KR100948234B1 - Manufacturing method of metallic yarn which have different color on both side and textiles which have irregular interval stripes and its weaving method - Google Patents

Manufacturing method of metallic yarn which have different color on both side and textiles which have irregular interval stripes and its weaving method Download PDF

Info

Publication number
KR100948234B1
KR100948234B1 KR1020090072988A KR20090072988A KR100948234B1 KR 100948234 B1 KR100948234 B1 KR 100948234B1 KR 1020090072988 A KR1020090072988 A KR 1020090072988A KR 20090072988 A KR20090072988 A KR 20090072988A KR 100948234 B1 KR100948234 B1 KR 100948234B1
Authority
KR
South Korea
Prior art keywords
sides
weaving
metallic
fabric
yarn
Prior art date
Application number
KR1020090072988A
Other languages
Korean (ko)
Inventor
이화선
Original Assignee
이화선
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이화선 filed Critical 이화선
Priority to KR1020090072988A priority Critical patent/KR100948234B1/en
Application granted granted Critical
Publication of KR100948234B1 publication Critical patent/KR100948234B1/en

Abstract

PURPOSE: A manufacturing method of metallic yarns having different colors, fabrics using the metallic yarn and a weaving method thereof are provided to weave the fabrics with raw yarns formed by cutting a film coated with the different colors. CONSTITUTION: A manufacturing method of metallic yarns having different colors includes a step for coating the both sides of a thin film with different colors, and a step for manufacturing the metallic yarns having a different coating layer on both sides of the film. A weaving method of the fabric using the metallic yarns includes the following steps: coating the both sides of the film with different colors; manufacturing the metallic yarns having different coating layers; and weaving the fabric with the metallic yarns. The fabric using the metallic yarns includes warp yarns(10) and weft yarns(20).

Description

양면이 다른 색을 갖는 메탈릭사 제조방법 및 이를 이용한 직물 및 그 제직 방법{Manufacturing method of metallic yarn which have different color on both side and Textiles which have irregular interval stripes and its weaving method}Manufacturing method of metallic yarn which has different color on both side and Textiles which have irregular interval stripes and its weaving method}

본 발명은 양면이 다른 색을 갖는 메탈릭사 제조방법 및 이를 이용한 직물 및 그 제직 방법에 관한 것이다.The present invention relates to a method of manufacturing metallic yarn having different colors on both sides, a fabric using the same, and a method of weaving the same.

메탈릭사(metallic yarn, 금속사)는 폭이 좁은 플라스틱 테이프나 알루미늄 또는 금절박을 실로 사용한 것인데, 2매의 아세트산 셀룰로스 또는 아세트산 셀룰로스 부틸의 필름을 합쳐 그 사이에 색소를 접착제와 같이 넣어 알루미늄박을 끼워서 제조하였다. Metallic yarn is made of narrow plastic tape or aluminum or gold foil as a thread.The two films of cellulose acetate or cellulose acetate butyl are combined together with a pigment in between to add an aluminum foil. It was prepared by sandwiching.

이러한 메탈릭사는 빛을 반사시켜 반짝이는 특성이 있어 고급스런 느낌을 줄 수 있으나, 구김이 안펴지고 충분한 내구력이 없어서 의류용으로는 부적합하였다.Such metallic yarns reflect light and have a shiny characteristic, which can give a luxurious feeling, but are not suitable for clothing because they are not wrinkled and do not have sufficient durability.

그런데, 메탈릭사가 섬유제품과 의류의 소재로서 사용된 것은 폴리에스테르 필름이 개발된 이후이며, 여기에다 금, 은 등의 색상을 착색시키고 세폭으로 절단하여 실 상태로 만들어, 섬유제품의 소재로 사용하여 왔다.However, Metallic was used as a material for textile products and garments after the development of polyester films, and the colors of gold, silver, etc. were colored, cut into thin sections, and used as materials for textile products. .

