KR101032880B1 - Composition of lacquer remover - Google Patents

Composition of lacquer remover Download PDF

Info

Publication number
KR101032880B1
KR101032880B1 KR1020100081211A KR20100081211A KR101032880B1 KR 101032880 B1 KR101032880 B1 KR 101032880B1 KR 1020100081211 A KR1020100081211 A KR 1020100081211A KR 20100081211 A KR20100081211 A KR 20100081211A KR 101032880 B1 KR101032880 B1 KR 101032880B1
Authority
KR
South Korea
Prior art keywords
lacquer
weight
composition
spray
dipropylene glycol
Prior art date
Application number
KR1020100081211A
Other languages
Korean (ko)
Inventor
유영옥
Original Assignee
주식회사 신도디앤텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 신도디앤텍 filed Critical 주식회사 신도디앤텍
Priority to KR1020100081211A priority Critical patent/KR101032880B1/en
Application granted granted Critical
Publication of KR101032880B1 publication Critical patent/KR101032880B1/en

Abstract

PURPOSE: A lacquer removal agent composition is provided to effectively remove the scribbling written by lacquer or oily spray while not damaging a coating surface when removing the scribbling lacquer or oily spray repainted on 2 liquid type hardened paint. CONSTITUTION: A lacquer removal agent composition comprises 65-95 weight% of dipropylene glycol monomethyl ether and 5-35 weight% of xylene, preferably, 91 weight% of dipropylene glycol methyl ether and 9 weight% of xylene in an excellent component ratio which does not damage a base surface and melts lacquer spray or oily magic pen ink. The lacquer removal agent composition includes 62-92 weight% dipropylene glycol methyl ether, and 7-33 weight% xylene and 1-5 weight% flavor additive.

Description

래커 제거제의 조성물{Composition of lacquer remover}Composition of lacquer remover [

본 발명은 래커스프레이나 유성낙서를 제거하기 위한 조성물에 관한 것으로, 더욱 상세하게는 2액형 경화도료의 바탕면 도막을 손상시키지 않으면서도 래커스프레이나 유성낙서를 선택적으로 제거할 수 있을 뿐만 아니라 특히, 작업자의 건강에 해를 끼칠 수 있는 톨루엔 등의 솔벤트가 포함되어 있지 않아 유해성이 낮으며, 화재 위험성도 낮은 래커 제거제의 조성물에 관한 것이다.The present invention relates to a composition for removing lacquer spray or oily graffiti, and more particularly, to a composition for removing lacquer spray or oily graffiti without damaging a base coat of a two-pack type cured paint, The present invention relates to a composition of a lacquer removing agent which is low in hazard and low in fire risk because it does not contain a solvent such as toluene which may harm the health of a worker.

일반적으로 래커스프레이나 유성도료는 호의(好意)의 목적 이외에도 자신의 뜻과 위배 되는 광고물에 덧칠을 하거나 장난삼아 타인의 광고물에 낙서를 하는 일이 종종 발생한다.In general, lacquer spray or oil paint is often used to paint on advertisements that violate their will, or to cheat on others' advertisements, in addition to favorable purposes.

한편, 고가의 광고물 등에 행해진 이러한 낙서를 제거하기 위하여 다양한 용제들의 혼합물로 구성되고 반응성이 매우 높은 래커시너(Lacquer thinner)가 주로 사용되고 있는데, 이러한 래커시너는 래커스프레이나 유성도료의 낙서 이외에도 2액형 경화도료의 경우 바탕면의 도막까지도 제거함으로써 광고물을 훼손하는 문제점이 발생하고 있다. On the other hand, a lacquer thinner which is composed of a mixture of various solvents and has high reactivity is mainly used in order to remove such graffiti which is performed on expensive advertisements and the like. In addition to the graffiti of lacquer spray or oil paint, In the case of a cured paint, there is a problem of removing the coating film on the base surface, thereby damaging the advertisement.

특히, 상기 래커시너는 인체에 위험성이 높은 톨루엔(Toluene)이나 장기간 노출시 인체에 위험을 미치는 부틸 셀로솔브(Butyl Cellosolve) 등의 유독성 용제들이 포함되어 있어 낙서를 제거하는 작업자의 건강을 해칠 수 있는 단점이 있다. Particularly, since the lacquerin contains toxic solvents such as toluene, which is highly dangerous to human body, and butyl cellosolve, which is dangerous to human body during long-term exposure, There are disadvantages.

