KR101422268B1 - A Process for Preparing Eco-friendly Paper - Google Patents

A Process for Preparing Eco-friendly Paper Download PDF

Info

Publication number
KR101422268B1
KR101422268B1 KR1020120081844A KR20120081844A KR101422268B1 KR 101422268 B1 KR101422268 B1 KR 101422268B1 KR 1020120081844 A KR1020120081844 A KR 1020120081844A KR 20120081844 A KR20120081844 A KR 20120081844A KR 101422268 B1 KR101422268 B1 KR 101422268B1
Authority
KR
South Korea
Prior art keywords
paper
environmentally friendly
present
pulp
water
Prior art date
Application number
KR1020120081844A
Other languages
Korean (ko)
Other versions
KR20140014815A (en
Inventor
이진오
Original Assignee
이진오
김정동
홍석호
정해수
김경식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이진오, 김정동, 홍석호, 정해수, 김경식 filed Critical 이진오
Priority to KR1020120081844A priority Critical patent/KR101422268B1/en
Publication of KR20140014815A publication Critical patent/KR20140014815A/en
Application granted granted Critical
Publication of KR101422268B1 publication Critical patent/KR101422268B1/en

Abstract

본 발명의 환경친화지의 제조방법은, 상지(上紙)인 돌종이와, 하지(下紙)인 펄프지, 그의 재생지, 또는 폴리프로필렌(PP)지의 일면에 아크릴 에멀젼(A/E) 50%(w/w), 알긴산 소다 7%(w/w), 전분 5%(w/w), 셀룰로우즈 7%(w/w), 방부제 0.2%(w/w), 소포제 0.2%(w/w), 이온조절 및 침투제 5.1%(w/w), 및 물 25.5%(w/w)로 구성된 접착제를 도포하고 서로 부착함으로써 합지(合紙)하고 건조하는 공정을 포함한다. 본 발명은 돌종이가 가진 장점과 돌종이의 단점을 보완 및 개선함으로써, 인쇄성, 내수성, 내유성, 내화학성 및 내구성이 뛰어날 뿐만 아니라, 제조과정에서 나무를 전혀 사용하지 않아 자연생태계를 보호하고, 소각시 대기오염 물질이나 이산화탄소를 배출하지 않는 등 친환경적이고 천연재료로서의 고급스러운 질감을 지닌 벽지, 쇼핑백, 포장용 박스, 봉투 등 범용적으로 사용될 수 있는 합지를 제공한다.The method for producing an environmentally friendly paper of the present invention is a method for producing an environmentally friendly paper comprising 50% of an acrylic emulsion (A / E) on a surface of a staple paper as an upper paper, a pulp paper as a lower paper, (w / w), sodium alginate 7% (w / w), starch 5% (w / w), cellulose 7% (w / w), preservative 0.2% (w / w), ion control and 5.1% (w / w) of a penetrating agent, and 25.5% (w / w) of water and adhering them to each other. The present invention is not only excellent in printability, water resistance, oil resistance, chemical resistance and durability, but also protects a natural ecosystem by not using any wood in the manufacturing process, It provides environmentally friendly and liquefied paper that can be used for general purposes such as wallpaper, shopping bag, packing box, and envelope, which have high quality textures as a natural material and do not emit air pollutants or carbon dioxide during incineration.

Description

환경친화지의 제조방법{A Process for Preparing Eco-friendly Paper}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a process for preparing an eco-

본 발명은 돌가루(탄산칼슘, CaCO3)를 주원료로 하는 원지(이하, "돌종이"라 함)와, 펄프(pulp)를 주원료로 하는 원지(이하, "펄프지"라 함), 그의 재생지 또는 PP(polypropylene) 원단(이하, "PP지"라 함)을 접착제를 이용하여 합지(合紙)함으로써, 벽지, 쇼핑백, 포장용 박스, 봉투 등에 사용하는 환경친화지를 제조하는 방법에 관한 것이다.
The present invention relates to a paper making method comprising the steps of mixing a raw paper (hereinafter referred to as "paper") made of stone powder (calcium carbonate, CaCO 3 ) as a main raw material, a raw paper (hereinafter referred to as "pulp paper" A shopping bag, a packaging box, an envelope, etc. by laminating recycled paper or PP (polypropylene) fabric (hereinafter referred to as "PP paper") using an adhesive.

