy properties of synthetic wood, which is an end product processed with the synthetic wood composition of the present invention, which is described in terms of physical properties and is not an unambiguous expression,
본 발명을 조성하는 각 조성물의 중량비와 입자크기는, 단순히 수치로서 한정 기재한 것이 아니며; The weight ratio and particle size of each composition constituting the present invention are not limited to simply numerical values;
완제품인 본 발명의 합성목재가 종래 기술의 천연목재 또는 합성목재에 비하여 내수성, 충격강도, 휨강도의 물성성능이 강화되고; The synthetic wood of the present invention as an article of the present invention is improved in water resistance, impact strength and bending strength as compared with the prior art natural wood or synthetic wood;
미끄럼 방지 효과 및 난연 성능이 개선되고, 폐자원의 재활용이 가능하여 원가절감이 되는 적정 구성의 각 조성물의 중량비와 입자크기로서, 본 발명의 실시예에 더욱 구체화 되어 있는바; 이는, 단순한 수치 한정에 불과 한 것이 아님을 분명히 한다.
Slip prevention effect and flame retardancy are improved, and the weight ratio and the particle size of each composition having a proper composition capable of recycling waste resources and cost reduction are further specified in the embodiment of the present invention; It is clear that this is not just a numerical limitation.
이하, 첨부된 도면에 의하여 본 발명의 "미끄럼 방지 및 물성성능이 강화된 합성목재 조성물 및 그의 제조방법"에 대하여 상세히 설명키로 한다.
BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail with reference to the accompanying drawings, in which a "synthetic wood composition reinforced with anti-slip properties and physical properties and a manufacturing method thereof" will be described in detail.
도 1은, 본 발명 합성목재 조성물로 가공된 합성목재 구성의 건축물인 펜스의 도면대용 사시 사진이고,BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a photograph of a fissure of a fence which is a structure of a synthetic wood structure processed with a synthetic wood composition of the present invention,
도 2는 본 발명 합성목재 조성물의 제조방법을 단계적으로 도시한 FLOW-SHEET이며,Fig. 2 is a FLOW-SHEET showing a stepwise process for producing a synthetic wood composition according to the present invention,
도 3은 본 발명 합성목재 조성물이 합성목재로 가공되는 제조장치를 개략적으로 도시한 개략도이다.
3 is a schematic view schematically showing a manufacturing apparatus in which a synthetic wood composition of the present invention is processed into a synthetic wood.
도 1에 도시한바와 같이; As shown in Fig. 1;
마루판, 천정판, 문짝, 문틀, 창호, 휀스(FENCE), 난간, 담장, 자전거 전용도로, 산책로와 같은 건축물의 외장재 또는 내장재로 사용되는, 본 발명의 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물("이하, 합성목재 조성물이라고 함")은;
The synthetic wood composition of the present invention, which is used as an exterior material or an interior material of a building such as a floorboard, a ceiling board, a door, a door frame, a window, a fence, a railroad, a fence, (Hereinafter referred to as a synthetic wood composition);
본 발명 1차조성물 100 중량%를 기준하여,
Based on 100 wt% of the primary composition of the present invention,
활엽수, 침엽수, 대나무 중 선택된 1종의 원목; 또는, 활엽수, 침엽수, 대나무 원목 중 선택된 1종의 원목이 집성화 되어 넓은 크기로 형성된 1종의 집성목; 또는, 파티클보드, 합판 중 선택된 1종의 목재; 또는 상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP); 이, 입자 크기 20 내지 180mesh, 수분 함량 0.1 내지 10%로 분쇄된 분말 상의, 목분 55 내지 85중량%와;
One selected from hardwood, conifer and bamboo; Or one kind of ginkgo which is formed into a wide size by agglomerating a selected one of hardwood, conifer, and bamboo wood; Or a wood selected from a particle board and a plywood; Or scrap (SCRAP), which is a waste resource generated after processing of the timber, glued wood, and wood; 55 to 85% by weight of wood powder, which is pulverized into a particle size of 20 to 180 mesh and a moisture content of 0.1 to 10%;
수지용융지수 0.5 내지 40, 굴곡 탄성율 9,500 내지 12,000, 열변형온도 90 내지 140℃의 합성수지인 폴리프로필렌(PP) 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T) 10 내지 30중량%와;
10 to 30% by weight of polypropylene (PP) or high density polyethylene (HDPE), which is a synthetic resin having a resin melt index of 0.5 to 40, a flexural modulus of 9,500 to 12,000 and a heat distortion temperature of 90 to 140 占 폚, or polyethylene teraphthalate (PET)
미끄럼방지 및 난연제인 화산석(Volcanic Rock), 화산재(Volcanic Ash), 에코트렉션(Ecotraction) 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물 5.0 내지 15중량%로; 1차 조성물이 조성된다.
From 5.0 to 15% by weight of a mixed melt obtained by mixing one or more selected from volcanic rock, volcanic ash and ecotraction which are anti-slip and flame retardant; A primary composition is formed.
또한, 상기 1차조성물 100 중량부에 대하여, Further, with respect to 100 parts by weight of the primary composition,
결합제인, 마레익 엔하이드라이드 폴리프로필렌(MALEIC ANHYDRIDE PP) 1.0 내지 8.0중량부와;1.0 to 8.0 parts by weight of a binder, meleic anhydride polypropylene (MALEIC ANHYDRIDE PP);
복합 산화방지제인, 산화방지제 0.1 내지 3.0 중량부 및, 칼슘 스테아린산염 0.1 내지 2.0 중량부와;0.1 to 3.0 parts by weight of an antioxidant, which is a complex antioxidant, and 0.1 to 2.0 parts by weight of calcium stearate;
광안정제 0.1 내지 2.0 중량부와;0.1 to 2.0 parts by weight of a light stabilizer;
자외선흡수제 0.1 내지 1.5 중량부와;0.1 to 1.5 parts by weight of an ultraviolet absorber;
활제 0.1 내지 1.5 중량부와;0.1 to 1.5 parts by weight of lubricant;
안료인 무기계 안료 0.1 내지 5.0 중량부가 첨가되어; 본 발명의 합성목재 조성물이 조성된다.
