KR101093370B1 - Diaphragm for hard dome-tweeter and fabricating method of the same - Google Patents

Diaphragm for hard dome-tweeter and fabricating method of the same Download PDF

Info

Publication number
KR101093370B1
KR101093370B1 KR1020100007867A KR20100007867A KR101093370B1 KR 101093370 B1 KR101093370 B1 KR 101093370B1 KR 1020100007867 A KR1020100007867 A KR 1020100007867A KR 20100007867 A KR20100007867 A KR 20100007867A KR 101093370 B1 KR101093370 B1 KR 101093370B1
Authority
KR
South Korea
Prior art keywords
thermoplastic fiber
diaphragm
inorganic material
indirect
manufacturing
Prior art date
Application number
KR1020100007867A
Other languages
Korean (ko)
Other versions
KR20110088119A (en
Inventor
이동현
Original Assignee
에스텍 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 에스텍 주식회사 filed Critical 에스텍 주식회사
Priority to KR1020100007867A priority Critical patent/KR101093370B1/en
Publication of KR20110088119A publication Critical patent/KR20110088119A/en
Application granted granted Critical
Publication of KR101093370B1 publication Critical patent/KR101093370B1/en

Abstract

하드 돔트위터용 진동판 및 이의 제조방법이 개시된다. 상기 하드 돔트위터용 진동판 및 이의 제조방법은 무기물에 의하여 진동판이 제조되므로, 상대적으로 부드러운 음색의 고음질을 재생할 수 있다.Disclosed are a vibration plate for a hard dome tweeter and a method of manufacturing the same. The diaphragm for the hard dome tweeter and a method of manufacturing the diaphragm are manufactured by an inorganic material, and thus can reproduce a high sound quality of a relatively soft tone.

Description

하드 돔트위터용 진동판 및 이의 제조방법 {DIAPHRAGM FOR HARD DOME-TWEETER AND FABRICATING METHOD OF THE SAME}Diaphragm for hard dome tweeter and manufacturing method thereof {DIAPHRAGM FOR HARD DOME-TWEETER AND FABRICATING METHOD OF THE SAME}

본 발명은 하드 돔트위터용 진동판 및 이의 제조방법에 관한 것이다.The present invention relates to a vibration plate for a hard dome tweeter and a manufacturing method thereof.

스피커란 전기신호를 진동판의 진동으로 바꾸어 공기에 소밀파(疏密波)를 발생시켜 음파를 방사하는 음향기기이다.A speaker is an acoustic device that converts an electric signal into vibration of a diaphragm to generate a small density wave in the air to emit sound waves.

스피커를 기능별로 분류하면, 200㎐ 이하의 음역대를 재생하는 우퍼, 200㎐∼5㎑의 음역대를 재생하는 미드레인지, 5㎑∼20㎑의 음역대를 재생하는 트위터로 대별된다. 그리고, 트위터는 진동판의 형상에 따라 일반트위터와 돔트위터로 분류되고, 톰트위터는 진동판의 재질에 따라 소프트 돔트위터와 하드 돔트위터로 분류된다.When the speakers are classified by function, they are classified into woofers for reproducing a range of 200 kHz or less, midranges for reproducing a range of 200 kHz to 5 kHz, and tweeters for reproducing a range of 5 kHz to 20 kHz. The tweeter is classified into a general tweeter and a dome tweeter according to the shape of the diaphragm, and the tom tweeter is classified into a soft dome tweeter and a hard dome tweeter according to the material of the diaphragm.

소트프 돔트위터용 진동판은 실크 또는 테트론 등의 직물에 라텍스 또는 우레탄 등과 같은 부드러운 재료를 코팅하여 성형한다. 소트프 돔트위터용 진동판의 외주면측에는 진동판의 진동을 제어하는 엣지가 일체로 형성된다.The diaphragm for soft dome tweeter is formed by coating a soft material such as latex or urethane on a fabric such as silk or tetron. An edge for controlling the vibration of the diaphragm is integrally formed on the outer circumferential surface side of the diaphragm for the soft dome tweeter.