일반적으로, 돌종이는 나무를 주원료로 하는 펄프를 사용하지 않고, 돌가루(stone powder, CaCO3 , 70~80%)와 폴리에틸렌(PE, 20~30%)을 주재로 포함하고 상기 두가지 원료의 융합을 위한 첨가제(1~3%)를 혼합한 무-펄프(pulp-free) 환경친화적 종이를 일컫는다. 돌종이는 다양한 인쇄기법의 구사가 가능하며, 내유성, 내화학성 및 내구성이 우수하고, 인체에 무해하며, 지구상에 풍부한 돌가루를 주원료로 사용하므로, 종래의 펄프를 주재로 한 종이보다 간단한 공정에 의해 경제적으로 제조될 수 있다.Generally, stone paper does not use wood pulp but mainly contains stone powder (CaCO 3 , 70 ~ 80%) and polyethylene (PE, 20 ~ 30%) and the two raw materials Refers to a pulp-free environmentally friendly paper in which additives for fusing (1-3%) are mixed. Stone paper can be used in a variety of printing techniques. It is superior in oil resistance, chemical resistance and durability, harmless to human body, and uses stone powder which is abundant on the earth as its main material. Can be manufactured economically.

특히, 기존 펄프지 1M/T(metric ton)을 생산하기 위해서는, 약 23그루의 큰 나무에 해당하는 4M/T의 펄프 칩(pulp chip)이 소요되는데 반하여, 돌종이는 제조과정에서 나무를 전혀 사용하지 않아 자연생태계를 보호하고, 물, 표백제, 강한 산성 및 알칼리계 화학 약품을 사용하지 않음으로써 수질 및 대기 오염을 저감시킨다. 또한, 돌종이의 제조공정은 펄프지의 제조에 비하여 약 68%, 재생지 제조에 비하여 약 39%만의 에너지를 사용하므로, 과다한 에너지 사용으로 인한 환경파괴를 현저히 감소시킨다. 더구나, 돌종이는 직사광선 아래에서 광분해(photo-degradable)되며, 소각처리시 유해 대기오염 물질이나 이산화탄소를 배출하지 않고, 펄프지보다 단순한 분해 및 펠렛화 공정을 통해 재활용이 용이하다는 장점이 있다.
In particular, in order to produce 1M / T (metric ton) of conventional pulp paper, pulp chips of 4M / T corresponding to about 23 large trees are required. On the contrary, It protects the natural ecosystem because it is not used and reduces water and air pollution by not using water, bleach, strong acid and alkali chemicals. In addition, the manufacturing process of the stonepaper uses about 68% of energy compared with the production of pulp paper, and uses only about 39% of energy compared with the production of recycled paper, thereby significantly reducing environmental destruction due to excessive energy use. In addition, stone paper is photo-degradable under direct sunlight and has the advantage that it is easier to recycle through decomposition and pelletizing process than pulp paper, without releasing harmful air pollutants or carbon dioxide during incineration process.

