KR101274502B1 - asymmetric extracting method, extracted materials fabricated by using the method, dice for asymmetric extraction and asymmetric extraction apparatus - Google Patents
asymmetric extracting method, extracted materials fabricated by using the method, dice for asymmetric extraction and asymmetric extraction apparatus Download PDFInfo
- Publication number
- KR101274502B1 KR101274502B1 KR1020110054555A KR20110054555A KR101274502B1 KR 101274502 B1 KR101274502 B1 KR 101274502B1 KR 1020110054555 A KR1020110054555 A KR 1020110054555A KR 20110054555 A KR20110054555 A KR 20110054555A KR 101274502 B1 KR101274502 B1 KR 101274502B1
- Authority
- KR
- South Korea
- Prior art keywords
- extruded material
- extrusion
- tapered portion
- extruded
- die
- Prior art date
Abstract
비대칭 압출방법, 이를 이용하여 압출된 압출재, 비대칭 압출용 다이스 및 비대칭 압출장치가 제공된다. 비대칭 압출방법에 의하면, 피압출재의 압출 방향을 기준으로 비대칭적 형상과 다단의 구멍 크기를 갖는 압출 구멍을 포함하는 다이스를 통해서 피압출재를 밀어내어 피압출재에 다단의 전단변형을 유도하면서 피압출재를 압출할 수 있다.An asymmetric extrusion method, an extruded material extruded using the same, a die for asymmetrical extrusion and an asymmetrical extrusion apparatus are provided. According to the asymmetric extrusion method, the extruded material is extruded while pushing the extruded material through a die including an extruded hole having an asymmetrical shape and a multi-stage pore size based on the extrusion direction of the extruded material. Can be extruded.
Description
본 발명은 재료의 성형방법에 관한 것으로서, 특히 재료의 집합조직을 제어할 수 있는 압출장치 및 압출방법에 관한 것이다. The present invention relates to a method for forming a material, and more particularly to an extrusion apparatus and an extrusion method capable of controlling the texture of the material.
압출방법은 판재 가공을 위해서 일반적으로 행해진다. 압출과정에서 재료의 변형과 더불어 재료의 집합조직이 변화될 수 있다. 재료의 집합조직은 그 재료의 물성, 예컨대 성형성에 큰 영향을 미치는 것으로 알려져 있다. 통상적으로, 금속 재료는 그 결정 구조에 따라서 고유의 슬립계를 갖고 있고, 이 금속 재료의 성형성은 이 슬립계의 작용 여부에 따라서 달라질 수 있다. 이러한 슬립계의 작용 여부는 그 금속 재료의 집합조직(texture)과 크게 관련된다. The extrusion method is generally performed for sheet metal processing. In addition to the deformation of the material during the extrusion process, the texture of the material may change. The texture of the material is known to have a great influence on the physical properties of the material, such as formability. Usually, the metal material has an inherent slip system according to its crystal structure, and the moldability of the metal material can vary depending on whether or not the slip system is operated. Whether such a slip system works is largely related to the texture of the metal material.
하지만, 통상적인 대칭 압출방법에 의하면, 판재 가공 시 재료의 집합조직을 제어하여 그 성형성을 향상하기 어렵다.However, according to the conventional symmetrical extrusion method, it is difficult to improve the formability by controlling the texture of the material during sheet metal processing.
이에, 본 발명은 전술한 문제점을 해결하기 위해 안출된 것으로서, 집합조직을 제어할 수 있는 압출방법, 이러한 방법을 이용하여 그 집합조직이 제어된 판재를 제공한다. 또한, 본 발명은 집합조직을 제어할 수 있는 다이스 구조 및 이를 포함하는 압출장치를 제공한다. 전술한 과제는 예시적으로 제시되었고, 본 발명의 범위가 이러한 과제에 의해서 제한되는 것은 아니다.Accordingly, the present invention has been made in order to solve the above-described problems, and provides an extrusion method that can control the texture, the plate material is controlled by using this method. In addition, the present invention provides a die structure and an extrusion apparatus including the same that can control the texture. The foregoing problem has been presented by way of example, and the scope of the present invention is not limited by this problem.
본 발명의 일 형태에 따른 피압출재를 판재 형상으로 압출하는 비대칭 압출방법이 제공된다. 상기 피압출재의 판면 방향을 기준으로 비대칭적 형상의 압출 구멍을 갖는 다이스를 통해서 상기 피압출재를 밀어내어 상기 피압출재의 두께 방향으로 내부에 전단변형을 유도하면서 상기 피압출재를 압출한다. 상기 압출 구멍은 다단의 구멍 크기를 갖고, 상기 압출하는 단계에서 상기 피압출재의 두께 방향으로 내부에 다단의 전단변형을 유도한다.An asymmetrical extrusion method of extruding an extruded material of one embodiment of the present invention into a plate shape is provided. The extruded material is extruded while pushing the extruded material through a die having an extrusion hole having an asymmetrical shape with respect to the plate surface direction of the extruded material, inducing shear deformation in the thickness direction of the extruded material. The extruded hole has a multistage pore size, and in the extruding step, a multi-stage shear deformation is induced in the thickness direction of the extruded material.
상기 압출 방법의 일 예에 있어서, 상기 다이스의 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 단계적으로 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 갖도록 배치될 수 있다.In one example of the extrusion method, the extrusion hole of the die includes a tapered portion whose width varies in stages along the extrusion direction of the extruded material, the tapered portion is asymmetric with respect to the plate surface direction of the extruded material It may be arranged to have a shape.
상기 압출 방법의 다른 예에 있어서, 상기 테이퍼 부분은 상기 피압출재의 상면 방향으로 기울어진 제 1 테이퍼 부분과 상기 피압출재의 하면 방향으로 기울어진 제 2 테이퍼 부분을 포함할 수 있다.In another example of the extrusion method, the tapered portion may include a first tapered portion inclined in an upper surface direction of the extruded material and a second tapered portion inclined in a lower surface direction of the extruded material.
상기 압출 방법의 또 다른 예에 있어서, 상기 다이스는 상기 판재 형상의 두께 방향을 따라서 상기 테이퍼 부분을 한정하는 적어도 한 쌍의 제 1 내면들을 포함하고, 상기 적어도 한 쌍의 제 1 내면들은 상기 압출 방향을 따라서 서로 다른 기울기를 갖도록 배치될 수 있다.In another example of the extrusion method, the die includes at least a pair of first inner surfaces defining the tapered portion along a thickness direction of the plate shape, and the at least one pair of first inner surfaces is in the extrusion direction. And may be arranged to have different inclinations.
상기 압출 방법의 또 다른 예에 있어서, 상기 적어도 한 쌍의 제 1 내면들 중 적어도 일부분은 상기 테이퍼 부분 내에서 상기 피압출재의 판면 방향과 평행할 수 있다.In yet another example of the extrusion method, at least a portion of the at least one pair of first inner surfaces may be parallel to the plate surface direction of the extrudate in the tapered portion.
본 발명의 다른 형태에 따른 비대칭 압출 방법이 제공된다. 컨테이너 내에 피압출재를 장입한다. 스템을 이용하여 상기 컨테이너 내의 상기 피압출재를 압축한다. 상기 컨테이너 전단에 결합되고 다단의 구멍 크기를 갖는 비대칭적인 형상의 압출 구멍을 포함하는 다이스를 통해서 상기 피압출재를 밀어내 상기 피압출재에 다단의 전단변형을 유도하면서 상기 피압출재를 판재 형상으로 압출한다. 상기 다이스의 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 갖도록 배치된다.According to another aspect of the present invention, an asymmetric extrusion method is provided. Charge the material to be extruded into the container. A stem is used to compress the extruded material in the container. The extruded material is extruded into a plate shape while pushing the extruded material through a die including an asymmetrically shaped extruded hole coupled to the front end of the container and having a multistage hole size to induce a multistage shear deformation to the extruded material. . The extrusion hole of the die includes a tapered portion whose width varies along the extrusion direction of the extruded material, and the tapered portion is disposed to have an asymmetrical shape with respect to the plate surface direction of the extruded material.
본 발명의 일 형태에 따른 압출재는 전술한 비대칭 압출방법들 중 적어도 어느 하나를 이용해서 피압출재로부터 압출되어 제조되고, 판재 형상을 갖는다.An extruded material of one embodiment of the present invention is manufactured by being extruded from an extruded material by using at least one of the asymmetrical extrusion methods described above, and has a plate shape.