0.1 to 5.0 parts by weight of an inorganic pigment as a pigment is added; A synthetic wood composition of the present invention is formed.
상기 목분은,The wood-
활엽수, 침엽수, 대나무 중 선택된 1종의 원목; One selected from hardwood, conifer and bamboo;
또는, 상기 활엽수, 침엽수, 대나무 원목 중 선택된 1종의 원목이 집성화 되어 넓은 크기로 형성된 1종의 집성목; Or one kind of aggregate formed into a wide size by aggregating one kind of logwood selected from the above-mentioned broad-leaved trees, softwoods, and bamboo logs;
또는, 파티클보드, 합판 중 선택된 1종의 목재; Or a wood selected from a particle board and a plywood;
또는, 상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP); 중, 선택된 1종 또는 1종 이상이 혼합된 입자 크기 20 내지 180mesh, 수분 함량 0.1 내지 10%로 분쇄, 가공된 분말 상의 목분 55 내지 85중량%로 조성되어 있으며;Or scrap (SCRAP), which is a waste resource generated after processing of the wood, glued wood, and wood; 55 to 85% by weight of powdered wood powder, which has been pulverized and processed to a particle size of 20 to 180 mesh and a moisture content of 0.1 to 10% mixed with one or more selected ones;
또한, 상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP)이 재사용 가능한 조성으로, 폐자원의 재활용이 가능하여 원가절감이 되는 조성으로 구성되어 있다.
In addition, SCRAP, which is a waste material generated after the processing of the wood, glued wood and wood, is a reusable composition, and is composed of a composition that enables recycling of waste resources and cost reduction.
상기 합성수지는,The above-
수지용융지수 0.5 내지 40, 굴곡 탄성율 9,500 내지 12,000, 열변형온도 90 내지 140℃의 합성수지인 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T) 10 내지 30중량%로 조성되어,(PP) or high density polyethylene (HDPE), which is a synthetic resin having a resin melt index of 0.5 to 40, a flexural modulus of 9,500 to 12,000 and a thermal deformation temperature of 90 to 140 ° C, or 10 to 30% by weight of polyethylene teraphthalate ≪ / RTI &
상기 조성의 목분과, 상기 물성 범위내의 합성수지인 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 혼합된 구성으로, 가공제품인 합성목재로 가공시에 종래기술의 천연목재 또는 합성목재에 비하여 내수성과 충격강도, 휨강도 물성이 강화된 조성과;(PP), high density polyethylene (HDPE), or polyethylene teraphthalate (PET), which is a synthetic resin within the above-mentioned physical property range, and a synthetic resin Compared to natural wood or synthetic wood, the composition has improved water resistance, impact strength and flexural strength;
또한, 상기 목분과 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 무독성 물질로서, 화재 발생시에 염소가스가 미 배출되어 인체에 무해한, 환경친화적인 조성으로 구성되어 있다.
In addition, the above wood is composed of polypropylene (PP), high density polyethylene (HDPE) or polyethylene teraphthalate (PET) as a non-toxic substance, and environmentally friendly composition in which chlorine gas is not discharged when a fire occurs and harmless to human body .
상기 미끄럼 방지 및 난연제는,
The anti-slip and flame-
입자크기 50 내지 300mesh의, 화산석(Volcanic Rock), 화산재(Volcanic Ash), 에코트렉션(Ecotraction) 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물인 미끄럼 방지 및 난연제 5.0 내지 15중량%로 조성되어;From 5.0 to 15% by weight of a non-slip and flame retardant, which is a mixed melt of one or more selected from volcanic rock, volcanic ash and ecotraction, having a particle size of 50 to 300 meshes, ;
종래기술의 천연목재 또는 합성목재에 비하여, 본 발명 합성목재 조성물로 가공된 완제품인 합성목재의 미끄럼 현상이 방지되는 동시에, Compared with the prior art natural wood or synthetic wood, the synthetic wood as an article finished with the inventive synthetic wood composition is prevented from slipping,
산화안티몬과 같은 별개의 난연제가 미투입된 조성임에도 불구하고 난연성능이 강화되어 화재 발생시에 화재가 번지지 않는 조성으로 구성되어 있다.
Although the composition of the flame retardant such as antimony oxide is not added, the flame retardant performance is strengthened so that the composition does not spread the fire when the fire occurs.
상기 결합제는,Preferably,
상기 조성의 목분과 합성수지인 폴리프로필렌(PP) 또는 고밀도 폴리에틸렌(HDPE)이 혼합시에 결합이 용이하고 결합구조를 견고히 구성하는 용도로 사용되며, Polypropylene (PP) or high density polyethylene (HDPE), which is a synthetic resin, is used for the purpose of easy bonding and solidly bonding structure,
1차조성물 100중량부를 기준으로, 마레익 엔하이드라이드 폴리프로필렌(MALEIC ANHYDRIDE PP) 1.0 내지 8.0 중량부가 사용된다.
1.0 to 8.0 parts by weight of meleic acid hydride polypropylene (MALEIC ANHYDRIDE PP) is used based on 100 parts by weight of the primary composition.