이와 같이, 돌종이는 친환경 및 에너지 절감 등 여러가지 장점이 있음에도 불구하고, 지금까지 돌종이 만의 기능 및 용도로 개발되어 쇼핑백, 포장용 박스, 봉투 등에 한정되어 사용되었는데, 그 이유로는 기존 펄프지의 물성과 비교하여 신축성 및 팽창성 과다로 후가공 공정상의 어려움이 있으며, 고시성(종이의 직립성, 흐느적거림이 큼)이 낮고, 밀도가 2.7~1.2배로 높아 같은 중량(평량, 1 metric meter당 g수)의 펄프 원지와 비교할 때, 상품화 및 대중화에 상당한 어려움이 있다는 점을 들 수 있다. Although stone papers have various advantages such as environmental friendliness and energy saving, they have been developed only for the functions and applications of stone papers and have been used for shopping bags, packing boxes, envelopes and the like. And the density is 2.7 to 1.2 times higher than that of the pulp raw paper of the same weight (basis weight, gram per 1 metric meter) , There are considerable difficulties in commercialization and popularization.

그럼에도 불구하고, 상술한 돌종이의 장점을 그대로 유지하면서 돌종이의 물리적 특성을 보완하기 위한 노력은 전무하였는바, 본 발명자들은 이러한 노력의 일환으로 돌종이와, 펄프지, 그의 재생지 또는 PP지를 합지함으로써, 돌종이의 물리적 특성을 보완하여 범용적으로 사용할 수 있는 신규한 환경친화지를 제조하기에 이르렀다.
Nevertheless, there has been no effort to supplement the physical properties of the stone paper while maintaining the merits of the stone paper described above. As a part of this effort, the present inventors have made efforts to improve the physical properties of the stone paper by using stone paper, pulp paper, Thereby completing the physical properties of the stone papers and producing new environmentally friendly papers which can be used universally.

본 발명자들은 종래의 벽지용(합지벽지) 접착제는 폴리비닐 알콜(polyvinyl alcohol, PVA)을 베이스로 아크릴 에멀젼을 5∼15% 첨가하여 접착성을 증진시키나, 결정적으로 합지를 제조하는데 있어서 가장 중요시되는 요소 중 하나인 내수성이 약하다는 결함을 가지고 있어, 돌종이를 포함하는 합지가 상품화되지 않고 있음에 주목하였다. 구체적으로, 종래의 벽지용(합지벽지) 접착제는 펄프지와 펄프지를 부착하는 데는 문제가 없으나, 한 면은 펄프지로 또 한 면은 자연분해가 가능한 필름 형태의 돌종이로 합지하는 경우, 원단의 물성이 펄프지와 달라 내수성에 약하다는 문제점을 야기시키는바, 친환경 가교형 아크릴 에멀젼(acryl emulsion)을 주성분으로 포함하고, 여기에 이온성 및 침투성을 추가로 고려한 접착제를 사용하여 합지함으로써, 내수성의 문제를 해결할 수 있음을 알아내었다.
The inventors of the present invention found that the conventional adhesive for wallpaper (wallpaper) improves adhesiveness by adding 5 to 15% of acrylic emulsion based on polyvinyl alcohol (PVA), but the most important Which is one of the elements, has a weak water resistance, and it has been noted that the lumber including the stone paper is not commercialized. Specifically, the conventional adhesive for wallpaper (wallpaper) has no problem in attaching pulp paper and pulp paper. However, when the paper is laminated with pulp paper on one side and film-type stone paper on which another side can be decomposed spontaneously, It has a problem that the physical properties are different from those of pulp paper and that it is weak in water resistance. As a result, it is possible to provide a water-repellent, water- I found that I could solve the problem.

본 발명은 상술한 바와 같은 점을 감안하여 안출한 것으로, 상지(上紙)인 돌종이와, 하지(下紙)인 펄프지, 그의 재생지 또는 PP지의 일면을 특유의 성분 및 성분비로 배합된 접착제를 도포하고 서로 부착함으로써, 내수접착성이 매우 우수하면서도 작업성 및 안정성이 담보되는 합지(合紙)의 제조방법을 알아내고, 본 발명을 완성하게 되었다.
Disclosure of the Invention The present invention has been made in view of the above-mentioned points, and an object of the present invention is to provide a papermaking paper which is an upper paper, a pulp paper which is a lower paper, The present inventors have found out a method for producing a slip sheet which is excellent in workability and stability while having excellent water-resistant adhesiveness, and completed the present invention.

