KR101400939B1 - Manufacturing method of combination fabrics using polypropylene/ramie fiber - Google Patents

Manufacturing method of combination fabrics using polypropylene/ramie fiber Download PDF

Info

Publication number
KR101400939B1
KR101400939B1 KR1020130016412A KR20130016412A KR101400939B1 KR 101400939 B1 KR101400939 B1 KR 101400939B1 KR 1020130016412 A KR1020130016412 A KR 1020130016412A KR 20130016412 A KR20130016412 A KR 20130016412A KR 101400939 B1 KR101400939 B1 KR 101400939B1
Authority
KR
South Korea
Prior art keywords
yarn
polypropylene
yarns
fabric
present
Prior art date
Application number
KR1020130016412A
Other languages
Korean (ko)
Inventor
홍영기
이시우
윤봉환
Original Assignee
건양대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 건양대학교산학협력단 filed Critical 건양대학교산학협력단
Priority to KR1020130016412A priority Critical patent/KR101400939B1/en
Application granted granted Critical
Publication of KR101400939B1 publication Critical patent/KR101400939B1/en

Abstract

The present invention is about weaving a combination fabric and or a Jacquard fabric using the polypropylene yarn or the covering yarn for the warp yarn and using the ramie yarn for the weft yarn, which relates to a combination fabric product or a Jacquard fabric product manufactured by special processing by hydrophilic material treatment in the polypropylene yarn or the covering yarn and improving the weaving technique, and the method for manufacturing the same. The manufactured polypropylene/ramie fiber combination fabric manufactured in the present invention has an excellent flatness, and has a regular focusing properties not lowering, and has the excellent physical properties to reduce the moo incidence.

Description

폴리프로필렌/모시 교직물 및 이의 제조방법{Manufacturing Method of Combination Fabrics using Polypropylene/Ramie Fiber}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polypropylene /

본 발명은 경사로서 폴리프로필렌 방적사 또는 커버링사를 사용하고, 위사로서 모시 방적사를 사용하여 형성되는 폴리프로필렌/모시 교직물 또는 자카드 직물을 직조하는 방법에 관한 것으로서, 본 발명의 제조방법은 경사용 폴리프로필렌 방적사나 커버링사를 친수화제로 처리하는 것을 포함하여 이루어지며, 또한 본 발명은 상기의 제조방법으로 제조된 폴리프로필렌/모시 교직물 제품 또는 자카드 직물 제품에 관한 것이다. The present invention relates to a method of weaving polypropylene / rayon fabrics or jacquard fabrics using polypropylene yarns or covering yarns as warp yarns and using warp yarns as weft yarns, The present invention also relates to a polypropylene / rayon fabric product or a jacquard fabric product produced by the above-mentioned manufacturing method, comprising the step of treating the yarn or covering yarn with a hydrophilic agent.

일반적으로, 폴리프로필렌 부직포는 기계적, 물리적 특성과 함께 양호한 가공성의 조합으로 인해 건축 및 농업 분야, 위생 및 의료품, 카페트, 직물과 같은 다양한 섬유 및 부직포가 적용되는 분야에 선택되는 물질이다. 또한, 폴리프로필렌 부직포는 경제성, 경량성, 성형성, 내약품성, 아름다운 외관 등의 우수한 특성을 가지고 있으므로 위생자재, 가전제품, OA기기 포장재료, 자동차 내장재료, 일회용 작업복 등 잡화에 널리 이용되고 있다.In general, polypropylene nonwoven fabrics are materials that are selected for applications where various fibers and nonwoven fabrics such as construction and agricultural fields, sanitary and medical articles, carpets, fabrics are applied due to a combination of good workability with mechanical and physical properties. In addition, polypropylene nonwoven fabric has excellent properties such as economical efficiency, light weight, moldability, chemical resistance and beautiful appearance, and thus it is widely used in various goods such as sanitary materials, home appliances, OA packaging materials, automobile interior materials, disposable work clothes .

그런데, 폴리프로필렌 부직포는 소수성으로 뛰어난 발수성을 나타내지만, 전기절연성이라는 특성을 가지고 있기 때문에 다른 물질과의 마찰 등에 의해 생긴 정전기를 장시간에 걸쳐 축적하는 성질을 가지고 있다.However, since the polypropylene nonwoven fabric exhibits excellent water repellency due to its hydrophobic property, it has a property of accumulating static electricity caused by friction with other materials for a long time because of its electrical insulating property.

