KR101173888B1 - Composition for water-repellent features and Korean paperHanji of water-repellent features and the manufacturing method thereof - Google Patents
Composition for water-repellent features and Korean paperHanji of water-repellent features and the manufacturing method thereof Download PDFInfo
- Publication number
- KR101173888B1 KR101173888B1 KR1020090097082A KR20090097082A KR101173888B1 KR 101173888 B1 KR101173888 B1 KR 101173888B1 KR 1020090097082 A KR1020090097082 A KR 1020090097082A KR 20090097082 A KR20090097082 A KR 20090097082A KR 101173888 B1 KR101173888 B1 KR 101173888B1
- Authority
- KR
- South Korea
- Prior art keywords
- water
- repellent
- hanji
- composition
- repellent composition
- Prior art date
Abstract
본 발명은 발수기능 조성물 및 발수기능 한지와 그 제조방법에 관한 것으로서, 더욱 상세하게는 친환경 불소계 발수제와 에탄올이나 나노실버 또는 4급 암모늄계 살균제를 물에 혼합하여 이루어지는 발수기능 조성물 및 발수기능 조성물을 코팅처리한 발수기능 한지와 그 제조방법에 관한 것이다.The present invention relates to a water-repellent composition and a water-repellent hanji and a method for producing the same, and more particularly, to a water-repellent composition and a water-repellent composition formed by mixing an environment-friendly fluorine-based water repellent and ethanol or nanosilver or quaternary ammonium-based fungicides in water. It relates to a water-repellent hanji coated and its manufacturing method.
본 발명에 따른 발수기능 조성물 및 발수기능 한지와 그 제조방법에 의하면, 상기 발수기능 조성물은 친환경 불소계 발수제에 천연 살균제인 에탄올 또는 나노실버 또는 4급 암모늄계 살균제를 물과 혼합하여 이루어지고 상기 발수기능 조성물을 침지, 분사 등의 방법으로 한지의 표면에 코팅처리함으로써 숨 쉬는 종이로 잘 알려진 한지 본래의 특성인 우수한 통풍기능을 유지하면서 탁월한 발수기능 및 살균기능을 발휘할 수 있게 하는 효과를 제공한다. According to the water-repellent composition and water-repellent hanji according to the present invention and a method for producing the water-repellent composition, the water-repellent composition is made by mixing ethanol or nanosilver or quaternary ammonium-based fungicide which is a natural fungicide in an environmentally friendly fluorine-based water repellent and water By coating the composition on the surface of Hanji by dipping, spraying, or the like, it provides an effect of exerting excellent water repellency and sterilization function while maintaining excellent ventilation function, which is an inherent characteristic of Hanji, known as a breathing paper.
친환경 발수제, 에탄올, 나노실버, 4급 암모늄계 살균제 Eco-friendly water repellent, ethanol, nano silver, quaternary ammonium sterilizer
Description
본 발명은 발수기능 조성물 및 발수기능 한지와 그 제조방법에 관한 것으로서, 더욱 상세하게는 불소계 발수제와 에탄올이나 나노실버 또는 4급 암모늄계 살균제를 물에 혼합하여 이루어지는 발수기능 조성물 및 발수기능 조성물을 코팅처리한 발수기능 한지와 그 제조방법에 관한 것이다. The present invention relates to a water-repellent composition and a water-repellent hanji, and to a method for manufacturing the same, and more particularly, to a water-repellent composition and a water-repellent composition formed by mixing a fluorine-based water repellent and ethanol or nanosilver or quaternary ammonium fungicides in water. It relates to the treated water-repellent hanji and its manufacturing method.
한지(韓紙)는 닥나무껍질 등의 섬유를 원료로 하여 한국 고유의 제조법으로 만든 종이를 수제 한지(手製 韓紙)라 하고 기계 한지(機械韓紙)는 닥나무를 100% 원료로 하거나 닥나무와 일반 펄프를 혼합하여 자동 연속 롤 생산하는 것을 통칭하여 말한다. Hanji is made of paper made from Korean bark, such as mulberry bark, and is made of handmade Korean paper. Machine Hanji is made from 100% raw material of mulberry, It is commonly known as mixing the pulp to produce automatic continuous rolls.
본 발명에서는 한지라 칭함은 100% 닥나무 원료로 하여 수제(수록지) 또는 기계로 생산하는 것, 그리고 닥나무와 일반 펄프 원료를 혼합하여 수제 또는 기계로 자동 제조되는 개량 한지 등을 한지로 칭한다.In the present invention, the term "hanji" refers to the production of handmade (collected paper) or machine by using 100% mulberry as raw material, and improved hanji, which is automatically manufactured by hand or machine by mixing the mulberry and general pulp raw material.
보통 우리가 현재 일반적으로 쓰는 종이를 양지(洋紙)라고 한다. 한지(韓紙)는 한국에서 손으로 뜬 종이(수록지)로서 중국의 수제지인 화지(華紙)나 일본의 수제지인 화지(和紙)와 구별하여 지칭한 것이다. 옛날의 계림지(鷄林紙)?삼한지(三韓紙)?고려지(高麗紙)?조선지(朝鮮紙)에서 시대가 변함에 따라 그 명칭이 한지로 바뀐 것이다.Usually, the paper we usually use today is called Yangji. Hanji is a hand-made paper from Korea and is distinguished from Chinese handmade paper and Japanese handmade paper. In the old Guilin, Samhanji, Goryeoji, and Joseonji, the name changed to Hanji as the times changed.
한지의 용도는 날로 그 적용의 범위가 넓어져 가고 있다. 종전의 화선지, 창호지, 벽지, 장판지 등에서 현대에 이르러서는 공예지, 장의용 수의지, 선물 포장지, 원예용 꽃다발 포장지(꽃 싸게지). 의류용 섬유 등으로 그 용도가 다양해져 감에도 추세에 부응하는 기술(발수 코팅 기술)이 따라가지 못하고 있는 실정이다.The use of hanji is expanding the scope of its application day by day. Craft papers, artisan papers, gift wrapping paper, and garden bouquet wrapping paper (flower wrapping paper) from the previous Japanese paper, window paper, wallpaper, and cardboard. The use of a variety of applications, such as textile for clothing (water-repellent coating technology) is not keeping up with the trend.
한지의 우수성은 이미 널리 알려져 있으나 장점의 이면에는 한지가 가지는 단점도 동시에 상존하고 있었다. 즉, 한지의 장점으로는 ①질기고 오래가는 것과 ②촉감이 부드럽고 통기성과 보온성이 뛰어나며 ③질감과 천연스런 섬유질의 무늬가 독특하며 ④양지에 비해 가볍고 ⑤산성비나 일반 저장 환경에도 양지처럼 잘 삭아지지 않는다. 동시에 닥나무 한지의 단점은 대체적으로 ①특유의 흡수성으로 물기에 약하며 ②먼지 등 오염이 쉽게 되고 ③접착풀 시공시 잘 늘어지며 ④한지 표 면의 섬유질 조직이 잘 피는(보푸라기) 등의 문제가 있다.The superiority of Hanji is already well known, but the disadvantages of Hanji existed at the same time. In other words, the advantages of Hanji are ① durable and durable ② soft, breathable and warmth, ③ unique texture and natural fiber ④ lighter than the sun ⑤ lighter than acid rain or general storage environment Do not. At the same time, the disadvantages of Korean paper mulberry are ① weakness due to its peculiar absorbency, ② easy to be polluted by dust, ③ easily stretched when glued pools are applied, and ④ fibrous tissues on the surface of Hanji are well bloomed.
