KR101406761B1 - Cleaning solution composition and the cleaning method therewith - Google Patents
Cleaning solution composition and the cleaning method therewith Download PDFInfo
- Publication number
- KR101406761B1 KR101406761B1 KR1020120117424A KR20120117424A KR101406761B1 KR 101406761 B1 KR101406761 B1 KR 101406761B1 KR 1020120117424 A KR1020120117424 A KR 1020120117424A KR 20120117424 A KR20120117424 A KR 20120117424A KR 101406761 B1 KR101406761 B1 KR 101406761B1
- Authority
- KR
- South Korea
- Prior art keywords
- cleaning
- cleaning liquid
- liquid composition
- copper
- composition
- Prior art date
Abstract
본 발명은 구리 연마 (화학적 기계적 연마, Chemical Mechanical Polishing, CMP) 공정 후 사용되는 세정액 조성물 및 이를 이용한 세정방법에 관한 것으로서, 본 발명의 세정액 조성물은, 4급 암모늄 화합물을 포함하는 유기물질 제거제; 알칸올 아민 또는 수산화 아민을 포함하는 포토레지스트 또는 폴리머 잔사 제거제; 5-아미노테트라졸, 요산 (Uric acid), 히드라진, 벤조티아졸, 벤조트리아졸 및 1,2,4-트리아졸로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 부식방지제; 및 순수 (純水);를 포함한다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning liquid composition used after a copper polishing (Chemical Mechanical Polishing, CMP) process and a cleaning method using the same, wherein the cleaning liquid composition of the present invention comprises an organic material remover including a quaternary ammonium compound; Photoresist or polymer residue removers comprising alkanolamines or hydroxylamines; A corrosion inhibitor comprising at least one selected from the group consisting of 5-aminotetrazole, uric acid, hydrazine, benzothiazole, benzotriazole and 1,2,4-triazole; And pure water.
Description
본 발명은 구리를 포함하는 금속배선의 CMP 공정 또는 에칭 공정 후 사용되는 세정액 조성물 및 이를 이용한 세정방법에 관한 것이다.
BACKGROUND OF THE
반도체 공정에서 배선의 선폭이 점차 감소함에 따라, 배선의 단면적 감소로 인해 저항이 증가되고 배선간 간격 감소로 인해 신호의 지연이 발생한다. 이러한 신호 지연을 줄이기 위해서, 배선의 소재는 낮은 비저항 특성을 가지는 구리 (Cu)로, 절연층 (dielectric)은 더 낮은 유전 상수를 갖는 물질로 대체되고 있다.As the line width of the wiring gradually decreases in the semiconductor process, the resistance is increased due to the reduction of the cross-sectional area of the wiring, and the signal is delayed due to the reduction of the wiring interval. In order to reduce this signal delay, the material of the wiring is replaced by copper (Cu) with low specific resistivity and the dielectric is replaced by a material with a lower dielectric constant.
그런데, 기존의 텅스텐(W)과 알루미늄 (Al) 배선 형성 공정에서 사용되던 건식 식각 (dry etch back) 공정을 구리 배선 형성 과정에 적용하면, 구리와 염소 (Cl)가 반응하여 휘발성이 낮은 구리-염소 착물 (complex)이 형성된다. 상기 구리-염소 착물은 기판 표면에 잔류하여 식각을 방해하는 장애물로 작용함으로써 패턴을 형성하는데 문제를 야기한다.However, when a dry etch back process used in a conventional tungsten (W) and aluminum (Al) wiring forming process is applied to a copper wiring forming process, copper reacts with chlorine (Cl) A chlorine complex is formed. The copper-chlorine complex remains on the surface of the substrate and acts as an obstacle that interferes with the etching, thereby causing a problem in forming a pattern.
이를 극복하기 위해, 화학적 기계적 연마 (Chemical Mechanical Polishing: CMP) 공정이 도입되었다. 즉, 상기 화학적 기계적 연마 공정을 이용한 다마신 공정 (damascene process)을 통해 반도체 기판 상에 구리 배선을 형성한다. 상기 화학적 기계적 연마를 이용한 구리 배선 형성 과정 시, 물질 간 제거 선택비 차이로 인한 산화막 침하 및 구리 침하 때문에, 구리 제거는 2단계에 걸쳐 이루어진다. To overcome this, a chemical mechanical polishing (CMP) process was introduced. That is, a copper wiring is formed on a semiconductor substrate through a damascene process using the chemical mechanical polishing process. During the copper wiring formation process using the chemical mechanical polishing, the copper removal is performed in two steps because of the oxide film settling and the copper settling due to the selection ratio between materials.
상기 화학적 기계적 연마 공정 후에는 구리 표면은 슬러리 내 포함된 입자와 유기 첨가제가 표면에 존재한다. 구리 화학기계적 연마 (CMP) 공정 시 슬러리 내 입자의 표면 흡착은 염기성 세정액 조성물을 사용함으로써 음의 제타전위 구현을 통하여 제거 및 재흡착 방지를 달성할 수 있다.After the chemical mechanical polishing process, the copper surface is present on the surface with particles and organic additives contained in the slurry. Surface adsorption of the particles in the slurry during the copper chemical mechanical polishing (CMP) process can achieve removal and re-adsorption prevention through the implementation of negative zeta potential by using a basic cleaning composition.
그러나 구리 화학기계적 연마 (CMP) 공정 시 사용되는 산화-부식방지 메커니즘에 의해서 형성된 불안정한 구리 산화막과 그 위에 형성되는 유기물 오염은 제거하는 것이 용이하지 않다. 그러므로 구리 화학기계적 연마 (CMP) 후 세정 공정에서는 유기물 오염층을 완전히 제거하고, 후속하는 공정까지 안정한 산화막을 형성을 통하여 구리막을 보호하는 것이 요구된다.However, it is not easy to remove the unstable copper oxide film formed by the oxidation-corrosion prevention mechanism used in the copper chemical mechanical polishing (CMP) process and the organic material contamination formed thereon. Therefore, in the cleaning process after copper chemical mechanical polishing (CMP), it is required to completely remove the organic contaminant layer, and to protect the copper film through formation of a stable oxide film to a subsequent process.
