KR101361174B1 - Stacked structure for water proof or heat insulation and its constructing method - Google Patents
Stacked structure for water proof or heat insulation and its constructing method Download PDFInfo
- Publication number
- KR101361174B1 KR101361174B1 KR1020120001739A KR20120001739A KR101361174B1 KR 101361174 B1 KR101361174 B1 KR 101361174B1 KR 1020120001739 A KR1020120001739 A KR 1020120001739A KR 20120001739 A KR20120001739 A KR 20120001739A KR 101361174 B1 KR101361174 B1 KR 101361174B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproof sheet
- nonwoven fabric
- waterproof
- woven
- waterproofing
- Prior art date
Abstract
방수 또는 단열을 위해 콘크리트 구조물의 바닥 또는 측벽에 시공되는 적층구조물이 개시된다. 이 적층 구조물은 상기 바닥 또는 측벽 상에 고정되는 방수시트와, 상기 방수시트 상에 고정된 부직포와, 스프레이 공법에 의해 상기 부직포 위에 형성되는 폴리우레아 마감층을 포함한다.Laminated structures are disclosed that are constructed on the bottom or sidewall of a concrete structure for waterproofing or insulation. The laminated structure includes a waterproof sheet fixed on the bottom or sidewall, a nonwoven fabric fixed on the waterproof sheet, and a polyurea finish layer formed on the nonwoven fabric by a spray method.
Description
본 발명은 건축물의 내외부 방수에 이용되는 적층구조물 및 이의 시공을 통한 건축물의 방수방법에 관한 것으로서, 더 상세하게는, 폴리우레아를 이용하는 방수용 적층구조물 및 이의 시공방법에 관한 것이다.The present invention relates to a laminated structure used for internal and external waterproofing of a building and a waterproofing method of the building through its construction, and more particularly, to a waterproof laminated structure using polyurea and a construction method thereof.
통상 건축물은 방수 또는 단열 시공이 요구된다. 방수 시공은 그 시공 위치에 따라 옥상 방수 시공, 지붕 방수 시공, 내벽 방수 시공 또는 외벽 방수 시공 등을 포함한다. 단열 시공은 저온창고, 냉동 창고, 버섯 재배사 또는 각종 사일로 탱크 등의 단열 또는 방열에 적용된다. 더 나아가, 지하철로, 지하도, 지하차도, 박스 구조물(Box structure) 또는 터널, 건축물 옥상, 지하주차장 상부, 지하층 외벽 등에는 구조물의 안전과 내구성을 위하여 누수를 방지하기 위한 방수 시공이 요구된다. Normally, buildings are required to be waterproof or insulated. Waterproof construction includes roof waterproofing, roof waterproofing, inner wall waterproofing or outer wall waterproofing depending on the construction location. Insulation construction is applied to the insulation or heat dissipation of low temperature warehouses, freezing warehouses, mushroom growers or various silo tanks. Furthermore, waterproof construction is required to prevent leakage for the safety and durability of structures such as subways, underpasses, underground roadways, box structures or tunnels, rooftops of buildings, upper part of underground parking lots, and basement outer walls.
통상 건축물 등의 방수 시공은 콘크리트 바닥 또는 벽면에 프라이머 층을 형성하고, 그 위에 여러 차례에 걸쳐 방수층 및/또는 도막층을 형성하는 방식으로 이루어진다. 일련의 공정들이 모두 시공 현장에서 모두 이루어지므로, 먼저 작업한 도막이 굳기 전에는 다음 작업이 어려워 시공 기간이 길어지며, 시공이 복잡하다는 문제점이 있다.In general, waterproof construction of a building or the like is performed by forming a primer layer on a concrete floor or a wall, and forming a waterproof layer and / or a coating layer on a plurality of times. Since a series of processes are all performed at the construction site, the first work is difficult before the next work is hardened, the construction period is long, and the construction is complicated.
본 발명의 발명자는 건축물의 방수 시공에 공장에서 미리 제작된 방수 시트를 이용하는 기술이 제안한다. 이러한 기술은 콘크리트 바닥 또는 벽면에 미리 제작된 방수 시트를 깔고 그 위에 마감층을 형성한다. 마감층과 방수 시트 사이에 별도의 도막층을 더 두는 것도 고려된다. The inventor of the present invention proposes a technique using a waterproof sheet made in advance in the factory for waterproof construction of buildings. This technique lays a prefabricated waterproof sheet on a concrete floor or wall and forms a finishing layer thereon. It is also contemplated to have a separate coating layer between the finish layer and the waterproof sheet.
그러나, 이 기술은 방수 시트와 그 위의 층 사이에 결합력이 약하여, 내구성이 떨어진다. 게다가, 절기 변화에 따라 또는 주변의 온도 조건의 변화에 따라 방수 시트가 팽창 및 수축을 거듭하며, 이로 인해, 방수 시트의 특정 영역, 특히, 다른 방수 시트와 인접하는 영역에서 비틀림을 야기하며, 더 나아가, 마감층 및/또는 도막층에 손상을 야기할 수 있다.However, this technique has a weak bonding force between the waterproof sheet and the layer thereon, which results in poor durability. In addition, the waterproof sheet expands and contracts with changing seasons or with changes in ambient temperature conditions, thereby causing torsion in certain areas of the waterproof sheet, in particular, in areas adjacent to other waterproof sheets, and more In addition, damage to the finish and / or coating layer may occur.