따라서, 바탕면의 도막을 훼손하지 않으면서 낙서만 선택적으로 제거하고, 작업자에게 유해성이 낮은 래커 제거제가 절실히 요구되고 있는 실정이다.Therefore, a lacquer removing agent which is selectively removed from the graffiti without damaging the coating film on the base surface and which is low in harmfulness to the operator is in desperate need.

본 발명은 상기와 같은 문제점을 해소하기 위하여 안출 된 것으로서, 본 발명의 첫 번째 목적은, 바탕면의 도장면을 훼손하지 않으면서도 선택적으로 낙서만을 제거하는 래커 제거제의 조성물을 제공하는 데 있다. SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and it is a first object of the present invention to provide a composition of a lacquer removing agent which selectively removes graffiti without damaging the coated surface of the base.

또한, 본 발명의 두 번째 목적은, 래커스프레이나 유성도료의 낙서 제거 작업을 하는 작업자의 건강을 고려하여 인체에 유해성이 낮은 래커 제거제의 조성물을 제공하는 데 있으며, 나아가, 종래의 광고물 부착방지 시트에 덧칠해진 래커스프레이나 유성도료의 낙서를 광고물 부착방지 시트제품을 훼손하지 않으면서도 낙서만을 선택적으로 제거할 수 있는 조성물을 제공하는 데 있다.A second object of the present invention is to provide a composition of a lacquer removing agent which is low in harmfulness to human body in consideration of the health of a worker who performs a lacquer spray or a grainy paint removing work. Further, It is an object of the present invention to provide a composition capable of selectively removing graffiti even without damaging the adhering water adhesion preventing sheet product by lacquer spray or greasy paint applied on the sheet.

상기와 같은 목적에 따른 본 발명의 래커 제거제의 조성물은 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 65 내지 95중량%와 자일렌(Xylene) 5 내지 35중량%의 혼합물로 구성되는 것에 의해 달성된다.The composition of the lacquer removing agent of the present invention according to the above object is composed of a mixture of 65 to 95% by weight of dipropylene glycol monomethyl ether (DPGME) and 5 to 35% by weight of xylene .

또한, 작업환경의 개선까지 고려한 구성으로서, 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 62 내지 92중량%, 자일렌(Xylene) 7 내지 33중량%, 향 첨가물 1 내지 5중량%로 구성되는 것에 의해 달성된다.Further, it is preferable that 62 to 92% by weight of dipropylene glycol monomethyl ether (DPGME), 7 to 33% by weight of xylene, and 1 to 5% by weight of fragrance additive ≪ / RTI >

이상에서 살펴본 바와 같이, 본 발명에 의한 래커 제거제의 조성물은 래커나 유성 스프레이로 인한 낙서를 효과적으로 제거할 수 있으며, 특히, 2액형 경화도료 상에 덧칠된 래커나 유성 낙서 제거시 바탕면의 도장면을 손상시키지 않으면서 낙서만 선택적으로 제거하는 장점이 있다.As described above, the composition of the lacquer removing agent according to the present invention can effectively remove the graffiti due to lacquer or oily spray, and in particular, it is possible to remove the painted surface of the base surface There is an advantage that only graffiti can be selectively removed without damaging it.

또한, 본 발명에 의한 래커제의 조성물은 작업자의 건강에 해를 끼칠 수 있는 톨루엔(Toluene)이나 부틸 셀로솔브(Butyl Cellosolve)가 전혀 포함되어 있지 않아 유해성이 낮으며, 화재 위험성도 낮다.In addition, the composition of the lacquer according to the present invention does not contain any toluene or butyl cellosolve which may harm the health of workers, and thus has low harmfulness and low fire risk.

나아가, 광고물 부착 방지시트 및 광고물 부착 방지도료에 덧칠된 래커나 유성 낙서를 선택적으로 제거할 수 있는 매우 유용한 발명이다.Further, it is a very useful invention that can selectively remove the lacquer and oily graffiti that are applied to the advertisement water adhesion preventive sheet and the advertisement water adhesion preventive paint.