상기 복합 산화방지제는,The composite antioxidant may be,
본 발명의 합성목재 조성물 가공 과정의 열안정화와, 완제품인 합성목재의 내후성 강화를 위한 용도로 사용되며, It is used for the purpose of thermal stabilization of the process of processing the synthetic wood composition of the present invention and for enhancing the weatherability of synthetic wood as an end product,
1차조성물 100중량부를 기준으로, 바람직하게는 포스페이트(PHOSPHATE) 계통의 산화방지제 0.1 내지 3.0 중량부 및 칼슘 스테아린산염 0.1 내지 2.0 중량부가 사용되며;
0.1 to 3.0 parts by weight of an antioxidant of the PHOSPHATE system and 0.1 to 2.0 parts by weight of calcium stearate are used, based on 100 parts by weight of the primary composition;
상기 광안정제는,The light stabilizer,
본 발명 합성목재 조성물로 가공된 완제품인 합성목재의 빛에 의한 광안정화를 위한 용도로 사용되며, It is used for light photostabilization of synthetic wood which is an article finished with the synthetic wood composition of the present invention,
1차조성물 100중량부를 기준으로, 바람직하게는 비스 2.2.6.6- 테트라 메틸- 4- 파이퍼리딜(Bis 2.2.6.6 - tetra methyl - 4 piperidil) 0.1 내지 2.0 중량부가 사용되며;
Preferably 0.1 to 2.0 parts by weight of bis 2.2.6.6-tetramethyl-4-piperidyl (Bis 2.2.6.6-tetramethyl-4-piperidyl) is used based on 100 parts by weight of the primary composition;
상기 자외선 흡수제는,The ultraviolet absorber may contain,
본 발명 합성목재 조성물로 가공된 완제품인 합성목재의 햇빛에 의한 자외선 흡수를 위한 용도로 사용되며, It is used for the absorption of ultraviolet rays by sunlight of synthetic wood which is an article finished with the synthetic wood composition of the present invention,
1차조성물 100중량부를 기준으로, 바람직하게는 벤조트리아졸(BenzotriBased on 100 parts by weight of the first composition, preferably benzotriazole
azole) 계통의 2-(2' - hydroxy -3' - tert - butyl - 5' - methyl - phenyl)-5-chlorobenzotriazol 0.1 내지 1.5 중량부가 사용되며;
0.1 to 1.5 parts by weight of 2- (2 '-hydroxy-3'-tert-butyl-5'-methyl-phenyl) -5-chlorobenzotriazole is used as the azole-
상기 활제는, The lubricant,
1차조성물 100중량부를 기준으로, 바람직하게는 폴리에틸렌 왁스 또는 폴리프로필렌 왁스 0.1 내지 1.5 중량부가 사용되며;
Preferably 0.1 to 1.5 parts by weight of polyethylene wax or polypropylene wax is used based on 100 parts by weight of the first composition;
상기 안료는, The above-
1차조성물 100중량부를 기준으로, 착색을 위한 안료인 무기계 안료 0.1 내지 5.0 중량부가 사용된다.
0.1 to 5.0 parts by weight of an inorganic pigment as a coloring pigment is used based on 100 parts by weight of the primary composition.
이하, 본 발명의 합성목재 조성물의 다른 실시상태에 대하여 설명키로 한다.Hereinafter, other embodiments of the synthetic wood composition of the present invention will be described.
필요에 따라, 본 발명의 합성목재 조성물이; If desired, the synthetic wood composition of the present invention may contain:
상기 1차조성물 100중량부를 기준으로,Based on 100 parts by weight of the primary composition,
광물질인 분말상의 실리카(Silica), 산화방지제인 산화티타늄(TiO2), 제올라이트계 항균제, 인산칼슘, 수산화알루미늄, 운모 중 선택된 1종 또는 1종 이상이 혼합 용융된, 혼합첨가물 0.3 내지 5.0중량부가 추가로 첨가된 조성의 합성목재 조성물로 구성 될수도 있으며;
0.3 to 5.0 parts by weight of a mixed additive in which one or more selected from the group consisting of silica in powder form, silica (antioxidant), titanium oxide (TiO2), zeolite antimicrobial agent, calcium phosphate, And may be composed of a synthetic wood composition having a composition added thereto;
상기 결합제 또는 복합 산화방지제, 광안정제, 자외선 흡수제, 활제, 안료 중 선택된 1종 또는 1종 이상이 미첨가된 조성의 합성목재 조성물로 구성 될수도 있으며;
And may be composed of a synthetic wood composition in which one or more selected from the above-mentioned binders or a composite antioxidant, a light stabilizer, an ultraviolet absorber, a lubricant, and a pigment is not added;
또한, 상기 1차조성물 100 중량부에 대하여,Further, with respect to 100 parts by weight of the primary composition,
원적외선 방사물질인 분말상의 옥 또는 게르마늄, 참숯, 황토, 산화마그네슘, 산화칼슘, 산화알루미늄, 산화철 중에서 선택된 1종 또는 1종 이상이 혼합 용융된, 원적외선 방사물 1.0 내지 10중량부가 첨가된 조성의 합성목재 조성물로 구성 될수도 있으며;
Synthesis of a composition containing 1.0 to 10 parts by weight of a far-infrared ray emulsion in which at least one selected from powdery oak or germanium, charcoal, yellow earth, magnesium oxide, calcium oxide, aluminum oxide and iron oxide is mixed and melted Wood composition;
상기 1차조성물 로만 조성된, 합성목재 조성물로 구성 될 수도 있다.
And may be composed of a synthetic wood composition, which is formed only with the primary composition.
상기와 같이, 본 발명 조성의 합성목재 조성물은; As described above, the synthetic wood composition of the present invention composition comprises:
종래기술 합성목재의 문제점을 해결 및,
[0002] Conventionally,
상기 조성의 목분과, 상기 물성 범위내의 합성수지인 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 혼합된 구성으로, 가공제품인 합성목재로 가공시에 종래기술의 천연목재 또는 합성목재에 비하여 내수성과 충격강도, 휨강도 물성이 강화된 조성과;
(PP), high density polyethylene (HDPE), or polyethylene teraphthalate (PET), which is a synthetic resin within the above-mentioned physical property range, and a synthetic resin Compared to natural wood or synthetic wood, the composition has improved water resistance, impact strength and flexural strength;
또한, 상기 목분과 폴리프로필렌(PP) 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 무독성 물질로서 인체에 무해하고, 화재 발생시에 염소가스가 미 배출되어 인체에 더욱 무해한, 환경친화적인 조성과;
In addition, the above-mentioned wood and polypropylene (PP) or high density polyethylene (HDPE) or polyethylene teraphthalate (PET) are non-toxic substances and harmless to the human body, Phosphorus composition;
상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP)인 폐자원의 재활용으로 원가절감이 되는 조성과;
A composition which is cost-reduced due to the recycling of scrap (SCRAP), which is a waste material generated after the processing of the above wood, glued wood and wood;
상기 미끄럼 방지 및 난연제에 의한, 종래기술의 천연목재 또는 합성목재에 비하여, 본 발명 합성목재 조성물로 가공된 완제품인 합성목재의 미끄럼 현상이 방지되는 동시에, It is possible to prevent the sliding of the synthetic wood which is an article finished with the synthetic wood composition of the present invention, compared with the prior art natural wood or synthetic wood by the non-slip and flame retardant,
산화안티몬과 같은 별개의 난연제가 미투입된 조성임에도 불구하고, 난연성능이 강화되어 화재 발생시에 화재가 번지지 않는 조성의; 미끄럼 방지 및 물성성능이 향상된 합성목재 조성물로 구성되어 있다.
