KR101230079B1 - Sheet for golf hitting mark - Google Patents
Sheet for golf hitting mark Download PDFInfo
- Publication number
- KR101230079B1 KR101230079B1 KR1020110125647A KR20110125647A KR101230079B1 KR 101230079 B1 KR101230079 B1 KR 101230079B1 KR 1020110125647 A KR1020110125647 A KR 1020110125647A KR 20110125647 A KR20110125647 A KR 20110125647A KR 101230079 B1 KR101230079 B1 KR 101230079B1
- Authority
- KR
- South Korea
- Prior art keywords
- golf
- display sheet
- film
- elastic fiber
- spot
- Prior art date
Abstract
Description
본 발명은 골프클럽으로 골프공을 타격시 타점을 보정하기 위한 골프타점표시시트에 관한 것이다.
The present invention relates to a golf score display sheet for correcting the RBI when hitting a golf ball with a golf club.
골프는 우리나라를 포함하여 전 세계적으로 많은 사람들이 즐기는 대중 스포츠의 하나로 자리를 잡아가고 있다. 대부분의 스포츠가 그러하듯이 골프 역시 개개인의 타고난 능력과 꾸준한 노력 정도에 따라 정확성 및 숙련성의 차이를 나타낸다. 특히, 어드레스에서 피니쉬까지의 스윙 동작중 골프공과 접촉하는 임팩트 시점에서 골프공이 골프 헤드 페이스의 어느 위치에 타격되며, 또한 임팩트 시점에서의 상기 페이스가 골퍼의 중심 위치에서 직각을 이루는가의 여부는 정확한 스윙을 하기 위한 매우 중요한 요인으로 작용하게 된다.Golf is becoming one of the most popular sports enjoyed by many people around the world including Korea. Like most sports, golf also differs in accuracy and skill, depending on the individual's natural ability and level of effort. In particular, the golf ball is hit at the golf head face at the impact point of contact with the golf ball during the swing operation from the address to the finish, and whether or not the face at the impact point is perpendicular to the golfer's center position is the correct swing. It is a very important factor for doing this.
일반적인 골프클럽은 상단부에 손으로 파지할 수 있는 그립이 마련된 샤프트와 상기 샤프트의 하단부에 접합되고 전면쪽으로 평면상의 페이스(타구면)가 형성되어 있는 헤드로 이루어진다.A typical golf club consists of a shaft provided with a grip which can be gripped by hand at the upper end and a head which is joined to the lower end of the shaft and has a flat face (ball surface) toward the front side.
상기 페이스의 중앙에는 스윗스팟이라는 가상의 점을 그려볼 수 있는데, 상기 스윗스팟 부근에 정확하게 타구되었을 때 골프공이 가장 이상적으로 날아갈 수 있다. 즉, 일반적인 골프 타격 원리에 의하면, 골퍼가 원하는 방향으로 정확히 타격하기 위해서는 상기 헤드의 페이스가 목표 타구방향에 대해 수직을 이루고 골프공이 상기 페이스의 중심, 예컨대 스윗스팟(Sweet Spot)에 오도록 정렬 유지된 상태에서 백스윙 후 상기 헤드가 목표 타구방향과 일치하도록 이동시키면서 타구하여야만 타격된 골프공이 정확한 궤도를 그리며 원하는 방향으로 날아가게 된다. 만일, 타구시 골프공과 접촉하는 타점이 스윗스팟과 일치하지 않으면 타격된 골프공은 어느 방향으로든 미소한 사이드 스핀(Side spin)을 유발하여 공의 궤적이 변화하게 될 뿐만 아니라, 헤드의 타력이 골프공에 완전히 전달될 수 없으므로 타구 이동거리도 줄어들게 된다.In the center of the face can be imagined a virtual spot called a sweet spot, the golf ball is most ideal to fly when hit accurately near the sweet spot. In other words, according to the general golf striking principle, in order for a golfer to strike exactly in the desired direction, the face of the head is perpendicular to the target batting direction and the golf ball is aligned so that the golf ball is at the center of the face, such as a sweet spot. After the backswing in the state, the head must be hit while moving to match the target hitting direction to hit the golf ball in the correct direction to draw the correct track. If the hitting contact with the golf ball does not coincide with the sweet spot when hitting the ball, the hit golf ball causes a slight side spin in any direction, which changes the trajectory of the ball, and the head's inertia causes the golf to hit. Since the ball cannot be completely delivered to the ball, the batting distance will be reduced.