본 발명의 일 형태에 따른 비대칭 압출용 다이스가 제공된다. 상기 다이스는 피압출재를 판재 형상으로 압출하기 위한 다단의 구멍 크기를 갖는 비대칭적 형상의 압출 구멍을 포함한다. 상기 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 갖는다.An asymmetrical extrusion die of one embodiment of the present invention is provided. The die includes an asymmetrically shaped extrusion hole having a multistage hole size for extruding the extruded material into a sheet shape. The extrusion hole includes a tapered portion whose width varies along an extrusion direction of the extruded material, and the tapered portion has an asymmetrical shape with respect to the plate surface direction of the extruded material.
본 발명의 일 형태에 따른 비대칭 압출 장치가 제공된다. 피압출재를 장입하기 위한 컨테이너가 제공된다. 상기 컨테이너의 전단에 결합되고, 상기 피압출재를 판재 형상으로 압출하기 위해 다단의 구멍 크기를 갖는 압출 구멍을 포함하는 다이스가 제공된다. 상기 피압출재를 밀어내도록 상기 다이스 반대편 상기 컨테이너 내부에 배치된 스템이 제공된다. 상기 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 다단의 비대칭적인 형상을 갖는다.An asymmetrical extrusion device of one embodiment of the present invention is provided. A container for charging an extruded material is provided. A die is provided that is coupled to the front end of the container and includes an extrusion hole having a multi-stage hole size for extruding the extruded material into a plate shape. A stem disposed inside the container opposite the die is provided to push the extruded material. The extrusion hole includes a tapered portion whose width varies along the extrusion direction of the extruded material, and the tapered portion has a multi-stage asymmetrical shape with respect to the plate surface direction of the extruded material.
본 발명의 실시예들에 따른 압출방법 및 압출장치를 이용하면, 피압출재의 집합조직을 제어하여 압출재의 성형성과 같은 재료물성을 크게 향상시킬 수 있다. 본 발명의 실시예들에 따라 제조된 판재 형상의 압출재는 상온에서도 전단변형이 잘 일어날 수 있도록 배치된 슬립계(slip system)를 갖게 됨에 따라 종래에 얻지 못했던 우수한 상온 성형성을 가질 수 있다.By using the extrusion method and the extrusion apparatus according to the embodiments of the present invention, by controlling the texture of the material to be extruded, it is possible to greatly improve the material properties such as formability of the extruded material. The plate-shaped extruded material prepared according to the embodiments of the present invention may have an excellent room temperature formability, which has not been obtained in the past, as it has a slip system disposed so that shear deformation may occur well even at room temperature.
도 1은 본 발명의 일 실시예에 따른 압출장치를 보여주는 개략적인 단면도이고;
도 2는 도 1의 압출장치의 다이스를 보여주는 부분 절단된 사시도이고;
도 3은 도 2의 다이스의 평면도이고;
도 4는 본 발명의 다른 실시예에 따른 다이스를 보여주는 부분 절단된 사시도이고;
도 5는 도 4의 다이스의 단면도이고;
도 6은 본 발명의 또 다른 실시예에 따른 다이스를 보여주는 단면도이고;
도 7은 본 발명의 또 다른 실시예에 따른 다이스를 보여주는 단면도이고;
도 8은 본 발명의 또 다른 실시예에 따른 다이스를 보여주는 단면도이고;
도 9는 본 발명의 또 다른 실시예에 따른 다이스를 보여주는 단면도이고;
도 10은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 +Z축 방향에서의 (0001) 극점도이고;
도 11은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 -Z축 방향에서의 (0001) 극점도이고;
도 12는 비교예에 따른 AZ31 판재의 (0001) 극점도이고;
도 13은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 진응력-진변형률 그래프이고;
도 14는 비교예에 따른 AZ31 판재의 진응력-진변형률 그래프이고;
도 15는 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 인장축에 대한 각도에 따른 r-값을 보여주는 그래프이고;
도 16은 조밀충진육방정(hexagonal closed packed; HCP) 구조의 슬립계를 보여주는 개략도이고;.
도 17은 HCP 구조의 결정방위에 따른 슬립계의 배치를 도시한 개략도이고; 그리고
도 18은 HCP 구조의 (0001) 극점도 내에 도 17의 시편들의 극점을 도시한 개략도이다.1 is a schematic cross-sectional view showing an extrusion apparatus according to an embodiment of the present invention;
2 is a partially cut perspective view showing a die of the extrusion apparatus of FIG. 1;
3 is a top view of the dice of FIG. 2;
4 is a partially cut away perspective view showing a die according to another embodiment of the present invention;
5 is a cross-sectional view of the dice of FIG. 4;
6 is a cross-sectional view showing a die according to another embodiment of the present invention;
7 is a cross-sectional view showing a die according to another embodiment of the present invention;
8 is a cross-sectional view showing a die according to another embodiment of the present invention;
9 is a cross-sectional view showing a die according to another embodiment of the present invention;
10 is a (0001) pole figure in the + Z axis direction of an AZ31 sheet extruded by an asymmetrical extrusion method according to an embodiment of the present invention;
11 is a (0001) pole figure in the -Z axis direction of an AZ31 sheet extruded by an asymmetrical extrusion method according to an embodiment of the present invention;
12 is a (0001) pole figure of the AZ31 sheet according to the comparative example;
13 is a true stress-strain graph of an AZ31 sheet extruded by an asymmetrical extrusion method according to an embodiment of the present invention;
14 is a true stress-strain graph of the AZ31 sheet according to the comparative example;
15 is a graph showing the r-value according to the angle with respect to the tensile axis of the AZ31 sheet extruded by the asymmetrical extrusion method according to an embodiment of the present invention;
FIG. 16 is a schematic showing a slip system of hexagonal closed packed (HCP) structure; FIG.
17 is a schematic diagram showing the arrangement of slip systems according to the crystallographic orientation of the HCP structure; And
18 is a schematic diagram showing the poles of the specimens of FIG. 17 within the (0001) pole figure of the HCP structure.
이하, 첨부한 도면을 참조하여 본 발명에 따른 바람직한 실시예를 설명함으로써 본 발명을 상세하게 설명한다. 그러나 본 발명은 이하에서 개시되는 실시예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예는 본 발명의 개시가 완전하도록 하며, 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 도면에서 구성 요소들은 설명의 편의를 위하여 그 크기가 과장 또는 축소될 수 있다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in various forms, and only the present embodiments are intended to complete the disclosure of the present invention and to those skilled in the art to fully understand the scope of the invention. It is provided to inform you. In the drawings, the components may be exaggerated or reduced in size for convenience of description.
본 발명의 실시예들에서, 집합조직(texture)은 다결정 재료의 결정립들(crystalline grains)이 일정한 방향으로 정렬된 상태를 나타낼 수 있다. 본 발명의 실시예들에서, 집합조직은 텍스처 또는 텍스쳐로 불릴 수도 있고, 그 명칭에 의해서 그 범위가 제한되지 않는다. 본 발명의 실시예들에서, 재료가 갖는 집합조직은 절대적인 개념보다는 상대적인 개념으로 사용된다. 즉, 어떤 재료가 소정 방향의 집합조직을 갖는다는 것은 그 재료의 상당부분의 결정립들이 그 방향의 집합조직을 갖는다는 것을 의미할 뿐, 그 재료의 모든 결정립들이 그 방향의 집합조직을 갖는다는 것을 의미하지는 않는다.In embodiments of the invention, the texture may represent a state in which crystalline grains of the polycrystalline material are aligned in a constant direction. In embodiments of the invention, the texture may be referred to as a texture or texture, and its scope is not limited by its name. In the embodiments of the present invention, the texture of the material is used in a relative concept rather than an absolute concept. In other words, a material having an aggregate in a certain direction means that a large part of the grains of the material have an aggregate in that direction, and that all grains of the material have an aggregate in that direction. It does not mean.
본 발명의 실시예들에서, 극점도(pole figure)는 재료의 결정방위 또는 집합조직의 분석에 있어서 결정학적 격자 면들의 분포 방향을 보여주는 평사투영(stereographic projection) 형태의 그림을 나타낸다. 극점도는 X-선 회절(X-ray diffraction; XRD) 분석을 이용하여 도시할 수 있다.In embodiments of the present invention, the pole figure represents a picture in the form of a stereoscopic projection showing the direction of distribution of the crystallographic lattice planes in the analysis of crystal orientation or texture of the material. The pole figure can be shown using X-ray diffraction (XRD) analysis.
본 발명의 실시예들에서, 피압출재는 압출이 수행되는 대상을 의미하고, 압출재는 피압출재로부터 압출이 완료되어 목적하는 형상으로 변경된 대상을 의미한다.In the embodiments of the present invention, the extruded material means an object to be extruded, and the extruded material means an object that is extruded from the extruded material and changed into a desired shape.