이러한 사용예로, 대한민국 등록특허 제10-544733호와 10-729493호에서와 같이 헤드타이(head tie) 또는 다마스크 원단에서 무늬를 형성하는 부분에 제한적으로 삽입되어 제직된 것이 있으나, 일부분에만 메탈릭사가 사용되므로 다른 원사들에 의하여 형성된 무늬를 돋보이게 하는 보조적인 역할만을 할 뿐 그 자체가 주도적으로 무늬를 형성하지는 못하였다.In this use example, there is a limited insertion into the portion forming the pattern in the head tie or damask fabric, as in Republic of Korea Patent Nos. 10-544733 and 10-729493, but only a part of the metallic Since yarns were used, they only played an auxiliary role to highlight the patterns formed by the other yarns, but they themselves did not form patterns.

그리고, 다른 예로는 상기한 메탈릭사를 무늬와 상관없이 사용하여 전체적으로 금속광택을 갖도록, 경사를 모두 메탈릭사로 제직한 직물(일명 메탈릭 오간디: metalic organdy)이 있으나, 이 경우에는 도 1에 나타내는 바와 같이 직물 전체가 하나의 색상만을 가지고 있고 색상으로 인한 어떠한 무늬도 형성되지 않기 때문에 광택을 가지고는 있지만 매우 단조로운 느낌을 줄 수 밖에 없었다.In addition, another example is a woven fabric (also known as metalic organdy) which is woven with all metallic yarns so as to have a metallic gloss as a whole using the metallic yarns irrespective of the pattern, but in this case, as shown in FIG. Likewise, the whole fabric has only one color and no pattern is formed, so it has a gloss but a very monotonous feeling.

또한, 상기한 메탈릭사로 줄무늬를 형성하기 위한 선행기술로 대한민국 등록실용신안공보제 20-0309578호에서는 메탈릭사를 경편 직물을 위한 다수의 바아(bar) 들 중 하나의 바아에 편성하여 메탈릭사가 타 원사와 함께 편직되어, 메탈릭사가 원단의 표면에 규칙적으로 일렬로 골을 이루도록 한 것이 있으나, 이 역시 메탈릭사가 표면에만 표출되므로 직물을 양면으로 사용하지 못하고, 메탈릭사가 원단의 일부에서만 규칙적으로 무늬를 형성하도록 되어 있어서 자연스러운 무늬와 다양한 색깔을 표출하지 못하였다.In addition, in the prior art for forming stripes with the metallic yarn described in Korean Utility Model Publication No. 20-0309578, the metallic yarn is knitted by knitting the metallic yarn on one of the bars for warp knitted fabrics. It is knitted together with the metallic yarn to make a regular line on the surface of the fabric, but this also because the metallic yarn is expressed only on the surface, so that the fabric cannot be used on both sides, and the metallic yarn regularly forms a pattern on only part of the fabric. It did not express natural patterns and various colors.

또한, 줄무늬를 형성하기 위한 다른 방법으로 색깔이 다른 다수의 메탈릭사를 정해진 위치에 배치하여 제직함으로, 사용된 색에 따라 다양한 무늬가 형성될 수 있으나, 이러한 무늬는 메탈릭사가 양면이 동일한 색을 가지므로 직물의 양면이 동일한 무늬를 가지게 되어 단조로운 느낌을 갖게 된다. 그리고, 작업자가 배치한 색깔 위치에 따라 줄무늬가 형성되므로 정해진 패턴이 지속적으로 반복되어, 인공적이고 규칙적인 느낌을 표출할 수 밖에 없었다.In addition, weaving by placing a plurality of metallic yarns of different colors in a predetermined position in another way to form a stripe, a variety of patterns can be formed according to the color used, but these patterns have the same color on both sides Therefore, both sides of the fabric will have the same pattern and will have a monotonous feeling. In addition, since stripes are formed according to the color position arranged by the worker, the predetermined pattern is continuously repeated, and the artificial and regular feelings have to be expressed.