본 발명이 해결하고자 하는 하나의 과제는, 종래기술의 문제점을 해결하기 위한 것으로서, 방수시트와 그 위에 시공되는 층과의 접합력을 높이기 위해 부직포를 일체화하고, 방수 및 단열 성능이 좋은 폴리우레아층으로 마감층을 시공하여, 내구성, 방수성 및 단열성을 높인, 방수 또는 단열을 위한 적층구조물을 제공하는 것이다. One problem to be solved by the present invention is to solve the problems of the prior art, to integrate a non-woven fabric to increase the bonding strength between the waterproof sheet and the layer to be constructed thereon, as a polyurea layer having good waterproof and thermal insulation performance The construction of the finishing layer is to provide a laminate structure for waterproofing or insulation, which has increased durability, waterproofness and insulation.
본 발명이 해결하고자 하는 다른 과제는 특정 영역에서 방수시트와 그에 인접한 방수시트를 신축 이음재로 연결하여, 절기 변화 등으로 인한 온도 변화에 에 따른 방수시트의 수축 및 팽창으로 일어날 수 있는 방수시트의 영구 변형과 그로 인한 마감층 및/또는 도막층의 손상을 억제할 수 있는 방수 또는 단열을 위한 적층구조물을 제공하는 것이다.Another problem to be solved by the present invention is to connect the waterproof sheet and the adjacent waterproof sheet in the specific area by the expansion joint, the permanent of the waterproof sheet that can occur due to shrinkage and expansion of the waterproof sheet due to temperature changes due to the season change, etc. It is to provide a laminated structure for waterproofing or thermal insulation that can suppress deformation and damage to the finishing layer and / or coating layer thereby.
본 발명의 일측면에 따라, 방수 또는 단열을 위해 콘크리트 구조물의 바닥 또는 측벽에 시공되는 적층구조물이 제공되며, 이 적층구조물은, 상기 바닥 또는 측벽 상에 고정되는 방수시트와, 상기 방수시트 상에 고정된 부직포와, 스프레이 공법에 의해 상기 부직포 위에 형성되는 폴리우레아 마감층을 포함한다.According to one aspect of the invention, there is provided a laminated structure to be installed on the bottom or sidewall of the concrete structure for waterproofing or heat insulation, the laminate is a waterproof sheet fixed on the floor or sidewall, and on the waterproof sheet A fixed nonwoven fabric and a polyurea finish layer formed on the nonwoven fabric by a spray method.
일 실시예에 따라, 상기 부직포와 상기 방수시트는 시공 현장 밖에서 합지되어 부직포 붙이 방수시트로 형성되고, 복수의 부직포 붙이 방수시트는 방수시트가 상기 바닥 또는 상기 측벽의 바탕면을 향하도록 고정된다.According to an embodiment, the nonwoven fabric and the waterproof sheet are laminated outside the construction site to form a nonwoven waterproof sheet, and the plurality of nonwoven waterproof sheets are fixed such that the waterproof sheet faces the bottom surface of the floor or the sidewall.
일 실시예에 따라, 상기 복수의 부직포 붙이 방수시트 각각은 이웃하는 부직포 붙이 방수 시트와 중첩되게 배치되고, 이웃하는 부직포 붙이 방수시트의 중첩 영역을 패스너가 관통해 상기 바탕면에 박힘으로써, 상기 복수의 부직포 붙이 방수시트가 고정된다.According to an embodiment, each of the plurality of nonwoven fabric waterproof sheets is disposed so as to overlap with a neighboring nonwoven fabric waterproof sheet, and the plurality of nonwoven fabric waterproof sheets are fastened through the overlapping area of the neighboring nonwoven fabric waterproof sheet and embedded in the base surface. Non-woven waterproof sheet is fixed.
일 실시예에 따라, 상기 적층구조물은 상기 폴리우레아 마감층과 상기 부직포 사이에 개재된 도막층을 더 포함한다.According to one embodiment, the laminate structure further comprises a coating layer interposed between the polyurea finish layer and the nonwoven fabric.
일 실시예에 따라, 상기 도막층과 폴리우레아 층을 시공 현장 밖에서 상기 부직포에 도포되어 형성된다.According to one embodiment, the coating layer and the polyurea layer is formed by applying to the nonwoven fabric outside the construction site.
일 실시예에 따라, 상기 도막층은 시공 현장에서 상기 바닥 또는 측벽에 고정된 방수시트 상의 부직포 상에 도막 재료를 도포하여 형성된다.According to one embodiment, the coating layer is formed by applying a coating material on the non-woven fabric on the waterproof sheet fixed to the floor or sidewall at the construction site.
일 실시예에 따라, 상기 방수시트는 PVC, TPO, 또는 EVA 계열 수지로 이루어진다.According to one embodiment, the waterproof sheet is made of PVC, TPO, or EVA-based resin.
일 실시예에 따라, 상기 복수의 부직포 붙이 방수시트는 상기 바닥에 고정되되 측벽 상으로 연장된 제1 부직포 붙이 방수시트를 포함하고, 상기 측벽에 고정된 제2 부직포 붙이 방수시트는 상기 제1 부직포 붙이 방수시트와 이격되며, 상기 적층구조물은 상기 제1 부직포 붙이 방수시트와 상기 제2 부직포 붙이 방수시트 사이를 연결하는 신축 이음재를 더 포함할 수 있다.According to an embodiment, the plurality of nonwoven fabric waterproof sheets may include a first nonwoven fabric waterproof sheet secured to the bottom but extending on a sidewall, and the second nonwoven fabric waterproof sheet secured to the sidewall may be the first nonwoven fabric. It is spaced apart from the waterproof sheet, the laminated structure may further include an expansion joint for connecting between the first nonwoven fabric waterproof sheet and the second nonwoven fabric waterproof sheet.