그 때문에 대전한 정전기에 의한 방전, 흡인, 반발로 인해 현대식 전자장치인 고가의 의료장비에 극도로 민감하게 작용하여 영구적 손상 등 여러 장해를 야기할 수 있다. 이들 정전기는 물질끼리의 마찰, 접촉에 의해 생기기 때문에 발생 자체를 막는 것은 곤란하다. 따라서, 이와 같은 합성섬유의 정전기 장해를 방지하기 위해서는 발생한 전하를 제거, 중화, 누설시키는 것이 필요하다. 정전기 장해를 방지하는 방법으로는 온도 및 습도의 조절, 코르나 방전 등이 많이 이용되고, 일부에는 대전 방지법으로써 활성제를 주성분으로 하는 섬유용 대전방지제로 표면 처리하고 있다.As a result, discharge, sucking, and repulsion due to charged static electricity are very sensitive to expensive medical equipment, which is a modern electronic device, and can cause permanent damage and the like. Since these static electricity is generated by friction and contact between the materials, it is difficult to prevent the generation of the static electricity. Therefore, it is necessary to remove, neutralize, and leak generated electric charges in order to prevent the electrostatic discharge of such synthetic fibers. As a method of preventing static electricity, temperature and humidity control, corona discharge and the like are widely used, and some of them are surface treated with an antistatic agent for fibers mainly comprising an activator as an antistatic method.

또한, 종래의 통상의 모시 직물지의 경우, 수작업에 의한 모시원사 제조 및 수직기에 의한 직물지의 제조로 한정되어 기계화 직조의 이용이 불가능하였을 뿐만 아니라, 또한 제직시 모시 한 올이 경사로 사용되므로 강도, 신도 및 섬유 굵기의 불균형 등으로 장력에 견디지 못하여 사절이 발생하였다. 모시섬유의 특성상 제직시 높은 습도를 유지하는 것이 필요한데, 기계화 직조로 인한 많은 결점으로 인해 생산성 향상 및 광폭화가 불가능하였다. 한편 새로운 형태의 모시방적사의 제조 기술로서, 모시원사를 이용한 복합사 제조기술에 의한 기계화 직조기술 및 편직기술의 자동화 생산기술이 소개되었으나, 이러한 방법으로 제조된 모시 직물과 편직물은 모시제품이 갖는 특성을 그대로 나타낼 수 없다는 결점을 가지고 있다.
In addition, in the case of conventional woolen fabrics, the use of mechanized woven fabrics is limited to the production of woolen fabrics by hand and the production of woven fabrics by a vertical machine, and in addition, And the unevenness of the fiber thickness. Due to the nature of the wool fibers, it is necessary to maintain high humidity during weaving, but it is impossible to improve the productivity and widen the productivity due to many drawbacks due to the mechanized weaving. On the other hand, as a manufacturing technique of a new type of spinning yarn, there has been introduced a mechanized weaving technique and a production technology of automatic knitting technology by a composite yarn manufacturing technique using ramie yarn. However, the ramie fabric and the knitted fabric manufactured by this method have characteristics Can not be expressed as it is.

대한민국 등록특허공보 제10-1155077호(2012.06.04.)Korean Registered Patent No. 10-1155077 (June 4, 2012) 대한민국 공개특허공보 제10-2011-0044571(2011.04.29.)Korean Patent Publication No. 10-2011-0044571 (April 29, 2011)

본 발명은 폴리프로필렌 방적사 또는 커버링사를 사용하여 직물을 제조함에 있어서, 폴리프로필렌 섬유의 소수성으로 인해 발생되는 제직상의 문제점과 결점으로 인한 불량률을 해결하기 위한 방법을 제공하기 위한 것으로서, 본발명의 제조방법에 의해 제조된 폴리프로필렌/모시 교직물 제품 또는 자카드직물 제품은 정전기가 저하된다는 특성을 나타낸다.The present invention provides a method for solving the defect rate due to problems and defects in the weaving process caused by the hydrophobicity of the polypropylene fiber in the production of a fabric using a polypropylene yarn or covering yarn, The polypropylene / ramie fabric product or jacquard fabric product produced by the method exhibits the characteristic that static electricity is degraded.