Despite the fact that a separate flame retardant such as antimony oxide is not added, the flame retardant performance is enhanced, so that the fire does not spread when a fire occurs; And a synthetic wood composition having improved slip properties and physical properties.
이하, 본 발명의 "미끄럼 방지 및 물성성능이 향상된 합성목재 조성물의 제조방법"에 대하여 설명키로 한다.Hereinafter, the "method for producing a synthetic wood composition with improved slip resistance and physical properties" of the present invention will be described.
도 2에 도시한바와 같이;(해당 조성물의 상세 조성은, 상기 언급된 합성목재 조성물 참조)
(As for the detailed composition of the composition, see the above-mentioned synthetic wood composition)
본 발명의, 미끄럼 방지 및 물성성능이 향상된 합성목재 조성물("이하, 합성목재 조성물이라고 함")의 제조방법은, 다음과 같은 S1 내지 S4 단계의 제조방법으로 제조되며; A method for producing a synthetic wood composition (hereinafter referred to as " synthetic wood composition ") of the present invention, which has improved slip resistance and physical properties, Is manufactured by the following manufacturing method of steps S1 to S4;
S1 내지 S4 단계로 제조된 본 발명 합성목재 조성물이, S5 및 S6 단계의 제조방법으로, 가공제품인 합성목재의 기재가 제조된다.
The synthetic wood composition of the present invention prepared in steps S1 to S4 is a production method of steps S5 and S6 to produce a synthetic wood base material as a processed product.
S1 단계: 원목 또는 집성목, 파티클보드, 합판, 목재의 가공 후 폐자원인 스크랩 중 선택된 1종 또는 1종 이상이 분쇄된 목분을 제조, 목분 55 내지 85 중량%가 믹서기에 투입, 1차 교반 및 건조되는 단계;Step S1: A wood powder obtained by pulverizing at least one selected from the group consisting of wood or algae, particle board, plywood, and scrap, which is a waste material after processing of wood, is prepared, and 55 to 85% by weight of wood powder is put into a blender, Drying;
활엽수, 침엽수, 대나무 중 선택된 1종의 원목; 또는, 상기 활엽수, 침엽수, 대나무 원목 중 선택된 1종의 원목이 집성화 되어 넓은 크기로 형성된 1종의 집성목; 또는, 파티클보드, 합판 중 선택된 1종의 목재; 또는, 상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP); 중 선택된 1종 또는 1종이상이, 입자 크기 20 내지 180mesh로 분쇄기에서 분쇄된 목분 55 내지 85 중량%가 믹서기에 투입, 70 내지 110℃ 온도에서 1차 교반 및 건조되어, 목분의 수분 함유량이 0.1 내지 10%로 형성된다.
One selected from hardwood, conifer and bamboo; Or one kind of aggregate formed into a wide size by aggregating one kind of logwood selected from the above-mentioned broad-leaved trees, softwoods, and bamboo logs; Or a wood selected from a particle board and a plywood; Or scrap (SCRAP), which is a waste resource generated after processing of the wood, glued wood, and wood; , 55 to 85% by weight of wood powder pulverized in a pulverizer with a particle size of 20 to 180 mesh is put into a blender, stirred at 70 to 110 캜 for one hour and dried, and the water content of wood powder is adjusted to 0.1 To 10%.
S2 단계: 합성수지인 폴리프로필렌 또는 고밀도 폴리에틸렌 또는 폴리에틸렌 테라프타레이트 10 내지 30중량%가 믹서기에 투입, 2차 교반되는 단계;Step S2: 10 to 30% by weight of polypropylene or high-density polyethylene or polyethylene teraphthalate, which is a synthetic resin, is put into a blender and secondarily stirred;
수지용융지수 0.5 내지 40, 굴곡 탄성율 9,500 내지 12,000, 열변형온도 90 내지 140℃의 합성수지인 폴리프로필렌, 또는 고밀도 폴리에틸렌, 또는 폴리에틸렌 테라프타레이트 10 내지 30중량%가 상기 믹서기에 투입, 90 내지 140℃ 온도에서 2차 교반된다.
10 to 30% by weight of polypropylene or high-density polyethylene, which is a synthetic resin having a resin melt index of 0.5 to 40, a flexural modulus of 9,500 to 12,000 and a heat distortion temperature of 90 to 140 캜, is introduced into the blender, Lt; / RTI >
S3 단계: 화산석 또는 화산재, 에코트렉션 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물이 분쇄된 미끄럼방지 및 난연제를 제조 및, 미끄럼방지 및 난연제 5.0 내지 15중량%가 믹서기에 투입, 3차 교반되어, 1차조성물의 생성 단계;Step S3: Preparation of a slip-resistant and flame retardant mixture in which a mixed melt obtained by mixing and mixing at least one selected from volcanic ash, volcanic ash and ecotrione is mixed, and 5.0 to 15% by weight of an anti-slip and flame retardant are added to a mixer Stirring the mixture to produce a primary composition;
화산석 또는 화산재, 에코트렉션 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물이, 입자크기 50 내지 300mesh로 분쇄기 또는 절단기에서 분쇄 또는 절단된 미끄럼방지 및 난연제 5.0 내지 15중량%가 상기 믹서기에 투입, 70 내지 110℃ 온도에서 3차 교반되어, 1차조성물이 생성된다.
5.0 to 15% by weight of a non-slip and flame retardant, which is a mixed melt obtained by mixing and mixing at least one selected from volcanic ash, volcanic ash and ecotrione, is pulverized or cut in a pulverizer or a cutter with a particle size of 50 to 300 meshes, And the mixture is stirred at a temperature of 70 to 110 DEG C to form a first composition.