그리고, 하드 돔트위터용 진동판은 알루미늄 또는 마그네슘 등과 같은 고강성의 금속 재료로 성형한다. 하드 돔트위터용 진동판의 외주면에는 별도로 성형된 엣지가 접착된다.Then, the vibration plate for hard dome tweeter is molded from a high rigid metal material such as aluminum or magnesium. Separately formed edges are bonded to the outer circumferential surface of the diaphragm for the hard dome tweeter.

상기와 같은 종래의 하드 돔트위터용 진동판은 금속으로 제조되므로 음색이 상대적으로 날카로운 단점이 있다.Since the diaphragm for the conventional hard dome tweeter as described above is made of metal, the tone is relatively sharp.

그리고, 알루미늄 또는 마그네슘 등의 금속은 상대적으로 고가이므로, 원가가 상승하는 단점이 있다.In addition, since a metal such as aluminum or magnesium is relatively expensive, the cost increases.

그리고, 알루미늄 또는 마그네슘 등의 금속은 내식성이 부족하여 표면에 아노다이징을 한다. 이때, 아노다이징 공정 도중, 불량이 발생할 수 있어 신뢰성이 저하되는 단점이 있다.And metals, such as aluminum or magnesium, lack an corrosion resistance and anodize the surface. At this time, a defect may occur during the anodizing process, and thus there is a disadvantage in that reliability is lowered.

상기와 같은 금속제의 하드 돔트위터용 진동판의 문제점을 해소하기 위하여 무기물로 하드 돔트위터용 진동판을 제조하기 위한 기술이 개발중에 있다.In order to solve the problems of the metal hard dome tweeter diaphragm as described above, a technology for manufacturing a hard dome tweeter diaphragm with inorganic materials is under development.

그러나, 무기물은 그 특성상, 하드 돔트위터용 진동판이 구비하여야 할 특징인 경량 및 박형으로 가공하기가 어렵다. 또한, 무기물은 자체의 결합력이 없어 원하는 형상으로 형성하기 어렵다. 또한, 무기물에 바인더인 수지를 혼합할 경우, 바인더가 금형에 접착되어 원하는 두께로 일정하게 성형하기가 어렵다.However, the inorganic material is difficult to be processed into light and thin, which is a characteristic that the diaphragm for the hard dome tweeter should be provided. In addition, the inorganic material does not have a binding force of its own, it is difficult to form a desired shape. In addition, when the resin, which is a binder, is mixed with the inorganic material, the binder is adhered to the mold and it is difficult to be molded to a desired thickness constantly.

본 발명은 상기와 같은 종래기술의 문제점들을 해결하기 위하여 안출된 것으로, 본 발명의 목적은 상대적으로 부드러운 음색의 고음질을 재생할 수 있는 무기물을 이용한 하드 돔트위터용 진동판 및 이의 제조방법을 제공함에 있다.The present invention has been made to solve the problems of the prior art as described above, an object of the present invention to provide a vibration plate for a hard dome tweeter using an inorganic material that can reproduce a high sound quality of a relatively soft tone and a method of manufacturing the same.

상기 목적을 달성하기 위한 본 발명에 따른 트위터용 진동판은, 무기물과 바인더(Binder)인 열가소성 섬유를 혼합하여 형성한다.The tweeter diaphragm according to the present invention for achieving the above object is formed by mixing an inorganic material and a thermoplastic fiber that is a binder (Binder).

