KR101088147B1 - Novel water-soluble nanocrystals and methods of preparing the same - Google Patents
Novel water-soluble nanocrystals and methods of preparing the same Download PDFInfo
- Publication number
- KR101088147B1 KR101088147B1 KR1020077018712A KR20077018712A KR101088147B1 KR 101088147 B1 KR101088147 B1 KR 101088147B1 KR 1020077018712 A KR1020077018712 A KR 1020077018712A KR 20077018712 A KR20077018712 A KR 20077018712A KR 101088147 B1 KR101088147 B1 KR 101088147B1
- Authority
- KR
- South Korea
- Prior art keywords
- water
- soluble
- subgroup
- nanocrystals
- group
- Prior art date
Abstract
원소주기율표(periodic system of the elements, PSE)의 서브족 IIb, 서브족 VIIa, 서브족 VIIIa, 서브족 Ib, 서브족 IV, 주족 II, 또는 주족 III의 원소로부터 선택된 적어도 하나의 금속 M1; 및 원소주기율표의 주족 V 또는 Vl의 원소로부터 선택된 적어도 하나의 원소 A;를 포함하는 코어를 포함하는 수용성 나노결정이 개시된다: 여기서 캡핑제는 상기 나노결정의 코어의 표면에 부착되고, 여기서 상기 캡핑제는 수용성 호스트 분자와 호스트-게스트 복합체를 형성한다. 원소주기율표(periodic system of the elements, PSE)의 서브족 IIb, 서브족 VIIa, 서브족 VIIIa, 서브족 Ib, 서브족 IV, 주족 II, 또는 주족 III의 원소로부터 선택된 적어도 하나의 금속 M1; 및 원소주기율표의 주족 V 또는 Vl의 원소로부터 선택된 적어도 하나의 원소 A;를 포함하는 코어를 포함하는 수용성 나노결정이 또한 개시된다: 여기서 캡핑제는 상기 나노결정의 코어의 표면에 부착되고, 여기서 상기 캡핑제는 수용성 호스트 분자에 공유결합적으로 연결된다. 원소주기율표 (periodic system of the elements, PSE)의 서브족 IIb, 서브족 VIIa, 서브족 VIIIa, 서브족 Ib, 서브족 IV, 주족 II, 또는 주족 III의 원소로부터 선택된 적어도 하나의 금속 M1을 포함하는 코어를 포함하는 수용성 나노결정이 또한 개시된다: 여기서 캡핑제는 상기 나노결정의 코어의 표면에 부착된다. 끝으로, 그러한 나노결정의 조성물과 용도가 개시된다.At least one metal M1 selected from elements of subgroup IIb, subgroup VIIa, subgroup VIIIa, subgroup Ib, subgroup IV, main group II, or main group III of the periodic system of the elements (PSE); And at least one element A selected from elements of the main group V or Vl of the Periodic Table of the Elements, wherein a capping agent is attached to the surface of the core of the nanocrystals, wherein the cap The ping agent forms a host-guest complex with a water soluble host molecule. At least one metal M1 selected from elements of subgroup IIb, subgroup VIIa, subgroup VIIIa, subgroup Ib, subgroup IV, main group II, or main group III of the periodic system of the elements (PSE); And at least one element A selected from elements of the main group V or Vl of the Periodic Table of the Elements is also disclosed, wherein the capping agent is attached to the surface of the core of the nanocrystals, wherein The capping agent is covalently linked to the water soluble host molecule. At least one metal M1 selected from elements of subgroup IIb, subgroup VIIa, subgroup VIIIa, subgroup Ib, subgroup IV, main group II, or main group III of the periodic system of the elements (PSE) Also disclosed is a water soluble nanocrystal comprising a core: wherein a capping agent is attached to the surface of the core of the nanocrystal. Finally, compositions and uses of such nanocrystals are disclosed.
나노결정, 수용성, 코어, 쉘, 호스트, 게스트, 복합체 Nanocrystalline, Water Soluble, Core, Shell, Host, Guest, Composite
Description
본 발명은 신규의 수용성 나노결정 및 그 제조방법에 관한 것이다. 본 발명은 또한 이에 한정되는 것은 아니나, 시험관에서 또는 생체내에서 생물학적인 재료 또는 공정의 검지 및/또는 시각화와 같은 다양한 분석적이고 생체의학적인 응용, 예를 들어 조직 또는 세포 이미징,을 포함한 그러한 나노결정의 용도에 관한 것이다. 본 발명은 또한 핵산, 단백질 또는 다른 생체분자와 같은 분석대상(analyte)의 검출에 사용될 수 있는 나노결정을 포함하는 조성물과 키트(kit)에 관한 것이다.The present invention relates to a novel water soluble nanocrystal and a method for producing the same. The invention also includes, but is not limited to, such nanocrystals, including various analytical and biomedical applications such as tissue or cell imaging, such as detection and / or visualization of biological materials or processes in vitro or in vivo. It relates to the use of. The invention also relates to compositions and kits comprising nanocrystals that can be used for detection of analytes such as nucleic acids, proteins or other biomolecules.
반도체 나노결정(양자점)은 광-방출 장치(Colvin et al, Nature 370, 354-357, 1994; Tessler et al, Science 295, 1506-1508, 2002), 레이저 (Klimov et al, Science 290, 314-317, 2000), 태양전지 (Huynh et al, Science 295, 2425-2427, 2002) 또는 세포 생물학과 같은 생화학적 연구 영역에 있는 형광성의 생물학적 라벨로서의 사용에 있어서 지대한 기본적이고 기술적인 관심을 받아 왔다. 예를 들어, Bruchez et al, Science, vol. 281, 2013-2015, 2001 Chan과 Nie, Science, Vol. 281, 2016- 2018, 2001; Klarreich, Nature, Vol. 43, 450-452, 2001에서 요약된 미국 특허등록6,207,392 또한 Mitchell, Nature Biotechnology, 1013-1017, 2001, 및 미국특허등록 6,423,551, 6,306,610 및 6,326,144를 참조하라.Semiconductor nanocrystals (quantum dots) are light-emitting devices (Colvin et al, Nature 370, 354-357, 1994; Tessler et al, Science 295, 1506-1508, 2002), lasers (Klimov et al, Science 290, 314-). 317, 2000), solar cells (Huynh et al, Science 295, 2425-2427, 2002) or use as a fluorescent biological label in the field of biochemical research such as cell biology. See, eg, Bruchez et al, Science, vol. 281, 2013-2015, 2001 Chan and Nie, Science, Vol. 281, 2016- 2018, 2001; Klarreich, Nature, Vol. See also US Pat. No. 6,207,392, summarized in 43, 450-452, 2001, also see Mitchell, Nature Biotechnology, 1013-1017, 2001, and US Pat. Nos. 6,423,551, 6,306,610 and 6,326,144.
생물학적 분석에서의 사용을 위한 감광성 비방사성 동위원소 검출 시스템의 개발은 DNA 시퀀싱, 임상 진단 검정법과 줄기 세포 및 분자 생물학 프로토콜과 같은, 많은 연구와 진단 영역에 상당한 영향을 주었다. 현재 비방사성 동위원소 검출 방법은 주로 색상 변화를 겪거나, 형광성, 발광성인 유기 리포터 분자에 주로 근거한다. 분자의 형광 라벨링은 생물학에서 표준 기법이다. 상기 라벨링은 종종 넓은 스펙트럼 모양, 짧은 존속시간, 광표백성(photobleaching) 및 세포에 대한 잠재적인 독성의 일반적 문제을 종종 일으키는 유기적 염료이다. 양자점의 최근의 만들어진 기술은 무기물 복합체 또는 입자를 사용하는 형광성의 라벨링의 개발을 위한 새로운 시대를 도래시켰다. 이러한 소재는 유기 염료에 비하여 종종 큰 스톡(stock) 이동, 긴 방출 반감기, 좁은 방출 피크 및 최소의 광표백(photo-bleaching)을 포함하여 실질적인 장점을 제공한다 (상기 인용문헌 참고).The development of photosensitive nonradioactive isotope detection systems for use in biological analysis has had a significant impact on many research and diagnostic areas, such as DNA sequencing, clinical diagnostic assays and stem cell and molecular biology protocols. Current non-radioactive isotope detection methods are mainly based on organic reporter molecules that undergo color changes, or which are fluorescent, luminescent. Fluorescent labeling of molecules is a standard technique in biology. Such labeling is an organic dye that often causes a general problem of broad spectral shape, short dwell time, photobleaching and potential toxicity to cells. The recent creation of quantum dots has brought a new era for the development of fluorescent labeling using inorganic composites or particles. Such materials often offer substantial advantages over organic dyes, including large stock shifts, long emission half-lives, narrow emission peaks and minimal photo-bleaching (see references above).
지난 10년간, 폭 넓고 다양한 반도체 나노 결정의 합성과 특징에 있어서 많은 연구가 이루어졌다. 최근의 발전은 상대적으로 단일분산 양자점의 대규모 제조로 이어졌다 (Murray et al, J. Am. Chem. Soc., 115, 8706-15, 1993; Bowen Katari et al, J. Phys. Chem. 98, 4109-17, 1994 Hines et al, J. Phys. Chem. 100, 468-71, 1996; Dabbousi et al, J. Phys. Chem. 101, 9463-9475,1997).In the last decade, much research has been done on the synthesis and characterization of a wide variety of semiconductor nanocrystals. Recent developments have led to the relatively large scale production of monodisperse quantum dots (Murray et al, J. Am. Chem. Soc., 115, 8706-15, 1993; Bowen Katari et al, J. Phys. Chem. 98, 4109 -17, 1994 Hines et al, J. Phys. Chem. 100, 468-71, 1996; Dabbousi et al, J. Phys. Chem. 101, 9463-9475, 1997).
또한, 발광성 양자점 기술에서의 발전은 양자점의 형광 효율과 안정성의 향상을 가져왔다. 양자점의 주목할 만한 발광성은 금속과 반도체 코어 입자가 여기 보어반지름 보다 더 작을 때, 약 1 내지 5 nm인 양자 크기의 제한에서 비롯된다. (Alivisatos, Science, 271, 933-37, 1996; Alivistos, J. Phys. Chem. 100, 13226-39, 1996; Brus, Appl Phys, A53, 465-74, 1991; Wilson et al, Science, 262, 1242-46, 1993) 최근 연구는 개선된 발광이 크기조절 가능이 더 낮은 밴드 갭 코어 입자를 더 높은 밴드 갭 무기물 쉘로 캡핑시킴에 의해 얻을 수 있다는 것을 보여주었다. 예를 들면, ZnS 층으로 패시베이트(passivated)된 CdSe 양자점은 실온에서 강하게 발광특성이 있고, 그들 방사 파장은 입자 크기를 변화시킴으로써 파랑에서 빨강으로 조정될 수 있다. 더욱이, ZnS 캡핑 층은 표면 비방사성 재결합 사이트를 패시베이트하고, 양자점의 안정성을 더 커지도록 한다. (Dabbousi et al, J. Phys. Chem. B101, 9463-75, 1997 Kortan 등, J. Am. Chem. Soc. 112, 1327-1332, 1990) In addition, developments in the luminescent quantum dot technology have led to improvements in fluorescence efficiency and stability of quantum dots. The notable luminescence of quantum dots results from a limitation of quantum size of about 1 to 5 nm when the metal and semiconductor core particles are smaller than the excitation radius. (Alivisatos, Science, 271, 933-37, 1996; Alivistos, J. Phys. Chem. 100, 13226-39, 1996; Brus, Appl Phys, A53, 465-74, 1991; Wilson et al, Science, 262, 1242-46, 1993) Recent studies have shown that improved luminescence can be obtained by capturing lower sized band gap core particles with higher band gap mineral shells. For example, CdSe quantum dots passivated with ZnS layers are strongly luminescent at room temperature, and their emission wavelengths can be adjusted from blue to red by changing the particle size. Moreover, the ZnS capping layer passivates the surface non-radioactive recombination sites and allows greater stability of the quantum dots. (Dabbousi et al, J. Phys. Chem. B101, 9463-75, 1997 Kortan et al., J. Am. Chem. Soc. 112, 1327-1332, 1990)
발광성 양자점 기술에서의 발전에도 불구하고, 종래의 캡핑된 발광성 양자점은 그들이 수용성이 아니기 때문에 생물학적인 응용에 적합하지 않다. Despite advances in luminescent quantum dot technology, conventional capped luminescent quantum dots are not suitable for biological applications because they are not water soluble.
이 문제를 극복하기 위하여, 양자점의 유기 패시베이팅(passivating) 층을 수용성 성분으로 대신하였다. 그러나, 결과로서 유도된 양자점은 전하 운반자 터널링(charge-carrier tunneling) 때문에 모체 보다 덜 발광성이다. (예를 들어, Zhong et al, J. Am. Chem. Soc. 125, 8589, 2003 참조). 2-머캡토에탄올 및 1-티 오-글리세롤과 같은 짧은 사슬의 티올은 수용성 CdTe 나노결정의 제조에서 또한 안정제로 사용되었다 (Rogach 등, Ber. Bunsenges. Phys. Chem. 100, 1772, 1996 Rajh 등, J. Phys. Chem. 97, 11999, 1993). 또 다른 접근에서 수용성 캐핑 화합물로서의 데옥시리보뉴클레익 액시드 (DNA)의 사용이 기술된다 (Coffer 등, Nanotechnology 3, 69, 1992). 모든 이러한 시스템에서, 코팅된 나노 결정체는 안정적이지 않고 광 발산 특성은 시간에 따라 저하되었다.To overcome this problem, the organic passivating layer of quantum dots was replaced with a water soluble component. However, the resulting quantum dots are less luminescent than the parent due to charge-carrier tunneling. (See, eg, Zhong et al, J. Am. Chem. Soc. 125, 8589, 2003). Short chain thiols, such as 2-mercaptoethanol and 1-thio-glycerol, have also been used as stabilizers in the preparation of water soluble CdTe nanocrystals (Rogach et al., Ber. Bunsenges. Phys. Chem. 100, 1772, 1996 Rajh et al. , J. Phys. Chem. 97, 11999, 1993). In another approach, the use of deoxyribonucleic acid (DNA) as the water soluble capping compound is described (Coffer et al., Nanotechnology 3, 69, 1992). In all these systems, the coated nanocrystals were not stable and the light divergence properties deteriorated with time.