일 실시예에 따라, 상기 방수시트는 절개 영역을 포함하되, 상기 방수시트의 저면에 접합되어 상기 절개 영역을 덮는 보수용 방수편을 더 포함한다.According to an embodiment, the waterproof sheet further includes a cutout region, and further includes a repair waterproof piece bonded to the bottom of the waterproof sheet to cover the cutout region.
본 발명의 다른 측면에 따라, 건축물의 콘크리트 바닥 또는 측벽의 방수 또는 단열을 위한 적층구조물의 시공방법이 제공되며, 이 시공방법은 방수시트의 일면에 부직포를 합지하여, 부직포 붙이 방수시트를 제조하는 단계와, 상기 바닥 또는 측벽의 바탕면에 상기 방수시트가 향하도록 상기 바탕면에 부직포 붙이 방수시트를 고정하는 단계와, 상기 부직포 붙이 방수시트 위에 스프레이 공법으로 폴리우레아를 도포하여 폴리우레아 마감층을 형성하는 단계를 포함한다.According to another aspect of the present invention, there is provided a construction method of a laminated structure for waterproofing or insulating the concrete floor or sidewall of the building, this construction method by laminating a nonwoven fabric on one side of the waterproof sheet, to produce a non-woven waterproof sheet Fixing the non-woven waterproof sheet to the base surface such that the waterproof sheet faces the bottom or sidewall of the floor or sidewall, and applying a polyurea to the non-woven waterproof sheet by spraying to form a polyurea finish layer. Forming a step.
일 실시예에 따라, 상기 시공방법은 상기 부직포 붙이 방수시트를 고정하는 단계 전에 상기 바탕면을 청소, 정리 및 씰링하는 단계를 더 포함한다.According to one embodiment, the construction method further comprises the step of cleaning, cleaning and sealing the base surface before the step of fixing the nonwoven fabric waterproofing sheet.
일 실시예에 따라, 부직포 붙이 방수시트를 고정하는 단계는 복수의 부직포 붙이 방수시트를 중첩되게 배치하고, 패스너로 이웃하는 부직포 붙이 방수시트들의 중첩 영역을 관통하여 상기 바탕면에 고정하는 것을 포함한다.According to one embodiment, the step of fixing the nonwoven waterproofing sheet includes a plurality of nonwoven waterproofing sheets overlapping, and fastening to the base surface through the overlapping area of neighboring nonwoven waterproofing sheets with a fastener. .
일 실시예에 따라, 상기 부직포 붙이 방수시트와 부직포 붙이 방수시트 중첩된 부분에 상기 폴리우레아를 더 형성하되, 상기 도막층과 폴리우레아층은 상기 부직포 붙이 방수시트를 제조하는 단계에서 도막층 및 폴리우레아층을 상기 부직포에 도포하여 형성된다.According to one embodiment, the non-woven waterproof sheet and the non-woven waterproof sheet is further formed with the polyurea, wherein the coating layer and the polyurea layer is a coating layer and poly in the step of manufacturing the non-woven waterproof sheet It is formed by applying a urea layer to the nonwoven fabric.
일 실시예에 따라, 상기 부직포 붙이 방수시트의 부직포와 상기 폴리우레아층 사이에 도막층을 더 형성하되, 상기 도막층은 상기 부직포 붙이 방수시트를 고정하는 단계 후에 상기 부직포 상에 도막 재료를 도포하여 형성된다.According to an embodiment, a coating layer is further formed between the nonwoven fabric of the nonwoven fabric waterproof sheet and the polyurea layer, wherein the coating layer is coated with the coating material on the nonwoven fabric after fixing the nonwoven fabric waterproof sheet. Is formed.
일 실시예에 따라, 상기 부직포 붙이 방수시트를 고정하는 단계와 상기 폴리우레아 마감층을 형성하는 단계 사이에 상기 방수시트의 절개 영역을 보수용 방수편을 이용하여 보수하는 단계를 더 포함할 수 있다.According to an embodiment of the present disclosure, the method may further include repairing a cutout region of the waterproof sheet using a repair waterproof piece between fixing the nonwoven fabric waterproof sheet and forming the polyurea finish layer. .
일 실시예에 따라, 상기 부직포 붙이 방수 시트를 고정하는 단계는 상기 바닥의 바탕면에 부직포 붙이 방수시트를 고정하고 상기 측벽의 바탕면 상에 상기 부직포 붙이 방수시트와 이격되게 다른 부직포 방수시트를 고정하며, 상기 서로 이격된 부직포 방수시트들 사이를 신축 이음재로 연결하는 것을 포함하며, 상기 폴리우레아 마감층을 형성하는 단계는 상기 바닥 및 상기 측벽의 바닥면들에 고정된 부직포 붙이 방수시트들과 상기 신축 이음재를 모두 덮도록 폴리우레아 마감층을 형성한다.According to an embodiment, the fixing of the nonwoven fabric waterproof sheet may include fixing the nonwoven fabric waterproof sheet to the base surface of the bottom and fixing the nonwoven waterproof sheet spaced apart from the nonwoven fabric waterproof sheet on the base surface of the sidewall. And connecting the spaced apart nonwoven fabric waterproof sheets to each other with a stretch joint material, wherein the forming of the polyurea finish layer comprises nonwoven fabric waterproof sheets fixed to the bottom and bottom surfaces of the sidewall and the nonwoven fabric. A polyurea finish layer is formed to cover all of the stretch joints.