또한, 상기 목적을 달성하기 위한 본 발명에 따른 트위터용 진동판의 제조방법은, 진공배관과 연통되고 형성하고자 하는 진동판과 대응되는 형상이 형성된 치구가 설치되며 물이 저장되는 용기의 내부에 무기물과 열가소성 섬유를 혼합하고, 상기 치구에 간접물을 설치하는 단계; 상기 간접물이 설치된 상기 치구의 부위를 물속에 잠긴게 한 후, 상기 진공배관의 내부 압력을 조절하여 상기 간접물에 상기 무기물과 상기 열가소성 섬유를 흡착하는 단계; 상기 간접물에 흡착된 상기 무기물과 상기 열가소성 섬유를 상기 간접물과 함께 상기 치구로부터 분리한 후, 형성하고자 하는 진동판의 형상과 대응되는 형상이 형성된 금형속에 넣고 상기 열가소성 섬유를 용융시켜 성형하는 단계; 성형된 상기 무기물과 상기 열가소성 섬유를 상기 간접물과 함께 상기 금형으로부터 분리하여 냉각시키는 단계; 성형된 상기 무기물과 상기 열가소성 섬유를 상기 간접물로부터 분리하는 단계를 수행한다.In addition, the manufacturing method of the tweeter diaphragm according to the present invention for achieving the above object, the jig is formed in communication with the vacuum pipe and is formed in a shape corresponding to the diaphragm to be formed, the inorganic material and the thermoplastic in the container in which water is stored Mixing fibers and installing indirect materials in the jig; Adsorbing the inorganic material and the thermoplastic fiber to the indirect material by adjusting the internal pressure of the vacuum pipe after submerging the part of the jig in which the indirect material is installed; Separating the inorganic material and the thermoplastic fiber adsorbed to the indirect material from the jig together with the indirect material, and putting the thermoplastic fiber into a mold having a shape corresponding to the shape of the diaphragm to be formed to melt and mold the thermoplastic fiber; Cooling the molded inorganic material and the thermoplastic fiber together with the indirect material from the mold; Separating the shaped inorganic material and the thermoplastic fiber from the indirect material.

본 발명에 따른 하드 돔트위터용 진동판 및 이의 제조방법은 무기물에 의하여 진동판이 제조되므로, 상대적으로 부드러운 음색의 고음질을 재생할 수 있다.The diaphragm for the hard dome tweeter according to the present invention and a method for manufacturing the diaphragm are manufactured by the inorganic material, and thus can reproduce a high sound quality of a relatively soft tone.

도 1은 본 발명의 일 실시예에 따른 하드 돔트위터용 진동판의 제조공정을 보인 도.1 is a view showing a manufacturing process of a vibration plate for a hard dome tweeter according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 일 실시예에 따른 하드 돔트위터용 진동판 및 이의 제조방법을 상세히 설명한다.Hereinafter, a diaphragm for a hard dome tweeter and a method for manufacturing the same according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings.

본 실시예에 따른 하드 돔트위터용 진동판은 무기물과 열가소성 섬유가 혼합되어 형성된다. 이때, 열가소성 섬유는 바인더(Binder)의 기능을 한다.The vibration plate for the hard dome tweeter according to the present embodiment is formed by mixing an inorganic material and a thermoplastic fiber. At this time, the thermoplastic fiber functions as a binder.

도 1은 본 발명의 일 실시예에 따른 하드 돔트위터용 진동판의 제조공정을 보인 도로서, 이를 설명한다.1 is a view showing a manufacturing process of the vibration plate for a hard dome tweeter according to an embodiment of the present invention, it will be described.

도시된 바와 같이, 단계(S10)에서는 물이 저장된 용기(11)의 내부에 무기물(31)과 바인더인 열가소성 섬유(35)를 분산시켜 혼합한다.As shown, in step S10, the inorganic material 31 and the thermoplastic fiber 35 as a binder are dispersed and mixed in the container 11 in which water is stored.