도 1a 내지 도 1h는 본 발명의 실시예에 의한 래커 제거제의 조성물 및 종래 래커 제거제의 성능실험 비교사진.
도 2a 내지 도 2h는 본 발명의 실시예에 의한 래커 제거제의 조성물 및 종래 래커 제거제의 2액형 경화도료 상의 낙서 제거에 대한 바탕면 훼손 정도를 나타내는 비교 사진
도 3a 내지 도 3d는 광고물 부착방지 시트 상의 래커 스프레이 및 유성도료에 대해 본 발명에 의한 래커 제거제 조성물을 실시한 전과 후의 성능실험 비교사진
도 4는 한국화학융합시험연구원(KTR)에 의뢰한 본 발명의 래커 제거제 조성물의 중금속 분석결과 데이터FIGS. 1A to 1H are comparative photographs of a performance test of a composition of a lacquer removing agent and a conventional lacquer removing agent according to an embodiment of the present invention.
FIGS. 2A to 2H are comparative photographs showing the degree of substrate surface damage to the removal of graffiti on a two-pack type curing paint of a composition of a lacquer removing agent and a conventional lacquer removing agent according to an embodiment of the present invention
3A to 3D are graphs showing a comparison of performance test before and after the lacquer removing composition according to the present invention for a lacquer spray and a oil-based paint on an anti-adherence sheet
4 is a graph showing the results of heavy metal analysis of the lacquer removing composition of the present invention commissioned by the Korean Chemical Fusion Test Institute (KTR)

상기 목적을 달성하기 위하여, 본 발명은,In order to achieve the above object,

디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 65 내지 95중량%, 자일렌(Xylene) 5 내지 35중량%로 구성되는 조성물을 제공한다.65 to 95% by weight of dipropylene glycol monomethyl ether (DPGME), and 5 to 35% by weight of xylene.

이하, 본 발명을 상세하게 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail.

본 발명에 사용되는 디프로필렌 글리콜 메틸에테르(DPGME)는 주용매로서 휘발도가 낮은 휘발성 용매이다.The dipropylene glycol methyl ether (DPGME) used in the present invention is a volatile solvent having low volatility as a main solvent.

상기 디프로필렌 글리콜 메틸에테르(DPGME)의 색상은 무채색으로서, 물리적으로는 액체상태이며, 달콤한 냄새가 난다.The color of the dipropylene glycol methyl ether (DPGME) is achromatic, physically liquid, and has a sweet smell.

특히, 인화점이 약 86℃로서, 종래의 래커 시너에 포함된 다른 유기용제보다 화재 위험성이 낮으며, 상온 및 상압에서 안정하여 반응성이 매우 낮은 특징이 있다. Particularly, the flash point is about 86 ° C, which is lower in fire risk than other organic solvents contained in the conventional lacquer thinner, and is stable at room temperature and atmospheric pressure, and has very low reactivity.

상기 디프로필렌 글리콜 메틸에테르(DPGME)는 래커 스프레이나 유성매직 등의 유성도료를 녹여 제거하는 역할을 한다.The dipropylene glycol methyl ether (DPGME) melts and removes oil-based paints such as lacquer spray and oil-based magic.

또한, 자일렌(Xylene)은 상기 디프로필렌 글리콜 메틸에테르(DPGME)가 녹인 안료의 찌꺼기가 다시 바탕면에 들러붙지 않도록 지우는 역할을 한다.Xylene also serves to erase the residue of the pigment in which the above-mentioned dipropylene glycol methyl ether (DPGME) is dissolved so as not to adhere to the substrate again.

본 발명에 의한 래커 제거제의 조성물은 상기 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether)가 65 내지 95중량%로 구성되고 자일렌(Xylene)은 5 내지 35중량%로 구성되며, 래커 스프레이나 유성매직을 가장 잘 녹이고 바탕면을 훼손하지 않는 우수한 성분비로 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 91중량%와 자일렌(Xylene) 9중량%로 구성됨이 바람직하다.The composition of the lacquer removing agent according to the present invention comprises 65 to 95% by weight of dipropylene glycol monomethyl ether (DPGME) and 5 to 35% by weight of xylene, It is preferable that 91% by weight of dipropylene glycol monomethyl ether (DPGME) and 9% by weight of xylene are preferable as the excellent component ratio that does not deteriorate the base surface.