종래의 리프트 오프 (Lift off) 방식 세정은 구리 산화막을 에칭함에 따라서 안정한 구리 산화막 형성을 통한 구리막 보호에 문제점이 있어, 구리 화학기계적 연마 (CMP) 후 유기물 오염을 완전하게 제거하고, 안정한 산화막 형성을 통해 구리막을 변질 없이 후속하는 공정까지 보호하는 세정액 조성물에 대한 요구가 있다.Conventional lift off cleaning has a problem of copper film protection through formation of a stable copper oxide film by etching a copper oxide film, thereby completely removing organic contamination after copper chemical mechanical polishing (CMP), and forming a stable oxide film There is a need for a cleaning composition that protects the copper film through subsequent processes without deterioration.
또한, 디바이스의 직접도가 증가함에 따라 금속배선층이 증가하는 추세이며, 금속배선층 간의 연결을 위해서 금속 간의 절연체 영역에 드라이 에칭방법으로 비아홀을 형성하여 금속 간을 연결시킨다. 이러한 공정의 경우 PR 패터닝 공정과 드라이 에싱 (ashing), PR 스트립 (Strip) 공정을 진행하여 비아홀을 형성한다.In addition, as the degree of directivity of the device increases, the metal wiring layer tends to increase. In order to connect the metal wiring layers, via holes are formed in the insulating region between the metals by dry etching to connect the metals. In such a process, the PR patterning process, the dry ashing process, and the PR strip process are performed to form a via hole.
에싱 및 PR 스트립 이후에 바이홀과 금속 표면에 잔유물이 남을 수 있고, 이러한 잔유물은 금속 배선 연결 시에 단락 등을 유발하는 요인으로 작용할 수 있으므로 완전한 제거가 필요하다. 이러한 완전한 잔유물 제거에 유리한 세정액 조성물에 대한 요구가 있다.
Residues may remain on the viaholes and metal surfaces after the ashing and PR strips, and these residues may act as a cause of short-circuiting when metal wiring is connected, thus requiring complete removal. There is a need for a cleaning fluid composition which is advantageous for such complete remnant removal.
본 발명은 상기의 문제점을 해결하기 위하여 발명된 것으로서, 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후 세정 과정에서 유기물 오염층을 완전히 제거하고, 후속 공정까지 안정적으로 유지되는 산화막을 형성할 수 있는 세정액 조성물 및 이를 이용한 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후 세정방법을 제공하는 것이다. SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a method of removing organic contaminants completely during a chemical mechanical polishing (CMP) process, an etching process, an ashing process or a cleaning process after a PR strip process, (CMP) process, an etching process, an ashing process, or a cleaning process after the PR strip process using the cleaning liquid composition and the chemical mechanical polishing (CMP) process.
본 발명은 희석 시에 조성물의 pH의 변화폭이 크지 않고, 세정 전후 표면의 접촉각 변화가 작고, 장시간 담지의 경우에도 표면의 화학적 결함이 발생하지 않는 안정적인 세정액 조성물 및 이를 이용한 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후 세정방법을 제공하는 것이다.
The present invention relates to a stable cleaning liquid composition which does not cause a wide variation in the pH of the composition during dilution, exhibits a small contact angle change before and after cleaning, and does not cause chemical defects on the surface even in the case of long-term loading, and a chemical mechanical polishing (CMP) , An etching process, an ashing process or a PR strip process.
본 발명의 세정액 조성물은, 4급 암모늄 화합물을 포함하는 유기물질 제거제; 알칸올 아민 또는 수산화 아민을 포함하는 포토레지스트 또는 폴리머 잔사 제거제; 5-아미노테트라졸, 요산 (Uric acid), 히드라진, 벤조티아졸, 벤조트리아졸 및 1,2,4-트리아졸로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 부식방지제; 및 순수 (純水);를 포함한다.The cleaning liquid composition of the present invention comprises an organic substance remover comprising a quaternary ammonium compound; Photoresist or polymer residue removers comprising alkanolamines or hydroxylamines; A corrosion inhibitor comprising at least one selected from the group consisting of 5-aminotetrazole, uric acid, hydrazine, benzothiazole, benzotriazole and 1,2,4-triazole; And pure water.
상기 유기물질 제거제는 상기 세정액 조성물 중 1 내지 50 중량%일 수 있다.The organic material removing agent may be 1 to 50% by weight of the cleaning liquid composition.
상기 포토레지스트 또는 폴리머 잔사 제거제는 상기 세정액 조성물 중 1 내지 50 중량%일 수 있다.The photoresist or polymer residue remover may be from 1 to 50% by weight of the cleaning composition.
상기 알칸올 아민은, 모노에탄올아민, 메틸에탄올아민, 에틸에탄올아민, 디에탄올아민, 트리에탄올아민 및 N-아미노-N-프로판올으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 것일 수 있다.The alkanolamine may include at least one selected from the group consisting of monoethanolamine, methylethanolamine, ethylethanolamine, diethanolamine, triethanolamine and N-amino-N-propanol.
상기 세정액 조성물은, 메르캅탄 화합물을 포함하는 킬레이트 시약을 더 포함하는 것일 수 있다.The cleaning liquid composition may further comprise a chelating agent comprising a mercaptan compound.
상기 메르캅탄 화합물은, 2-메르캅토에탄올, 글루타티온, 시스테인 및 메티오나인으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함할 수 있다.The mercaptan compound may include at least one selected from the group consisting of 2-mercaptoethanol, glutathione, cysteine, and methionine.
상기 킬레이트 시약은 상기 세정액 조성물 중 0.005 내지 5 중량%일 수 있다.The chelating agent may be 0.005 to 5% by weight of the cleaning liquid composition.
상기 부식방지제는 상기 세정액 조성물 중 0.001 내지 3 중량%인 것일 수 있다.The corrosion inhibitor may be 0.001 to 3% by weight of the cleaning liquid composition.
본 발명의 세정액 조성물은, 아스코르브산, 엘라직산, 갈산 및 카테콜로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 산화방지제를, 상기 세정액 조성물 중 0.01 내지 5 중량%로 더 포함할 수 있다.The cleaning liquid composition of the present invention may further comprise an antioxidant comprising at least any one selected from the group consisting of ascorbic acid, elaidic acid, gallic acid and catechol in an amount of 0.01 to 5 wt% of the cleaning liquid composition.