상기에 전술한 바와 같이 서양에서 만든 양지에 비해 한지는 탁월한 장점이 있는 반면 그 장점으로 인한 반대의 단점도 동시에 가지고 있어 현대생활의 적용에 제한적으로 이용되고 있는 실정이다.As described above, Hanji has excellent advantages over Western-made Yangji, but also has the opposite disadvantages due to its advantages, which are used in a limited way in the application of modern life.
한지는 특유의 흡수성으로 물에 매우 취약하며 이로 인한 오염이 쉽게 되어 이를 보완하기 위해 발수기능을 부여하는 방법을 다각적으로 모색하였다. 그 예로써 왁스. 실리콘. 불소 등의 물질을 유기용제와 희석하는 공법을 선택해 시도한 결과 한지 고유의 품질을 상당히 훼손하는 역기능을 초래하여 현재에 이르기까지 이룩하지 못한 업계에 숙원의 과제로 남아 있다.Hanji was very vulnerable to water due to its unique absorbency, so it was easy to contaminate it. As an example wax. silicon. As a result of selecting a method of diluting a substance such as fluorine with an organic solvent, it has caused dysfunction that significantly impairs the inherent quality of Hanji, and remains a matter of ambition in an industry that has not been achieved until now.
상기 물질 등을 한지에 코팅하는 과정에서 원지의 수축과 통기성에 장애를 주는 것과 동시에 이 물질들을 용해, 교반하는 용도의 유기용제의 폐해로 2차 환경오염을 수반하는 문제가 있었다. In the process of coating the material and the like on the paper, there is a problem with secondary environmental pollution due to the damage of the organic solvent for the purpose of dissolving and stirring the materials and at the same time to the shrinkage and breathability of the base paper.
더욱이 이러한 종래의 기술로는 천연이며 친환경적인 한지에 비친환경적 요소가 가미되어 결국 순수한 고유 제품의 성격을 잃게 만드는 치명적 결함이 있었다. Moreover, such a conventional technique has a fatal flaw that adds non-environmental elements to natural and eco-friendly hanji, which eventually loses the character of pure original products.
전술한 바와 같이 한지의 단점으로 대두된 항목의 주요 원인은 바로 발수기능이 없기 때문이다. 그러나, 발수기능을 해결하기 위하여 단편적인 처방을 하였을 경우 한지의 장점을 해쳐 한지의 고유의 가치를 훼손하므로 매우 신중하며 과학적으로 접근해야 한다. As mentioned above, the main cause of the items that have emerged as a disadvantage of Hanji is that it does not have a water repellent function. However, in order to solve the water-repellent function, a fragmentary prescription undermines the merits of Hanji, which undermines the value of Hanji.
지금까지 업계에선 문제의 발수기능을 부여하기 위한 시도로 여러 종의 화학제 물질을 코팅한 결과 한지의 수축 문제와 숨 쉬는 한지 고유의 기공을 막아 본래의 성질을 잃게 하는 것, 그리고 천연 닥나무 원료의 비 균일적 조직과 표면 특성으로 인하여 발수기능 물질을 코팅하여도 정상적인 발수기능이 발휘되지 않았다. So far, the industry has attempted to impart water-repellent functions to prevent the shrinkage of Hanji and the pores inherent in the breathing Hanji as a result of coating various chemical substances, and to lose the original properties Due to the non-uniform texture and surface properties, coating of water repellent material did not show normal water repellency.
그 예로써 닥 한지 아이템 중 특별한 문양과 표면 조직을 가지는 "낙수지(빗방울이 떨어진 듯한 제지 조직 문양) 아이템"의 경우 지금까지의 기존 기술로는 만족시킬만한 대안이 없었다. For example, the "dripping paper (paper tissue pattern that looks like raindrops)" items with special patterns and surface texture of the paper are not satisfactory with the existing technology.
한지 특성은 양지와 같이 비교적 평활도가 균일하지 않고 밀도가 고르지 못해 제지과정 특성상 자연적인 기공과 제지 조직이 매우 거칠게 형성되어 있다. 그러므로 한지에 발수기능을 부여하는 기술은 그 어느 종이보다 까다롭고 난해한 조건이 전제하고 있다.The characteristics of Hanji are relatively uneven and uneven in density, so natural pores and paper tissues are very rough due to the nature of the papermaking process. Therefore, the technology for imparting water repellency to Korean paper is presumed to be more difficult and difficult than any other paper.
그 예로써 양지에 비해 제지 조직이 지극히 불균일하며 2차 발수기능성 가공 조건이 어렵고 한지 본래의 기능(질감과 색상, 숨쉬는 기공 등)을 훼손하지 말아야 한다는 대전제가 있는 것이다.For example, there is a charging agent that the paper tissue is extremely non-uniform compared to the sun, the secondary water-repellent processing conditions are difficult, and the original function (texture, color, breathing pores, etc.) should not be damaged.
즉, 한지에 발수기능을 부여하는 것은 보통 시중의 예처럼 필름식 평면 단순 라미네이팅 방식 적용은 아니되며 한지의 원료가 되는 닥나무 섬유질의 각각 미세한 한 올마다의 360도 전 방향을 조성물 고형분이 에워싸는 방식으로 발수제 물질 입자가 결착되어야만 거칠고 밀도가 불규칙한 제지 조직에 관계없이 완전한 발수기능을 가지게 할 수 있는 난해한 조건인 것이다.That is, to impart a water repellent function to the hanji is not applied to the film-type flat simple laminating method as in the commercial example, but in a way that the composition solids around 360 degrees every minute of each of the mulberry fibers that is the raw material of the hanji When water-repellent material particles are bound, it is a difficult condition to have full water repellency regardless of coarse and irregular papermaking tissue.
본 발명은 상기한 바와 같은 문제점을 완벽하게 해결하기 위하여 안출된 것으로서, 한국에서의 오랜 역사동안 전통으로 이어져 내려오는 한지에 발수 및 기타기능을 부여하는 것으로 더욱 상세하게는 수제 한지 또는 기계 한지(닥 나무와 펄프를 합성하여 제조하는 연속 롤 생산)에 발수기능을 나타나게 하는 기술이다. The present invention has been made in order to solve the above problems completely, and in more detail, to give a water-repellent and other functions to the traditional Korean paper that has been passed down to tradition for a long history in Korea, more specifically handmade Korean paper or machine It is a technology to show the water repellent function in the production of continuous rolls produced by synthesizing wood and pulp.
본 발명은 한지의 기존 장점은 그대로 살리면서 단점을 완벽히 보완하여 결국 상품성이 뛰어난 제품으로서 한지의 재탄생을 노리는 획기적인 기술을 제공하는 것을 그 목적으로 한다. The present invention aims to provide a breakthrough technology aiming at rebirth of Hanji as a product having excellent merchandise, while completely complementing the disadvantages while keeping the existing advantages of Hanji.
또한, 수천 년을 맥을 이어 온 천연 한지 고유의 우수한 장점은 온전히 보장하면서 단점에 대해서는 현대과학을 접목하여 한지 발명 후 현재까지 해결하지 못한 숙원의 난제를 개선한 새로운 개념의 닥나무 한지를 제조할 수 있게 하는 것이 본 발명의 목적인 것이다. In addition, it is possible to manufacture a new concept of Korean paper mulberry, which improves the difficulties of ambition that has not been solved until the invention of Hanji by incorporating modern science on the shortcomings while fully guaranteeing the unique advantages of natural Hanji, which have inherited Mac for thousands of years. It is an object of the present invention.
또한, 본 발명은 한지의 특성에 적합한 무공질 발수제가 아닌 "미 다공질의 특성을 가지며 불규칙하고 매우 거친 한지 조직에 입체적이고 효과적인 발수기능"을 제공하는 것을 그 목적으로 한다. It is also an object of the present invention to provide a "three-dimensional and effective water repellent function to irregular, very coarse Hanji tissue" rather than a non-porous water repellent suitable for the characteristics of Hanji.