도 1은 본 발명의 일 실시예에 따른 비대칭 압출장치를 보여주는 개략적인 단면도이다. 도 2는 도 1의 압출장치의 다이스를 보여주는 부분 절단된 사시도이다. 도 3은 도 2의 다이스의 평면도이다.1 is a schematic cross-sectional view showing an asymmetric extrusion apparatus according to an embodiment of the present invention. 2 is a partially cut perspective view showing a die of the extrusion apparatus of FIG. 3 is a plan view of the dice of FIG. 2.
도 1을 참조하면, 피압출재(50)를 장입하기 위한 컨테이너(110)가 제공될 수 있다. 예를 들어, 피압출재(50)는 빌릿(billet) 형태로 컨테이너(110) 내의 내부 구멍(115) 내에 장입될 수 있다. 다른 예로, 피압출재(50)는 분말 형태 또는 압분체 형태로 컨테이너(110) 내의 내부 구멍(115) 내에 장입될 수도 있다. 컨테이너(110)는 피압출재(50)를 수용할 수 있도록 다양한 형상의 내부 구멍(115) 및 외형을 가질 수 있다. 따라서 피압출재(50) 및 컨테이너(110)의 형상은 다양하게 변형될 수 있고, 이 실시예의 범위를 제한하지 않는다.Referring to FIG. 1, a
스템(stem, 120)은 피압출재(50)를 컨테이너(110) 내로 밀어 넣어 압축시킬 수 있도록 컨테이너(110) 내에 배치될 수 있다. 예를 들어, 피압출재(50)의 효과적인 압축을 위해서, 스템(120)의 외형은 컨테이너(110)의 내부 구멍(115)의 형상에 맞추어질 수 있다. 다른 예로, 스템(120)의 외형은 내부 구멍(115)의 형상과 일치하지 않을 수 있고, 이 경우 피압출재(50)의 일부분이 컨테이너(110) 내에서 압축되지 않고 잔류할 수 있다. 스템(120)은 램(ram) 또는 압축기와 같이 불릴 수도 있고, 그 용어 및 형상에 의해서 이 실시예의 범위가 제한되지 않는다.The
다이스(130)는 스템(120) 반대편의 컨테이너(110)의 전단에 결합될 수 있다. 예를 들어, 스템(120), 컨테이너(110) 및 다이스(130)는 일렬로, 예컨대 도 1의 X축 방향으로 배열되어 결합될 수 있다. 이러한 X축 방향이 피압출재(50)의 압출 방향이 될 수 있고, 압출은 이러한 X축 방향을 따라서 일축 방향으로 이루어진다. 이 실시예의 변형된 예에서, 스템(120), 컨테이너(110) 및 다이스(130)가 일렬로 배열되지 않을 수도 있고, 이 경우 압출 방향은 주로 다이스(130)를 기준으로 결정될 수 있다.The
다이스(130)는 피압출재(50)의 압출 형상을 한정하는 압출 구멍(135)을 가질 수 있다. 피압출재(50)는 다이스(130) 내의 압출 구멍(135)을 통과하면서 판재 형상의 압출재(60)로 변환될 수 있다. 예컨대, 도 1에서 XY 평면은 압출재(60)의 판면 방향이 되고, Z축 방향은 압출재(60)의 두께 방향이 되고, X축 방향은 압출재(60)의 길이 방향이 되고, Y축 방향은 압출재(60)의 폭 방향이 될 수 있다.The
압출 구멍(135)은 그 폭이 가변되는 테이퍼 부분(134)과 그 폭이 일정한 고정 부분(132)을 포함할 수 있다. 스템(120)에 의해서 압축된 피압출재(50)는 테이퍼 부분(134)을 통과하면서 그 폭과 형상이 실질적으로 가변되고 이어서 고정 부분(132)을 통과하면서 압출재(60)의 형상으로 압출될 수 있다. 압출 구멍(135)의 테이퍼 부분(134)은 후술하는 바와 같이 압출재(60)의 집합조직을 제어하기 위해서 압출 방향(X축 방향)을 기준으로 비대칭적인 형상을 가질 수 있다. The
도 2 및 도 3을 더 참조하면, 판재 형상의 압출을 위해서, 압출 구멍(135)은 YZ 평면을 기준으로 사각 단면, 예컨대 직사각 단면 형상을 가질 수 있다. 다이스(130)는 압출 구멍(135)을 한정하는 한 쌍의 제 1 내면들(142, 144) 및 한 쌍의 제 2 내면들(146, 148)을 포함할 수 있다. 제 1 내면들(142, 144)은 피압출재(50) 또는 압출재(60)의 두께 방향(Z축 방향)을 따라서 이격 배치되고, 제 2 내면들(146, 148)은 피압출재(50) 또는 압출재(60)의 폭 방향(Y축 방향)으로 이격 배치될 수 있다.2 and 3, in order to extrude the plate shape, the
제 1 내면들(142, 144)은 압출재(60)의 판면을 한정할 수 있다. 제 1 내면들(142, 144)은 압출재(60) 내에 두께 방향으로 전단변형을 효과적으로 유도하기 위해서 압출재(60)의 판면 방향(XY 평면)을 기준으로, 즉 판면 상하로 비대칭적으로 배치될 수 있다. 예컨대, 제 1 내면들(142, 144)은 서로 다른 기울기로 신장될 수 있다. 예를 들어, 제 1 내면(142)은 압출 방향(X축 방향)에 대해서 소정의 기울기를 갖고, 제 1 내면(144)은 압출 방향(X축 방향)과 평행할 수 있다. 한편, 이 실시예에서 압출은 일 방향(X축 방향)으로 진행되고, 따라서 제 1 내면(142)과 압출 방향(X축 방향)이 이루는 각도는 90o 미만이고, 예컨대 10o ~ 80o 범위일 수 있다.The first
이에 따르면, 피압출재(50)는 제 1 내면들(142, 144) 사이에서 그 변형각도가 달라져 큰 전단변형을 받을 수 있다. 이 실시예에서, 제 1 내면(144)이 압출 방향과 평행하기 때문에 제 1 내면들(142, 144) 사이에서 전단변형은 다소 직선적일 수 있고, 따라서 그 제어가 용이할 수 있다. 이러한 전단변형은 압출재(60)의 판면 방향의 집합조직 변형에 큰 영향을 줄 수 있다. 이러한 집합조직의 변화는 후술하는 바와 같이 압출재(60)의 성형성에 큰 영향을 미칠 수 있다.According to this, the extruded
제 2 내면들(146, 148)은 압출재(60)의 측면을 한정할 수 있다. 압출재(60)가 판재 형상을 갖는 경우, 제 2 내면들(146, 148)은 압출재(60)의 집합조직에 큰 영향을 미치지 않을 수 있다. 이에 따라, 제 2 내면들(146, 148)은 대칭적으로 배치될 수 있고, 예컨대 압출재(60)의 두께 방향(Z축 방향)에 평행할 수 있다. 이 실시예의 변형된 예에서, 제 2 내면들(146, 148)은 비대칭적으로 배치될 수도 있다.The second
이하에서는 본 발명의 일 실시예에 따른 비대칭 압출방법을 설명한다. 이 실시예에 따른 비대칭 압출방법은 예시적으로 도 1 내지 도 3의 압출장치를 참조하여 설명할 수 있다. Hereinafter will be described an asymmetric extrusion method according to an embodiment of the present invention. The asymmetric extrusion method according to this embodiment can be described with reference to the extrusion apparatus of FIGS.