추가 연구에서, Spanhel 등은 Cd(OH)2-캡핑된 CdS 졸(Spanhel et al, J. Am. Chem. Soc. 109, 5649, 1987)을 발표했다. 그러나, 콜로이드 나노결정은 매우 좁은 수소 이온 농도 범위(pH 8-10)에서만 제조될 수 있었고, 단지 10보다 큰 pH에서만 좁은 형광 밴드를 나타냈다. 그러한 pH 의존성은 소재의 유용성을 매우 제한하고, 특히, 그런 나노결정은 생물학적인 시스템의 용도에 적합하지 않다.In a further study, Spanhel et al. Published Cd (OH) 2 -capped CdS sol (Spanhel et al, J. Am. Chem. Soc. 109, 5649, 1987). However, colloidal nanocrystals could be prepared only at very narrow hydrogen ion concentration ranges (pH 8-10) and showed narrow fluorescence bands only at pH greater than 10. Such pH dependence greatly limits the usefulness of the material, and in particular, such nanocrystals are not suitable for use in biological systems.
국제 특허 출원 WO 00/17656에서 상기 나노결정을 수용성으로 하기 위하여 화학식 SH(CH2)n-COOH 및 SH(CH2)n-SO3H의 각각의 카복실 산 또는 술폰산 화합물에 의해 캡핑된 코어-쉘 나노결정이 기술된다. 유사하게, PCT 출원 WO 00/29617과 영국 특허 출원 GB 2342651은 머캡토 아세트산(mercapto acetic acid) 또는 머캡토운데카노 산(mercaptoundecanoic acid )과 같은 유기산을 나노결정을 수용성으로 만들고 단백질 또는 핵산과 같은 생체분자의 컨쥬게이션에 적합하게 하기 위하여 나노결정의 표면에 부착하는 것을 기술하였다. 영국 특허 출원 2342651은 또한 나노결정이 수용성을 가지도록 캡핑 물질로 트리옥틸포스핀의 사용을 기술한다.Core-capped by respective carboxylic or sulfonic acid compounds of the formulas SH (CH 2 ) n -COOH and SH (CH 2 ) n-SO 3 H in order to make the nanocrystals water-soluble in the international patent application WO 00/17656. Shell nanocrystals are described. Similarly, PCT application WO 00/29617 and British patent application GB 2342651 make organic crystals, such as mercapto acetic acid or mercaptoundecanoic acid, soluble in nanocrystals and made bioactives such as proteins or nucleic acids. Attachment to the surface of the nanocrystals has been described to suit the conjugation of molecules. British patent application 2342651 also describes the use of trioctylphosphine as the capping material so that the nanocrystals are water soluble.
국제 특허 출원 WO 00/27365는 수용성 제재로 디아미노카복실산 또는 아미노산의 사용을 기술한다. International patent application WO 00/27365 describes the use of diaminocarboxylic acids or amino acids as water soluble agents.
국제 특허 출원 출원WO 00/17655은 친수성 부분 및 소수성 부분을 갖는 가용(캡핑)제를 이용하여 수용성을 나타내는 나노결정을 기술한다. 캐핑제는 소수성 그룹을 통하여 상기 나노결정에 부착되고 반면에 카르복실산 또는 메타크릴산 그룹과 같은 친수성 그룹은 수용성을 제공한다. 추가적인 국제 특허 출원 (WO 02/073155)에서 수용해성 제재로서 하이드록사메이트, 하이드록사믹 산의 유도체 또는 에틸렌디아민과 같은 다좌 배위 착화제(multidentate complexing agent)를 사용한 수용성 나노결정이 기술된다. 마지막으로, 국제 특허 출원 PCT WO 00/58731은 혈구 개체군의 분석을 위해 사용된 나노결정이 개시되고, 여기에서 약 3,000 내지 약 3,000,000의 분자량을 갖는 아미노 유도체화 폴리사카리드가 상기 나노결정과 결합된다International patent application WO 00/17655 describes nanocrystals that exhibit water solubility using a soluble (capping) agent having a hydrophilic portion and a hydrophobic portion. Capping agents are attached to the nanocrystals through hydrophobic groups, while hydrophilic groups such as carboxylic or methacrylic acid groups provide water solubility. A further international patent application (WO 02/073155) describes water soluble nanocrystals using multidentate complexing agents such as hydroxyxamate, derivatives of hydroxyxamic acid or ethylenediamine as water soluble agents. Finally, international patent application PCT WO 00/58731 discloses nanocrystals used for analysis of blood cell populations, wherein amino derivatized polysaccharides having a molecular weight of about 3,000 to about 3,000,000 are combined with the nanocrystals.
그러나, 이러한 발전에도 불구하고 생물학적 검정에서 검출 목적으로 사용할 수 있는 발광성 나노결정이 요구된다. 이러한 점에서, 생체분자의 생물학적 활성을 보존하는 방법으로 생체분자에 부착될 수 있는 나노결정이 도움이 될 것이다. 나아가, 수성 매질에서 안정한 현탁액 또는 용액으로서 제조되고 저장될 수 있는 수용성 반도체 나노 결정이 바람직하다. 결국, 이러한 수용성 나노결정 양자점은 고양자 효율을 가진 에너지 방사를 가능하게 하고, 좁은 입자 크기를 가져야 한다.However, despite these advances, there is a need for luminescent nanocrystals that can be used for detection purposes in biological assays. In this regard, nanocrystals that can be attached to biomolecules will be helpful in ways that preserve the biological activity of the biomolecules. Furthermore, water soluble semiconductor nanocrystals that can be prepared and stored as stable suspensions or solutions in an aqueous medium are preferred. After all, these water soluble nanocrystalline quantum dots enable energy radiation with high quantum efficiency and should have a narrow particle size.
따라서, 상기의 필요를 충족하는 나노결정을 제공하는 것이 본 발명의 목적이다.Therefore, it is an object of the present invention to provide nanocrystals that meet the above needs.
이러한 목적은 각각의 독립 청구항의 특징을 가진 나노결정과 나노결정의 제조공정 의해 해결된다.This object is solved by the nanocrystals and the nanocrystal manufacturing process having the characteristics of each independent claim.
일 실시예에서, 그러한 나노결정은 원소주기율표(periodic system of the elements, PSE)의 서브족 Ib, 서브족 IIb, 서브족 IIIb, 서브족 IVb, 서브족 Vb, 서브족 VIb, 서브족 VIIb, 서브족 VIIIb, 주족 II, 주족 III 또는 주족 IV의 원소로부터 선택된 적어도 하나의 금속 M1을 포함하는 코어를 포함하는 수용성 나노결정이고, In one embodiment, such nanocrystals are subgroup Ib, subgroup IIb, subgroup IIIb, subgroup IVb, subgroup Vb, subgroup VIb, subgroup VIIb, subgroup of the Periodic System of the Elements (PSE). A water-soluble nanocrystal comprising a core comprising at least one metal M1 selected from elements of group VIIIb, main group II, main group III or main group IV,
여기서 캡핑제는 상기 나노결정의 코어의 표면에 부착되고, Wherein the capping agent is attached to the surface of the core of the nanocrystals,
여기서 상기 캡핑제는 수용성 호스트 분자와 호스트 게스트 복합체를 형성한다. 따라서, 이 실시예에서 본 발명은 순수 금속 코어를 포함하는 수용성 나노결정의 새로운 부류에 관한 것이다.Wherein the capping agent forms a host guest complex with a water soluble host molecule. Thus, in this example the present invention relates to a new class of water soluble nanocrystals comprising a pure metal core.
또 다른 실시예에서, 본 발명의 나노결정은 원소주기율표(periodic system of the elements, PSE)의 서브족 Ib, 서브족 IIb, 서브족 IVb, 서브족 Vb, 서브족 VIb, 서브족 VIIb, 서브족 VIIIb, IIB-VIB, IIIB-VB, 또는 IVB, 주족 II, 주족 III 또는 주족 IV의 원소로부터 선택되는 적어도 하나의 금속 M1,In another embodiment, the nanocrystals of the present invention comprise subgroup Ib, subgroup IIb, subgroup IVb, subgroup Vb, subgroup VIb, subgroup VIIb, subgroup of the Periodic System of the Elements (PSE). At least one metal M1 selected from elements of VIIIb, IIB-VIB, IIIB-VB, or IVB, main group II, main group III or main group IV,
주기율표(PSE)의 주족 V 또는 VI의 원소로부터 선택되는 적어도 하나의 원소 A,At least one element A selected from elements of the main group V or VI of the periodic table (PSE),
를 포함하는 코어를 포함하는 수용성 나노결정:A water-soluble nanocrystal comprising a core comprising:
여기서 캡핑제는 상기 나노결정의 코어의 표면에 부착되고, Wherein the capping agent is attached to the surface of the core of the nanocrystals,
여기서 상기 캡핑제는 수용성 호스트 분자와 호스트 게스트 복합체를 형성한다.Wherein the capping agent forms a host guest complex with a water soluble host molecule.
본 발명의 또 다른 실시예에서 그러한 나노결정은 원소주기율표(PSE)의 서브족 IIB-VIB, IIIB-VB 또는 IVB, 주족 II 또는 주족 III의 원소로부터 선택되는 적어도 하나의 금속 M1 및 원소주기율표의 주족 V 또는 Vl의 원소로부터 선택되는 적어도 하나의 원소를 포함하는 코어를 포함하는 수용성 나노결정이고,In another embodiment of the present invention such nanocrystals comprise at least one metal M1 selected from the elements of the subgroups IIB-VIB, IIIB-VB or IVB, main group II or main group III of the Periodic Table of the Elements and the main group of the Periodic Table of Elements. Is a water-soluble nanocrystal comprising a core comprising at least one element selected from elements of V or Vl,
여기에서 캡핑제는 상기 나노결정의 코어의 표면에 부착되고,Wherein the capping agent is attached to the surface of the core of the nanocrystals,
여기에서 캡핑제는 수용성 호스트 분자와 공유결합으로 연결되고, 및Wherein the capping agent is covalently linked with the water soluble host molecule, and
여기서 상기 호스트 분자는 탄수화물, 시클릭 폴리아민, 시클릭 디펩티드, 칼릭스아렌 및 덴드리머로 이루어진 군으로부터 선택된다.Wherein said host molecule is selected from the group consisting of carbohydrates, cyclic polyamines, cyclic dipeptides, kalixarenes and dendrimers.
또 하나의 실시예에서, 상기 나노결정은 In another embodiment, the nanocrystals are
원소주기율표(PSE)의 서브족 IIb, IIB-VIB, IIIB-VB 또는 IVB, 주족 II 또는 주족 III의 원소로부터 선택되는 적어도 하나의 금속 M1; 및At least one
원소주기율표의 주족 V 또는 VI의 원소로부터 선택되는 적어도 하나의 원소; At least one element selected from elements of main group V or VI of the periodic table of elements;
를 포함하는 코어를 포함하는 수용성 나노결정이고,It is a water-soluble nanocrystal containing a core comprising a,
여기서 소수성 캡핑제는 상기 나노결정의 코어의 표면에 부착되고, Wherein the hydrophobic capping agent is attached to the surface of the core of the nanocrystals,
여기서 상기 소수성 캡핑제는 크라운 에테르에 공유결합적으로 연결되고, 및Wherein said hydrophobic capping agent is covalently linked to the crown ether, and
여기서 상기 소수성 제재는 화학식(I)을 갖고,Wherein the hydrophobic agent has formula (I),
HAX-Y-Z,H A XYZ,
여기서, here,
X는 S, N, P 또는 O=P에서 선택되는 말단기이고,X is a terminal group selected from S, N, P or O = P,
A는 0 내지 3의 정수이고,A is an integer from 0 to 3,
Y는 적어도 3개의 주사슬 원자를 포함하는 분절(moiety)이고, Y is a moiety containing at least three main chain atoms,
Z는 소수성 말단기이다.Z is a hydrophobic end group.
Y는 최소한 3 개의 주사슬 원자를 가지는 분절이고, Z는 소수성 말단기다.Y is a segment having at least three main chain atoms, and Z is a hydrophobic end group.
따라서, 본 발명은 나노결정이 쉽게 물에 용해되도록 호스트 분자가 (반도체) 나노결정의 표면 특성을 변형하기 위해 사용될 수 있고, 그럼에도 불구하고 수성 매질에서 높은 물리적 화학적 안정성을 갖음을 발견함에 근거로 한다. 또한. 그러한 호스트 분자, 예를 들어 그러나 이에 제한되는 것은 아니지만, 덴드리머, 칼릭스아렌 또는 시클로덱스트린과 같은 탄수화물은(본 발명에 사용된 호스트 분자가 비록 친수성 구멍을 가질 수 있을지라도) 넓은 범위의 유기 분자를 게스트로서 받아 들이도록 하는 다소 큰 소수성 내부 구멍을 주로 갖는다. 따라서, 소수성 (또는 친수성) 구멍을 갖는 호스트 분자는 양자점의 표면개질을 위해 사용되는 소수성 (또는 친수성) 제재와 함께 호스트-게스트 복합체를 형성하기에 적합하다. 게다가, 그러한 호스트 분자는 다수의 생물학적인 프로브의 컨쥬게이션을 위해 주로 사용되는 여러가지 화합물(결합제)와 호스트-게스트 복합체를 또한 형성할 수 있으며, 따라서 여러가지 생물학적 응용에 적합한 발광 나노결정의 생체분자 컨쥬게이트에 대한 새롭고 정밀한 방법을 제공한다. 게다가 호스트 분자는 히드록실기 또는 카르복실기와 같은 수많은 용매 노출 활성화기(solvent exposed activatable group)를 포함할 수 있다. 이 활성화 가능기는 상기 호스트 분자와 호스트-게스트 복합체를 형성하는 나노결정에 관여하는 생체물질의 쉬운 공유결합 컨쥬게이션을 또한 허용한다.Thus, the present invention is based on the discovery that host molecules can be used to modify the surface properties of (semiconductor) nanocrystals so that nanocrystals are readily soluble in water and nevertheless have high physical and chemical stability in aqueous media. . Also. Such host molecules, such as, but not limited to, carbohydrates such as dendrimers, kalixarenes or cyclodextrins, although the host molecules used in the present invention may have hydrophilic pores, It mainly has a rather large hydrophobic inner hole that accepts as a guest. Thus, host molecules with hydrophobic (or hydrophilic) pores are suitable for forming host-guest complexes with hydrophobic (or hydrophilic) agents used for surface modification of quantum dots. In addition, such host molecules can also form host-guest complexes with various compounds (binders) that are primarily used for the conjugation of multiple biological probes, thus biomolecular conjugates of luminescent nanocrystals suitable for various biological applications Provides a new and precise way for. In addition, the host molecule may comprise a number of solvent exposed activatable groups such as hydroxyl or carboxyl groups. This activatable group also allows easy covalent conjugation of the biomaterials involved in the nanocrystals forming the host molecule with the host molecule.