이와 같이 정확한 타격은 목표 타구방향에 대해 수직으로 페이스를 유지하는 것과 헤드가 목표 타구방향과 일치하도록 타구하는 것 등의 두 가지 요건을 모두 만족시켜야만 달성이 가능하지만 대부분의 사람은 이론과 같은 정확한 스윙을 항상 유지할 없음은 물론이고 숙련된 프로골퍼라 하더라도 어느 정도의 타격 오차는 늘존재한다.This exact hit can only be achieved by satisfying both of the following requirements: keeping the face perpendicular to the target direction and hitting the head to match the target direction. Of course, there is always a certain amount of hitting error even a skilled professional golfer as well as not always maintained.
따라서 대다수의 골퍼들은 무수한 스윙 연습을 통해 임팩트 순간의 페이스 방향을 정확하게 유지함과 아울러 상기 페이스의 스윗스팟 위치에서 골프공이 타격될 수 있게 하고자 많은 시간과 노력을 기울이고 있으므로 연습 과정에서 스윗스팟 부근에 제대로 타구되었는지의 여부를 즉시 확인할 수 있는 장치가 필요하다.Therefore, the majority of golfers spend a lot of time and effort to maintain the exact direction of the face at the moment of impact through countless swing exercises, and to be able to hit the golf ball at the sweet spot position of the face, so the ball hits the sweet spot in the practice It is necessary to have a device that can immediately check whether or not.
타점표시장치로는 두 겹의 종이 사이에 숯가루를 구비하여 타격시 먹지와 같은 원리에 의하여 종이에 타점군을 형성하는 장치가 있으나, 타격 시 영구적인 자국이 발생하므로 4~5회 사용시 계속 교체해야 하는 문제가 있다. 특히 물에 젖은 골프공을 사용하는 경우에는 쉽게 찢겨지므로 수명이 더 짧아진다.The spot display device is a device that forms a spot group on paper according to the same principle as having a batter with charcoal powder between two layers of paper. There is a problem that needs to be done. In particular, water-soaked golf balls are easily torn and shorter in life.
다른 타점표시장치로는 두 겹의 필름 사이에 점성이 있는 물질이 코팅되어 타격시 페이스쪽에 위치한 짙은 색상의 필름이 앞쪽에 구비된 필름에 붙어 타점군을 형성하고, 재사용시에는 공기 주입구를 이용하여 상기 두 필름을 떨어뜨려 사용하는 장치가 있으나, 공기를 주입하더라도 두 필름이 잘 떨어지지 않으며 10여 차례 이상 사용시 필름에 구멍이 형성되어 더 이상 타점 마커로써 작용하지 못하는 문제가 있다. 또한, 종래 한국등록특허 제414618호에는 완충시트(부직포) 상면에 타점표시시트(폴리비닐클로라이드)를 구비한 스윗스팟테이프가 개시되어 있다. 상기 스윗스팟테이프에는 골프클럽으로 골프공을 타격시 타점군이 형성되어 타점을 확인할 수 있지만, 1회 이상은 사용이 불가능하여 연습시 상기 스윗스팟테이프를 계속 교체해야 하는 문제가 있다.
In other spot display devices, a viscous material is coated between two layers of film so that a dark colored film placed on the face is attached to the film provided at the front to form a spot group, and when reused, an air inlet is used. There is a device that uses the two films to drop, but even if the air is injected, the two films do not fall well, and when used more than 10 times there is a problem that the hole formed in the film no longer acts as a spot marker. In addition, Korean Patent No. 414618 discloses a sweet spot tape having a spot display sheet (polyvinyl chloride) on an upper surface of a buffer sheet (nonwoven fabric). In the sweet spot tape, a hitting group is formed when hitting a golf ball with a golf club, but it is possible to check the hitting spot, but there is a problem that the sweet spot tape must be continuously replaced during practice.
본 발명은 섬유 바닥면에 대하여 수직 방향으로 기모가 형성된 탄성섬유를 포함하는 골프타점표시시트를 제공하는 것을 목적으로 한다.An object of the present invention is to provide a golf score display sheet comprising elastic fibers brushed in a direction perpendicular to the fiber bottom surface.