S4 단계: 1차조성물에, 결합제와 복합 산화방지제, 광안정제, 자외선흡수제, 활제, 안료가 믹서기에 투입, 4차 교반되어, 합성목재 조성물의 제조, 완료단계;Step S4: The binder is mixed with a composite antioxidant, a light stabilizer, an ultraviolet absorber, a lubricant, and a pigment into a blender, and the mixture is stirred four times to prepare and finish a synthetic wood composition;
상기 1차조성물 100중량부에, 결합제인 마레익 엔하이드라이드 폴리프로필렌 1.0 내지 8.0중량부와, 복합 산화방지제인 산화방지제 0.1 내지 3.0중량부 및 칼슘 스테아린산염 0.1 내지 2.0중량부와, 광안정제 0.1 내지 2.0중량부와, 자외선흡수제 0.1 내지 1.5중량부와, 활제 0.1 내지 1.5중량부, 안료인 무기계 안료 0.1 내지 5.중량부를 투입, 50 내지 90℃ 온도에서 4차 교반되어, 본 발명의 합성목재 조성물이 제조된다.
To 100 parts by weight of the first composition are added 1.0 to 8.0 parts by weight of a binder, meleeenhydride polypropylene, 0.1 to 3.0 parts by weight of an antioxidant as a complex antioxidant, 0.1 to 2.0 parts by weight of calcium stearate, 0.1 to 1.5 parts by weight of an ultraviolet absorber, 0.1 to 1.5 parts by weight of a lubricant and 0.1 to 5 parts by weight of an inorganic pigment as a pigment are added and stirred at a temperature of 50 to 90 ° C for 4 hours to obtain a synthetic wood A composition is prepared.
또한, 상기 S4 단계로 제조된 본 발명의 합성목재 조성물이, 하기의 S5 단계로 페렛으로 제조되며; Further, the synthetic wood composition of the present invention prepared in the step S4 is made into a ferret in the following step S5;
하기의 S6 단계로, 본 발명의 합성목재 조성물이 가공된, 미끄럼 방지 및 물성성능이 향상된 합성목재("이하, 합성목재라고 함")의 기재가 제조된다.
In the following step S6, a base material of synthetic wood (hereinafter referred to as " synthetic wood ") in which the synthetic wood composition of the present invention is processed and which has improved slip resistance and physical properties is produced.
S5 단계: 합성목재 조성물의 페렛(PELLET) 제조 단계Step S5: Pellet preparation step of synthetic wood composition
상기 S4 단계로 제조된 합성목재 조성물이, 페렛 제조 압출기의 호퍼에 투입되어 스크류 히팅 온도 110 내지 250℃로 합성목재 조성물이 페렛 제조금형으로 이송, 페렛 제조금형 히팅 온도 110 내지 190℃에서 페렛이 제조 된 후, 상온에서 건조된다.
The synthetic wood composition prepared in the above step S4 is put into a hopper of a pelletizing extruder, and the synthetic wood composition is transferred to a mold for producing pellets at a screw heating temperature of 110 to 250 ° C. And dried at room temperature.
S6 단계: 합성목재의 기재 제조 단계; (도 3 참조) Step S6: a base material manufacturing step of synthetic wood; (See Fig. 3)
도 3에 도시한바와같이, 상기 건조된 페렛(20)을 압출기(300)의 호퍼(310)에 투입, 상기 압출기(300)의 제 1 스크류(320) 히팅 온도 180 내지 240℃, 제 2 스크류(330) 히팅 온도 170 내지 200℃로 이송 및, 진공가스 배출부(360)에서 진공 가스가 외부로 배출 된 후, 제 3 스크류(340) 히팅 온도 140 내지 170℃, 제 4 스크류(350) 히팅 온도 150 내지 180℃로 상기 페렛(20)이 기재 제조금형(370)으로 이송되어, 기재 제조금형(370) 히팅 온도 140 내지 180℃에서 합성목재 기재로 압출 된 후, 냉각조(380)에서 냉각 후, 절단기로 절단되어; 본 발명의 합성목재 조성물이 가공된 가공제품인 합성목재의 기재가 제조된다.
3, the dried
필요에 따라, 본 발명의 합성목재 조성물의 제조방법이; If necessary, the process for producing a synthetic wood composition of the present invention comprises:
상기 S4 단계에, 1차조성물 100중량부를 기준으로,In step S4, based on 100 parts by weight of the first composition,
광물질인 분말상의 실리카(Silica), 산화방지제인 산화티타늄(TiO2), 제올라이트계 항균제, 인산칼슘, 수산화알루미늄, 운모 중 선택된 1종 또는 1종 이상이 혼합 용융된, 혼합첨가물 0.3 내지 5.0중량부가 추가로 첨가된 구성의 합성목재 조성물의 제조방법으로, 구성 될수도 있으며;
0.3 to 5.0 parts by weight of a mixed additive in which one or more selected from the group consisting of silica in powder form, silica (antioxidant), titanium oxide (TiO2), zeolite antimicrobial agent, calcium phosphate, A method of producing a synthetic wood composition having a composition added thereto;
상기 S4 단계의 결합제 또는 복합 산화방지제, 광안정제, 자외선 흡수제, 활제, 안료 중 선택된 1종 또는 1종 이상이 미첨가된 조성의 합성목재 조성물의 제조방법으로 구성 될수도 있으며;
A method of preparing a synthetic wood composition having a composition wherein at least one selected from the group consisting of a binder or a composite antioxidant, a light stabilizer, an ultraviolet absorber, a lubricant, and a pigment is not added;
상기 S4 단계에, 1차조성물 100중량부를 기준으로,In step S4, based on 100 parts by weight of the first composition,
원적외선 방사물질인 분말상의 옥 또는 게르마늄, 참숯, 황토, 산화마그네슘, 산화칼슘, 산화알루미늄, 산화철 중에서 선택된 1종 또는 1종 이상이 혼합 용융된, 원적외선 방사물 1.0 내지 10중량부가 첨가된 조성의 합성목재 조성물로 구성 될수도 있으며;
Synthesis of a composition containing 1.0 to 10 parts by weight of a far-infrared ray emulsion in which at least one selected from powdery oak or germanium, charcoal, yellow earth, magnesium oxide, calcium oxide, aluminum oxide and iron oxide is mixed and melted Wood composition;
상기 S4 단계가 배제된, S1 내지 S3단계로 구성된 1차조성물 로만 조성된, 합성목재 조성물의 제조방법으로 구성 될 수도 있다.And a method of manufacturing a synthetic wood composition, which is constituted only with the primary composition composed of the steps S1 to S3, wherein the step S4 is excluded.