본 발명은 경사로서 폴리프로필렌 방적사 또는 커버링사를 이용하고, 위사로서 이용한 폴리프로필렌/모시 교직물에 관한 것으로, 상기 경사의 제조 방법은 (a) 폴리프로필렌 방적사 또는 커버링사를 준비하는 단계; (b) 상기 폴리프로필렌 방적사 또는 커버링사에 2 내지 5중량%의 친수화제로 처리하는 단계; 및 (c) 7 내지 10중량%의 호부처리제(카르복시메틸셀룰로스, 폴리비닐알코올, 탄수화물, 아크릴)로 처리하는 단계를 포함하는 것을 특징으로 한다.The present invention relates to polypropylene / woven fabrics used as weft yarns using polypropylene yarns or covering yarns as warp yarns, which method comprises the steps of: (a) preparing a polypropylene yarn or covering yarn; (b) treating the polypropylene yarn or covering yarn with 2 to 5% by weight of a hydrophilic agent; And (c) 7 to 10% by weight of an antiseptic agent (carboxymethyl cellulose, polyvinyl alcohol, carbohydrate, acrylic).

본 발명의 또 다른 적절한 실시 형태에 따르면, 상기 위사의 제조방법은 (a) 모시 방적사를 준비하는 단계; (b) 모시 방적사를 왁스로 처리하는 단계를 포함하는 것을 특징으로 한다.According to another preferred embodiment of the present invention, the method of manufacturing a weft yarn comprises the steps of: (a) preparing a warp yarn; (b) treating the fleece yarn with wax.

본 발명은 상기 경사와 위사를 공급하여 직조하는 방식을 갖는 폴리프로필렌/모시 교직물의 제조방법을 제공하는 것을 목적으로 한다.
A further object of the present invention is to provide a method for producing a polypropylene / woven fabrics having a method of weaving by feeding the warp and weft.

본 발명에서 제조된 폴리프로필렌/모시 교직물은 평활성이 우수하고, 집속성이 저하되지 않고 균일하며, 정전기 발생을 줄일 수 있는 우수한 물성을 나타낸다.The polypropylene / woven fabrics produced in the present invention exhibit excellent smoothness, uniform properties without deteriorating the collector properties, and excellent physical properties capable of reducing the generation of static electricity.

또한, 본 발명은 폴리프로필렌/모시를 이용한 고 생산성의 기계화 직조가 용이하고 기계화 제직시 사절이 발생하지 않으며, 폴리프로필렌의 정전기를 방지할 수 있을 뿐만 아니라, 모시섬유의 기능성을 유지할 수 있다는 장점이 있다. 게다가 본 발명의 제조방법은 후가공 공정에 의하여, 다양한 문양의 폴리프로필렌/모시 교직물을 제조할 수 있다는 특징이 있어서,기계화 직조방법으로는 다양한 문양의 자카드 직물지를 제조하는 것이 어렵다는 결점을 해결할 수 있다는 효과가 있다.In addition, the present invention is advantageous in that it is easy to mechanically weave a high productivity using polypropylene / ramie yarns and does not cause yarn breakage during mechanized weaving, can prevent static electricity of polypropylene, and can maintain the functionality of ramie fibers have. In addition, since the manufacturing method of the present invention is characterized in that it is possible to produce polypropylene / woven fabrics of various patterns by post-processing, it is possible to solve the drawback that it is difficult to manufacture jacquard fabrics of various patterns as the mechanized weaving method .

또한 본 발명의 폴리프로필렌/모시 교직물의 다양한 문양의 자카드 직물지는 직조디자인 방법에 따라 기계화 직조의 광폭화 제조가 가능하고, 또한 폴리프로필렌의 소수성의 특징과 모시의 고유기능을 유지함으로써 높은 부가가치를 창츨할 수 있다는 경제성을 가진다. In addition, the jacquard fabrics of various patterns of the polypropylene / woven fabrics of the present invention can be widened in accordance with the weaving design method, and the hydrophobic characteristics of the polypropylene and the inherent functions of the ramie are maintained, It is economical to be able to.