도 1 내지 도 3을 참조하면, 컨테이너(110) 내에 피압출재(50)를 장입할 수 있다. 이어서, 스템(120)을 이용하여 컨테이너(110) 내의 피압출재(50)를 압축할 수 있다. 이어서, 다이스(130)를 통해서 피압출재(50)를 밀어내어 판재 형상의 압출재(60)를 형성할 수 있다. 전술한 바와 같이, 다이스(130)가 압출 방향에 대해서 비대칭적인 형상의 압출 구멍(135)을 갖기 때문에, 피압출재(50)에 전단변형을 유도하면서 피압출재(50)를 압출할 수 있다. 이러한 비대칭 압출방법은 위 도 1 내지 도 3의 압출장치에 대한 설명을 참조하여 더욱 상세하게 이해될 수 있다.1 to 3, the extruding
위와 같이, 피압출재(50)에 전단변형을 유도함으로써 압출재(60)의 집합조직이 제어될 수 있다. 이에 따라, 압출재(60)의 집합조직은 피압출재(50)의 집합조직과 달라질 수 있다. 따라서 통상적인 압출조건에서 성형성이 나쁜 피압출재(50)의 경우, 그 집합조직을 변형하여 압출함으로써 압출재(60)의 성형성이 개선될 수 있다.As described above, by inducing shear deformation in the extruded
본 발명의 다른 실시예에 따른 비대칭 압출방법에 따르면, 피압출재(50)의 장입 단계 및 피압출재(50)의 압축 단계는 다양하게 변형되거나 또는 생략될 수 있다. 예를 들어, 피압출재(50)가 다이스(130) 내로 바로 장입되어 다이스 (130) 내에서 압축될 수 있다. 다른 예로, 피압출재(50)의 장입 단계, 압축 단계 및 압출 단계가 서로 구분되지 않고 일련의 압출 단계로 지칭될 수도 있다.According to the asymmetric extrusion method according to another embodiment of the present invention, the charging step of the extruded
전술한 실시예들에 따른 비대칭 압출방법은 도 1 내지 도 3의 압출장치를 참조하여 설명되었지만, 그 범위가 이러한 장치 구조에 제한되지 않는다. Although the asymmetric extrusion method according to the above embodiments has been described with reference to the extrusion apparatus of FIGS. 1 to 3, the range is not limited to this apparatus structure.
한편, 전술한 비대칭 압출방법들에 따라 제조된 압출재(60)는 이후 그 두께를 더 얇게 하기 위해서 위 비대칭 압출절차를 반복적으로 거치거나 또는 압연 절차를 더 거칠 수도 있다.On the other hand, the extruded
도 4는 본 발명의 다른 실시예에 따른 다이스(130a)를 보여주는 부분 절단된 사시도이다. 도 5는 도 4의 다이스(130a)의 단면도이다. 이 실시예에 따른 다이스(130a)는 도 1 내지 도 3의 다이스(130)에서 일부 구성을 변형한 것에 해당하고, 따라서 두 실시예들에서 중복된 설명은 생략된다.4 is a partially cut perspective view showing a
도 4 및 도 5를 참조하면, 압출 구멍(135a)은 도 1 내지 도 3의 압출 구멍(135)으로부터 변형된 형상을 갖는다. 압출 구멍(135a)은 여전히 압출 방향(X축 방향)에 대해서 비대칭적인 형상을 가질 수 있다. 이 실시예에서, 테이퍼 부분(134a)을 한정하는 제 1 내면들(142, 144a)은 압출 방향(X축 방향)을 기준으로 서로 다른 각도의 기울기를 가질 수 있다. 제 1 내면(144a)은 압출 방향과 평행하지 않고, 제 1 내면(142)과 다른 각도의 기울기로 신장될 수 있다. 제 1 내면들(142, 144a)의 기울기는 예시적으로 도시되었고, 제 1 내면들(142, 144a)이 서로 다른 기울기를 갖는 범위 내에서 다양하게 변형될 수 있다.4 and 5, the
이에 따르면, 압출 구멍(135a)의 테이퍼 부분(134a)은 여전히 압출 방향을 기준으로 비대칭적인 형상을 가질 수 있다. 특히, 압출 구멍(135a)의 테이퍼 부분(134a)은 압출재(도 1의 60)의 판면 방향(XY 평면)을 기준으로 비대칭적인 형상을 가질 수 있다. According to this, the tapered
이에 따라, 피압출재(도 1의 50)는 제 1 내면들(142, 144a) 사이에서 그 변형각도가 달라져 전단변형을 여전히 받을 수 있다. 다만, 제 1 내면들(142, 144a)이 모두 압출 방향에 대해서 기울어져 있다는 점에서, 그 전단변형이 다소 복잡해질 수 있다. 이러한 전단변형은 압출재(도 1의 60)의 집합조직 변형에 영향을 줄 수 있다.Accordingly, the object to be extruded (50 in FIG. 1) may still undergo shear deformation because its deformation angle is changed between the first
도 6은 본 발명의 또 다른 실시예에 따른 다이스(130b)를 보여주는 단면도이다. 이 실시예에 따른 다이스(130b)는 전술한 다이스들(130, 130a)에서 일부 구성을 변형한 것에 해당하고, 따라서 실시예들에서 중복된 설명은 생략된다.6 is a cross-sectional view illustrating a
도 6을 참조하면, 압출 구멍(135b)은 여전히 압출 방향(X축 방향)에 대해서 비대칭적인 형상을 가질 수 있다. 압출 구멍(135b)은 제 1 테이퍼 부분(134b1), 제 2 테이퍼 부분(134b2) 및 고정 부분(132)을 포함할 수 있다. 제 1 테이퍼 부분(134b1) 및 제 2 테이퍼 부분(134b2)은 피압출재(도 1의 50)에 서로 상보적인 전단 변형을 유도하도록 구성될 수 있다. 예를 들어, 제 1 테이퍼 부분(134b1) 및 제 2 테이퍼 부분(134b2)은 서로 인접하게 배치될 수 있고, 서로 반대 방향으로 기울어진 형상을 가질 수 있다.Referring to FIG. 6, the
구체적으로, 제 1 테이퍼 부분(134b1)은 피압출재(도 1의 50)의 상면 방향으로 기울어지고, 제 2 테이퍼 부분(134b2)은 피압출재(도 1의 50)의 하면 방향으로 기울어지게 배치된다. 제 1 테이퍼 부분(134b1)은 그 기울기가 가변하는 상부의 제 1 내면(142b)과 피압출재(도 1의 50)의 압출 방향(X축 방향)에 평행한 하부의 제 1 내면(144b)을 포함할 수 있다. 제 2 테이퍼 부분(134b2)은 그 기울기가 가변하는 하부의 제 2 내면(144b)과 피압출재(도 1의 50)의 압출 방향(X축 방향)에 평행한 상부의 제 1 내면(142b)을 포함할 수 있다.Specifically, the first tapered portion 134b1 is inclined in the upper surface direction of the material to be extruded (50 in FIG. 1), and the second tapered portion 134b2 is disposed inclined in the lower surface direction of the extruded material (50 in FIG. 1). . The first tapered portion 134b1 has a first
이 실시예의 변형된 예에서, 제 1 테이퍼 부분(134b1) 및 제 2 테이퍼 부분(134b2)은 그 기울어진 방향이 서로 뒤바뀔 수도 있다. 나아가, 압출 구멍(135b)은 제 1 테이퍼 부분(134b1) 및 제 2 테이퍼 부분(134b2)이 2회 이상 반복된 다단 형상을 가질 수도 있다.In a modified example of this embodiment, the inclined directions of the first tapered portion 134b1 and the second tapered portion 134b2 may be reversed. Further, the
이 실시예에 따르면, 피압출재(도 1의 50)는 제 1 테이퍼 부분(134b1) 및 제 2 테이퍼 부분(134b2)을 거치면서 서로 상보적인 전단변형을 받을 수 있다. 이에 따르면, 피압출재(도 1의 50)의 집합조직을 판면 양쪽에서 제어할 수 있어서, 전체적으로 집합조직을 균일하게 할 수 있다.According to this embodiment, the material to be extruded (50 in FIG. 1) may be subjected to complementary shear deformations while passing through the first tapered portion 134b1 and the second tapered portion 134b2. According to this, the texture of the extruded material (50 in Fig. 1) can be controlled on both sides of the plate, so that the texture of the aggregate can be made uniform as a whole.
