KR101433879B1 - Constructing method of waterproof and root isolation structure using punched joint tape and triple bond in joint part - Google Patents
Constructing method of waterproof and root isolation structure using punched joint tape and triple bond in joint part Download PDFInfo
- Publication number
- KR101433879B1 KR101433879B1 KR1020130043770A KR20130043770A KR101433879B1 KR 101433879 B1 KR101433879 B1 KR 101433879B1 KR 1020130043770 A KR1020130043770 A KR 1020130043770A KR 20130043770 A KR20130043770 A KR 20130043770A KR 101433879 B1 KR101433879 B1 KR 101433879B1
- Authority
- KR
- South Korea
- Prior art keywords
- joint
- sheet
- parts
- waterproof
- weight
- Prior art date
Abstract
Description
본 발명은 3중층 복합 방수·방근구조의 시공방법에 관한 것으로, 보다 상세하게는, 방수·방근 일체형 시트가 맞닿아 이어지는 접합부에서도 시트에 사용된 PET 필름의 연속성을 확보하여 접합부에서 방근 특성의 연속성이 확보되어 접합부로 뿌리가 침투하는 것을 차단할 수 있는 천공된 조인트 방근보강재 및 이를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법에 관한 것이다.
The present invention relates to a construction method of a triple-layer composite waterproofing and anti-skid structure, and more particularly, to a method of constructing a triple-layer composite waterproofing and anti-skid structure by securing the continuity of a PET film used in a sheet even in a joining portion in which a waterproof / And a method of constructing a combined waterproofing and anti-skid structure in which the adhesive strength of a joint is improved by using a triple layer structure using the same.
최근 많은 건물에서 옥상녹화 및 실내정원을 설치하고 있는데 이는 냉난방 에너지 절약, 공기 정화, 소음 경감 및 도시 경관 향상 등 환경과 경제적 측면에서 여러가지 이점이 있어서 권장되고 있다. 이와 같은 옥상녹화의 많은 이점에도 불구하고 활성화되지 못하고 있는 데에는 여러가지 이유가 있겠지만, 그중에서도 식물 뿌리가 성장하면서 건축물을 파손시키게 될 뿐만 아니라 방수층의 파손으로 건축물의 방수에 문제가 발생한다는 것이다. 즉, 옥상 또는 실내에 심은 식물의 뿌리가 방근시트를 뚫고 들어가서 그 하부에 있는 방수층까지 파손시켜 방수에 문제가 발생한다는 것이다.
In recent years, many buildings have installed green roofs and indoor gardens, which are encouraged because of environmental and economic advantages such as energy saving, air purification, air purification, noise reduction and improvement of cityscape. Despite the many advantages of rooftop greening, there are various reasons for not being activated. However, in addition to damaging the buildings due to the growth of the plant roots, the damage of the waterproof layer causes problems in the waterproofing of the buildings. That is, the roots of roots planted on the roof or in the room penetrate the antifouling sheet and damage the waterproof layer at the bottom, causing problems with waterproofing.
본 출원인은 상기와 같은 문제를 해결하기 위하여 많은 연구 개발을 거듭한 끝에 특허등록 제872127호 "방근시트와 이 방근시트를 이용한 복합방수·방근구조의 시공방법"에 대하여 특허를 받았는데, 콘크리트층의 상부에 방수층을 형성하고 그 상부에 방근시트를 부착하여 시공하는데, 방근시트는 PET필름과, PET필름 하부에 부착시킨 부직포와, 부직포 하부에 함침시킨 고점착 연질형 고무화 아스팔트 및 PET필름의 상부에는 보강코팅층을 형성하여 구성한 것이다. 이와 같은 방근시트를 단부가 겹쳐지도록 배치하여 접착시킨 다음 접합부의 상부에 PET테이프를 부착시켜 시공하는 공법이다.
The present applicant has obtained many patents on patent registration No. 872127 entitled " Method of constructing a composite waterproofing and gypsum structure using a carpet sheet and a carpet sheet "after a lot of research and development to solve the above problems. The weatherproof sheet includes a PET film, a nonwoven fabric attached to the bottom of the PET film, a high-adhesion soft-type rubberized asphalt impregnated in the lower portion of the nonwoven fabric, and an upper portion of the PET film Is formed by forming a reinforcing coating layer. These barrier sheets are arranged so that their ends are overlapped and adhered, and a PET tape is adhered to the upper part of the joint to construct the barrier sheet.