본 발명의 다른 측면에 따라, 방수 또는 단열을 위해 건축물에 시공되는 적층구조물이 제공된다. 이 적층구조물은, 제1 부직포 붙이 방수시트와; 상기 제1 부직포 붙이 방수시트와 이격되게 배치된 제2 부직포 붙이 방수시트와, 상기 제1 부직포 붙이 방수시트와 상기 제2 부직포 붙이 방수시트 사이를 연결하는 신축 이음재와, 상기 제1 부직포 붙이 방수시트, 상기 제2 부직포 붙이 방수시트 및 상기 신축 이음재를 모두 덮도록 형성되는 도막층 또는 마감층을 포함한다.According to another aspect of the present invention, there is provided a laminated structure which is constructed in a building for waterproofing or insulation. The laminated structure includes a first nonwoven fabric waterproof sheet; A second nonwoven waterproof sheet disposed to be spaced apart from the first nonwoven waterproof sheet, an elastic joint member connecting the first nonwoven waterproof sheet and the second nonwoven waterproof sheet, and the first nonwoven waterproof sheet The coating layer or the finishing layer is formed to cover all of the second nonwoven fabric waterproof sheet and the expansion joint material.
일 실시예에 따라, 상기 신축 이음재의 양측은 상기 제1 부직포 붙이 방수시트와 상기 제2 부직포 붙이 방수시트의 부직포 상에 부착된다.According to one embodiment, both sides of the expansion joint is attached to the nonwoven fabric of the first nonwoven waterproof sheet and the second nonwoven waterproof sheet.
본 발명에 따르면, 방수시트와 그 위에 시공되는 층과의 접합력을 높이기 위해 부직포를 일체화하고, 방수 및 단열 성능이 좋고 고탄력을 갖는 폴리우레아층으로 마감층을 시공하여, 내구성, 방수성 및 단열성을 높인, 방수 또는 단열을 위한 적층구조물을 구현하여 건축물의 콘크리트 바닥 및 콘크리트 내외 벽면에 적용할 수 있다. 본 발명의 한 실시예에 따르면, 온도에 따라 팽창 또는 수축된 방수시트의 영구 변형에 대하여, 특정 영역의 방수시트의 이음 부위에 고탄력을 갖는 신축 이음재를 마련해, 그 신축 이음재가 방수시트의 수축 및 팽창에 따라 탄력적으로 작용하여, 방수시트의 비틀림 및 그로 인한 방수 구조의 내구성 저하를 막을 수 있다.According to the present invention, the nonwoven fabric is integrated to increase the bonding strength between the waterproof sheet and the layer constructed thereon, and the finishing layer is constructed of a polyurea layer having good waterproof and heat insulating performance and high elasticity, thereby improving durability, waterproofness, and heat insulation. By implementing a laminated structure for waterproofing or insulation, it can be applied to the concrete floor of the building and the inside and outside walls of the building. According to one embodiment of the present invention, with respect to the permanent deformation of the waterproof sheet expanded or contracted according to temperature, a flexible joint member having a high elasticity is provided at the joint portion of the waterproof sheet in a specific region, and the stretch joint member is used to contract the waterproof sheet and It acts resiliently upon expansion, preventing twisting of the waterproof sheet and thereby lowering durability of the waterproof structure.
도 1은 본 발명의 일 실시예에 따른 건축물의 방수/단열을 위한 적층구조물을 설명하기 위한 단면도.
도 2는 본 발명의 다른 실시예에 따른 건축물의 방수/단열을 위한 적층구조물을 설명하기 위한 단면도.
도 3은 본 발명의 또 다른 실시예에 따른 건축물의 방수/단열을 위한 적층구조물을 설명하기 위한 단면도.
도 4는 본 발명에 따른 방수 또는 단열을 위한 적층구조물의 시공방법을 설명하기 위한 공정 순서도.1 is a cross-sectional view for explaining a laminated structure for waterproof / insulation of the building according to an embodiment of the present invention.
Figure 2 is a cross-sectional view for explaining a laminated structure for waterproof / insulation of the building according to another embodiment of the present invention.
Figure 3 is a cross-sectional view for explaining a laminated structure for waterproof / insulation of the building according to another embodiment of the present invention.
Figure 4 is a process flow chart for explaining the construction method of the laminated structure for waterproofing or insulation according to the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. 또한, 본 발명의 실시예는 당해 기술분야에서 통상의 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위하여 제공되는 것이며, 하기 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. In addition, the embodiments of the present invention are provided to more fully explain the present invention to those skilled in the art, the following examples can be modified in various other forms, the scope of the present invention Is not limited to the following examples.
도 1은 본 발명의 일 실시예에 따른 방수용 적층구조물을 설명하기 위한 단면도이다.1 is a cross-sectional view illustrating a waterproof laminate structure according to an embodiment of the present invention.