도 7은 본 발명의 또 다른 실시예에 따른 다이스(130c)를 보여주는 단면도이다. 이 실시예에 따른 다이스(130c)는 전술한 다이스들에서 일부 구성을 변형한 것에 해당하고, 따라서 실시예들에서 중복된 설명은 생략된다.7 is a cross-sectional view illustrating a
도 7을 참조하면, 압출 구멍(135c)은 여전히 압출 방향(X축 방향)에 대해서 비대칭적인 형상을 가질 수 있다. 압출 구멍(135c)은 테이퍼 부분(134c) 및 고정 부분(132)을 포함할 수 있다. 테이퍼 부분(134c)은 그 구멍 크기가 단계적으로 변하는 다단 구멍을 포함할 수 있다. 예를 들어, 테이퍼 부분(134c)은 압출 방향(X축 방향)을 따라서 그 구멍 크기가 단계적으로 감소하는 다단 구멍 형상을 가질 수 있다.Referring to FIG. 7, the
예를 들어, 제 1 내면(144c)은 압출 방향(X축 방향)에 평행하고, 제 1 내면(142c)은 압출 방향(X축 방향)에 기울어진 부분과 평행한 부분을 교대로 포함할 수 있다. 이에 따라, 압출 구멍(135c)은 테이퍼 부분(134c)에서 그 폭이 단계적으로 감소될 수 있다.For example, the first
이 실시예에 따르면, 피압출재(도 1의 50)는 테이퍼 부분(134c)을 거치면서 다단의 단계적인 전단변형을 받을 수 있다. 이에 따르면, 전단 변형을 단계적으로 가함으로써 집합조직을 제어하면서도 피압출재(도 1의 50)의 압출을 상대적으로 용이하게 할 수 있다.According to this embodiment, the material to be extruded (50 in FIG. 1) may be subjected to multiple stages of shear deformation while going through the tapered
도 8은 본 발명의 또 다른 실시예에 따른 다이스(130d)를 보여주는 단면도이다. 이 실시예에 따른 다이스(130d)는 전술한 다이스들에서 일부 구성을 변형한 것에 해당하고, 따라서 실시예들에서 중복된 설명은 생략된다.8 is a cross-sectional view illustrating a
도 8을 참조하면, 압출 구멍(135d)은 여전히 압출 방향(X축 방향)에 대해서 비대칭적인 형상을 가질 수 있다. 압출 구멍(135d)은 테이퍼 부분(134d) 및 고정 부분(132)을 포함할 수 있다. 테이퍼 부분(134d)은 그 구멍 크기가 단계적으로 변하는 다단 구멍 형상을 가질 수 있다. 예컨대, 테이퍼 부분(134d)에서 구멍 크기는 압출 방향(X축 방향)을 따라서 단계적으로 감소할 수 있다.Referring to FIG. 8, the
예를 들어, 제 1 내면들(142d, 144d)은 압출 방향(X축 방향)에 대해서 기울어진 부분과 평행한 부분을 교대로 포함할 수 있다. 제 1 내면(142d)의 기울어진 부분과 제 2 내면(144d)의 기울어진 방향은 서로 반대 방향일 수 있다. For example, the first
이 실시예에 따르면, 피압출재(도 1의 50)는 테이퍼 부분(134d)을 거치면서 판면 양쪽에서 단계적인 전단변형을 받을 수 있다.According to this embodiment, the material to be extruded (50 in FIG. 1) may be subjected to step shear deformation on both sides of the plate while passing through the tapered
도 9는 본 발명의 또 다른 실시예에 따른 다이스(130e)를 보여주는 단면도이다. 이 실시예에 따른 다이스(130e)는 전술한 다이스들에서 일부 구성을 변형한 것에 해당하고, 따라서 실시예들에서 중복된 설명은 생략된다.9 is a cross-sectional view illustrating a
도 9를 참조하면, 압출 구멍(135e)은 여전히 압출 방향(X축 방향)에 대해서 비대칭적인 형상을 가질 수 있다. 압출 구멍(135e)은 테이퍼 부분(134e) 및 고정 부분(132)을 포함할 수 있다. 테이퍼 부분(134e)은 그 구멍 크기가 단계적으로 변하는 다단 구멍 형상을 가질 수 있다. 예를 들어, 테이퍼 부분(134e)은 압출 방향(X축 방향)을 따라서 그 구멍 크기가 단계적으로 감소하는 다단 구멍 형상을 가질 수 있다. 이 실시예에서 테이퍼 부분(134e)의 도 7의 테이퍼 부분(134c)과 달리 대칭적인 형상을 갖다가 비대칭적인 형상으로 변형된다. Referring to FIG. 9, the
예를 들어, 제 1 내면(144e)은 압출 방향(X축 방향)에 평행하고, 제 1 내면(142e)은 압출 방향(X축 방향)에 평행한 부분으로 시작하여 기울어진 부분과 평행한 부분을 교대로 포함할 수 있다. 이에 따라, 압출 구멍(135e)은 테이퍼 부분(134e)에서 그 폭이 일정하다가 이후 단계적으로 감소될 수 있다.For example, the first
이 실시예에 따르면, 피압출재(도 1의 50)는 테이퍼 부분(134e)을 거치면서 단계적인 전단변형을 받을 수 있다. According to this embodiment, the material to be extruded (50 in FIG. 1) may undergo a step shear deformation while passing through the tapered
도 4 내지 도 9의 다이스들(130a, 130b, 130c, 130d, 130e)을 이용한 압출방법은 전술한 설명으로부터 이해될 수 있고, 나아가 도 2 및 도 3의 다이스(130)를 이용한 압출방법에 대한 설명을 더 참조하여 이해될 수 있다.Extrusion method using the dice (130a, 130b, 130c, 130d, 130e) of Figures 4 to 9 can be understood from the above description, and further for the extrusion method using the
이 실시예의 변형된 예에서, 전술한 다이스들의 구조는 적어도 일부분에서 비대칭적인 압출을 허용하는 범위 내에서 부분적으로 서로 결합될 수도 있다.In a modified example of this embodiment, the structures of the dies described above may be partially joined to one another within a range that allows asymmetrical extrusion at least in part.
전술한 비대칭 압출장치 및 비대칭 압출방법이 적용되는 피압출재(도 1의 50)는 다양한 재료를 포함할 수 있다. 예를 들어, 피압출재(50)는 집합조직을 갖는 다양한 금속 또는 그 금속 합금을 포함할 수 있다. 이러한 금속 또는 금속 합금은 다양한 결정 구조를 가질 수 있으며, 예컨대 조밀충진육방정(hexagonal closed-packed; HCP), 면심입방정(face centered cubic; FCC), 체심입방정(body centered cubic;BCC) 구조 등을 가질 수 있다. 보다 구체적으로 보면, 피압출재(50)는 마그네슘(Mg), 티타늄(Ti), 지르코늄(Zr), 아연(Zn), 알루미늄(Al), 구리(Cu), 철(Fe) 등과 같은 금속 또는 그 합금을 포함할 수 있다. 철 합금의 경우 주철, 탄소강, 고속도강, 전기강판(Fe-Si 합금) 등을 포함할 수 있다. 전술한 피압출재(50)의 금속 원소 또는 금속 구조는 예시적으로 제시되었고, 이 실시예의 범위는 이에 제한되지 않는다.The extruded material (50 in FIG. 1) to which the aforementioned asymmetric extrusion apparatus and asymmetric extrusion method are applied may include various materials. For example, the extruded
이하에서는 설명의 편의를 위해서 피압출재(도 1의 50)로써 조밀충진육방정(HCP) 구조를 갖는 금속 또는 금속 합금을 예로 들어 비대칭 압출장치 및 압출방법으로 압출된 판재의 특성에 대해서 구체적으로 설명한다. 예를 들어, HCP구조를 갖는 금속으로는 마스네슘(Mg), 아연(Zn), 지르코늄(Zr), 티타늄(Ti) 등을 들 수 있다. Hereinafter, for convenience of description, the characteristics of the plate extruded by an asymmetric extrusion apparatus and an extrusion method will be described in detail using a metal or metal alloy having a dense packed hexagonal crystal (HCP) structure as an extruded material (50 in FIG. 1). do. For example, magnesium (Mg), zinc (Zn), zirconium (Zr), titanium (Ti), etc. are mentioned as a metal which has an HCP structure.
도 16은 조밀충진육방정(hexagonal closed packed; HCP) 구조의 슬립계를 보여주는 개략도이다. 도 17은 HCP 구조의 결정방위에 따른 슬립계의 배치를 도시한 개략도이다. 도 18은 HCP 구조의 (0001) 극점도 내에 도 17의 A, B, C, D 결정의 극점을 도시한 개략도이다.FIG. 16 is a schematic diagram showing a slip system of hexagonal closed packed (HCP) structure. FIG. 17 is a schematic view showing the arrangement of slip systems according to the crystallographic orientation of the HCP structure. FIG. 18 is a schematic diagram showing poles of the A, B, C, and D crystals of FIG. 17 within a (0001) pole figure of the HCP structure. FIG.
도 16을 참조하면, HCP 구조를 갖는 금속의 가공 시 주로 {0001}<1120>의 기저면 슬립계(basal plane slip system)와 {1010}<1210> 프리즘 슬립계(prismatic slip system), {1011}<1210> 피라미드 슬립계(piramidal slip system) 등의 제한적인 슬립계와 쌍정계(twin system)가 작용하는 것으로 알려져 있다. 이러한 HCP 구조를 갖는 금속은 그 제한적인 슬립계로 인해서 상온에서 성형성이 좋지 않다. Referring to FIG. 16, a base plane slip system of {0001} <1120> and a {1010} <1210> prismatic slip system, {1011} mainly in the processing of a metal having an HCP structure It is known that a limited slip system such as a pyramidal slip system and a twin system work. The metal having such an HCP structure is poor in formability at room temperature due to its limited slip system.