하지만, 실제 시공을 하다보니 상기 방수·방근구조는,However, in actual construction, the waterproofing /
첫째, 방근시트 상부가 PET 필름으로 되어 있어서 상부가 매끈매끈하기 때문에 방근층을 형성할 때 방근시트가 겹치는 접합부의 상부에 PET 테이프를 부착시켜 시공하므로, 시간이 지남에 따라 PET 테이프의 접착력이 약화되어 방근시트의 접합부에서 들뜸이나 박리현상이 일어나 나무 뿌리가 접합부 사이로 침투하여 방근층이 훼손되어 방근은 물론 방수에도 하자가 발생하게 되는 문제가 있고,First, PET tape is attached to the upper part of the junction where the antifogging sheet overlaps when the antifogging layer is formed because the upper part of the antiperspiratory sheet is made of PET film, so that the adhesive strength of the PET tape is weakened over time So that there is a problem that the roots of the tree penetrate into the joints and the roof layer is damaged to cause defects in the waterproofing as well as the side walls.
둘째, 접착제로 PET 필름과 부직포를 접착시킨 후 부직포에 고점착 연질형 고무화 아스팔트를 함침시켜서 방근시트를 성형했기 때문에, 시간이 지남에 따라 부직포가 함침된 고점착 연질형 고무화 아스팔트의 성분 중에 있는 유성(油性)물질(즉, 오일 성분)의 영향으로 접착제의 기능이 상실되게 되어 결과적으로 PET 필름과 부직포가 박리되는 문제가 나타났다.
Second, since the PET film and the nonwoven fabric are adhered with the adhesive and the nonwoven fabric is impregnated with the high-adhesion soft rubberized asphalt to form the anti-woven sheet, the nonwoven fabric is impregnated with the non- The function of the adhesive is lost due to the influence of the oily substance (i.e., oil component) contained in the PET film, resulting in peeling of the PET film and the nonwoven fabric.
본 출원인은 상기 특허가 갖는 문제를 해결하기 위하여 많은 연구 개발을 거듭한 끝에 특허등록 제924114호 "자착식 고무화 아스팔트시트 및 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법"을 특허받았는데, 이는 방수시트로 방수층을 형성한 다음 그 상부에 방근시트로 방근층을 형성하는 시공법이어서, 별도의 방수시트와 방근시트를 사용하므로 자재비가 많이 들어갈 뿐만 아니라 두 번의 시공을 해야 하기 때문에 공사비와 공사기간이 많이 소요되어 시공상 문제가 있었다.
The present applicant has repeated many researches and developments in order to solve the problems of the patent, and the inventor of the present invention has found that the patent application No. 924114 "The construction of composite waterproofing and anti-glare structure using self-inflating rubberized asphalt sheet, self-inflating rubberized asphalt sheet, Method, "which is a construction method in which a waterproof layer is formed with a waterproof sheet and a barrier layer is formed on the upper part with a waterproof sheet. Since a separate waterproof sheet and a natural sheet are used, Therefore, it took a lot of construction cost and construction period and there was a problem in construction.
또, 상기 특허들을 더욱 발전시켜 특허등록 제1214810호 "방수·방근 일체형 시트 및 이를 이용한 방수·방근구조의 시공방법"을 특허받았는데, 이는 상기 특허들의 실제 시공에서 나타난 문제점들의 일부는 해결되었으나, 모든 방수 및 방근 시공에 있어서 가장 핵심적인 기술이 시트의 접합부 처리인바, 본 출원인은 시트의 접합부위를 통해 뿌리가 침투하는 것을 근원적으로 차단할 수 있는 기술에 대하여 지속적인 연구 개발을 계속하던 중에 본 발명에 이르게 되었다.
Further, the above-mentioned patents are further developed to obtain a patent for patent No. 1214810 entitled " waterproofing and anti-tactile sheet and method of constructing a waterproofing and anti-skid structure using the same, The applicant of the present application continued to research and develop a technology capable of fundamentally blocking the infiltration of roots through the jointed portion of the sheet, .
본 발명은 상기와 같은 많은 연구 개발을 거치면서 도출된 것으로, 본 발명의 목적은, 방근보강재의 길이방향을 따라 가장자리에 균일하게 천공 구멍을 형성함으로써 방근보강재 자체가 유연하고, 시트 접합부의 접착력도 현저하게 향상시킬 수 있는 천공된 조인트 방근보강재를 제공하기 위한 것이다.
SUMMARY OF THE INVENTION The present invention has been accomplished through the above-mentioned various research and development. It is an object of the present invention to provide a reinforcement structure for a vehicle, wherein the reinforcement itself is flexible by forming perforations uniformly along the longitudinal direction of the reinforcement, And to provide a perforated joint web reinforcement that can be significantly improved.
본 발명의 또 다른 목적은, 방수·방근 일체형 시트가 맞닿게 시공되는 접합부의 상부에 중심부를 제외한 양측 가장자리를 따라 일정 간격으로 천공되어 있고 PET 필름이 구비되어 만들어진 조인트 방근보강재를 사용함으로써, 시트의 접합부에서도 PET 필름에 의한 방근 특성의 연속성이 확보되어 접합부로 뿌리가 침투하는 것을 차단할 수 있는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법을 제공하기 위한 것이다.