도 1을 참조하면, 콘크리트 건축물의 일부가 보여지며, 이 콘크리트 건축물은 콘크리트 바닥(2) 및 그 콘크리트 바닥(2)에 수직으로 세워진 콘크리트 측벽(4)을 포함한다. 본 실시예에 따른 방수용 적층 구조물(100)은 콘크리트 바닥(2)과 콘크리트 측벽(4)에 시공되어 있다. 방수용 적층 구조물이 시공되는 콘크리트 바닥(2)의 면과 콘크리트 측벽(4)의 면을 공히 '바탕면'이라 정의하고 도면부호 B를 부여한다.Referring to FIG. 1, a portion of a concrete structure is shown, which includes a
상기 방수용 적층 구조물(100)은 상기 바탕면(B)로부터 차례로 방수시트(110), 부직포(120) 및 마감층(140)을 포함한다. The waterproof laminated
상기 방수시트(110)는, 시공 장소가 아닌 공장에서 제작된 것으로, PVC(Poly Vinyl Chloride), TPO(Thermo Plastic Olefin Polymer) 또는 EVA(Ethylene Vinyl Acetate) 계열 재료로 제작될 수 있다. 상기 부직포(120)는 예를 들면 폴리에스터 재료로 만들어진 것일 수 있으며, 시공 장소가 아닌 공장에서 상기 방수시트(110)의 상면에 일체로 합지된다. 상기 부직포(110)는 예를 들면 열 접합 방식에 의해 상기 방수시트(110)의 일면에 합지된다..The
상기 마감층(140)은 시공 현장에서 형성된 폴리우레아층을 포함하며, 이 폴리우레아층은 폴리우레아를 스프레이 공법에 의해 방수시트(100)와 부직포(120)가 일체화된 상부에 도포하여 형성된다. 상기 마감층, 즉, 상기 폴리우레아층(140)은 방수시트(110)에 대해 접합이 잘 안되지만, 폴리우레아가 상기 부직포(120)의 망목들에 채워지도록 도포되어 형성되므로, 상기 부직포(120)가 있는 방수시트(110)의 상면에 신뢰성 있게 접합될 수 있다. The
마감층, 즉, 폴리우레아층(140)을 형성하는 폴리우레아는 주재료인 이소시아네이트(Isocyanate)와 반응제인 폴리아민(Polyamine)이 결합하여 우레아로 형성된 것으로서, 도포 후 1분 이내에 경화가 완료될 정도로 경화속도가 빠르다. 이러한 빠른 경화 속도는 방수용 적층구조물의 시공 시간을 줄이는데 크게 기여한다. 또한, 폴리우레아는 솔벤트를 사용하지 않아 친환경적이며, 경사면, 수직면, 천정면 등 시공면에 제한을 받지 않는다. 전술한 것과 같은 초속경화 폴리우레아는 위와 같은 시공 상의 장점 외에 방수 특성이 좋고, 외관이 우수하며, 부식 방지 특성도 좋아 건축물의 방수 또는 단열재료로서 매우 적합하다. The polyurea forming the finishing layer, that is, the
방수시트(110)의 재료는 PVC(Poly Vinyl Chloride), TPO(Thermo Plastic Olefin Polymer) 또는 EVA(Ethylene Vinyl Acetate) 계열의 수지가 이용된다. 이들 수지를 방수시트(110)와 함께 이용될 때의 단점인 방수시트(110)에 대한 나쁜 접착성은 방수시트(110)에 일체화된 부직포(120)에 의해 해결된다. 설명의 편의를 위해 방수 시트(110) 및 그 방수 시트(110)의 일면에 의해 일체화된 부직포(120)를 포함하는 시트재를 부직포 붙이 방수 시트(M)라 정의한다.As the material of the
본 실시예에 따르면, 콘크리트 바닥(2) 상에는 복수의 부직포 붙이 방수 시트(M)가 배치된다. 이웃하는 부직포 붙이 방수 시트(M)들은 서로 중첩되어 있으며, 체결구(F)가 이웃하는 부직포 붙이 방수 시트(M, M)들의 중첩 영역을 관통하여 콘크리트 바닥(2)에 박힘으로써 상기 부직포 붙이 방수 시트(M)들이 고정된다. 또한, 부직포(120)를 방수시트(110)의 모서리를 지나도록 더 연장하여, 이웃하는 부직포 붙이 방수 시트(M, M)들의 부직포 연장부들을 예를 들면 열풍에 의해 열 접합하면, 부직포 붙이 방수 시트(M, M)들 간에 더 신뢰성 연결을 보장할 수 있다. According to this embodiment, a plurality of nonwoven fabric waterproof sheets M are disposed on the
또한, 다른 부직포 붙이 방수 시트(M)가 동일 또는 유사한 방식으로 콘크리트 측벽(4)에 고정된다. In addition, the other nonwoven waterproof sheet M is fixed to the
콘크리트 바닥(2)의 부직포 붙이 방수 시트(M)가 연장되어 일정 높이로 콘크리트 측벽(4)에 고정될 수 있다. 이때, 콘크리트 바닥(2)으로부터 연장된 부직포 붙이 방수 시트(M)와 콘크리트 측벽(4)에 고정된 부직포 붙이 방수 시트(M)는 이격된다. The nonwoven waterproof sheet M of the
위와 같이 서로 이격된 부직포 붙이 방수 시트(M)들 사이를 연결하도록 신축 이음재(150)가 설치된다. 상기 신축 이음재(150)는 일측과 타측에서 상기 부직포 붙이 방수시트들(M, M)의 부직포(120, 120)들에 접합된다. 방수시트(110)가 절기 변화 또는 그로 인한 온도 변화에 따라 수축 또는 팽창하지만, 상기 신축 이음재(150)는 고탄력을 가지므로 방수시트(110)의 수축 또는 팽창을 탄성적으로 잡아주어 방수시트(110)의 비틀림을 막을 수 있다. 상기 신축 이음재(150)는 예를 들면 라텍스와 같은 고탄력 재료를 포함할 수 있다.Stretch joint 150 is installed to connect between the non-woven waterproof sheet (M) spaced apart from each other as described above. The
콘크리트 바닥(2) 및 콘크리트 측벽(4)에 미리 설치된 부직포 붙이 방수 시트(M)를 덮도록 마감층인 폴리우레아층(140)이 형성된다. 상기 폴리우레아층(140)은 앞에서도 설명한 바와 같이, 스프레이 공법에 의해 형성되며, 초급속으로 경화된다. 상기 폴리우레아층(140)은 폴리우레아를 스프레이 공법을 이용하여 2회 또는 그 이상 실시하여 형성될 수 있다. A
도 2는 본 발명의 다른 실시예에 따른 방수용 적층구조물을 설명하기 위한 단면도이다.2 is a cross-sectional view illustrating a waterproof laminate structure according to another embodiment of the present invention.
