KR101352409B1 - Filler for artificial turf having charcoal adsorption layer - Google Patents
Filler for artificial turf having charcoal adsorption layer Download PDFInfo
- Publication number
- KR101352409B1 KR101352409B1 KR1020130013959A KR20130013959A KR101352409B1 KR 101352409 B1 KR101352409 B1 KR 101352409B1 KR 1020130013959 A KR1020130013959 A KR 1020130013959A KR 20130013959 A KR20130013959 A KR 20130013959A KR 101352409 B1 KR101352409 B1 KR 101352409B1
- Authority
- KR
- South Korea
- Prior art keywords
- filler
- weight
- parts
- adsorption layer
- charcoal
- Prior art date
Abstract
Description
본 발명은 숯흡착층을 가지는 인조잔디용 충진재에 관한 것으로서 더욱 상세하게는 열가소성 탄성체에 다공성을 가지는 목분을 첨가하여 펠렛형태로 제조한 다음 펠렛 외부면의 일정 부분에 정전기 발생을 방지하고 미세먼지 흡착기능이 우수한 숯흡착층을 형성함에 따라 목분의 수분흡수 및 방열기능과 숯흡착층의 정전기 발생 방지기능이 융화된 숯흡착층을 가지는 인조잔디용 충진재 및 이의 제조방법에 관한 것이다.
The present invention relates to a filler for artificial turf having a charcoal adsorption layer, and more specifically, to a thermoplastic elastomer, wood powder having a porosity is added to produce a pellet, and then to prevent static electricity from adhering to a portion of the outer surface of the pellet and adsorbing fine dust. The present invention relates to a filling material for artificial turf having a charcoal adsorption layer in which moisture absorption and heat dissipation of wood flour and anti-static function of the charcoal adsorption layer are fused, thereby forming a charcoal adsorption layer having excellent function, and a method of manufacturing the same.
인조잔디는 천연잔디의 감촉을 지니면서 오래 사용할 수 있고 유지비가 적게 들며 쿠션으로 인한 부상을 방지하는 등의 장점으로 세계적으로 크게 설치가 증가해오고 있다.Artificial turf has the texture of natural grass, can be used for a long time, has a low maintenance cost, and prevents the injury caused by cushion.
인조잔디 구조로는 카페트형 인조잔디에 천연잔디와 유사한 질감을 부여하기 위하여 고무칩과 모래를 충진하는 방식의 인조잔디가 많이 사용되고 있다. 그러나 인조잔디 충진재로 사용되는 폐타이어 고무칩으로부터 발생하는 유해성이 사회적 이슈로 등장하고 있다.Artificial turf structure is a kind of artificial turf which is filled with rubber chips and sand to give a carpet-like artificial turf similar texture to natural turf. However, the hazard caused by the waste tire rubber chip used as artificial turf filler is emerging as a social issue.
폐타이어 고무칩은 검은색을 띠고 있기 때문에 태양광을 흡수하여 구장의 온도를 상승시키므로 운동환경을 악화시킬 수 있다. 기온이 섭씨 30℃를 넘어가는 여름이면 고무칩에서 매캐한 냄새가 발생하며 뜨거운 지열에 녹아내린 고무칩이 달라붙기도 한다. 분쇄에 의해 폐타이어칩이 만들어지는 공정 특성상 장기간 사용시 분쇄칩이 부스러지면서 분진을 유발하여 주변을 오염시킬 수 있다. 유럽에서는 인조잔디에서 중금속, 다핵방향족 탄화수소, 톨루엔, 벤젠, 니트로사민등 유해물질이 검출되었다는 보고가 나오고 있으며 인조잔디 충진재로 폐타이어를 대체할 대체물질에 대한 요구가 확대되고 있다.Since the waste tire rubber chip is blackish, it absorbs the sunlight and raises the temperature of the ballpark, which can deteriorate the running environment. In the summer when the temperature exceeds 30 ° C, there is a smell coming from the rubber chip, and the rubber chip melted in the hot geothermal heat may stick to it. Due to the characteristics of the process of producing waste tire chips by pulverization, the pulverized chips may be crushed during long-term use, causing dust to contaminate the surroundings. In Europe, it has been reported that harmful substances such as heavy metals, polynuclear aromatic hydrocarbons, toluene, benzene and nitrosamine have been detected in artificial turf, and the demand for alternative materials to replace waste tires with artificial turf filler is increasing.
이에 따라 유해성이 있는 폐타이어칩을 대신해 최근 사용되고 있는 EPDM고무를 가교시켜 만든 고무칩의 경우, 가교된 물질을 칩으로 만들기 위해서는 필수적으로 분쇄를 거쳐야하고 이 분쇄칩은 시공 후 분진을 발생시키므로 비산문제가 있고 불규칙한 표면형상에 의해서 고무칩 사이에 불필요한 공간이 발생하여 고무칩 간의 응집력을 분산시키므로 잔디가 적절히 지지되지 못하는 단점이 있다.Therefore, in the case of a rubber chip made by crosslinking EPDM rubber which is recently used instead of a harmful waste tire chip, it is essential to grind the crosslinked material in order to make it into a chip. This grinding chip generates dust after construction, And an unnecessary space is generated between the rubber chips due to the irregular surface shape, so that the cohesion between the rubber chips is dispersed, so that the grass is not properly supported.