한편, 상기한 메탈릭사는 바탕지에 무늬를 형성하는 자수사로로 많이 사용되는 것으로, 메탈릭사가 무늬를 형성하기는 하지만 자수사로 사용되므로 표면과 비교하여 이면이 깨끗하게 처리되지 않아서 양면직물로는 사용할 수 없는 문제점이 있었다.On the other hand, the metallic yarn is used as an embroidery yarn to form a pattern on the base paper, the metallic yarn to form a pattern, but because it is used as embroidery yarn, the back side is not clean compared to the surface can not be used as a double-sided fabric There was this.

상기한 문제점을 해결하기 위한 본 발명의 목적은 첫째, 양면이 다른 색을 갖는 메탈릭사를 제공하여, 다양한 색상의 직물을 제직할 수 있도록 하거나, 직물의 양면을 모두 사용할 수 있도록 하는 데 있다.An object of the present invention for solving the above problems is, first, to provide a metallic yarn having a different color on both sides, to be able to weave a fabric of various colors, or to use both sides of the fabric.

둘째, 상기한 바와 같이 양면이 다른 색을 갖는 메탈릭사를 경사로하여 직물을 제직함으로서 불규칙한 줄무늬가 형성된 직물을 제공하는 데 있다. 그리하여, 조직도나 문지 등 줄무늬를 형성하기 위한 디자인 수단을 필요로 하지 않아 생산이 용이하고, 줄무늬의 간격이 규격화되지 않고 불규칙적으로 배치되므로 미감, 특히 색감이 우수하면서, 메탈릭사의 광택과 다양한 색감으로 인하여 고급스러운 느낌의 직물을 얻을 수 있도록 하는 데 목적이 있다.Second, as described above, weaving the fabric by inclining metallic yarns having different colors on both sides to provide a fabric having irregular stripes. Therefore, it is easy to produce because it does not require design means for forming stripes such as organization charts or rubs, and the spacing of stripes is not standardized and irregularly arranged so that the aesthetics, especially the color, are excellent, The purpose is to make the fabric feel luxurious.

상기한 목적을 달성하기 위한 본 발명의 특징은, 얇은 필름의 양면을 각각 다른 색으로 코팅한 후 슬릿을 통과시켜 양면에 다른 코팅층을 갖는 메탈릭사를 제조하는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사 제조 방법에 있다.Features of the present invention for achieving the above object, both sides of the thin film, each coated with a different color and then passed through the slit to produce a metallic yarn having a different coating layer on both sides having a different color Metallic company manufacturing method.

그리고, 본 발명의 다른 특징은 얇은 필름의 양면을 각각 다른 색으로 코팅한 후 슬릿을 통과시켜 양면에 다른 코팅층을 갖는 메탈릭사를 제조하고, 상기한 메탈릭사를 이용하여 직물을 제직하는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물 제직 방법에 있다.In addition, another feature of the present invention is to coat each side of the thin film with a different color and then pass through the slit to produce a metallic yarn having a different coating layer on both sides, characterized in that weaving fabric using the metallic yarn There is a method of weaving fabrics using metallic yarns on which both sides have different colors.

상기에서 제직 과정은, 종광을 포함한 제직용 구성품에 양면에 다른 코팅층 을 갖는 메탈릭사를 복수의 색상이 임의의 비율로 교대로 배치되도록 꿰어주는 통경(Drawing in) 단계와; 통경이 완료되면 종광을 포함한 제직용 구성품을 설정된 위치로 고정하고 경사에 적정한 장력이 균일하게 주어지도록 하여 통경 단계와 상관없이 경사의 방향이 결정되도록 하는 경승 단계와; 경사 사이로 위사를 투입하여 직물을 제직하여 불규칙한 간격의 줄무늬가 형성되는 제직 단계로 구성된다.The weaving process may include a drawing step of stitching metallic yarns having different coating layers on both sides of the woven component including heald so that a plurality of colors are alternately arranged at an arbitrary ratio; A tilting step of fixing the weaving component including heald to a set position when the diameter is completed, so that a proper tension is uniformly given to the inclination so that the direction of the inclination is determined regardless of the diameter step; It is composed of a weaving step of weaving the fabric by weaving the weft between the slopes to form stripes of irregular intervals.