또한, 작업환경을 개선하기 위하여, 레몬과 같은 과일향 또는 허브향을 첨가한 구성으로서, 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether)가 62 내지 92중량%로 구성되고, 자일렌(Xylene)은 7 내지 33중량%로 구성되며, 레몬향 또는 허브향과 같은 향 첨가물이 1 내지 5중량%로 구성된다.Further, in order to improve the working environment, a composition containing 62 to 92% by weight of dipropylene glycol monomethyl ether (DPGME) as a constituent added with a fruit flavor such as lemon or a herb flavor, ) Is composed of 7 to 33% by weight, and fragrance additives such as lemon fragrance or herb fragrance comprise 1 to 5% by weight.

향 첨가물을 포함시키며, 래커 스프레이나 유성매직을 잘 녹이고, 바탕면을 훼손하지 않는 바람직한 성분비는 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 89 내지 90중량%와 자일렌(Xylene) 8 내지 9중량%, 향 첨가물이 1 내지 2중량%로 구성된다.The preferred proportions of ingredients that do not deteriorate the base surface include liquefying the lacquer spray or oily magic, and 89 to 90% by weight of dipropylene glycol monomethyl ether (DPGME) and 8 to 90% by weight of xylene, 9% by weight, and the fragrance additive is 1 to 2% by weight.

상기와 같은 본 발명에 의한 래커 제거제의 조성물은 래커나 유성 스프레이로 인한 낙서를 효과적으로 제거할 수 있다.The composition of the lacquer removing agent according to the present invention as described above can effectively remove graffiti due to lacquer or oily spray.

이를 증명하기 위한 것으로, 도 1a 내지 도 1h는 본 발명의 실시예에 의한 래커 제거제의 조성물 및 종래 래커 제거제의 성능실험 비교사진으로서, 일반 스테인리스 스틸(Stainless steel) 판(Plate)에 래커스프레이를 분사하거나, 유성도료에 의한 낙서의 제거성능을 비교하기 위한 것이다.1A to 1H are photographs showing comparative performances of a composition of a lacquer removing agent and a conventional lacquer removing agent according to an embodiment of the present invention. The lacquer spray is sprayed onto a general stainless steel plate. Or the removal performance of graffiti by the oil based paint.

특히, 도 1a와 도 1c는 각각 스테인리스 스틸(Stainless steel) 판(Plate)에 래커스프레이를 분사한 사진을 첨부한 도면이고, 도 1e와 도 1g는 각각 스테인리스 스틸 판에 유성매직으로 낙서한 사진을 첨부한 도면이다.1A and 1C are drawings each showing a spray of a lacquer spray on a stainless steel plate. FIGS. 1E and 1G are photographs of a stainless steel plate scratched with a metaphorical magic Fig.

또한, 도 1b와 도 1f는 각각 종래 래커 제거제인 래커 시너로 래커스프레이와 유성매직을 지우기 위해 래커 시너로 처리한 사진을 첨부한 도면이고, 도 1d와 도 1h는 각각 본 발명에 의한 래커 제거제의 조성물로 처리한 사진을 첨부한 도면이다.1B and 1F are photographs of lacquer thinner, which is a conventional lacquer removing agent, and lacquer thinner, respectively, in order to remove lacquer spray and oil magic. FIG. 1D and FIG. Fig. 5 is a photograph showing a photograph obtained by processing with a composition. Fig.

도 1b와 도 1d를 참조하면, 일반 스테인리스 스틸 판에 분사된 래커스프레이를 종래의 래커 시너나 본 발명에 의한 래커 제거제의 조성물로서 모두 깨끗이 지운 모습을 보이고 있다.Referring to FIGS. 1B and 1D, the lacquer spray sprayed on a general stainless steel plate is shown as a clear lacquer for both the conventional lacquer thinner and the lacquer removal composition of the present invention.

도 1f와 도 1h를 참조하면, 일반 스테인리스 스틸 판에 낙서 된 유성매직은 종래의 래커 시너나 본 발명에 의한 래커 제거제의 조성물에 의해 모두 깨끗이 지워진다.Referring to FIG. 1F and FIG. 1H, the oil-based magic grained on a general stainless steel plate is cleaned by both the conventional lacquer thinner and the composition of the lacquer removing agent according to the present invention.