모든 알려진 나노결정은 본 발명에 사용될 수 있다. 어떤 원소 A도 존재하지 않는 실시예에서, 상기 나노결정은 단지 금, 은, 동 (서브족 Ib), 티타늄 (서브족 IVb), 테르븀 (서브족 IIIb), 코발트, 플래티늄, 로듐, 루테늄 (서브족 VIIIb), 납(주족 IV) 또는 그것의 합금과 같은 금속으로 단지 이루어진다. 이러한 점에서, 만약, 아래에서 본 발명이 단지 카운터 원소(counter element) A를 포함하는 나노결정에 관한 참고로서 예를 든다면, 순수한 금속 또는 금속 합금으로 이루어지는 나노결정은 또한 모든 이러한 실시예에서 사용될 수 있든 것은 명백하다. 본 발명에 사용되는 나노결정은 Zn, Cd, Hg (서브족 IIb), Mg (주족II), Mn (주족VIIb), Ga, In, Al, (주족 III) Fe, Co, Ni (서브족 VIIIb), Cu, Ag, 또는 Au (서브족 Ib)과 같은 금속으로부터 형성된 이원 나노결정과 같은 잘 알려진 코어-쉘 나노결정(양자점)일 수 있다. 상기 나노결정은 임의의 족 II-VI 반도체 나노 결정일 수 있으며, 여기서 상기 코어 및/또는 상기 쉘은 CdS, CdSe, CdTe, MgTe, ZnS, ZnSe, ZnTe, HgS, HgSe, 또는 HgTe를 포함한다. 상기 나노결정은 또한 임의의 족 III-V 반도체 나노결정일 수 있고, 여기서 상기 코어 및/또는 쉘은 GaN, GaP, GaAs, GaSb, InN, InP, InAs, InSb, AlN, AlP, AlAs, AlSb을 포함한다. 본 발명에서 사용될 수 있는 코어-쉘 나노결정의 구체적 예로 ZnS 쉘 을 포함하는 나노결정 ((CdSe)-ZnS 나노결정) 또는(CdS)- ZnS-나노결정을 포함하지만 이에 한정되지는 않는다.All known nanocrystals can be used in the present invention. In embodiments in which no element A is present, the nanocrystals are only gold, silver, copper (subgroup Ib), titanium (subgroup IVb), terbium (subgroup IIIb), cobalt, platinum, rhodium, ruthenium (sub) Consisting only of a metal such as group VIIIb), lead (main group IV) or an alloy thereof. In this regard, if the present invention is exemplified below as reference only to nanocrystals comprising counter element A, nanocrystals consisting of pure metals or metal alloys may also be used in all such embodiments. It is obvious whether it is possible. Nanocrystals used in the present invention are Zn, Cd, Hg (subgroup IIb), Mg (group II), Mn (group VIIb), Ga, In, Al, (group III) Fe, Co, Ni (subgroup VIIIb ), Well known core-shell nanocrystals (quantum dots), such as binary nanocrystals formed from metals such as Cu, Ag, or Au (subgroup Ib). The nanocrystal may be any group II-VI semiconductor nanocrystal, wherein the core and / or the shell comprises CdS, CdSe, CdTe, MgTe, ZnS, ZnSe, ZnTe, HgS, HgSe, or HgTe. The nanocrystals may also be any group III-V semiconductor nanocrystals, wherein the core and / or shell comprises GaN, GaP, GaAs, GaSb, InN, InP, InAs, InSb, AlN, AlP, AlAs, AlSb do. Specific examples of core-shell nanocrystals that can be used in the present invention include, but are not limited to, nanocrystals ((CdSe) -ZnS nanocrystals) or (CdS) -ZnS-nanocrystals including ZnS shells.
그러나, 본 발명은 상기의 기술된 코어-쉘 나노결정의 사용에만 한정되지 않는다. 예를 들면, 또 다른 실시예로서 수용성이 가능한 상기 나노결정은 조성물 M11 - XM2XA를 갖는 균일한 삼원 합금으로 구성되는 나노결정일 수 있고,However, the present invention is not limited to the use of the core-shell nanocrystals described above. For example, as another embodiment, the nanocrystals that are water-soluble may be nanocrystals composed of a uniform tertiary alloy having the composition M1 1 - X M2 X A,
여기서 a) M1및 M2는, A가 원소주기율표의 주족 VI의 원소일 경우, 원소 주기율표의 서브족 IIb, 서브족 VIIa, 서브족 VIIIa, 서브족 Ib 또는 주족 II의 원소로부터 독립적으로 선택되며, 또는 b) M1 및 M2는, A가 원소주기율표의 주족 V의 원소일 경우, 둘다 원소주기율표의 주족 III의 원소로부터 선택된다. Wherein a)
또 다른 실시예에서 균일한 사원 합금으로 구성되는 나노결정이 사용될 수 있다. 이런 유형의 사원 합금은 조성물 M11 - xM2xAyB1 -y를 포함할 수 있고,In another embodiment, nanocrystals consisting of a uniform quaternary alloy may be used. Temple alloys of this type may comprise the composition M1 1 - x M2 x A y B 1 -y ,
여기서 a) M1과 M2는, A 및 B 둘 다 원소주기율표의 주족 VI의 원소일 경우, 독립적으로 원소주기율표(PSE)의 서브족 IIb, 서브족 VIIa, 서브족 VIIIa, 서브족 Ib 또는 주족 II의 원소에서 독립적으로 선택되고, 또는 b) M1과 M2는, A와 B 둘 다 원소주기율표의 주족 V의 원소일 경우, 독립적으로 원소주기율표의 주족 III의 원소에서 선택된다.Wherein a) M1 and M2 are independently of subgroup IIb, subgroup VIIa, subgroup VIIIa, subgroup Ib or main group II of the Periodic Table of the Elements when both A and B are elements of the main group VI of the Periodic Table of the Elements Or b) M1 and M2 are independently selected from the elements of main group III of the periodic table, provided that both A and B are elements of main group V of the periodic table of elements.
균일한 삼원 또는 사원 나노결정의 이러한 유형의 예는 Zhong 등, J. Am. Chem. Soc, 2003 125, 8598-8594 Zhong 등, J. Am. Chem. Soc, 2003 125, 13559-13553 및 국제출원 WO 2004/054923에서 기술되었다.Examples of this type of uniform ternary or quaternary nanocrystals are described in Zhong et al., J. Am. Chem. Soc, 2003 125, 8598-8594 Zhong et al., J. Am. Chem. Soc, 2003 125, 13559-13553 and in international application WO 2004/054923.
그러한 삼원의 나노결정은 Such ternary nanocrystals
i) 나노결정의 생성에 적합한 형태의 원소 M1을 포함하는 반응 혼합물을 적합한 온도 T1으로 가열하고, 이 온도에서 나노결정의 생성에 적합한 형태서의 원소 A를 첨가하고, 상기 이원 나노결정 M1A를 형성하는데 적합한 온도에서 충분한 기간의 시간동안 상기 반응 혼합물을 가열한 후, 상기 반응 혼합물을 냉각하는 단계 및i) The reaction mixture comprising element M1 in a form suitable for the production of nanocrystals is heated to a suitable temperature T1, at which temperature element A in the form suitable for the production of nanocrystals is added and the binary nanocrystal M1A is formed. Heating the reaction mixture for a sufficient time period at a temperature suitable for cooling the reaction mixture, and
ii) 상기 형성된 이원 나노결정 M1A를 침전시키거나 분리시킴 없이, 적합한 온도 T2로, 상기 반응 혼합물을 재가열하고, 이 온도에서의 반응혼합물에 충분한 양의 나노결정의 생성에 적합한 형태의 상기 원소 M2를 추가하고, 그 다음에 충분한 기간의 시간동안 상기 삼원 나노결정 M11-XM2XA을 형성하기에 적합한 온도에서 가열하고, 그 다음에 상기 반응물을 상온으로 냉각시키고, 그리고 상기 삼원 나노결정 M11-XM2XA을 분리하는 단계에 의해 이원 나노결정 M1A를 형성하는 단계를 포함하는 공정에 의하여 얻어질 수 있다.ii) reheating the reaction mixture to a suitable temperature T2 without precipitating or separating the formed binary nanocrystal M1A, and the element M2 in a form suitable for the production of a sufficient amount of nanocrystals in the reaction mixture at this temperature Add, and then heat at a temperature suitable for forming the three - way nanocrystal M1 1-X M2 X A for a sufficient period of time, and then cool the reaction to room temperature, and the three-way nanocrystal M1 1 It can be obtained by a process comprising the step of forming a binary nanocrystal M1A by separating -X M2 X A.
이러한 삼원 나노결정에서 색인 x는 0.001 < x < 0.999, 바람직하게는 0.01 < x < 0.99, 0.1 < 0.9, 또는 더욱 바람직하게는 0.5 < x < 0.95의 값을 가진다. 보다 더욱 바람직한 실시예에서, x는 약 0.2 또는 약 0.3에서 약 0.8 또는 약 0.9사이의 값을 가질 수 있다. 여기에서 사용된 사원 나노결정에서, y는 0.001 < y < 0.999, 바람직하게는 0.01 < y < 0.99의, 또는 더욱 바람직하게는 0.1 < x < 0.95 또는 약 0.2와 약 0.8 사이의 값을 가진다 In such ternary nanocrystals the index x has a value of 0.001 <x <0.999, preferably 0.01 <x <0.99, 0.1 <0.9, or more preferably 0.5 <x <0.95. In even more preferred embodiments, x can have a value between about 0.2 or about 0.3 and about 0.8 or about 0.9. In the quaternary nanocrystals used herein, y has a value of 0.001 <y <0.999, preferably 0.01 <y <0.99, or more preferably 0.1 <x <0.95 or between about 0.2 and about 0.8
II-VI 삼원 나노결정의 몇몇 실시예에서, 거기에 포함된 상기 원소 M1과 M2는 독립적으로 Zn, Cd 및 Hg로 이루어진 군으로부터 선택되는 것이 바람직하다. 이러한 삼원 합금에 있는 원소주기율표의 족 VI의 원소 A는 바람직하게는 S, Se 및 Te로 이루어진 군으로부터 선택된다. 그러므로, 이러한 원소 M1, M2 및 A의 모든 조합은 본 발명의 범위내에 있다. 몇몇의 바람직한 실시예에서, 사용된 나노결정은 ZnxCd1 - xSe, ZnxCd1 - xS, ZnxCd1 - xTe, HgxCd1 - xSe, HgxCd1 - xTe, HgxCd1 - xS, ZnxHg1 - xSe, ZnxHg1-xTe, 및 ZnxHg1 - xS의조성을 갖는다. In some embodiments of II-VI ternary nanocrystals, the elements M1 and M2 contained therein are preferably selected from the group consisting of Zn, Cd and Hg. The element A of the group VI of the periodic table of the ternary alloys is preferably selected from the group consisting of S, Se and Te. Therefore, all combinations of these elements M1, M2 and A are within the scope of the present invention. In some preferred embodiments, the nanocrystals used are Zn x Cd 1 - x Se, Zn x Cd 1 - x S, Zn x Cd 1 - x Te, Hg x Cd 1 - x Se, Hg x Cd 1 - x Te, Hg x Cd 1 - x S, Zn x Hg 1 - x Se, Zn x Hg 1-x Te, and Zn x Hg 1 - x S.
이러한 점에서, 상기 M1과 M2는 본 발명 전체에 걸쳐 교환 가능하게 사용될 수 있다, 예를 들면 Cd와 Hg를 포함하는 합금에서 이 중 어느 하나가 M1 또는 M2로 명명될 수 있다. 마찬가지로 원소주기율표의 족 V 또는 VI의 원소에 대한 A 및 B도 교환 가능하게 사용된다 그러므로 본 발명의 사원 합금에서 Se 또는 Te는 둘다 원소 A 또는 B로서 명명될 수 있다.In this regard, the M1 and M2 may be used interchangeably throughout the present invention, for example, any of these may be named M1 or M2 in an alloy comprising Cd and Hg. Similarly, A and B for elements of group V or VI of the Periodic Table of the Elements are also used interchangeably. Therefore, Se or Te may both be designated as elements A or B in the quaternary alloy of the present invention.
몇몇 바람직한 실시예에서, 여기에서 사용된 상기 삼원 나노결정은 조섬물 ZnxCd1-xSe를 포함한다. 그러한 나노결정은 x가 0.10 < x < 0.90 또는 0.15 < x < 0.85의 값을 갖고, 그리고 더욱 바람직하게는 0.2 < x < 0.8의 값을 갖는다. 다른 적절한 실시예에서 나노결정은 조성물 ZnxCd1-xS를 가진다. 그러한 나노결정은 바람직하게는 x가 0.10 < x < 0.95의 값 및 보다 바람직하게는 0.2 < x < 0.8의 값을 가진다.In some preferred embodiments, the ternary nanocrystals used herein comprise coarse Zn x Cd 1-x Se. Such nanocrystals have a value of x of 0.10 <x <0.90 or 0.15 <x <0.85, and more preferably of 0.2 <x <0.8. In another suitable embodiment the nanocrystals have the composition Zn x Cd 1-x S. Such nanocrystals preferably have x having a value of 0.10 <x <0.95 and more preferably 0.2 <x <0.8.
본 발명의 II-IV 나노결정의 경우에는, 원소 M1과 M2는 바람직하게는 독립적으로 Ga 및 인디움(Indium)에서 선택된다. 상기 원소 A는 바람직하게는 P, As 및 Sb에서 선택된다.In the case of II-IV nanocrystals of the present invention, the elements M1 and M2 are preferably independently selected from Ga and Indium. The element A is preferably selected from P, As and Sb.
상기한 기술된 바와 같이, 모든 나노결정(양자점)은, 그것의 표면이 상기 코어 나노결정(의 표면)에 대해 친화성을 가지는 (말단)기를 가진 캡핑제와 반응될 수 있는 한 본 발명에 사용될 수 있다. 따라서, 캡핑제는 주로 상기 나노결정의 표면과 공유 결합을 형성한다. 코어-쉘 나노결정의 경우에는, 공유결합은 캡핑제와 나노결정의 쉘 사이에 보통 형성된다. WO 2004/054923에서 기술된 것처럼 균일한 3원 또는 4원 나노결정이 사용되는 경우에, 공유 결합은 균일한 코어의 표면과 캡핑제 사이에 형성된다. 캡핑제는 예를 들어 호스트 분자의 내부 구멍의 소수성(또는 친수성)에 의존하는 실질적 친수 또는 실질적 소수 성질의 어느 하나일 수 있다. 이러한 점에서, 이러한 친수성 부분이 소수성 내부 구멍을 가지는 호스트 분자와 분자(즉 캡핑제)의 소수성 부분에 의하여 상기 호스트 게스트 복합체의 형성을 방해하지 않는한, 용어의 의미 내에서 "(실질적으로) 소수성 분자˝는 또한 소수성 부분 외에 친수성 부분을 포함할 수 있을 알 수있다. 마찬가지로, 이러한 소수성 부분이 친수성 내부 구멍을 가지는 호스트 분자와 분자(즉 캡핑제)의 친수성 부분에 의하여 상기 호스트 게스트 복합체의 형성을 방해하지 않는한, "(실질적으로) 친수성 분자˝라는 용어는 친수성 부분 외에 소수성 부분을 포함할 수 있는 분자를 포함한다. As described above, all nanocrystals (quantum dots) can be used in the present invention as long as their surface can be reacted with a capping agent having (terminal) groups having affinity for the core nanocrystals (surface of). Can be. Thus, the capping agent mainly forms covalent bonds with the surface of the nanocrystals. In the case of core-shell nanocrystals, covalent bonds are usually formed between the capping agent and the shell of the nanocrystals. In the case where uniform ternary or quaternary nanocrystals are used as described in WO 2004/054923, covalent bonds are formed between the surface of the uniform core and the capping agent. The capping agent can be either of substantially hydrophilic or substantially hydrophobic nature, depending for example on the hydrophobicity (or hydrophilicity) of the internal pores of the host molecule. In this respect, "(substantially) hydrophobic within the meaning of the term, unless such hydrophilic moieties interfere with the formation of the host guest complex by host molecules having hydrophobic internal pores and hydrophobic moieties of the molecule (ie, the capping agent). It will also be appreciated that the molecule 또한 may also include hydrophilic moieties in addition to hydrophobic moieties, and likewise the formation of the host guest complex by the hydrophobic moieties of the molecule (ie, the capping agent) and the host molecule having hydrophilic inner pores. Unless disturbed, the term "(substantially) hydrophilic molecule" includes molecules that may include hydrophobic moieties in addition to hydrophilic moieties.