상기 S1 내지 S4 단계로 구성된, 본 발명의 합성목재 조성물의 제조방법에 의하여;
By the process for producing a synthetic wood composition according to the present invention comprising the steps of S1 to S4;
상기 조성의 목분과, 상기 물성 범위내의 합성수지인 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 혼합된 구성으로, 가공제품인 합성목재로 가공시에 종래기술의 천연목재 또는 합성목재에 비하여 내수성과 충격강도, 휨강도 물성이 강화된 제조방법과;
(PP), high density polyethylene (HDPE), or polyethylene teraphthalate (PET), which is a synthetic resin within the above-mentioned physical property range, and a synthetic resin A manufacturing method in which water resistance, impact strength and flexural strength are enhanced compared to natural wood or synthetic wood;
또한, 상기 목분과 폴리프로필렌(PP), 또는 고밀도 폴리에틸렌(HDPE), 또는 폴리에틸렌 테라프타레이트(P.E.T)가 무독성 물질로서, 화재 발생시에 염소가스가 미 배출되어 인체에 무해한, 환경친화적인 제조방법과;
In addition, the above-mentioned wood and polypropylene (PP), high density polyethylene (HDPE), or polyethylene teraphthalate (PET) are nontoxic substances, and an environmentally friendly manufacturing method in which chlorine gas is not discharged when a fire occurs and harmless to the human body ;
상기 원목, 집성목, 목재의 가공 후 발생된 폐자원인 스크랩(SCRAP)인 폐자원의 재활용으로 원가절감이 되는 제조방법과;
A manufacturing method in which costs are reduced by recycling waste resources that are scrap (SCRAP), which is a waste resource generated after processing of the wood, glued wood, and wood;
상기 미끄럼 방지 및 난연제에 의한, 종래기술의 천연목재 또는 합성목재에 비하여, 본 발명 합성목재 조성물로 가공된 완제품인 합성목재의 미끄럼 현상이 방지되는 동시에, It is possible to prevent the sliding of the synthetic wood which is an article finished with the synthetic wood composition of the present invention, compared with the prior art natural wood or synthetic wood by the non-slip and flame retardant,
산화안티몬과 같은 별개의 난연제가 미투입된 조성임에도 불구하고, 난연성능이 강화되어 화재 발생시에 화재가 번지지 않는 제조방법으로 구성되어 있으며;
Despite the fact that a separate flame retardant such as antimony oxide is not added, it is composed of a manufacturing method in which the flame retardant performance is enhanced and the fire does not spread when a fire occurs;
또한, 상기 S5 단계로 제조된 펠렛이 S6 단계의 합성목재의 기재로 압출기에 투입, 가공된 제조방법에 의하여; Further, the pellet produced in the step S5 is put into an extruder with the base material of the synthetic wood of the step S6 and processed by the manufacturing method;
가공성이 우수하여 가공제품인 합성목재의 표면층의 표면질감이 향상되고, 가공제품인 합성목재의 제조가 용이하여 작업성이 대폭 향상된 구성의, 미끄럼 방지 및 물성성능이 향상된 합성목재 조성물의 제조방법으로 구성되어 있다.
And a process for producing a synthetic wood composition having improved surface properties of a surface layer of a synthetic wood which is excellent in workability and improved in workability due to easy production of a synthetic wood as a processed product, have.
이하, 본 발명을 실시예를 들어 더욱 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to examples.
실시예는, 상기 S1 내지 S4 단계의 제조방법으로 제조된 본 발명의 합성목재 조성물이, 상기 S5 및 S6 단계로 가공된 합성목재가 사용된, 펜스(FANCE)이고;
The embodiment is a FANCE in which the synthetic wood composition of the present invention produced by the manufacturing method of the above S1 to S4 is used in the synthetic wood processed in the above S5 and S6 steps;
비교예 1은, 천연목재로 제조된 시중에서 유통되는 천연목재 재질의 펜스 이며;Comparative Example 1 is a natural wooden fence made of natural wood and distributed on the market;
비교예 2는 목분과 합성수지인 염화비닐수지로 구성된 합성목재 조성물로 가공된 시중에서 유통되는 합성목재 재질의 펜스(FANCE)로서, 상기 실시예 및 비교예 1,2의 주요 물성 분석결과치는 표 1, 2에 나타내었다.
Comparative Example 2 is a fence of a synthetic wood material which is manufactured by a synthetic wood composition composed of wood and a synthetic resin such as vinyl chloride resin. The results of the main physical properties analysis of the above Examples and Comparative Examples 1 and 2 are shown in Table 1 , Respectively.
