KR101169046B1

KR101169046B1 - Filler for artificial grass and artificial grass structure comprising the same

Info

Publication number: KR101169046B1
Application number: KR1020110015595A
Authority: KR
Inventors: 김진국
Original assignee: 경상대학교산학협력단
Priority date: 2011-02-22
Filing date: 2011-02-22
Publication date: 2012-07-26
Also published as: WO2012115345A1

Abstract

PURPOSE: Filler for artificial turf and an artificial turf structure therewith are provided to absorb external heat within a determined temperature range and to emit internal heat to the outside out of the determined temperature range. CONSTITUTION: Filler for artificial turf comprises base polymer and high molecules for controlling a temperature. The melting point of the high molecules is a temperature of 15-35 degrees. The heat capacity of the high molecules is 200-400Kj/kg within the melting point range.

Description

Filler for artificial grass and artificial grass structure comprising the same

본 발명은 인조 잔디 충전제 및 이를 포함하는 인조 잔디 구조물에 관한 것이다.
The present invention relates to artificial turf fillers and artificial turf structures comprising the same.

천연 잔디를 대체하기 위한 인조 잔디는 보편적으로 인조 잔디 파일 사이에 충전제를 충전시킴으로써 일정 무게로 지면에 안전하게 배치되도록 한 구조물의 형태를 띤다. 이의 일예를 도시하면 도 1과 같고, 실제 시공의 일예를 도시하면 도 2와 같다. Artificial grass for replacing natural grass is generally in the form of a structure that is securely placed on the ground at a certain weight by filling a filler between artificial grass piles. An example thereof is shown in FIG. 1, and an example of actual construction is shown in FIG. 2.

이러한 충전제(도 1에서 고무칩, 규사에 해당)의 일예로 재활용 연질플라스틱, 경탄 및 가소제 또는 재활용 연질 플라스틱 대신에 EPDM, 폐타이어 분말 등의 탄성력을 지닌 것도 있다. 또 다른 일예로 스티렌-에틸렌-부타디엔-스티렌(이하, SEBS) 등 열가소성 고무를 사용한 일예도 있다. An example of such a filler (corresponding to rubber chips and silica sand in FIG. 1) may be an elastic force such as EPDM and waste tire powder instead of recycled soft plastics, hard coal and plasticizers or recycled soft plastics. As another example, there is an example in which thermoplastic rubber such as styrene-ethylene-butadiene-styrene (hereinafter, SEBS) is used.

충전제의 다른 일예로 천연고무와 황토 분말의 미립자를 사용하여 충전제를 사용한 일예, 재활용이 가능한 SEBS와 폴리프로필렌, 폴리에틸렌을 사용한 일예도 있고, 또한 방향성 성분, 친수성 성분 및 항균성 성분 등을 함유하여 친환경적 요소를 가미한 일예도 있다. Other examples of fillers include natural rubber and fine particles of ocher powder, fillers used, and recycled SEBS, polypropylene, and polyethylene. Also, it contains aromatic, hydrophilic, and antimicrobial components. There is also an example that adds.

인조 잔디는 천연잔디가 가지지 못하는 관리의 편리성이라는 장점이 있어서 축구장, 야구장 등 운동구장에 사용되고, 환경적으로 문제가 되고 있는 골프장 그린으로 사용하려는 노력을 하고 있다. 그러나 인조 잔디를 사용하는데 있어서 저해요소가 있는데, 주요한 저해요소는 열복사 기능이 천연잔디에 비해 떨어지기 때문에 여름철에 상당히 더운 느낌을 줄 뿐만 아니라 운동시 겨울에는 차가운 느낌 및 마찰열을 많이 발생시켜 미끄럼이 발생하였을시 화상을 입을 염려가 크다는 점이다.
Artificial turf has the advantage of easy management that natural grass does not have, so it is used for sports fields such as soccer and baseball fields, and is trying to use it as a green golf course that is an environmental problem. However, there is an inhibitory factor in the use of artificial turf. The main inhibitory factor is that the heat radiation function is lower than that of natural grass, so it not only gives a considerably hot feeling in summer but also generates a lot of cold feeling and frictional heat during the exercise, which leads to slippage. If you do, there is a big risk of burns.