본 발명에 따른 발수기능 조성물은 친환경 불소계 발수제 5~15 중량%와 에탄올 30~40 중량%를 물 45~65 중량%에 혼합하여 이루어지거나, 불소계 발수제 5~15 중량%, 나노실버 0.02~0.05 중량% 및 잔부는 물로 이루어지거나, 불소계 발수제 5~15 중량%, 4급 암모늄계(Quaternary ammonium compound, QAC) 살균제 0.2~0.5 중량% 및 잔부는 물로 이루어지는 것을 특징으로 한다. The water-repellent composition according to the present invention is made by mixing 5 to 15% by weight of environmentally friendly fluorine-based water repellent and 30 to 40% by weight of ethanol in 45 to 65% by weight of water, or 5 to 15% by weight of fluorine-based water repellent, 0.02 to 0.05 weight of nanosilver. % And the balance is made of water, or 5 to 15% by weight of a fluorine-based water repellent, quaternary ammonium compound (QAC) disinfectant 0.2 to 0.5% by weight and the balance is characterized in that made of water.
한편, 본 발명에 따른 발수기능 한지는 상기 발수기능 조성물이 상기 한지의 어느 일면 또는 양면에 코팅처리되어 형성되는 것을 특징으로 한다. On the other hand, the water-repellent hanji according to the invention is characterized in that the water-repellent composition is formed by coating on one or both sides of the hanji.
한편, 본 발명에 따른 발수기능 한지 제조방법은 한지의 제조방법에 있어서, 한지의 원료가 되는 닥나무를 이용하여 제조한 닥섬유를 탈수한 다음 상기 닥섬유를 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물에 침지한 후 80~180 ℃의 건조대에 부착하여 20~60초 동안 건조하여 제조되는 것을 특징으로 한다. On the other hand, the water-repellent function of the Korean paper manufacturing method according to the present invention, in the manufacturing method of the Korean paper, the water repellent of any one of claims 1 to 3 after dehydrating the mulberry fiber prepared using the mulberry that is the raw material of the hanji After immersing in the functional composition is attached to a drying stand of 80 ~ 180 ℃ characterized in that it is prepared by drying for 20 to 60 seconds.
한편, 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 원료가 되는 닥나무를 이용하여 제조한 닥섬유를 탈수한 다음 상기 닥섬유를 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물에 침지하거나 상기 닥섬유에 상기 발수기능 조성물을 분사한 후 100~500 ㎏의 압력 롤에서 짠 다음 80~180 ℃의 열풍 건조로에서 20~60초 동안 열풍 건조하여 제조되는 것을 특징으로 한다. On the other hand, the manufacturing method of the water-repellent function Hanji according to the present invention, in the manufacturing method of the hanji, dehydration of the medicinal fiber made from the mulberry that becomes the raw material of the hanji and then the medicinal fiber of any one of claims 1 to 3 After immersing in the water-repellent composition or spraying the water-repellent composition on the mulberry fiber is squeezed in a pressure roll of 100 ~ 500 kg and then hot air drying for 20 to 60 seconds in a hot air drying furnace of 80 ~ 180 ℃.
한편, 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 표면에 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물을 코팅하는 코팅단계와; 상기 발수기능 조성물이 코팅된 한지를 80~180 ℃의 열풍 건조로에서 20~60초 동안 열풍 건조하는 건조단계로 이루어지는 것을 특징으로 한다. On the other hand, the manufacturing method of the water-repellent hanji according to the present invention, the manufacturing method of the hanji, the coating step of coating the water-repellent composition of any one of claims 1 to 3 on the surface of the hanji; Hanji coated with the water-repellent composition is characterized in that it consists of a drying step of hot air drying for 20 to 60 seconds in a hot air drying oven of 80 ~ 180 ℃.
한편, 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 표면에 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물을 코팅하는 코팅단계와; 상기 발수기능 조성물이 코팅된 한지를 80~180 ℃의 건조 롤에서 20~60초 동안 건조하는 건조단계로 이루어지는 것을 특징으로 한다. On the other hand, the manufacturing method of the water-repellent hanji according to the present invention, the manufacturing method of the hanji, the coating step of coating the water-repellent composition of any one of claims 1 to 3 on the surface of the hanji; Hanji coated with the water-repellent composition is characterized in that it consists of a drying step of drying for 20 to 60 seconds in a drying roll of 80 ~ 180 ℃.
또한, 상기 코팅단계는 상기 한지를 상기 발수기능 조성물에 침지하거나 상기 한지에 상기 발수기능 조성물을 분사하거나 또는 롤 코팅방법으로 이루어지는 것을 특징으로 한다. In addition, the coating step is characterized in that the hanji immersed in the water-repellent composition or spraying the water-repellent composition on the hanji or roll coating method.
또한, 상기 롤 코팅방법은 상하로 배치되어 서로 반대방향으로 맞물려 회전하는 압동 롤과 메쉬 롤로 구성되며, 상기 메쉬 롤은 외주연에 다수의 미세홈이 형성된 메쉬가 음각 형성되고 상기 발수기능 조성물이 수용되는 발수기능 조성물통에 침지되어 회전하면서 상기 발수기능 조성물을 상기 압동 롤과 상기 메쉬 롤 사이를 통과하는 상기 한지의 표면에 코팅하는 것을 특징으로 한다. In addition, the roll coating method is composed of a pressure roll and a mesh roll which is arranged up and down to rotate in engagement with each other in the opposite direction, the mesh roll is engraved mesh formed with a plurality of fine grooves on the outer periphery and the water repellent composition is accommodated It is characterized in that the water-repellent composition is coated on the surface of the hanji passing through between the pressure roll and the mesh roll while being immersed in the water-repellent composition to be rotated.
본 발명에 따른 발수기능 조성물 및 발수기능 한지와 그 제조방법에 의하면, 상기 발수기능 조성물은 친환경 불소계 발수제에 천연 살균제인 에탄올 또는 나노실버 또는 4급 암모늄계 살균제를 물과 혼합하여 이루어지고 상기 발수기능 조성물을 침지, 분사, 롤 코팅 등의 방법으로 한지의 표면에 코팅처리함으로써 숨 쉬는 종이로 잘 알려진 한지 본래의 특성인 우수한 통풍기능을 유지하면서 탁월한 발수기능 및 살균기능을 발휘할 수 있게 하는 효과를 제공한다. According to the water-repellent composition and water-repellent hanji according to the present invention and a method for producing the water-repellent composition, the water-repellent composition is made by mixing ethanol or nanosilver or quaternary ammonium-based fungicide which is a natural fungicide in an environmentally friendly fluorine-based water repellent and water By coating the composition on the surface of Hanji by dipping, spraying, roll coating, etc., it provides the effect of exerting excellent water repellency and sterilization function while maintaining excellent ventilation function which is the original characteristic of Korean paper known as breathing paper. do.
빗방울의 직경은 안개비의 경우 100㎛, 소낙비가 3,000㎛인 반면에 수증기의 분자 직경은 0.0004㎛에 지나지 않으므로 도1a에서 도시한 바와 같은 구형 모양을 한 입자로 구성되는 본 발명에 의한 발수기능 조성물을 한지의 표면에 코팅처리함으로써 0.1~10.0㎛ 정도의 미세공을 갖도록 "독특한 그물 모양의 체인"의 발수처리층을 형성시키게 되며 물 분자는 막고(발수) 기체는 통과(통풍)시키는 발수기능 및 통풍기능을 부여하게 되는 것이다. 즉, 0.0004㎛(0.4나노) 분자 직경을 가지는 수증기는 발수처리층을 통과하게 되어 결국 숨 쉬는 한지의 고유 기능인 통풍기능을 훼손시키지 않고 효과적으로 보장, 발휘할 수 있게 하는 것이다. The raindrop diameter is 100 μm for the fog ratio and 3,000 μm for the rain shower, whereas the molecular diameter of the water vapor is only 0.0004 μm, so that the water-repellent composition according to the present invention is composed of spherical particles as shown in FIG. By coating the surface of Hanji to form a water repellent layer of "unique mesh-shaped chain" to have micropores of about 0.1 ~ 10.0㎛, and water repellent function to block water molecules (water repellent) and gas to pass (vent) It will give a ventilation function. That is, water vapor having a 0.0004 μm (0.4 nanometer) molecular diameter passes through the water repellent treatment layer, thereby effectively guaranteeing and exerting without damaging the ventilation function, which is a unique function of the Hanji breathing.
또한, 한지는 우수한 통풍기능으로 인하여 유리가 창호용으로 이용되기 전 수 천년의 역사 동안 창호지로 애용되어왔는데 이를 오늘날 현대식 건물의 이중 창문 중 내측 유리창문을 대신해 본 발명에 따른 발수기능 한지를 창호지용으로 채용한다면 극서기 에어컨디셔너를 가동하거나 동절기 보온 통풍 유지에 매우 효과적으로 대체할 수 있다. 그 이유는 발수, 방오 기능(살균기능 포함) 발휘로 재래 한지와 같이 쉽게 오염되거나 훼손되지 않아 위생적(공기 출,입 과정에서 한지의 항균 및 살균기능으로 걸러짐)이며 미려한 외관을 유지하는 것이 가능해 훌륭한 자연적인 공기 정화 및 필터 기능을 제공할 수 있게 된다. In addition, Hanji has been used as a window paper for thousands of years before glass is used for windows because of its excellent ventilation function. Today, the water-repellent Hanji paper according to the present invention replaces the inner glass window among the double windows of modern buildings. If employed, it can be a very effective alternative to running ultra-weather air conditioners or maintaining warm winter ventilation. The reason is that water repellency and antifouling function (including sterilization function) are not easily contaminated or damaged like traditional Korean paper, so it is hygienic (filtered by the antibacterial and sterilization function of Hanji during air release and entry) and it is possible to maintain a beautiful appearance. It will provide excellent natural air purification and filter functions.
나아가, 한지 본래의 우수한 통풍성에 더하여 탁월할 발수기능 및 살균기능을 갖는 상기 발수기능 조성물을 시멘트나 곡류 등의 포장재로 사용하는 크라프트 지대나 과수원예의 농업용 과수봉투에 코팅처리하여 적용할 수 있게 된다. In addition, the water-repellent composition having excellent water repellency and sterilization function in addition to the original breathability of Hanji can be applied to the agricultural fruit orchard bag of the kraft zone or orchard horticulture used as a packaging material such as cement or grains.
즉, 열기(熱氣)가 있는 상태에서 포장되는 시멘트나 곡류의 크라프트 지대의 경우 자연스런 열기 배출을 이룰 수 있고 유통, 저장 등에도 매우 안전한 발수, 통풍기능을 제공할 수 있으며, 과일이 성숙되는 과정에서 병충해 및 농약 살포시 농약이 과육에 오염되는 것을 차단하는 목적으로 농가에서 채택되는 과수봉투의 경우 상기 통풍기능에 의하여 과일이 성장하는 동안 왕성한 호흡을 할 수 있도록 숨 쉬는 기공을 보장할 수 있고 반대로 상기 발수기능에 의하여 농약살포, 우천 병충해의 자연노출 조건에서는 과실을 보호해줄 수 있는 효과를 제공하게 되어 과수가 절대적 필요조건인 호흡을 위한 안전한 기공 구조를 제공하는 반면에 특유의 발수기 능으로 과수를 보호함과 동시에 살균기능을 발휘하여 보다 위생적이고 쾌적한 과수의 성숙을 돕는 이상적인 기술을 제공한다. In other words, in the case of cement or cereal krafts that are packaged in the presence of heat, natural hot air discharge can be achieved, and it can provide very safe water-repellent and ventilation function for distribution and storage. In the case of fruit orchard bags adopted by farmers for the purpose of preventing pesticides from being contaminated with pulp during the spraying of pests and pesticides, the ventilation function can guarantee the breathing pores for vigorous breathing while the fruit is growing. By the function, it provides the effect to protect the fruit in the natural exposure conditions of pesticide spraying and rainy pests, while the fruit water provides a safe pore structure for breathing, which is an absolute requirement, while the water repelling function protects the fruit. At the same time, it helps sterilize more hygienic and pleasant fruit by showing sterilization function. It provides the technology.
또한, 통상의 한지에 서예 행위(붓글씨 또는 그림)을 한 후에 본 발명에 의한 발수기능 조성물에 침지하거나 상기 발수기능 조성물을 분사함으로써 발수기능 및 살균기능을 통하여 붓글씨나 그림의 수명을 오래 유지할 수 있는 효과를 제공할 수 있다. In addition, after performing a calligraphic act (calligraphic or painting) in a conventional Hanji or immersed in the water-repellent composition according to the present invention or by spraying the water-repellent composition, the life of the calligraphic or painting can be maintained for a long time through the water-repellent function and sterilization function Can provide an effect.
이하, 본 발명에 따른 발수기능 조성물 및 발수기능 한지와 그 제조방법을 첨부한 도면을 참조하여 상세히 설명하면 다음과 같다. Hereinafter, with reference to the accompanying drawings, a water-repellent composition and a water-repellent hanji according to the present invention and a manufacturing method thereof are as follows.
도1a는 본 발명에 따른 발수기능 조성물의 나노 구형 모형이고 도1b는 본 발명에 따른 발수기능 조성물의 나노 캡슐 모형도이며, 도2는 종래 수제 한지의 제조방법의 공정도이고 도3은 본 발명에 따른 발수기능 한지의 제조방법에서의 롤 코팅 장치도이며, 도4는 본 발명에 따른 발수기능 한지의 발수기능 실험결과 사진이고 도5a는 본 발명에 따른 발수기능 한지의 색상변화 결과 사진이며, 도6a는 본 발명에 따른 발수기능 한지의 색상변화 결과 사진이고 도6b는 도6a의 확대 사진이며, 도7은 본 발명에 따른 다른 실시예의 발수기능 실험결과 사진이다. Figure 1a is a nano-spherical model of the water-repellent composition according to the present invention and Figure 1b is a nanocapsule model of the water-repellent composition according to the present invention, Figure 2 is a process diagram of a manufacturing method of conventional handmade hanji and Figure 3 according to the present invention Figure 4 is a roll coating device in a method of manufacturing a water-repellent hanji, Figure 4 is a photograph of the water repellent function test results of the water-repellent hanji according to the invention and Figure 5a is a color change result photo of the water-repellent hanji according to the present invention, Figure 6a Is a color change result photograph of the water repellent function Hanji according to the present invention, Figure 6b is an enlarged picture of Figure 6a, Figure 7 is a photograph of the water repellent function test results of another embodiment according to the present invention.
1. 발수기능 조성물1. Water repellent composition
본 발명에 따른 발수기능 조성물은 불소계 발수제 5~15 중량%와 에탄올 30~40 중량%를 물 45~65 중량%에 혼합하여 이루어지거나, 불소계 발수제 5~15 중량%, 나노실버 0.02~0.05 중량% 및 잔부는 물로 이루어지거나, 불소계 발수제 5~15 중량%, 4급 암모늄계(Quaternary ammonium compound, QAC) 살균제 0.2~0.5 중량% 및 잔부는 물로 이루어지는 것을 특징으로 한다. The water repellent composition according to the present invention is made by mixing 5 to 15% by weight of fluorine-based water repellent and 30 to 40% by weight of ethanol to 45 to 65% by weight of water, or 5 to 15% by weight of fluorine-based water repellent, and 0.02 to 0.05% by weight of nanosilver. And the balance is made of water, or 5 to 15% by weight of a fluorine-based water repellent, quaternary ammonium compound (QAC) disinfectant 0.2 to 0.5% by weight and the balance is characterized in that made of water.
이에 의하면, 본 발명에 따른 발수기능 조성물은 한지에 발수, 방오, 항균, 그리고 항곰팡이 능력을 부여하는 조성물로서 친환경 불소계 발수제 5~15 중량%와 에탄올 30~40 중량% 또는, 나노실버 0.02~0.05 중량%(200~500ppm) 또는, 4급 암모늄계 살균제 0.2~0.5 중량%를 증류수와 배합하여 48시간 충분히 교반하여 이루어진다. According to the present invention, the water-repellent composition according to the present invention is a composition for imparting water repellency, antifouling, antibacterial, and antifungal ability to Korean paper, 5 to 15 wt% of environmentally friendly fluorine-based water repellent and 30 to 40 wt% of ethanol, or 0.02 to 0.05 nano silver. A mixture of distilled water and 0.2% to 0.5% by weight of the wt% (200 ~ 500ppm) or quaternary ammonium sterilizer is sufficiently stirred for 48 hours.
이에 의하면, 상기 발수기능 조성물은 한지에 우수한 발수기능을 발휘하게 함은 물론이고 부가적으로 방오, 항균, 항곰팡이 기능 및 한지 표면의 제지 조직이 퍼짐을 방지하는 효과를 얻을 수 있게 되는 것이다. According to this, the water-repellent composition is capable of exerting excellent water repellent function on the paper, as well as additionally preventing the spread of antifouling, antibacterial, anti-fungal function and paper tissue on the surface of the paper.
또한, 상기 불소계 발수제는 환경호르몬인 APEO(Alkyl phenol ethoxylates)가 첨가되지 않은 환경 기준에 적합한 친환경 발수제를 사용하는 것이고 이에 친환 경 살균제인 상기 에탄올이나 나노실버 또는 4급 암모늄계 살균제와 혼합하여 사용함으로써 본 발명에 따른 발수기능 조성물은 친환경 원료로 이루어지므로 인체에 무해하고 2차적 환경오염이나 한지의 재활용에 전혀 문제가 없는 자원 리싸이클 개념에 적합한 친환경적 기술을 제공하게 되는 것이다. In addition, the fluorine-based water repellent is to use an eco-friendly water repellent suitable for environmental standards that do not add the environmental hormone APEO (Alkyl phenol ethoxylates) is used by mixing with the ethanol, nano silver or quaternary ammonium-based fungicide which is an environmental sterilizer Since the water-repellent composition according to the present invention is made of an eco-friendly raw material, it is to provide an eco-friendly technology suitable for the concept of resource recycling that is harmless to the human body and does not have any problem in secondary environmental pollution or recycling of Hanji.
또한, 상기 불소계 발수제는 천연 무기소재인 SiO2에 불소를 첨가한 발수제로서 친환경 살균제로 상기 에탄올을 사용할 경우에 상기 에탄올은 휘발성이 강하여 지속성의 문제가 있으므로 도1b에서 도시한 바와 같이 마이크로 또는 나노 크기의 미세공(11)이 형성되는 다공질성이고 천연소재인 나노 SiO2(12)에 상기 에탄올(11)을 포집, 숙성시켜 제어함으로써 상기 에탄올이 서서히 휘발되어 방출되는 서방(徐放) 타입 형태로 가공하여 살균력의 지속성을 유지할 수 있어 천연 살균제인 상기 알코올의 살균력을 극대화시킨 것이다. In addition, the fluorine-based water repellent is a water-repellent agent added fluorine to SiO 2 which is a natural inorganic material, when the ethanol is used as an environmentally friendly disinfectant, since the ethanol is highly volatile, there is a problem of sustainability, as shown in FIG. The
또한, 상기 에탄올(ethanol) 또는 에틸 알코올(ethyl alcohol)은 무색의 가연성 화합물로 알코올의 한 종류이며 단백질을 응고시키므로 강력한 소독 및 살균 작용이 있는 친환경 살균제이다.In addition, the ethanol (ethanol) or ethyl alcohol (ethyl alcohol) is a colorless combustible compound is one kind of alcohol and coagulates protein, so it is an environmentally friendly disinfectant with strong disinfection and sterilization action.
또한, 상기 나노실버는 순은(실버, Silver)을 전기분해를 이용하여 나노(Nano) 크기(nm, 10-9m) 수준의 초미립자로 만든 것으로서 나노화된 은(나노실버) 는 강력한 항균 및 살균 작용이 있는 친화경 항균제 및 살균제이다. 이는 650여종의 세균과 바이러스를 멸균할 수 있고 진균류(Fungi)에도 아주 탁월한 효과를 발휘하는 것으로 알려져 있다.In addition, the nano silver is made of pure silver (silver, Silver) to ultra-fine particles of the nano (Nano) size (nm, 10 -9 m) level using electrolysis, nano silver is a powerful antibacterial and bactericidal action It is an affinity antibacterial and fungicide. It is able to sterilize over 650 bacteria and viruses and is known to be very effective against fungi.
또한, 상기 4급 암모늄계(Quaternary ammonium compound, QAC) 살균제는 통상 Quat 또는 Qac's로 불리우는 양이온 계면활성제형 살균소독제이다. 즉, 분자내에 친수기와 소수기를 함께 가지고 있는 양이온 계면활성제를 물에 용해한 제품으로서 대상물질에 잘 침투하며 미생물의 세포막에 작용하여 세포내 물질을 유출시키고, 대사효소를 저해하며 미생물을 사멸시키며 독성이 적고, 색, 부식성 및 냄새가 없는 친환경 살균제이다.In addition, the quaternary ammonium compound (QAC) fungicide is a cationic surfactant type disinfectant which is commonly called Quat or Qac's. In other words, it is a product dissolving cationic surfactant which has hydrophilic group and hydrophobic group in water in water and penetrates into target material and acts on cell membrane of microorganism to leak intracellular substance, inhibit metabolic enzyme, kill microbe and It is a small, colorless, corrosive and odorless eco-friendly disinfectant.
2. 발수기능 한지2. Water repellent
한편, 본 발명에 따른 발수기능 한지는 상기 발수기능 조성물이 상기 한지의 어느 일면 또는 양면에 코팅처리되어 형성되는 것을 특징으로 한다. On the other hand, the water-repellent hanji according to the invention is characterized in that the water-repellent composition is formed by coating on one or both sides of the hanji.
이에 의하면, 친환경 발수제인 상기 불소계 발수제에 천연 살균제인 에탄올(서방 타입의 나노캡슐) 또는 나노실버 또는 4급 암모늄계 살균제를 물과 함께 혼합하여 이루어지는 본 발명에 따른 상기 발수기능 조성물을 한지에 코팅 처리함으로써 발수 및 방오, 항균, 항곰팡이 기능을 가지는 한지를 구성하게 되는 것이다.According to the present invention, the water-repellent composition according to the present invention is formed by mixing fluorine-based water-repellent agent, which is an eco-friendly water repellent, with a natural disinfectant, ethanol (sustained-type nanocapsules) or nanosilver or quaternary ammonium-based disinfectant, together with water. By doing so, it is to make the hanji having water repellent and antifouling, antibacterial, anti-fungal function.
한지는 pH 7.0 이상으로 시간이 흐를수록 결이 고와지고 수명이 1,000년 이상 가는 것으로 알려져 있다. 반면에 양지는 pH 4.0 이하의 산성지로서 수명이 대개 50년에서 100년 정도가 되면 누렇게 변하는 황변색 현상을 일으키며 삭아버리는 상당한 차이가 있다.It is known that Hanji has a higher pH and a lifespan of more than 1,000 years. On the other hand, it is an acidic paper with a pH of less than 4.0, and there is a significant difference in the yellowing color which is yellowed when the life is about 50 to 100 years.
본 발명에 사용되는 발수기능 조성물은 pH 4.5±0.5의 약산성으로 코팅시 물을 베이스로 처방한다. 따라서, 정상조건의 건조시 한지의 pH 부문에 영향을 주지 않아 한지 본래의 품질을 보호할 수 있다.The water-repellent composition used in the present invention has a weak acidity of pH 4.5 ± 0.5 to prescribe water as a base when coating. Therefore, it is possible to protect the original quality of the hanji by not affecting the pH section of the hanji when drying under normal conditions.
3. 발수기능 한지의 제조방법3. Manufacturing method of water repellent Hanji
한지는 보통 수제 한지 및 기계 한지로 대략적으로 구분되고 한지 제조방법 또한 각기 달라서 본 발명에 따른 발수기능 조성물을 한지에 코팅하여 발수기능 한지를 제조하는 방법 한지 제조방법에 따라 달라지게 된다. Hanji is usually roughly divided into handmade Hanji and machine Hanji, and the method of manufacturing Hanji is also different, so that the method of manufacturing a water-repellent hanji by coating the water-repellent composition according to the present invention will vary depending on the method of manufacturing Hanji.
(1) 수제 한지의 제조방법에서의 발수기능 한지의 제조방법(1) Manufacturing method of water repellent function of handmade Korean paper
본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 원료가 되는 닥나무를 이용하여 제조한 닥섬유를 탈수한 다음 상기 닥섬유를 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물에 침지한 후 80~180 ℃의 건조대에 부착하여 20~60초 동안 건조하여 제조되는 것을 특징으로 한다. Water repellent function according to the present invention is a method of manufacturing Hanji, the water repellent function of any one of claims 1 to 3 after dehydrating the medicinal fiber made from the mulberry that is the raw material of the hanji After immersing in the composition, it is attached to a drying stand of 80 ~ 180 ℃ characterized in that it is prepared by drying for 20 to 60 seconds.
수제 한지의 제조방법은 지방이나 장인에 따라 약간의 차이가 있으나 이를 대략적으로 나타내면 도2와 같다. 도2에서 도시한 바와 같은 공정은 전통적 수가공에 의하여 이루어지고 있으며, 모든 공정은 오관의 판단에 의존하여 진행된다. 상기 수가공 전통공법에서는 도2의 ⑧항의 "탈수하기(물 짜기)" 공정과 ⑨항의 "건조작업" 공정 중에서 상기 본 발명에 따른 발수기능 조성물을 코팅처리하는 것이 가장 적합하다.The method of manufacturing handmade Hanji is slightly different depending on fat or craftsman, but the approximation is as shown in FIG. The process as shown in Fig. 2 is performed by traditional handiwork, and all the processes are performed depending on the judgment of the five senses. In the traditional hand-made method, it is most suitable to coat the water-repellent composition according to the present invention among the "dehydrating (water squeeze)" process of Figure 8 and the "drying operation" process of ⑨ of Figure 2.
더욱 상세하게는 도2의 ⑧항의 "탈수하기" 탈수공정(물 짜기)" 후 상기 본 발명에 따른 발수기능 조성물에 침지하여 기존 공정 정도의 "물 짜기"가 진행되었을 때 ⑨항의 "건조작업"에서 침지한 닥섬유를 건조대 철판에 붙여 건조하는 것으로 코팅공정이 이루어지고 최종적으로 본 발명에 따른 발수기능 한지가 제조되게 된다. 단, ⑨항의 "건조작업"에서 상기 건조대 철판 온도가 80~180℃에서 20초에서 60초 이내가 적당하나 제조하는 한지의 두께에 따라 그 값을 달리할 수 있다. 이로써 수제 한지 제조 공정에서 상기 본 발명에 따른 발수기능 조성물을 코팅하는 방법이 큰 공정 변화와 조건 없이 적용 가능한 것은 일반 유기용제를 사용하는 것과는 달리 상기 본 발명에 따른 발수기능 조성물이 수용성으로 이루어진 것이기 때문이다.More specifically, after "dewatering" dewatering process (water squeeze) of the ⑧ section of Fig. 2 immersed in the water-repellent composition according to the present invention, when the "water squeeze" of the existing process degree was carried out "drying operation" of ⑨ The coating process is made by attaching the medicinal fiber immersed in the drying iron plate to dry, and finally the water-repellent hanji according to the present invention is produced, except that the drying iron plate temperature is 80 ~ 180 ℃ in "drying operation" 20 seconds to 60 seconds may be appropriate, but the value may vary depending on the thickness of the Korean paper manufactured.The method for coating the water-repellent composition according to the present invention in a handmade paper manufacturing process is applied without significant process changes and conditions. This is possible because the water-repellent composition according to the present invention is water-soluble, unlike using a general organic solvent.
(2) 기계 한지의 제조방법에서의 발수기능 한지의 제조방법(2) Manufacturing method of water repellent function Korean paper in the manufacturing method of the machine Korean paper
기계 한지는 상기 도2에서 도시한 제조공정이 전통적 수가공에 의하여 이루어지는 수제 한지 공정과는 달리 연속 롤 생산체제로 기계작업에 적합한 준비된 한지 재료를 투입, 일괄 생산하는 방식이다. 상기 도2의 ⑦항의 "닥 섬유 만들기-물질하기"에서 ⑧항의 "탈수하기-물짜기", ⑨항의 "건조하기"와 롤(Roll) 권취(감기) 공정이 일괄 라인에서 처리된다.Unlike the handmade hanji process, in which the manufacturing process shown in FIG. 2 is a traditional hand-made process, the hanji is a method of adding a batch of prepared hanji material suitable for mechanical work in a continuous roll production system. The process of "dehydration-watering" of section ⑧, "drying" of section ⑨, and roll winding (winding) process of section ⑧ of "dock fiber making-material" of ⑦ of FIG. 2 are processed in a batch line.
1) 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 원료가 되는 닥나무를 이용하여 제조한 닥섬유를 탈수한 다음 상기 닥섬유를 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물에 침지하거나 상기 닥섬유에 상기 발수기능 조성물을 분사한 후 100~500 ㎏의 압력 롤에서 짠 다음 80~180 ℃의 열풍 건조로에서 20~60초 동안 열풍 건조하여 제조되는 것을 특징으로 한다. 1) The method for producing water-repellent hanji according to the present invention, in the method of manufacturing Hanji, dehydration of the mulberry fiber prepared using the mulberry that becomes the raw material of the hanji and then the mulberry fiber according to any one of claims 1 to 3 After immersing in the water-repellent composition or spraying the water-repellent composition on the mulberry fiber is squeezed in a pressure roll of 100 ~ 500 kg and then hot air drying for 20 to 60 seconds in a hot air drying furnace of 80 ~ 180 ℃.
상기 기계 한지 제조공정 중 도2의 ⑦항의 "닥 섬유 만들기-물질하기" 공정에서 상기 본 발명에 따른 발수기능 조성물을 일정비율 희석시켜 적용하는 방법은 현실적으로 무리이다. 그 예로서 ⑧항의 "탈수하기-물짜기" 공정에서 ⑨항의 "건조하기" 공정은 컨베어 연속이동 방법으로 이루어지는 과정에서 소실되는 물이 많기 때문에 상기 본 발명에 따른 발수기능 조성물의 낭비 요소가 많다.The method of diluting and applying a predetermined ratio of the water repellent composition according to the present invention in the process of making the “dough fiber-material” of ⑦ of FIG. As an example, the "drying" process of the item ⑨ in the "dehydrating-watering" process of item ⑧ has a lot of waste elements of the water-repellent composition according to the present invention because a lot of water is lost in the process consisting of the conveyor continuous movement method.
그러므로 가장 적합한 방법은 상기 수제 한지의 제조방법에서의 발수기능 한지의 제조방법과 동일한 것으로 도2의 ⑧항의 "탈수하기-물짜기" 공정과 ⑨항의 "건조하기" 공정의 중간 공정 영역에서 기계를 개조하거나 새로운 발수기능 코팅 유니트(Unit)를 설치하는 것이 적합하며, 이 유니트 조건은 한지를 상기 본 발명에 따른 발수기능 조성물에 침지하거나 한지에 상기 본 발명에 따른 발수기능 조성물을 분사(Spray)하는 방식으로 하고 이어 100~500㎏ 정도의 압력 롤(Roll))에서 짠 다음 건조 온도는 섭씨 80~180℃에서 열풍 건조로 통과를 20~60초간 실시하면 상기 본 발명에 따른 발수기능 조성물을 한지와 원만하게 결착시킬 수 있다.Therefore, the most suitable method is the same as the manufacturing method of the water-repellent function Hanji in the manufacturing method of the handmade Hanji, the machine in the intermediate process region of the "dehydration-watering" process of Figure 2 ⑧ and "drying" process of ⑨ It is suitable to retrofit or install a new water repellent coating unit, and the condition of the unit is to immerse the hanji in the water repellent composition according to the present invention or to spray the water repellent composition according to the present invention to the hanji. And then After squeezing in a pressure roll (about 100-500 kg), the drying temperature is 20 to 60 seconds after passing through a hot-air drying furnace at 80 to 180 degrees Celsius to bind the water-repellent composition according to the present invention with Hanji. Can be.
2) 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 표면에 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물을 코팅하는 코팅단계와; 상기 발수기능 조성물이 코팅된 한지를 80~180 ℃의 열풍 건조로에서 20~60초 동안 열풍 건조하는 건조단계로 이루어지는 것을 특징으로 한다. 2) The method for producing a water-repellent hanji according to the present invention comprises the steps of coating the water-repellent composition of any one of claims 1 to 3 on the surface of the hanji; Hanji coated with the water-repellent composition is characterized in that it consists of a drying step of hot air drying for 20 to 60 seconds in a hot air drying oven of 80 ~ 180 ℃.
한편, 본 발명에 따른 발수기능 한지의 제조방법은 한지의 제조방법에 있어서, 한지의 표면에 제1항 내지 제3항 중 어느 한 항의 발수기능 조성물을 코팅하는 코팅단계와; 상기 발수기능 조성물이 코팅된 한지를 80~180 ℃의 건조 롤에서 20~60초 동안 건조하는 건조단계로 이루어지는 것을 특징으로 한다.On the other hand, the manufacturing method of the water-repellent hanji according to the present invention, the manufacturing method of the hanji, the coating step of coating the water-repellent composition of any one of claims 1 to 3 on the surface of the hanji; Hanji coated with the water-repellent composition is characterized in that it consists of a drying step of drying for 20 to 60 seconds in a drying roll of 80 ~ 180 ℃.
또한, 상기 코팅단계는 상기 한지를 상기 발수기능 조성물에 침지하거나 상기 한지에 상기 발수기능 조성물을 분사하거나 또는 롤 코팅방법으로 이루어지는 것을 특징으로 한다. In addition, the coating step is characterized in that the hanji immersed in the water-repellent composition or spraying the water-repellent composition on the hanji or roll coating method.
이에 의하면, 상기 방법은 기계에서 완성된 한지(기계 한지)를 독립된 코팅 전용기에 의하여 정상적인 코팅을 하는 방법이다. 즉, 한지에 본 발명에 따른 발수기능 조성물을 한지에 코팅하여 건조로를 통과시켜 80~180℃ 열풍 건조를 이용하거나 건조 롤(대형 다림질 롤)을 이용해 건조하여 코팅처리를 완성하는 방법이다. 상기 코팅단계에서 본 발명에 따른 발수기능 조성물을 한지에 코팅시키는 방법으로 더욱 상세하게는 상기 한지를 상기 발수기능 조성물에 침지하거나 상기 한지에 상기 발수기능 조성물을 분사하거나 또는 롤 코팅방법으로 이루어지게 된다. According to this, the method is a method for the normal coating of the hanji (machine Hanji) completed in the machine by an independent coating dedicated machine. In other words, by coating the water-repellent composition according to the present invention on Hanji through a drying furnace, using a 80 ~ 180 ℃ hot air drying or drying using a drying roll (large ironing roll) to complete the coating process. In the coating step, the method of coating the water repellent composition according to the present invention on hanji in more detail, the hanji is immersed in the water repellent composition or the water repellent composition is sprayed on the hanji or roll coating method .
첫째, 상기 한지를 상기 발수기능 조성물에 침지하거나 상기 한지에 상기 발수기능 조성물을 분사하는 방법은 한지를 상기 발수기능 조성물 탱크에 완전히 잠수시켜 지나가게 하거나 한지에 상기 발수기능 조성물을 분사(Spray)한 후 연이어 과도포된 상기 발수기능 조성물을 100~500㎏ 압력으로 충분히 짠 다음 80~180℃ 열풍 건조로를 20~60초간 통과시키는 방법이다. 다만, 이는 비교적 얇은 한지의 경우에는 이에 적합하지 않다. First, the method of immersing the hanji in the water-repellent composition or spraying the water-repellent composition to the hanji is to completely pass the hanji to the water-repellent composition tank or spray the water-repellent composition to the Hanji (Spray) 100 to 500 kg after the subsequent over-coating Squeeze it sufficiently under pressure and pass it through 80 ~ 180 ℃ hot air drying furnace for 20 ~ 60 seconds. However, this is not suitable for relatively thin hanji.
둘째, 상기 롤 코팅방법은 도3에서 도시한 바와 같이 상하로 배치되어 서로 반대방향으로 맞물려 회전하는 압동 롤(23)과 메쉬 롤(23')로 구성되며, 상기 메쉬 롤(23')은 외주연에 다수의 미세홈이 형성된 메쉬가 음각 형성되고 상기 발수기능 조성물이 수용되는 발수기능 조성물통(26)에 침지되어 회전하면서 피딩 롤(21)과 권취 롤(21')의 회전에 의하여 상기 압동 롤(23)과 상기 메쉬 롤(23') 사이를 통과하는 상기 한지의 표면에 상기 발수기능 조성물을 코팅하고 80~180℃ 열풍 건조로를 20~60초간 통과시켜 상기 권취 롤(21')로 권취하는 방법이다. 이에 의하면, 색상, 수축, 변형 등 2차 가공의 폐해 없이 이상적인 본 발명에 따른 발수기능 한지의 가공이 가능하다. Second, the roll coating method is composed of a
또한, 상기 건조단계는 도3에서 도시한 바와 같이 열풍 건조로를 이용할 수도 있고, 건조 롤(대형 다림질 롤)에서 비교적 설비가 간단하게 처리하는 방법도 가능하다. In addition, the drying step may use a hot air drying furnace as shown in Figure 3, it is also possible to simply process the equipment in a drying roll (large ironing roll).