또한, 본 발명은 필름 상면에 상기 필름에 대하여 수직 방향으로 탄성섬유 기모가 형성된 것을 포함하는 골프타점표시시트를 제공하는 것을 다른 목적으로 한다.
In addition, another object of the present invention is to provide a golf score display sheet comprising an elastic fiber brush is formed in a vertical direction with respect to the film on the film upper surface.
상기한 목적을 달성하기 위하여 본 발명은 섬유 바닥면에 대하여 수직 방향으로 기모가 형성된 탄성섬유를 포함하여, 압력을 받으면 기모가 수평 방향으로 기울어지고 수분이 공급되면 수직 방향으로 일어서는 것을 특징으로 하는 골프타점표시시트를 제공한다.In order to achieve the above object, the present invention includes an elastic fiber having a brush in the vertical direction with respect to the bottom surface of the fiber, when the pressure is raised, the brush is inclined in the horizontal direction, characterized in that rises in the vertical direction when water is supplied Provide a golf score sheet.
상기 골프타점표시시트는 0.3 kgf/㎠ 이상의 압력을 받으면 상기 탄성섬유의 기모가 바닥면에 대하여 수평 방향으로 기울어지며, 상기 기모가 기울어진 탄성섬유에 수분이 공급되면 기모가 바닥면에 대하여 수직 방향으로 형성될 수 있다.When the golf score display sheet is subjected to a pressure of 0.3 kgf / ㎠ or more, the raising of the elastic fiber is inclined in the horizontal direction with respect to the bottom surface, and when the water is supplied to the inclined elastic fiber, the raising is perpendicular to the bottom surface. It can be formed as.
상기 탄성섬유 하면에 순차적으로 필름, 점착제층 및 이형필름을 더 구비할 수 있다.The lower surface of the elastic fiber may be further provided with a film, an adhesive layer and a release film.
또한, 본 발명은 필름 상면에, 상기 필름에 대하여 수직 방향으로 탄성섬유 기모가 형성되어, 압력을 받으면 기모가 수평 방향으로 기울어지고 수분이 공급되면 수직 방향으로 일어서는 것을 특징으로 하는 골프타점표시시트를 제공한다.In addition, the present invention is formed on the upper surface of the film, the elastic fiber brush is formed in the vertical direction with respect to the film, when the pressure is raised, the brush is tilted in the horizontal direction and when the water is supplied to the golf RBI display sheet, characterized in that standing in the vertical direction To provide.
상기 필름의 하면에 순차적으로 점착제층 및 이형필름을 더 구비할 수 있다.The lower surface of the film may be further provided with an adhesive layer and a release film.
상기 탄성섬유 기모는 함수율이 14% 이하일 수 있다.The elastic fiber brush may have a water content of 14% or less.
상기 탄성섬유 기모의 길이는 0.3 내지 1.2mm일 수 있다.The length of the elastic fiber brush may be 0.3 to 1.2mm.
상기 필름의 두께는 0.05 내지 0.5mm일 수 있다.The thickness of the film may be 0.05 to 0.5mm.
상기 골프타점표시시트의 두께는 0.5 내지 1.5mm일 수 있다.The golf score display sheet may have a thickness of 0.5 to 1.5 mm.
상기 골프타점표시시트는 스윗스팟홀이 형성될 수 있다.
The golf spot display sheet may be formed with a sweet spot hole.
본 발명의 골프타점표시시트는 골프공에 의하여 압력이 가해지면 탄성섬유 기모가 수직 방향에서 수평 방향으로 기울어져 쉽게 타점군을 확인할 수 있으므로 자세교정 및 원인분석이 용이하며, 실전에서도 연습시의 타격감을 유지할 수 있어 단기간 내에 타격 실력이 향상된다. Golf score display sheet of the present invention is easy to posture correction and cause analysis, because the elastic fiber brushed inclined from the vertical direction to the horizontal direction when the pressure is applied by the golf ball, easy to check the spot group, hitting during practice in practice Keep your senses and improve your batting skills in a short time.