그리고, 본 발명의 또 다른 특징은 얇은 띠형으로 형성되고 양면에 다른 색의 코팅층이 형성되어 통경 및 경승 단계를 거치면서 불규칙한 줄무늬가 형성되도록 코팅층의 위치가 통경 단계와 상관없이 임의로 결정되는 경사와, 상기한 경사와 제직되는 위사를 포함하며, 직물의 길이방향으로 불규칙한 간격의 줄무늬가 형성되고, 이면은 표면과 대칭되는 색으로 형성되는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물에 있다.In addition, another feature of the present invention is that the inclination of the coating layer is arbitrarily determined irrespective of the diameter step so that a thin stripe is formed, and coating layers of different colors are formed on both sides to form irregular stripes while passing through the diameter and tilting steps. In the fabric using a metallic yarn having a different color on both sides, characterized in that the inclination and weaving weaving, and the stripes of irregular intervals in the longitudinal direction of the fabric is formed, the back surface is formed in a color symmetrical with the surface. have.

상기에서 경사는 폴리에스테르 필름 양면에 다른 색의 코팅층이 형성된 메탈릭사를 사용하여 제직된 직물이 광택을 갖도록 하고, 위사는 원착사를 사용한다.The inclination in the above is to make the fabric woven using a metallic yarn formed with a coating layer of a different color on both sides of the polyester film, the weft yarn is used.

상기에서 원착사(dope dyed yarn)는 방사공정에서 폴리에스테르 수지(POLYESTER RESIN)에 안료가 분산된 상태로 혼합되어, 방사되는 과정에 색사가 생산되는 것으로 일반 염색사와 같이 별도의 염색공정이 필요하지 않는 것을 말한다.In the above, the dope dyed yarn is mixed in a state in which pigments are dispersed in a polyester resin in a spinning process, and a color yarn is produced during the spinning process, and a separate dyeing process is not required like a general dyed yarn. Say that doesn't.

상기한 바와 같은 본 발명에 의하면 양면이 다른 색으로 코팅된 필름을 절개하여 제조된 원사를 이용하여 직물을 제직하므로, 종래의 메탈릭사가 양면이 같은 색을 가짐으로서 발생되는 단조로운 미감을 개선하여, 색상을 다양하게 하고, 광택을 갖는 무늬가 형성되도록 하여 직물이 고급스러움을 가질 수 있게 되는 효과가 있어, 무대복을 포함한 의류나, 인형 장식품, 결혼식 혹은 생일 등의 행사용 의류, 벽지, 양말, 스타킹, 넥타이, 스카프, 액자, 신발, 가방 등애 다양하게 사용되어 해당 제품의 색감을 다양하게 하면서 고급스러운 느낌을 갖도록 하는 효과가 있다.According to the present invention as described above, weaving the fabric using a yarn prepared by cutting a film coated with a different color on both sides, thereby improving the monotonous aesthetics caused by having the same color of the conventional metallic yarn, color It is effective to make the fabrics have a high quality by making the pattern to have a glossy pattern, clothing including stage clothes, doll ornaments, clothing for events such as wedding or birthday, wallpaper, socks, stockings, Neckties, scarves, frames, shoes, bags, etc. are used in a variety of ways to vary the color of the product has an effect that makes you feel luxurious.

또한, 상기한 바와 같은 본 발명의 메탈릭사로 제직된 직물은 동일한 위치에서 양면이 다른 색상을 가지게 되고, 직물의 표면과 이면의 구분이 없어지므로 양면을 모두 사용할 수 있게 된다.In addition, the fabric woven with the metallic yarn of the present invention as described above will have a different color on both sides at the same position, so that the distinction between the surface and the back side of the fabric can be used both can be used.