도 2를 참조하면, 본 실시예에 따른 방수용 적층구조물(100)은 폴리우레아층(140)과 부직포 붙이 방수 시트(M) 사이에 개재된 도막층(130)을 포함할 수 있다. 상기 도막층(130)은 방수 또는 단열 기능을 갖는 도막 재료를 상기 부직포 붙이 방수시트(M)의 부직포(120)에 발라 형성될 있다. 도막 재료는 방수 및/또는 단열 성능이 좋음과 동시에 그 위에 형성되는 폴리우레아층(140)과의 접착성 또한 좋은 재료가 선택된다. 본 실시예에서는, 폴리우레탄이 도막층(130)의 재료로 이용되었다. 도막층(130) 또한 도막 재료를 몇 번에 걸쳐 도포하여 형성될 수 있다. 상기 도막층 및 폴리우레아층을(130) 시공 현장이 아닌 공장에서 부직포 붙이 방수 시트(M)에 미리 형성될 수 있다. 그러나, 시공 현장에서 형성될 수도 있음은 물론이다. 상기 도막 재료도 상기 부직포(120)의 망목들에 의해 상기 부직포 붙이 방수 시트(M)에 견고하고 신뢰성 있게 접착된다.Referring to FIG. 2, the
도 3은 본 발명의 다른 실시예에 따른 방수용 적층구조물을 설명하기 위한 단면도이다. 도 3을 참조하면, 건축물의 코너 영역에서 방수시트(110)가 부분적으로 제거되어 있고, 이에 의한 콘크리트 노출 부분이 방수시트(110)와 동일 재료로 이루어진 보수용 방수편(110a)에 의해 막혀 보수되고 있다. 상기 보수용 방수편(110a)은 상기 방수시트(110)의 제거된 영역보다 넓은 면적을 가지며, 상기 방수시트(110)의 하부면, 부직포가 없는 면 아래에서 그 면에 열에 의해 접합된다.3 is a cross-sectional view illustrating a waterproof laminate structure according to another embodiment of the present invention. Referring to FIG. 3, the
도 4는 본 발명에 따른 방수 또는 단열을 위한 적층구조물의 시공방법을 설명하기 위한 순서도이다.4 is a flowchart illustrating a construction method of a laminated structure for waterproofing or heat insulating according to the present invention.
도 4를 참조하면, 본 실시예에 따른 시공방법은, 부직포 붙이 방수시트 제조 단계(s1)와, 현장 시공 준비 단계(s2)와, 부직포 붙이 방수시트 고정 단계(s3)와, 마감층 형성 단계(s4)를 포함한다.Referring to Figure 4, the construction method according to the embodiment, the non-woven waterproof sheet manufacturing step (s1), the site construction preparation step (s2), the non-woven waterproof sheet fixing step (s3) and the finishing layer forming step (s4).
부직포 붙이 방수시트 제조 단계(s1)는 시공현장이 아닌 공장에서 수행되며, PVC(Poly Vinyl Chloride), TPO(Thermo Plastic Olefin Polymer) 또는 EVA(Ethylene Vinyl Acetate) 계열의 방수시트의 일면에 예를 들면 폴리에스터 재료로 만들어진 부직포를 합지하여 부직포 붙이 방수시트 제조한다. 이때, 부직포 상으로 도막층 및 폴리우레아을 추가로 형성할 수 있다. 도막층과 폴리우레아층은 생략될 수 있으며, 또한, 공장이 아닌 시공현장에서 부직포 상으로 형성될 수도 있다. 이때, 부직포는 방수시트의 일측 모서리를 넘어 연장되도록 부착될 수 있다. 그 부직포의 연장부는 시공 현장에서 이웃하는 부직포 붙이 방수시트를 연결할 때 이용될 수 있다. Non-woven waterproof sheet manufacturing step (s1) is carried out at the factory, not the construction site, for example on one side of the waterproof sheet of PVC (Poly Vinyl Chloride), TPO (Thermo Plastic Olefin Polymer) or EVA (Ethylene Vinyl Acetate) series Non-woven fabric made of polyester material is laminated to produce a non-woven waterproof sheet. In this case, the coating layer and the polyurea may be further formed on the nonwoven fabric. The coating layer and the polyurea layer may be omitted, and may also be formed as a nonwoven fabric at a construction site other than a factory. In this case, the nonwoven fabric may be attached to extend beyond one side edge of the waterproof sheet. The extension of the nonwoven fabric can be used to connect neighboring nonwoven waterproof sheets at construction sites.