본 발명의 일 구현예에서는 마찰열을 줄이고 천연잔디와 같이 여름에는 시원한 느낌을, 겨울에는 따뜻한 느낌을 줄 수 있는 인조 잔디용 충전제를 제공하고자 한다.In one embodiment of the present invention is to provide a filler for artificial turf that can reduce the friction heat and give a cool feeling in the summer, such as natural grass, warm in the winter.

본 발명의 다른 일 구현예에서는 마찰열이 적고 천연잔디와 같이 여름에는 시원한 느낌을, 겨울에는 따뜻한 느낌을 가질 수 있는 인조 잔디 구조물을 제공하고자 한다. Another embodiment of the present invention is to provide an artificial turf structure that has a low frictional heat and has a cool feeling in summer, such as natural grass, a warm feeling in winter.

본 발명의 일 구현예에서는 베이스 폴리머; 및 융점이 15℃ 내지 35℃이고, 융점 범위 내에서 열용량이 200KJ/kg 내지 400KJ/kg인 온도조절고분자를 포함하는 인조 잔디용 충전재를 제공한다.In one embodiment of the present invention; And it provides a filler for artificial turf having a melting point of 15 ℃ to 35 ℃, a thermostatic polymer having a heat capacity of 200KJ / kg to 400KJ / kg within the melting point range.

본 발명의 바람직한 일 구현예에 의한 인조 잔디용 충전재에 있어서, 온도조절고분자는 그 중량이 전체 조성 중 1 내지 10중량%일 수 있다.In the artificial turf filler according to a preferred embodiment of the present invention, the temperature control polymer may have a weight of 1 to 10% by weight of the total composition.

본 발명의 바람직한 일 구현예에 의한 인조 잔디용 충전재에 있어서, 베이스 폴리머는 스티렌-에틸렌-부타디엔-스티렌 고무 및 폴리프로필렌을 포함하는 것일 수 있다. In the filler for artificial turf according to a preferred embodiment of the present invention, the base polymer may include styrene-ethylene-butadiene-styrene rubber and polypropylene.

본 발명의 일 구현예에 의한 인조 잔디용 충전재는 무기계 충전재, 안료 및 내후제 중에서 선택되는 단독 또는 이들의 혼합물을 포함할 수 있다. The filler for artificial grass according to one embodiment of the present invention may include an inorganic filler, a pigment and a weathering agent alone or a mixture thereof.

본 발명의 일 구현예에 의한 인조 잔디용 충전재는 시차주사열량계로 분석하였을 때 -20℃ 내지 20℃ 범위에서 전이 온도를 나타낸다. Artificial turf filler according to an embodiment of the present invention shows a transition temperature in the range of -20 ℃ to 20 ℃ when analyzed by a differential scanning calorimeter.

본 발명의 예시적인 일 구현예에서는 상기 일 구현예들에 의한 인조 잔디용 충전재를 포함하는 인조 잔디 구조물을 제공한다.In one exemplary embodiment of the present invention provides an artificial turf structure comprising a filler for artificial turf according to the embodiments.

본 발명의 일 구현예에에 의한 인조 잔디 충전물은 일정 온도 범위 내에서는 외부 열을 흡수하고 그 이상의 온도 범위에서는 자체열을 방출하여 온도를 일정하게 유지하려는 특성을 가져 천연잔디와 같이 여름에는 시원한 느낌을, 겨울에는 따뜻한 느낌을 줄 수 있다.
Artificial turf filling according to an embodiment of the present invention has a characteristic of absorbing external heat within a certain temperature range and releasing its own heat in a higher temperature range to maintain a constant temperature, such as natural grass feels cool in summer In winter, it can give a warm feeling.