본 실시예에 사용되는 무기물(31)은 운모, 세라믹 또는 글라스 비즈 중에서 선택된 어느 하나이고, 열가소성 섬유(35)는 폴리비닐 알코올(Polyvinyl Alcohol), 폴리에스테르(Polyester), 폴리프로필렌(Polypropylene) 또는 폴리에틸렌(Polyethylene) 중에서 선택된 어느 하나이다. 그리고, 무기물(31)과 열가소성 섬유(35)의 부피비는 비율이 70∼95％ : 30％∼5％이다.The inorganic material 31 used in the present embodiment is any one selected from mica, ceramic or glass beads, and the thermoplastic fiber 35 is made of polyvinyl alcohol, polyester, polypropylene, or polyethylene. (Polyethylene) any one selected from. And the ratio of the volume ratio of the inorganic material 31 and the thermoplastic fiber 35 is 70 to 95%: 30% to 5%.

열가소성 섬유(35)의 비율을 높게 하면 무기물(31)의 결합력을 증대시켜 강성을 향상시킬 수는 있으나, 열가소성 섬유(35)가 과도한 비율로 혼합되면 성형공정이 어렵고 진동판(30)의 물성이 저하될 수 있으므로, 열가소성 섬유(35)는 적절한 비율로 혼합하는 것이 바람직하다.When the ratio of the thermoplastic fibers 35 is increased, the bonding strength of the inorganic material 31 may be increased to improve rigidity. However, when the thermoplastic fibers 35 are mixed at an excessive ratio, the molding process is difficult and the physical properties of the diaphragm 30 are deteriorated. As such, the thermoplastic fibers 35 are preferably mixed in an appropriate proportion.

그리고, 혼합된 무기물(31)과 열가소성 섬유(35)의 물에 대한 희석비는 중량비 기준 0.1％ : 0.0001％인 것이 바람직하다.The dilution ratio of the mixed inorganic material 31 and the thermoplastic fiber 35 with respect to water is preferably 0.1% by weight to 0.0001% by weight.

용기(11)의 내부에는 형성하고자 하는 진동판(30)(S70 참조)과 대응되는 형상이 형성된 치구(13)가 설치된다. 치구(13)는 진공배관(15)과 연결되어 승강가능하게 설치되는데, 진동판(30)과 대응되는 형상이 형성된 치구(13)의 표면에는 진공배관(15)과 연통된 미세한 연통공(미도시)이 형성된다.A jig 13 having a shape corresponding to the diaphragm 30 (see S70) to be formed is formed in the container 11. The jig 13 is connected to the vacuum pipe 15 so as to be lifted up and down. The surface of the jig 13 having a shape corresponding to the diaphragm 30 is formed on the surface of the micro-communication hole communicating with the vacuum pipe 15 (not shown). ) Is formed.

진동판(30)을 제조하기 위한 최초의 상태는 치구(13)가 상승하여 물의 외측으로 노출된다. 그리고, 진동판(30)과 대응되는 형상이 형성된 치구(13)의 표면에는 면포 등으로 제조된 간접물(17)이 설치된다. 간접물(17)은 치구(13)에 고정되지 않고, 착탈된다.The initial state for manufacturing the diaphragm 30 is the jig 13 is raised and exposed to the outside of the water. In addition, an indirect object 17 made of a cotton cloth or the like is installed on the surface of the jig 13 having a shape corresponding to the diaphragm 30. The indirect object 17 is not fixed to the jig 13 and is detached.

단계(S20)에서는 간접물(17)이 물에 잠기도록 치구(13)를 하강시키고, 진공배관(15)의 압력을 진공으로 하강시킨다. 그러면, 압력차에 의하여 간접물(17)의 표면에는 무기물(31)과 열가소성 섬유(35)가 흡착된다.In step S20, the jig 13 is lowered so that the indirect material 17 is submerged in water, and the pressure of the vacuum pipe 15 is lowered to vacuum. Then, the inorganic material 31 and the thermoplastic fiber 35 are adsorbed on the surface of the indirect material 17 due to the pressure difference.