<실시예><Examples>
불소계 발수제 10 중량%와 에탄올 35 중량%를 물 55 중량%에 혼합하여 제조한 본 발명에 따른 발수기능 조성물을 종래의 한지에 상기 분사하는 방법에 의하여 코팅하고 150~180℃ 열풍 건조로를 20~60초간 통과시켜 제조한 것을 사용하였다. 이 때 사용된 한지의 절반 부분에만 분사하여 상기 발수기능 조성물이 코팅처리되게 하고 나머지 절반 부분은 비처리되게 하여 양자를 비교할 수 있게 제조하였다. The water-repellent composition according to the present invention prepared by mixing 10% by weight of a fluorine-based water repellent and 35% by weight of ethanol in a conventional Korean paper by coating the water-repellent composition according to the present invention and 20 to 60 to 150-180 ° C. hot air drying furnace. What was produced by passing for seconds was used. At this time, only one half of the used paper was sprayed to allow the water repellent composition to be coated and the other half to be untreated to prepare both.
도4는 본 발명에 따른 발수기능 한지의 발수기능 실험결과 사진으로서 종래 한지와 본 발명에 따른 발수기능 한지에 각각 물방울을 뿌렸을 때 물방울의 흡수 여부를 비교한 사진이다. Figure 4 is a photograph of the water repellent function test results of the water-repellent function Hanji according to the present invention is a photograph comparing the absorption of water droplets when sprayed on the water repellent function in accordance with the present invention.
즉, 도4에 나타난 바와 같이 본 발명에 따른 발수기능 조성물이 비처리된 한지(종래 한지, 31')의 경우에는 물방울이 흡수되어 물 얼룩(32')이 나타나는 반면에, 본 발명에 따른 발수기능 조성물을 코팅처리한 한지(발수기능 한지, 31)의 경우에는 물방울이 흡수되지 않고 물방울(32) 상태로 유지되고 있어 본 발명의 따른 발수기능 한지의 경우 탁월한 발수기능을 발휘함을 확인할 수 있다. That is, as shown in Figure 4, in the case of the untreated water repellent composition according to the present invention (traditional Korean paper, 31 '), water droplets are absorbed to appear water stain (32'), while the water repellent according to the present invention In the case of Hanji (water repellent Hanji, 31) coated with the functional composition is not absorbed water droplets are maintained in the state of the
또한, 도5와 도6a는 본 발명에 따른 발수기능 한지의 색상변화 결과 사진으로서 상기와 동일한 방법으로 한지를 제조하였으며 다만 원료가 되는 한지를 색상이 있는 한지를 사용한 경우이다. In addition, Figure 5 and Figure 6a is a case of using the Korean paper as a result of the color change of the water-repellent function Hanji according to the present invention as described above, but using the hanji with the color.
도5와 도6a에 나타난 바와 같이 본 발명에 따른 발수기능 조성물을 상기 색상이 있는 한지에 처리한 경우에도 색상에 전혀 변화를 주지 않음을 확인할 수 있다. 이는 상기한 바와 같이 본 발명에 따른 발수기능 조성물이 유기용제를 사용하지 않고 물을 베이스로 하기 때문이다. 5 and 6a, even when the water-repellent composition according to the present invention is treated with the above color, it can be seen that the color does not change at all. This is because, as described above, the water-repellent composition according to the present invention is based on water without using an organic solvent.
한편, 도6a의 한지는 낙수지(빗방울이 떨어진 듯한 문양으로 꽃다발 포장지로 주로 사용)의 경우인데 상기 문양은 한지의 섬유 조직이 거의 비워져 있는 부분(33)에 의하여 나타난다. 도 6a에 나타난 바와 같이 상기 한지의 섬유 조직이 거의 비워져 있는 부분(33)에서도 물방울은 흡수되지 않고 물방울(32) 상태로 유지하고 있어 여전히 탁월한 발수기능을 발휘함을 확인할 수 있다. On the other hand, the hanji of Figure 6a is a case of a drop of paper (used mainly as a bouquet wrapping paper as a pattern that looks like rain drops), the pattern is represented by the
도7은 본 발명에 따른 다른 실시예의 발수기능 실험결과 사진으로서 한지에 황토를 섞어 제조한 황토벽지를 시험대상으로 하였다. 도7에 나타난 바와 같이 황토벽지의 경우에도 마찬가지로 본 발명에 따른 발수기능 조성물로 코팅처리된 황토벽지(41)와 비처리된 황토벽지(41')의 발수기능이 확연히 차이가 나 본 발명에 따른 발수기능 조성물로 코팅처리된 황토벽지(41)의 경우 탁월한 발수기능을 발휘함을 확인할 수 있다. Figure 7 is a water repellent test results of another embodiment according to the present invention as a photograph of the ocher wallpaper prepared by mixing the ocher to Hanji. As shown in FIG. 7, in the case of the ocher wallpaper, the water repellent function of the
한편, 이상에서 설명된 본 발명은 그에 관한 최선의 구성상태를 열거하였으나 이에 국한되는 것은 아니며 이하 첨부되는 청구범위의 범주를 벗어나지 않고 실시될 수 있다면 이전까지 서술된 구성예의 변경을 고려해 볼 수 있음은 물론이다.On the other hand, the present invention described above lists the best configuration of the present invention, but is not limited thereto, and if the present invention can be practiced without departing from the scope of the appended claims, it can be considered that the modification of the configuration described before Of course.
도1a는 본 발명에 따른 발수기능 조성물의 나노 구형 모형.Figure 1a is a nano-spherical model of the water repellent composition according to the present invention.
도1b는 본 발명에 따른 발수기능 조성물의 나노 캡슐 모형도.Figure 1b is a nanocapsule model of the water repellent composition according to the invention.
도2는 종래 수제 한지의 제조방법의 공정도.2 is a process chart of a conventional method for manufacturing handmade Korean paper.
도3은 본 발명에 따른 발수기능 한지의 제조방법에서의 롤 코팅 장치도.Figure 3 is a roll coating device in the manufacturing method of the water-repellent hanji according to the present invention.
도4는 본 발명에 따른 발수기능 한지의 발수기능 실험결과 사진.Figure 4 is a photograph of the water repellent function test results of the water repellent function Hanji according to the present invention.
도5a는 본 발명에 따른 발수기능 한지의 색상변화 결과 사진.Figure 5a is a photograph of the color change results of the water-repellent hanji according to the present invention.
도6a는 본 발명에 따른 발수기능 한지의 색상변화 결과 사진.Figure 6a is a photograph of the color change results of the water-repellent hanji in accordance with the present invention.
도6b는 도6a의 확대 사진. 6B is an enlarged photograph of FIG. 6A.
도7은 본 발명에 따른 다른 실시예의 발수기능 실험결과 사진. Figure 7 is a photograph of the water repellent function test results of another embodiment according to the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
11. 에탄올11.ethanol
12. 나노 SiO2 12. Nano SiO 2
13. 미세공13. Fine pores
21. 피딩 롤21. Feeding Roll
21'. 권취 롤21 '. Coiling roll
22. 한지22. Hanji
23. 압동 롤23. Rolling Roll
23'. 메쉬 롤23 '. Mesh roll
24. 열풍기24. Heaters
25. 열풍 건조로25. Hot air drying furnace
26. 발수기능 조성물통26. Water repellent composition container
31. 발수기능 조성물이 코팅처리된 한지(발수기능 한지)31. Hanji coated with water repellent composition (water repellent hanji)
31'. 발수기능 조성물이 비처리된 한지(종래 한지)31 '. Hanji without traditional water repellent composition (traditional Korean paper)
32. 물방울 32. Droplets
32'. 물 얼룩32 '. Water splash
33. 한지의 섬유조직이 비워져 있는 부분33. Part of the fiber tissue of Hanji
41. 발수기능 조성물이 코팅처리된 황토벽지(발수기능 한지+황토)41. Yellow soil wallpaper coated with a water repellent composition (water repellent hanji + ocher)
41'. 발수기능 조성물이 비처리된 황토벽지(종래 한지+황토)41 '. Loess wallpaper without water repellent composition (conventional Hanji + loess)
100. 발수기능 조성물100. Water repellent composition
Claims (10)