일 실시예에서 "표면 캐핑"을 위하여 사용하는 상기 캡핑제는 화학식(I)을 가지며, In one embodiment the capping agent used for "surface capping" has formula (I),
화학식(I) HAX-Y-Z,Formula (I) H A XYZ,
여기서, X는 S, N, P 또는 O=P에서 선택되는 말단기이고, A는 0 내지 3의 범위의 정수이고, Y는 적어도 3개의 주사슬 원자를 포함하는 분절(moiety)이고, Z는 적합한 호스트 분자와 호스트-게스트 포함 복합체를 형성할 수 있는 소수성 말단기이다.Wherein X is an end group selected from S, N, P or O = P, A is an integer ranging from 0 to 3, Y is a segment containing at least three main chain atoms, and Z is It is a hydrophobic end group capable of forming a host-guest containing complex with a suitable host molecule.
주로, 상기 캡핑제의 분절 Y는 3에서 50의 주사슬 원자를 포함한다. 상기 분절 Y는 주로 이 제재에 현저하게 소수성 특성을 수여하는 어떠한 적합한 분절도 원칙적으로 포함할 수 있다.Mainly, segment Y of the capping agent contains 3 to 50 main chain atoms. The segment Y may in principle comprise any suitable segment which confers significantly hydrophobic character to this agent.
Y에 사용될 수 있는 적합한 분절의 예로 CH2- 기와 같은 알킬 분절, 시클로헥실기와 같은 시클로알킬 분절, - OCH2CH2- 기와 같은 에테르 분절, 또는 벤젠 고리 또는 나프탈렌 고리와 같은 방향족 분절을, 몇몇개의 예로, 포함한다.Examples of suitable segments which may be used for Y include alkyl segments such as CH 2 -groups, cycloalkyl segments such as cyclohexyl groups, ether segments such as OCH 2 CH 2 -groups, or aromatic segments such as benzene rings or naphthalene rings, Examples include four.
상기 분절 Y는 선형 사슬화, 분지화 될 수 있고, 주사슬 원자에 또한 치환을 가질 수도 있다. The segment Y may be linearly chained and branched, and may also have a substitution at the main chain atom.
Z는, 몇 개의 예로, - CH3기, 페닐기 (-C6H5), -SH, 히드록실기 (OH), 산기 (예를 들면, -SO3H, PO3H 또는 -COOH), 염기 (예를 들면, R=CH3 또는 -CH2-CH3인 NH2 또는 NHR1), 할로겐(-Cl, -Br, -I, -F), -OH, -C≡CH, -CH=CH2, 트리메틸실릴기 (-Si(Me)3), 페로센기 또는 아다만틴기(adamantine group)일 수 있다.Z is, in some instances, a -CH 3 group, a phenyl group (-C 6 H 5 ), -SH, a hydroxyl group (OH), an acid group (e.g., -SO 3 H, PO 3 H or -COOH), Base (e.g., NH 2 or NHR 1 with R = CH 3 or -CH 2 -CH 3 ), halogen (-Cl, -Br, -I, -F), -OH, -C≡CH, -CH = CH 2 , trimethylsilyl group (-Si (Me) 3 ), ferrocene group or adamantine group.
몇몇 실시예에서, CH3(CH2)nCH2SH, CH3O(CH2CH2O)nCH2SH, HSCH2CH2CH2(SH)(CH2)nCH3, CH3(CH2)nCH2NH2, CH3O(CH2CH2O)nCH2NH2, P((CH2)nCH3)3, O=P((CH2)nCH3)3와 같은 화합물은 캡핑제로 사용되고, 여기서 n은 30≥n≥6의 정수이다. 다른 실시예에서는 n은 30≥n≥8의 정수이다.In some embodiments, CH 3 (CH 2 ) n CH 2 SH, CH 3 O (CH 2 CH 2 O) n CH 2 SH , HSCH 2 CH 2 CH 2 (SH) (CH 2 ) n CH 3 , CH 3 (CH 2 ) n CH 2 NH 2 , CH 3 O (CH 2 CH 2 O) n CH 2 NH 2 , P ((CH 2 ) n CH 3 ) 3 , O = P ((CH 2 ) n CH 3 ) Compounds such as 3 are used as capping agents, where n is an integer of 30 ≧ n ≧ 6. In another embodiment n is an integer of 30 ≧ n ≧ 8.
이 점에에서, 더 소수성이거나 실질적으로 소수성 특성을 제공하는 캡핑제의 예로, 여기에 한정되지는 않지만, 1-머캡토-6-페닐 헥산 (HS-(CH2)6-Ph), 1,16-디머캡토-헥사데칸(HS-(CH2)16-SH), 18-머캡토-옥타데실아민(HS-(CH2)18-NH2), 트리옥틸포스핀, 또는 6-머캡토-헥산 (HS-(CH2)5-CH3)를 포함한다.In this respect, examples of capping agents that provide more hydrophobic or substantially hydrophobic properties include, but are not limited to, 1-mercapto-6-phenyl hexane (HS- (CH 2 ) 6 -Ph), 1, 16-dimercapto-hexadecane (HS- (CH 2 ) 16 -SH), 18-mercapto-octadecylamine (HS- (CH 2 ) 18 -NH 2 ), trioctylphosphine, or 6-mercapto -Hexane (HS- (CH 2 ) 5 -CH 3 ).
더 소수성의 또는 실질적으로 친수성 특성을 제공하는 캡핑제의 예로, 이에 한정되지는 않지만, 6-머캡토-헥사노익 산 (HS-(CH2)6-COOH), 16-머캡토-헥사데코닉 산 (HS-(CH2)16-COOH), 18-머캡토-옥타데실아민(HS-(CH2)18-NH2), 6-머캡토-헥실아민 (HS-(CH2)6-NH2) 또는 8-히드록시-옥틸티올 HO-(CH2)8-SH을 포함한다.Examples of capping agents that provide more hydrophobic or substantially hydrophilic properties include, but are not limited to, 6-mercapto-hexanoic acid (HS- (CH2) 6 -COOH), 16-mercapto-hexadeconic acid (HS- (CH 2) 16 -COOH), 18-mercapto-octadecylamine (HS- (CH 2 ) 18 -NH 2 ), 6-mercapto-hexylamine (HS- (CH 2 ) 6 -NH 2 ) Or 8-hydroxy-octylthiol HO- (CH 2 ) 8 -SH.
호스트 분자가 캡핑제와 반응할 수 있고, 상기 캡핑된 나노결정 및 상기 호스트 분자 사이에 형성된 복합체에 수용성을 제공할 수 있는한, 어떠한 호스트 분자도 본 발명에 사용될 수 있다. 주로, 호스트 분자는 수산기, 카르복실레이트기, 술포네이트기, 포스페이트기, 아민기, 카르복사미드기 또는 이와 유사한기와 같이 용매 노출된 극성기를 포함하는 수용성 화합물이다.Any host molecule can be used in the present invention as long as the host molecule can react with the capping agent and provide water solubility to the complex formed between the capped nanocrystal and the host molecule. Primarily, the host molecule is a water soluble compound comprising a solvent exposed polar group such as a hydroxyl group, a carboxylate group, a sulfonate group, a phosphate group, an amine group, a carboxamide group or the like.
적절한 호스트 분자의 예로 탄수화물, 시클릭 폴리아민, 시클릭 펩티드, 크라운 에테르, 덴드리머 등을 포함하지만, 이에 제한되지 않는다.Examples of suitable host molecules include, but are not limited to, carbohydrates, cyclic polyamines, cyclic peptides, crown ethers, dendrimers, and the like.
호스트 분자로 사용될 수 있는 시클릭 폴리아민의 예는1,4,8,11- 테트라아자시클로테트라데칸 (또한 시클램으로 알려짐) 및 1,4,7,11-테트라아자시클로테트라데칸(이소시클램), 1-(2-아미노메틸)-1, 4,8,11-테트라아자시클로테트라데칸(스콜피안드), 1,4,8,11-테트라아자시클로테트라데칸-6,13-디카복실레이트와 같은 그것의 유도체와 같은 테트라아자 거대고리분자(macrocylic moleculer)를 포함하며, 이것들은 예를 들어Sroczynski 및 Grzejdaziak, J. Incl. Phenom. Macrocyclic Chem. 35, 251-260, 1999, 또는 Bernhardt et al, J. Aus. Chem, 56, 679-684, 2003, hexaza macrocyclic complexes, (Hausmann, J. et al., Chemistry, A European Journal, 2004, 10, 1716; Piotrowski, T.et al., Electroanalysis, 2000, 12, 1397), 또는 octaza macrocyclic compounds (Kobayashi, K. et al., J. Am. Chem. Soc. 1992, 114, 1105)에 기술되어 있다. 앞에서의 Kobayashi, K. et al에 의해 기술된 옥타자 매크로시클릭 화합물은 또한 극성 게스트 분자 (예를 들면, 친수성 캐핑제)의 수용에 적합한 화합물의 일례이다. 제한된 정도로 또한 수용성일 수 있는 시클릭폴리아민, 예를 들어 5,5,7,12,14,14-헥사메틸-1,4,8,11테트라아자시클로테트라데칸 (Me6cylcam)을 사용하는 것이 가능하고, 카르복실레이트기 또는 설포네이트기와 같은 극성기를 제공하는 치환체로 그것을 개질하는 것이 또한 가능하다. 호스트 분자로 사용될 수 있는 매크로시클릭 아민의 다른 실시예는 Odashima, K., Journal of Inclusion phenomena and molecular recognition in chemistry, 1998, 32, 165 (예를 들어, 이 논문의 화합물 24 내지 26을 참조하라)에서 기술된 화합물이다.Examples of cyclic polyamines that can be used as host molecules include 1,4,8,11-tetraazacyclotetedecane (also known as cycllam) and 1,4,7,11-tetraazacyclotetedecane (isocycllam ), 1- (2-aminomethyl) -1,4,8,11-tetraazacyclotetradecane (scorpionand), 1,4,8,11-tetraazacyclotetradecane-6,13-dicarboxyl Tetraaza macrocylic molecules such as derivatives thereof, such as late, which are described, for example, in Sroczynski and Grzejdaziak, J. Incl. Phenom. Macrocyclic Chem. 35, 251-260, 1999, or Bernhardt et al, J. Aus. Chem, 56, 679-684, 2003, hexaza macrocyclic complexes, (Hausmann, J. et al., Chemistry, A European Journal, 2004, 10, 1716; Piotrowski, T. et al., Electroanalysis, 2000, 12, 1397 Or octaza macrocyclic compounds (Kobayashi, K. et al., J. Am. Chem. Soc. 1992, 114, 1105). Octamic macrocyclic compounds described by Kobayashi, K. et al, above, are also examples of compounds suitable for the acceptance of polar guest molecules (eg, hydrophilic capping agents). It is possible to use cyclic polyamines, for example 5,5,7,12,14,14-hexamethyl-1,4,8,11tetraazacyclotetracane (Me6cylcam), which may be water soluble to a limited extent and It is also possible to modify it with a substituent which provides a polar group, such as a carboxylate group or a sulfonate group. For other examples of macrocyclic amines that can be used as host molecules, see Odashima, K., Journal of Inclusion phenomena and molecular recognition in chemistry, 1998, 32, 165 (see, for example, compounds 24-26 of this paper). ).
적절한 칼릭스아렌의 예로 부틸칼릭스[4]아렌테트라아세틱산 테트라에틸 에스테르, Dondoni et al, Chem. Eur., J. 3, 1774, 1997에 기술된 테트라갈락토실칼릭스아렌 (Davis, AP. et al., Angew. Chem. Int. Edit., 1999, 38, 2979.), 옥타아미노아미드 레소신[4]-아렌 (Kazakov, E.K. et al., Eur. J. Org. Chem., 2004, 3323.), 4-술포닉 칼릭스[n]-아렌 (Yang, W.Z., J. Pharm. Pharmacology, 2004, 56, 703.), 술폰화된 티아칼릭스[4 또는 6]-아렌 (Kunsasgi- Mate S., Tetrahedron Letters, 2004, 45, 1387), Kobayashi et al., J. Am. Chem. Soc. 116, 6081, 1994 및 Yanagihara et al., J. Am. Chem. Soc. 114, 10307, 1992에 기술된 칼릭스아렌을 포함한다.Examples of suitable calix arenes include butylcalix [4] arentetraacetic acid tetraethyl ester, Dondoni et al, Chem. Tetragalactosylcalixarene (Davis, AP. Et al., Angew. Chem. Int. Edit., 1999, 38, 2979.), described in Eur., J. 3, 1774, 1997, octaaminoamide lesosin [4] -Aren (Kazakov, EK et al., Eur. J. Org. Chem., 2004, 3323.), 4-sulphonic calix [n] -aren (Yang, WZ, J. Pharm.Pharmacology, 2004, 56, 703.), sulfonated tiacalix [4 or 6] -aren (Kunsasgi-Mate S., Tetrahedron Letters, 2004, 45, 1387), Kobayashi et al., J. Am. Chem. Soc. 116, 6081, 1994 and Yanagihara et al., J. Am. Chem. Soc. Calixarenes described in 114, 10307, 1992.