It is still another object of the present invention to provide a waterproofing and antifogging sheet which is formed by joining a jointed portion of a sheet to be joined to a waterproof and antiperspirant sheet at a predetermined interval along both side edges except a central portion thereof, It also provides a construction method of composite waterproofing and anti-skid structure which has improved adhesion of joints with triple layer structure by using perforated joint web reinforcement which can prevent penetration of roots into joints by continuity of PET properties .
본 발명에 따른 천공된 조인트 방근보강재는 시트와 시트 사이의 접합부에 접착시키는데 사용되는데, 조인트 방근보강재는, PET(Polyethylene Terephthalate) 필름과, 상기 필름의 상부와 하부에 열경화성수지 접착제에 의해 각각 접착된 부직포를 구비하여 구성되고, 길이방향을 따라 양측 가장자리에 일정 간격으로 균등하게 천공 구멍이 형성된 것을 특징으로 한다.
The perforated joint web reinforcement according to the present invention is used for adhering to a joint between a seat and a sheet, wherein the joint web reinforcement is made of a PET (polyethylene terephthalate) film and a thermosetting resin adhesive A nonwoven fabric is provided, and perforations are uniformly formed at both side edges along the longitudinal direction at regular intervals.
본 발명에 따른 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법은, 콘크리트 표면에 프라이머를 도포하여 프라이머층을 형성하는 단계; 프라이머층의 상부에 방수기능과 방근기능을 함께 구비하고 자착기능이 있는 방수·방근 일체형 시트를 시트 단부(端部)가 일정 간격 이격되게 하여 접착시키는 단계; 접착된 상기 시트와 시트 사이에 접합부를 형성하는 단계; 접합부를 형성한 후에 방수·방근층 전체면의 상부에 합성수지를 도포하는 단계를 거쳐서 시공하며, 상기 접합부를 형성하는 단계에서는, 일정 간격 이격된 시트와 시트 사이에 고경질우레탄 또는 FRP를 충전한 다음, 양단(兩端)이 양측에 위치한 시트 각각에 위치하도록 하여 조인트 방근보강재를 접착시킨 후 조인트 방근보강재의 상부에 다시 고경질우레탄 또는 FRP를 도포하여 형성하며, 상기 조인트 방근보강재는, 가운데 위치시킨 PET 필름의 상부와 하부에 열경화성수지 접착제에 의해 부직포를 각각 접착시키며, 양측 가장자리에 길이방향을 따라 일정 간격으로 천공 구멍을 형성한 것인 것을 특징으로 한다.
A method of constructing a composite watertight / skid structure having a triple-layered structure using a perforated joint web reinforcement according to the present invention, the method comprising: forming a primer layer on a concrete surface by applying a primer; A step of adhering a waterproof and antistatic integrated sheet having a waterproof function and an anticycling function on the top of the primer layer and having a sticking function such that end portions of the sheet are spaced apart from each other by a predetermined distance; Forming a bond between the bonded sheet and the sheet; A step of applying synthetic resin to the upper part of the entire surface of the waterproofing and antifouling layer after forming the joint part, and in the step of forming the joint part, high-hardness urethane or FRP is filled between the sheet and the sheet spaced apart at regular intervals Rigid Urethane or FRP is applied to the upper portion of the joint lateral reinforcement so that both joints are positioned on both sides of the joint, and the joint lateral reinforcement is positioned at the center The nonwoven fabric is adhered to the upper and lower portions of the PET film by a thermosetting resin adhesive, and perforations are formed at both side edges of the PET film at regular intervals along the longitudinal direction.
바람직하게는, 방수·방근 일체형 시트는, PET 필름, PET 필름의 상부와 하부에 열경화성수지 접착제에 의해 각각 접착된 부직포; 상부가 상기 PET 필름의 하부에 접착된 부직포에 함침된 고점착 연질형 자착식 콤파운드; 상기 고점착 연질형 자착식 콤파운드의 하부에 부착시킨 이형지를 구비하여 구성되고, 상기 고점착 연질형 자착식 콤파운드는, 스트레이트 아스팔트 35∼60중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 5∼10중량부, 프로세스 오일 10∼20중량부, 접착부여제(전분) 1∼5중량부, 흡유제(화산재) 1∼5중량부, 충전재(돌로마이트) 5∼15중량부, 스테아린산 알미늄 3∼5중량부, 내산화 및 내균열 노화방지제 3∼5중량부, 검로진 3∼5중량부로 구성된다.