현장 시공 준비 단계(s2)는 건축물의 콘크리트 바닥 또는 내외 측벽의 바탕면에 대해 수행된다. 이 현장 시공 준비 단계(s2)는 바탕면 청소 및 정리, 바탕면 씰링, 탈기공 설치 등의 작업을 포함할 수 있다. The site construction preparation step s2 is performed on the concrete floor of the building or on the base surface of the inner and outer sidewalls. This site construction preparation step (s2) may include operations such as cleaning and cleaning the ground surface, sealing the ground surface, and installing the deaerator.
부직포 붙이 방수시트 고정 단계(s3)는 콘크리트 바닥 및/또는 콘크리트 측벽의 바탕면에 복수의 부직포 붙이 방수시트를 배열하고 고정하는 것을 포함한다. 부직포 붙이 방수시트의 배치는 방수시트가 바탕면을 향하도록 그리고 부직포가 바탕면의 반대편을 향하도록 이루어진다. 부직포 붙이 방수시트들을 모서리 부근에서 중첩되게 배치하고, 패스너가 부직포 붙이 방수시트의 중첩된 하부 영역을 관통하여 바탕면에 박힘으로써 부직포 붙이 방수시트들이 바탕면에 고정된다. 이때, 이웃하는 부직포 붙이 방수시트들의 연장부를 열풍으로 접할 수 있다.The step of fixing the nonwoven waterproof sheet (s3) includes arranging and fixing the plurality of nonwoven waterproof sheets on the concrete floor and / or the base surface of the concrete sidewall. The placement of the nonwoven waterproof sheet is such that the waterproof sheet faces the substrate and the nonwoven fabric faces away from the substrate. The nonwoven waterproof sheets are disposed on the base surface by overlapping the nonwoven waterproof sheets with a fastener penetrating the overlapping lower region of the nonwoven waterproof sheet. At this time, the extensions of the adjacent nonwoven fabric waterproof sheets may be in contact with hot air.
상기 부직포 붙이 방수시트 고정 단계(s3)는 콘크리트 측벽 바탕면 상에 고정된 부직포 붙이 방수 시트와 그와 이격된 채 콘크리트 바닥 바탕면으로부터 콘크리트 측벽 바탕면 상으로 연장된 부직포 붙이 방수 시트 사이를 고탄력을 갖는 신축 이음재로 연결하는 작업을 포함할 수 있다. 앞에서도 설명한 바와 같이, 방수시트가 절기 변화 또는 그로 인한 온도 변화에 따라 수축 또는 팽창하지만, 상기 신축 이음재가 고탄력을 가지므로 방수시트의 수축 또는 팽창을 탄성적으로 잡아주어 방수시트의 비틀림을 막을 수 있다. The non-woven waterproof sheet fixing step (s3) is a high elasticity between the non-woven waterproof sheet secured on the concrete side wall base surface and the non-woven waterproof sheet extended from the concrete floor base surface to the concrete side wall surface spaced apart therefrom. It may include connecting to the expansion joint having. As described above, the waterproof sheet shrinks or expands according to the season change or the resulting temperature change, but since the expansion joint material has high elasticity, the waterproof sheet elastically grips the contraction or expansion of the waterproof sheet to prevent the waterproof sheet from twisting. have.
마감층 형성 단계(s4)는 부직포 붙이 방수시트들을 덮도록 폴리우레아를 도포하여 이루어진다. 마감층과 부직포 붙이 방수시트들의 부직포들 사이에 도막층과 폴리우레아층이 있을 수 있는데, 이 도막층 및 폴리우레아층은 공장에서 부직포 상에 도막 재료를 도포하여 형성될 수 있고, 시공 현장에서 마감층 형성 직전에, 도막 재료를 부직포 상에 도포하여 형성될 수 있다. 폴리우레아층 여러 회에 걸친 폴리우레아의 스프레이 작업에 의해 형성될 수 있다 Finishing layer forming step (s4) is made by applying a polyurea to cover the non-woven waterproof sheet. There may be a coating layer and a polyurea layer between the nonwoven fabric of the finishing layer and the non-woven waterproof sheets, which may be formed by applying a coating material onto the nonwoven fabric at the factory and finishing at the construction site. Immediately before layer formation, the coating film material may be formed by applying onto a nonwoven fabric. Polyurea layer can be formed by spraying polyurea over several times
마감층 형성 단계(s4) 이전, 또는 마감층 형성 단계(s4) 직전의 도막층 형성 단계 이전에, 부직포 붙이 방수시트의 절개부를 보수용 방수편으로 보수하는 작업이 수행될 수 있다. 건축물의 코너 영역 또는 돌출부 또는 오목부가 존재하는 영역에서는 작업의 편의를 위해 방수시트의 일부를 절개할 필요가 있는데, 그 절개된 영역은 방수시트의 역할을 대신할 수 있는 보수용 방수편으로 보수한다. 상기 방수편은 방수시트와 열 접합이 잘 될 수 있는 동일 또는 유사 재료로 선택된다. 보수용 방수편은 절개 영역보다 큰 면적을 가져야 하며, 부직포가 아닌 방수시트의 면에 접촉하도록 배치된다.Before the finishing layer forming step (s4), or before the coating layer forming step immediately before the finishing layer forming step (s4), the operation of repairing the cutout portion of the non-woven waterproof sheet with a waterproof waterproof piece may be performed. In the corner area of the building or in the area where protrusions or recesses exist, it is necessary to cut a part of the waterproof sheet for the convenience of the work. . The waterproof piece is selected from the same or similar material that can be well thermally bonded with the waterproof sheet. The repair waterproofing piece should have a larger area than the incision area and is arranged to contact the surface of the waterproof sheet, not the nonwoven fabric.