[실시예][Example]
1차조성물 100중량%를 기준으로, Based on 100 wt% of the primary composition,
입자크기 40mash, 수분함량 6.3%의 목분 55중량%와, 폴리프로필렌 30중량%와, 미끄럼방지 및 난연제인 입자크기 75mash의 화산석 15중량%가 믹서기에 투입, 상기 S1, S2 단계의 해당 온도 범위로 1,2,3차 교반되어, 1차조성물이 제조 후; 55% by weight of wood powder having a particle size of 40 mash and a moisture content of 6.3%, 30% by weight of polypropylene and 15% by weight of a volcanic stone having a particle size of 75 mash as a non-slip and flame retardant were put into a blender, 1, 2, and 3, whereby the primary composition is prepared after the preparation;
상기 1차조성물 100중량부에 대하여,With respect to 100 parts by weight of the primary composition,
결합제인 마레익 엔하이드라이드 폴리프로필렌 5.5중량부와, 복합 산화방지제인 포스페이트 계통의 산화방지제 1.0중량부 및 칼슘 스테아린산염 0.7중량부, 광안정제인 비스 2.2.6.6- 테트라 메틸- 4- 파이퍼리딜 0.5중량부, 자외선흡수제인 벤조트리아졸 계통의 2-(2' - hydroxy -3' - tert - butyl - 5' - methyl - phenyl)-5-chlorobenzotriazol 0.5중량부, 활제인 폴리에틸렌 왁스 0.8 중량부, 무기계 안료 1.0중량부를 믹서기에 투입하여, 78℃ 온도에서 4차 교반되어, 본 발명의 합성목재 조성물을 제조 하였으며;5.5 parts by weight of a binder, melejuenhydride polypropylene, 1.0 part by weight of a phosphate-based antioxidant as a complex antioxidant and 0.7 parts by weight of calcium stearate as a light stabilizer, 2.2.6.6-tetramethyl-4-piperidyl 0.5 0.5 part by weight of 2- (2'-hydroxy-3 '-tert-butyl-5'-methyl-phenyl) -5-chlorobenzotriazole of the benzotriazole system as an ultraviolet absorber, 0.8 part by weight of a lubricant polyethylene wax, 1.0 part by weight of pigment were added to a blender and stirred at 78 占 폚 for 4 times to prepare a synthetic wood composition of the present invention;
상기 합성목재 조성물을 페렛 제조 압출기의 호퍼에 투입, 스크류 전단부 온도 180℃, 중앙부 온도 200℃, 후면부 온도 170℃로 이송, 금형온도 180℃로 페렛을 제조하여 상온에서 건조한 후, The synthetic wood composition was fed into a hopper of a pelletizing extruder, and the pellet was transferred at a screw front end temperature of 180 ° C, a center temperature of 200 ° C and a rear surface temperature of 170 ° C, a mold temperature of 180 ° C,
압출기의 호퍼에 상기 페렛을 투입, 제 1스크류 온도 190℃, 제 2스크류 온도 170℃로 이송 및 진공가스를 진공가스 배출부로 배출한 후, 제 3스크류 온도 140℃, 제 4스크류 온도 180℃로 이송하여, 180℃ 금형에서 압출, 기재를 제조 냉각조에서 냉각 및 절단기로 절단, 합성목재 기재를 제조하였으며; 상기 합성목재 기재를 펜스로 가공하였다.
The pellet was fed into a hopper of an extruder, and the first screw temperature was 190 ° C., the second screw temperature was 170 ° C., and the vacuum gas was discharged to the vacuum gas discharger. The third screw temperature was 140 ° C. and the fourth screw temperature was 180 ° C. And extruded in a 180 DEG C mold, the substrate was cooled and cut with a cutting machine in a manufacturing cooling bath to prepare a synthetic wood base; The synthetic wood substrate was processed with a fence.
[비교예 1][Comparative Example 1]
천연목재로 제조된 천연목재 재질의 펜스를 시중에서 구입 하였다.
Natural wooden fences made of natural wood are commercially available.
[비교예 2][Comparative Example 2]
목분 55중량% 및, 합성수지인 염화비닐수지와 첨가제 45중량%로 구성된 합성목재 조성물로 가공된 합성목재 재질의 펜스를 시중에서 구입 하였다.
55% by weight of wood powder, and a synthetic wood fence processed with a synthetic wood composition composed of vinyl chloride resin as a synthetic resin and 45% by weight of an additive were commercially available.
- GR 규격 : 한국 목재 재활용 규격
- GR Specification: Korean Wood Recycling Standard
Flammability
KSF 3230
20㎝ 이하Carbonization length:
Below 20㎝
상기 표 1, 2에 기재된바와 같이, 본 발명 조성의 합성목재 조성물로 가공된 펜스인 실시예가, 종래기술의 천연목재로 가공된 펜스인 비교예 1과, 종래 기술의 염화비닐수지 혼합 조성물이 사용된 합성목재로 가공된 펜스에 비하여 충격강도, 휨강도, 물흡수율(내수성)이 가장 우수 하였으며;
As shown in Tables 1 and 2, the fence samples processed with the synthetic wood composition of the present invention were compared with Comparative Example 1, which was a fence processed with natural wood of the prior art, and Comparative Example 1, Impact strength, bending strength and water absorption (water resistance) were superior to those of synthetic wood treated fences;
특히, 본 발명 조성의 합성목재 조성물로 가공된 펜스인 실시예가, 표면층에 본 발명 조성의 미끄럼 방지 및 난연제인 입자크기 75mash의 화산석이 분포 산재 됨으로 인하여 미끄럼 현상이 방지되고, 연소시에 탄화길이 13㎝, 나머지 불꽃이 5초 이하로서, 난연성능이 우수한 동시에 인체에 유해한 염소가스가 미발생 되었으며;In particular, the fence example processed with the synthetic wood composition of the present invention has slidability due to the non-slip and flame retardant agent of the present invention distributed on the surface layer and dispersed and dispersed in the volcanic stone having a particle size of 75 mash, and the carbonization length 13 Cm and the remaining flame was 5 seconds or less, excellent flame retardant performance and no chlorine gas harmful to human body were generated;
본 발명의 제조방법으로 인하여 표면층의 표면질감이 우수하고, 작업성이 향상되는 것으로 판명 되었다.
It has been found that the surface texture of the surface layer is excellent and the workability is improved owing to the production method of the present invention.
또한, 상기 비교예 1은, 물흡수율(내수성)이 취약하고, 충격강도가 저하되며, 실시예를 1배로 기준할때 천연목재의 재질로 2배의 원가 상승이 됨으로서 사용상의 문제점 및, 표면층이 미끄러워 안전사고의 위험과, 연소시에 탄화길이 30㎝, 나머지 불꽃이 15초로서 기준치에 불합격, 난연성능이 현저히 저하되어 화재 발생시에 화재가 더욱 번지는 문제점이 있는 것으로 판명 되었으며;
In addition, in Comparative Example 1, the water absorption rate (water resistance) was poor, the impact strength was lowered, and the cost increased twice as much as the natural wood material when the example was used at one time, It is found that there is a risk of safety accident when slippery, the carbonization length is 30 cm at the time of burning, and the remaining flame is 15 seconds, which fails to meet the reference value, and the flame retardant performance is remarkably deteriorated.