결국, 본 발명의 주된 목적은 돌종이와, 펄프지, 그의 재생지 또는 폴리프로필렌(PP)지의 일면을 접착제를 도포하고 서로 부착하여 합지함으로써 환경친화지를 제조하는 방법을 제공하는 것이다.
As a result, a main object of the present invention is to provide a method for producing an environmental friendly paper by applying an adhesive to one side of a stone paper, a pulp paper, a recycled paper thereof or a polypropylene (PP) paper and laminating them together.

본 발명의 환경친화지의 제조방법은, The method for producing an environmental friendly paper of the present invention comprises:

상지(上紙)인 돌종이와, 하지(下紙)인 펄프지, 그의 재생지 또는 PP지의 일면에 아크릴 에멀젼(A/E) 50%(w/w), 알긴산 소다 7%(w/w), 전분 5%(w/w), 셀룰로우즈 7%(w/w), 방부제 0.2%(w/w), 소포제 0.2%(w/w), 이온조절 및 침투제 5.1%(w/w) 및 물 25.5%(w/w)로 구성된 접착제를 도포하고 서로 부착함으로써 합지(合紙)하고 건조하는 공정을 포함한다. 이때, 상지로는 0.05~0.20mm 두께 및 60~200gsm(gram per square meter) 평량 규격의 돌종이를 사용하는 것이 바람직하다. 또한, 상기 환경친화지의 제조방법의 합지공정 이후에, 상지인 돌종이의 전체 또는 부분에 인쇄하고 합지를 건조시킨 다음, 인쇄 및 건조가 완료된 합지에 소정의 무늬를 넣는 엠보싱 또는 재단하는 가공 공정을 추가로 포함할 수도 있다.
50% (w / w) of an acrylic emulsion (A / E), 7% (w / w) of sodium alginate was applied on one side of a recycled paper or PP paper, , 5% w / w starch, 7% w / w cellulite, 0.2% w / w preservative, 0.2% w / w defoamer, 5.1% w / And 25.5% (w / w) of water, and adhering them to each other, followed by laminating and drying. At this time, it is preferable to use stone paper having a thickness of 0.05 to 0.20 mm and a basis weight of 60 to 200 gsm (gram per square meter) as the upper part. Further, after the laminating process of the above-described method for producing an environmentally friendly paper, embossing or cutting is performed by printing on the whole or part of the uppermost staple paper, drying the laminated paper, and then printing and drying the finished laminated paper with a predetermined pattern And may be further included.

이하, 첨부된 도면을 참조하여, 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 일 실시예에 따른 상지인 돌종이와, 하지인 펄프지, 그의 재생지 또는 PP지를 접착제에 의해 부착하는 합지공정(S1) 및 상기 합지를 인쇄, 건조, 엠보싱 및 재단하는 가공공정(S2)을 순서적으로 도시한 공정도이다.Fig. 1 is a schematic view showing a lamination process (S1) for adhering a top paper, a bottom paper, a pulp paper, a recycled paper or PP paper thereof with an adhesive, and a process for printing, drying, embossing and cutting the laminated paper according to an embodiment of the present invention And step (S2) are sequentially shown.

도 1에 도시된 바와 같이, 본 발명에 따른 환경친화지의 제조방법은. As shown in FIG. 1, the method for producing an environmentally friendly paper according to the present invention comprises:

돌종이를 상지로 하고, 펄프지, 그의 재생지 또는 PP지를 하지로 하는 소정의 합지 준비단계(S1-1)와, A predetermined lint preparation step (S1-1) in which the staple paper is used as the upper, and the pulp paper, the recycled paper or the PP paper is not used,

준비된 상지 또는 하지의 일면을 접착제로 도포하고 서로 부착함으로써 접착하는 단계(S1-2)와, (S1-2) of applying one surface of the prepared upper or lower surface with an adhesive and sticking them together,

접착된 합지를 건조시키는 건조단계(S1-3)를 포함한다.
And a drying step (S1-3) of drying the bonded laminated paper.