한국 공개특허공보 10-0799262호에는 스티렌-에틸렌부타디엔-스티렌(SEBS), 올레핀계 탄성체, 미네랄 오일, 무기 충전제, 내후성 안정제 및 무기 안료를 포함하는 친환경 인조잔디용 충진재 조성물이 기재되어 있다.Korean Unexamined Patent Publication No. 10-0799262 discloses an environmentally friendly filler composition for artificial turf including styrene-ethylenebutadiene-styrene (SEBS), olefinic elastomer, mineral oil, inorganic filler, weathering stabilizer and inorganic pigment.
상기 문헌에는 칩이 분쇄에 의해 제조되는 것이 아닌 압출에 의한 펠렛 형상으로 제조되어 시공 후 분진이 발생하지 않게 된다.In this document, chips are produced in pellet form by extrusion, rather than by grinding, so that dust does not occur after construction.
하지만 이러한 인조잔디용 충진재들은 여름철 정오 무렵에서와 같이 강한 직사광선으로부터 노출될 경우 상당히 뜨거워지게 되어 인조잔디 사용자들이 마찰로 화상이 발생할 우려가 있으며, 잦은 정전기로 인해 사용자의 불편이 초래되었다.However, these artificial turf fillers are quite hot when exposed to strong direct sunlight, such as around midday in the summer, the artificial turf users may be burned by friction, and frequent static electricity caused user inconvenience.
아울러 장시간 사용할 경우 인조잔디 내에 축적된 미세먼지 등이 사용자들의 기관지 등으로 흡입되어 건강을 해치게 된다. In addition, when used for a long time, the fine dust accumulated in the artificial turf is inhaled into the bronchus of the user and harm the health.
따라서 이러한 충진재로 인한 화상 우려 및 정전기, 미세먼지 등을 효과적으로 제거할 수 있는 인조잔디용 충진재의 개선이 요구된다.
Therefore, there is a need for improvement of fillers for artificial turf, which can effectively remove burn concerns, static electricity, and fine dust caused by such fillers.
본 발명은 상기의 문제점을 해결하기 위해 안출된 것으로서 열가소성 탄성체에 다공성을 가지는 목분을 첨가함으로써 수분 및 미세먼지 등을 흡수하는 보습 및와 필터링 효과가 향상됨은 물론 인조잔디의 온도가 상승할 경우 흡수한 수분을 서서히 발산함으로써 온도를 하강시키는 온도조절기능을 수행하며 상기 목분이 첨가된 충진재 상에 일정 부분 숯흡착층을 형성함으로써 다량의 음이온을 방출하여 정전기 발생을 억제하고 다공성 구조로 인해 미세먼지를 흡착율이 우수한 숯흡착층을 가지는 인조잔디용 충진재 및 이의 제조방법을 제공함에 그 목적이 있다.
The present invention has been made to solve the above problems, by adding wood powder having a porosity to the thermoplastic elastomer to improve the moisturizing and filtering effect of absorbing moisture and fine dust, as well as moisture absorbed when the temperature of the artificial turf rises By gradually releasing the temperature control function to lower the temperature, and by forming a certain charcoal adsorption layer on the wood powder added filler to release a large amount of negative ions to suppress the generation of static electricity and the adsorption rate of fine dust due to the porous structure It is an object of the present invention to provide an artificial turf filler having a superior charcoal adsorption layer and a method of manufacturing the same.
본 발명은 상기의 목적을 달성하기 위해 아래와 같은 특징을 갖는다.The present invention has the following features in order to achieve the above object.
본 발명은 인조잔디 하부측에 충진되는 인조잔디용 충진재에 있어서, 상기 충진재는 열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 포함하는 조성물을 압출 및 펠렛화하여 제조하되, 상기 펠렛화된 충진재의 외부면 또는 내부면에는 숯흡착층이 형성된다.The present invention is a filler for artificial turf is filled in the artificial turf lower side, the filler is 5 to 50 parts by weight of wood powder, 10 to 50 parts by weight of wood powder binder, 100 to 400 parts by weight of inorganic filler, It is prepared by extruding and pelletizing a composition comprising 50 to 200 parts by weight of mineral oil and 2 to 10 parts by weight of a processing aid for changing the physical properties of the elastic body and preventing color discoloration, and on the outer surface or the inner surface of the pelletized filler An adsorption layer is formed.
여기서 상기 숯흡착층은 상기 펠렛화된 충진재의 외부면에 도포되어 형성되거나 충진재의 외부면을 일정 부분 스크래칭하여 형성되는 홈부에 도포되어 형성되며, 상기 숯흡착층은 숯분말과 바인더를 혼합한 숯도포제에 상기 펠렛화된 충진재를 딥코팅 또는 분무코팅하여 형성된다.Here, the charcoal adsorption layer is formed by being applied to the outer surface of the pelletized filler is formed or applied to the groove portion formed by scratching a portion of the outer surface of the filler, the charcoal adsorption layer is charcoal mixed with the charcoal powder and binder It is formed by dip coating or spray coating the pelletized filler in the coating agent.
아울러 본 발명의 다른 실시예로 상기 숯흡착층은 펠렛화된 충진재의 내측에 형성되되, 상기 충진재는 외측으로부터 물이 내부를 관통하여 배출되도록 관통로가 하나 이상 형성된다. In addition, in another embodiment of the present invention, the charcoal adsorption layer is formed inside the pelletized filler, wherein the filler is formed with one or more passages through which water is discharged from the outside.