무기물(31)과 열가소성 섬유(35)의 비율, 진공배관(15) 내부의 진공압력의 세기, 진공배관(15) 내부의 진공압력 시간 등을 적절하게 조절하면, 진동판(30)의 중량을 조절할 수 있다.If the ratio of the inorganic material 31 and the thermoplastic fiber 35, the strength of the vacuum pressure in the vacuum pipe 15, the vacuum pressure time in the vacuum pipe 15, etc. are properly adjusted, the weight of the diaphragm 30 is adjusted. Can be.

단계(S30)에서는 치구(13)를 상승시켜, 간접물(17)을 물 외측으로 노출시킨다. 그러면, 간접물(17)에 흡착된 무기물(31)과 열가소성 섬유(35)도 물 외측으로 노출되므로, 간접물(17)과 함께 물 외측으로 노출된 무기물(31)과 열가소성 섬유(35)를 간접물(17)과 함께 치구(13)로부터 분리시킨다.In step S30, the jig 13 is raised to expose the indirect material 17 to the outside of the water. Then, since the inorganic material 31 and the thermoplastic fiber 35 adsorbed to the indirect material 17 are also exposed to the outside of the water, the inorganic material 31 and the thermoplastic fiber 35 exposed to the outside of the water together with the indirect material 17 are exposed. It is separated from the jig 13 together with the indirect material 17.

단계(S40)에서는 형성하고자 하는 진동판(30)과 대응되는 형상이 형성된 금형(19)속에 간접물(17)에 흡착된 무기물(31)과 열가소성 섬유(35)를 간접물(19)과 함께 넣고, 단계(S50)에서는 무기물(31)과 열가소성 섬유(35)를 성형한다. 금형(19)은 상부금형(19a)과 하부금형(19b)을 가진다.In step S40, the inorganic material 31 and the thermoplastic fiber 35 adsorbed to the indirect material 17 are placed together with the indirect material 19 in the mold 19 having a shape corresponding to the diaphragm 30 to be formed. In step S50, the inorganic material 31 and the thermoplastic fiber 35 are molded. The mold 19 has an upper mold 19a and a lower mold 19b.

이때, 무기물(31)과 열가소성 섬유(35)는 130∼210℃의 온도에서, 0.5∼5㎏／㎠의 압력으로, 약 5∼100초 성형된다. 그러면, 열과 온도에 의하여 열가소성 섬유(35)가 용융되고, 열가소성 섬유(35)는 용융되면서 무기물(31) 전체에 골고루 분포된다.At this time, the inorganic material 31 and the thermoplastic fiber 35 are shape | molded for about 5 to 100 second by the pressure of 0.5-5 kg / cm <2> at the temperature of 130-210 degreeC. Then, the thermoplastic fiber 35 is melted by heat and temperature, and the thermoplastic fiber 35 is melted and evenly distributed throughout the inorganic material 31.

무기물(31)과 열가소성 섬유(35)를 고온, 고압에서 성형할 때 발생하는 증기는 간접물(17)을 통하여 외부로 배출된다.Steam generated when the inorganic material 31 and the thermoplastic fiber 35 are formed at high temperature and high pressure is discharged to the outside through the indirect material 17.

단계(S60)에서는 성형된 무기물(31)과 열가소성 섬유(35)를 간접물(17)과 함께 금형(19)으로부터 분리한 다음 상온에서 냉각시킨다. 그러면, 열가소성 섬유(35)의 냉각에 의하여 무기물(31)과 열가소성 섬유(35)는 상호 결합력이 생겨 성형된 형상을 유지한다.In step S60, the molded inorganic material 31 and the thermoplastic fiber 35 are separated from the mold 19 together with the indirect material 17 and then cooled at room temperature. Then, the inorganic material 31 and the thermoplastic fiber 35 are formed by the cooling of the thermoplastic fiber 35 to maintain a molded shape by mutual bonding force.

마지막으로, 단계(S70)에서는 간접물(17)로부터 무기물(31)과 열가소성 섬유(35)를 분리하면, 진동판(30)이 제조된다. 간접물(17)은 면포로 마련되므로, 무기물(31)과 열가소성 섬유(35)는 용이하게 분리된다.Finally, in step S70, when the inorganic material 31 and the thermoplastic fiber 35 are separated from the indirect material 17, the diaphragm 30 is manufactured. Since the indirect material 17 is provided with a cotton cloth, the inorganic material 31 and the thermoplastic fiber 35 are easily separated.