도 2a 내지 도 2h는 본 발명의 실시예에 의한 래커 제거제의 조성물 및 종래 래커 제거제의 2액형 경화도료 상의 낙서 제거에 대한 바탕면 훼손 정도를 나타내는 비교 사진이다.FIGS. 2A to 2H are comparative photographs showing the degree of substrate surface deterioration with respect to removal of graffiti on a two-pack type curing paint of a composition of a lacquer removing agent and a conventional lacquer removing agent according to an embodiment of the present invention.

특히, 도 2a와 도 2c는 각각 분체도장 된 스테인리스 스틸(Stainless steel) 판(Plate)에 래커스프레이를 분사한 판에 대한 사진을 첨부한 도면이고, 도 2b는 종래 래커 제거제인 래커 시너로 처리한 사진을 첨부한 도면이며, 도 2d는 본 발명에 의한 래커 제거제의 조성물로 처리한 사진을 첨부한 도면이다.In particular, FIGS. 2A and 2C are photographs of a plate sprayed with a lacquer spray on a stainless steel plate coated with powder, respectively, and FIG. 2B is a view of a plate coated with a lacquer thinner And FIG. 2D is a view showing a photograph treated with the composition of the lacquer removing agent according to the present invention.

도 2c를 참조하면, 분체도장 된 스테인리스 스틸 판에 분사된 래커스프레이를 지우기 위해 종래 래커 제거제인 래커 시너로 처리한 스테인리스 스틸 판(Plate)은 분체도장 된 도장막이 부풀어 올라 스테인리스 스틸 판으로부터 탈리 되는 것을 확인할 수 있다.Referring to FIG. 2C, a stainless steel plate treated with a lacquer thinner, which is a conventional lacquer removing agent, is used to remove a lacquer spray sprayed on a powder coated stainless steel plate. The stainless steel plate, which has been coated with the powder, is removed from the stainless steel plate Can be confirmed.

그러나, 도 2d를 참조하면, 분체도장 된 스테인리스 스틸 판에 분사된 검정색 래커 스프레이를 지우기 위해 본 발명에 의한 래커 제거제의 조성물을 처리한 결과로서, 분체도장 된 기존 도막이 탈리 되는 등의 문제점이 발생 되지 않았으며, 래커 스프레이만이 선택적으로 제거되는 것을 확인할 수 있다.However, referring to FIG. 2d, as a result of treating the composition of the lacquer removing agent of the present invention to erase the black lacquer spray sprayed on the powder coated stainless steel plate, there arises a problem that the existing coated film with powder coating is removed , And that only the lacquer spray is selectively removed.

또한, 도 2e와 도 2g는 각각 분체도장 된 스테인리스 스틸 판에 유성매직이 낙서 된 사진을 첨부한 도면으로서, 낙서 된 유성매직을 지우기 위해 종래의 래커 시너로 처리한 사진을 첨부한 도면인 도 2f는 분체도장 된 도장막이 부풀어 올라 스테인리스 스틸 판으로부터 탈리 되었으나, 본 발명에 의한 래커 제거제의 조성물을 처리한 도 2h의 경우 기존 도막은 탈리 되지 않고 래커스프레이만 제거된 것을 확인할 수 있다.FIGS. 2E and 2G are photographs depicting oil-based magic on a powder coated stainless steel plate, respectively. FIGS. 2F and 2F, which are photographs of a conventional lacquer thinner, The coated paint film was swollen and removed from the stainless steel plate. However, in the case of FIG. 2H where the composition of the lacquer removing agent of the present invention was treated, it can be confirmed that the existing coating film was not removed but only the lacquer spray was removed.