아울러 본 발명에 따른 인조잔디용 충진재의 제조방법은 열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 혼합하여 조성물을 생성하는 단계와; 상기 생성된 조성물을 압출하여 펠렛화하여 1차 충진재를 제조하는 단계와; 상기 1차 충진재의 외부면에 바인더 용제 100 중량부에 대해 숯분말 30 내지 60 중량부를 혼합하여 제조된 숯도포제를 도포하여 2차 충진재를 생성하는 단계;를 포함하여 이루어진다.In addition, the method for preparing artificial turf filler according to the present invention is 5 to 50 parts by weight of wood powder, 10 to 50 parts by weight of wood powder binder, 100 to 400 parts by weight of inorganic filler, and 50 to 200 parts by weight of mineral oil based on 100 parts by weight of thermoplastic elastomer. And mixing 2 to 10 parts by weight of a processing aid for changing physical properties of the elastic body and preventing color fading to produce a composition; Extruding the resulting composition to pelletize to prepare a primary filler; Forming a secondary filler by applying a charcoal coating agent prepared by mixing 30 to 60 parts by weight of the charcoal powder with respect to 100 parts by weight of the binder solvent on the outer surface of the primary filler.
여기서 상기 숯도포제를 도포하기 전에 1차 충진재의 외부면을 일정 부분 스크래칭하여 홈부를 형성한 후 홈부에 숯도포제를 도포하여 숯흡착층이 형성된다.
Here, before applying the charcoal coating agent, the outer surface of the primary filler is scratched to form a groove portion, and then the charcoal coating agent is applied to the groove portion to form a charcoal adsorption layer.
본 발명에 따르면 다공성을 가지는 목분의 첨가에 따라 수분을 흡수하여 보습 효과를 가지며, 인조잔디의 온도가 상승할 경우 흡수한 수분을 서서히 발산함으로써 온도를 하강시키는 효과가 있다.According to the present invention has a moisturizing effect by absorbing moisture in accordance with the addition of wood powder having a porosity, and when the temperature of the artificial turf rises, there is an effect of lowering the temperature by gradually releasing the absorbed moisture.
아울러 충진재 외부면 상에 형성되는 스크래치 홈부에 숯흡착층을 형성함에 따라 목분의 기능을 크게 저해하지 않으면서 동시에 숯흡착층의 정전기 발생 방지 및 미세먼지 흡착기능을 유도하는 효과가 있다. In addition, by forming a charcoal adsorption layer on the scratch groove formed on the outer surface of the filler, there is an effect of preventing the generation of static electricity and fine dust adsorption of the charcoal adsorption layer while not significantly inhibiting the function of the wood powder.
또한 충진재 내부에 숯흡착층을 형성하고 충진재 내부가 외부와 연통되도록 관통로를 형성시킴에 따라 오염물질 흡착 효과는 유지하면서 외력에 의한 숯흡착층의 손상을 방지하여 내구성이 증대된다.
In addition, the charcoal adsorption layer is formed inside the filling material and the penetration path is formed so that the inside of the filling material communicates with the outside, thereby maintaining the adsorption of contaminants and preventing damage to the charcoal adsorption layer by external force, thereby increasing durability.
도 1은 본 발명의 일실시예에 따른 충진재의 구조를 나타내는 도면이다.
도 2는 본 발명의 다른 실시예에 따른 충진재의 구조를 나타내는 도면이다.
도 3은 본 발명의 또 다른 실시예에 따른 충진재의 구조를 나타내는 도면이다.
도 4은 본 발명의 일실시예에 따른 충진재의 제조과정을 나타내는 순서도이다.1 is a view showing the structure of a filler according to an embodiment of the present invention.
2 is a view showing the structure of a filler according to another embodiment of the present invention.
3 is a view showing the structure of a filler according to another embodiment of the present invention.
Figure 4 is a flow chart showing the manufacturing process of the filler according to an embodiment of the present invention.
이하에서는 본 발명에 따른 탄성칩에 대해 첨부되는 도면과 함께 상세하게 설명하도록 한다.Hereinafter will be described in detail with the accompanying drawings for the elastic chip according to the present invention.
도 1은 본 발명의 일실시예에 따른 충진재의 구조를 나타내는 도면이며, 도 2는 본 발명의 다른 실시예에 따른 충진재의 구조를 나타내는 도면이다.1 is a view showing the structure of a filler according to an embodiment of the present invention, Figure 2 is a view showing the structure of a filler according to another embodiment of the present invention.