도 1은 본 발명의 경사에 폴리프로필렌 방적사 또는 폴리프로필렌 커버링사를 개략적으로 나타낸 것이다.
도 2는 본 발명에 따른 상기 원사를 이용한 자카드 직물지 직조공정 상세도 이다. 1 schematically shows a polypropylene yarn or polypropylene covering yarn in the warp of the present invention.
2 is a detailed view of a jacquard weaving fabric weaving process using the yarn according to the present invention.

본 발명은 경사로서 폴리프로필렌 방적사 또는 커버링사를 사용하고, 위사로서 모시 방적사를 사용하여 폴리프로필렌/모시 교직물 또는 자카드 직물을 직조하는 제조 기술에 관한 것이다. The present invention relates to a fabrication technique for weaving polypropylene / rayon fabrics or jacquard fabrics using polypropylene yarns or covering yarns as warp yarns and wool yarn as weft yarns.

또한, 폴리프로필렌/모시 교직물를 이용한 기계화 직조기술에 의한 광폭화와 다양한 문양의 자카드 직물지를 제조하는 기술에 관한 것이다. The present invention also relates to a technique for widening by mechanized weaving techniques using polypropylene / woven fabrics and a technique for manufacturing jacquard fabrics of various patterns.

구체적으로, 상기 교직물 또는 자카드 직물의 제조방법은 기계화 직기 또는 자카드직기의 직조디자인 방법에 의해 종래의 제직용 원사의 경사, 위사를 모노필라멘트형 원사로 대체하여 직물지를 직조하는 것에 관한 것이다. Specifically, the method for producing a fabric or a jacquard fabric relates to weaving a fabric by replacing the warp and weft of a conventional weft yarn with a monofilament yarn by a mechanized weaving machine or a weaving design method of a jacquard machine.

본 발명에서의 폴리프로필렌/모시 교직물은 아래와 같은 방법으로 제조될 수 있다. The polypropylene / ramie fabric according to the present invention can be produced by the following method.

유선, 상기 경사의 제조 방법은 (a) 폴리프로필렌 방적사 또는 커버링사를 준비하는 단계; (b) 상기 폴리프로필렌 방적사 또는 커버링사에 2 내지 5중량%의 친수화제(옥틸나트륨설폰숙신산)로 처리하는 단계; 및 (c) 7 내지 10중량%의 호부처리제(카르복시메틸셀룰로스, 폴리비닐알코올, 탄수화물, 아크릴)로 처리하는 단계를 포함하는 것을 특징으로 한다.A method of producing a wire, the warp comprising: (a) preparing a polypropylene yarn or covering yarn; (b) treating the polypropylene yarn or covering yarn with 2 to 5 wt% of a hydrophilic agent (octyl sodium sulfonesuccinic acid); And (c) 7 to 10% by weight of an antiseptic agent (carboxymethyl cellulose, polyvinyl alcohol, carbohydrate, acrylic).

본 발명의 또 다른 적절한 실시 형태에 따르면, 상기 위사의 제조방법은 (a) 모시 방적사를 준비하는 단계; (b) 모시 방적사를 왁스로 처리하는 단계를 포함하는 것을 특징으로 한다.According to another preferred embodiment of the present invention, the method of manufacturing a weft yarn comprises the steps of: (a) preparing a warp yarn; (b) treating the fleece yarn with wax.

본 발명은 상기 경사와 위사를 공급하여 직조하는 방식을 갖는 폴리프로필렌/모시 교직물의 제조방법을 제공하는 것을 목적으로 한다. A further object of the present invention is to provide a method for producing a polypropylene / woven fabrics having a method of weaving by feeding the warp and weft.

본 발명에 따른 폴리프로필렌/모시 교직물의 제조 방법에 대하여 첨부된 도면을 참조하여 보다 상세히 설명한다. A method for producing a polypropylene / woven fabric according to the present invention will be described in more detail with reference to the accompanying drawings.

도1은 본 발명에 따른 폴리프로필렌 경사와 모시 위사를 이용한 교직물을 직조하는 공정의 상세도이며, 도2는 본 발명에서 따른 폴리프로필렌/모시 교직물을 이용한 자카드 직물지를 직조하는 공정의 상세도이다. FIG. 1 is a detailed view of a process of weaving a woven fabric using a polypropylene warp and a warp yarn according to the present invention, and FIG. 2 is a detailed view of a process of weaving a jacquard fabric using a polypropylene / woven fabric according to the present invention.