또한, 상기한 원사를 종광에 건 후 제직을 위하여 적정한 장력으로 당기면 얇은 띠형으로 형성된 원사가 당겨지는 과정에서 표면과 이면의 위치가 임의로 바뀌게 되므로, 직물을 제직하면 불규칙적인 줄무늬가 표출되며, 제직된 직물은 표면과 이면이 대칭되는 다른 색을 갖게 되므로 미감 특히 색감이 우수한 직물을 제공할 수 있게 된다.In addition, when the yarn is pulled to the heald and pulled at an appropriate tension for weaving, the position of the front and back sides is arbitrarily changed in the process of pulling the thin band-shaped yarn, and thus, irregular stripes are displayed when weaving the fabric. The fabric has a different color where the surface and the back face are symmetrical, which makes it possible to provide a fabric with excellent aesthetics, especially color.

그리고, 상기한 바와 같은 직물의 줄무늬를 별도의 디자인과정 없이도 표현할 수 있어서 생산효율이 향상되는 효과가 있고, 별도로 디자인을 해서 형성된 줄무늬가 아니므로 제직 과정에서 줄무늬의 위치 및 간격이 계속적으로 변경되므로 직물을 제직하다가 직기를 세워서 경사에 장력이 해제되면 동일한 직물에 있어서도 다른 줄무늬가 형성된다.And, the stripes of the fabric as described above can be expressed without a separate design process has the effect of improving the production efficiency, and because the stripes are not formed by designing separately, the position and spacing of the stripes in the weaving process is continuously changed When weaving and standing up the loom and the tension is released on the warp, different stripes are formed on the same fabric.

이하 본 발명의 실시예를 첨부한 도면을 참조하여 보다 상세하게 살펴본다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings.

본 발명의 실시예에서는 줄무늬 직물을 제직하는 과정을 예로서 설명한다.In the embodiment of the present invention, a process of weaving a striped fabric will be described as an example.

도 2는 본 발명에 따른 메탈릭사 제조 과정을 나타내는 도면으로, 설명의 편의를 위하여 (b) 및 (c)에서는 양면의 색이 다름을 표시하기 위하여 필름 및 메탈릭사의 일부를 접어서 표시하였다. 그리고, 도 3은 본 발명에 따른 직물을 나타내는 도면이다.FIG. 2 is a view illustrating a manufacturing process of metallic yarn according to the present invention. For convenience of description, in (b) and (c), parts of the film and metallic yarn are folded and displayed to indicate that the colors of both surfaces are different. 3 is a view showing a fabric according to the present invention.

본 발명에 따른 불규칙한 간격의 줄무늬를 갖는 직물 제직 방법은 양면에 다른 색의 코팅층을 갖는 띠형 메탈릭사를 제조하고 권사하는 메탈릭사 제조 단계와, 상기한 메탈릭사를 종광을 포함한 제직용 구성품에 서로 다른 색이 상부를 향하도록 교대로 꿰어주는 통경(Drawing in) 단계와; 통경이 완료되면 종광을 포함한 제직용 구성품을 설정된 위치로 고정하고 경사에 적정한 장력이 균일하게 주어지도록 하는 경승 단계와; 경사 사이로 위사를 투입하여 직물을 제직하는 제직단계로 구성된다.Fabric weaving method having a stripe of irregular intervals according to the present invention is different from the metal yarn manufacturing step of producing and winding a strip-shaped metallic yarn having a coating layer of a different color on both sides, and the above-mentioned metallic yarn in a woven component including a heald. A drawing in step of alternately stitching the colors to face upwards; A tilting step of fixing the weaving component including the heald to a set position when the diameter is completed and giving a proper tension to the inclined uniformly; It consists of a weaving step of weaving the fabric by inserting the weft between the warp.