도면을 참조하면 본 발명에 따른 충진재(100)는 열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 포함하는 조성물을 압출 및 펠렛화하여 제조한 다음 상기 펠렛화된 충진재의 외부면에 숯흡착층을 형성하여 이루어진다.Referring to the drawings, the
즉, 본 발명에 따른 충진재(100)는 1차적으로 제조된 펠렛 형태의 충진재층(10)에 그 외부면상으로 전체 또는 일정부분에 숯흡착층(20)을 형성하여 이루어지는 것이다.That is, the
우선 상기 펠렛화된 충진재, 즉 펠렛 형태의 충진재층(10)은 열가소성 탄성체, 목분, 목분바인더, 무기 충전제, 미네랄오일, 가공조제 등이 혼합되어 압출되는데, 여기서 상기 열가소성 탄성체는 목분을 이용한 수지 조성물의 탄성을 유지시켜주기 위하여 첨가되는 것으로서, 상기 목분만 사용하였을 경우에는 상기 목분은 탄성이 좋으나, 상기 목분 사이의 공극이 커서 눌림 현상 등이 일어날 수 있기 때문에 열가소성 탄성체가 혼합됨이 바람직하다.First, the pelletized filler, that is, the
이러한 상기 열가소성 탄성체는 여러 종류가 사용될 수 있으나, 주로 스티렌계 블록 공중합체(styrene block copolymer), 수소첨가된 스티렌계 블록 공중합체(block copolymer), 에틸렌-부틸렌 고무(ethylene butylene rubber), 에틸렌비닐아세테이트(ethylene vinylacetate), α-폴리올레핀계(polyolefin) 탄성체, 염소화 폴리에틸렌(chlorinated polyethlene), 열가소성 폴리우레탄(thermoplastic polyurethane) 등이 사용되며, 이중 하나 또는 하나 이상을 혼합하여 사용한다.The thermoplastic elastomer may be used in various kinds, but mainly styrene block copolymer, hydrogenated styrene block copolymer, ethylene butylene rubber, ethylene vinyl Acetate (ethylene vinylacetate), α-polyolefin elastomer, chlorinated polyethlene, thermoplastic polyurethane and the like are used, and one or more of them are used in combination.
여기서 스티렌계 열가소성 탄성체로는 스티렌-부타디엔-스티렌(SBS), 스티렌-에틸렌·부틸렌-스티렌(SEBS), 스티렌-에틸렌·프로필렌-스티렌 (SEPS), 수소화 폴리 이소프렌-부타디엔(SEEPS), 및 스티렌-이소프렌-스티렌 공중합체(SIS) 등의 스티렌계 공중합체를 단독 또는 조합하여 사용할 수 있다.The styrene-based thermoplastic elastomers include styrene-butadiene-styrene (SBS), styrene-ethylene butylene-styrene (SEBS), styrene-ethylene-propylene-styrene (SEPS), hydrogenated polyisoprene-butadiene (SEEPS), and styrene Styrene-based copolymers such as isoprene-styrene copolymer (SIS) can be used alone or in combination.
아울러 목분은 열가소성 탄성체 100중량부에 대해 5 내지 50중량부를 첨가하게 되는데, 바람직하게는 5 내지 20 중량부를 첨가한다.In addition, the wood powder is added to 5 to 50 parts by weight based on 100 parts by weight of the thermoplastic elastomer, preferably 5 to 20 parts by weight.
이러한 목분의 첨가에 따라 본 발명에 따른 인조잔디용 충진재가 보습효과가 증대됨은 물론 내광성 내열성 내한성이 우수하게 되며 안료 등을 이용하여 조색이 용이하게 될 수 있는 특징을 가진다.According to the addition of wood flour, the filler for artificial turf according to the present invention increases the moisturizing effect, as well as excellent light resistance, heat resistance, cold resistance, and has a feature that can be easily colored using a pigment or the like.
상기 보습효과는 목분의 다공성 구조로 인해 습한 환경에서 수분을 흡수하였다가 건조한 상태에서 서서히 흡수한 수분을 발산함으로써 온도조절 기능을 수행하며 어느 정도의 수분 함유로 인해 사용자가 미끄러질 경우 발생되는 마찰열에 의한 화상을 방지할 수도 있다.The moisturizing effect is a function of temperature control by absorbing moisture in a humid environment due to the porous structure of wood powder and releasing moisture absorbed slowly in a dry state and by frictional heat generated when the user slips due to a certain amount of moisture. Burns can also be prevented.
한편 상기 열가소성 탄성체와 목분이 균일하게 잘 혼합될 수 있도록 목분바인더가 10 내지 50 중량부로 혼합되게 되는데, 바람직하게는 10 내지 40 중량부가 혼합된다.Meanwhile, the wood powder binder is mixed in an amount of 10 to 50 parts by weight so that the thermoplastic elastomer and wood powder are uniformly mixed well, and preferably 10 to 40 parts by weight.
이러한 목분바인더로는 다양하게 선택될 수 있는데, 예를 들면 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene), 폴리스티렌(polystrene), 아클리로니트릴-부타디엔-스티렌 수지(resin), 아크릴로니트릴-스티렌-아크릴레이트수지(acrylonitrile-strene-acrylate resin), 폴리메틸메타크릴레이트(polymethylmethacrylate) 중 하나 또는 하나 이상을 혼합하여 사용될 수 있다.The wood powder binder may be variously selected, for example, polyethylene, polypropylene, polystyrene, acrylonitrile-butadiene-styrene resin, acrylonitrile-styrene- One or more of acrylate resin (acrylonitrile-strene-acrylate resin), polymethylmethacrylate (polymethylmethacrylate) may be used in combination.
또한 본 발명에 따른 인조잔디용 탄성 충진재 조성물에는 무기 충전제가 100 내지 400 중량부, 바람직하게는 270 내지 370 중량부가 첨가되는데, 이러한 무기 충전제는 충진재의 강성을 높이고 열변형을 방지할 목적으로 첨가되며 탄산칼슘(CaCO3), 활석(talc), 운모(mica), 클레이(clay), 실리카(SiO2), 황산바륨(BaSO4), 탄산마그네슘(MgCO3) 등을 단독 또는 조합하여 사용할 수 있으나 가격 측면에서 탄산칼슘이 가장 바람직하다.In addition, the inorganic filler composition for artificial turf according to the present invention is added to the
여기서 상기 무기 충전제가 100 중량부보다 적으면 충진재의 비중이 낮아져 빗물 등에 의해 유실될 수 있고, 400 중량부보다 많으면, 경도가 지나치게 상승하여 탄성감이 없어질 수 있다.If the inorganic filler is less than 100 parts by weight, the specific gravity of the filler may be lowered and may be lost due to rain water. If the amount of the inorganic filler is greater than 400 parts by weight, the hardness may be excessively increased and elasticity may be lost.
한편 본 발명에 따른 충진재에는 미네랄오일이 50 내지 200 중량부, 바람직하게는 50 내지 150 중량부가 첨가되는데, 이러한 미네랄오일은 혼합 컴파운드의 가공성을 향상시키고 무기 충전제의 다량첨가로 인한 경도상승을 방지하여 유연성을 부여할 수 있다.On the other hand, the filler according to the present invention is added to 50 to 200 parts by weight, preferably 50 to 150 parts by weight of mineral oil, such mineral oil improves the processability of the mixed compound and prevents the increase in hardness due to the addition of a large amount of inorganic filler Flexibility can be given.
여기서 상기 미네랄오일이 50 중량부 보다 적으면 가공시 유동성이 저하될 수 있고, 상기 200 중량부 보다 많으면 블리딩(bleeding)의 우려가 있을 수 있다.Here, if the mineral oil is less than 50 parts by weight, fluidity may decrease during processing, and if the mineral oil is more than 200 parts by weight, there may be a bleeding fear.
또한 상기 가공조제는 충진재의 물성변화 및 색상 변색 방지를 위해 2 내지 10 중량부가 첨가되는데, 이러한 가공조제로는 수지 안정제 및 안료 등이 해당된다.In addition, the processing aid is added to 2 to 10 parts by weight in order to change the physical properties of the filler and to prevent color fading, such processing aids include resin stabilizers and pigments.
상기 수지 안정제는 열 안정제, 산화방지제, 자외선 안정제 등이 포함되는데, 여기서 열 안정제는 주석계, 납계, 카드뮴계, 아연계 등이 사용될 수 있고, 산화방지제는 아민계, 페놀계, 인계 등이 사용될 수 있으며, 자외선 안정제는 벤조페논계(Benzophenone), 벤조트리아졸계(Benzotriazole), 힌더드아민계(Hindered amine) 등이 사용될 수 있다.The resin stabilizer includes a heat stabilizer, an antioxidant, a UV stabilizer, etc., wherein the heat stabilizer may be used in the tin-based, lead-based, cadmium-based, zinc-based, etc., the antioxidant is used amine-based, phenol-based, phosphorus-based The UV stabilizer may be benzophenone-based, benzotriazole-based, hindered amine-based, or the like.
또한 상기 안료는 충진재의 색깔이 흑색일 경우, 태양광을 잘 흡수하여 온도 상승의 원인이 될 수 있으므로, 흑색에서 벗어나 다양한 색상을 갖는 탄성 충진재를 제조할 수 있도록 해준다.In addition, when the color of the filler is black, it may absorb the sunlight well and cause a temperature increase, thereby allowing the elastic filler having a variety of colors to be separated from the black.
예를 들어, 인조잔디와 같은 색인 녹색의 안료를 더 포함할 수 있다.For example, it may further comprise a pigment of the index green, such as artificial turf.
이러한 충진재 조성물은 본 발명의 일실시예에 따라 압출 및 펠렛화하여 인조잔디용 탄성 충진재를 제조하게 되는데, 인조잔디용 탄성 충진재는 상술한 인조잔디용 충진재 조성물을 일반적인 압출장치, 즉 밴버리 니더(banbury kneader), 부스니더(Buss kneader), 싱글 스크류 압출기, 트윈 스크류 압출기 등을 사용하여 압출 및 펠렛화함으로써 제조될 수 있다.The filler composition is extruded and pelletized according to an embodiment of the present invention to produce an elastic filler for artificial turf, the elastic filler for artificial turf is a conventional extrusion apparatus, ie Banbury kneader (banbury kneader) kneader), Buss kneader, single screw extruder, twin screw extruder and the like can be produced by extrusion and pelletization.
인조잔디용 충진재 조성물을 압출기에 투입하여 고온에서 압출할 경우, 압출장치의 압축헤드에 입자를 0.5 내지 3 mm 범위로 크기를 조절할 수 있는 다이스를 설치하여 핫 컷팅(hot cutting)이나 언더워터 컷팅(underwater cutting)방식으로 자동 컷팅시키면 평균적으로 0.5 내지 3 mm 크기를 갖는 타원형이나 원형의 펠렛 형상의 칩을 제조할 수 있다.When the filler composition for artificial turf is extruded at a high temperature by inserting it into an extruder, a die that can adjust the size of the particles in the range of 0.5 to 3 mm is installed in the compression head of the extruder so that hot cutting or underwater cutting ( Automatic cutting by the underwater cutting method can produce an elliptical or circular pellet-shaped chip having an average size of 0.5 to 3 mm.
상술한 인조잔디용 탄성 충진재는 폐타이어처럼 분쇄된 칩이 아니라 균일한 입자크기로 압출하여 제조한 펠렛 형상으로 이루어졌기 때문에 분진을 발생시키지 않고 내열성 및 탄성이 우수하며 인체에 무해하고 환경문제를 일으키지 않는다.The above-mentioned elastic filler for artificial turf is not a pulverized chip like a waste tire but a pellet formed by extruding into a uniform particle size. Therefore, it does not generate dust, has excellent heat resistance and elasticity, is harmless to the human body, Do not.
이에 따라 펠렛화된 충진재는 그 외부면의 전체 또는 일정 부분에 숯흡착층(20)이 형성되는데, 이러한 상기 숯흡착층(20)은 상기 펠렛화된 충진재의 외부면에 도포되어 형성되거나 충진재의 외부면을 일정 부분 스크래칭하여 형성되는 홈부에 도포되어 형성된다.Accordingly, the pelletized filler is formed on the whole or a portion of the outer surface of the
여기서 상기 숯흡착층은 숯분말과 바인더를 혼합한 숯도포제를 상기 펠렛화된 충진재의 외부면 또는 스크래칭하여 형성된 홈부에 도포하여 형성하는데, 상기 숯분말은 참나무를 1000도 고온에 가열하여 백탄을 생성한 후 500매쉬 크기로 분쇄하여 수득한다. Here, the charcoal adsorption layer is formed by applying a charcoal coating agent mixed with a charcoal powder and a binder to the groove formed by scratching the outer surface of the pelletized filler, wherein the charcoal powder is heated to 1000 degrees high temperature to produce white coal After grinding to 500 mesh size.
물론 참나무 외에도 다양한 나무를 가열하여 숯을 획득할 수 있다.Of course, in addition to oak, various trees can be heated to obtain charcoal.
이에 따라 바인더 100 중량부에 대해 수득한 숯분말 30 중량부 내지 60 중량부를 혼합하여 숯도포제를 생성하며 보다 균일한 혼합을 위해 별도의 분산제를 추가로 혼합할 수 있다.Accordingly, 30 to 60 parts by weight of the obtained charcoal powder is mixed with respect to 100 parts by weight of the binder to produce a charcoal coating agent, and a further dispersant may be further mixed for more uniform mixing.
상기 숯흡착층을 펠렛화된 충진재의 일정 부분에만 형성하기 위해 펠렛화된 충진재를 부분적으로 스크래칭하여 홈부를 형성한 후 상기 숯도포제를 홈부상에 도포하는데, 펠렛화된 충진재의 원활한 스크래칭을 위해 별도의 점착시트 상에 상기 펠렛화된 충진재를 고루 펴서 부착시킨 후 그 상부측으로 또 다른 점착시트를 밀착하여 부착한다.In order to form the charcoal adsorption layer only on a predetermined portion of the pelletized filler, the pelletized filler is partially scratched to form a groove, and then the charcoal coating agent is applied to the groove, and is separately used for smooth scratching of the pelletized filler. After spreading the pelletized filler evenly attached to the pressure-sensitive adhesive sheet of another adhesive sheet to adhere to the upper side closely.
그런 다음 상기 상부 또는 하부측에 위치되는 점착시트에 커터 또는 칼 등의 스크래칭 수단으로 스크래칭을 수행한 후 점착시트 상으로 숯도포제를 분무 방식 또는 딥 방식으로 도포하여 건조한다.Then, scratching is performed on the pressure sensitive adhesive sheet positioned on the upper or lower side by a scratching means such as a cutter or a knife, and then the charcoal coating agent is applied onto the pressure sensitive adhesive sheet in a spray or dip manner and dried.
일정 시간 경과 후 숯도포층이 점착시트의 스크래치 부분에 충분히 도포되어 건조되면 점착시트와 충진재를 서로 분리하면 되는데, 이에 따라 분리된 충진재에는 숯흡착층(20)이 형성되게 된다. After a certain period of time, if the charcoal coating layer is sufficiently coated on the scratch portion of the pressure-sensitive adhesive sheet and dried, the pressure-sensitive adhesive sheet and the filler may be separated from each other.
물론 이외에도 다양한 방식으로 펠렛화된 충진재에 일정부분만 숯흡착층이 형성되도록 수행할 수 있으며, 본 발명은 이에 한정되지 않는다. Of course, in addition to the charcoal adsorption layer may be performed to form only a portion of the filler pelletized in various ways, the present invention is not limited thereto.
이와 같은 숯흡착층의 부분 형성에 의해 숯흡착층이 형성되지 않은 충진재의 외부면 상으로는 목분의 기능에 의해 수분을 원활하게 흡수하여 고온에서 열을 방출함으로써 온도조절 기능을 수행하며, 숯흡착층이 형성된 충진재의 외부면 상으로는 다량의 음이온 방출에 의해 정전기 발생이 방지되고 다공성으로 이루어지는 숯의 특성상 미세먼지 등의 흡착이 이루어져 사용자가 인조잔디 사용시 발생되는 미세먼지량이 현격하게 감소된다.
By forming the charcoal adsorption layer, the charcoal adsorption layer does not form the charcoal adsorption layer on the outer surface of the filler to absorb moisture smoothly by the function of wood powder to release the heat at high temperature, the charcoal adsorption layer is Electrostatic generation is prevented by the release of a large amount of negative ions on the outer surface of the formed filler, the adsorption of fine dust, etc. due to the characteristics of the charcoal made of porous, the amount of fine dust generated when the user uses the artificial turf is significantly reduced.
도 3은 본 발명의 또 다른 실시예에 따른 충진재의 구조를 나타내는 도면이다.3 is a view showing the structure of a filler according to another embodiment of the present invention.
도면을 참조하면 본 실시예에 따른 충진재(100)는 그 내부면 내에 숯흡착층이 형성되고 숯흡착층(20) 외측으로 충진재층(10)이 형성되게 된다. Referring to the drawings, the
이를 위해서 다양한 제조 방법이 가능하며, 일예로 숯분말과 바인더를 혼합하여 우선 구형태의 숯칩을 형성한 후 액상 형태의 충진재 조성 혼합물로 숯칩 외측으로 도포시켜 충진재층(10)을 형성하거나 충진재 조성 혼합물에 숯칩을 침지시켜 충진재층(10)을 형성할 수 있을 것이다. To this end, various manufacturing methods are possible. For example, the charcoal powder and the binder are mixed to form a charcoal chip in a spherical shape, and then the
이외에도 다양한 형태로 충진재의 내부측에 숯흡착층(20)이 형성되도록 제조할 수 있으며 본 발명은 이에 한정되지 않는다. In addition, the
한편 본 실시예에 따른 충진재(100)에는 숯흡착층(20)이 외부에 노출되도록 관통로(30)가 형성되는데, 이러한 관통로(30)는 충진재(100)의 일측 외부에서 타측 외부로 관통 형성되는데 이때 충진재(100)의 중심 또는 중심 부근을 지나가도록 관통형성됨이 바람직하다. Meanwhile, in the
이와 같은 관통로(30)의 형성에 의해 숯흡착층(20)이 외부의 직접적 충격을 받지 않게 되면서도 충진재를 통과하는 물이 관통로(30)를 따라 흘러가게 됨에 따라 오염물질을 흡착하는 흡착효과는 유지될 수 있다. Adsorption effect of adsorbing contaminants as the
이는 외면에 숯흡착층(20)이 형성되는 경우 다른 충진재와의 마찰이나 외부 압력에 의해 긁히거나 박리되는 등의 손상이 발생될 수 있는데, 숯흡착층(20)을 충진재층(10)으로 보호함에 따라 숯흡착층(20)의 손상을 감소시킬 수 있으며 이로 인해 먼지 등의 오염물질 흡착효과가 오래 지속될 수 있게 되는 것이다.
When the
도 4는 본 발명의 일실시예에 따른 충진재의 제조과정을 나타내는 순서도이다.Figure 4 is a flow chart showing the manufacturing process of the filler according to an embodiment of the present invention.
도면을 참조하면 본 발명의 일실시예에 따른 충진재 제조방법은 우선 열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 혼합하여 조성물을 생성한다(S100).Referring to the drawings, the method for producing a filler according to an embodiment of the present invention is based on 100 parts by weight of thermoplastic elastomer, 5 to 50 parts by weight of wood powder, 10 to 50 parts by weight of wood powder binder, 100 to 400 parts by weight of inorganic filler, and mineral oil 50 To 200 parts by weight and 2 to 10 parts by weight of the processing aid for changing the physical properties and color fading of the elastic body to produce a composition (S100).
이러한 조성물 생성이 완료되면 생성된 조성물을 별도의 압출기를 통해 압출하여 펠렛 형태로 제조함으로써 1차 충진재를 제조한다(S200).When the production of such a composition is completed, the resulting composition is extruded through a separate extruder to prepare a pellet in order to prepare a primary filler (S200).
이에 따라 제조된 1차 충진재는 별도의 건조과정을 거친 후 상기 1차 충진재의 외부면에 바인더 용제 100 중량부에 대해 숯분말 30 내지 60 중량부를 혼합하여 제조된 숯도포제를 도포하여 2차 충진재를 생성하는 단계(S300)로 이루어진다. The primary filler thus prepared is subjected to a separate drying process and then coated with a charcoal coating agent prepared by mixing 30 to 60 parts by weight of charcoal powder with respect to 100 parts by weight of the binder solvent on the outer surface of the primary filler. Generating step (S300) is made.
전술한 바와 같이 상기 숯도포제는 1차 충진재의 외부 전면에 도포되어 형성될 수 있으나, 목분의 기능과 숯의 기능을 융합하여 유도하도록 1차 충진재의 외부면을 일정 부분 스크래칭하여 홈부를 형성한 후 홈부에 숯도포제를 도포하여 숯흡착층이 형성됨에 바람직하다. As described above, the charcoal coating agent may be applied to the outer front surface of the primary filler, but the groove may be formed by scratching a part of the outer surface of the primary filler to induce the fusion of the wood flour and the charcoal function. Charcoal coating agent is applied to the groove to form a charcoal adsorption layer is preferred.
이에 따라 생성된 본 발명에 따른 인조잔디용 충진재는 천연 물질인 목분 및 숯을 인조잔디 충진재에 함유시켜 그 기능이 천연 물질과 흡사하고 중금속과 휘발성 유기화합물 및 분진의 발생이 없으며 인체에 무해하고, 보습성, 내한성, 내열성, 유해가스 흡착 및 내마모성이 증가됨은 물론 정전기 발생 억제 특성을 가진다.