본 발명에서 호스트 분자로 사용될 수 있는 고리형 펩티드의 예는Guo, W et al., Tetrahedron Letters, 2002, 43, 5665; 또는 Peng Li et al., Current Organic Chemistry, 2002, 6에서 기술된 칼릭스아렌을 포함하는 디시클로디펩티드를 포함하지만 여기에 한정되지는 않는다.Examples of cyclic peptides that can be used as host molecules in the present invention include Guo, W et al., Tetrahedron Letters, 2002, 43, 5665; Or dicyclodipeptides including Calixarene described in Peng Li et al., Current Organic Chemistry, 2002, 6.
호스트 분자로서 사용할 수 있는 크라운 에테르는 어떠한 고리 크기도 가질 수 있고, 예를 들면, 8, 9, 10, 12, 14, 15, 16, 18 또는 20 원자를 포함하는 고리계를 가질 수 있고, 그들 중 일부 원자는 주로 산소 또는 황과 같은 헤테로 원자이다. 여기에서 사용된 전형적인 크라운 에테르는 수용성 8-크라운-4 화합물 (여기에서 4는 헤테로 원자의 수를 표시한다), 9-크라운-3 화합물, 12-크라운-4 화합물, 15-크라운-5 화합물, 18-크라운-6 화합물 및 20-크라운-8 화합물(참고. 또한 그림 2E)을 포함하지만 여기에 한정되지는 않는다. 그러한 적절한 크라운 에테르의 몇가지 예로 (18-크라운-6)-2,3,11,12 테트라 카르복시산 또는 1,4,7,10-테트라자아실코도데칸-1,4,7,10 테트라 카르복시산을 포함한다.Crown ethers that can be used as host molecules can have any ring size, for example, can have a ring system comprising 8, 9, 10, 12, 14, 15, 16, 18 or 20 atoms, and Some of the atoms are mainly hetero atoms such as oxygen or sulfur. Typical crown ethers used herein include water-soluble 8-crown-4 compounds (where 4 represents the number of hetero atoms), 9-crown-3 compounds, 12-crown-4 compounds, 15-crown-5 compounds, 18-crown-6 compounds and 20-crown-8 compounds (see also Figure 2E), but are not limited to these. Some examples of such suitable crown ethers include (18-crown-6) -2,3,11,12 tetracarboxylic acid or 1,4,7,10-tetrazaacylcododecane-1,4,7,10 tetracarboxylic acid do.
원칙적으로, 적어도 부분적으로 상기 캡핑제를 수용할 수 있는 친수성 또는 소수성 구멍(친수성 또는 소수성 캡핑제가 사용되는지 여부에 의존하는)을 제공하는 모든 수용성 덴드리머가 본 발명에서 사용되었다. 덴드리머의 적절한 종류는 폴리프로필렌 이민 덴드리머, 폴리아미도 아민 덴드리머, 폴리 아릴 에테르 덴드리머, 폴리리신 덴드리머, 탄수화물 덴드리머, 실리콘 덴드리머 (예를 들면 Boas and Heegard, Chem. Soc. Rev. 33, 43-63, 2004에서 리뷰되었다)를 포함하지만 여기에 한정되지는 않는다. In principle, all water soluble dendrimers that provide hydrophilic or hydrophobic pores (depending on whether hydrophilic or hydrophobic capping agents are used) capable of receiving at least partially the capping agent have been used in the present invention. Suitable types of dendrimers include polypropylene imine dendrimers, polyamido amine dendrimers, polyaryl ether dendrimers, polylysine dendrimers, carbohydrate dendrimers, silicone dendrimers (e.g., Boas and Heegard, Chem. Soc. Rev. 33, 43-63, Reviewed in 2004), but is not limited to such.
일 실시예에서, 본 발명의 나노결정은 호스트 분자로서 탄수화물을 포함한다. 이 탄수화물 호스트 분자가 올리고사카리드, 녹말 또는 시클로덱스트린 분자일 수 있으며 여기에 한정되지는 않는다 (참고. Davisand Wareham, Angew. Chem. Int. Edit. 38, 2979-2996, 1999).In one embodiment, the nanocrystals of the present invention comprise carbohydrates as host molecules. This carbohydrate host molecule may be an oligosaccharide, starch or cyclodextrin molecule, but is not limited thereto (see Davisand Wareham, Angew. Chem. Int. Edit. 38, 2979-2996, 1999).
호스트 분자가 올리고사카리드인 실시예에서, 이 올리고사카리드는 주사슬에 2 내지 20 단량체 사이를, 예를 들어 6, 포함할 수 있다. 이러한 올리고머는 선형 또는 가지형 사슬이 될 수 있다.In embodiments where the host molecule is an oligosaccharide, the oligosaccharide may comprise between 2 and 20 monomers,
적절한 올리고사카리드의 예는 1,3-(디메틸렌)벤젠디일-6,6'-O-(2,2'-옥시디에틸)-비스-(2, 3, 4-트리-O-아세틸-β-D-갈락토피라노시드), 1,3-(디메틸렌)벤젠디일-6,6’-O-(2,2’-옥시디에틸)-비스-(2,3,4-트리-0-메틸-β-D-갈락토피라노시드) Shizuma et al., J. Org. Chem. 2002, 67 4795), 시클로트리키스-(1,2,3,4,5,6)-[α-D-글루코피라노실)-(1,2,3,4)-α-D- 글루코피라노실], (Cescutti et al., Carbohydrate Research, 2000, 329, 647), 아세틸레노사카리드 (Burli et al., Angew. Chem. Int. Edit. 1997, 36, 1852), 또는 시클릭 프룩토-올리고사카리드(Takai et al., J. Chem. Soc. Chem. Commun., 1993, 53.)을 포함하나 여기에 한정되는 것은 아니다.Examples of suitable oligosaccharides are 1,3- (dimethylene) benzenediyl-6,6'-O- (2,2'-oxydiethyl) -bis- (2, 3, 4-tri-O-acetyl -β-D-galactopyranoside), 1,3- (dimethylene) benzenediyl-6,6'-O- (2,2'-oxydiethyl) -bis- (2,3,4- Tri-0-methyl-β-D-galactopyranoside) Shizuma et al., J. Org. Chem. 2002, 67 4795), cyclotrikis- (1,2,3,4,5,6)-[α-D-glucopyranosyl)-(1,2,3,4) -α-D-glucopyra Nosyl], (Cescutti et al., Carbohydrate Research, 2000, 329, 647), acetylrenossaccharide (Burli et al., Angew. Chem. Int. Edit. 1997, 36, 1852), or cyclic fructo- Oligosaccharides (Takai et al., J. Chem. Soc. Chem. Commun., 1993, 53.), but are not limited thereto.
만약 녹말이 호스트 분자로 사용되면, 녹말은 약 1,000 내지 약 6,000 Da의 분자량 Mw를 가질 수 있다. 몇몇 실시예에서, 녹말은 약 4,000 Da ≥ Mw ≥ 약 2,000 Da의 분자량 Mw를 가진다. 또한 사용될 수 있는 녹말은 아밀로오스, 예를 들어 α아밀로오스 또는 β-아밀로오스를 포함할 수 있다.If starch is used as the host molecule, the starch may have a molecular weight Mw of about 1,000 to about 6,000 Da. In some embodiments, the starch has a molecular weight Mw of about 4,000 Da ≧ Mw ≧ about 2,000 Da. Starches that may also be used may include amylose, for example αamylose or β-amylose.
호스트 분자로서 적절한 시클로덱스트린의 예로 α-시클로덱스트린, β-시클로덱스트린, γ -시클로덱스트린, 디메틸-α-시클로덱스트린, 트리메틸-α-시클로덱스트린, 디메틸-β-시클로덱스트린, 트리메틸-β-시클로덱스트린, 디메틸-γ-시클로덱스트린 및 트리메틸-γ-시클로덱스트린을 포함한다.Examples of suitable cyclodextrins as host molecules include α-cyclodextrin, β-cyclodextrin, γ-cyclodextrin, dimethyl-α-cyclodextrin, trimethyl-α-cyclodextrin, dimethyl-β-cyclodextrin, trimethyl-β-cyclodextrin , Dimethyl-γ-cyclodextrin and trimethyl-γ-cyclodextrin.
상기한 공개에 따라서, 본 발명은 According to the above disclosure, the present invention
원소주기율표(PSE)의 서브족 IIB-VIB, IIIB-VB 또는 IVB, 주족 II 또는 주족 III의 원소로부터 선택되는 적어도 하나의 금속 M1 및 (이원 나노결정이 사용되는 경우에) 원소주기율표의 주족 V 또는 주족VI의 원소로부터 선택되는 적어도 하나의 원소를 포함하는 코어를 가지는 나노결정을 캡핑제와 반응시켜 상기 나노결정의 코어의 표면에 상기 캡핑제를 부착시키는 단계;At least one metal M1 selected from elements of subgroups IIB-VIB, IIIB-VB or IVB, main group II or main group III of the Periodic Table of Elements (PSE) and main group V of the Periodic Table of Elements (if a binary nanocrystal is used) or Attaching the capping agent to the surface of the core of the nanocrystals by reacting a nanocrystal having a core comprising at least one element selected from elements of main group VI with a capping agent;
그 다음에 상기 반응제와 수용성 호스트 분자 사이에 호스트 게스트 복합체를 형성하기 위하여 상기 얻어진 나노결정을 호스트 분자와 접촉시키는 단계;를 포함하는 수용성 나노결정을 제조하는 방법에 대한 일실시예를 제공한다. 상기 (캐핑) 반응제는 친수성 또는 소수성 중 하나일 수 있다. 상기에 개시된 바와 같이 순수한 금속 나노결정 또는 균일한 삼원 또는 사원 나노결정이 사용되는 경우에, 동일한 반응이 상기 반응의 나노결정을 제조하기 위하여 수행될 수 있다. Thereafter, contacting the obtained nanocrystals with a host molecule to form a host guest complex between the reactant and the water-soluble host molecule, provides an embodiment of a method for producing a water-soluble nanocrystals comprising. The (capping) reactant can be either hydrophilic or hydrophobic. When pure metal nanocrystals or uniform ternary or quaternary nanocrystals are used as disclosed above, the same reaction can be carried out to produce nanocrystals of the reaction.
이 반응은 나노결정의 표면에서 상기 캡핑제를 운반하는 상기 나노결정을 분리하면서 일반적으로 2단계로 수행된다. 예를 들면, 트리옥틸포스핀, 트리옥틸포스핀 옥사이드 또는 머캡토운데카노산과 같은 반응제와 반응하는 나노결정은 분리되고, 그들을 호스트 분자와 반응시키기 전에, 어떤 적절한 유기 용매 (예를 들어 그들의 몇몇개의 이름을 들면, 클로로포름, 메틸렌 클로라이드, 테트라히드로푸란)에 임의의 원하는 시간동안 저장된다.This reaction is generally carried out in two steps, separating the nanocrystals carrying the capping agent from the surface of the nanocrystals. For example, nanocrystals that react with a reactant such as trioctylphosphine, trioctylphosphine oxide or mercaptodecanoic acid are separated and, before reacting them with the host molecule, any suitable organic solvent (e.g. For example, chloroform, methylene chloride, tetrahydrofuran) for any desired time.
상기 캡핑된 나노결정과 상기 호스트 분자 사이에 상기 호스트-게스트 복합체는 다양한 반응조건에서 쉽게 형성될 수 있다. 예를 들면, 복합체 형성은 상기 나노결정의 용액을 호스트 분자 수용액, 예를 들면 시클로덱스트린 용액과 반죽함으로써, 또는 각각의 수용액으로 상기 나노결정을 환류함으로써 형성될 수 있다. 후자의 방법을 위해, 유기 용매에 존재하는 나노결정은 확장된 기간의 시간동안 환류 후에 수용성 용액으로 이송될 수 있다. (예를 들면 실시예 2를 보라) 다른 복합체 형성 방법으로 적절한 기간의 시간동안 실온에서 시클로덱스트린 용액 또는 다른 호스트 분자와 같은 호스트 분자의 용액에서 나노결정 현탁액을 교반하는 단계 또는 배양하는 단계를 포함한다. 일반적인 배양시간은 약 1 내지 약 10일의 범위일 수 있으나, 더 짧거나 더 긴 배양시간이 물론 또한 사용될 수 있다.The host-guest complex between the capped nanocrystals and the host molecule may be easily formed under various reaction conditions. For example, complex formation can be formed by kneading a solution of the nanocrystals with an aqueous host molecule solution, such as a cyclodextrin solution, or by refluxing the nanocrystals with each aqueous solution. For the latter method, the nanocrystals present in the organic solvent can be transferred to the aqueous solution after reflux for an extended period of time. (See Example 2, for example.) Other complexing methods include stirring or culturing the nanocrystalline suspension in a solution of host molecules such as a cyclodextrin solution or other host molecule at room temperature for an appropriate period of time. . Typical incubation times may range from about 1 to about 10 days, but shorter or longer incubation times may of course also be used.
본 발명은 또한 수용성 나노결정을 제조하는 방법에 관한 것이다. 이 방법은 원소주기율표(PSE)의 서브족 Ib, IIb, IIB-VIB, IIIB-VB 또는 IVB, 주족 II 또는 주족 III으로부터 선택되는 적어도 하나의 금속 M1, 및 원소주기율표의 주족 V 또는 VI의 원소로부터 선택되는 적어도 하나의 원소 A를 포함하는 코어를 포함하는 나노결정과 (캡핑) 반응제와 반응시키는 단계를 포함한다. 이 방법에서 상기 반응제는 탄수화물, 시클릭 폴리아민, 시클릭 디펩티드, 칼릭스아렌 그리고 덴드리머로 구성되는 군에서 선택되는 수용성 호스트 분자와 공유결합적으로 연결된다.The present invention also relates to a method for producing water soluble nanocrystals. The method is based on the elements of the Periodic Table (PSE) of at least one metal M1 selected from subgroups Ib, IIb, IIB-VIB, IIIB-VB or IVB, Main Group II or Main Group III, and Main Group V or VI of the Periodic Table of the Elements Reacting with the (capping) reactant with the nanocrystals comprising a core comprising at least one element A selected. In this method the reactant is covalently linked with a water soluble host molecule selected from the group consisting of carbohydrates, cyclic polyamines, cyclic dipeptides, kalixarenes and dendrimers.