도 5는 본 발명의 또 다른 실시예에 따른 건축물의 방수/단열을 위한 적층구조물을 설명하기 위한 단면도이다.5 is a cross-sectional view for explaining a laminated structure for waterproofing / insulating a building according to another embodiment of the present invention.
도 5를 참조하면, 이웃하는 부직포 붙이 방수 시트(M, M)들이 이격된 상태로 콘크리트 바닥(2)에 고정되어 있고, 이웃하는 부직포 붙이 방수 시트(M, M)들 사이는 앞선 실시예에서 설명된 것과 같은 신축 이음재(150)에 의해 맞대어 연결되어 있다. 그 위로는 도막층(130, 140')들이 형성되되, 상기 도막층들은 무기질 탄성 도막 방수재로 이루어진 무기질 탄성 도막층(140')을 포함한다. 본 실시예에서는, 무기질 탄성 도막층(140')이 앞선 실시예에서 설명된 것과 같은 일반 도막층 위에 형성되었지만, 그 일반 도막층이 생략되고 부직포 붙이 방수 시트(M, M)들과 신축 이음재(150)를 바로 덮도록 무기질 탄성 도막층(140')이 형성될 수 있다. 또한, 상기 무기질 탄성 도막층(140')은 중간 도막층 또는 마감 도막층으로 이용될 수 있다. 그리고, 본 실시예에서는, 앞선 실시예에서 설명된 것과 같은 폴리우레아층이 생략되었지만, 상기 무기질 탄성 도막층(140')은 폴리우레아층의 상부 또는 하부에 위치하는 층으로 이용될 수 있다.Referring to FIG. 5, the neighboring nonwoven waterproof sheets M and M are fixed to the
상기 무기질 탄성 도막층(140')을 구성하는 무기질 탄성 복합 방수재는, 공중합 고분자 에멀전 무기질 파우더로 형성될 수 있으며, 방수성, 탄성 및 접착력이 우수하다.The inorganic elastic composite waterproofing material constituting the inorganic
이 무기질 탄성 도막층(140')은 내열성, 내후성, 내동결 융해성이 뛰어나, 크랙 방지 효과가 우수하며. 염분, 알카리 등에 대한 물리적 화학적 저항성이 우수한다. 그리고, 콘크리트에 무해한 무기질의 무독성재료이다, 이 무기질 탄성 도막층(140')은 공장 또는 시공 현장에서 무기질 탄성 도막 방수재를 도포하여 형성될 수 있으며, 현장에서 시공시 탄성 도막 방수재를 붓이나 로울러로 균일하게 도포하여 형성될 수 있다. The inorganic elastic coating layer 140 'is excellent in heat resistance, weather resistance, and freezing and melting resistance, and has an excellent crack prevention effect. It has excellent physical and chemical resistance to salt, alkali and the like. The inorganic elastic coating layer 140 'may be formed by applying an inorganic elastic coating waterproofing material at a factory or a construction site, and applying the elastic coating waterproofing material to a brush or roller at the construction site. It can be formed by applying uniformly.
바람직한 일 실시예에 따라, 상기 무기질 탄성 도막층(140')은 [표 1]의 구성비를 갖는 액상 재료 69 중량부와 [표 2]의 구성비를 갖는 분말 재료 100 중량부를 혼합하여 얻어진 무기질 탄성 도막 재료에 의해 형성될 수 있다.According to a preferred embodiment, the inorganic
Claims (19)
방수시트의 일면에 부직포를 합지하여, 부직포 붙이 방수시트를 제조하는 단계;
상기 바닥 또는 측벽의 바탕면에 상기 방수시트가 향하도록 상기 바탕면에 부직포 붙이 방수시트를 고정하는 단계와;
상기 부직포 붙이 방수시트 위에 스프레이 공법으로 폴리우레아를 도포하여 폴리우레아 마감층을 형성하는 단계를 포함하는 것을 특징으로 하는 방수 또는 단열을 위한 적층구조물의 시공방법.In the construction method of the laminated structure for waterproofing or insulating the concrete floor or sidewall of the building,
Manufacturing a non-woven waterproof sheet by laminating a nonwoven fabric on one surface of the waterproof sheet;
Fixing the nonwoven fabric waterproof sheet to the base surface such that the waterproof sheet faces the base surface of the bottom or sidewall;
A method of constructing a laminated structure for waterproofing or insulation, comprising the step of forming a polyurea finish layer by applying a polyurea on the non-woven waterproof sheet with a spray method.
상기 폴리우레아 마감층을 형성하는 단계는 상기 바닥 및 상기 측벽의 바닥면들에 고정된 부직포 붙이 방수시트들과 상기 신축 이음재를 모두 덮도록 폴리우레아 마감층을 형성하는 것을 특징으로 하는 방수 또는 단열을 위한 적층구조물의 시공방법.The method of claim 10, wherein fixing the nonwoven fabric waterproof sheet is fixed to the nonwoven fabric waterproof sheet on the base surface of the bottom and the other nonwoven waterproof sheet spaced apart from the nonwoven fabric waterproof sheet on the base surface of the side wall It includes connecting between the spaced apart non-woven waterproof sheets with elastic joint material,
Forming the polyurea finish layer is waterproof or heat-insulating, characterized in that to form a polyurea finish layer to cover both the non-woven waterproof sheet and the expansion joint fixed to the bottom surface of the bottom and the side wall Construction method of laminated structure for.