Preferably, the waterproof / antistatic integrated sheet is a nonwoven fabric bonded to the top and bottom of a PET film or a PET film by a thermosetting resin adhesive, respectively; A high-adhesion soft-type injection molded compound in which an upper portion is impregnated in a nonwoven fabric adhered to a lower portion of the PET film; Wherein the highly adhesive soft type compounding compound comprises 35 to 60 parts by weight of straight asphalt, 10 to 20 parts by weight of styrene butadiene styrene, 5 to 20 parts by weight of butyl rubber 5 10 to 20 parts by weight of a process oil, 1 to 5 parts by weight of an adhesive agent (starch), 1 to 5 parts by weight of an oil absorbent (ash), 5 to 15 parts by weight of a filler (dolomite) 3 to 5 parts by weight of an anti-oxidation and anti-cracking antioxidant, and 3 to 5 parts by weight of a chelating agent.
바람직하게는, 조인트 방근보강재의 폭은 70∼120㎜이며, 천공 구멍은 가장자리의 양측 10∼30㎜ 부분에 일정 간격으로 형성되어 있고, PET 필름의 두께는 0.02∼0.20㎜이다.
Preferably, the width of the joint near side stiffener is 70 to 120 mm, and the perforation holes are formed at intervals of 10 to 30 mm on both sides of the edge, and the thickness of the PET film is 0.02 to 0.20 mm.
상기와 같은 특징을 갖는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법은, PET 필름이 구비되어 제작된 방수·방근 일체형 시트가 맞대져서 시공되는 접합부의 상부에 중심부를 제외한 양측 가장자리를 따라 일정 간격으로 천공되어 있고 PET 필름이 구비되어 만들어진 조인트 방근보강재를 접착했기 때문에 시트가 이격된 접합부에서도 PET 필름이 구비된 조인트 방근보강재에 의해 PET 필름이 계속 이어지게 되므로, 접합부에서의 방근 특성의 연속성이 확보됨은 물론 맞대진 부분에 충전된 고경질우레탄 또는 FRP가 조인트 방근보강재의 양측 가장자리에 형성된 천공 구멍을 통해 올라와서 조인트 방근보강재와 시트 사이의 접착력을 더욱 향상시켜 주게 되므로 접합부로 뿌리가 침투하는 것을 근원적으로 차단할 수 있다.
The combined waterproofing and anti-skid construction method using the perforated joint web reinforcement having the above-described characteristics in which the adhesive strength of the joints is improved by the three-layered structure is characterized in that the waterproof and anti- Since the joint joint reinforcement material made by PET film is perforated at regular intervals along the both side edges except the central part at the upper part of the joint part, the PET film is continued by the joint joint reinforcement material provided with the PET film The continuous rigidity of the joint at the joint portion is ensured, and at the same time, the high rigidity urethane or FRP filled in the inward portion comes up through the perforation hole formed at the both side edges of the joint side reinforcement member to increase the adhesive force between the joint side reinforcement member and the seat So that the roots penetrate into the joints. Can be essentially blocked.
또한, 본 발명에서는 기능이 서로 다른 방수시트와 방근시트를 하나의 시트로 만든 방수·방근 일체형 시트를 사용했기 때문에 하나의 시트가 방수기능과 방근기능을 동시에 갖게 되므로 자재비를 절감할 수 있을 뿐만 아니라 방수시공과 방근시공이 동시에 이루어지기 때문에 공사비를 현저하게 줄일 수 있고 공사기간도 훨씬 단축할 수 있다.
Further, in the present invention, since the waterproof sheet and the antistatic sheet made of the waterproof sheet and the antiperspirant sheet having different functions are used, one sheet can have both waterproof function and antinociceptive function, Since waterproofing and anti-glare are performed at the same time, the construction cost can be significantly reduced and the construction period can be shortened.
도 1은 본 발명에 따른 시공방법으로 시공한 구조의 단면도이다.
도 2는 방수·방근 일체형 시트의 단면도이다.
도 3은 조인트 방근보강재를 도시한 도면이다.1 is a cross-sectional view of a structure constructed by a construction method according to the present invention.
Fig. 2 is a sectional view of the waterproof / antistatic integrated sheet.
3 is a view showing a joint lateral reinforcement.
본 발명에 따른 복합 방수·방근구조의 시공방법의 가장 큰 기술적 특징은, 중심부를 제외한 양측 가장자리를 따라 일정 간격으로 천공되어 있고 PET 필름이 구비되어 만들어진 조인트 방근보강재를 시트가 맞대진 접합부에 접착시킴으로써, 시트가 이격된 접합부에서도 조인트 방근보강재에 의해 PET 필름이 계속 이어지게 하여 접합부에서의 방근 특성의 연속성을 확보하고, 맞대진 부분에 충전된 고경질우레탄 또는 FRP가 조인트 방근보강재의 양측 가장자리에 형성된 천공 구멍을 통해 올라와서 조인트 방근보강재의 상부에 도포한 고경질우레탄 또는 FRP과 합체되어 경화되면서 조인트 방근보강재와 시트 사이의 접착력을 더욱 향상시켜 접합부로 뿌리가 침투하는 것을 근원적으로 차단하게 했다는 점이다.