상기 세정액 조성물은 pH가 8 내지 14일 수 있다.The cleaning composition may have a pH of 8 to 14.
상기 세정액 조성물은, 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 상기 세정액 조성물로 세정한 구리 표면의 접촉각이 45 이하일 수 있다.The cleaning liquid composition may have a contact angle of a copper surface cleaned with the cleaning liquid composition of 45 or less after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process, or a PR strip process.
상기 세정액 조성물은, 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 금속 표면 세정 시, 희석비 0 ~ 1:100으로 사용하는 것일 수 있다.The cleaning liquid composition may be used at a dilution ratio of 0 to 1: 100 at the time of metal surface cleaning after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process or a PR strip process.
본 발명의 구리 화학기계적 연마 (CMP) 공정 세정방법은, 구리 표면을 화학기계적 연마 (CMP)하는 단계; 및 상기의 세정액 조성물을 이용하여 상기 연마된 구리 표면을 세정하는 단계;를 포함한다.A copper chemical mechanical polishing (CMP) process cleaning method of the present invention comprises: chemical mechanical polishing (CMP) a copper surface; And cleaning the polished copper surface using the cleaning composition as described above.
본 발명의 에칭, 에싱 또는 PR 스트립 표면의 세정방법은, 금속막 또는 절연막을 에칭, 에싱 또는 PR 스트립하는 단계; 및 상기의 세정액 조성물을 이용하여 상기 에칭, 에싱 또는 PR 스트립된 금속 표면 또는 절연막을 세정하는 단계;를 포함한다.
The etching, ashing or cleaning method of the PR strip surface of the present invention comprises etching, ashing or PR stripping a metal film or an insulating film; And cleaning the etched, ashed or PR stripped metal surface or insulating film using the cleaning composition as described above.
본 발명의 세정액 조성물은 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후 세정 과정에서 구리 등의 금속 표면 상의 잔여 입자 및 유기물 오염층을 완전히 제거하고, 후속 공정까지 안정적으로 유지되는 산화막을 얻을 수 있다.The cleaning liquid composition of the present invention can completely remove residual particles and organic contaminants on the surface of metal such as copper during a cleaning process after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process or a PR strip process, An oxide film can be obtained.
또한, 세정 공정에서 희석액으로 사용하는 경우에도 조성물의 pH가 안정적으로 유지되고, 세정 전후 표면의 접촉각 변화를 최소화할 수 있다.In addition, even when used as a diluting solution in the cleaning step, the pH of the composition is stably maintained, and the change in the contact angle of the surface before and after cleaning can be minimized.
또한, 본 발명의 세정작용은 반도체 소재의 표면으로부터 잔류입자를 효과적으로 제거하고 금속이 반도체 소재 표면상에 재침착하는 것을 방지한다.In addition, the cleaning action of the present invention effectively removes residual particles from the surface of the semiconductor material and prevents the metal from re-depositing on the surface of the semiconductor material.
또한, 본 발명의 세정액 조성물을 이용하여 세정 공정을 거친 표면의 접촉각은 종래의 세정액을 이용한 경우보다 낮으므로 세정 단계 이후 공정에서의 결합 발생 (defect)를 현저히 감소시킬 수 있다.
Further, since the contact angle of the surface of the cleaning liquid composition of the present invention after the cleaning process is lower than that of the conventional cleaning liquid, the defects in the cleaning process can be significantly reduced.
도 1은 본 발명의 실시예 1 및 비교예 1~3의 세정액 조성물로 세정 공정을 수행한 후의 구리 표면의 접촉각을 나타낸 그래프이다.
도 2은 본 발명의 실시예 1 및 비교예 1~3의 세정액 조성물로 세정 공정을 수행한 후의 잔여 유기물량을 나타낸 그래프이다.
도 3은 무처리 구리 기판 (A), BTA 오염 기판 (B) 및 본 발명의 실시예 1의 세정액으로 처리한 기판 (C)의 TOF-SIMS 분석 결과이다.
도 4는 순수 (DI water) 및 본 발명의 실시예 1의 세정액으로 처리한 기판의 화학 부식을 측정한 그래프이다.
도 5는 순수 (DI water) 및 본 발명의 실시예 1의 세정액으로 처리한 기판의 갈바닉 (galvanic) 부식을 측정한 그래프이다.
도 6은 본 발명의 실시예 1의 세정액으로 세정한 후 중앙부 및 가장자리부의 표면 거칠기를 나타내는 구리웨이퍼 5 ㎛ × 5 ㎛ 배율에서의 원자력 현미경 (AFM)스캔 사진이다.
도 7은 본 발명의 실시예 2 및 실시예 3의 세정액으로 PR 스트립 공정을 실시한 후 접촉각을 측정하여 유기물 세정 성능을 평가한 결과 그래프이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a graph showing a contact angle of a copper surface after a cleaning process with the cleaning composition of Example 1 of the present invention and Comparative Examples 1 to 3; FIG.
Fig. 2 is a graph showing the amounts of residual organic compounds after the cleaning process with the cleaning composition of Example 1 of the present invention and Comparative Examples 1 to 3; Fig.
3 is a TOF-SIMS analysis result of the untreated copper substrate (A), the BTA contaminated substrate (B) and the substrate (C) treated with the cleaning liquid of the first embodiment of the present invention.
4 is a graph showing chemical corrosion of pure water (DI water) and the substrate treated with the cleaning liquid of the first embodiment of the present invention.
5 is a graph showing galvanic corrosion of pure water (DI water) and a substrate treated with the cleaning liquid of Example 1 of the present invention.
6 is an atomic force microscope (AFM) scan image of a
FIG. 7 is a graph showing the results of evaluating organic cleaning performance by measuring the contact angle after PR stripping with the cleaning liquids of Examples 2 and 3 of the present invention. FIG.
본 발명의 세정액 조성물은, 4급 암모늄 화합물을 포함하는 유기물질 제거제; 알칸올 아민 또는 수산화 아민을 포함하는 포토레지스트 또는 폴리머 잔사 제거제; 5-아미노테트라졸, 요산 (Uric acid), 히드라진, 벤조티아졸, 벤조트리아졸 및 1,2,4-트리아졸로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 부식방지제; 및 순수 (純水);를 포함한다.The cleaning liquid composition of the present invention comprises an organic substance remover comprising a quaternary ammonium compound; Photoresist or polymer residue removers comprising alkanolamines or hydroxylamines; A corrosion inhibitor comprising at least one selected from the group consisting of 5-aminotetrazole, uric acid, hydrazine, benzothiazole, benzotriazole and 1,2,4-triazole; And pure water.