이러한 HCP 구조를 갖는 금속의 경우, 상온에서 기저면 슬립계 이외의 변형기구에 대한 임계분해전단응력(critical resolved shear stress)값은 기저면 슬립계의 임계분해전단응력에 비해 매우 크다. 따라서 기저면 슬립계를 중심으로 슬립계의 배치가 HCP 구조의 상온 성형성에 중요한 영향을 끼치게 된다.In the case of a metal having such an HCP structure, the critical resolved shear stress value for deformation mechanisms other than the base slip system at room temperature is much larger than the critical resolved shear stress of the base slip system. Therefore, the arrangement of the slip system around the base surface slip system has an important effect on the room temperature formability of the HCP structure.
도 17 및 도 18을 참조하면, 제 1 시편(A)과 같이 기저면 슬립계가 압출재의 판면과 평행하게 배치되는 경우(ND 방향에 수직한 경우) 또는 제 2 및 제 3 시편들(B, C)과 같이 기저면 슬립계가 판면 방향(RD 방향)에 수직하거나 횡축방향(TD 방향)에 수직하게 배치되는 경우에는 상온에서의 성형성이 열악하게 된다. 이는 압출재의 성형 시 주변형 방향(예컨대, ND, RD 및 TD 방향)과 기저면 슬립계가 서로 수직하거나 수평을 이루게 되어 외부응력에 대해 기저면 슬립계의 작동이 어려워지기 때문이다.Referring to FIGS. 17 and 18, when the base slip system is disposed parallel to the plate surface of the extruded material (perpendicular to the ND direction) as in the first specimen A, or the second and third specimens B and C As described above, when the base surface slip system is disposed perpendicular to the plate surface direction (RD direction) or perpendicular to the horizontal axis direction (TD direction), moldability at room temperature becomes poor. This is because the peripheral surface direction (for example, ND, RD and TD directions) and the base surface slip system are perpendicular or horizontal to each other when molding the extruded material, making it difficult to operate the base surface slip system against external stress.
반면, 제 4 시편(D)과 같이 기저면 슬립계가 슬립면 및 슬립방향 면에서 주변형 방향과 일정각도를 유지하도록 배치되는 경우에는, 재료의 변형이 용이해져 상온 성형성이 우수하다.On the other hand, when the base surface slip system is arranged to maintain a constant angle with the peripheral type direction in the slip surface and the slip direction surface as in the fourth specimen D, the deformation of the material is facilitated and the room temperature formability is excellent.
이러한 재료 내에서의 기저면 슬립계의 배열방향과 분포는 HCP 구조의 (0001) 극점도(pole figure)를 통해 확인할 수 있다. 이하에서는 HCP 구조를 갖는 AZ31 판재를 예로 들어 보다 구체적으로 설명한다. AZ31 판재는 마그네슘에 알루미늄과 아연이 함유된 마그네슘 합금의 일 예이다.The arrangement and distribution of the base slip system in these materials can be confirmed by the (0001) pole figure of the HCP structure. Hereinafter, the AZ31 plate having the HCP structure will be described in more detail. The AZ31 sheet is an example of a magnesium alloy containing magnesium in aluminum and zinc.
도 10은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 +Z축 방향에서의 (0001) 극점도이다. 도 11은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 -Z축 방향에서의 (0001) 극점도이다. 도 12는 비교예에 따른 AZ31 판재의 (0001) 극점도이다.10 is a (0001) pole figure in the + Z axis direction of the AZ31 sheet extruded by the asymmetrical extrusion method according to an embodiment of the present invention. 11 is a (0001) pole figure in the -Z axis direction of the AZ31 sheet extruded by the asymmetrical extrusion method according to an embodiment of the present invention. 12 is a (0001) pole figure of the AZ31 sheet according to the comparative example.
도 10 내지 도 11을 참조하면, 본 발명의 실시예에 따라서 비대칭 압출된 AZ31 판재는 (0001) 극점도 상에서 기저면, 즉 (0001) 면의 결정방향이 중심에서 확연히 벗어나 있음을 알 수 있다. 비대칭 압출된 AZ31 판재의 (0001) 극점도 상의 배치는 도 17 및 도 18의 제 4 시편(D)과 유사하다. 따라서 비대칭 압출된 AZ31 판재는 그 기저면 슬립계가 주변형 방향과 일정각도를 유지하도록 배치되어 우수한 성형성을 나타낸다.10 to 11, it can be seen that the AZ31 plate asymmetrically extruded according to the embodiment of the present invention is a crystal direction of the base surface, that is, the (0001) plane is clearly off from the center on the (0001) pole figure. The arrangement on the (0001) pole figure of the asymmetrically extruded AZ31 sheet is similar to the fourth specimen D of FIGS. 17 and 18. Thus, asymmetrically extruded AZ31 sheet material is arranged so that its base surface slip system maintains a constant angle with the peripheral direction, showing excellent formability.
반면, 도 12에 도시된 바와 같이, 대칭 압연 또는 대칭 압출된 비교예에 따른 AZ31 판재는 (0001) 극점도 상에서 기저면의 결정방향이 중심에 배치되어 있음을 알 수 있다. 이러한 배치는 도 17 및 도 18의 제 1 시편(A)과 유사하고, 따라서 비교예에 따른 AZ31 판재는 우수한 성형성을 기대하기 어렵다.On the other hand, as shown in FIG. 12, it can be seen that the AZ31 sheet material according to the comparative example, which is symmetrically rolled or symmetrically extruded, has a crystallographic direction of the base surface at the center thereof. This arrangement is similar to the first specimen A of FIGS. 17 and 18, so that the AZ31 sheet according to the comparative example is difficult to expect excellent formability.
도 13은 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 진응력-진변형률 그래프이다. 도 14는 비교예에 따른 AZ31 판재의 진응력-진변형률 그래프이다.13 is a true stress-strain graph of the AZ31 sheet extruded by the asymmetric extrusion method according to an embodiment of the present invention. 14 is a true stress-strain graph of the AZ31 sheet according to the comparative example.
도 13을 참조하면, 본 발명의 실시예에 따라서 비대칭 압출된 AZ31 판재의 경우 약 30% 이상의 높은 연신율을 보임을 알 수 있다. 반면, 도 14에 도시된 바와 같이, 비교예에 따른 AZ31 판재의 경우 15~20%의 낮은 연신율을 보임을 알 수 있다. 따라서 비대칭 압출방법을 이용하여 AZ31 판재의 연신율을 크게 향상시킬 수 있음을 알 수 있다. 이러한 연신율을 향상은 AZ31 판재의 성형성 향상으로 이어질 수 있다.Referring to FIG. 13, in the case of the asymmetrically extruded AZ31 sheet according to the embodiment of the present invention, it can be seen that a high elongation of about 30% or more is shown. On the other hand, as shown in Figure 14, in the case of the AZ31 plate according to the comparative example it can be seen that the low elongation of 15 ~ 20%. Therefore, it can be seen that the elongation of the AZ31 sheet can be greatly improved by using the asymmetric extrusion method. This improvement in elongation can lead to improved formability of the AZ31 sheet.
도 15는 본 발명의 일 실시예에 따른 비대칭 압출방법에 의해 압출된 AZ31 판재의 인장축에 대한 각도에 따른 r-값을 보여주는 그래프이다.15 is a graph showing the r-value according to the angle with respect to the tensile axis of the AZ31 sheet extruded by the asymmetrical extrusion method according to an embodiment of the present invention.
도 15를 참조하면, 비대칭 압출된 AZ31 판재는 인장각도에 따른 이방성이 크지 않으며 철강 수준의 높은 r-값을 갖는 것을 알 수 있다.Referring to FIG. 15, it can be seen that the asymmetrically extruded AZ31 sheet has not high anisotropy according to the tensile angle and has a high r-value of steel level.
전술한 바에 따르면, 본 발명의 실시예들에 따라 비대칭 압출된 AZ31 판재는 비교예에 따른 AZ31 판재와 현저히 다른 집합조직을 갖게 되고, 이에 따라서 높은 연신율 및 우수한 성형성을 나타냄을 알 수 있다.As described above, the AZ31 plate asymmetrically extruded according to the embodiments of the present invention has a significantly different texture than the AZ31 plate according to the comparative example, it can be seen that exhibits high elongation and excellent formability.