The most significant technical feature of the composite waterproofing and anti-skidding structure according to the present invention is that by bonding a joint web reinforcement made of a PET film, which is perforated at regular intervals along both side edges except for the center portion, The PET film is continued by the joint web reinforcement even at the joints where the sheets are spaced apart to ensure continuity of the characteristic of the joint at the joint portion and the high rigidity Urethane or FRP filled in the engaging portion is formed in the perforations The reinforcing material is brought into contact with the high rigidity urethane or FRP applied on the upper part of the joint web site reinforcement to harden the joint, thereby further improving the adhesion between the joint web reinforcement and the sheet, thereby preventing the roots from penetrating into the joint.
본 발명에 따른 복합 방수·방근구조의 시공방법은, 콘크리트 표면에 프라이머를 도포하여 프라이머층을 형성하는 단계, 프라이머층의 상부에 방수기능과 방근기능을 함께 구비하는 방수·방근 일체형 시트를 시트 단부(端部)가 일정 간격 이격되게 하여 접착시키는 단계, 접착된 상기 시트와 시트 사이에 접합부를 형성하는 단계, 접합부를 형성한 후에 방수·방근층 전체면의 상부에 합성수지를 도포하는 단계를 거쳐서 시공하며, 접합부에서는 시트(10)와 조인트 방근보강재(20) 및 합성수지 도막층(40)으로 3중층을 이루게 되어 더욱 강력한 접착력을 유지할 수 있게 된다.
A method of constructing a composite watertight and skid structure according to the present invention includes the steps of forming a primer layer by applying a primer to a concrete surface, forming a waterproof and antidotal integrated sheet having a waterproof function and an anti- A step of forming a joint between the bonded sheet and the sheet, a step of applying a synthetic resin to the entire surface of the waterproofing / antifogging layer after the joint is formed, In the joining portion, a triple layer is formed of the
접합부를 형성하는 단계에서는, 일정 간격만큼 이격되어 접착된 시트(10)와 시트(10) 사이에 고경질우레탄 또는 FRP(30)를 충전한 다음, 그 위에 양단(兩端)이 양측에 위치한 시트 각각에 위치하도록 하여 조인트 방근보강재(20)를 접착시킨 후 조인트 방근보강재(20)의 상부에 다시 고경질우레탄 또는 FRP를 도포하여 형성한다.
In the step of forming the joints, a high-hardness urethane or
조인트 방근보강재(20)는 길이방향을 따라 중심부에 천공 구멍(27)이 형성되어 있지 않기 때문에 천공되지 않은 부분이 시트(10)와 시트(10) 사이의 이격된 부분에 위치하게 되어 PET 필름의 연속성을 확보할 수 있게 된다. 따라서 방수·방근층을 형성한 전체 면에 걸쳐 동일한 재질의 PET 필름이 단절되지 않고 연속적으로 위치하게 되므로 방수·방근층을 뚫고 뿌리가 침투하지 못하도록 차단할 수 있게 된다.
Since the
조인트 방근보강재(20)는, 도 3에 도시한 바와 같이, 가운데 위치시킨 PET (Polyethylene Terephthalate) 필름(23)의 상부와 하부에 열경화성수지 접착제(22, 24)에 의해 부직포(21, 25)를 각각 접착시키고, 양측 가장자리에 길이방향을 따라 일정 간격으로 천공 구멍(27)을 형성하여 구성한 것이다.
3,
조인트 방근보강재(20)의 폭은 70∼120㎜이며, 천공 구멍(27)은 가장자리의 양측 10∼30㎜ 부분에 일정 간격으로 균등하게 형성된 것인데, 이와 같이 천공 구멍(27)을 형성함으로써 천공된 부분의 강성이 낮아지고 유연성이 증대되기 때문에 방수·방근층을 형성할 바탕면에 굴곡이 있더라도 굴곡면을 따라 유연하게 대처하여 조인트테이프(20)의 접착력을 현저하게 향상시킬 수 있다.