상기 유기물질 제거제는 4급 암모늄 화합물을 사용하며, 잔류하는 유기물질을 제거하는 역할을 하며, 나아가 세정액 조성물의 pH를 조절하는 기능도 나타낸다. 이러한 유기물질 제거제는 상기 세정액 조성물 중 1 ~ 50 중량%, 바람직하게는 1 ~ 20 중량%, 더 바람직하게는 1 ~ 10 중량%일 수 있다.The organic material removing agent uses a quaternary ammonium compound and serves to remove remaining organic substances and also to control the pH of the cleaning liquid composition. Such an organic material removing agent may be 1 to 50% by weight, preferably 1 to 20% by weight, more preferably 1 to 10% by weight in the cleaning liquid composition.
상기 포토레지스트 또는 폴리머 잔사 제거제는 알칸올 아민 또는 수산화 아민을 사용하며, 상기 세정액 조성물 중 1 ~ 50 중량%, 바람직하게는 3 ~ 20 중량%일 수 있다.The photoresist or polymer residue removing agent may be an alkanolamine or a hydroxylamine, and may be 1 to 50 wt%, preferably 3 to 20 wt%, of the cleaning liquid composition.
상기 세정액 조성물은, 메르캅탄 화합물을 포함하는 킬레이트 시약을 더 포함하는 것일 수 있다.The cleaning liquid composition may further comprise a chelating agent comprising a mercaptan compound.
상기 메르캅탄 화합물은, 2-메르캅토에탄올, 글루타티온, 시스테인 및 메티오나인으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함할 수 있고, 상기 킬레이트 시약은 상기 세정액 조성물 중 0.005 ~ 5 중량%, 바람직하게는 0.1 ~ 3 중량%일 수 있다.The mercaptan compound may include at least any one selected from the group consisting of 2-mercaptoethanol, glutathione, cysteine, and methionine, and the chelating agent may be used in an amount of 0.005 to 5 wt% May be 0.1 to 3% by weight.
상기 알칸올 아민은, 모노에탄올아민, 메틸에탄올아민, 에틸에탄올아민, 디에탄올아민, 트리에탄올아민 및 N-아미노-N-프로판올으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 것일 수 있다.The alkanolamine may include at least one selected from the group consisting of monoethanolamine, methylethanolamine, ethylethanolamine, diethanolamine, triethanolamine and N-amino-N-propanol.
상기 부식방지제는 상기 세정액 조성물 중 0.001 ~ 3 중량%일 수 있다.The corrosion inhibitor may be 0.001 to 3 wt% of the cleaning liquid composition.
본 발명의 세정액 조성물은 아스코르브산, 엘라직산, 갈산 및 카테콜로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 산화방지제를 상기 세정액 조성물 중 0.01 내지 5 중량%로 더 포함할 수 있다. 산화방지제를 포함하는 경우에 구리 금속 표면을 보호하여 과도한 산화를 방지할 수 있다.The cleaning liquid composition of the present invention may further comprise an antioxidant containing at least one selected from the group consisting of ascorbic acid, elaidic acid, gallic acid and catechol in an amount of 0.01 to 5 wt% of the cleaning liquid composition. If it contains an antioxidant, the copper metal surface can be protected to prevent excessive oxidation.
상기 유기물질 제거제로 사용되는 4급 암모늄 화합물은, 암모늄 히드록시드 및 테트라알킬암모늄 히드록시드, 예컨대 테트라메틸암모늄 히드록시드 (TMAH), 테트라에틸암모늄 히드록시드, 테트라프로필암모늄 히드록시드, 트리메틸에틸암모늄 히드록시드, (2-히드록시에틸)트리메틸암모늄 히드록시드, (2-히드록시에틸)트리에틸암모늄 히드록시드, (2-히드록시에틸)트리프로필암모늄 히드록시드, (1-히드록시프로필)트리메틸암모늄 히드록시드에서 선택되는 적어도 어느 하나 및 이들의 혼합물일 수 있고, 다만, 이에 제한되지는 않는다.The quaternary ammonium compound used as the organic substance remover may be ammonium hydroxide and tetraalkylammonium hydroxide such as tetramethylammonium hydroxide (TMAH), tetraethylammonium hydroxide, tetrapropylammonium hydroxide, Trimethylammonium hydroxide, (2-hydroxyethyl) trimethylammonium hydroxide, (2-hydroxyethyl) triethylammonium hydroxide, (2-hydroxyethyl) -Hydroxypropyl) trimethylammonium hydroxide, and mixtures thereof, but is not limited thereto.
유기물질 제저제로 사용된 4급 암모늄 화합물 등은 반도체 유기물질 등을 제거하는 세정액으로 사용되고 있으며, 세정 효과가 탁월하다. 특히 염기성 용매로 용액 내 음의 제타전위를 구현하여 정전기적 반발력을 통해서 세정 후 파티클 (Particle) 재흡착 방지를 할 수 있다. Quaternary ammonium compounds used as an organic substance-removing agent are used as a cleaning liquid for removing semiconductor organic substances and the like, and the cleaning effect is excellent. Particularly, by implementing a negative zeta potential in a solution with a basic solvent, particle adsorption can be prevented after cleaning through electrostatic repulsion.
Cu 슬러리 내 연마제 입자는 음의 제타전위를 띄고 있으며, CMP 공정 후 금속이온이 포함되지 않은 염기성 유기 용매를 사용하면 입자를 용이하게 제거할 수 있고, 또한 재흡착 방지가 가능하다. 유기물질 제거제는 최종 pH 조절제로서의 역할을 수행하기 때문에 그 함량은 적절한 성능을 나타내는 pH 수준으로 결정된다.The abrasive grains in the Cu slurry have a negative zeta potential. When a basic organic solvent containing no metal ion is used after the CMP process, particles can be easily removed and re-adsorption can be prevented. Since the organic substance remover plays a role as a final pH adjusting agent, its content is determined to be a pH level indicating an appropriate performance.
상기 세정액 조성물은 pH가 8 내지 14일 수 있다.The cleaning composition may have a pH of 8 to 14.