또한 이 방법에서, 상기 나노결정 코어에 친화성을 갖는 말단기를 가지면 캡핑제로 사용될 수 있다. 이것은 상기 캡핑제가 친수성 또는 소수성 반응제일 수 있다는 것을 의미한다. 이 친수성이거나 소수성 캡핑제가 그것의 말단 그룹을 통하여 나노결정과 반응하고, 나노결정의 표면과 주로 공유결합을 형성한다. (참고. Masihul et al., J. Am. Chem. Soc. 2002, 43, 1132) 코어-쉘 나노결정의 경우에는, 공유 결합은 보통 나노결정과 캡핑제의 쉘과 형성된다. WO2004/054923에서 기술된 것처럼 균일한 삼원이거나 사원 나노결정이 사용되는 경우, 공유 결합이 균일한 코어의 표면과 캡핑제 사이에 형성될 것이다.Also in this method, if the end group having an affinity for the nanocrystalline core can be used as a capping agent. This means that the capping agent can be a hydrophilic or hydrophobic reactant. This hydrophilic or hydrophobic capping agent reacts with the nanocrystals through its end groups and forms mainly covalent bonds with the surface of the nanocrystals. (See Masihul et al., J. Am. Chem. Soc. 2002, 43, 1132) In the case of core-shell nanocrystals, covalent bonds are usually formed with the nanocrystals and the shell of the capping agent. If uniform ternary or quaternary nanocrystals are used as described in WO2004 / 054923, covalent bonds will be formed between the surface of the uniform core and the capping agent.
이 방법의 몇몇 실시예에서 식(II) HIX-Y-B 를 가지는 캡핑제가 사용되고, 여기에서In some embodiments of this method a capping agent having the formula (II) H I XYB is used, wherein
X는 S, N, P 또는 O=P로부터 선택되는 말단기,X is a terminal group selected from S, N, P or O = P,
I는 1내지 3의 범위의 정수,I is an integer ranging from 1 to 3,
Y는 적어도 3개의 주사슬 원자를 포함하는 분절, 및 Y is a segment containing at least three main chain atoms, and
B는 상기 캡핑제와 공유결합적으로 연결되는 수용성 호스트 분자이다.B is a water soluble host molecule covalently linked with the capping agent.
이러한 점에서, 상기 캡핑제와 상기 호스트 분자 사이에 형성된 상기 공유결합은 결합인 어떠한 공유결합유형일 수 있고, 예를 들면, C-C 결합, 에테르 결합(-O-), 티오에테르 결합 (-S-), 에스테르 결합, 아미드 결합 또는 이미드 결합이 있다. 공유결합의 유형은 보통 캡핑제와 호스트 분자를 연결하는 접근방법에 단지 의존한다. 예를 들면, 만약 캐핑제가 할로겐화 알킬이고 호스트 분자가 자유로운 (또는 활성화된) 히드록실 또는 티올기를 가지면, 에테르 또는 티오에테르 결합이 형성된다 (실시예 3 및 5를 보라). 또한, 만약 캐핑제가 공유결합을 위한 아민기를 제공하고 호스트 분자가 반응성 카르복시기를 가진다면, 에스테르 결합이 형성된다. 따라서, 상기 호스트 분자와 상기 캡핑제의 공유 결합을 위한 반응성기의 적절한 조합의 선택은 당 분야의 통상의 지식을 가진 자의 지식내에 포함된다. In this regard, the covalent bond formed between the capping agent and the host molecule may be any covalent bond type that is a bond, for example, a CC bond, an ether bond (-O-), a thioether bond (-S-) , Ester bonds, amide bonds or imide bonds. The type of covalent bond usually depends only on the approach of connecting the capping agent and the host molecule. For example, if the capping agent is halogenated alkyl and the host molecule has free (or activated) hydroxyl or thiol groups, ether or thioether bonds are formed (see Examples 3 and 5). Also, if the capping agent provides an amine group for covalent bonds and the host molecule has a reactive carboxyl group, an ester bond is formed. Thus, the selection of a suitable combination of reactive groups for the covalent linkage of the host molecule with the capping agent is included within the knowledge of one of ordinary skill in the art.
이러한 점에서, 공유결합이 (식 (II) HlX-Y-B의 화합물을 산출하기 위해) 나노결정과의 반응 전에 캡핑제와 호스트 분자 사이에 형성되는 것이 필수적이 아님을 알 수 있다. 오히려, 캡핑제가 나노결정과 먼저 반응되고 그 후에 캡핑제와 호스트 분자 사이에 공유결합이 형성된다는 것도 본 발명의 범위 내에 있다.In this respect, it can be seen that it is not necessary that a covalent bond be formed between the capping agent and the host molecule prior to reaction with the nanocrystals (to yield the compound of formula (II) HX-Y-B). Rather, it is also within the scope of the present invention that the capping agent first reacts with the nanocrystals and then a covalent bond is formed between the capping agent and the host molecule.
이 방법의 일 실시예에서, 사용된 캡핑제가 화학식:In one embodiment of this method, the capping agent used is of the formula:
HAX-Y-ZH A XYZ
을 가진다: 여기서, X가 S, N, P 또는 O=P로부터 선택되는 말단기이고, A는 0 내지 3의 범위의 정수이고, Y는 적어도 3개의 주사슬 원자를 가지는 분절이다. 주로, (캐핑) 반응제의 상기 분절 Y는 3 내지 50개의 주사슬 원자를 포함한다. 상기 분절 Y는 주로 이 반응제에 현저하게 소수성 특성을 수여하는 임의의 적절한 분절을 포함할 수 있다. 상기 분절 Y에 사용될 수 있는 적절한 분절의 예는 예를 들어, CH2-기와 같은 알킬분절, 시클로헥실기와 같은 시클로알킬 분절, -OCH2CH2- 기와 같은 에테르 분절, 또는 벤젠 고리 또는 나프탈렌 링과 같은 방향족 분절을 포함한다. Y는 선형 또는 가지형 사슬일 수 있고 주사슬 원자에 치환기를 가질 수 있다. Z는 예를 들어 -SH 기, 히드록시기(OH), 산기 (예를 들어, -SO3H, PO3H 또는 -COOH), 염기기 (예를 들어, NH2 또는 NHR1, 여기서 R =CH3 또는 -CH2-CH3), 할로겐(-Cl, - Br, -I, -F)와 같은 상기 호스트 분자에 공유결합적으로 연결할 수 있는 임의의 작용기일 수 있다.Wherein X is a terminal group selected from S, N, P or O = P, A is an integer ranging from 0 to 3, and Y is a segment having at least three main chain atoms. Mainly, the segment Y of the (capping) reactant contains 3 to 50 main chain atoms. The segment Y may comprise any suitable segment which confers predominantly hydrophobic character on the reactant. Examples of suitable segments that can be used in segment Y are, for example, alkyl segments such as CH 2 -groups, cycloalkyl segments such as cyclohexyl groups, ether segments such as -OCH 2 CH 2 -groups, or benzene rings or naphthalene rings Aromatic segments such as; Y may be a linear or branched chain and may have a substituent on the main chain atom. Z is for example a -SH group, a hydroxyl group (OH), an acid group (eg -SO 3 H, PO 3 H or -COOH), a base group (eg NH 2 Or NHR 1 , wherein R = CH 3 or -CH 2 -CH 3 ), any functional group capable of covalently linking to said host molecule such as halogen (-Cl,-Br, -I, -F) have.
본 발명은, 여기에서 기술된 것처럼, 주어진 분석대상에 대한 결합 친화성을 가지는 분자에 컨쥬게이트된 나노결정에 관하여 더 언급한다. 주어진 분석대상에 대해 결합 친화성을 가지는 분자에 대한 컨쥬게이션에 의해, 표지 화합물 또는 프로브가 형성된다. 이 프로브에서 본 발명의 나노결정은 예를 들면 주어진 분석대상의 검출에 사용될 수 있는 전자기 스펙트럼의 가시 또는 인접 적외선 영역에서, 방사선을 방출하는 라벨 또는 태그로서 역할을 한다.The present invention further refers to nanocrystals conjugated to molecules having binding affinity for a given analyte, as described herein. Conjugation to molecules having binding affinity for a given analyte results in the formation of a labeling compound or probe. In this probe, the nanocrystals of the present invention serve as labels or tags that emit radiation, for example in the visible or adjacent infrared region of the electromagnetic spectrum, which can be used for detection of a given analyte.
원칙적으로 모든 분석대상은 적어도 어느정도 특별히 상기 분석대상과 결합할 수 있는 특별한 결합 파트너가 존재하는 것에 대하여 탐지될 수 있다. 분석대상은 약품과 같은 화학 화합물(예를 들어, 아스피린 또는 리바비린(Ribavirin)), 또는 단백질과 같은 생화학분자 (예를 들면, 트로포닌에 대한 특이적 항체 또는 세포 표면 단백질) 또는 핵산 분자가 될 수 있다. 관심있는 분석대상에 대하여 결합 친화성을 갖는 (또한 분석대상 결합 파트너로서 언급되는) 적절한 분자에 결합될 때, 리바비린과 같이, 상기 결과된 프로브는 환자의 혈장에서의 약품의 레벨을 체크하기 위한 형광 면역검정법에 사용될 수 있다. 심장 근육의 손상에 대한, 그리과 따라서 일반적으로 심장 마비에 대한 표지 단백질인 트로포닌의 경우에, 항트로포닌 항체와 독창적 나노결정의 컨쥬게이션은 심장 마비의 진단에 사용될 수 있다. 독창적 나노결정과 종양에 연합된 세포 표면 단백질에 특이적인 항체와의 컨쥬게이션인 경우, 이 콘쥬게이트는 종양 진단 또는 이미징으로 사용될 수 있다. 또 다른 예는 나노결정과 스트렙타비딘(Streptavidin)의 콘쥬게이트이다(도 6 참고).In principle, all analytes can be detected at least to some extent specifically that there is a particular binding partner capable of binding with the analyte. The analyte may be a chemical compound such as a drug (eg, aspirin or ribavirin), or a biochemical molecule such as a protein (eg, a specific antibody or cell surface protein against troponin) or a nucleic acid molecule. have. When bound to the appropriate molecule with binding affinity (also referred to as the binding partner of analysis) for the analyte of interest, such as ribavirin, the resulting probes are fluorescent for checking the level of drug in the patient's plasma. It can be used in immunoassays. In the case of troponin, which is a marker protein for damage to the heart muscle and thus generally for heart failure, the conjugation of the antitroponin antibody with the original nanocrystals can be used for the diagnosis of heart failure. In the case of the conjugation of the original nanocrystals with antibodies specific for cell surface proteins associated with the tumor, the conjugates can be used for tumor diagnosis or imaging. Another example is a conjugate of nanocrystals and streptavidin (see FIG. 6).
분석대상은 또한 바이러스 입자, 염색체 또는 전세포를 포함하는, 그러나 이에 한정되지는 않는, 복합적 생물학적 구조일 수 있다. 예를 들면, 만약 상기 대상분석물 결합 파트너가 세포막에 부착되는 지질이면, 그런 지질과 연결된 본 발명의 나노결정을 포함하는 콘쥬게이트는 전세포의 검출 및 시각화로 사용될 수 있다. 세포 염색 또는 세포 이미징과 같은 목적을 위해, 가시 광선을 방출하는 나노결정이 바람직하게 사용된다. 본 개시에 따라서 분석대상 결합파트너에 컨쥬게이트된 본 발명의 나노 입자를 포함하는 표지 화합물의 사용에 의해 탐지될 분석대상은 바람직하게는 생체분자다.The analyte may also be a complex biological structure, including but not limited to viral particles, chromosomes or whole cells. For example, if the subject analyte binding partner is a lipid attached to a cell membrane, the conjugate comprising the nanocrystals of the present invention linked to such lipid can be used for detection and visualization of whole cells. For purposes such as cell staining or cell imaging, nanocrystals that emit visible light are preferably used. The analyte to be detected by the use of a labeling compound comprising a nanoparticle of the present invention conjugated to an analyte binding partner according to the present disclosure is preferably a biomolecule.
그러므로, 더 적절한 실시예에서, 분석대상에 대해 결합 친화성을 가지는 분자는 단백질, 펩티드, 면역원성 합텐의 특성를 지닌 화합물, 핵산, 탄수화물 또는 유기분자이다. 분석대상 결합 파트너로 사용된 단백질은 예를 들어 항체, 항체 조각, 리간드, 아비딘, 스트렙타비딘 또는 효소일 수 있다. 유기분자의 예는 비오틴, 디곡시게닌, 세로트로닌, 폴산 유도체(folate derivatives) 등과 같은 화합물이다. 핵산은 DNA, RNA 또는 PNA 분자, 긴 핵산뿐만 아니라10 내지 50 bp를 가진 짧은 올리고핵산염으로부터 선택될 수 있고, 그러나 이에 한정되지는 않는다.Thus, in a more suitable embodiment, the molecule having a binding affinity for the analyte is a protein, peptide, compound having the properties of an immunogenic hapten, nucleic acid, carbohydrate or organic molecule. The protein used as the binding partner of analysis can be, for example, an antibody, antibody fragment, ligand, avidin, streptavidin or an enzyme. Examples of organic molecules are compounds such as biotin, digoxigenin, serotonin, folate derivatives and the like. Nucleic acids can be selected from, but are not limited to, DNA, RNA or PNA molecules, long nucleic acids as well as short oligonucleotides having 10 to 50 bp.
생체분자의 검출용으로 사용할 때 본 발명의 나노결정은 호스트 분자의 표면 노출된 기를 통하여 결합 활성을 가지는 분자에 컨쥬게이트될 수 있다. 이 목적을 위해, 아민, 히드록실 또는 카르복실레이트 기와 같은 표면 노출된 기는 연결 제재(linking agent)와 반응될 수 있다. 여기에서 사용된 것처럼 연결 제재는 본 발명의 나노결정을 결합 친화성을 가지는 분자에 연결할 수 있는 임의의 화합물을 의미한다. 상기 분석대상 결합 파트너에 나노결정을 컨쥬게이트시키기 위해 사용될 수 있는 연결 제재의 유형의 예는 비스-말레이미드 가교제, 디설피드 교환 가교제 및 비스-N-히드록시석신이미드 에스테르 가교제와 같은 이중 기능기의 연결 제재이다. 적절한 연결 제재의 예는 N,N’-1,4-페닐렌디말레이미드, 비스말레이미도에탄, 디티오비스-말레이미도에탄, 1,11-비스-말레이미도테트라에틸렌글리콜, C-6 비스 디설피드, C-9 비스 디설피드, 디석신이미딜 글루타레이트, 디석신이미딜 수버레이트, 에틸렌글리콜 비스-(석신이미딜석시네이트)이다. 그러나, 만약 수용성 호스트 분자에 공유결합적으로 연결된 캡핑제를 포함하는 본 발명의 나노결정이 사용되면, 상기 호스트 분자는 원하는 결합 친화성을 갖는 선택된 분자와 결합된 (전 또는 후에 호스트 게스트 복합체를 형성할 수 있는) 적합한 연결 제재와 같이 컨쥬게이트를 형성할 수 있다. 예를 들면, 만약 시클로덱스트린이 호스트 분자로 사용되면, 연결 제재는 관심있는 분자와 공유결합을 형성하기 위하여 적합한 반응기를 갖는 페로센 유도체, 아다만탄 화합물, 폴리옥시에틸렌 화합물, 아로마틱 화합물을 포함하나 이에 한정되지는 않는다. (참고. 도 6).When used for the detection of biomolecules, the nanocrystals of the present invention may be conjugated to molecules having binding activity through surface exposed groups of the host molecule. For this purpose, surface exposed groups such as amine, hydroxyl or carboxylate groups can be reacted with a linking agent. As used herein, linking agent means any compound capable of linking the nanocrystals of the present invention to a molecule having a binding affinity. Examples of the types of linking agents that can be used to conjugate nanocrystals to the binding partner of interest are bifunctional groups such as bis-maleimide crosslinkers, disulfide exchange crosslinkers and bis-N-hydroxysuccinimide ester crosslinkers. Is a sanction of connection. Examples of suitable linking agents include N, N'-1,4-phenylenedimaleimide, bismaleimidoethane, dithiobis-maleimidoethane, 1,11-bis-maleimidotetraethylene glycol, C-6 bis disulfide , C-9 bis disulfide, disuccinimidyl glutarate, disuccinimidyl suverate, ethylene glycol bis- (succinimidyl succinate). However, if a nanocrystal of the present invention comprising a capping agent covalently linked to a water soluble host molecule is used, the host molecule forms a host guest complex (before or after) with a selected molecule having the desired binding affinity. Conjugates may be formed as appropriate linking agents. For example, if cyclodextrin is used as the host molecule, linking agents include, but are not limited to, ferrocene derivatives, adamantane compounds, polyoxyethylene compounds, aromatic compounds having suitable reactors to form covalent bonds with the molecule of interest It is not limited. (See Fig. 6).