The width of the joint near
종래의 PET 필름을 사용한 테이프는 PET 필름이 뻣뻣하기 때문에 바탕면의 굴곡에 유연하게 대처할 수가 없어서, 결국 굴곡부에서 접합부가 들뜬 상태로 시공되게 되므로 접착력이 약해서 접합부를 통해 뿌리가 침투할 수 있는 문제점을 항시 갖고 있었다. 하지만, 본 발명의 조인트 방근보강재(27)는 상기와 같은 문제를 완전히 해결했을 뿐만 아니라 시트가 이격된 부분에 충전된 고경질우레탄 또는 FRP(30)가 천공 구멍(27)을 통해 올라와서 조인트 방근보강재(20)의 상부에 추가적으로 도포하는 고경질우레탄 또는 FRP와 합체되어 경화되면서 조인트 방근보강재(20)와 시트(10) 사이의 접착력을 더욱 향상시켜 주게 된다.Since the conventional PET film is stiff, the conventional PET film can not flexibly cope with the curvature of the ground surface. As a result, since the joint is excavated at the bent portion, the adhesive force is weak and the roots can penetrate through the joint portion I always had. However, not only the above-mentioned problem is completely solved, but also the joint rigid reinforcing
PET 필름(13, 23)은 경도가 높고 뻣뻣하기 때문에 두께가 두꺼우면 굽혀지기 어렵고 제품 단가도 상승하게 되므로, PET 필름(13, 23)의 두께는 0.02∼0.20㎜ 정도로 하는 것이 바람직하다.
Since the PET
방수·방근 일체형 시트(10)는, PET 필름(13)과, PET 필름(13)의 상부와 하부에 각각 접착제(12, 14)에 의해 접착된 부직포(11, 15)와, 상부가 PET 필름(13)의 하부에 접착된 부직포(15)에 함침된 고점착 연질형 자착식 콤파운드(16) 및 고점착 연질형 자착식 콤파운드(16)의 하부에 부착시킨 이형지(17)를 구비하여 구성된다.
The waterproof /
고점착 연질형 자착식 콤파운드(16)는 스트레이트 아스팔트 35∼60중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 5∼10중량부, 프로세스 오일 10∼20중량부, 접착부여제(전분) 1∼5중량부, 흡유제(화산재) 1∼5중량부, 충전재(돌로마이트) 5∼15중량부, 스테아린산 알미늄 3∼5중량부, 내산화 및 내균열 노화방지제 3∼5중량부, 특수첨가제 3∼5중량부로 구성된 것인데, '고점착', '연질'의 특성을 갖고 있어서 콘크리트 바탕면에 안정적으로 고착될 수 있을 뿐만 아니라 바탕면에 균열이 발생하더라도 콤파운드의 우수한 신장력으로 인해 시트가 파단되지 않고 방수·방근층을 유지되게 된다.
The high-adhesion soft-type
접착부여제(전분)는 고구마, 옥수수 등의 식물성 접착제로 피착면과의 접착성을 부여하기 위한 것이고, 흡유제(화산재)는 배합 성분 중 프로세스 오일이 표면으로 올라오는 것을 방지하기 위한 것이며, 충전재(돌로마이트)는 콤파운드 표면을 강화하고 강도를 보강하기 위한 것이며, 스테아린산 알미늄은 응집력 강화 및 열안정제 기능을 한다.The adhesive agent (starch) is for imparting adhesiveness to the adherend surface with a vegetable adhesive agent such as sweet potato or corn. The oil absorbent agent (ash material) is for preventing the process oil in the compounding ingredient from coming to the surface, (Dolomite) is to reinforce the compound surface and reinforce the strength, and aluminum stearate acts as cohesive strengthening and heat stabilizer.
시트의 산화 및 균열을 방지하기 위한 내산화 및 내균열 노화방지제는 PA(phenyl-α-naphthylamine), DCD(Substituted diphenylamine) 및 RD(trimethyl dihydroquinoline)를 같은 비율로 혼합한 것이다. 또한 특수첨가제는 고점착 접착력 강화와 흘러 내림을 방지하기 위한 것으로 검로진을 사용한다.
The anti-oxidation and anti-crack antioxidants to prevent oxidation and cracking of the sheet are a mixture of PA (phenyl-α-naphthylamine), DCD (Substituted diphenylamine) and RD (trimethyl dihydroquinoline) in the same ratio. In addition, special additive is used to strengthen high adhesive strength and to prevent flow down.
접착제(12, 14)는 PET 필름(13)의 상부와 하부에 위치하는 부직포(11, 15)가 PET 필름(13)에서 분리되지 않도록 접착시키기 위한 것인데, 시간이 지나더라도 접착력을 유지하기 위해서는 고점착 연질형 자착식 콤파운드의 성분 중에 있는 유성(油性)물질(즉, 오일 성분)의 영향으로 접착제의 기능이 상실되지 않아야 하므로, 본 발명에서는 접착제로 열경화성수지를 사용하는데, 열경화성수지는 폴리우레탄계수지에 금속카바이드를 배합한 것 또는 에폭시수지계를 사용한다.
The
PET 필름(13)과 부직포(11, 15)의 접착력을 향상시키기 위해서는 PET 필름(13) 양면에 코로나 방전 처리를 하여 기재(PET 필름)의 표면을 개질시키는데, PET 필름(13)의 양면에 코로나방전 처리를 하면 스크래치(scratch) 등이 형성되어 접착면적을 넓혀 주기 때문에 접착력이 현저하게 향상된다.