선택적으로, 상술한 바와 같이 제조된 환경친화지는 합지의 용도 및 목적에 따라 가공공정(S2)으로서,Alternatively, the environmentally friendly fabric produced as described above may be used as a processing step (S2)

상지인 돌종이의 전체 또는 부분에 인쇄하는 인쇄단계(S2-1)와, A printing step (S2-1) of printing on the whole or a part of the top sheet,

인쇄된 합지를 건조시키는 인쇄건조 단계(S2-2)와, A printing and drying step (S2-2) of drying the printed lumber,

인쇄 및 건조가 완료된 합지에 소정의 무늬를 넣는 엠보싱 단계(S2-3)와, An embossing step (S2-3) of inserting a predetermined pattern into a laminate in which printing and drying are completed,

소정의 규격에 따라 절단하는 재단 단계(S2-4)를 추가로 포함할 수도 있다.
And a cutting step S2-4 for cutting according to a predetermined standard.

구체적으로, 상기 합지공정(S1)은 당업계에서 통상적으로 사용되는 합지기에 소정의 규격에 따라 롤 단위로 합지를 거치하는 합지 준비단계(S1-1)와, 0.05~0.20mm 두께 및 60~200gsm(gram per square meter) 평량 규격의 돌종이를 상지(上紙)로, 최종 합지의 용도 및 목적에 부합하는 평량 규격의 펄프지, 그의 재생지 또는 PP지를 하지(下紙)로 하여, 본 발명에 따른 접착체를 도포하고 합지기를 통해 서로 부착하는 합지 접착단계(S1-2)와, 부착된 종이를 열챔버(heat chamber)에서 열풍을 이용하여 건조시키거나 또는 열로라(heated roller)로 직접 열을 전달하여 건조시키는 합지 건조단계(S1-3)를 포함한다.Specifically, the laminating step (S1) includes a laminating step (S1-1) of laminating a laminate in a roll unit according to a predetermined standard to a papermaking machine commonly used in the art, The paper of the basis weight of 200 gsm (gram per square meter) was used as the upper paper, and the pulp paper of the basis weight conforming to the purpose and purpose of the final paper, the recycled paper thereof or the PP paper was used as the lower paper, (S1-2) of applying a bonding agent according to the present invention and attaching the same to each other through a bonding machine, and drying the attached paper by using hot air in a heat chamber or by direct heating with a heated roller And a joint drying step (S1-3) in which heat is transferred and dried.

한편, 선택적 가공공정(S2)은 상기 합지공정(S1)을 통해 제조된 합지의 용도 및 목적에 따라 상지인 돌종이 전체 또는 부분을 인쇄하는 단계(S2-1)와, 인쇄된 합지를 건조시키는 인쇄건조 단계(S2-2)와, 인쇄 및 건조가 완료된 합지에 무늬를 넣는 엠보싱 단계(S2-3)와, 소정의 재단규격에 따라 절단하는 재단 단계(S2-4)를 포함한다.
On the other hand, the selective processing step (S2) includes a step (S2-1) of printing all or part of the staple paper which is the upper staple in accordance with the purpose and purpose of the staple produced through the stapling step (S1) A printing and drying step (S2-2), an embossing step (S2-3) of inserting a pattern into the laminated fabric after printing and drying, and a cutting step (S2-4) of cutting in accordance with a predetermined cutting standard.