또한, 본 발명은 여기에서 기술된 수용성 나노결정의 적어도 일 유형을 포함하는 조성물에 관한 것이다. 상기 나노결정은 플라스틱 비드, 자기성 비드 또는 라텍스 비드에 통합될 수 있다. 게다가, 여기서 기술된 나노결정을 포함하는 탐지 키트 또한 본 발명의 일부이다.The invention also relates to a composition comprising at least one type of water soluble nanocrystals described herein. The nanocrystals can be incorporated into plastic beads, magnetic beads or latex beads. In addition, detection kits comprising the nanocrystals described herein are also part of the present invention.
본 발명은 다음의 비제한적인 실시예와 첨부 도면에 의해 더 예시되며, 여기서:The invention is further illustrated by the following non-limiting examples and accompanying figures, wherein:
도 1은 시클로덱스트린(CD) (반응식 a)과 호스트-게스트 복합체를 형성하는 나노결정의 코어의 표면에 소수성 반응제를 부착시키거나 또는 수용성 나노결정의 수용성 호스트 분자 (반응식 b)와 공유결합적으로 연결되는 본 발명의 수용성 나노결정의 개략도이다.1 is attached to a surface of a core of nanocrystals forming a host-guest complex with cyclodextrin (CD) (Scheme a) or covalently attached to a water-soluble host molecule (Scheme b) of a water soluble nanocrystal. It is a schematic diagram of the water-soluble nanocrystal of the present invention linked to.
도 2는 시클로덱스트린 (도 2a), 시클릭폴리아민 (도 2b), 시클릭(디)펩티드 (도 2c), 칼릭스아렌 (도 2d), 크라운 에테르 (도 2e) 및 덴드리머(도 2f) 구조의 개략도이다FIG. 2 shows cyclodextrin (FIG. 2A), cyclicpolyamine (FIG. 2B), cyclic (di) peptide (FIG. 2C), carlixarene (FIG. 2D), crown ether (FIG. 2E) and dendrimer (FIG. 2F) structure. It is a schematic diagram of
도 3은 γ-시클로덱스트린의 첨가에 의해 일어나는 클로로포름(도 3a)에서 수용액으로의 TOP-캡핑된 CdSe/ZnS 코어-쉘 나노결정의 상전이를 나타낸다FIG. 3 shows the phase transition of TOP-capped CdSe / ZnS core-shell nanocrystals from chloroform (FIG. 3A) into an aqueous solution caused by the addition of γ-cyclodextrin.
도 4는 γ-시클로덱스트린과 호스트-게스트 복합체를 형성하는 CdSe/ZnS 코어-쉘 나노결정의 투과전자현미경(TEM) 사진을 나타낸다4 shows a transmission electron microscope (TEM) image of CdSe / ZnS core-shell nanocrystals forming γ-cyclodextrin and host-guest complex.
도 5는 호스트-게스트 복합체 형성 전에 초기 나노결정과 비교되는 본 발명의 CdSe/ZnS 코어-쉘 나노결정의 형광 강도를 나타낸다5 shows the fluorescence intensity of the CdSe / ZnS core-shell nanocrystals of the present invention compared to the initial nanocrystals prior to host-guest complex formation.
도 6은 γ-시클로덱스트린과 호스트-게스트 복합체를 형성하는 본 발명의 CdSe/ZnS 코어-쉘 나노결정의 광발광에 대한 pH의 효과를 나타낸다FIG. 6 shows the effect of pH on photoluminescence of CdSe / ZnS core-shell nanocrystals of the present invention to form γ-cyclodextrin and host-guest complex
도 7은 50℃에서 본 발명의 CdSe/ZnS 코어-쉘 나노결정의 열 안정성을 나타낸다7 shows the thermal stability of CdSe / ZnS core-shell nanocrystals of the present invention at 50 ° C.
도 8은 게스트-호스트 복합체를 포함하는 본 발명의 나노결정의 개략적인 제조 공정도를 나타내고, 여기서 호스트 분자는 컨쥬게이트 (도 8a)의 제조에 사용될 수 있는 자유 반응기를 가진다. 도 8은 또한 본 발명의 수용성 나노결정의 콘쥬게이트를 제조하기 위한 시클로덱스트린과 같은 호스트 분자와 호스트-게스트 복합체를 형성할 수 있는 리간드의 예(도 8b)를 보여줄 뿐 만 아니라 본 발명의 나노결정과 스트렙타비딘의 컨쥬게이트의 개략도(도 8c)를 보여준다.FIG. 8 shows a schematic process flow diagram of a nanocrystal of the present invention comprising a guest-host complex, wherein the host molecule has a free reactor that can be used for the preparation of the conjugate (FIG. 8A). 8 also shows examples of ligands capable of forming host-guest complexes with host molecules such as cyclodextrins for preparing conjugates of water soluble nanocrystals of the invention (FIG. 8B) as well as nanocrystals of the invention. A schematic of the conjugate of and streptavidin is shown (FIG. 8C).
실시예Example 1 One
TOPO 캡핑된 (CdSe)- ZnS 나노결정 (양자점, QD)의 제조Preparation of TOPO Capped (CdSe) -ZnS Nanocrystals (Quantum, QD)
트리옥틸포스핀 (TOP)/트리옥틸포스핀옥시드 (TPPO) 캡핑된CdSe 나노결정이 다음과 같이 제조되었다. TOPO(30g)는 플라스크에 놓여지고 진공(~ 1토르) 하에서, 180℃에서, 1 시간 동안 건조되었다. 플라스크는 그 다음 질소로 채워졌고 35O℃로 가열되었다. 비활성 대기 분위기의 건조박스에서 다음의 주사액이 제조되었다: CdMe2 (200 ml), 1 M TOPSe 용액 (4.0 ml) 및 TOP (16 ml). 주사액은 완전히 혼합되었고, 주사기에 충전되었고, 건조박스로부터 제거되었다.Trioctylphosphine (TOP) / trioctylphosphine oxide (TPPO) capped CdSe nanocrystals were prepared as follows. TOPO (30 g) was placed in a flask and dried for 1 hour at 180 ° C. under vacuum (˜1 Torr). The flask was then filled with nitrogen and heated to 35O < 0 > C. The following injections were prepared in a dry box in an inert atmosphere: CdMe 2 (200 ml), 1 M TOPSe solution (4.0 ml) and TOP (16 ml). Injections were mixed thoroughly, filled into syringes and removed from the dry box.
열은 반응으로부터 제거되었고 상기 반응 혼합물은 하나의 연속된 주사로 격렬히 교반되는 TOPO로 이동되었다. 가열은 반응 플라스크에 주어졌고, 온도는 점차로 260-280℃까지 상승되었다. 반응 후에, 반응 플라스크는 ~ 60℃로 냉각하도록 허용되었고, 부탄올 20 ml은 TOPO의 응고를 방지하기 위해 첨가되었다. 과량의 메탄올의 첨가는 입자가 응집하도록 한다. 상기 응집물은 원심분리에 의해 상청액에서 분리되었다 결과적으로 생성된 분말은 광학적으로 깨끗한 용액을 생산하기 위하여 다양한 유기 용매류에서 분산될 수 있다.Heat was removed from the reaction and the reaction mixture was transferred to TOPO which was vigorously stirred in one successive scan. Heating was given to the reaction flask and the temperature was gradually raised to 260-280 ° C. After the reaction, the reaction flask was allowed to cool to ˜60 ° C. and 20 ml of butanol was added to prevent solidification of the TOPO. The addition of excess methanol causes the particles to aggregate. The aggregates were separated from the supernatant by centrifugation. The resulting powder can be dispersed in a variety of organic solvents to produce an optically clear solution.
TOPO 5g을 포함하는 플라스크는 190℃, 진공하에서, 수시간 동안 가열후 냉각되었고, 그 다음에 0.5 ml 트리옥틸포스핀 (TOP)이 추가되었다. 헥산에 분산된 대략 0.1-0.4μ몰의 CdSe 양자점은 주사기를 통하여 반응기로 이송되었고 상기 용매는 펌핑으로 제거되었다. 디에틸 징크 (ZnEt2) 및 헥사메틸디실라티안 ((TMS)2S)는 각각 Zn과 S의 전구체로서 사용되었다. 상기 전구체의 당량은 불활성 대기 분위기의 글러브 박스 안에서 2-4 ml TOP에 용해되었다. 전구체 용액은 주사기에 충전 되었고 반응 플라스크에 붙어 있는 부가적인 깔때기로 옮겨졌다. 상기 첨가가 완료된 후에, 상기 혼합물은 90℃로 냉각되었고 수시간 동안 교반되었다. 부탄올은 상온으로 냉각하면서 TOPO가 고형화하는 것을 막기 위해 혼합물에 첨가되었다.The flask containing 5 g of TOPO was cooled after heating for several hours at 190 ° C. under vacuum, followed by the addition of 0.5 ml trioctylphosphine (TOP). Approximately 0.1-0.4 μmol of CdSe quantum dots dispersed in hexanes were transferred to the reactor through a syringe and the solvent was removed by pumping. Diethyl zinc (ZnEt 2 ) and hexamethyldisilatiane ((TMS) 2 S) were used as precursors of Zn and S, respectively. The equivalent of the precursor was dissolved in 2-4 ml TOP in a glove box in an inert atmosphere. The precursor solution was filled into a syringe and transferred to an additional funnel attached to the reaction flask. After the addition was complete, the mixture was cooled to 90 ° C. and stirred for several hours. Butanol was added to the mixture to prevent TOPO from solidifying while cooling to room temperature.
실시예Example 2 2
γ-시클로덱스트린과의 호스트-게스트 복합체 형성에 의한 수용성 나노결정의 제조Preparation of Water-Soluble Nanocrystals by Host-Guest Complex Formation with γ-cyclodextrin
TOP/TOPO로 캡핑된 소수성을 가진 실시예 1에서 얻은 나노결정은 200μl의 클로로포름/헥산 (1:1) 혼합물에 용해되었다. 약 0.5 g의 γ-시클로덱스트린과 나노결정 용액이 20 ml 탈이온수의 용액에 첨가되었다. 상기 혼합물은 흐린 용액이 형성될 때까지 약 8 시간동안 환류되었다. 회전식 증발기는 대부분의 물을 제거하기 위해 사용되었고, 상기 형성된 호스트-게스트 내포 복합체는 원심분리기로 분리되었다. 얻어진 고체는 자유 시클로덱스트린 분자를 제거하기 위하여 물로 세척되었다. TOP/TOPO를 통하여 시클로덱스트린과 호스트-게스트 복합체를 형성하는, 그렇게 얻어진 나노결정은 고체상으로 저장되었다. 그들은 초음파의 처리에 의하여 물에 그들을 녹임으로써 쉽게 물로 이동될 수 있다. 호스트-게스트 복합체에 의하여 보호되는 나노결정은 상대적으로 장 시간 동안 고체 상태에서 안정적임이 밝혀졌다. The nanocrystals obtained in Example 1 with hydrophobicity capped with TOP / TOPO were dissolved in 200 μl of chloroform / hexane (1: 1) mixture. About 0.5 g of γ-cyclodextrin and nanocrystal solution were added to a solution of 20 ml deionized water. The mixture was refluxed for about 8 hours until a cloudy solution formed. Rotary evaporators were used to remove most of the water, and the host-guest inclusion complexes formed were separated by centrifugation. The solid obtained was washed with water to remove free cyclodextrin molecules. The nanocrystals thus obtained, which form a cyclodextrin and host-guest complex via TOP / TOPO, were stored in the solid phase. They can be easily transferred to water by dissolving them in water by the treatment of ultrasound. Nanocrystals protected by the host-guest complex have been found to be stable in the solid state for a relatively long time.
호스트-게스트 복합체의 형성에 의한 수용성 γ-CD 개질 양자점의 형성은 광학적으로 따라질 수 있다. TOP/TOPO-캡핑된 CdSe/ZnS코어 쉘-나노결정을 포함하는 클로로포름 용액에 Y-시클로덱스트린을 첨가할 때, 상기 형성된 나노결정은 유기 클 로로포름 상(도 3a)에서 수용액(도 3b)으로 이동했다. Formation of water-soluble γ-CD modified quantum dots by formation of host-guest complexes can be optically followed. When Y-cyclodextrin is added to a chloroform solution containing TOP / TOPO-capped CdSe / ZnS core shell-nanocrystals, the formed nanocrystals are transferred from an organic chloroform phase (Figure 3a) to an aqueous solution (Figure 3b). Moved.