도 1은 일반적인 인조 잔디 구조물의 단면을 도시한 일예.
도 2는 인조 잔디 구조물의 시공의 일예를 도시한 일예.
도 3은 온도조절 고분자가 갖는 온도조절 기능을 참조적으로 확인하기 위하여, 본 발명의 일 구현예에서 사용한 온도조절 고분자를 섬유 중에 포함하는 경우의 열특성을 관찰한 그래프.
도 4는 본 발명의 일 구현예에 의해 얻어진 충전재의 외관.
도 5는 대조구에 의해 얻어진 충전재의 외관.
도 6은 본 발명의 일 구현예에 의해 얻어진 충전재에 대하여 DSC에 의해 열특성을 관찰한 결과 그래프. 1 is an example showing a cross section of a typical artificial turf structure.
Figure 2 is an example showing an example of the construction of the artificial turf structure.
Figure 3 is a graph observing the thermal properties when the temperature control polymer used in one embodiment of the present invention in order to confirm the temperature control function of the temperature control polymer in the fiber.
4 is an appearance of a filler obtained by an embodiment of the present invention.
5 is an appearance of a filler obtained by the control.
Figure 6 is a graph of the thermal properties observed by DSC for the filler obtained by one embodiment of the present invention.

본 발명은 다양한 변경을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 명세서에서 사용되는 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
As the invention allows for various changes and numerous embodiments, particular embodiments will be illustrated in the drawings and described in detail in the written description. However, this is not intended to limit the present invention to specific embodiments, it should be understood to include all changes, equivalents, and substitutes included in the spirit and scope of the present invention. The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.

본 발명은 인조 잔디용 충전재를 제공하는데, 인조 잔디용 충전재는 통상 인조 잔디의 파일상의 형성물 사이에 분산되어 파일상의 형성물을 수직인 상태로 유지시켜 인조 잔디 구조물에 파일상의 형성물이 눕는 것을 방지할 목적으로 적용되는 것이 보통이다. The present invention provides a filler for artificial turf, artificial turf filler is usually dispersed between the pile on the pile of artificial turf to keep the pile on the pile vertical to keep the pile lying on the artificial turf structure It is usually applied for the purpose of prevention.

본 발명의 일 구현예에서는 이러한 고유한 기능은 물론이고, 온도조절기능을 갖는 인조 잔디용 충전재를 제공하는 바, 이는 융점이 15℃ 내지 35℃이고, 융점 범위 내에서 열용량이 200KJ/kg 내지 400KJ/kg인 온도조절고분자를 포함하여 달성된다. In one embodiment of the present invention, as well as such a unique function, provides a filler for artificial grass having a temperature control function, which has a melting point of 15 ℃ to 35 ℃, heat capacity within the melting point range of 200KJ / kg to 400KJ Achieved by including thermostatic polymers of / kg.

상기 및 이하의 기재에서 온도조절고분자는 일정 온도 범위 내에서는 외부 온도를 흡수하고, 그 이상의 온도 범위에서는 자체열을 방출하여 온도를 일정하게 유지하려는 특성을 갖는 것으로 이해될 수 있으며, 이러한 온도조절고분자를 섬유에 적용한 경우의 열특성을 참고적으로 제시하면 도 3과 같다. In the above and the following description, the temperature control polymer may be understood to have a characteristic of absorbing an external temperature within a certain temperature range and releasing its own heat to maintain a constant temperature in a higher temperature range. Referring to the thermal properties when applying to the fiber as shown in FIG.

도 3을 참조하여 보면, 주위 온도(공기 온도, Ambient Temperature) 하에서, 일반적인 섬유 의류로 느껴지는 온도(Normal Textile Wear), 온도조절고분자를 포함하는 섬유 온도(TempFeel Textile Wear) 및 체온(Body Temperature)를 비교하여 나타내었는데, 온도조절고분자를 포함하는 경우 외부 온도보다는 높은 온도를 나타내지만 실제 체온이나 일반적인 섬유에 비하여 적정의 온도를 유지하는 것을 확인할 수 있다. Referring to Figure 3, under the ambient temperature (air temperature, Ambient Temperature), the temperature (Normal Textile Wear) felt as a general textile clothing, the temperature (TempFeel Textile Wear) and the temperature (Body Temperature) including thermoregulated polymer In comparison, the temperature control polymer containing higher temperature than the external temperature, but it can be seen that maintain the proper temperature compared to the actual body temperature or common fibers.

이러한 결과로 볼 때, 온도조절고분자는 일정 온도 범위 내에서는 외부 온도를 흡수하고, 그 이상의 온도 범위에서는 자체열을 방출하여 온도를 일정하게 유지하려는 특성을 가지며, 이러한 온도조절고분자를 인조 잔디용 충전재 중에 포함시키는 경우 섬유에서 나타내는 고유한 성능을 발휘할 수 있을 것으로 충분히 예측할 수 있다. As a result, thermoregulated polymer absorbs external temperature within a certain temperature range and emits its own heat in a temperature range higher than that to maintain a constant temperature. If included in, it can be expected that the inherent performance shown in the fiber can be exhibited.

이러한 점에 착안하여 본 발명의 일 구현예에 의한 인조 잔디용 충전재는 온도조절고분자를 포함하는데, 특히 외부 온도를 흡수하고 자체열을 방출하는 적정의 기준 온도를 고려할 때 융점이 15℃ 내지 35℃이고, 융점 범위 내에서 열용량이 200KJ/kg 내지 400KJ/kg인 온도조절고분자인 것이 바람직하다. In view of this point, the artificial turf filler according to one embodiment of the present invention includes a thermoregulatory polymer, and in particular, considering the appropriate reference temperature for absorbing external temperature and releasing self-heat, the melting point is 15 ° C. to 35 ° C. It is preferable that it is a thermosetting polymer whose heat capacity is 200KJ / kg-400KJ / kg within melting | fusing point range.

만일 온도조절고분자의 융점 범위가 상기 범위를 벗어나면 보관상 및 온도조절 기능 발휘상 문제가 있을 수 있고, 또한 융점 범위 내에서 열용량이 상기 범위를 벗어나면 사계절의 온도조절 효과를 적절하게 하지 못하여 지나치게 첨가량을 늘려야 하기 때문에 비경제적인 문제가 있을 수 있다. If the melting point range of the thermoregulatory polymer is out of the above range, there may be a problem in storage and exertion of the temperature control function. Also, if the heat capacity is out of the above range within the melting point range, the temperature control effect of the four seasons may not be adequately adequate. There may be an uneconomical problem because the amount of addition must be increased.

이와 같이 온도조절고분자를 인조 잔디용 충전재 중 포함시키면 섬유에서 적용하여 발현하는 도 3과 같은 온도조절기능과 유사한 경향을 나타낼 것이며, 이로써 인조 잔디가 갖는 여름철의 온도가 높은 단점을 보완할 수 있다. As such, the inclusion of the thermoregulatory polymer in the artificial turf filler will show a tendency similar to the temperature control function as shown in FIG. 3 applied to the fiber, thereby compensating for the disadvantage that the temperature of the artificial turf has a high temperature in summer.

이러한 점은 인조 잔디용 충전재로 유용한 베이스 폴리머에 온도조절고분자를 3중량% 함량으로 첨가하여 얻어진 입상물에 대하여 열특성을 시차주사열량계로 측정한 결과, 동일 조성에서 온도조절고분자를 포함하지 않는 경우(대조구)에 비하여 융점이 더 높아졌고, 특이적으로 -20℃에서 20℃ 범위에서 커다란 피크가 나타났으며 이때의 열용량은 8.922J/g으로 측정되었다. 이러한 결과는 이러한 온도 범위에 대하여 열특성을 스스로 조절할 수 있는 것을 의미하는 것으로 해석될 수 있다. This is because when the thermal properties of the granules obtained by adding 3 wt% of the thermoregulating polymer to the base polymer, which is useful as a filler for artificial turf, were measured by differential scanning calorimetry, the thermosetting polymer was not included in the same composition. The melting point was higher than that of (control), and specifically, a large peak appeared in the range of -20 ° C to 20 ° C with a heat capacity of 8.922 J / g. These results can be interpreted to mean that the thermal properties can be adjusted by themselves over this temperature range.

이러한 온도조절고분자를 포함하는 경우 그 함량은 전체 조성 중 1 내지 10중량%인 것이 바람직할 수 있는데, 그 함량이 증가하면 온도조절 기능은 좋아지나 가격적인 면에서 불리하기 때문에 상기 범위 이내인 것이 바람직할 수 있다. In the case of including such a temperature-controlled polymer, the content may be preferably 1 to 10% by weight of the total composition. When the content is increased, the temperature-controlling function is improved, but it is preferable to be within the above range because it is disadvantageous in terms of price. can do.

한편 온도조절고분자로는 상업적으로 시판되고 있는 것들을 사용할 수 있는데, 그 일예로는 독일 Revepherm사 및 일본 Ashai Chemical사에서 제조되는 온도조절고분자 등을 일예로 들 수 있으나 이에 한정이 있는 것은 아니다. Meanwhile, as the temperature controlling polymer, commercially available ones may be used. Examples thereof include, but are not limited to, temperature controlling polymer manufactured by Revepherm of Germany and Ashai Chemical of Japan.

이와 같은 온도조절고분자 이외에 본 발명의 인조 잔디용 충전재는 통상의 인조 잔디용 충전재 중에 포함될 수 있는 베이스 폴리머 및 그 외의 첨가제 등을 포함함은 물론이다. In addition to the thermoregulated polymer, the artificial turf filler of the present invention may include a base polymer and other additives that may be included in a conventional artificial turf filler.

베이스 폴리머의 일예는 각별히 한정이 있는 것은 아니나, 폴리올레핀계 재료, 예를 들어 폴리에틸렌, 폴리프로필렌을 사용할 수 있고, 및/또는 열가소성 탄성중합체, 일예로 스티렌-부타디엔-스티렌 또는 스티렌-에틸렌-부타디엔-스티렌 등의 열가소성 재료를 사용할 수 있음은 물론이다. One example of the base polymer is not particularly limited, but may be a polyolefin-based material such as polyethylene, polypropylene, and / or a thermoplastic elastomer, for example styrene-butadiene-styrene or styrene-ethylene-butadiene-styrene It is a matter of course that thermoplastic materials such as these can be used.

본 발명의 바람직한 일 구현예에서는 폴리프로필렌과 SEBS를 베이스 폴리머로 포함한다. In a preferred embodiment of the present invention, polypropylene and SEBS are included as the base polymer.

본 발명의 일 구현예에 의한 인조 잔디용 충전재는 당업계에 알려져 있는, 다른 존재 가능한 충전재 및 첨가제를, 본 발명의 효과를 저해하지 않는 함량 범위 내에서 더 포함할 수 있음은 물론이다. 그 일예로 탄산칼슘 등과 같은 무기계 충전재, 내후제, 안료, 프로세스 오일 등을 들 수 있다. The artificial turf filler according to one embodiment of the present invention may further include other possible fillers and additives known in the art within a content range that does not impair the effects of the present invention. Examples thereof include inorganic fillers such as calcium carbonate, weathering agents, pigments, process oils and the like.

무기계 충전재의 일예로는 탈크 또는 탄산칼슘 등을 들 수 있다.Examples of the inorganic fillers include talc or calcium carbonate.

내후제는 자외선 안정화제, 자외선 차단제 및 산화방지제로 이루어진 군으로부터 선택되는 1종 이상인 것이 바람직하다. 자외선 안정화제의 예로는 폴리[[6-[(1,1,3,3-테트라메틸부틸아미노)-1,3,5-트리아진-2,4-디일]-[4-(2,2,6,6-테트라메틸-피페리딜)이미노]헥사메틸렌[4-(2,2,6,6-테트라메틸피페리딜)이미노]]을 들 수 있고, 자외선 차단제의 예로는 2-(2H-벤조트리아졸-2-일)-4,6-비스(1-메틸-1-페닐에틸) 페놀을 들 수 있으며, 산화방지제의 예로는 N,N'-헥사메틸렌-비스-(3,5-디-tert-부틸-4-히드록시하이드로시나미드)을 들 수 있다. The weathering agent is preferably at least one member selected from the group consisting of ultraviolet stabilizers, sunscreen agents and antioxidants. Examples of ultraviolet stabilizers include poly [[6-[(1,1,3,3-tetramethylbutylamino) -1,3,5-triazine-2,4-diyl]-[4- (2,2 , 6,6-tetramethyl-piperidyl) imino] hexamethylene [4- (2,2,6,6-tetramethylpiperidyl) imino]]. Examples of the sunscreen agent include 2 -(2H-benzotriazol-2-yl) -4,6-bis (1-methyl-1-phenylethyl) phenol, and examples of antioxidants are N, N'-hexamethylene-bis- ( 3,5-di-tert-butyl-4-hydroxyhydrocinamide) can be mentioned.

안료는 착색에 의해 원하는 색상을 발현시키는 역할을 한다. 무기 안료는 당업계에 공지된 것이라면 어느 것이든 무방하다.The pigment serves to express the desired color by coloring. The inorganic pigment may be any known in the art.

프로세스 오일은 균질한 혼합에 도움을 줌으로써 물성의 불균제화가 초래되지 않도록 한다. 또한, 프로세스 오일은 확장제(extender)/충전제 (filler)의 역할을 하기 때문에 완제품 비용을 낮출 수 있으며, 완제품 충진재의 인장 강도, 경도, 반발 탄성 등의 특성을 다양하게 변화시킬 수 있고, 충전제의 분산을 도와주며, 열을 흡수 분산시키고, 다른 구성성분들의 혼합을 빠르게 하여 에너지 소모를 줄일 수 있으며, 점도를 낮추어 천연 잔디와 유사한 촉감을 발현하도록 한다. 프로세스 오일의 일예로는 파라핀계 미네랄 오일 또는 파라핀-나프텐계 미네랄 오일 등을 들 수 있다.
Process oils aid in homogeneous mixing so that disproportionation of the properties is not caused. In addition, process oil acts as an extender / filler to reduce the cost of the finished product, and can vary the properties of the finished filler such as tensile strength, hardness, resilience, and the like. It absorbs and dissipates heat, speeds up the mixing of other ingredients, reduces energy consumption, and lowers the viscosity to create a texture similar to natural grass. Examples of process oils include paraffinic mineral oils and paraffinic-naphthenic mineral oils.

본 발명의 다른 일 구현예에서는 이러한 충전재를 포함하는 인조 잔디 구조물을 제공하며, 이의 일예는 도 1 및 도 2를 들 수 있으나 이에 한정이 있는 것은 아니다. Another embodiment of the present invention provides an artificial turf structure including such a filler, an example of which may include FIGS. 1 and 2, but is not limited thereto.

통상 인조 잔디 구조물은 기반 위에 부설된 인조 잔디를 가지며, 인조 잔디의 파일 사이에 충전재가 충전되어 있다. 기반은 지면을 평탄하게 고르게 한 간이 포장면이 이용되지만, 이것 이외에 자갈 등을 깔아 넣어도 좋고 아스팔트 등으로 포장된 기설 포장면을 이용하여도 좋다.The artificial turf structure typically has artificial turf laid on the foundation and is filled with filler between piles of artificial turf. As a base, a simple pavement with even ground is used, but in addition to this, gravel or the like may be used or an existing pavement wrapped with asphalt or the like.

더 나아가서는 기반 위에 탄성 포장 등을 설치하여도 좋고, 본 발명의 일 구현예에 있어서 기반의 구성은 사양에 따라서 변경 가능하며, 임의적 사항이다.Furthermore, an elastic package or the like may be installed on the foundation, and in one embodiment of the present invention, the construction of the foundation may be changed according to specifications and is optional.

인조 잔디는 바탕직물에 소정 간격으로 파일이 심어져 있다. 바탕직물은 예컨대 폴리프로필렌, 폴리에틸렌 등의 열가소성 수지가 적절하게 선택되지만 리사이클성을 고려하여 용융성이 좋은 저밀도 폴리에틸렌을 사용할 수도 있다. 또한 바탕직물은 합성수지제의 평직물일 수 있고, 이외에도 면상물을 펀칭 등의 방법으로 심은 것도 사용할 수 있다. 바탕직물의 색은 사양에 따라서 임의로 결정될 수 있다. Artificial turf is planted with piles at predetermined intervals on the base fabric. For the base fabric, a thermoplastic resin such as polypropylene or polyethylene is appropriately selected, but low density polyethylene having good meltability may be used in consideration of recycling properties. In addition, the base fabric may be a plain fabric made of a synthetic resin, and besides, a planted cotton material may be used by punching or the like. The color of the base fabric can be arbitrarily determined according to the specification.