또한, 상기 기울어진 탄성섬유 기모에 수분이 공급되면 탄성섬유 기모가 필름에 대하여 수직 방향으로 다시 일어나므로 1회용이 아닌 드라이버용의 경우에는 100회 이상 사용할 수 있으며, 이로 인하여 중간에 타점표시장치를 교체하는 수고가 필요 없을 뿐만 아니라 타격의 집중도를 높이고 자신이 친 공의 타점을 확인할 수 있으므로 연습에 재미를 더할 수 있다. In addition, when water is supplied to the inclined elastic fiber brushing, the elastic fiber brushing occurs again in the vertical direction with respect to the film, so that it can be used more than 100 times for a driver that is not a one-time use. Not only does it need to be replaced, but it also increases the concentration of the hit and allows you to check the hit of your ball, which can be fun to practice.
또한, 본 발명의 골프타점표시시트는 골프클럽의 헤드 전면쪽에 위치한 페이스 전체에 걸쳐 배치되므로 골프클럽의 손상을 방지할 수 있다.In addition, since the golf score display sheet of the present invention is disposed over the entire face located on the front of the head of the golf club can prevent damage to the golf club.
또한, 본 발명의 골프타점표시시트는 골프공에 의하여 탄성섬유 기모가 오염되더라도 수분만 공급되면 오염이 쉽게 제거된다.
In addition, the golf score display sheet of the present invention, even if the elastic fiber brushed by the golf ball is contaminated easily if only moisture is supplied.
도 1은 본 발명의 바람직한 일실시예에 따른 방법에 의해 제조된 골프타점표시시트를 적용한 사진이며,
도 2a는 본 발명의 바람직한 일실시예에 따른 골프타점표시시트 단면도이고,
도 2b는 본 발명의 다른 실시예에 따른 골프타점표시시트 단면도이며,
도 3은 도 1의 탄성섬유 기모를 촬영한 SEM 사진이고,
도 4a는 도 1의 골프타점표시시트에 압력이 가해지기 전을 나타낸 사진이며,
도 4b는 도 1의 골프타점표시시트에 압력이 가해져 타점군이 형성된 사진이고,
도 4c는 도 4b의 압력이 가해져 타점군이 형성된 골프타점표시시트에 수분이 공급되어 탄성섬유 기모가 원상태로 일어선 사진이며,
도 5a는 도 1의 골프타점표시시트에 압력이 가해지기 전을 촬영한 현미경 사진이고,
도 5b는 도 1의 골프타점표시시트에 압력이 가해진 후를 촬영한 현미경 사진이다. 1 is a photograph applying the golf score display sheet manufactured by the method according to an embodiment of the present invention,
Figure 2a is a cross-sectional view of the golf score display sheet according to an embodiment of the present invention,
Figure 2b is a cross-sectional view of the golf spot display sheet according to another embodiment of the present invention,
Figure 3 is a SEM photograph of the brushed elastic fiber of Figure 1,
Figure 4a is a photograph showing before the pressure is applied to the golf RBI display sheet of Figure 1,
4B is a photograph in which a spot group is formed by applying pressure to the golf spot display sheet of FIG. 1;
Figure 4c is a photograph of the elastic fiber brush raised to the original state by supplying moisture to the golf spot display sheet is formed by the pressure of Figure 4b is formed a spot group,
Figure 5a is a micrograph taken before the pressure is applied to the golf RBI display sheet of Figure 1,
5B is a micrograph taken after the pressure is applied to the golf spot display sheet of FIG. 1.
본 발명은 골프공에 의하여 압력이 가해지면 탄성섬유가 기울어 타점군이 표시되고, 탄성섬유가 기울어진(누운) 부분에 수분을 공급하면 원상태로 일어서는 탄성섬유를 포함하는 골프타점표시시트에 관한 것이다.
The present invention relates to a golf spot display sheet comprising an elastic fiber when the pressure is applied by a golf ball, the elastic fiber is inclined to display the spot group, and the elastic fiber is elastic when the moisture fiber is supplied to the inclined (lying) portion. will be.
이하, 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail.
본 발명에 따른 골프타점표시시트는 필름 상면에 상기 필름에 대하여 수직 방향으로 구비되는 탄성섬유를 포함하는 것으로서, 도면을 참조하여 보다 상세하게 설명하면 다음과 같다.