상기 비교예 2는, 물흡수율(내수성), 충격강도 물성은 일부 충족되나, 휨강도 물성이 현저히 저하 되었으며, 염화비닐수지 혼합 사용으로 인한 표면층이 더욱 미끄러워 안전사고의 위험이 더욱 증가되었으며, 연소시에 탄화길이 22㎝, 나머지 불꽃이 11초로서 기준치에 불합격, 난연성능이 저하되어 화재 발생시에 난연성능의 문제점과, 염소가스의 배출로 인체에 유해한 것으로 판명 되었다.In Comparative Example 2, although the water absorption rate (water resistance) and the impact strength properties were partially satisfied, the physical properties of the flexural strength were significantly lowered, and the surface layer due to the use of the vinyl chloride resin mixture was further slippery, And the remaining flame was 11 seconds, and the flame retardant performance deteriorated due to the failure to meet the reference value, which proved to be detrimental to the human body due to the problem of flame retardancy at the time of fire occurrence and discharge of chlorine gas.
20 : 페렛
300 : 압출기
310 : 호퍼
320, 330,340,350 : 제 1,2,3,4 스크류
360: 진공가스배출부 370 : 기재 제조금형
380 : 냉각조20: Ferret
300: extruder
310: Hopper
320, 330, 340, 350: 1st, 2nd,
360: Vacuum gas discharging part 370: Mold manufacturing machine
380: Cooling tank
Claims (9)
수지용융지수 0.5 내지 40, 굴곡 탄성율 9,500 내지 12,000, 열변형온도 90 내지 140℃의 합성수지인 폴리프로필렌 또는 고밀도 폴리에틸렌 또는 폴리에틸렌 테라프타레이트 10 내지 30중량%로, 조성된 1차조성물과;
상기 1차조성물 100 중량부에 대하여,
결합제 1.0 내지 8.0중량부와, 복합 산화방지제인 산화방지제 0.1 내지 3.0 중량부 및 칼슘 스테아린산염 0.1 내지 2.0 중량부와, 광안정제 0.1 내지 2.0 중량부와, 자외선흡수제 0.1 내지 1.5 중량부와, 활제 0.1 내지 1.5 중량부와, 안료인 무기계 안료 0.1 내지 5.0 중량부가 첨가된 합성목재 조성물에 있어서;
상기 1차조성물 100중량%를 기준으로,
입자크기 50 내지 300mesh의 화산석, 화산재, 에코트렉션 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물인 미끄럼방지 및 난연제 5.0 내지 15중량%로 조성 됨을 특징으로 하는, 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물.A synthetic wood composition for use as an interior and exterior material of a building comprises one kind of logwood selected from among broad-leaved trees, coniferous trees and bamboo, or one selected from broad-leaved trees, coniferous trees and bamboo logs based on 100 wt% (SCRAP), which is a waste material generated after processing of wood, aggregate, wood, or a selected one kind of wood selected from particle board, plywood, 55 to 85% by weight of powdered wood powder,
A resin composition having a resin melt index of 0.5 to 40, a flexural modulus of 9,500 to 12,000, a heat distortion temperature of 90 to 140 DEG C, and 10 to 30% by weight of polypropylene or high density polyethylene or polyethylene teraphthalate;
With respect to 100 parts by weight of the primary composition,
0.1 to 2.0 parts by weight of a light stabilizer, 0.1 to 1.5 parts by weight of an ultraviolet absorber, 0.1 to 1.5 parts by weight of a lubricant 0.1, To 1.5 parts by weight, and 0.1 to 5.0 parts by weight of an inorganic pigment as a pigment are added;
Based on 100 wt% of the primary composition,
To 5.0 to 15% by weight of a non-slip and flame retardant, which is a mixed molten mixture of one or more selected from volcanic ash, volcanic ash, and ecotrone having a particle size of 50 to 300 meshes Wherein the synthetic wood composition has improved slip resistance and physical properties.
S1 단계: 원목 또는 집성목, 파티클보드, 합판, 목재의 가공 후 폐자원인 스크랩 중 선택된 1종 또는 1종 이상이 분쇄된 목분을 제조, 목분 55 내지 85 중량%가 믹서기에 투입, 1차 교반 및 건조되는 단계; 및,
S2 단계: 합성수지인 폴리프로필렌 또는 고밀도 폴리에틸렌 또는 폴리에틸렌 테라프타레이트 10 내지 30중량%가 믹서기에 투입, 2차 교반되는 단계; 와,
S4 단계: 1차조성물에, 결합제와 복합 산화방지제, 광안정제, 자외선흡수제, 활제, 안료가 믹서기에 투입, 4차 교반되어, 합성목재 조성물의 제조, 완료단계; 로 재조되는 합성목재 조성물의 제조방법에 있어서;
상기 S2 단계의 후 단계와 S4 단계의 전 단계에,
S3 단계: 화산석 또는 화산재, 에코트렉션 중 선택된 1종 또는 1종 이상이 혼합 용융된 혼합용융물이 분쇄된 미끄럼방지 및 난연제를 제조 및, 미끄럼방지 및 난연제 5.0 내지 15중량%가 믹서기에 투입, 3차 교반되어, 1차조성물의 생성 단계; 로 1차 조성물이 제조 됨을 특징으로 하는, 미끄럼 방지 및 물성성능이 강화된 합성목재 조성물의 제조방법.A method of manufacturing a synthetic wood composition for use as an interior or exterior material of a building,
Step S1: A wood powder obtained by pulverizing at least one selected from the group consisting of wood or algae, particle board, plywood, and scrap, which is a waste material after processing of wood, is prepared, and 55 to 85% by weight of wood powder is put into a blender, Drying; And
Step S2: 10 to 30% by weight of polypropylene or high-density polyethylene or polyethylene teraphthalate, which is a synthetic resin, is put into a blender and secondarily stirred; Wow,
Step S4: The binder is mixed with a composite antioxidant, a light stabilizer, an ultraviolet absorber, a lubricant, and a pigment into a blender, and the mixture is stirred four times to prepare and finish a synthetic wood composition; ≪ RTI ID = 0.0 > 1, < / RTI >
In the steps after the step S2 and all the steps of the step S4,
Step S3: Preparation of a slip-resistant and flame retardant mixture in which a mixed melt obtained by mixing and mixing at least one selected from volcanic ash, volcanic ash and ecotrione is mixed, and 5.0 to 15% by weight of an anti-slip and flame retardant are added to a mixer Stirring the mixture to produce a primary composition; Lt; RTI ID = 0.0 > Wherein the synthetic wood composition is produced by a method comprising the steps of: