KR101345578B1 - Heat-resistant processing system of nonwoven - Google Patents

Heat-resistant processing system of nonwoven Download PDF

Info

Publication number
KR101345578B1
KR101345578B1 KR1020130038242A KR20130038242A KR101345578B1 KR 101345578 B1 KR101345578 B1 KR 101345578B1 KR 1020130038242 A KR1020130038242 A KR 1020130038242A KR 20130038242 A KR20130038242 A KR 20130038242A KR 101345578 B1 KR101345578 B1 KR 101345578B1
Authority
KR
South Korea
Prior art keywords
flame retardant
nonwoven fabric
treatment system
nonwoven
drying
Prior art date
Application number
KR1020130038242A
Other languages
Korean (ko)
Inventor
박태화
손범익
Original Assignee
(주)세종이엔지
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)세종이엔지 filed Critical (주)세종이엔지
Priority to KR1020130038242A priority Critical patent/KR101345578B1/en
Application granted granted Critical
Publication of KR101345578B1 publication Critical patent/KR101345578B1/en

Abstract

The present invention relates to a flame retardancy processing system of a nonwoven fabric which impregnates a flame retardant into a nonwoven fabric and dries the nonwoven fabric and, more specifically to a flame retardancy processing system of a nonwoven fabric, which includes impregnation, dehydration, and drying devices in a single conveyor line for impregnating into a flame retardant into a nonwoven fabric supplied from a supplying device and drying and depositing the nonwoven fabric; uses a magnetron emitting microwaves to the drying device instead of a heating device to simplify the structure of the processing system by not installing a thick insulation unit; and is easily installed.

Description

부직포 난연 처리 시스템{heat-resistant processing system of nonwoven}Heat-resistant processing system of nonwoven

본 발명은 부직포를 난연 처리하는 시스템에 관한 것으로서 상세하게는 부직포에 난연제를 함침한 후 건조시키는 부직포 난연 처리 시스템에 관한 것이다. The present invention relates to a system for flame retardant nonwoven fabrics, and more particularly, to a nonwoven flame retardant treatment system in which a nonwoven fabric is impregnated with a flame retardant and then dried.

보다 상세하게 본 발명은 단일의 컨베이어라인에 함침, 탈수, 건조 장치를 구비하여 공급장치에 의해 공급된 부직포가 하나의 라인에서 난연제가 함침된 후 건조되어 증착되게 한 것으로서, 특히, 건조 장치로 마이크로파(microwave)를 조사하여 난연제를 건조시킴으로써 단열을 위해 두꺼운 단열벽을 설치하지 않아 구조가 단순할 뿐만 아니라 설치가 용이한 부직포 난연 처리 시스템에 관한 것이다.
More specifically, the present invention is to provide a non-woven fabric supplied by the supply device by impregnating, dehydrating, drying device in a single conveyor line to be dried and deposited after the flame retardant is impregnated in one line, in particular, microwave drying device The present invention relates to a non-woven flame retardant treatment system that is simple in structure and easy to install due to the absence of a thick insulating wall for insulation by irradiating microwaves and drying the flame retardant.

일반적으로 부직포는 섬유를 직포공정을 거치지 않고, 평행 또는 부정방향(不定方向)으로 배열하고 합성수지 접착제로 결합하여 펠트 모양으로 만든 것으로 가공법에 따라 침지식(浸漬式)과 건식(乾式)으로 제조되고 있으며, 침지식은 섬유를 합성수지 접착제에 넣어 적셨다가 건조 ㅇ열처리한 것으로 종이와 비슷하고, 건식은 섬유를 얇은 솜모양으로 만든 것에 합성수지를 내뿜고 열을 가하여 건조시킨 것이다. 이러한 부직포는 섬유가 얽혀 있어서 종횡의 방향성이 없으며, 자른 가장자리가 풀리는 일도 없기 때문에 여러 가지 용도로 사용되고 있다. In general, non-woven fabrics are made of felt or non-woven fabrics arranged in parallel or in an inverted direction and bonded with synthetic resin adhesives without being woven, and manufactured by dipping and drying according to processing methods. The immersion method is a fiber heat-soaked in synthetic resin glue and dried and heat-treated, similar to paper, and the dry type is dried by exposing synthetic resin to heat and making fiber into thin cotton. Such a nonwoven fabric is used for various purposes because the fibers are entangled, there is no vertical and horizontal orientation, and the cut edges do not loosen.

이러한 부직포와 관련된 기술로는 다양한 것이 있고, 이중 난연성을 갖는 부직포를 제작하기 위한 기술로는 특허문헌 1내지 3이 있다. There are various techniques related to such a nonwoven fabric, and Patent Literatures 1 to 3 are techniques for producing a nonwoven fabric having double flame retardancy.

특허문헌 1은 부직포에 난연 성질을 부가하기 위해 부직포에 난연액을 흡수시킨 후 건조시키는 다량의 열풍을 공급하여 건조시키고, 이때 발생되는 다량의 수분을 건조기 밖으로 확실히 배풍할 수 있게 한 것이고, Patent document 1 is to add a flame retardant to the nonwoven fabric to supply a large amount of hot air to dry after absorbing the flame retardant solution to the nonwoven fabric, and to dry a large amount of moisture generated at this time can be surely vented out of the dryer,

특허문헌 2는 발수성 및 난연성에 대한 실용상 만족도를 크게 개선시킨 발수성 부직포에 대한 것으로서, 효율적이고 간단한 방법으로 발수성 및 난연성을 동시에 가지면서 제전성의 문제점을 해결한 부직포의 제조방법에 관한 것이며, Patent document 2 relates to a water-repellent nonwoven fabric that has greatly improved practical satisfaction with water repellency and flame retardancy, and relates to a method for manufacturing a nonwoven fabric that has solved problems of antistatic properties while simultaneously having water repellency and flame retardancy in an efficient and simple manner.

특허문헌3은 폴리에스테르 섬유와 폴리프로필렌 섬유 중 적어도 하나의 섬유로부터 벽지로 적합한 두께 및 크기를 가지는 시트 형상의 부직포를 제조하는 공정; 상기 부직포를 수성 안료, 항균제 및 방향제 중에서 적어도 하나와 난연제를 포함하는 수용액에 침지시키는 공정; 상기 수성 안료, 항균제 및 방향제 중에서 적어도 하나와 난연제가 함침된 부직포를 건조하는 공정; 및 상기 건조된 부직포지의 한쪽 표면에 원하는 모양의 무늬를 인쇄하는 공정을 포함하는 부직포 제조 방법에 관한 것이다. Patent document 3 is a process for producing a sheet-shaped nonwoven fabric having a thickness and size suitable for wallpaper from at least one of the polyester fibers and polypropylene fibers; Immersing the nonwoven fabric in an aqueous solution comprising at least one of an aqueous pigment, an antibacterial agent, and an aromatic and a flame retardant; Drying the nonwoven fabric impregnated with at least one of the aqueous pigment, the antimicrobial agent and the fragrance and the flame retardant; And it relates to a nonwoven fabric manufacturing method comprising the step of printing a pattern of the desired shape on one surface of the dried nonwoven fabric.

이러한 종래의 난연성 부직포를 제작하기 위한 방법이나 장치와 관련된 기술에서 사용되는 방법은 통상적으로 부직포를 난연제에 함침 공정, 열풍을 공급하여 난연제를 건조시키는 공정으로 이루어지고 있으나, 이렇게 열풍을 공급할 경우 공급되는 열풍에 의해 주위의 다른 장치들이 가열되고 작업공간이 더워져 작업에 어려움이 있으므로 열풍을 차단시키기 위해 건조장치에 단열수단을 설치하여야 하고, 이렇게 단열수단을 설치하기 위해서는 많은 비용이 소요될 뿐만 아니라 장치가 비대해지는 단점이 있었다. The conventional method for manufacturing a flame retardant nonwoven fabric or a method used in a device related art is generally made of a process of impregnating a nonwoven fabric with a flame retardant, and a process of drying a flame retardant by supplying hot air. Since the other devices around them are heated by the hot air and the working space becomes hot, it is difficult to work. Therefore, heat insulation means must be installed in the drying apparatus to block the hot air. There was a drawback to bloat.

즉, 열풍을 공급하기 위해서는 대용량의 히터를 구비하여야 하고, 이 히터에서 발생된 열을 건조가 이루어지는 공정에 공급하여야 하므로 장치가 지나치게 비대해질 뿐만 아니라, 건조 라인에 공급된 열에 의해 주위가 가열되어 작업자가 작업을 할 수 없으므로 단열을 위한 단열제 등을 설치하여야 하므로 설비비가 많이 소요되는 문제가 있다.
That is, in order to supply hot air, a large-capacity heater must be provided, and the heat generated from the heater must be supplied to a drying process, so that the apparatus is not overly enlarged and the surroundings are heated by the heat supplied to the drying line, There is a problem that it takes a lot of equipment costs because it can not work because it must install a heat insulator for insulation.

1. 대한민국 실용신안등록 제0349800호1. Republic of Korea Utility Model Registration No. 0349800 2. 대한민국 특허공개 제0983809호2. Korean Patent Publication No. 0983809 3. 대한민국 특허등록 제0173072호3. Republic of Korea Patent Registration No. 0173072

본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위해 개발된 것으로서, 구조가 단순할 뿐만 아니라, 열효율이 우수한 부직포 난연 처리 시스템을 제공하는 것을 목적으로 한다. The present invention was developed to solve the problems of the prior art as described above, and an object thereof is to provide a nonwoven flame retardant treatment system having a simple structure and excellent thermal efficiency.

특히, 본 발명은 공급장치에 의해 이송라인에 공급된 부직포를 함침 장치에서 난연제를 함침하고, 바로 탈수 과정을 거쳐 물의 일부를 배출한 후, 밀폐된 공간에 마그네트론을 설치하여 구성된 건조장치를 통과시키면서 건조가 이루어지게 함으로써, 건조장치를 구성함에 단열제 등의 부수적인 구조물을 설치하지 않아도 되어 구조가 단순해질 수 있게 한 부직포 난연 처리 시스템을 제공하는 것을 목적으로 한다.In particular, the present invention impregnated the flame retardant in the impregnating device of the non-woven fabric supplied to the transfer line by the supply device, and immediately after draining a part of the water through the dehydration process, while passing through the drying device configured by installing a magnetron in a closed space It is an object of the present invention to provide a non-woven flame retardant treatment system that allows the structure to be simplified by making drying, without having to install ancillary structures such as a heat insulator in the drying device.

따라서 건조장치에서 강한 열이 발생되지 않음으로 단열 수단을 설치하지 않아도 되어 장치의 제작함에 소요되는 비용을 절감할 수 있을 뿐만 아니라, 장치가 지나치게 비대해지는 것을 방지할 수 있는 부직포 난연 처리 시스템을 제공하는 것을 목적으로 한다.
Therefore, since no strong heat is generated in the drying apparatus, there is no need to install a heat insulating means, thereby reducing the cost of manufacturing the apparatus, and providing a nonwoven flame retardant treatment system that can prevent the apparatus from becoming excessively large. For the purpose of

이러한 목적을 이루기 위한 본 발명은 이동수단에 의해 이송된 부직포를 이송하는 이송컨베이어; 상기 이송컨베이어의 초입에 설치되고 난연액이 저장되어 통과하는 부직포에 난연액을 함침시키는 함침장치; 상기 함침장치에서 난연액이 함침된 부직포를 가압하여 수분의 일부를 배출시키는 탈수장치; 상기 탈수장치에서 수분의 일부가 배출된 부직포에 마이크로파를 조사하여 부직포가 머금은 수분을 활성화시켜 배출하는 다수의 마이크로파 발생기를 포함하는 건조장치를 포함하는 것을 특징으로 한다.The present invention for achieving this object is a conveying conveyor for conveying the nonwoven fabric conveyed by the moving means; An impregnating device for impregnating the flame retardant in the nonwoven fabric installed at the beginning of the transfer conveyor and storing the flame retardant; Dehydration apparatus for discharging a portion of the water by pressing the non-woven fabric impregnated with the flame retardant in the impregnation device; It characterized in that it comprises a drying apparatus including a plurality of microwave generators for activating and discharge the moisture contained in the nonwoven fabric by irradiating microwaves to the nonwoven fabric from which some of the moisture is discharged from the dehydration device.

또한, 본 발명은 상기 함침장치에 저장된 난연액의 온도를 100~200℃로 유지하는 것이 바림작하고, 상기 탈수장치는 이송컨베이어를 지나는 부직포를 상하에서 가압하는 두 개의 가압롤러로 이루어질 수 있으며, 상기 건조장치의 입구에는 부직포의 건조 효율을 높일 수 있도록 예열하기 위한 예열장치를 더 설치할 수 있다.In addition, the present invention preferably maintains the temperature of the flame retardant solution stored in the impregnation device at 100 ~ 200 ℃, the dehydration device may be composed of two pressure rollers for pressing the nonwoven fabric passing through the conveying conveyor up and down, At the inlet of the drying apparatus may be further provided with a preheating device for preheating to increase the drying efficiency of the nonwoven fabric.

또한, 마이크로파 발생기들 사이에는 격벽을 설치하여 각 격실을 분리함으로써 이웃 격실의 공기가 서로 혼합되는 것을 방지하는 것이 바람직하고, 부직포로부터 분리된 수분을 흡입하여 배출하기 위한 배기팬을 더 설치할 수 있다. In addition, it is preferable to prevent the air from neighboring compartments from being mixed with each other by separating partitions by installing partitions between the microwave generators, and an exhaust fan for sucking and discharging moisture separated from the nonwoven fabric may be further provided.

또한, 마이크로파 발생기가 설치된 공간의 벽은 전자파차폐판으로 구성하여 전자파에 작업자가 노출되는 것을 방지할 수 있다.
In addition, the wall of the space in which the microwave generator is installed may be configured as an electromagnetic shielding plate to prevent the worker from being exposed to the electromagnetic waves.

본 발명은 부직포를 건조시키는 수단으로 직접 열을 발생시키는 전열기 등을 사용하지 않음으로써 부직포에 직접 열기가 접촉되어 부직포가 손상되는 것을 방지할 수 있다. The present invention can prevent the nonwoven fabric from being damaged by direct heat contacting the nonwoven fabric by not using a heater or the like that directly generates heat as a means for drying the nonwoven fabric.

또한, 본 발명은 부직포를 건조시키기 위해 수단을 발열 수단이 아니라 마이크로파발생기를 사용함으로써 건조장치에서 열이 발생하지 않아 단열을 위한 복잡한 장치를 설치하지 않아도 되어 시스템의 구성이 단순하여 제작이 용이하고 유지보수를 쉽게 할 수 있는 효과가 있다. In addition, the present invention by using a microwave generator instead of a heating means to dry the nonwoven fabric does not generate heat in the drying apparatus does not need to install a complex device for thermal insulation, the configuration of the system is simple and easy to manufacture and maintain The effect is easy to repair.

또한, 마이크로파를 조사하여 부직포로부터 배출된 수분을 배기팬으로 흡입하여 배출시킬 수 있게 함으로써 건조 효율을 높일 수 있는 것이다.
In addition, it is possible to increase the drying efficiency by irradiating microwaves to suck the moisture discharged from the nonwoven fabric into the exhaust fan to discharge.

도 1은 본 발명에 따른 부직포 난연 처리 시스템의 일예의 구성도
도 2는 본 발명에 따른 부직포 난연 처리 시스템의 일예의 평면 배치도
도 3은 본 발명에 따른 부직포 난연 처리 시스템의 일예의 정면 배치도
도 4는 본 발명에 따른 부직포 난연 처리 시스템을 구성하는 탈수장치와 함침장치의 측면도
도 5는 본 발명에 따른 부직포 난연 처리 시스템을 구성하는 탈수장치의 사시도
도 6은 본 발명에 따른 부직포 난연 처리 시스템을 구성하는 함침장치의 사시도
도7은 본 발명에 따른 부직포 난연 처리 시스템을 구성하는 건조장치의 일부를 확대하여 도시한 평면도1 is a configuration diagram of an example of a nonwoven flame retardant treatment system according to the present invention
2 is a plan layout view of one example of a nonwoven flame retardant treatment system according to the present invention.
3 is a front layout view of an example of a nonwoven flame retardant treatment system according to the present invention.
Figure 4 is a side view of the dewatering device and impregnation device constituting the nonwoven flame retardant treatment system according to the present invention
Figure 5 is a perspective view of the dewatering device constituting the nonwoven flame retardant treatment system according to the present invention
Figure 6 is a perspective view of the impregnation device constituting the nonwoven flame retardant treatment system according to the present invention
7 is an enlarged plan view of a part of a drying apparatus constituting the nonwoven flame retardant treatment system according to the present invention;

이하, 첨부된 도면을 참고하여 본 발명에 따른 부직포 난연 처리 시스템의 일예를 상세하게 설명한다.
Hereinafter, an example of a nonwoven flame retardant treatment system according to the present invention will be described in detail with reference to the accompanying drawings.

본 발명은 단열 수단을 설치하지 않음으로써 전체 구성이 단순하여 제작이 용이하고 유지관리를 쉽게 할 수 있는 건조장치(40)를 구비한 부직포 난연 처리 시스템을 제공하기 위한 것으로, 상기 건조장치(40)는 부직포에 함침된 난연액을 건조하기 위한 수단으로 마이크로파발생기(41)를 구비하고 있다. The present invention is to provide a non-woven flame retardant treatment system having a drying device 40 that is easy to manufacture and easy to maintain, because the overall configuration is simple by not installing a heat insulating means, the drying device 40 Has a microwave generator 41 as a means for drying the flame retardant liquid impregnated with a nonwoven fabric.

이러한 본 발명에 따른 부직포 난연 처리 시스템은 도 1내지 도 3에 도시한 바와 같이, 공급장치(MF)에 의해 이송된 부직포를 이송하는 이송컨베이어(10)와, 상기 이송컨베이어의 초입에 설치되고 난연액이 저장되어 통과하는 부직포에 난연액을 함침시키는 함침장치(20)와, 상기 함침장치(20)에서 난연액이 함침된 부직포를 가압하여 수분의 일부를 배출시키는 탈수장치(30)를 구비하고 있다. Such a nonwoven fabric flame retardant treatment system according to the present invention, as shown in Figures 1 to 3, the conveying conveyor 10 for conveying the nonwoven fabric conveyed by the supply device (MF), and the flame retardant is installed at the beginning of the conveying conveyor The impregnation device 20 for impregnating the flame retardant liquid in the non-woven fabric that is stored and passed through the liquid, and the dewatering device 30 for pressurizing the non-woven fabric impregnated with the flame retardant liquid in the impregnation device 20 to discharge a part of the water and have.

상기 공급장치(MF)는 통상적으로 물건을 이동시키는 대차 등을 이용하여 구성될 수 있고 다양하게 변형하여 실시 할 수 있는 것으로 이에 대한 상세한 설명은 생략한다. The supply device (MF) can be generally configured using a balance, such as moving the goods and can be carried out in a variety of modifications and a detailed description thereof will be omitted.

상기 이송컨베이어(10)는 통상적인 컨베이어시스템과 동일 유사하게 롤러들 사이에 벨트를 걸러 구동수단으로 롤러를 회전시킴에 의해 벨트가 회동되게 한 것을 선택하여 사용할 수 있다. 물론, 부직포의 무계나 넓이 등을 고려하여 롤러의 크기와 구동수단인 모터의 용량 및 벨트의 폭을 선택하여 사용할 수 있으나. 상기한 바와 같이 본 발명은 열을 이용한 것이 아니라 마이크로파발생기에서 발생된 고주파를 이용한 것으로 마이크로파에 의해 영향을 받지 않은 합성수지 등으로 만들어진 벨트를 사용하는 것이 바람직하다.The conveying conveyor 10 can be selected and used to rotate the belt by rotating the roller by the drive means by filtering the belt between the rollers similarly to the conventional conveyor system. Of course, the size of the roller and the capacity of the motor as the driving means and the width of the belt may be selected in consideration of the non-woven fabric or the width of the nonwoven fabric. As described above, the present invention uses a high frequency generated from a microwave generator, not heat, and preferably uses a belt made of synthetic resin or the like not affected by microwaves.

상기 함침장치(20)는 공급장치에 의해 공급되는 부직포에 난연액을 함침하기 위한 장치로 도 2 및 도 3에 도시한 바와 같이, 탈수장치(30)의 전단에 설치되어 있고, 도 4 및 도 6에 도시한 바와 같이, 통체 형상을 이루는 함침챔버(20c)를 구비하고 있다. The impregnation device 20 is a device for impregnating a flame retardant in a nonwoven fabric supplied by a supply device, as shown in FIGS. 2 and 3, and is installed at the front end of the dehydration device 30. As shown in FIG. 6, the impregnation chamber 20c which has a cylindrical shape is provided.

상기 함침챔버(20c)에는 난연액이 저장되어 있어 부직포(100)를 난연액에 담가 함침시키거나 난연액 분사수단을 구비하여 분사에 의해 난연액을 함침시킬 수 있으나, 함침 효율을 높이기 위해서는 함침챔버(200c)에 난연액을 저장한 상태에서 부직포를 담가 함침하는 것이 바람직하다. Flame retardant is stored in the impregnation chamber 20c to impregnate the nonwoven fabric 100 in the flame retardant, or to impregnate the flame retardant by spraying with a flame retardant injection means, in order to increase the impregnation efficiency. It is preferable to impregnate the nonwoven fabric in a state where the flame retardant is stored at 200c.

또한, 상기 함침챔버(20c)의 내부에는 다수의 롤러(21, 22)를 구비하고 있다. In addition, a plurality of rollers 21 and 22 are provided inside the impregnation chamber 20c.

상기 롤러들(21, 22)은 부직포에 난연액이 보다 효과적으로 함침되게 하기 위한 것이다. 통상적으로 부직포를 난연액에 함침할 경우 부직포에 표면장력이 생겨 난연액이 부직포에 충분히 함침되지 않게 된다. 이에 따라 부직포를 자극하여 표면장력이 깨뜨려야 하며, 이를 위해 상기 롤러들(21, 22)을 설치하여 부직포를 자극할 수 있게 한 것이다. The rollers 21 and 22 are intended to more effectively impregnate the flame retardant in the nonwoven fabric. In general, when the nonwoven fabric is impregnated with a flame retardant solution, the surface tension is generated in the nonwoven fabric so that the flame retardant is not sufficiently impregnated with the nonwoven fabric. Accordingly, the surface tension should be broken by stimulating the nonwoven fabric, and for this purpose, the rollers 21 and 22 may be installed to stimulate the nonwoven fabric.

상기 롤러들(21, 22) 중 도면상 아래에 설치된 롤러(21)는 구동수단30m)에 의해 회전되고 위에 설치된 롤러(22)는 승강수단(20e)에 의해 상하로 승강되어 롤러(21)와의 사이의 거리를 조절할 수 있게 하여 부직포의 두께에 맞추어 롤러들(21, 22) 사이의 거리를 조절할 수 있게 하였다. Among the rollers 21 and 22, the roller 21 installed below in the drawing is rotated by the driving means 30m, and the roller 22 installed above is lifted up and down by the elevating means 20e, so that the roller 21 The distance between the rollers 21 and 22 can be adjusted according to the thickness of the nonwoven fabric.

또한, 상기 함침장치(20)에 저장된 난연액이 보다 효율적으로 부직포에 함침되게 하기 위하여 난연액의 온도를 100~200℃로 유지하는 것이 바람직하다. 난연액을 가열하여 상기의 온도가 유지되게 함으로써 난연액의 물 입자가 분해되어 보다 쉽게 부직포에 함침되는 것이다. In addition, in order for the flame retardant stored in the impregnation apparatus 20 to be more efficiently impregnated in the nonwoven fabric, it is preferable to maintain the temperature of the flame retardant at 100 to 200 ° C. By heating the flame retardant to maintain the above temperature, water particles of the flame retardant are decomposed and more easily impregnated into the nonwoven fabric.

상기 롤러들(21, 22)은 도시한 바와 같이 다수의 쌍이 설치될 수 있고 이들 중 상기 함침장치(30)를 향한 단부에 설치된 롤러들(21, 22)은 부직포에 함침된 난연액의 일부를 탈수하는 기능도 수행할 수 있다. The rollers 21 and 22 may be provided with a plurality of pairs as shown in the drawings, and among them, the rollers 21 and 22 installed at the end facing the impregnation device 30 may be a part of the flame retardant impregnated in the nonwoven fabric. Dehydration can also be performed.

상기 함침장치(20)에 의해 난연액이 함침된 부직포는 탈수장치(30)에 공급되어 탈수가 이루어진다. The nonwoven fabric impregnated with the flame retardant by the impregnation device 20 is supplied to the dewatering device 30 to perform dehydration.

상기 탈수장치(30)는 다양하게 변형하여 실시 할 수 있으나 바람직하게는 도 4 및 도 5에 도시한 바와 같이, 두 개의 롤러(31, 32)로 구성한 것이다. 즉, 도면상 아래쪽에 설치된 지지롤러(31)와 위에 설치된 가압롤러(32) 사이를 부직포가 통과하면서 부직포가 머금고 있는 물을 배출시키는 것이다. The dewatering device 30 may be implemented by various modifications, but preferably, as shown in FIGS. 4 and 5, two rollers 31 and 32 are formed. That is, while the nonwoven fabric passes between the support roller 31 installed below and the pressure roller 32 installed above in the drawing, the water contained in the nonwoven fabric is discharged.

물론, 상기 지지롤러(31) 또는 가압롤러(232) 중 어느 하나는 구동수단(미도시)에 의해 호전하여 부직포를 이동시킬 수 있어야 하고, 가압롤러(32)는 승강수단(30e)에 의해 상하로 승강되어 지지롤러(31)와의 사이의 거리가 조절되어 부직포를 가압하는 힘을 조절할 수 있다. Of course, any one of the support roller 31 or the pressure roller 232 is to be improved by the drive means (not shown) to be able to move the nonwoven fabric, the pressure roller 32 is up and down by the lifting means (30e) As it is raised and lowered, the distance between the support roller 31 is adjusted to adjust the force for pressing the nonwoven fabric.

상기 탈수장치(30)의 하부에는 탈수된 물이 저장되는 집수통(30w)을 더 설치할 수 있다. A lower portion of the dewatering device 30 may be further provided with a collecting tank 30w for storing dehydrated water.

상기 승강수단(20e, 30e)은 회전함에 의해 승강하는 회전축에 손잡이를 설치하여 수동으로 구성하거나, 유압실린더 등 다양하게 변형하여 실시 할 수 있는 것으로 이에 대한 상세한 설명은 생략한다. The lifting means 20e and 30e may be configured manually by installing a handle on a rotating shaft that is lifted by rotating, or may be variously modified such as a hydraulic cylinder, and a detailed description thereof will be omitted.

상기와 같이 탈수장치(30)에 의해 부직포로부터 물을 제거하여도 잔류하는 수분이 부직포에 남아 있고 난연액이 부직포에 고착되지 않은 상태가 된다. As described above, even if water is removed from the nonwoven fabric by the dehydration device 30, the remaining water remains in the nonwoven fabric and the flame retardant is not fixed to the nonwoven fabric.

이에 따라 건조과정을 수행하여 잔류 수분을 제거함과 동시에 난연제가 부직포에 고착되게 하는 것이다. 이러한 건조 과정은 건조장치(40)에 의해 이루어지고, Accordingly, the drying process is performed to remove residual moisture and to fix the flame retardant to the nonwoven fabric. This drying process is made by a drying apparatus 40,

상기 건조장치(40)는 도 2 및 도 3에 도시한 바와 같이 마이크로파를 생성하는 다수의 마이크로파발생기(41)를 격실(40r) 벽의 일측에 설치하여 구성된다. The drying apparatus 40 is configured by installing a plurality of microwave generators 41 for generating microwaves on one side of the wall of the compartment 40r as shown in FIGS. 2 and 3.

상기 건조장치(40)는 도시한 바와 같이 복수의 마이크로파발생기(41)를 설치하여 구성할 수 있고, 수개의 마이크로파발생기(41)가 한 쌍을 이루도록 설치되며, 마이크로파발생기(41) 쌍은 격벽(40w)에 의해 구획된 각 격실(40r)에 각각 설치될 수 있다. The drying apparatus 40 may be configured by installing a plurality of microwave generators 41, as shown in the drawing, several microwave generators 41 are installed to form a pair, and the pair of microwave generators 41 are partition walls ( It can be installed in each compartment 40r partitioned by 40w), respectively.

상기 마이크로파발생기(41)는 통상적으로 마그네트론(magnetron)이라 불리는 것으로, 원통형 음극, 음극과 동축인 양극(coaxial anode)으로 이루어지며 이 사이에 직류전압을 걸어서 전기장을 형성시키는 이극 진공관으로서, 외부의 자석을 이용하여 마그네트론의 길이 방향으로 자기장을 걸어주고 이를 공진회로에 연결하면 매우 높은 주파수로 발진하며, 짧은 시간 동안 큰 출력을 방출할 수 있다. 이러한 마그네트론의 발진된 고주파의 마이크로파가 부직포에 함침된 난연액의 물을 고주파로 진동시켜 부직포로부터 분리할 수 있는 것이다. The microwave generator 41 is commonly called a magnetron, and is composed of a cylindrical cathode, a coaxial anode coaxial with a cathode, and is a bipolar vacuum tube that forms an electric field by applying a DC voltage therebetween. Using the magnetic field in the longitudinal direction of the magnetron and connecting it to the resonant circuit oscillates at a very high frequency and can emit a large output for a short time. The oscillated high frequency microwave of the magnetron can be separated from the nonwoven fabric by vibrating the water of the flame retardant impregnated in the nonwoven fabric at high frequency.

상기 마이크로파발생기(41)는 도 2내지 도 3에 도시한 바와 같이, 다수가 설치될 수 있으며, 이렇게 배열된 마이크로파발생기(41)를 부직포가 경유하면서 부직포에 함침된 난연액이 건조되는 것이다. 2 to 3, a plurality of the microwave generator 41, may be installed, the flame-retardant liquid impregnated in the nonwoven fabric is dried while the non-woven fabric via the microwave generator 41 arranged in this way.

상기 복수의 마이크로파발생기(41)는 전술한 바와 같이, 격벽(40w)에 의해 서로 구획된 격실(40r)에 설치되는 것이 바람직하고, 이렇게 설치된 각각의 마이크로파발생기를 부직포가 통과하는 동안 점차 수분이 건조되며, 이러한 과정에서 건조가 시작되는 부분은 수분이 많으나 점차 수분이 적어지게 된다. 이러한 건조 환경에서 모든 마이크로파발생기가 하나의 공간이 설치되면, 공기가 서로 혼합되어 건조효율이 떨어질 수 있으므로 상기한 바와 같이 격실을 형성하여 이웃하는 격실의 공기가 서로 혼합되지 않게 하여 건조효율을 높인 것이다. As described above, the plurality of microwave generators 41 are preferably installed in the compartments 40r partitioned from each other by the partition walls 40w, and moisture is gradually dried while the nonwoven fabric passes through each of the microwave generators thus installed. In this process, the part where the drying starts is more moisture, but gradually becomes less moisture. In this drying environment, if one microwave generator is installed in one space, the air may be mixed with each other to reduce the drying efficiency, thereby forming a compartment as described above to increase the drying efficiency by preventing the air in neighboring compartments from mixing with each other. .

또한, 상기 마이크로파발생기(41)는 고주파로 발진하고 이렇게 발진된 고주파는 인체에 해를 끼칠 수 있으므로 마이크로파에 작업자가 노출되지 않게 하여야 한다. 이렇게 마이크로파가 격실 내부로부터 외부로 방출되지 않도록 격실의 벽은 전자파차폐판으로 구성하여야 한다. In addition, the microwave generator 41 oscillates at a high frequency, so the high frequency oscillated may cause harm to the human body so that the worker is not exposed to the microwaves. The walls of the compartment should be made of electromagnetic shielding plates so that microwaves are not emitted from the inside of the compartment to the outside.

또한, 상기 각각의 격실에는 마이크로파가 외부로 노출되는 것을 방지하되 내부의 상황을 육안으로 확인할 수 있도록 투시창(44)이 형성되어 있으며, 이 투시창(44)은 다소의 구멍이 형성된 천공판으로 구성될 수 있다. In addition, each compartment is provided with a see-through window 44 to prevent exposure of microwaves to the outside, but to visually check the situation inside, the see-through window 44 may be composed of a perforated plate with a few holes. have.

또한, 마이크로파를 조사함에 따라 부직포로부터 분리된 수분을 포함한 공기를 외부로 배출시킴으로써 부직포의 수분을 더욱 효과적으로 건조시킬 수 있으므로 일측에는 부직포로부터 분리된 수분을 흡입하여 배출하기 위한 배기팬(43)을 더 구비하는 것이 바람직하다. In addition, by irradiating the microwave with the air containing moisture separated from the non-woven fabric to the outside can be dried more effectively the moisture of the non-woven fabric on one side further exhaust fan 43 for sucking and discharging the water separated from the non-woven fabric It is preferable to provide.

상기 배기팬(43)은 도시한 바와 같이 각각의 격실(40r)마다 설치하거나 용량이 큰 것을 하나만 설치할 수도 있다. 상기 배기팬(43)을 다수 설치할 경우 배기팬과 각 격실 사이에는 연결덕트를 설치하여 연결하고 배기팬에서 흡입하여 배출되는 배출구에는 배기덕트(43d)로 서로 연결하여 하나의 배기덕트로 배기를 할 수 있게 하였다. As shown in the drawing, the exhaust fan 43 may be provided for each compartment 40r or only one having a large capacity. When a plurality of exhaust fans 43 are installed, a connection duct is installed between the exhaust fan and each compartment and connected to each other by an exhaust duct 43d to exhaust outlets sucked from the exhaust fan and exhausted by one exhaust duct. Made it possible.

이와 같이 배기팬(43)에 의해 격실(40r) 내부의 공기가 배출되기 위해서는 공기가 공급되어야 하고 이를 위해 상기 각 격실(40r)의 일측에는 흡기구(42)가 형성되어 있다. As described above, in order for the air inside the compartment 40r to be discharged by the exhaust fan 43, air must be supplied. For this purpose, an air inlet 42 is formed at one side of each compartment 40r.

또한 본 발명에 따른 부직포 난연 처리 시스템은 예열장치(50)를 더 구비하는 것이 바람직하다. In addition, it is preferable that the nonwoven flame retardant treatment system according to the present invention further includes a preheating device 50.

상기 마이크로파발생기(41)에서 발생된 고주파를 부직포에 조사한다 하더라도 건조효율이 떨어질 수 있으므로 부직포를 예열시켜 수분이 일정온도로 가열된 상태로 건조장치에 공급하는 것이 바람직하다. Even if the high frequency generated by the microwave generator 41 is irradiated to the nonwoven fabric, the drying efficiency may be lowered. Therefore, the nonwoven fabric may be preheated and supplied to the drying apparatus while the moisture is heated to a predetermined temperature.

상기 예열장치(50)에서 가열되는 온도는 120~200℃ 정도가 바람직하다. The temperature heated in the preheater 50 is preferably about 120 ~ 200 ℃.

상기 예열장치(50)는 부직포가 통과하는 챔버(50c)와, 상기 챔버 내에 가열된 공기를 순환시키는 송풍팬(50f)을 포함한다. 상기 예열장치(50)를 통해 공급되는 가열된 공기는 외부에 설치된 히터에 의해 가열되고, 상기 송풍팬(50f)에 의해 송풍되어 예열장치의 챔버(50c)에 공급되고, 부직포를 가열한 후 배기구를 통해 배기된다. 상기 챔버(50c)의 일측에는 투시창(50w)을 구비하여 챔버(50c)의 내부에서 이루어지는 상황을 감시할 수 있게 하였다.
The preheater 50 includes a chamber 50c through which the nonwoven fabric passes, and a blowing fan 50f for circulating the heated air in the chamber. The heated air supplied through the preheater 50 is heated by a heater installed externally, blown by the blower fan 50f, supplied to the chamber 50c of the preheater, and the exhaust port after heating the nonwoven fabric. Exhaust through. One side of the chamber 50c is provided with a see-through window 50w to monitor the situation made inside the chamber 50c.

10: 이송컨베이어
20: 함침장치
20c: 함침챔버 21, 22: 롤러
30: 탈수장치 31: 지지롤러 32: 가압롤러
30w: 집수통
40: 건조장치
41: 마이크로파발생기
40w: 격벽 40r: 격실
42: 흡기구 43: 배기팬 43d: 배기덕트
44: 투시창
50: 예열장치
50c: 챔버 50f: 송풍팬 50w: 투시창
100: 부직포10: Transfer Conveyor
20: impregnation device
20c: impregnation chamber 21, 22: roller
30: dewatering device 31: support roller 32: pressure roller
30w: sump
40: drying device
41: microwave generator
40w: bulkhead 40r: compartment
42: intake port 43: exhaust fan 43d: exhaust duct
44: viewing window
50: preheater
50c: chamber 50f: blowing fan 50w: viewing window
100: non-woven

Claims (8)

이동수단에 의해 이송된 부직포를 이송하는 이송컨베이어(10);
상기 이송컨베이어의 초입에 설치되고 난연액이 저장되어 통과하는 부직포에 난연액을 함침시키는 함침장치(20);
상기 함침장치(20)에서 난연액이 함침된 부직포를 가압하여 수분의 일부를 배출시키는 탈수장치(30);
상기 탈수장치(30)에서 수분의 일부가 배출된 부직포에 마이크로파를 조사하여 부직포가 머금은 수분을 활성화시켜 배출하는 다수의 마이크로파 발생기(41)를 포함하는 건조장치(40)를 포함하고
상기 마이크로파 발생기(41)들 사이에는 격벽(40w)이 설치되어 다수의 격실(40r)로 구획된 것을 특징으로 하는 부직포 난연 처리 시스템.A conveying conveyor 10 for conveying the nonwoven fabric conveyed by the moving means;
An impregnating device (20) installed at the beginning of the conveying conveyor to impregnate the flame retardant in the nonwoven fabric which is stored and passed through the flame retardant;
Dehydration device 30 for discharging a portion of the water by pressing the non-woven fabric impregnated with flame retardant liquid in the impregnation device (20);
And a drying apparatus 40 including a plurality of microwave generators 41 for activating and discharging moisture contained in the nonwoven fabric by irradiating microwaves to the nonwoven fabric from which some of the moisture is discharged from the dehydrating apparatus 30.
Non-woven fabric flame retardant treatment system, characterized in that partition (40w) is installed between the microwave generator (41) partitioned into a plurality of compartments (40r). 제1항에 있어서,
상기 함침장치(20)에 저장된 난연액은 100~200℃인 것을 특징으로 하는 부직포 난연 처리 시스템.The method of claim 1,
Flame retardant liquid stored in the impregnation device 20 is characterized in that 100 ~ 200 ℃ nonwoven flame retardant treatment system. 제1항에 있어서,
상기 탈수장치(30)는 부직포의 하부를 지지하는 지지롤러(31)와, 상기 지지롤러의 위에 설치되어 지지롤러와의 거리가 조절되어 부직포를 가압하는 가압롤러(32)로 이루어진 것을 특징으로 하는 부직포 난연 처리 시스템.The method of claim 1,
The dewatering device 30 is characterized in that consisting of a support roller 31 for supporting the lower portion of the nonwoven fabric, and a pressure roller 32 installed on the support roller to adjust the distance between the support roller and pressurize the nonwoven fabric. Nonwoven flame retardant treatment system. 제1항에 있어서,
상기 건조장치(40)의 입구에는 부직포의 건조 효율을 높일 수 있도록 예열하기 위한 예열장치(50)가 더 설치된 것을 특징으로 하는 부직포 난연 처리 시스템.The method of claim 1,
Non-woven flame retardant treatment system, characterized in that the preheating device 50 is further installed at the inlet of the drying device 40 to increase the drying efficiency of the nonwoven fabric. 제4항에 있어서,
상기 예열장치(50)는 부직포가 통과하는 챔버(50c)와, 상기 챔버 내에 가열된 공기를 순환시키는 송풍팬(50f)을 포함하는 것을 특징으로 하는 부직포 난연 처리 시스템.5. The method of claim 4,
The preheater (50) is a non-woven flame retardant treatment system, characterized in that it comprises a chamber (50c) through which the nonwoven passes, and a blowing fan (50f) for circulating the heated air in the chamber. 삭제delete 제1항에 있어서,
상기 격실(40r)의 일측에는 부직포로부터 배출된 수분을 흡입하여 배출하기 위한 배기팬(43)이 더 설치된 것을 특징으로 하는 부직포 난연 처리 시스템.The method of claim 1,
Non-combustible flame retardant treatment system, characterized in that one side of the compartment (40r) is further provided with an exhaust fan (43) for sucking and discharging moisture discharged from the nonwoven fabric. 제1항에 있어서,
상기 격실(40r)의 벽은 전자파차폐판으로 구성된 것을 특징으로 하는 부직포 난연 처리 시스템.The method of claim 1,
The wall of the compartment (40r) is a non-woven flame retardant treatment system, characterized in that consisting of the electromagnetic shield plate.
KR1020130038242A 2013-04-08 2013-04-08 Heat-resistant processing system of nonwoven KR101345578B1 (en)