상기에서 경사는 폴리에스테르 필름의 양면에 각각 다른 색의 코팅층이 형성된 메탈릭사를 사용하여 제직된 직물이 광택을 갖도록 하고, 위사는 20분사 원착사를 사용한다.In the above inclination, the woven fabric is polished using metallic yarns formed with coating layers of different colors on both sides of the polyester film, and the weft yarns use 20-spray primary yarns.

이러한 메탈릭사는 통상 금사，은사처럼 반짝이는 실을 지칭하는 것으로, 강렬한 색상과 세련된 이미지 연출이 가능해 스카프，넥타이 등 고급 패션액세서리의 소재로 많이 쓰이는데, 종래의 메탈릭사는 통상 양면에 동일한 색의 코팅층을 형성하였으나, 본 발명에서는 도 2의 (a)와 같이 표면에 알루미늄 혹은 은이 증착된 폴리에스테르 필름의 양면에 (b)와 같이 분홍색과 녹색으로 코팅층을 형성하고, 이를 슬릿을 통과시켜 원하는 폭으로 절개하면 (c)와 같이 양면이 다른 색을 갖는 메탈릭사가 제조되고 이를 보빈에 권사함으로서 메탈릭사를 제작한다.These metallic yarns generally refer to shiny threads like gold yarn and silver, and can be used as a material for high-end fashion accessories such as scarves and neckties because they can produce intense colors and sophisticated images. Conventional metallic yarns usually form coating layers of the same color on both sides. However, in the present invention, as shown in (a) of FIG. 2, if the coating layer is formed in pink and green on both sides of the polyester film on which aluminum or silver is deposited on the surface as shown in (b), it is cut through the slits and cut to a desired width. Metallic yarns having different colors on both sides are prepared as shown in (c), and the metallic yarns are manufactured by winding them on bobbins.

이와 같이 제조된 메탈릭사는 경사로 사용하기 위하여 정경 과정을 거치게 되는데, 상기한 정경 과정은 경사를 직기에 공급하기 위하여 한 올 한 올의 경사를 평행하게 배열시키고 장력을 일정하게 하여 정경빔에 실을 감아주는 것을 말한다.The metallic yarn manufactured as described above undergoes a canon process for use as a warp yarn. The above warp process is to arrange warp beams in parallel with each other in order to supply a warp yarn to a loom and wind the yarn in a warp beam with a constant tension. I say giving.

그리고, 상기한 바와 같이 제조된 정경 과정을 거친 메탈릭사를 경사로 사용하기 위하여 종광과 바디 및 드롭퍼 등에 경사를 걸어주는 통경 단계를 거치는데, 종광에 메탈릭사를 걸어주는 과정에서 작업자는 분홍색과 초록색이 교대로 상부를 향하도록 메탈릭사의 방향을 결정하여 걸어준다.In addition, in order to use the metallic yarn that has undergone the canonical process manufactured as described above, the inclined stage is inclined to the heald and the body and the dropper, and in the process of hanging the metallic yarn to the heald, the worker is pink and green. Alternately walk in the direction of metallic yarn to face upward.

이때 경사의 초록색과 녹색을 1:1로 교대되도록 걸어줄 수도 있고, 2:2 또는 1:2 등 다양하게 변형시켜서 교대로 걸어줄 수도 있으며, 이와 같이 색이 교대로 위치되도록 하여야 제직된 후의 줄무늬에서 각 줄무늬를 형성하는 색의 배치가 균일하게 나타나며, 상부를 특정색만으로 하여 종광에 걸어줄 경우에는 해당 색이 지배적으로 표출되는 줄무늬가 형성되므로 미감을 떨어뜨리게 된다.At this time, the green and green of the slope can be hanged alternately by 1: 1, or can be alternately hanged by changing variously, such as 2: 2 or 1: 2. Stripes after weaving should be placed alternately. In the arrangement of the colors forming each stripe is uniformly appeared, and when the upper part is a specific color only to hang on the heald, the color is dominantly expressed streaks are formed, thereby reducing the aesthetics.