제조된 진동판(30)은 필요에 따라 아크릴 수지, 페놀, 멜라민 또는 요소 수지 중에서 선택된 어느 하나에 함침될 수 있다(S80). 이는 진동판(30)을 경화(硬化)시키기 위함이다.The manufactured diaphragm 30 may be impregnated in any one selected from acrylic resin, phenol, melamine or urea resin as necessary (S80). This is for curing the diaphragm 30.

본 실시예에 따른 진동판(30)은 무기물에 의하여 제조되므로, 상대적으로 부드러운 음색의 고음질을 재생할 수 있다.Since the diaphragm 30 according to the present embodiment is manufactured by an inorganic material, it is possible to reproduce a high sound quality of a relatively soft tone.

이상에서는, 본 발명의 일 실시예에 따라 본 발명을 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 변경 및 변형한 것도 본 발명에 속함은 당연하다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Of course.

30: 진동판 31 : 무기물
35 : 열가소성 섬유30: diaphragm 31: mineral
35: thermoplastic fiber

Claims (13)

운모, 세라믹 또는 글라스 비즈 중에서 선택된 어느 하나의 무기물과 폴리비닐 알코올, 폴리에스테르, 폴리프로필렌 또는 폴리에틸렌 중에서 선택된 어느 하나로서 바인더(Binder)인 열가소성 섬유를 혼합하여 형성한 하드 돔트위터용 진동판에 있어서,
상기 무기물의 부피 : 상기 열가소성 섬유의 부피 = 70∼95％ : 30％∼5％인 것을 특징으로 하는 하드 돔트위터용 진동판.In the diaphragm for hard dome tweeter formed by mixing any one inorganic material selected from mica, ceramic or glass beads and a thermoplastic fiber which is a binder as any one selected from polyvinyl alcohol, polyester, polypropylene or polyethylene,
Volume of the said inorganic substance: Volume of the said thermoplastic fiber = 70-95%: 30%-5%, The diaphragm for hard dome tweeters characterized by the above-mentioned. 제1항에 있어서,
상기 무기물과 상기 열가소성 섬유의 혼합물은 아크릴 수지, 페놀, 멜라민 또는 요소 수지 중에서 선택된 어느 하나에 함침 성형된 것을 특징으로 하는 하드 돔트위터용 진동판.The method of claim 1,
The mixture of the inorganic material and the thermoplastic fiber is impregnated and molded in any one selected from acrylic resin, phenol, melamine or urea resin diaphragm for hard dome tweeter. 진공배관과 연통되고 형성하고자 하는 진동판과 대응되는 형상이 형성된 치구가 설치되며 물이 저장되는 용기의 내부에 무기물과 열가소성 섬유를 혼합하고, 상기 치구에 간접물을 설치하는 단계;
상기 간접물이 설치된 상기 치구의 부위를 물속에 잠긴게 한 후, 상기 진공배관의 내부 압력을 조절하여 상기 간접물에 상기 무기물과 상기 열가소성 섬유를 흡착하는 단계;
상기 간접물에 흡착된 상기 무기물과 상기 열가소성 섬유를 상기 간접물과 함께 상기 치구로부터 분리한 후, 형성하고자 하는 진동판의 형상과 대응되는 형상이 형성된 금형속에 넣고 상기 열가소성 섬유를 용융시켜 성형하는 단계;
성형된 상기 무기물과 상기 열가소성 섬유를 상기 간접물과 함께 상기 금형으로부터 분리하여 냉각시키는 단계;
성형된 상기 무기물과 상기 열가소성 섬유를 상기 간접물로부터 분리하는 단계를 수행하는 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.A jig is installed in communication with the vacuum pipe and formed with a shape corresponding to the diaphragm to be formed, mixing the inorganic material and the thermoplastic fiber in a container in which water is stored, and installing an indirect material in the jig;
Adsorbing the inorganic material and the thermoplastic fiber to the indirect material by adjusting the internal pressure of the vacuum pipe after submerging the part of the jig where the indirect material is installed;
Separating the inorganic material and the thermoplastic fiber adsorbed to the indirect material from the jig together with the indirect material, and then putting the thermoplastic fiber into a mold having a shape corresponding to the shape of the diaphragm to be formed to melt and mold the thermoplastic fiber;