본 발명에 따른 폴리프로필렌 방적사 또는 커버링사(12)는 모시방적사(13)로 이루어지는 교직물은 도1과 같이 경사빔(22)에서 송출된 여러 가닥의 폴리프로필렌방적사 또는 커버링사(12)와 북(25)에 감겨진 위사용 모시방적사(13)가 서로 교차하여 제조된다. The polypropylene yarn or covering yarn 12 according to the present invention is characterized in that the woven fabric made up of the warp yarns 13 comprises a plurality of strands of polypropylene yarns or covering yarns 12 delivered from the warp beam 22, 25 are wound around the staple yarns 13 to form a yarn.

다양한 문양의 폴리프로필렌/모시 자카드 직물지 경우, 도2와 같이 폴리프로필렌원사(12) 모시원사(13)를 판지로 되어있는 카드(34)를 통해 무늬를 형성하는 기계화된 자카드 직기를 이용하여, 경사용 폴리프로필렌원사(12)를 자카드가 종광(40)에 적용시켜 제조되며, 본 방명에 따른 자카드 직물지의 제조방법은 한개의 카드(34)가 한 개구의 형태를 결정하여 줌으로써 하나의 무늬를 완성하는데 상당하는 매수의 카드(34)를 필요로 한다.
As shown in Fig. 2, the polypropylene yarn 12 is made of a mechanized jacquard loom, which forms a pattern through the card 34 made of cardboard, in the case of various patterns of polypropylene / The method of manufacturing jacquard fabrics according to the present invention is characterized in that a single card 34 determines the shape of one opening to complete one pattern The number of cards 34 is required.

10: 직물빔 12: 경사용 폴리프로필렌원사
13: 위사용 모시원사 24: 종광
26: 바디 34: 카드
40: 자카드기 종광10: Fabric beam 12: Lightweight polypropylene yarn
13: Stitch yarn 24: Hemp
26: Body 34: Card
40: jacquard heavily

Claims (3)

경사로서 폴리프로필렌 방적사 또는 커버링사를 이용하고, 위사로서 모시 방적사를 이용하여 폴리프로필렌/교직물을 제조하는데에 있어서,
상기 경사는 (a) 폴리프로필렌 방적사 또는 커버링사를 준비하는 단계;
(b) 방적된 폴리프로필렌 원사를 2 내지 5중량%의 친수화제로 처리하는 단계; 및
(c) 7 내지 10중량%의 호부처리제로 처리하는 단계를 포함하는 것으로 제조되고,
상기 위사는 (a) 모시 방적사를 준비하는 단계;
(b) 모시 방적사를 왁스로 처리하는 단계를 포함하는 것을 특징으로 하는 폴리프로필렌/모시 교직물의 제조방법.In the production of polypropylene / coated fabrics using polypropylene yarns or covering yarns as warp yarns and wool yarn as weft yarns,
Wherein the warp comprises: (a) preparing a polypropylene yarn or covering yarn;
(b) treating the spun polypropylene yarn with 2 to 5 weight percent of a hydrophilic agent; And
(c) treating with 7 to 10% by weight of an anti-foaming agent,
(A) preparing a ramie yarn;
(b) treating the ramie yarn with wax. < Desc / Clms Page number 20 > 제 1항에 있어서,
상기 친수화제는 디옥틸나트륨설폰숙신산으로 쓰이고,
상기 호부처리제는 카르복시메틸셀룰로스, 폴리비닐알코올, 탄수화물, 아크릴 중에서 선택되는 것을 특징으로 하는 폴리프로필렌/모시 교직물의 제조방법.The method according to claim 1,
The hydrophilic agent is used as dioctyl sodium sulfosuccinic acid,
Wherein the excrement treating agent is selected from carboxymethyl cellulose, polyvinyl alcohol, carbohydrate, and acrylic. 제 1항 또는 제 2항의 제조방법으로 부터 제조된 폴리프로필렌/모시 교직물.A polypropylene / ramie fabric produced from the process of any one of claims 1 or 2.
KR1020130016412A 2013-02-15 2013-02-15 Manufacturing method of combination fabrics using polypropylene/ramie fiber KR101400939B1 (en)