상술한 본 발명의 제조방법에 의해 제조된 합지의 구성을 도 2에 도시하였다. 도 2는 본 발명의 일 실시예에 따른 상지인 돌종이와, 하지인 펄프지, 그의 재생지 또는 PP지를 접착제에 의해 부착하고 상지에 인쇄한 합지의 구성을 모식적으로 도시한 단면도이다.
Fig. 2 shows the structure of the laminate produced by the manufacturing method of the present invention described above. FIG. 2 is a cross-sectional view schematically showing a structure of a top sheet, a bottom sheet of pulp paper, a recycled paper of the bottom paper, or a PP paper adhered thereto with an adhesive and printed on the upper side according to an embodiment of the present invention.

본 발명은 돌종이가 가진 장점과 돌종이의 단점을 보완 및 개선해 줄 수 있는 펄프지, 그의 재생지 또는 PP지를 상기 돌종이와 함께 합지함으로써, 인쇄성, 내수성, 내유성, 내화학성 및 내구성이 뛰어날 뿐만 아니라, 제조과정에서 나무를 전혀 사용하지 않아 자연생태계를 보호하고, 소각시 대기오염 물질이나 이산화탄소를 배출하지 않는 등 친환경적이고 천연재료로서의 고급스러운 질감을 지닌 벽지, 쇼핑백, 포장용 박스, 봉투 등 범용적으로 사용될 수 있는 합지를 제공한다.
The present invention is excellent in printability, water resistance, oil resistance, chemical resistance and durability by combining pulp paper, recycled paper or PP paper, which can complement and improve the disadvantages of stone paper, It is environment-friendly and has a luxurious texture as a natural material such as wallpaper, shopping bag, packing box, envelope etc. It protects the natural ecosystem by not using any trees at the manufacturing process and does not emit air pollutant or carbon dioxide during incineration. Lt; RTI ID = 0.0 > a < / RTI >

도 1은 본 발명의 일 실시예에 따른 상지인 돌종이와, 하지인 펄프지, 그의 재생지 또는 PP지를 접착제에 의해 부착하는 합지공정 및 상기 합지를 인쇄, 건조, 엠보싱 및 재단하는 가공공정을 순서적으로 도시한 공정도이다.
도 2는 본 발명의 일 실시예에 따른 상지인 돌종이와, 하지인 펄프지, 그의 재생지 또는 PP지를 접착제에 의해 부착하고 상지에 인쇄한 합지의 구성을 모식적으로 도시한 단면도이다.FIG. 1 is a schematic view showing the process of printing, drying, embossing and cutting the laminated paper according to an embodiment of the present invention, a lamination process of attaching a base paper, a pulp paper, a recycled paper or a PP paper thereof with an adhesive, This is a process diagram shown in a book.
FIG. 2 is a cross-sectional view schematically showing a structure of a top sheet, a bottom sheet of pulp paper, a recycled paper of the bottom paper, or a PP paper adhered thereto with an adhesive and printed on the upper side according to an embodiment of the present invention.

이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위한 것으로, 본 발명의 요지에 따라 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 당해 기술분야에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
Hereinafter, the present invention will be described in more detail with reference to Examples. It is to be understood that both the foregoing description and the following detailed description are exemplary, explanatory and are intended to be illustrative, and not restrictive. The scope of the invention is defined by the appended claims rather than by the foregoing description. will be.

실시예 1~7: 상지와 하지를 부착하기 위한 접착제의 제조 및 합지
 Examples 1 to 7 : Preparation of an adhesive for attaching the upper and lower limbs and lumber

우선, 상지와 하지를 부착하기 위한 접착제를 다음 표 1과 같은 원료 성분의 비율로 배합하여 제조하였다.
First, an adhesive for attaching the upper and lower limbs was prepared by blending the raw material components as shown in Table 1 below.