Golf spot display sheet according to the present invention includes an elastic fiber provided in the vertical direction with respect to the film on the film upper surface, described in more detail with reference to the drawings as follows.
도 1은 본 발명의 바람직한 일실시예에 따른 방법에 의해 제조된 골프타점표시시트를 적용한 사진이며, 도 2a는 본 발명의 바람직한 일실시예에 따른 골프타점표시시트 단면도이고, 도 2b는 본 발명의 다른 실시예에 따른 골프타점표시시트 단면도이며, 도 3은 도 1의 탄성섬유 기모를 촬영한 SEM 사진이고, 도 4a는 도 1의 골프타점표시시트에 압력이 가해지기 전을 나타낸 사진이며, 도 4b는 도 1의 골프타점표시시트에 압력이 가해져 타점군이 형성된 사진이고, 도 4c는 도 4b의 압력이 가해져 타점군이 형성된 골프타점표시시트에 수분이 공급되어 탄성섬유 기모가 원상태로 일어선 사진이며, 도 5a는 도 1의 골프타점표시시트에 압력이 가해지기 전을 촬영한 현미경 사진이고, 도 5b는 도 1의 골프타점표시시트에 압력이 가해진 후를 촬영한 현미경 사진이다. 1 is a photograph applying the golf RBI display sheet manufactured by the method according to a preferred embodiment of the present invention, Figure 2a is a cross-sectional view of the golf RBI display sheet according to an embodiment of the present invention, Figure 2b is a present invention 3 is a cross-sectional view of a golf RBI display sheet according to another embodiment of the present invention, FIG. 3 is a SEM photograph of brushed elastic fibers of FIG. 1, and FIG. 4A is a photo showing the pressure applied to the golf RBI display sheet of FIG. 1. FIG. 4B is a photograph in which the RBI group is formed by applying pressure to the golf RBI display sheet of FIG. 1, and FIG. 4C is supplied with moisture to the golf RV display sheet in which the RBI group is formed by applying the pressure of FIG. It is a fishing boat photograph, FIG. 5A is a microscope picture taken before the pressure is applied to the golf spot display sheet of FIG. 1, and FIG. 5B is a microscope picture taken after the pressure is applied to the golf spot display sheet of FIG.
도 1에 도시된 바와 같이, 골프타점표시시트(100)는 골프클럽의 헤드 전면쪽에 위치한 페이스 전체에 걸쳐 배치된다.As shown in Figure 1, the golf
또한, 도 2a에 도시된 바와 같이, 상기 골프타점표시시트(100)는 바닥면(탄성섬유 바닥면)에 대하여 수직 방향으로 기모(121)가 형성된 탄성섬유(120)를 포함하며, 기모(121)가 형성되지 않은 탄성섬유(120)의 다른 면에 접착제(130), 필름(110), 점착제층(140) 및 이형필름(150)이 순차적으로 형성된다. In addition, as shown in Figure 2a, the golf
또한, 도 2b에 도시된 바와 같이, 상기 골프타점표시시트(100)는 필름(110) 상면에 상기 필름(110)에 대하여 수직 방향으로 탄성섬유 기모(121)가 구비되며, 필름(110) 하면에 점착제층(140)과 이형필름(150)이 순차적으로 형성된다. 상기 탄성섬유(120)는 접착제(130)에 의하여 필름(110)에 구비된다. 필름(110) 상면에 수직 방향으로 탄성섬유 기모(121)를 형성하는 것은 정전기 방식 등을 사용한다. In addition, as shown in Figure 2b, the golf
필름 상면에 수직 방향으로 탄성섬유 기모를 형성하는 방법은 상기 정전기 방식에 국한되지 않으며, 당 분야에서 사용되는 일반적으로 방법이 적용될 수 있다.The method of forming the elastic fiber brush in the direction perpendicular to the upper surface of the film is not limited to the electrostatic method, and generally used in the art may be applied.