전술한 HCP 구조를 갖는 금속 또는 금속 합금에 대한 설명은 다른 구조, 예컨대 BCC 구조, FCC 구조 등을 갖는 금속 또는 금속 합금에 대해서도 유사한 원리로 적용될 수 있다.The description of the metal or metal alloy having the above-described HCP structure may be applied on a similar principle to metals or metal alloys having other structures, such as BCC structures, FCC structures, and the like.
발명의 특정 실시예들에 대한 이상의 설명은 예시 및 설명을 목적으로 제공되었다. 따라서 본 발명은 상기 실시예들에 한정되지 않으며, 본 발명의 기술적 사상 내에서 해당 분야에서 통상의 지식을 가진 자에 의하여 상기 실시예들을 조합하여 실시하는 등 여러 가지 많은 수정 및 변경이 가능함은 명백하다.The foregoing description of specific embodiments of the invention has been presented for purposes of illustration and description. Therefore, the present invention is not limited to the above embodiments, and various modifications and changes can be made by those skilled in the art within the technical spirit of the present invention in combination with the above embodiments. Do.
50: 피압출재 60: 압출재
110: 컨테이너 120: 스템
130, 130a, 130b, 130c, 130d, 130e: 다이스
135, 135a, 135b, 135c, 135d, 135e: 압출 구멍
132: 고정 부분
134, 134a, 134b, 134c, 134d, 134e: 테이퍼 부분
142, 144: 제 1 내면 146, 148: 제 2 내면50: Extruded material 60: Extruded material
110: container 120: stem
130, 130a, 130b, 130c, 130d, 130e: dice
135, 135a, 135b, 135c, 135d, 135e: extrusion hole
132: fixed part
134, 134a, 134b, 134c, 134d, 134e: tapered portion
142, 144: first
Claims (19)
상기 피압출재의 판면 방향을 기준으로 비대칭적 형상의 압출 구멍을 갖는 다이스를 통해서 상기 피압출재를 밀어내어 상기 피압출재의 두께 방향으로 내부에 전단변형을 유도하면서 상기 피압출재를 압출하는 단계를 포함하고,
상기 다이스의 압출 구멍은 다단의 구멍 크기를 갖고, 상기 압출하는 단계에서 상기 피압출재의 두께 방향으로 내부에 다단의 전단변형을 유도하며,
상기 다이스의 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 단계적으로 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 갖도록 배치되며,
상기 피압출재에 서로 상보적인 전단 변형을 유도하도록, 상기 테이퍼 부분은, 상기 피압출재의 상면 방향으로 기울어진 제 1 테이퍼 부분과, 상기 제 1 테이퍼 부분과 인접하게 배치되며 상기 피압출재의 하면 방향으로 기울어진 제 2 테이퍼 부분을 포함하며,
상기 제 1 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 상부면과 상기 피압출재의 압출 방향에 평행한 하부면을 포함하며,
상기 제 2 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 하부면과 상기 피압출재의 압출 방향에 평행한 상부면을 포함하는, 비대칭 압출방법.In the method of extruding the to-be-extruded material in the form of a plate in the uniaxial direction,
Extruding the extrudate while pushing the extrudate through a die having an extrusion hole having an asymmetrical shape with respect to the plate surface direction of the extrudate, inducing shear deformation therein in the thickness direction of the extrudate; ,
The extrusion hole of the die has a multi-stage pore size, and in the step of extruding induces a multi-stage shear deformation in the thickness direction of the extruded material,
The extrusion hole of the die includes a tapered portion whose width varies in steps along the extrusion direction of the extruded material, the tapered portion is arranged to have an asymmetrical shape with respect to the plate surface direction of the extruded material,
The tapered portion is arranged to be adjacent to the first tapered portion and the first tapered portion inclined in the upper surface direction of the extruded material to induce shear deformations complementary to the extruded material. A second tapered portion inclined,
The first tapered portion includes an upper surface having a slope with respect to the extrusion direction of the extruded material and a lower surface parallel to the extrusion direction of the extruded material,
And the second tapered portion comprises a lower surface having a slope with respect to the extrusion direction of the extruded material and an upper surface parallel to the extrusion direction of the extruded material.
스템을 이용하여 상기 컨테이너 내의 상기 피압출재를 압축하는 단계; 및
상기 컨테이너 전단에 결합되고 다단의 구멍 크기를 갖는 비대칭적인 형상의 압출 구멍을 포함하는 다이스를 통해서 상기 피압출재를 밀어내 상기 피압출재에 다단의 전단변형을 유도하면서 상기 피압출재를 판재 형상으로 일축 방향으로 압출하는 단계를 포함하고,
상기 다이스의 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 갖도록 배치되며,
상기 피압출재에 서로 상보적인 전단 변형을 유도하도록, 상기 테이퍼 부분은, 상기 피압출재의 상면 방향으로 기울어진 제 1 테이퍼 부분과, 상기 제 1 테이퍼 부분과 인접하게 배치되며 상기 피압출재의 하면 방향으로 기울어진 제 2 테이퍼 부분을 포함하며,
상기 제 1 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 상부면과 상기 피압출재의 압출 방향에 평행한 하부면을 포함하며,
상기 제 2 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 하부면과 상기 피압출재의 압출 방향에 평행한 상부면을 포함하는, 비대칭 압출방법.Charging an object to be extruded into a container;
Compressing the extrudate in the container using a stem; And
The extruded material is uniaxially oriented in a plate shape while pushing the extruded material through a die including an asymmetrically shaped extruded hole coupled to the front end of the container and having a multi-stage hole size to induce a multistage shear deformation to the extruded material. Extruding to
The extrusion hole of the die includes a tapered portion whose width varies along the extrusion direction of the extruded material, the tapered portion is disposed to have an asymmetrical shape with respect to the plate surface direction of the extruded material,
The tapered portion is arranged to be adjacent to the first tapered portion and the first tapered portion inclined in the upper surface direction of the extruded material to induce shear deformations complementary to the extruded material. A second tapered portion inclined,
The first tapered portion includes an upper surface having a slope with respect to the extrusion direction of the extruded material and a lower surface parallel to the extrusion direction of the extruded material,
And the second tapered portion comprises a lower surface having a slope with respect to the extrusion direction of the extruded material and an upper surface parallel to the extrusion direction of the extruded material.
상기 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 비대칭적인 형상을 가지며,
상기 피압출재에 서로 상보적인 전단 변형을 유도하도록, 상기 테이퍼 부분은, 상기 피압출재의 상면 방향으로 기울어진 제 1 테이퍼 부분과, 상기 제 1 테이퍼 부분과 인접하게 배치되며 상기 피압출재의 하면 방향으로 기울어진 제 2 테이퍼 부분을 포함하며,
상기 제 1 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 상부면과 상기 피압출재의 압출 방향에 평행한 하부면을 포함하며,
상기 제 2 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 하부면과 상기 피압출재의 압출 방향에 평행한 상부면을 포함하는, 비대칭 압출용 다이스.An extrusion hole having an asymmetrical shape having a multi-stage hole size for extruding the extruded material in the form of a plate in a uniaxial direction,
The extrusion hole includes a tapered portion whose width varies along the extrusion direction of the extruded material, the tapered portion has an asymmetrical shape with respect to the plate direction of the extruded material,
The tapered portion is arranged to be adjacent to the first tapered portion and the first tapered portion inclined in the upper surface direction of the extruded material to induce shear deformations complementary to the extruded material. A second tapered portion inclined,
The first tapered portion includes an upper surface having a slope with respect to the extrusion direction of the extruded material and a lower surface parallel to the extrusion direction of the extruded material,
And the second tapered portion includes a lower surface having an inclination with respect to the extrusion direction of the extruded material and an upper surface parallel to the extrusion direction of the extruded material.