접착제의 성분 및 성분비(단위: %(w/w))Component and composition ratio of adhesive (unit:% (w / w)) 원 료Raw material 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 실시예 6Example 6 실시예 7Example 7 A/EA / E 70   70 60  60 30  30 50  50 50  50 50  50 50  50 알긴산 소다Alginate soda 10  10 20  20 10  10 10  10 7   7 7   7 전분Starch 5   5 15  15 10  10 7   7 5   5 5   5 셀룰로우즈Cellulosic 4   4 10  10 10  10 10  10 5   5 7   7 방부제antiseptic 0.2   0.2 0.2   0.2 0.2   0.2 0.2   0.2 0.2   0.2 0.2   0.2 소포제Defoamer 0.2   0.2 0.2   0.2 0.2   0.2 0.2   0.2 0.2 0.2 0.2 0.2 이온 조절 및 침투제Ion control and penetration agent 5.1   5.1 5.1   5.1 5.1   5.1 5.1   5.1 5.1   5.1 5.1   5.1 물water 30   30 15.5  15.5 19.5  19.5 14.5  14.5 17.5  17.5 27.5  27.5 25.5  25.5 계system 100  100 100 100 100 100 100 100 100 100 100 100 100 100

* A/E; 아크릴 에멀젼
* A / E; Acrylic emulsion

이어, 상기 표 1에 기재된 바와 같이 배합한 접착제를 돌종이와 펄프지의 일면에 도포하고 서로 부착함으로써 합지(合紙)하였다. 구체적으로, 0.10mm 두께 및 150gsm(gram per square meter) 평량 규격의 돌종이를 상지로 하고 펄프지(크라프트지, 아트원제지(주))를 하지로 하여, 상기 표 1에 기재된 바와 같은 비율로 배합한 접착제를 상지 또는 하지의 일면에 1m2 당 15g의 비율로 도포하고 합지기를 이용하여 서로 부착한 다음, 최종적으로 합지된 종이를 열챔버를 이용하여 건조시켜, 환경친화지를 제조하였다.
Then, an adhesive compounded as shown in Table 1 was applied to one side of a stone paper and pulp paper, and they were attached to each other to form a laminate. Concretely, a paper having a thickness of 0.10 mm and a basis weight of 150 gsm (gram per square meter) was used as a top paper and pulp paper (Kraft Paper, Art One Paper Co., Ltd.) The compounded adhesive was applied to one surface of the upper or lower surface of the base paper at a ratio of 15 g per 1 m 2 , adhered to each other using a pliing machine, and finally, the plied paper was dried using a heat chamber to prepare an environmentally friendly paper.

이어, 아래와 같은 판정기준으로 작업성, 안정성, 내수접착성 등을 측정하고, 이를 종래의 아크릴계(acrylic) 접착제(아크릴 접착제, (주)디에스켐)로 합지한 경우(비교실시예)와 비교하였다.
Then, the workability, stability, water resistance and the like were measured by the following criteria and compared with the case of using a conventional acrylic adhesive (acrylic adhesive, Dicchem Co., Ltd.) (Comparative Example) .

본 발명(실시예 1 내지 실시예 7) 및 종래의 접착제(비교 실시예)로 부착된 합지의 작업성, 안정성, 내수접착성The workability, stability, and water resistance of the laminate adhered with the present invention (Examples 1 to 7) and conventional adhesives (Comparative Examples) 측정항목Metrics 비교
실시예compare
Example 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 실시예 6Example 6 실시예 7Example 7 작업성Workability 33 33 33 33 44 44 44 55 안정성stability 22 33 33 33 44 44 55 55 내수접착성Water resistance 20분20 minutes 33 22 22 22 33 33 44 55 1시간1 hours 33 1One 22 22 22 33 44 55 5시간5 hours 33 1One 22 22 22 22 33 55 24시간24 hours 22 1One 1One 22 22 22 33 55

작업성 및 안정성Workability and stability 판정기준Criteria 내수접착성 판정 기준Water-based adhesion judgment criteria

5...매우 양호 5...한쪽 면에 100% 전이        5 ... very good 5 ... 100% transition on one side

4...양호 4...90%이상 한쪽 면에 전이         4 ... Good 4 ... More than 90% Transition to one side