상기 접착제(130)는 탄성섬유와 필름을 접착할 수 있는 것이라면 특별히 제한되지 않는다. 또한, 점착제(140)는 필름과 골프클럽의 페이스와 점착될 수 있는 것이라면 특별히 제한되지 않으며, 이형필름(150)은 당 분야에서 사용되는 통상의 필름(예, 이형지, 코팅지)을 사용한다. 본 발명에서 이형필름은 이형지로 동일한 의미로 사용된다.The adhesive 130 is not particularly limited as long as it can bond the elastic fiber and the film. In addition, the adhesive 140 is not particularly limited as long as it can be adhered to the face of the film and golf club, the
상기 필름(110)은 골프공에 의하여 여러 차례 강한 압력을 받더라도 찢어지지 않고 탄성섬유(120) 및 기모(121)와 접착이 용이한 것으로서, 구체적으로 폴리에스테르필름, 폴리에틸렌테레프탈레이트필름, 폴리프로필렌필름, 연질폴리염화비닐필름, 실리콘코팅필름, 폴리스티렌필름으로 이루어진 군에서 선택된 1종을 들 수 있으며, 바람직하게는 폴리에스테르필름이다. The
상기 필름(110)의 두께는 0.05 내지 0.5 mm, 바람직하게는 0.07 내지 0.3 mm이어야 골프타점표시시트를 사용하지 않는 경우와 비교하여 비거리에 변화가 없다. 필름(110)의 두께가 0.07 mm미만인 경우에는 골프공에 의하여 압력으로 필름이 찢어질 수 있으며, 두께가 0.3 mm를 초과하는 경우에는 골프타점표시시트를 사용하지 않는 경우와 비교하여 비거리가 짧아진다. The thickness of the
상기 탄성섬유 기모(121)는 도 3에 도시된 바와 같이 수직 방향으로 서 있으며, 탄성을 가지고 물을 흡수하는 구조로 셀룰로스계 섬유의 모세관 현상으로 인해 수분이 공급되면 팽윤하여 기모(121)들이 다시 일어서게 된다.The
따라서 본 발명의 골프타점표시시트(100)를 100회 이상 사용할 수 있다.Therefore, the golf
탄성섬유 기모(121)의 길이는 0.3 내지 1.2 mm, 바람직하게는 0.5 내지 1.0mm이다. 탄성섬유 기모(121)의 길이가 0.3 mm미만인 경우에는 타점군(170)을 확인하기 어려우며, 길이가 1.2mm를 초과하는 경우에는 수분 흡수 후 회복이 완전치 않고 골프타점표시시트를 사용하지 않는 경우와 비교하여 비거리가 짧아진다. 기모가 형성된 탄성섬유를 사용하는 경우에는 기모를 제외한 바닥면의 탄성섬유의 두께는 0.05 내지 0.5mm인 것이 바람직하다.The length of the
본 발명의 골프타점표시시트(100)의 두께는 0.5 내지 1.5mm인 것이 바람직하다. 상기 두께를 벗어나는 경우에는 골프타점표시시트를 사용하지 않는 경우와 비교하여 비거리가 짧아진다. The thickness of the golf
이러한 탄성섬유(120) 및 기모(121)는 구체적으로 폴리우레탄, 레이온, 폴리에테르 및 폴리에스테르로 이루어진 군에서 선택된 1종 또는 2종 이상을 들 수 있으나, 바람직하게는 레이온을 단독으로 사용하는 것이다. The
가죽 등의 기모를 사용하는 경우에도 타격 시 자국이 생길 수는 있으나, 복원을 위해 손으로 문지르는 작업이 수행되며, 젖은 공을 타격하거나 비가 오는 날에는 사용할 수 없는 단점이 있다.Even when using a brush such as leather, the marks may be generated at the time of hitting, but rubbing is performed by hand for restoration, and there is a disadvantage that it cannot be used on a wet ball or a rainy day.
상기 탄성섬유 기모는 함수율이 14% 이하인 것이 바람직하다, 함수율이 너무 큰 경우에는 상대적으로 물이 빠져 나가는 비율이 낮아 타격 자국을 확인하기 어려운 단점이 있다.It is preferable that the water content of the elastic fiber brush is 14% or less. If the water content is too large, a relatively low rate of water escape is difficult to identify the blow marks.