상기한 통경단계가 완료되면 경승단계를 수행하게 되는데 상기한 경승 단계는 경사에 필요한 모든 준비작업을 마친 경사빔을 직기에 걸고 종광, 바디, 드롭퍼 등을 소정의 위치에 고정시켜 경사의 전단을 클로스로울러(Cloth roller)에 고정시킨 다음 시직을 하면서 경사의 장력을 균일하게 조정하고 직물조직이 올바로 되어 있는지 확인하고 직물의 외관 및 품질이 계획한대로 나타나는지 확인하는 단계로서 경사 준비공정의 최후 공정이다.When the above-mentioned passage stage is completed, the stage of stabilization is performed. The stage of stabilization includes closing the warp beam after finishing all preparation work necessary for the warp and fixing the heald, body, and dropper at a predetermined position to close the slope of the slope. It is the final step of the slope preparation process as it is fixed to the roller and then the work is adjusted to uniformly adjust the tension of the warp and check that the fabric structure is correct and that the appearance and quality of the fabric appear as planned.

이러한 경승(Looming) 단계에서 경사는 종광에 걸어지는 과정에서는 느슨하게 늘어진 상태로 있으나 경승 단계에서 경사가 당겨지면서 경사는 상부로 향하는 색이 임의로 결정되는데, 예를 들어 종광에 경사를 걸때는 분홍색이 상부로 향하도록 하더라도 실제 경승 단계에서는 녹색이 상부로 향하게 된다.In this step of ramping, the slope is loosely stretched in the course of walking on the heald, but in the stage of ramping, the slope is randomly determined as the color of the slope is directed upwards. Even if you turn to, the green will go up in the actual stage of the race.

이러한 경승 단계를 거치고 제직을 위한 모든 준비가 완료되면 위사를 경사사이로 투입하면서 제직을 하게 된다.After all these stages of weaving and all preparations for weaving are completed, weaving is carried out while wefts are introduced between the warp yarns.

이러한 본 발명에 따라 제직된 직물은 도 3에 나타내는 바와 같이 얇은 띠형으로 형성되고 표면과 이면에 다른 색의 코팅층이 형성된 경사(10) 및 상기한 경사(10)와 제직되는 위사(20)를 포함하며, 직물의 길이방향으로 불규칙한 간격의 직선무늬가 형성되고, 이면은 표면과 대칭되는 색으로 형성된다.The woven fabric woven according to the present invention includes a warp yarn 10 which is formed in a thin band shape and has a coating layer of a different color formed on its front and back surfaces as shown in FIG. 3 and the weft yarn 20 woven with the warp yarn 10 described above. In addition, irregularly spaced linear patterns are formed in the longitudinal direction of the fabric, and the rear surface is formed in a color symmetrical with the surface.

구체적으로 도 3에 나타내는 바와 같이 메탈릭사가 분홍색과 초록색 코팅층을 갖는 경우 1번 줄무늬 부분에서 한쪽면에 분홍색 줄무늬가 표시되면 반대면의 동일한 위치에는 초록색 줄무늬가 형성된다.Specifically, as shown in FIG. 3, when the metallic yarn has a pink and green coating layer, if a pink stripe is displayed on one side of the first stripe portion, a green stripe is formed at the same position on the opposite side.

그리고, 같은 면에서도 임의의 간격의 분홍색 줄무늬 옆에는 초록색 줄무늬가 형성되는데, 이러한 줄무늬는 경사의 색에 따라 그 간격이 정해지게 되는 것이다.In addition, green stripes are formed next to the pink stripes at random intervals on the same surface, and the stripes are determined according to the color of the slope.

한편, 상기한 바와 같이 줄무늬를 형성하지 않고 미리 설정된 무늬에 따라 메탈릭사의 색상배치를 조절하여 직물을 제직할 수도 있다.On the other hand, it is also possible to weave the fabric by adjusting the color arrangement of the metallic yarn according to a predetermined pattern without forming a stripe as described above.