In order to improve the adhesion between the
옥상녹화의 경우 방수·방근시공이 마지막이 아니라 그 상부에 조경을 위한 추가공사가 진행되기 때문에 조경공사를 위해 방수·방근층 위로 작업자가 보행을 하고 성토(盛土)할 흙이나 조경석 등의 중량물이 운반 및 적재되는 과정에서 방수·방근시트가 훼손될 수도 있어서, 고경질우레탄 또는 FRP를 도포하여 접합부를 형성하고 난 다음, 방수·방근층을 형성한 전체 면의 상부에 합성수지 도막제를 도포하는 것이 바람직한데, 이때 합성수지는 폴리우레아수지, 우레탄수지, 불포화 폴리에스테르수지, 아크릴수지 중 어느 하나 또는 혼합하여 사용하는 것이 바람직하다.
In the case of rooftop greening, waterproofing and weatherproofing is not the last, but additional work is done for the landscaping above it. Therefore, for the landscaping work, the workers walk on the waterproof, The waterproofing and antifouling sheet may be damaged during transportation and loading, so that a high-hardness urethane or FRP is applied to form a joint, and then a synthetic resin coating agent is applied to the entire upper surface of the waterproofing / antifouling layer At this time, it is preferable to use a synthetic resin in combination with any one of a polyurea resin, a urethane resin, an unsaturated polyester resin, and an acrylic resin.
이와 같이 옥상에 노출공법으로 방수·방근층을 형성하고 난 다음 방수·방근층 전체 면의 상부에 합성수지를 도포해 두면, 옥상 방수·방근시공 공사가 끝난 후 상당기간(몇 개월 내지 몇 년)이 경과한 후에 옥상에 조경공사를 할 경우가 있더라도 별도의 방근시공을 하지 않고 곧바로 옥상녹화를 위한 조경공사를 할 수 있는 장점이 있다.
If you apply a synthetic resin to the upper part of the waterproofing and weatherproofing layer after forming the waterproofing and weatherproofing layer by the exposure method on the roof like this, a considerable period (several months to several years) after completion of the roof waterproofing / There is an advantage that the landscape construction for rooftop greening can be carried out directly without a separate route construction even if there is a case where the landscape construction is performed on the roof after passing.
이상의 설명은 본 발명을 예시적으로 설명한 것이고, 명세서에 게시된 실시예는 본 발명의 기술사상을 한정하기 위한 것이 아니라 설명하기 위한 것이므로 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명의 기술사상을 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 그러므로 본 발명의 보호범위는 청구범위에 기재된 사항에 의해 해석되고, 그와 균등한 범위 내에 있는 기술적 사항도 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention. Various modifications and variations will be possible without departing from the spirit of the invention. Therefore, the scope of the present invention should be construed as being covered by the scope of the appended claims, and technical scope within the scope of equivalents thereof should be construed as being included in the scope of the present invention.
10 : 시트 11, 15 : 부직포
12, 14 : 접착제 13 : PET 필름
16 : 고점착 연질형 자착식 콤파운드
17 : 이형지
20 : 조인트 방근보강재 21, 25 : 부직포
22, 24 : 접착제 23 : PET 필름
27 : 천공 구멍
30 : 고경질우레탄(또는 FRP)
40 : 합성수지 도막층10:
12, 14: Adhesive 13: PET film
16: high-adhesion soft-type adhesive compound
17: release paper
20:
22, 24: Adhesive 23: PET film
27: Perforation hole
30: High hard urethane (or FRP)
40: Synthetic resin coating layer
Claims (6)
상기 시공방법은,
콘크리트 표면에 프라이머를 도포하여 프라이머층을 형성하는 단계;
프라이머층의 상부에 방수기능과 방근기능을 함께 구비하고 자착 기능이 있는 방수·방근 일체형 시트를 시트 단부(端部)가 일정 간격 이격되게 하여 접착시키는 단계;
접착된 상기 시트와 시트 사이에 접합부를 형성하는 단계;
접합부를 형성한 후에 방수·방근층 전체면의 상부에 합성수지를 도포하는 단계;
를 거쳐서 시공하며, 상기 접합부를 형성하는 단계에서는, 일정 간격 이격된 시트와 시트 사이에 고경질우레탄 또는 FRP를 충전한 다음, 양단(兩端)이 양측에 위치한 시트 각각에 위치하도록 하여 조인트 방근보강재를 접착시킨 후 조인트 방근보강재의 상부에 다시 고경질우레탄 또는 FRP를 도포하여 형성하며,
상기 조인트 방근보강재는, 가운데 위치시킨 PET 필름의 상부와 하부에 열경화성수지 접착제에 의해 부직포를 각각 접착시키며, 양측 가장자리에 길이방향을 따라 일정 간격으로 천공 구멍을 형성한 것인 것을 특징으로 하는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법.