도 4 및 도 5에 도시된 바와 같이, 본 발명의 골프타점표시시트(100)는 골프공에 의하여 압력을 받지 않으면 탄성섬유 기모가 필름에 대하여(또는 섬유 바닥면) 수직 방향으로 서 있으나(도 4a 및 5a), 골프공에 의하여 0.3 kgf/㎠ 이상의 압력을 받으면 기모가 필름에 대하여(또는 섬유 바닥면) 수평 방향으로 기울어져(도 5b, 흰 부분) 타점군(170)을 형성한다. 상기 기울어진 탄성섬유에 수분이 공급되면 즉시 탄성섬유가 원상태(필름에 대하여 수직 방향)로 일어난다. As shown in Figures 4 and 5, the golf
상기 타점군(170)은 골프공에 의한 압력에 의하여 탄성섬유 기모가 기울어진 부분과 탄성섬유 기모가 서 있는 부분의 상이한 빛 반사에 의하여 구분된다. The
또한, 타점군(170)은 골프타점표시시트(100)를 수분에 적신 상태에서 사용하면 골프공의 타격에 의한 압력에 의하여 수분이 빠져나감과 동시에 탄성섬유 기모가 기울어지므로 더욱 선명하게 표시된다. In addition, when the
이러한 골프타점표시시트(100)의 중앙부에 골프클럽의 페이스의 스윗스팟을 중심으로 하여 반경 7mm 정도의 스윗스팟홀(160)이 구비된다.The center of the golf
상기 구비된 스윗스팟홀(160)은 관통홀로 형성되므로 골프공이 스윗스팟에 타격되면 골프타점표시시트에 타점군이 형성되지 않는다.
Since the provided
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention. Such variations and modifications are intended to be within the scope of the appended claims.
실시예 1.Example 1.
두께가 0.07mm인 폴리에스테르필름 상면에 접착제를 이용하여 폴리에스테르필름에 대하여 수직 방향으로 레이온 기모를 구비하고 상기 폴리에스테르필름 하면에 점착제를 도포한 후 이형필름을 구비함으로써 골프타점표시시트를 제조하였다. 이때 레이온 기모의 길이는 0.7mm이며, 함수율은 8.42%이다.
A golf spot display sheet was prepared by providing a rayon brush in the vertical direction with respect to the polyester film by using an adhesive on an upper surface of a polyester film having a thickness of 0.07 mm, and applying a pressure-sensitive adhesive on the lower surface of the polyester film. . At this time, the length of the brushed rayon was 0.7mm, and the moisture content was 8.42%.
실시예 2.Example 2.
레이온 섬유 바닥면에 대하여 수직 방향으로 레이온 기모가 형성되며, 레이온 섬유의 하면에 접착제를 도포한 후 두께가 0.07 mm인 폴리에스테르필름를 구비하고, 상기 폴리에스테르필름 하면에 점착제를 도포한 후 이형필름을 구비함으로써 골프타점표시시트를 제조하였다. 이때 레이온 기모의 길이는 0.7mm이며, 함수율은 8.42%이다.
Rayon raising is formed in a direction perpendicular to the bottom surface of the rayon fiber, and after the adhesive is applied to the bottom surface of the rayon fiber, a polyester film having a thickness of 0.07 mm is provided, and a release film is applied after applying an adhesive to the bottom surface of the polyester film. By providing a golf score display sheet was prepared. At this time, the length of the brushed rayon was 0.7mm, and the moisture content was 8.42%.
실시예 3. Example 3.
상기 실시예 1과 동일하게 실시하되, 함수율은 14%인 골프타점표시시트를 제조하였다.
The same procedure as in Example 1 was carried out, but a golf score display sheet having a water content of 14% was prepared.
실시예 4. Example 4.
상기 실시예 1과 동일하게 실시하되, 폴리에스테르필름의 두께를 0.1mm로 하여 골프타점표시시트를 제조하였다.
The same procedure as in Example 1 was carried out, but the golf spot display sheet was prepared with a thickness of the polyester film 0.1mm.
실시예 5. Example 5.
상기 실시예 1과 동일하게 실시하되, 레이온 기모의 길이를 1.1mm로 하여 골프타점표시시트를 제조하였다.
A golf score display sheet was manufactured in the same manner as in Example 1 except that the length of the rayon brush was 1.1 mm.
비교예. Comparative example.
완충시트(부직포) 상면에 타점표시시트(폴리비닐클로라이드)를 구비하여 두께가 1 mm인 골프타점표시시트를 제조하였다.