또한, 본 발명에서는 PR 잔여물의 제거 효과를 높이기 위하여 알칸올 아민 또는 수산화 아민을 사용한다.Also, in the present invention, an alkanolamine or a hydroxylamine is used to enhance the removal effect of the PR residue.
킬레이트 시약의 경우, 세정 공정이 진행될 때 발생하는 금속 이온의 착화제로 작용을 한다. 또한 약산을 띠게 됨으로써 염기성 유기 용매와 약산-강염기의 버퍼 용액을 형성하여 희석비에 관계없이 적절한 pH 영역이 유지되게 한다. 특히, 메르캅탄 화합물을 포함하는 킬레이트 시약을 포함하는 경우 세정 후 접촉각이 매우 작은 값을 갖는 것으로 보아 친수성이 잘 유지되도록 하는 역할을 하는 것을 알 수 있다. In the case of a chelating reagent, it acts as a complexing agent for the metal ion that occurs when the cleaning process proceeds. In addition, a weak acid is formed to form a buffer solution of a basic organic solvent and a weak acid-strong base so that an appropriate pH region is maintained regardless of the dilution ratio. In particular, when a chelating reagent containing a mercaptan compound is included, it can be seen that the contact angle after washing has a very small value, and thus plays a role in maintaining good hydrophilicity.
부식방지제의 경우, 세정 작용시 금속 표면을 보호하는 작용을 하며, 과량 첨가시 웨이퍼 표면에 잔류하여 오히려 유기물 오염을 유발할 수 있다.In the case of the corrosion inhibitor, it acts to protect the metal surface during the cleaning operation and may remain on the surface of the wafer when added in excess, which may cause contamination of the organic matter.
본 발명의 세정액 조성물은, 상기 세정액 조성물을 이용하여 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 상기 세정액 조성물로 세정한 구리 표면의 접촉각이 45 이하, 바람직하게는 20~42 일 수 있다. The cleaning liquid composition of the present invention is characterized in that, after the copper chemical mechanical polishing (CMP) process, the etching process, the ashing process or the PR strip process using the cleaning liquid composition, the contact angle of the copper surface cleaned with the cleaning liquid composition is 45 or less, 20 to 42 days.
화학기계적 연마 (CMP) 공정 또는 금속막의 에칭 공정, 및 세정 후 접촉각이 증가하는 것은 표면이 소수성으로 변환된 것을 의미한다. 초순수에 담지한 후 세척하고 질소 가스로 완전 세척한 상태의 구리 (fresh Cu)의 표면의 접촉각이 41.6 정도이므로, 화학기계적 연마 (CMP) 공정 또는 금속막의 에칭 공정, 및 세정 후 접촉각이 45 이하 (친수성 (hydropilic))로 유지되어야 한다. 접촉각이 45를 넘게 되면 상기 검토대로 표면이 부식방지제에 의하여 소수성으로 변환된 것임을 나타낸다. 화학기계적 연마 (CMP) 또는 에칭 후 세정 공정은 연마 후 표면에 잔류하는 유기물 오염층을 제거하는 것이 목적이므로, 세정 작용 외에는 표면에 영향을 미치지 않는 것이 바람직하다. 그러므로 세정 후 접촉각에 있어서도 세정 전 접촉각을 기준으로 표면의 특성 변화가 없는 것으로 평가 가능한 수준인 45도 이하를 유지하는 것이 바람직하다.An increase in the contact angle after a chemical mechanical polishing (CMP) process or an etching process of a metal film, and cleaning means that the surface is converted into a hydrophobic property. (CMP) process or a metal film etching process, and a contact angle of 45 or less after cleaning, since the contact angle of the surface of copper (fresh Cu) which is completely washed with nitrogen gas is about 41.6 Lt; RTI ID = 0.0 > hydrophilic < / RTI > When the contact angle exceeds 45, it indicates that the surface has been converted to a hydrophobic property by the corrosion inhibitor as described above. The chemical mechanical polishing (CMP) or post-etching cleaning step is intended to remove the organic contamination layer remaining on the surface after polishing, so that it is preferable that it does not affect the surface other than the cleaning action. Therefore, it is desirable to maintain the contact angle after cleaning to 45 degrees or less, which is a level that can be evaluated as no change in surface characteristics based on the contact angle before cleaning.
상기 세정액 조성물은, 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 금속 표면 세정 시, 희석비 0 (희석 없이 사용) ~ 1:100으로 사용하는 것일 수 있다. 희석비가 1:100 보다 크면 조성물 함량이 너무 낮아서 저장안정성 및 경시안정성에서 문제가 있을 수 있다. The cleaning liquid composition may be used at a dilution ratio of 0 (without dilution) to 1: 100 at the time of cleaning a metal surface after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process or a PR strip process. If the dilution ratio is more than 1: 100, the composition content is too low, which may cause problems in storage stability and aging stability.
본 발명의 구리 화학기계적 연마 (CMP) 공정 세정방법은, 구리 표면을 화학기계적 연마 (CMP)하는 단계; 및 상기의 세정액 조성물을 이용하여 상기 연마된 구리 표면을 세정하는 단계;를 포함한다.A copper chemical mechanical polishing (CMP) process cleaning method of the present invention comprises: chemical mechanical polishing (CMP) a copper surface; And cleaning the polished copper surface using the cleaning composition as described above.
본 발명의 에칭, 에싱 또는 PR 스트립 표면의 세정방법은, 금속막 또는 절연막을 에칭, 에싱 또는 PR 스트립하는 단계; 및 상기의 세정액 조성물을 이용하여 상기 에칭, 에싱 또는 PR 스트립된 금속 표면 또는 절연막을 세정하는 단계;를 포함한다.The etching, ashing or cleaning method of the PR strip surface of the present invention comprises etching, ashing or PR stripping a metal film or an insulating film; And cleaning the etched, ashed or PR stripped metal surface or insulating film using the cleaning composition as described above.
이하 실시예 및 비교예를 통하여 본 발명을 더욱 상세히 설명한다. 다만, 이는 설명을 위한 것일 뿐, 본 발명이 이에 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, this is for illustrative purposes only, and the present invention is not limited thereto.