The artificial turf filler according to the present invention produced by the present invention contains natural wood flour and charcoal in artificial turf filler, its function is similar to that of natural substance, and is free of heavy metals, volatile organic compounds and dust, and harmless to human body. Moisture resistance, cold resistance, heat resistance, harmful gas adsorption and abrasion resistance is increased as well as has the ability to suppress the generation of static electricity.
이와 같이 본 발명은 도면에 도시된 일실시예를 참고로 설명되었으나, 이는 예시적인 것에 불과하며, 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to those precise embodiments, and many alternatives, modifications, and variations will be apparent to those skilled in the art. I will understand.
따라서, 본 발명의 진정한 기술적 보호범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다.
Accordingly, the true scope of the present invention should be determined by the technical idea of the appended claims.
10 : 충진재층 20 : 숯흡착층
30 : 관통로 100 : 충진재10: filling layer 20: charcoal adsorption layer
30: through passage 100: filling material
Claims (6)
상기 충진재는 열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 포함하는 조성물을 압출 및 펠렛화하여 제조하되,
상기 펠렛화된 충진재의 외부면 또는 내부면에는 숯흡착층이 형성되는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재.
In the grass filling material for artificial turf lower side,
The filler is 5 to 50 parts by weight of wood powder, 10 to 50 parts by weight of wood powder binder, 100 to 400 parts by weight of inorganic filler, 50 to 200 parts by weight of mineral oil, and prevention of color change of the elastic body with respect to 100 parts by weight of thermoplastic elastomer. To prepare a composition comprising 2 to 10 parts by weight of the processing aid for extrusion and pelletization,
Filler for artificial turf having a charcoal adsorption layer, characterized in that the charcoal adsorption layer is formed on the outer surface or the inner surface of the pelletized filler.
상기 숯흡착층은
상기 펠렛화된 충진재의 외부면에 도포되어 형성되거나 충진재의 외부면을 일정 부분 스크래칭하여 형성되는 홈부에 도포되어 형성되는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재.
The method of claim 1,
The charcoal adsorption layer
Filler for artificial turf having a charcoal adsorption layer, characterized in that the coating is formed on the outer surface of the pelletized filler is formed or applied to the groove portion is formed by scratching a portion of the outer surface of the filler.
상기 숯흡착층은
숯분말과 바인더를 혼합한 숯도포제에 상기 펠렛화된 충진재를 딥코팅 또는 분무코팅하여 형성되는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재.
3. The method of claim 2,
The charcoal adsorption layer
Filler for artificial turf having a charcoal adsorption layer, characterized in that formed by a deep coating or spray coating the pelletized filler in a charcoal coating agent mixed with a charcoal powder and a binder.
상기 숯흡착층은
펠렛화된 충진재의 내측에 형성되되,
상기 충진재는 외측으로부터 물이 내부를 관통하여 배출되도록 관통로가 하나 이상 형성되는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재.
The method of claim 1,
The charcoal adsorption layer
Formed inside the pelletized filler,
The filler is artificial turf filler having a charcoal adsorption layer, characterized in that at least one through-path is formed so that water is discharged through the inside from the outside.
열가소성 탄성체 100 중량부에 대해 목분 5 내지 50 중량부, 목분바인더 10 내지 50 중량부, 무기 충전제 100 내지 400 중량부, 미네랄오일 50 내지 200 중량부 및 탄성체의 물성변화 및 색상 변색 방지를 위한 가공조제 2 내지 10 중량부를 혼합하여 조성물을 생성하는 단계와;
상기 생성된 조성물을 압출하여 펠렛화하여 1차 충진재를 제조하는 단계와;
상기 1차 충진재의 외부면에 바인더 용제 100 중량부에 대해 숯분말 30 내지 60 중량부를 혼합하여 제조된 숯도포제를 도포하여 2차 충진재를 생성하는 단계;를 포함하여 이루어지는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재의 제조방법.
In the manufacturing method of the artificial turf filler to be filled in the artificial turf lower side,
5 to 50 parts by weight of wood powder, 10 to 50 parts by weight of wood powder binder, 100 to 400 parts by weight of inorganic filler, 50 to 200 parts by weight of mineral oil, and processing aid for changing the physical properties of the elastomer and preventing color discoloration. Mixing 2 to 10 parts by weight to produce a composition;
Extruding the resulting composition to pelletize to prepare a primary filler;
Applying a charcoal coating agent prepared by mixing 30 to 60 parts by weight of charcoal powder with respect to 100 parts by weight of the binder solvent on the outer surface of the primary filler to generate a secondary filler; charcoal adsorption layer comprising a Method for producing a filler for artificial turf having a.
상기 숯도포제를 도포하기 전에 1차 충진재의 외부면을 일정 부분 스크래칭하여 홈부를 형성한 후 홈부에 숯도포제를 도포하여 숯흡착층이 형성되는 것을 특징으로 하는 숯흡착층을 가지는 인조잔디용 충진재의 제조방법.The method of claim 5,
Before applying the charcoal coating agent scratches the outer surface of the primary filler to form a groove portion and then the charcoal coating layer is formed by applying a charcoal coating agent to the groove of the artificial turf filler having a charcoal adsorption layer, characterized in that Manufacturing method.