A spotting sheet (polyvinyl chloride) was provided on the upper surface of the buffer sheet (nonwoven fabric) to prepare a golfing spot display sheet having a thickness of 1 mm.
시험예.Test example.
제조된 골프타점표시시트를 골프클럽의 헤드 전면쪽에 위치한 페이스에 설치하여 측정하였다.The manufactured golf score display sheet was installed on the face located on the front side of the golf club and measured.
1. 탄성섬유 기모의 복귀 시간측정: 탄성섬유 기모에 수분을 공급한 후 탄성섬유 기모가 원상태로 일어서는 시간을 측정하였다.1. Measurement of recovery time of raising the elastic fiber raising: The time taken for the elastic fiber raising to stand after measuring the elastic fiber raising was measured.
2. 타점군 선명도 측정: 골프공이 의하여 형성되는 타점군의 선명도를 육안으로 확인하였다.2. RBI group sharpness measurement: The sharpness of the RBI group formed by the golf ball was visually confirmed.
◎: 3 m 거리에서 타점군의 모양이 100% 확인됨◎: 100% of the RBI group at 3m distance
○: 3 m 거리에서 타점군의 모양이 70%이상 확인됨○: More than 70% of the spot groups were identified at a distance of 3 m.
□: 3 m 거리에서 타점군의 모양이 50%이상 확인됨□: At least 3% of the RBI group is identified at a distance of 3 m
△: 3 m 거리에서 타점군의 모양이 30%이상 확인됨(Triangle | delta): More than 30% of the RBI group was confirmed at a distance of 3 m.
X: 3 m 거리에서 타점군의 모양이 확인안됨
X: RBI group's shape is not confirmed at 3 m
안됨comeback
no
위 표 1에 나타낸 바와 같이, 본 발명의 실시예 1 내지 5는 탄성섬유 기모의 복귀시간이 짧으며, 타점군이 선명하나, 비교예는 타점군이 선명하지 못하고, 비거리가 짧은 것을 확인하였다. 특히 비교예는 방향성이 없는 부직포이므로 기모의 회복이 전혀 이루어지지 않음을 확인할 수 있었다.
As shown in Table 1, Examples 1 to 5 of the present invention has a short return time of brushing the elastic fiber, the spot group is clear, the comparative example was confirmed that the spot group is not clear, the distance is short. In particular, the comparative example was confirmed that no recovery of brushing because the nonwoven fabric without a direction.
100: 골프타점표시시트 110: 필름
120: 탄성섬유 121: 탄성섬유 기모
130: 접착제 140: 점착제층
150: 이형필름 160: 스윗스팟홀 100: golf score display sheet 110: film
120: elastic fibers 121: brushed elastic fibers
130: adhesive 140: adhesive layer
150: release film 160: sweet spot hole
Claims (10)
A golf score display sheet comprising an elastic fiber having a brush in the vertical direction with respect to the bottom surface of the fiber, the brush is inclined in the horizontal direction when the pressure is applied, and stand up in the vertical direction when water is supplied.
The method of claim 1, wherein the golf score display sheet is subjected to a pressure of 0.3 kgf / ㎠ or more inclined in the horizontal direction with respect to the bottom surface of the elastic fibers, brushed when the moisture is supplied to the inclined elastic fibers Golf score display sheet, characterized in that formed in the vertical direction with respect to the bottom surface.
The golf score display sheet according to claim 1 or 2, further comprising a film, a pressure-sensitive adhesive layer, and a release film sequentially on the lower surface of the elastic fiber.
An elastic fiber brush is formed in the vertical direction with respect to the film on the upper surface of the film, and when the pressure is applied, the brush is inclined in the horizontal direction, and when the moisture is supplied, the golf score display sheet.
The golf score display sheet according to claim 4, further comprising a pressure-sensitive adhesive layer and a release film sequentially on the lower surface of the film.
The golf score display sheet according to claim 1 or 4, wherein the elastic fiber brush has a water content of 14% or less.
The golf score display sheet according to claim 1 or 4, wherein the length of the elastic fiber brush is 0.3 to 1.2 mm.
The golf score display sheet according to claim 4, wherein the film has a thickness of 0.05 to 0.5 mm.
The golf score display sheet according to claim 1 or 4, wherein the golf score display sheet has a thickness of 0.5 to 1.5 mm.