γ -CD 개질 양자점의 형성은 또한 1H-NMR, FT-IR 스펙트로스카피 및 X-선회절(XRD) 측정(데이타 미도시)에서 확인되었다. 투과 전자 현미경 사진 (TEM) (도 4)과 형광 이미지 (예를 들어 도 5)는 γ시클로덱스트린을 가지고 호스트-게스트 복합체를 형성하는 양자점이 높은 균일-분산 입자를 형성한다는 것을 보여준다. 도 5는 개질되지 않은 TOP/TOPO-캐핑된 코어 쉘 나노결정(클로로포름에서 측정된)보다 호스트-복합체(물속에서 측정된)의 형성 후에 본 발명의 CdSe/ZnS 코어-쉘 나노결정이 보다 높은 형광강도를 갖는 것을 부가적으로 보여준다 반면에, 방출최대파장은 변화없었다. 도 6의 광발광 측정은 γ-시클로덱스트린으로 호스트 게스트-복합체를 형성하는 CdSe/ZnS 코어-쉘 나노결정이 pH7.4의 PBS 버퍼(개방원) (즉, 생리학의 조건 하)에서 매우 안정적이고, 심지어 pH5.0(정삼각형) 및 pH 3.0(역삼각형)의 수용액에서 각각 만족스런운 안정성을 보여준다. 마지막으로, 도 7은 γ-시클로덱스트린으로 호스트-게스트 복합체를 형성한 후에 CdSe/ZnS 코어-쉘 나노결정이 5O℃로 가열될 때 수용액에서 우수한 열 안정성을 보임을 예시한다.Formation of γ-CD modified quantum dots was also confirmed in 1 H-NMR, FT-IR spectroscopy and X-ray diffraction (XRD) measurements (data not shown). Transmission electron micrographs (TEM) (FIG. 4) and fluorescence images (eg FIG. 5) show that the quantum dots forming the host-guest complex with γcyclodextrin form high homogeneously-dispersed particles. 5 shows higher fluorescence of CdSe / ZnS core-shell nanocrystals of the present invention after formation of host-composite (measured in water) than unmodified TOP / TOPO-capped core shell nanocrystals (measured in chloroform). On the other hand, the maximum emission wavelength was not changed. The photoluminescence measurement of FIG. 6 shows that CdSe / ZnS core-shell nanocrystals forming host guest-complexes with γ-cyclodextrin are very stable in PBS buffer (open source) at pH 7.4 (ie under physiological conditions). And even satisfactory stability in aqueous solutions of pH 5.0 (forward triangle) and pH 3.0 (inverted triangle) respectively. Finally, Figure 7 illustrates that after forming the host-guest complex with γ-cyclodextrin, the CdSe / ZnS core-shell nanocrystals show good thermal stability in aqueous solution when heated to 50O < 0 > C.
실시예Example 3 3
β-시클로덱스트린 모노알킬티올(옥탄티올)의 제조Preparation of β-cyclodextrin monoalkylthiol (octane thiol)
LiH (5 mmol)가 건조된 THF (50 ml)의 건조된 터트-부틸디메틸실릴(TBDMS)-보호된 시클로덱스트린(TBDMSCD) (2.2 mmol)의 용액에 첨가되었고, 약 3시간동안 환류되었다. 그 후에 트리페닐 메탄올 보호된 8-브로모-1-옥탄티올(4 mmol)을 첨 가했고 밤새 환류시켰다. 용매는 진공에서 제거되었고 잔류물은 클로로포름에서 용해되었다. 상기 용액은 희석된 HCI 용액으로 세척되었고, 소금물로 세척되었고, 그리고 건조되었다. 정제는 실리카(200-400 메쉬) 컬럼 크로마토그래피에 의해 실시되었다. 얻어진 고체는 TFA(10 ml)에 용해되었다. 상기 용액이 무색이 되었을 때, 감소된 압력하에서 잔류한 산의 무색인 자취와 가공하지 않은 반응 생성물이 물에 용해되었다. 정제를 위해, 상기 시클로덱스트린 옥탄티올은 미반응물질을 제거하기 위하여 디에틸 에테르로 세척되었다. 냉동진공건조 후, 생성물은 21%의 수율의 파우더로서 얻어졌다. 1HNMR (D2O, δ, ppm): 5.1, 3.9 - 3.2, 2.4, 1.5 - 1.0.LiH (5 mmol) was added to a solution of dried THF (50 ml) of dried tert-butyldimethylsilyl (TBDMS) -protected cyclodextrin (TBDMSCD) (2.2 mmol) and refluxed for about 3 hours. Triphenyl methanol protected 8-bromo-1-octanethiol (4 mmol) was then added and refluxed overnight. The solvent was removed in vacuo and the residue dissolved in chloroform. The solution was washed with diluted HCI solution, washed with brine, and dried. Purification was carried out by silica (200-400 mesh) column chromatography. The solid obtained was dissolved in TFA (10 ml). When the solution became colorless, the colorless trace of the acid remaining under reduced pressure and the crude reaction product dissolved in water. For purification, the cyclodextrin octathiol was washed with diethyl ether to remove unreacted material. After freeze drying, the product was obtained as a powder in a yield of 21%. 1 HNMR (D 2 O, δ, ppm): 5.1, 3.9-3.2, 2.4, 1.5-1.0.
실시예Example 4 4
시클로덱스트린 모노알킬티올로서 리간드 교환에 의한 수용성 양자점의 제조Preparation of Water-Soluble Quantum Dots by Ligand Exchange as Cyclodextrin Monoalkylthiols
Zhong et al., J. Am. Chem. Soc. 125, 8589, 2003에서 기술된 것처럼 상기 TOP/TOPO 캡핑된 양자점의 정제는 양자점을 클로로포름에 용해시킴에 의해 행해졌고 아세톤과 메탄올로부터 침전되었다. 상기 얻어진 양자점은 깨끗한 용액을 형성하기 위하여 건조된 클로로포름에서 용해되었다. 교반 하에서, 실시예 3에서 제조된 과량의 시클로덱스트린 모노알칼티올은 부분적으로 첨가되었다. 매번, 시클로덱스트린 모노알칼티올 (옥탄티올)은 상기 용액이 깨끗하게 될 때까지 첨가되었다. 첨가가 완료된 후, 상기 반응 혼합물은 밤새 실온에서 계속 교반되었다. 용매는 진공하에서 제거되었고 상기 얻어진 고체는 자유 시클로덱스트린 모노알킬티올을 제거하기 위하여 디에틸 에테르로 세척되었다. 결과로서 얻어진 분말은 수집되었고, 순수한 수용액으로부터 원심분리에 의해 더 정제되었다. 냉동진공건조 후, 상기 생성물은 수집되었고, 1HNMR에 의해 특정되었다. 1HNMR (D2O,δ, ppm ) : 5.1, 4.1-3.2, 2.3, 1.5-1.0, 0.9-0.8.Zhong et al., J. Am. Chem. Soc. Purification of the TOP / TOPO capped quantum dots as described in 125, 8589, 2003 was done by dissolving the quantum dots in chloroform and precipitated from acetone and methanol. The obtained quantum dots were dissolved in dried chloroform to form a clear solution. Under stirring, the excess cyclodextrin monoalkalthiol prepared in Example 3 was partially added. Each time cyclodextrin monoalkalthiol (octanethiol) was added until the solution was cleared. After the addition was complete, the reaction mixture was continued to stir overnight at room temperature. The solvent was removed under vacuum and the solid obtained was washed with diethyl ether to remove free cyclodextrin monoalkylthiol. The resulting powder was collected and further purified by centrifugation from pure aqueous solution. After freeze drying, the product was collected and characterized by 1 HNMR. 1 HNMR (D 2 O, δ, ppm): 5.1, 4.1-3.2, 2.3, 1.5-1.0, 0.9-0.8.
실시예Example 5 5
6-티오-β-시클로덱스트린의 제조Preparation of 6-thio-β-cyclodextrin
퍼-6-이오도-β-시클로덱스트린(1 g)은 DMF (10 ml)에 용해되었다 티오요소(0.301 g)가 첨가되었고 상기 반응 혼합물이 질소 분위기 하에서 70℃로 가열되었다. 19 시간 뒤에, 디메틸포름아미드(DMF)는 노란색 기름을 제공하기 위하여 감압하에서 제거되었으며, 그것은 물(50 ml)에서 용해되었다. 수산화나트륨(0.26 g)이 추가되었고 상기 반응 혼합물이 질소 분위기 하에서 완만한 환류로 가열되었다. 1 시간 뒤에, 결과로서 얻어진 현탁액은 수용성 KHSO4로 산성화되었고, 상기 결과로서 얻어진 침전물은 여과되었고, 증류수로 완전히 세척되었고, 건조되었다. DMF의 마지막 잔류물을 제거하기 위해, 상기 생성물은 물 (50 mL)에 현탁되었고 깨끗한 용액을 부여하기 위해 최소량의 수산화칼륨이 첨가되었다 그 다음에 상기 생성물은 수용성 KHSO4로서 산성화함으로써 재침전되었다. 결과로서 얻은 미세한 침전물은 조심스럽게 여과되었고 연회색 분말의 퍼-6-티오-시클로덱스트린 (65%)을 P2O5로 진공에서 건조하여 얻었다. 1H NMR (DMSO, δ, ppm) 2.16, 2.79,3.21, 3.36- 3.40, 3.60, 3.68, 4.95, 5.83, 5.97.Per-6-iodo-β-cyclodextrin (1 g) was dissolved in DMF (10 ml) Thiourea (0.301 g) was added and the reaction mixture was heated to 70 ° C. under a nitrogen atmosphere. After 19 hours, dimethylformamide (DMF) was removed under reduced pressure to give a yellow oil, which was dissolved in water (50 ml). Sodium hydroxide (0.26 g) was added and the reaction mixture was heated to gentle reflux under a nitrogen atmosphere. After 1 hour, the resulting suspension was acidified with aqueous KHSO 4 and the resulting precipitate was filtered, washed thoroughly with distilled water and dried. To remove the last residue of DMF, the product was suspended in water (50 mL) and a minimum amount of potassium hydroxide was added to give a clean solution. The product was then reprecipitated by acidifying with aqueous KHSO 4 . The resulting fine precipitate was carefully filtered and obtained by drying the light gray powder of per-6-thio-cyclodextrin (65%) in vacuo with P 2 O 5 . 1 H NMR (DMSO, δ, ppm) 2.16, 2.79, 3.21, 3.36-3.40, 3.60, 3.68, 4.95, 5.83, 5.97.
실시예Example 6 6
6-티오-β-시클로덱스트린에 의해 캡핑된 수용성 양자점의 제조Preparation of Water-Soluble Quantum Dots Capped by 6-thio-β-cyclodextrin
TOP/TOPO 캡핑된 양자점의 정제는 실시예 2와 4에서 기술된 절차와 유사하다. 상기 얻어진 양자점은 투명한 용액을 형성하기 위하여 건조된 피리딘에 용해되었다. 교반 하에서, 6-티오-β시클로덱스트린이 첨가되었다. 10분 후, 상기 반응은 투명하게 되었다. 교반은 밤새 실온에서 계속되었다. 대부분의 용매는 제거되었고 그리고 나서 50 ml 디에틸 에테르가 첨가되었다. 백색 분말이 수집되었고 이에틸에테르로 다시 행구어졌다. 얻어진 분말은 여과되었고 건조되었다. 1HNMR (DMSO, δ, ppm): 5.8, 5.1, 4.1-3.2, 2.6, 2.2, 1.5-1.0.Purification of TOP / TOPO capped quantum dots is similar to the procedure described in Examples 2 and 4. The obtained quantum dots were dissolved in dried pyridine to form a clear solution. Under stirring, 6-thio-βcyclodextrin was added. After 10 minutes, the reaction became clear. Stirring continued at room temperature overnight. Most of the solvent was removed and then 50 ml diethyl ether was added. White powder was collected and rinsed again with diethyl ether. The powder obtained was filtered and dried. 1 HNMR (DMSO, δ, ppm): 5.8, 5.1, 4.1-3.2, 2.6, 2.2, 1.5-1.0.
실시예Example 7 7
본 발명의 나노결정을 포함하는 컨쥬게이트의 제조Preparation of Conjugates Containing Nanocrystals of the Invention
도 8a는 적절한 호스트 분자와 캡핑제의 호스트-게스트 복합체를 포함하는 본 발명의 나노결정을 제조하기 위한 반응식을 보여준다.8A shows a scheme for preparing a nanocrystal of the present invention comprising a host-guest complex of a suitable host molecule and a capping agent.
상술한 바와 같이, 상기 나노결정의 표면에 부착되는 적합한 캡핑제는 긴 알킬 사슬 또는 폴리옥시알킬 사슬을 가진 티올 화합물일 수 있다. 그러한 캡핑된 나노결정이 수용성 나노결정을 매우 안정하게 이끄는 시클로덱스트린과 같은 호스트 분자와 반응될 수 있다. 진단 도구로 사용될 수 있는 나노결정의 컨쥬게이트의 제조를 위해 그런 호스트 분자는 단지 몇몇개의 실시예를 들면, 비오틴, 디곡시게닌, 작은 분자 약품과 같은 관심있는 리간드 또는 스트렙타비딘, 아비딘 또는 항체와 같은 단백질과 컨쥬게이트될 수 있다.As mentioned above, suitable capping agents attached to the surface of the nanocrystals may be thiol compounds with long alkyl chains or polyoxyalkyl chains. Such capped nanocrystals can be reacted with a host molecule such as cyclodextrin, which leads to a very stable water soluble nanocrystal. For the preparation of conjugates of nanocrystals that can be used as diagnostic tools such host molecules may be used only with a few embodiments, for example ligands of interest such as biotin, digoxigenin, small molecule drugs or streptavidin, avidin or antibodies. It can be conjugated with the same protein.
상기 콘쥬게이트가 용매노출 친수성 기(예를 들어, -OH, COOH 또는 NH2기)와 같은 자유 반응성 기를 상기 관심있는 리간드(도 8a참고)와 반응함에 의해 제조될 수 있다. 상기 콘쥬게이트는 상기 게스트 분자와 상기 관심있는 리간드와 연결되는 적합한 호스트 분자 사이에 호스트-게스트 복합체를 하나 더 형성함에 의하여 또한 제조될 수 있다. 예를 들어, 시클로덱스트린 화합물과 그러한 (제2의) 호스트-게스트 복합체를 형성함에 사용할 수 있는 예시적인 호스트 분자는 도 8b에 도시되었다. 이점에서 상기 선택된 호스트 분자에 대해 적절한 게스트를 선택하는 것이 당 분야의 통상의 지식을 가진 자의 지식내에 포함됨을 알 수 있다. 호스트-게스트 복합체를 통하여 본 발명의 나노결정의 콘쥬게이트를 형성하는 이 방법은 도 8c에 도시된 스트렙타비딘 컨쥬게이트에 의해 예시된다.The conjugate can be prepared by reacting a free reactive group such as a solvent exposed hydrophilic group (eg, -OH, COOH or NH 2 group) with the ligand of interest (see FIG. 8A). The conjugate may also be prepared by forming one more host-guest complex between the guest molecule and a suitable host molecule linked with the ligand of interest. For example, exemplary host molecules that can be used to form cyclodextrin compounds and such (secondary) host-guest complexes are shown in FIG. 8B. It can be seen from this that the selection of an appropriate guest for the selected host molecule is within the knowledge of one of ordinary skill in the art. This method of forming the conjugate of the nanocrystals of the present invention via a host-guest complex is illustrated by the streptavidin conjugate shown in FIG. 8C.
Claims (71)