Cooling the molded inorganic material and the thermoplastic fiber together with the indirect material from the mold;
Separating the molded inorganic material and the thermoplastic fiber from the indirect material manufacturing method of the diaphragm for a hard dome tweeter. 제3항에 있어서,
상기 무기물은 운모, 세라믹 또는 글라스 비즈 중에서 선택된 어느 하나인 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The inorganic material is a manufacturing method of the vibration plate for hard dome tweeter, characterized in that any one selected from mica, ceramic or glass beads. 제3항에 있어서,
상기 열가소성 섬유는 폴리비닐 알코올, 폴리에스테르, 폴리프로필렌 또는 폴리에틸렌 중에서 선택된 어느 하나인 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The thermoplastic fiber is a manufacturing method of the vibration plate for hard dome tweeter, characterized in that any one selected from polyvinyl alcohol, polyester, polypropylene or polyethylene. 제3항에 있어서,
상기 무기물의 부피 : 상기 열가소성 섬유의 부피 = 70∼95％ : 30％∼5％이고,
혼합된 상기 무기물과 상기 열가소성 섬유의 물에 대한 희석비는 중량비 기준 0.1％ : 0.0001％인 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The inorganic material volume: the volume of the thermoplastic fiber = 70 to 95%: 30% to 5%,
A dilution ratio of the mixed inorganic material and the thermoplastic fiber with respect to water is 0.1% by weight based on 0.0001% of the manufacturing method of the diaphragm for a hard dome tweeter. 제3항에 있어서,
상기 간접물에 흡착된 상기 무기물과 상기 열가소성 섬유는 상기 금형속에는 130∼210℃의 온도에서, 0.5∼5㎏／㎠의 압력으로, 5∼100초 성형되는 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The inorganic material and the thermoplastic fiber adsorbed to the indirect material are formed in the mold at a temperature of 130 to 210 ° C. at a pressure of 0.5 to 5 kg / cm 2 for 5 to 100 seconds. Manufacturing method. 제3항에 있어서,
성형된 상기 무기물과 상기 열가소성 섬유는 상기 간접물과 함께 상온에서 냉각되는 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The molded inorganic material and the thermoplastic fiber is cooled with the indirect material at room temperature, characterized in that the manufacturing method of the diaphragm for hard dome tweeter. 제3항에 있어서,
상기 간접물은 면포인 것을 특징으로 하는 하드 돔트위터용 진동판의 제조방법.The method of claim 3,
The indirect material is a manufacturing method of the diaphragm for a hard dome tweeter, characterized in that the cotton cloth. 제3항 내지 제9항 중, 어느 한 항에 있어서,
성형되어 상기 간접물로부터 분리된 상기 무기물과 상기 열가소성 섬유는 아크릴 수지, 페놀, 멜라민 또는 요소 수지 중에서 선택된 어느 하나에 함침 성형되는 단계를 더 수행하는 것을 특징으로 하는 하드 돔트위터용 진동판.The method according to any one of claims 3 to 9,
And forming the inorganic material and the thermoplastic fiber separated from the indirect material by impregnation with any one selected from acrylic resin, phenol, melamine or urea resin. 삭제delete 삭제delete 삭제delete
KR1020100007867A 2010-01-28 2010-01-28 Diaphragm for hard dome-tweeter and fabricating method of the same KR101093370B1 (en)