실시예Example 및 And 비교예Comparative Example
실시예 1로서, 본 발명의 세정액 조성물로서 4급 암모늄 화합물은 5 중량%, 메르캅탄 화합물을 포함하는 킬레이트 시약 1 중량%, 5-아미노테트라졸 부식방지제 0.5 중량% 및 잔여 순수를 포함하는 실시예 1의 세정액 조성물을 제조하였다. As Example 1, the cleaning liquid composition of the present invention was prepared in the same manner as in Example 1 except that the quaternary ammonium compound was used in an amount of 5 wt%, a chelating reagent containing a mercaptan compound in an amount of 1 wt%, a 5-aminotetrazole corrosion inhibitor in an amount of 0.5
실시예 2로서,다른 조건은 실시예 1과 동일하되, 알칸올 아민 10 중량%를 추가로 포함하는 세정액 조성물을 제조하였다.As Example 2, a cleaning liquid composition was prepared which further contained 10% by weight of alkanolamine in the same manner as in Example 1 except for the other conditions.
실시예 3으로 다른 조건은 실시예 2와 동일하되, 산화방지제로 아르코르브산을 0.5 중량%를 추가하여 세정액 조성물을 제조하였다.Other conditions were the same as Example 2 except that 0.5% by weight of ascorbic acid was added as an antioxidant to prepare a cleaning liquid composition.
비교예로서, 다른 조성은 실시예 1과 동일하게 유지하고, 킬레이트 시약이 글리신 (glycine)을 포함하는 경우 (비교예 1), 아르기닌 (arginine)을 포함하는 경우 (비교예 2), EDTA (ethylenediamine tetraacetic acid, 에틸렌디아민테트라아세트산, 화학식: (HOOCCH2)2NCH2CH2N(CH2COOH)2)를 포함하는 경우 (비교예 3)를 준비하였다.As a comparative example, the other composition was kept the same as in Example 1, and in the case where the chelating agent contained glycine (Comparative Example 1), when arginine was contained (Comparative Example 2), EDTA (ethylenediamine tetraacetic acid, ethylenediaminetetraacetic acid, and (HOOCCH 2 ) 2 NCH 2 CH 2 N (CH 2 COOH) 2 ) (Comparative Example 3).
실제 세정액의 사용에 있어서는 상당한 비율로 희석하여 사용함을 고려하여 실시예 1 및 비교예 1~3의 세정액 조성물 원액 및 1:50 희석액을 이용하여 연마 화학기계적 연마 공정을 거친 구리 웨이퍼 표면을 세정한 후, 접촉각을 측정하고, 입자 제거율 및 잔여 유기물량 (유기물 제거율)을 측정하고, TOF-SIMS 분석을 실시하였다.The surface of the copper wafer subjected to the polishing chemical mechanical polishing process was cleaned by using the cleaning liquid composition stock solution of Example 1 and Comparative Examples 1 to 3 and a 1:50 dilution in consideration of the use of the actual cleaning liquid in a considerable dilution ratio , The contact angle was measured, the particle removal rate and residual organic amount (organic matter removal rate) were measured, and TOF-SIMS analysis was performed.
한편, 실시예 1의 세정액 조성물 1:50 희석액으로 세정 과정을 수행하고, 4-point probe로 세정 전후 측정하여 그 차를 기초로 제거된 양을 나타내어 시간당 제거량을 확인함으로써 에칭율을 측정하였다.
On the other hand, the cleaning rate was measured with a 1: 50 dilution of the cleaning liquid composition of Example 1, and the amount of cleaning was measured based on the difference between the measured values before and after cleaning with a 4-point probe.
접촉각Contact angle 측정 Measure
도 1은 본 발명의 실시예 1 및 비교예 1~3의 세정액 조성물로 세정 공정을 수행한 후의 구리 표면의 접촉각을 나타낸 그래프이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a graph showing a contact angle of a copper surface after a cleaning process with the cleaning composition of Example 1 of the present invention and Comparative Examples 1 to 3; FIG.
구리 웨이퍼를 1분간 담지한 후 접촉각을 측정한 결과, 본 발명의 실시예 1은 원액 및 1:50 희석액에서, 특히 1:50 희석액에서 30 이하의 상대적으로 매우 낮은 접촉각을 나타내었다. 이를 통하여 실시예 1의 세정액을 사용하는 경우 세정에 의한 소수성으로의 변화를 방지하여 친수성이 유지되고 있는 것임을 알 수 있다.
As a result of measuring the contact angle after carrying the copper wafer for 1 minute, Example 1 of the present invention showed a relatively low contact angle of 30 or less in the stock solution and 1:50 dilution, especially in the 1:50 dilution. It can be seen from the above that when the cleaning liquid of Example 1 is used, the hydrophilicity is maintained by preventing the change to hydrophobic by washing.
입자 제거율 측정Measure particle removal rate
아래의 표 1는 실시예 1 및 비교예 1~3의 세정액 조성물의 원액 및 1:50 희석액의 잔여 입자 제거 정도를 측정한 결과이다. 슬러리 내에 포함되어 있는 입자를 효과적으로 제거하였는지를 확인하기 위한 것이다. 실리카 슬러리에 강제 오염된 구리 기판에 세정을 한 후 FE-SEM을 통하여 기판 표면을 스캔하여 입자 제거 정도를 측정하였다.
Table 1 below shows the results of measuring the degree of removal of residual particles of the washing liquid composition and the 1:50 dilution of the washing liquid compositions of Example 1 and Comparative Examples 1 to 3. [ To confirm that the particles contained in the slurry were effectively removed. The silica slurry was cleaned on a copper substrate that had been contaminated by force, and the surface of the substrate was scanned through FE-SEM to measure the degree of particle removal.
유기물 제거율 측정Measurement of organic matter removal rate
유기물의 제거 효과를 확인하기 위해서, BTA로 오염된 구리 표면을 본 발명의 실시예 1의 세정액 조성물로 세정한 후 잔여 유기물 량을 측정하였다.In order to confirm the removal effect of the organic matter, the copper surface contaminated with BTA was washed with the cleaning liquid composition of Example 1 of the present invention, and the amount of residual organic matter was measured.
도 2은 본 발명의 실시예 1의 세정액 조성물로 세정 공정을 수행한 후의 잔여 유기물량을 나타낸 그래프이다. 2 is a graph showing the amount of residual organic compounds after the cleaning process is performed with the cleaning composition of Example 1 of the present invention.