도 1은 종래의 메탈릭사를 이용한 직물을 나타내는 도면1 is a view showing a fabric using a conventional metallic yarn

도 2는 본 발명의 메탈릭사 제조 과정을 나타내는 도면Figure 2 is a view showing a metallic yarn manufacturing process of the present invention

도 3은 본 발명에 따라 제직된 직물을 나타내는 도면3 shows a fabric woven in accordance with the present invention.

Claims (5)

얇은 필름의 양면을 각각 다른 색으로 코팅한 후 슬릿을 통과시켜 양면에 다른 코팅층을 갖는 메탈릭사를 제조하는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사 제조 방법.Both sides of the thin film is coated with a different color, respectively, and then passed through the slit to produce a metallic yarn having a different coating layer on both sides of the metallic yarn manufacturing method having a different color on both sides. 얇은 필름의 양면을 각각 다른 색으로 코팅한 후 슬릿을 통과시켜 양면에 다른 코팅층을 갖는 메탈릭사를 제조하고, 상기한 메탈릭사를 이용하여 직물을 제직하는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물 제직 방법.Both sides of the thin film are coated with different colors, and then passed through the slit to produce a metallic yarn having a different coating layer on both sides, and the two sides of the metallic with different colors, characterized in that weaving fabrics using the metallic yarn described above. Fabric weaving method using yarn. 제 2항에 있어서, 상기한 제직 과정은The method of claim 2, wherein the weaving process is 종광을 포함한 제직용 구성품에 양면에 다른 코팅층을 갖는 메탈릭사를 복수의 색상이 임의의 비율로 교대로 배치되도록 꿰어주는 통경(Drawing in) 단계와; A drawing step of stitching metallic yarns having different coating layers on both sides of the woven component including heald so that a plurality of colors are alternately arranged at an arbitrary ratio; 통경이 완료되면 종광을 포함한 제직용 구성품을 설정된 위치로 고정하고 경사에 적정한 장력이 균일하게 주어지도록 하여 통경 단계와 상관없이 경사의 방향이 결정되도록 하는 경승 단계와; A tilting step of fixing the weaving component including heald to a set position when the diameter is completed, so that a proper tension is uniformly given to the inclination so that the direction of the inclination is determined regardless of the diameter step; 경사 사이로 위사를 투입하여 직물을 제직하여 불규칙한 간격의 줄무늬가 형성되는 제직 단계로 구성되는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물 제직 방법.A weaving method using metallic yarns having different colors on both sides, characterized by comprising a weaving step of weaving the fabric by weaving the weave between the warp yarns to form stripes at irregular intervals. 얇은 띠형으로 형성되고 양면에 다른 색의 코팅층이 형성되어 통경 및 경승 단계를 거치면서 불규칙한 줄무늬가 형성되도록 코팅층의 위치가 통경 단계와 상관없이 임의로 결정되는 경사와, 상기한 경사와 제직되는 위사를 포함하며, 직물의 길이방향으로 불규칙한 간격의 줄무늬가 형성되고, 이면은 표면과 대칭되는 색으로 형성되는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물.It is formed in a thin band and formed on both sides of the coating layer of different colors to form irregular stripes while passing through the diameter and tilting step, the position of the coating layer is arbitrarily determined irrespective of the diameter step, and the inclined and weft weaving And a stripe having irregular intervals in the longitudinal direction of the fabric, and a back surface formed with a color symmetrical with the surface. 제 4항에 있어서, 경사는 폴리에스테르 필름 양면에 다른 색의 코팅층이 형성된 메탈릭사를 사용하는 것을 특징으로 하는 양면이 다른 색을 갖는 메탈릭사를 이용한 직물.The fabric using a metallic yarn having a different color on both sides, characterized in that the inclined is a metallic yarn having a coating layer of a different color formed on both sides of the polyester film.
KR1020090072988A 2009-08-07 2009-08-07 Manufacturing method of metallic yarn which have different color on both side and textiles which have irregular interval stripes and its weaving method KR100948234B1 (en)