A method of simultaneously constructing a waterproof and antiperspirant structure using a waterproof / antiperspirant sheet,
The method includes:
Applying a primer to the concrete surface to form a primer layer;
A step of adhering a waterproof and antistatic integrated sheet having a waterproof function and an anticycling function on the top of the primer layer and having a sticking function such that end portions of the sheet are spaced apart from each other by a predetermined distance;
Forming a bond between the bonded sheet and the sheet;
Applying synthetic resin on the entire surface of the waterproofing / antifouling layer after forming the joint portion;
Rigid Urethane or FRP is filled between a sheet and a sheet spaced apart from each other by a predetermined distance and then both ends of the sheet are positioned on both sides of the sheet, Rigid urethane or FRP is applied to the upper part of the joint web site reinforcement,
Characterized in that the joint moving web reinforcement is made by bonding a nonwoven fabric to a top and a bottom of a PET film positioned at the center by a thermosetting resin adhesive and forming perforations at both side edges along the longitudinal direction at regular intervals A method of construction of composite waterproofing and reinforced concrete structure with improved adhesion of joints in triple layer structure by using joint joint reinforcement.
PET 필름;
상기 PET 필름의 상부와 하부에 열경화성수지 접착제에 의해 각각 접착된 부직포;
상부가 상기 PET 필름의 하부에 접착된 부직포에 함침된 고점착 연질형 자착식 콤파운드;
상기 고점착 연질형 자착식 콤파운드의 하부에 부착시킨 이형지;
를 구비하여 구성되고, 상기 고점착 연질형 자착식 콤파운드는,
스트레이트 아스팔트 35∼60중량부;
스틸렌 부타디엔 스틸렌 10∼20중량부;
부틸고무 5∼10중량부;
프로세스 오일 10∼20중량부;
접착부여제(전분) 1∼5중량부;
흡유제(화산재) 1∼5중량부;
충전재(돌로마이트) 5∼15중량부;
스테아린산 알미늄 3∼5중량부;
내산화 및 내균열 노화방지제 3∼5중량부;
검로진 3∼5중량부;
로 구성되는 것을 특징으로 하는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법.
The waterproof / antistatic integrated sheet according to claim 2,
PET film;
A nonwoven fabric bonded to the upper and lower sides of the PET film by a thermosetting resin adhesive;
A high-adhesion soft-type injection molded compound in which an upper portion is impregnated in a nonwoven fabric adhered to a lower portion of the PET film;
A releasing paper adhered to a lower portion of the high-adhesion soft-type compounding compound;
Wherein the high-adhesion soft-type compounded compound is composed of:
35 to 60 parts by weight of straight asphalt;
10 to 20 parts by weight of styrene-butadiene styrene;
5 to 10 parts by weight of butyl rubber;
10 to 20 parts by weight of a process oil;
1 to 5 parts by weight of an adhesive agent (starch);
1 to 5 parts by weight of an oil absorbent (ash);
5-15 parts by weight of a filler (dolomite);
3 to 5 parts by weight of aluminum stearate;
3 to 5 parts by weight of an anti-oxidation and anti-cracking antioxidant;
3 to 5 parts by weight of chewing gum;
The method of claim 1 or 2, wherein the reinforcing member is made of a perforated joint.
상기 합성수지는 폴리우레아수지, 우레탄수지, 불포화 폴리에스테르수지, 아크릴수지 중 어느 하나인 것을 특징으로 하는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법.
3. The method of claim 2,
Wherein the synthetic resin is one of a polyurea resin, a urethane resin, an unsaturated polyester resin, and an acrylic resin. The present invention relates to a composite waterproofing / anticorrosive construction method in which a bonded structure is improved in a triple layer structure using a perforated joint web reinforcement .
상기 조인트테이프의 폭은 70∼120㎜이며, 천공 구멍은 가장자리의 양측 10∼30㎜ 부분에 일정 간격으로 형성되는 것을 특징으로 하는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법.
3. The method of claim 2,
Wherein the joint tape has a width of 70 to 120 mm and the perforation holes are formed at intervals of 10 to 30 mm on both sides of the edge at a predetermined interval. Construction method of combined waterproofing and anti-skid structure.
상기 PET 필름의 두께는 0.02∼0.20㎜인 것을 특징으로 하는 천공된 조인트 방근보강재를 사용하여 3중층 구조로 접합부 접착력을 향상시킨 복합 방수·방근구조의 시공방법.The method according to claim 2 or 3,
Wherein the thickness of the PET film is 0.02 to 0.20 mm. The method of claim 1, wherein the thickness of the PET film is 0.02 to 0.20 mm, and the adhesive strength of the joint is improved by a triple layer structure using the perforated joint web reinforcement.