상기 컨테이너의 전단에 결합되고, 상기 피압출재를 판재 형상으로 일축 방향으로 압출하기 위해 다단의 구멍 크기를 갖는 압출 구멍을 포함하는 다이스; 및
상기 피압출재를 밀어내도록 상기 다이스 반대편 상기 컨테이너 내부에 배치된 스템을 포함하고,
상기 압출 구멍은 상기 피압출재의 압출 방향을 따라서 그 폭이 가변되는 테이퍼 부분을 포함하고, 상기 테이퍼 부분은 상기 피압출재의 판면 방향을 기준으로 다단의 비대칭적인 형상을 가지며,
상기 피압출재에 서로 상보적인 전단 변형을 유도하도록, 상기 테이퍼 부분은, 상기 피압출재의 상면 방향으로 기울어진 제 1 테이퍼 부분과, 상기 제 1 테이퍼 부분과 인접하게 배치되며 상기 피압출재의 하면 방향으로 기울어진 제 2 테이퍼 부분을 포함하며,
상기 제 1 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 상부면과 상기 피압출재의 압출 방향에 평행한 하부면을 포함하며,
상기 제 2 테이퍼 부분은 상기 피압출재의 압출 방향에 대하여 기울기를 가지는 하부면과 상기 피압출재의 압출 방향에 평행한 상부면을 포함하는, 비대칭 압출장치.A container for charging the extruded material;
A die coupled to a front end of the container, the die including an extrusion hole having a multi-stage hole size for extruding the extruded material in a uniaxial direction into a sheet shape; And
A stem disposed inside the container opposite the die to push the extrudate;
The extrusion hole includes a tapered portion whose width varies along the extrusion direction of the extruded material, the tapered portion has a multi-stage asymmetrical shape with respect to the plate surface direction of the extruded material,
The tapered portion is arranged to be adjacent to the first tapered portion and the first tapered portion inclined in the upper surface direction of the extruded material to induce shear deformations complementary to the extruded material. A second tapered portion inclined,
The first tapered portion includes an upper surface having a slope with respect to the extrusion direction of the extruded material and a lower surface parallel to the extrusion direction of the extruded material,
And the second tapered portion includes a lower surface having a slope with respect to the extrusion direction of the extruded material and an upper surface parallel to the extrusion direction of the extruded material.
상기 피압출재의 판면 방향을 기준으로 비대칭적 형상의 압출 구멍을 갖는 다이스를 통해서 상기 피압출재를 밀어내어 상기 피압출재의 두께 방향으로 내부에 전단변형을 유도하면서 상기 피압출재를 일축의 압출 방향으로 압출하는 단계를 포함하고,
상기 압출 구멍은 다단의 구멍 크기를 갖고, 상기 압출하는 단계에서 상기 피압출재의 두께 방향으로 내부에 다단의 전단변형을 유도하며,
상기 압출 구멍은, 상기 일축의 압출 방향을 따라서 그 폭이 단계적으로 가변되며 상기 판재 형상의 판면 방향을 기준으로 비대칭적인 형상을 가지는, 테이퍼 부분; 및 상기 피압출재가 최종적으로 통과되며 그 폭이 일정하며 상기 일축의 압출 방향과 평행한 고정 부분; 을 포함하며,
상기 테이퍼 부분은 상기 판재 형상의 판면 방향을 기준으로 비대칭적인 형상을 갖도록 배치되고,
상기 다이스는 상기 판재 형상의 두께 방향을 따라서 상기 테이퍼 부분에 이격 배치된 한 쌍의 제 1 내면들 및 상기 판재 형상의 폭 방향을 따라서 이격 배치된 한 쌍의 제 2 내면들을 포함하고, 상기 한 쌍의 제 2 내면들은 상기 일축의 압출 방향과 평행하게 배치된, 비대칭 압출방법.In the method of extruding the to-be-extruded material in the form of a plate in the uniaxial direction,
The extruded material is extruded in the uniaxial extrusion direction while pushing the extruded material through a die having an asymmetrical extrusion hole with respect to the plate surface direction of the extruded material to induce shear deformation in the thickness direction of the extruded material. Including the steps of:
The extrusion hole has a multistage pore size, and in the extruding step, the extruded holes induce a multistage shear deformation therein in the thickness direction of the extruded material,
The extrusion hole, the tapered portion, the width of which is varied in stages along the uniaxial extrusion direction and has an asymmetrical shape with respect to the plate surface direction of the plate shape; And a fixed portion of the extruding material finally passed and having a constant width and parallel to the uniaxial extrusion direction; / RTI >
The tapered portion is disposed to have an asymmetrical shape with respect to the plate surface direction of the plate shape,
The die includes a pair of first inner surfaces spaced apart from the tapered portion along the thickness direction of the plate shape and a pair of second inner surfaces spaced apart along the width direction of the plate shape. Wherein the second inner surfaces of the substrate are disposed parallel to the uniaxial extrusion direction.
상기 한 쌍의 제 1 내면들 중의 한 면은 상기 일축의 압출 방향과 항상 평행하게 신장하는, 비대칭 압출방법.The method of claim 10,
Wherein one of the pair of first inner surfaces extends always parallel to the uniaxial extrusion direction.
상기 한 쌍의 제 1 내면들은 상기 일축의 압출 방향을 따라서 서로 다른 기울기를 갖도록 배치된, 비대칭 압출방법.The method of claim 10,
And the pair of first inner surfaces are arranged to have different inclinations along the uniaxial extrusion direction.
상기 압출 구멍의 단면은 직사각 형상이고, 상기 직사각 형상은 상기 한 쌍의 제 1 내면들 및 상기 한 쌍의 제 2 내면들에 의해서 한정되는, 비대칭 압출방법.The method of claim 10,
Wherein the cross section of the extrusion hole is rectangular in shape, the rectangular shape being defined by the pair of first inner surfaces and the pair of second inner surfaces.
상기 압출 구멍을 한정하도록, 상기 판재 형상의 두께 방향을 따라서 상기 테이퍼 부분에 이격 배치된 한 쌍의 제 1 내면들 및 상기 판재 형상의 폭 방향을 따라서 이격 배치된 한 쌍의 제 2 내면들을 포함하고,
상기 테이퍼 부분은 상기 판재 형상의 판면을 기준으로 비대칭적인 형상을 갖고,
상기 한 쌍의 제 2 내면들은 상기 일축의 압출 방향과 평행하게 배치된,
비대칭 압출용 다이스.It has an asymmetrical shape with respect to the plate surface of the plate shape in order to extrude the extruded material in a plate shape along the uniaxial extrusion direction while inducing shear deformation therein in the thickness direction of the material to be extruded, and along the single axis extrusion direction. An extrusion hole including a tapered portion having a variable width and a fixed portion through which the extruded material is finally passed and having a constant width thereof and parallel to the uniaxial extrusion direction; And
And a pair of first inner surfaces spaced apart in the tapered portion along the thickness direction of the plate shape and a pair of second inner surfaces spaced apart in the width direction of the plate shape to define the extrusion hole. ,
The tapered portion has an asymmetrical shape with respect to the plate surface of the plate shape,
The pair of second inner surfaces are disposed parallel to the uniaxial extrusion direction,
Dies for asymmetric extrusion.
상기 컨테이너의 전단에 결합되고, 상기 피압출재의 두께 방향으로 내부에 전단변형을 유도하면서 상기 피압출재를 판재 형상으로 일축의 압출 방향을 따라서 압출하기 위한 직사각 형상의 압출 구멍을 포함하는 다이스; 및
상기 피압출재를 밀어내도록 상기 다이스 반대편 상기 컨테이너 내부에 배치된 스템을 포함하고,
상기 압출 구멍은 상기 일축의 압출 방향을 따라서 그 폭이 단계적으로 가변되는 테이퍼 부분과 상기 피압출재가 최종적으로 통과되며 그 폭이 일정하며 상기 일축의 압출 방향과 평행한 고정 부분을 포함하며, 상기 테이퍼 부분은 상기 판재 형상의 판면을 기준으로 비대칭적인 형상을 갖고,
상기 다이스는 상기 판재 형상의 두께 방향을 따라서 상기 테이퍼 부분에 이격 배치된 한 쌍의 제 1 내면들 및 상기 판재 형상의 폭 방향을 따라서 이격 배치된 한 쌍의 제 2 내면들을 포함하고, 상기 한 쌍의 제 2 내면들은 상기 일축의 압출 방향과 평행하게 배치된,
비대칭 압출장치.A container for charging the extruded material;
A die coupled to a front end of the container, the die including a rectangular extrusion hole for extruding the extruded material in a plate shape along a uniaxial extrusion direction while inducing shear deformation therein in the thickness direction of the extruded material; And
A stem disposed inside the container opposite the die to push the extrudate;
The extrusion hole includes a tapered portion whose width varies in stages along the uniaxial extrusion direction, and a fixed portion through which the extruded material is finally passed, the width of which is constant and parallel to the uniaxial extrusion direction, wherein the taper The part has an asymmetrical shape with respect to the plate surface of the plate shape,
The die includes a pair of first inner surfaces spaced apart from the tapered portion along the thickness direction of the plate shape and a pair of second inner surfaces spaced apart along the width direction of the plate shape. The second inner surfaces of are arranged parallel to the uniaxial extrusion direction,
Asymmetric Extruder.
19. An asymmetric extrusion apparatus according to claim 18, wherein one of the pair of first inner surfaces extends always parallel to the uniaxial extrusion direction.