도 2와 같이 본 발명의 실시예 1의 세정액으로 세정한 경우, 오염물질을 대부분이 제거되는 것을 확인할 수 있었다.
As shown in FIG. 2, it was confirmed that most of the contaminants were removed when the cleaning solution was washed with the cleaning solution of Example 1 of the present invention.
TOFTOF -- SIMSSIMS 측정 Measure
도 3은 무처리 구리 기판 (A), BTA 오염 기판 (B) 및 본 발명의 실시예 1의 세정액으로 처리한 기판 (C)의 TOF-SIMS 분석 결과이다. 이온을 구리 기판 표면에 충돌시켜 생성된 이차 이온을 에너지와 질량에 따라 분리하여 검출하는 방법을 통하여 기판 표면의 유기물을 분석하였다.
3 is a TOF-SIMS analysis result of the untreated copper substrate (A), the BTA contaminated substrate (B) and the substrate (C) treated with the cleaning liquid of the first embodiment of the present invention. Ions were collided with the surface of the copper substrate and secondary ions were separated by energy and mass to detect the organic matter on the surface of the substrate.
화학 부식 측정Chemical corrosion measurement
도 4는 순수 (DI water) 및 본 발명의 실시예 1의 세정액으로 처리한 기판의 화학 부식을 측정한 그래프이다.4 is a graph showing chemical corrosion of pure water (DI water) and the substrate treated with the cleaning liquid of the first embodiment of the present invention.
순수로 세정할 경우에는 킨크 (kink)가 발생하는데 반해, 본 발명의 실시예 1의 세정액 조성물로 세정하는 경우에는 킨크가 전혀 발생하지 않는 것을 확인할 수 있다. 이로부터 본 발명의 세정액이 부식 억제 효과가 우수함을 확인할 수 있다. 전압 값을 변화시키면서 전류 값의 변화를 측정하여 Tafel plot으로 나타내면 불규칙한 전류값의 변화구간이 존재함은 표면 부식이 발생한 것으로 유추할 수 있다.
It can be confirmed that no kink is generated in the case of cleaning with the cleaning liquid composition of Example 1 of the present invention, while kink is generated when cleaning with pure water. From this, it can be confirmed that the cleaning liquid of the present invention has excellent corrosion inhibiting effect. When the change of the current value is measured while changing the voltage value, if there is an irregular current value change interval, it can be deduced that surface corrosion has occurred.
갈바닉Galvanic 부식 측정 Corrosion measurement
도 5는 순수 (DI water) 및 본 발명의 실시예 1의 세정액으로 처리한 기판의 갈바닉 (galvanic) 부식을 측정한 그래프이다. 5 is a graph showing galvanic corrosion of pure water (DI water) and a substrate treated with the cleaning liquid of Example 1 of the present invention.
구리 (Cu)와 탄탈륨 (Ta) 사이에는 갈바닉 부식이 발생하는데, 순수로 세정하는 경우에는 구리와 탄탈륨 사이의 포텐셜 차이가 200 mV로 매우 높게 나타나나, 본 발명의 실시예 1의 세정액으로 세정한 경우에는 구리와 탄탈륨 사이의 포텐셜 차이가 20 mV로 낮아지는 것을 알 수 있다. 따라서, 본 발명의 세정액 조성물은 갈바닉 부식을 방지하는 효과가 우수한 것을 알 수 있다. 전해질 용액에 두 금속이 접촉된 상태로 담겨 있을 때, 두 금속의 전위차가 작으면 전자의 이동이 억제되고 부식을 방지 할 수 있다.
Galvanic corrosion occurs between copper (Cu) and tantalum (Ta). In the case of cleaning with pure water, the potential difference between copper and tantalum is as high as 200 mV. However, The potential difference between copper and tantalum is reduced to 20 mV. Therefore, it can be seen that the cleaning liquid composition of the present invention has an excellent effect of preventing galvanic corrosion. When the two metals are in contact with the electrolyte solution and the potential difference between the two metals is small, the movement of the electrons is inhibited and corrosion can be prevented.
식각율Etch rate 및 표면 거칠기 측정 And surface roughness measurement
도 6은 본 발명의 실시예 1의 세정액으로 세정한 후 중앙부 및 가장자리부의 표면 거칠기를 나타내는 구리웨이퍼 5 ㎛ × 5 ㎛ 배율에서의 원자력 현미경 (AFM)스캔 사진이다.6 is an atomic force microscope (AFM) scan image of a
실시예 1의 세정액 조성물의 세정 과정에서 구리의 식각율을 측정한 결과, 0.24 Å/m으로 매우 낮은 값이 확인되었고, 이는 구리의 에칭 없이 세정이 이루어져 이후 단계에 발생 가능한 문제를 방지하는 효과가 있는 것으로 볼 수 있다.As a result of measuring the etching rate of copper in the cleaning process of the cleaning liquid composition of Example 1, a very low value of 0.24 Å / m was confirmed. This is an effect of preventing the problems that may occur in subsequent steps due to cleaning without etching of copper .
또한, 실시예 1의 세정액으로 세정한 후에 중앙부 및 가장자리부의 표면 거칠기를 측정한 결과, 매우 우수한 거칠기 특성을 갖는다는 것을 알 수 있다.
The surface roughness of the central portion and the edge portion after cleaning with the cleaning liquid of Example 1 was measured, and as a result, it was found that the surface roughness was very excellent.
상기와 같이 본 발명의 실시예 1 및 비교예 1~3의 세정액을 비교하여 여러 가지 지표를 통하여 성능을 측정한 결과, 원액 및 1:50 희석액의 세정 후 표면의 접촉각, 입자 및 유기물 세정 완성도, 표면 결함 여부, 에칭율 등에 있어서 본 발명의 세정액 조성물이 우수한 특성을 나타냄을 확인할 수 있었다.
As a result of measuring the performance of the cleaning solution of Example 1 of the present invention and Comparative Examples 1 to 3 through various indicators, it was found that the contact angle of the undiluted solution and 1:50 diluted solution, It is confirmed that the cleaning liquid composition of the present invention exhibits excellent properties in terms of surface defects, etching rate and the like.