도 3a 내지 도 3b는 광고물 부착방지 시트 상의 래커 스프레이 및 유성도료에 대해 본 발명에 의한 래커 제거제 조성물을 실시한 전과 후의 성능실험 비교사진으로서, 도 3a 및 도 3b를 참조하면, 도 3a는 광고물 부착방지 시트 상에 래커 스프레이가 분사된 사진이고, 도 3b는 본 발명에 의한 래커 제거제의 조성물로 처리한 결과를 보여 주는 사진으로서, 기존 도막은 탈리 되지 않고 래커 스프레이만 선택적으로 제거되는 것을 확인할 수 있다.3A and 3B are comparative photographs of a performance test before and after a lacquer removing composition according to the present invention for a lacquer spray and a oil-based paint on an advertisement adherence preventing sheet. Referring to FIGS. 3A and 3B, FIG. 3B is a photograph showing the result of treatment with the composition of the lacquer removing agent according to the present invention, and it was confirmed that only the lacquer spray was selectively removed without removing the existing coating film have.

또한, 도 3c와 도 3d를 참고하면, 도 3c는 광고물 부착방지 시트 상에 유성매직으로 낙서를 한 사진이고, 도 3d는 본 발명에 의한 래커 제거제의 조성물로 처리한 결과를 보여주는 사진으로서, 기존 도막은 탈리 되지 않고 유성매직만 선택적으로 제거되는 것을 확인할 수 있다.3C and 3C are photographs showing graffiti scrolling on the anti-adherence sheet, FIG. 3D is a photograph showing the result of treatment with the composition of the lacquer removing agent according to the present invention, It can be confirmed that only the oily magic is selectively removed without removing the existing coating film.

도 4는 한국화학융합시험연구원(KTR)에 의뢰한 본 발명의 래커 제거제 조성물의 중금속 분석결과 데이터로서, 도 4를 참고하면, 본 발명에 의한 래커 제거제의 조성물에는 인체에 해로운 중금속이 포함되어 있지 않음을 알 수 있다.FIG. 4 is a result of heavy metal analysis of the lacquer removing composition of the present invention commissioned by the Korean Chemical Fusion Test Institute (KTR). Referring to FIG. 4, the composition of the lacquer removing composition of the present invention contains heavy metals .

특히, 도 1a 내지 도 4의 실험에 사용한 본 발명의 래커 제거제의 조성물은 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 90중량%, 자일렌(Xylene) 9중량%, 향 첨가물 1중량%의 조성비로 구성되는 조성물을 사용하였다.Specifically, the composition of the lacquer removing agent of the present invention used in the experiments of FIGS. 1A to 4 was prepared by mixing 90 wt% of dipropylene glycol monomethyl ether (DPGME), 9 wt% of xylene, 1 wt% Of the composition was used.

실험결과를 보여주는 도 1a 내지 도 4에서 알 수 있듯이, 본 발명에 의한 래커 제거제의 조성물에는 작업자의 건강에 해를 끼칠 수 있는 톨루엔(Toluene)이나 부틸 셀로솔브(Butyl Cellosolve)가 전혀 포함되어 있지 않아 유해성이나 화재 위험성도 낮고, 래커나 유성 스프레이로 인한 낙서를 효과적으로 제거할 수 있으며, 특히, 2액형 경화도료 상에 덧칠된 래커나 유성 낙서 제거시 바탕면의 도장면을 손상시키지 않으면서 낙서만 선택적으로 제거하는 장점이 있다.As can be seen from FIGS. 1A to 4 showing experimental results, the composition of the lacquer removing agent according to the present invention does not contain any toluene or butyl cellosolve which may harm the health of the operator It is possible to effectively remove the graffiti due to lacquer or oil spray, and in particular, to remove the lacquer or oil-based graff on the two-pack type hard coating, .

Claims (2)

디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 65 내지 95중량%, 자일렌(Xylene) 5내지 35중량%로 구성되는 것을 특징으로 하는 래커 제거제의 조성물A composition of a lacquer removing agent characterized by comprising 65 to 95% by weight of dipropylene glycol monomethyl ether (DPGME) and 5 to 35% by weight of xylene 디프로필렌 글리콜 메틸에테르(DPGME, Dipropylene glycol monomethyl ether) 62 내지 92중량%, 자일렌(Xylene) 7 내지 33중량%, 향 첨가물 1 내지 5중량%로 구성되는 것을 특징으로 하는 래커 제거제의 조성물Wherein the composition comprises 62 to 92% by weight of dipropylene glycol monomethyl ether (DPGME), 7 to 33% by weight of xylene and 1 to 5% by weight of a flavoring additive.
KR1020100081211A 2010-08-23 2010-08-23 Composition of lacquer remover KR101032880B1 (en)