3...현장사용 문제없음 3...85%이상 한쪽 면에 전이        3 ... No problem with field use 3 ... More than 85% Transition to one side

2...문제발생 2...50%이상 한쪽 면에 전이        2 ... problem occurred 2 ... more than 50% transition on one side

1...사용불가 1...20분만에 완전 박리        1 ... not available 1 ... complete peeling in 20 minutes

상기 표 2에서 보듯이, 실시예 7이 작업성, 안정성, 내수접착성 등의 측면에서 가장 적합한 결과를 얻었는 바, 아크릴 에멀젼(A/E) 50%(w/w), 알긴산 소다 7%(w/w), 전분 5%(w/w), 셀룰로우즈 7%(w/w), 방부제 0.2%(w/w), 소포제 0.2%(w/w), 이온조절 및 침투제 5.1%(w/w) 및 물 25.5%(w/w)로 구성된 접착제가 본 발명의 환경친화지의 제조에 가장 적합하며, 상기 각 배합비율을 벗어난 접착제로 제조된 합지는 상기 측정항목의 측면에서 바람직하지 않음을 알 수 있었다.     As shown in Table 2, the most suitable results were obtained in terms of workability, stability, and water resistance of the adhesive in Example 7. As a result, the acrylic emulsion (A / E) 50% (w / w) and the alginic acid 7% w / w starch 5% w / w cellulite 7% w / w preservative 0.2% w / w defoamer 0.2% w / w / w) and 25.5% (w / w) of water are most suitable for the production of the environmentally friendly paper of the present invention, and the laminates made of the adhesive out of the respective blend ratios are not preferable in view of the above measurement items And it was found.


Claims (3)

상지(上紙)인 돌종이와, 펄프지, 그의 재생지 및 폴리프로필렌(PP)지로 구성되는 그룹으로부터 선택되는 어느 하나인 하지(下紙)의 일면에 아크릴 에멀젼(A/E) 50%(w/w), 알긴산 소다 7%(w/w), 전분 5%(w/w), 셀룰로우즈 7%(w/w), 방부제 0.2%(w/w), 소포제 0.2%(w/w), 이온조절 및 침투제 5.1%(w/w), 및 물 25.5%(w/w)로 구성된 접착제를 도포하고 서로 부착함으로써 합지(合紙)하고 건조하는 공정을 포함하는 환경친화지의 제조방법.
50% (w / w) of an acrylic emulsion (A / E) is coated on one surface of a lower sheet of a lower sheet which is selected from the group consisting of a staple paper which is an upper sheet and a recycled paper and a polypropylene (PP) w / w), sodium alginate 7% w / w starch 5% w / w cellulose 7% w / w preservative 0.2% w / w defoamer 0.2% ), Applying an adhesive composed of 5.1% (w / w) of ion control and penetration agent, and 25.5% (w / w) of water and attaching them to each other.
제1항에 있어서.
상지(上紙)로는 0.05~0.20mm 두께 및 60~200gsm(gram per square meter)의 평량 규격의 돌종이를 사용하는 것을 특징으로 하는
환경친화지의 제조방법.
The method of claim 1,
And a stone paper having a basis weight of 0.05 to 0.20 mm in thickness and 60 to 200 gsm (gram per square meter) is used as the upper paper
Method of manufacturing environmentally friendly paper.
제1항에 있어서.
상기 제조된 합지의 상지(上紙) 면에 인쇄하고 건조시킨 다음, 무늬를 넣고 재단하는 가공 공정을 추가로 포함하는
환경친화지의 제조방법 .
The method of claim 1,
A process of printing and drying on the upper surface of the prepared laminate and then cutting and cutting the laminate
Method of manufacturing environmentally friendly paper.
KR1020120081844A 2012-07-26 2012-07-26 A Process for Preparing Eco-friendly Paper KR101422268B1 (en)