PRPR 스트립 후 After Strip 접촉각Contact angle 측정 Measure
PR 잔유물의 제거 평가를 위하여 구리 막 위에 PR이 도포된 웨이퍼를 본 발명의 실시예 2 및 실시예 3의 세정액에 5분 동안 디핑한 후 PR 제거 정도를 측정하였다.For evaluation of the removal of PR residue, the wafer on which the PR was coated on the copper film was dipped in the cleaning solution of Example 2 and Example 3 of the present invention for 5 minutes, and the degree of PR removal was measured.
도 7은 본 발명의 실시예 2 및 실시예 3의 세정액으로 PR 스트립 공정을 실시한 후 접촉각을 측정하여 유기물 세정 성능을 평가한 결과 그래프이다.FIG. 7 is a graph showing the results of evaluating organic cleaning performance by measuring the contact angle after PR stripping with the cleaning liquids of Examples 2 and 3 of the present invention. FIG.
도 7에서 확인할 수 있듯이, 20 ℃, 30 ℃에서는 접촉각의 큰 변화가 없었으나, 40 ℃, 50 ℃에서는 5분 세정 후 접촉각이 확연히 감소하는 것을 확인할 수 있었다. 이는 효과적으로 PR 잔유물이 제거되는 것을 나타내는 것이다.As can be seen from FIG. 7, there was no significant change in the contact angle at 20 ° C and 30 ° C, but it was confirmed that the contact angle was significantly reduced after 5 minutes of washing at 40 ° C and 50 ° C. This indicates that the PR remnants are effectively removed.
Claims (14)
알칸올 아민 또는 수산화 아민을 포함하는 포토레지스트 또는 폴리머 잔사 제거제;
5-아미노테트라졸, 요산 (Uric acid), 히드라진, 벤조티아졸, 벤조트리아졸 및 1,2,4-트리아졸로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 부식방지제; 및
순수 (純水);
를 포함하고,
메르캅탄 화합물을 포함하는 킬레이트 시약을 더 포함하는 것인 세정액 조성물.
Organic substance removers comprising quaternary ammonium compounds;
Photoresist or polymer residue removers comprising alkanolamines or hydroxylamines;
A corrosion inhibitor comprising at least one selected from the group consisting of 5-aminotetrazole, uric acid, hydrazine, benzothiazole, benzotriazole and 1,2,4-triazole; And
Pure water;
Lt; / RTI >
Wherein the chelating agent further comprises a chelating agent comprising a mercaptan compound.
상기 유기물질 제거제는 상기 세정액 조성물 중 1 내지 50 중량%인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the organic substance remover is 1 to 50% by weight of the cleaning liquid composition.
상기 포토레지스트 또는 폴리머 잔사 제거제는 상기 세정액 조성물 중 1 내지 50 중량%인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the photoresist or polymer residue remover is 1 to 50 wt% of the cleaning composition.
상기 알칸올 아민은, 모노에탄올아민, 메틸에탄올아민, 에틸에탄올아민, 디에탄올아민, 트리에탄올아민 및 N-아미노-N-프로판올으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 것인 세정액 조성물.
The method according to claim 1,
Wherein the alkanolamine comprises at least any one selected from the group consisting of monoethanolamine, methylethanolamine, ethylethanolamine, diethanolamine, triethanolamine and N-amino-N-propanol.
상기 메르캅탄 화합물은, 2-메르캅토에탄올, 글루타티온, 시스테인 및 메티오나인으로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 것인 세정액 조성물.
The method according to claim 1,
Wherein the mercaptan compound comprises at least any one selected from the group consisting of 2-mercaptoethanol, glutathione, cysteine, and methionine.
상기 킬레이트 시약은 상기 세정액 조성물 중 0.005 내지 5 중량%인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the chelating agent is 0.005-5 wt% of the cleaning composition.
상기 부식방지제는 상기 세정액 조성물 중 0.001 내지 3 중량%인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the corrosion inhibitor is 0.001 to 3% by weight of the cleaning liquid composition.
아스코르브산, 엘라직산, 갈산 및 카테콜로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는 산화방지제를, 상기 세정액 조성물 중 0.01 내지 5 중량%로 더 포함하는 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the cleaning liquid composition further comprises an antioxidant containing at least any one selected from the group consisting of ascorbic acid, elaidic acid, gallic acid and catechol in an amount of 0.01 to 5 wt% of the cleaning liquid composition.
상기 세정액 조성물은 pH가 8 내지 14인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the cleaning liquid composition has a pH of 8 to 14.
상기 세정액 조성물은, 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 상기 세정액 조성물로 세정한 구리 표면의 접촉각이 45 이하인 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the cleaning liquid composition has a contact angle of a copper surface cleaned with the cleaning liquid composition of 45 or less after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process, or a PR strip process.
상기 세정액 조성물은, 구리 화학기계적 연마 (CMP) 공정, 에칭 공정, 에싱 공정 또는 PR 스트립 공정 후, 금속 표면 세정 시, 희석비 0 ~ 1:100으로 사용하는 것을 특징으로 하는 세정액 조성물.
The method according to claim 1,
Wherein the cleaning liquid composition is used at a dilution ratio of 0 to 1: 100 at the time of metal surface cleaning after a copper chemical mechanical polishing (CMP) process, an etching process, an ashing process or a PR strip process.
제1항 내지 제4항, 제6항 내지 제12항 중 어느 한 항의 세정액 조성물을 이용하여 상기 연마된 구리 표면을 세정하는 단계;
를 포함하는 구리 화학기계적 연마 (CMP) 공정 세정방법.
Chemical mechanical polishing (CMP) of the copper surface; And
Cleaning the polished copper surface using the cleaning composition of any one of claims 1 to 4 and 6 to 12;
(CMP) process. ≪ / RTI >
제1항 내지 제4항, 제6항 내지 제12항 중 어느 한 항의 세정액 조성물을 이용하여 상기 에칭, 에싱 또는 PR 스트립된 금속 표면 또는 절연막을 세정하는 단계;
를 포함하는 에칭, 에싱 또는 PR 스트립 표면의 세정방법.Etching, ashing or PR stripping a metal film or an insulating film; And
Cleaning the etched, ashed or PR stripped metal surface or insulating film using the cleaning composition of any one of claims 1 to 4 and 6 to 12;
Wherein the surface of the etched, ashed, or PR strip surface is cleaned.