파일은 바탕직물의 표면으로부터 선단까지 소정의 길이를 갖는 형상이며, 이러한 파일은 폴리프로필렌이나 폴리에틸렌 등의 열가소성 수지일 수 있고, 리사이클성을 고려하여 저밀도 폴리에틸렌을 사용할 수도 있다. 파일은 통상 녹색으로 착색될 수 있으나 이에 한정이 있는 것은 아니다. The pile has a shape having a predetermined length from the surface to the tip of the base fabric. The pile may be a thermoplastic resin such as polypropylene or polyethylene, and low density polyethylene may be used in consideration of recycling properties. The pile may typically be colored green but is not limited thereto.

이러한 인조 잔디에 충전재로서 상술한 일 구현예에 의한 충전재를 충전할 수 있다. The artificial turf may be filled with the filler according to the above-described embodiment as a filler.

이와 같은 인조 잔디 구조물은 천연잔디와 같이 여름에는 시원한 느낌을, 겨울에는 따뜻한 느낌을 줄 수 있다.
Such artificial turf structure can give a cool feeling in summer and warm in winter like natural grass.

이하 본 발명을 실시예에 의거 설명하지만, 본 발명이 이들 실시예에 의거하여 한정되는 것은 아니다. Hereinafter, although an Example demonstrates this invention, this invention is not limited based on these Examples.

실시예 Example

본 실시예는 온도조절고분자를 인조 잔디용 충전재로 포함하여 열적특성의 변화가 있음을 확인하여 실질적으로 본 발명의 인조 잔디용 충전재가 온도조절기능을 발현할 수 있음을 평가하기 위한 것으로, 온도조절고분자를 제외한 다른 조성에 각별히 한정을 두고자 하는 것이 아니다. This embodiment is to evaluate the change in the thermal properties including the thermoregulated polymer as the artificial turf filler to substantially evaluate the fact that the artificial turf filler of the present invention can express the temperature control function, temperature control There is no particular limitation on the composition other than the polymer.

본 실시예에서 사용된 인조 잔디용 충전재 조성은 다음 표 1과 같은 조성을 갖는다. 이와 같은 조성으로부터 통상의 방법에 따라 이축압축기를 사용하여 압출하여 인조 잔디용 충전재를 제조하여 이를 실시예로 하였다. 다음 표 1에서 온도조절고분자는 Revepherm사 제품으로 융점 28℃이고, 융점에서의 열용량이 240KJ/kg인 것이다.The filler composition for artificial turf used in the present embodiment has the composition shown in Table 1 below. From such a composition, an extrusion was made using a twin-screw compressor according to a conventional method to prepare artificial grass fillers . In Table 1 The thermoregulatory polymer is made by Revepherm and has a melting point of 28 ℃ and a heat capacity of 240KJ / kg.

얻어진 압출물의 외관은 도 4로 도시한 것과 같은 파란색 볼 형태의 것이다.The external appearance of the obtained extrudate is in the form of a blue ball as shown in FIG.

구성Configuration 함량content SEBSSEBS 20wt%20wt% PPPP 10wt%10wt% Process OilProcess Oil 10wt%10wt% CaCO₃ CaCO ₃ 55wt%55wt% 안료Pigment 2wt%2wt% UV흡수제UV absorbers 0.5wt%0.5wt% 온도조절고분자Thermostatic Polymer 2.5wt% 2.5wt%

이와 같은 조성으로부터 얻어지는 인조 잔디용 충전재는 다음 표 2와 같은 물성을 만족한다. The filler for artificial grass obtained from such a composition satisfies the physical properties shown in Table 2 below.

시험항목Test Items 측정치Measure 관련규격Related Standard 인장강도 (Kg/㎠)Tensile Strength (Kg / ㎠) 4040 ASTM D 638ASTM D 638 인열강도 (Kg/㎠)Tear strength (Kg / ㎠) 1818 ASTM D 624ASTM D 624 신율 (%)Elongation (%) 350350 ASTM D 638ASTM D 638 비중(g/cm2)Specific gravity (g / cm2) 1.41.4 ASTM D 1505ASTM D 1505 경도Hardness 5858 ASTM D2170ASTM D2170

한편 상기 표 1과 같은 조성에서 온도조절고분자만을 제외하고 동일한 방법으로 이축압출기를 사용하여 압출체를 제조하여 이를 대조구로 제조하였다. 얻어진 압출물의 외관은 도 5로 도시한 것과 같은 그린색 볼 형태의 것이다.
On the other hand, except for the temperature-controlled polymer in the composition shown in Table 1 by using the twin-screw extruder in the same manner to produce an extruded body was prepared as a control. The external appearance of the obtained extrudate is in the form of a green ball as shown in FIG.

상기 실시예 및 대조구로부터 얻어지는 압출물에 대하여 시차주사열량계(DSC, 모델명 DSC Q20, TA Instrument사 제작)를 이용하여 열적특성을 조사하여 그 결과를 도 6으로 나타내었다. The extrudate obtained from the examples and the control was examined for thermal properties using a differential scanning calorimeter (DSC, model name DSC Q20, manufactured by TA Instrument), and the results are shown in FIG. 6.

도 6의 결과로부터, 온도조절고분자를 포함하는 경우(실시예) 동일 조성에서 온도조절고분자를 포함하지 않는 경우(대조구)와 대비하여 융점이 더 높아졌고, 특이적으로 -20℃에서 20℃ 범위에서 커다란 피크가 나타났으며 이때의 열용량은 8.922J/g으로 측정되었다. 이러한 결과는 이러한 온도 범위에 대하여 열특성을 스스로 조절할 수 있는 것을 의미하는 것으로 해석될 수 있다. From the results of FIG. 6, the melting point was higher compared to the case of not including the temperature control polymer (control) in the case of containing the temperature control polymer (example), specifically -20 ℃ to 20 ℃ range A large peak appeared at and the heat capacity was measured to be 8.922 J / g. These results can be interpreted to mean that the thermal properties can be adjusted by themselves over this temperature range.

이러한 특성 피크는 일반적인 무기계 충전재의 첨가로는 나타나지 않는 피크로서, 온도조절고분자의 특성피크로 해석된다.
This characteristic peak is a peak which does not appear with the addition of a general inorganic filler, and is interpreted as the characteristic peak of the temperature-controlled polymer.

이러한 결과로부터 본 발명의 인조 잔디용 충전재는 일정 온도 범위 내에서는 외부 열을 흡수하고 그 이상의 온도 범위에서는 자체열을 방출하여 온도를 일정하게 유지하려는 특성을 가져 천연잔디와 같이 여름에는 시원한 느낌을, 겨울에는 따뜻한 느낌을 줄 수 있어, 천연잔디를 대체할 수 있는 인조 잔디 구조물에 유용함을 확인할 수 있다. From these results, the artificial grass filler of the present invention It absorbs external heat within a certain temperature range and releases its own heat in a higher temperature range to maintain a constant temperature. Like natural grass, it can feel cool in summer and warm in winter. It can be seen that it is useful for artificial turf structure that can replace the.

Claims

Base polymers; And
Melting point is 15 to 35 ℃, within the melting point range of artificial turf filler comprising a thermostatic polymer having a heat capacity of 200 to 400KJ / kg.

The method of claim 1,
Thermostatic polymer is the artificial turf filler having a weight of 1 to 10% by weight of the total composition.

The method of claim 1,
And wherein the base polymer comprises styrene-ethylene-butadiene-styrene rubber and polypropylene.

The method of claim 1,
Inorganic fillers, pigments and fillers for artificial grass comprising a single or a mixture thereof selected from weathering agents.

The filler for artificial turf according to claim 1, wherein the filler has a transition temperature in the range of -20 ° C to 20 ° C when analyzed by a differential scanning calorimeter.

Artificial turf structure comprising the filler for artificial turf of claim 1.